By N. H. Emmons

(Canal Zone Meeting, November, 1910.) AN interesting development of copper blast-furnace construction has been brought about in adapting the blast-furnace to be a "burner" for sulphuric acid making. When the Tennessee Copper Co. first decided to construct an acid-plant, the standard type of brick-top furnace, supported by structural steel, was the only one in use at this plant. All the tests for temperature and strength of gas had been made on these furnaces, and had been satisfactory. When, however, the acid-plant was put on the flue, and the flue had to have a damper put in it to force the gas into that plant, troubles began. The furnaces were fairly tight, and for a few months the work was quite satisfactory., Fig. 1 shows the old type of furnace-top used at the start. It was soon found that this top would not stand the temperatures, particularly when dampered back, as was necessary to force the gas into the Glover towers. The structural steel, of which the furnace skeleton was constructed, warped and twisted so badly that it was not safe to use the furnaces. This effect is shown by Fig. 2, which is a photograph of old No. 4 furnace, after the brick-work had been removed. It became apparent that a new type of top was necessary and the engineering force was started oil the design of a new furnace-top, with the result that a low top, with brick-lined flues at each end below the feed-floor, leading to the main concrete dust-chamber, was constructed. This furnace, No. 7, is shown in Fig. 3. The charging-doors are made of cast-iron sections, three sections to a door, and three doors to a side. A door to the furnace was made of cast copper, but the heat was so great that the copper bent readily, due to the jarring of its * General Manager, Tennessee Copper Co.

Feb 1, 1911

By ROY BERENTZ

MANUFACTURE is the transformation of material by the application of energy and power. The energy of a man exerted throughout a day is equivalent to about one horsepower-hour of mechanical work an amount which can be purchased for less than 2c. It is evident that manual labor is uneconomical if mechanical energy can be applied effectively, or without disproportionate expense. Since manual energy is relatively so costly, economy demands that mechanical power be employed so as to reduce the human effort connected with mining operations to a minimum. Power, like other commodities, is most efficiently produced in large quantities. Mechanical transmission, once prevailing, is being rapidly superseded by electric drive. There are many reasons for this change; such as increased production, ease and accuracy of control, convenient application, ease of moving, etc.

Jan 1, 1930

By C. E. Birchenall, J. R. Stubbles

ThE equilibrium between lead, lead sulfide (PbS), and atmospheres of H2 and H2S has been determined previously by Jellinek and Deubel,' and SudO.' Blbem and Kroger3,4 used Jellinek's data to calculate the sulfur dissociation pressures of PbS crystals (of

Jan 1, 1960

By J. R. Thoenek S. L. Windes

The amplitudes and frequencies of vibratiolls of a four-story stucco building were measured by specially developed electrocapacitive seismometers. Records were made on three floor levels with as many as 10 seismometers recording simultancously. Sources of vibration were: (1) an electric motor with unbalanced pulley, maximum speed 1800 r.p.m., maximum centrifugal force 90 lb., (2) truck traffic (both solid and pneumatic tires) moving over inequalities in the street in front of the house, (3) falling weights dropped on the street pavement from different heights, (4) miscellaneous sources, including a man jumping on the floor of the house and slamming doors. Tests were made to determine the natural frequencies of floor and wall panels by varying the speed of the unbalanced motor and by exciting the panels with a single impulse. The vibrations recorded were compared to records of vibrations from quarry blasts and it was observed that the vibrations from truck traffic were comparable to those recorded from quarry blasts and in no instance was there any damage to the building. As the tests were all of a negative character as far as damage was concerned, no index of destruction is formulated. Instead, the records are presented simply as vibration measurements obtained in an ordinary house under typical conditions.

Jan 1, 1940

By J. R. Thoenek S. L. Windes

The amplitudes and frequencies of vibratiolls of a four-story stucco building were measured by specially developed electrocapacitive seismometers. Records were made on three floor levels with as many as 10 seismometers recording simultancously. Sources of vibration were: (1) an electric motor with unbalanced pulley, maximum speed 1800 r.p.m., maximum centrifugal force 90 lb., (2) truck traffic (both solid and pneumatic tires) moving over inequalities in the street in front of the house, (3) falling weights dropped on the street pavement from different heights, (4) miscellaneous sources, including a man jumping on the floor of the house and slamming doors. Tests were made to determine the natural frequencies of floor and wall panels by varying the speed of the unbalanced motor and by exciting the panels with a single impulse. The vibrations recorded were compared to records of vibrations from quarry blasts and it was observed that the vibrations from truck traffic were comparable to those recorded from quarry blasts and in no instance was there any damage to the building. As the tests were all of a negative character as far as damage was concerned, no index of destruction is formulated. Instead, the records are presented simply as vibration measurements obtained in an ordinary house under typical conditions.

