By L. C. Chang, T. A. Read

Diffusionless transformation in Au-Cd single crystals containing about 50 atomic pet Cd was investigated by means of X-ray analysis of the orientation relationships, electrical resistivity measurements, and motion picture studies of the movement of boundaries between the new and old phases during transformation. The nucleation of diffusionless transformation by imperfections and the generation of imperfections by diffusionless transformation were discussed. THAT connections exist between plastic deformation and diffusionless phase changes has long been recognized. Thus it is often possible to produce a diffusionless phase change in a temperature range, above that in which the change occurs spontaneously, by cold-working the initial phase. Certain aspects of the dislocation theory of the plastic deformation of crystalline solids also provide for a rather direct connection between the processes involved in plastic deformation and in diffusionless phase changes. Heidenreich and Shockleyl have pointed out that simple edge dislocations in f.c.c. metals are probably unstable, and that the more probable lattice imperfections, called extended edge dislocations, consist of two half dislocations separated by a distance of the order of magnitude of 100A. The region about two atomic planes thick between the half dislocations because of this stacking fault may be described as having the hexagonal close-packed structure. Presumably the stacking faults observed by Barrett" fter cold-working f.c.c. Cu-Si alloys resulted from the passage of such half dislocations through the lattice of the initial phase. It is now becoming clear that the development of a detailed theory of the atomic movements involved in diffusionless phase changes will require a consideration of the role played by lattice imperfections, just as such considerations are necessary to the understanding of plastic deformation mechanisms. This point of view has been recently set forth, for example, by Cohen, Machlin, and Paranjpe3 who pointed out the role which might be played by screw dislocations in nucleating diffusionless phase changes. The present paper reports on some aspects of the diffusionless phase change in single crystals of the beta phase alloy Au-Cd which serve to emphasize further the importance of lattice imperfections in diffusionless phase changes. The diffusionless phase change of Au-Cd possesses several remarkable features. One of these is that the interface between the high-temperature beta phase and the low-temperature orthorhombic phase typically moves with a low velocity, in contrast to the behavior observed in the transformation of austenite to martensite. Motion pictures of this slow interface motion have been prepared in the course of the work reported here. Another important feature of the Au-Cd transformation is the small amount of undercooling observed. The reverse transformation occurs on reheating to a temperature only 20" higher than the transformation temperature observed on cooling, and under some circumstances the hysteresis observed is substantially less than this. This narrow temperature range between transformation on heating and cooling is presumably in part a consequence of the fact that the transformation requires a lattice shear of only about 3". Finally, the orthorhombic product phase possesses unusual mechanical properties, as was first pointed out by olander' and Benedicks." After completion of the transformation on cooling the specimen can be severely deformed, yet on the release of load it springs back to its original shape in a rubber-like manner. Explanation of this phenomenon will require an understanding of the lattice imperfections in the orthorhombic structure and, correspondingly, of those in the initial body-centered cubic structure. Single crystals of Au-Cd alloy containing 47.5 and 49.0 atomic pct Cd were prepared from fine gold (99.95 pct purity) and chemically pure cadmium (99.99 pct purity) by melting the alloy in an evacuated and sealed fused quartz tubing and growing into single-crystal form by the Bridgman method. The Au-Cd alloy containing 47.5 atomic pct Cd undergoes a diffusionless transformation from an ordered body-centered cubic structure to an orthorhombic structure when it is cooled to about 60°C, while the reverse transformation takes place when the alloy is heated to about 80°C, according to electrical resistivity studies. The structures of these two phases have been studied by Blander,4 reinvestigated by Bystrom and Almin.e he lines of Debye photo-gram of powdered samples of Au-Cd alloy containing 47.5 atomic pct Cd prepared in this laboratory were identified and agreed fairly well with those of

Jan 1, 1952

By P. K. Foster, C. M. Payne, A. McNabb

Some measurements of the rate of loss of hydrogen from cylinders of iron and steel are analyzed in terrns of a trapping theory. The apeement is encozcraging and gives rise to estimates for the density of traps in the metal. Furthermore, the results appear to be consistent with the assumption that the diffusion constant D for the steady flux of hydrogen through iron lies on the extrapolation of the linear curve (log D us 1/T) obtained at higher temperatures. IT has been shown in a previous paper1 that the literature relating to hydrogen diffusion in steels contains sufficient evidence to invalidate the application of Fick's laws to hydrogen diffusion in steel at low temperatures. To account for the deviations from simple diffusion behavior a trapping theory was developed, and the fundamental laws modified accordingly. In the present paper, new data on the evolution of hydrogen from long cylinders are presented, and together with some published data are examined in terms of the requirements of the theory.' Properties of solutions of the basic equations derived previously1 and appropriate to the present experimental conditions are outlined in the first section as they determine the form in which the experimental data must be presented for a comparison of theory and experiment. Two new solutions not previously reported have been derived as described in the Appendix. The experiments and treatment of data are then given in Sections 2 and 3 and the results are discussed in Section 4. 1) THEORETICAL CONSIDERATIONS The hydrogen-diffusion theory1 applied in this paper postulated that lattice-dissolved hydrogen at a concentration C diffuses randomly in accordance with Fick's first law, but that the lattice contains a uniform density N of traps which can capture and delay hydrogen atoms. kC atoms are trapped per second in a region containing unit concentration of vacant traps while p are released per second in a region containing unit concentration of occupied traps. On this basis it was shown (Eq. [30] of Ref. 1) that, when local changes in the lattice-dissolved concentration C are slow enough for equilibrium to be established with the traps, the system is represented in dimensionless form by the equation:

