By H. C. Brassfield, R. E. Fryxell, E. C. Duderstadt, E. A. Aitken, P. K. Conn

Permeation rates of hydrogen through are-cast tungsten were measured at temperatures from 1300" to 2600°C with hydrogen pressure differentials of 1 and 0.1 atm across isothermal membranes. Rates were nearly Proportional to square root of pressure, were inversely ProPortional to membrane thickness, and were temperature-dependent according to the equation: p = permeation coefficient in cu cm (stp)-mm per sq cm-min-atmlr2, R = gas constant in cal per mole-OK, T = absolute temperature in OK. Permeation rates of oxygen through tungsten were deternlined in the range 1965" to 2300°C and at calculated oxygen (02) pressures of 3.3 x 10-4 to 2.2 x at?n using sealed capsules containing Kmown quantities of tungsten oxide. Permeation coefficients obtained in this manner had a temperature dependency in the range of 40 to 45 kcal per mole of permeating species. Permeation coefficients for oxygen were higher than those for hydrogen in the temperature range studied. This is probably the result of oxygen solubility being much greater than hydrogen solubility at these temperatures at a gzven pressure. The purpose of this investigation was to determine experimentally the permeabilities of hydrogen and oxygen through polycrystalline tungsten at temperatures ranging from 1300° to 2600°C. Permeation rates of hydrogen through tungsten have been measured at temperatures up to 925°C,but no previous measurements have been reported for the temperature range covered in this investigation. Some diffusion measurements3&apos;&apos; and solubility measurements3 have been made for hydrogen at temperatures below 2200°C. No previous permeability studies of oxygen through tungsten are known to the authors; however, efforts have been made to determine diffusion rates5-&apos; and solubilities PERMEATION THEQRY Permeation has been defined by ortton" as the overall steady-state flow process from the gas phase on one side of a membrane or wall to the gas phase on the other side and includes the steps of adsorption, solution, diffusion, exsolution, and desorption; in a given temperature range, any of these processes may be rate-controlling. For diatomic gases, which dissociate prior to diffusion, the quantity of gas which permeates through a membrane or wall at a given temperature is directly proportional to the surface area of the membrane, the length of time of permeation, and the difference between the square roots of the pressures on each side of the membrane, and it is inversely proportional to the thickness of the membrane when diffusion-controlled, thus: q = total amount of gas permeating a membrane, p = temperature-de pendent permeation coefficient, A = area of membrane exposed, / = time, p i = gas pressure of high-pressure side, p2 = gas pressure of low-pressure side, d = thickness of membrane. When the surface reactions are not rate-controlling steps and the solution of the gas in the metal follows Henry&apos;s law, the permeation coefficient, P, is equal to the product of diffusivity and solubility. The permeation coefficient is also temperature-dependent according to the equation: Po = permeation constant, Q = activation energy, R = gas constant, T = absolute temperature. MATERIALS The tungsten materials used in this investigation were greater than 99.9 pct pure. The interstitial impurities ranged from < 1 to 50 pprn C, 7 to 35 ppm O, less than 15 pprn N, and undetectable quantities of hydrogen. Previous high-temperature studies of are-cast tungsten have shown that thermal treatment similar to that which the hydrogen permeation cells experienced reduces the carbon content from starting levels of 50 to 60 ppm to about 30 ppm. Metallic impurities were in the low (1 to 50) ppm range. The argon gas used in this investigation contained about 8 ppm N. None of the following gases were

Jan 1, 1968

By Kung-Lee Wang, Brian W. Mackenzie, Warren E. Morrison, DeVerle P. Harris, George F. Sharrard

The term "mineral economics" is applied to a wide range of activities in the mineral industries. Earlier chapters have described the application of economic concepts to the mineral industries-supply, demand, conservation, tariffs, etc. The solution of mineral economics problems is often assisted by the application of quantitative methods. The purpose of this chapter is to describe a number of quantitative methods-econometric, operations research, and management science techniques-which find application in the analysis of mineral economics problems. These methods include input-output analysis, trend analysis, forecasting techniques, simulation, multivariate statistical analysis, mathematical programming, and market research techniques. The purpose of this introductory section is to provide a mineral economics framework for the application of these methods. Mineral economics is a subdivision of economics that is justified by a sufficient number of economic problems in the mineral industry requiring special experience and an unusual combination of skills. These problems are concerned with the conversion of minerals as geologic resources to minerals as economic goods. The mineral conversion process is outlined in Fig. 8.A.1. The physical occurrence of mineral deposits in nature and the market demand for mineral products in the economy provide the basic stimuli. The conversion process embodies a number of sequential stages-exploration, the development of mineral deposits, and mineral processing facilities and, consequently, productive activity to supply market demand. Changes in demand and the depletion of deposits illustrate the dynamics of the process. Mineral economics applies economic con-

