By Carlos Carnurri

A characterization of mechanical properties of fire refined copper has been done in order to link ductility with oxygen content. The results show four different copper mechanical behaviours as temperature increases, where the oxygen con- tent, as Cu20 segregated, has a deleterious effect on ductility. It is concluded that until 500 ppm oxygen content, the fire refined copper could be rolled without remelting for deoxidation. Also a subsequent cold rolling could be done without intermediate annealing.

Jan 1, 1994

By Phillip B. Messersmith, Emmanuel P. Giannelis

"A versatile in-situ polymerization approach is described for the synthesis of polymerceramic nanocomposites consisting of two-dimensional layers of mica-type silicate (MTS) within polymer matrices. Functionalized, organically modified mica-type silicates (OMTS) were used to promote delamination/dispersion of the host layers and initiate polymerization of organic rrionomer. Epoxy nanocomposites prepared in this manner exhibit substantial modulus reinforcement at low silicate loadings. The water vapor permeability of the poly(?-caprolactone) nanocomposite containing 4.8% silicate by volume was reduced by nearly an order of magnitude compared to pure poly (?-caprolactone).IntroductionPolymer matrix nanocomposites are a relatively new class of materials with dimensions typically in the range of 1-100 nm.1 In general, because of the ultrafine phase dimensions involved, nanocomposites exhibit new and improved properties when compared to their micro- or macrocomposite counterparts. We as well as others are currently investigating the design, synthesis and characterization of polymer-ceramic nanocomposites. Our effort, in particular, has focused on the use of mica-type silicates (MTS) with various thermoplastic and thermosetting matrices.2-5MTS's belong to the general family of 2: 1 layered silicates. Their crystal structure consists of layers of two silica tetrahedral sheets fused to an edge-shared octahedral sheet of either aluminum or magnesium hydroxide. Stacking of the layers leads to a regular van der Waals gap or interlayer.6 Isomorphic substitution within the layers generates negative charges that are counterbalanced by cations residing in the interlayers. Although the natural forms of MTS's usually contain hydrated Na+ or K+ ions, ion exchange reactions with organic cations (e.g. alkylammonium ions) can render the normally hydrophilic MTS's organophilic."

Jan 1, 1994

By C. J. Beyke

Slags and/or mattes from three secondary lead producers were studied as part of an effort to develop treatment methods for these lead-bearing residues. Each company used a somewhat different production process. Company A used a reverberatory furnace followed by a blast furnace. Company B used only a blast furnace. Company C used both a reverberatory and a blast furnace, and the scrap material was desulfurized with sodium carbonate prior to smelting. The slag matrix produced from sulfur-bearing scrap consisted mainly of iron-calcium silicates; the slag from desulfurized material was similar, but also contained sodium. In all the slags most lead was present in metallic form, often alloyed with tin, antimony, arsenic, and/or iron. Slag from Company B contained the most alloying elements, often as discrete subparticles within the lead droplets. Mattes were produced at Companies A and B; predominant phases were pyrrhotite and magnetite, while lead was present in metallic form and as galena.

Jan 1, 1995

By O. E. Omotoso

This study is part of an ongoing investigation to understand the mechanism of stabilization/solidification of hazardous chromium wastes in ordinary Portland cement (OPC). Tricalcium silicate (C3S*),a major component of OPC is mixed with reagent grade Cr(lll) and Cr(VI) solutions, to simulate complex cementiCr waste systems. Scanning electron microscopy (SEM) and energy disperse spectrometry (EDS) were employed to provide microstructural and chemical information. Transmission electron microscopy (TEMlEDS), apart from complimenting the SEM, was used to probe the distribution of Cr in the hydration products of C3S and to provide crystallographic information. 29Si MAS NMR (magic angle spinning - nuclear magnetic resonance) Was used to characterize the influence of Cr on the hydrated silicate structure.

Jan 1, 1995

By Chang Wei, Zhigan Deng, Yizhao WANG, Cunxiong Li, Gang Fan, Xingbin Li

During the process of hematite precipitation, the transformation of Na jarosite convert into hematite has been studied in a batch reactor at different temperatures, ranging from 170°C to 200°C with 3h of the retention time in the presence of 30g/L Fe ( ) and 4g/L Na+. The composition of precipitation was seriously depended on the temperature, at 170°C hematite and sodium jarosite are the reaction products of iron precipitate, with an increasing in reaction temperature the sodium, sulfur content in precipitated decreased and sulfur mainly exist in forms of SO4 2-, and when temperature over 200°C hematite was the only phase in product. An increasing temperature was not only beneficial to iron precipitation, also conducive to jarosite conversion to form high quality hematite precipitate.

