By Richard D. Hagni

Microscopic examination of selected, representative, unweathered samples of Birmingham, Alabama, Silurian, sedimentary iron ores has fully revealed the nature of the phosphorous-bearing mineral grains. The grains are composed of carbonate-fluorapatite (collophane), range in size from 1 um to 2.25 mm, and exhibit varied types of intergrowth with hematite. Modal analyses conducted under cathodolumi-nescence have provided quantitative data on the a3undance of each of 15 types of phosphorous-bearing mineral grains and made it possible to assess the potential phosphorous liberation from four types of iron ore. The results indicate that 27% of the total phosphorous contained in the iron ores in the western part of the Birmingham district can be expected to be liberated by fine grinding; 60% for ores in the eastern part of the district.

Jan 1, 1982

By Jiayan Li, Yi Tan, Yao Liu, Yaqiong Li, Shenrui Wu

"A metallurgical grade silicon (MG-Si) refining concept process was presented. Under vacuum conditions, silicon was selectively oxidized by high purity silicon dioxide to form gaseous silicon monoxide while impurities with low vapor pressure in MG-Si were rejected in residue; Then high purity silicon was obtained from the disproportionation of condensed silicon monoxide; and by-produced silicon dioxide was recycled for the oxidation step. Thermodynamics on boron rejection during the oxidation were studied in this work. In the temperature range of 1200-1800K, the saturated vapor pressure of boron, and the Gibbs free energy changes, the equilibrium partial pressures of silicon monoxide and boron oxides of potential reactions were calculated. And the effect of boron activity in MG-Si was also discussed. The results indicated that boron in MG-Si can be rejected during the oxidation and it showed the potential for the further development of the new refining process.IntroductionAs global energy consumption growing dramatically, higher prices of energy and global warming problem have attracted more and more attention [1]. As a clean and renewable energy industry, the photovoltaic (PV) industry converts solar energy to electricity using solar cell device and has a growth rate of about 30% in recent years. It has caused a shortage of silicon feedstock due to that about 90% of solar cells are made of crystalline silicon. And high energy consumption during the production of silicon material, i.e. solar grade silicon (SoG-Si), is main obstacle for its mass production."

Jan 1, 2012

By Fabio J. Esper, Guillermo R. Martín-Cortés, Francisco R. Valenzuela-Díaz, Cassio P. Carvalho, Giorgio Grotti, Reginaldo B. Santos

"Rejected sands from smelting metallurgical process because contain lead and others heavy metals are a problem to dispose as waste in all the countries. A procedure that is being proposed for it is to incorporate it on common clay bodies in the fabrication of structural ceramic products as bricks, blocks and roof tiles. The main goal of this paper is to present the results obtained with mixtures of sands from smelting metallurgical process with common clay from Jundiaí, São Paulo, Brazil. Preliminary incorporation tests (1,0% in weight) were made with hand formed spherical samples. With the higher compression strength of the spheres after drying and firing (950ºC) experiments on bricks production were made for quality technological test. Seven hundred hallow blocks containing 1,0% waste were produced and presented ceramic properties similar to those without sand incorporation. Introduction In last the fifteen years the LMPSol - Raw Materials & Non-metallic Solids Laboratory – Metallurgic Eng. & Materials Depto. – Polytechnic School - University of São Paulo comes studying the possibilities of incorporate industrials waste materials to the production of bricks and other products of construction aiming at to remove pollution products of the environments and to user the properties of the same ones in the structural ceramics products. Examples are the study of the influence of rejected steel furnace dusts in structural ceramic [1], another example is the main subject of the present paper: use of rejected sand from smelting metallurgical process in the production of bricks an other products of structural ceramics. Antecedents More or less one year ago, specialist and members from the direction board of METALÚRGICA GROFE LTD. Company contacted researchers and professors of the LMPSol – PMT – EPUSP seeking for a solution to their concern with the disposal of rejected sand from smelting metallurgical process."