Jan 1, 1965

G. SHERBURNE LAGERS (written discussion*).-Mr. Kennedy's discussion1 of Mr. Matteson's paper takes the form of a criticism of my own comments2 on this paper. Mr. Kennedy is a respected authority on matters pertaining to the salt-dome oil fields, and his characterization of my "elaborate figures" as "worthless" is sufficiently candid and comprehensive to warrant a brief reply. My "voluminous figures" consisted simply of a rough estimate of the minimum quantity of salt in the Humble dome, and a calculation of the volume of sea water and of the volume of saturated brine which this salt would represent. Mr. Kennedy apparently interprets my remarks as opposing the idea that so large a volume of salt could have been deposited from sea water, for lie cites the area and thickness of European salt beds; but nothing was further from my intention. Given an arm of the sea, an arid climate, and evaporation under a hot sun, it is easy to conceive the formation: of almost any thickness of bedded salt. I cited the figures in connection with Harris' theory of the origin of salt domes, according to which the plugs were formed by the deposition of salt from ascending brine solutions, owing to the drop in temperature as they neared the surface. I pointed out the well-known fact that the solubility of salt is only slightly affected by temperature, and that a drop of 80° C. would cause the deposition of less than one-tenth of the salt in solution; hence that more than ten times the volume of salt actually forming the plug must have been involved. If ten times the salt actually in sight be computed in terms of brine and multiplied by 50 or 60 to take into account all of the known salt domes, the resulting figure is so enormous that I am not at all as sure as Mr. Kennedy seems to be that the porous stratified rocks of eastern Texas and western Louisiana could contain or furnish so great a volume of migratory brine.

Jan 8, 1918

By D. E. Swets, P. C. Frank, D. L. Fry

THE hydrogen-steel system has received considerable attention in the past several years. Recent experiments in this laboratory have shown that another group of operations, namely, sanding and grinding,' must be added to the already well-estab- lished list of phenomena that cause hydrogen to permeate steel. Qualitative tests which have been made with a very sensitive ion-gage type of detector similar to that used by Norton,' showed that sanding a steel surface caused hydrogen permeation. A metal type 6~6 vacuum tube was used as the ion gage with an electrometer to measure the ion c~rrent.~ The protective enamel coating was removed from the tube.

Jan 1, 1959

By W. Julian Parton

Treatment of the breaker wash-water discharges to remove the suspended particles of finely divided material is usually most efficiently and economically accomplished in settling or thickening tanks. The purpose of these tanks is to separate the excess water from the solids by sedimentation whereby the solid particles suspended in the water are thickened by the force of gravity. The water overflowing these tanks is either reused for coal cleaning or discharged directly to the streams. The settled solids, which are in a relatively concentrated condition, forming a sludge or thick pulp, can be disposed of by pumping to a storage dam, by slushing into mine workings, by processing for recovery of coal, or filtering by vacuum or centrifugal means and discharging with the breaker refuse. The scope of this paper will be limited to the discussion of settling and thickening equipment, the factors that influence the settlement of solids, and a brief description of tests that can be made to determine the size of settling facilities required for any particular condition. The practical application of sedimentation to the treatment of coal falls into two groups, one of classification or hydro-separation, and the other of clarification and thickening. Classification may be employed to prepare a relatively low-grade fuel, which can be used as is or can be further processed separately. Clarification and thickening is employed where the primary objective is to recover a relatively dewatered solid and return a satisfactorily clear water to breaker or streams. Operation and Types oF Settling Equipment When a stream of water flows across a tank, the time required for a particle to travel from the feed inlet to the overflow must be a little greater than that required for the finest particles or flocs in the feed to settle out of the stream. Theoretically, the liquid in a settling tank should rise at a more or less constant rate throughout the area of the tank Under these conditions the rising velocity of the water must be less than the settling rate of the finest particles if clarification is to be obtained. When classification of particles is to be made in the tank, the overflow velocity must be greater than the settling velocity of the particles that are to be removed with the tank overflow. The performance of a settling tank, then, depends on the settling rate of the solids and the current velocities in the tank. The oldest types of sedimentation employ intermittent types of settling tanks of any convenient shape. Means are provided for filling the tank with pulp and allowing it to settle until quiet, for moving the clean liquor and for removing the thickened sludge. The operation is necessarily intermittent but a sufficient number of tanks is employed so that a continuous flow of clear water is maintained. Continuous methods for the sedimentation of slurries were developed in the metallurgical industry. Cones from which settled solids were discharged by gravity