Jan 1, 1940

By E. I. Larsen, E. F. Swazy, F. R. Hensel

High strength, high-conductivity copper-base alloys have found considerable use in the resistance welding and electrical industry in the form of castings, forgings, or wrought products. There are a number of parts utilized by these industries which would lend themselves to manufacture by powder metallurgical methods provided the required physical and electrical properties are obtainable with such methods. The present paper describes the results of a study of certain copper-base powder metallurgical products susceptible to precipitation hardening. Copper Powders The general types of commercially available copper powders are flake, spherical and electrolytic. Micrographs of these three types are shown in Figs. I, 2 and 3. The difference in particle shape is pronounced and obvious. The type of powder used is determined, or at least indicated, by the final properties desired in the finished article. The type of powder employed during the present investigation was electrolytic powder shown in Fig. 3, and was chosen because of its particular adaptability to the work described in this Paper. The screen and chemical analyses of this powder are shown in Table I. In the preparation of compacts of high electrical conductivity, the purity of the copper powder is of importance in addition to other factors, such as density and the state of internal stresses. These variables were studied briefly by pressing a number of compacts to various pressed densities, sintering them for one hour in hydrogen at 975OC and repressing. The size of the finished compacts was 1/4, by % by 8 in. The time interval from the application to the termination of pressure was approximately 20 sec. Some of the compacts were annealed before testing. The results are listed in Figs. 4 to 8, inclusive. In Fig. 4 the curves of pressed density vs. compacting pressure, and sintered density versus compacting pressure show the typical direct relationship of pressure and density. Compacting pressures exceeding about 30 tons per sq. in. result fiequently in expansion during sintering for the type of powder used. Fig. 5 indicates that variations in the initial pressed density within the range of about 5 to 6 grams per c, c., affect only slightly the pressure required to obtain a

Jan 1, 1946

By E. I. Larsen, E. F. Swazy, F. R. Hensel

High strength, high-conductivity copper-base alloys have found considerable use in the resistance welding and electrical industry in the form of castings, forgings, or wrought products. There are a number of parts utilized by these industries which would lend themselves to manufacture by powder metallurgical methods provided the required physical and electrical properties are obtainable with such methods. The present paper describes the results of a study of certain copper-base powder metallurgical products susceptible to precipitation hardening. Copper Powders The general types of commercially available copper powders are flake, spherical and electrolytic. Micrographs of these three types are shown in Figs. I, 2 and 3. The difference in particle shape is pronounced and obvious. The type of powder used is determined, or at least indicated, by the final properties desired in the finished article. The type of powder employed during the present investigation was electrolytic powder shown in Fig. 3, and was chosen because of its particular adaptability to the work described in this Paper. The screen and chemical analyses of this powder are shown in Table I. In the preparation of compacts of high electrical conductivity, the purity of the copper powder is of importance in addition to other factors, such as density and the state of internal stresses. These variables were studied briefly by pressing a number of compacts to various pressed densities, sintering them for one hour in hydrogen at 975OC and repressing. The size of the finished compacts was 1/4, by % by 8 in. The time interval from the application to the termination of pressure was approximately 20 sec. Some of the compacts were annealed before testing. The results are listed in Figs. 4 to 8, inclusive. In Fig. 4 the curves of pressed density vs. compacting pressure, and sintered density versus compacting pressure show the typical direct relationship of pressure and density. Compacting pressures exceeding about 30 tons per sq. in. result fiequently in expansion during sintering for the type of powder used. Fig. 5 indicates that variations in the initial pressed density within the range of about 5 to 6 grams per c, c., affect only slightly the pressure required to obtain a

Jan 1, 1946

By Byron W. Cheever

In the Journal of the Iron and Steel Institute for 1881 (vol. ii., page 379), will be found an article upon this subject. The analyses there reported mere of samples taken from an ingot made especially rich in impurities and then cast in a sand-mould in order to give the elements a better chance to redistribute themselves, on account of the steel solidifying more slowly than when cast in an iron mould. Wishing to ascertain how much, if any, segregation takes place when the steel is cast in the ordinary way, I placed the subject in the hands of Mr. W. J. Olcott, a graduate of the Michigan University, who has carefully collected and analyzed samples taken from different parts of ingots and billets. In this undertaking he found himself somewhat embarrassed on account of being distant from steel-works, and therefore unable to supervise the selection of samples. He found, however, a competent and willing aid in the person of E. F. Wood, M.E., chemist of the Pittsburgh Bessemer Steel Company, Limited, who has spared no pains in collecting the desired samples and furnishing drawings and descriptions of the ingots from which the samples were taken. The following are the results obtained: Ingot No. 1. This ingot was about 5 feet long and 13 X 131/4 inches at the point of fracture, which was 2 feet from the bottom. The samples

