Search Documents

By Strathmore R. B. Cooke, Paul B. Queneau

The kinetics of the dissolution of scheelite in basic solutions of carbonate and fluoride were investigated. Work was also done with solutions of alkali metal chloride, hydroxide, phosphate, and mixtures of phosphate and fluoride. The study was conducted at 90 psig and at temperatures ranging from 100" to 155"C, and both natural and synthetic scheelite single crystals were used. The interaction of scheelite with carbonate solutions generally followed a parabolic rate law, and resulted in the formation of calcite crystals on the attached surface. The transport of the CO3 through the calcite to the scheelite surface was probably rate -controlling between 115" and 135°C. Positive deviations from Parabolic behavior were observed at 100" and 155?C, presumably due to the calcite grain growth, and to the formation of a noncoherent calcite layer, respectively. The leaching of scheelite with alkaline fluoride solution produced a calcium fluoride reaction-product which covered the surface as a sheet-like layer. Below 110°C the dissolution rate was parabolic; at 115" and 135°C it was linear. In the linear region, the periphery of the calcium fluoride layer lifted from the sample. Only the lower layers, braced by the scheelite substratum, remained unbroken. This bound layer, approximately constant in thickness, limited the rate at which the fluoride could attack the scheelite. The phosphate and phosphate-fluoride leaches dissolved scheelite at a linear rate; solid reaction products were respectively hydroxyapatite and fluorapatite. Sodium hydroxide and chloride were not effective leachants, and did not produce observable solid reaction products. THE feasibility of pressure leaching of scheelite pulps with basic solutions containing either carbonate or fluoride ions, as indicated by the following equations, has been established by previous investigators:1-3 200°C CaWO4s + CO37q - CaCO3s+WO4aq [1] 200°C CaWO4s + 2Faq ^ CaF2s+WO4aq [2] It is to be noted that a commercial process employing reaction [I] is in use at Union Carbide's operation near Bishop, Calif. In the earlier work referred to, it was apparent that the precipitation of the solid reaction-product on the scheelite particles sharply reduced contact of the leachant with the scheelite. We have extended this work by studying the kinetics of dissolution employing single crystals of scheelite of known exposed surface area. In addition, the effectiveness of solutions of phosphate, of phosphate with fluoride, and of chloride and hydroxide as leachants for scheelite have been investigated. EXPERIMENTAL Apparatus. The low-pressure autoclave used in this wo (100 psig maximum) is essentially that of J. Halpern4 as modified by F. A. Forward.5 Constructed entirely of 316 stainless steel, its maximum capacity is 4000 ml. The temperature in the autoclave was regulated to *0.5?C by a Wheelco thermocouple controller. A 4-in. diam, three-bladed impeller, circulated solution upward against the sample, and a strobo-scope permitted holding the stirring rate to *15 rpm. A check valve and a "pop" type safety valve were installed, a sample holder was fixed to an externally adjustable rod, and a water-cooled condenser was placed in series with the sampling valve. The stainless steel sample holder, Fig. 1, held the epoxy-mounted sample (f) five mm above the impeller. Tightening the tapered sleeve (d) positioned the epoxy-resin specimen-mount by forcing it back against the spacer (c). The mount (e) was 1 in. diam. Sample Description and Preparation. Both synthetic and natural scheelite crystals were leached. The former were single crystals of 99.95 pct purity which were leached approximately perpendicular to the "c" axis; they were supplied by the Gallard-Schlesinger Chemical Manufacturing Corp. The natural crystals, supplied by Minerals Unlimited, were transparent, analyzed 99.8 pct CaWO4, and in ultraviolet illumination exhibited the characteristic blue glow of substantially molybdenum-free scheelite. To permit exposure of an essentially constant surface area of scheelite to the leachant, the samples were mounted in Scotchcast Brand Resin No. 250 (Minnesota Mining and Manufacturing Co.). The mount-

Jan 1, 1970

By J. H. Swisher

In measuvements of the solubility of nitrogen in fer-rilic Fe-P alloys, tile nitrogen solubility is found to be Less in pIrospliorus-bearing alloys than in pure iron. The reduction in solubility is about 20 pct in a 1.0 wt pct P alloy at 1300°C and about 30 pct in a 0.23 wt pct P alloy at 440°C. Diffusion coefficient measurements at 1150 and 585°C show that phosphorus also decreases the nitrogen diffusivity in iron. In previous work on the Fe-P-N system, phosphorus was found to reduce the nitrogen solubility in liquid iron slightly.&apos; Indirect evidence for similar behavior in a Fe at low temperature was obtained by Dickenscheid and Brauner.&apos; These authors found that phosphorus reduces the height of the internal-friction peak due to dissolved nitrogen. The results of Dickenscheid and Brauner were confirmed by J. C. Swartz of this Laboratory in a single internal-friction experiment using the same specimen stock as in the solubility measurements described below. In the present investigation, the solubility of nitrogen in a fer rite-stabilized Fe-1.0 wt pct P alloy was measured in the temperature range from 800" to 1300°C. Additional experiments were performed in the temperature range from 440° to 585°C, using an Fe-0.23 wt pct P alloy and NH3-H2 gas mixtures. EXPERIMENTAL The experiments were performed in a vertical tube furnace wound with platinum wire. For experimental temperatures of 800°C and above, a mixture of 5 pct Hz in N2 was used as the reacting gas. The gas mixture was prepurified from oxygen by passage over platinized asbestos at 450°C, and subsequently over anhydrone to remove water. Flow rates of the gases were measured with capillary flow meters. The temperature was measured before and after each experiment with a Pt/Pt-10 pct Rh thermocouple. The specimens used for the high-temperature solubility measurements were in the form of rectangular plates, 0.534 by 1.6 by 3.8 cm. The specimens were cleaned in trichloroethylene and annealed for 2 hr in hydrogen at the beginning of each experiment. In measuring the nitrogen solubility, the specimens were held in the reacting gas until equilibrated, then cooled in a water-cooled copper block at the bottom of the furnace. The time needed for equilibration at 1150°C was determined by measuring the average nitrogen content of the 1.0 pct P alloy as a function of reaction time. As will be described, the nitrogen diffusivity in the alloy at 1150°C is only slightly less than its calculated diffusivity in pure iron. At temperatures other than 1150°C, the reaction time used in measuring the nitrogen solubility was about twice the calculated equilibration time for pure iron at the same temperature. With a few exceptions, the procedure for the low-temperature solubility measurements was the same as that described above. The compositions of the NH3-H2 gas mixtures were determined by collecting gas samples from the gas train and analyzing them for NH3 by titration with HC1. The specimen thicknesses were less than those used for the high-temperature experiments, eg., 0.124 and 0.051 cm for measurements at 585° and 440°C, respectively. Nitrogen concentrations were obtained by chemical analysis, using the Kjeldahl method. The Fe-P alloys were made by adding ferrophos-phorus to electrolytic Plastiron (Type 104 A). Commercial ferrophosphorus, containing 3 pct Mn and 0.35 pct Si as the major impurities, was first purified by melting under an FeO slag. In a separate heat, the electrolytic iron was melted and vacuum-carbon-deoxidized prior to making the ferrophosphorus addition. The principal impurities and their concentrations in weight percent in the 1.0 pct P alloy are as follows: Mn, 0.01; Si, <0.01; C, 0.01; 0, 0.003; and N, 0.0012. The impurity levels in the 0.23 pct P alloy are con-

