By H. E. Cline, E. F. Koch, J. L. Walter

It has been postulated and, in a few instances shown, that some kind of dislocation structure will be present at semicoherent interfaces to accommodate small lattice mismatches. In the present study of the NiAl-Cr eutectic, regular arrays of interface dislocations are observed at the boundary between the chromium-rich rods and the NiAl-rich matrix. The networks were examined by transmission electron microscopy and selected area diffraction. The rods and the matrix have a crystallographic relationship in which all directions and planes of the two phases are parallel. The dislocation networks are cmposed of a<100> dislocations lying on the intersections of the cylinders with (100) planes. Dislocations forming hexagonal rather than square arrays are also observed at certain areas of the network. The morphology of the network is consistent with the interpretation of mismatch being accommodated by interface dislocations in the cylindrical geometry. The measured spacing between dislocations was used to calculate an apparent lattice mismatch between the phases (˜0.35 PCt)interface network energy (-140 ergs per sq cm), and network strengthening (-10,000 psi). It has been proposed by Frank and Van der Merwe1 that dislocations should be present at the boundary between two semicoherent crystallographically related phases. The role of the interface dislocations would be to reduce the internal stresses, caused by the mismatch in atomic spacing across the interface. Such dislocations have been observed at the interface between expitaxially grown films and Substrates.2-4 Interfacial dislocations have also been observed at precipitate-matrix interfaces.&apos;-&apos; Directionally solidified eutectics have been shown to have semicoherent phases1&apos; and would, therefore, be expected to have interfacial dislocations as found by Weatherly at a lamellar fault in A1-A12Cu.11 The NiAl-Cr eutectic appeared to be a promising system to examine because both phases are cubic, the lattice mismatch is small, and the phases are crys-tallographically related. Furthermore, the eutectic is easily thinned for transmission microscopy. Indeed, interfacial dislocations were observed and this report describes the nature of the dislocation networks in the boundary between the NiAl-rich ma-trix-phase and the fine chromium-rich rods.21 I) EXPERIMENTAL PROCEDURE Ingots, 3/4 in. in diam and 6 in. long were made by melting in vacuum and casting under argon using 99.9 pct pure material. The composition, in at. pct, was 33 pct Ni, 33 pct Al, and 34 pct Cr. The ingots were then placed in A1203 crucibles on a water-cooled base, melted by means of induction, and withdrawn from the hot zone at the rate of 1 in per hr under argon.* * T his material was first directionally solidified in this laboratory by E. R. Stover Slices were taken perpendicular to the growth direction of the directionally solidified ingot for metallography and for transmission electron microscopy. The electron transmission samples were thinned mechanically, then thinned electrolytically in A-2 electrolyte* *A-2 electrolyte: 62 ml perchloric acid, 700 ml ethanol, 100 ml butylcellosolve, 137 ml distilled H20. until a hole appeared in the foil. 11) EXPERIMENTAL RESULTS A) Optical Microscopy. The microstructure, viewed on a plane perpendicular to the growth direction, is shown in Fig. 1. The structure consists of cells or colonies of parallel chromium-rich rods in the NiAl matrix. The cells occur when there are impurities present12 or, in a ternary eutectic, if the composition is slightly off the eutectic composition. The axis of the chromium-rich rods is parallel to the growth direction except near the cell boundaries. Here the rods may assume angles to the growth direction; however, examination shows that the crystallographic relationship between the rod and the matrix remains the same. Fig. 1 includes cell boundaries where the rods formed at a large angle to the growth direction. The variation of rod position across the cells made it possible to Fig. 1-Structure on plane perpendicular to growth direction. Rods near cell walls are at large angle to growth direction. Magnification 315 times.

Jan 1, 1970

By P. J. Spencer, J. N. Pratt

The vapor pressure of manganese over liquid Mn-Sn alloys has been determined by a high-temperature torsion-effusion technique. Alloys containing from 8 to 100 at. pct Mn were investigated in the temperature range jrom 1280" to 1580" and the measured pressure values were used to calculate the partial and integral thermodynamic properties of the liquid alloys. The activities show small negative departures from ideality while the integral heats and excess entropies of mixing are asymmetric inform, changing from positive to negative with increasing manganese content. The possible contribution of various factors to the observed thermodynamic properties is discussed. COMPARATIVELY few thermodynamic data are available for manganese alloy systems.&apos; Therefore, as part of a continuing program of studies of the thermodynamic properties of transition metal alloys, measurements have been made on various binary alloys involving this element. In recent publications,2~3 investigations of liquid Mn-Cu alloys and of the Mn-Au system in both solid and liquid states have been reported. For the first-mentioned system the work suggested that magnetic interactions may be responsible for the observed form of the thermodynamic properties, while in the second the influence of the electrochemical factor appears to be dominant. The present paper describes a similar study of liquid Mn-Sn alloys. Again the thermodynamic properties have been obtained from vapor pressure measurements made by use of a high-temperature torsion-effusion technique.4 A detailed description of the apparatus and of the experimental procedures used in alloy preparation and pressure measurement may be found elsewhere.2&apos;4 EXPERIMENTAL RESULTS Sixteen alloys, ranging in composition from 8 to 100 at. pct Mn, were prepared from spectroscopically standardized manganese of 99.99 pct purity and tin of 99.999 pct purity, both supplied by Johnson-Matthey and Co., Ltd. One-gram samples of the alloys were obtained by carefully weighing appropriate amounts of the pure components into an effusion cell; this was then suspended in the apparatus and the metals melted together in situ by heating under vacuum to approximately 1550°K. After allowing sufficient time for a homogeneous liquid alloy to be formed, vapor pressure measurements were commenced. These were determined as rapidly as possible at a series of steady temperatures within the range of interest. The duration of experimental runs on individual samples was kept sufficiently short to ensure insignificant varia- tion of alloy composition during investigation. After completing pressure measurements, the alloys were rapidly cooled and their compositions checked by weighing or chemical analysis. All experiments were conducted using effusion cells machined entirely from boron nitride. Measurements were made using a variety of cells with orifice areas ranging from 0.0032 to 0.0075 sq cm and lengths of the order of 0.04 cm; the usual effusion correction factors for orifice geometry and molecular distribution were calculated using Freeman and Searcy&apos;s equation5 and had values between 0.6 and 0.75 for the orifices employed here. The vapor pressures of manganese over the alloys were measured at approximately 20°K intervals in the temperature range 1280" to 1580°K. In view of the close approximation of the measured pressures to Clausius-Clapeyron behavior in the experimental temperature range, the data for each alloy have been expressed by equations of the form: logp(atm) =-A/T + B A least-squares computer treatment was applied to the vapor pressure values in order to obtain the coefficients A and B with their associated error. The resulting equations are listed in Table I, together with the equation for pure solid manganese obtained from a previous study.4 To minimize the effect of possible apparatus calibration errors, the activities and partial free energies of manganese in the alloys were calculated by initial reference to the latter equation, obtained from identical torsion-effusion measurements. The immediately resulting thermodynamic quantities, based on a solid manganese reference state, were then converted to refer to the more appropriate supercooled pure liquid manganese standard; tabulated values of the free energies of solid and liquid manganese from Hultgren et al.&apos; were used for this purpose. Partial entropies of solution of manganese were calculated from the temperature coefficients of the free energies and partial heats from the Gibbs-Helmholtz relationship.

