By W. L. Phillips

Stress-strain curves were obtained for single crystals of 70 pct Ag-30 pct Zn tested in tension and shear. Samples tested in tension and shear had comparable resolved shear stresses and stress-strain curves. The {111} <110> slip system was observed. It zoas found that the9.e is a barrier to slip in both latent close -packed directions and that the magnitude of these barriers is proportional to prior strain during easy glide. It was observed that cross-slip in tension and shear was most frequent in crystals with an initial orientation near <100> "Oershoot" zoas observed in tension. The amount of this "overshoot" was independent of initial orientation. AN idealized concept of plastic deformation indicates that a single crystal should yield at some stress that is dependent on crystal perfection and it should then continue to deform plastically by the process of easy glide which is characterized by a linear stress-strain curve and a low coefficient, d/dy, of work hardening. Hexagonal metal crystals generally conform to this ideal concept of laminar flow. In fcc metals the range of easy glide is always restricted in magnitude and it is strongly dependent on orientation, composition, crystal size, shape, surface preparation, and temperature. Since one of the principal differences between the two crystal systems, both of which deform by slip on close packed planes, is the existence of latent slip planes in the fcc crystals, it has been proposed that the transition from easy glide to turbulent flow, characterized by rapid linear hardening, is due to slip on secondary planes intersecting the primary plane.ls Several theories have been proposed to explain the linear hardening and parabolic stages of the stress -strain curve.6"10 The easy-glide region is the least understood of the three stages. The stress-strain characteristics of Cu-Zn, which shows a long easy-glide region, have been extensively investigated."-" In light of recent ideas on dislocations, cross-slip, effect of solute atoms, and stacking fault energy, it was felt that the certain features of this earlier work might be compared with another alloy, Ag-30 pct Zn, which also exhibits a long easy-glide region. Tension and shear stress at room temperatures were employed. The results obtained, together with some interpretation of the observations, are described below. EXPERIMENTAL PROCEDURE The silver and zinc used for mixing the alloys were 99.99 pct pure. The two components were weighed to within 0.1 pct of the weights required fo the alloy composition. They were then placed in a closed graphite mold and the mold and contents were heated in 100°C stages from 500&apos; to 900°C with sufficient time and vigorous agitation at each stage provided to dissolve the silver. The crucible was then heated to 1150°C and agitated violently before being quenched in oil. The resulting alloy rod was machined free of sur face defects and then placed in a graphite mold designed for growing single crystals. The graphite mold was closed with a graphite plug and was encased in a pyrex glass tube which was connected to a vacuum system. The tube and mold assembly were placed in a furnace; the tube was evacuated and the furnace was rapidly heated to a temperature sufficient for fusing and sealing the glass. The glass-encased evacuated mold and contents were then lowered through a vertical furnace. The top section of the furnace was held at 100 °C above the melting point of the alloy. The lowering rate was 1.5 in. per hr. The tension specimens were 1/4 in. diam; the shear specimens were 1/2 in. diam. These specimens were then removed from the mold, etched, and chemically polished with hot (60°C) Chase etch reagent (Crz03-4.0 g, NH4C1-7.5 g, NHOs-150 cc, HzS04-52 cc, and Hz0 to make 1 liter). In preparation for tensile testing, the specimens were carefully machined to a diameter of about 0.200 in. to permit a gage length of 6 in., annealed for 16 hr at 800&apos; to reduce coring, and then cleaned and polished. A modified Bausch-type shear apparatus which has been described previously18 were employed. The gage length was 1/8 in. This shear apparatus was placed in an Instron tensile testing machine. EXPERIMENTAL RESULTS A) Tension. Several specimens were extended at room temperature to determine the effect of initial orientation on the stress-strain curves of Ag-30 pct Zn. The initial orientation and the resolved shear stress supported by the active slip system at various total strains are plotted in Fig. 1. The critical resolved shear stress, t,, initial rate of work hardening, d/dy, and length of the easy-glide region are independent of orientation. The arrival at the symmetry line is shown by an arrow in Fig. 1. During the easy-glide region of the stress-strain

Jan 1, 1963

By R. R. Vandervoort, W. L. Barmore

Tensile creep experiments were conducted on high-purity, poly cvystalline rhenium from 1500" to 2300°C at stresses from 1500 to I0,OOO psi in a vacuum of 10-a torr. The apparent activation energy for creep was 60 kcal per mole, and the steady-state creep rate varied directly with stress to the 3.4 power. Dislocation substructure that developed during creep was studied by transmission electron microscopy. Possible rate-controlling deformation mechanisms are discussed. The creep behavior of most metals at elevated temperature can be represented by the following equation:&apos;&apos;&apos; t = Cf(s)(^)(s/E)nD [1] where i = steady-state creep rate, C = constant, f(s) = a function involving microstructure, s = applied stress, E = the average elastic modulus at test temperature, n = constant, D = diffusion coefficient According to this well-established relationship, metals with higher elastic moduli and lower diffusion coefficients should have greater creep resistance at the same stress and temperature and equivalent mi-crostructures. While no diffusion data are available, the diffusivity of rhenium should be less than that for most other refractory metals because of its high melting point and hcp crystal structure. The Sherby-Simnad relation for calculating atomic mobility in metallic systems3 predicts that the diffusion coefficient for rhenium is less than that experimentally determined for tungsten4 in the temperature region 1500. to 2200°C. At these temperatures the elastic modulus for tungsten5 is only slightly larger than the extrapolated modulus for rhenium.6 Thus, rhenium is a good possibility for a a high-temperature structural material, but few data on the creep of rhenium have been reported. This investigation was undertaken to study the high-tempera-ture deformation behavior of rhenium in detail. EXPERIMENTAL TECHNIQUES The material used in this study was consolidated from high-purity powder. After cold pressing the powder to a plate a in. thick, the billet was sintered in hydrogen at 2250°C for 24 hr. The plate was reduced to 0.100 in. by cold cross rolling with intermediate anneals at 1650°C for 20 min between passes. The plate was further reduced to 0.060 in. by unidirectional cold rolling with similar heat treatments between passes, and then finally stress-relieved in hydrogen at 1650°C for 30 min. Specimens tested at 1900°C and below were pretest-annealed at 1900°C for 2 50 hr. Specimens tested above 1900°C were pretest-annealed at 2400°C for 5 hr. The impurity content in the "as-received" plate was quite low, table I. Essentially no change in impurity levels was detected in specimens after creep testing. All creep tests and annealing treatments were conducted in a vacuum of 10-8 torr in a test furnace heated by a tungsten mesh element. The load was applied to the specimens through a bellows, and stresses were maintained to ±1 pct of the selected value by periodic corrections for changes in specimen cross-sectional area during creep and for changes in the bellows spring force due to load column extension. One-inch-diameter tungsten force rods were used in the hot zone of the furnace. Deformation at temperature was measured by optically tracking gage marks on the specimen. Temperature was measured by a calibrated optical pyrometer and was determined to ±5"C. Grain sizes were determined by the linear intercept method and specimens were examined in the "as-polished" condition, using polarized light. Specimens annealed at 1900°C had a grain size of 52 ± 5µ , and those annealed at 2400°C had a grain size of 148 * 11 µ. Pieces were cut from the gage section of creep-tested specimens and planed to a thickness of about 0.010 in. by spark discharge machining. Thin foils for viewing by transmission electron microscopy were obtained by electropolishing in a solution of 6:3:1 ethyl alcohol, perchloric acid, and butoxy ethanol, respectively, using the window technique. Bath temperature was —4OoC, and the cell potential was 35 v. The foils were examined in Siemens Elmiskop I, operating at 100 kv. RESULTS AND DISCUSSION In order to analyze the results from creep experiments, Eq. [I] is rewritten in the following form: <=Kf(s)ne-/RT [2] where K = constant, ?// = apparent activation energy for creep,

