Search Documents

By W. S. Hyler, L. W. Berger, R. I. Jaffee

Hydrogen additions of 390 ppm to A-55 titanium and 368 ppm to Ti-8 pet Mn have no deleterious Hydrogenadditionseffect on the unnotched and notched rotating-beam fatigue properties of these materials. 'These amounts of hydrogen, however, are sufficient to cause severe notch-impact thesematerials.embrittlement in A-55 titanium and pronounced loss of tensile ductility in Ti-8 pet Mn. The lack of embrittling effect in fatigue in the latter alloy is consistent with the postulated strain-aging mechanism of hydrogen embrittlement in a-ß alloys. There is a significant strain-agingincrease in the unnotched endurance limit of A-55 titanium with the addition of hydrogen. This increase may be explained as the result of internal heating effects which would dissolve the hydride and cause solid-solution strengthening. TITANIUM and its alloys may be seriously embrittled by relatively small amounts of hydrogen. The form which this embrittlement takes has been shown to vary with alloy type. The a alloys, for example, suffer most strongly from loss of notch-bend impact toughness' when sufficient hydrogen is added, and this effect has generally been associated with the presence of hydride phase in the micro-structure. In a-ß alloys, on the other hand, hydrogen is most detrimental to tensile ductility in slow-speed tests,2-1 and the embrittlement may be detected in a most convincing manner by means of rupture tests at room temperature. This particular kind of embrittlement has not been associated with a change in microstructure, but has been classified rather generally as associated with a strain-aging type of mechanism.' In the present paper, the effect of an embrittling amount of hydrogen on the rotating-beam fatigue properties of both an a and an a-ß titanium alloy is covered. For this study, annealed commercially pure (A-55) titanium was chosen as an a alloy, and equilibrated and stabilized Ti-8 pet Mn as representative of a typical a-ß alloy. Nominal hydrogen levels of 20 and 400 ppm were evaluated, the latter amount having been shown previously to be severely detrimental to the impact toughness of commercially pure titanium and to cause pronounced strain-aging embrittlement in the Ti-8 pet Mn alloy. The only report of the effect of hydrogen on the fatigue properties of titanium is given by Anderson et al.,° in which a push-pull type of fatigue test was conducted on as-received commercial-purity titanium sheet. Much scatter was found in the results, but generally the presence of hydrides slightly decreased the fatigue strength of unnotched specimens in the longitudinal direction. The results of notched tests were masked too greatly by scatter to be significant. Experimental Procedure Preparation of Materials—Analyses of the A-55 titanium and the Ti-8 pet Mn alloy used in this investigation are given in Table I, which indicates the 8 pet Mn alloy to be more nearly a 6 pet Mn alloy. This alloy will be referred to as Ti-8 pet Mn, however, since this is the commercially designated composition. Both alloys were received in the form of5/8-in. diam rod and, after suitable surface preparation, 5-in. lengths were vacuum annealed at 820°C. Half of the rods for each material were then hydrogenated at 820°C to a nominal hydrogen content of 400 ppm. The hydrogenated and vacuum-annealed A-55 rods were hot swaged at 700°C from 5/8-in. diam to 1/4-in. diam, and then annealed 1 hr at 800°C and air cooled prior to preparation into test specimens. Fabrication of the Ti-8 pet Mn alloy was by hot swaging to 3/8-in. diam at 760" and then 1/4-in. diam at 704°C. This material was then annealed 1 hr at 704", followed by furnace cooling to 593"C, and finally air cooling to room temperature. Evaluation—In order to examine more completely the effects of hydrogen on the particular materials studied, slow-speed tensile and notch-bend impact properties were determined in addition to fatigue data. Tensile specimens were of the standard ASTM type with a reduced section of 1/8-in. diam and a gage length of 1/2 in. A subsize cylindrical Izod specimen was used for impact tests. These specimens had a 45" notch with a 0.005-in. radius and a 0.150-in. root diam, and the stress concentration factor of this notch in bending was Kr = 3. Both the ten-

Jan 1, 1959

By R. R. Estill

THE rank of the Ruhr coal ranges from a high volatile bituminous coal to an anthracite, depending to some extent on the original depth of the seam. The average Ruhr coal corresponds to a soft bituminous American coal of a coking quality. The average thicknesses of individual coal seams being mined are also comparable (59 in. against 65 in. in the United States). However, consideration of seam conditions and mining conditions other than those just mentioned emphasizes differences rather than similarities with United States soft coal. In general, the Ruhr seams now being mined are much more folded and inclined than American seams. Dips of 20' and 30" are common in seams now being worked, and 30 pct of the coal reserves in the district are in seams dipping more than 35". Only on the tops and bottoms of folds do we find rather flat coal seams. In addition to the folding there is extensive displacement by cross faulting plus a certain amount of strike faulting of an overthrust nature, which results locally in doubling or omission of seams. Because of the long history of mining in the Ruhr, nearly all coal lying near the surface has long since been mined out, and we find that the average depth of mining is at present about 2300 ft below the surface. Deep mining, folding, and faulting result in seam conditions requiring a great deal more roof support than one finds in American soft coal mines. In fact only in the anthracite district and the Rocky Mountain and Pacific coal fields do we find somewhat similar conditions. It is easy to say, therefore, that the problem of mechanization of coal cutting and loading in the German mines is quite different from that which we have so effectively met in America with our mobile cutters and loaders, duck bill loaders, and a room and pillar system of mining our drift and slope mines. Partly because of more limited coal reserves, the traditional German mining system is largely the longwall method, which gives an almost complete coal recovery. Backfilling must be extensively practiced to protect the longwall faces, the over and underlying seams and workings, and especially the surface industrialized areas and barge canals. The German engineers have accordingly concentrated their efforts on the design of cutters, loaders, and conveyors suitable to longwall methods rather than room and pillar methods. Undercutters with cutter bars like American models have been in use in the Ruhr since well before World War 11. In 1941 they accounted for 8.5 pct of the production. This percentage, of course, includes coal which was undercut but nevertheless had to be broken down with air hammers or with explosives. The most common of these cutters is the Eickhoff Standard cutter (see fig. 1). This machine does about 95 pct of the undercutting in the Ruhr today, and is available with either compressed air or electrical power and in at least four different sizes. A variation of the cutter is this one with two cutter bars (fig. 2). At the end of 1947 about 200 of these machines and similar cutters were accounting for 13.2 pct of the total production, a production which was, however, only 60 pct of the 1941 production rate, so that the actual cutter tonnage was only up to a small amount over 1941. In 1941 about 3 pct of the production was accounted for by shearing machines making their cut perpendicular to the longwall face. They were similar to those used in the States. These machines are today considered obsolete and now account for only 0.7 pct of the total production. They are located at only a few mines and at present do not seem to have much of a future in the Ruhr. For the future, the Ruhr miner is looking forward to rather extensive mechanization of face work, with two major types of equipment being developed almost simultaneously. On one hand there is the development of cutter loaders for use in relatively hard coal. They represent the further extension of ideas developed after relatively long experience with the Eickhoff cutter. On the other hand there has been since 1942 an intense interest in the Ruhr in the development of face-stripping methods, particularly by the Kohlenhobel (coal plow) and its modification. At the end of 1947 these cutter loaders, Kohlen-hobels and scrapers together were actually accounting for only about 1.4 pct of total production while air hammers still broke 77.1 pct and as much as 1.2 pct was actually broken by hand picks. However,