Jan 1, 1947

By W. Julian Parton

Treatment of the breaker wash-water discharges to remove the suspended particles of finely divided material is usually most efficiently and economically accomplished in settling or thickening tanks. The purpose of these tanks is to separate the excess water from the solids by sedimentation whereby the solid particles suspended in the water are thickened by the force of gravity. The water overflowing these tanks is either reused for coal cleaning or discharged directly to the streams. The settled solids, which are in a relatively concentrated condition, forming a sludge or thick pulp, can be disposed of by pumping to a storage dam, by slushing into mine workings, by processing for recovery of coal, or filtering by vacuum or centrifugal means and discharging with the breaker refuse. The scope of this paper will be limited to the discussion of settling and thickening equipment, the factors that influence the settlement of solids, and a brief description of tests that can be made to determine the size of settling facilities required for any particular condition. The practical application of sedimentation to the treatment of coal falls into two groups, one of classification or hydro-separation, and the other of clarification and thickening. Classification may be employed to prepare a relatively low-grade fuel, which can be used as is or can be further processed separately. Clarification and thickening is employed where the primary objective is to recover a relatively dewatered solid and return a satisfactorily clear water to breaker or streams. Operation and Types oF Settling Equipment When a stream of water flows across a tank, the time required for a particle to travel from the feed inlet to the overflow must be a little greater than that required for the finest particles or flocs in the feed to settle out of the stream. Theoretically, the liquid in a settling tank should rise at a more or less constant rate throughout the area of the tank Under these conditions the rising velocity of the water must be less than the settling rate of the finest particles if clarification is to be obtained. When classification of particles is to be made in the tank, the overflow velocity must be greater than the settling velocity of the particles that are to be removed with the tank overflow. The performance of a settling tank, then, depends on the settling rate of the solids and the current velocities in the tank. The oldest types of sedimentation employ intermittent types of settling tanks of any convenient shape. Means are provided for filling the tank with pulp and allowing it to settle until quiet, for moving the clean liquor and for removing the thickened sludge. The operation is necessarily intermittent but a sufficient number of tanks is employed so that a continuous flow of clear water is maintained. Continuous methods for the sedimentation of slurries were developed in the metallurgical industry. Cones from which settled solids were discharged by gravity

Jan 1, 1947

By W. J. Rogers, L. J. Dwiggins, R. O. Williams

THERE has been comparatively little work on the importance of strain rate and temperature as variables in the formation of deformation textures. For this reason the present work was started, the choice of compression being in part that of convenience and in part because of the absence of quantitative data in this area. These do not turn out to be important variables within the range studied which permits the results to be condensed into this note. Samples 1/4 in. in diam and 1/2 in. long were machined from 99.9 pct pure commercial aluminum and recrystallized to a fine grain size. A set of five samples were deformed between a spring-driven weight and an anvil resulting in roughly 20 pct strain each time. The strain rate varied because of decle-ration and shortening of the sample but would average about 10&apos; per min. Deformation at temperatures over the range of -76" to 150°C were obtained by heating or cooling the samples. Complete lubrication could be obtained by oil since the short time of contact did not permit its escape. The samples were compressed to a total true strain of 1.4 to 1.6. A larger sample was prepared similarly with spiral grooves in the ends to hold paraffin which provided essentially complete lubrication. This sam ple was compressed slowly at room temperature at a rate of about 2 per min to a total strain of 1.0. Cylindrical samples were carefully machined from these discs with a radial direction as an axis. They came from the center half of the samples and were roughly 1/16 in. in diam. The samples were etched down 15 pct to remove any surface effects. Diffraction data were then obtained for six different kinds of planes by the use of the Norton technique as applied to a fiber texture. Direct comparison between the raw data failed to reveal any significant difference between any of the samples and consequently the data from only one sample was completely reduced. The particular sample had been deformed at O°C The background was subtracted from the intensity data which were averaged over the four quadrants and then normalized to random. These data were then used to obtain fiber-axis distribution charts as previously described.2 For this sample the (422) plane was also run to assist in this inversion. The final result, Fig. 1, provided a comparable fit to that previously obtained from fiber data. About 85 pct of the material forms an elliptical texture around the <110> direction. The radius (at half height) is 5.5 deg along the (111) boundary and 8 deg along the (100) boundary. The remaining 15 pct forms a ridge running from this texture to near the <311> direction. The regions around the (100) and (111) planes are devoid of material. The earlier qualitative results of ~arrett~ are in complete agreement with the present results. The possibility has been dis-cused that the material around the <311> results from friction between the sample and compression plates.4 The present results are considered proof that such is not the case because of the uniformity of sample deformation and the requirement of axial symmetry before fiber-axis distribution charts can be accurately obtained. Recently results have been obtained to show that strain rate and temperature are important variables in the extrusion of aluminum.5 Perhaps the most important observation was that the partial recrystal-lization occurred even at room temperature. Strain rate was considered to be a factor only in that it produced a temperature change. There are many differences between the two experiments, the most important possibly being that their material was roughly ten times the purity of the present material. The present experiment, however, may not be as definitive as desired in this respect since it has been shown that compressed aluminum recrystallizes without a texture change6 although supplementary