Jan 1, 1970

By George R. Elliott

Methods are presented for measuring and comparing "degree" of water drive, and for observing the control that rate of withdrawal exerts over decline of reservoir pressure. Degree of water drive is studied from pressure-production curves of 10 reservoirs; the method used to present these comparatively is to convert cumulative oil production from barrels to percentage of ultimate. Degree of water drive is also represented by a "water-encroachment factor," representing barrels of water influx per pound-month per acre-foot of oil reservoir. Pressure-production curves for the water-drive reservoirs after a period of declining pressure show a diminishing angle of slope, in some cases to the point where pressure ceases to decline or where it even increases; the shapes of these curves are in marked contrast to the dissolved-gas type of curve, which shows a general trend toward zero pressure at ultimate oil recovery. Yearly rate of oil production in percentage of ultimate oil recovery is correlated with pressure decline. The correct rate of production of oil with its associated gas and water sustains pressure in reservoirs having a high water-encroachment factor. For reservoirs having a low water-encroachment factor, it is necessary to inject the produced water and even inject large volumes of water from an outside source. The discussion of the actual reservoirs is preceded by a general review and is followed by a substantial bibliography. It is now generally accepted that water drive is capable of yielding 60 to 80 per cent of the original oil in place in most reservoirs, as compared with 20 to 40 per cent for dissolved-gas drive. There is no need to question the importance of controlling a reservoir in order to take advantage of such an efficient mechanism. What is a water-drive reservoir? Oil reservoirs usually combine two or more of the four basic mechanisms: dissolved-gas drive, gas-cap drive, water drive, gravity drainage. A water-drive reservoir is one in which water advances to take the place of the oil and gas produced. When the oil withdrawal rate is sufficiently low, the water will tend to maintain pressure. The maximum effectiveness is attained when the water follows the oil withdrawal so closely that little or no decline in pressure occurs. Oil in its underground reservoir is associated with water. This water is significant in the production of the oil according to the source of supply and the permeability of the surrounding formation. As oil is produced and the pressure is lowered, water can move in to replace the oil. With adequate supply and sufficient permeability, actual movement takes place on an extensive scale. The first movement of water takes place by expansion of the water and its associated fluids. While this expansion is of little importance in some fields, in others it is sufficient to supply all of the energy required for the production of oil. When a pressure differential has been established

Jan 1, 1946

By George R. Elliott

Methods are presented for measuring and comparing "degree" of water drive, and for observing the control that rate of withdrawal exerts over decline of reservoir pressure. Degree of water drive is studied from pressure-production curves of 10 reservoirs; the method used to present these comparatively is to convert cumulative oil production from barrels to percentage of ultimate. Degree of water drive is also represented by a "water-encroachment factor," representing barrels of water influx per pound-month per acre-foot of oil reservoir. Pressure-production curves for the water-drive reservoirs after a period of declining pressure show a diminishing angle of slope, in some cases to the point where pressure ceases to decline or where it even increases; the shapes of these curves are in marked contrast to the dissolved-gas type of curve, which shows a general trend toward zero pressure at ultimate oil recovery. Yearly rate of oil production in percentage of ultimate oil recovery is correlated with pressure decline. The correct rate of production of oil with its associated gas and water sustains pressure in reservoirs having a high water-encroachment factor. For reservoirs having a low water-encroachment factor, it is necessary to inject the produced water and even inject large volumes of water from an outside source. The discussion of the actual reservoirs is preceded by a general review and is followed by a substantial bibliography. It is now generally accepted that water drive is capable of yielding 60 to 80 per cent of the original oil in place in most reservoirs, as compared with 20 to 40 per cent for dissolved-gas drive. There is no need to question the importance of controlling a reservoir in order to take advantage of such an efficient mechanism. What is a water-drive reservoir? Oil reservoirs usually combine two or more of the four basic mechanisms: dissolved-gas drive, gas-cap drive, water drive, gravity drainage. A water-drive reservoir is one in which water advances to take the place of the oil and gas produced. When the oil withdrawal rate is sufficiently low, the water will tend to maintain pressure. The maximum effectiveness is attained when the water follows the oil withdrawal so closely that little or no decline in pressure occurs. Oil in its underground reservoir is associated with water. This water is significant in the production of the oil according to the source of supply and the permeability of the surrounding formation. As oil is produced and the pressure is lowered, water can move in to replace the oil. With adequate supply and sufficient permeability, actual movement takes place on an extensive scale. The first movement of water takes place by expansion of the water and its associated fluids. While this expansion is of little importance in some fields, in others it is sufficient to supply all of the energy required for the production of oil. When a pressure differential has been established

Jan 1, 1946

By J. L. Walter

Extra-low carbon iron sheet, when deformed and annealed, undergoes exaggerated or abnormal grain growth in the critically deformed regions of the sheet. This exaggerated pmth occurs, for low strains (3 to 6 pct), only in sheet which has a fine dispersion of precipitates in the subsurface region of the sheet and fewer and coarser precipitates in the sheet interior. These particles have been identified as manganese sulfides. Wing the anneal, grains near the surface are gvowth-inhibited by the fine particles but the grains in the interior are free to grow normally. With the additional driving force provided by the strain energy, the interior grains first grow into the small subsurface pains. Eventually, these growing grains grow completely through the sheet. Calculations of limiting grain sizes at various values of strain indicate that a volume fraction of precipitates in excess of 10-&apos; would be required to eliminate exaggerated growth in material strained to 10 pct. OPEN-COIL annealing has made decarburization of sheet steel both efficient and economically practical. Use of such material for porcelain-enameling stock is one of many possible applications of low-carbon iron since carbon in steel is deleterious to porcelain-enameling properties.&apos; However, the extra-low carbon iron presently available presents another problem, that of exaggerated grain growth in regions where the sheet has been deformed as by bending or stretching. In exaggerated grain growth a few grains start to absorb their neighbors and these may become very much larger than the average grains of the sheet. Other names for exaggerated grain growth are coarsening, critical grain growth, secondary recrystallization, abnormal grain growth, or discontinuous grain growth. While this grain growth does not affect the enameling qualities of the low-carbon iron sheet, their presence results in a marked reduction of tensile-yield strength in the region of the sheet containing the large grains. The loss of tensile yield strength may render the material unsuitable for many applications . This report describes the results of a study undertaken to determine the cause of the exaggerated grab growth in extra-1ow carbon iron and, if possi- ble, to prescribe practical procedures for its prevention. GENERAL THEORY The driving force for exaggerated grain growth is the grain boundary free energy. This driving force is proportional to (l/rl + l/r2) where rl and r2 are the mutually perpendicular radii of curvature of the boundary between the growing grain and the grain being consumed. Thus, the greater the difference in size between the growing grain and the matrix grains, the higher the driving force for grain growth. If, however, the matrix grains are free to grow simultaneously, the driving force for exaggerated growth will be diminished. Stability toward growth of the matrix grains may be caused by a) a strong single orientation texture (texture inhibition),&apos; b) a dispersed second phase,3"5 c) the thickness effect,&apos; or d) intergranular segregation.7"9 As exaggerated growth occurs when growth of the matrix grains has been slowed by the stabilizing processes mentioned above, there must be an additional factor acting to promote growth of a few of the grains to the point where they are enough larger than the matrix grains that boundary energy driving forces are sufficient to cause continued growth. For instance, at the annealing temperature, growth-inhibiting inclusions may slowly dissolve and coalesce. Eventually, a grain boundary becomes unlocked and migration occurs at the expense of neighboring grains. Or, an additional driving force may be supplied to some of the grains if the material is strained. Then, since some grains will be strained less than others, the difference in strain energy between adjacent grains may be sufficient to overcome boundary locking and allow growth of the grains with lower strain energies. In the present study, therefore, such factors as the presence or absence of dispersed phases, the nature of the exaggerated growth, and the effect of strain have been considered. EXPERIMENTAL PROCEDURE I) Material and Processing. Three types of low-carbon iron were used in this study; types A and B were commercial grades, each from a different supplier.* The precise details of the processing of