Jan 1, 1969

By J. G. Balkestein, J. W. R. Baerts

During an attempt to develop a method for accurate, rapid, continuous analysis of ash content of wal, the Dutch State Mines Laboratory found that the absorption coefficient for X-rays was related to ash content. This relationship was utilized in the development of an apparatus called CendreX, used to measure the absorption and in turn the ash content. The principle, procedure, accuracy, and applications of the CendreX automatic determination of ash in coal are discussed in detail. Until recent years coal preparation research was concentrated on the possibilities and efficiency of preparation equipment. Ever increasing demands for quality in coal, however, have caused researchers to become concerned with quality control. One of the characteristics strongly influencing quality (calorific value) and, consequently, the price of coal is ash content. Both customer and producer require that the ash content be controlled. To make this possible it is necessary for the producer to collect samples from the coal stream in the washery and to determine their ash content. On the strength of the results obtained the production process can then be adjusted, if required. Until recently incineration was the only method for determining ash content. When coal is incinerated with oxygen, it takes at least 15 min to determine the ash content. Even then some time may be lost in passing on the data. Therefore, this discontinuous and time-consuming method does not make a suitable starting point for checking, re-adjusting, or modifying the production process. Since it was not possible to accelerate incineration by mechanization and automation, another type of rapid continuous analysis had to be found. This would have to depend on some coal characteristic closely linked with ash content. At the Central Laboratory of Dutch State Mines, Dijkstra and Sieswerda found that the absorption coefficient for X-rays was suitable for this purpose. An apparatus based on the measurement of this characteristic was developed. Named CendreX,* this patented equip- *A Stamicarbon N. V. registered trademark. ment, used in combination with a sampler and conditioning apparatus, permits continuous determination of ash content with satisfactory exactness to within 3 min.t At the American Mining Congress meeting of May 1961, Log A. Updegraff, surveying aspects of continuous analyaia, reported on the CendreX appartus (Mining Congress Journal, August 1961). Since the first Condition for correct ash determination, whatever the method used, is always a sample taken in the right way, some practical aspects of sampling will be discussed first. SAMPLING In coal handling operations, each grain has its characteristic properties. In both the cross-sectional and longitudinal direction of the product stream the mixture of these grains is imperfectly blended. The elimination of the factor of segregation between the cross-sections from the direction of the stream is the principal aim of continuous analysis. Therefore, the samples to be analyzed are withdrawn in various places from the segregated product stream in such a way that they form a semi-continuous flow. In order to be truly representative of the product stream, the sample flow must fulfil two conditions: 1) The sample flow must be sufficiently large to insure that adventitious differences between the composition of the product stream and sample flow will be as small as possible. 2) All grains through the entire cross section of the product stream must have an equal chance to get into the sample flow. Since there is always a segregation through the cross section the sample flow will have a bias if the sampler collects only part of this section. In order to prevent the volume of the sample flow from becoming too large, the cross sections are taken discontinuously. However, this discontinuity gives rise to the adventitious differences that arise between the composition of product stream and the sample flow, and these differences become greater and are more deranging as the fluctuations follow each other more quickly. Moreover, the intervals between the morrnents of sampling mean a delay in the analysis. The aim will, therefore, be to collect small samples, or in other words thin cross-sectional increments, taken at sufficiently high frequencies. The following points should also be taken into account: 1) The smallest dimension of the openings in the sample collector must be equivalent to at least 3 d in

Jan 1, 1962

By T. M. Morris

A SEARCH of the literature reveals that no measurements have been made of the forces acting between a small solid particle whose surface is hydrophobic, and an air bubble to which the solid adheres, both immersed in water. Analyses have been made of the forces acting to support a greased solid on the surface of water, and the forces acting to cause a solid, whose surface is hydrophobic, to adhere to an air bubble in water. The latter analysis T. M. MORRIS, Junior Member AIME, is in the Department of Metallurgical Engineering and Mineral Dressing, School of Mines and Metallurgy, Rolla, Mo. New York Meeting, February 1950. TP 2734 B. Discussion of this paper (2 copies) may be sent to Transactions AIME before Feb. 28, 1950. Manuscript received May 16, 1949. This paper is the result of work done for part of a doctor&apos;s thesis at the Missouri School of Mines and Metallurgy. is often incomplete, however, because the internal pressure of the bubble has been neglected. It will be demonstrated that the internal gas pressure is not a negligible factor when dealing with bubbles of the size encountered in flotation. A study of the forces acting between an air bubble attached to a large flat surface is informative. It must be borne in mind, however, that this is not the condition present in a flotation cell, where the particle is small compared to the size of the bubble. The bubble is allowed to spread to its maximum contact angle on a large flat surface in the first case, whereas in the second case, the spread of the bubble is limited to the surface of the small particle which is presented to the bubble. Kabanov and Frumkinl studied the forces acting to cause adhesion of bubbles of hydrogen to a large surface of mercury, which served as an electrode in a dilute sulphuric acid solution. The force acting to hold the bubble to the mercury surface was found to be the vertical component of the surface tension between hydrogen and the sulphuric acid solution. The forces tending to cause the bubble to separate from the mercury surface were found to be: (1) the force exerted due to the internal pressure of the bubble acting upon the area of contact between the bubble and the mercury surface, and (2) the buoyant force of the bubble minus the hydrostatic force acting at the base of the bubble. These investigators photographed bubbles that were just on the verge of separating from the mercury surface. From these photographs, they measured the contact angle between the mercury surface and the tangent to the hydrogen-solution interface at the point of contact between bubble and mercury surface. They calculated the volume of the bubble and the internal pressure of the bubble. The equivalence between the upward acting and downward acting forces was remarkable. Wark2 pursued an investigation similar to that of Kabanov and Frumkin, and at the same time. His deductions verified those of Kabanov and Frumkin. He also considered the conditions present in flotation and was aware of the effect of the internal pressure of the bubble. Further, he proposed several conditions under which a small solid particle would adhere to an air bubble in water. In 1922, Edser," an English physicist, made the following statement. "It must be remembered that no particle could float stably, but for the possibility of variation of the contact angle, for if this were a constant, a slight tilt would inevitably cause the particle to sink." Wark criticized this statement, maintaining that the contact angle does not vary. The experimental data to be presented indicates that Edser was correct. Experimental Procedure: Briefly, the experimental procedure was as follows. A bubble of air was generated in distilled water. A rod of known diameter, one end of which was water repellent, was attached to this bubble. The weight of the &apos;rod was measured. The internal pressure of the bubble was measured with a manometer. The hydrostatic head from the surface of the water to the bottom of the rod was measured. The angle between the horizontal projection of the end of the rod and the tangent to the bubble at the circle of contact be-

Jan 1, 1951

By T. M. Morris

A SEARCH of the literature reveals that no measurements have been made of the forces acting between a small solid particle whose surface is hydrophobic, and an air bubble to which the solid adheres, both immersed in water. Analyses have been made of the forces acting to support a greased solid on the surface of water, and the forces acting to cause a solid, whose surface is hydrophobic, to adhere to an air bubble in water. The latter analysis T. M. MORRIS, Junior Member AIME, is in the Department of Metallurgical Engineering and Mineral Dressing, School of Mines and Metallurgy, Rolla, Mo. New York Meeting, February 1950. TP 2734 B. Discussion of this paper (2 copies) may be sent to Transactions AIME before Feb. 28, 1950. Manuscript received May 16, 1949. This paper is the result of work done for part of a doctor&apos;s thesis at the Missouri School of Mines and Metallurgy. is often incomplete, however, because the internal pressure of the bubble has been neglected. It will be demonstrated that the internal gas pressure is not a negligible factor when dealing with bubbles of the size encountered in flotation. A study of the forces acting between an air bubble attached to a large flat surface is informative. It must be borne in mind, however, that this is not the condition present in a flotation cell, where the particle is small compared to the size of the bubble. The bubble is allowed to spread to its maximum contact angle on a large flat surface in the first case, whereas in the second case, the spread of the bubble is limited to the surface of the small particle which is presented to the bubble. Kabanov and Frumkinl studied the forces acting to cause adhesion of bubbles of hydrogen to a large surface of mercury, which served as an electrode in a dilute sulphuric acid solution. The force acting to hold the bubble to the mercury surface was found to be the vertical component of the surface tension between hydrogen and the sulphuric acid solution. The forces tending to cause the bubble to separate from the mercury surface were found to be: (1) the force exerted due to the internal pressure of the bubble acting upon the area of contact between the bubble and the mercury surface, and (2) the buoyant force of the bubble minus the hydrostatic force acting at the base of the bubble. These investigators photographed bubbles that were just on the verge of separating from the mercury surface. From these photographs, they measured the contact angle between the mercury surface and the tangent to the hydrogen-solution interface at the point of contact between bubble and mercury surface. They calculated the volume of the bubble and the internal pressure of the bubble. The equivalence between the upward acting and downward acting forces was remarkable. Wark2 pursued an investigation similar to that of Kabanov and Frumkin, and at the same time. His deductions verified those of Kabanov and Frumkin. He also considered the conditions present in flotation and was aware of the effect of the internal pressure of the bubble. Further, he proposed several conditions under which a small solid particle would adhere to an air bubble in water. In 1922, Edser," an English physicist, made the following statement. "It must be remembered that no particle could float stably, but for the possibility of variation of the contact angle, for if this were a constant, a slight tilt would inevitably cause the particle to sink." Wark criticized this statement, maintaining that the contact angle does not vary. The experimental data to be presented indicates that Edser was correct. Experimental Procedure: Briefly, the experimental procedure was as follows. A bubble of air was generated in distilled water. A rod of known diameter, one end of which was water repellent, was attached to this bubble. The weight of the &apos;rod was measured. The internal pressure of the bubble was measured with a manometer. The hydrostatic head from the surface of the water to the bottom of the rod was measured. The angle between the horizontal projection of the end of the rod and the tangent to the bubble at the circle of contact be-

