By M. T. Baquera

A comparison of microstructures associated with W single-crystal ([001], [011], [111]) rods prior to deformation (as grown), and after quasi-static compression (at a strain rate of ~1/s) by transmission electron microscopy (TEM) shows several orders of magnitude difference in dislocation density. Dislocation substructures were not significantly different amongst the deformed sample orientations. In contrast, [001] W rods penetrated into steel targets, at impact velocities of ~1.3 km/s, exhibited heavy dislocation densities and dynamic recrystallization as very distinct microstructural regimes accommodating the penetration process. Twinning on {112} also occurred as a precursor to, or remnant of, these microstructures near the projectile head. These results suggest that deformation accommodating the extreme strains and strain rates associated with the penetration of a single-crystal rod into a metal target is not adequately represented by conventional deformation

Jan 1, 2006

By Keith S. McIntosh

The fire assay process for the quantitative recovery of platinum group elements (PGE?s) prior to subsequent analysis traditionally is a time-consuming process. Samples derive from various ore types and contain PGE?s at the ppm or ppb levels, making concentration of the elements mandatory before assaying. Traditionally sample turn-around times are of the order of 24 hours. The whole sequence of sample preparation, fire assay and subsequent analysis of PGE?s have been automated by Anglo Platinum. Some of the major challenges on the road to automation will be discussed and the novel solutions that were implemented. The engineered solution included robotic automation of the whole sequence, from sample preparation, up to the final element by element assay. The final system allowed for rapid (less than one hour) and accurate analysis of PGE?s even in streams containing very low levels, such as flotation tailing streams and drill core samples.

Jan 1, 2006

By Ram Avtar

High tensile thick plates (>80mm, weight ~3000 Kg) of medium carbon low alloy steel, when heat treated, manifested higher percentage of crystalline area (>20%) in fractured surface. Such problem was not encountered in thinner plates. The genesis of higher crystallinity in fracture was examined. It was observed that the thicker plate undergone slower rate (Average 0.9oC/Sec.) from soaking temperature to Ms temperature) of cooling after austenising during oil quenching and thereby quenched microstructure had upper bainites. During tempering of as quenched bainite, additional precipitation took place at the lath boundaries of bainite. This led to weakening of grain boundaries and aided easy crack propagation during fracture and resulted in formation of higher percentage of crystalline area in fractured surface. Enhancement in cooling rate (Average 1.8oC/Sec. from soaking temperature to Ms temperature) of austenised plate by switching over from oil quenching to water quenching practice resulted in complete transformation of austenite into martensite and produced ductile fracture (zero Crystallinity). Plates conformed improvement in mechanical properties between 2-5%.

Jan 1, 2009

By Fiseha Tesfaye, Pekka Taskinen

"Thermodynamics of the equilibrium phase assemblage Ago_9Cul.lS-Cu2-xS-CuS have been studied by an EMF -method. The ternary phase was synthesized from the pure Cu2S and Ag2S in vacuum furnace at high-temperature and mixed with appropriate compositions of Cu2S and CuS to form the cathode electrode. The EMF-measurements were made on the solid-state galvanic cell Pt(-) I Ag I RbAg,ils I Ago9Cu1.1S-Cu2-xS-CuS I Pt(+), in a temperature range from 316 K to 498K.Based on the measured EMF vs. T relations, thermodynamic functions (?fG° , ?fS and ?fH°) of stromeyerite (Ag0.9Cu1.1S) in equilibrium with Cu2-xS and CuS have been determined. The obtained experimental values have been compared with the available literature values. New experimentally determined thermodynamic properties of the solid solution (Ag,Cu)2Sss were determined.IntroductionDue to intense mining of high grade sulfide ore minerals in the past, recently, the available sulfide ores are poor in metals and becoming increasingly complex; such that, the production of high grade metals by the conventional pyrometallurgical processes is compromised. Consequently, smelters are in need to modify their operating flow sheets and strategies for processing more complex feed materials economically, while meeting the strict environmental regulations. To make the appropriate modifications, accurate thermochemical data of phases and phase assemblages which exist in these complex ore minerals are essential.Silver-bearing sulfosalts are encountered in ore minerals for the production of base metals and are common sources of silver. Among the silver-based sulfosalts, stromeyerite (Ag0_9Cu1.1S) is relatively common ore mineral in most hydrothermal vein and replacement deposits [1]. Recently, the ternary chalcogenide compound Ago0.93Cu1,07S has been studied, intensively, due to its high ionic conductivity and gradual disorder in the sequential phase transitions [2]. Therefore, accurate knowledge of the thermodynamic properties of stromeyerite has considerable fundamental and practical interest in many aspects of extractive, chemical and physical metallurgy."

