By M. Nicholas, D. M. Poole

The diameters of sessile drops have been found to increase linearly with time in five reacting binary metal systems. The spreading rates of the drops are markedly dependent on temperature and on prior alloying of the solid with the lower melting point metal, hut are independent of the drop volume, wetting atruosphere , solid-surface roughness, and prior alloying of the drop with the substrate metal. A mechanism has been suggested that relates the linear-spreading rate to lateral diffusion of the liquid-metal atoms into the solid at the drop edge. An Arrhenius- type equation has been derived that describes the temperature dependence 0) the spreading rate, and although the agreement between the actual and the predicted pre-exponen-tial terms is poor that between the activation energies is excellent and the variation in the spreading rate of copper on Ni-Cu alloys produced by different extents of alloying can be predicted with considerable accuracy. CHEMICAL interactions frequently change the wetting behavior of solid-liquid systems causing, for example, "secondary spreading1 of sessile drops beyond the size defined by the surface and interfacial tensions of the unreacted components. The kinetics of the contact-angle decreases associated with this spreading are similar for many systems, but few studies have been made with the objective of determining whether the similarities are a reflection of a common mechanism. Some workers2,3 have assumed the secondary spreading is controlled by changes in the liquid surface and liquid-solid interfacial tensions and hence by the composition of the liquid, and contact-angle changes measured by the vertical-plate technique have been used to follow the course of liquid-solid chemical reactions.4 Other processes that have been invoked to explain these time-dependent changes in specific systems include the removal of adsorbed gas from the liquid-solid interface.5 penetration of containment layers on the solid Surface,6 interdiffusion,1,7 reori-entation of the solid surface into a wettable configuration: vapor-phase transport of the liquid onto the solid in advance of the drop,9 and, from vertical-plate studies. capillary flow between oxide layers and the solid surface.10 One of the reasons for the profuseness of these suggestions may be the complexity of the contact-angle change kinetics. However, in an analysis of secondary spreading gold and copper on UC,11 it was found that the diameter of the contact area between the sessile drop and the solid surface showed a simple linear increase with time although contact-angle changes were more complex. To check whether the linearity was merely fortuitous! additional exploratory work was conducted with four reacting metal-metal systems: Au on Ni. Cu on Ni, Cu on Fe, and Ag on Au. Linear spreading was observed in every case even though the kinetics of the contact-angle changes were complex. A further detailed study of the kinetics of linear spreading of five reacting metal-metal systems has been made with the object of determining the mechanism involved. The influence of variables such as temperature, drop volume. and the initial composition of the drop on the linear-spreading rate has been measured and compared with those predicted by a number of possible mechanisms. The systems employed in this study (Cu and Au on Ni and Pt, and Ag on Au) were selected because of the availability of potentially relevant chemical and physical property data. the simplicity of their phase diagrams at the wetting temperatures, and the ease of experimentation. EXPERIMENTAL TECHNIQUES The purities of the metals used in the study were: copper, 99.9 pct; gold. 99.96 pct; nickel, 99.2 pct; platinum 99.99 pct; and silver, 99.999 pct. The wetting tests were performed in a split tantalum tube vacuum resistance furnace of a conventional design. The furnace element was held vertically and was 1 $ in. in diam and 6 in, long. Viewing ports were provided in the water-cooled chamber to enable the specimens to be observed in both the horizontal and vertical planes. The temperature in the hot zone of the furnace could be held at 1500" i 5°C for an indefinite time. The surfaces of the solid-plaque metals were ground flat on Microcut paper and both the sessile drop and substrate metals were ultrasonically cleaned in methyl alcohol prior to their insertion in the furnace. After loading, the furnace was pumped down to a pressure of 2 x 10-5 mm of mercury and degassed for 30 min at 900° to 950°C. The temperature was then increased at more than 100°C per min to that used in the wetting test. The vacuum at the wetting temperature was better than 5 x 10-5 mm of mercury. Dewetting and retraction of the drop on cooling did not occur and the contact-area diameters, therefore, were measured after solidification with a vernier traveling microscope. The diameters quoted later are arithmetic means of ten measurements. The standard error of the mean never exceeded 3 pct and was often less than 1 pct.