Jan 1, 1976

By W. F. Domis, F. von Gemmingen, R. W. Whitmore, F. Garofalo

Constant-load creep-rupture tests at 1100°, 1300° and 1500°F were made on a Type-316, 18 Cr-8 Ni-ZMo, austenitic stainless steel to determine the relationship between ruptzire life and other aspects of creep behavior, The test program was designed on a statistical basis to check the variability of various creep properties and to determine emprically the dependence of minimutn creep rate and ruptzire life on initial stress, The dependence of the rupture life, tn, on the initial stress, a,, is found to be related to the stress dependence of the wrinimum creep rate, i,, and secondary creep strain, The instabilities or breaks found in the conventionual log - logt, plots can be traced to either a change in the linear dependence of log i, on log a, or to a change in secondary creep strain. In the alloy tested, rupture is found to be predowmanantly of the inter crystalline type, For this material, the secondary creep strain is -found to depend on the nature of the grain boundary precipitate, which affects grain boundary migration. It has been shown for a variety of metals and al tested at elevated temperatures under creep conditions that the empirical relationship exists between rupture life, tr, and minimum creep rate, i,. This relationship, in which C and a are in some cases independent of stress or temperature, shows in a general way that creep rupture depends on creep behavior prior to tertiary creep stage. To determine more fully the factors which control creep rupture requires, therefore, more knowledge of the relationship between rupture and creep behavior. To obtain such information, constant-load creep-rupture tests have been made on a Type-316, 18 Cr-8 Ni-2 Mo, austenitic stainless steel at 11000, 1300°, and 1500°F. These tests were designed on a statistical basis to determine the variability of the various creep properties measured and to determine empirically the stress dependence of minimum creep rate and rupture life. As a result of this work, various empirical relations have been established defining more closely the factor, C, in the relation between rupture life and minimum creep rate. This factor is found to be proportional to the amount of strain during secondary creep. The variation of secondary creep strain with rupture life and temperature is determined and its effect on rupture behavior discussed. The variability in minimum creep rate and rupture life is also dis- cussed and the dependence of these quantities on initial stress is interpreted. TEST MATERIAL AND TEST PROCEDURES The material tested is an austenitic stainless steel, AISI Type 316, of the following composition: C, 0.07 pct; Mn, 1.94 pct; P, 0.01 pct; S, 0.021 pct; Si, 0.38 pct; Cr, 18 pct; Ni, 11.4 pct; Mo, 2.15 pct; All 0.003 pct and N, 0.043 pct. The material was received as a hot-rolled 0.5-in. diam bar which was sectioned into 3.25 in. long blanks. Each blank was heat treated by holding 1/2 hr at 2000° F followed by water quenching. A 3/8-in. coupon was removed from each heat-treated blank and the microstructure was examined, the grain size determined, and the hardness measured. The microstructure was found to be uniform from blank to blank and the grain size was found to range from 4 to 6 ASTM numbers. Hardness, measured using a 20-kg load, varied between 127 and 148 Vpn. Tensile creep-rupture specimens having a 0.25 in. diam within a 1.5-in. reduced section were machined from the heat-treated blanks. Constant-load tests were made on these specimens at 1100°, 1300°, and 1500 F. Six specimens were tested at each stress level. Three creep-rupture machines were employed for tests at each temperature, two specimens being tested in each machine for each stress level. To minimize any effect due to local inhomogeneities along the length of the as-received bar the specimens were randomized before test. Each specimen was tested to rupture and in most cases an autographic extension-time curve was obtained. For very low stress levels at 1500°F no auto-

Jan 1, 1962

By B. R. Queneau

Steel has been chosen as the metal whose solidification will be used to tie in the principles discussed in the previous papers. Although steel is the most important [ ] practical example that could be chosen, its solidification is complicated by the presence of many elements added either intentionally or present as impurities. The liquid steel bath in an open-hearth furnace contains carbon, manganese, phosphorus, sulphur, and many residual alloying elements such as nickel, copper, and molybdenum. The bath also contains oxygen, the concentration of which is a function of the carbon content, as shown in Fig. I. Deoxidizers such as silicon and aluminum may be added either before or after tapping depending on the grade of steel being made. There are four types of steel ingots: Killed, semikilled, capped, and rimmed, and these differ from each other in their state of oxidation. Each type of steel has advantages in the production of specific steel products, and it should be emphasized that no one type should be considered superior to the others. Fully deoxidized steels, known as killed steels, have little or no gas evolution on solidification. When the steel solidifies in the mold, shrinkage occurs which causes a large void known as "pipe." To minimize the amount of metal that has to be discarded on account of pipe, a big-end-up mold is used together with a refractory "hot top" which supplies molten steel to the main body of the ingot while solidification proceeds, Fig. 2. A section through a 32x32 in. ingot is shown in Fig. 3. The "hot top" volume is about 15 pct of the ingot, and the yield from killed steel in billet form is about 8o pct of the ingot weight. High quality machinery and tool steels are rolled from killed-steel ingots, but at the present time this represents less than 20 pct of the total steel production in the United States. In order to reduce cost and to increase