Jan 1, 1968

By W. Rostoker

Single isothermal sections were constructed for the titonium-rich corners of the systems Ti-Fe-O, Ti-Cr-O, and Ti-Ni-0 with a view to locating the shape and disposition of the ternary intermediate-phase fields for the compounds isomorphous with Fe3W3C. IN a previous note,&apos; it was reported that a group of ternary intermediate phases existed which occurred in the general composition range Ti,X,O-Ti&O where X was one of the following elements: copper, nickel, cobalt, iron, or manganese. In two instances, binary intermediate phases occurred (Ti²Cu and Ti²Ni) which appeared to be isomorphous. The X-ray diffraction patterns of the phases could be indexed on a cubic lattice whose cell edge was of the order of 11 kX. Karlsson2 stated that the line extinctions and line intensities indicated that these phases were isomorphous with Fe³W³C and therefore belonged to the space group Oh. This author also noted that no unique phase of this type occurred at the composition Ti,Cr,O. This latter statement was accepted as true at the time the previous technical note was written.&apos; However, work continued along these lines and that reported here has shown that a phase isomorphous with Fe³W³C does exist in the vicinity of the composition Ti³Cr³O but not at or near Ti4 Cr²O. The lattice parameter of this phase was found to be 13.01 kX. Metallographic examination of both as-cast and annealed specimens of these supposed ternary oxide phases disclosed structures which were far from single phase in many instances. It was considered a point of some interest to locate more positively the composition coordinates of the single-phase fields. To this end, single isothermal sections for the systems Ti-Fe-O (1000°C), Ti-Cr-0 (1000°C), and Ti-Ni-0 (900"C) were constructed. Phase relationships were studied by both X-ray diffraction and metallotrra~hic methods. Allovs were prepared as 10 g buttons by melting in a noncon-sumable electrode, water-cooled copper crucible arc-melting furnace using a helium atmosphere. Oxygen was introduced quantitatively by the use of weighed amounts of TiO² or TiO. Iodide titanium and the purest available alloying metals were used. All results are discussed in terms of the nominal composition of the melts. Previous experience with making oxygen-rich alloys had shown that oxygen losses were not significant if a homogeneous melt was produced. Weight-loss measurements were used to check loss in metallics during melting. Anneals were conducted in evacuated Vycor bulbs, and annealing times ranged from 24 hr at 1000 °C to 48 hr at 900°C. To achieve equilibrium in certain sluggish alloys, seven-day anneals were used. Debye-Scherrer powder patterns were taken in a 14 cm diam camera using filtered CuK radiation (K² = 1.541232 kX; K., = 1.53739 kX). Specimens were prepared by crushing and screening previously annealed buttons. In general, the X-ray diffraction results were used to identify the major phases, while the metallographic examinations were more useful in indicating the number of phases present. By the use of the combined results and general fundamental rules governing ternary equilibrium, it was possible to construct isothermal sections in good detail. In some instances where auxiliary lattice-parameter data were available, it was possible to lay down tie lines and to locate more positively corners of three-phase fields. Isothermal Section of the System Ti-Fe-O at 1000°C The binary systems Ti-O³ and Ti-Fe4 have been published. Binary phases, TiO, TiFe, and TiFe2, are likely to be encountered in the titanium-rich corner of the system. The structures are NaCl (Bl), CsCl (B2), and MgZn, (C14) types, respectively. Although preliminary X-ray diffraction studies indicated the presence of a ternary phase in the composition range Ti,Fe,O-TiJ?e,O, metallographic examination of two specimens at these compositions revealed the presence of other phases. Thirty-eight alloys were used to delineate the phase boundaries of the isothermal section illustrated in Fig. 1. The five almost single-phase ter-

Jan 1, 1956

By D. J. Rose, W. M. Armstrong, A. C. D. Chaklader

The wetiability of single crystals of MgO by specimens of vacuum-cast iron was studied using the sessile drop technique in vacuo at 1550ºC. Formation of FeO at the liquid-vapor interface caused the contact angle (6) to decrease from 117 to 65 deg during the first minute. After cooling, all specimens possessed a peculiar annular interfacial deposit of Fe,O,. Within the annulus the interface showed no sign of chemical attack. Chemical reaction occurred where the iron was alloyed with Ti, V, Cr, Nb(Cb), Ta, cmd Zr. Vnriation of 6 with alloy concentration was studied. Although vanadium md chromium improved the wettability of MgO by iron, the effect of Zr, Ti, Nb, and Ta was indeterminable because the 8 derived from sessile drop considerations was that of the metal against a restrictive peripheral volume of liquid oxide wetting the substrate. INTEREST in the nature of metal-ceramic interactions has been stimulated by progressive development of metal-ceramic combinations. One of the more valuable methods used for bond investigation is the sessile drop technique. Recent attempts to improve wettability through solute additions to the drop have revealed that the solute may a) react with the oxide creating new compounds at the solid-liquid interface, b) adsorb at the interface in a monolayer formation, or c) distribute throughout the drop uniformly causing no wettability variation. This work, part m in a series1,2 of investigations of interface reactions between metals and ceramics, embraces a study of the Fe-MgO system. MgO possesses a large negative free energy of formation (-173 kcal per g mole 0, at 1550ºC) compared to FeO at this temperature (-73 kcal per g mole 02). Hence the electronegativity difference between the drop and substrate allows selection from an extensive group of metal solutes with intermediate electronegativity differences that would, in the absence of chemical reactions, be expected to adsorb pre- ferentially at the solid-liquid interface. However, the high oxygen pressure of MgO in vacuo creates an oxidation environment which influences the solute behavior. Recent studies of the Fe-MgO systemJ74 have been restricted by chemical reactions that obscured observations. In view of the current interest in liquid-phase sintering of metal-ceramic combinations under partial oxidizing conditions,5 a more comprehensive study of the Fe-MgO system seemed beneficial. EXPERIMENTAL PROCEDURE 1) Specimen Preparation. Optical-grade MgO single crystals and Ferrovac vacuum-cast iron were used in all experiments. A spectrographic analysis of the iron indicated 0.008 C, 0.05 V, 0.005 Mo, 0.01 Ti, 0.002 S, 0.01 Cr, 0.001 Mg, 0.01 Si, 0.003 A1 (wt pct). The MgO crystals were cleaved along (100) planes into plates approximately 20 by 20 by 1 mm. Following annealing in vactto at 1100°C for 3 hr, surface irregularities were removed by a chemical etch in phosphoric acid at 100°C. The iron rod was machined into small cylinders approximately 0.250 in. in diam and length and these were carefully cleaned in organic and acidic solutions to remove surface impurities. All specimens were weighed to the nearest 0.1 mg. 2) Apparatus. The apparatus described in detail by previous authors1,2 was modified for this work. A Polaroid Land Camera was incorporated into the optical system so that drop measurements at ten-second intervals after melting were possible with ultra-high-speed self-develop ing film. 3) Procedure. The iron cylinders were placed upright on the MgO plates and positioned in the molybdenum susceptor. After furnace assembly the system was pumped down to a vacuum of 1 µ and flushed with H2 at 800°C. The system was again evacuated to 5 x 10-5 mm of mercury and the temperature raised to 1550°C within 2 min. The molten drops were photographed at appropriate time intervals. TWO min after melting the iron vapor pressure caused gas discharge, or corona, within the tube. The specimens were then slowly cooled to room temperature, sectioned and examined metallographi-cally. X-ray identification of interfacial reaction products was attempted by the powder diffraction technique. Alloying elements (Ti, V, Cr, Zr, Ta, Nb) were added to the iron in various concentrations up