Jan 1, 2016

By C. Liliane Carvalho

In the current study, bio-oxidation tests were carried out in shaking flasks with a flotation concentrate containing the sulphides pyrite, arsenopyrite and gudmidite. The tests were performed with mesophilic microorganisms (At. ferrooxidans) at 30 °C and also with the moderate thermophile S. thermosulfidooxidans, at 50 °C. The effects of (i) previous adaptation of the microorganisms to the concentrate, (ii) ferrous iron concentration and (iii) pulp density (2%, 4% and 6% (w/v)) on the dissolution of the sulphide were studied through arsenic extractions. S. thermosulfidooxidans was more sensitive to the pulp density in comparison to At. ferrooxidans as a reduction in sulphide oxidation was observed with the increase in the solid content to 6%. Therefore, the mesophilic strain was selected for further work, which comprised a rolling bottle experiment at 10% solids. After 40 days of bio-oxidation, the solid material was subjected to cyanidation, which revealed 85% gold extraction as compared to 21% from the original concentrate. The antimony sulphide grains in the bio-oxidized product showed similarity to what was observed in the original sample, suggesting such particles were not susceptible to the bio-oxidation process.

By James R. Myers

A source of clean gas containing sulfur dioxide and sufficient oxygen for conversion to sulfur trioxide is essential to the production of sulfuric acid. SO2 containing gases obtained from roasting sulfide ores are heavily contaminated with inorganic dust and volatile impurities. If not removed, these contaminants will reduce product acid quality, foul the catalyst beds and mist eliminators, and accelerate equipment corrosion. This paper reviews conventional gas cleaning systems for metallurgical acid plants, followed by a discussion of modern systems utilizing DynaWave Scrubber technology. This technology is based on a unique approach togas scrubbing that can concurrently accomplish several gas cleaning/processing tasks. Scrubbing liquid is injected into the gas stream to create a "Froth Zone". This is a region of extreme turbulence, with a very high rate of liquid surface renewal. It efficiently removes both particulate matter and gas contaminants, and is also a cost effective quenching device for gases as hot as 1250 o C.

Jan 1, 1992

By Oszkar Bíró, Peter Mittag, Bernhard Aigner, Stefan Pirkeri, Philipp Glttleri

"This paper considers CFD modeling of processing and melting of small metallic particles by means of electrical heating. The particles fall continuously onto a liquid metal bath which is heated by an electric arc. After melting of the particles liquid metal is tapped.The charging behavior of the particles in the supply unit as well as in the reactor freeboard is studied by means of Euler-Euler granular simulations. The flow situation in the metal bath due to gas injection and magnetic fields is calculated by combining Navier-Stokes and Maxwell solvers. The macroscopic melting process occurring during the continuous charging of the particles is studied by kinetic laws for melting reactions. The temperature field is evaluated by balancing heat sources due to Joule's heating and heat losses due to latent heat of melting as well as convection and radiation.As a result of these simulations the fully three-dimensional flow fields of particles and gas in the atmosphere is obtained. Furthermore the flow field as well as the magnetic field in the metal bath can be studied. As a main result the three-dimensional concentration field of the still unsolved particles in the liquid metal can be evaluated.IntroductionIn this paper a metallurgical process for melting small iron particles is investigated by means of CFD-simulations. In a first process step the preheated and already mostly reduced iron particles fall continuously into the reactor through a vertical tube mounted at the lid of the furnace. In a second step the particles are melted in the liquid metal bath. Meanwhile the melt is heated by electric arcs to provide the heat needed for melting the incoming particles.In Figure I a sketch of the geometry setup considered in this paper is provided. The particles fall from a height of approximately 12 meters onto the bath surface in the center of the furnace. The melt is heated by electric arcs that are placed symmetrically around the center axis."