Jan 1, 1967

By M. M. Fine

Normally the U. S. produces less than 10 pct of its annual manganese requirement. About 95 pct of domestic consumption is used by the steel industry.' The strategic and critical nature of manganese has been recognized by its inclusion in the national stockpile and by intensified research directed toward cataloging and evaluating domestic manganiferous deposits. The USBM has participated in these activities for many years with field and laboratory studies to assess the extent and potential utilization of domestic manganese ores. One area of particular interest is in the vinicity of Batesville, Ark., where deposits have been mined since 1849 for both manganese and ferruginous manganese ores. Production is centered in Independence County, but deposits are also found in Sharp, Izard, and Stone counties in north-central Arkansas. Miser has described the geology and manganese mineralization in some detail.'. * "he rocks of the area are sedimentary, consisting of sandstone, limestone, shale, and chert. The two formations of greatest importance,' Fernvale limestone and Cason shale, are host rocks of the primary manganese mineralization. Through 1955 the district produced some 230,000 long tons of manganese ore (35 pct Mn or more) and 236,000 tons of ferruginous manganese (10 to 35 pct Mn).5 Most of the ore has been mined from deposits of manganese oxides in residual clays resulting from weathering of the two formations noted above. Concentration methods have been primitive, consisting for the most part of washing. hand picking, and jigging. A significant accomplishment in the district in recent years was the USBM recognition and investigation of the huge manganese potential represented by unaltered Fernvale limestone. systematic reconnaissance of manganiferous limestone and other occurrences has been in progress since 1953 to delineate the extent and tonnage of manganiferous materials. Results of that survey have appeared in two recent publications,1-5 which ascribe to the district an inferred reserve of 166 million long dry tons at a grade of 5 to 6 pct Mn. Most of this was mancaniferous limestone with an estimated content of 5 pct Mn. Specifications: Beneficiation was carried out on a group of manganiferous limestones to develop a way to recover commercial-grade concentrate from this extensive resource. The following chemical specifications were established by the GSA for metallurgical manganese ore acceptable for delivery to the national stockpile: Size specifications were not considered, as it was assumed that the concentrates could be pelletized or sintered. Manganiferous Limestones: Of the 11 samples tested to date, six were taken by cutting vertical channels across beds of limestone outcrops. Diamond drilling through overlying barren chert into unex-posed limestone provided four samples, and the last was a churn drill sample. In general, the samples were dlrk, fossiliferous limestone containing small amounts of braunite, hausmannite, rhodochrosite, massive and micaceous iron and manganese silicates, quartz, barite, and glauconite. The braunite and other manganese oxides partly to completely replaced some of the calcite and fossil material. The calcite was generously stained with mangenese and iron oxides. Phosphorus was present in all samples as collophanite grains, calcium phosphate fossil replacements. or an unidentified manganese-bearing carbonate. The difficulty in separating this complex array of minerals was further complicated by a very intimate association. Although some manganese grains as large as Ik in. were noted, grinding to subsieve sizes would have been necessary to liberate the components. Figs. 1 and 2 are micrographs, at X100, of typical polished sections in which white areas are manganese. gray is gangue, and black areas are surface depressions. By comparison with the 100 mesh opening, it is seen that some of the grains are coarse enough to respond, perhaps to tabling or flotation, but many are obviously beyond the scope of ohysical processing. Partial chemical analyses of the eight samples that were ultimately amenable to concentration are presented in Table 1. BENEFlClATlON RESEARCH Tabling: To take advantage of the presence of sand-size grains, both jigging and tabling were considered at the outset. Jigging was largely ineffective, but tabling achieved a partial recovery from most samples. As an example, the surface material from Baxter Hill was crushed to —28 mesh, hydraulically classified, and the coarsest spigot fraction was tabled to yield a concentrate, middling. and tailing. The latter two were reground to pass 48 mesh, combined with the primary fines, re-classified, and retabled. The middling and tailing were again ground, this time to pass 150 mesh, and deslimed at 20µ in a 3-in. hydraulic cyclone. The cyclone underflow was returned to the table to reclaim a small amount of high-grade manganese. An interesting facet of the gravity concentration developed on certain samples in which braunite was the principal manganese constituent. Since braunite has a Mohs hardness of 6 to 6.5, while the host rock, limestone. is only 3, a differential size reduction took place during crushing, and the

Jan 1, 1960

By Edward L. Fidler, Thomas E. Finch

Thin seam coal mining in the western US nominally equates to recovery of stray seams associated with thicker, major seams. The thin or stray seams encountered are generally recovered, but not in all cases. The alternative to extraction is, of course, spoiling. The majority of thin seams are encountered somewhere in the overburden above the major seam or in the parting between thick seams. Although some are true strays and appear anywhere in the geologic sequence, others might be classified as thin "rider" seams immediately above or below a thick seam and separated by some equally thin parting. For the purpose of this discussion, stray or thin seams are defined as those which are less than 1.2 m thick or represent less than 10% of the expected extractable coal. [Figure 1] is a graphic representation of typical thin, stray, or rider seams which actually appear in a western operation. Operationally, stray seams create irritating scheduling problems and require special handling techniques which do not always lead to efficient equipment utilization. Additionally, coal recovery from a thin seam is considerably less than the 95% usually recovered from thick seams. Higher recovery in thin seams leads to dilution problems, which depreciates Btu quality, and most western coals are not in a position to lose heating value. Thin western seams also undulate and pinch or swell more than thick seams, and this leads to more difficult recovery. Often they are associated with equally dark carbonaceous shales and visual selectivity is difficult at best during daylight hours. Resource Recovery Regulations Thin seam recovery in western mines is encouraged by both federal and state regulations and by the mining industry's concern for total resource recovery. [Table 1] lists the western coal states and their recovery regulations. The federal regulations are found in the Surface Mining Control and Reclamation Act of 1977. They state, "General performance standards shall . . . require the operation as a minimum to … conduct the surface coal mining operations so as to maximize the utilization and conservation of the solid fuel resource being recovered." Economic stimulation for thin seam recovery appears to be marginal or at the least controversial. Scheduling and operational problems often outweigh the nebulous profits created by engineering analysis. The only alternative to extracting thin seams occurring above major production seams is to strip directly through them and lose the resource to the spoil pile. Although this is not palatable to environmental emotions or resource promoters, it is the most simple expedient to operations people.