Jan 1, 1951

By J. Sibakin, R. D. Hindson

In order to devise a practicable soaking pit schedule for use at The Steel Co. of Canada Ltd.'s Hamilton Works, soaking pit heating temperatures, sooking times, pit capacity, and safe maximum mill drafts were correlated with fluctuations in the current or load of the bloom mill driving motor. Other variables such as total delays in the pit, rolling schedules, mill delays, and track times were also investigated. IN order to show an easily applied and accurate means of establishing soaking pit heating temperatures, soaking times, pit capacity, and safe maximum mill drafts, these various factors are correlated herein with fluctuations in the current or load of the bloom mill driving motor. Rolling practices have a considerable influence on the production capacity of a blooming mill. The maximum values of the torque, in particular, are of importance, since even instantaneous current peaks lead to the tripping of the motor by the overload relay and result in loss of mill time. The establishment of safe maximum drafts and accelerations for ingots of different sizes and of a soaking pit practice which would ensure a consistent and satisfactory plasticity of the metal is of considerable importance for increasing the efficiency of both the blooming mill and the soaking pits. The Bloom Mill Dept. of the Hamilton Works, The Steel Co. of Canada Ltd., is equipped with one 44 in. mill driven by a 7000 hp motor with the setting of the overload relay at 22.0 ka. The speed of rotation of the motor is regulated after the Ward-Leonard system. There are three basic speeds of 9.5, 28, and 47 rpm and a further possibility of increasing the speed by weakening the field. This last possibility is hardly ever used during practical operations. The rolling program of the blooming mill is varied, both in the size of the ingots to be handled and in the steel grades. The total tonnage handled by the mill is about 2,000,000 ingot tons per year. At the time of the investigation, the Bloom Mill Dept. was equipped with 22 soaking pits (6 regenerative, 14 bottom-fired, and 2 one-way top-fired pits) with a total bottom area of 2770 sq ft. The pits are fired with a blast furnace-coke oven gas mixture having a calorific value of 155 Btu per cu ft. The foregoing figures show that the production program was such as to impose the necessity of a most efficient usage of the available equipment. For this purpose, the operations of the 44 in. mill and of the soaking pits were investigated, and the results of the investigation were used as a basis for a revised soaking pit schedule and drafting practice. The plasticity of an ingot of a certain chemical composition when being rolled is determined mainly by the following factors: I—the ingot size, both thickness and width; 2—the length of the gas soak; and 3—the surface temperature. The first two factors determine the uniformity of the temperature distribution over the cross-section of an ingot. The third factor introduces the level of the heating of an ingot. The torque produced by an ingot being rolled is determined by the area of the metal displaced, its plasticity, and acceleration values. On the other hand, with shunt motors the torque is determined by the current. This can be assumed to be correct with only a small degree of error for compound motors with a relatively small effect of the series windings as long as the velocity is not regulated by weakening the field. Since the spread is relatively unimportant when compared to the width of an ingot and since it is also reduced several times during rolling by edging passes, the draft alone and not the area of the metal displaced may be taken into consideration with ingots of a similar size. It is therefore possible to determine the main features of the heating and drafting of an ingot by measuring the current and acceleration of the mill motor. After the acceleration has been taken into account, the amount of current will be an indication of how the motor responds to a heating and/or drafting practice and these practices can be adjusted in order to get the desired result. As peak currents are more likely when heavier ingots are rolled, the rolling of plate and slab ingots was investigated. Conditions prevailing when smaller ingots are rolled can be deduced from the results obtained on heavier ingots. All measurements were made when plain carbon grades under 0.15 pct C were rolled. The motor current, the voltage across the armature, and the rpm were recorded simultaneously on synchronized charts, Fig. 1, which moved with the speed of 6 in. per min. Each draft was recorded by a special observer. The rpm curve made it possible to establish the acceleration at any given moment. For purposes of correlation, the maximum current during a pass and the corresponding acceleration were used. The charts made it possible to establish the position of the roller's lever at any given moment as well as the total time of a pass. The slab ingots were divided into three groups (28x35, 28x45, and 27Mx53 in. ingots) and each group was investigated separately. Since they account for most of the current peaks, only flat passes were used for purposes of correlation, a total of 1373 having been investigated.

Jan 1, 1956

By K. H. Kilgren

At high formation pressures the distillate produced from a gas-condensate reservoir may be black in color. In this event the dense gas phase existing above the dew point is correspondingly dark. Volumetric phase data and an analysis of a reservoir fluid exhibiting these characteristics, together with a description of the visual equilibrium cell in which these observations were made, are presented in this paper. INTRODUCTION Previously the author, like many others in the oil and gas industry perhaps, tacitly assumed that the expressions black or dark oil system, crude oil system and bubble-point system were synonymous. Crude oil reservoir fluids are bubble-point systems and yield a black or dark stock-tank oil of relatively low API gravity. Conversely, a clear or amber colored trap distillate of high API gravity is assumed indicative of a dew point system or a gas-condensate reservoir fluid. This broad classification appears satisfactory for shallow reservoirs, but as the following study demonstrates, may be misleading when applied to deep reservoirs. Theoretically, there is no reason to exclude the possibility of producing a dark, low-gravity distillate from a gas-condensate reservoir. At sufficiently high values of pressure and temperature, heavy, dark-colored hydrocarbons may exist in the vapor state of a multi-component system. If enough dark-colored components are present in the reservoir vapor phase, the resulting condensate will be dark. The reservoir fluid investigated in the present study supports this contention. Stock-tank production was black in color and measured 29" APT gravity. From outward appearances, the liquid closely resembled a medium gravity crude oil. Experimental measurements proved the reservoir fluid was in reality a gas-condensate system. Volumetric phase data for this high-pressure system and a description of the visual cell in which the study was conducted successfully are presented in this paper. THEORY Phase behavior of a reservoir fluid can be predicted accurately with reference to a pressure-temperature phase diagram. If the reservoir temperature is lower than the critical temperature of the hydrocarbon fluid in place, bubble-point behavior will be observed. If the reservoir temperature lies between the critical and cricondentherm temperature, dew point behavior and retrograde condensation will occur. For reservoir temperatures above the cri- condentherm, only a single gas phase can exist in the reservoir regardless of pressure. Providing the composition of the reservoir fluid were known, it would be possible to predict the critical temperature and estimate the phase behavior from equilibrium relationships. However, the usual practice is to obtain a sample of reservoir fluid, subject it to varying pressures at the reservoir temperature and observe the phase behavior experimentally. The latter method was used to obtain the data reported here. WELL AND TRAPPING INFORMATION A summary of pertinent data for the well from which the reservoir fluid was sampled is presented in Table 1. This well is located offshore Louisiana. Except for the pressure which substantially exceeds hydrostatic pressure, the information does not appear unusual. Prior to the sampling program, the well was produced for 22 hours at a stock tank oil rate of 139 B/D. Average trapping conditions and gauging data for the six-hour test period that followed are summarized in Table 2. Samples of the first-stage trap gas and liquid were obtained during the latter portion of the test period. Ambient temperature remained 5 to 10F below trap temperature and presented no problem for sampling. Surface wind and moderate foaming of stock-tank oil presented some difficulty in obtaining accurate stock-tank gauges. SAMPLE ANALYSIS Compositions of the gas and liquid samples are shown in Table 3. The trap gas was analyzed by isothermal chromatography which revealed only a trace of heptane in the stream. The trap liquid was initially analyzed by low-temperature fractional distillation, yielding a bottom product of heptane and heavier components. Specific gravity of this fraction was measured and the mol weight was determined by freezing point depression. The hexane and lighter overhead gas collected during distillation was

Jan 1, 1967

By S. G. Cupschalk, J. J. Wert, R. A. Buchanan

The uniaxial deformation of thermally ordered and disordered polycrystalline Cu3Pt was studied by means of the X-ray line - broadening analysis according to Warren and Averbach and the extension of this analysis to ordered fcc materials by Mikkola and Cohen. Because of the heat treatment history, extinction had a pronounced effect on the X-ray spectra of ordered and disordered C%Pt at small plastic strains. After an appropriate correction for extinction, the long-range order in thermally ordered ChPt was found to decrease at a slow constant rate with plastic strain. Furthermore, the antiphase domain probability increased at a constant rate to 17.5 pct strain. The effective particle size behavior indicated that the stacking fault energy is lower in ordered than in disordered Cu3Pt. Analysis of the stress-strain curves shouled that ordered Cuzt has a slightly lower yield Point but a much higher work-hardening rate than disordered Cu3Pt. THE presence of long-range order in a solid-solution alloy has a marked effect on its mechanical properties. While this effect has been known qualitatively for many years, it was not until recently that detailed investigations have been performed to determine the exact role long-range order plays in this strengthening mechanism. The development of an advanced, quantitative. X-ray diffraction analysis by Warren and Averbachl and the extension of this analysis to the L1, type super lattice by Mikkola and cohen2 have greatly accelerated research in this field. The research reported in this paper consisted of two primary phases. The first phase was to determine the effect of long-range order on the tensile properties of polycrystalline Cu3Pt. This objective was accomplished by comparing the stress-strain behavior of thermally ordered CusPt to that of thermally disordered CusPt. The second phase of the research was to determine the difference between the atomic arrangements in thermally ordered and thermally disordered Cu3Pt as a function of uniaxial deformation and thereby gain a deeper insight into the mechanism by which long-range order affects the tensile properties. This second objective was accomplished by applying the Warren-Averbach method of peak profile analysis to the X-ray diffraction patterns obtained from ordered and disordered Cu3Pt after given amounts of uniaxial deformation. EXPERIMENTAL PROCEDURE The Cu3Pt was prepared by vacuum melting and casting. After a homogenization anneal, the ingot was cold-rolled to sheet form. Two tensile specimens with gage sections of 2.50 by 0.500 by 0.115 in. were carefully machined from the sheet. The specimens were polished with a final step of 600-grit paper to insure smooth diffracting surfaces. Finally, one specimen was heat-treated to yield an average grain diameter of 0.016 mm and an initial degree of long-range order, S, of 0.825. The other specimen was water-quenched from above the critical temperature, 645"C, to yield an average grain diameter of 0.017 mm and zero long-range order. The heat treatment history of each specimen is shown in Table I. The tensile tests were performed utilizing a Research Incorporated Model 900.95 Materials Testing System. This unit employs a closed-loop feedback system which maintains a constant strain rate through an extensometer clipped to the gage section of the tensile specimen. A strain rate of 1.32 i0.02 x 10"4 sec-' was employed in testing both specimens. In the X-ray diffraction analysis, a General Electric XRD-5 diffractometer equipped with a pulse-height analyzer set for 90 pct efficiency was employed. The goniometer speed selected was 0.2 deg, 20, per min. Filtered Cu radiation was used for all peaks and all peaks were chart-recorded. Because of nonuni-form grain size. it was necessary to spin the specimens during X-ray analysis in order to obtain reproducible integrated intensities. The spinning rate was 2000 i100 rpm. The application of the Warren-Averbach method of peak broadening analysis to a diffraction pattern is very time consuming if done manually. In this research, the calculations involved were performed with the aid of a computer program by wagner.3 As reported by Wagner, the program is written in Fortran TV computer language. It was modified to Fortran I1 so as to be handled by the IBM 7072 computer at Van-derbilt University. In the X-ray diffraction analysis of uniaxially deformed Cu3Pt, the 100, 200. 400. 111, and 222 reflections were recorded from the initially ordered sample after 'plastic strains of 3.0, 6.0, 9.0, 12.0,