Jan 1, 1951

By Robert A. Kinzie

PAGE Introduction.............334 Climate.............335 History............335 Geology.............341 Mining..............343 Shafts............343 Stations and Ore-Bins....345 Levels. Drifts. Cross-Cuts, Winzes. etc........347 Stoping Surface-Pits,......... 351 Underground Stoping........... 332 Chutes. Drilling. etc.....354 Tramming............. 358 Sampling. Maps and Assaying.........360 Labor.............361 Machinery.............362 Milling,..............362 Crushers.............366 Battery-Foundations...........368 Power (Water—Coal)...........373 Methods of Catching the Free Gold...374 Screens..............376 Apron-Plates,.......376 Concentration..........378 Clean-Up,.............378 Labor..............382 Costs..............382 Introduction. The Treadwell Group comprises five mines. four of which are situated on the northeast side of Douglas island. directly opposite the town of Juneau, and one about four miles back of Juneau. These mines are owned by four separate companies. but are all under the same general management. Those situated on Douglas island are : The Treadwell mine. owned by the Alaska Treadwell Gold Mining Co.. the Mexican mine. owned by the Alaska Mexican Gold Mining Co.; and the Ready Bullion and Seven-Hundred-Foot mines. owned by the Alaska United Gold Mining Co. The Juneau mine. owned by the

Jan 1, 1904

By J. T. Eash, E. M. Wise

In a previous communication1 the improvement in slrength, harden-ability and color, occasioned by replacing gold in a typical gold-silver-copper alloy by various amounts of platinum, or palladium, was discussed. In the present paper the results of further studies upon the constitution and the nature of the hardening transformation in these alloys are presented. This research may be summarized as follows: 1. The liquidus and solidus have been determined for the alloys of the palladium and platinum series. Cooling curves were utilized for determining the liquidus of the palladium alloys but this method proved unsuitable for the platinum alloys so that a novel quenching method was utilized for the latter. Both the liquidus and solidus of the palladium alloys increase steadily with the palladium content. The liquidus of the platinum alloys increases rapidly with the platinum content, while the solidus temperature increases with the platinum content up to about 14 atomic per cent platinum, but suffers no further increase with additional increments of platinum up to 20 atomic per cent at least, owing to a peritectic reaction. 2. Palladium, and even more effectively platinum, reduces the rate of grain growth. Owing to this fact and to the increase in the solidus temperature, "overheating" does little or no damage to alloys containing reasonable quantities of these elements. This is confirmed both by tensile tests and metallographic examination. 3. The excess phase present in one of the high-platinum-content alloys has been isolated and chemically analyzed and was found to consist almost wholly of platinum, gold, and copper, evidently derived from the compound AuCu, by the partial replacement of gold by platinum. 4. The variation in the solubility of this platinum-content phase in the alpha solid solution with the temperature has been determined. This

Jan 1, 1933

By H. L. Shergold, O. Mellgren

Concentration of fine quartz particles at the iso-octane/water interface has been investigated under different conditions of pH and dodecylamine concentration. The results obtained from the related studies on the effect of amine concentration and pH on the interfacial tension, adsorption density, electrokinetic potential, contact angle, and concentration of the various amine species in the system are presented. A good correlation was obtained between these different variables. It is well-known that very fine mineral particles are difficult to float in conventional flotation machines. Flotation rate studies have revealed that the rate of flotation of fine mineral particles is much smaller than that of coarser size fractions. The theories accounting for this behavior have been discussed by Arbiter and Harris1 and also Meloy.2 Theoretically, a hydrophobic fine particle might never make contact with a bubble because of the presence of an energy barrier in the vicinity of the air/water interface.&apos; This energy barrier will have electrostatic, hydrodynamic, and Van der Waals force components. It was thought that by using an oil phase instead of air the energy barrier would be decreased so that fine particles could be concentrated at the oil/water interface more readily than at the air/water interface. The technique used involves dispersing the fine particles in water, containing the appropriate chemical reagents, and injecting a fine dispersion of iso-octane oil droplets into the pulp. After vigorous conditioning, the pulp is passed into a separating column where the oil droplets coated with a layer of mineral particles rise to the surface to form a separate layer. Air is introduced into the base of the separating column to ensure that heavy agglomerates of oil and particles report with the organic layer. This technique has been described previously4 and adopted by Lai and Fuerstenau5 who studied the alumina-dodecyl sulfonate system. The interfacial phenomena in the system composed of hematite, water, and iso-octane in the presence of sodium dodecyl sulfate have been studied and the results reported" earlier. This paper describes the results obtained from investigations into the interfacial phenomena in the quartz/water/iso-octane system in the presence of dodecylamine. The technique used in measuring the interfacial tension, electrokinetic potential, contact angle, and adsorption density were similar to those described previously? Materials Selected pieces of a high purity natural quartz, from the Isle of Man, were crushed in a laboratory jaw crusher and pulverizer. The — 52+72 mesh size fraction was retained and leached with successive washes of hot concentrated hydrochloric acid to remove iron impurities. When no iron was detected in the solution by ammonium thiocyanate, the quartz was washed thoroughly with distilled water until the conductivity of the wash water assumed that of the distilled water. Samples of 25 g of the —52+72 mesh quartz were ground for 5.25 min in an agate vibratory mill. The ground product was 100% —44 m and 57% —10 am, as determined by the Andreasen pipette. The specific surface area of the sample used for the adsorption and flotation tests was 0.94 sq m g-l. This corresponds to a mean particle diameter of 2.4 am. The —44 am quartz sample was stored under vacuum in the presence of silica gel crystals. For the contact angle determination between the three phases, quartz, iso-octane, and water, a piece of the natural quartz was ground into a block about 15 mm long, 15 mm wide, and 5 mm thick. One surface of the block was then polished by successively finer grades of silicon carbide "paper." The final polishing was conducted with alumina on a "hyprocel" paper. The polished quartz specimen was cleaned using nitric acid and ethyl alcohol followed by a wash with distilled water and then stored under distilled water. This pro-

