By F. Forscher

Pronounced porosity, decreasing with distance from the fracture surface, is found in the necked region of tensile specimens tested at room temperature or liquid nitrogen temperature. A hydrogen solution treatment followed by a quench prevents pore formation in tests at —196°C, but has little effect on tests made at room temperature. Reduction of area values at —196°C are strikingly improved by the same treatment, but show no improvement in room temperature tests. The experimental results support the hypothesis that strain-induced porosity results with hydride initially present or, in material containing less than 50 ppm H, with hydride precipitated by strain aging. ZIRCONIUM'S advent as an engineering material in nuclear reactor construction has brought forth many investigations concerned with the properties of this metal and its alloys. Some attention has been given to the ductility of the metal.1, 2 Particularly, the effect of hydrogen on the impact strength was noted," indicating a pronounced dependence of ductility on the hydrogen content and its distribution in the metal. Micro graphic:' and X-ray diffraction studies' have shown that a precipitated hydride phase causes embrittlement in zirconium,' which implies a distinctly different mechanism from that causing hydrogen embrittlement in steels."-' In the latter case, it is assumed that atomic hydrogen diffuses to rifts, where it forms molecular hydrogen under such internal pressures that it causes the rifts to enlarge, leading to fracture. Thermo-dynamic studies of the Zr-H system8, 9 also indicate that the internal pressure of molecular hydrogen would be too low to cause any damage to the zirconium at room temperature, and the formation of a zirconium hydride (d phase) is favored." It is noteworthy that this phase has a face-centered-cubic structure and nearly 18 pet larger molar volume than close-packed-hexagonal a-zlrconlum' Other features of the ductility of zirconium are the absence of a typical cup-cone failure upon tensile testing, a pronounced strain-induced porosity in the necked region of a tensile bar, Fig 1, and the associated spongy appearance of the fracture surface A tremendous improvement in ductility at liquid nitrogen temperature can be observed following a heat treatment that retains the commonly present quan- tities (10 to 50 ppm) of hydrogen in solution. Such tests show a typical cup-cone failure and the absence of strain-induced porosity, Fig. 2. The present paper reports results of an investigation into the causes of strain-induced porosity in zirconium. Room temperature tensile fractures of mild steel, aluminum, and titanium have also been examined for strain-induced porosity. In each case porosity could be detected, but the amount was orders of magnitude less than was found in zirconium. Of the three metals, titanium showed the strongest effect. Material, Specimens, and Preparation The greater part of this investigation was done on Westinghouse crystal bar zirconium, are-melted, forged, and hot-rolled. Chemical analyses of the hot-rolled plates are given in Table I, along with those of the Foote crystal bar zirconium used in this work. The specimens were machined from the hot-rolled plate (1550°F) of 1/2 in. thickness and subsequently heat-treated according to one of the treatments shown in Table IS. All specimens were machined round, the longitudinal axis in the rolling direction, with a gage

Jan 1, 1957

By Ralph W. M. Lai, D. W. Fuerstenau

This paper presents the results of a study of the principles which control the distribution of ultrafine particles between an oil phase and an aqueous phase. Alkyl sulfonates were used to control the wettability of fine alumina particles and to stabilize the water-isooctane emulsion system in the extraction process. The effects of sulfonate chain length, sulfonate adsorption, pH, and oil-water ratio on the recovery of solids in the oil phase were investigated. Higher extraction was found under conditions which yield higher hydrophobicity and large interfacial area of the oil-water emulsion. Today there is considerable interest in developing methods for the recovery of fine particles from disseminated ores. One such method might be the extraction of fine particulate solids from aqueous suspensions into an oil phase, and one example of a successful industrial process based on oil-water distribution phenomena is the emulsion flotation process used in concentrating manganese ore.' The oil agglomeration process of Farnand, Smith, and Puddington has been suggested for concentrating tin ore. Patents 3-4 for oil flotation processes extend back to that of William Haynes in 1860. The basis of all these processes is directly related to the stabilization of emulsions with solid particles. The first extensive study of oil-water emulsions stabilized by finely divided solids was made by Pickering. Later, Briggs,6 weston, 7 Chessman and King,8 and Leja and Schulman9 experimentally demonstrated how solid particles control water-oil and oil-water systems. Hildebrand10 suggested that fine particles can stabilize an emulsion because the fine particles are partially wettable by both oil and water, that is, that the contact angle must be finite. Takakuwa and Takamori 11 recently applied emulsion inversion to the study of collector adsorption in flotation systems. At the Royal School of Mines, Shergold and Mellgren12 are currently carrying out a comprehensive study of the extraction of fine particles into an organic liquid phase. In the present study of the liquid extraction or oil flotation of ultrafine particles, the recovery of hydro-philic alumina particles of 0.1-µ average diameter was determined after separating an isooctane-water mixture (emulsion) into its two phases. Alkyl sulfonates of different chain lengths were used to change the wettability of the alumina and to effect emulsifi-cation of the oil-water mixture. The effects of the oil-water volume ratio, sulfonate adsorption, and pH on the recovery of the fine particles were investigated. Since the surface charge on an oxide such as alumina is determined by the adsorption or interaction of H+ and OH- with the surface, pH control is extremely important. Furthermore, since the zero point of charge (zpc) of alumina13-14 occurs at pH 9 to 9.4, major adsorption effects with anionic collectors in these systems will occur below pH 9. The results of the foregoing investigation are discussed in terms of the recovery of the fine particles, the oil-water ratio, contact angles, surface tension, the adsorption of sulfonate onto the solid surface, and the emulsifica-tion of oil. MATERIALS AND EXPERIMENTAL METHODS Materials: The particulate solid used in all the experiments was Linde "A" alumina, a high-purity, readily available form of a-alumina. The surface area of the alumina, as evaluated from measurements of stearic acid adsorption from benzene, was 14.5 sq m per gm, based on a value of 20.5 sq Å for the cross-sectional area of stearic acid.13 All aqueous solutions were prepared from triply distilled conductivity water. Other materials included high-purity crystals of sodium alkyl sulfonates, isooctane, and, for pH adjustments, reagent grade hydrochloric acid and sodium hydroxide-Because sulfonic acids are strong acids, they are