Jan 1, 1963

By Gerhard Derge

A SERIES of studies of the corrosion of tin is under way in the Metals Research Laboratory at the Carnegie Institute of Technology. The complete program includes examination of the corrosion properties of high-purity tin and the changes produced in these properties by the addition of varying amounts of alloying elements. Other studies of this subject have been made recently under the sponsorship of the International Tin Research and Development Council, but these researches have been confined largely to the weakly acid environments commonly encountered in the canning industry.1 There is little information available regarding the corrosion of tin under alkaline conditions, but such data would be of value, for a large amount of the metal is used under such conditions. The potential measurements to be described were made because they seemed to offer the most rapid method for obtaining a general view of the conditions to be encountered in such service. These experiments will also serve to establish a technique that will be of value in further studies. It must be emphasized that the results reported are those of controlled laboratory experiments and that the conclusions drawn cannot yet be applied to service conditions; rather, they point to the directions in which more exhaustive experimental work may be done to best advantage. EXPERIMENTAL PROCEDURE The first work was devoted entirely to the problem of obtaining reproducible results from a series of potential measurements. Only the methods finally adopted as standard will be described here, except when the variations from these have furnished results of interest. The cell used is shown schematically in Fig. 1. The electrolyte is contained in the vessel A (an inverted bell jar), whose ground top is fitted to the transite-board lid B. The controlled atmosphere can be admitted

Jan 1, 1938

By F. C. Kelley, L. L. Wyman

In order to clarify and amplify the existing data concerning the action of the cementing material in cemented tungsten carbide alloys, the authors have initiated this investigation of the entire range of cobalt-tungsten carbide alloys. Inasmuch as the ultimate objective is relative to what actually goes on during the sintering of cemented tungsten carbide materials, this work was necessarily restricted to heat treatments similar to those used in actual production of these materials. In the course of numerous experiments, the authors have noted several conditions that indicated that there was a solubility to be considered. Among these factors are the following: 1. Many of the alloys showed a much larger amount of binding constituent to be present than could possibly be accounted for by the cobalt content. 2. In many areas, grains of the carbide constituent are much larger than the particles of carbide originally added. In addition, these grains are of very regular contour. 2a. In samples of cemented tungsten carbide which had been fused in the atomic hydrogen torch in the presence of excess binder constituent, immense grains are formed, and their shapes are very regular. This is also true when the cemented tungsten carbide of 13 per cent. Co content is fused alone in the atomic hydrogen torch. Contrary to general expectation, chemical analysis of this material, after fusion in the atomic hydrogen torch, checks the analysis of unfused material. 3. In making the cemented tungsten carbide materials by the process of exerting the pressure at the time of heating a certain portion of the &apos; contents squeezed out of the mold. Chemical analysis has shown that this material contains approximately 12 to 20 per cent. of tungsten. The microstructure shows a cored dendritic structure interlaced with eutectic network, and some graphite, as shown in Fig. 1. 4. Thermal analysis of these materials has consistently indicated an arrest point close to 1350" C.

Jan 1, 1931

By G. M. Willis, F. L. Hennessy

The oxygen pressure in equilibrium with silver and Ag2O-B2O3 melts has been measured between 800&apos; and 900°C, to obtain the thermodynamic properties of the liquid. The compound Ag20. 4B20:1 appears to exist in the liquid, which shows marked heat content and entropy effects. A KNOWLEDGE of the thermodynamic properties of binary liquid silicates, borates, and phosphates would be of considerable assistance in the interpretation of the behavior of multi-component metallurgical slags. However, the literature contains comparatively few studies of the thermodynamics of binary slags. The system Ag20-B,O, attracted our attention as it was known to give a single liquid phase,&apos;,&apos; in which high contents of silver could be obtained (up to 61 pct Ag according to Foex2). Further, it would be expected that the partial pressure of oxygen over melts in equilibrium with metallic silver could be used to determine the activity of Ag2O in the Ag,O-B,O, system. In many respects, it may be expected that the reaction of a basic oxide with boric oxide would be analogous to its reaction with silica. Liquid immiscibility frequently occurs in both borate and silicate systems. With B2O3 and SiO reaction with a basic oxide presumably involves a breakdown of the three-dimensional network of the acid oxide by reaction with oxygen atoms common to more than one silicon or boron atom. Ag2O-B2O3 was therefore investigated as a model of a slag system in the hope that its thermodynamic properties would assist in understanding those of other systems. Several methods for determining the activity of a component in a slag have been described in the literature. Chang and Derge" used high temperature electromotive force measurements to obtain the activity of SiO2 in CaO-SiO2 and Ca0-Al203-Si02 slags, but the cell reaction in their work is not clear. low has used rate of volatilization and vapor pressure measurements combined with phase diagrams to obtain activities in the systems KO-SiO,, Na,O-SiO, and Li,O-SiO," and PbO-SiO26 Taylor and Chipman7 extrapolated their results for the distribution of FeO between liquid iron and CaO (+Mg0)-FeO-SiOl slags to obtain the activity of FeO in the binary FeO-SiO2 system. In principle, one of the most direct methods for obtaining the activity of a metallic oxide in a phase is by comparison of the equilibrium oxygen pressure for the system metal-pure oxide with that of metal oxide-containing phase. Schenck and othersa have studied the stabilization of Ag2O on combination with other oxides (MO,) in the solid state by measurements of the oxygen pressure in systems of the type Ag-Ag,O-xM0,-MOy-0, (gas). Schuhmann and Ensio" have determined the activity of FeO in iron silicate slags in equilibrium with solid iron, using CO/CO2 mixtures to establish known partial pressure of oxygen. Although the method gives the activity of FeO without ambiguity, the slag is not a binary system, and interpretation of the results in terms of the hypothetical binary system FeO-SiO, is not possible. If a metal is solid at temperatures at which the properties of the slag containing its oxide are to be studied, this method has the considerable experimental advantage that the metal can be used as the container for the slag, and contamination by contact with refractories is avoided. In this work, crucibles for Ag2-B,O, melts were made from silver, and the liquid brought to equilibrium with definite pressures of oxygen gas. The oxygen pressure PO, thus fixes the activity of Ag20 in the liquid silver borate. For the reaction at a given temperature. is substantially constant, is directly proportional to the square root of the equilibrium oxygen pressure. Varying the oxygen pressure changed the silver oxide content of the liquid and it was possible to obtain the activity of Ag2O over a range of composition. Experimental Procedure In principle, the method consisted of bringing melts in silver crucibles or boats to equilibrium at a fixed temperature under a definite pressure of oxygen and analyzing the glass after solidification. Materials: B2O3 glass was prepared from A.R. quality boric acid by fusion in platinum. The silver