Jan 1, 1971

By F. A. Crossley

The titanium-rich end of the Ti-A1 system has been investigated up to 35 at. pct A1 (23 wt pet). One conzpound Ti3Al was found to occur between primary a and TiAl. It is ordered hcp with DO19 structure, it has virtually no solid-solubility range, and it has a closed maximum at about 875°C. OIL either side of the compound are a +Ti3Al two-phase fields. The limiting a1uminum solubility in primary a at the titanium-rich end is indicated to be 7.5 at. pct A1 (4.4 wt pet) at 550°C and about 6.8 at. pct Al fl wt pct) at 500°C. Quenching alloys from above the a + Ti3Al two-phase field produces the following structures with respect to alloy composition: Up to 13 at. pct A1 (7.8 wt pet), a solid solution; from 15 to 18 at. pct A1 (9 to 11 wt pct), shear transformation product or martensite; from 19 to approximately 30 at. pct (11 to 19 wt pet), submicro-scopic coherent Ti3Al in an a malvix. The twin hcp phase fields reported in the literature are the result of nonequilibrium corzdztions. Ti-A1 alloys, once partitioned by dwelling- in the a + ß phase field during either hot working or heat treatment, are extremely difjicult to homogenize at temperatures below 1000°C. Such partitioned alloys exhibit the characteristics or symptoms of two-phase materials, and may be said to suffer the "twin-phase syndrome". THE earliest investigations of the Ti-A1 system by Ogden et al.1 and Bumps et al.2 reported wide solubility of the primary solid solutions. Aluminum was reported soluble in the low-temperature allomorph to the extent of 37 at. pct (25 wt pct), and the first intermediate phase was reportedly TiA1. Somewhat later Kornilov et al.3 reported a similar diagram with phase boundaries displaced towards lower aluminum contents and higher temperatures. Beginning about this time (1956) reports in the literature made it very clear that one or more intermediate phases occurred at lower aluminum contents than TiAl.4-17 These reports included five major investigations of the titanium-rich end of the Ti-A1 diagram.4,12,14,16,17 Three of these diagrams show two two-phase fields below 37 at. pct Al, while two of them show a single two-phase field. The existence of the phase Ti3A1 is firmly established and is included in each of the diagrams, except one—that of Sato and Huang.12 The new phases are reportedly hcp and differ from primary a only slightly when disordered, and when ordered the "a" parameter is approximately one,4,12,15 two, 6-10,13,14 or four14 times that for primary a. Beyond this, however, the diagrams are remarkable for their lack of agreement. Two tacit assumptions are usually made in phase-diagram determinations of metal systems. These are: 1) equilibrium anneals bring the alloy to equilibrium or to indistinguishable closeness to it, and 2) equilibrium conditions established at elevated temperatures are either "frozen" by rapid quenching for evaluation at room temperature, or quench-transformation products are recognized as such. In the current investigation evidence was obtained that over substantial composition ranges neither of these two conditions was met in any of the more recent major investigations. I) MATERIALS, METHODS, AND TECHNIQUES The alloys of this investigation were prepared by nonc on sum able electrode arc melting. Materials used in the preparation of the alloys are summarized in Table I. The investigative tools employed were: optical and electron microscopy, differential thermal analysis (DTA), disatometry, X-ray diffraction, electron diffraction, and resistometry. Alloys for microscopic and X-ray investigations were prepared as 15-g melts. Alloys containing from 7 through 11 at. pct A1 were hot-rolled out of a furnace at 900°C, from 12 through 15 at. pct out of a furnace at 1000°C, and from 16 through 18 at. pct out of a furnace at 1125°C. Alloys containing more than 18 at. pct A1 could not be hot-rolled. The ingots were covered with Markal coating prior to hot rolling to minimize atmospheric contamination. After hot rolling, alloys containing up to 15 at. pct A1 were ground and pickled to remove 7 mils from each surface; alloys containing 16 and 18 at. pct A1 were skinned to a