Jan 1, 1981

IT is customary to make an alloy of copper in the same way, not to increase its quantity as with gold or silver, but to corrupt it for the art of casting and to destroy a certain natural viscosity in it. For this result it is accompanied by tin and also, sometimes, brass. But its proper and true alloy is fine tin, except, however, when you wish to make hammered works. For these, copper must be pure and without any trace [of impurity], otherwise it cannot be hammered thin, gilded in the fire, drawn into a wire, or made into vessels for use as is customary; but in casting, tin is almost essential. When you come to this association, just as it changes nature and appearance according to the proportion of tin which you give it, so it changes name and is no longer called copper but bronze, or, for a greater distinction of the quantity of tin for every hundred or more of copper, it is called by skilled workmen metal of more or less fineness as it contains more or less tin. This is recognized by the whiteness and brittleness: changing from red, which is the color of copper, it becomes white; from soft and flexible it becomes hard and brittle as glass. This admixture removes it so far from its original nature that one who does not know that it is a compound material believes it to be one of the number of metals engendered by Nature. Now, so that you may understand well, I tell you that various kinds of this are made, all according to the proportions of the quantities and according to the kind of work. For one kind of bronze is desired by those who make statues; this is not desired by those who make artillery or by those who make bells, mortars, basins, and similar cast objects. Now in order to alloy it into the species of bronze, eight, nine, ten, up to twelve pounds of tin are put with every hundred pounds of copper. Those who want it to make bells put twenty-three, twenty-four, twenty-five, and twenty-six, depending on the tone, on whether they are large or small in form, and on whether they wish to make the tone deep or sharp and clear. From twelve upwards is used for all other works that need it, either for hardness or to give them fluidity in casting by surpassing the degree of

Jan 1, 1942

By F. J. Mehringer, C. W. MacGregor

VARIOUS investigations have been carried out to determine the effects of cold-rolling on the common physical properties as represented by the yield strength, tensile strength, percentage of elongation and ordinary reduction of area. Very little information is available in the literature with reference to the effects of cold-rolling on the true stress-strain properties. Since the ordinary physical properties base both the stresses and the strains on the original dimensions of the test piece, which are greatly changed during the test, they are essentially empirical values and do not represent physically either true stresses or true strains. Consequently, they do not give an accurate picture of the effects of different conditions, both mechanical and metallurgical, on the strength and ductility of the material. It is not, however, the purpose of this paper to review the various advantages accruing from the use of true stress and true strain values, since these have been shown elsewhere,1-12 but to utilize them in representing the various effects considered. The true stress S and true strain (e = q') values mentioned above for the tension test are defined by1 [ ] where P, A, Ao are the axial load, the instantaneous area and the original area of cross section, respectively. From simultaneous readings of the axial load and the dimension or dimensions determining the instantaneous area of cross section, the true stress-strain curve is constructed by using the relations given in Eq. I. It is then the object of this paper to discuss the general effects of cold-rolling on the true stress and strain values for a low-carbon steel together with the effects of age-hardening and directionality on these properties. PRELIMINARY INVESTIGATIONS The material considered throughout the paper is a low-carbon steel of the following chemical analysis: C, 019 per cent; S, 0. 118; P, 0.092; Mn, 0.85; Si, 0.01. The stock was received in bars, 7 by 3/4 in., and was first annealed for one hour at 1650°F. followed by a furnace cool. Photomicrographs of this material showed considerable directionality even in the annealed condition. In view of the possible effects of the nonhomogeneity and directionality in this material, it was considered important to investigate their influence on the true stress-strain diagrams. In addition, the effect of strain-aging in this steel was also made the subject of a preliminary study. Elect of Aging on True Stress-strain Properties Since a certain time element would elapse between the cold-rolling operation and the final tension tests, it was determined to investigate the aging character-

