By P. N. Anyalebechi

"The as-cast microstructure of two commercial-size ingots of aluminum alloy 3004 produced by the electromagnetic casting process was quantitatively characterized. This involved the quantitative determination of through-thickness and across-width variations in dendrite cell size, grain size, macrosegregation of alloying elements, interparticle spacing, and the types, volume fractions, and sizes of the constituent or second phase particles. More than ninety-five percent of the constituent phases in the ingots consisted of the A16(Mn,Fe) phase; the desirable a-Al 12(Fe,Mn)3Si phase was not detected in any of the ingots by Guinier X-ray diffraction analyses or electron probe X-ray microanalyses. A significant microstructural heterogeneity through the thickness and across the width of both ingots was observed. For example, macrosegregation, and the sizes of the constituent phase particles, dendrite cells, and grains increased concomitantly from edge to mid-width and from surface to center of the ingots. There was a -20% depletion (negative macrosegregation) of Mg and a +54-87% enrichment (positive macrosegregation) of Ti in the center of the ingots. With the exception of grain size, there was no significant microstructural difference between the two ingots examined. The causes and practical implications of the observed microstructural heterogeneity in the ingots are discussed.IntroductionThe first step in the fabrication of majority of wrought products of aluminum and its alloys is the casting of large ingots or billets of simple shapes (round or rectangular). The sizes of the ingots vary from 10 mm to 450 mm diameter or 25 mm to 780 mm thick. The quality of the finished products is established at the ingot casting stage. This is because the microstructural characteristics, such as secondary dendrite cell size or arm spacing, amount of alloying elements retained in solid solution, macrosegregation, and the characteristics of second phases, produced during casting cannot be reversed by subsequent processing. Up until twenty-five years ago, the effect of as-cast microstructure of large ingots on the structure and behavior of thin sheets (0.34 mm thick) during drawing and ironing processes was incorrectly assumed to be minimal or nonexistent. This was based on the erroneous notion that the thermal treatments and large reduction (>99.94%) and strain that the ingot undergoes during production of the sheets completely destroys the original ingot structure and its inherent heterogeneity. However, the effects of ingot structure can, a priori, be deduced from the observed effects of constituent phase particle size, type and volume fraction on recrystallization, development of texture during annealing and deformation, and earing. In fact, careful examination of the behavior of products produced from different size ingots or castings have shown that the original microstructure of the ingot has a direct impact on the properties and performance of the end products."

Jan 1, 2011

By Mario Sanchez, Jose Palacios, Fernando Parada

Carbon steels have less than 0.02% copper and have low atmospheric corrosion resistance. The addition of at least 0.20 wt% Cu improves this property. Also, 0.8 wt% Cu in steel shows a hardening potential for developing high strength corrosion resistant steels. Copper slags containing 42–45% of iron, silica and minor amounts of copper were used for producing Fe–Cu alloys by reducing the oxides contained in the slag to obtain a Fe-0.84 wt% Cu alloy, which could be suitable as feeding material to manufacture a corrosion resistance steel, and also would be an alternative for minimizing the copper industry ’s environmental impact, and to introduce the application of the Circular Economy concept to the natural resources exploitation, especially in countries where their economy is strongly based in mining and metallurgical extraction.