Jan 1, 1967

THOSE MARKED THUS * ARE MEMBERS, MARKED THUS t ARE ASSOCIATES THESE SIGNS DOUBLED INDICATE LIFE MEMBERS AND ASSOCIATES RESPECTIVELY THE FIGURES AT THE END OF THE ADDRESS INDICATE THE YEAR OF ELECTION HEAVY FACED TYPE SIGNIFIES HONORARY MEMBERSHIP ` *AARONS, JULIAN B , Mine Supt, The Boulder Deep Levels, Ltd , Boulder, Western Australia, &apos;05 *ABADIE, EMILE R, Cons and Min Engr, 1004 James Flood Bldg, San Francisco, Cal &apos;76 *ABBE, CLEVELAND, JR, GeOl Aid, U S Geological Survey, Washington, D C &apos;00 *ABBOTT, AI ARTHUR, Cerro de Pasco Mining CO , Cerro de Pasco, Peru, So America &apos;95 *ABBOTT, ARTHUR V , Electrical Engr , Westinghouse, Church, Kerr & CO , 8 Bridge St, New York, N Y &apos;82 *ABBOTT, CLARENCE E, Chief Min Engr, Care Fayal Mine, Eveleth, Minn &apos;04

Jan 1, 1910

By Eckley B. Coxe

The subject of this paper will be treated as briefly as possible under the following heads : I. The latest designs of some of the machinery used at these collieries in the preparation of coal. 11. The means employed for elevating, conveying and transporting the coal and slate in and about the breaker. 111. The means employed for raising the coal from the mines to the top of the breaker. IV. The iron breaker as a structure. V. The preparation of the coal as effected in the iron breaker. A key to the plates and the letters and numbers designating different parts, will be found at the end of the paper. I. Preparing Coal. Anthracite coal as it comes from the mines is not marketable. The "run of mine" cannot, as in the case of bituminous coal, be sold. Anthracite, being very compact and practically free from volatile combustible matter, burns only at the surface, and it is, therefore, deemed important to have the lumps as nearly of a uniform size as possible, so that between them a large amount of surface will remain exposed to the action of the air without checking the draught too much, or allowing enough air to pass to cool the coal below the ignition-point, In other words, if the pieces of coal of the size of a chestnut and smaller are mixed with lumps of the size of an egg they fill the air-passages and prevent a free draught. It has long been recognized, therefore, that one of the most important points in preparation is to have a uniform sizing, and also to make as large a number of different sizes as can be produced without too

Jan 1, 1891

THOSE MARKED THUS * ARE MEMBERS, MARKED THUS ?ARE ASSOCIATES. THESE SIGNS DOUBLED INDICATE LIFE MEMBERS AND ASSOCIATES RESPECTIVELY. THE FIGURES AT THE END OF THE ADDRESS INDICATE THE YEAR OF ELECTION. HEAVY-FACED TYPE SIGNIFIES HONORARY MEMBERSHIP. *AARONS, J. BOYD, Vivian Gold Mining Co., Ltd., Harris, West. Australia. &apos;05 *ABADIE, EMILE R., Cons. and Min. Engr., 214 Union Savings Bank Bldg., Oakland, Cal. &apos;76 ?ABBÉ, MAX F., Prest., Abbé Engineering Co, 220 Broadway, New York, N.Y. &apos;07 ? ABBÉ, PAULO., Secy.,Abbé Engineering Co., 220 Broadway, New York, N.Y. &apos;07 *ABBOTT, CHARLES W., Min. Engr. Pioche, Nev. ?08 *ABBOTT, CLARENCE Chief EDgr., Iron Mines, Dic Tennessee Caol, Iron & R. R. Co., Bessemer, Ala. &apos;04 *ABBOTT, JAMES W., Min. Engr: Ploche, Lincoln Co., Nev. &apos;94

