By H. E. Cline, E. F. Koch, J. L. Walter

It has been postulated and, in a few instances shown, that some kind of dislocation structure will be present at semicoherent interfaces to accommodate small lattice mismatches. In the present study of the NiAl-Cr eutectic, regular arrays of interface dislocations are observed at the boundary between the chromium-rich rods and the NiAl-rich matrix. The networks were examined by transmission electron microscopy and selected area diffraction. The rods and the matrix have a crystallographic relationship in which all directions and planes of the two phases are parallel. The dislocation networks are cmposed of a<100> dislocations lying on the intersections of the cylinders with (100) planes. Dislocations forming hexagonal rather than square arrays are also observed at certain areas of the network. The morphology of the network is consistent with the interpretation of mismatch being accommodated by interface dislocations in the cylindrical geometry. The measured spacing between dislocations was used to calculate an apparent lattice mismatch between the phases (˜0.35 PCt)interface network energy (-140 ergs per sq cm), and network strengthening (-10,000 psi). It has been proposed by Frank and Van der Merwe1 that dislocations should be present at the boundary between two semicoherent crystallographically related phases. The role of the interface dislocations would be to reduce the internal stresses, caused by the mismatch in atomic spacing across the interface. Such dislocations have been observed at the interface between expitaxially grown films and Substrates.2-4 Interfacial dislocations have also been observed at precipitate-matrix interfaces.&apos;-&apos; Directionally solidified eutectics have been shown to have semicoherent phases1&apos; and would, therefore, be expected to have interfacial dislocations as found by Weatherly at a lamellar fault in A1-A12Cu.11 The NiAl-Cr eutectic appeared to be a promising system to examine because both phases are cubic, the lattice mismatch is small, and the phases are crys-tallographically related. Furthermore, the eutectic is easily thinned for transmission microscopy. Indeed, interfacial dislocations were observed and this report describes the nature of the dislocation networks in the boundary between the NiAl-rich ma-trix-phase and the fine chromium-rich rods.21 I) EXPERIMENTAL PROCEDURE Ingots, 3/4 in. in diam and 6 in. long were made by melting in vacuum and casting under argon using 99.9 pct pure material. The composition, in at. pct, was 33 pct Ni, 33 pct Al, and 34 pct Cr. The ingots were then placed in A1203 crucibles on a water-cooled base, melted by means of induction, and withdrawn from the hot zone at the rate of 1 in per hr under argon.* * T his material was first directionally solidified in this laboratory by E. R. Stover Slices were taken perpendicular to the growth direction of the directionally solidified ingot for metallography and for transmission electron microscopy. The electron transmission samples were thinned mechanically, then thinned electrolytically in A-2 electrolyte* *A-2 electrolyte: 62 ml perchloric acid, 700 ml ethanol, 100 ml butylcellosolve, 137 ml distilled H20. until a hole appeared in the foil. 11) EXPERIMENTAL RESULTS A) Optical Microscopy. The microstructure, viewed on a plane perpendicular to the growth direction, is shown in Fig. 1. The structure consists of cells or colonies of parallel chromium-rich rods in the NiAl matrix. The cells occur when there are impurities present12 or, in a ternary eutectic, if the composition is slightly off the eutectic composition. The axis of the chromium-rich rods is parallel to the growth direction except near the cell boundaries. Here the rods may assume angles to the growth direction; however, examination shows that the crystallographic relationship between the rod and the matrix remains the same. Fig. 1 includes cell boundaries where the rods formed at a large angle to the growth direction. The variation of rod position across the cells made it possible to Fig. 1-Structure on plane perpendicular to growth direction. Rods near cell walls are at large angle to growth direction. Magnification 315 times.

Jan 1, 1970

By A. K. Schellinger, R. D. Lalkaka

IF the ball mill is considered only from an energy standpoint, it can be thought of as a converter of kinetic energy into heat energy and surface energy. The law of the conservation of energy must apply to the ball mill as it does to any machine or process in nature. The heat energy output of the ball mill is apparent to any casual observer of the operating mill since the outflow pulp will be appreciably warmer than the inflow water and rock. The rock in the ball mill is crushed by shearing of its ionic bonding caused by some impact-induced stresses beyond the elastic limit. As the bonds holding the mineral crystal lattices together are ruptured, new surface area is created on each unit of which a definite number of unsaturated bonds exist. Such unsaturated energy of bonding may be termed the "surface energy," and is a potential energy figure. This created energy was withdrawn from the ball mill system and represents an absorption, or disappearance of heat. To reduce the size of the rock, surface area must be created and with it the at- tendant characteristic surface energies of the minerals concerned. Thus the creation of surface energy, from an energy viewpoint, is the creation of useful work by the ball mill. Because of the controversial nature of the energy efficiency figures for modern operating ball mills, it seemed worthwhile to approximate the ordinary magnitude of such efficiencies from the above viewpoint. This was done by an energy balance of the three aforementioned forms of energy, kinetic, heat, and surface energy, for two 9Y2x10-ft grate-type ball mills grinding cement raw materials. Kinetic energy input to the balls was approximated as closely as possible while the heat energy output was measured by means of a thermometer and water and rock flow rates. The assumption was made