Jan 1, 1951

By Carl Altstetter, Roy Adams

Measurements of enthalpy changes and transformation temperatures me reported for the fcc -hcp marten-sitic transformation in pure cobalt single and multi-variant crystals andpolycrystalline specimens. From these measurements the free-energy difference between the two phases was calculated for both heating and cooling and for repeated cycles through the transformation. For heating of single crystals the average value of enthalpy change was 113 cal per mole but on cooling it was 84 cal per mole. This difference is interpreted in terms of lattice imperfections which are introduced during transformation. A calorimeter suitable for measurement of enthalpy changes of athertnal transformations is described. COBALT exhibits an allotropic phase transformation at around 417°C&apos; where an hcp phase (a = 2.507, c = 4.0686, c/a = 1.6228)~ stable at low temperatures transforms to an fcc phase stable up to 1495°C. The transformation has a hysteresis of about 30°C— the exact magnitude of the hysteresis depending on the number of transformation cycles, grain size, impurity content, and prior treatment.&apos;-6 The athermal character of the transformation and surface relief due to transformation shear indicate that the transformation is martensitic. Pole mechanisms for the transformation have been discussed by Sebilleau and Bibrin, Bilby, Seeger,&apos; and Basinski and Christian. These authors have proposed that the cooling transformation is effected by rotation of a Shockley partial dislocation around a pole dislocation with a screw component of 2a/3(111). Such a rotation would change the stacking of close-packed planes from the abcabc fcc stacking to the ababab hcp stacking sequence. This mechanism would predict a lattice correspondence of {111}fcc~~(0002~cp, have been observed. One would expect the heating transformation to occur similarly, involving dislocation movements on the (0002)hcp. However, a high density of pole dislocations and high dislocation ve- locity are required to account for microscopic observations. Furthermore, the high back stress developed on the Shockley partial dislocation as it rotates toward the sessile dislocation associated with it makes it doubtful that this is in fact the transformation mechanism. A mechanism for spontaneous nucleation of partial dislocations1*l2 seems more reasonable. If a single crystal of cobalt is cycled through the transformation but never heated above 600°C, it will remain single."13 However, if the specimen is heated through the transformation and held for a short time at or above 1000°C before cooling, the cooling transformation usually involves all four {lll}fcc habits, resulting in neighboring orientations of hcp differing by 70.5 deg. This condition is termed multivariance and has been observed by Bibring and sebilleau5 and Nelson and ~ltstetter.&apos; The latter authors used single crystals of cobalt grown in an electron beam zone refiner. They proposed that the strongly directional cooling caused the initial cooling transformation to occur on the {lll)fcc most nearly perpendicular to the temperature gradient. Transformation shear on one set of {lll}fcc planes immobilized dislocations on the other {lll}fcc planes involved in the initial transformation. Since there is only one (0002)hcp plane orientation, the product of subsequent heating transformations could have no more than two variants—the original fcc orientation or its twin. If, however, the specimen was annealed at a high temperature, such as 1000°C, there would be relaxation of dislocations into low-energy configurations, and in the absence of a sharp temperature gradient transformation on all four (111 Ifcc planes could occur. If a dislocation mechanism is responsible for the transformation, the perfection of the lattice should affect the reversibility of the transformation. Mutual constraints of neighboring grains in polycrystalline material would inhibit dislocation movement resulting in increasingly sluggish transformation. Indeed, Nelson and Altstetter found the M, to decrease and the A, to increase in going from single crystals to multi-variant specimens to polycrystals. The effect is enhanced by decreasing the grain size of a solid specimen or a powder.6&apos;14 Data on the free-energy difference necessary to initiate the transformation gives information about the driving force of the transformation. This is an important consideration in the understanding of the transformation mechanism. The free-energy change associated with the transformation of the hcp phase to the fcc phase at some temperature T different from the equi-

Jan 1, 1969

By S. Stopek, E. D. Hinkley, R. H. Rediker

Epitaxial heterojunctions have been prepared by melting the lower -melting-point semiconductor of the interface between two dijferent semiconductors. when the temperature is reduced, the melted material recrystallizes, having alloyed into the higher -melting-point semiconditctor. The electrical and elcctro-optical properties of such single-crystal heterojunctions between GaAs and Gash and between p-type InAs and n-type Gash are the subject of this paper. The forward current varies as exp (AV), where A is substantially independent of temperatuve. For Gds-Gash heterojunctions at temperatures above, 370°K, if the current-voltage relationship were to he expressed as exp (qV/nkT), then n would he less than unity. The injection luminescence associated with forward current is, for the most part, characteristic. of the lower bandgap semicondutctor. These results can he explained by carrier injection into the lower bandgap semiconductor by tunneling through a barrier at the interface. The photovoltaic effect measured for incident photons having energies in the range between the bandgaps of the two semiconductors is much smaller than that produced by higher-energy photon The smallness of this between -the-gap photovoltaic response can he explained by the low probability for penetration of the barrier by the carriers produced in the smaller -bandgap semiconductor. THE technique of interface alloying has been used to produce single-crystal junctions between dissimilar semiconductors.&apos; Oriented wafers are placed on a carbon heater strip, Fig. 1. so that semiconductor S1, which has the lower melting point, is supported by semiconductor S2. Electrical current passed through the heater strip produces a temperature gradient such that S2 is at a higher temperature than S1. As the temperature is raised the lower face of S1 begins to melt. Before the entire wafer can melt, however, the heater-strip current is turned off and, as illustrated in Fig. l. the melted portion recrystallizes, having alloyed into S2. Junctions have been fabricated by the above procedure between GaAs and germanium, between GaAs and GaSb, and between InAs and GaSb. Mroczkowski, Lavine. and Gatos have described the metallurgical and chemical aspects of the GaAs-Ge junction.2 The transition from GaAs to germanium is not monotonic and a portion of the recrystallized region consists of the GaAs-Ge eutectic. Since gallium is an acceptor and arsenic is a donor in germanium, since germanium dopes GaAs, and since the electrical properties of the GaAs-Ge eutectic have not been investigated, any interpretation of the electrical characteristics in terms of simple heterojunction theory would be incorrect. That the rectification of GaAs-Ge heterojunctions is not a property of the impurity doping of the GaAs or the germanium, but is most probably due to the impurity distribution in the recrystallized region, is clear from the fact that forward conduction occurred for all the GaAs-Ge interface-alloy junctions (whether they be n-n,n-p. p-n. or p-p) when the germanium was biased positively. The electrical characteristics of these GaAs-Ge heterojunctions will not be discussed further in this paper. Electron-beam microprobe analysis of GaAs-GaSb heterojunctions showed that the transition from arsenic to antimony atoms was without structure. and that the transition occurred within a 2 to 3 region.&apos; In this paper we will describe the electrical properties of the GaAs-GaSb heterojunctions as well as electrical and electro-optical properties of the InAs-GaSb heterojunctions. A band model for the junction will be proposed which can explain these properties. ELECTRICAL PROPERTIES OF GaAs-GaSb HETEROJUNCTIONS After interface alloying. in preparation for the electrical and electro-optical experiments, ohmic contacts were made by conventional means. For example. Kovar tabs clad with tin were alloyed to n-GaAs or similar tabs clad with Au-Zn were alloyed to p-GaAs. The units were mounted and then etched. All four combinations of conductivity types

Jan 1, 1965

By John Tabor, R. B. Spivey

INTRODUCTION Shafts have been sunk in a number of ways. By and large, however, most have been sunk by drill, blast, muck, and slip form methods. Most methods have provided satisfactory means of completion. The major drawbacks to the conventional methods have been: (1) un- reliable cost estimates for completion; (2) unreliable rates of progress; and (3) unreliable integrity of the shaft lining. Recently , engineering design studies have been done that strongly indicate, that, by the use of existing proven technology, shafts can be completed faster, more cheaply, safer, and with a better lining that has been possible using conventional methods. THE METHOD The alternate method utilizes the techniques of big hole drilling, shield excavator tunnelling, and pre-cast concrete lining. Big Hole Drilling - Drilled shafts have been completed for several years and I don&apos;t intend to address the technology, only to point out the use of drilled shafts is an alternate method of shaft sinking. Ideally, in a multi-shaft mine, the first shaft would be blind bored and cased to a size, whereby it can handle the muck from the excavation of subsequent shafts. It should be an 8&apos; to 10&apos; completed diameter. The cost of such a shaft in sedimentary formations compares favorably with a conventional shaft. However, it is much faster. For additional shafts, the role of the drill is to complete small holes (3&apos; to 4&apos;) to the desired horizon. This is merely a hole to allow slashing to a larger size with easier muck removal from an underground drift connected to the previously drilled shaft. The smaller holes, just as the larger one, should be cased and grouted into place so as to assure a smooth open hole. SHIELD EXCAVATOR Theory and History - Tunnelling Shields have been in common use for several decades, and steam powered shields were used in England over 100 years ago. The purpose of the shield is to provide temporary ground support, protect personnel during operation, and to house the excavating equipment. The excavating equipment approach has varied from attempts at a continuous or semi-continuous boring machine, the tunnel mole, to a mechanical or hydraulic digging arm. The shield may or may not be an active digging element. If not active, the boring tool or cutter is advanced ahead of the shield to full diameter and then the shield is moved up to the cutter, or the shield advances along with the cutter. If active, the cutter opens a conical free face, and the shield is either jacked forward so that the leading edge spalls rock to the free face or poling plates are thrust forward to spall to the free face. In either approach, various methods of muck removal are incorporated into the shield. These may be gathering arms, conveyors, or with moles, hydraulic transport, where the cuttings are sufficiently fine. The efficiency of the muck removal system is critical as excavation is rapid and the system could easily become muck-bound. Application to Shaft Sinking- Technically, the use of a shield to sink vertical shafts is no different than a tunnelling operation. It is, in fact, less complex in most respects. Muck and water removal are difficult in a blind-driven shaft. However, where an underground opening is available for handling muck and water, rapid shield sinking is possible, using a pilot hole for muck and water to fall through and be removed from below. The Tabor Mining Shield is basically a caisson approach, whereby, the ground is only seen at the face or bottom. It does have hydraulic jacks to force it downward and has segmented cutting edges which allows forepoling ahead of the shield. The hydraulic excavator allows mining in the center of the face around the previously drilled hole with the forepoling segments slabbing to this free face. First, the drilled hole is cased and grouted. The machine is a tube with an excavator. The work cycle is as follows: (1) The casing and grout are cut at predetermined intervals by shaped charges. (2) The casing is crushed by the excavator, removed from the hole and hoisted to the surface. (3) The excavator then rips out a face around the hole by digging the formation in tension and breaking the pieces

