By J. W. Halley

THE effects of tin on steel have become increasingly important because of the necessity of using poorly detinned scrap, tin cans, and terne plate, in the open hearth. Since a tin can contains about 1.5 per cent tin, it would be possible to have up to 0.75 per cent tin in steel made with a 50 per cent scrap charge. In order to use tin-containing scrap, it is necessary to know the effect of tin on various grades of steel. The following investigation is by no means comprehensive but covers a number of steels in which tin content is important. PUBLISHED WORK A number of investigations of the effects of tin on rolling quality and physical properties have been published. It has been found that tin increases strength and hardness and reduces ductility and notched impact resistance. The decrease in ductility and notched impact resistance becomes more marked as the carbon decreases. McKimm1 found no change in Olsen ductility, Rockwell hardness, yield strength, tensile strength or elongation in cold-reduced strip containing up to 0.124 per cent tin. A tin content of 0.15 per cent gave difficulties in rolling and increased the hardness but 0.21 per cent tin showed no change in properties from material containing very little tin. No explanation of this contradiction is offered. Andrew and Peile2 investigated steels containing 0.01 to 0.25 per cent carbon and up to 0.63 per cent tin. They found an increase in tensile strength of from 100 to 200 lb. per sq. in. for each 0.01 per cent tin on normalized samples. The elongation and reduction of area were decreased and the notched impact resistance was reduced markedly. Quenched and drawn samples did not show embrittling if water-quenched from the draw temperature of 1148°F. (620°C.). They could find no evidence of tin under the microscope. Whitely and Braithwaite3 investigated the effect of tin on rail steel containing 0.55 to 0.06 per cent carbon. They found that 0.08 per cent tin caused a marked decrease in elongation, notched impact resistance and the degree of bend. The tensile strength was increased in some tests and not in others. Bolsover and Barraclough4 investigated the effect of tin up to 0.50 per cent on a 0.35 per cent carbon steel and on several alloy steels with from 0.30 to 0.40 per cent carbon. They found a comparatively uniform decrease in notched impact resistance with increasing tin on quenched and drawn samples. If the samples were quenched from the drawing temperature or reheated to the drawing temperature and quenched, the embrittling was much less severe. Steels containing molybdenum suffered much less embrittlement than other steels. EXPERIMENTAL WORK Effect of Tin on Low-carbon Rimmed Steel Increasing quantities of tin were added to four ingots of a heat of the following ladle analysis: carbon, 0.08 per cent; manganese, 0.39; phosphorus, 0.009; sulphur, 0.025.

Jan 1, 1942

By J.W. Halley

The effects of tin on steel have become increasingly important because of the necessity of using poorly detinned scrap, tin cans, and terne plate, in the open hearth. Since a tin can contains about 1.5 per cent tin, it would be possible to have up to 0.75 per cent tin in steel made with a 50 per cent scrap charge. In order to use tin-containing scrap, it is necessary to know the effect of tin on various grades of steel. The following investigation is by no means comprehensive but covers a number of steels in which tin content is important. Published Work A number of investigations of the effects of tin on rolling quality and physical properties have been published. It has been found that tin increases strength and hardness and reduces ductility and notched impact resistance. The decrease' in ductility and notched impact resistance becomes more marked as the carbon decreases. McKimml found no change in Olsen ductility, Kockwell hardness, yield strength, tensile strength or elongation in cold-reduced strip containing up to 0.124 per cent tin. A tin content of 0.1j per cent gave difficulties in rolling and increased the hardness but 0.21 per cent tin showed no change in properties from material containing very little tin. No explanation of this contradiction is offered. Andrew and Peile2 investigated steels containing 0.10 to 0.25 per cent carbon and up to 0.63 per cent tin. They found an increase in tensile strength of from 100 to 200 lb. per sq. in. for each 0.01 per cent tin on normalized samples. The elongation and reduction of area were decreased and the notched impact resistance was reduced markedly. Quenched and drawn samples did not show embrittling if water-quenched from the draw temperature of 1148°F. (620°C.). They could find no evidence of tin under the microscope. Whitely and Braithwaite3 investigated the effect of tin on rail steel containing 0.55 to 0.60 per cent carbon. They found that 0.08 per cent tin caused a marked decrease in elongation, notched impact resistance and the degree of bend. The tensile strength was increased in some tests and not in others. Bolsover and Barraclough4 investigated the effect of tin up to 0. 50 per cent on a 0.35 per cent carbon steel and on several alloy steels with from 0.30 to 0.40 per cent carbon. They found a comparatively uniform decrease in notched impact resistance with increasing tin on quenched and drawn samples. If the samples were quenched from the drawing temperature or reheated to the drawing temperature and quenched, the embrittling was much less severe. Steels containing molybdenum suffered much less embrittlement than other steels. Experimental WoRk Effect of Tin on Low-carbon Rimmed Steel Increasing quantities of tin were added to four ingots of a heat of the following ladle analysis: carbon, 0.08 per cent; manganese, 0.39; phosphorus, 0.009; sulphur, 0.025.