Jan 1, 1954

By S. G. Cupschalk, J. J. Wert, R. A. Buchanan

The uniaxial deformation of thermally ordered and disordered polycrystalline Cu3Pt was studied by means of the X-ray line - broadening analysis according to Warren and Averbach and the extension of this analysis to ordered fcc materials by Mikkola and Cohen. Because of the heat treatment history, extinction had a pronounced effect on the X-ray spectra of ordered and disordered C%Pt at small plastic strains. After an appropriate correction for extinction, the long-range order in thermally ordered ChPt was found to decrease at a slow constant rate with plastic strain. Furthermore, the antiphase domain probability increased at a constant rate to 17.5 pct strain. The effective particle size behavior indicated that the stacking fault energy is lower in ordered than in disordered Cu3Pt. Analysis of the stress-strain curves shouled that ordered Cuzt has a slightly lower yield Point but a much higher work-hardening rate than disordered Cu3Pt. THE presence of long-range order in a solid-solution alloy has a marked effect on its mechanical properties. While this effect has been known qualitatively for many years, it was not until recently that detailed investigations have been performed to determine the exact role long-range order plays in this strengthening mechanism. The development of an advanced, quantitative. X-ray diffraction analysis by Warren and Averbachl and the extension of this analysis to the L1, type super lattice by Mikkola and cohen2 have greatly accelerated research in this field. The research reported in this paper consisted of two primary phases. The first phase was to determine the effect of long-range order on the tensile properties of polycrystalline Cu3Pt. This objective was accomplished by comparing the stress-strain behavior of thermally ordered CusPt to that of thermally disordered CusPt. The second phase of the research was to determine the difference between the atomic arrangements in thermally ordered and thermally disordered Cu3Pt as a function of uniaxial deformation and thereby gain a deeper insight into the mechanism by which long-range order affects the tensile properties. This second objective was accomplished by applying the Warren-Averbach method of peak profile analysis to the X-ray diffraction patterns obtained from ordered and disordered Cu3Pt after given amounts of uniaxial deformation. EXPERIMENTAL PROCEDURE The Cu3Pt was prepared by vacuum melting and casting. After a homogenization anneal, the ingot was cold-rolled to sheet form. Two tensile specimens with gage sections of 2.50 by 0.500 by 0.115 in. were carefully machined from the sheet. The specimens were polished with a final step of 600-grit paper to insure smooth diffracting surfaces. Finally, one specimen was heat-treated to yield an average grain diameter of 0.016 mm and an initial degree of long-range order, S, of 0.825. The other specimen was water-quenched from above the critical temperature, 645"C, to yield an average grain diameter of 0.017 mm and zero long-range order. The heat treatment history of each specimen is shown in Table I. The tensile tests were performed utilizing a Research Incorporated Model 900.95 Materials Testing System. This unit employs a closed-loop feedback system which maintains a constant strain rate through an extensometer clipped to the gage section of the tensile specimen. A strain rate of 1.32 i0.02 x 10"4 sec-&apos; was employed in testing both specimens. In the X-ray diffraction analysis, a General Electric XRD-5 diffractometer equipped with a pulse-height analyzer set for 90 pct efficiency was employed. The goniometer speed selected was 0.2 deg, 20, per min. Filtered Cu radiation was used for all peaks and all peaks were chart-recorded. Because of nonuni-form grain size. it was necessary to spin the specimens during X-ray analysis in order to obtain reproducible integrated intensities. The spinning rate was 2000 i100 rpm. The application of the Warren-Averbach method of peak broadening analysis to a diffraction pattern is very time consuming if done manually. In this research, the calculations involved were performed with the aid of a computer program by wagner.3 As reported by Wagner, the program is written in Fortran TV computer language. It was modified to Fortran I1 so as to be handled by the IBM 7072 computer at Van-derbilt University. In the X-ray diffraction analysis of uniaxially deformed Cu3Pt, the 100, 200. 400. 111, and 222 reflections were recorded from the initially ordered sample after &apos;plastic strains of 3.0, 6.0, 9.0, 12.0,

Jan 1, 1970

By R. Floyd Farris

Al thorough knowledge of the behavior of cement slurries under elevated temperatures and pressures is necessary in order to solve properly the many problems presented in deep-well cementing operations. In the earlier days of the petroleum industry the depths of wells were shallow as compared to those of today, and the subsurface temperatures and pressures were not of sufficient magnitude to affect seriously the problem of proper control of cement-slurry properties. Today, however, the search for new reserves has extended drilling to such depths that bottom-hole temperatures of more than 200°F. and bottom-hole pressures of 3000 to 5000 lb. are not uncommon. Moreover, there is every indication that within the next few years wells will be drilled to even greater depths and bottom-hole temperatures and pressures will be correspondingly higher than those with which we are concerned today. It has been realized for some time that the behavior of cement slurries at high temperatures and pressures might be very different from that at atmospheric tempera-ture-pressure conditions, but while the temperature effects have been investigated with a reasonable degree of thoroughness, the pressure effects have received little public attention. While the trend toward deeper drilling may make changes in cementing technique and the choice of cements imperative, it was the purpose of this investigation to consider factors having a bearing on the latter, only secondary consideration being ,given, for the present, to details of tech-nique and equipment for oil-field use. More specfically, the purpose of this work was to consider the effect of temperature and pressure upon the behavior of cement slurries. Although it has long been recognized that cements thicken and set rapidly with increasing temperatures, practical methods for the quantitative determination of these effects are comparatively recent developments. In 1935 Silcox and Rule1 presented such a method, describing apparatus designed to measure the consistency-time relationship of cement slurries at relatively high temperatures. The practical importance of this apparatus in furnishing useful data for the evaluation of cement slurries for cementing operations has been emphasized in various technical publications by such writers as E. L. Davis,~ I. F. Bing-ham,3 and J. E. Weiler.4 A paper describing the numerous tests now used to evaluate cements for oil wells was presented in 1939 by W. W. Robinson.= Robinson describes the Consistometer and the Thickening-Time Tester, showing similarity of data from the two devices, and points out that the purpose of each apparatus is to determine the allowable time that a cement may be pumped at a given temperature. At the present time, however, it is believed that results from the Thickening-Time Tester and the Consistometer have not given a