Jan 1, 2008

By Qingchun Yu, Baoqiang Xu, Yongnian Dai, Bin Yang, Fulong Zhu

"In this paper, the mechanism of the carbothermic reduction-chlorination process to extract aluminum from alumina in vacuum was investigated. The carbon monoxide (CO) content of the gas, phases of the reduction slag, surface morphology of the reduction slag and the product aluminum were measured by means of gas chromatography (GC), XRD, and SEM. The experimental results indicated that the content of CO in the gas decreased, but Al4C3 increased with time at 1773K during the carbothermic reduction process of alumina. AlCl(g) and graphite (C) were produced by the reaction between Al4C3 and AlCh(g) at 1773K, and then aluminum beads generated after the decomposition of AlCl(g). It implied the mechanism of alumina carbothermic reduction-chlorination process in vacuum involves three steps as follows: the carbothermic reduction of A}z03 to produce Al4C3, the chlorination of Al4C3 by AlCh(g) to produce AlCl(g), and the decomposition of AlCl(g) to produce Al(l).IntroductionAluminum is the basic raw material for many industries [1], and it is used extensively because of various excellent properties such as light weight, good malleability, high strength, excellent thermal conduction, high corrosion resistance and so on [2]. Industrial production of aluminum currently includes refining alumina and electrolytic aluminum processes. However, its development has been effected by some factors such as high energy consumption and heavy environmental burdens [3]. In the past several decades, there had been numerous attempts to produce aluminum by new methods. Extracting aluminum from alumina or bauxite directly by carbothermic reduction-chlorination process had been studied [ 4-6]. Although the alumina carbothermic reduction process [7~9] had been studied, the mechanism of the carbothermic reduction-chlorination process had not been systematically elucidated.In order to investigate the mechanism of the carbothermic reduction-chlorination process in vacuum, GC, XRD and SEM techniques will be used to determine the CO content and to characterize the surface morphology and composition of the slags at various temperatures."

Jan 1, 2011

By Dimitrios Fillippou

Magnesium hydroxide is used in a number of industrial applications, from the neutralisation of acid effluents to the production of pharmaceuticals. High-quality magnesium hydroxide powders can be produced by hydrating slow-reacting magnesia in dilute magnesium acetate solutions. The process of magnesia hydration shows many similarities with a typical hydrometallurgical leaching operation; however, its kinetics are crucial not only for process design and control, but also for the production of powders with a desirable particle morphology. This article shows the results of an experimental work whereby industrial heavily-burned magnesia powders were hydrated in 0.01 to 0.1 mol/L magnesium acetate solutions at temperatures ranging between 333 and 363 K. Examination of the magnesium hydroxide produced and the analysis of the kinetic data suggest that the hydration of heavily-burned magnesia in magnesium acetate solutions is a dissolution-precipitation process controlled by the dissolution of magnesia particles. The activation energy was estimated to be 60 kJ/mol, while the reaction order with respect to magnesium acetate concentration was found to be about one.

Jan 1, 1999

By Gang Qi

The solubility of nitrogen in pure molybdenum was measured over the temperature range 2173 to 2473 K and up to one atmosphere (101 kPa) of nitrogen gas pressure. Both thermochemical and kinetic aspects of this phenomenon were considered in this study. The solution of nitrogen in molybdenum may be expressed by the reaction 1/2N2(g) = {N} (Mo,s), for which the standard Gibbs energy is given by the expression {A}G° = 78,500 + 27.36T Joules/g atom N. The formation of molybdenum nitrides, specifically Mo2N, was considered. Attention was also focused on the mechanism of nitrogen solution in molybdenum. Estimates of the diffusivity of nitrogen atoms in solid molybdenum were derived from the kinetic data.