Jan 1, 1885

By K. R. Janowski, H. Conrad

As part of a program to establish the effect of crystal imperfections on laser output, a detailed study was made of the dislocation structure of ruby crystals obtained from varioius sources. Using KHSO4 as an etchant, a detailed mapping of the dislocation structure on the (0001) and the (1150) planes was carried out. A less extensive study was made of the rhombohedral planes. The average dislocation density on the basal plane was 1.5 to 3 x 106 cm&apos;2 and on the (1120) planes -5 x 10&apos; cm-2. Howe7!er, considerable variation existed between areas on a given plane. The subboundaries in the basal plane tended to lie along [1100] type directions while those on the (1120) plane tended to lie: a) parallel to the basal plane, b) along truces of the (1101) plane, and c) along normals to the traces of the (0001) planes. The orientations suggest that mang of the dislocations lie on the (0001), (1701), and (1150) planes A Laue back-rellection nnalysis Of c-axis wander in one crystal revealed a gradual increase in misorientation from me end of the crystal to the other, with a maximum variation of 1°35&apos;. Slight etching of a mechanically polished crystal revealed mumerous polishing scratches, suggesting the existence of a plastic flow layer. It is recognized that chromium concentration, lineage, and other crystalline imperfections play a role in the efficiency of ruby lasers.&apos; Consequently, it is desirable to establish in detail the imperfection structure of ruby crystals to be used as lasers. Some exploratory work along this line had already been done by Barnes&apos; and Dils and Martin.&apos;" How- referred to as the morphological system, as described by Kronberg.4 The Miller indices given in the present paper will be based on this morphological system. In this system, the three common growth planes are the (0001), the {1120}, and the {1101}.5 Since these planes are of high stability, it is expected that they are most suitable for study by the etch-pit technique. In the present investigation, a detailed mapping of the dislocation structure was carried out for the (0001) and the (1130) planes. A less extensive study was made of the etch-pit structure on rhombohedra1 planes. An analysis of dislocations in sapphire (the ruby host) was first made by kronberg,4 who postulated that slip on the (0001) plane occurred by motion of dislocations with Burgers vector 1/3 <1150> and that these dislocations might dissociate into quarter partials. An etch-pit technique using boiling phosphoric acid was developed by Scheuplein and Gibbs6, 7 for identifying dislocations intersecting the (0001) planes and the planes near (2021) in sapphire. Al-ford and Stephens8 were able to reveal dislocations on the (0001) and {1120} planes in sapphire and ruby by etching in fused potassium bisulfate (KHS04) at 675°C. The termini of basal dislocations [(000l), <1120>] were revealed by Palmour and Kriegel9 on {1120} and {1010} by thermally etching sapphire. Bond and Harvey10 were able to decorate dislocations in sapphire by adding 1 pet by weight of ZrO2 to the Al2O3 powder used in the growth of the crystals by the Verneuil technique and then heating the grown crystals for 4 hr at 1500°C. They found, using optical transmission microscopy, that many dislocations had straight segments which were parallel to one of the six [1120] directions in the basal plane. Single dislocation lines curved smoothly from one alignment to the other, turning through angles of 60 to 120 deg. Also observed were isolated hexagonal loops, approximately 10 µ in diameter, the sides of which lay along the same directions as did the longer dislocations. MATERIAL AND ETCHING PROCEDURE The ruby specimens used in this study (all containing approximately 0.04 pet Cr) had been obtained from four different sources: Linde Co., Meller Co., Valpey Crystal Corp., and those grown at Aerospace Corp.* For the initial phase of this study, several specimens were cut from the slab shown schematically in Fig. 1 which had previously been cut from a disk boule obtained from the Linde