Jan 1, 1970

By Larry Kaufman, Martin Schatz

The effect of pressure on the extension of the ? loop in the FeSi system has been determined by means of metallogvaphic studies and hardness measurements performed on a series of high-purity Fe-Si alloys containing 7.5, 11.0, and 13.9 at. pct Si, respectively. These mensurements, performed at 42 kbar and temperatures up to 1200oC, indicate that the ? loop is expanded to about 10 at. pct Si at 42 kbar as opposed to a maximum extension of 4 at. pct Si at 1 atm. Comparison of the experimental results with thermodynamic predictions of the pressure shifts yields satisfnctory results. DURING the past few years, several studies have been performed in our laboratory1-' in order to determine the effect of high pressure on phase equilibrium in pure iron and iron-base alloys. The purpose of these studies has been to elucidate the effects of high pressure experimentally and to compare the observed results with predicted pressure effects derived on the basis of known thermody-namic and volumetric data at 1 atm. These studies have included work on pure iron2,5,7 as well as Fe-Ni,1,5 Fe-cr,l,5 and Fe-c4-6 alloys. In addition, Tanner and Kulin3 have reported results of pressure studies on two Fe-Si alloys containing 2.0 and 6.25 at. pct Si. At the time of this latter study, no detailed information was available concerning the difference in volume between the a (bcc) and ? (fcc) phases in the Fe-Si system as a function of silicon content. In order to compare their observations with calculated pressure shifts, Tanner and Kulin were forced to assume that silicon had no effect on the difference in volume between a and ? iron. The resulting discrepancy between their calculation of the a/? phase boundary at 42 kbar and the observed results led them to the conclusion that silicon additions probably decrease the difference in volume between a and ? iron. Recently: Cockett and Davis8,9 have reported de- tailed studies of the lattice parameters of a series of Fe-Si alloys at temperatures ranging from 20" to 1150°C. These measurements, performed on alloys in the bcc and fcc range, show that silicon does indeed decrease the difference in volume between a and ? iron. By correcting the calculations of Tanner and Kulin in line with the observed effect of silicon they were able to show improved agreement between computed and observed pressure shifts.' The present measurements were undertaken to provide additional corroboration of this effect, by extending the range of composition, in addition to exploring a situation where large extensions of a ? loop could result in impingement of the ? field with an ordered bcc phase (based on Feo.75Sio.25). I) EXPERIMENTAL PROCEDURES AND RESULTS The alloys investigated were obtained from Dr. F. Kayser of M.I.T. They were prepared at the Ford Scientific Laboratory by vacuum melting electrolytic iron and high-purity silicon. The melts were poured under an argon atmosphere into hot-topped steel molds. Subsequently the ingots were hot-worked down to 1/2-in.-diam rods. Three alloys containing 7.5, 11.0, and 13.9 pct Si were studied. Carbon, regarded as the principal impurity, analyzed at, or below, 0.001 wt pct for all of the alloys. Prior to pressure-temperature treatment, the rod was annealed for 24 hr in vacuum at 1000°C, water-quenched, and subsequently machined into 0.100-in.-diam by 0.100-in.-long specimens. Subsequent to machining, the specimens were again annealed and then examined metallographically. They were found to exhibit a clear coarse-grained ferrite similar to Figs. 10 and 110 of Ref. 1 and Fig. 2 of Ref. 3. Subsequently, specimens of each alloy were equilibrated at 42 kbar at various temperatures in supported piston apparatus.1,3,4,6 Three specimens, one of each alloy, were wrapped in platinum and exposed simultaneously. The pressure-temperature cycle consisted of increasing the pressure from ambient to 42 kbar at 25oC, heating rapidly to the desired temperature, holding for 15 min, and quenching to 100°C, followed by slower cooling to 25°C and pressure release. The temperature was measured with a Pt/Pt-13 pct Rh thermocouple which was not corrected for pressure effects. Subsequently, specimens were examined metallographically and by

Jan 1, 1964

By D. W. Levinson, L. F. Mondolfo, N. A. Gjostein

MANY investigations are reported in the literature on the age hardening of Al-Mg-Zn alloys but most of them are concerned mainly with mechanical property changes. The present investigation was started to determine the structural changes in an AlMgZn alloy. The alloy composition was chosen in the existing phase diagram" so as to lie on the quasi-binary section Al-(AlZn)Mg Actually, it was found that the diagram as published was inexact at the lower temperatures and that the phase in equilibrium with aluminum at the lower temperatures is not the ternary compound. Technique The alloy used for the investigation was prepared from high purity materials and the resulting composition as determined by chemical and spectro-graphic analysis was: Zn, 6.17 pct; Mg, 2.13 pct; CU, 0.03 pct; Si, 0.009 pct; Fe, 0.005 pct; and the remainder, aluminum. An ingot -in. thick was cast, homogenized, hot and cold-rolled to strip 0.064-in. thick for dilato-metric and powder work, and to foil 0.005-in. thick for single crystal work. Solution treatment temperature for all specimens was 475°±5°C for periods of at least 1 hr, either in air furnaces or lead baths. Aging was done in oil or Pb-Bi baths controlled to within ±3°C. The aging was investigated at the following temperatures: room (30°), 130°, ZOO0, 260°, and 300°C. For the dilatometric study, the length changes were measured continuously, at temperature, using strips of alloy 10 in. long, shaped as channels to eliminate undesirable deflection due to bending. To compensate for thermal expansion and contraction due to the variations in the temperature of the aging baths, the dilatometers were built of the same alloy as the one being tested, with the same shape and size, but with material fully annealed. Gages on which 0.0005 in. could be read and 0.0001 in. estimated were used to measure the dilation. Length changes were also measured at room temperature. Strips approximately 10 in. long were solution-treated, quenched, and measured in a supermicrome-ter in which 0.0001 in. could be read and 0.00001 in. estimated. The specimens were immediately aged for a given time, remeasured, and then the cycle was repeated, including the solution treatment. The error of measurement with this technique was somewhat larger, but the results confirmed those obtained by continuous measurements. The sheet used for the dilatometric work was checked to determine grain orientation. Both X-rays and etching methods revealed a rather coarse grain size but only a negligible amount of preferred orientation. Thus, volume changes calculated from length changes are not invalidated by preferential orientation effects. Pieces of the sheet used for the dilatometric work were also used for the metal -lographic work. Filings for the powder X-ray study were produced from a homogenized piece of sheet. These filings were magnetically purged of iron, screened to 200 mesh, sealed in a Pyrex tube containing an argon atmosphere, and solution-treated. When quenching, the glass tube was broken, so that the powder dropped directly into cold water. After drying with alcohol, the powder was sealed into capillary tubes containing an argon atmosphere and then aged for the required times. In spite of all these precautions the three strongest lines of a( Al2o) appeared in all patterns, and were used as internal standards. By the use of these standards, accurate corrections for film shrinkage were obtained. For the back reflection patterns, annealed nickel powder was mixed with the specimen to act as internal standard. A preliminary investigation was made in small (57.3 mm diam) powder cameras. From these patterns the changes which took place in the solid-