Jan 1, 1991

By K. Ohmori, K. Takeya, S. Yoshizawa, A. Kawamoto, T. Ishikawa

"High performance Sm2Fe17N3 magnet powder is developed nitriding Sm2Fe17 alloy that 'is made using a reduction and diffusion method. Typical remanence, coercivity and maximum energy product of the fine powder are 1.40 T, 1.13 T and 323 kJ/m3, respectively. Decreasing samarium content, oxygen content and the amount of a-Fe are found to be the important factors to realize high-energy product.High performance injection molded Sm2Fe17N3 anisotropic magnet is also developed using the powder and an original binder system developed in order to mold at low temperature. Typical remanence, coercivity and maximum energy product obtained are 0.77 T, 0.78 T and 103 kJ/m3, respectively in the density of 4.77 Mg/m3The temperature coefficient of remanence is -0.07 %/K and that of coercivity is -0.54.%/K. The initial irreversible flux loss of the magnet that has a permeance of two is -5 % at 100 °C and the irreversible .flux loss of it is -4.4 % exposing it at 80 °C for 1000h.IntroductionSm2Fe17N3 alloy powder is expected to be very useful for a bonded magnet. The reasons are as follows. The magnetization is as large as the Nd2Fe14B alloy. Curie temperature is even higher than the alloy. The uni-axial anisotropy is comparatively higher than the alloy. Consequently it is possible to obtain high coercivity after just milling the powder and therefore possible to obtain high-energy product in a bonded magnet as it is realized in the SmCo5 bonded magnet. On the other hand, sintering is difficult because it will be decomposed into samarium nitride and a-Fe when heating it up to 500°C:"

Jan 1, 2000

By Kimio Itagaki, Makoto Ohtsuka, Kouki Chiba, Minoru Matsumoto

"The properties of Ni-Mn-Ga films such as chemical composition, crystal structure, microstructure and transformation temperature were investigated with respect to sputtering conditions in the present study. The Ni-Mn-Ga films were deposited on a polyvinyl alcohol substrate with a radio-frequency magnetron sputtering apparatus using the NisoMn2sGa2s and Nis2Mn:«1Ga24 targets. After separating from the substrates, the films were annealed at the temperature between 873 and 1273 K for 3.6 ks. The chemical composition of the films depended on the radiofrequency generating power, however, there was no dependence on the heat treatment temperature. Each deposited film had a columnar grain structure. After heat treatment, the width of columnar grains widened and then became indistinct with increasing heat treatment temperature. The Heusler type cubic crystal structure of the fi4n with heat treatment at 1073 K changed to the tetragonal one through the martensitic structural transformation during cooling. The martensitic structural transformation temperature increased with increasing nickel content of films, while the Curie temperature decreased. The film obtained at 200 W using the Nis2Mn24Ga24 target after heat treatment at 1073 K showed one-way shape memory effect through the reverse martensitic structural transformation during heating.IntroductionThe ternary intermetallic compound NiiMnGa has a Heusler-type crystal structure and is an intelligent material, which has a shape memory effect and a ferromagnetic property. The martensitic structural transformation occurs within the ferromagnetic temperature region. The cubic crystal structure of L21 at high temperature changes to a tetragonal one through the martehsitic structural transformation during cooling. The films of this compound can be applied for an actuator of micro-machines."

Jan 1, 2000

By Norihiro Murayama

Syntheses of zeolitic materials were carried out from coal fly ash by alkali hydrothermal treatment as part of the reuse and recycle technologies of coal ash, For the obtained zeolites, the cation exchange capacity and acid resistance, which are very important in the practical use of cation exchanger in aqueous solution, are investigated during this stufY, The cation exchange amounts of the NaP, CaP and K-CHA zeolites are measured for various cations such as K+, Na +, NH4+ Ca2+, Mg2+, Pb2+, Cd2+ and so on. The change in crystallization degree are researched as a function of pH. The simultaneous removal ability of NH4+ and PO43- in solution is examined for an example of the water purification with CaP zeolite. From these results, the characteristic and its mechanism of cation exchange are clarified for the various zeolitic materials obtained from coal fly ash.