Jan 1, 1961

By M. Karfakis, K. Kim, R. V. de la Cruz

The in situ deformability of a closely jointed basalt rock mass was determined by two different methods: the NX-borehole jack method where displacements of opposing curved platens were related to applied hydraulic pressures, and the modified Goodman jack method where tangential strains on the borehole walls were related to induced tangential stresses. The modulus obtained by the modified Goodman jack method were much higher than those obtained by the NX-borehole jack method. To explain the discrepancy, the influence of fractures and test variables, such as depth, orientation, hole location, and applied pressure on the calculated modulus of the rock mass, were analyzed by factorial analysis. It was found that the orientations and measurement depths have statistically significant effects. The in situ deformability values obtained by nonlinear regression analysis were also found comparable with other measurements and empirically predicted values for the basalt rock mass.

Jan 1, 1984

By R. D. Hagni

The following is a case study illustrating the use of thin sections and polished sections of crude ore to predict metallurgical response. By examining polished sections of the metallurgical products, the textural and mineralogical reasons for unsatisfactory separation can be explained. An area of oxidized Negaunee Iron-Formation located south of Negaunee, Michigan, in the Marquette Iron Range, has been considered for roast reduction-magnetic separation. Preliminary metallurgical studies and subsequent pilot plant testing produced varied results. These results prompted this microscopic study which began with an examination of 126 thin sections and 82 polished sections prepared from 126

Jan 1, 1967

By Alexander Field

IN THE light of the experimental data on equilibrium for the reaction C + FeO = Fe + CO in molten steel recently obtained by Kinzel and I Egan,1 it is necessary to revise current theories regarding the nature of equilibrium between carbon and FeO in the basic open-hearth furnace. According to the measurements of these investigators the equilibrium constant m for the above reaction for a pressure of dissolved CO equal to 1 atm. is equal to 0.0005 at 1550° C., when concentrations of carbon and. FeO are expressed in percentages by weight. Their work also shows that, with the pressure of CO fixed at 1 atm., not only is the product of carbon and FeO constant, but carbon and FeO are each independently constant-a circumstance which might have been predicted from theoretical considerations. At 1550° C., carbon is constant at about 0.025 per cent. and FeO at about 0.020 per cent., with the pressure of dissolved -CO equal to 1 atm., the product of these two constants being equal to the originally mentioned constant of 0.0005. Available data on the dissolved FeO content of samples taken from the metal bath at practical slag-metal equilibrium prove that this FeO content is determined solely by temperature and the effective FeO content of the slag. The distribution constant r at 1550° C., as determined by Herty, Gaines, Larsen, Simkins, Geruso and Watkins2 is equal to 0.0086. A slag would have to contain 0.020/0.0086 = 2.3 per cent. effective FeO or less in order to prevent the metal from containing more dissolved FeO than that required for equilibrium with CO at 1 atm. pressure. Such low percentages of FeO are never found in basic open-hearth slags at the completion of a heat when rate of carbon drop has become practi-