Jan 1, 1964

By R. A. Oriani

The partial molal volume of hydrogen is one of the parameters that describe the elastic interaction between the solute and the stress fields about inclusions, dislocations, and cracks. As such the partial molal volume is probably of importance in the elucidation of phenomena such as hydrogen embrittlement and hydrogen yield point. A knowledge of this quantity would also be helpful in thinking about the state of dissolved hydrogen in iron. However, because of the very low lattice solubility of hydrogen in iron the usual ways of determining the lattice expansion are not practicable. It is therefore of interest to apply the thermodynamics of stressed bodies to two sets of measurements of the effect of elastic stress upon the permeability of hydrogen in order to deduce a value of the partial molal volume, VH, of hydrogen dissolved in a iron. Beck ..&apos; and previously de Kazinczy, observed that a uniaxial tensile stress increases the permeability of hydrogen in iron and in various steels. Beck et 01. employed Armco iron and A.I.S.I. 4340 steel, whereas de Kazinczy used a steel the composition of which was 0.13 C, 0.23 Si, 0.46 Mn, 0.006 P, and 0.038 S. Upon releasing the stress the permeability increment disappeared if the stress was below the elastic limit. Both investigators employed cathodic charging to introduce the hydrogen. de Kazinczy measured the permeation through a thin-walled tube by collecting the gas, whereas Beck et al. measured the permeation through sheets of various thicknesses by a very sensitive electrochemical technique. Both investigators measured the steady-state permeation at constant rate of hydrogen ion discharge, and Beck measured in addition the hydrogen diffusivity by a time-lag technique which is independent of the boundary conditions. Beck et al. and de Kazinczy found a linear relationship between log (J,/Jo) and the stress, where Ju/Jo is the ratio of the flux of hydrogen when the metal is under uniaxial tensile stress, a, to the flux under zero stress, for the same temperature and charging current. Beck et al. found in addition that the diffusivity of hydrogen is not changed by stress. Both investigators concluded that the observed change in permeability is due to an increase in hydrogen concentration, and furthermore that the increase in concentration is due directly to the thermodynamic effect of stress upon concentration. Accepting this assessment of the situation for reasons given below, one may use the equation3j4 in order to evaluate I/H, the partial molal volume of hydrogen. This equation is valid for the domain of a/E «¦ 1 (where E is the Young&apos;s modulus) and under the assumption that hydrogen expands the lattice isotrop-ically. From the data of Beck el al, one calculates V7H - 2.0 cu cm per g-atom, and from those of de Kazinczy one obtains 1.8 cu cm per g-atom. That the increase of concentration with stress is indeed of thermodynamic origin is attested to by the facts that the experimental results conform to the thermodynamic relation, Eq. [I], and that the results are the same whether a pure iron1 or each of two different steels172 is used. Neither of these facts wou1.d necessarily be expected if the effect of stress were, rather, to increase the ratio kn/k, of the kinetic factors of the following competing reactions: H(ads) — H (dissolved) Such a change of kinetics at the surface could be an alternative explanation of the effect of stress on the permeability. Although this writer does not deem this explanation to be the correct one for the reasons given above, it must be admitted that unambiguous proof that the phenomenon has a thermodynamic origin does not yet exist. Two kinds of experiments may be suggested. One is to plate a variety of metals on the input surface of the steel and repeat the stress experiment at a variety of hydrogen charging currents. The other is to employ somewhat thicker specimens in order to be able to apply uniaxial compressive stress. Eq. [I] shows that ln(c,/c,) depends on the sign of the stress, but it is difficult to see a physical basis for which k2/kl would depend on the sign of a. The present value of V^ in a iron agrees with phragmen&apos;s5 estimate, which he based on comparisons with the lattice expansion by hydrogen of titanium, zir-

Jan 1, 1967

By NORMAN D. FitzGkrald

IN 1942 the outstanding characteristic of the petroleum industry was the multiplicity of war-induced distortions in virtually every segment of the business. So devastating was the success of the Nazi submarine campaign along the shores of the western Atlantic and on transoceanic routes that within six months after our entry into the war petroleum rationing was necessary in the East Coast area. The conquest of the Netherlands Indies by the Japanese three months after the opening of the war in the Pacific cut off our normal sources of rubber, and in our first year of war nationwide rationing of gasoline had to be invoked to conserve rubber-borne transportation facilities. Meanwhile the oil industry faced the imperative necessity for rapid expansion in the output of aviation gasoline and later accepted the vast responsibility for developing a new industry. synthetic rubber manufacture. Probably no other essentially peacetime industry has been forced to make so many complicated adjustments, yet its response to its wartime obligations has been nothing short of dramatic.

Jan 1, 1943

(Members, are urged -to send in for this column any notes of interest concerning themselves or their fellow-members,). Members and guests R: ho called at Institute headquarters during the period Dec: 10, 1916 to Jan. 10, 1917: F. L. Antisell, Perth Amboy, N. J. William Kelly, Vulcan, Mich. F. J Brulé, Toronto, Ont., Canada. W. H. Lanagan, San Francisco, Cal. Zar T. Crittenden, The. Pas, Mau, Canada. S. Lefevre, Forest Glen, N Y Thomas F. Donnelly, Tucson, Ariz. &apos; D. A. Lyle, St..David&apos;s, Pa. - John Davenport, Brighton, 14 lass. -Domingo Nugués, Buenos Aires, Argon-. E. E. Ellis, Birmingham, Ala. tine. N. H. Emmons, 3d, Copperhill, Tenn. - H. L. Scaife, Clinton, S. C. W.. E. Erdofy, New York, N. Y. Mortimer A. Sears, Washington, D. C. C. L. French, New York, N. Y. E. Spurny, New York, N. Y.&apos; , M. H. Gannon, Butte,. Mont. R. K. Stockwell, Santiago, Chile. R. E. Hoffman, Hannibal, Mo. Benjamin F. Tibby, Salt Lake City, Utah. C. Vey Holman, Rockland, Me. Arthur P. Watt, St. Francois, Mo. Arthur P. Allen has left the employ of the Calumet &- Hecla Mine and is now with the Highland Min. Co., Ashcroft, B. C., Canada. H: C. Bellinger has been appointed. general manager of the Chuqui- - c mata mine-of the Chile Exploration Co. -