Jan 1, 1969

By V. A. Phillips, M. Safdar Ali

The tensile properties of Cu-0.20 pct Al, Cu-0.45 pct Mg, Cu-0.27 pct Cr, and Cu-0.22 pct Be solid-solution alloys were studied at -196°, 18°, 2509 and 500°C on wires internally oxidized at 900°and 1000°C. Internal oxidation produced marked increases in yield strength relative to pure copper, particularly at low temperature. The yield strength decreased with increase in temperature to a much greater extent than predicted by current theories of dispersion hardening. The strengthening effect of internal oxidation persisted throughout the entire stress-strain curve, but since a marked loss of ductility occurred at all test temperatures, only modest increases in tensile strength were realized. INTERNAL oxidation involves the preferential oxidation of a baser solute in a relatively noble solvent by diffusion of oxygen into the solid. Since the process is diffusion controlled, it is expedient to carry it out at a high temperature often approaching the melting point. The amount of solute is limited and the oxidation conditions adjusted so that oxygen diffuses inwards to meet the solute causing reaction to progress inwards and form subscale instead of only sur face scale. The reaction can be made to occur throughout the thickness of thin material producing a fine dispersion of oxide inside the metal. C. S. Smith1"3 appears to have been the first to recognize the true nature of the process of internal oxidation. Although extensive kinetic and metal-lographic studies followed by Rhines and coworkers,4-5 Chaston7 andMeijering and Druyvesteyn8 working independently were the first to report hardening effects due to internal oxidation. These results prompted detailed studies of the effects of internal oxidation on the hardness, tensile, creep, and fatigue properties of a number of alloys by G. C. Smith and coworkers9-12 in England, on hardness by Gottardi13 in Italy, and on hardness and tensile properties by wood14 in the U.S.A. Publications dealing with other aspects of internal oxidation will not be reviewed here. Internal oxidation of solutes having a high affinity for oxygen provides a means of obtaining very fine dispersions stable in a suitable atmosphere at temperatures well above those at which most age harden ing precipitates coalesce. The process therefore offers a method of producing thin sheet and wire of possibly outstanding creep resistance. The size limitation might be overcome by internally oxidizing porous powder compacts made from alloy powder before final sintering. PREPARATION OF ALLOYS The alloy ingots, which were approximately 5 1/2 in. long by 1 in. diam, were made up in a high-frequency furnace, using as raw materials OFHC copper, 99.99 + pct Al, high-purity magnesium, and master alloys of Cu-4.19 pct Be and Cu-10 pct Cr. The alloys containing aluminum and magnesium were melted ii closed high-purity graphite crucibles and solidified in the crucible which was lowered partly Out of the coil to give a hot-top effect. The alloys containing beryllium and chromium were made by melting in vacuo in alumina-lined sillimanite crucibles. The magnesium, chromium, and beryllium

Jan 1, 1960

By K. H. Coats

This paper describes an approximate technique for handling the problem of percolation of evolved gas upwards through the oil column in computer simulation of natural depletion. This technique has been incorporated into a general model for simulating three-phase flow in one, two or three dimensions. The mathematical model for perfonning these calculations is described in detail in a separate article. 1 While vertical gas percolation occurs during natural depletion in a reservoir of any configuration, it is especially pronounced in the pinnacle reel or bioherm. The reel may have an areal extent less than one section with a thickness of up to 800 It. The upward percolation of evolved gas often limits the time step in calculations as little as one day. Using this small time step, computer expense for a single 30- to 40-year simulation on even a one-dimensional basis has exceeded 92,000. The method described here for handling the percolation allows time steps of 60 days or more (depending on reservoir size and production rate), resulting in a considerable reduction in computing expense. The method also allows calculations in which secondary gas caps build up in tight zones of the oil column below the main gas cap. The validity of the method is indicated in connection with an example pinnacle reef field. Calculated results using a 2-day time step (where the method in question is not needed and not invoked) are compared with results using the method and a 60-day time step. The comparison shows good agreement. Results from one- and two-dimensional simulations of the reef are presented along with the corresponding computing times on the CDC 6600 computer. A three-dimensional simulation was also performed and the required computing time is given. INTRODUCTION A general analysis for simulating three-dimensional, three-phase flow in reservoirs has been developed. 1 In applying this model to reservoirs undergoing natural depletion, a time-step restriction was encountered due to the flow of evolved gas upwards through the oil column and toward the gas cap. A remedy for this problem has been incorporated in the analysis and is described here. The time-step restriction is encountered only in calculations which include flow in the vertical or near vertical direction. The restriction occurs to some extent in reservoirs of any geometrical configuration, but it is especially pronounced in the pinnacle reef or bioherm where the ratio of thickness to areal extent is unusually large. This paper describes the problem, a method of handling it, incorporation of the method in the three-dimensional, three-phase model, and, finally, a test of the method's validity in an application to an example pinnacle reef reservoir. THE PROBLEM During the early stages of reservoir depletion, pressure falls below bubble point in progressively lower regions of the oil column. Continuing production results in evolution of dissoived gas throughout the oil column. This gas then percolates upwards toward the top of the reservoir. If the gas encounters a sufficiently low permeability zone in its travel upward, then it can accumulate and form a secondary gas cap. If no zones are encountered which are tight enough to hold gas against the gravity forces, then the gas travels on until it reaches the top of the sand or the main gas cap. Numerical simulation of multiphase flow in reservoirs is generally performed with time steps such that the flow of a fluid into or out of a block in one time step is a fraction (considerably less than one) of the total amount of that fluid present in the block. Use of a time step where the time step's

Jan 1, 1969

By Oscar A. Glaeser

THE mine and plant of the United Verde Copper Co., located in Yav-api County, at Jerome, Arizona, have been described in various technical publications and, therefore, a brief outline of its essential features will suffice. The orebodies are of the schist replacement type, the main sulfide mass being a large lens-shaped body approximately 7 acres in cross-sectional area. In general, the mineralization is found along the iron-schist contact, with the orebodies extending about 1000 ft. along this contact and varying from a few feet to 250 ft. in width. The mine is located on a mountain slope and has openings into it on three horizons, as follows: 1. Raises and ore passes open vertically into the shovel pit. These extend down to the 1000-ft. level, where they terminate as loading bins in the Hopewell adit. The main fan intake air shaft, which also extends vertically down to the 1000-ft. level, has its surface opening on the hillside at the extreme north end of the shovel pit, and the main mine air return exhausts through a raise at the extreme south end of the shovel pit. 2. The 500-ft. level adit. 3. The Hopewell adit on the 1000-ft. level. The mine has a vertical downward extent of 2000 ft. below the 1000-ft. level. Underground operations are carried on through two main shafts, both of which are wholly underground. Shaft 5 is the ore-hoisting shaft. It has three compartments and extends from the 800 to the 3150-ft. level. Shaft 6 is the service shaft, and is used for lowering and hoisting men and material. It has a large cage compartment and three smaller compartments for counterweights, ladderway, and pipe and power lines. This shaft extends from the 500 to the 2550-ft. level, and is now being extended to the 3000-ft. level. An air shaft for the downward movement of fresh air from the fan has been provided, and extends to the 2550-ft. level at this time. Work has been started to extend this air shaft to the 3000-ft. level. A return airway for vitiated mine air, in the form of raises and short connecting drifts, extends downward to the 2100-ft. level. The underground mining operations extend from the 300 to the 3000-ft. level. There are about 45 stopes in active operation on the 17 levels