Jan 1, 1963

By E. T. Hayes, A. H. Roberson, M. H. Davies

R. F. Dornagala and D. J. McPherson (Armour Research Foundation, Chicago)—I should like to compliment the authors for a workmanlike job in determining the partial phase diagram of a system comprised of two rnetals which are certainly not easy to work with. We are completing work at Armour Research Foundation on an Atomic Energy Commission-sponsored project for the determination of eight zirconium binary diagrams. Work on the Zr-Cr system has been completed and should be published within the next year. For our work, Westinghouse Grade 3 iodide crystal bar served as the zirconium melting stock. Johnson-Matthey, electrolytic chromium, specially treated for oxygen removal, was employed. The overall constitution of the system determined at Armour Research Foundation is in very good agreement with the present work. We found a eutectic at 18 pct Cr and 1280 °C, somewhat lower than the value reported. This temperature was confirmed by thermal analysis, incipient melting studies, and regular isothermal anneals. The eutectoid was located close to 1 pct Cr and 835°C by metallographic analysis of annealed specimens. Maximum solubility of chromium in /S zirconium was 4.5 pct at the eutectic temperature. Chromium solubility in a zirconium was less than 0.28 pct at all temperatures. We found the compound at 53 pct to melt around 1700°C, with an open maximum, but determined its crystal structure to be hexagonal close-packed (MgZn, type). The lattice parameters were in excellent agreement with those determined by Wallbaum in 1942. The diagrams are in substantial agreement, and .part of the differences are undoubtedly due to the use of different zirconium melting stock. M. K. McQuillan (Birmingham, England)—I read this paper with a great deal of interest, as it covered the same field as some work of my own.&apos; There are a number of points in the present paper on which I would like to comment. First, I should say that I, too, used zirconium prepared by magnesium reduction of the tetrachloride and electrolytically prepared chromium, and melted the alloys in a Kroll-type arc furnace. The purity of my alloys should, therefore, be comparable with the purity of those of the present authors, and any differences in our observations would not be expected to be attributable to this cause. The differences between my observations and theirs concern the presence of the eutectic, the temperature of the eutectoid, and the melting point of the compound. I would be very much interested in any further evidence the authors may have for the occurrence of the eutectic at 1380°C. During the course of my work I noted that a number of my alloys containing 60 to 90 pct Zr melted at about 1400 °C, and for a time assumed that a eutectic occurred at this temperature as described in the paper. On further investigation, however, I found that the structures of the as-melted alloys could not be made to fit in with this interpretation of the system. If a eutectic exists in this region of the system it would be expected that the as-melted alloys would show the usual type of cast structure, i.e., dendrites of the compound plus eutectic. This, however, does not occur, as may be seen from Fig. 9. The compound seen there is not dendritic in form, and the remaining material is by no means certainly eutectic. It may be argued that a compound such as ZrCrl would not form dendrites but would tend to crystallize in geometric shapes. In this case, however, I have evidence to the contrary, as on the chromium side of the compound, where a eutectic occurs at about 1545"C, the compound formed from the liquid takes on a conventional dendritic form, and the eutectic is observed in the interdendritic spaces in the usual way. There is no reason to suppose that the compound would behave differently in an alloy lying on the zirconium side of the compound composition if a eutectic existed there too.

Jan 1, 1953

By P. E. Busby, C. Wells

FURTHER study of data used in determinations of 1—rates of diffusion of boron in austenite and 2—solubilities of boron in the a and phases of iron and steel&apos; has provided an equation for the diffusion of boron in a iron. In brief, the previously published data were accumulated from the results of deboron-izing (and decarburizing) experiments carried out in the range of 700° to 1300°C. Diffusion coefficients (D?) for boron in austenite were calculated using the Grube solution of Fick&apos;s law. However, only solubility values were estimated from the discontinuous concentration-penetration curves, Fig. 1, which are characteristic of diffusion in two phases. Dr. Carl Wagner&apos; has recently provided a solution for calculating D values from penetration curves of this type as follows: Cl1.1 —C8/C8- C11.1 = vp ? e ? erf (?) and D = ?/4?2 t where C11,12, C8, C11, and E have the values shown in Fig. 1. D is the diffusion coefficient, sq cm per sec; t is time of deboronizing anneal, see; and ? is a di-mensionless parameter. For a given diffusion experiment, the value of ? can be readily obtained by graphical solution from a plot of y vs the right-hand part of Eq. 1. D may then be evaluated from Eq. 2. The avplication of this solution to previously re-ported results, of which excerpts are given in Table I, permits the calculation of diffusion coefficients for boron in a iron. On the basis of these meager data, it is tentatively concluded that the diffusion of boron in a may be represented by the equation Da = 1011 e-92,900/RT where R is the gas constant, cal X 0C-1 X mol-1; and T is the absolute temperature, OK. Although the frequency factor, 106 sq cm per sec, is admittedly several orders of magnitude higher than expected, the value of Q, 62,000 cal per mol, appears reasonable and is, in fact, very similar to that for the self-diffusion of iron. It is pertinent to mention at this point that the value of Q obtained for the diffusion of boron in austenite by means of the Wagner solution is 19,000 cal per mol and is in excellent agreement with the value previously reported1 in the equation DT = 2xl0-3 e-21,000/RT [4] which was determined by the application of the Grube solution to other data. The fact that determined constants A and Q in the equation D? = A e-Q/RT were practically the same, independent of whether the Wagner or Grube solutions were used in determinations of D values, strengthened the authors&apos; belief that the computed values of D (Table I) using the Wagner solution are reliable. The relative values in Eqs. 3 and 4 for the diffusion of boron in the a and ? phases, respectively, suggest that boron forms a substitutional solid solution in a iron and an interstitial solid solution in ? iron. The same tentative conclusion has been reached by McBride et al.3 on the basis of relative solubilities, atom diameter, and the size of the interstitial hole in a and ? iron. In connection with the data for test 14 listed in Table I, it is of interest to calculate the solubility of boron in a iron using the D value given by Eq. 3. As might be anticipated from the small movement of the interface in test 14, proper substitutions in Eqs. 2 and 1 give a low value, approximately 0.0004 pct B, at 850°C. Apparently at 835°C (test 13) it is possible to obtain 0.0018 pct B, and at 850°C only 0.0004 pct B into solution in the a phase before a second phase appears. These observations are consistent with the Fe-B constitution diagram proposed by McBride, Spretnak, and Speiser.3 References P. E. Busby, M. E. Warga, and C. Wells: Diffusion and Solubility of Boron in Iron and Steel. Trans. AIME (1953) 197, p. 1463; Journal of Metals (November 1953). &apos;W. Jost: Diffusion in Solids, Liquids, Gases. (1952) pp. 69-71. New York. Academic Press Inc. "C. C. McBride, J. W. Spretnak, and R. Speiser: A Study of the Fe-Fe2B System. Trans. ASM (1954) 46, p. 499.