Jan 1, 1982

By M. C. Flemings, T. Z. Kattamis

Dendrite morphology and grain size were studied in bulk samples of iron and nickel base alloys under-cooled up to 300°C. In the alloys studied, dendrite morphology gradually changes with increasing undercooling from the usual dendritic structure to a structure composed of cylindrical dendrite arms. At a critical undercooling of approximately 170°C in these alloys there is an abrupt transition to a fine-grained structure of spherical morphology. Final dendrite-arnz spacing of melts nucleated at less than the critical undercooling decreases with increasing undercooling and with decreasing distance from a chilled surface. Grain size of melts nucleated at greater than the critical undercooling decreases similarly with these factors. It is concluded that structure coarsening, with reduction of surface area as driving force, is the principal mechanism determining final dendrite-arm spacing in melts nucleated at small undercoolings and grain site in melts nucleated at large undercoolings. IN solidification of highly undercooled melts, nuclea-tion and growth of the solid is accompanied by a rapid release of latent heat of fusion. The heat release is sufficiently rapid in bulk specimens that it takes place essentially adiabatically with respect to the surroundings; hence the specimen heats up ("recalesces") to some maximum recalescence temperature. For bulk liquid metals and alloys, a simple thermal balance shows the undercoolings obtainable in bulk samples are not sufficient to lower the maximum recalescence temperature below the equilibrium solidus temperature. Hence, some liquid always remains at the end of recalescence; this liquid must solidify by rejection of heat to the surroundings. Metals, including iron and nickel base alloys, normally freeze with only a few degrees of undercooling. In general, nucleation begins on impurity particles present in the metal, at a "heterogeneous nucleation temperature" that is quite close to the equilibrium liquidus temperature. Very small droplets of metal can be undercooled considerably before nucleation occurs,1-4 presumably because subdivision of the liquid reduces the probability of solid impurity in a given droplet. Following early work on metal droplets,&apos; a series of studies has shown that it is possible, without great difficulty, to undercool bulk samples of many metals and alloys. Undercoolings obtainable are approximately two tenths of the melting point for nickel, iron, copper, and other metals and alloys.5-9 Specimen sizes have generally been in the range of 50 to 500 g. Studies on undercooling to date have been concerned primarily with techniques of undercooling and with nucleation and growth kinetics. Only limited consideration has been given to dendrite morphology in under- cooled alloys. One such study, in bulk Cu-Ni alloy,8 showed that at small undercoolings a typical dendritic structure was obtained. At undercoolings the order of 175°C the structure of a Cu-40 pct Ni alloy became "ray or starlike", and a dense network of subbound-aries appeared. At still larger degrees of undercooling, of the order of 250°C, the structure became more random and included an ensemble of globular forms. Comparable results were obtained by walker10 on Cu-Ni alloys, and by Kamenetskaya et al.11 in research on Cu-Ni, Sb-Bi, Fe-Ni, and Fe-Cr alloys. In this work, study was made of the processing parameters influencing dendrite morphology and grain size in undercooled alloy melts. Experiments were specifically designed to show the effects of coarsening ("ripening") during solidification on final casting morphology. EXPERIMENTAL PROCEDURE Apparatus used was patterned after that of Walker,10 Fig. l(a). Melting was by induction under reduced pressure of helium. Two different types of crucible materials were used; there was no difficulty in obtaining substantial undercooling in both types of materials. Alumina crucibles were used for the bulk of the runs made, with a glass coating separating the metal from the crucible walls. Other runs were made using fused silica crucibles with or without slag coating. A graphite susceptor was employed around the crucible to aid in melting and to reduce melt stirring. The major portion of the experimental work was on

Jan 1, 1967

By C. S. Matthews, M. J. F. Rosenbaum

The purpose of thir work wax to lcarn it~lzut infori~lation could he obtained from various typs of pilot water floods and to attempt to find the optunum pilot patter11, for a revervoir which had previously been depleted by a solution gas drive. The study was made in the laboratory with mathemetical methods a dynamic analog and a potentiotnetric analog. Results werp tested against the field llistorics of a nrrnlber of pilot water floods. At a reasonable valrre of currzulative injection, the total production rate for the one-injector five-spot should reach about 6.5 per cent of injection rate, and for a four-injector five-spot, about 9 per cent. Accurate estimates of ultimate recovery cannot be made on the basis of such snzall prorluction rates. However, with a pilot composed of nine ir1jector.s and 16 producers the production rate is approximately 50 pcr cent of injection rate at a reasonable value of camulative injection. Sonle inforn~ation for extended performance predictions might he obtained from such a large pilot. These conclusions were drawn on the basis of results obtained for unit mobility ratio, and a sturly using tlre potentiometric analog was made of the effect of other mobility ratios to determine the range of applicability of these predictions. For the four-injector, five-spot pilot with the ratio of production to injection rate (before water breakthrough) is about twice that for with it is about two-thirds; and with M0= 10, it is about one-third For high mobility ratios, it was found that the production rate increased considerably as water-cut increased. These result can be used to modify, qualitatively, the inter.pretntions based on curves for the unit rnobilit\. ratio CaSeS. It was found that the maximum ratio of production rate to injection rate obseriled in field pilot floods was of rhe scime order as that prerdicted by these methods. The time required to reach thisr maximum did not generally agree with the time predicted for a homogeti~orir reservoir. The differcrlce between predicted and observed time of response gives an indication of the permeability profile and of the condition of the producin,g wells. Pilot water floods of the pattern type are generally carried out in reservoirs which have been depleted by solution gas drive and are at low pressure. Under these conditions, oil and water can be considered incompressible. It is assumed that, as the water is injected, an oil bank forms ahead of it and that there is a distinct interface between the water zone (or bank) and the oil zone (or bank) and between the oil zone and the region ahead of the oil zone. It is further assumed that only gas is mobile in the unflooded (gas) region, only oil is mobile in the oil bank and only water is mobile in the water bank. The saturations and the mobilities associated with each zone are assumed uniform. We idealize our reservoir to be homogeneous, horizontal and of constant thickness. Effects of gravity within the producing layer are assumed negligible. If the actual time-dcpendent flow problem is approximated by a acries of steady-state problems. the potential and stream function in the oil bank and water hank satisfy Laplace&apos;s equation in two dimensions. We can therefore use a poteiitiometric analog of this system. Potentiometric models have yielded uscful results in this laboratory&apos; and clsewhere in the study of a variety of secondary recovery problems. For the case where M = I, we generally prefer to use theoretical mcthods as well as a simpler dynamic analog. Except where otherwise noted, the ratio, side of five-spot/wellbore radius. is taken to be 3,600. a figure which corrcsponds to a normal-size wellbore in a 10-acre well spacing. THEORETICAL EVALUATION OF VARIOUS PILOT PATTERNS, Mw0 = 1 <&apos;he theoretical models which we used to examine the performance of various pilots are shown in Fig. 1. Image theory was used to determine the ratio of production rate to injection rate as a function of the volumc of the flood. The ratio of production rate to injection rate was chosen because this is an easily measurable quantity which is characteristic of a pilot