Jan 1, 1917

By Peter Greenfield, Paul A. Beck

Thirty binary systems of vanadium and chromium group transition elements with second and third long period transition elements were explored in regard to the intermediate phases formed. It was found that the phases predominating in these systems are s, AB type with ordered a-tungsten or C8 structure, close-packed-hexagonal with small unit cell dimensions and, finally, phases isomorphous with 1-manganese. IN recent years, considerable information has become available concerning the intermediate phases in binary systems of the transition elements. Thus, the s phase has been found to occur in most of the binary systems of vanadium, chromium, and molybdenum with the group of elements manganese, iron, cobalt, and nickel.&apos; It was observed that, while the rr phases formed by chromium with manganese, iron, or cobalt possess a considerable temperature range of stability, particularly in the Cr-Co system, the corresponding s phases with molybdenum are limited to a temperature range of less than 400" above about 1200°C. Goldschmidt&apos; reported v phases of tungsten with iron and cobalt, and these are apparently stable only at (and above?) 1400°C." Exploratory work in this laboratory with Fe-W and Co-W alloys of approximately 60 atomic pct W annealed at 1300°C did not produce X-ray patterns suggesting the presence of a phase. It appears then that the phases of iron and cobalt with the chromium group elements decrease in stability as the two components are chosen from long periods further removed from each other. From the available information, it might be concluded that the controlling factor is the increasing difference in atomic radii between the components. In contrast to the a phase, the phases formed by iron and cobalt with chromium group elements&apos; are stable only when the latter have large atomic radii (molybdenum and tungsten); the corresponding phases with chromium do not occur. When the difference in atomic size becomes still larger (r,/r,, approaching the ideal value of 1.225), the u and p phases are replaced by Laves phases (AB,), as in the alloys of iron and cobalt with columbium," tantalum." and titanium."-" However, atomic size certainly cannot be the sole determining factor, since, for instance, in contrast to the very stable (Mo, Co)p phase, no such phase occurs in the Mo-Ni system even though the atomic diameters of cobalt and nickel are nearly the same. Similarly, chromium and cobalt form a a phase in a wide temperature range," but the corresponding s phase in the Cr-Ni system is missing. It has been shown that the composition of the u phase in various binary and ternary systems of transition elements in the first long period may be correlated in a fairly quantitative manner with the number of electron vacancies. The influence of electronic structure is probably present also in binary and ternary phases&apos; and to some extent, apparently, even in Laves phases." " Although the absence of phases in the Cr-Ni and Mo-Ni systems has not as yet been explained on the basis of electronic structure, it appears reasonable to suspect a connection. One of the great difficulties in arriving at well founded rules in regard to the alloying behavior of transition elements lies in the lack of reliable information concerning the details of their electronic structure in the metallic and alloy form. The theoretical penetration of this field appears to be beset by very considerable difficulties, even when the complications due to alloy formation are disregarded. Another great source of uncertainty is the scarcity of phase diagram information even for binary systems of the transition elements so that only a very limited basis is provided for generalizations as to the occurrence of intermediate phases. For instance, very few binary phase diagrams of second and third long period transition element systems have so far been published. The present work was undertaken in order to survey the various types of intermediate phases occurring in 30 binary systems of elements of the group vanadium, columbium, tantalum, chromium, molybdenum, and tungsten with the elements rhenium, ruthenium, rhodium, palladium, and platinum. For most of these binary systems phase diagrams are very incompletely or not at all known, as will be further reviewed.*

Jan 1, 1957

By H. B. Pulsifer

ABOUT 15 varieties, or modifications, of the best magnesium available were prepared and subjected to etching tests, then examined for microstructure. Of the 30-odd etching reagents that were tried, nearly half, mostly ammonium salts, etched the metal satisfactorily. The surfacing and etching of magnesium is shown to be a very simple and quick operation. The density and hardness of magnesium were determined. The most interesting new observations relate to the finding of the hexagonal etch figures, the crystal laminations, and the fact that the metal is plastic, cold, when restrained or quickly deformed. Under slowly applied pressure cold metal deforms slightly, then shears to fracture without plastic flow. The chief structural features of magnesium are presented in two reduced photographs and 30 photomicrographs. MATERIALS TESTED There are only two sources in the United States from which new metal can be procured: the American Magnesium Corpn. and the Dow Chemical Co. No pronounced structural or property differences in the metals from these two companies were disclosed by the work of this investigation. The following materials were obtained from the manufacturers: 1. Massive crystals of distilled metal (American Magnesium Corpn.). 2. Rods of hot-extruded metal, ½ -in. squares and 5/8-in. rounds (American Magnesium Corpn.). 3. Sheet magnesium, 0.005-in. thick (American Magnesium Corpn.). 4. Cast stick metal, 1 3/8-in. dia. (Dow Chemical Co.). 5. Magnesium-aluminum alloy, hot-rolled plate, ½ in. thick (American Magnesium Corpn.). From these materials, were prepared: 6. Sections from a furnace-cooled ingot made from distilled crystal. 7. Cold-strained pieces from (6), (4) and (2). 8. Pieces cold-squeezed to fracture from (6), (4) and (2). 9. Hammer-struck pieces from (6), (4) and (2). 10. Steam-hammer struck pieces from (6), (4) and (2). 11. Sections from furnace-cooled ingot of the magnesium-aluminum alloy.