Jan 2, 1917

By LEONARD S. AUSTIN

THE works of The Boleo Mining Co. are situated at Santa Rosalia, Lower California, on the opposite side of the Gulf of California from Guaymas, the, nearest railroad town. The copper deposits were discovered in 1868, and the name Boleo arose from the fact that the ore particles were agglomerated as little balls of carbonate or oxychlorides of copper. When worked on. a small scale, only ore carrying 20 to 25 per cent copper was mined; this was shipped to Europe for reduction In 1884 The Boleo Mining Co. was organized and,-the mine put in condition. Even then, due to the low price of copper, only the richer ore continued to be shipped. To operate the mine successfully the company made radical changes in the methods of development and spent money freely for construction of adequate plants for the treatment of low-grade ore. Finally, the owners of the various adjacent mining claims combined their interests and formed a joint enterprise attractive to French capital.

Jan 1, 1929

By G. L. Kehl, Emilo Jaraiz F., J. S. Brett

The transformation of eutectoid beryllium bronze has been quantitatively investigated at 550° and 592°C, the temperature region where the products of p decomposition are a fine lamellar eutectoid and a coarse lamellar aggregate which replaces the fine eutectoid with prolonged annealing. Metallographic evidence indicates that the coarse lamellar aggregate forms preferentially in the most densely lamellated regions of the fine eutectoid and favors the hypothesis that the development of the coarse lamellar aggregate in the fine eutectoid is due to the occurence of a cellular segregation reaction. WHEN eutectoid beryllium bronze (Cu-94 pct, Be-6 pct) is isothermally transformed at high temperatures in the and y region after quenching from the fl field, the principal initial decomposition process is G one of growth of approximately spherical nodules composed of a number of lamellar colonies of the a and y phases. After the initial reaction has proceeded substantially or completely, depending on the transformation temperature, a second reaction occurs wherein the fine lamellar eutectoid is replaced by a coarser lamellar aggregate composed of the same oand yphases.&apos; This reaction is not simply a spheroidization of the initial fine eutectoid but the nucleation and growth of a coarser, structurally different, and more stable distribution of the @and yphases. Fig. 1 illustrates the replacement of the initial fine lamellar structure by a coarse lamellar aggregate. The a phase is the dark mottled constituent; the light constituent the y phase. The phase diagram for the copper-rich end of the Cu-Be system2 is shown in Fig. 2. The a phase has the face-centered cubic structure characteristic of copper-rich solid solutions. The B phase is a disordered body-centered cubic structure, while the y phase is body-centered cubic, ordered (CsC1, B2 type). A. viswanathanS investigating Debye patterns of Cu-6 pct Be discovered that a transitory phase appeared on very rapid quenching from the /3 region which was absent when the quenching velocity was moderate. The phase could be assigned a body-centtred cubic structure with a lattice parameter of 2.876. Tempering at 100°C for 2 hr after quenching resulted in complete disappearance of the phase. The work of Fillnow and Mack&apos; is the only previously published study of the isothermal transformation of eutectoid beryllium bronze. Their study elucidated the nature of decomposition at various subcritical temperatures in an exploratory fashion. The purpose of the research reported in this paper was principally to obtain quantitative information on the isothermal decomposition of the fl phase and to clarify the relationships existing between the fine lamellar eutectoid and the coarse lamellar aggregate. EXPERIMENTAL PROCEDURE The material used in this investigation was an almost eutectoid Cu-Be alloy bar furnished by D.J. Mack. The alloy had been melted under a protective carbon cover and centrigugally cast into a graphite mold preheated to 490 "C. Segregation was minimized by violent agitation during melting and pouring. The analysis of the casting was 93.85 pct Cu, 5.60 pet Be with traces of Si, Mg, Mn, Co, and Al. To determine the minimum soaking time necessary to insure specimen homogeneity, a number of specimens were held in the P region at 788OC for times fron 1 min to 12 hr and isothermally transformed at 550°C. Specimens betatized less than 12 min exhibited partial transformation at times shorter