Jan 1, 1929

By J. H. Schulman, M. H. Buckenham

Although much interest has been taken in the use of mixed collectors in flotation, this investigation is probably the first in which oppositely charged collectors have been considered. The results obtained and the techniques used could well be applied in the behavior of other mixe the behavior of other mixed collector systems and could possibly explain the effective flotation results which have been reported when various collector combinations have been used. Collectors conventionally employed in flotation systems are soluble in water, but many of their homologs of longer hydrocarbon chain length are insoluble. The properties and behavior of these insoluble compounds may be conveniently studied when they are spread as monolayers at the air/water interface on the Langmuir-Adam trough. Although some extrapolation is involved in applying effects observed at this interface to the solid/liquid interface where the action of collectors is most important in flotation, the technique nevertheless is most useful for the study and interpretation of flotation phenomena. Of particular interest in this field are investigations on the insoluble monolayers of the fatty acids, alkyl sulfates and alkyl amines; the penetration of these insoluble monolayers by soluble surface active components and their interaction with metal ions from the underlying solution.'-' Unfortunately, the insoluble xanthates and related compounds do not exhibit stable monolayer properties due to rapid oxidation at the air/water interface and, therefore, cannot be studied directly in this way. These approaches have enabled Leja and Schulman8 to suggest mechanisms explaining dynamic attachment of mineral particles to air bubbles involving collector-frother interaction and the adsorption of collectors onto mineral surfaces. In this and other papers 9-12 considerable evidence is presented to support the concept of collector-frother and metal ion-monolayer interaction and to emphasize the value of monolayer techniques in elucidating the flotation system. Molecular interactions resulting from monolayer penetration are determined by the nature of and the association between both the polar and nonpolar groups of the two molecules concerned. Stable complexes are formed on penetration when interaction takes place between both the polar and nonpolar groups, and although the resultant complexes are not necessarily true chemical compounds, the properties of the molecularly associated complexes are very different from those of the individual components. Shortening of, or changes from, a straight hydrocarbon chain in one of the reacting molecules reduces considerably the stability of the associated complex as do changes in temperature, pH and substrate composition. The effect of hydrocarbon chain length becomes most important when observed effects are to be applied in flotation studies where soluble homo-logs and, therefore, much shorter hydrocarbon chain lengths are used. The present investigation is based on Langmuir trough work carried out by Bowcott,l3 who studied the penetration of insoluble amine monolayers by potassium lauryl xanthate. Bowcott observed that cetyl amine monolayers were readily penetrated by xanthate, but found that with time the high film pressures resulting from penetration and association fell off, indicating decomposition and ejection of xanthate from the film. This decomposition was pH dependent. Of particular interest in this work were studies on an equimolecular mixed monolayer of the fully N-substituted ammonium compound, for example, cetyl trimethyl ammonium iodide (CTAI) and potassium cetyl xanthate. Despite the fact that the CTAI is water soluble and the xanthate on its own is incapable of forming a monolayer, the mixed film was stable up to a surface pressure of 67 dynes per cm. In this condensed state the xanthate was stabilized against atmospheric oxidation, although iodine injected beneath the film caused an immediate collapse. The stabilizing of xanthate against oxidation by association with an alkyl trimethyl ammonium bromide (TAB) could be important in flotation, and a study of the performance and behavior of mixed collectors therefore was undertaken. A modified Hallimond tube operated under controlled conditions was used to evaluate flotation. Surface tension measurements were made to investigate the properties of the soluble

Jan 1, 1963

By J. T. Raleigh, D. L. Flock

This study investigated the nature of formation plugging with bacteria and attempted to relate its characteristics to physical rock properties. Fifteen core samples of four specific formation types were defined and plugged using a commonly occurring, uniform sized dead bacteria, Bacillus subtilis. Two of the formation types were fairly uniform-grained sandstones and two were heterogeneous carbonates. The injection rate and concentration of solids in the brine were held constant during the test runs. The pore geometry factor G was a significant petro-physical rock characteristic for correlation with depth of plugging, but lacked importance as a parameter for rate of plugging. Although the G factor may not completely describe porous rock geometry for plugging predictions, for reservoirs with multi-pore systems, there is evidence that the pore geometry factor might form a basis for establishing injection water specification in more llornogeneous reservoirs with only primary porosity development. INTRODUCTION GENERAL PURPOSE Injecting water into oil-bearing formations to increase recovery is common practice in the petroleum industry. One of the most serious operational problems involved with water injection wells is the tendency of the porous rock immediately adjacent to the injection wellbore to plug partially. This results in increased injection pressures and/or a decrease in the rate of injection. This plugging in injection wells can result from a number of causes, including bacteria contained in the injected water.1 The purpose of this work was to investigate the nature of injection plugging with bacteria and to attempt to relate its characteristics to physical rock properties. Many variables exist in research of this type, so, to reduce them, injection rate and concentration of bacteria in brine were held constant. The bacteria used for plugging was a uniform-sized, dead bacteria, Bacillus subtilis, a micro-organism commonly found in water, air and soils. Four specific porous rock types were plugged—two consolidated sandstones and two heterogeneous carbonates. The experimental work involved two distinct phases. The first concerned determining the physical rock properties and the second was the experimental work of actually plugging the selected core samples. PORE GEOMETRY FACTOR Capillary pressure is necessary to displace a wetting fluid from a capillary opening with a nonwetting fluid. The factors which govern capillary pressure are the surface or interfacial tension of the fluids involved, the system wettability and the equivalent pore radius. Thus: P,= 2ucososrd..........(1) Thomeer used the idea that the location and shape of the capillary pressure curve reflect characteristics of the pore structure of any porous media sample.' He presented the mathematical description of capillary pressure curves and of indicated differences in pore geometry of samples. where G = pore geometry factor PC = capillary pressure Pi = displacement pressure (V,)p, = fractional bulk volume occupied by the displacing fluid at any capillary pressure (V,), = fractional bulk volume occupied by the displacing fluid at infinite pressure or total interconnected pore volumes. The shape of the curve is defined by the pore geometry factor G. The curve shape is related directly to the sorting and interconnection of the pores of the sample. The location of an infinite number of curves can be defined by the same asymptotes. However, these curves differ in shape, each curve being described by a specific value of G. Thus, the description of a curve is unique when, in addition to the position of its asymptotes, its shape is defined. These curves can be used graphically to determine the characteristic parameters of any arbitrarily located curve. Those parameters that can be approximated from any capillary pressure curve are: (1) total interconnected pore volume, represented by (V,),- ; (2) extrapolated displacement pressure, the abscissa axis; and (3) pore geometry factor, by the curve shape. PROPERTIES OF BRINE AND BACTERIA The fluid used throughout this study was an aqueous solution of sodium chloride, 25,000 ppm by weight. The addition of salt to fresh water was intended to eliminate clay swelling in the sandstone cores and to retard leaching in the limestone cores. The viscosity of the brine solution at 100F, the temp-