Jan 1, 1957

By B. J. Bayles, J. A. Ford, M. J. Salkind

Unidirecltonally sulidijied AL-A13Ni was found to exliibit excellent microstructural stability to 508°C. Above this temperature the transverse micvostructure coarsened in a manner analogous to "Ostwald Ripening", but the A13Ni whiskers did not spheroidize or foreshorlen. The coarsened whiskers reinforced the matrix as effectirely as the finer whiskevs and no reduction in room-temperature tensile strength mas noled after exposure for 90 hr at 96 pel 0-1 the absollite melling temperature of the eulectic. The slability was auribucted to the presence of low-index (and presurrlably lor-energy) cvystallographic interjaces between phases. The driving force for microstructural coursening was presumed to be the reduction of interfacial energy between the phases. Finer micvoslructures were found to coarsen more rapidly than those which weve imitally coarser. FIBER-reinforced metals have been shown to exhibit good short-time tensile properties at elevated temperatures.1-4 However, many elevated-temperature applications require long-time property retention which dictates the necessity for microstructural stability. Two types of instability are common to fiber composities. The first, chemical instability, is due to chemical reaction between the matrix and the relnforcing phase. Petrasek and weeton5 have shown that chemical reaction between tungsten wire and several copper alloy matrices resulted in degradation of the reinforcing phase and reduction in strength of the composite materials. Kreider and Leverant4 have noted similar behavior for boron-reinforced aluminum above 400°C. The second type of instability arises in systems in which the phases are essentially chemically stable with respect to each other and is characterized by spheroidization and/or agglomeration of the reinforcing phase. parratt6 has reported this type of degradation to occur relatively rapidly at moderate temperatures for nickel and cobalt alloys containing whiskers of silicon nitride, aluminum oxide, and silicon carbide and has identified it as "physicochemical" instability. Although both types of instability are the result of the differences in the chemical potential between the fibrous phase and the matrix, they may be differentiated by the fact that the second type, "physicochemi-call' instability, results in little or no net change in the composition or amount of each phase present. It does, however, result in a morphological change which profoundly affects the strengthening mechanism. Chemical interaction. on the other hand, results in a change in the composition and amount of one or more of the phases present, or the appearance of a new phase. In the latter case, the appearance of the mi-crostructure, that of a fibrous phase aligned in a matrix, may remain essentially unchanged, but the chemical degradation of the fiber results in markedly reduced composite strength. This investigation was initiated in an attempt to evaluate the microstructural and related mechanical property changes of a whisker-reinforced eutectic composite after elevated-temperature exposure. The composite system chosen for this study was the uni-directionally solidified A1-A13Ni eutectic which Lemkey. Hertzberg, and Ford7,8 demonstrated to behave as a whisker-reinforced composite. The microstructure of the unidirectionally solidified material consists of aligned needles of A13Ni in a matrix of aluminum. EXPERIMENTAL PROCEDURE Eutectic ingots having a nominal composition of 6.2 wt pct Ni were produced by melting 99.99+ pct A1 and 99.99 pct Ni in recrystallized alumina crucibles in an argon atmosphere. The analyses of the starting materials are listed in Table I. These master heats were cut up? melted by induction heating, and unidirectionally solidified vertically in 1/2 -in.-ID. 6-in.-long graphite crucibles, in a dynamic argon atmosphere. Therma1 gradients in the liquid were determined by measuring the temperature in the melt as a function of apparatus travel distance, as discussed by Kraft and Albright.9 The rate of solidification was assumed to be equal to the uniform rate at which the crucible assembly was withdrawn from the furnace. Ingots representative of nominal growth rates of 2, 5, and 11 cm per hr were produced and the solidification parameters are summarized in Table 11. Ingots used for met allographic analysis were pre-

Jan 1, 1968

By H. A. Jr. Koch, C. A. Hutchinson

Miscible phase displacement of oil from reservoirs has been emphasized in the past few years. The reason for this emphasis lies in the high oil recovery attainable by this process. Removal of capillary effects in the reservoir leads to recoveries approaching 100 per cent in the area contacted by the miscible phase. The miscible slug process is one means of obtaining a miscible displacement. Here a band or slug of I,PG is injected into the reservoir prior to gas injection. The idea is to maintain the band of LPG "wedged" between the gas and oil phases and thus achieve a miscible phase displacement. A second method lor achieving miscibility is through the injection of a gas which is not miscible with the reservoir fluid but which develops a zone of miscibility in [he reservoir through mass trans-ier with the reservoir oil.' This mass transfer results in either an enrichment of the lean injected gas by intermediates from the oil or an enrichment of the oil by intermediates from a rich injection gas or one that has been enriched on the surface by LPG addition. We are interested here in discussing the process in which miscibility is developed at the displacement front by the evaporation of interrnediatcs from the oil phase into the gas phase. This process "builds up" its own slug of miscible material at the displacement front and therefore does not require the injection of LPG to obtain miscibil-ily. Each process has its own area of applicability. Generally, the high pressure gas process is applicable only with reservoir fluids which con-!ain a high concentration of inter- mediates. If the high pressure gas process is technically feasible at pressures less than 4,500 psi, it is probably more desirable economically than the slug process. The slug process has broad applicability in the shallower reservoirs and with reservoir fluids which contain a relatively low concentration of LPG and natural gasoline constituents. This paper deals with some new concepts of the high pressure gas injection process where it is proposed that flue gas can be substituted for hydrocarbon gas without sacrificing our goal of miscibility. MECHANISM Introduction Considerable effort has been devoted to study of the mechanics ot the high pressure gas injection proc-one generalization result-ing from some of these studies was that the composition of the injected gas is relatively unimportant in establishing the miscibility pressure* for a given reservoir fluid. This generalization is correct for the composition range of gases typically encountered in the field. Two such gases are a gasoline plant tail gas containing 85 per cent methane and 15 per cent ethane, and a field separator gas containing 70 per cent methane and 30 per cent heavier components. The most important factor which sets the miscibility pressure in the operation is the reservoir fluid composition, particularly the concentration of LPG-natural gasoline constituents. The injected gas is the agent by which the LPG-natural gasoline constituents are concentrated at the displacing front to create a miscible displacement. Based on these results, it appeared feasible that some inexpensive gas, such as flue gas, might be substituted for hydrocarbon gas for use in the high pressure gas process. A re-examination of the phase relations of the high pressure gas injection process should clarify the principle behind using flue gas (essentially nitrogen) as an injection gas. Three Component Diagram The phase relations of the high pressure gas injection process have been illustrated by the use of the three component diagrams.'," In Fig. 1 we have arbitrarily represented the multi-component reservoir system by three components; methane, ethane through hexane, and heptanes plus. The solid curve ABC is the phase boundary curve. It represents the locus of compositions which have fixed saturation pressure at a fixed temperature; the lower branch AB shows bubble point compositions, the upper branch BC, the dew point compositions. Point B is the coniposition of the critical mixture at this temperature and pressure. The dashed lines (tie lines) connect vapor and liquid compositions which are in equilibrium. Let us consider Reservoir Fluid D which we wish to displace in 21 miscible manner by gas injection. Let us further restrict the discussion to the case where miscibility between an injection gas and the reservoir fluid at the displacement front is developed by gas enrichment in the reservoir. For this case, any gas whose composition lies between Points C and E on the right side of the three component diagram can be used to give a miscible displacement of Reservoir Fluid D. This is true because the more mobile injected gas moves faster than the displaced oil and is in continuous contact with virgin oil at the displacement front. This leads to a continuing enrichment 01' the gas at the displacement front by evaporation of the C, - C,