Mar 1, 2018

By Takeo Fujino, Nobuaki Sato, Junichi Hasegawa, Masato Nakazawa, Kohta Yamada

"Tantalum oxide thin films were deposited on quartz substrates by laser ablation of Ta2O5 target using Nd:YAG pulse laser. Deposition-was observed when a laser light energy higher than 200 mJ and its repetition rate higher than 3 Hz. A thin film of 0.1 µm thickness was obtained by the ablation using a laser light of 300 mJ and 6 Hz for 2 sec. The thickness of the film increased with increasing energy, repetition rate and irradiation time of laser. By the SEM observation, it was found that many island-like particles were deposited on quartz substrate forming a thin film. The obtained thin film, which was identified as ? Ta-O by X-ray diffraction, was oxidized to Ta2O5 by the heat treatment in air at I273 K for 3 h.IntroductionTransition metal oxides have a potential to show special characteristics in electrical, magnetic and/or optical properties. When such compounds are fabricated in the form of thin film, the special properties would be improved or new characters would appear in comparison with bulk materials. Tantalum penta-oxide is widely used as a capacitor since Ta2O5 shows high dielectric constants up to high temperatures. The tantalum solid capacitor has been fabricated by the electrical oxidation of sintered Ta metal cylinder followed by MnO2 film coating. However, further improvements, reduction and layered structure formation, are required for compacting the devices. The layered structure of thin films would be applicable for the above requirements. The formation ofTa2O5 film by low pressure CVD1), photo CVD2) and magnetron sputtering3l were reported. The laser ablation -method is one of the most convenient techniques for the deposition of thin films from their compounds, such as oxides. Formation of Ta2O5 film by pulse laser deposition (PLD) method using ArF excimer4), Nd:YAG (533nm)5) and TEA CO2 6 lasers was reported. In these PLD studies, ablation was carried out in relatively high oxygen pressures resulting in formation of Ta2O 5 film. In this paper, the deposition of tantalum oxide thin film by the laser ablation of Ta2O 5 using Nd:YAG pulse laser was examined at a viliety oxygen pressures ranging from 10-8 to 10 Torr. The morphology of the films was also investigated in relation with substrate temperature and oxygen pressure."

Jan 1, 2000

By Guoqiang Lv, Xi Yang, Wenhui Ma

Cast multicrystalline silicon ingots are widely used in photovoltaic manufacturing. A key issue to achieve high solar cell efficiencies is to attain an optimized temperature field during directional solidification (DS) process. This paper reports numerical investigation of multicrystalline silicon (mc-Si) ingot production using two major types of DS furnace. Specific examination is made on thermal distribution, interface shape and stress field. Evaluation is performed for the applicability of thermal system design to reduce thermal stress, improve crystal quality and enhance energy efficiency. The effects of procedure parameters and geometric configuration on temperature distribution are discussed as well to provide the viable solutions for systems optimization.

Jan 1, 2015

By Adegbenjo Adewale Oladapo, Ibitoye Simeon Ademola, Ladiipo Olufemi Akinbiyi, Adegbola Adekunle Amos, Adeboje Taiwo Bode, Raji Fatai Olasunkanmi

The combined effects of the addition of Silicon (Si) as alloying element and low temperature annealing on the tensile properties of 70/30 brass with Nickel (Ni) and Iron (Fe) contaminants is investigated in this paper. Melts of cartridge brass were made to which 0, 0.5, 1, 2, 3 and 4 wt % of Si was added. These were sand cast into rods of 600 mm by 10 mm diameter and were thereafter machined into standard tensile test samples. Some of these samples were annealed in a muffle furnace at temperatures of 250, 300, 350, 400 and 450 oC respectively and the others were used as control. Subsequently, all the heat treated and non heat treated samples were subjected to tensile tests on a Hounsfield Extensometer and the load – extension plots retrieved were analyzed. Microstructural characterizations of the samples were carried out using Accu-Scope Optical Microscope. The results showed that cartridge brasses subjected to alloying and annealing treatments had improved tensile and yield strengths. However, the tensile properties were increased and maintained within acceptable limits at stress relieve annealing temperatures.

Jan 1, 2015

By A. S. Block-Bolten

Two innovations in nickel-arsenic separation have been studied on a laboratory scale. The first requires only a nitric acid atmospheric leach without preliminary roasting and leads to favorable final conditions for precipitation of arsenic as highly stable FeAsO4, The second is an NaOH-H2O2 pressure leach which is an alternative to the known NaOH-O2 pressure leach. Either method offers the possibility of rapid and efficient separation of nickel from arsenic and is applicable, for example to the high grade niccolite deposits in the Great Slave Lake area of northern Canada.