Jan 1, 1966

By S. H. Moll, R. E. Ogilvie

The investigation of solid-state diffusion phenomena may lead to much information concerning binary alloys. In particular, a study of the concentration gradients present in multiphase diffusion couples can lead to the determination of the solubility limits of the single-phase fields in the phase diagram. The specific concentration gradient which results from the heat treatment of a diffusion couple depends not only upon the time and temperature of diffusion, but also upon the number of phases existing in equilibrium at the diffusion temperature. Such concentration gradients possess sharp discontinuities whose terminal points correspond to the solubilities existing at the limits of the two-phase field in the phase diagram at the diffusion temperature. In general, there will be a discontinuity in the concentration curve for each two-phase field which exists in the phase diagram between the concentration limits of the couple. A number of investigators have analyzed the gradients present in multiphase diffusion couples. 1-8 The iron-titanium phase diagram exhibits a y loop in the temperature range from 900" to 1400°C, and the limit of the a + y field lies at some composition which is less than 1 wt pct Ti for any temperature. It was felt that a diffusion study could yield values not only for the diffusion coefficients involved, but also for the chemical solubilities in the phase diagram. The concentration gradients were analyzed by an X-ray absorption technique developed by Ogilvie.6 The absorption of a monochromatic X-ray beam is measured in steps parallel to the diffusion direction and the resulting intensity gradients are transformed into concentration gradients by applying the laws of X-ray absorption in a binary system. This technique has been applied by ogilvie6 to the systems Ni-Au, Cu-Au, Fe-Cr, and Ni-Cr; by Gelles7 to the systems Be-Fe, and Be-Ni and by Hilliarde to the system Al-Zn. Linear X-Ray Absorption Analysis—The use of X-ray absorption analysis as a tool for determining concentration gradients arises from the fact that the beam is absorbed according to the quantity and species of elements present in the sample and not according to their state of aggregation. This method is more advantageous than the chemical analysis of machined layers since it is less time consuming and less expensive and can analyze a very small area. IF a homogeneous binary alloy (A + B) is analyzed with two different monochromatic X-ray beams I0(2) and lo(2) the following relation between the transmitted intensities, the intrinsic absorption coefficients of A and B for the two different radiations and the weight fraction of each element may be derived.' In (I/Io) (a+b) xa(u/p)a(2) + xb(u/p)8(2) Eq. [1] is independent of specimen thickness and density, but requires that either element A or B possess an absorption edge between the wavelength limits of the two monochromatic beams. I, is evaluated for each radiation by measuring the transmitted intensity through a varying number of foils of a suitable absorber. A plot of the natural logarithm of the transmitted intensity as a function of the number of foils, when extrapolated to zero foils, yields the value of I,. If a plot of the ratio in Eq. [ I] is calculated as a function of xA, then a master curve results. From

Jan 1, 1960

By W. Ivanick, Frank W. Glaser

ORDERING reactions of Fe-Si compositions in the a region have been mentioned in a number of review articles.7-8 However, little is known in regard to the critical temperature, T at which this transformation takes place. Greiner and Stoughton,' in a study of the constitution of iron-rich Fe-Si alloys below 800°C, placed the onset of order at a composition of about 4 to 5 wt pct (7.5 to 9.5 atomic pct) Si. They observed that at this composition the ductility and strength begin to decrease sharply and brittleness develops. During X-ray studies they observed only the appearance of superlattice lines for compositions containing 12.5 atomic pct Si. More recent X-ray diffraction studies- etected the appearance of superstructure lines (corresponding to the calculated positions of [Ill] and [ZOO] reflections) for alloys containing 9.5 atomic pct. This fact confirms Greiner and Stoughton's original hypothesis in regard to the onset of order at compositions containing about 7.5 to 9.5 atomic pct Si. The physical properties.of Fe-Si alloys containing more than 10 atomic pct Si have been studied only to a limited extent. Their extreme brittleness and difficulties of sample preparation render them of little industrial use in comparison with alloys in the 0 to 10 atomic pct Si range. The properties of Fe-Si alloys reported to date are mostly properties measured at room temperature on ordered compositions It appears that because of experimental difficulties fully disordered alloys could not be produced in the critical composition ranges and their properties could therefore not be reported. In Figs. la, lb, and lc, a summary of physical properties of Fe-Si alloys, measured during recent investigations of the influence of silicon additions to iron, is presented. No mention of determination of the critical temperature, T for disorder could be found in the literature. The following is an account of work done in an attempt to: 1) produce the disordered state of various Fe-Si alloys and establish the critical temperature, T for disordering, and 2) compare the electrical and thermal conductivity characteristics of the ordered and disordered phases as functions of composition. Materials, Preparation of Test Samples, and Testing Methods Fe-Si alloys with high silicon contents (about 10 atomic pct) are usually prepared using powder metallurgy techniques. This method insures accurate compositions and high purity through the use of protective atmospheres during solid state diffusion alloying of the mixed powders."" Iron and silicon powders were mixed in the desired proportions, cold or hot pressed, and then homogenized at 1150°C for periods ranging from 6 to 12 hr under a protective getter and in a hydrogen atmosphere. Fully homogenized samples were quenched in water from various and successively higher temperatures to establish the critical temperature for disorder. Temperatures were determined using Pt—Pt-Rh thermocouples in contact with the test samples. Test bars were approximately 0.6x1.25x7.5 cm. Electrical measurements were made at room temperature by determining the potential drop over a 1.5 cm span for a current of 10 amp. Densities of the samples were determined by immersion. High temperature electrical resistivities were measured using previously described techniques.'" Specific heat conductivity up to 200°C was measured by heating one end of the test bar and water-cooling the other; heat conductivity was then obtained by subtracting the rate at which heat entered the water from the

Jan 1, 1957

By Worthen Bradley, R. G. Hall

THIS paper will attempt to show how a metallurgical problem at one California quicksilver mine was solved, and how the solution was applied successfully at another mine. The pronouns "we" and "our," as used below, refer to the Bradley Mining Co. of San Francisco. The term "concurrent firing" for the purpose of this paper can be defined as feeding and firing a rotary kiln at the same end-that is, of course, the upper end. This is as opposed to "counter-current firing," the orthodox method, in which a kiln is fed at the upper and fired at the lower end. The terms "quicksilver" and "mercury" are used interchangeably. EARLY REFERENCES The earliest work on nonferrous metallurgy, we believe, was The Pirotechnia of Vannocio Biringuccio,1 its first edition having been printed in Italy in 1540. Quoting from its chapter entitled "Concerning Quicksilver and Its Ore": Quicksilver . . . is one of the gods and has divine strength in itself, and also, to the annoyance of the alchemists, it is winged. Hence, when it sees that it is in gravest danger, it loosens itself from . . . every bond . . . and flies away into the heavens, escaping from the hands of those who crucify it. Almost laughing, it leaves all its adversaries mocked and scorned, with their phials and filters empty . . . How thorough a job, under certain conditions, it can do of mocking its adversaries and leaving their phials and filters empty, was found out four centuries later at the Sulphur Bank mine, on the east shore of Clear Lake, in Lake County, California. The other mine mentioned in the title is the Reed, in Yolo County, California, 35 miles by road southeast of Sulphur Bank. Reed and Sulphur Bank ranked respectively fifth and seventh in U. S. production in 1943. The earliest direct reference we can find to furnacing troubles at these mines was by Thomas Egleston in 1890.2 Speaking of Sulphur Bank, Egleston says: Sometimes there is more sulphur than cinnabar in the ore, which is a detriment to both . . . making the sulphur impure, and rendering the cinnabar difficult to work on account of the soot. In some of the early . . . furnaces the accumulation of soot from the excess of sulphur has been known to penetrate as far as the fan blower at the end of the . . . condensers, and completely prevent its revolution. In order to get rid of the inconvenience of this accumulation . . . , as well as to get a commercial value from the sulphur, it (the sulphur) is now separated by steam and sold. It is claimed that the sulphur alone pays all the expenses of . . . the mine. The mine was first worked for sulphur, and the cinnabar it contained was considered to be an inconvenience, and was carefully picked out and thrown away. as its richness and value were not