Jan 1, 2001

By R. C. Chaturvedi, S. B. Padwal

"Padwal and Chaturvedi have developed the model based on M-K theory, considering Hosford's yield criterion and critical thickness strain criterion"" to predict the sheet metal forming limits under simple (constant) strain ratio paths. This analysis has been extended in this paper to predict the sheet metal forming limits under complex strain paths. The effects of exponent ""a"" in Hosford's yield criterion and strain paths on the forming limits under complex strain paths are studied using this analysis. The predictions of the present analysis are compared, both for simple and complex strain paths, with experimental results of Ishigaki for A.K. steel and also with the predictions of Rao and Chaturvedi's model. The quantitative analysis of the error in predicting the forming limits has also been carried out using a method suggested by the authors earlier.1. INTRODUCTIONThe constant strain ratio condition has been assumed in the theories developed for prediction of forming limit diagrams (FLO). In actual forming operation, this condition is seldom satisfied. Even in the case of simple single stage press formed components, the strain path becomes curved and non-linear. In the case of pressings with complex shapes, or multiple stages of forming, the changes in strain path are more pronounced and even abrupt.Experimental study of the forming limits, under two stage strain paths, by Ishigaki [1], has shown that the forming limits are path dependent. It has been observed that the forming limits lower than that under simple strain paths, may be obtained under certain strain paths (when the first stage strain path is either equibiaxial tension or uniaxial tension, followed by the second stage strain path as plane strain). Rasmussen's work [2J, on the theoretical study of forming limits under curvilinear strains paths, has shown that a large drop in formability can result from very small changes in strain path. Thus if a deformation process gives rise to failures due to plastic instability, the failure is not necessarily due to insufficient formability of the material. In such cases, FLOs based on constant strain ratio path should not be used directly in predicting the success or failure of the forming operation. Thus the knowledge of forming limits under complex strain paths is of great importance to the interpretation of press-shop problems."

Jan 1, 1994

By K. S. Han, M. Yoshimuura, H. Fujita, Y. Sato, S. W. Song

"Film of LlCoO2 as cathode material for rechargeable lithium microbatteries has been fabricated on the platinum metal substrate by electrochemical-hydrothermal method in concentrated LiOH solution at 200 °C as Soft Solution-Processing. The film fabrication has been understood in terms of dissolution of cobalt metal powders and subsequent oxidative deposition on the substrate. The film structure was characterized using scanning electron microscope, X-ray diffraction analysis; X-ray photoelectron spectroscopy and micro-Raman spectroscopy.IntroductionRapid growth of wireless communications and emerging integrated optoelectronic circuits caused the miniaturization· cif electronic devices, thus the demand for high energy density microbatteries as a power source for the microelectronics increases. In this regard, all solid-state lithium microbatteries including LiCoO2 and LlMn2O 4 [l-4], the most promising intercalation cathode material, have been developed. However, major difficulty of .fabrication of a lithium microbattery arose from the preparation of cathode film, according to a· recent report on Rare Metal News [5]. Although many attempts have been made to deposit the cathode films, all those methods are mostly chemical vapor deposiiton (CVD), various evaporation, sputtering techniques and spray pyrolysis. These methods require preparation of bulk cathode materials cir its precursor, then deposition with complicated instruments including high· vacuum system, and even postsynthesis annealing to obtain desire electrochemical 'properties. It is clear that all of these techniques are neither economic nor environmentally friendly. Compared to those methods, film form.ation from an aqueous solution is thought to be simpler and more economical, and requires much· less energy consumption. Our .group has demonstrated the utility of Soft SolutionProcessing [6,7], which is defined as environmentally friendly processing using (aqueous) solutions, to produce films of a variety of functional solid materials. According to the Pourvaix's diagram [8], some metal can be dissolved in an alkaline solution and consequently combined with hydroxyl group or oxygen anion forming metalate or metalite. Cobalt also seemed to form cobaltite, HCoOi in strong alkaline solution in the Pourvaix's pH-potential diagram. Based on this information, it was expected that LiCoO2 could be prepared using the cobalt metal in Li OH solution by Soft Solution-Processing. Recently, we reported the successful single step fabrication of electrochemically active LlCoO2 films on the cobalt metal substrate by hydrothermal methods without any post-synthesis annealing as Soft SolutionProcessing [9,10]. Film formation mechanism could be elucidated by the following evidences. . As expected from Pourvaix's diagram, cobalt metal was dissolved in concentrated LiOH solution forming dissolved cobalt species which was detected by an observation of absorption band in UV-VIS absorption spectrum [10]. Thus the reaction was assumed to be started from dissolution. Time dependent potential of Co electrode exhibited only one-step evolution with 0.6 eV from Co metal to LiCoO2 [10]. Another strong evidence was the finding of LiCoO2 powder precipitates at the bottom of tetlon beaker after the reaction [11]. Based on those experimental findings, it was understood that film is formed by dissolution-precipitation mechanism [9-11]."

