By Chikabumi Yamauchi, Mitsuru Tanahashi, Tsuyoshi Taniguchi, Nobuo Furuta, Toshiharu Fujisawa

"It is essential to clarify the equilibrium relations among nonmetallic inclusions of the Mn0-SiO2-CrOx system and molten stainless steel in order to control non-metallic inclusions formed by the deoxidation of stainless steel with silicon. In the present study, the phase equilibria of the MnO-SiO2-CrOx system were measured by conducting the following experiments under controlled oxygen partial pressure, Po2, at 1873 K:1) Phase equilibria of the MnO-Cr20 3 binary system were measured for Po2 = 2 x 10-6 ~2 x 102 Pa.2) Phase equilibria of the MnO-SiO2-CrOx ternary system were measured for Po2 = 2 X 10-6 Pa.Based on the results, the phase diagram of this ternary system was established under the condition of the Si-deoxidation process of stainless steel (Po2 = 2 x 10-6 Pa and T = 1873 K).IntroductionAt the deoxidation stage in steelmaking process, generally multiple deoxidizers participate in deoxidation reactions, and the composition of deoxidation products ""non-metallic inclusions"" greatly varies depending on deoxidizing efoments and their contents. In order to control non-metallic inclusions formed by the refining process of steel, it is essential to clarify the equilibrium relations among non-metallic inclusions and molten steel.Especially, during the refining process of stainless steel, nonmetallic inclusions in molten steel seem to- change as follows. After the oxidation refining, Mn-chromite is formed in molten steel as non-metallic inclusion. By the deoxidation with silicon addition (mainly less than 1 mass%), Mn-chromite inclusions are changed their compositions to Mn-silicate. Segawa et al.[l] have reported the effect of amount of silicon addition on composition and mass ratio· of non-metallic inclusions during the Sideoxidation process of 18Cr-8Ni stainless steel at 1873 K, as shown in Figuri; L At higher silicon content than 0.5 mass%, only Mn-silicate was identified as non-metallic inclusion. On the other hand, at lower silicon content, both of Mn-chromite (MnO Cr2O 3) and Mn-silicate were identified. However, the thermodynamic and the kinetic analyses of the above-mentioned Sicdeoxidation process have not been made due to lack in the thermodynamic data for the non-metallic inclusions· of the MnO-SiO2-CrOx system, such as the phase diagrams, the activities of the components, and the free energy of intermediate compounds. In relation to the phase diagram of this system, those of the MnO-SiO2 [2] and the SiO2-Cr2O 3 [3] binary systems have been only reported"

Jan 1, 2000

By Jay. M. Khodadadi, Josef Štetina, František Kavicka

"With the aid of the proper original numerical model of solidification the instruction for preparation of input parameters for numerical simulation of technological processes, with change of the phase or structure, will be presented. A method of calculation analysis of influence of therrpophysical properties of materials entering the system of casting-mould-cores environment, and also of boundary conditions on the required simulation accuracy will be suggested. For the cast material, the influence of heat .conductivity, specific heat capacity, density and latent heat of phase transformation also has been analysed. For metallic or non-metallic moulding material"" the influence of the see main parameters has been analysed and, furthermore, their combination, influence of thermal conductivity, and of heat storage. The order of influence of all quoted parameters of a casting and moulding material was established. For example heat conductivity in the liquid state is on the last place. From the boundary conditions the -most important influence on the total solidification time and · on the mechanism of forming of temperature field has the ·boundary condition on the casting mould boundary, then follows the boundary condition on the level of a molten metal. The negligible influence has the boundary condition on the mould frame and on the bottom.IntroductionThe original and universal mathematical model of solidification, cooling and heating has been set up and checked, in order to be capable of analysing a one- to three-dimensional steady or unsteady temperature field of the casting-mould-environment system and, namely, of the system as a whole or its arbitrary parts, during any industrial technological process whose individual processes could be solidification, cooling, heating, refrigeration and others, in any sequence or singly. The model enables the simulation of traditional and also non-traditional technologies of casting in foundries, metallurgical plants, forging operations, heat treatment processes, etc. If solidification is not the matter, the metal part of the system need not be called the casting but a component, a block, a forging and the like."