Jan 1, 1945

By A. J. Griest, P. D. Frost, J. R. Doig

During the past 5 years, research directed toward the development of titanium alloys having improved strength-ductility relationships and heat treatability has been carried out at Battelle for the U. S. Air Force.1"3 In the course of this work, a method of heat treating ß-stabilized titanium alloys was developed which produced a wide range of useful properties.4 The heat treatment consisted of two steps: a) solution treating at temperatures in the a-ß phase region, and b) overaging at a lower temperature in the range 800°to 1100°F. Corollary to the alloy development work, research was conducted on the mechanism of the heat-treatment reaction. The investigations of Frost and co-workers on isothermal transformation in Ti-Cr5 and Ti-Mn8 alloys disclosed the existence of the transition phase, w, during the course of the decomposition of metastable ß phase. Subsequent work at Battelle7,8 'and at Case Institute by Brotzen and co-workerss further clarified the nature of the decomposition process. Beta decomposition was found to proceed by the following series of reactions: 1 2 3 4 a + Ti, My (in eutectoid systems). ßo, ßr, and ßU refer to ß phase of original, enriched, and ultimate alloy contents, respectively. Omega is a transition phase having a complex structure. 10-13 Step 4, of course, occurs only in ß-eutectoid systems. This paper presents data correlating transformation behavior with mechanical properties for the following alloys: Ti-8Mn, Ti-8Mn-2A1, Ti-4Mn-4A1, Ti-6Al-4V, and Ti-4Fe. The isothermal decomposition of ß in titanium-manganese alloys of similar composition has been investigated by Frost and coworkers8 and the effect of various annealing treatments on alloys in this system has been studied by Holden, Ogden, and Jaffee.14 The compositions Ti-8Mn-2Al, Ti-4Mn-4A1, and Ti-6A1-4V, were studied in the present work in an effort to define more clearly the effect of aluminum on the response to solution and aging treatments. Ogden, Holden, and Jaffee15 have invesitgated the effect of aluminum on the response of a similar alloy (Ti-8.8Mn-2.46A1) to annealing treatments, and Luini and Lee16 have made an exploratory investigation of the heat-treatability of the Ti-4Mn-4Al alloy. The Ti-4Fe alloy was studied as an example of a moderate1y active eutectoid system. Holden, Ogden, and Jaffee 17 have studied Ti-Fe alloys and have presented some hardness data for aging at 400°C for alloys of Ti-2.56, 5.01, and 7.35 iron after quenching from the a-ß field (750°C). EXPERIMENTAL PROCEDURES The experimental procedures generally used in the precipitation-hardening study are outlined in the following sections. Departures from these techniques are noted in the discussions of the individual alloys. Table I presents the nominal and actual compositions of the alloys studied, together with the swaging and rolling temperatures. In all cases, these temperatures were in the a-ß field and the microstructures consisted of an equiaxed a-ß mixture. Melting and Fabrication—Except for the commer-

Jan 1, 1960

By Albert G. Zima

According to recently puhlished statistics, it is predicted that as much oil must be produced during the next 16 years as has been produced during the past 75, in order to satisfy the high rate of consumption of petroleum products. During 1934, over 17,000 oil wells were completed in the United States, and it is expected that over 20,000 additional wells will be drilled during the current year. Were it not for the remarkable progress made during recent years in the improvement of drilling technique and in the development of equipment used in the production phase of the oil industry, it is doubtful whether sufficient oil could be produced to meet present requirements. A few years ago, wells seldom were deeper than 3500 to 4000 ft., owing to the limitations of the drilling methods and equipment employed. Today, however, through the application of scientific drilling methods and the adaptation of modern equipment and improved materials, many wells range from 6000 to 8000 ft. in depth, and a few recent completions exceed 10,000 feet. Drill Tools Modern rotary drilling tools are the product of ingenious design and careful selection and adaptation of materials used in their construction. They must withstand terrific abrasion and, because of their compactness, must be designed to resist exceedingly high unit stresses. In bits, core drills and reamers, the bodies are made of either forged or cast alloy steels, heat-treated to develop a combination of high strength and toughness. To provide sufficient strength to the threaded portions and to protect the threads from distortion or damage, the box or pin sections of the tools are hardened to approximately 310 to 330 Brine11 hardness number. Drill and reamer cutters are generally of the movable type; i.e., serrated cones, cylinders or disks, which can readily be replaced when

Jan 1, 1935

By N. A. Stockett

Southeast Missouri is the largest and oldest lead-producing district in the United States. For the year 1941, the statistical picture of pig-lead production, stated in short tons (partly estimated by the Engineering and Mining Journal) is as follows. Tons World production................. 2,000,000 United States Production .........- 460,000 Southeast Missouri production..... 142,000 The consumption of primary lead in the United States in 1941 was approximately 900,000 tons, or almost double the country's production. The largest previous year's in in the United States was 718,000 tons, in 1926. The largest quantities of lead are used for cable sheathing, storage batteries and white lead. During 1941 tetraethyl lead for auto and aviation gasoline consumed 50,000 tons of lead. The entire lead production of Southeast Missouri is now mined by the St. Joseph Lead Co., whose dominant position as the largest producer in the United States of lead directly from ores is best shown by the fact that in 1941 it produced approximately 31 per cent of the lead production of the United States from its mines in southeast Missouri, where 22,000 tons of ore, averaging over 3.00 per cent lead, is mined per working day. It is known that lead was mined at Mine La Motte, Madison County, Missouri, by Renault in 1723. Other white men and Indians probably did some mining prior to that time. Since 1865, the recorded production to Jan. I, 1942, shows that the St. Joseph Lead Co. and the various other companies that have operated in St. Francois County mined lead ore, which, after milling and smelting losses produced 5,980,000 short tons of pig lead. • About 95 per cent of the present lead production of Southeast Missouri is mined in St. Francois County. The northern part of this area is 60 miles south of st. Louis. The remainder of the lead is obtained at Mine La Motte, about 25 miles southeast from the center of the producing area in st.Francois county, Prospecting In this district, most of the ore is discovered by surface and underground diamond drills and by prospect drilling underground with rock drills. Each 2-ft. length of the cuttings from these Jack-hamer prospect holes is assayed for lead. These holes are marked and the records are entered on maps. It has been found that close drilling—100-ft. centers of holes, and sometimes less—is necessary in order to locate most of the smaller commercial ore bodies, many of which previously had been missed by drilling the areas with holes spaced 200-ft. centers or more. To date, geophysical and other methods of prospecting, apart from diamond and Mining Practices of the St. Joseph Lead Company in Southeast Missouri