Jan 1, 2000

By Chikabumi Yamauchi, Mitsuru Tanahashi, Tsuyoshi Taniguchi, Nobuo Furuta, Toshiharu Fujisawa

"It is essential to clarify the equilibrium relations among nonmetallic inclusions of the Mn0-SiO2-CrOx system and molten stainless steel in order to control non-metallic inclusions formed by the deoxidation of stainless steel with silicon. In the present study, the phase equilibria of the MnO-SiO2-CrOx system were measured by conducting the following experiments under controlled oxygen partial pressure, Po2, at 1873 K:1) Phase equilibria of the MnO-Cr20 3 binary system were measured for Po2 = 2 x 10-6 ~2 x 102 Pa.2) Phase equilibria of the MnO-SiO2-CrOx ternary system were measured for Po2 = 2 X 10-6 Pa.Based on the results, the phase diagram of this ternary system was established under the condition of the Si-deoxidation process of stainless steel (Po2 = 2 x 10-6 Pa and T = 1873 K).IntroductionAt the deoxidation stage in steelmaking process, generally multiple deoxidizers participate in deoxidation reactions, and the composition of deoxidation products ""non-metallic inclusions"" greatly varies depending on deoxidizing efoments and their contents. In order to control non-metallic inclusions formed by the refining process of steel, it is essential to clarify the equilibrium relations among non-metallic inclusions and molten steel.Especially, during the refining process of stainless steel, nonmetallic inclusions in molten steel seem to- change as follows. After the oxidation refining, Mn-chromite is formed in molten steel as non-metallic inclusion. By the deoxidation with silicon addition (mainly less than 1 mass%), Mn-chromite inclusions are changed their compositions to Mn-silicate. Segawa et al.[l] have reported the effect of amount of silicon addition on composition and mass ratio· of non-metallic inclusions during the Sideoxidation process of 18Cr-8Ni stainless steel at 1873 K, as shown in Figuri; L At higher silicon content than 0.5 mass%, only Mn-silicate was identified as non-metallic inclusion. On the other hand, at lower silicon content, both of Mn-chromite (MnO Cr2O 3) and Mn-silicate were identified. However, the thermodynamic and the kinetic analyses of the above-mentioned Sicdeoxidation process have not been made due to lack in the thermodynamic data for the non-metallic inclusions· of the MnO-SiO2-CrOx system, such as the phase diagrams, the activities of the components, and the free energy of intermediate compounds. In relation to the phase diagram of this system, those of the MnO-SiO2 [2] and the SiO2-Cr2O 3 [3] binary systems have been only reported"

Jan 1, 2000

By U. Meyer, A. Alonso, P. Banios

The sampling of cathodes has changed with the introduction of the ISA-process in copper refineries. A Jernkontoret joint working group of refineries and rod plants from both primary and recycled copper plants has been investigating whether the actual sampling of cathodes is representative for this type of cathodes. As a first stage, samples were sent to the members of the working group with the objective to find an easy basis for a comparison of the results of the next stages. All samples show the same tendency for nearly all elements. In some cases, there may exist differences in calibration and for some elements the detection limits are too high, especially when Optical Spectrometry is used. In the second stage, discs were compared with melted samples to answer the question whether the punching of discs is sufficient for the quality control of the cathode. The analyses of the discs represent fairly well the cathode quality. There are differences between cathodes from different crops. Three punches are sufficient to determine the cathode quality. Finally, samples from various lots of cathodes were compared with samples from the rod produced from these cathodes. The impurity content of the rod corresponds to the impurity content of the cathode.

Jan 1, 2000

By Zhihe Dou, Zimu Zhang, Guozhi Lv, Yan Liu, Xiaoli Jiang

"Cyclic heat stewed slag washing water carries high content of alkali and calcium and may cause serious tube scaling and impose an adverse impact on normal production. This study proposes a solution to utilize washing water by absorbing and mineralizing CO2, potentially restraining scaling and being able to create calcium carbonate powders. Effects of water flux on water quality, utilization ratio of CO2 and yield of calcium carbonate powder have been investigated; meanwhile, features of calcium carbonate powder are also represented. On the other hand, effects of factors such as as injection flux, pressure of CO2 on utilization ratio of CO2, morphology and purity of calcium carbonate are also investigated. The results show unambiguously that after soften injection of CO2, calcium ions were removed effectively via precipitation, alleviating the scaling problem. High purity yet fine carbonate powder could be achieved.IntroductionNowadays, 0.34 tons of blast furnace slags will be produced when producing 1 ton of pig iron; ensuing that, 0.12 tons of steel slag will be generated with 1 ton steel production while 1.57 billion tons of steel output all over the world in the year of 2012. It is therefore a critical issue to realize zero discharge of steel slags to achieve sustainable development and cyclic economy of iron and steel industry. In recent years, research institute of MCC and China JINGYE engineering company developed a heat stewed steel slag self-decomposition technology GENERATION III to solve the problem of instability of steel slags and realize the zero discharge. However, the problem of circulation line scaling which may cause the clogging, even exploding, need to be solved. The principles of the technology are: directly spraying water to the high temperature steel slag when it is poured into the hot closed pot, realizing the selfdecomposition via utilizing the waste heat of steel slag. The washing water is recycled to achieve a cyclic utilization. The process is shown in Figure 1."