Jan 1, 1952

By R. A. Walker, R. G. Bradburn, B. C. Flintoff

The events which led to computer control of the grinding circuit at Brenda Mines are described, beginning with mill operating philosophy. High production rates are encouraged so that, despite severe upstream disturbances, a manual control method to meet this philosophy had developed. Unfortunately, due to the time interval between manual control adjustments, losses in production resulted. An analog control method was devised and, although superior to manual control in some situations, was found to suffer from several practical limitations. The data logging capabilities of a control computer seemed warranted. Circuit testwork combined with an analysis of operating data showed that (1) metallurgical personnel at times could increase production rates by as much as 10% over that achieved by grinding operators; (2) the chosen data base required an increase of 2% or more to be statistically significant; and (3) for a 2% increase there would be a significant rate of return of investment in computer installation. Consequently one grinding circuit was fully instrumented, and a rented computer was installed by Brenda personnel. Prior to installation, Brenda metallurgical and instrumentation personnel were trained in the use of the computer. An experimental program was devised with short and long-term objectives. The short-term objective was to develop a practical control strategy which would yield immediate production improvement. This goal has been successfully met as described in this paper. Statistically significant increases in excess of 2% have been established. Work is being completed for the permanent installation of computer control on all four grinding circuits at the present time. Long-term objectives are (1) off-line analysis of the circuit using mathematical models of process units; (2) on-line experiments to study alternative control tactics; and (3) possible expansion of computer facilities to the crushing plant.

Jan 1, 1978

By Bernard E. Fernow

About eight years ago a comprehensive study of American timbers was begun in the U. S. Division of Forestry with a twofold object. On the one hand, it was desired to deternliiie the working-qualities of our numerous economically important timbers, and to furnish reliable standards of strength. 011 the other hand, it was intended to get a clearer insight into the properties and behavior of wood in general, with a view of establishing more rational methods in its use, and to furnish data for physical inspectioil which would permit an intelligent application of the standards of strength, and place upon a rational foundation the so-called " factor of safety," which is at present a mere baseless guess. The first object, namely, the establishment of standards for any given species, requires a very large series of tests, since Wood is an exceedingly variable substance, so much so that in the same tree a variation of 50 per cent. in strength may be found; hence the greater need of rational data of inspection. So far, the insufficient appropriations and facilities at our disposal have permitted us to establish really reliable standards for five species of southern conifers only. These have been deduced from nearly 20,000 tests. Besides these, 10,000 other tests have furnished indicatious regarding some two dozen other species. This work is now entirely abandoned, waiting for more prosperous times. The study of wood in general, however, can be carried on with smaller means, and has this year yielded not only very interesting, but highly important results, which will soon be published in detail. It is the purpose of this paper to make to the Institute the

Jan 1, 1899

By C. E. Birchenall, H. M. Schadel

Vapor pressure of silver over silver-gold alloys has been measured over a range of temperatures for four compositions. Orifice effusion has been compared with electromotive force measurement as a means for determining thermodynamic activities in these solid metallic alloys. Correlated activity coefficients are given for silver-gold alloys for the temperature range 200&apos; to 1000°C. SOUND development of a technique for the measurement of some property of matter requires a comparison with other recognized procedures which have been used to measure the same property. Such a check is especially useful if the assumptions on which the applications stand are basically different for the two methods. Agreement in the results tends to confirm both sets of assumptions. The electromotive force method for determining thermodynamic activities depends upon the reversibility of the electrode processes and a knowledge of the valence states involved. The orifice effusion technique of determining vapor pressures requires that certain mean free path conditions be met, that the state of association of the vapor be known, and that efficient collection of vapors be maintained. Thus the requirements are quite different in nature. Although procedures often exist by which the fulfillment of these conditions may be tested internally, agreement of thermodynamic activities for a single system obtained by both methods constitutes a more severe test of the assumptions. The binary alloy system silver-gold is excellent for this purpose for several series of emf measure-