Jan 1, 1982

By Shuqiang Guo, Xionggang Lu, Yuyang Bian, Weizhong Ding, Lan Jiang, Kai Tang, Changyuan Lu

For recovery of rare earth elements from the NdFeB based permanent magnet scraps, a high temperature process was used. Permanent magnets scraps were firstly oxidized in air. The optimal oxidation conditions under air are at temperature of 700oC holding for 30min. After the oxidation process, the oxides were reduced by graphite crucible at 1500oC under Ar atmosphere. By this way, the rare earth elements were recovered in the form of oxides, and Fe was separated to the metal phase. Boron distributed in both the rare earth oxides (REO) containing slag and the metal phase. In order to reduce the boron contents in the rare earth oxides, the carbon saturated iron bath and NdFeB added carbon saturated iron bath were used to refine the slag. By this process, the rare earth oxides with a comparatively high purity of 98.2% were gotten.

Jan 1, 2015

By Shengli Wu, Fengjie Zhang, Feng Chang, Hua Lu, Kaiping Du

In order to make a complete understanding of steel plant metallurgical dusts and to realize the goal of zero-waste, a study of their properties was undertaken. For these purposes, samples of two sintering dusts (SD), two blast furnace dusts (BFD), and one electric arc furnace dust (EAFD) taken from the regular production process were subjected to a series of tests. The tests were carried out by using granulometry analysis, chemical analysis, X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectroscopy via SEM (EDS), and Fourier transform infrared spectroscopy (FTIR). The dominant elements having an advantage of reuse are Fe, K, Cl, Zn, C. The dominant mineralogical phases identified in sintering dust are KCl, Fe2O3, CaCO3, CaMg(CO3)2, NaCl, SiO2. Mineralogical phases exist in blast furnace dust are Fe2O3, Fe3O4, with small amount of KCl and kaolinite coexist. While in electric arc furnace dust, Fe3O4, ZnFe2O4, CaCO3, CaO, Ca(OH)2 are detected.

Jan 1, 2015

By Alaina Mallard, Jannette Chorney, David Hutchins, Grant C. Wallace, Jerome P. Downey

Current commercial processes for producing ceramic carbides require temperatures of 1400–2000 °C and often use extensive milling operations to produce a powder product. A process that could reduce the energy requirements of commercial carbide production could allow for these materials to be implemented in a greater number of applications. In this study, tungstate (WO4 2−) and silicate (SiO3 2−) anions were adsorbed onto activated carbon and converted into silicon carbide (SiC) whiskers and a mixture of tungsten and tungsten carbide (W/WC) crystals via carbothermal reduction using inert and reducing gas atmospheres at temperatures much lower than what is required by current commercial processes (950 °C for W/WC/W2C and 1200 °C for SiC). The adsorption process was statistically-optimized via a central composite response surface analysis using DesignExpert 9. Inductive coupled plasma optical emission spectroscopy (ICP-OES) was used to measure, and optimize, adsorption efficiency while the carburization products were characterized using X-ray diffraction and scanning electron microscopy.

Mar 1, 2017

By D. Raghavan

In recent years, the environmental issues related to the landfill shortage received considerable importance. Many polymeric solid wastes have high resistivity to chemical and biological degradation, and options are sought by which these wastes can be recycled and reused, or reduced in volume. The present study investigated the biodegradation of polyethylene by Aspergillus niger, and biodesulfurization of rubber by pure and mixed cultures of Thiobacillus thiooxidans and Thiobacillus ferrooxidans. The fungus, A. niger, was found to metabolize portions of polyethylene. Quantitative calorimetric measurements revealed that the amorphocity of the sample decreased during biodegradation. Removal of sulfur from synthetic rubber samples containing 2 to 15% sulfur, was studied in shake flask experiments and the associated oxygen consumption was studied in Warburg respirometers. The mixed bacterial cultures were more effective in the desulfurization of rubber samples than the pure cultures of T. thiooxidans and T. ferrooxidans. The data obtained in these studies may have far reaching consequence for the development of new effective processes regarding the remediation and management of discarded polymeric packaging wastes and car tire rubber materials.