Jan 1, 2003

By H. Fukuyama

The wetting behavior of single crystalline MgO by fayalite-type slag melts has been studied by the sessile drop technique incorporated with high temperature X-ray radiography. The experiments were performed under oxygen partial pressures of 10-6 and 10-4 Pa at 1473 K. Mass ratios of iron to silica, Fe/Si~, in the slag employed were 1.4 and 2.0. To investigate the interfacial reaction, experiments using high density MgO crucibles were also conducted. The reactions at the interfaces were examined by Electron Probe Microanalysis. The contact angles between the slag melts and the MgO substrates were found to be relatively low, ranging from 30 to 10 degrees. The surface tension of the slag was 0.4 N/m for a slag of Fe/Si02 = 2.0. Two phases, magnesiowiistite and olivine, were observed at the interface. Interdiffusivity in magnesiowiistite solid solution was determined as a function of iron oxide content. Phase relations between magnesiowilstite and olivine, and the growth rates of both phases, are also discussed

Jan 1, 1996

By Zhongning Shi, Ramana G. Reddy

"By cyclic voltammetry and potentiostat electrodeposition using Potentiostat/Galvanstat, electrochemical behavior on Ag electrode in electrolyte 0.2M NaOH+0.01MPb(NO3)2-0.01M TeO2 -0.01M TlNO3 solution were also carried out at 298K. The processes of electrodeposition of Tl2Te3 and PbTl4Te3, a thermoelectric material, are reported along with analysis of the composition of the obtained deposits. The results showed that two different underlying processes are occurring depending on deposition potential. One process involves the reduction of TeO3 2- and Tl+ to Tl2Te3 in a potential interval of -0.70V < E < - 0.89V (vs. Hg/HgO). A second process at more negative reduction potentials involves reduction of TeO3 2-, Pb2+ and Tl+ to PbTl4Te3 in a potential interval of -1.02V < E < - 1.19V. The crystalline Tl2Te3 and PbTl2Te3 were deposited electrochemically on Ag substrates at -0.84V and -1.10V respectively. Thermoelectric (TE) material can form a temperature gradient across the material to make electric voltage, which is popular in waste heat utilization and recovery industry. Lead telluride, PbTe, is a small band gap semiconductor of 0.32eV at 300K. PbTe can change its n-type semiconductors with Pb-rich to p-type semiconductors with Te-rich[1]. And it is one of the best TE materials used in thermoelectric generators working between 500K and 600K, or even at a higher temperature of 800K.Three facto,rs play a role in the performance of a thermoelectric material: electrical conductivity (s), thermal conductivity(?), and the Seebeck coefficient (S). These can be combined with absolute temperature (T) to give a figure of merit (ZT) for the material, ZT = s2sT/?. By increasing the electrical conductivity and decreasing the thermal conductivity, which can enhance the ZT value, many efforts, such as alloying with other elements and making the materials nano-sized, have been done to improve its properties recently. Hsu et al. reported that the ZT value of Cubic AgPbmSbTe2+m is increased to 2.2 by doping Ag-Sb to PbTe.[2]."

Jan 1, 2011

By C. Lupi

"The energy consumption of copper production by electrowinning, generally represents more than 1/4 of the total energy requirement in hydrometallurgical traditional process (roasting, leaching, purification and electrowinning). The considerable saving can be achieved just in this step that requires about 2.2 kWhlkg of the produced copper. To save energy the cell voltage, or more appropriately its anodic component, can be reduced: that is because the anodic voltage represents the main component of cell voltage and so it is largely responsible for the excessive energy consumption in copper sulphate electrowinning.In this work some ways are studied to lower the anodic voltage. First the cobalt ions were added to the sulphate solution in order to study the catalytic effect on oxygen discharge. Then lead alloys anodes (Pb-Ag, Pb-Sb-Ag and Pb-Ca) were used to promote a better oxygen evolution as a result of a different anodic surface. Their behaviour was compared with the PbSb traditional ones. Finally, as already pointed out by several authors for zinc electrowinning, ethylene glycol was employed as anodic depolariser in order to verify its effectiveness in the case of copper electrowinning. By combining all the above-mentioned ways, energy saving ranging from 20% to 27% is achieved.All the tests were carried out on a laboratory pilot-plant for long time to simulate the industrial conditions. The obtained copper deposits were observed by SEM to highlight their morphology."