Jan 1, 2000

By C. M. Egert, S. Rajic

"We have developed a monolithic micro-spectrometer suitable for a variety of sensing applications including industrial process monitoring. The device consists of a solid structure with a volume less than 6 cubic centimeters. All optical components of the spectrometer including two aspheric mirrors, a diffraction grating, and entrance and exit surfaces are fabricated onto the surface of the structure. All light paths are internally contained within the structure. The result is a small, rugged spectroscopic sensor ideally suited for use as a process monitor. Due to its monolithic nature the device requires no post-fabrication alignment; nor can it be knocked out of alignment during use. Although many materials and thus wavelength regions were possible, the prototype device discussed here was produced in PMMA by precision diamond turning. However, lower cost manufacturing approaches involving injection molding are under development to produce an affordable sensor.Due to its rugged monolithic design, small footprint, and low cost the monolithic micro-spectrometer is ideally suited for distributed monitoring applications often required for industrial processes. It is expected that modified versions of this sensor designs will be required for specific applications so as to maximize the performance and resolution over the operating range. For example, the prototype device described here operates over a wavelength range of 500 nm to 1000 nm. The performance of this device as a real-time surface monitoring sensor will be discussed in detail. Our approach of using wavelength dependant scattering resulted in the reduction to practice of a miniature, monolithic, rugged, low-cost, micro-instrument in a sensor sized package. The process sensor applications community has been faced by the cost versus performance issue. Simple go/no-go sensors are typically inexpensive but they provide very limited and sometimes dubious data. Scaled down traditional instruments offer very good measurand information but are typically cost prohibitive, fragile, and still relatively large. This work will bridge the gap between these two extreme sensing alternatives."

Jan 1, 1997

By W. John Rankin

The finite and non-renewable nature of mineral resources poses unique challenges for sustainability: How can mineral and material needs of society be satisfied indefinitely? How can the benefits of exploitation of minerals best be captured for present and future generations? How can the environmental problems caused by large scale mining and processing best be ameliorated? These issues are rarely addressed, or if so only incidentally, in traditional courses in geology, mining, metallurgy and materials yet addressing them will increasingly be a major role for professionals in the minerals and materials industry and related sectors and agencies. This paper describes a framework for examining these and other sustainability issues related to meeting future material needs from non-renewable resources. The framework may be useful for educational purposes, either as the basis of a dedicated subject or by including the elements of it throughout a traditional course in relevant subjects.

Jan 1, 2014

By L. L. Tavlarides, N. V. Deorkar

"Recovery/Recycling of metal ions from industrial process waste streams is a preferred alternative to disposal by conventional techniques. This paper presents methods for preparation of inorganic chemically active adsorbents to be used in fixed bed adsorbers. Methods for immobilization of chelating agents on the inorganic supports are discussed. The prepared adsorbents are characterized to determine coverage density of functional groups, effect of pH on metal ion removal efficiency, regeneration efficiency and uptake capacity. Results from the laboratory scale and bench scale experiments are presented here.IntroductionRemoval of heavy metal ions from processing wastes in various industries is an important problem. Waste streams in electroplating, electronic, catalyst preparation and hydrometallurgical industries contain metal ions such as copper, nickel, chromium, lead, tin, cadmium, silver, gold and platinum. One major concern for the non-ferrous metal industry is secondary recovery of precious metals and cyanide from cyanide leachate from smelter residue and hydrometallurgical waste streams.Recovery methods recently considered include evaporation, electrolyte metal recovery, reverse osmosis (1), adsorption, ion exchange (2,3), membrane separation (4,5) and Solvent extraction. These processes have met with various levels of limited success. The use of liquid ion exchange molecules to selectively extract metal ions for on-site treatment of these waste streams is currently receiving substantial interest (6,7). This interest seems from an awareness of the advances made in the development of commercial extractants for metal ion separation in hydrometallurgical industries (8). However, separation by solvent extraction processes is generally considered to be economical in the range of aqueous metal ion concentrations from 0.01 to 1.0 mol/lit (9). In order to exploit the selectivity of chelating agents, the idea of immobilizing chelating agent into a solid matrix has attracted growing attention in recent years. Many supports such as inorganic oxides, organic polymers, cellulose powder and polyurethane foam can be used for immobilization of chelating agents. Over the last decade, considerable efforts have been directed toward attachment/introduction of chelating agents into a polymer matrix (10,11). Inorganic supports as compared to polymer supports provide high mechanical strength, chemical and thermal stability, and high reaction rates due to open pore structure. On the contrary, organic resins shrink and swell, thus affecting mass transfer (12). Many of the disadvantages of polymer supports can be excluded by the use of inorganic supports. Innovative use of immobilization techniques can produce inorganic chemically active adsorbents with comparable capacity, stability and reaction rates. Consequently, the objective of our program is the development of inorganic chemically active adsorbents to be used in a fixed-bed unit operation as an alternative heavy metal ion recovery process. Methods of preparation of inorganic chemically active adsorbents, (ICAAs) characterization and applications are discussed in this paper. A brief summary of the results from laboratory scale studies and bench scale studies is presented."