Jan 1, 1961

By G. W. Tower

THE YEAR 1931 was for most American copper producers one of restricted output but extremely low production cost.. When compared with 1929, the marked reductions in costs achieved in 1931, operating at rates in many instances a third to a half of capacity, can only be regarded as remarkable. In fact, the recent shut-down of several large operations suggests the probability that 1931 costs represent a bare minimum for many properties. Before discussing the 1931 results a few remarks on cost data are appropriate. The type of cost tabulation here presented was first published in 1929, (A. B. Parsons. E. & M. I. June 8, 1929), and has appeared each, succeeding year following in general the calculation method and company set-up of the original article. (. G. W. Tower, E. & III. L, July 8. 1930; S. D. Strauss, E. & M. J.; July 27, 1931). As far as possible the leading American copper companies are included. In considering these cost tabulations it must be borne in mind that the information from which they have been prepared is entirely contained in the annual report of each company; and that a multiplicity of interests and a condensed income statement for some of the larger companies, such as Cerro de Pasco and Kennecott, make the cost figure an arbitrary one depending upon sundry metal credits, metal products, miscellaneous income, etc. For Granby, Howe Sound. Magma, and Noranda, sundry metal credits are important. Furthermore Andes, Chile and Greene Cananea give costs only against copper sold. Although the individual costs here figured are by no means absolute they are computed by the same method each year and offer a basis of annual comparison; and with attention to footnotes the premises on which the costs are based may be easily followed.

Jan 1, 1932

By J. O. Betterton, D. S. Easton

A detailed investigation was made of the phase diagram of silver-zirconium, particularly in the region 0 to 36 at. pct Ag. The system was found to be characterized by two intermediate phases Zr2Ag and ZrAg and a eutectoid reaction in which the -zirconium solid solution decomposes into a-zirconium and Zr2Ag. It was found that impurities in the range 0.05 pct from the iodide-type zirconium were sufficient to introduce deviations from binary behavior, and that with partial removal of these impurities an increase in the a-phase solid solubility limit from 0.1 to 1.1 at. pct Ag was observed. The phase diagram of the silver-zirconium system is of interest as an example of alloying a transition metal from the left side of the Periodic Table with a Group IB element. Silver would normally act as a univalent metal, its filled 4d-shell remaining undisturbed during the alloying. However, there is a possibility that some of the 4d electrons might transfer to the zirconium. An insight into such a question can occasionally be obtained by comparison of phase diagrams. The silver-zirconium system forms part of a more complete review of various solutes in zirconium in which these valency effects were studied.&apos; Earlier work on the silver-zirconium system was done by Raub and Enge1,2 who investigated the silver-rich alloys. After the start of the present experhents, work on this system was reported by Kemper3 and by Karlsson4 which for the most part agrees with the phase diagram presented here. EXPERIMENTAL PROCEDURE The alloys were prepared by arc casting on a water-cooled, copper hearth with a tungsten electrode and in a pure argon atmosphere. Uniform solute composition was attained by multiple melting on alternate sides of the same ingot. Progressive improvements in the vacuum conditions inside the apparatus during the course of the experiments reduced the Vickers hardness increase of the pure zirconium control ingot from 10 to 20 points, observed initially, to negligible amounts at the end of the experiments. Such hardness changes in zirconium are a well known indication of purity. For example, -01 wt pct additions of oxygen, nitrogen, and carbon increase hardness by 6, 10, and 3 VPN respectively. &apos;9&apos; Further verification that the final casting technique did not add a significant quantity of impurities was obtained when pure zirconium was arc cast and then isothermally annealed in the vicinity of the allotropic transition. The transition was always observed to take place over the same temperature range as in the original crystal bar. The alloy ingots were annealed in sealed silica capsules for times and temperatures which varied between 1 day at 1300°C and 60 days at 700°C. The best method found to prevent the reaction of the zirconium with the silica was foil wrapping of molybdenum or tantalum. With this method, samples of pure zirconium were found to be unchanged in hardness after annealing for 3 days at 1200°C. In most of the experiments the protection of these foils was supplemented by an additional layer of zirconium foil inside the molybdenum or tantalum foil. The alloys, foil, and the capsule were outgassed at pressures in the range 10 to l0-7mm Hg in the temperature range 800" to 1100°C before each anneal in order to remove hydrogen and other impurities, and to provide a suitable container for the high purity, inert atmosphere, which is essential in the annealing of zirconium. The temperature measurements were made with Pt/Pt + 10 pct Rh thermocouples calibrated frequently during the experiments against the melting points of zinc, aluminum, silver, gold, and palladium. For the longer anneals the sum of various temperature errors was generally well within ± 2°C. For short-time anneals and during thermal analysis the overall temperature error is considered to be within ± 0.5°C. The compositions of the alloys from the quenching experiments were determined by chemical analysis at Johnson Matthey and Company, Ltd., under the direction of Mr. F. M. Lever. The actual metallo-graphic samples were individually analyzed in every case, and prior to the analyses two or more sides of each specimen were examined to insure that the specimen was not segregated. The sum of the solute and solvent analyses was in each case within the range 99.9 to 100.1 pct. In the course of the experiments, minor impurities in the range 0 to 500 ppm were found to have significant effects on the zirconium-rich portion of the phase diagram. Similar effects had been encountered previously in other zirconium phase-