Jan 1, 1954

By John Cobb

THE attempts of British investigators to arrive at definite knowledge concerning the nature of the nitrogenous constituents of coal have been mainly made through studies of the behavior of coal on carbonization and gasification. There have been carried out numerous determinations of ,the distribution of nitrogen in the products of carbonization under laboratory and large-scale conditions; and by a careful consideration of the extent to which nitrogen is liberated, say as ammonia, at different temperatures and under different conditions of operation as regards atmosphere, it has been possible to form some general notions as to the nature of the nitrogenous compounds present in the coal, and at the same time to arrive at clearer ideas as to what are the important operative factors in determining the ammonia yield under working conditions. This work has been spread over many years and is summarized below. The difficulties of connecting the results in such a way as to allow of the nitrogenous constituents of the coal being described in terms of specific organic structure are great. They arise, for example, in the carbonization process, because the phenomena of decomposition observed at any one temperature can only refer to compounds decomposing at that temperature, each of them with a previous history of chemical transformations occurring at lower temperatures. To put it in another way, the compounds occurring in the coke at any stage are not in the least likely to be those present in the original coal. The same difficulty, in a milder form, occurs when the method of differential solution is attempted. There is always the preliminary question, almost impossible to answer, as to how far the separation by the use of the solvent has involved some form of decomposition of the original compounds. In the following summary, an attempt has been made to bring together results obtained by British workers.

Jan 3, 1925

By John W. Cobb

The attempts of British investigators to arrive at definite knowledge concerning the nature of the nitrogenous constituents of coal have been mainly made through studies of the behavior of coal on carbonization and gasification. There have been carried out numerous determinitions of the distribution of nitrogen in the products of carbonization under laboratory and large-scale conditions; and by a careful consideration of the extent to which nitrogen is liberated, say as ammonia,. at different temperatures and under different conditions of operation as regards atmosphere, it has been possible to form some general notions as to the nature of the nitrogenous compounds present in the coal; and at the same time to arrive at clearer ideas as to what are the important operative factors in determining the ammonia yield under working conditions. This work has been spread over many years and is summarized below. The difficulties of connecting the results in such a way as to allow of the nitrogenous constituents of the coal being described in terms of specific organic structure are great. They arise, for example, in the carbonization process, because the phenomena of decomposition observed at any one temperature can only refer to compounds decomposing at that temperature, each of them with a previous history of chemical transformations occurring at lower temperatures. To put it in &other way, the compounds occurring in the coke at any stage are not in the least likely to be those present in the original coal. The same difficulty, in a milder form, occurs when the method of differential solution is attempted. There is always the preliminary question, almost impossible to answer, as to how far the separation by the use of the solvent has involved some form of decomposition of the original compounds. In the following summary, an attempt has been made to bring together results obtained by British workers.

Jan 1, 1925

By R. J. Lutton

Empirical data from 91 rock excavations have been used to construct a family of slope curves on a chart relating excavation height and inclination. The highest and steepest slopes from each excavation are plotted and connected by a line. The 31 1ines appear to establish one or two geometrical slope fields through which the curves are projected. The curves apparently represent a lumped eflect of many factors too complex to be considered individually. Important factors such as geological structure or ground-water conditions can dominate the picture, but where these factors do not overshadow others, the slope chart should be useful for estimating or checking optimum inclination. The U.S. Army Corps of Engineers (USAE) has been engaged since 1962 with the U.S. Atomic Energy Commission in a joint research program to develop nuclear excavation technology. The Corps is responsible for collecting the requisite data on engineering and construction problems associated with nuclear excavation. The ultimate objective is to develop a capability to use nuclear explosives as a construction tool on public works projects such as harbors and canals. The present study on empirical inclination-height curves for conventionally excavated slopes is an outgrowth of an investigation&apos; sponsored by the USAE Nuclear Cratering Group on applicability of data from existing excavations in establishing guides for engineering judgment in crater excavation. Data were generously contributed by over 50 mining companies among other organizations. Inasmuch as several companies preferred that their contribution be anonymous, all data are treated so here. Some Factors Affecting Stability Many factors affect or are suspected of affecting the stability of excavated slopes, e.g., adverse structural orientation, degree of structural ordering, ground water, climatic conditions, mechanics of excavation, and plan-profile configuration. Such factors are lumped together in developing a slope chart. Obviously geological structure and ground water can overshadow all other factors. Where such is the case, the simplification of slope charts may give an erroneous picture (not conservative enough). A further complication results from the fact that the concept of stability may vary according to the use of the excavations. For example, slope adjustments that would be regarded as failure in a powerhouse excavation, might be tolerable in a mining operation. Mine slopes are continually being modified by further excavation, and instability that would develop in a similar permanent excavation slope over a period of years might not have time to develop in a mine. Inclination vs. Height Charts Charts of inclination vs. height for particular formations or conditions have been used in the past as an aid for designing excavation slopes. Some of these have been based upon empirical analyses of collections of data and experience. MacDonald" and Lane have presented slope tables and charts for excavated and natural slopes in relatively weak sandstone and shale. Coates&apos; has shown an inclination-height chart for slopes in incompetent rock. Most organizations have developed slope design criteria which relate bench widths, heights, and inclinations to use in various rocks. Slope data collected in present studies can be similarly used to develop inclination-height charts; however, a plot of all slopes on such a chart shows very little because of the wide spread of the data. Reasons for the dispersion of points are: (1) many slopes are not carried at optimum inclination, particularly in mines where maintaining roadways and following irregularities of ore bodies are more important than achieving steep inclinations; (2) many engineers and geologists with varied backgrounds and viewpoints have been involved in designing these slopes; and (3) each slope is characterized by a unique combination of factors affecting stability and in turn optimum inclination. Significant curves can sometimes be constructed where the points can be grouped into related clusters from the same excavation. The essence of this approach appears when only two slopes from each excavation are considered—the highest slope and the steepest slope, connected by a line segment (Fig. 1). This reduces considerably the usable data because in many cases only one of these two slopes is available. Nevertheless, the concession seems justified. Construction of Slope Curves Ninety-one pairs of points and connecting line segments were assembled in this study. The line segments were assumed to approximate a geometrical slope field (Fig. 2), and a family of curves has been visually projected through to represent the slope field. It should be