Jan 1, 1996

By L. I. Rosato

A novel hydrometallurgical process for the recovery of silver and gold from neutral leach residue that is based upon leaching with thiourea, is described. Laboratory and pilot plant studies have shown that 80-90% of the silver and 60-70% of the gold can be recovered by:? ( i) leaching zinc calcine with 'Spent electrolyte at pH 2.0-3.0 to generate a precious metal-bearing zinc ferrite residue, (ii) leaching of the thickened zinc ferrite with 3-5 g/L thiourea in a six stage carbon-in-pulp circuit, (iii) elution of silver and gold from the loaded carbon with a thiourea- butanol solution, (iv) thermal regeneration of the stripped carbon and (v) recovery of the precious metals from the pregnant eluate by cementation with zinc dust. The reasons for adopting the thiourea CIP leach and the preferred operating parameters for each process step are presented. The requirements for the destruction of any thiourea transferred to the zinc circuit are outlined, and the results of an integrated one tonne/day pilot plant operation at Canadian Electrolytic Zinc are given.

Jan 1, 1990

By Hebi Yin

A two-dimensional finite element solidification model was developed to simulate the transport phenomena occurring during laser deposition of AISI 410 stainless steel during the Laser Engineered Net Shaping (LENS®) process. The molten pool geometry and the distribution of temperature, solute concentration and velocity were calculated during deposition of a thin wall plate. An analysis of the simulations results revealed the importance of heat transfer by both conduction and convection as well as the roles of the driving forces for convection in the molten pool. The heat transfer and the flow pattern in the molten pool are considerably dependent on the travel speed of the laser beam. For the alloy and process parameters in the simulations, no significant macrosegregation was observed. The temperature-dependent properties and thermodynamic variables involved in solidification modeling were calculated using Thermo-Calc software. The results of this work contribute to the current understanding of transport phenomena in the molten pool of laser deposition processes.

Jan 1, 2008

By Bemd. E. Langner

At Norddeutsche AfFmerie the CollaMat is an important instrument for controlling the activity of glue in copper electrolyte. Thanks to on-line measuring of the glue activity appropriate action can to taken in the event of sudden changes, such as an intemption in the glue supply, as well as long-term trends, such as continuously decreasing glue activity over days or weeks. Laboratory tests on the dependence of glue degradation on temperature have shown that relatively small increases in temperature of only 3OC cause the half change value of the glue degradation to reduce by 25 %. It is a similar picture with the sulphuric acid concentration in electrolyte. An increase in the acid concentration from 160 g/l to 200 g/l can - depending on the temperature - likewise result in a decrease in the half change value of up to 25 %.