Jan 1, 1955

By G. W. Healy, L. F. Sander

was investigated by reacting thin discs of calcium oxide with gas mixtures of CO2, CO, and Son. Its value was 19,300 * 300 cal independent of temperature in this range. No solid solubility of sulfur in calcium oxide was detected within the limits of the experimental method and it is estimated to be below 0.025 pct by weight. The importance of lime in desulfurization is well-established but complete information on the pure phase equilibrium: CaO + 1/2 s2 = CaS + +02 [11 is not yet available. The goal of this work was to evaluate solid solubility of CaS in CaO and to determine the free-energy change associated with Reaction [I] at temperatures of 1400" to 1650°C. The equilibrium constant for Reaction [1] can be written: It is convenient to rewrite Eq. [2] in the form: where A = {Ps /PqJ1&apos;2 has been referred to&apos; as the "sulfurizing power&apos; of a gas mixture. In this work, thin discs of CaO were suspended in a vertical tube furnace and exposed to CO + CO2 + SOz gas mixtures having known values of A. The samples were then analyzed for sulfur. As expected, X-ray diffraction confirmed that CaS was the only sulfur-bearing phase formed at the relatively low oxygen pressures used. EXPERIMENTAL PROCEDURE Reagent-grade CaCO3 was pressed in a 3/8-in.-diam pill die and prefired in air to produce CaO discs weighing between 0.004 and 0.01 g. Several discs were used to provide a suitable weight for chemical analysis while maintaining a large surface area to react with gas mixtures. These were placed in a platinum mesh basket and suspended in the gas stream in the hot zone of a vertical tube furnace. Desired gas mixtures were prepared from cp grade CO and CO2 and anhydrous grade SO2. The method of soap bubble displacement was used to calibrate capillary flow meters. While this gave excellent results with CO and Con, some problems with bubble insta- bility and soap film "drag" arose with the use of SO2 at low flow rates. Hence, frequent sampling and analysis of gas mixtures was carried out to insure proper control of the ingoing SOZ. The furnace used for gas:solid equilibration was a vertical mullite tube externally wound with 60 pct Pt-40 pct Rh wire having a diameter of 0.028 in. An inner tube of $ in. ID served as the reaction chamber having Pyrex ground joints sealed to the mullite to provide gas-tight connections at top and bottom. A Pt-Pt 10 pct Rh thermocouple was inserted into a protection tube adjacent to the sample basket to measure sample temperature during a run. Constant-temperature control to 2C was observed at any desired set point within the range of this investigation. This was accomplished by a control thermocouple imbedded in the furnace windings which served to actuate an electronic controller wired for high-low operation. The sulfur analyses of the solid samples were carried out using a stoichiometric combustion technique based on the method of Fincham and Richardson. Some analyses were done using a modified evolution method3 but these were used primarily to check the results of the combustion method. The results were in good agreement but the combustion technique of-ferred an advantage in economy of time and material. CALCULATION OF GAS EQUILIBRIA Heating a given mixture of CO + CO + SO2 to high temperatures gives rise to a large number of product species. The details of calculating the partial pressures of these products of interaction and dissociation can be found in several references4,5 and need not be repeated here. The thermodynamic data selected for the major species in the gas mixtures are shown in Table I. Equilibrium constants from these reactions were combined with oxygen, carbon, and sulfur balances and a computer program written to facilitate the calculations. Some early difficulties in reproducing experimental results were finally traced to the effect of atmospheric pressure changes. No reference to consideration of this question had been found in the

Jan 1, 1969

By F. J. Haller

IN 1943, we found, in the new Mather operation, a very unusual and disappointing condition in the footwall rock where all of our main haulageways were to be located. With the exception of a few hundred feet out of the thousands then planned and since driven, all of the openings require support. In general, the ground is not particularly heavy, at least by our standards, but it must be supported and the back carefully covered. Also, our operations require rather wide plat openings (16 to 18 ft) and rather flat curves at the turn-outs, all of which adds to the problem. When this completely unforeseen condition was discovered, ordinary timbering was the only answer, because of the impossibility of obtaining adequate steel supplies in time due to war shortages. Then by the time steel supplies were obtained and a practice developed, we found ourselves with between four and five miles of main haulage drifts and plat openings of a permanent nature, all of which were supported by hardwood timber, some of which had already rotted to an unsafe degree. Also, our drifting program was adding some two miles per year to the above figure. F. J. HALLER, Member AIME, is Superintendent, Mather Mine, Cleveland-Cliffs Iron Co., Ishpeming, Mich. AIME Columbus Meeting, September 1949. TP 2840 A. Discussion (2 copies) may be sent to Transactions AIME before May 31, 1950. Manuscript received Aug. 22, 1949. Revision received Jan. 17, 1950. To give all of the details of our experiments, studies, and experiences would fill a large book, but we were satisfied that our organization had done an excellent job, starting from scratch. You can appreciate our surprise when we discovered that we had added very little to an existing record. Attention was called to a footnote in a copy of "Carnegie Pocket Companion" year 1923. The note read: "Full information as to uses of H-Beams is given in pamphlet entitled &apos;Steel Mine Timbers.&apos; " A search of our Engineering Library brought to light a pamphlet printed in 1911 showing extensive use of steel for this purpose. Except for welding in place of riveting, we have added very little to the designs in that book. We have, however, developed an experience which proves, at least to our own satisfaction, that steel mine supports pay off under the proper conditions. We are now convinced, in spite of the relatively high initial cost of materials, that steel sets, because of comparatively low installation cost, are actually cheaper than either treated or untreated wood sets, if they are properly designed and adapted. Several Sections in Use: Convenience guided our first experiments in steel sets, since for a number of years, we had used the 4-in. WF, 10 lb per ft section in 10-ft lengths as safety forepoles along with wood forepoles. This section replaced the 40-lb rail which had formerly been used for the purpose. Having the 4-in. WF sections on hand, it was natural that our first experiments in steel sets involved their use. Later, the rolling of the 10-lb section was discontinued in favor of the much stronger 13-lb section, which is now standard for both legs and caps in areas of no particular weight, but which, none the less, require permanent support. Our experiments involved the use of the 10- and 13-lb sections as legs and 6- and 8-in. I beams, 16 and 23 lb per ft, respectively, as caps. Experience soon indicated that, if the ground were heavy enough, and the opening wide enough to require a cap stronger than 13-lb, the 8-in, 23-lb should be used, eliminating the 6-in. I beam. We now know that the 8-in. WF section of the same weight, which we propose to use in the future, is considerably stronger for the amount of money involved. Comparative Strengths: Tables I to IV giving strengths of several species of timbers as compared with the structural sections that we now use have been prepared in accordance with accepted practice. Experience indicates that failure due to compression perpendicular to the grain of the wood does not destroy the effectiveness of a wood set frequently enough to be a practical factor. Therefore, no table of these values is included.

Jan 1, 1951

By D. C. Hilty, W. Crafts

J. Chipman—It has been my privilege to discuss this work with the authors on several occasions and to observe at first hand the experimental methods employed. I wish, therefore, to emphasize certain points which they have mentioned only briefly with regard to the experimental techniques. The rotating induction furnace as here employed interposes liquid metal between slag and refractory thus preventing the two nonmetallic parts of the system from reaching equilibrium with one another. It is therefore impossible for the metallic phase to be completely in equilibrium with both the slag and the crucible. The metal also acts as a partially permeable membrane allowing certain components, including oxygen, to diffuse from slag to crucible. This transfer results in building up on the face of the crucible a layer of material whose composition is in part dependent on that of the bath. Reactions between the layer and the solid refractory are slow, as evidenced by the rather good life of the crucible. Hence it seems probable that the layer is more nearly in equilibrium with the metal than with the underlying crucible material and that, once it is established under a bath of a given composition, its further reactions with that bath are slow. Additions to slag or bath may be followed by changes in the layer; and time must be allowed for virtual completion of such changes, before it can be assumed that slag and metal are in equilibrium. We may judge from the results reported that, in general, this was the case and that the data represent at least quite close approximations to slag-metal equilibrium. Data on deoxidation and on oxygen solubility are no better than the analytical methods employed. The vacuum fusion method as used by the authors seems entirely adequate for the samples analyzed. I have had frequent occasion to compare results with their laboratory, always with very satisfactory agreement. The determination of aluminum at very low concentrations is perhaps an even more difficult procedure. Here also the colorimetric method used has been worked out with great care and is undoubtedly the most dependable method available. The discrepancy between observed and calculated deoxidation or solubility lines is not to be explained as the result of experimental errors, either in the sampling or analysis of the metal. Nor is it to be blamed upon inaccuracies in the several kinds of indirect data upon which the calculated results were based. It is true that both the observed and the calculated lines admit of some uncertainty as to their exact locations, but the uncertainties are small compared to the wide gap which separates the two lines. The authors have pointed out the real cause of the discrepancy. In all of their experiments the solid phase was not Al2O3 but a mixed oxide containing iron and aluminum. This suggests an extension of the calculated values to include equilibrium with the spinel FeO . A12O3. The free energies of FeO and A12O3 are known, that of the spinel is not. However, it cannot differ greatly from that of its component oxides for even in the more stable spinel, chromite, the free energy of formation from the oxides is less than 10,000 cal. For purposes of calculation we shall call this free energy X and solve for values of X lying between zero and 10,000 cal. The other data required are taken from the forthcoming revision of "Basic Open Hearth Steelmaking" and are given in the following equations in which underlined symbols indicate elements dissolved in liquid steel and the standard concentrations are 1 pct. ?F° at 1600°C, cal ?LA = 2 Al + 3 O; + 107,200 FeO = Fe + 0; + 5,460 FeO + A12O3 = Fe + 2A1 + 4 0; + 112,660 — X The corresponding equilibrium concentrations are shown in fig. 21. The line marked A12O3 corresponds to the first equation, those marked FeO . AL2O3 correspond to the last, with X = 0, 5000 and 10,000 cal, respectively. The two upper lines represent the data of Hilty and Crafts and of Wentrup and Hieber. The points are the observations of Hilty and Crafts in the presence of 0.50 pct Mn.