By D. A. Elgillani, M. C. Fuerstenau

With either sulfonate or oleate as collector, quartz responds to flotation with moderate additions of calcium only at moderately high pH, where some portion of the activator has hydrolyzed to caOH+ . Calculations of the concentrations of various ionic and precipitated species of calcium and collectors suggest that the products of [(CaOH+) (RSO3)] and [(CaOH+)(01-)] determine whether flotation is obtained under specific conditions. Ion products on the order of 10-12 were calculated for both the sulfonate and oleate systems. The activating effect of calcium ion in nonmetallic flotation systems is of considerable interest because of the normal presence of calcium in natural water. As a result, this phenomenon has received quite some attention in the past. Kraeber and Boppel1 showed that quartz could be activated by calcium above pH 10 with sulfonate as collector. The feasibility of selectively separating quartz from hematite with calcium activation at relatively high pH was demonstrated by Clemmer, Clemmons, Rampacek, Williams, and stacy.2 Cooke and Digre3 showed with a bubble pick-up method that the minimum quantity of calcium ion required as activator for complete pick-up of particles occurs at pH 11.5 for an addition of 20 mg per liter sodium oleate. They also showed that larger additions of calcium (10-fold increase per unit decrease of pH) must be added for complete bubble pick-up as the pH is reduced. Schuhmann and Prakash,4 using a vacuum flotation technique, found that quartz could be floated with moderate additions of calcium chloride and oleic acid at neutral pH, providing the metal ion was present in stoichiometric excess over the quantity needed to form the normal soap with oleic acid. They also reported that calcium will function as an activator only in basic media. More recently, Eigeles and volova5 have shown that essentially complete flotation of quartz is obtained with 6 x 10-4 mole per liter calcium chloride and 1.7 x 10-5 mole per liter sodium oleate at pH 11.6. while no flotation is obtained at about pH 10.9 and below. The importance of adsorption of activator and collector at the air-liquid interface is also demonstrated in these systems. The important role that metal ion hydrolysis assumes in quartz activation systems was also demonstrated recently.6-8 A detailed investigation of metal activation in sulfonate flotation of quartz was undertaken in one system7 and yielded a number of interesting and important observations. Quantification of the data of this system7 to the extent desired was not possible, though, because certain species could neither be ignored nor accounted for accurately. These difficulties can be circumvented when calcium is involved as activator. This detailed analysis was undertaken to obtain a more quantitative explanation of calcium and metal ion activation in quartz flotation. EXPERIMENTAL MATERIALS AND METHODS Sodium alkyl aryl sulfonate9 mol wt 450, and pure potassium oleate were used as collectors. All other reagents used were reagent grade in quality, i.e., n-amyl alcohol as frother, KOH for pH adjustment, and calcium chloride. Conductivity water, made by passing distilled water through an ion exchange column, was used in the investigation. Quartz was prepared by leaching the sized sample (48 x 150 mesh) with HC1 until no iron could be detected in the leach liquor. The experimental equipment and procedure were the same as that described previously.6,10 EXPERIMENTAL RESULTS As the presence of precipitates was noted in all of the systems to which ca++ and collector were added, experiments were undertaken to determine the solubility products of calcium sulfonate and calcium oleate using a nephelometer. With this technique, collector is titrated into a known solution, which in this case was 5 x 10-5 mole per liter CaCl2 at pH 5.5. Upon precipitation of the calcium-col lector salt, e.g., calcium oleate, light is scattered and detected

Jan 1, 1967

By John E. Hockett

The need for basic information about the relationship between resistance to dejormatim (flow stress), temperature, strain, and strain rate, for the solution of metal-fovming problems, is pointed out. Some early attempts to satisfy the need are mentioned. A brief description of a machine called a Cam Plastome-ter is given, including the processing of results of testing in the machine. Next, a program of testing aluminum in compression over a wide range of constant true-strain rates (0.1 to > 200 sec-1) and a modevately broad range of temperatures (223° to 673°K) is described. The results of this program are presented in the form of true-stress us true-strain cuvves. The data in these curves are presented in the form of relationships between true stress and true-strain rate in sermilogarithmic and log-log form, as functions of temperatures—for several true strains. Finally, true stress, for a given true strain, is displayed as a function of log true-strain rate and absolute temperature, i.e., a surface. SINCE the publication of Hill&apos;s book1 on plasticity theory, increasingly rapid advances have been made in analytical solutions to forming problems. Methods in common use are the slab method, the uniform deformation energy method, the limit analysis method, the slipline field method, and the semiexperimental method called "visioplasticity". These approaches, and examples of their use, are covered in detail by Johnson and Melloor2 and by Thornsen, Yang, and Kobayashi.3 unfortunately, practically all of the above work has had to rely upon a number of basic assumptions, e.g., homogeneous deformation and Coulomb (sliding) friction; and virtually no dependence of the mechanical behavior of the deforming metal, upon temperature, strain, and strain rate, has been included. It is with this dependency that this paper is concerned. Loizou and sims4 looked at the above relationship for lead using both a constant compression-speed Cam Plastometer and a constant true-strain-rate Cam Plastometer designed by Orowan.5 Alder and Phillips8 investigated the relationships for aluminum, copper, and steel in the same constant true-strain-rate Plastometer. cook7 tested twelve steels at temperatures ranging from 1170° to 1473°K in the same Plastometer over a range of true-strain rates of 1.5 to 100 sec-&apos;. The writer tested commercially pure aluminum at room temperature and depleted uranium at temperatures from 573" to 873°K at strain rates from 10-3 to 1.0 sec-1 in a Cam Plastometer designed and built at Los Alamos Scientific Laboratory.8 During the past few years the Cam Plastometer at Los Alamos has been used for a number of relatively minor experiments on brass, mild steel, duralumin, Armco iron, and depleted uranium. In this time the machine has been continually modified and improved. It was decided to utilize fully the wide range of strain rates now available with the machine by testing a material about which some information was already in the literature. Prior work on commercially pure aluminum6 appeared to deserve confirmation and expansion. So it was decided to explore the resistance to compression of this material over the currently available range of constant true-strain rates and a convenient range of temperatures. This paper is a report of that exploration. I) EQUIPMENT AND PROCEDURE The principal item of equipment is, of course, the Cam Plastometer, the working part of which is shown in Fig. 1. In this figure, an aluminum specimen may be seen between two tungsten carbide platens, in position for a room-temperature test. Above the upper carbide platen is a load cell. Output from the load cell is amplified and applied to a galvanometer in a recording oscillograph. Auxiliary equipment includes the oscillograph, the control console, a counter, and a time-mark generator. The counter is first used in adjusting the time base. Then it registers the count, of sixty pips per revolution generated by the rotating cam, in each second. These pips and the time base are also applied to galvanometers in the oscillograph. Thus, load, time, and cam position are recorded simultaneously. Heating of a specimen prior to compression is done

Jan 1, 1968

By S. Feuerstein, L. Rice

The effect of low pressures on the flow and fracture behavior of molybdenum is described. For poly crystalline samples, room-temperature tensile tests indicate greater ductility under 10 Torr than under intermediate pressures up to and including atmospheric pressure (760 Torr). In addition, tests conducted at 760 Torr under atmospheres of air, dry nitrogen, and purified argon exhibited no apparent difference in mechanical properties. Critical tests involving baking in situ as well as those involving single-crystal deformation further imply that the ductility effect is a pressure-dependent phenomenon related only to the fracture process. This dependency is discussed in terms of adsorption and diffusion contributions. THE effect of very low pressures on material properties has heretofore been presumed to be important only for substances possessing relatively high vapor pressures at ambient temperatures. Research has therefore been concentrated primarily on organic solids and liquids, and in some instances on metals such as zinc and cadmium. Most vacuum-effect studies&apos; on the mechanical behavior of metals have been performed under conditions of either cyclic loading or creep rupture at elevated temperatures, i.e., over extended time periods. These studies were not restricted to high vapor pressure materials but also encompassed such metals as gold, copper, and nickel. Very little concern, however, was placed upon the importance of a vacuum environment on the mechanical behavior of metals subjected to a simple unidirectional deformation at ambient temperatures. A tension test is generally of short duration as compared to a creep test, and at room temperature vacuum effects if any would be expected to be surface-limited. In early 1963, Kramer and podlaseck2 reported a change in the bulk flow behavior of aluminum single crystals during room-temperature tension tests. The deformations were performed under pressure conditions of 760 to 3.4 X 10-8 Torr and indicated for the first time a vacuum surface effect contributing to the bulk tensile behavior of metal specimens. As a consequence, an experimental program was initiated in this Laboratory to study the effects of ultrahigh-vacuum conditions on the mechanical behavior of metals. The results of a preliminary study on poly-crystalline molybdenum3 revealed, unlike Kramer&apos;s observations of changes in the stress-strain behavior, only an increased ductility under ultrahigh vacuum. Flow behaviors were nearly identical for all tests re- gardless of pressure. This paper presents comprehensive results obtained in this area of research. 1) EXPERIMENTAL PROCEDURE Three material categories were used in this study: sintered and are-cast polycrystalline molybdenum of nominal purity 99.93+ pct and single-pass electron-beam zone-refined molybdenum single crystals having a nominal purity level of 99.99+ pct. The interstitial levels (weight percent) as determined by the Materials Testing Laboratories, Division of Magnaflux Corp., were as follows: sintered molybdenum (C— 0.005, H—0.0004, O—0.015, N—0.008); and arc-cast molybdenum (C-0.0038, H-0.0003, O-0.015, N-0.023). Single-crystal molybdenum obtained from Materials Research Corp. had a typical interstitial analysis of C-0.0015, H-0.00007, O—0.00045, and N-0.0001. Tensile specimens having a 5 mm diam by 50.8 mm length were prepared from these materials. An average grain diameter of 0.059 mm was obtained for the sintered specimens following a 4-hr, 1600°C heat treatment. Grain sizes from 0.019 to 0.149 mm were obtained in the arc-cast specimens following heat treatments from 1100° to 1600°C for 1 hr. This series of specimens was used exclusively for the grain-size effect studies. All samples were electrolytically polished in 97 pct sulfuric acid solution prior to testing. Experiments were performed at room temperature in an ion-pumped ultrahigh-vacuum system positioned in an Instron tensile machine, Fig. 1. A constant strain rate of 4.2 x 10-4 sec-1 as derived from crosshead displacement was assumed for the deformations. Starting vacuums ranged from 2 to 0.5 X 10-10 Torr. These pressure measurements were made using corrected values4 of an NRC Redhead gage. Comparative readings were also made against a G.E. triggered dis-