Jan 1, 1943

By J. W. Halley

The effects of tin on steel have become increasingly important because of the necessity of using poorly detinned scrap, tin cans, and terne plate, in the open hearth. Since a tin can contains about 1.5 per cent tin, it would be possible to have up to 0.75 per cent tin in steel made with a 50 per cent scrap charge. In order to use tin-containing scrap, it is necessary to know the effect of tin on various grades of steel. The following investigation is by no means comprehensive but covers a number of steels in which tin content is important. Published Work A number of investigations of the effects of tin on rolling quality and physical properties have been published. It has been found that tin increases strength and hardness and reduces ductility and notched impact resistance. The decrease' in ductility and notched impact resistance becomes more marked as the carbon decreases. McKimml found no change in Olsen ductility, Kockwell hardness, yield strength, tensile strength or elongation in cold-reduced strip containing up to 0.124 per cent tin. A tin content of 0.1j per cent gave difficulties in rolling and increased the hardness but 0.21 per cent tin showed no change in properties from material containing very little tin. No explanation of this contradiction is offered. Andrew and Peile2 investigated steels containing 0.10 to 0.25 per cent carbon and up to 0.63 per cent tin. They found an increase in tensile strength of from 100 to 200 lb. per sq. in. for each 0.01 per cent tin on normalized samples. The elongation and reduction of area were decreased and the notched impact resistance was reduced markedly. Quenched and drawn samples did not show embrittling if water-quenched from the draw temperature of 1148°F. (620°C.). They could find no evidence of tin under the microscope. Whitely and Braithwaite3 investigated the effect of tin on rail steel containing 0.55 to 0.60 per cent carbon. They found that 0.08 per cent tin caused a marked decrease in elongation, notched impact resistance and the degree of bend. The tensile strength was increased in some tests and not in others. Bolsover and Barraclough4 investigated the effect of tin up to 0. 50 per cent on a 0.35 per cent carbon steel and on several alloy steels with from 0.30 to 0.40 per cent carbon. They found a comparatively uniform decrease in notched impact resistance with increasing tin on quenched and drawn samples. If the samples were quenched from the drawing temperature or reheated to the drawing temperature and quenched, the embrittling was much less severe. Steels containing molybdenum suffered much less embrittlement than other steels. Experimental WoRk Effect of Tin on Low-carbon Rimmed Steel Increasing quantities of tin were added to four ingots of a heat of the following ladle analysis: carbon, 0.08 per cent; manganese, 0.39; phosphorus, 0.009; sulphur, 0.025.

Jan 1, 1943

Theo. B. ComstocK, Los Angeles, Cal. (communication to the Secretary*):—Mr. Blake's recent paper upon this topic undoubtedly partly explains the rationale of a part of the known facts bearing upon discolorat'ion and encrustation of rocks. His quotation from Humboldt, with reference to certain South American examples, may be questioned in the light of further facts, which do not appear to bear out the great traveler's theory of causation. There is no available evidence that the waters of the tropical rivers referred to by Professor Blake contain dissolved organic matter in the varying proportions required to demonstrate Humboldt's guess, nor do the concomitant facts in any manner bear out the hypothesis that the blackening in one case and its absence in the other may, perhaps, be traced to differences in the chemical reactions of the respective waters. Careful consideration of Professor Blake's illustrations, in connection with numerous personal observations extending over widely-scattered areas, convinces me that elements of

Jan 1, 1905

By James Boyd

THE Bureau of Mines for a number of years has been seeking additional ways and means of improving the efficiency of its operations and increasing its service to the public. It has become obvious that changes in the organization of the Bureau are essential to a more effective accomplishment of its functions and objectives. The old organization was defective in meeting current needs in that the Bureau's field activities were neither sufficiently coordinated with the national program nor were they particularly responsive to local needs of the mineral industries. Further, the traditional organization hampered the efforts of the Bureau to obtain, analyze and provide to the policy-making agencies of the Government essential information and advice in such a form that the requirements of domestic industry could be fully taken into consideration in the development of domestic and foreign policies. Consequently, the Bureau has now modified its organizational structure.

Jan 1, 1949

By Robert Glass Cleland

UPON the death of its founder, Phelps, Dodge & Co. entered upon a new chapter in its long and varied history. Thereafter, for nearly a decade, William E. Dodge largely determined and executed the policies of the company. The old firm, dissolved automatically by Phelps's death, was succeeded by a new partnership consisting of Anson G. Phelps, Jr., William E. Dodge, Daniel James, James Stokes, William E. Dodge, Jr., and D. Willis James, one of the three sons of Daniel James. Each of the first three partners owned a twenty-five-per-cent interest in the company, Stokes had a fifteen-per-cent interest, and the two younger partners each held five per cent. The new company bought Anson Phelps's holdings in the old firm from Olivia Phelps, his widow and executrix, for approximately seven hundred thousand dollars; but the new partnership, designed by agreement to last the usual five-year period, was brought to an end shortly before that time by the death of the younger Anson Phelps from small- pox. Perhaps because of poor health, the son had never been as deeply concerned with business as his father, but found