Jan 1, 1943

By N. F. Schulz, H. A. Lex

Representative samples of typical manganiferous iron ores from the Cuyuna Range, Minn., were reduced to the metallic iron state at temperatures just short of fusion with an excess of coke in the manner prescribed by the R-N Direct Reduction Process. The magnetic separation characteristics of the reduced ores were determined at several grinds by means of the Davis magnetic tube concentrator. The efficiency of metallic iron concentration by magnetic separation was a direct function of the degree of metallization of the ore sample and of the degree of liberation at-tained in grinding. Some improvement of liberation characteristics was observed if a small amount of sodium chloride was present in the ore during reduction. Despite the extremely fine-grained structure of the crude ores, iron concentrates containing more than 90% Fe at iron unit recoveries of 90% or more were obtained from well-metallized samples of three of the four ores tested. The rejection of manganese to the tailings corresponding to such separations varied from 80% to 95%. The manganiferous iron ores of the Cuyuna Range in Minnesota constitute a major potential source of manganese in the United States provided that a technically and economically feasible process can be devised for its recovery. The iron and manganese of these ores occur chiefly as oxides or carbonates in the form of very small, irregular, discrete grains embedded in a matrix of quartz or other siliceous gangue. The present investigation was undertaken as a sequel to an earlier one conducted jointly by the U.S. Bureau of Mines and the R-N Corp. Those results indicated that the R-N Direct Reduction Process might be a means for recovering both a metallic iron concentrate and a marketable manganese by-product from Cuyuna manganiferous iron ores.' The R-N Process is one of many proposed schemes for the treatment of crude iron ores involving the di- rect reduction of the iron content to metallic iron followed by physical extraction of the iron. In general, it consists of the following stepsz2 1) Iron oxide in crushed natural ores or iron concentrates is about 95% reduced to metallic iron at elevated temperatures but without fusion in a rotary kiln in the presence of a solid carbonaceous fuel (usually coke), limestone, and combustible gases. 2) The kiln product, consisting of metallized ore, excess coke, lime, and coke ash is cooled. The excess coke is recovered and recycled to the kiln feed. 3) The metallized ore is ground for liberation and magnetically separated to yield a metallic iron concentrate. 4) The metallic iron concentrate is agglomerated by a briquetting process. The reduction kiln temperatures must be high enough for the desirable chemical reactions to proceed at practical rates without causing fusion of any of the ore constituents. The time of exposure of the ore to the reducing conditions must be ample for 90% to 95% metallization of the iron oxides present. If more than 95% of the iron is metallized, however, difficulties may arise in the briquetting step, presumably because of accompanying higher carbon content of the metallic iron. Although not always necessary, powdered limestone or dolomite may be added at some time during reduction to aid in eliminating sulfur and phosphorus from the final product.3,4 Other additives, notably sodium chloride, when present during reduction, result in improved liberation characteristics of the metallic iron from certain reduced ores.'v6 Under the reducing conditions normally employed, P(co + H2)= 1 atmosphere, and 1830' to 2150°F (1000° to 1170°C), the R-N Process is claimed to be adaptable to a wide variety of low, medium, and high grade iron and manganiferous iron ores. The manganese oxides and carbonates are reduced mostly to nonmagnetic MnO which is rejected to the nonmagnetic tailings. Manganese-bearing pyroxenes of the original ore, however, may be rejected poorly, if at all, apparently because these minerals occur within the iron lattice or are entrapped in the metal particles.7 The investigation was limited to studies of the Cuyuna ores listed in Table I, which were reduced to the metallic iron state under various conditions

Jan 1, 1969

By J. Paces, E. Miller, K. L. Komarek

The resistivity was determined as a function of temperature over the composition range from pure cadmium to 40 at. pct Cd. Melts with cadmium contents less than 85 at. pct had negative temperature coefficients of resistinity. On cooling below a transition temperature close to the liquidus temperature, the slope of the resistivity-temperature curve changed sharply. The activation energy calculated from the slope was 0.07 ev above the transition temperature and 0.14 ev below. The resistivity vs composition curve shows two maxima corresponding in composition approximately to CdSb and Cd3Sb2. THE relationship between the structure of a liquid and that of the crystal formed on solidification is at present not well-under stood. Various experimental determinations of the properties of liquids indicate that deviations from random atomic arrangements in liquids occur and that the properties of a solid and of its melt are closely related. Thermody-namic activities of liquids usually show negative deviations in systems where compound formation occurs in the solid,' and X-ray data indicate that close-packed solids and their melts frequently have nearly the same coordination number. Electrical resistivities and viscosities of liquids frequently exhibit maxima at compositions corresponding to compounds in the solid state. It should be of interest to study systems which have both stable and metastable compounds in the solid, and to determine if the short-range order in the liquid is affected by the existence of the metastable solid phase. The Cd-Sb system exhibits such a metastable phase. The phase diagram is shown in Fig. 1.3 The stable system has one intermetallic compound, CdSb, crystallizing in the orthorhombic crystal structure, with a melting point of 456°C. The metastable system also has one compound, Cd3Sb2, melting at 420°C and crystallizing in the monoclinic structure. Metastable alloys transform to the stable crystal structure in the temperature range from 250o to 350°C. Several distinct indications of very strong short-range order in the liquid phase have been reported in this system, with a close relation between the ordering in the liquid and the existence of both the stable and metastable solid phases. Scheil and Baach4 have observed distinctly different vapor pressures for liquid Cd-Sb alloys depending on whether the liquid solidified to the metastable- or stable-phase configuration. They observed an unusually sharp increase of the activity in a limited temperature interval immediately above the liquidus temperature of stable alloys, followed by a sudden decrease in slope to what they considered normal values. On cooling, the activity data reproduced the values in the normal range but then deviated from the values obtained on heating. They also observed that specimens of the stable phase upon melting and resolidifying always crystallized in the stable crystal structure as long as the melt was not heated to more than 485° to 525°C; otherwise solidification to the metastable phase occurred. However, in a later investigation, these results were not reproduced (13). The resistivity of liquid Cd-Sb alloys has been investigated by Matuyama 5, Oleari and Fioram, 8 and Belaschenko (141, but only above 500°C, the temperature region where Scheil and Baach observed no vapor-pressure anomalies. The data of Matuyama and of Oleari and Fiorani are reproduced in Fig. 5 and show a maximum in resistivity at 50 at. pct Cd. The data of Oleari and Fiorani, however, show the maximum as being rounded, and their values in general are slightly higher than those of Matuyama.