Jan 1, 1945

By E. B. Brauer, B. F. Pennington, E. W. Hough, G. L. Stegemeier

Interfacial tension divided by the difference in density between the liquid and the vapor phases was determined experimentally by the pendant drop method on several isotherms in the two phase region below the critical point for the methane-normal decane system. The density difference data of Sage and Lacey was used in the calculation of interfacial tension. Both interfacial tension and and interfacial tension divided by density difference were found to vanish at the critical point. Interfacial tensions of less than one dyne/centimeter were observed as far as 1,000 pounds per square inch below the critical pressure. EXPERIMENTAL PROCEDURE The interfacial tension divided by the density difference for the methane-normal decane system was determined at the 100°, 130°, 160' and 190°F isotherms, from pressures of about 1,000 psi to the critical pressure, which is more than 5,000 psi for these isotherms. Particular emphasis was placed upon the investigation at pressures slightly below the critical pressure where the interfacial tension is less than 0.5 dyne/cm. Volumetric properties in the two-phase region, including the critical pressures and temperatures, were taken from the work of Sage and Lacey.1 The experimental pendant-drop technique used for the determination of interfacial tensions at high pressures incorporated the ideas of Michaels and Hauser,2 Hough, et a1,3 Walker4 and Heuer.5 In addition, the technique for determination of extremely small interfacial tension by Jennings6 was utilized in the region near the critical points. A detailed description of the apparatus is given in a dissertation by one of the authors.7 Cleaning operations on the stainless-steel sample system included successive washings with chromic acid, tap water and, finally, distilled water. Subsequent cleanings were performed with re-distilled normal pentane, which had an extremely low residue upon evaporation. Specific composition requirements necessitated a fairly precise sample introduction — although, fora two-phase, two-component system, the composition of each phase is completely determined if pressure and temperature are controlled. The normal decane was delivered into the evacuated sample system as a liquid from a burette. The methane was then introduced into the system from a calibrated isothermal container, so that pressure differentials could be used to determine the amount introduced. High pressures were obtained by compressing the sample with a mercury injection pump until the critical pressure was reached for the particular isotherm being studied. Experimental data were then obtained for specific pressures by first decreasing the pressure slightly so that two phases would appear, and then photographing a drop at that pressure. Subsequent photographs were made at increments throughout the pressure range. Calculation of interfacial tension divided by density difference was made from measurements

By Walter Crafts, C. M. Offenhauer

IN a previous study' of the carbide phase of chromium steels, it was shown that chromium carbide (Cr7C3) is a more stable carbide than cementite (Fe3C) at tempering temperatures above about 500°C. in quenched steels containing from about r1to 7.5 per cent chromium. Below this temperature the carbide phase was found to consist of cementite in all of the steels examined. In the present investigation it was found that a similar change in the carbide phase takes place in molybdenum and in chromium-molybdenum steels at approximately the same tempering temperatures. The approximate ranges of occurrence of the alloy carbides Cr7C3, Cr4C, and Mo2C have been determined in steels containing up to 5 per cent chromium, 1 per cent molybdenum and 0.60 per cent carbon. The experimental steels were made in small high-frequency furnaces from Armco ingot iron, low-carbon ferrochromium and calcium molybdate and were poured into 2-in. ingots, which were forged to 1-in. round bars. Sections of the bars were heated to the carbide-solution temperature and cooled rapidly to induce austenite transformation at relatively low temperatures. The steels were subject to some segregation, therefore comparatively high temperatures were necessary to dissolve all of the carbides. The microstructure of the quenched specimens was examined to verify the belief that the carbides had been dissolved, and also to determine the nature of the nonmartensitic structure of incompletely hardened steels. Ferrite and pseudomartensite were present in some of the specimens, but all specimens were quenched at such a rate that pearlite was not formed, in order to ensure the formation of the carbides at temperatures lower than about 500°C. It had been found previously' that in chromium steels the chromium carbide could be produced by transformation of austenite in the pearlite range above 500°C., and, in order to start the tempering treatment with the carbide present as cementite, the absence of pearlite was considered to be essential. The specimens were tempered for 64 hr. to permit the formation of the stable carbide. After tempering, the specimens were submitted to microscopic and X-ray examination. The carbides were separated either electrolytically in a 5 per cent HCl electrolyte or with an acidified copper-potassium chloride solution. The crystal structure of the carbide phases was determined by the Debye-Scherrer type of X-ray patterns. The X-ray patterns obtained from specimens near the boundaries between two types of carbides were generally weak and diffuse as compared with the other patterns. For this reason, and because the more soluble components may be masked, the boundaries between the phases could not be determined precisely. However, the X-ray analysis of electrolytically separated carbides has given consistently reproducible results