Jan 1, 1971

By K. Prins

ONE of the more pressing problems faced by the coal industry today is the development of adequate means for meeting conservation laws, particularly those involving stream pollution, in various parts of the country. Discharge of dirty coal washery water into streams and rivers is almost universally frowned upon. Many states have enacted laws carrying heavy fines to curb the practice. The Prins stream-cleaner is one of the latest machines to enter the market. It is closely related to the cyclone thickener in principle. Eleven stream-cleaners are currently operating, ranging in size from 4 to 16 in. diam. In more recent installations the water enters directly in line and on a tangent with the impeller. The impeller consists of a vertical shaft up through a packing gland and bearings, and a V-belt pulley. The lower part is a tubing fastened to the shaft above, extending through the water intake compartment and provided with six vertical flat bars welded to the tubing. Portholes are situated in the upper end of the tubing, immediately below the point where shaft and tubing join together. The portholes are placed so that they are in open communication with the upper compartment of the stream-cleaner from which the processed water is discharged. The impeller is motor driven with a wide range vari-pitch drive employed between motor and impeller. The motor is mounted vertically, and the mounting provided with a vertical hinge allowing for needed adjustment of the wide range vari-pitch drive. The dirty coal washery water entering the machine under 20 lb psi pressure, flows from the compartment above the impeller, between the impeller blades, and is whirled around in the vertical section of the impeller enclosure. The speed of the impeller supplies centrifugal force and velocity required for separating suspended solids from water. The lower part of the machine consists of a cone, whose action is similar to other machines of the same type. The underflow discharge orifice is a cold rolled steel block machined to correspond with the cone angle and allows insertion of steel tubes of different diam. On 16 in. machines a 1 ¾ in. ID vertical discharge pipe is used. Provision is made for attaching a curved section of the same diam to the vertical pipe, to which, in turn, different lengths of horizontal pipe can be connected. Curved Pipe Advantageous It has been found that a curved pipe offers resistance to discharged material flow. In addition, the rotary motion of the underflow can be easily arrested in a curved pipe. Impeller speed of the 16 in. diam machine is provided from 400 to 800 rpm. A speed of about 474 rpm is suitable for maintenance of a constant underflow in coal slurry. In one installation 5x ¼ in. coal is cleaned in a Jeffrey Baum type washer at a 225 tons per hr rate. Washer installation is of the conventional type and a drag type sludge tank is used for water clarification purposes. Capacity of the water system, including the Baum washer, is about 40,000 gal. Before placing the stream-cleaner in operation, it was necessary to flush out the entire system every five days of two shift operations. The only time the system is drained now is for repair work on the sludge conveyor or the rig. The suction line of the stream-cleaner pump terminates in a number of small branch lines located at a depth of about 4 ft above the sludge conveyor. Each branch line extends the full width of the tank and is provided with four intake ports, each one with a funnel shaped inlet projecting downward. The arrangement provides an extensive pick-up area, for dirty water, and the inlets are arranged for a low rim velocity, preventing the taking in of coarse particles. The funnels are also arranged to extend up or down in the tank. They are set to pick up -60 mesh material exclusively.&apos; The material is a high ash and high sulphur product and thus has to be disposed in the refuse conveyor. The underflow of the stream-cleaner is discharged on top of the washery refuse which is carried in a drag type horizontal conveyor, discharging into another refuse conveyor inclined at 30º with a short horizontal loading section. Some Disadvantages The impeller inherits certain disadvantages because of the nature of its construction. Additional moving parts make it subject to wear and maintenance costs. The advantage of being able to maintain a constant speed, however, to produce desired water velocity in the machine outweighs the drawbacks. Better separation between water and solids can be obtained by regulating time of residence of water through adjustment of valves in the intake and discharge lines. The amount of fines encountered during plant operation will vary because of higher or lower moisture in coal passing over fine coal vibrating screens. Even the amount of fines picked up by underground loading machines will be inconstant. Consequently, the percentage of solids will vary in water to be processed. The velocity in the feedlines to the slurry thickeners will fluctuate, with the required water velocity lacking. Another advantage advanced for the machine is its ability to operate on 15 to 25 lb line pressures at the water intake, reducing pump power required and pump maintenance.