Jan 1, 1964

By W. L. Mamme, G. Y. Chin

The problem of selection of the active slip systems for a crystal undergoing an arbitrary strain was analyzed by Taylor and by Bishop and Hill in terms of a minimum (internal) and a maximum (external) work criterion, respectively. These two criteria have now been generalized to include crystallographic slip on several sets of slip systems, twinning mixed with slip, and slip by (noncrystallographic) pencil glide. The generalized treatment also takes into account the possibility of a Bauschinger effect and of unequal hardening among the shear systems, which were considered in the Bishop and Hill work. Optimization techniques of linear and nonlinear programming are shown to be applicable for the numerical calculation of the minimum or maximum work. In the case of crystallographic shear, the constraint functions are linear and hence the optimal work is obtained as the saddle value of the lagrangian function Wi(y) e minimum and W,(u) + (a) for the maximum, where Wi is the (internal) work, We is the (external) work, Y is the crystallographic shear strain, u is the applied stress, and and are constraints. It is shown that the Lagrangians are functionally the same and the saddle value of one problem is identical to the saddle value of the other, proving that the two analyses are completely equivalent. In the case of pencil glide, although the constraint functions are nonlinear and neither convex nor concave, the equivalence of the optimal values to the saddle value of the Lagrangian (which is again identical for both problems) is still valid. WHEN a crystal deforms plastically by crystallographic shear, five independent shears are generally required to accommodate five independent strain components specifying the deformation. Assuming slip as the only shear mechanism, Taylor1 in 1938 analyzed the deformation in terms of a minimum work criterion. He hypothesized that of all combinations of five slip systems which are capable of accommodating the deformation, the active combination is that one for which the internal work C is a minimum, where 1 TI is the critical resolved shear stress for slip on the 1-th slip system and is the corresponding simple shear. By further assuming equal 72 for all equivalent slip systems and no Bauschinger effect, Taylor re- duced the minimum work problem to one of minimum and applied the analysis to the case of axisym- Metric flow by {111}(110) slip in fcc crystals. However, he did not consider the question of whether the resolved shear stress has in fact attained the critical value for slip on the newly found active systems without exceeding it on the inactive systems. In 1951 Bishop and ill' put forth the maximum work analysis in which slip is again assumed as the only deformation mechanism. In this analysis, the work o1 done in a given strain ij by a stress ujj not violating the yield condition is maximized. In addition, the analysis takes into account the possibility that the critical resolved shear stress for slip may not be equal among the slip systems and that the slip behavior may exhibit the Bauschinger effect. As with Taylor, a single set of slip systems—{111)(110) — was analyzed numerically. It thus appears that the Bishop and Hill treatment is on a more sound physical basis than the Taylor treatment. However, Bishop and Hill showed that where there is equal hardening among all slip systems and when there is no Bauschinger effect, Eq. [11 ] of Ref. 2, as assumed by Taylor, the results of their maximum work analysis are the same as those of Taylor's minimum work analysis. Hence at least under those conditions there is an implication that the Taylor analysis does lead to a critical resolved shear stress for slip on the predicted active systems without violating the yield condition on the inactive systems. Recently, the Taylor analysis was applied for numerical solutions of the axisymmetric flow problem, for slip on {110}(111), {112}(111). {123)(111) systems as well as a mixture of all three sets of svstems."1 Computational techniques based on the optimization theories of linear and nonlinear programming4 were employed in these solutions. The same techniques were employed in the solutions of an axisymmetric flow problem of deformation by slip on (111) (110) systems and twinning on (111)(112) systems5 which had been considered theoretically from a modified Taylor approach. The utilization of these techniques has led to the realization that the solutions of Taylor's minimum work problem imply the solutions of Bishop and Hill's maximum work problem. The two problems turn out to be dual problems in the well known sense of mathematical programming. It is thus the purpose of this paper to first generalize the minimum and maximum work analyses to include crystallographic slip on several sets of slip systems, twinning mixed with slip, and slip by (non-crystallographic) pencil glide, as well as the possibility of a Bauschinger effect and of unequal hardening

Jan 1, 1970

By R. I. Jaffee, F. C. Holden, H. R. Ogden

Ti-Mn alloys were studied in order to determine the factors affecting the mechanical properties of &stabilized titanium alloys. The principal compositional factors have been found to be solid-solution strengthening, the martensitic transformation, and instability of the P phase. Structural factors, such as grain size and shape, were found to have more influence on ductility and toughness than on strength. THE alloys of titanium with the &stabilizing elements offer the chief hope for developing useful heat treatments. Conversely, the heat-treatment response possible with the p-stabilizing elements causes difficulties such as weld embrittlement and thermal instability during service at elevated temperature. Therefore, it is of considerable technical importance to understand the factors that govern the heat-treatment responses in these alloys, so as to be able to soften the alloys if they are embrittled by an adventitious heat treatment, to render them stable in service, or to harden them while maintaining adequate ductility and toughness. The Ti-Mn system is a good example with which to demonstrate the factors that govern strength and heat-treatment response in. a P-stabilized system. The region of the a-j3 transformation, after the work of Maykuth, Ogden, and Jaffee,' is shown in Fig. 1. The a solubilities are low. This means that, in the two-phase a-p field, partition of manganese between the two phases occurs practically only to the P phase. The solid-solution effects are therefore chiefly the result of solution in the ,8 phase. The eutectoid occurs at 20 pct Mn and 550°C, and proceeds very sluggishly. It can be ignored in heat treatments in hypo-eutectoid alloys, except for long-time storage at low temperatures below the eutectoid temperature. Even here, there is some question that diffusion proceeds far enough to involve eutectoid decomposition. Three compositional factors bear on the mechanical properties and structure of titanium a-P alloys. These are: 1—solid-solution strengthening, 2—mar-tensite transformation, and 3—P instability. Combined with the purely structural factors of grain size and shape, these govern the properties of the alloys. Perhaps the most important factor is solid-solution strengthening. The facts that manganese dissolves in a titanium to a maximum of only 0.5 pct and most of the manganese partitions to the p phase dominate the structure and properties of the a-/3 alloys. Because of the overwhelming preference of manganese for the ,3 phase, the P phase is harder and the a phase is softer. The relative amounts of both phases may be modified by heat treatment in the a-P field as application of the lever rule in the two-phase field clearly shows. A critical temperature in the Ti-Mn diagram is 800°C. This is the P transus temperature of the 6.4 pct Mn alloy, which has the lowest manganese content which will form all retained-P phase on quenching to room temperature. Any quench performed from below 800°C will produce a structure consisting of only a, a plus retained P, or retained p, for alloys of the compositions used in this work. For alloys containing less than 6.4 pct Mn, any quench from above 800°C will always result in structures