Jan 1, 1997

By K. J. Cathro

A hydrometallurgical process is described for the recovery of copper from chalcopyrite concentrates. The process is based on a cupric chloride leach, the concentrate having first been "activated" by heating it with sulphur at a temperature near 400°C. This activation process converts most of the iron of the chalcopyrite to pyrite, which is insoluble in the cupric chloride leachant. The copper is converted to the mineral idaite, which dissolves readily in hot cupric chloride: at 106°C, 98% of the copper is extracted in a three-stage countercurrent leach, the leaching tirqe being 1 hour per stage. The sulphur of the chalcopyrite appears as elemental sulphur, which is recycled for the activation of further concentrate, the final leach residue consisting of pyrite, plus the gangue present in the original concentrate. The copper extracted can be recovered by electrowinning, using a diaphragm cell. Current efficiency (one-electron basis) is about 70% but the cell voltage is only about 1 V, so that power consumption is three times lower than for the conventional sulphate electrowinning process. The leachant is simultaneously regenerated in the anode compartment. The behaviour of minor elements in the concentrate has also been studied.

Jan 1, 1976

By M. L. Sorokin

The thermodynamic of nickel production from laterite ore and from sulfide concentrate can be analyzed using PO2 - PS2 diagram of the Ni-Fe-S-0-SiO2 system. The procedure of the diagram computation is suggested and the diagrams for various temperature and Fe/Ni ratio are calculated. Three-suffix Margules equations are used for the calculation of the thermodynamic properties of three solutions: liquid matte, liquid slag and solid Fe-Ni alloy. The diagrams are used for the considerations about direct one-stage metallic nickel production.

Jan 1, 1994

By Zhigeng Xu

Pressure leach of a Yunnan marmatite concentrates with adding coal as the elemental sulfur disperser was investigated. The experimental results show that the coal with carbon content higher than 70% is incapable of dispersing elemental sulfur from minerals and cannot improve the leaching of zinc. The coal with low carbon content (lignite coal) can act as excellent sulfur-disperser in the pressure leaching at 423K. The mechanism of lignite coal as sulfur disperser was further discussed by ultraviolet, infra-red spectrum and mass spectrum.

Jan 1, 2008

By S. Street

The Environment process, invented by Prof. H.K.Womer and developed at the University of Wollongong, simultaneously treats ferruginous and organic wastes via bath smelting. Conceived in the late 1980&apos;s, the patented process was originally developed using steelworks dust to settle solids from sewage, producing a composite material suitable for smelt reduction. Work began on the process in 1990 with the Australian patent having a priority date of February 1990. Early research focussed on settling of solids from sewage, while pyrometallurgical investigations examined smelting in small induction furnaces. By 1992 smelting trials had been undertaken in pneumatic and electric arc furnaces, the process being successfully demonstrated up to on 8 tonne scale. The success of this particular trial, and other smaller trials, resulted in construction of a 100kg DC arc furnace which was commissioned in 1993. By 1994 the main project focus was on development of the smelting technology. Over 3 years of trials on the DC arc furnace have identified and clarified many of the pyrometallurgical reactions. optimum operating parameters, as well as demonstrating the versatility of the process for treating a wide range of wastes. Currently the Illawarra Technology Corporation (lTC), the commercial arm of the University of Wollongong, is pursuing commercialisation of the process.