Jan 1, 1952

By Verne C. Fryklund, S. Warren Hobbs

The Coeur d'Alene district in the panhandle of Idaho is one of the major lead-zinc-silver producing areas in the world. The value of recorded production to date has exceeded $2 billion. Country rock comprises six formations of the fine-grained, highly siliceous, and slightly metamorphosed Precambrian Belt Series. Small stocks of monzonitic rocks and several varieties of dikes intrude the sediments. The district is at the intersection of a north trending major anticlinal uplift and the west northwest-trending Lewis and Clark line of which the Osburn fault is the dominant feature. The district structure is complicated and comprises folds, some of which are overturned, and a complex of faults of diverse ages and directions of movement. Late Cretaceous stocks but are also probably Cretaceous in age. The productive veins are localized within a series of 12 subparallel, straight mineral belts that trend approximately N65°W and that appear to be controlled by deep fractures in the basement rocks. The mineral belts are in two groups, separated by 15 miles of post-mineralization movement on the Osburn fault. Veins and ore shoots are variously disposed within each mineral belt. Many crop out at the surface, but others apex several thousand feet beneath it. Local controls that influence the position of ore shoots within the mineral belts include the brittle character of host rock attitude of bedding relative to the mineralized fracture, and the amount and direction of movement on faults. Depth appears to have had little effect on the occurrence or type of ore. Ore occurs in a series of steeply dipping replacement veins of relatively simple mineralogy. Six periods of mineralization, ranging from Precambrian to Tertiary in age, are recognized. The productive galena sphalerite-bearing and tetrahedrite-bearing veins-of the main period of mineralization-are younger than the

Jan 1, 1968

By C. A. Stickels

In a recent paper, Held1 showed that rolling conditions can have a marked effect on the volume fraction of surface texture produced in low-carbon steel. This variation in rolling texture is reflected in the recrys-tallization texture and affects the plastic properties of the annealed sheet. The fact that roll friction can influence the surface deformation texture in iron and steel has been known for some time;'= but the magnitude of the effect has never been shown quite so clearly before. The analogous effect during wire drawing has been recognized for many year.4 Dillamore and Roberts5 examined surface textures in warm- and cold-rolled aluminum and copper. They found that when a surface texture was present it could be described as the interior texture rotated about the transverse sheet direction. The angle of rotation was a function of the type of lubrication, the amount of reduction per pass, and the temperature of rolling. The purpose of the present note is to show that surface textures in cold-rolled iron can also be described as interior textures rotated about the transverse sheet direction. Vacuum-melted electrolytic iron* was straight- rolled 90 pct at room temperature in a two-high rolling mill with 5-in.-diam rolls. Two rolling procedures were used: a) no lubrication with reductions of about 0.035 in. per pass, and b) heavy lubrication with lano-line and reductions of about 0.002 in. per pass. The final sheet thickness was 0.030 in. (110) pole figures were determined by transmission through specimens taken from the sheet surface and sheet midplane. The surface texture of the sheet cold-rolled according to procedure a is shown in Fig. l.* The shapes of the low-intensity contour lines indicate that the texture can be described as a partial fiber texture with a (110) fiber axis normal to the sheet. The approximate range of orientstions present is (011)[211] — (0ll)[100] — (011)[211]. This range of orientations is what one would obtain by rotating the interior texture 90 deg about the transverse sheet direction. The intensity of (110) and (222) reflections from planes parallel to the surface was measured after removing metal from the surface by chemical polishing. The surface texture here was confined to the outer