Jan 1, 2014

By E. A. Werner, A. Pichler, A. Spalek, G. Reisner, P. Stiaszny

"Interstitial free (IF) sheet steels are used for complex shaped parts because of their excellent formability. If a deep drawn part is subjected· to a impact deformation at low temperature brittle fracture of the part may occur. This phenomenon\ is called secondary work embrittlement (SWE). One possibility to characterize this material/structural behavior is the drop-weight test. The result of .this .test is a temperature at and below which a crack can initiated in a deep drawn part under the investigated set of parameters. This paper addresses the influence of the preforming process on the sus- . . ceptibili.ty of IF steels to SWE.IntroductionInterstiiial:free (IF-) steels are frequently used in the automotive industry for complex· shaped p·arts because of their excellent deep drawability. The microstructure of the steel consists of a highly ductile ferritic matrix with embedded precipitates of nitrides and/or carbides. Brittle fracture can occur in deep drawn parts, if they are subjected to a high speed deformation at lo""w temperature. This phenomenon is called ~econdary Work gmbrittlement (SWE) [1-11]. Up to now there are no standardized testing procedures available to quantify the sensibility of IF-sheet steel to SWE. Neveitheless, a reasonable testing procedure which allows to quantify the tendency of a predeformed part to SWE is necessary for further material development. A commonly used test method is the drop-weight test performed at low temperatures. In such ·tests a cone-like drop weight expands a deep drawn cylindrical cup [l-3, 6, 8, 9, 11]. From this expansion experiment the temperature is determined at and below which a brittle crack can be initiated in the deep drawn cup under the investigated impact test parameters. The highest measured temperature at which a deep drawn cup fails by brittle fracture is called frack appearances !emperature (CAPT). The lower the value of the CAPT the lower is the sensibility of a deep drawn part of IF-sheet steel to SWE. This paper aims to clarify the role of the preforming process on the impact behavior of an IF steel. For this purpose a numerical analysis of the deep drawing process and cup expansion tests are conducted."

Jan 1, 2000

By Kazuyuki Kakegawa

"Sintered body of lead zirconate titanate (PZT) was prepared through the spark plasma sintering (SPS) technique. When the mixture of raw materials was calcined at 800°C and sintered at 900°C for 10 min. with SPS technique, the sintered body had almost theoretical density but was a mixture of lead titanate (PT) and PZT. When a calcining temperature of 1100°C was employed, sintered body had a single PZT phase but a lower density. High dielectric constant was obtained for a sample calcined at 800°C, sintered with SPS tecbriique and fired again in the air at 1100°C.IntroductionSpark plasma sintering (SPS) is a recently developed technique for sintering metals and ceramics1. The scheme of SPS is shown in Fig. 1. Sample is put in a graphite die in a vacuum chamber. It is pressed and pulse voltage is applied. The electric current heats the die. It is said that the pulse causes a spark-plasma between particles in the sample. Because of the spark- plasma, sample can be sintered at temperatures lower than that in the ordinary sintering by several hundred degrees of Celsius. The sintering period is also very short2Low sintering temperature and short sintering period in SPS technique cause low reaction rate. It is both disadvantage and advantage. In some cases, the reaction cannot be completed under the SPS conditions. If a mixture of several compositions having different properties can be sintered without a compositional change by the diffusion during the sintering, combination of properties, and therefore a design of property will be possible3. The low reaction rate of SPS may enable such combination."