Jan 1, 1995

By Leonid N. Shekhter, Corby G. Anderson, Esra Cankaya-Yalcin, Daniel G. Gribbin, Joseph D. Lessard, Larry F. McHugh

"A new process for smelting copper, Looping Sulfide Oxidation™ (LSO™) significantly and positively alters the smelting energy balance. This process uses copper oxide in conjunction with air for the desulfurization of copper and chalcopyrite concentrates. Copper oxide is regenerated in a flash type furnace and then ""looped"" back for the oxidation of the copper concentrate. Heat and material balances show that the Looping Sulfide Oxidation™ process requires significantly lower net energy than conventional technology. This process produces anode copper and higher S02 content off-gases for efficient formation of sulfuric acid. Additionally, the process yields slags with lower copper solubility as compared to the conventional technology.IntroductionBased on the positive results from LSO™ investigations [1], further lab investigations into co=on sulfides and metal oxides were performed. It was discovered that chalcopyrite (CuFeS2) is oxidized with copper (II) oxide. In this reaction over 98.5% of sulfur was removed as S02, while a significantly improved energy balance was observed. This paper intends to analyze both the conventional flash smelting process and the newly developed Looping Sulfide Oxidation™ process, comparing heat and material balance results. LSO™ yields improvements to the energy footprint for copper, opening the door to new copper processing opportunities."

Jan 1, 2013

By A. J. Rigby

Refractory linings in converters or anode furnaces used to over-oxidize the blister copper will suffer rapid deterioration, due to prolonged contact with copper oxide-rich slag. Nitrogen stirring with COP KIN porous plugs and use of SEMTECH OPC in converters and anode refining vessels can considerably reduce both refractory wear and processing times. In addition, careful control of the vessel atmosphere and the use of real-time optical process control minimize both slag volume and contact time with the vessel refractory.

Jan 1, 2005

By Batric Pesic

Solvent extraction of nickel and cobalt from the real leach solutions was studied by using a novel extraction system. The extraction system was a mixture of 2,6-bis-[5-n-nonylpyrazol-3¬y]] pyridine (BNPP) and dinonylnaphthalene sulfonic acid (DNSSA). The BNPP represents a novel molecule, which was designed and synthesized in our laboratory. Real solutions for the study were prepared by leaching of two different cobalt-nickel bearing concentrates, cobaltite [CoAsS] concentrate from Blackbird Mine, Idaho, and siegenite [(Ni,Co)3S4] concentrate from Missouri Lead-Belt. The major strength of the system was the selectivity of extraction toward nickel and cobalt from iron containing solutions. Other metals such as Mn, Mg, Ca, Al and As were not extracted. Due to the irreversibility of copper extraction, its removal from solution was required prior to the extraction of nickel and cobalt. Zinc was not as strongly extracted (i.e. its stripping was readily achieved) as was copper . Flowsheets for the recovery of nickel and cobalt were also developed.

Jan 1, 1997

By J. Brent Hiskey, Rebecca Grace Copp

The solvent extraction of yttrium and neodymium from copper pregnant leach solutions (PLS) using Primene JM-T, a primary aliphatic amine, has been studied. Effect of contact time, pH, sulfate concentration, and extractant concentration were investigated using synthetic and actual PLS systems. Standard experimental conditions were 5 minute contact time, pH ~2.5, and 10 % v/v Primene JM-T concentration. Distribution isotherms were constructed for the pure systems and for actual copper leach solutions. Synthetic solutions contained 100 ppm Y and ~75 ppm Nd. Samples of PLS contained 2 - 10 ppm Nd and 14 - 30 ppm Y. Results showed that complete extraction of both yttrium and neodymium occurred within five minutes and at pH values greater than 1. It was also found that sulfate concentration does not inhibit extraction at any concentration. Additionally, the distribution isotherms created show that extraction for these metals can operationally take place in one stage.

Jan 1, 2016

Today’s world relies upon advanced green technologies that are made of critical elements with unique properties. Examples include rare earth elements (REEs) that are critical in the manufacturing of wind turbines and electric/hybrid vehicle batteries, key components of a greener future that face supply uncertainty and near zero recycling. To tackle their supply challenges, activities have begun for urban mining from waste electrical and electronic equipment (WEEE) that contain considerable amount of REEs, but their current level of recycling is less than 1%. Current recycling practices use either pyrometallurgy, which is energy intensive, or hydrometallurgy that utilizes large volumes of acids and solvents and generates large volumes of hazardous waste. In this study, we developed a novel and sustainable process to recycle REEs from WEEE, NiMH batteries in particular. The developed process relies on supercritical fluid extraction (SCFE) utilizing CO2 as the solvent, which is abundant, safe, cost effective, and inert. The effect of seven operating parameters, namely temperature, pressure, residence time, sample to chelating agent ratio, agitation rate, complex formulation, and methanol addition on REE extraction efficiency was investigated, and optimum operating conditions were determined. This work is the first to utilize a very efficient and safe process that runs at low temperature to extract metals from postconsumer products with minimum hazardous waste generation, while offering about 90% leaching efficiency for REEs. We expect our process to find widespread applicability in urban mining of REEs using green chemistry.