Jan 1, 1968

By H. E. Cline

Solidification of Pb-Sn alloys ranging in composition from 1.2 to 56 at. pct Pb ws observed with polarized light. Lamellar structures were observed over a larger range of compositions in alloys containing excess tin than excess lead, as expected from constitutional supercooling. The occurrence of pools of supercooled liquid surrounded by lead is explained by the difficulty in nucleating tin. Cells and dendrites weve observed in tin-rich alloys. Evidence was found that the degenerate structure formed at low growth rates, the formation of faults, and abrupt changes in composition and structure can be attributed to non-steady-state growth. The apparent interface shape was observed to have deep grooves at the interphase boundaries. HUNT and Jackson have observed the shape of the interface during growth of organic eutectics. They observed the formation of lamellar faults and shape instabilities upon changes in growth rate. The lamellar structure in these organic eutectics was not restricted to the eutectic composition. Recent work by Mollard and Flemings2 indicated that Pb-Sn alloys from 12 to 26 at. pct Pb could be solidified with a lamellar or rodlike structure if a sufficiently steep temperature gradient was used at a slow growth rate. Observations of the solid liquid interface of the Pb-Sn eutectic were made by Davies3 using polarized light. Photographs were at too low a magnification to determine the interface shape, but he has concluded that tin was the leading phase. In the following experiments, solidification of a range of Pb-Sn alloys from 1.2 to 56 at. pct Pb was observed using polarized light, to determine the factors controlling stability of the lamellar structure. EXPERIMENTAL Procedure. One hundred-gram ingots of alloys prepared from 99.999 pct pure Pb and Sn were cast into graphite molds under argon. The compositions of the alloys were 1.2, 6, 12, 26, 36, 46, and 56 at. pct Pb. Two-gram pieces were melted between two cover glass slides which were squeezed into a 1-mm separation. Samples were then observed under polarized light in a hot stage shown in Fig. 1. A long working distance objective designed for viewing at 500 times was used. Photography was made difficult by the lack of illumination and contrast at these high magnifications. By using an elliptical polarization compensator, as suggested by A. Holik, the contrast and illumination could be optimized. Photographs could be taken only at slow growth rates to avoid excessive interface motion during the 15-sec exposure used. The solidification rate was varied by increasing or decreasing the power to the heater. It was found that insulation was necessary to avoid undesired growth rate fluctuations. The temperature gradient, as measured with two thermocouples 1 cm apart, was 80" ± 20°C per cm during all the experiments reported here. The advantage of this procedure is in being able to observe solidification while it is occurring. However, the observations are restricted to the glass-metal surface and may be influenced by this surface. Also, one has no knowledge of the interior of the sample, in contrast to studies of the freezing of transparent organic eutectics.' Observations. The alloy near the eutectic composition (26 at. pct Pb) solidified in a lamellar structure when the growth rate was uniform. If the growth

Jan 1, 1968

By F. N. Rhines, A. S. Nemy

The mode of high-temperature tertiary creep of 523-0 aluminum alloy was found to be strongly stress dependent. The occurrence of necking and/or fissures during tertiary creep exhibited a sequence with varying stress, wherein fissures with no necking occur at a minimum stress and necking with no fissures occur at a maximum stress. At an intermediate stress, tertiary creep begins without necking but with fissures in a region just beneath the external surface, followed by necking and the development of fissures along the axis of the specimen. The results are interpreted in terms of grain boundary gliding and the hydrostatic stresses produced by restraints to grain boundary gliding. THERE appear to be two possible reasons for the existence of a period of accelerating elongation prior to rupture during high-temperature creep in metals; namely, 1) a change in the structure of the metal itself, leading to a change in its response to loading, and 2) a reduction in the cross section of the metal resulting in a higher unit loading. Howe,' by annealing and retesting broken low-temperature creep specimens, found that irreparable damage is done once a metal is subjected to creep. Andrade2 first pointed out the association between the reduction in cross section and the increase in creep rate. The present research was designed to investigate both of these factors by retesting specimens machined from material which had been subjected to high-temperature creep testing short of rupture. EXPERIMENTAL METHOD An aluminum alloy, 52s-0, was selected for these studies because it is constitutionally simple, is strong enough to be relatively insensitive to mechanical damage during machining,3 and undergoes accelerating creep in a convenient temperature range. This alloy is hardened by 2.6 wt pct Mg in solid solution and is not subject to overaging effects; it has a very small quantity of an insoluble impurity phase, Mg2Si, finely dispersed throughout its micro-structure. Creep specimens, similar in design to ASTM 0.252-in. tensile specimens, were machined from 3/4-in. round stock and the surfaces were electro-polished. A 24-hr anneal at 500°C was then applied to stabilize the grain size to an average diameier of 0.27 mm. Subsequent heating for as long as 700 hr at the intended test temperatures produced no change in the tensile properties, indicating a well-stabilized state of the material. Corresponding to each of the typical testing conditions listed in Table I, one creep specimen was tested to destruction and this test was employed as a guide in the selection of times for subsequent tests. Duplicate creep tests were then run to various points along the creep curve to produce specimens which were used to determine changes in mechanical properties and microstructures. The latter were examined at the midsections of the specimens. Other specimens were tested to various stages of tertiary creep, after which they were remachined to new cylindrical test specimens, electropolished and re-tested in creep. RESULTS The major findings of this investigation may be illustrated by a comparison of the results of three sets of creep tests. These were run at 400°C at three stress levels, namely 750, 1000, and 1500 psi. In presenting these results in Figs. 1, 5, and 8, the creep curves are given in pairs: That curve of each pair which is drawn through filled circles corresponds to the initial test, and the curve drawn through open circles (and designated by - R) represents the result of retesting the same specimen after machining to a new cylindrical surface. The load was readjusted to the original unit stress at the beginning of each retest.