Jan 1, 1959

By Ernest R. Woakes

Cana, originally called Santa Cruz de Cana, is situated in the province of Darien, in the Republic of Colombia, S. A. The river Cana is a tributary of the Tuyra, which flows into the Gulf of San Miguel, and thence into the Pacific Ocean some 80 rniles S.E. of the City of Panama. • The Espiritu Santo mine lies on the S. side of the Cana river at the foot of the Espiritu Santo range. The plateau of Cana has an elevation of 2000 feet above sea-level, and the mine is about 200 feet above the plateau. The map of the Darien accompanying this paper is the only correct one in existence. It was made by Lucien N. Bonaparte Wyse for the Panama Canal Co., and has been copied fur the present use, with permission, by Mr. L. G. Inglis. The dotted line on this map shows the route from the coast to Cana. As this mine was one of the most celebrated at the time of the Spanish occupation, it is only natural that there are a great many traditions and writings concerning its former workers and production. Dampier mentions it, though he does not seem to have been nearer to it than El Real de Santa Maria, the port on the Rio Tuyra, about 50 miles by road from Cana. Senor Vicente Restrepo&apos;s work, entitled Estudio sobre las Minas de Oro y Plata de Colombia, translated by C. TV. Fisher and published in New York in 1886, is, perhaps, the best treatise on Colombian mines. He has devoted a great deal of attention to the subject of the Espiritu Santo mine, and has had access to all that dealt with it in the archives of Bogota. It will be interesting to quote a few pasaages from the above work, which seemed like a romance to the writer of this paper some years ago, when he first came across the history. Being actually in Cana at the time, and knowing the present company had

Jan 1, 1900

By G. F. Tagg

In an earlier paper1, the author described a method of interpreting earth-resistivity curves, based on the theoretical investigation of a single horizontal underlying stratum. If the four-electrode system of Wenner is employed, the resistivity in a homogeneous soil is given by the formula where a is the electrode separation and R is the resistance of the earth between the two inner electrodes. If the earth is not perfectly homogeneous, the application of this formula gives an apparent specific resistance varying with the electrode separation. In the special case of the single horizontal underlying stratum, there is a surface layer of thickness h and resistivity p1 and a lower layer, extending to infinity, of resistivity pz. It has been shown by Lancaster-Jones2 that the apparent resistivity obtained by an application of equation 1 is related to the true resistivities, the depth h and the electrode separation a by an expression of the formhere pa is the apparent resistivity and F is a function (actually an infinite series), of the ratio h/a, and a reflection coefficient k = (p2 — p1)/(p2 + p1). For given values of h/a and k, the right-hand side of equation 2 can be calculated, and curves drawn showing the relationship between pa/p1, h/a and k. Such a set of curves for the case when p1 > p2 is given in Fig. 1. When pl is less than pz it is more convenient to use conductivity instead of resistivity. Hence, if oa = the apparent conductivity = lip, and a1 = the conductivity of the upper layer = l/pl, it follows that GeophyGical prospecting by earth-resistivity methods is frequently applied to investigation of structural problems in geology. Fig. 1 indicates a scheme of the general arrangement used in these methods of measurements. The battery (or generator) E is connected with two "current electrodes" I1 and I2. The current of intensity J, supplied by this battery, passes through the earth between these elcc- trodes. A potential difference U will be measured between two other electrodes V1 and Vz, called "potential electrodes." According to the configuration of electrodes (Fig. I), the resistivity of a homogeneous soil results from the formula