Jan 1, 1943

By Orville A. Derby

In view of the recent important discussions before this Institute on the genesis of metalliferous deposits, certain features in the occurrence of gold which seem to be more clearly developed in Brazil than elsewhere can hardly fail to be of interest. As the observations here recorded have necessarily been of a somewhat cursory character, they will be presented in the form of brief notes, without any attempt to draw conclusions as to their genetic significance. Gold in Gneiss.—The statement made by me many years ago† that in the districts of Campanha and S?o Gongalo, in southern Minas Geraes, gold occurs in gneiss, can now be reaffirmed in the most positive manner, on the strength of a recent examination of fresh material, confirmed by the testimony of an experienced mining captain from the Morro Velho mine, who, being skeptical on this point, made a prospectingtour in the district. The specimens examined, though so far decomposed as to be readily disaggregated, were clearly of

Jan 1, 1903

By R. E. Lindstrom, D. G. Peterson, H. J. Heinen

Alkaline alcohol solutions were investigated by the Federal Bureau of Mines for improving the desorption rate of gold and silver from metal-laden activated carbon generated in gold processing circuits. Factors affecting the desorption, such as temperature, alcohol content, type of alcohol, and alkalinity, were studied. Nearly complete metal desorption was obtained in 5 to 6 hr at 80º C using a solution containing about 20 vol-pct alcohol and 1 pct sodium hydroxide. Sodium sulfide was shown to be effective for selectively precipitating silver from the carbon strip solutions, thereby providing a means for producing high- purity gold by subsequent electrolysis.

Jan 1, 1976

By Harry A. Roe

THE power drag scrapers and the slackline cableway excavator have been called "long-range excavators." Broadly, their field of usefulness is restricted to work in which their long range of action permits them to operate economically, and which other, possibly more conventional, excavating units cannot do. Both of these machines dig or lift material and transport it to a remote dumping point. They combine these two functions in a single machine, nearly always in a single straight-line motion. [ ] The purpose of this paper is to examine the important features that distinguish the machines in this group from each other, as well as from other groups. The Machines The "power drag scraper" is a long-range excavating machine that employs a bottomless drag scraper operated back and forth between digging and dumping points by two haulage cables. The typical arrangement is that of Fig. 1. This is the "slusher" of the underground mine, as well as the "dragline scraper" of the sand and gravel industry, and other open-pit mining operations.

Jan 1, 1937

By T. A. Rickard

The lodes of Cripple Creek, Colo., partake of the composition of the geological formation which they traverse. The prevailing rocks are andesitic breccia, lying upon granite, and also bodies of phonolite, trachytic phonolite, nepheline-basalt, etc., penetrating both the granite and the breccia. At Kalgoorlie, in West Australia, the prevailing rock is schistose, and has not been certainly identified, though microscopic sections indicate the probability that it was originally an acid eruptive. The lodes are essentially bands, more highly schistose than the encasing rock, and impregnated to a notable degree with disseminated pyrites and secondary calcite. During 1899 Cripple Creek produced 425,590 tons of ore, having a gross value of $15,658,254; during the same period the output of Kalgoorlie was 467,048 tons, valued at $17,724,587. In chemical composition, the ores at Cripple Creek and Kalgoorlie, respectively, present differences equally interesting to the petrographer and the metallurgist. In both cases we have to deal with altered eruptives as the matrix of the ore; but the much older rock of Kalgoorlie has undergone more decompo-

Jan 1, 1901

By N. A. Parlee, A. E. Lord

Measurements of the solubility of lead in liquid iron were made at 1550°, 1600°, 1650°, and 1700°C using two different methods, i.e., 1) liquid iron-liquid lead equilibration and 2) liquid iron-lead vapor equilibration. LEAD was long considered insoluble in liquid iron1. Today steels containing 0.15 to 0.35 pct Pb are used. One laboratory has found a solubility of about 0.5 pet in the 1600°C range. Recently Miller and Elliott2 gave 0.60 pct as the result of one determillation at 1540°C. Because these findings resulted from the

Jan 1, 1961

By J. C. Bayles

An obstacle to the more careful and satisfactory study of metals has been the difficulty in harmonizing the results of chemical and physical tests. These give us records of observations made from different and often widely separate points of view, and while it is true that they furnish bases for more or less accurate triangulations into the realm of speculation, it is doubtful if, with only the laboratory and the testing machine, our investigations would not move in parallel lines, leaving between them an unexplored field in which must probably be sought the information which shall connect the results of chemical and physical tests, and give to both a practical value which neither has yet been found to possess. The use of the microscope in the study of metals is not a new thing, but it is only lately that it has begun to attract the attention it merits or to show results of tangible value to the metallurgist. Among recent valuable contributions to the literature of this subject, I have been especially interested in the work of Mr. A. Martens, of

Jan 1, 1883

By M. A. Bryant, J. C. Goodwin, T. B. Faddies, L. D. Kornze

The Mercur Gold Mine is located 56 km (35 air miles) southwest of Salt Lake City in north central Utah; In July 1981 Getty Mining Company made the decision to put Mercur into production. The first gold bar was poured in April 1983. This paper provides details on: 1) the history of the camp, 2) past production, 3) geology of the deposit, 4) the exploration and development program, 5) ore reserve estimates, 6) detailed geologic pit mapping, 7) production blasthole sampling techniques and 8) the use of geostatistics (kriging) in handling assays and gold extractions to produce the required mill feed.