By Margarete Kalin

Mine abandonment is associated with the securing of access to underground workings, shafts, raises and adits. Waste rock piles and tailings are generally contoured and revegetated. When the waste materials contain pyritic material seepages can often emerge long after the physical reclamation work has been carried out. Their extent and origin has to be delineated to facilitate remedial measures. The depth to which the seepages extended can be determined with an electromagnetic (EM) survey. This paper reports on the experience gained using a winter and a summer EM survey correlated with measurements of specific conductivity at the sediment water interface. Lake sediments and ponds which represent a homogenous background material are good media, where specific conductivity and electromagnetic conductivity can be correlated. The origin of the seepage within the recontoured mine site requires detailed site knowledge, as many anomalies in heterogenous materials such as represented by a mine site are evident.

Jan 1, 1994

By Y. Wang, L. Liu, G. Xu, Y. Lv J. Sheng H. Zhang

In order to increase the service life of large scale coke dry quenching furnaces, the damage mechanism of lining was investigated, and the structure and properties of lining refractories used in cooling section were researched. The results showed that the abrasive wear volume of lining bricks at one fourth height section under skew tunnel was smaller than other sections. The wear loss of mullite brick and dense clay brick used in the lining of cooling section were respectively 8.02 cm3 and 11.65 cm3 in fifteen minutes. The mullite brick was laid with clay brick alternatively. By the different wear rate, the surface of lining was rough and uneven in the later service life, and short brick was easily dropped from lining. During the service, the basis wore off more easily than the aggregate. It is necessary to improve the wear resistance property, which will increase the service life of cooling section’s lining for coke dry quenching furnaces.

Jan 1, 2016

By J. L. Watson

The composite nature of titanomagnetites found on the west coast of the north island of New Zealand is an important parameter in the beneficiation of the black beach sands for export to Japan. To investigate this composite nature, borehole and plant samples from the Waipipi Ironsands Ltd property were subjected to a series of separations in heated Clerici solutions at densities varying from 3.2 to 4.6 g/cc. The resulting density fractons were analyzed magnetically and a set of distribution curves for composite grains proposed. In addition the experi¬mental data was plotted to produce titanomagnetite sand 'washability curves" which illustrate the possible problem areas in beneficiation that may arise due to composite titanomagnetite grains. From this data a set of guidelines are suggested for interpreting the curves in terms of ease of gravity concentration. The composite nature or liberation of titanomagnetite grains is shown to favor high and low grade composites with few intermediate compositions being isolated. The relationships between grain size, borehole depth and liberation are examined and related to beneficiation procedures for the black sand deposit.

Jan 1, 1982

By Qian Xu, Xionggang Lu, Xingli Zou, Zhongfu Zhou, Shuhua Geng, Hongwei Cheng

Herein we report an electrochemical route from oxides (SiO2, TiO2)/sulfide (MoS2)/carbon mixture precursors to Mo-Si-Ti-C composites in molten salt. The electrochemical process was carried out in molten CaCl2 at 800 °C with a potential of 3.1 V, and a graphite-based anode was used in the electroreduction process. The reaction mechanism and the influences of the stoichiometry of the initial mixture precursor on the morphology and phase composition of the final products were investigated. It has been found that Mo5Si3/MoSi2/Mo3Si/Mo, Mo5Si3/MoSi2/Mo2C/SiC, and Mo5Si3/Mo2C/Ti3SiC2/TiC/Mo composites can be electrosynthesized directly from their oxides/sulfide/carbon mixture. The preliminary experimental results suggest that the electroreduction process can be used for the controllable electrolytic production of alloys/carbide-containing composites from oxides/sulfides/carbon precursors.