Jan 1, 1952

Jan 1, 1889

By Ralph W. Bailey, William B. Price

During the past three or four years, the fabricators of silicon-bronze alloys have endeavored to induce users of phosphor bronze to use instead the silicon-bronze alloys, claiming that the silicon bronzes are superior to the phosphor bronzes for switches and springs, or where high fatigue resistance is desired. This paper gives the results of tests comparing several phosphor bronzes with a 3 per cent silicon bronze and a copper-nickel-tin alloy (Adnic), all processed by the Scovill Manufacturing Co. So far as the authors are aware, sheet-metal fatigue tests have not been made on any of the alloys included in this report, except on one phosphor bronze, material C, Table 1, which was tested by Townsend and Greenall1. Endurance Limit The majority of fatigue tests are designed to determine the endurance limit of a material. The number of repetitions of stress that will serve to establish an endurance limit varies with different materials. For ferrous materials, H. F. Moore2 has shown that stresses that do not cause failure up to 10,000,000 stress cycles will not cause failure up to 100,000,000 (and sometimes to 1,000,000,000) cycles. Thus an endurance limit for ferrous materials can be determined with a minimum of 10,000,000 stress cycles. For nonferrous materials, no such generalization holds. R. R. Moore3 has shown that for manganese bronze and elektron metal, 13,000,000 and 28,000,000 cycles, respectively, will serve to determine an endurance limit, while certain duralumin specimens gave no indications of having reached an endurance limit up to 400,000,000 stress cycles. J. B. Johnson6 showed that an endurance limit for duralumin was not found by tests running up to 500,000,000 cycles. H. F. Moore2

Jan 1, 1937

By Ruder, W. E.

CONSIDERABLE interest has been shown lately in various types of furnaces for the production of high, temperatures, both for laboratory purposes and for small industrial uses. Dr. J. A. Harker1 described certain modifications of the Arsem graphite resistance helix for high-temperature work at the National Physical Laboratory. Dr. Northrup ,also has developed two interesting forms of high-temperature furnaces. In 1911, Messrs. Winne and Dantsizen2 described two forms, of resistance furnaces using ductile molybdenum or tungsten as resistors. Since the discovery, by this laboratory, of methods for producing these metals in ductile form, their use as resistance elements in the research laboratory of the General Electric Co. has grown to such an extent that they are now almost indispensable. These furnaces are used here for alloy research, annealing, heat-treating, and practically all f the thermal processes requiring temperatures above 900° C. Various types of furnaces have been developed to meet the general needs of laboratory work, and it is the purpose of this paper briefly to describe some of these furnaces. A tubular furnace wound with a metallic resistor is the simplest type to construct, and almost every laboratory has made such furnaces. The only essential difference between a furnace wound with platinum or base metal and one wound with tungsten or molybdenum is that the coils of the latter must be heated in a neutral or reducing atmosphere. It has long been our custom here to build our resistance furnaces with a metallic casing from which the tube could be easily removed for rewinding. The heat-insulating material-usually calcined magnesia, alumina, silica, or silex, depending upon the nature of the resistor-is used in powdered form so that it can he readily removed and replaced. In order to adapt this method to tungsten or molybdenum windings, it