Jan 1, 1993

By J. -P. Nepper

It has been possible to largely contain converter aisle emissions of SO2 and fumes in the case of batch-wise operated Peirce Smith converters during normal blowing periods with the help of suitably designed primary hoods. Controlling the escape of off-gas during the periods of turning the converter in or out of the stack has been problematic in the past. Effective automated contro1 systems have been deve1oped for the purpose and successfully applied in smelter operations in Spain, Taiwan and Germany. This has led not only to an effective reduction of emissions in the converter environment but also to an improvement in the converter operation.

Jan 1, 1992

By M. L. Apel

A conceptual approach to the bioremediation of uranium mill tailings (UMT) is presented., This approach focuses on, biosorption to remediate the. effluent solution and bioleaching remediate the. solid fraction. Comparative biosorption studies were performed with synthetic single metal solutions using a commercially available biopolymer. The maximum rate of metal sorption by calcium alginate was found to be 5.43, 6,39, 6.48, and 9.74 mg dm-3 min-1 for U022*, Ba2+, Cd2+ and Zn2+, respectively. Activation energy (AEa) for barium uptake by calcium alginate beads was determined to be 11.5 kJ, indicating a diffusion controlled reaction mechanism. Thermodynamic values (AG+ AH+ and ASt) of the metal-alginate activated complex, as reported in the literature, were found to be in agreement with those calculated from this research. Results show that this biopolymer can be effectively applied in the removal of select metals prevalent in uranium mill tailing effluents and associated waste streams.

Jan 1, 1991

By Tao Xuea

Gold frequently occurs in nature in the form of a gold-silver alloy. Thus, investigation of the electrochemical behavior of gold-silver alloys in cyanide solution has practical significance. In this paper, the potentiodynamic method is used to determine the anodic polarization curves of gold-silver alloys (Au-10% Ag and Au-50% Ag) in cyanide solutions. To facilitate the interpretation of the results, complementary experiments conducted in NaOH solution in the absence of cyanide are also reported. The results for the Au-Ag alloys are compared with the polarization behavior of pure gold and pure silver. With the aid of potential-pH diagrams for the Au- and Ag-CN-H20 systems and electrochemical kinetics concepts, the dissolution mechanism of gold-silver alloys, the effect of the presence of silver on the cyanidation of gold, as well as the factors which control the anodic reaction rate are clarified.

Jan 1, 1998

By K. C. Liddell

"Cu/Ni multilayers exhibiting giant magnetoresistance were deposited from a single electrolyte under stepped potentiostatic control. To enable transport measurements to be made without remounting the multilayer film, we developed a novel method that involved plating on a thin metallic basal layer atop a rigid non-conducting Si substrate. Rotating ring-disk electrode techniques were used to monitor the composition and thickness of individual plated layers. Transmission electron microscopy confirmed that the interfaces between adjacent layers were sharp and that the structure of the layers was uniform throughout the film. Atomic force microscopy images indicated that the film's surface was smooth and free of defects.ELECTRODEPOSITION OF THIN MULTILAYER MAGNETIC MATERIALSI. IntroductionElectrodeposition of compositionally modulated films will in all likelihood continue to be used to produce the read heads for stored magnetic data. However, the next generation of head materials will require both improved sensitivity and reduced film thickness. Certain multi layers consisting of thin alternating ferromagnetic and nonmagnetic layers exhibit giant magneto resistance and consequently are promising candidates for read head applications. We have successfully made multilayer films with giant magnetoresistance that have total thicknesses as low as 25 nm, approximately 120 times thinner than the thinnest similar films reported in the literature. This paper describes early results from our work on electrodeposition and characterization of Cu/Ni multilayers, a model system with enhanced magnetic and mechanical properties, including the GMR effect. The structure and composition of the multilayers were determined using TEM, AFM, and electrochemical methods, and their magnetoresistance was measured by the standard four-probe technique. A novel method developed in this work enabled the transport properties of the ultrathin films to be measured reliably without the need to dissolve the cathode or handle the films. To provide a context for these results, short accounts of other work on giant magnetoresistance and multilayer electrodeposition are also included."