Jan 1, 2014

By J. Antrekowitsch

Keywords: residues, fluorides, chlorides, zinc, steel mill dust The recyclability of various nonferrous metal wastes often suffers from a relatively high fluorine and chlorine content. Both are inserted in most cases by the use of plastic contaminated scrap and a wide variety of different coatings. These halogens lead to poor product qualities and off gas contamination. Especially the history of zinc recovery from steel mill dusts shows, that the today common hydrometallurgical options are on their limit and therefore are not sufficient in most cases. This thermochemical study should give more information about different pyrometallurgical options, that offer both a chlorine and fluorine reduction and efficient zinc recovery, preferably in one process step. Selective evaporation in different atmospheres and conversion with the use of hydrogen are the main parts in this study. The results combined with the relatively small information available from literature should provide a basis for further investigations in this field.

Jan 1, 2005

By T. Nagano

Mitsubishi Metal Corporation started the development work of a new process for continuous production of copper in 1961. After a series of experimental and semi-commercial operations, the first commercial plant of the Mitsubishi Continuous Copper Smelting and Converting Process was put into operation in March, 1974. The new plant, which has a design capacity of 4,000 metric ton copper per month, was built within the premises of Naoshima Smelter, replacing the old No.1 reverberatory smelter there. The SO2-rich exhaust gas from this new plant is blended with the off-gas of the No.2 reverberatory furnace for production of sulfuric acid and the overall emission of sulfur at Naoshima has been greatly reduced. The operation of the continuous plant has been satisfactory and several advantageous features of the Mitsubishi Process have been proven on a commercial scale. This paper first gives a brief description of the history of the development work and the characteristic features of the process. The paper then describes the new commercial plant and operating data obtained so far.

Jan 1, 1976

By Tian Sugui

By means of the measurement of the enduring property and microstructure observation, an investigation has been made into the influences of the element Re and TCP phase on the enduring property of the single crystal nickel base superalloys. Results show that the needle-like TCP phase is precipitated along the <110> orientation on {111} planes in Re-containing/free superalloys during the long term aging, the TCP phase is identified as µ phase, and the precipitated µ phase in 4.5%Re alloy is gradually spheroidized during aging. Thereinto, the needle-like µ phase may obviously decrease the enduring lifetimes of the alloys due to the consumption of the refractory elements and the effect of the stress concentration. But the stress concentration is not easily generated in the regions near the spherical-like µ phase, which is a main reason of reducing the enduring lifetime of 4.5%Re alloy to a small extent.

Jan 1, 2010

By Jose R. Parga

In mining operations, cyanidation is the ,predominant method by which gold and silver are recovered from their ores and it is recognized that cyanide consumption can be a major factor that contributes to the operating costs for such operations. Also after extraction and recovery of precious metals a certain amount of cyanide is delivered to the tailings pond and must be considered with respect is environmental problems due to the toxicity of cyanides. In this regard, the Air-Sparged Hydrocyclone (ASH) has been used as a reactor for the treatment of cyanide solutions in two ways; first for cyanide recovery by acidulation using the Mexican modification of the Mills-Crowe process and second for cyanide destruction by oxidation with the use of chlorine dioxide (ClO2). In both cases, excellent performance can be achieved using the high capacity ASH system.