Jan 1, 1928

By John R. Don

This paper, under the title of "The Genesis of Auriferous Lodes from a Chemical Point of View, Illustrated by Analyses of Samples Taken from the Chief Auriferous Area of New Zealand, Victoria and Queensland, by John R. Don, D.Sc., M.A., Lecturer on Geology in the University of Otago, N. Z.," was submitted by the author with the frank confession that its length, covering several hundred printed pages of the Transactions of the Institute, would preclude its acceptance for publication in full. But the great value of the original work which it records rendered its rejection on that ground highly undesirable ; and, after correspondence with Dr. Don, it was agreed that the Secretary should condense the paper, subject to the author&apos;s approval, omitting what was not essentially connected with the original work reported. In the discharge of this laborious and difficult duty, the Secretary&apos;s chief trouble has been his regret to cut out the acute criticisms and admirable theoretical and historical summaries of Dr. Don on the general subject of the science of ore-deposits. It should be added, that the original paper has been returned to the author, with full permission to publish it through any other medium (due mention being made of the first publication by the Institute of portions thereof), and a cordial expression of the hope that the treatise, as a whole, may be thus published, to the advantage of science. The Secretary begs to add, that many of the portions necessarily omitted from this condensed version would constitute, in his judgment, interesting and valuable separate contributions. In attempting to condense this paper, it was necessary at the outset to cut out the tint three chapters, of which the following brief outline is therefore given. Chapter I., introductory in character, indicates the importance of chemical analysis in the investigation of the genesis of ore-deposits, emphasizing the value of Prof. Posepny&apos;s Institute paper, and especially of the discussion which it aroused, and stating in general terms the theories of "lateral secretion" and "ascension." Chapter 11. describes the scope of the investigation undertaken by the author, the chief purpose of which was to determine which of the above-named theories was favored by the evidence obtained. This evidence consists chiefly (though not wholly) of analyses of the country-rock taken at various distances from the auriferous "reefs," (a) on deep mine-levels; (b) in the surface or "vadose" region : and also (c) of underlying, neighboring or connected crystallines (granite, gneiss, etc.). In addition to these investigations, there is a separate inquiry into the question of the deposition of gold in marine basins, suggested by the fact that most of the gold in the lodes of Australasia occurs in stratified deposits. Chapter 111. discusses the principles and methods followed by the author in the examination of country-rock for the purpose described. After giving his reasons for believing that careful tests of carefully-chosen samples of country-rock taken at varying distances from the ore-deposit might throw light upon the question

Jan 1, 1898

By W. H. Bassett

A 10-year, sea-water, corrosion test of tubes of several copper alloys has shown that many alloys withstood attack by solution, pitting, and dezinkification; a 1-year, salt-spray test of sheet-metal specimens of the same composition showed the same results. THE late J. P. Sparrow, chief operating engineer of the New York Edison Co., carried out a series of practical tests on condenser tubes of several copper alloys and reported on the results to the Association of Edison Illuminating Companies at its meeting in&apos; September, 1913. In the preparation of these tubes the senior author had the pleasure of cooperating. Copper-zinc alloys in the proportions of 60-40, 70-30, 80-20, 90-10, and Admiralty metal, which is in effect 70-30 with 1 per cent. of tin, were tried. Monel metal and several copper-nickel alloys, and 8, 5, and 3 per cent. aluminum bronze were also tried. At the time of this report, the aluminum bronze had been in service for 4 1/2 years and seemed to be giving especially good results but later it began to fail and showed no substantial improvement over Admiralty metal. Monel metal was unsatisfactory and the nickel alloys apparently did not give better service than the Admiralty alloy. Previous to the publication of the report, and after considerable discussion, it was agreed that a test where tubes of different kinds could be under laboratory observation would be advisable, so the apparatus described here was set up in The American Brass Co.&apos;s Waterbury Laboratory. This was fitted with tubes of copper, brass, bronze, nickel silver, cupro-nickel and other alloys, and the test started Oct. 11, 1912. Salt water from East River, New York harbor, was barrelled and transported to the laboratory for the test. A fresh supply, completely replacing the water in service, was obtained at the end of each six months period.

Jan 1, 1925

By G. Purcell, S. C. Sun

The objective of the present study was to detennine the role played by double bonds in the flotation of a very pure mineral using 18-carbon unsaturated fatty acids as collectors. Streaming potential measurements were made on a plug of pure synthetic rutile in solutions of inorganic electrolytes and unsaturated 18-carbon fatty acid soaps. Experimental results from these tests are detailed in the paper. The collector effectiveness of oleic acid with one double bond, linoleic acid with two double bonds, and linolenic acid with three double bonds has been a matter of speculation for many years, and conflic- ting experimental evidence1-8 has not clarified the issue. The overall objective of the present study was to determine the role played by double bonds in the flotation of a very pure mineral using 18-carbon un-saturated fatty acids as collectors. Since zeta potential is dependent on adsorption and orientation of ions at the solid-liquid interface, its variation under different conditions of pH and collector concentration should throw some light on the behavior of unsatu-rated fatty acids in flotation pulps. Titanium dioxide, in the form of rutile, was chosen for the investigation because it is now available in a very pure, synthetic, crystalline state, and despite the fact that it is one of the most important synthetic inorganic chemicals in commercial use, its electro-kinetic properties have not been closely studied. Electrokinetic properties of rutile in various aqueous solutions are discussed in this paper. Adsorption information gained from the streaming potential measurements enabled the flotation resultsg to be explained in a qualitative way, thus providing a clearer

Jan 1, 1963

By Ulick R. Evans, Maurice Cook

The structural changes in metals brought about by annealing follow-ing a deformation at a low temperature has been the subject of many investigations. No less than eleven metals and alloys have been studied in some detail; namely, aluminum, tungsten,2 iron,3 copperI4 gold, zinc,6 cadmium, tin: lead: brass,1° and cupronickel. As a result, it is possible to frame a qualitative statement of the effect of the degree of deformation and the temperature of annealing on the structure finally attained.