Jan 1, 1955

By S. G. Epstein

Using the capillary-reservoir technique, electromi-gvation rates of cadmium and indium in liquid bismuth were measured at several temperatures. The electric mobility of cadmium Jrom 305° to 535°C and indium from 310° to 595°C can be expressed as a function of temperature by the equations UIn = 1.52 x 10-3 exp sq caz per v-sec Migraion of both solutes was cathode-divected at a rate rnore than four tiMes tHAt previously found for siluer in liquid bisnmth. The electric mobilities of cadmium and indiulrz in liquid bismuth at 500° C are nearly identical with their respective mobilities in mercury at room temperature. AS part of a systematic study of the variables which are considered to control electromigration in liquid metals, the electromigration rates of cadmium and indium in liquid bismuth have been measured. Mass transport properties of silver in liquid bismuth have been reported previously,&apos; and measurements of tin and antimony in liquid bismuth are forthcoming. Comparisons will be made with literature values for these same solutes in mercury.2&apos;3 This series of solutes was selected to determine the effect of the solute valence on its electromigration. Silver, cadmium, indium, tin, and antimony have nearly equal atomic masses but have chemical valences ranging from +1 to +5. They are all fairly soluble in bismuth above 300°C and all have radioactive isotopes, which are an aid in making analyses. EXPERIMENTAL TECHNIQUE Electromigration of cadmium and indium in liquid bismuth was measured by the modified capillary-reservoir technique previously described.&apos; In this method irradiated cadmium or indium is added to bismuth to form alloys containing about 1 wt pct solute (<2 at. pct solute). Several quartz or Pyrex capillaries: 1 mm ID and 5 cm long, vertically oriented, are simultaneously filled in the reservoir of the liquid alloy. A direct current is passed through two of the capillaries, which contain tungsten electrodes sealed in the upper end. The other capillaries sample the reservoir during the experiment. After a measured time interval the capillaries are removed from the reservoir and rapidly cooled. The glass is then broken away from the solidi- fied alloy, which is then weighed, dissolved in acid, and analyzed for solute content by chemical and radiochem-ical techniques. An electric mobility (velocity per unit field) can be calculated from the amount of solute entering or leaving each capillary by the simplified expression1 in which Ui is the electric mobility of the solute, ?mi the solute weight change, Ci the solute concentration of the reservoir, I the current, p the alloy resistivity, and l the duration of the experiment. This expression is valid as long as the experiment is terminated before a concentration gradient develops across the capillary orifice. Earlier experiments showed that the concentration gradient formed initially at the electrode changes with time and eventually reaches the orifice, due to back-diffusion. This condition produces a solute exchange between capillary and reservoir by diffusion or convection, opposing the electromigration, which results in a lower measured value for the electric mobility. To determine if the concentration gradient had reached the orifice, the capillaries used in some of the experiments were sectioned at 1-cm intervals and the solute content of the alloy from each section was radiochemically determined. A typical concentration profile for an experiment with indium in bismuth is shown in Fig. 1; cadmium in bismuth showed similar behavior. As illustrated in the graph, very little back-diffusion has occurred in the capillary containing the cathode, since the concentration gradient is confined to the upper 1 cm of the capillary. In the capillary containing the anode, however, the concentration gradient is much broader, extending nearly to the orifice, even though the net change in solute concentration is nearlv the same in both capillaries. Since cadmium and indium probably lower the density of bismuth when alloyed, depletion of the solute from the alloy adjacent to the anode would increase the density of the liquid in the uppermost region of the capillary. This would give rise to convective mixing within the capillary, causing the broadened concentration gradient. Conversely, the alloy adjacent to the cathode should have a reduced density as the solute concentration is increased by migration, explaining the "normal" concentration profiles found in these capillaries. This disparity was not found for electromigration of silver in bismuth. Both metals have similar densities at the operating temperatures, and nearly symmetrical concentration profiles were found in the two capillaries of each exueriment. This density effect was also apparently encountered when an attempt was made to measure diffusion coefficients for indium in liquid bismuth by the same technique which was successfully used to measure diffusion of silver in bismuth.&apos; Capillaries 1 mm ID and 2 cm

Jan 1, 1968

By N. A. Stockett

Southeast Missouri is the largest and oldest lead-producing district in the United States. For the year 1941, the statistical picture of pig-lead production, stated in short tons (partly estimated by the Engineering and Mining Journal) is as follows. Tons World production................. 2,000,000 United States Production .........- 460,000 Southeast Missouri production..... 142,000 The consumption of primary lead in the United States in 1941 was approximately 900,000 tons, or almost double the country&apos;s production. The largest previous year&apos;s in in the United States was 718,000 tons, in 1926. The largest quantities of lead are used for cable sheathing, storage batteries and white lead. During 1941 tetraethyl lead for auto and aviation gasoline consumed 50,000 tons of lead. The entire lead production of Southeast Missouri is now mined by the St. Joseph Lead Co., whose dominant position as the largest producer in the United States of lead directly from ores is best shown by the fact that in 1941 it produced approximately 31 per cent of the lead production of the United States from its mines in southeast Missouri, where 22,000 tons of ore, averaging over 3.00 per cent lead, is mined per working day. It is known that lead was mined at Mine La Motte, Madison County, Missouri, by Renault in 1723. Other white men and Indians probably did some mining prior to that time. Since 1865, the recorded production to Jan. I, 1942, shows that the St. Joseph Lead Co. and the various other companies that have operated in St. Francois County mined lead ore, which, after milling and smelting losses produced 5,980,000 short tons of pig lead. • About 95 per cent of the present lead production of Southeast Missouri is mined in St. Francois County. The northern part of this area is 60 miles south of st. Louis. The remainder of the lead is obtained at Mine La Motte, about 25 miles southeast from the center of the producing area in st.Francois county, Prospecting In this district, most of the ore is discovered by surface and underground diamond drills and by prospect drilling underground with rock drills. Each 2-ft. length of the cuttings from these Jack-hamer prospect holes is assayed for lead. These holes are marked and the records are entered on maps. It has been found that close drilling—100-ft. centers of holes, and sometimes less—is necessary in order to locate most of the smaller commercial ore bodies, many of which previously had been missed by drilling the areas with holes spaced 200-ft. centers or more. To date, geophysical and other methods of prospecting, apart from diamond and Mining Practices of the St. Joseph Lead Company in Southeast Missouri

Jan 1, 1943

By Robert Anderson

The diffraction of x-rays by cold-worked and heavily polished surfaces of metals gives, no evidence of an amorphous state and typically perfect crystallographic diffraction&apos; patterns are obtained. Severely cold-worked metals, reduced as much as 98 per cent. in area, give true crystallographic diffraction patterns, and polished surfaces of large single crystals of metal give typical crystallographic patterns. The conclusion is drawn, on basis of x-ray evidence, that metals are fragmented on cold work and polishing and not amorphized. THE purpose of this paper is to report evidence, regarding, metal: structures, that is contradictory to the amorphous-metal, hypothesis of Beilby, and particularly evidence that is opposed to the proposition that a vitreous amorphous layer is produced by polishing a piece of metal. According to the theory of Beilby, which has been developed, by Rosenhain and others, polishing a piece of metal greatly affects the condition of the metal at or near the surface polished, making that surface entirely different in character from the metal beneath. A vitreous amorphous surface film is said to be formed. The polishing process, on the basis of Beilby&apos;s explanation, is well known-and does not&apos; require discussion here, but it is advisable to seek the precise meaning of,., the term "amorphous." According to Beilby, "amorphous means. Non-crystalline in the most intimate sense of the word&apos;; the molecules are not marshalled in crystalline order and orientation." According to Rosenhain, the amorphous condition is that assumed by a metal when, the .crystalline arrangement is completely broken up so that the atoms exist in a state of disorderly arrangement similar to that ;which exists in the liquid state. Thus, from the point of view of the phase rule, the "amorphous phase" is regarded as being identical with the liquid phase. Amorphous metal is often likened to an undercooled liquid. A crystalline substance is one in which the atoms are arranged in space according to some definite repeating geometrical pattern. The existence of amorphous metal has not been definitely proved.

Jan 1, 1925