Jan 2, 1918

By J. J. Predali, J. M. Cases

J. J. Predali and J. M. Cases (Attachè de Recherche and Charge de Recherche, respectively, Centre de Recherches sur la Valorisation des Minerais, Institut Polytechnique de Nancy, Nancy, France)-The role of CO, in carbonate flotation is one of the parameters of a complex phenomenon: the adsorption of salts of fatty acids onto minerals. The authors therefore must be congratulated for their work. Their experimental results suggest some questions: 1) Recovery with C02, benzoic acid, or HCl, look very similar [(Fig. 1)] to that with the use of air; however, the recovery decreases very slightly (<10%). But in these two kinds of experiments, two parameters are different: the pH which is near 5.8 (with C02) becomes 9.1(without C02) and the concentration of Ca* I x 10-3 mole per 1 (without C02) becomes 1.9 X 10&apos; mole per 1 (without COO. 2) Adsorption experiments (Fig. 2) permit computing the surface coverage 9 which is 7.4% (without C02) and 8% (without CO_.) for an initial concentration of 12 X 10-6 mole per 1 in sodium oleate. It seems doubtful to us that this small variation can produce large increases of the recovery in flotation. 3) It is difficult to correlate adsoption and flotation experiments because they do not seem to have been done with the same size of particles. The concentration needed to obtain 95% recovery (Fig. 1) is about 3.0 X 10_" mole per l, that is, 1.13 X 10-6 mole for about

Jan 1, 1973

By A. E. Dwight

Lattice parameters were determined for eighteen equiatornic alloys of the CsCl-type structure, ten of which were previously un-reported. It was found that fomation of the CsCl-type structure in binary alloys of the transition elements is largely dependent on position of the elements in the periodic table. The relative size of the two elements was not found to be a controlling factor. A recent paper by Beck, Darby, and Arora1 corre-lates the occurrence of CsC1-type ordered structures with the position of the constituent elements in the periodic table for the first long period. It was also suggested that a definite increase in relative bond strength between unlike atoms occurred when, in binary alloys of iron-group elements, the other component is changed from a chromium-group element, to a vanadium-group element, to titanium. A later paper by Philip and Beck2 noted that the lattice contraction increased in the order CrFe, VFe, and TiFe. It was also noted by Philip and Beck2 that the lattice contractions of CsC1-type alloys decreased in the order: TiFe, TiCo, and TiNi, which is an apparent reversal of the contractions expected from the position in the periodic table. It was suggested that the increasing lattice contraction is an indication of increased stability, i.e., greater A-Bbond strength. The present investigation was carried out to determine whether the relation of the position in the periodic table to the formation of the CsC1-type structure was also correct for alloys involving the second and third long-period elements. A systematic search was made for CsC1-type structures among equiatomic alloys and for those found, the lattice contraction was determined. EXPERIMENTAL TECHNIQUE The elements Y, Gd, Ti, Zr, Hf, V, and Cb are designated the A group and the elements Mn, Re, Fe, Ru, Os, Co, Rh, Ir, Ni, Pd, Pt, Cu, Ag, and Au are designated the B group. Equiatomic alloys were prepared for 57 AB combinations. The alloys were arc melted in a multicrucible furnace3 in buttons ranging from 5 to 20 g. Chemical analyses were not made, as the charge weights agreed closely with those of the buttons after melting. The alloy buttons were homogenized at 800° to 900°C. Metal log raphic and X-ray specimens were prepared and heat treated at temperatures from 600° to 1200°C. Specimens for X-ray diffraction were usually ground to a powder in an agate mortar; however, needle-shaped solid specimens were used when the alloy was sufficiently ductile to permit their preparation. Diffraction patterns were taken with a Straumanistype Debye-Scherrer camera using filtered Cu or Co radiation. The lattice parameters were obtained in A by plotting the calculated a0 values against the cos29/sin 0 + cos2?/? function and extrapolating linearly to ?= 900. Metallographic control specimens were polished on cloth wheels with diamond paste and etched with various phosphoric and nitric acid reagents. RESULTS The eighteen equiatomic alloys listed in Table I gave evidence of a cubic structure with two atoms in the unit cell, although two of these cubic structures exist only at elevated temperatures and transform to a tetragonal structure on quenching. Nine of these eighteen alloys gave diffraction patterns with super-lattice lines showing that the structure is of the CsC1-type. The lack of superlattice lines in patterns of the other nine alloys may be attributed to the small difference in atomic scattering power of the components. Metallographic study indicates the occurrence of nine narrow single-phase fields at the AB composition. Any or all of these nine may also have a CsC1-type structure. The VFe alloy was found to have a CsCl-type structure by Philip and Beck2 through the use of CrKa radiation (for which the scattering factor of V is anomalously low), whereas the Cu radiation used