By D. M. Waldorf

Steam permeability measurements have been made in the laboratory on several samples of natural reservoir materials. The steam temperatures and pressures were selected to simulate conditions which might exist in a reservoir during the injection of steam. For each sample tested, the experimental permeability to superheated steam was comparable to that measured with air and no evidence of plugging was detected. Some samples were exposed to water at various temperatures and plugging was found to occur in materials which contained significant quantities of monmorillonite clay. Temperature had little effect on the degree of plug-ning between 75 and 325 F. The measured pemeabilities tended to increase slightly with temperature, but the changes were small compared with the initial loss of per~neability on wetting. Sequential pemzeability measurements were made on two samples using air, water, steam, water and air, in that order. Both samples were water-sensitive and plugged extensively after the initial injection of water. Upon exposure to superheated steatm the samples dehydrated and their permenbilities to superheated steam were comparable to those initially measured with air. The remaining measuretnetzts with water and air confirmed that the water plugging was reversible and that the samples were not seriorrsly damaged during the tests. INTRODUCTION The swelling of water-sensitive clays during water floods has long been recognized as a potential source of reservoir damage. The recent extensive application of steam injection and stimulation has compounded this problem since both hot water and steam (as well as fresh water at reservoir temperatures) are, at sume time, in contact with the producing zone adjacent to the bore of a steam injection well. The purpose of this paper is to present data which compare the sensitivity of some natural sedimentary rock samples to water at various temperatures, and to super-heated steam. Some properties of montmorillonite clay are briefly reviewed, and comparisons are drawn between empirical data and the predicted behavior of the montmorillonite known to be present in the samples. PROPERTIES OF MONTMORILLONIT E CLAY Water initially adsorbs on dry N a -montmorillonite clay in discrete layers in the interlaminar space between clal platelets. The platelet spacing, which is 9.6 A (angstroms) for a dehydrated clay, has been observed to expand in discrete steps to 12.4, 15.5, 18.4 and 21.4 A spacings, indicating the formation of four discrete layers of regularly oriented water molecules.' The first two layers are easily formed by hydrating a dry sample to equilibrium in an atmosphere with carefully controlled humidity. The formation of the higher layers is more difficult. The usual X-ray diffraction patterns of the more highly hydrated samples indicate a gradual increase in the average spacing betwcen 15.5 and 19.2 A, followed by a discontinuous expansion to 31 A when the weight ratio of water to dry clay is between 0.5 and 1.2.' Platelet expansion above 31 A proceeds monotonically as the moisture is increased and no regular arrangement of the platelets ib observed. Water-sensitivity in sedimentary rocks is usually associated with Na-montmorillonite clay when it is in the noncrystal-line state. Mering3 found that the average lattice spacing of sodium montmorillonite hydrated at 68 F and 70 per cent relative humidity was 15.5 A, and that the spacing, at 92 per cent humidity was 16.5 A. The water adsorbed at the higher humidity has the same free energy as liquid water at 65.6 F. Kolaian and Low' used a tensiometer to measure the thermodynamic properties of water in diffuse suspensions of montmorillonite clays relative to pure water. They observed that water in suspensions as dilute as 6 per cent clay became partially oriented when left undisturbed. The bonding associated with this orientation was not extensive because the free energy difference between the water in suspension and pure water was only a few millicalories per mole. They also found that the measured free energy difference decreased rapidly with temperature and became negligible above 100 F. This evidence indicates that montmorillonites contained in sedimentary rocks would dehydrate to a crystalline structure when exposed to superheated steam, and that the rock permeability measured with steam would be equivalent to that measured with air. The effect of elevated temperatures on the swelline of montmorillonite clays in aqueous suspensions has not been investigated. The Gouy-Chapman diffuse-ion-layer theory has been used to predict the swelling pressure of clay suspensions in dilute salt solutions at room temperature with reasonable success. theory also correctly predicts the direction of the thermal response of Na-mont-morillonite swelling pressures in dilute salt suspensions, 9 Over the temperature range of 33 to 68 F, an increase in

Jan 1, 1966

By S. S. Shen, M. J. Pool, P. J. Spencer

Heats of solution of silver and copper in dilute Ag-Cu-Sn alloys at 720°K have been determined using a liquid metal-solution calorieter. Values of the se2f-interaction coefficient n AgAghave been calculated at constant copper concentrations and n Cu Cuhas been determined at constant silver contents. The reliability of the experimental data is shown by the very good agreement between nCujAg and ij &$; these interaction coefficients have experimental values of -9100 and - 9590 cal per g-atom, respectively. Certain solution models are shown to be inadequate for prediction of solute interaction coefficients in dilute Ag-Cu-Sn alloys. In a previous publication' the results of a thermody-namic study of dilute Ag-Au-Sn alloys were presented. The present work represents the continuation of a program to investigate dilute alloys of the noble metals with tin and in particular is concerned with solute interactions in the Ag-Cu-Sn system. By determination of the magnitude and sign of the various interaction coefficients in dilute alloys it is possible to gain some understanding of the different types of solute-solute and so lute-solvent bonding changes that occur as the solute concentrations are varied. Hence systematic studies of alloys with similar physical characteristics as regards size, structure, electronegativity, and so forth, of their components can contribute a great deal to present theoretical knowledge of solutions. The recent definition of an enthalpy interaction coefficient, 11, by Lupis and Elliott2 is of particular value in calorimetric studies such as the present one: where j and i are solutes and s is the solvent; Si is the relative partial molar enthalpy of component i and x represents the mole fraction of solute or solvent. Values of ?Hi can be obtained directly by solution calorimetry and data for n are thus easily determined, often with a high degree of accuracy. ?Hi is related to the relative partial molar enthalpy at infinite dilution, ?Hi and to the enthalpy interaction coefficients by the expression: ?Hi?Hi + X;nz+ ... [2] The aim of the present work was to determine the self-interaction coefficients n AgAgand 178: in alloys of different compositions and also to establish values for n Agcg| and ncuAg. Since it is a thermodynamic requirement (resulting from the Maxwell-type relationships which can be applied to partial molar properties) that nAgcu and ncuAg should be equal, a further aim of this study was to demonstrate the agreement between experiment and theory. EXPERIMENTAL A description of the liquid metal-solution calorimeter used in this research has already been published,3 and no further details of its construction and operation will therefore be given here. Copper supplied by the American Smelting and Refining Co. was indicated by them as being 99.999 pct pure, and the silver obtained from A. D. Mackay, Inc., was also quoted as being 99.999 pct pure. A solvent bath consisting of between 70 and 80 g of 99.99 pct pure Sn was used for each series of experimental drops. Its weight was accurately determined and the appropriate amounts of copper or silver were added to give alloys of the desired composition. Approximately 0.00125 g-atom additions were used for determinations of the heat of solution of silver in the bath, while, for copper, specimens consisting of approximately 0.0015 g-atom were used. The heat capacity of the bath was determined at regular intervals during a series of drops using tin or tungsten calibration samples. The heats of solution of silver and copper in pure tin were first determined as a function of their concentration in order to establish the self-interaction coefficients 7AgAg and ncucu Alloys containing a constant 0.01, 0.02, 0.03, and 0.04 mole fraction of copper were then used to study 17:: in alloys of different copper content, while alloys of the same mole fractions of silver were used to determine equivalent data for 178: at constant silver concentrations. The composition of the bath was held at the desired copper or silver concentration by making calculated additions of the appropriate solute throughout the experiment. From the limiting values of ?HAg in the constant copper content alloys it was possible to study ?HAg as a function of xCu and hence to determine 42:. A similar analysis of the re, values permitted calculation of nAgcu. Heat content and heat capacity data from Hultgren et al* were used to calculate heat of solution values from the measured heat effects at the experimental temperature of 720°K. RESULTS AND DISCUSSION Determinations of ?HAg. A preliminary investigation of the heat of solution of silver in pure tin at 720°K was first made in order to establish the value of nAgAg before additions of copper were made and also to compare the value of ?HOAg(l) with that obtained in the previous study of Ag-Au-Sn alloys.' Then the heat of solution of silver in Cu-Sn alloys was investigated as a func-