Jan 1, 1951

By F. J. Haller

IN 1943, we found, in the new Mather operation, a very unusual and disappointing condition in the footwall rock where all of our main haulageways were to be located. With the exception of a few hundred feet out of the thousands then planned and since driven, all of the openings require support. In general, the ground is not particularly heavy, at least by our standards, but it must be supported and the back carefully covered. Also, our operations require rather wide plat openings (16 to 18 ft) and rather flat curves at the turn-outs, all of which adds to the problem. When this completely unforeseen condition was discovered, ordinary timbering was the only answer, because of the impossibility of obtaining adequate steel supplies in time due to war shortages. Then by the time steel supplies were obtained and a practice developed, we found ourselves with between four and five miles of main haulage drifts and plat openings of a permanent nature, all of which were supported by hardwood timber, some of which had already rotted to an unsafe degree. Also, our drifting program was adding some two miles per year to the above figure. F. J. HALLER, Member AIME, is Superintendent, Mather Mine, Cleveland-Cliffs Iron Co., Ishpeming, Mich. AIME Columbus Meeting, September 1949. TP 2840 A. Discussion (2 copies) may be sent to Transactions AIME before May 31, 1950. Manuscript received Aug. 22, 1949. Revision received Jan. 17, 1950. To give all of the details of our experiments, studies, and experiences would fill a large book, but we were satisfied that our organization had done an excellent job, starting from scratch. You can appreciate our surprise when we discovered that we had added very little to an existing record. Attention was called to a footnote in a copy of "Carnegie Pocket Companion" year 1923. The note read: "Full information as to uses of H-Beams is given in pamphlet entitled &apos;Steel Mine Timbers.&apos; " A search of our Engineering Library brought to light a pamphlet printed in 1911 showing extensive use of steel for this purpose. Except for welding in place of riveting, we have added very little to the designs in that book. We have, however, developed an experience which proves, at least to our own satisfaction, that steel mine supports pay off under the proper conditions. We are now convinced, in spite of the relatively high initial cost of materials, that steel sets, because of comparatively low installation cost, are actually cheaper than either treated or untreated wood sets, if they are properly designed and adapted. Several Sections in Use: Convenience guided our first experiments in steel sets, since for a number of years, we had used the 4-in. WF, 10 lb per ft section in 10-ft lengths as safety forepoles along with wood forepoles. This section replaced the 40-lb rail which had formerly been used for the purpose. Having the 4-in. WF sections on hand, it was natural that our first experiments in steel sets involved their use. Later, the rolling of the 10-lb section was discontinued in favor of the much stronger 13-lb section, which is now standard for both legs and caps in areas of no particular weight, but which, none the less, require permanent support. Our experiments involved the use of the 10- and 13-lb sections as legs and 6- and 8-in. I beams, 16 and 23 lb per ft, respectively, as caps. Experience soon indicated that, if the ground were heavy enough, and the opening wide enough to require a cap stronger than 13-lb, the 8-in, 23-lb should be used, eliminating the 6-in. I beam. We now know that the 8-in. WF section of the same weight, which we propose to use in the future, is considerably stronger for the amount of money involved. Comparative Strengths: Tables I to IV giving strengths of several species of timbers as compared with the structural sections that we now use have been prepared in accordance with accepted practice. Experience indicates that failure due to compression perpendicular to the grain of the wood does not destroy the effectiveness of a wood set frequently enough to be a practical factor. Therefore, no table of these values is included.

Jan 1, 1951

By B. S. Butler

A. D. Mutch (Falconbridge Nickel Mines Ltd., Ona-ping, Ontario)—This contribution is prompted by the fact that the writer has recently published an article&apos;!&apos; which has in part the same general conclusions as B. S. Butler&apos;s, namely, the form of the standard mineral paragenesis in hypogene deposits and the parallel transition from early high temperature acid to late low temperature alkaline or neutral solutions. Since the writer also recognizes that he is not fully qualified to discuss the formation of ore deposits as a chemical problem, this discussion will be limited to summarizing other observations and will suggest how Butler&apos;s Table II might be made more effective. The form of Butler&apos;s table is not unlike that widely used by European geologists&apos;" in which the various minerals are related to the types of ore fluids—peg-matitic, pneumatolic and hydrothermal. Thus the decrease in temperature and change in pH of the ore-bearing fluids as recognized by Butler may also be paralleled by perhaps even greater changes in composition, density, and character. W. H. Newhouse&apos;s article:" on the sequence of hypo-gene ore mineral deposition is still one of the most complete analyses of the problem. In it he makes four major observations: 1) The order of O, S, As, Sb is the same as their increasing atomic weights and the same as their melting points. 2) The order of the metallic elements is the same as the Schuermann series. 3) The general mineralogical order is paralleled by decreasing heats of formation. 4) The order is generally in decreasing hardness, higher metal content, and higher specific gravity. The order of 0, S, As, and Bi is also the same as their relative abundance. Another point worth mentioning about this series is that As, Sb, Bi, when abundant, often substitute for sulfur in the early pyrite-like minerals, whereas later in the sequence these elements appear to act more like metals. This behavior may be a further indication of the acid character of the early fluids. C. J. Sullivan"&apos; has attempted to show that the sequence of the metallic elements is related to the order of their melting points and has discussed the interrelationship of the different types of bonding of sulfo-phile and oxiphile elements in minerals. Items 3 and 4 might best be summarized by saying that bonding of the minerals in the series appears to be from ionic to covalent to metallic, the early minerals being light in weight, hard, and near-transparent; the intermediate minerals of intermediate weight, semi-transparent, and semi-conducting; and the end minerals heavy, soft, and malleable, opaque and good conductors. A rapid fall in temperature has been assumed to be the cause of ore deposition in many deposits. Perhaps this in turn is the effect of a rapid release of energy in the form of pressure release and change of volume, the first minerals to form being those with the highest heats of formation which absorb the released energy the most rapidly. Butler&apos;s Table II could probably be streamlined and made more effective if the listed compounds were assembled as mineralogical groups as in Dana. Thus the sulfides, arsenides, antimonides, bismuthides, and sulfa salts could be arranged in AX,, AX, A2X2, etc. groups. Since these are continuous substitution series, in which the fields of stability and the heats of formation of the various individual minerals can be fairly regarded as similar, this should be accomplished with no loss of clarity. The occurrence of the individual minerals and the precise sequence of the mineral deposition in any one deposit is probably more dependent on the concentration and relative abundance of the component elements. The assembling of geological data in tabular form such as Butler&apos;s Table II will continue to be a very effective method of studying geological phenomena. The importance of this particular problem has been pointed out by C. F. Park,% who concludes that understanding of mechanisms of the standard paragenesis and interrelated problems of mineral zoning in space and time is one of the major keys to classification of ore deposits.