Jan 1, 1960

By C. Hertzler

The difference of means of milling characteristics by rock and ore type is tested in a statistical manner in the paper. The null hypothesis being tested is that the sample means of two different populations are equal. It is assumed that the null hypothesis is true when performing the test. Because of this, acceptance of this hypothesis leads to the conclusion that the sample means of the two different populations are equal (or there is no significant difference between the sample means), not that the samples come from the same population, as the author asserts. Rejection of the null hypothesis leads to the conclusion that the sample means of the two different populations are not equal. A P value for this test is reported in Table 2 and is incorrectly identified as the probability that the two samples came from different populations. Actually, what was recorded was 100(1 - p) where p is the usual p-value. The usual p-value measures, on a scale of zero to one, the extent to which the data agree with the null hypothesis. It is the probability of observi" a value of the test statistic (Z score) that is at least as contradictory to the null hypothesis as the one computed from the sample data (McClave and Dietrich 11, 1982). The author makes no mention of the fact that were these tests to be conducted together, the chances of determining that the null hypothesis is not true when it is really true are increased considerably (Snedecor and Cochran, 1980). This is a multiple comparisons problem and should be dealt with accordingly. The usual methods involve adjusting the level of the individual tests. Table 2 reports an incorrect 100(1 - p) value in the comparison of concentrate grades for other rock types with .30 to .69% Cu vs other rock types with .70 + % Cu; 86% should be 98.6%. Although the article can be criticized for poor data presentation and discussion of that data, the point the author makes regarding the use of these statistics in the ore reserve estimation process is well taken. It does not appear that inaccuracies in the statistical interpretations have hindered that usefulness.

Jan 1, 1985

By Raymond Dugdale, Fathi Habashi

There has been a recent interest in studying the action of anhydrous sulfur trioxide on ores to convert the metal values into a water-soluble form as a substitute for leaching by sulfuric acid. For example, Svenke1 converted the small amounts of uranium in slate ash into a water-soluble form by treating the material with SO, at about 600°C. Chao and Sun found that a variety of aluminum-bearing minerals could be sulfatized by SO, in the temperature range 400° to 600°C usually in the presence of a catalyst such as sodium sulfate. Kruse3 patented a process for beryllium recovery from the low grade ore in Utah by first reacting it with SO, at 560° to 750°C then leaching the product with water. In the present report, the action of SO, was examined in the temperature region 100°-300°C which was not investigated by those workers. Experimental Tests were conducted on a beryllium ore sample from Utah, the analysis of which is given in Table 1. It corresponds closely to a saponite ore type as given by Crocker et al. It was in powder form 45% passing a 400

Jan 1, 1973

By V. Rajaram, I. P. Nielsen, H. D. Raymond

The Parachute Creek member of the Green River formation in the Piceance Basin, Colorado, contains vast reserves of oil shale, nahcolite, dawsonite, and other accessory minerals. The dry alkali process of sulfur dioxide removal using nahcolite (naturally occurring sodium bicarbonate) has great potential. A room and pillar mining scheme has been designed to extract a nahcolite zone occurring at a depth of 472 m, from the lease application area of the Yankee Gulch joint venture. Geotechnical parameters affecting mine design will be discussed. A preliminary development plan for mining at the rate of 1000 t/d will be described in detail.

Jan 12, 1979

By D. C. Jillson

BRIDGMAN1,2 melted metals in a graphite or hard glass tube and lowered the tube through a furnace to make it cool from one end only. Because of the difficulty of eliminating all vibration of the mold, others have raised the furnace instead. Neither way seems as desirable as a setup with no motion of either the mold or the furnace. A furnace in which both the shape and the slope of the temperature gradient could be controlled and varied over a wide range and in which such a gradient could be moved from one end of the furnace to the other, freezing the specimen from one end to the other, at any desired rate, all by means of isolated external control, seemed to offer definite advantages. In addition to eliminating the possibility of vibration due to moving parts, it might also give better control over the direction and rate of heat flow. Such an apparatus was assembled and is shown schematically in fig. 1. Equipment Furnace: A clay-carborundum tube of 3 1/2 in. ID with a % in. wall thickness was used as the core. This had a main winding of No. 12 B.&S. gauge Nichrome V with some compensation for heat loss at the ends. Taps to this winding were made at points 12 in. from each end. Fig. 2 shows details of this winding and of the two end windings. Each end winding was wound over Micanite over the main winding. No. 15 B.&S. gauge Nichrome V was used for these, and again taps were supplied at two inter-mediat,e points on each. The tube was supported in an 18 in. OD black iron shell with brick insulation. The input to each of the windings was regulated by means of a variable transformer. Temperature Regulation: A chromel-alumel thermocouple located near the furnace wall in the center of the furnace was connected with a Celec-tray controller, type PIC, 300" to 900°C range, which opened and closed a shunt across an external variable resistance in the main winding circuit. An "anticipatory response" device also was incorporated to minimize the cyclic effect of the control mechanism. Eleven survey couples in a common pyrex glass protection tube were located near the furnace wall and spaced 2 in. apart. The couple leads went to a common reference junction box where they were connected to copper leads from a selector switch which, in turn, was connected to a type K potentio-meter. This arrangement permitted rapid temperature surveys. The knob on the controller dial was replaced with a threaded brass spool turned at a controlled rate by a thin iron wire one end of which was attached to a gear train and the other to a small weight heavy enough to prevent slipping of the wire on the spool. The gear train, driven by a 1-rpm Telechron motor, contained a series of different sized interchangeable gears and threaded drums permitting a range of travel speeds from 0.10 in. per hr up to a hypo-