Jan 1, 1930

By D. T. Peters, S. Floreen

The age hardening behavior of an Fe-8Ni-13Mo alloy was studied after the matrix had been varied to produce either ferrite, cold u~orked ferrite, or nzassive nzartensite. The aging behavior of the cold worked ferrite and murtensite structures were very similar. The martensite aging kinetics were much different from those observed in earlier studies of aging of maraging steels, even though the martensite wzatri.r had the same dislocation structure as those found in maraging steels. The results suggest that the previously observed precipitation kinetics of maraging steels ?nay have been controlled by the nucleation be-haviov, which in turn were dictated by the alloy compositions and the resultant identities of the precipitating phases. IT is well known that the rate of precipitation from solid solution depends not only on the degree of super-saturation, but also on the density and distribution of dislocations in the matrix structure. These imperfections often act as nucleation sites, and may also enhance atomic mobility. &apos;Thus, the presence of dislocations is important since the type and distribution of precipitates may be determined by them. The precipitate density and morphology in turn affects the mechanical properties of the alloy. A number of studies have been devoted to the precipitation characteristics in various types of maraging steels.&apos;-" These are iron-base alloys containing 10 to 25 pct Ni along with other substitutional elements such as Mo, Ti, Al, and so forth, that are used to produce age hardening. The carbon contents of these steels are quite low, and carbide precipitation is not believed to play any significant role in the aging reactions. After solution annealing and cooling these alloys generally transfclrm to a bcc lath or massive martensite structure characterized by elongated martensite platelets that are separated from each other by low angle boundaries, and that contain a very high dislocation den~it~.~~~~~~~~-~~ Age hardening is then conducted at temperatures on the order of 800" to 1000°F to produce substitutional element precipitation within the massive martensite matrix. Most of the aging studies to date have revealed several common traits in these alloys, regardless of the particular identity of the precipitation elements. Generally hardening has been found to be extremely rapid, with incubation times that approach zero. The agng kinetics, at least up to the time when reversion of the martensite matrix to austenite begins to predominate, frequently follow a AX/~~ = ktn type law, where x is hardness or electrical resistivity, t is the time, and k and n are constants. The values of n are frequently on the order of 0.2 to 0.5, which are well below the idealized values of n based on diffusion controlled precipitate growth models. Finally, the observed activation energy values are typically on the order of 30 kcal per mole, and thus are well below the nominal value of about 60 kcal per mole found for substitutional element diffusion in ferrite. The common explanation of these observations is that the precipitation kinetics are controlled by the massive martensite matrix structure. Thus, the absence of any noticeable incubation time has been attributed, after ~ahn," to the fact that the precipitate nucleation on dislocations may occur without a finite activation energy barrier. The low values of the activation energy are generally assumed to be due to enhanced diffusivity in the highly faulted structure. If this explanation that the precipitation kinetics are dominated by the matrix structure is correct then one should observe a distinct difference in lunetics between aging in a martensitic matrix and aging the same alloy when it has a ferritic matrix. Such a comparison cannot be made with conventional maraging compositions, but could be made with the alloy used in the present study. In addition, the ferritic structure of the present alloy could be cold worked to produce a high dislocation density so that one could determine whether ferrite in this condition would age similarly to martensite. EXPERIMENTAL PROCEDURE The composition of the alloy used in this study was 8.1 pct Ni, 13.0 pct Mo, 0.10 pct Al, 0.13 pct Ti, 0.012 pct C, bal Fe. The alloy was prepared as a 40 lb vacuum induction melt. The heat was homogenized and hot forged at 2100°F to 2 by 2 in. bar, and then hot rolled at 1900°F to $ in. bar stock. The aging lunetics were followed by Rockwell C hardness and electrical resistivity measurements. Samples for hardness testing were prepared as small strips approximately 2 by $ by 4 in. thick. Electrical resistivity was studied on cylindrical samples approximately 2 in. long by 0.1 in. diam. The method for making the alloy either martensitic or ferritic was based on the fact that the alloy showed a closed y loop type of phase diagram. At high temperatures, above approximately 24003F, the alloy was entirely ferritic. Small samples on the order of the dimensions described above remained entirely ferritic after iced-brine quenching from this temperature. In practice, a heat treatment of 1 hr in an inert atmosphere at 2500°F followed by water quenching was used to produce the ferritic microstructure. These samples were quite coarse grained and usually en-

Jan 1, 1970

By E. S. Machlin

RECENTLY, there has been much activity in the field of nucleation of martensitic transformations.&apos;- One of the problems in this field is the calculation of the rate of nucleation (number of plates nucleated per unit untransformed volume per unit time) in terms of observable parameters. Two such observable parameters are the fraction of the length of a straight line which corresponds to the portion of the total length of the line that lies in the martensitic phase and the number of plates intersected by this straight line per unit length of line. Because of the necessity of a valid answer to this problem, the following investigation was undertaken. Although this problem has been treated in the past, a derivation of the relation between the volume and linear fractions of martensite will be described to illustrate the method used in the succeeding analyses. It is assumed that the martensitic plates are in the form of a right circular cylinder having a small height relative to the radius of the base. The volume fraction of martensite is then: fr = lXNl,hjAl [1] where f, is the volume fraction of martensite, and Nij is the number of plates per unit total volume having the area Ai and the height hi. The linear fraction of martensite is obtained as follows. For the plates having the particular area A, and height h,, the fraction sin 0 dB* will have their cylinder axes between the angles 0 and 0 + d0 to the straight line along which the linear fraction of mar-