Jan 1, 1967

By D. A. Elgillani, S. Atak, D. A. Rice, M. C. Fuerstenau, R. B. Bhappu

Quartz and feldspar cannot be floated with sulfonate at any pH; spodumene floats over a narrow acid pH range, while beryl responds moderately over a broad pH range. After wet-grinding in a steel mill, beryl, quartz, and spodumene float well with sulfonate below about pH 7, whereas the improvement in the response of feldspar is not so marked. A mechanism by which iron can be adsorbed on these minerals is presented. Also, the responses of leached, natural, and wet-ground beryl to amine, sulfonate, and oleate flotation are shown and related to the measured zero-points-of-charge of these materials. Earlier work with leached beryl showed that good flotation could be obtained with alkyl aryl sulfonate over a rather wide pH range using a Fagergren flotation cell.&apos; When a similar response was observed with leached quartz, it was decided that unintentional activation was being obtained from the metallic components of the Fagergren cell. To obviate this difficulty, a microflotation cell was designed, and an experimental technique was devised. These have been described elsewhere. Experiments conducted with the small cell showed that leached quartz could not be floated at any pH with any sulfonate addition,3 which is in agreement with the observations of Kraeber and Boppel.4 Similarly, it was also found that leached beryl responded to sulfonate flotation only over a narrow pH range rather than the broad range reported earlier.1 This early work,1 however, revealed the important effect that wet-grinding in a steel mill has on the flotation response of certain silicates. That is, it was found that quartz and especially beryl floated well over an unusually wide pH range after wet-grinding in a steel mill. Microcline, however, floated poorly below pH 4, even though wet-ground under the same conditions. The work of Eigeles6 on adsorption of oleic acid on leached quartz and iron-contaminated quartz at constant pH is in agreement with these flotation data. Other research has shown that ferric iron, added as a salt to the system, functions as an activator in the narrow pH range in which Fe +++ iron hydrolyzes to its hydroxy complexes.3,5 These phenomena indicate that iron functions differently in flotation systems depending on its method of introduction. The object of this paper is to determine the mechanism by which iron is adsorbed on certain minerals, the mechanism of collector adsorption after iron abstraction, and the role that Fe++ and Fe+++ assume in the selective separation of these minerals. EXPERIMENTAL MATERIALS AND METHODS Sodium alkyl aryl sulfonate, mol wt 450,7 pure potassium oleate, and pure dodecylamine were used as collectors. All other chemicals were reagent grade in quality, i.e., n-amyl alcohol as frother; HC1, H2SO4, and KOH for pH adjustment; and ferric chloride as activator. Conductivity water, made by passing distilled water through an ion exchange column, was used in the experimental work. All minerals used in the investigation were hand-picked specimens. Sample Preparation: Each of the minerals was crushed through 8 mesh, and the product was divided into two groups, one to be ground dry and the other wet. Dry grinding was accomplished with an alumina mortar and pestle. The product was dry-screened to 48 x 150 mesh, cleaned magnetically, deslimed in conductivity water, and dried. Preparation of the samples by wet-grinding involved grinding a 200-g charge of the mineral (-8 mesh) at 60% solids with natural water in a mild steel rod mill for four minutes. This charge was then wet-screened immediately with natural water to 48 x 150 mesh, dried, and cleaned magnetically. Some experiments were also conducted with leached beryl and quartz. These products were prepared by leaching the sized sample (48 x 150 mesh) with concentrated HC1 with a percolation technique until no iron could be detected in the leach liquor. Following this step, the sample was rinsed with conductivity

Jan 1, 1967

By Ralph Hultgren, Prodyot Roy

Manganese vapor pressures from 1250° to 1500°K were measured by conventional Knudsen and torsion-effusion methods in twelve Fe-Mn alloys with compositions from 9 to 80 at. pct Mn. The Knudsen re-sults agveed approximately with previous measurements found in the literature which indicated the solutions were nearly ideal. However, except for the higher manganese compositions, the initial torsion readings indicated much (up to 50 pct) higher vapor presszcres than the Knudsen method. These high readings decreased steadily with time. The results are interpreted as due to depletion of surface concentration of manganese during evaporation. Thus the initial torsion readings are the most nearly correct and Knudsen methods on alloys are to be regarded with suspicion unless it can be demonstrated that diffusion rates are rapid enough to replenish surface concentrations depleted by evaporation. For the lowest manganese contents and highest temperatures, depletion causes initial torsion readings to be too low. FEW thermodynamic data are available for alloys of the high-melting transition metals due primarily to experimental difficulties at the high temperatures involved. Measurement of vapor pressure is one of the most promising techniques to be applied to this problem. From the vapor pressure of a component of an alloy phase, its activity or its partial molar Gibbs energy can be directly calculated. From measurements over a sufficient range of temperatures and compositions the partial and integral Gibbs energies, enthalpies, and entropies may be determined through Gibbs-Duhem integration. For solid phases of variable composition, which commonly are found in alloys, measured vapor pressures are low because of depletion of the surface concentration of the more volatile component as it is selectively vaporized. Diffusion from the interior tends to restore the depleted concentration. The seriousness of the effect depends on the relative rates of diffusion and vaporization. Although depletion has been recognized as a factor,&apos; direct measurements of its rate are lacking and quantitative estimates of its effect on measurements are uncertain. In the present work the vapor pressures above a series of Fe-Mn alloys have been measured by the torsion-effusion method. This method permits a measurement of the vapor pressure of manganese as soon as the sample comes to temperature and continuously throughout the run. The rate of decline of the apparent vapor pressure measures the rate of depletion and the torsion reading at zero time should be correct. At high manganese concentrations (70 and 80 at. pct Mn), the torsion reading remained nearly constant; surface depletion was negligible. There was a slow drop in measured pressure due to bulk loss of manganese from the sample. However, for lower manganese contents, especially at high temperatures, the depletion effect was considerable and the apparent vapor pressure decreased steadily with time. For these alloys the Knudsen method should give pressures which are too low. The measurement of pressure in the Knudsen method cannot be made until enough manganese has been vaporized to be weighable. The Knudsen result is therefore an integrated average between the initial and final vapor pressures. To verify this, conventional Knudsen measurements were also made with results in approximate agreement with previously published Knudsen measurements for these alloys. As expected, for the lower manganese contents the initial torsion readings of pressure were as much as 50 pct higher than the Knudsen. THE APPARATUS The apparatus, shown in Fig. 1, is capable of operating to temperatures up to 2000°K. A vacuum of 5 x 10"6 mm Hg can be maintained. Temperatures were measured to +3° by a W-Re thermocouple placed in the dummy cell, N. The torsion cell consisted of two alumina crucibles with holes in their covers. They were placed in the molybdenum holder shown suspended from the torsion wire. Rectangular torsion wires (1 by 4 mm) were found to have superior sensitivity and less residual distortion than circular (2-mm-diameter) wires. The precision of angular measurement was found to be *0.025 deg; the variation is no doubt due to temperature fluctuation and vibration. For the Knudsen experiments the alumina cell was set on the support, N. SAMPLE PREPARATION 800-g samples were prepared by melting together electrolytic iron and electrolytic manganese and pouring the melt into a water-cooled copper mold. Melting and pouring were done under a helium at-