Jan 1, 1970

By J. L. Walter, W. R. Hibbard

A GREAT deal of work has been done on the rolling of single crystals of iron. Barrett and evensoon studied end orientations of heavily cold-rolled iron crystals and found that some crystals maintained a sharp single orientation during rolling. Others rotated into two or more orientations, and some fragmented and approached the entire polycrystalline texture depending on the original orientation of both the normal and rolling directions. Barrett, Ansel, and Mehl2 studied iron-silicon alloys and found that the addition of silicon to the iron had little effect on heavily rolled polycrystalline material. Dunn3 has extensively studied the cold-rolling and recrystallization of silicon-iron single crystals. Dunn found that for single crystals having initial orientation between (110) [001] and (111) [112], the principalcomponent of the cold-rolled texture is (111) [112]. Koh and Dunn4 studied the cold-rolled textures of single crystals having initial orientations in the range (001) [110] to (111) [IT01 and found that these are stable end orientations. They also found that all orientations having a [110] direction parallel to the transverse direction rotate to either the (001) [110] or the (111) [112] stable end orientation except for orientations near (112) [11], which divide and produce a final texture consisting of (001) [110]and (111) [112] components. Crystals having a (111) <112>-type texture re-crystallized to a (120) [001] or (110) [001]-type texture. Crystals having orientations with a range of (001) to (335) in the rolling plane and [110] in the rolling direction recrystallized5 to a wide spread of the initial orientations resulting from a multiplicity of 30-deg rotations about several (110) poles. The present study was undertaken to relate other orientations of crystals of silicon-iron to their cold-rolling and recrystallization textures, so that one might rationalize polycrystalline recrystallization data on the basis of the known deformation texture and the behavior of single crystals in these orientations. PROCEDURE Samples were obtained from a cylindrical ingot of 3 pct silicon iron prepared as follows: Armco iron was melted with high-purity silicon flakes under an atmosphere of argon to minimize oxidation. The alloy was poured into a special mold to form an ingot which consisted partially of large columnar crystals. Plates were cut from the columnar portions of the ingot with the longitudinal direction parallel to the columnar axes and ground to 0.040 in. thick. The plates were heavily etched to a thickness of 0.032 in. to remove the cold-worked surface. Orientations of seventeen crystals were determined by Laue back-reflection techniques keeping the mean columnar axis as the reference direction. The plate was then cut in two, parallel to the columnar axis. One portion of the plate was rolled at room temperature parallel to the columnar axis to a reduction in thickness of 84 pct. The remaining portion of the plate was rolled also at room temperature across the columnar axis to a reduction of 66 pct, at which point the crystals began to separate at the boundaries. After rolling, nine individual crystals were removed from the strip by cutting along the crystal boundaries with a jeweler&apos;s saw. Fig. 1 shows the original orientations of the six crystals that were straight-rolled and of the three crystals (4, 7, and 8) that were cross-rolled. Each rolled crystal was carefully etched to approximately 0.002 in. thick. Textures of the cold-rolled crystals were determined by use of the diffractometer with a non-integrating sample holder. The pole figures were made for the (200) poles using molybdenum Ka radiation and were plotted by an automatic stereographic projection recorder.&apos; Spurious poles were determined by rerunning portions of the pole figures using strontium oxide to filter out the Ka radiation. The central portions of the pole figures have not been determined. The pole figures were completed to about 55 deg from the periphery at which point the sample holder interfered with passage of the beam. Following the determination of the cold-rolled

Jan 1, 1959

By Charles C. Peterson, Ronald E. Enstrom

Significant improvements have been made in the ursine systern for epitaxial vapor gvowtlz of Gds. The electron concentration has been reduced to below 1015 cm-3 with electron-mobility values as high as 7200 sq on per v-sec at 30PK and 60,000 sq cw7 per v-sec at 77°K. These high-purity layers have been successfully gvown on n&apos; layers with thicknesses as snzall as 1 p and as large as 125 p. Furthermore, high-purity layers have been incorporated into an structure without degradation of electrical properties. Different impurity gradients at the n&apos; to n interface were achieved. Using these structures, Gunn oscillators have been operated at frequencies as low as 0.4 GHz and as high as 40 GHz, which equals the highest valzle yet reported. The frequencies nleasured are in reasonable apeenlent with those calculated fron7 the n-layer widths and the transit times. CW operatiolz has been achieved from 3 to 20 GHz. In Gunn devices for >40 GHz operation (i.e., witk an n-layer tkickness below 2.5p), the n layer has been generally too pure to permit oscillations to occuv. ThE mechanism of the Gunn oscillator&apos; is now generally understood.2-5 Electron transfer from the (000) minimum to the ( 100) minima leads to a voltage-controlled negative resistance, which results in the formation of domains of high and low electric fields which travel through the crystal with a characteristic velocity of about 107 cm per sec. When a constant voltage is applied to the sample, this domain motion generaliy leads to oscillations at the transit time frequency, fT = 107/L, where L is the thickness of the active n layer.&apos; In this case, a single high-field domain is nucleated at the cathode and grows until it reaches the anode, where it is absorbed; a new domain then forms at the cathode.5 There are related modes of oscillation of the same device in which a tuned circuit causes a periodic variation of the voltage across the device. The frequency then may be either above or below fT. It has been shown that oscillations will occur when n • L 2 1012 cm"2, where n is the carrier concentration in the active region. At lower doping densities, 10" 5 n . L 5 lo&apos;&apos;, the doping is said to be subcritical for oscillation and the description of the device operation changes since the domains become comparable in thickness to the device thickness, L. Nevertheless, such devices have been found to be "active" and, in fact, are useful as amplifiers.778 For CW operation, one wishes to minimize the power dissipation, which is related to the electric field, E, and the low-field resistivity, p. Below threshold, the power dissipation density is approximately Typically, at threshold where E -- 3 x 103 v per cm, the dissipation density is 107/p watts per cu cm, p in ohm-cm. Furthermore, it is desirable to provide good conduction of the heat generated in the active region. The temperature rise, AT, across the active layer of a sandwich structure, with a heat sink on one side, is given by AT = (E&apos;/P)(L~/~~) where it is assumed that the thermal conductivity, u, and resistivity, p, of GaAs do not vary appreciably over the range of temperature and electric fields existing in the layer. This expression shows that, subject to maintaining an appropriate (n . L) product, CW operation is favored by a higher resistivity, a lower threshold field, and a thinner device. The above device requirements place some severe restrictions on the materials to be used, especially for high-frequency (>10 GHz) operation. Here, it is necessary to prepare very thin (<10 µ) layers of GaAs, in a state of high purity (-1 ohm-cm), complete with very low-resistance ohmic contacts. Problems of handling such thin and fragile samples become inereasingly severe as the frequency is raised. Furthermore, while good low-resistance ohmic contacts are easily applied to low-resistivity GaAs, contacting difficulties are encountered for these higher-resistivity materials.

Jan 1, 1968

By Charles F. Hickey, Eric B. Kula

Thermomechanical treatments applied to the maraging steels include a) cold working in the austenitic condition at 650°F, followed by transformation to martensite and aging, b) cold working in the murtensitic condition and aging, and c) cold working in the aged condition with and without subsequent reaging. The strength increases in these steels are very small compared to the increases observed in conventional carbon and alloy steels. The changes that are observed are compatible with the strengthening mechanisms operative during thermomechanical treatment of conventional steels, however. Differences are caused by the absence of a carbide precipitate and the low work-hardening rate in both the solution-treated and the aged conditions. ThE 18 pct Ni maraging steels represent a class of steels which are finding great interest for high-strength applications.1~2 They are essentially carbon-free, and contain 7 to 9 pct Co, 3 to 5 pct Mo, and 0.2 to 0.8 pct Ti. Although austenitic at elevated temperatures, they can be air-cooled to room temperature to form a martensite, which because of the absence of carbon is relatively soft. On subsequent reheating age hardening occurs and strength levels of 250 to 300 ksi yield strength can be attained. These steels appear to be particularly suitable for studying the response to various thermome-chanical treatments for additional reasons other than the obvious one of attempting to improve their already attractive properties. Thermomechanical treatments can be defined as treatments whereby plastic deformation, generally below the recrystal-lization temperature, is introduced into the heat-treatment cycle of a steel in order to improve the properties. With an absence of intermediate transformation products on air cooling the maraging steels have good hardenability and hence can readily be cold-worked in the austenitic condition prior to transformation to martensite. Further, they can be worked in the martensitic condition prior to aging, and even can be deformed in the fully aged condition. Finally, it is of interest to compare their re- sponse to that of the more conventional alloy and carbon steels, where the role of carbides is important in the strength increase by thermomechani-cal treatments. The thermomechanical treatment of conventional steels has been the subject of a recent review.&apos; I) MATERIALS AND PROCEDURE The steel used in this investigation was a commercially produced vacuum-melt heat, which had been rolled to 0.090 in. and mill-annealed. The composition of the alloy was as follows: 0.02 C, 0.08 Mn, 0.10 Si, 0.009 P, 0.009 S, 18.96 Ni, 7.34 Co, 5.04 Mo, 0.29 Ti, 0.05 Al, 0.004 B, 0.01 Zr, and 0.05 Ca. Unless otherwise stated the heat treatments used were the standai-d solution treatment at 1500°F for 1 hr, air cool, followed by a 900°F, 3 hr age. In this condition, the material exhibited 232 ksi yield strength and 239 ksi tensile strength. Mechanical properties were determined by Vicker&apos;s hardness measurement (20 kg) and by tensile tests on standard 1/2-in.-wide, 2-in.-gage-length sheet tensile specimens. Notch tensile tests were run using the 1-in.-wide NASA type, edge-notched specimen.4 Fracture-toughness determinations were made on 3-in.-wide, center-notched, fatigue-cracked specimens, following the recommendations of the ASTM Committee on Fracture-Toughness Testing.4 An electric-potential technique was used for measuring the crack size at the onset of rapid crack propagation5 which is necessary for calculations of Kc, the critical stress-intensity factor under plane-stress conditions. The critical stress-intensity factor under plane-strain conditions KI, was also calculated, using the stress at which the first observable crack growth occurred. 11) RESULTS A) Cold-Worked in the Austenitic Condition. The reported M, temperature for the 18 pct Ni maraging steel is about 310°F.1 Therefore, a temperature of 650°F was selected as suitable for rolling in the austenitic condition. Specimens were solution-treated at 1500°F for 1 hr, air-cooled to 650°F, and rolled varying percentages from 0 to 60 pct, at 20 pct reduction per pass. Tensile and hardness properties after aging at 900°F for 3 hr are shown in Fig. 1. The tensile strength increases from 253 to 271 ksi and the yield strength from 247 to 265 ksi as a result of a reduc-