Jan 1, 1996

By Shaohua Ju

Siderite ore is abundant around the world, due to its inert properties of low grade, mudding when milling and low magnetic, and it is very hard to be beneficiated. Nowadays, decomposition by roasting becomes the main process for utilization of the siderite ore. The methods of energy input for roasting are normally electrical heating, coal or gas combustion. Because traditional roasting methods owns some disadvantiges, such as low energy utilization, high cost and/or large exhaust pollution, only about 10% of the siderite ores in China were used as iron concentrate. In this work, the possibility of roasting siderite ore with microwave energy is studied by both laboratory and pilot experiments. The result of laboratory experiments showed that the optimized condition is roasting for 20 min with a power density of 3 W/g, and the Fe content of the final sample obtained is about 59.12%. The pilot experiments result showed that the decomposition is thoroughly, and the main phases of the roasted material are magnetite and wustite, and the energy consumption of the roasting process is 695.8 KWh/t.

Jan 1, 2014

By Animesh Jha

"Fine ceramic powders (<500 nm) exhibit exceptional physical and mechanical properties in engineered structural ceramics. The production of fine powders, in particular the non-oxide ceramics, via a cheaper route than the organic solvent route has been rather elusive. This paper examines the physical chemistry of sub-oxide vapour-phase reduction reaction for the nucleation of non-oxide ceramic phase. Well known vapour species eg SiO and BO in the production of technical ceramic powders (SiC, BN) are particularly discussed for understanding the nucleation process of SiC and BN ceramic phases respectively. The regimes of partial pressures and temperatures are particularly 'identified. The calculated nucleation rate as a function of the temperature is compared with the experimental results on powder morphology. The production of amorphous and nanocrystalline h-BN powders is discussed in the context of substrate structure and thermodynamic parameters.IntroductionThe physical and mechanical properties of ceramic components are strongly dependent on the powder particle size and morphology used for their fabrication. For example the strength (Os) of the structural ceramic components increases with decreasing average grain-size (d) in accordance with the Hall-Petch relationship: Os = 0""0 + k/(d)1/2. Here k is an empirical constant which can be established from the graphical relationship. However as the particle size approaches submicrometer-size range, the dependence of strength on the particle size becomes more complex [1]. The design of ceramic components based on nanometer-size particles have recently become an important field which can offer ceramic materials with properties comparable to their metal counterparts. Several materials based on these concepts have been developed and reported by Niihara [2]. For example, the Al2O 3-SiC nanocomposite, having average B-SiC grain size 0.3-2um with intragranular SiC particulates of 5-10 nm has unusually high strengths (1100 MN/m2) at low and elevated temperatures combined with enhanced fracture toughness (> 4 MN-ml.5) which is an unusual combination in structural ceramics. Besides mechanical properties, as the particle size of ceramic powders approaches the nanometer-size range, the charge transport properties also improve by many times. The effect of particle size on the electrical conductivity of Si3N4-TiN composites has been well documented [3.4]. The size of ceramic particulates without doubt plays a pivotal role in determining the properties of ceramic components."

Jan 1, 1996

By Xie Hao

According to its raw materials orthogonal test scheme is designed and a large number of systemic experiments were carried out in order to study the sintering characteristics of three types of fine ores in Kunming Iron&Steel Co.Ltd(KISC). The effects of carbon mixture ratio and basicity on sintering time, agglomeration ratio, physical properties and utilize coefficient were researched via single factor analysis and range analysis. The experimental results show the best mixture ratio of each fine ore. Analysis found that the influence of the carbon mixture ratio is more significant than which of the basicity on the sintering process except agglomeration ratio of foreign ore.

Jan 1, 2009

By Sabine Knott

The thermodynamic properties of four liquid ternary zinc alloys, Au-Sn-Zn, Ag-Sn-Zn, AI-Sn- Zn and Cu-In-Zn were measured with an electromotive force (emf) method at three or four cross-sections with an constant X:Sn or Cu-In ratio. At the Au-Sn-Zn and AI-Sn-Zn system calorimetric measurements were also carried out in order to compare the integral enthalpy of mixing from the direct measurements with the data of the emf measurements, which were derived by Gibbs-Duhem integration.

Jan 1, 2003