Jan 1, 1953

By Corliss R. Kinney

Since the first atomic bomb exploded over Japan, a great deal of speculation has been published about the use of atomic energy instead of coal for the production of power. Atomic energy, in time, may displace coal for this purpose, but atomic energy will not displace coal in supplying chemical raw materials to the rapidly expanding carbon-chemicals market. Modern civilization demands large quantities of carbon compounds and the logical source of many of these is coal. Consequently, many progressive operators are considering the possibilities of the utilization of coal as a chemical raw material as never before. Furthermore, the demand for clean, smokeless, and ashless fuels will continue to increase and the only way to handle coal under those conditions is to take it apart, just as crude petroleum is taken apart. One can readily imagine where the petroleum industry would be now if it had insisted on selling customers only crude oil, perhaps emulsified with a little salt water to correspond to the moisture and mineral matter in raw coal. The time seems to be coming at an accelerated Dace when mine operators will find that competing for a highly selective fuel market by producing a larger tonnage at smaller cost will be less profitable than to increase the value of a smaller tonnage many fold by producing something more valuable to industry and civilization than raw coal. For example, about 750,000 tons of carbon black selling for $50 to $60 per ton was produced in the United States in 1945. This tonnage is insignificant compared with the total production of coal in the United States, but a very tidy tonnage, together with the coal necessary to operate the process, for any mine operator fortunate enough to obtain a method of producing a better carbon black from coal. From the point of view of tonnage, the manufacture of coke of various kinds and its by-products is at present the most important source of carbon chemicals from coal. Nearly 20 per cent of the coal mined in this country is used for this purpose. A large proportion of the coke is used for the production of iron and steel, but even in this operation a considerable part of the coke is used for a chemical purpose; that is, the reduction of the ore to metallic iron. In addition, large quantities of coke are used in manufacturing many important products that find their way into the market. Possibilities of Acetylene One of the important chemicals manufactured from coke is calcium carbide, from which many products are made. One of these is acetylene. This hydrocarbon can also be manufactured from natural gas or from waste oil-refinery gas and these industries will probably offer competition for the manufacture of acetylene. Coke-oven gas can be used for making acetylene and should receive consideration

Jan 1, 1947

By Corliss R. Kinney

Since the first atomic bomb exploded over Japan, a great deal of speculation has been published about the use of atomic energy instead of coal for the production of power. Atomic energy, in time, may displace coal for this purpose, but atomic energy will not displace coal in supplying chemical raw materials to the rapidly expanding carbon-chemicals market. Modern civilization demands large quantities of carbon compounds and the logical source of many of these is coal. Consequently, many progressive operators are considering the possibilities of the utilization of coal as a chemical raw material as never before. Furthermore, the demand for clean, smokeless, and ashless fuels will continue to increase and the only way to handle coal under those conditions is to take it apart, just as crude petroleum is taken apart. One can readily imagine where the petroleum industry would be now if it had insisted on selling customers only crude oil, perhaps emulsified with a little salt water to correspond to the moisture and mineral matter in raw coal. The time seems to be coming at an accelerated Dace when mine operators will find that competing for a highly selective fuel market by producing a larger tonnage at smaller cost will be less profitable than to increase the value of a smaller tonnage many fold by producing something more valuable to industry and civilization than raw coal. For example, about 750,000 tons of carbon black selling for $50 to $60 per ton was produced in the United States in 1945. This tonnage is insignificant compared with the total production of coal in the United States, but a very tidy tonnage, together with the coal necessary to operate the process, for any mine operator fortunate enough to obtain a method of producing a better carbon black from coal. From the point of view of tonnage, the manufacture of coke of various kinds and its by-products is at present the most important source of carbon chemicals from coal. Nearly 20 per cent of the coal mined in this country is used for this purpose. A large proportion of the coke is used for the production of iron and steel, but even in this operation a considerable part of the coke is used for a chemical purpose; that is, the reduction of the ore to metallic iron. In addition, large quantities of coke are used in manufacturing many important products that find their way into the market. Possibilities of Acetylene One of the important chemicals manufactured from coke is calcium carbide, from which many products are made. One of these is acetylene. This hydrocarbon can also be manufactured from natural gas or from waste oil-refinery gas and these industries will probably offer competition for the manufacture of acetylene. Coke-oven gas can be used for making acetylene and should receive consideration

Jan 1, 1947

By Tracy C. Jarrett

In making gold alloys possessing certain physical properties, such i~nportant factors as corrosion resistance, color, hardness and melting points must be considered. All of these requirements depend directly upon the composition. It is possible to obtain the same colored gold alloy by using different compositions, but in doing so one may bring in some undesirable property. Other investigations have been carried on in this field by F. E. Carter,&apos; E. M. Wise12 and L. Sterner-Rainer2 To make a complete study of the effect of composition upon these properties, a systematic investigation was carried on involving a range of copper content from 85 to 65 per cent. Elements such as zinc, silver and nickel were used to replace in part the copper content. The gold content in all the alloys remained constant. Only 10-karat gold alloys of those containing 41.6 per cent gold will be considered. All of the alloys were made in an induction furnace. Each alloy was cast in a 3 by 1/4 by 3/4-in. ingot. The method of obtaining the melting points and making color determinations was described in a previots paper.4 The Rockwell B scale with the 1/16-in. ball and 100-kg. weight was used for all hardness determinations. The submersion of test pieces in concentrated nitric acid is one of the standard corrosion tests used in the optical trade. A test piece in the 50 per cent cold-worked condition, % by 2 by 0.045 in., is blanked from a skip using a die, and the weight loss per square inch of surface is taken as a means of comparison. The time for this test is 2 1/2 hr. of actual submersion of the test picce in the acid. This standard test was applied to all of the 10-karat gold alloys discussed in this paper. The tensile tests were made upon strips of the dimensions shown in Fig. 1. The test pieces after blanking were annealed at 1300" F. for 20 min. and cooled in air. Thc "drop of the beam" method was used in determining the yield point, as there was a very marked "drop" when the yield point was reached.