Jan 1, 1959

By W. F. Hosford, E. W. Kelley

Deformation studies have been conducted at room temperature on single crystals of magnesium and magnesium alloys with thorium and with lithium. Single crystals oriented to suppress shear on the easily activated basal slip systems were deformed by plane-strain compression. Compression along the C axis was accommodated by {1011} banding. Compression perpendicular to the unconstrained c axis activated {1012} twinning, and, after virtually complete twinning, deformation continued by {1011) banding in the twinned material. Compression perpendicular to the constrained c axis was accommodated by the simultaneous operation of (1012) twinning against the constraint and (1011 ) banding. Although this orientation was favorable for {1010)(1210) prism and {1011}(1~10) pyramidal slip, these modes were not observed in pure magnesium or in Mg-0.5 pct Th. However, {10i0)(1~10) prism slip was observed in crystals of Mg-4 pct Li during compression perpendicular to the constrained c axis. Fracture in all materials occurred parallel to (1124) or {l~il) depending on the orientation and composition of the specimen. THE mechanical behavior of the hcp metals is strongly anisotropic. Although several slip systems have been reported the slip is cpmmonly in the directions of closest packing, the (1210),&apos; and this does not produce strains parallel to the c axis. Hence the inherent anisotropy. The deformation mode most easily activated in magnesium at room temperature is (0001)(1210)- basal slip. Also {1010}(1~10) prism slip and {1011)(1210) pyramidal slip have been reported, primarily at elevated temperatures.2"4 However, at room temperature the shear stresses to activate the prism and pyramidal modes are roughly a hundredfold greater than that required for basal slip.&apos;j4 Thus prism and pyramidal slip may be expected only under special conditions of loading. Strains normal to the basal plane can be produced by twinning, however. Many twinning modes have been reported for magnesium,&apos; with (1012) twinning the most common and relatively easy to activate. Magnesium can deform by (1012) twinning when stressed along the c axis jn tension, but not in compression. In contrast, (1011) twinning is activated by compression along the c axis and not by tension. In addition to primary twinning, secondary twinning or slip can occur within the reoriented material of primary twins.&apos; In general at least five independent shear systems must be active to bring about an arbitrary shape change such as that in the individual grains of a deforming polycrystalline material.&apos; Because basal slip can_ provide only two independent shear systems and (1012) twinning can only accommodate an extension of the c axis, other deformation modes must be active in magnesium for an arbitrary shape change to occur. The purpose of this investigation has therefore been to study the various deformation modes in magnesium at room temperature, with special emphasis on those modes that are less easily activated. The effect of the alloying elements, thorium and lithium, has also been investigated. In polycrystalline aggregates, unambiguous identification of deformation modes is extremely difficult and the direct evaluation of the resolved shear stresses to activate them is not feasible. On the other hand, uni-axial tension and compression experiments on single crystals may not activate some of the- deformation modes because basal slip and/or {1012) twinning cannot be suppressed in most orientations. However, it should be possible to activate all possible deformation modes using oriented single crystals and plane-strain compression. Identification of active deformation systems and evaluation of the resolved shear stresses required to activate them should be facilitated. Wonsiewicz and Backofen have recently completed an investigation of the plasticity of pure magnesium crystals at various temperatures utilizing plane-strain compression and selected crystal orientations. This technique has also been used in the present work. The seven orientations selected for study are indicated in Table I. Plane-strain compression along the c axis (orientations A and B) should activate some deformation mode _other than basal, prism, or pyramidal slip, or (1012) twinning. In orientations C and D, prism or pyramidal slip would be expected to take place. When the compressive load is applied perpendicular to an unconstrained c axis (orientations E and F) the three slip modes should be suppressed but not (10i2) twinning. In orientation G, basal slip should occur.

Jan 1, 1969

By P. L. Rittenhouse, M. L. Picklesimer

A rapid and seniquantitative method of determining prefered orientation on large numbers of. Zircaloy-2 specimens was desired. knoop microhardness measurerrzetzls were irvestigated as a solldtion to this pro6lem. The variation of Knoop microhardness measurerlerzts on selected planes as a function of &apos;irzdenle axis relutilje lo cryslallograplzic or fabrication divectals were used to corzstrrcl a polar coordinate hardness contour map. With use of an empirical relationslip between the single-crystal hardnesses and those of the polycrystalline material conentional pole figures could be constructed which compare favorably also obtained. To determine preferred oriention qualitatively from hardness data requires a minimum of twelve measurements per plane on three, preferattention to grain size, specimen prepartion, and in-rreinetzt, and analjlsis is of the order of- 45 to 60 rrin. THE design of structures from Zr alloys requires consideration of preferred orientation and the resulting anisotropy of mechanical properties. Rapid and semi-quantitative methods of evaluating anisotropy and of determining preferred orientation are needed for quality control and for examining the large number of test specimens required in development programs. The variation of Knoop microhardness with indenter orientation has been studied in single crystals of several hcp metals including titanium.&apos; beryllium,&apos; magneium, and zinc.4 The maximum hardness observed on any crystallographic plane other than the basal plane invariably occurred when the long axis of the Knoop indenter was either parallel or perpendicular to the projection of the [ OOOI.] direction on the plane of examination. When the major slip mode was (0001)(i2i0j the maximum hardness occurred at the parallel positio! but when the operating slip system was {10i0) (i210) the hardness was a maximum perpendicular to the [0001] projection. A minimum hardness was always observed at a rotation of 90 deg from the maximum. It follows that the orientation of the projection of the [0001] can be determined on any non-basal plane by making hardness measurements at a number of indenter orientations. The determination of the orientation of the [0001] projection on two non-parallel, preferably orthogonal, surfaces of the specimen will allow location of the [0001] direction in the specimen. It seems possible that such measurements could be used to examine, at least qualitatively, the preferred orientation existing in polycrystalline hcp materials. An investigation of the microhardness anisotropy in Zircaloy-2 was undertaken to ascertain whether these measurements could be used for this task. EXPERIMENTAL PROCEDURE Single crystals of Zircaloy-2 were grown by an a-8-a annealing sequence using electron-beam heating.= The orientation of the crystals was determined by a conventional back-reflection Laue technique. The crystals were then mounted on a goniometer head and the desired crystallographic faces were milled and chemically polished. Polycrystalline Zircaloy-2 specimens were prepared from fabricated sheets or plates. Inverse pole figures for these materials were obtained using the X-ray diffraction techniaue described by Jetter, McHargue, and illiams.&apos; A Wolpert-Greis Micro-Reflex hardness-testing machine was used to make the Knoop microhardness measurements. The single-crystal and polycrystalline specimens were loaded to 0.5 and 2.0 kg, respectively. Determination of the scatter of hardness numbers as a function of applied load for several indenter orientations on several specimen surfaces showed that the loads selected were the lightest consistent with minimum scatter. Heavier loads did not appreciably decrease the scatter and produced hardness impressions too large to be conveniently measured with the equipment used. Seven crystallographic planes of the single crystals were examined, while six planes of examination were used in studying Zircaloy-2 polycrystals. The specimens were rotated 10 to 15 deg after each measurement and from four to eight impressions were made at each angle of rotation. RESULTS The two angles which were used to relate crystallographic directions and planes in the hcp cell to the planes of examination of the single crystals are shown in Fig. 1. 8 is the angle between the c axis. [0001]. and the normal, N, to the plane of examination. a is the angle between the long diagonal of the Knoop indenter and the projection of the c axis on the plane of examination. For exampIe, if P = 90 deg and a = 0 deg, the plane of examination is of the family