Jan 1, 2016

By Mark Samonds

"Manufacturing processes which involve liquid to solid and solid state transformations in metals encompass a wide variety of physical phenomena. The past twenty years have seen a steady evolution in the complexity and scope of numerical models of these processes, beginning with thermal analyses without phase change. Recently, a few software packages have become available which have true multi-physics capabilities. This permits the treatment of thermal, fluids, stress, electromagnetic, chemical reaction and microstructure development aspects altogether in a fully coupled simulation. This paper will consider various aspects of these types of models.Coupled thermal and fluid flow analyses of continuous castings have been around for fifteen years. Coupled thermal and free surface fluid flow simulations of shape castings have been available for ten years, including view factor radiation models for investment castings. Only recently, however, have fully coupled thermal, fluid, and stress analyses become practical. This implies the reverse coupling of the mechanical deformations to the solution of the energy and momentum equations through modification to the interface heat transfer coefficients and the fluid domain geometry. This has been implemented with a combined eulerian-lagrangian finite element method. Appropriate mechanical constitutive models will also be discussed.Many types of defects need to be predicted in casting processes. Those related to stress include hot tearing, hot cracking, part distortion, and thermal fatigue in dies. Macroporosity, microporosity, and microsegregation are determined by the solidification behavior and microstructure development in a casting. In particular, microporosity is influenced by dissolved gases, the morphology of the mushy zone, the liquid to solid density change, and the local pressure conditions. Macrosegregation is caused by the partitioning of solutes during. solidification and subsequent thermo-solutal convection. An additional transport equation is required for each solute that is being tracked. Computational thermodynamics is being incorporated into these types of analyses to determine transformation temperatures, partition coefficients, densities, and enthalpies. In combination, the microstructure and microporosity models can frequently predict a variety of mechanical models, such as yield strength, tensile strength, and elongation."

Jan 1, 2001

By Zhiqian Zhang, Chao Wu, Chao Li, Hongxu Li, Yu Chen, Xiangxin Hao

"In this paper, the life cycle assessment models for automobile lightweight materials including high-strength steel, aluminum alloy and magnesium alloy are developed by Gabi software. The evaluation models and evaluation indicators such as acidification effects, rich eutrophication effect, ozone layer depletion effects, global warming, resource consumption and formation of ozone potential were taken into account. It is shown that the effects of acidification and ozone formation are mainly derived from the run phase of high-strength steel and they have strong environmental impact load. While considering the entire life cycle with materials production phase and resource consumption, the aluminum and magnesium alloy appe art o have large r environmental load than high-strength steel. Base d on the evaluation, some optimization tips are proposed.IntroductionAs the increasing of car ownership, automobile has its two sides. One which is the convenient, efficient and fast traffic vehicle; the other is aggravating energy consumption, emissions and environmental pollution. The car industry faces heavy pressure with energy saving, safety and environmental protection. Nowadays, the main study ways for automotive energy-saving and environmental protection are power system improvement, alternative energy sources and technologies. For limitation of technique, development cycle and market share, the development of car is little progress at this stage and the application has been restricted. And another important way is the lightweight of vehicle. Usually there are three ways to get the lightweight automobile body structure, automobile body structure optimized design, using advanced body manufacturing technology, development and application of lightweight high strength body material.The life cycle assessment (LCA)[1lis commonly used to evaluate environmental factors and potential environmental impacts of products and services. As an environmental management tool of product-oriented, it becomes increasingly popular in industry. In this study, the concept of LCA and GaBi software was used to develop models for the three automotive lightweight materials, evaluate the environmental impact and make horizontal and vertical contrast by choosing variety of evaluation systems and indexes."

Jan 1, 2013

By Gabriel Plascencia

Copper was oxidized in the temperature range from 300 to 1000 °C under different pressures of oxygen, In the range from 300 to 500 °C, copper oxidizes following the logarithmic rate law; while in the range from 600 to 1000°C oxidation follows the parabolic rate law. Transition from logarithmic to parabolic growth occurs at about 525°C. X-ray diffraction was performed on oxide scales to account for the CuO/Cu2O ratio at different temperatures. Activation energies found in this work are in good agreement with reported values.

Jan 1, 2003