Jan 1, 2000

By Saskia Duyvesteyn

For many applications in hydrometallurgy and water treatment it would be advantageous to use ion-exchange resins in stirred reactors. However, attrition of the resin may lead to significant losses of both resin and metal values and prevent water quality goals from being reached. We have studied the recovery of fine resin particles by froth flotation, using the model copper - Dow XFS4195 chelating resin system. As the functional group on the resin is a bis-picolylamine, the resin should be amenable to flotation by anionic collectors, such as sodium dodecylsulfate and sodium dodecylsulfonate. The kinetics of copper loading from dilute aqueous solutions in an agitated vessel were studied as a function of copper concentration, pH and resin bead size. The flotation of unloaded resin was investigated for different types of collector, collector concentration, conditioning time, and resin bead size. Potential applications are discussed.

Jan 1, 1995

By R. J. Mitchell

Results from investigations into impurity distributions over cathodes are presented with implications for various sampling methods, Selection of an optimum treatment procedure for the test sample is outlined. The impact of both these studies on the development of an in-house method for sampling Isa Process cathode is discussed. The economic compromise actually undertaken, satifying wants and needs to sustain confidence in high grade cathode purity is detailed.

Jan 1, 1987

By Yongqi Sun, Zuotai Zhang

Our study investigated the influence of P2O5 and B2O3 on the viscosity and crystallization behavior of Ti-bearing blast furnace (Ti-BF) slags for the purpose of Ti extraction. The investigation of the crystallization behaviors were carried out using a single hot thermocouple technique (SHTT) and the viscosity was obtained by rotating cylinder method. For the viscosity, the results showed that P2O5 substantially increased the slag viscosity. P2O5 is a network-forming oxide, which increased the degree of polymerization of slags and accordingly increased the slag viscosity. However, both of slag viscosity and apparent activation energy for viscous flow remarkably decreased with B2O3 addition. As a typical network forming oxide, B2O3 was introduced into the network and existed dominantly as 2-D structure, BO3 triangular, which caused a simpler structure and a decreasing slag viscosity. As for the crystallization behaviors of Ti-BF slags, both P2O5 and B2O3 enhanced the crystallization trend of rod-shape rutile and suppressed the crystallization trend of dendrite CaTiO3. Therefore the added P2O5 and B2O3 caused the primary phase change from CaTiO3 to rutile. Additionally, it was found that the rod-shape rutile showed a 1-D growth, whereas the dendrite CaTiO3 showed a 3-D growth style.

Jan 1, 2015

By R. W. Lawrence

A high rate biological reduction technology has been developed to provide low cost hydrogen sulphide for various uses in water treatment and metallurgical processes. Commercial operations produce sulphide safely at a fraction of the cost of chemical sulphide. The biologically produced H2S is used for treatment of acid wastewater and selective metal recovery whereby metals present in wastewater streams are recovered in high grade metal sulphide concentrates that are sold to smelters. The combination of biological H2S production and selective metal recovery is currently marketed under the process name BioSulphide-Thiopaq. The process can be applied on a stand-alone basis or in conjunction with a conventional lime water treatment. Process advantages include: reduced lime treatment costs, reduced volume of waste sludge free of toxic metals leading to reduced long term environmental liabilities, selective recovery of metals and, in some cases, net profit from water treatment achieved through the sale of metal concentrates. Three case studies are presented to provide examples water treatment and metal recovery: the Caribou Mine, New Brunswick; the Phelps Dodge Bisbee operations, Arizona; and Falconbridge?s Raglan nickel mine in Quebec. A fourth case study is presented to highlight environmental control for treatment of ARD in the Leadville mining district of Colorado. Process flowsheets, capital and operating costs are presented for the four case studies

Jan 1, 2003

By Travis Knight

Mixed uranium and refractory metal carbide systems have been proposed for space nuclear power and propulsion applications. Solid-core space nuclear reactors could be utilized for low- earth-orbit (LEO) to geosynchronous-earth-orbit (GEO) transfers, manned missions to the moon or mars, and orbiter missions to the outer planets. However, these high performance space nuclear reactors present some challenging materials engineering requirements for operating in a high temperature, high radiation, and hot hydrogen environment. Since the RoverNERVA programs were concluded in 1973, significant advances in ultrahigh temperature materials technology have been made which can be applied to the development of an advanced solid-core nuclear fuel. Nuclear thermal propulsion (NTP) was first studied in the U.S. beginning in the mid-1950's during the RoverNERVA programs. During that time, about 20 rocket reactors were built and tested. More recently, Russian nuclear rocket reactor tests with pseudo-ternary carbide nuclear fuels (U, Zr, Nb)C and (U, Zr, Ta)C have been operated at temperatures as high as 3300 K for one hour. This study examined the processing parameters for fabricating the pseudo-ternary carbide, (U, Zr, Nb)C.

Jan 1, 1999