Jan 1, 1941

By R. Floyd Farris

Al thorough knowledge of the behavior of cement slurries under elevated temperatures and pressures is necessary in order to solve properly the many problems presented in deep-well cementing operations. In the earlier days of the petroleum industry the depths of wells were shallow as compared to those of today, and the subsurface temperatures and pressures were not of sufficient magnitude to affect seriously the problem of proper control of cement-slurry properties. Today, however, the search for new reserves has extended drilling to such depths that bottom-hole temperatures of more than 200°F. and bottom-hole pressures of 3000 to 5000 lb. are not uncommon. Moreover, there is every indication that within the next few years wells will be drilled to even greater depths and bottom-hole temperatures and pressures will be correspondingly higher than those with which we are concerned today. It has been realized for some time that the behavior of cement slurries at high temperatures and pressures might be very different from that at atmospheric tempera-ture-pressure conditions, but while the temperature effects have been investigated with a reasonable degree of thoroughness, the pressure effects have received little public attention. While the trend toward deeper drilling may make changes in cementing technique and the choice of cements imperative, it was the purpose of this investigation to consider factors having a bearing on the latter, only secondary consideration being ,given, for the present, to details of tech-nique and equipment for oil-field use. More specfically, the purpose of this work was to consider the effect of temperature and pressure upon the behavior of cement slurries. Although it has long been recognized that cements thicken and set rapidly with increasing temperatures, practical methods for the quantitative determination of these effects are comparatively recent developments. In 1935 Silcox and Rule1 presented such a method, describing apparatus designed to measure the consistency-time relationship of cement slurries at relatively high temperatures. The practical importance of this apparatus in furnishing useful data for the evaluation of cement slurries for cementing operations has been emphasized in various technical publications by such writers as E. L. Davis,~ I. F. Bing-ham,3 and J. E. Weiler.4 A paper describing the numerous tests now used to evaluate cements for oil wells was presented in 1939 by W. W. Robinson.= Robinson describes the Consistometer and the Thickening-Time Tester, showing similarity of data from the two devices, and points out that the purpose of each apparatus is to determine the allowable time that a cement may be pumped at a given temperature. At the present time, however, it is believed that results from the Thickening-Time Tester and the Consistometer have not given a

Jan 1, 1941

By Sidney A. Swensrud

MUCH discussion has occurred as to the use or uses which might be made after the war of either or both .of the large diameter (24 inch and 20 inch) War Emergency pipe lines built by y the United States Government during the war, to move crude petroleum and refined products such as gasoline and light distillate fuels. Indeed, the disposition and future use of these lines constitutes, in the minds of many people, one of the most important problems of postwar readjustment in the Oil Industry. The two lines, running from points in Texas to the New York-New Jersey-Philadelphia area, were constructed only because of the inability during the war to continue normal ocean tanker movements from the Gulf Coast to the East Coast. Physically they could continue after the war to move crude or refined products, and it appears that lines of such large diameter as these, if operated at or near capacity, could move these liquids at costs per barrel which might be considered in the same general cost range as for tanker movements.1 If, therefore, we were to look forward at the end of the war to a shortage of tankers, it is probable that the continued use of these pipe lines for petroleum movements to the East Coast would be worth considering, as against building new tankers to take over the movement, provided there were no other economic or national defense reasons for restoring tanker fleets and no other better use for the pipe lines. Because of the extensive tanker construction program which has been and still is in progress, and because of our Navy&apos;s marked success in combating the submarine problem, it appears to be quite possible, however, that instead of a shortage of tankers at the end of the war, we may have a surplus instead. If this should turn out to be the case, then there would seem to be considerable doubt that these lines would continue to be used for moving petroleum or products to the East Coast at the expense of tying up tankers. It would hardly seem probable that the owner of any such tankers would ship via one of the large lines at the expense of tying up one of its own tankers, unless the pipe line tariff rate charged was lower than the out-of-pocket cost of operating a tanker as against the out-of-pocket cost of keeping it tied up. And considering that a substantial part of the cost of operating a tanker goes on even when it is tied up, it is very difficult to figure out how any pipeline tariff could be established that would be low enough to compete with individually owned tankers that otherwise would be idle. Certainly a pipe line tariff rate high enough to cover direct costs plus even a low rate of depreciation and return on the investment would be far above the out-of-pocket tanker operating costs. In view of these considerations, it has seemed desirable to examine with some care some of the various alternatives that have been suggested as to other possible uses to which these lines might be put. One of these is for transportation of natural gas to the New York-New Jersey Philadelphia area. This Eastern area, located at the destination of these lines, contains the heaviest concentration of population in the United States, and is not now served with natural gas. At the other end of the lines lie the greatest discovered natural gas reserves in the United States, if not in the world, and many

Jan 1, 1944

By Toshimi Yamane

The internal friction of cold-worked titanium iso-thermally annealed at temperature below the recrystallization temperature was measured. The internal friction was calculated from the half width of a resonance curve of the specimen which was vibrated transversally by the electromagnetic method. The experimental results were as follows: 1) The specimens annealed for a long time at temperature below the re crystallization temperature after cold working have the strain-amplitude dependent internal friction. 2) The internal friction increased by the cold working was decreased during the isothermal annealing. The reason of decrease of the internal friction is considered to be caused by the annihi-lation of lattice defects. 3) There is a linear relation between logQt-1/Q0-1 and (1/T)2/3 below the recrys-tallization temperature, where Q0-1 is the internal friction standing 24 hr at the room temperature after cold rolling, Qt-1 is the internal friction annealed at T°K for t min. 4) The hardness of the cold-worked titanium does not change by the annealing at 300°C for a long time but decreases by annealing at 400ºand 460°C. METALS, when cold worked, show sharp changes in physical and mechanical properties&apos; The internal friction of cold-worked metals increases sharply and has a maximum value1,2 connected with working de- grees. The increased internal friction of cold-worked metals is recovered by annealing. This phenomenon is the well known effect called Köster effect. The recovery of the internal friction occurs earlier than the changes in tensile properties, hardness, or X-ray diffraction, and is very sensitive to the structure of a metal. The mechanism of the recovery at a temperature lower than the recrystallization temperature is being considered variously by many investigators: there are such views as the annihilation of dislocations by smith,&apos; the rearrangement of dislocations mentioned by Nowick,4 and interaction of dislocation with point defects.5 Smith and Nowick also considered the interaction but it is so difficult for them to explain the rearrangement mechanism systematically, it being not considered a special model; therefore, we do not explain it quantitatively. Experiments measuring the recovery of the internal friction of cold-worked metals were performed by Gordon and Nowick6 on NaCl, and by Smith on copper. In addition, there are many studies, particularly those of measurements on copper by other investigators. There are comparatively many investigations on aluminum and iron which are the cubic system,&apos;-&apos; but only a few on metals of the hexagonal system.10 In view of this, I investigated cph titanium at room temperature and measured the internal friction after annealing isothermally at temperature lower than the recrystallization temperature. SAMPLES AND EXPERIMENTAL METHOD samples for the experiment were cut from a 6-mm titanium plate. The long direction of samples was