Jan 1, 1998

By Michael J. Nicol

Growing environmental and occupational safety concerns about the use of cyanide in gold processing has increased the interest in more acceptable alternatives. The most likely of these is thiosulfate. However, the thiosulfate process lacks a proven in-pulp method of recovering the dissolved gold, because activated carbon is not effective for the absorption of the gold thiosulfate complex .. Anion exchange resins do offer a possible route for in-pulp recovery. This paper describes work aimed at the evaluation of the effectiveness of commercially available anion exchange resins for the recovery of gold from thiosulfate leach liquors? and pulps. It has been found that strong-base resins are superior to weak-base resins in that they have a larger capacity, which assists in reducing the competition from other anions within a leach solution. Further studies with a selected commercial strong-base resin have shown that competing polythionateanions (particularly tri-and tetrathionate). Lower the maximum possible gold loading but that gold is selectively recovered over other base metal anions in solution. Kinetic experiments found that while? competilig anibns did not affect the initial rate? of gold loading it was important to minimise the contact time of the resin in solution so to prevent displacement of loaded gold by competing anions over longer times. A small-scale resin-in-pulp plant investigation showed gold can be recovered from a leach pulp by a strong-base resin to yield gold loadings of 3000 mg/L, barren pulp containing less than 0.05 mg/L of dissolved gold and. copper loadings of 500 mg/L. Loaded copper was displaced gold and at a loading of 2000 mg/L gold the copper loading was minimal «500 mg/L). The resin was found to recover gold adsorbed on the solids that would, otherwise have. reported to tails if a solid/liquid separation method were used. A patented two-step elution process in which copper and then gold are separately eluted from the resin is also discussed.

Jan 1, 1998

By Hugo Cabrera-Real

This work investigated the chemical and mineralogical properties of CaO-SiO2-CrOx-CaF2- MgO slags. Synthetic slags were prepared and the effect of the slag basicity (CaO/SiO2) and MgO contents on the stability of the mineralogical species formed was analyzed. The morphology and composition of the slags were analyzed by XRD and SEM-EDS, whilst their chemical stability was evaluated by leaching with an aqueous acetic acid solution. It was found that in slags with CaO/SiO2 = 1, the main Cr-compound was MgCr2O4 spinel, which forms octahedron crystals. Small amounts of CaCr2O4 and CaCrO4 were also observed. It was found that increasing the slag basicity from 1 to 2 the compounds MgCr2O4 and CaCr2O4 were formed together with the Cr(V)-containing compound complex Ca5(CrO4)3F which forms hexagonal crystals. The results showed that the highest chromium concentration levels in the leaching liquors corresponded to slags with CaO/SiO2 = 2, probably owing to the formation of Ca5(CrO4)3F.

Jan 1, 2010

By Józef Czemecki

Polish copper concentrates are characterized by high levels of impurities, particularly Pb and As. Two technologies are being used for copper concentrate smelting at KGHM Polska Meidz S.A., namely the shaft furnace process (Legnica Copper Smelter, Glogów I Copper Smelter) and a single-stage process for direct to blister concentrate smelting in a flash furnace (Glogów II Copper Smelter). Both technologies are used at different physical and chemical conditions which results, in different impurities behavior. The paper presents flow sheets for copper production in a plant using the shaft furnace process and in another in which a single stage flash process is used. The metals distribution in particular semi-products is given as well as a method for elimination of impurities from the copper production cycle. Methods are also discussed for alloy and matte converting and copper refining to obtain low Pb and As concentrations in anode copper (0.3% Pb and 1500 ppm As maximum) that are being used in the KGHM Polska Meidz plants. Useful co-operation between the plants using different technologies, aimed at the limiting the effect of undesired impurities on the quality of blister copper produced, is also described.