Jan 1, 1960

By John G. Baragwanath

THE September issue of the Engineering and Mining Journal carried an item regarding the Cercapuquio Mining Co. which was mentioned as a large producer of lead, zinc, and cadmium, situated near Huancayo, Peru. The paragraph caught my eye because I had not heard of the property in thirty years and I recollect all too well the circumstances of its accouchement. In 1916 1 was making my headquarters in the town of Huancayo, then the terminus of the Central Railway of Peru, and was examining mines and prospects in that general area for Cerro de Pasco. In the course of my work I became acquainted with an engaging and energetic "practical" miner named Balarin, a Dalmatian living in Huan¬cayo, and made numerous trips in his excellent company. One day Balarin came to the down-at-heels hostelry where I stopped and told me that a Cholo prospector, a character by the name of Jose, had just reached town and claimed to have made a discovery in a little known locality called Cercapuquio. Lead-silver, Balarin said, and showed me a sample of galena about the size of his fist. "Fine," I remarked. "When do we leave?"

Jan 1, 1947

With the coming of the month of 'October the various sections are beginning active work for the winter. The Colorado, Washington, Montana, and New York Sections are all doing good work in raising funds for the hospital bed at Rheims which is to be a memorial to the members of the A. I. M. E. who gave their lives in the great war. We hope that all the other sections will begin to work with this object in view and will make even a better record than they did with the Belgian Relief Fund. It was with much regret that the President, Mrs. James F. Kemp, and the Secretary, Mrs. Sidney J. Jennings, were obliged to forego the pleasure of attending the Chicago meeting in September. They were, however, ably represented by Mrs. Arthur S. Dwight who gave an informal talk after which was formed the Illinois Section, which has our best wishes for all success-" Over the top and the best of luck!"

Jan 11, 1919

By T. Watanabe, S. Karashima, H. Oikawa

Creep tests of a! iron and its solid-solution Fe-Mo, Fe-Co, and Fe-Si alloys with bcc structure were conducted under constant stresses in ferromagnetic and paramagnetic temperature regions above 0.5T,(T, is the absolute melting temperature). It was found their high-temperature creep behavior changed in the vicinity of the magnetic transformation temperature, that is Curie temperature, TC. In the ferromagnetic region below the steady-state creep rates were lower than those expected from the extrapolation of the data in the paramagnetic region, the amount of decrease being affected by solute addition. Also, activation energies for steady-state creep were different in the two temperature regions. The observed changes were concluded to be due to the effect of ferromagnetism on diffusion. It is well-known that plastic deformation of metals and alloys in the temperature region where mobility of atoms becomes high enough is controlled by atomic diffusion." Many experimental results394 on fcc and hcp materials have been reported to confirm this view. In bcc metals and alloys, not much basic investigation of creep deformation has been performed. In particular, experimental work on iron5-&apos; and its alloys, covering a quite wide temperature range is extremely scarce. On the other hand, the effect of ferromagnetism on diffusion has recently been demonstrated in a iron and its alloys;&apos; it has been made clear that diffusion rates in ferromagnetic temperatur~e region are significantly lower than those expected from diffusion measurement in the paramagnetic region. Therefore, it is concluded that the magnetic effect influences the high-temperature creep behavior in a! iron and in its alloys. The present authors have conducted creep experiments on a iron and its solid-solution alloys over a very wide temperature range, and have demonstrated the magnetic effect. A part of the result has already been reported elsewhere.26 In this paper, the experimental results will be described in detail. While the manuscript was in preparation, a similar magnetic effect on creep deformation of a iron was reported by Ishida . Though their experiments covered an extremely wide temperature range, the creep stresses varied from several thousand psi to several ten thousand psi with decreasing temperature. Consequently, it may be said that there remain some questions concerning their results. I) EXPERIMENTAL PROCEDURE The materials used in the experiments were pure iron and its alloys; they were prepared by vacuum melting (10"" mm Hg) electrolytic iron (99.9 pct), molybdenum powder (99.9 pct), ultrapure silicon, and cobalt pellet (99.5 pct) in alumina crucibles. The ingots were hot-forged to plates 10 mm thick and 50 mm wide, and then were hot-rolled at about 700°C into sheets 1 mm thick. Creep specimens, 5 mm in width and 15 mm in gage length, were machined from the sheets. They were annealed at temperatures which were well above their respective recrystallization temperatures. The chemical compositions of the metal and alloys are shown in Table I together with their heat treatments. High-temperature creep tests by the use of a lever-type creep testing machine were carried out in argon atmosphere under constant tensile stress. In order to keep &eep stress constant within about *0.5 pct, stress change due to specimen elongation was compensated by tensile force of a stainless-steel bellows which was inserted between the loading lever and lower specimen grip with the assumptions of a linear relationship between change in cross section and strain and uniform strain along the section. Beyond the limit of compensation by the bellows, small amounts of load were removed after appropriate strains. The testing temperatures were maintained to within i2"C of the reported values. Creep deformation was auto-graphically recorded at the upper (moving) specimen grip using a linear differential transformer which was held by a stainless-steel rod mechanically connected to the lower specimen grip. It was also directly measured with a dial-gage reading to -& mm. 11) EXPERIMENTAL RESULTS AND DISCUSSION 1) Creep Curves of a Iron and Its Alloys. Creep curves of a! iron, Fe-Si, Fe-Co, and Fe-Mo (<2 at. pct Mo) alloys usually consisted of three stages, that is transient (primary), steady-state (secondary), and accelerating (tertiary) stages. An example is illustrated in Fig. 1 for a! iron. However, in Fe-Mo alloys with more than 2 at. pct Mo, an inverse transient creepZ8 was observed as indicated in Fig. 2. The inverse behavior, which varied with the amount of molybdenum, may be due to the substructure* in the annealed specimen as was sug-