Jan 1, 1985

By T. D. Mueller, F. C. Miller, Jr. Earlougher R. C.

In analyzing pressure buildup tests for field wells producing both oil and gas, the common practice is to use a modification of single-phase flow theory. Validity of such an approximation has been demonstrated for single-well solution-gas-drive systems. This paper indicates that such approximations are also valid for two-well solution-gas'-drive systems. From this it is inferred that the technique can be used for multiple-well systems. A computer was used to simulate the behavior of a two-well solution-gas-drive reservoir to test the validity of the above type of analysis. Simulation results indicate that pressure buildup tests in such a system can be analyzed within engineering accuracy for formation permeability and pressure. A rule of thumb is given for estimating the length of time a well must be shut in for the pressure in a nearby producing well to increase significantly. To observe such an increase, the shut-in well would have to be left shut in much longer than normal. INTRODUCTION An important technique for obtaining data concerning a producing petroleum reservoir is the pressure buildup test. Such a test, when properly conducted and analyzed, provides information on the average reservoir pressure and the permeability in the major drainage area of a well. The theory upon which the analysis of a pressure buildup test is based assumes that the behavior of the fluid in the reservoir is adequately described by the diffusivity equation.1 Use of the diffusivity equation implies that a single fluid of small and constant compressibility is flowing. To analyze a pressure buildup test in situations which involve more than one fluid phase, the single-fluid analysis is extended. This paper verifies the extension of pressure buildup analyses to two-phase, two-well systems. Miller, Dyes and Hutchinson1 have presented a technique for analyzing pressure buildup tests in circular bounded reservoirs. Their method requires that the reservoir be producing at pseudo-steady state (constant pressure gradients) prior to shut-in. An alternate reservoir model, presented by Horner,2 assumes that the reservoir is infinite. The Homer model does not assume a Pseudo-steady state prior to shut-in, but the assumption that the reservoir is infinite implies that the average pressure can be determined only if the total production prior to shut-in is small compared to the total fluid originally present. Limitations imposed by the pseudo-steady state and infinite reservoir assumptions are avoided by the technique proposed by Matthews, Brons and Hazebroek.3 Their method can be used to calculate both the Permeability and the average pressure in bounded single-well systems which are not necessarily at steady state. They also suggested determining the average pressure of a multi-well reservoir producing from pseudo-steady state by volumetrically averaging the static pressures of the individual wells. Matthews and Lefkovits4 used numerical simulation techniques to verify that this method does produce adequate results for single-phase, multiple-well systems. Perrine5 proposed modifications to the single-phase theory so that pressure buildup tests in multiple-phase systems could be analyzed. He suggested replacing the single-phase mobility (k/µ) by the sum of the mobilities of the individual phases, and replacing the fluid compressibility by an average compressibility weighted by the saturations of the separate phases. By using numerical techniques to solve the two-phase flow problem for a single-well system, he concluded that this approximation gives results within engineering accuracy. More recently, Weller6 has shown that, for a gas-oil system with a single well at the center of a circular reservoir, pressure buildup tests can be analyzed adequately by using the modification proposed by Perrine. Feller's results also indicate that, as the gas saturation increases, this analysis becomes less accurate. To date, no evidence is available to show that the Perrine approximations can be combined with the Matthews-Brons-Hazebroek technique to calculate the average pressure of a multi-well,

By O. Schaaber

THE existence of isothermal martensite without the presence of the athermal form thus far has been established only in a 6 pct Mn, 0.6 pct C steel' and a 23 pct Ni, 3.5 pct Mn-Fe alloy.' " Theoretical calculations, moreover, predict this phenomenon to be observable only within narrow composition limits.' In all other steels, it is generally considered that martensite inevitably forms upon cooling below the M, temperature. Even the possibility of isothermal martensite transformation has been questioned for the common steels, although Averbach and Cohen" showed that martensite formation does not stop when the cooling is arrested and that as much as 5 pct retained austenite may transform isothermally to martensite at room temperature. This note presents some observations made on a number of low alloy steels by dilatometric and inductive measurement of isothermal austenite transformation at various temperatures close to the Ms. In the dilatometer studies reported previously, austenitized specimens were immersed in a salt bath maintained at proper temperature and immediately inserted into the dilatometera8' already at thermal equilibrium with the bath. The dilation was read on a dial gage divided into 0.001 mm intervals. Induction measurements were made with a separate excitation source and a test coil, sealed together in a salt-tight case. The increase in the induced voltage caused by the transformation products was recorded at a paper speed of 4 mm per sec. The steels studied are listed in Table I. Specimens prepared from steels 1 and 2 were in the form of hollow cylinders 60 mm long, 10 mm ID, 14 to 16 mm OD, while specimens of steels 3 and 4 were in the form of notched-bar impact test specimens, DVM type. Specimens of steel 5 were in the form of strip, 7x0.3 mm. In the bainitic range, curves representing the amount of transformation vs log time have a single step appearance, as is shown by the curve of isothermal transformation at 320°C in Fig. 1.Y ransformation proceeds in accordance with the Austin-Rickett equationo P -----------= k t" 100-P where P is the percentage of transformed austenite, t is time, and k and n are constants. Near the M, temperature, however, complex curves having two steps are observed. As shown in a previous papera for steel 3 isothermally transformed at 245"C, such complex curves can be separated into two separate transformations or reactions each following the Austin-Rickett equation. The values of n in the equation for a number of such two-step transformations are listed in Table 11 for steel 1. At transformation temperatures of 250" and 235"C, evidence of a second transformation is very