Jan 1, 1965

By W. L. Phillips

Stress-train curves were obtained for single crystals of silver, Ag-5 pct Zn, Ag-10 pct Zn, and Ag-20 pct Zn tested in tension and shear at 78°, 195°, and 297°K. At room temperature the critical resolced shear stress gC increased, the length of&apos; the easy-glide region increased, and the rate of&apos; work hardening dwving easy glide decreased with increasixg zinc concentration. The change in the ratio of uc at room temperature to that at lower temperatures was significantly greater for the alloys than for pure silver. It was found that an increment in stress was necessary to continue slip when the slip direction was rotated 60 deg. The magnitude of this increment increased with strain for all alloys, increased with zinc concentration for a given strain, and for a given strain increased with decreasing -temperature. DESPITE its practical importance in improving the mechanical properties, alloying is not fully understood. Except for copper alloys few sets of systematic data are available. Von Goler and Sachs&apos; studied the deformation of Cu-Zn alloys of increasing zinc content and found that, for dilute alloys, the critical resolved shear stress increases linearly with concentration. The range of easy glide was found to increase with increasing zinc content. Schmid and seliger,2 Sachs and Weerts,3 and Osswald4 have shown that with Mg-A1, Au-Ag, and Cu-Ni crystals, respectively, the critical resolved shear stress also varies linearly with concentration. More recently, Linde and his coworkers have investigated the variation of the critical shear stress of copper alloyed with tin , antimony, indium, germanium, silicon, nickel, and gold. They found that the slope of the critical resolved shear stress is related to the change of lattice parameter with composition, and also to the difference in Goldschmidt&apos;s atomic diameter between solvent and solute atoms. Garstone, Honey-combe, and creetham6 have shown that similar relationships can be found for small additions of silver, gold, and germanium to pure copper. They found that, with increasing silver or gold concentration, the critical shear stress for glide is increased by alloying, and so is the range of easy glide, which reaches as much as 60 pct for 0.50 pct Ag alloy and 0.62 pct Au alloy, as compared to 6 pct for pure copper of similar initial orientation. They also found that the alloying additions had little effect on the rate of hardening during easy glide, the slope scarcely changing with increasing alloy content. General secondary slip was detected only when the crystals began to harden rapidly. Although the slip appeared to be very fine in the early stages of deformation, coarser slip bands were formed towards the end of the extensive easy-glide range. The present investigation describes the deformation characteristics of single crystals of Ag-Zn containing different concentrations of zinc. Tension and shear testing were used for this study. EXPERIMENTAL PROCEDURE The method of growing the single crystals, sample preparation, and method of testing have been described in detail previously.&apos; EXPERIMENTAL RESULTS A) Tension-Room Temperature. The initial orientations and stress-strain curves of single crystals of silver, Ag-10.0 pct Zn, and Ag-20.0 pct Zn are shown in Fig. 1. It is evident that there is considerable change in the stress-strain characteristics as a function of zinc concentration. The effects of zinc concentration on the critical resolved shear stress for both CU-zn8 and Ag-Zn alloys are summarized in Fig. 2. At all concentrations the resolved shear stress of the Cu-Zn alloys is higher than that of the Ag-Zn alloys. The resolved shear stress increases parabolically as a function of composition for both alloy systems. The length of easy-glide region increased with increasing zinc concentration, Fig. 3b). As the length increased the slope (do/de) decreased slightly, Fig. 3(b). Metallographic investigations demonstrated two significant effects of increasing zinc concentration. First, the amount of clustering increased, compare Figs. 4(a) and (b). The slip lines changed from uniform in pure silver to clustered in the Ag-20 pct Zn and Ag-30 pct Zn alloys. Second, the amount of cross slip decreased as the amount of clustering decreased.

Jan 1, 1968

By E. T. Turkdogan, J. H. Swisher

The solubility of oxygen in zone-refined iron was determined in the temperature range.from 881" to 1350°C. The solubility in a iron at 881°C ms found to be about 2 to 3 ppm; in y iron, the solubility was found to increase from about 2 to 3 ppm at 950°C to about 25 ppm at 1350°C. The permeability of oxygen in an iron -0.1 pct Al alloy was determined in the y iron range, using an internal oxidation technique. By combining the permeability and solubility data, the diffzisivity of oxygen in y and a iron was calculated. The oxygen diffusivity in solid iron may be s~immarized as follows: 8820 For 6 iron and IN a recent paper, Hepworth, Smith, and Turkdogan1 reported on the solubility, permeability, and diffusivity of oxygen in 6 iron, together with permeability data for oxygen in a iron. In the present investigation, similar measurements were made in the ? phase region. In addition, a solubility measurement was performed in the a phase region to permit calculation of the diffusivity of oxygen in a, iron. References to early work on this subject are given in the previous publication.&apos; EXPERIMENTAL Solubility Measurements. The oxygen solubility was determined by equilibrating cylindrical samples 0.3 in. diam by 14 in. long of zone-refined iron in water vapor-hydrogen gas mixtures. The zone-refined iron was prepared by B. F. Oliver of this laboratory, using an apparatus and technique described elsewhere.2&apos;3 Six zone-melting passes were used to achieve a total impurity level of about 30 ppm. Of this 30 ppm, the combined nickel and cobalt content was about 20 ppm, oxygen was 4 ppm, and all oxidizable impurities less than 1 pprn each. A vertical resistance furnace wound with molybdenum wire was used for the experiments. The temperature was measured before and after each experiment with a Pt/Pt-10 pct Rh thermocouple. In the gas train, flow rates of hydrogen and argon were measured with capillary flow meters, and the resulting mixtures were passed through a column containing 90 pct oxalic acid dihydrate and 10 pct anhydrous oxalic acid to obtain predetermined ratios of H2O to H2. The vapor pressure of H2O above this mixture as a function of temperature is well-known.4 The exit gas was ana- lyzed periodically for H2O, and good agreement (+3 pct) with the calculated composition was obtained. The zone-refined iron specimens were held in the furnace for a sufficient length of time for equilibration, e.g., 18 hr at 1350°C and 1 week at 881°C, then quenched in a brine solution. After removing the surface oxide from the samples by machining, duplicate analyses were obtained by a combined vacuum fusion-infrared method; oxygen analysis was reproducible within 2 ppm. Permeability Measurements. The permeability of oxygen in alloys containing about 0.1 pct A1 was determined by internal oxidation and measurement of the subscale thickness as a function of time. The experimental alloys were prepared by adding aluminum to electrolytic iron (grade 104A plastiron) that had previously been vacuum-carbon deoxidized. The resulting ingots contained about 20 ppm O, 100 pprn C, 40 pprn Si, 50 ppm Mo, 20 ppm P, 20 ppm S, and 20 pprn Zr as the principal impurities. After hot rolling the ingots to 1-in.-thick slabs, specimens were machined from the stock in the form of rectangular plates, 4 by 5 by 2 in. The general procedure for the permeability experiments was the same as those for the solubility measurements. The specimens were cooled in a reducing atmosphere rather than quenched, however, in order to maintain a clean surface for measurement of the sub-scale thickness. This measurement was made on a polished cross section of each specimen, using a microscope with a micrometer stage. The inclusions formed at the lowest temperature 1033°C were too small to be seen with an optical microscope. An electron micrograph showing the size and shape of individual particles is shown in Fig. 1. The dark band in the picture is a boundary between two subgrains. The subscale thickness in these samples was measured with an optical microscope after heavily etching in 2 pct nital, which gave contrast between the subscale and the unoxidized zone.

Jan 1, 1968

By N. S. Stoloff, R. C. Ku, R. G. Davies

The stress-strain behavior of Fe-Co and Fe- V alloys containing up to 25 pct solute have been studied in the temperature range 25° to - 196°C. The microyield stress is independent of temperature for all alloys studied, while the temperature dependence of the ordinary yield stress is large and comparable to that for unalloyed iron. An alloy-softening phenomenon is observed for many alloys relative to unalloyed iron, and appears to be a consequence of removal of inter-stitials from solution and their subsequent agglomeration. The ductile to brittle transition temperature is increased markedly by both cobalt and vanadium. Transmission electron microscopy observations reveal that cross slip and cell formation are restricted with increasing solute, which can account for many aspects of yielding and fracture behavior. IRON and other metals of bcc structure slip on many planes of the (111) zone at moderate and elevated temperatures, giving rise to wavy glide. At low temperatures, however, there is a tendency for slip to be restricted to planes of only one or two crystallographic types; in the case of Fe-Si alloys for example, (110) glide predominates, giving rise to planar slip bands."&apos; Restriction of cross slip at low temperatures in iron has been linked by Brown and Ekvall3 to increased strain hardening in the preyield microstrain region, leading to an apparently large temperature dependence of the yield stress. Support for this view has been provided by Lawley and Gaigher4 from a transmission electron microscope study of molybdenum. They concluded that dislocations at lower temperatures, by virtue of their inability to change planes readily, are unable to interact and annihilate, leading to an increase in internal stress and work-hardening capacity. Restriction of cross slip at low temperatures has also been suggested to be an important factor in determining the ductile to brittle transition of single-phase solids, including metals of bcc structure.5 It is pertinent to note that most solute elements tend to raise the ductile to brittle transition temperature of poly crystalline ferrite,6,7 although in some cases, e.g., Fe-Cr7 and Fe-Al,8 the dilute alloys may actually yield at lower stresses than unalloyed iron. It appears, therefore, that solute elements may have an effect analogous to lowering the test temperature with regard to restricting cross glide. Such an effect has indeed been observed in the ionic alloy system KCl-KBr,9 in which bromine atoms, although causing little misfit and consequently little effect on the yield stress of KC1, have a pronounced effect in restricting wavy glide and inducing brittleness. The purpose of the present investigation was to determine the effects of selected solute atoms on the yield stress and fracture behavior of iron, and to elucidate in turn how the slip character was related to these properties. Since it is known that interstitial atoms exert a strong influence on the mechanical behavior of iron, the solute elements chosen for study were vanadium, which reacts strong with interstitials,10 and cobalt, which does not form highly stable interstitial compounds." EXPERIMENTAL PROCEDURE Four-pound ingots of each of the following alloys were vacuum-melted in zirconia crucibles: Fe-1, 5, 10, 25 at. pct Co, and Fe-1, 4, 10, 20 at. pct V. An ingot of unalloyed iron from the same original stock as that used for the alloy was remelted under similar conditions to eliminate variations in interstitial content arising from differing thermal histories. Chemical analyses of the iron, cobalt, and vanadium melt stock are listed in Table I. All ingots were rolled and swaged, commencing at 850°C, to 1/4-in.-diameter bar. The bars were then annealed at 850°C for 1 hr (except that the 10 and 20 pct V alloys were heated for 2 hr) to give a uniform equiaxed grain size of about 0.05 mm. Tensile samples of 0.125 in. diameter by 0.8 in. gage length were utilized for studies of the ductile to brittle transition. A second set of tensile samples were utilized for microstrain experiments in which strain sensitivity of 1 x 10"6 was achieved by a capacitance method.3 Cylindrical compression samples 0.250 in. diameter by 0.4 in. long also were prepared to study the influence of composition on the macroscopic yield stress, and for metallographic analyses of defor-