Jan 1, 1967

By K. I. Savage, S. C. Sun

This paper describes a process developed to recover coal, clays and pyrite from coal wastes. The process consists of fine grinding followed by coal and pyrite flotation which leaves the clays in the flotation pulp. A bituminous coal refuse containing 10% sulfur and 30% carbonaceous material was treated by this method to yield a coal product containing 4% sulfur, 10% ash; a pyrite product containing 45% sulfur (84% FeS2), 1% carbonaceous material; and a clay product containing 2% sulfur (3.5% FeS2). The coal yield was about 89%. The pyrite yield was about 77%. The process steps may be entirely flotation, or gravity separation (hydrocycloning) may be used to increase the pyrite : coal ratio in the flotation feed. Cost estimates for the process show a profit of $2.28 per ton of low pyrite grade refuse, but these do not include labor, maintenance, overhead and plant depreciation. The development of this process consisted of three parts: (1) exploratory tests, (2) op-timazation tests and (3) confirmatory tests. The objectionable qualities that sulfur imparts to coal have been commented upon from early times, and they have become more objectionable as the uses of coal have grown. In whatever form coal takes — raw, carbonized or gasified —the sulfur content remains objectionable, and therefore its compounds are removed as completely as possible. It has long been known that sulfur occurs in coal in different forms. In 1861, sulfur was said to exist in the state of sulfuric acid in combination with a base; in combination with iron as iron pyrites; as bisulfides of iron; and in combination with the organic elements of coal.&apos; Pyritic sulfur is a term loosely used to cover the sulfur associated with iron in its various forms. The mineralogically recognized forms are pyrite (FeS2), pyrrhotite (Fe 1-x S) and marcasite (FeS2). The particle sizes of pyrites vary widely. Isolated grains of marcasite smaller than 15 microns have been found disseminated through coal.2 Hair-like "veins" of pyrite filling cracks in vitrain have been found. At the other extreme, lumps or nodules of pyrites large enough for removal by hand picking have been encountered. Organic sulfur, unlike pyritic sulfur, does not exist as discrete particles, but is instead intimately associated with the coal structure and thus it is impossible to remove it or reduce its concentration by physical or mechanical means.2 In the preparation of coal for its various markets, the pyrite minerals (pyrites) are separated from the raw coal feed. This separation process concentrates the pyrites in the tailings or other waste products. It would be desirable to recover these pyrites for three reasons: (1) Pyrites are potential sources of sulfur and iron. In 1967, for the fifth consecutive year, Free World consumption of sulfur exceeded production.3 Propelled by the shortage, the domestic price of sulfur has risen from $24 to $38 per long ton (bright). (2) The refuse, when placed in piles, becomes ignited. The pyrites (FeS2) bum, giving off SO,. Thus, the pyrites are a cause of air pollution. (3) Also, the pyrites undergo chemical reaction when exposed to air. The refuse is leached by waters which result in stream pollution due to the water-soluble iron and acidic reaction products. Coal refuse also contains coal minerals and clay minerals. Therefore, any process for recovering the pyrites must successfully separate them from the coal and clay minerals. In the study discussed here, ten different bituminous coal refuse samples were successfully upgraded in pyrite content. These samples represented a wide variety of coal waste materials from Pennsylvania and other states. The variabilities of the sulfur and coal contents are shown in Table I. The extremes are Sample J, a high sulfur-low coal, and Sample B, a low sulfur-high coal. Definitions of some of the symbols or terms used in this report are given below: Mesh size—Tyler standard mesh screen sieves with an opening based on the square root of two. Fe —Indicates iron, as determined by a stannous reduction-dichromatic oxidation method. S—Indicates sulfur, as determined by the ASTM "Eschka" method for sulfur in coal.

Jan 1, 1969

By E. B. Hughes, F. G. Norris

Oxidation is characteristic of all processes for making steel from pig iron. This thought has been aptly expressed by H. W. Graham13 in the recent Howe Memorial Lecture, "The process of steel-making consists of using iron oxide to reduce the carbon content of the pig iron to the desired level." Direct oxidation refers to the reaction that results from introducing oxygen either alone or mixed with other gases directly into the steel bath. In working a heat, oxygen in some form is added to the steel to remove the undesirable constituents as oxides. There are two general methods of supplying this oxygen to the open hearth bath. The method in which the oxygen is added as a compound such as Con or iron ore is designated an indirect method because the steel bath must first decompose the compound to attain oxygen in a usable form. The other method in which oxygen is added to the bath in the elemental or gaseous form, more or less diluted by other gases such as nitrogen, is a direct method because no decomposition is necessary before the oxygen reacts with iron to form FeO which is dissolved in the bath in a usable form. Bubble formation (at least of a macroscopic size) presents no problem in case of direct oxidation because the reacting agent (oxygen) is in the form of bubbles when entering the metal. Regardless of whether oxygen is intro- duced into the bath directly or indirectly, several reactions proceed concurrently. In the presence of the bath of molten iron, FeO is formed either by oxidation of iron by oxygen or reduction of oxides by iron. This FeO dissolved in the molten iron is the source of oxygen for the oxidation of manganese, carbon, silicon, and phosphorus if these are present. The oxidation of carbon from steel is the controlling steelmaking reaction. The introduction of oxygen into the bath, its reaction in the elimination of impurities, and its control by the use of de-oxidizing additions have been subjects of importance since steel was first made by the bessemer process. Direct oxidation is, in a sense, an application of the bessemer principle to the open hearth process. Graham13 states: "The use of oxygen or air jets introduced into the metal bath is essentially an effort to approach in the open hearth the turbulence, rapid interface reaction, and high production rate per hour that exists in the bessemer process." The general subject, "Oxygen in Steel-making," was given new life by the studies of Herty and associates starting about1925. The current interest in elemental oxygen is intimately related to the large scale production of oxygen developed during the war period. Some of the first applications were made during the early summer of 1946 at the Steel Co. of Canada using oxygen with the fuel. Such a use is of considerable interest and importance in contributing to faster heats but is not the subject of the present discussion which deals entirely with the introduction of elemental oxygen directly into the open hearth bath.

Jan 1, 1949

By E. B. Hughes, F. G. Norris

Oxidation is characteristic of all processes for making steel from pig iron. This thought has been aptly expressed by H. W. Graham13 in the recent Howe Memorial Lecture, "The process of steel-making consists of using iron oxide to reduce the carbon content of the pig iron to the desired level." Direct oxidation refers to the reaction that results from introducing oxygen either alone or mixed with other gases directly into the steel bath. In working a heat, oxygen in some form is added to the steel to remove the undesirable constituents as oxides. There are two general methods of supplying this oxygen to the open hearth bath. The method in which the oxygen is added as a compound such as Con or iron ore is designated an indirect method because the steel bath must first decompose the compound to attain oxygen in a usable form. The other method in which oxygen is added to the bath in the elemental or gaseous form, more or less diluted by other gases such as nitrogen, is a direct method because no decomposition is necessary before the oxygen reacts with iron to form FeO which is dissolved in the bath in a usable form. Bubble formation (at least of a macroscopic size) presents no problem in case of direct oxidation because the reacting agent (oxygen) is in the form of bubbles when entering the metal. Regardless of whether oxygen is intro- duced into the bath directly or indirectly, several reactions proceed concurrently. In the presence of the bath of molten iron, FeO is formed either by oxidation of iron by oxygen or reduction of oxides by iron. This FeO dissolved in the molten iron is the source of oxygen for the oxidation of manganese, carbon, silicon, and phosphorus if these are present. The oxidation of carbon from steel is the controlling steelmaking reaction. The introduction of oxygen into the bath, its reaction in the elimination of impurities, and its control by the use of de-oxidizing additions have been subjects of importance since steel was first made by the bessemer process. Direct oxidation is, in a sense, an application of the bessemer principle to the open hearth process. Graham13 states: "The use of oxygen or air jets introduced into the metal bath is essentially an effort to approach in the open hearth the turbulence, rapid interface reaction, and high production rate per hour that exists in the bessemer process." The general subject, "Oxygen in Steel-making," was given new life by the studies of Herty and associates starting about1925. The current interest in elemental oxygen is intimately related to the large scale production of oxygen developed during the war period. Some of the first applications were made during the early summer of 1946 at the Steel Co. of Canada using oxygen with the fuel. Such a use is of considerable interest and importance in contributing to faster heats but is not the subject of the present discussion which deals entirely with the introduction of elemental oxygen directly into the open hearth bath.