Jan 1, 1940

By G. F. Tagg

In an earlier paper1, the author described a method of interpreting earth-resistivity curves, based on the theoretical investigation of a single horizontal underlying stratum. If the four-electrode system of Wenner is employed, the resistivity in a homogeneous soil is given by the formula where a is the electrode separation and R is the resistance of the earth between the two inner electrodes. If the earth is not perfectly homogeneous, the application of this formula gives an apparent specific resistance varying with the electrode separation. In the special case of the single horizontal underlying stratum, there is a surface layer of thickness h and resistivity p1 and a lower layer, extending to infinity, of resistivity pz. It has been shown by Lancaster-Jones2 that the apparent resistivity obtained by an application of equation 1 is related to the true resistivities, the depth h and the electrode separation a by an expression of the formhere pa is the apparent resistivity and F is a function (actually an infinite series), of the ratio h/a, and a reflection coefficient k = (p2 — p1)/(p2 + p1). For given values of h/a and k, the right-hand side of equation 2 can be calculated, and curves drawn showing the relationship between pa/p1, h/a and k. Such a set of curves for the case when p1 > p2 is given in Fig. 1. When pl is less than pz it is more convenient to use conductivity instead of resistivity. Hence, if oa = the apparent conductivity = lip, and a1 = the conductivity of the upper layer = l/pl, it follows that GeophyGical prospecting by earth-resistivity methods is frequently applied to investigation of structural problems in geology. Fig. 1 indicates a scheme of the general arrangement used in these methods of measurements. The battery (or generator) E is connected with two "current electrodes" I1 and I2. The current of intensity J, supplied by this battery, passes through the earth between these elcc- trodes. A potential difference U will be measured between two other electrodes V1 and Vz, called "potential electrodes." According to the configuration of electrodes (Fig. I), the resistivity of a homogeneous soil results from the formula

Jan 1, 1940

By L. H. Reiss, J. Groult, L. Montadert

Many fields, where the reservoir is composed of sandy layers, show great complexity because of the lack of continuity which results from a particular type of seditnentation. This complexity may be a factor of prime importance in studying reservoir drainage, especially in the displacement of oil by water or gas. This paper describes work done to study this heterogeneity and its influence in the exploitation of the fields of the lower Devonian sandy shale in the Fort Polignac Basin in Algeria. Two lines of research were followed. 1. On the border of the hasin, a detailed sedimentological study established rules for the distribution of the sandy zones, which furnished hypotheses necessary for devising a geologic model of the reservoir. A certain number of sandy zones were recognized and characterized by their sedimentation. 2. In the interior of the basin, production logs deterrnined the productivity profile. Study of these point data led to a description of the distribution of oil and gas phases in the reservoir so that the continuity of different zones between the wells could be deduced. These techniques were applied to the study of the lower Devonian sandy shale reservoir of Zarzaitine. The sedimentological study guiding the correlation work, with the aid of the conventional static data (logs and cores), led to the establishment of a useful geologic model of the reservoir. Production logs, thanks to the contribution of dynamic elements, permitted corrobora-tion of the model. In particular, the logs confirmed separation, as proposed by the sedimenfological study, of two comparable sandy groups by revealing the continuity of a thin impermeable layer, invisible on conventional logs. INTRODUCTION The heterogeneity of sandstone reservoirs considerably influences the distribution of fluids, as well as their displacement in the reservoir. Rational development of a field and maximum recovery of hydrocarbons are closely tied to an exact and precise knowledge of the intern architecture. We will try to show how it is possible I refine the knowledge of the reservoir by seeking qui different and varied sources of information. Productic geology, the group of techniques which leads to idei concerning reservoir architecture and its geometric descris tion, furnishes the framework of this undertaking. Of these techniques. those used so far are qui varied. Descriptive as well as quantitative, the technique partake as much of classical geology as of reservo science. They include (1) geologic studies of the enti basin, especially a stratigraphic and sedimentologic study of the reservoir member at its outcrop, detail1 observations of cores taken from wells and, finall oriented cores; (2) interpretation of geophysical dat (3) interpretation of electric logs, nuclear and sonic lo and dipmeters: (4) petrophysical study of the reserve on samples taken from wells; (5) reservoir dynamics (stu of the production history and, in particular, interpretati of production logs); and (6) analysis of the fluids a thermodynamic studies. This incomplete list could also include (1) study the migration of the fluids, (2) geochemistry (chemi characterization of the oils), (3) regional hydrodynamii and (4) injection and detection of tracers. If most of these techniques are classic, attention i nevertheless be called to applying two of the techniql in conjunction: the study of the reservoir member its outcrop and the study of dynamic distribution fluid phases in the reservoir through use of product logs, used in the study of the sandy shale reservoirs the lower Devonian of the Fort Polignac Basin, Alge in particular, their application to the study of the 2 zaitine field where they have led to a new and satisfact model of the reservoir will be described. THE ZARZAITlNE FIELD Situated in the interior of the Fort Polignac 8 about 150 kilometers (km) north of the lower Devol outcrop, the Zarzaitine Devonian oil field was discovc On Ian. 28, 19&apos;&apos; (Figs. 1 and l8). It is in the fern a monocline truncated by two perpendicular fault: great throw, with a downthrown section to the north\: Erosion at the top of the structure has caused one of it to disappear. It is a reservoir with a gas cap an m coefficient on the order of 1:5, open to the aql On the northeast, with the oil zone covering an Of 106 sq km and with initial oil reserves of 222 mi

Jan 1, 1967