Jan 1, 1963

By D. J. Mack, R. E. Reiswig

Six examples of the peritectoid transformation were selected from the literature and studied by the method of isothermal transformation. The kinetics and mechanisms of five of the examples are presented as TTT diagrams and photomicrographs. The exist-enc- of a peritectoid in the sixth case is doubtful. ALTHOUGH the peritectoid transformation per se has been known for many years, no precise published data exist concerning the kinetics or mechanisms involved in transformations of this type, except for the brief treatment by Rhines, et al. 1,10 Bearing in mind the fact that investigations of recent years are uncovering more and more peritectoids and suspected peritectoids, a thorough study of the well-established peritectoids appeared to be in order. It was for this reason that a study of the kinetics and morphological mechanisms of six binary peritectoids was undertaken. The six peritectoids selected from the literature for study were those reported at 7.02 wt pct Al-Ag, 26.0 wt pct Sb-Cu, 30.5 wt pct Sb-Cu, 32.3 wt pct Sn-Cu, 8.35 wt pct Si-Cu, and 21.2 wt pct Al-Cu. These selections were based on availability and purity of components, ease of preparation and heat-treatment, and estimated reliability of the available equilibrium diagrams in the regions of interest. EXPERIMENTAL PROCEDURE The alloys used in this investigation were induction melted in electrode-grade graphite and chill-cast in cast-iron split molds. In all cases, the alloys were so brittle that they could easily be broken into samples weighing 1 or 2 g. Chemical analyses showed that the alloys used were close to the respective peritectoid compositions reported in the literature and that the impurity levels were low in all cases. Metallographic examination showed uniform distributions of phases in all samples, indicating uniformity of composition in the samples studied. Isothermal transformation studies were carried out in fused-salt media, using the familiar inter-rupted-quench method. Uniformity of temperature in the salt baths was maintained by continuous stirring with a stainless-steel agitator. On the basis of actual observations of the temperature fluctuations, the estimated temperature control was + 10C for the Ag-Al and Cu-Sb alloys and ±30C for the Cu-Sn, Cu-Si, and Cu-Al alloys. The accuracy of all temperature measurements was estimated to be ±1°C. It was found necessary to mount metallographic specimens of the Ag-Al alloy in cold-curing methyl methacrylate, since the temperatures encountered in mounting in bakelite or lucite caused an appreciable degree of transformation to the ß phase. For the other alloys, wood-flour-filled bakelite mounts were used to avoid extraneous X-ray diffraction lines during the later examination of the metallographic specimens on a Norelco Geiger-counter d if f r ac tomete r. In the X-ray diffraction procedure, agreement between the published diffraction patterns and those obtained in this study was good. This was particularly important for phase identification, since the literature contained little in the way of micrograph description in some cases. Etching of the silver-aluminum alloy for metallographic examination was done by swabbing with either of the following reagents: 1) 10 g CrO3, 1 g (NH4), SO2, 0.5 g NH4NO3, 100 ml H2O, or 2) 10 ml NH4OH, 1 ml 20 pct KOH, 4 ml 3 pct H2O2, 5 ml H2O. The other alloys were etched with the usual bichromate etchant: 2 g K2Cr2O7, 1.5 g NaC1, 8 ml conc. H2SO4, 100 ml H20 (swabbed vigorously). EXPERIMENTAL RESULTS A) The Ag-Al peritectoid at 7.02 wt pct Al— The phase equilibrium involved in this peritectoid is shown in Fig. I.2 The phase boundaries in the vicinity of the peritectoid were most comprehensively established by Hume-Rothery, et al,3 who placed the equilibrium temperature at 448 °C and the equilibrium compositions of the a ß&apos; and y phases at 6.11, 7.02, and 7.24 wt pct Al, respective The alloy used in this study analyzed4 6.95 wt pct A making it slightly hypoperitectoid according to the accepted equilibrium diagram. The rate of the transformation a+ y — ß&apos; varies rapidly with degree of undercooling below the equilibrium temperature, passing through a maximum in the vicinity of 350°C. Thus the TTT dia-

Jan 1, 1960

By John Chipman, Minu N. Dastur

This paper presents equilibrium data on the reaction of water vapor with vanadium dissolved in liquid iron at 1600°C. The thermo-dynamic behavior of vanadium and oxygen when present together in the melt is discussed. A deoxidation diagram is presented which shows the concentrations and activities of vanadium and oxygen in equilibrium with V209 or FeV2O4. STUDIES of the chemical behavior of oxygen dissolved in pure liquid iron1-3 have served to determine with a fair degree of accuracy the thermody-namic properties of this binary solution. The practical problems of steelmaking, however, involve not the simple binary but ternary and more complex solutions. Only a beginning has been made toward understanding the behavior of such systems. The silicon-manganese-oxygen relationship was studied long ago by Korber and Oelsen4 and more recently by Hilty and Crafts." The carbon-oxygen reaction was investigated by Vacher and Hamilton6 and by Marshall and Chipman.7 A number of deoxidizing reactions have been studied empirica1lys&apos;10 with the object of determining the appropriate "deoxidation constants." The work of Chen and Chipman" afforded a clear-cut view of the effect of the alloy element, chromium, on the thermodynamic activity of oxygen in liquid ternary solutions. These investigators determined the oxygen content of experimental melts which had been brought into equilibrium with a controlled atmosphere of hydrogen and water vapor and were able to show that the presence of chromium decreases the activity coefficient of oxygen. They determined also the conditions under which the two deoxidation products, Cr2O3 and FeCr2O4, were formed and showed that the activity of residual oxygen is considerably less than its percentage. It was the object of this investigation to apply a similar method to the study of molten alloys of iron, vanadium, and oxygen. Vanadium was once considered a moderately potent deoxidizer, but this is now known to be erroneous, in the light of its behavior in steelmaking practice. Its reaction with oxygen retains a certain amount of practical interest in that a high percentage of one element places a limit on the amount of the other that can be retained. As a deoxidizer it will be shown that vanadium lies between chromium and silicon. Experimental Method The apparatus was that used by the authors3 in their study of the equilibrium in the reaction: H2(g) +O = H2O(g);K,= [1] PII., ao Crucibles of Norton alundum or of pure alumina were used. The latter were made in this laboratory and were of high strength and low porosity. Under conditions of use they imparted no significant amount of aluminum (less than 0.01 pct) to the bath. Temperature measurements were made with the optical equipment and calibration chart of Dastur and Gokcen.= The charge was made up of calculated amounts of ferrovanadium (20 pct V) and clean electrolytic iron totaling approximately 70 g. The first few heats were made in alumina crucibles with an insufficient amount of vanadium so that no oxide of vanadium would be precipitated under the particular gas composition. All the heats were made at 1600 °C under a high preheat and with four parts of argon to one part of hydrogen in the gas mixture to prevent thermal diffusion. The rate of gas flow was maintained constant at 250 to 300 ml per min of hydrogen. The time for each heat was three quarters of an hour after the melt had melted and attained the required temperature (1600°C). The water-vapor content of the entrant gas mixture was gradually raised in succeeding heats, keeping the vanadium content of the melt constant. This was controlled by manipulation of saturator temperature. A point was reached when for a given H2O:H2 ratio some of the dissolved vanadium was oxidized and appeared as a thin, bright oxide film on top of the melt. By raising the temperature of the melt it was possible to dissolve the oxide film which reappeared as soon as it was cooled down to 1600°C. The temperature readings taken on the oxide film were consistently higher by 80" to 85 °C as observed by the optical pyrometer. The heat was allowed to come to equilibrium under a partial covering of this oxide film. At the end of the run the power and preheater were shut off and the crucible containing the melt was lowered down into the cooler region in the furnace. This method of quenching proved quite