Jan 1, 1949

By M. Kitada, U. Kawabe, F. Ishida, T. Doi

The relations between micros tructures and critical current density in transverse magnetic field were experimentally investigated due to each transformation of the 0 to 0&apos; + P" phases at 700&apos; C for superconductmainly examined using replication electron microscopy. The ß&apos; or a precipitates were found to pin down magnetic flux lines in these alloys. The effects of precipitation upon the critical current density were discussed in relation with the size, spacing, and characler of these precipitates. HIGH magnetic field superconductors, such as Nb-Zr, Nb-Ti, and Nb-Zr-Ti alloys, have been recently put to extensive practical use as winding materials for superconducting magnets.13 The critical current density of these hard superconductors under an applied magnetic field is an important characteristic for magnet materials and is very sensitive to metallurgical structure. It is generally known that the critical current density is increased by introducing dislocations and precipitates into a superconductor; that is, dislocations and precipitates are presumed to be barriers that hinder quantized flux lines from moving.4&apos;5 Theoretical6&apos;7 and experimental analyses of the motion of flux lines and the interaction between flux lines and various defects have already been reported by many authors. Metallographic analysis of high magnetic field superconductors such as Nb-Zr and Nb-Ti is difficult, so that no quantitative relationship between microstruc-ture and critical current density has been established yet. In this paper, the effect of precipitation on the critical current density in magnetic field was investigated for two superconducting alloys, Nb-40Zr-10Ti and Nb-5Zr-60Ti. In these alloys the resistive critical field H, at 4.2oK was about 100 kG and the critical current density Jc at 80 kG was of the order of 104 amp per sq cm.13-l5 The superconducting properties were examined in relation to the microstructural changes due to transformation of i) the ß to ß&apos; + ß" phases at 700°C for Nb-40Zr-10Ti alloy and ii) the ß to a + ß phases at 500°C for Nb-5Zr-6OTi alloy. The effect of size, spacing, and character of precipitates on flux line pinning was in particular examined. The microstructures were studied by means of residual resistivity, microhardness, and tensile strength measurements as well as by X-ray diffraction, optical, and replication electron microscopies. I) EXPERIMENTAL PROCEDURE Pure niobium, zirconium, and titanium, in the form of rods 0.8 cm in diam, served as raw materials. Results of chemical analyses of these rods are given in Table I. Ingots of the alloys, 0.4 cm in diam and 3 cm in length, were prepared by means of levitation melting, utilizing a copper mold in an argon-gas atmosphere. Samples from the ingot then were cold-worked by grooved mill to 0.2 cm in diam, heat-treated homogeneously (in the ß phase region) for 5 hr at 1100° in a vacuum of 1 x 106 Torr, and finally cold-drawn to 0.025 cm in diam. For heat treatments, samples were wrapped in niobium foil and sealed in an argon-gas atmosphere in fused quartz capsules. Water quenching was done after each heat treatment. Subsequently H-J, were performed at 4.2° by slowly transporting the current through the samples 4 cm long, under transverse magnetic field, until the least detectable resistive terminal voltage was observed. The resistive critical field H, was taken as the field at which 100 pv appeared at 4.2°K across a sample 3 cm in length, with a current of 5 ma. The critical temperature T, was measured by means of a conventional four-probe resistivity technique and taken as the temperature at which the sample resistance reached one-half of full restoration of the normal-state resistance with a current l ma flowing through a sample 2 cm in length. Precipitates were observed by means of optical microscopy and carbon replication electron microscopy. The etching solution consisted of 5 ml HF, 10 ml H2SO4 10 ml H2O2, and 50 ml H2O, and shadowed carbon replicas were examined in a itachi HU-11 electron microscope operated at 50 kv. X-ray diffraction photographs were taken by a 11.46-cm-diam Debye-Scher-rer camera using copper Ka radiation. The micro-hardness was measured under a load of 200 g using

Jan 1, 1969

By C. H. Li, R. J. Stokes, T. S. Liu

Poly crystalline silver chloride specimens having different micro structures were prepared by extruding monocrystals or precompressed powder at varying temperatures. Extrusion at high temperature (370°C) produced a Fully recrystallized equi-axed material which was brittle and fractured by simple cleavage below its transition temperature (60°C for notched specimens). Extrusion at low temperatures (down to -196°C) produced an extremely tough cold-worked material with grains elongated in the extrusion direction. This material fractured below its transition temperature (which varied from —20" to —200°C) by an intergranular mode. It is concluded that cold work increases the resistance to transgranular cleavage. Fracture is then de-flected to propagate intergranularly ouer surfaces making an angle with the tensile axis with a corresponding improvement in notch toughness. This deflection is greater for extruded powder than for extruded monocrystals because of the extremely elongated grain shape. PREVIOUS work1,&apos; on the fracture properties of fully recrystallized silver chloride under notch impact conditions has indicated that the fracture behavior is rather invariant. Thus polycrystalline materials originating from a number of sources ranging from relatively pure Harshaw single crystals to commercial-purity powder and prepared by hot extrusion at 370°C all fracture by simple cleavage with a ductile-brittle transition at 60°C, see Fig. 1. This behavior is also typical for fully annealed single crystals and appears to be fundamental to silver chloride for the particular loading conditions and notch configuration adopted. One way in which this characteristic fracture behavior can be modified is by the dispersion of alumina particles in the silver chloride matrix.&apos; Then, particularly when the alumina particles are in the shape of spheres, the duc tile-brittle transition is much less sharply defined and occurs over a range of temperature, the transition temperature is lowered considerably and the fracture mode changes from simple cleavage to a fibrous or shear mode. The reason for this change is believed to be partly due to the nucleation of cavities in the region of the dispersed alumina particles which influences the state of stress locally and the distribution of plastic constraint at the root of the notch. It is emphasized however that this is not the sole factor responsible for the increase in toughness. In extruded materials it is reasonable to expect that the resultant grain size, texture, and the residual cold work will be influenced by the presence of a dispersed phase. The present experiments were initially designed to determine the extent to which cold work influenced the fundamental ductile-brittle transition temperature and fracture mode of silver chloride. They were stimulated by the discovery that silver chloride could be extruded at temperatures as low as -25°C when commercial-purity powder was used and as low as -196°C when single crystals were used. This working temperature was far below that previously used (370°C) and it was found that such extruded material was exceedingly tough. The reasons for the enhanced toughness and its relation to the previous work on silver chloride-alumina compacts will be discussed. EXPERIMENTAL PROCEDURE Materials Used. Two forms of silver chloride were used in this study: i) silver chloride powder

Jan 1, 1964

By Anton Eilers, R. W. Raymond, O. H. Hann

THIS paper will treat of such works only as beneficiate ores directly in the mining districts. And when it is said that more than twenty

Featured at the 1977 SME-AIME Fall Meeting in St. Louis is a Lead-Zinc Update, organized to complement the 1970 AIME World Symposium on Mining and Metallurgy of Lead and Zinc, also held in St. Louis. The 21 papers comprising the Update are to be presented during four technical sessions at the Fall Meeting; in addition, the papers have been collected in a bound book available at meeting time.

Jan 9, 1977