Jan 1, 1965

By W. F. Hosford, E. W. Kelley

Deformation studies have been conducted at room temperature on single crystals of magnesium and magnesium alloys with thorium and with lithium. Single crystals oriented to suppress shear on the easily activated basal slip systems were deformed by plane-strain compression. Compression along the C axis was accommodated by {1011} banding. Compression perpendicular to the unconstrained c axis activated {1012} twinning, and, after virtually complete twinning, deformation continued by {1011) banding in the twinned material. Compression perpendicular to the constrained c axis was accommodated by the simultaneous operation of (1012) twinning against the constraint and (1011 ) banding. Although this orientation was favorable for {1010)(1210) prism and {1011}(1~10) pyramidal slip, these modes were not observed in pure magnesium or in Mg-0.5 pct Th. However, {10i0)(1~10) prism slip was observed in crystals of Mg-4 pct Li during compression perpendicular to the constrained c axis. Fracture in all materials occurred parallel to (1124) or {l~il) depending on the orientation and composition of the specimen. THE mechanical behavior of the hcp metals is strongly anisotropic. Although several slip systems have been reported the slip is cpmmonly in the directions of closest packing, the (1210),&apos; and this does not produce strains parallel to the c axis. Hence the inherent anisotropy. The deformation mode most easily activated in magnesium at room temperature is (0001)(1210)- basal slip. Also {1010}(1~10) prism slip and {1011)(1210) pyramidal slip have been reported, primarily at elevated temperatures.2"4 However, at room temperature the shear stresses to activate the prism and pyramidal modes are roughly a hundredfold greater than that required for basal slip.&apos;j4 Thus prism and pyramidal slip may be expected only under special conditions of loading. Strains normal to the basal plane can be produced by twinning, however. Many twinning modes have been reported for magnesium,&apos; with (1012) twinning the most common and relatively easy to activate. Magnesium can deform by (1012) twinning when stressed along the c axis jn tension, but not in compression. In contrast, (1011) twinning is activated by compression along the c axis and not by tension. In addition to primary twinning, secondary twinning or slip can occur within the reoriented material of primary twins.&apos; In general at least five independent shear systems must be active to bring about an arbitrary shape change such as that in the individual grains of a deforming polycrystalline material.&apos; Because basal slip can_ provide only two independent shear systems and (1012) twinning can only accommodate an extension of the c axis, other deformation modes must be active in magnesium for an arbitrary shape change to occur. The purpose of this investigation has therefore been to study the various deformation modes in magnesium at room temperature, with special emphasis on those modes that are less easily activated. The effect of the alloying elements, thorium and lithium, has also been investigated. In polycrystalline aggregates, unambiguous identification of deformation modes is extremely difficult and the direct evaluation of the resolved shear stresses to activate them is not feasible. On the other hand, uni-axial tension and compression experiments on single crystals may not activate some of the- deformation modes because basal slip and/or {1012) twinning cannot be suppressed in most orientations. However, it should be possible to activate all possible deformation modes using oriented single crystals and plane-strain compression. Identification of active deformation systems and evaluation of the resolved shear stresses required to activate them should be facilitated. Wonsiewicz and Backofen have recently completed an investigation of the plasticity of pure magnesium crystals at various temperatures utilizing plane-strain compression and selected crystal orientations. This technique has also been used in the present work. The seven orientations selected for study are indicated in Table I. Plane-strain compression along the c axis (orientations A and B) should activate some deformation mode _other than basal, prism, or pyramidal slip, or (1012) twinning. In orientations C and D, prism or pyramidal slip would be expected to take place. When the compressive load is applied perpendicular to an unconstrained c axis (orientations E and F) the three slip modes should be suppressed but not (10i2) twinning. In orientation G, basal slip should occur.

Jan 1, 1969

By F. A. Forward, V. N. Mackiw

The paper relates to the laboratory and pilot plant studies that have been carried out by Sherritt Gordon Mines Ltd., Metallurgical Research Div., in developing the ammonia pressure leach process for extracting copper, nickel, cobalt, and sulphur from high grade nickel concentrate produced from Lynn Lake ores, and describes in some detail the chemistry of the process. IT is well known&apos;.&apos; 2 that copper, nickel, cobalt, zinc, ferrous iron, and a number of other metals combine with ammonia in aqueous solution to form complex ions of the form [Me(NH,)x]"+. The stability and solubility of these ions depend on the concentration of the metal ion in solution, on the amount of NH, present, and on the amount and type of anions present, e.g., OH-, C0;-, NO,, C1-, SO;-. If ammonia is partially or completely removed from such solutions, for example by boiling, the soluble ammines tend to decompose and the metals precipitate as basic salts. These properties of metal ammines have found practical application in the commercial recovery of copper, nickel, and cobalt from a variety of ores. In an operation formerly conducted at Kennecott"" the mill tailing containing 0.80 pct Cu as copper carbonate was leached by percolation with an ammonia-ammonium carbonate solution to dissolve the copper as the ammine. At Calumet and Hecla0-" With a mill tailing containing about 0.4 pct Cu as metallic copper, it has been found necessary to aerate the ammonia-ammonium carbonate leach solutions between stages to oxidize the solubilized copper. At Nicarol"-" where nickel and cobalt occur as oxides and silicates which are not soluble in ammonia, the ore is heated to decompose silicates and to selectively reduce the nickel and cobalt to metal, leaving the iron as Fe,O,, and is then leached with ammonia-ammonium carbonate solution accompanied by aeration to dissolve nickel and cobalt as ammines. In each of these leaching operations, the anion present is CO, and the metals can be precipitated from the leach solution as oxide (copper) or hydroxide and carbonate (nickel and cobalt) by boil- ing off NH, and C02 both of which are recycled to treat a subsequent ore charge. The products-—oxide, hydroxide, or carbonate—can be treated by conventional smelting, calcining, or electrolytic methods to convert them to refined metals. Thus the procedures mentioned utilize the properties of the ammines to extract copper, nickel, and cobalt from nonsulphide ores and separate them from the leach solutions. These processes have the advantage that they can be carried out in closed vessels at atmospheric pressure, that the leaching solutions are specific for the desired metals, that the metals can be recovered as relatively pure compounds by the boiling operation, and that the NH, and CO, can be recycled. Also, as the leach solutions after boiling and filtration are substantially free of metals, NH,, and CO,, they can be discarded, thus facilitating the control of the water balance in the leaching circuit. When, as is the case with Sherritt Gordon concentrates, sulphides are treated with ammonia solution in the presence of oxygen, the leach solution contains SO,--, and an entirely different set of conditions is encountered. The ammine sulphates (of nickel, for example) are more soluble than the carbonates and can be only partially decomposed by boiling. The SO, and NH, in the solutions can not be recovered by boiling. Thus, despite the more favorable leaching conditions resulting from high solubility of the ammine sulphates, the recovery of metals, NH,, and SO, from the solutions must be effected by other means. Sherritt Gordon Nickel Concentrate Treatment The Ni-Cu-Co flotation concentrate produced at Lynn Lake&apos;" contains 12 to 16 pct Ni, 1 to 2 pct Cu, 0.2 to 0.5 pct Co, 33 to 40 pct Fe, 28 to 34 pct S, 8 to 20 pct insoluble, and less than 0.02 oz per ton precious metals. The nickel is present chiefly as pentlandite, the copper as chalcopyrite, and the iron as pyrrhotite and pyrite. Most of the cobalt is thought to be present in pentlandite, although it is known that a small amount occurs as Co-Ni-pyrite.

Jan 1, 1956