Jan 1, 1952

By I. F. Jackson, H. L. Hartman

Hard-metal inserts have received considerable attention in the mining industry recently for a variety of excavating and penetrating purposes. Their use in percussive drilling and in coal cutting machines is well known, but attempts to utilize them in cutting materials such as dimension stone have been discouraging because of excessive tool wear and failure. Particular attention is given to those properties of hard-metal inserts that affect their resistance to wear. A consideration of the actual wear mechanism shows the importance of correct mounting of the inserts and of the selection of suitably powered driving motor so as to achieve minimum tool wear and maximum tool life. Comparisons are made between the performances of types of hard-metal inserts, relating their inherent properties with results obtained in laboratory tests. As part of a broad program to improve the quarrying and processing of industrial minerals, The Pennsylvania State University has been investigating the machinability of slate under laboratory and field conditions. It should be emphasized that the results of the research presented in this paper are also applicable to other natural structural materials, and particularly to the more workable ones such as limestone and sandstone. Improvements which accrue in cutting and sawing should prove of benefit to all the dimension stone industry. Further, it may be pointed out that the results reported here are applicable to rotary drilling (with drag bits) as well as to cutting and sawing of rock. INVESTIGATIONS IN RELATED FIELDS The investigation was initiated with an extensive survey of available literature related to metal cutting and to rotary drilling. The following similar features between metal cutting and slate cutting became evident: 1) Hard-metal inserts are widely used as a cutting tool in both cases. 2) The forces acting on the tool may be resolved into normal and tangential components. 3) Rate of penetration and tool wear are important criteria in each case. On the other hand, important differences also exist: 1) Most metals, exhibit plastic behavior, while slate (and most rock) is a brittle material under normal conditions. 2) In metal cutting the component of force acting parallel to the surface of the workpiece is considerably greater than the force holding the tool against the workpiece. 111 slate cutting, this situation is reversed. Similarities between drag-bit rotary drilling and slate cutting are as follows: 1) In both casts, a tool, usually of the hard-metal insert type, is used to penetrate a brittle material. 2) The drilling forces and related variables, such as rotation speed, are similar. 3) Chip formation in each case is essentially the same. 4) The shape of the tool is similar in rotary drilling and slate cutting. Important differences are also apparent: 1) The objective of drilling is to produce a directed hole, while in cutting it is to form a kerf. In core drilling, however, a kerf is also produced. 2) The horizonta1 component of force in rotary drilling decreases from the center to the outside of the tool, whereas in slate cutting the component is almost uniformly distributed across the width of the tool. 3) The power absorbed in the drill rod is greater in rotary drilling. 4) The clogging action of chips, if excessive power is applied to the tool and if flushing is insufficient, is more serious in rotary drilling. Because of the striking similarities between metal cutting and slate cutting, and between rotary drilling and slate cutting, it was considered that the findings of investigators in those fields would serve as a guide for experimental studies of slate cutting. The following is thus devoted to a discussion of those aspects of metal cutting and rotary drilling pertinent to the present investigations.

Jan 1, 1962

By Leon McCulloch

WIIen clean iron and metallic zinc dust, protected from the air, arc heated below the melting point of zinc, the iron takes on a coating that has excellent protective value. This coating is a brittle alloy of zinc and iron, and the process is called sherardizing. Although the zinc particlcs are covered with oxide and cannot touch the iron, an extremcly small amount of the zinc vaporizes and the vapor, reaching the iron, alloys with it. Other zinc then vaporizes to replace that which has been removed from the atmosphere. This process continues indefinitely at a decreasing rate, for the coating already formed permits zinc to diffuse through it to combine with the iron beneath. In this way, the coating grows outward from the surface of the iron, as the bark grows from a tree. The method of growth was clcarly seen while sherardizing small cubes of cast iron, at about 450" C., in a srnall glass-stoppcrcd bottle enclosed in a rotating drum. The dust contained about 3 per cent. iron, which prevented caking, and coatings % in. thick were grown in a few hours. After a heavy layer had been formed, the cubes mere again treated for a shorter time. The layer last formed was seen to lie next to the iron, instead of at the outer surface, showing that the growth was from the surface of the iron outward. The coatings split at the edges and corners, leaving the iron exposed there. Flakes of graphite from the iron were lifted upward and embedded in the coatings. The composition of sherardized coatings varies from the outer surface inward, as would be expected from the mode of growth. That is, the iron content increases slowly at first, then more rapidly as the iron is approached. At the surface the least amount of iron possible is 6 per cent., as the experiments described below have shown. A study was made of the effect of iron in zinc dust on the proccss and on the resulting coatings. Glass bulbs, holding the small pieces to be sherardized, together with enough zinc dust to make them two-thirds full, were heated in a small, rotating electrically heated and controlled furnacc. The bulbs had 6-in. (15 cm.) necks, of 96-in. (9.Fj mm.) tubing, plugged

Jan 1, 1923

By Leon McCulloch

WIIen clean iron and metallic zinc dust, protected from the air, arc heated below the melting point of zinc, the iron takes on a coating that has excellent protective value. This coating is a brittle alloy of zinc and iron, and the process is called sherardizing. Although the zinc particlcs are covered with oxide and cannot touch the iron, an extremcly small amount of the zinc vaporizes and the vapor, reaching the iron, alloys with it. Other zinc then vaporizes to replace that which has been removed from the atmosphere. This process continues indefinitely at a decreasing rate, for the coating already formed permits zinc to diffuse through it to combine with the iron beneath. In this way, the coating grows outward from the surface of the iron, as the bark grows from a tree. The method of growth was clcarly seen while sherardizing small cubes of cast iron, at about 450" C., in a srnall glass-stoppcrcd bottle enclosed in a rotating drum. The dust contained about 3 per cent. iron, which prevented caking, and coatings % in. thick were grown in a few hours. After a heavy layer had been formed, the cubes mere again treated for a shorter time. The layer last formed was seen to lie next to the iron, instead of at the outer surface, showing that the growth was from the surface of the iron outward. The coatings split at the edges and corners, leaving the iron exposed there. Flakes of graphite from the iron were lifted upward and embedded in the coatings. The composition of sherardized coatings varies from the outer surface inward, as would be expected from the mode of growth. That is, the iron content increases slowly at first, then more rapidly as the iron is approached. At the surface the least amount of iron possible is 6 per cent., as the experiments described below have shown. A study was made of the effect of iron in zinc dust on the proccss and on the resulting coatings. Glass bulbs, holding the small pieces to be sherardized, together with enough zinc dust to make them two-thirds full, were heated in a small, rotating electrically heated and controlled furnacc. The bulbs had 6-in. (15 cm.) necks, of 96-in. (9.Fj mm.) tubing, plugged