Jan 1, 1997

By Tiejun Chun, Jian Pan, Deqing Zhu, Vinicius Mendes

"Fine manganese fines are characterized by large amount and low price compared to lump manganese ores. However, fine manganese must be agglomerated as EAF (electric arc furnace) feed. In this paper, high quality fired pellets were produced by simulating grate-kiln process to supply the feed for EAF from some imported manganese ore fines containing high combined water. Manganese ore fines assaying 44.47wt%Mn, 5.89wt%Fe, 12.09%LOI and with 72.7wt% ranging between 0.5mm and 8mm, are pretreated up to the particle size of 84.7wt% passing 0.074mm by HPGR (high press grinding roller) twice in open circuit. The finely ground manganese fines were mixed with 1.2wt% bentonite, balled at 15% moisture for 7min in disc pelletizer. The drop numbers, compressive strength and thermal shock temperature of green balls reach 11 times/0.5m, 11 N/pellet and 360oC, respectively. After the green balls drying in the oven, the dry pellets were preheated at 1050oC for 12 min and then fired at 1300oC for 12 min in electric tube furnace. The compressive strength of fired pellets reaches 2621 N/pellet. Therefore, these pellets are high quality burden for blast furnace or EAF due to high mechanical strength and high Mn grade of 49.11wt% and low detrimental elements.IntroductionManganese, mainly using as deoxidizing agent, desulfurization agent and alloying elements, is widely used in the steel company. With the rapid development of iron and steel industry in China, domestic manganese ores cannot meet the requirement, resulting large quantities manganese ores import to China [1-4]. Compared to lump manganese ores, fine manganese ores containing high combined water are characterized by large amount and low price. However, they must be agglomerated as EAF (electric arc furnace) feed. There are three ways to agglomerate the manganese fine ores, sintering, briquetting and pelletizing [5-6]. Compared to the other two methods, pelletizing technology possesses the following superiorities, such as uniform size distribution of product, stabilizing chemical composition of product and lower energy consumption in producing. Therefore, pelletizing is a superior way to treat the fine manganese ores [7]. The systematic research of producing manganese oxide pellets by fine manganese ores containing high combined water was studied in this paper."

Jan 1, 2011

By M. Kawakami

In relation to the designing of a new-type blast furnace, the reaction of carbonaceous materials with CO2 is expected to occur at as low temperature as possible. In order to get a highly reaetive carbonaceous material at low temperature, the reaction kinetics was investigated by measuring such quantities as the reaction rate from weight loss, the amount of CO adsorption and specific surface area by BET method. The reaction rates were large in the order of the Bintyo char, metallurgical coke, graphite and glassy carbon. If the rate was converted to the rate per unit area, however, those of the Bintyo char was smaller than that of graphite. Thus, it is suggested that the rate of the Bintyo char is influenced by the pore diffusion of CO2. The rate had a positive relation with the amount of CO adsorption, showing that the rate determining step would be the desorption of CO from the active side on the surface. The rate independent of surface area was derived, combining all the obtained data.

Jan 1, 2003

By Shengli Wu, Jiacong Zhang, Mingyin Kou, Bingjie Wen, Heng Zhou

The COREX process, which is considered to be able to replace the blast furnace, still has some gaps to reach the designed productivity. The metallization degree is regarded as one of the limitations of the COREX process. In the present work, several parameters affecting the metallization degree of direct reduced iron (DRI) are analysed by SPSS software (Statistical Product and Service Solution). Melting rate, oxidation degree of reducing gas, oxidation degree of top gas, top gas consumption per ton of burden, temperature of reducing gas, and burden distribution index are con firmed as the main factors affecting metallization degree. Based on this, a linear equation has been developed for predicting metallization degree. Additionally, improving the melter gasi fier vault temperature appropriately, increasing the proportion of high volatile matter coal, and optimizing the type and particle size of iron ore and the pattern of burden distribution have been shown to improve the metallization degree.