Jan 1, 1956

By E. L. Dougherty

A phenomenological theory for a one-dimensional unstable miscible displacement similar in type to the Buckley-Leverett model but including the effects of mixing is proposed An equation giving the fractional flow of pure solvent through an oil phase containing dissolved solvent is derived including the effects of gravity and nonbomogeneities. Numer ical integration of the resulting pair of nonlinear hyperbolic partial differential equations gives volumes of dissolved and undissolved solvent as functions of space and time. Parameters in the model which characterize mixing due to dispersion were determined from experimental data; the parmeters correlated with viscosity ratio. The results indicate that the rate of dispersive mixing is proportional to volumetric flow rate Incorporated into our equations were Koval's heterogeneity factor H. which characterizes mixing due to channeling. This allowed satisfactory predictions of displacement behavior observed in horizontal floods in nonhomo-geneous cores; but in most cases the values of H which we used were considerably larger than those used by Koval. INTRODUCTION It has been shownl,2,3 that for favorable viscosity ratios, the diffusion equation with convection satisfactorily describes the behavior of a miscible displacement in a porous media. Numerous attempts to develop a satisfactory mathematical description for the case of unfavorable viscosity ratio have been reported, but they have met with only partial success. These attempts, which are reviewed by oval! have taken two approaches: (1) development of a flow model akin to the Buckley-Leverett approach for immiscible displacement neglecting the effects of mixing5,6 and (2) simultaneous application of Darcy's Law for flow and the diffusion equation with a convection term for mass transfer.7,8,9 We set out to construct a mathematical model of Type 1 including, though, the effects of mixing. Based upon a set of hypotheses, we derived a pair of nonlinear hyperbolic partial differential equations which describe in a one-dimensional system the combined effects of flow and mixing. To work with these equations it was necessary to develop a fractional flow formula. The combined system was integrated numerically using the method of characteristics. In our equations the mixing process is characterized by four parameters. Three of these, labeled ß, P1 and P2, account for dispersive type mixing. The fourth is the heterogeneity factor H, proposed by Koval to account for channeling due to nonhomogeneities in the porous media. Values of the parameters which would cause agreement between theory and experiment were determined by trial-and-error for miscible floods conducted in horizontal cores of both homogeneous and heterogeneous materials. Calculations were also performed for vertical floods in homogeneous cores. The purpose of this paper is (1) to present the details of the mathematical analysis, (2) to present the results of the calculations, (3) to consider what light the results shed on the mixing process in an unstable miscible displacement, and (4) to provide a firmer foundation for the correlation technique developed by Koval for predicting the behavior of unstable miscible floods. STATEMENT OF PROBLEM The problem is to construct a mathematical model which describes in one dimension the observed behavior in an unstable miscible displacement. The approach is phenomenological in that the equations are based on assumptions which violate certain physical precepts known to apply to the displacement phenomenon. However, the assumptions do allow us to account mathematically for the more essential phenomena. The work is of value if we can quantitatively predict experimental results which heretofore could not be predicted, even though the synthetic nature of the model belies complete explanation of the observations. We assume that the system is comprised of two contiguous flowing phases. One phase, which we call free solvent, has the properties of pure solvent. We call the fraction of the pore volume occupied by this phase the solvent saturation, designated s. The oil phase consists of oil containing dissolved