Jan 1, 1969

By J. F. Smith

ELASTIC constants of yttrium and eleven of the rare earth elements have been measured. This has been accomplished by measuring the propagation velocities of ultrasonic pulses. The velocity measurements were made by noting the elapsed time between an applied pulse and the appearance of successive echoes. The pulse-echo technique has become relatively common, and the basis of the measurement is outlined in several standard tests, e.g., Heuter and Bolt.1 Two important assumptions are made when using this method for the determination of elastic moduli. First, the pulse is assumed to propagate as a plane wave. To justify this assumption, the cross section of the test specimen should be large compared to the wave length of the transmitted pulse. For these measurements on the rare earth elements the minimum cross section wave length ratio was about 20. A second assumption which must be made when using polycrystalline specimens is that the grains are sufficiently numerous and randomly oriented so that the specimen may be approximated as elasti-cally isotopic. The grain size in the as-cast specimens which were used is believed to be sufficiently fine for this approximation, and the degree of preferred orientation is believed to be small. Supporting this viewpoint is the fact that elasticity measurements by the pulse-echo technique on as-cast specimens of other metals give results which are in satisfactory agreement with values obtained by other techniques. Hence, it is believed that the measured elasticity values for the rare earth elements are not apt to be seriously in error due to the assumption of elastic isotopy. The apparatus used in this determination was a modified Sperry Reflectoscope with a precisely calibrated time base circuit. Piezoelectric transducers were used both to generate the pulse and to detect the echoes. X-cut quartz crystals were used for the longitudinal modes, and Y-cut quartz crystals were used for the shear modes. Frequencies of 2.25 and 5 megacycles per sec were employed. Most of the specimens were 2.5 to 5.0 cm in length. Results Table I is a tabulation of the measured propagation velocities of longitudinal waves and of shear waves, together with densities obtained by Sped- ding, Daane, and Herrmann2 from lattice parameter measurements. The shear modulus, Poisson&apos;s ratio, and Young&apos;s modulus were calculated from the data in Table I through use of the following relationships: µ = pv32 [1] s=2-(vb/vs)2/2[1-(vb/vs)2] [2] and Y= 2µ(l+s) [3] where s is the shear modulus, Y is the Young&apos;s modulus, s is Poisson&apos;s ratio, p is the density, V0 is the longitudinal wave velocity, and v, is the shear wave velocity. The calculated quantities are shown in Table 11. Compressibility values can be computed from the relationship and the computed values may be compared with measured values obtained by Bridgman.8 Table III lists the data for such a comparison. The agreement is satisfactory, being particularly good for neodymi- um and gadolinium, poor for samarium, and intermediate for the other elements. Some variation is expected since Bridgman&apos;s measurements are isothermal, whereas the present measurements are adiabatic. In addition there may be some effect due to small variations in purity. Though most of the rare earth metals measured by Bridgman and all of the metals used in the present measurements were prepared at this laboratory, minor purity variations might exist since the samples came from different lots. Also, any imperfections such as dislocations, vacancies, voids, grain boundaries, microcracks, etc., should contribute to the volume change of a com-

Jan 1, 1958

By John H. Bassarear, A. A. Dor

INTRODUCTION Primary grinding mills as defined in this paper, are autogenous or semi-autogenous rotating, tumbling mills having a coarse feed with a top size usually varying from 150 to 300 mm (6 to 12 inches). Most frequently, the feed to these mills is the product of primary crushing plants but in some cases run of mine ore is used as feed such as at Benguet, McDermitt, L-Bar Sohio, Bear Creek and others. The size of the largest lumps in the mill feed is principally determined by limits set by the mill feed trunnion diameter and by the type and size of conveying equipment used for handling and of bins and stockpiles used for storage. The use of primary mills in mineral processing plants has expanded very significantly in the last twenty years, and they have been successfully applied to the treatment of a wide variety of ores in both wet and dry grinding applications. In the present state of technological development for primary grinding mills, there is a wide choice of acceptable options with respect to type and size, grinding flowsheet and grinding media. The choice of the optimum combination which would result in the most satisfactory condition of operation, from the standpoint of both metallurgical results and costs, depends on the nature of the ore, the required characteristics of the grinding products and on various geographic and economic circumstances. The effects of such factors and considerations on the choice and sizing of primary grinding mills and flowsheets are reviewed and discussed in the following pages. PRIMARY MILLS SELECTION Inherent Characteristics of Primary Grinding Primary grinding is complex because it involves several comminution mechanisms which occur simultaneously and to some degree interfere with one another. These mechanisms of impact, attrition and abrasion have been described earlier. The relative importance of these three main grinding actions and their mutual balance resulting in a continuous uniform operation of the mill depend to a very large extent on the nature of the ore and its physical properties. Homogenous, single mineral ores will behave quite differently from heterogenous ores consisting of different minerals bound together along defined