Jan 1, 1951

By N. F. Mott

Jan 1, 1961

By John C. Sawyer

The mechanism of catastrophic oxidation of chromium and 446 stainless steel is examined. Data are presented to show that accelerated oxidation of these two materials, as caused by lead oxide, can occur in the absence of a liquid layer contrary to presently accepted theory. An alternate theory is proposed in which the rate of accelerated oxidation is a function of the rate at which lead oxide destroys the protective oxide formed on the base metal. An example of the application of the theory is given for the catastrophic oxidation of chromium in the presence of lead oxide. WHEN stainless iron-, nickel-, or cobalt-base alloys are heated in air to moderate temperatures in the presence of certain metallic oxides, oxidation will proceed at an accelerated rate. This phenomenon, often called "catastrophic oxidation", is most pronounced for the stainless steels. With these alloys the condition is so severe that large masses of oxide will form on the surface of the alloy in 1 hr or less at temperatures of 1200o to 1700oF. While a number of oxides are known to cause this effect, PbO, V2O5, and Moo3 are the most familiar, having been the subject of one or more investigations which have appeared in the literature.1-7 In presenting the results of these investigations, many of the authors have offered possible explanations to account for the more rapid rate of oxidation observed; however, the liquid layer theory as proposed by Rathenau and Meijering 2 has been the most commonly accepted mechanism. The liquid layer theory proposes that a low-melting oxide layer is formed on the surface of the alloy as the result of the interaction of the alloy oxide and the contaminating oxide. When the temperature of oxidation is above the melting point of the oxide on the surface, a liquid layer will form and oxidation will proceed at an accelerated rate. At temperatures below the melting point of the surface oxide, oxidation will proceed more slowly in the normal manner. It is argued that the rates of diffusion of oxygen and metal ions through the liquid layer are extremely rapid thereby accounting for the high rate of oxidation. Various experimental data have been presented to show that the temperature at which accelerated oxidation first becomes apparent coincides with the melting point of the eutectic oxide which would be present on the surface. Some exceptions have been observed, e.g., silver will oxidize in the presence of Moo3 at temperatures below the lowest melting eutectic; on the other hand, stainless steel will not be catastrophically oxidized at 1500oF in a molten bath of PbO and SiO2. In reviewing the various theories which have been used to explain catastrophic oxidation, Kubaschewski and Hopkins 8 favor the liquid layer theory, but note that, ".. .as experimental observations are not altogether in agreement with this theory (liquid layer theory), one should consider it a necessary but not a sufficient condition." In contemplating the liquid layer theory, it appears that sufficient evidence has not been presented to establish the theory beyond question. As a means of further clarification, a program of research was undertaken to determine in greater detail the mechanism of accelerated oxidation as caused by lead oxide. The first part of the program deals with a comparison of the oxidation of both AISI 446 stainless steel and chromium metal in the presence of lead oxide, vs the oxidation of these two materials in air alone. These comparisons are made at a number of different temperatures, most of which are below the melting point of the surface oxides. The second part of the program is concerned with a presentation of an alternate theory of accelerated oxidation exemplified by the system Cr-PbO-Air. PROCEDURE AND RESULTS Several experimental methods are commonly used to follow the progress of oxidation. One of these, the weight-gain method, was chosen for this work. This procedure requires that a specimen of the alloy be weighed, oxidized for a given period of time at an elevated temperature, and reweighed—the difference between the two weights being noted. The weight gain of the specimen represents the amount of oxygen acquired from the atmosphere to transform a portion of the specimen to oxide. In those cases where there is a tendency for the specimen or oxide to volatilize at the testing temperature, additional data must be collected so that a correction factor can be determined. This factor must be applied to the weight change in order to ascertain the actual amount of oxidation which has taken place. The specimens used for this work were 1 1/2 in.

Jan 1, 1963