Mar 1, 2018

By Jung-Ah Kim

Precipitated Calcium Carbonate (PCC) is obtained through calcination, hydration, and carbonation. Thus, the change in each process condition determines the particle size or morphology of PCC. To date, studies on precipitated calcium carbonate have mainly focused on process manufacturing PCC, aimed matter. Still, few studies on calcination or hydration have been conducted. Therefore, this study sought to investigate the effect of hydration condition on the synthesis characteristics of aragonite PCC. Results showed that the particle size of calcium hydroxide changed based on the variation of the initial hydration temperature. In particular, higher initial temperature resulted in the larger particle size of calcium hydroxide used in synthesis. The particle size and yield of aragonite also increased when calcium hydroxide made at high temperature was used. The water/solid ratio or total amount at the hydration time had no effect on the manufacturing process of aragonite, however.

Jan 1, 2006

By A. M. T. S. Bandara

The solubility of rare earth (RE) salts in aqueous solutions depends on many factors including the type of cations and anions in solution, their concentrations, temperature and the type of solid precipitated. Experiments were conducted using anhydrous La2(SO4)3 and Ce2(SO4)3⋅8H2O as solids and lanthanum(III) perchlorate prepared by dissolving La2O3 in HClO4 solutions as RE-sources. Solutions of H2SO4, H3PO4 and their mixtures in the presence or absence of Na+, Ca2+, Fe(III) or Al(III) as perchlorates served as test solutions. Saturated solutions and precipitated solids were assayed and characterized using standard techniques to show that the La(III) and Ce(III) ions precipitate as hydrated sulphates, phosphates or double salts with sodium, depending upon the solution composition. The change in solubility of RE-salts with solution composition and temperature is the result of the composite effect of changes in solubility products (pKSP) of salts, pKa of acids and other equilibrium constants for ion-association.

By Huyang Xie, Rishi Raj, Vera A. Versteeg

"A new method for MOCVD has been developed in which a precursor solution is directly injected into a reaction chamber. The vaporization of short pulses of liquid is facilitated by atomization with a piezoelectrically-operated nozzle. The system has been used successfully to grow oriented, thin Ti02 (rutile) films on sapphire substrates with the crystalline relationship (101)[010]R I (1120)[0001]s. A growth rate of approximately 2 monolayers per pulse was achieved at 650°C for a reactant impingement rate of about 800 monolayers per pulse. Also, epitaxial LiTaO3 thin films were grown on (0001) sapphire from a single source, bimetallic precursor, lithium tantalum hexa-t-butoxide as the precursor. X-ray diffraction shows that the LiTaOa c-axis is normal to the sapphire surface. The x-ray pole figure and crosssection TEM diffraction show that the films were also in-plane oriented, with sapphire [1010] parallel to lithium tantalate [1010]. These films are shown to have extremely low optical attenuation, and refractive index that compares well with bulk values.IntroductionMetalorganic chemical vapor deposition (MOCVD) techniques have come into increasing use in recent years, due to the growing versatility and availability of precursors and improved environmental advantages over the halogenated compounds used for conventional CVD. Most commonly, the films are deposited by dissolving the metalorganic reactant (typically a metal alkoxide) in a carrier gas, which is carried through heated lines to a heated substratel . The metal alkoxides decompose by pyrolysis, leaving the films on substrates. While this method has been used to produce excellent epitaxial and heterepitaxial films, it has the disadvantages of complexity: the precursor must be heated to fix its vapor pressure, the gas flow rate carefully controlled, and the carrier lines heated to prevent condensation before reaching the reactor. Additionally, this conventional method cannot be used with certain low-volatility precursors that decompose upon heating."

Jan 1, 1994