By O. Chanute

all of' level atid grade curve excepting Nos. 897, 898, 899, and 900, because of the impossibility of grouping them in the same nlonner, no two Iraving the chemical composition and physical prnprtiw as tho only v:iriubles. Phosphorus ~tnits have been taken to show the relatia h:wdnes. Of these 16 groups, 10 decidedly indicate slower wear firr tile harder rail. Of the remaining 6 groups, three (groups 2, 9, and 15) come well within the limits of error (.25 pound per yard) inherent in the palculation of the data as pointed out by Dr. Dndley; they catrnot, therefore, be considered tls exceptions. Group 2 and 15 arc but little outside of the limita of error. Rail 923 of group 9 is obviously abnornlal. This is probahly due to its being overheated, which the chemical analysis shows might easily be the case, and which the physical tc~ts and its low specific gravity tend to c-nfirm. We inry say, then, thnt 13 of these 16 groups fairly indicate, if they do not definitely point out, th:kt, under the same condition% tbe harder rail gives the slower wear. Of course, these comparisons are too few to enable us to arrive at positive ~?o-nclusions; but indications thus obtained are, I believe, fir more vsluitblc and tresttvc~rthy than those fhzt averages rvottld give us, mnde up from any ~lumhr of rails under intloy difi~rcal, conditions. Finally, it, seems to me, that the conclusions arrived at earlier in my remarks, together with, and confirmed by the last, show strong evidence that, under the same conditions, the harder rail will givc the slower wear. 0. C~~anute, New York CITY: We are very much shlipl, 1 ant sure, to Mr. Sandberg for his paper upn " Rail Ryaifications and Rail Inspertion in Europe." We have in thp United States bithhrto Been inspecting mils sonlewl~at haphazard, and we ore glad to gtbt tfie results of Mr. Sandberg's long experience. We recognize that he was an)ong the first, if not the very firwt, to iipply mare rittional and scientific rules to the designing of irou rails., niora recently, to adapt tlitve rules to the clesigtting of steel I':I~]R, to conform to the oapaljilities and rqniretnento of this new n1:ttcrial. Although we have generally adopted, in this country, sectinns for hteel rails which marly of our railway men think even bottar than those of Mr. Snlldlmrg, he is neverthelees the Ieat3er in foot.iito11~ we have followed ever since it has been est~blished

Jan 1, 1881

By John Jermain Porter

PAGE. I. INtroduction............ 191 I1. Derivation of Formula foR Fuel-RequiRements.... 192 1. Heat Available in the Hearth........193 a. Method of Calculation..193 b. Data for the Determination of Critical Temperature.. 195 2. Heat Necessary in the Hearth ...... 197 a. To Care for Slag..197 b. To Care for Pig-Iron...198 c. To Reduce Silicon........198 d. For Other Items.........199 3. The Effects of Rate of Driving ..... 199 4. Loss of Carbon Between Throat and Hearth.....201 a. Solubility of Coke..201 b. Carbon-Loss Due to Flux....201 c. Effects of Reducibility of Ore..202 5. The Formula as Used........203 III. The LImitations of the Formula........ 204 1. Through Effects of Irregular Furnace-Work.....204 2. Through Ratio Between Heat-Requirements in Shaft and Hearth. 20.5 IV. The Formula Applied to Actual Furnace-Records,.. 209 1. Description of Furnace-Stock........ 209 2. Furnace Dam..........210 3. Application of Formula..211 4. Average Furnace-Practice..213 V. Sources of Error........... 214 VI. SuggesTions for Practical Methods of Fuel-Economy... 215 VII. Efficiency as a Factor in Furnace-Management.... 219 1. The Efficiency Principle........ 219 2. The Application to the Blast-Furnace..220 I. Introduction. The heat-balance of the blast-furnace has been a favorite subject for discussion for many years. and its study has contributed much to our knowledge. and still possesses a certain academic interest. As a means of accounting for differences in fuel-consumption, however. it has failed utterly. and it is evident that we must look elsewhere for the means of accomplishing this end.

Jan 1, 1912

By Y. C. Liu

IN the study of the rolling recrystallization of face-centered-cubic metals, a most unusual observation is the frequent occurrence of a sharp re-crystallization texture of cube orientation. Although the general conditions under which this texture occurs are known,2,3 its origin is still not well understood. Based on the observed relationship between the {110}<112> deformation texture and the (113}<211> recrystallization texture, regardless of the effect of alloying elements2,4,5 or the symmetry of the deformation texture,&apos; there is a strong indication that a specific component of the deformation texture is related to a specific component of the recrystallization texture. Using the rotational reorien-tation relationship as a means of correlating the deformation and recrystallization textures, it was proposed that the deformation component which related the cube texture has {358)<523> indices."&apos; The investigation reported here was undertaken to seek experimental evidence for the validity of this proposition. Experimental Procedure Two copper single crystals having an initial orientation within 2" of (358) [523] indices were prepared in the manner described in Ref. 5. The purity of the copper was between 99.94 and 99.97 pct. The original dimensions of the crystals were as follows: specimen A, 0.465 in. thickness, 0.844 in. width, and 0.955 in. length; specimen B, 0.535 in. thickness, 1.120 in. width, and 1.36 in. length: Rolling was done on a laboratory rolling mill according to the following schedule: 0.010 in. per pass to 50 pct reduction in thickness, 0.005 in. per pass to 70 pct reduction inthickness, 0.002 in. per pass to 85 pct reduction in

Jan 1, 1958