Jan 1, 1940

By Tracy C. Jarrett

In making gold alloys possessing certain physical properties, such i~nportant factors as corrosion resistance, color, hardness and melting points must be considered. All of these requirements depend directly upon the composition. It is possible to obtain the same colored gold alloy by using different compositions, but in doing so one may bring in some undesirable property. Other investigations have been carried on in this field by F. E. Carter,&apos; E. M. Wise12 and L. Sterner-Rainer2 To make a complete study of the effect of composition upon these properties, a systematic investigation was carried on involving a range of copper content from 85 to 65 per cent. Elements such as zinc, silver and nickel were used to replace in part the copper content. The gold content in all the alloys remained constant. Only 10-karat gold alloys of those containing 41.6 per cent gold will be considered. All of the alloys were made in an induction furnace. Each alloy was cast in a 3 by 1/4 by 3/4-in. ingot. The method of obtaining the melting points and making color determinations was described in a previots paper.4 The Rockwell B scale with the 1/16-in. ball and 100-kg. weight was used for all hardness determinations. The submersion of test pieces in concentrated nitric acid is one of the standard corrosion tests used in the optical trade. A test piece in the 50 per cent cold-worked condition, % by 2 by 0.045 in., is blanked from a skip using a die, and the weight loss per square inch of surface is taken as a means of comparison. The time for this test is 2 1/2 hr. of actual submersion of the test picce in the acid. This standard test was applied to all of the 10-karat gold alloys discussed in this paper. The tensile tests were made upon strips of the dimensions shown in Fig. 1. The test pieces after blanking were annealed at 1300" F. for 20 min. and cooled in air. Thc "drop of the beam" method was used in determining the yield point, as there was a very marked "drop" when the yield point was reached.

Jan 1, 1940

By Robert C. Edmiston

The measurement of temperatures in exploratory drill holes yields information on regional and local geothermal gradients and mean surface temperatures. This data may be beneficial to the mining geologist interested in the occurrence and oxidation of metallic sulfide minerals or to the mining engineer interested in subsurface temperatures or water movement. Additionally, the estimation of mean surface temperatures by the projection of thermal gradients to the ground surface provides data on which to evaluate infrared imagery as an exploration tool. Temperature measurements in 30 diamond drill holes in the Silver Bell mining district of Arizona show that a regional geothermal gradient of 2.45°C per 100 m increases to 3.03°C per 100 m near the ground surface. It is also found that an anomaly in the mean annual surface temperature of 0.5°C is associated with the shallow occurrence of disseminated sulfides. Changes in the geothermal gradient due to topography, water circulation, and formation changes also occur.

Jan 1, 1976

By J. H. Henderson, J. Naar

The displacement of a wetting fluid from a porous medium by a non-wetting fluid (drainage) is now reasonably well understood. A complete explanation has yet to be found for the analogous case of a wetting fluid being spontaneously imbibed and the non-wetting phase displaced (imbibition). During the displacement of oil or gas by water in a water-wet sand, the porous medium ordinarily imbibes water. The amount of oil recovered, the cost of recovery and the production history seem then to be controlled mainly by pore geometry. The influence of pore geometry is reflected in drainage and imbibition capillary-pressure curves and relative permeability curves. Relative permeability curves for a particular consolidated sand show that at any given saturation the permeability to oil during imbibition is smaller than during drainage. &apos; Low imbibition permeabilities suggest that the non-wetting phase, oil or gas, is gradually trapped by the advancing water. This paper describes a mathematical image (model) of consolidated porous rock based on the concept of the trapping of the non-wetting phase during the imbibition process. The following items have been derived from the model. 1. A direct relation between the relative permeability characteristics during imbibition and those observed during drainage. 2. A theoretical limit for the fractional amount of oil or gas recoverable by imbibition. 3. An expression for the resistivity index which can be used in connection with the formula for wetting-phase relative permeability to check the consistency of the model. 4. The Iimits of flow performance for a given rock dictated by complete wetting by either oil or water. 5. The factors controlling oil recovery by imbibition in the presence of free gas. The complexity of a porous medium is such that drastic simplifications must be introduced to obtain a model amenable to mathematical treatment. Many parameters have been introduced by others in Iprogressing" from the parallel-capillary model to the randomly interconnected capillary models independently proposed by Wyllie and Gardner3 and Marshall4. To these a further complication must be added since an imbibition model must trap part of the non-wetting phase during imbibition of the wetting phase. Like so many of the previously introduced complications, this fluid-block was introduced to make the model performance fit the observed imbibition flow behavior. THE IMBIBITION MODEL ASSUMPTIONS The following assumptions are common to many two-phase models previously described. 1. The wetting characteristics of the medium are clearly defined. 2. When two fluids co-exist in the medium, the wetting phase will fill the smaller pores and the non-wetting fluid the bigger ones. 3. The pores have a circular cross section. 4. Apparent pore radii are related to the capillary pressure (drainage) by