Jan 1, 1964

By R. G. Ward, D. R. Gaskell

Using the maximum bubble pressure technique, the densities of iron silicates at 1410°C have been measured blowing helium, nitrogen, and argon. By ensuring equilibrium between the melt and the blowing gas with respect to oxygen potential and by minimizing tempcrature cycling of the furnace, iron precipitation in the melt has been prevented. Thus the previously reported effect of blowing-gas composition on the densities of the melts has been eliminated. Consideration of the oxygen densities of the melts gives an indication of the structural changes accompanying composition change. The density-composition relationship of iron oxide-silica melts in contact with solid iron has been the subject of several investigations1-7 and considerable disparities exist among the various results obtained. Of these investigations, all except one5 have employed the maximum bubble pressure method. In the most recently reported of these investigations1 the density-composition relationship obtained blowing nitrogen differed from that obtained blowing argon. The measured densities obtained under nitrogen were greater than those obtained under argon, the difference being a maximum at the pure liquid iron oxide composition and decreasing with increasing silica content. This observation rationalized the disparities existing among the results of the earlier investigations, showing that two lines, one for nitrogen and the other for argon, could be drawn to fit all the earlier results. No explanation for this phenomenon could be offered. Chemical analysis of rapidly quenched samples of melt for dissolved nitrogen, and direct weighing measurements, excluded solution of nitrogen in the melt from being the cause of the increase in density. The range of blowing gases was extended by Ward and Hendersons who measured the density of liquid iron oxide bubbling helium, nitrogen, neon, argon, and krypton. The measured density was found to decrease smoothly with increasing atomic number of the bubbling gas. The work reported here is a continuation of the program initiated by Ward and Sachdev7 to study the densities in multicomponent melts in which the iron oxide-silica system is the solvent. As such it is necessary to explain or eliminate the anomalous densities of iron silicates under different atmospheres, and the present rede termination was carried out towards this end. EXPERIMENTAL The maximum bubble pressure method of density determination was again employed and the experimen- tal apparatus used was essentially the same as that used by Ward and Sachdev.7 A molybdenum-wound resistance furnace heated an ingot iron crucible of internal diameter 1 in. containing a 2-in. depth of melt. The bubbling gas was blown through a 1/4 -in.-diam mild steel tube onto the end of which was welded a 2-in. extension of 1/4 -in.-diam ingot iron rod, drilled out to 5/32 in., and chamfered to an angle of 45 deg. The blowing tube was introduced to the furnace through a sliding seal and its position was controlled by a vertically mounted micrometer screw which allowed the depth of immersion to be determined with an accuracy of ± 0.01 cm. A Pt/Pt-10 pct Rh thermocouple was located below the crucible and temperature control was effected initially by means of an on-off controller and later by a saturable core reactor. The bubble pressure was determined by measurement of a dibutyl phthalate manometer using a cathetometer. PREPARATION OF MATERIALS Iron oxide was produced by melting ferric oxide in an inductively heated iron crucible in air. The liquid was quenched by pouring onto an iron plate. Silica was prepared by dehydrating silicic acid at 650°C for 12 hr. RESULTS Before any measurements of the density of a melt were made, the density of distilled water at room temperature was measured bubbling helium and argon. Both gases gave the density as 1.00 ± 0.01 g per cu cm which showed that the density of the manometric fluid (dibutyl phthalate) was not affected by contact with the blowing gas. With the furnace controlled by an on-off temperature controller an attempt was made to measure the density of pure liquid iron oxide by bubbling argon. The furnace atmosphere gas and bubbling gas were dried over magnesium perchlorate and deoxidized over copper turnings at 600°C. It was found that the pressure required to blow a bubble at a given depth increased slowly with time, and thus it was impossible to obtain a unique value for the density of the melt. Inspection of the blowing tube after removal from the furnace showed that rings of dendritic iron had precipitated from the melt onto the immersed part of the tube. This is shown in Fig. l(a) where the various "steps" correspond to different depths of immersion. The precipitation of iron was considered to be due to one or both of two possible causes: i) The composition of the liquid iron oxide is that of the liquidus at the temperature under consideration and can be expressed by the equilibrium

Jan 1, 1968

By M. E. Wadsworth, T. L. MacKay

Sintered UO, samples were leached in sulfuric acid solutions of various concentrations. A pressurized system was used so that it was possible to investigate the kinetics of the reaction to 270°C with oxygen overpressures as high as 900 psi. The rate was observed to be a function of the concentration of hydrogen ions and directly proportional to the partial pressure of oxygen. Evidences are presented which indicate that a UO2 surface site reacts with a molecule of water to form a hydroxyl complex which in turn can dissociate with the characteristics of a weak acid. A rate determining step has been proposed which involves the reaction between an oxygen molecule and the hydroxyl complex on the surface of UO,. ThE 2 principal methods for uranium dissolution are carbonate and acid leaching. The sulfuric acid leach is the more popular and is used for the treatment of the majority of the ores of Africa, Canada, and the United States. Low recoveries in basic leach circuits led investigators at the University of British columbia1 to study leaching of uranium ores in pressurized vessels. Early in the study of dissolution of uranium it was found that only uranium in the hexava-lent state could be leached in acid or basic circuits. Therefore, the use of oxygen over-pressure in an autoclave offered an interesting approach to solving the low recovery problems of carbonate leaching. UO, was used in this study because it could be obtained in high purity and also because it is representative of the most refractory of the primary uranium minerals. A pressurized system was used to provide a means whereby important temperature and pressure parameters could be varied for the evaluation of the kinetic processes. The mechanism for the dissolution of UO2 should be similar for any of the uraninite type minerals. At the present all of the kinetic studies that have been conducted have been in carbonate media. Peters and Halpern2 carried out a kinetic study of the leaching of pitchblende. Their specimens were pitchblende ores selected on the basis of high grade and homogeneity. Pearson and wadsworth3 conducted a kinetic study of the dissolution of UO2 in carbonate solutions with results very similar to those obtained by Peters and Halpern. EXPERIMENTAL The UO2 as received* was found by spectroscopic *Mallinckrodt reagent, supplied by the Atomic Energy Commission. analysis to have a purity of 99.94 pct 0.03. It was ground in a mechanical agate mortar and screened through a 400-mesh sieve. Thin flat disks of UO2 were prepared by pressing the sized powder in a specially constructed die at a total pressure of approximately 25 tons per sq in. The pressed disks were approximately 0.25 cm thick, 1.6 cm diam, and 3.5 g in weight. As pressed, the samples were approximately 65 pct of theoretical density. It was essential that a binder such as poly-vinyl alcohol be added before pressing to prevent formation of cracks when fired. It was found by trial and error that pressed disks sintered close to 1870°C in a hydrogen atmosphere, reach densities between 91 and 91.5 pct of the theoretical density. At this density the samples had no measurable porosity based upon a 2-hr emersion in boiling water. An X-ray examination of these sintered UO2 disks showed them to be identical with the original UO2 received. Reaction of UO2 with the alundum furnace core was prevented by placing molybdenum between the samples and the core according to the method of Corwin and Eyerly.4 Leaching studies were carried out in a specially designed autoclave, the details of which have been presented e1sewhere.6 The main features of the equipment as applied to a kinetic study are: 1) solution samples may be removed during the course of a single run; and 2) temperature and agitation are carefully controlled. Two-ml samples removed from the autoclave during the course of a run were analyzed for U3O8 content with a Beckman model DK-2 spectrophotometer by the method of