Jan 1, 1925

By Robert Goodrich

EXPERIMENTS ON A PORPHYRY COPPER ORE FROM BISBEE, ARIZ. THIS research was done partly in the non-ferrous laboratory of the Department of Metallurgy of Columbia University, under the direction of Dr. Edward F. Kern, and completed elsewhere. Acknowledgment is due to Prof. Arthur L. Walker, Dr. Edward F. Kern and Dr. William Campbell of the Department of Metallurgy, for their kind advice and for the inspiration derived from their instruction. This report is given under the following heads: Petrographic Description (Microscopic Study); Sampling and Preparing Ore for Treatment; Chemical Analysis; Treatment of Ore. PETROGRAPHIC DESCRIPTION Texture: Variable. Fine to medium mixed aggregate. Original structure: Obscure. Secondary structure: Fractured; healed.

Jan 8, 1915

By R. E. Steiner, A. F. Weinberg, R. J. Van Thyne

Uranium solubility in molten bismuth was determined in the temperature range 350" to 600°C, varying from 0.09 wt pct to near 2 wl pct, respectively. Zirconium and magnesium, simulated fission products, and sodium were found to increase or decrease uranium solubility in bismuth in the temperature range 370° to 420°C, depending upon the addition or temperature. Data were obtained by both chemical analysis of samples obtained by filtration from saturated melts and by measurement of the variation of electrical resistance with temperature. IN a study for the United States Atomic Energy Commission, a Liquid Metal Fuel Reactor Experiment (LMFRE) was proposed in which a solution of uranium dissolved in molten bismuth served as both the fuel solution and the primary coolant. It was proven necessary to add other elements to this solution for certain desirable properties: 1) zirconium acts to prevent reaction of the fuel solution with the graphite core (which would result in the formation of uranium carbide) and also to inhibit mass transfer of iron and chromium from the walls of the reactor tubing to cold spots resulting in blockage; and 2) magnesium acts as a deoxidant and prevents loss of uranium. In addition to these intentional additives, other elements entering the solution are: 1) fission products which are a by-productof reactor operation, 2) sodium (the secondary coolant) through possible small leaks in the heat exchange system, and 3) iron and chromium from the container walls. Each of these elements may affect the solubility of uranium in the fuel solution. Since the concept of this reactor is based upon a liquid solution, the relatively low solubility of uranium in bismuth will dictate the minimum temperature at which the reactor heat exchanger can be operated. The solubility of uranium in liquid bismuth and the effect of some additives on this solubility have pre- viously been investigated1-&apos; (more recent results6" became avaliable after initiation of this investigation). However, some discrepancies between the various results have been noted, and also the cumulative effect of the several additions or impurities was not known. This investigation was commenced to obtain definitive results. MATERIALS Analyses of the materials used are presented in Table I. Although ostensibly of extreme purity (99.999 wt pct), the bismuth was found to contain a significant amount of impurities, probably oxides. Except for determination of the binary system, Bi-U, prior to use all bismuth was hydrogen-refined and

Jan 1, 1962

By D. T. Peters, C. R. Cupp

Aging of commercial 18 pct Ni maraging steel and of related binary, ternary, and quaternary alloys has been studied by electrical resistivity, X-ray diffrac-tion, and hardness measurements. The aging process is in three stages: 1) recovery of martensite; 2) two precipitation reactions; 3) formation of nickel- rich austenite. The main objective of this work was to discover the nature of the Co-Mu interaction. Addition of cobalt to the Fe-18 pct Ni-5pct Mo alloy results in acceleration of the pvecipitation reaction by increasing the super-sat~lration 0f molybdenum. The cobalt-containing al- loys show no incubation period for the precipitation reaction, but the alloy without cobalt shows an initial slow reaction. These results are interpreted in terms of precipitation on dislocations. At low aging temperatures, the presence of cobalt leads to the appearance of a second type of precipitate which is a particularly effective hardener. Cobalt was found to retard the formation of austenite. Overaging is a combination of classical overaging and the formation of austenite in the structure. he- activation energy for the precipitation reaction determined from resistivity ,measurements is 42.8 kcal per mole and the growth of the precipitate is found to obey at law at high tenzperatures and a tU3 law at low temperatures. HE mechanism of strengthening of the 18 pct Ni maraging steels has been studied extensively since 1962.&apos;-? The strengthening is due to precipitation hardening of the martensitic matrix. The main precipitate is an inter metallic compound involving molybdenum, but there is disagreement about its identity.

Jan 1, 1967