Jan 1, 1982

By J. Gordon Parr, D. H. Polonis

The formation and subsequent decomposition of metastable phases in Ti-Ni alloys containing up to 11 pet (atomic) Ni have been studied. The decomposition of a completely retained ß phase and of a completely transformed 8 phase in a 6 pet alloy has been followed by X-ray diffraction and metallographic methods and by hardness determinations made during the process. The possible mechanisms of the reactions are discussed. PREVIOUS investigations of the Ti-Ni system have usually been limited to phase diagram studies; but little attention has been given to metastable phases and tempering processes. These are important, however, since equilibrium conditions are rarely achieved—nor, perhaps, are they desired—in practice. Up to the present time the available transformation data for titanium alloys appear to be restricted to isothermal transformation curves for selected binary and ternary systems. No quantitative studies have been made of the mechanism by which equilibrium is approached. Several independent investigations have been carried out to determine the Ti-Ni phase diagram. Early work by Wallbaum&apos; and later by Long et al.&apos; produced tentative phase diagrams which were not representative of true binary conditions, since the alloys were contaminated with oxygen and nitrogen. The most recent diagram (Fig. 1) is due to Margolin et al.," and a slight modification of the a + ß/ß boundary (shown dotted) has been proposed by McQuillan.&apos; The structure of the phase Ti,Ni was shown by Duwez and Taylor" to be face-centered-cubic, with 96 atoms per structure cell. The formation of a martensitic ß phase (close-packed-hexagonal) in Ti-Ni alloys has generally been observed when specimens of low nickel content are rapidly cooled from the 0 (body-centered-cubic) range. Margolin et al. reported an increasing tendency for P to be retained in lump specimens as the nickel content increases. McQuillan&apos; has studied the effect on the microstructure of delay time in quenching, and has reported the formation of pro- eutectoid a precipitate in a quenched hypoeutectoid alloy. In a previous study of Ti-Fe alloys," experiments were made on powder specimens produced by filing alloy ingots. Techniques were devised for the preparation and heat treatment of alloys, and X-ray diffraction methods were used both for structure determinations and phase ratio estimations. A similar approach has been made in this study of Ti-Ni alloys. Experimental Methods Ten alloys ranging from 0.25 pet to 18 pet Ni* * All compositions are in atomic percentages unless otherwise stated. were prepared from iodide titanium bar stock (hardness Rf 72) and Johnson-Matthey spectrographic standard nickel by levitation melting.&apos; As a check

Jan 1, 1957

By David White

ATTENTION has been given to the sources and supply of the raw vegetal matter and. the conditions of its submission to the process of sedimentation. An original and most valuable review has been made of the more important or significant chemical compounds originally contained in the organic debris, and of the biochemical changes-undergone by the latter during deposition. Consideration also has been given to the factors controlling the selective biochemical decomposition, in whole or in part, of :this debris, and the deposition, as, sediments, of the undecomposed plant structures and compounds, together with more or less of the so-called "ulmic," or "humic," organic decomposition products in colloidal solution.1 BIOCHEMICAL CHANGES END IN PEAT FORMATION The biochemical process terminates in the peat stage of coal formation, and with the cessation of this process organic sedimentation is completed. All subsequent changes result from geological causes and conditions. The deposits are in the form of peats of different types, organic muds, oozes, etc. They are essentially uncompressed and are wholly unconsolidated, and their water content is great, amounting to over 85 per cent. near the surface of the deposit. Many of the chemical compounds remain as in the once living organisms; others are biochemically broken down and new ones formed.

Jan 2, 1925

By John Johnston

THIS necessarily brief sketch will attempt to summarize the high lights of perhaps the best meeting so far held by the Iron and Steel Division. All sessions were well attended and the discussion was vigorous and of a high order. The technical sessions opened. on Tuesday morning. "Precipitation Hardening of Copper Steels" was discussed by Cyril S. Smith and Earl W. Palmer, and dealt with steel with a 1 per cent copper content. Discussion brought out that there were no fabricating difficulties, but that the surface might be somewhat checked due to intergranular penetration of copper which could be easily taken care of. Probable advantages of steels of this type for high temperatures were pointed out. "An Improved Nickel-chromium Hardened Chilled Cast Iron," by J. S. Vanick, described a wear-resistant cast iron and evoked a lively discussion.