By R. E. Reed-Hill, W. H. Hartt

High-purity magnesium single crystals, oriented with basal plane parallel to stress axis, were deformed in tension at room temperature so as to form second-order (1011)- (1012) twins. Investigation by optical and replica electron microscopy revealed that these twins can support very large internal strains approaching 1000 pct and that fracture follows as a direct consequence of these strains. At low strains the basal plane within (10i1)- (10i2) twins rotates with increasing deformation until it becomes approximately parallel to the twin boundaries. This rotation is not consistent with deformation by basal slip in the double twin, but may be rationalized in terms of nonbasal slip. Observations also indicate that basal slip in the primary (1011) twin, prior to second-order twinning, may contribute to this rotation. Deformation markings that are difficult to interpret in terms of slip on previously observed systems were noted in the twin bands. A possible means of rationalizing these markings is to relate them to grain boundary shear. The fracture associated with these twins is thought to initiate by formation of voids at the twin boundaries. These grow into microcracks, with ultimate fracture occurring by tearing of the interconnecting regions. THE significance of deformation and fracture along second-order (10i1)-(10i2) twins in polycrystalline magnesium1-&apos; and many magnesium alloys4 was discussed in a previous paper.5 It was noted that this double twinning mode effectively controls the room-temperature deformation and fracture of magnesium single crystals, oriented with the basal plane parallel to the tensile axis. Reed-Hill and Robertson6 observed that, although these crystals may fracture at a macroscopic strain of less than 1 pct, shear strains up to 1000 pct could occur within (1011)- (10i2) twin bands. They concluded that the fracture was "ductile" and resulted from concentrating the deformation into a very small volume. The present research was undertaken to obtain a better understanding of the deformation and fracture associated with these twins. EXPERIMENTAL TECHNIQUES The experimental procedure involved straining high-purity magnesium single crystals in tension at room temperature. Specimens were oriented so that the applied stress direction was within 2 deg of the [1010] crystal axis. The specimen cross section was rectangular with faces closely parallel to (1210) and (0002). The specimen preparation and testing procedures have been described in detail elsewhere.5 Second-order (1011)- (1072) twins nucleated during straining were studied using optical and replica electron microscopy techniques. For the latter, cellulose acetate-carbon double replicas were employed. Observations were made on the (1210) crystal surface, which is the plane of shear for twins of this type. In addition to the single crystals, some investigations were carried out on longitudinal polycrystalline specimens. These were obtained from high-purity magnesium plate with a texture in which the basal planes of the grains tended to be nearly parallel to the specimen axis. All. polycrystalline specimens were annealed prior to testing in order to produce a coarse grain structure, permitting Laue back-reflection X-ray photographs to be obtained from grains of interest. EXPERIMENTAL RESULTS a) Deformation Within ( 101 l )-( 1072) Twins. Fig. 1 is an optical micrograph demonstrating the extent of the plastic deformation that can occur in (1011)-(10i2) twin bands. Notice at the lower left corner of the photograph the large displacement of the dark band (a polishing step) where it crosses the twins. The shear strain in the twin band at this position was computed to be 700 pct, using the ratio of step width to twin thickness. It was previously shown5 that (1011)- (1012) twin bands are often composed of small, separate twins aligned close to the macroscopic habit plane. Fig. 2 is an electron micrograph from near the upper end of the twin band in Fig. 1. This illustrates that the twin habit often does not coincide exactly with the macroscopic band habit, but may be inclined at a slightly smaller angle to the matrix basal plane. Figs. 3 through 6 are electron micrographs of the twin band in Fig. 2 illustrating successive steps in the development of deformation inside the band. A twin band such

Jan 1, 1969

By G. R. St. Pierre, L. M. Adelsberg, R. Speiser

OXIDE platelets have been observed&apos;-3 in oxidized tantalum adjacent to the metal-oxide interface, Fig. 1. The origin and identity of the platelets are important with respect to the proposal of an acceptable mechanism of tantalum oxidation. At reaction temperatures below 750°C, it has been established that the platelets

Jan 1, 1967