Jan 1, 1923

By L. H. Reiss, J. Groult, L. Montadert

Many fields, where the reservoir is composed of sandy layers, show great complexity because of the lack of continuity which results from a particular type of seditnentation. This complexity may be a factor of prime importance in studying reservoir drainage, especially in the displacement of oil by water or gas. This paper describes work done to study this heterogeneity and its influence in the exploitation of the fields of the lower Devonian sandy shale in the Fort Polignac Basin in Algeria. Two lines of research were followed. 1. On the border of the hasin, a detailed sedimentological study established rules for the distribution of the sandy zones, which furnished hypotheses necessary for devising a geologic model of the reservoir. A certain number of sandy zones were recognized and characterized by their sedimentation. 2. In the interior of the basin, production logs deterrnined the productivity profile. Study of these point data led to a description of the distribution of oil and gas phases in the reservoir so that the continuity of different zones between the wells could be deduced. These techniques were applied to the study of the lower Devonian sandy shale reservoir of Zarzaitine. The sedimentological study guiding the correlation work, with the aid of the conventional static data (logs and cores), led to the establishment of a useful geologic model of the reservoir. Production logs, thanks to the contribution of dynamic elements, permitted corrobora-tion of the model. In particular, the logs confirmed separation, as proposed by the sedimenfological study, of two comparable sandy groups by revealing the continuity of a thin impermeable layer, invisible on conventional logs. INTRODUCTION The heterogeneity of sandstone reservoirs considerably influences the distribution of fluids, as well as their displacement in the reservoir. Rational development of a field and maximum recovery of hydrocarbons are closely tied to an exact and precise knowledge of the intern architecture. We will try to show how it is possible I refine the knowledge of the reservoir by seeking qui different and varied sources of information. Productic geology, the group of techniques which leads to idei concerning reservoir architecture and its geometric descris tion, furnishes the framework of this undertaking. Of these techniques. those used so far are qui varied. Descriptive as well as quantitative, the technique partake as much of classical geology as of reservo science. They include (1) geologic studies of the enti basin, especially a stratigraphic and sedimentologic study of the reservoir member at its outcrop, detail1 observations of cores taken from wells and, finall oriented cores; (2) interpretation of geophysical dat (3) interpretation of electric logs, nuclear and sonic lo and dipmeters: (4) petrophysical study of the reserve on samples taken from wells; (5) reservoir dynamics (stu of the production history and, in particular, interpretati of production logs); and (6) analysis of the fluids a thermodynamic studies. This incomplete list could also include (1) study the migration of the fluids, (2) geochemistry (chemi characterization of the oils), (3) regional hydrodynamii and (4) injection and detection of tracers. If most of these techniques are classic, attention i nevertheless be called to applying two of the techniql in conjunction: the study of the reservoir member its outcrop and the study of dynamic distribution fluid phases in the reservoir through use of product logs, used in the study of the sandy shale reservoirs the lower Devonian of the Fort Polignac Basin, Alge in particular, their application to the study of the 2 zaitine field where they have led to a new and satisfact model of the reservoir will be described. THE ZARZAITlNE FIELD Situated in the interior of the Fort Polignac 8 about 150 kilometers (km) north of the lower Devol outcrop, the Zarzaitine Devonian oil field was discovc On Ian. 28, 19&apos;&apos; (Figs. 1 and l8). It is in the fern a monocline truncated by two perpendicular fault: great throw, with a downthrown section to the north\: Erosion at the top of the structure has caused one of it to disappear. It is a reservoir with a gas cap an m coefficient on the order of 1:5, open to the aql On the northeast, with the oil zone covering an Of 106 sq km and with initial oil reserves of 222 mi

Jan 1, 1967

By P. E. Rider, K. A. Gschneidner, O. D. McMasters

The solid solubilities for thirteen rare-earth metals in gold were determined by using the X-ray parametric method. Solubilities ranged from 0.1 at. pct for lanthanum in gold up to 8.8 at. pct for scandium in gold. The solubilities from lanthanum to gadolinium were very small and essentially constant, but a sharp increase occurred from gadolinium to scandium. The large solubilities for the heavy rare-earth metals were not expected because of the large size and electrochemical differences between rare-earth atoms and the gold atom. Contributions from first- and second-order elasticity theory plus an electronic contribution were found to reasonably account for a more favorable size factor. Electron transfer from the rare-earth metal to the gold Is thought to occur such that the resultant rare-earth and gold electronegativities are favorable for solid-solution formation. It was also found that this mutual adjustment of size and electronegutivity does not occur if the pure-metal size factors are greater than a critical value of 25 pet. The eutectic temperatures for ten systems were determined and these remained fairly constant at approximately 809 "C for the lighter lanthanide metal-gold systems until the Er-Au system was reached, at which Point the eutectic temperature successively increased reaching a maximum of 1040°C in the Sc-Au system. This rise was correlated to the size factor becoming more favorable for solid-solution formation at erbium. The valence state of ytterbium was found to change from two in the pure metal to three when ytterbium is dissolved in the gold matrix. RECENT results1 reported concerning the solubility of holmium in copper, silver, and gold, showed that the solubility of holmium in gold was quite large, 4.0 at. pct, compared with 1.6 in silver and 0.02 in copper. The small solubilities of holmium in silver and copper are quite reasonable in view of the large size difference (22.2 and 38.2 pct, respectively), large electronegativity difference (0.59 for both systems), and possible unfavorable valency factor (assuming one for silver and copper and three for holmium). The large solubility in gold, however, is unexpected because these same factors are also unfavorable for holmium and gold (22.5 pct size difference and 0.69 electronegativity difference), and because the light rare-earth metals, lanthanum, cerium, and praseodymium, have negligible solid solubilities in gold.2 In view of this unexpected behavior, it was felt that a study of the solid solubilities of most of the rare-earth metals in gold would be desirable to better understand the factors involved in the formation of solid solutions. Of the rare-earth metals added to gold in this study, only ytterbium is divalent in the pure metallic state (the other rare-earth metals are all trivalent) and many of its physical properties (such as the metallic radius, electronegativity, and so forth) are much different from those of the normal trivalent rare-earth metals.&apos; The properties of ytterbium are such that one would expect solid-solution formation to be less favorable for ytterbium in gold than for any of the normal trivalent rare-earth metals. But chemically ytterbium is known to possess a stable trivalent state, and it is quite possible that ytterbium may alloy as a trivalent metal under certain conditions rather than as a divalent metal. Because of the dual valency nature and because so little is known about the alloying behavior of ytterbium, the gold-rich ytterbium-gold alloys are of special interest. EXPERIMENTAL PROCEDURE Materials. The gold used in this investigation had a purity of 99.99 pct with respect to nongaseous impurities. In general the rare-earth metals were prepared by reduction of the corresponding fluoride by calcium metal.3 The impurity contents of the metals used in this study are given in Table I. Preparation of Alloys. Two- or 3-g alloy samples were prepared by arc melting. The samples, with the exception of some of the Er-Au alloys, had weight losses of 0.5 pct or less. All alloy concentrations noted in this paper are nominal compositions. After arc melting, the alloys were wrapped in tantalum foil, sealed off in quartz tubing under a partial atmosphere of argon, homogenized for approximately 200 hr at 780°C, and then quenched in cold water. X-Ray Methods. The X-ray parametric method was used in determining the solubility of the rare-earth metals in gold. filings were sealed in small tantalum tubes by welding under a helium atmosphere. The tantalum tubes were then sealed in quartz tubing under a partial argon atmosphere, and annealed for times ranging from 1/2 to 3 hr (the length of time was inversely proportional to the an-

Jan 1, 1965