Jan 1, 1933

By R. K. Ham, M. L. Wayman

TD-Nickel has been broken in tension and in fatigue at voom temperature. Rod specimens failed in tension by necking, with axial cracks attributed to voids elongated in the extrusion direction. Fatigue specimens failed in shear. Thin-film electron microscopy showed that the subgrain structure of TD-Nickel was very stable, and that particle-matrix detachment was very difficult, in tension and fatigue. TD-Nickel softened slightly during fatigue but had a high fatigue ratio (0.5at 10&apos; cycles). Fractography suggested that Stage I fatigue crack propagation is greatly extended in TD-Nickel. Td-NICKEL* is a dispersion of 2 pct by volume of thoria (ThO2) in nickel, produced by powder-metallurgical methods including compaction, sintering, and extrusion. The spherical thoria particles, which may have a mean diameter of a few hundred angstroms, are dispersed with a mean planar spacing of a few thousand angstroms. By a combination of cold working and annealing, a subgrain or cell structure of dislocations intimately associated with the dispersion can be produced.&apos; This gives the material useful tensile properties which are extremely resistant to exposure to high temperatures.&apos;-= At the same time, the material shows considerable ductility.3&apos;4 At the beginning of the present work, it was considered of great interest to investigate the mechanical stability of TD-Nickel under conditions of fatigue. On the one hand, materials which derive strength from a cold-worked structure are unstable in that they are susceptible to fatigue softening: in addition, the presence of discontinuities such as the particle-matrix interfaces might be expected to assist in the initiation and propagation of fatigue cracks, in that they may provide local concentrations of internal stress and sites for the initiation of voids." On the other hand, the substantial ductility of TD-Nickel suggests that if it obeys Coffin&apos;s relation8 (or the more refined form proposed by Manson9) it should have good fatigue resistance. The initial purpose of this investigation was to assess the importance of these factors. Also, relatively little fundamental work has been done on the mechanism of fatigue in dispersion-strengthened materials. Work on overaged A1-4 pct CU10-12 revealed a very large Bauschinger effect indicative of internal stresses at the particles, and very great fatigue hardening1&apos; presumably due to the multiple slip stimulated by these internal stresses, followed by softening which was initially due to softening in the matrix, but later might have arisen from cracking at the particle-matrix interfaces. The study of overaged Al-4 pct Cu could not settle this latter point by the electron microscopy of thin films, since the dispersion is too coarse. A previous study of the fatigue of internally oxidized copper13 was complicated by inter granular failure, attributed to oxide particles at grain bouhdaries; internal oxidation of single crystals, however, improved their fatigue properties.&apos;3 Investigations of SAP (sintered aluminum powder) are complicated by the complex particle shapes, and the possibility of continuous internal oxide films.14 It was hoped to avoid these difficulties with TD-Nickel, which had the further advantages that it was commercially available and suitable for study by the thin-film technique. 1) MATERIALS AND EXPERIMENTAL PROCEDURE TD-Nickel was purchased from the Driver-Harris Co. as 3/9-in.-diam rod which had been extruded, swaged, and "stress-relieved" (normally at 1010°C for 1 hr). Continuous-radius fatigue specimens with a minimum diameter of -0.1 in. were ground to shape and electropolished in 40 pct phosphoric, 35 pct sul-furic, 25 pct water at 25oC, with a stainless-steel cathode, at -6 v. Fatigue tests were carried out at room temperature with a Sonntag SF-1-U machine operating in push-pull at 1800 cycles per min, and in an Instron TT-C-L modified for reversed stressing at 26 cycles per min as described elsewhere.10 Round tensile specimens were ground with 0.85-in. gage lengths of 0.135 in, diam, electropolished, and tested in a Tinius Olsen hydraulic machine. The surfaces of fatigue specimens were examined with a Reichert metallograph. Discs for electron microscopy with a Siemens Elmiskop I were spark-cut 0.01 in. thick with a modified Servomet 11 employing a tool of moving molybdenum wire, cleaned in 50 pct acetic, 30 pct nitric, 10 pct phosphoric, and 10pctsul-furic at 85oC, and thinned by the window method in the electropolishing solution at -20°C and -6 v. Two-stage replicas (parlodion, then Pt-50 pct C self-shadowed at 40 deg) were taken from fatigue fracture surfaces for electron microscopy. Plane sections parallel to the specimen axis and containing the direction of fatigue crack propagation were polished, etched with Carapella&apos;s reagent, and examined optically. Transmission Laue X-ray photographs of as-received material electropolished to a point were used to determine preferred orientation. 2) RESULTS 2.1) The Structure of As-Received Material. Grains -1 µ diam and elongated 20 to 30 u in the direction of the rod axis were observed, With&apos; elongated "intergran-ular" voids (-4 p diam and -90 µ long and identified as such using longitudinal and transverse sections and

Jan 1, 1968

By AIME AIME

TO attempt to say anything adequate about Eugene McAuliffe as a human being, engineer, or executive in this brief space is ridiculous, for one could extol his virtues at length in all three catagories. Too, one might dwell on his good humor, and also his modesty, for lie did not wish even these few words to be said, "having no illusions regarding either ability or achievement, not even blessed with good looks." Mr. McAuliffe was born in England just seventy years ago. Twenty years later he started at the bottom with the Northern Pacific, gradually being promoted to locomotive fireman, engineer, and so

Jan 1, 1936