Jan 1, 1959

By F. D. Patchen

Changes in the properties of partland cement upon the addition of fine-ground silica are discussed. Data were collected from formulations cured for periods up to 60 days at temperatures varying from 180" to 350°F. Compressive strengths, permeabilities and thickening times are compared. It is demonstrated that addition of find-ground silica in proper proportion results in a hydrated cement with superior properties above 230°F; i.e., early compressive strengths are higher and increase with additional curing, permeabilities are significantly lnrver and thickening times are increased. X-ray analysis of hydrated cement samples have been used to determine more fully the complex chemistry of these systems. Dicalcium silicate alpha-hydrate was found in all neat cements cured above 260°F. A 10 weight per cent silica addition produced a maximum amount of this phase. Xonotlite and tobermorite have been identified as hydration products at 320°F in systems containing 35 or more weight per cent silica. Formation of these components appears to be primarily responsible for the gain in strength and reduction of permeability observed after the addition of silica. INTRODUCTION For several years it has been recognized that loss of compressive strength occurs when portland cement is cured at a temperature above 250°F. This phenomenon has been called "strength retrogression". More recently it has been recognized that increased permeability usually is associated with decreased compressive strength at these temperatures. At curing temperatures above 300°F, these factors reach serious proportions. A compressive strength loss of 50 per cent between curing times of 24 hours and 14 days has been reported,&apos; and permeabilities as high as 10 md have been measured in neat cements cured at 320°F for seven days.&apos; Earlier investigators,&apos; although unsuccessful in eliminating strength retrogression, stated ". . . .it appears possible that by the proper selection of additives for cement, strength loss with age at high temperatures can be either eliminated or considerably lessened". One solution suggested was the use of a pozzolanic material, hydrated lime, and a retarder. Menze15 in 1934 discovered that portland cement containing finely divided silica possessed high compressive strengths when the curing temperature was 350°F. The use of such a composition is now an established practice in the manufacture of steam-cured cement blocks. It is reasonable to assume that the same beneficial effect can be used advantageously in high-temperature oilwell cementing operations. Ludwig first mentioned the use of sand for this purpose. Later, a portland cement containing moderate additions of silica flour and retarded with CMHEC, a cellulose derivative. was recommended for high-temperature application." These formulations have been successfully employed in the field."&apos;" This paper presents the results of a research program to test the efficacy of finely ground silica in increasing the compressive strength and reducing the permeability of oilwell cement compositions containing portland cement. Included also are X-ray diffraction patterns of powdered samples which have been used to determine some of the important chemical reactions occurring in these systems. LABORATORY PROCEDURES AND MATERIALS All compressive-strength test specimens were prepared and cured from a slurry in accordance with API RP 10B, with two modifications. A final curing pressure of 5,000 psi was maintained for a one- or three-day period; but, for further curing, pressures were reduced to the vapor pressure of water at the curing temperature. Also, the water content was varied in samples containing silica to maintain the slurry viscosity within a range of 5 to 15 poise as measured on a consistometer. Test specimens at 180°T were cured in a water bath at atmospheric pressure. At higher temperatures the specimens were cured in a steam-jacketed high-pressure curing vessel at 5,000 psi for a one- or three-day period. cubes cured for longer periods were removed from the pressure-curing vessel after 24 hours, sealed in small bombs containing water and placed in an aging oven.

By G. P. Conard, E. H. Rennhack

The creep behavior of hot-rolled, hypoeutectic Zn-Ti alloys was investigated in the temperature range from 0.43 to 0.53 TM. Secondary flow was found to originate primarily from strain-induced gvain growth where grain boundary )nigvation served to relieve the strain energy of distortion introduced by slip, grain boundary sliding, and subgvain formation. The extent to which this recovery mechanism operated was determined by the ratio of grain width to the spacing between planar fibers of TiZn,, compound particles generated in these alloys during rolling. When this ratio was unity, creep resistance demonstrated a marked improvement. In this condition, which was fulfilled by annealing following rolling, structural stability was enhanced with decreasing grain size below the equicohesive temperature (-0.5Tm), while the reverse was true above this temperature. TITANIUM concentrations approaching the eutectic composition of 0.23 wt pctl have been shown to promote a significant increase in the creep resistance of rolled zinc,2 The alloying effect created with titanium is somewhat unique; a structure closely resembling that of a fiber-reinforced metal composite can be developed which selectively modifies creep strength in preference to other mechanical properties. In an earlier investigation,~ the present authors found that, while the fiber network, composed of individual TiZn,, compound particles, had a distinct influence on rolled texture, the crystallographic variations produced were of minor importance with respect to creep. Rather, creep resistance seemingly increased when the grain size appeared to coincide with the in-terfiber spacing. The work described here was undertaken to explore this effect in greater detail. EXPERIMENTAL PROCEDURE Three zinc-base alloys containing 0.05, 0.12, and 0.16 wt pct Ti were prepared from CP zinc and iodide titanium in the form of 4 by 2 by f in. chill-cast ingots. The melting and casting procedures for these alloys have been detailed el~ewhere.~ Individual ingots of each alloy were hot-rolled at 200°C (392°F) to total reductions of 10, 25, 50, 75, and 90 pct in from one to five passes, respectively, employing a 10-min reheat prior to each rolling pass. With grain, tensile-type creep specimens with a 1-in.-long, -in.-wide gage section were machined from the rolled strips for test purposes. Annealing studies to explore the influence of grain size on secondary creep flow were carried out at 400°C (752°F) in argon for times extending up to 60 min. The grain-size effect was evaluated in terms of average grain width and length values statistically derived from lineal intersection measurements.4 A similar method was applied in establishing the average interfiber spacing, i.e., average perpendicular distance between adjacent planar fibers. The creep characteristics of the alloys were investigated by means of constant-load and constant-stress creep tests. The former tests were conducted at 25°C (77°F) under an initial stress of 10,000 psi, while the latter were performed in the range from 25°C (77°F) to 90°C (194°F) at stress levels varying from 8000 to 22,000 psi. Total specimen strain, as determined with Budd HE-1161-B strain gages, was in excess of 0.10. Maintenance of constant stress was achieved through periodic load reductions made at 0.01 strain intervals to compensate for the attendant incremental reduction in specimen cross-sectional area. The maximum indicated error in the applied stress at these strain intervals was less than 3.0 pct. RESULTS AND DISCUSSION Constant-Load Creep. In an effort to clarify the in-terrelation between interfiber spacing and grain size with respect to the creep resistance of the Zn-Ti alloys, their separate effects on secondary creep rate were determined as a function of titanium content and rolling reduction. These results are set forth in Figs. 1 and 2, respectively. The average grain diameter plotted in Fig. 2 was resolved from average grain width and length values. No data are presented for reductions of less than 50 pct because of the inability to obtain consistent measurements on these strips. The curves of Fig. 1 indicated that, for a given titanium content, a decrease in interfiber spacing, as produced with increasing reduction, promoted a decrease in creep rate. Depending on titanium content, however, wide variations in creep rate occurred at the same interfiber spacing suggesting that interfiber spacing, by itself, has little or no influence on creep resistance. Grain size, on the other hand, decreased progressively with both increasing rolling reduction and titanium content, the effect of which led to a pronounced decrease in creep rate, particularly when the average grain diameter became smaller than 3.0 x 10"4 in., Fig. 2. The continuity of this relationship tended to support the view that grain size rather than interfiber spacing was predominant in controlling secondary creep. Annealing Effect. The observed dependence of creep flow on grain size suggested that a further contribution to creep resistance would result when the alloys were annealed to effect a coincidence between grain width and interfiber spacing, see Fig. 3(b). ~eiides creating an immediate barrier to grain boundary movement, annealing offered the possibility of providing increased structural stability by eliminating many high-energy, mobile grain boundaries.= To test this hypothesis, specimens from the Zn-0.16 Ti strips reduced 75 and

Jan 1, 1967

By D. M. Metcalf

MOST PEOPLE think of peat as an inferior substitute for coal as a fuel, and will be surprised to learn that it is extensively mined in this country for use as fertilizer rather than as a fuel. Some years ago the Florida Humus Co. began producing it at Zellwood, Orange County, Fla., in a small way for local use. When, however, the company secured an Institute member, M. H. Cuise, to apply his wide experience in mining to the problems here it was found possible to decrease production costs 70 per cent and increase output tenfold. The obvious way in which to decrease costs was to replace shovel-and- horse methods with machinery, much of which, in order to keep down-invested capital, was improvised by remodeling second-hand equipment, changing the design where necessary to meet the special conditions involved.

Jan 1, 1932

By AIME AIME

THIS journal is fully indexed-every issue, as soon as published-in a set of card?, which thus brings ready to your hand any article on any subject in this journal or in any one of 1700 other journals in all languages. This Engineering Index Service, instituted in January, 1928, is to be found in the Public Libraries of Newark, Cleveland, Bridgeport, Baltimore and the John Crerar Library, Chicago. Engineers in any field who live or work in New Jersey will find this mammoth index to the latest engineering literature in the Public Library of Newark, N. J.

Jan 1, 1929