Jan 1, 1998

By J. M. Tannenbaum

A depth-sensing micro-indentation technique is developed for evaluating mechanical properties of materials at elevated temperatures (to 1200°C). System description and design considerations of the test apparatus are described. Based on Hertzian spherical indentation approach, the micro-indentation test apparatus is capable of determining Young?s modulus and creep strength of test materials with flat, tubular, or curved architectures from room to 1200°C under either air or controlled gaseous environments. Calibration tests were conducted on a H13 Tool Steel coupon from 22°C to 500°C and single crystal Haynes 230 alloy at 1000°C with excellent agreement to the literature values. Indentation creep tests of Haynes 230 alloy were carried out at 1200°C with preliminary results showing good correlation to creep exponents. Further system refinements will be investigated, and additional testing will be conducted.

Jan 1, 2010

By Amy Anderson

The Silica (SME) Technology has been utilized on three separate projects focusing upon the stabilization of mercury-contaminated materials: at the Mother Lode Mine in Oregon, the Sulfur Bank Mercury Mine in California and at a former chloralkali plant in British Columbia. Each of the projects relied primarily on the results collected via EPA Method 1311 TCLP, with additional tests such as SPLP, humidity cell tests and other supporting tests employed as well. Both technical and economic performance of the silica-based technology was evaluated as well as that of competing technologies in some cases. Results established that in each of the three projects an SME chemical dosage rate of 3% chemical by weight of soil/sludge was the optimal ratio required to achieve project treatment objectives, TCLP test results exhibited a reduction in the leachable mercury from the treated materials ranging between 75% and 99% as compared to untreated material, satisfying the technical objectives for each project, Project costs ranged from $l5.00 - $18.26 per metric ton.

Jan 1, 2003

By Carl W. Lam

The increased obsolescence rate of electronic products has made it evermore pertinent to understand the potential environmental impact of materials choices to help guide electronic waste (e-waste) management and promote awareness of high burden materials. Methods for screening for the performance of materials and their potential burden on human health and the environment can be used to comparatively select constituents of present and prospective electronic products. These methods should be able to yield more robust information when linked to other decision-making strategies where integrated data on consumer preferences, production quantities, and regulatory initiatives are sparse or unavailable. A framework is presented here for generating metrics of ecological toxicity, human health toxicity (cancer and non-cancer categories) and global resource consumption for evaluating environmental impact of materials (specifically metals) in electronic products. The time-dependent impact trends of United States? printed wiring board (PWB) metals usage, principally derive

Jan 1, 2010

By David B. George

Kennecott Utah Copper adopted Outokumpu Flash Smelting and Kennecott-Outokumpu Flash Converting in 1995, a process based on granulating high grade copper matte. While nickel mattes and very small quantities of copper matte had been commercially granulated for years, no large scale copper matte granulation system had been built. This paper summarizes the history and benefits of copper matte granulation, the Kennecott design basis, the successful operation for over 10 years and potential problems inherent in some matte granulation approaches.

Jan 1, 2006

By Djona M. Gaballah I.

Selective chlorination of unroasted and roasted spent hydrorefming catalysts was studied between 300 and 600°C using the following gas mixtures : C12+CO, C12+N2 and CI2+air. Such materials contain Co, Ni and Mo compounds supported by alumina and/ or silica. They also contain variable amounts of V compounds, C, S, etc., accumulated during the life time of the catalyst. Direct oxychlorination of the C+S rich sample allows higher extraction rates than those obtained by the carbochlorination of the same roasted one. It seems that the roasting step doesn&apos;t favor the economic metals&apos; recovery. Results of the chlorination of C+S poor spent catalysts, in the presence of CO, in the chlorinating gas mixture, or of carbon added to the sample, were comparable. Cobalt and nickel chlorides were .extracted from the chlorination residues by their dissolution with acidified water, whereas molybdenum and vanadium chlorinated compounds were recovered by selective condensation from the vapor phase. The recovery rates of valuable metals as well as the selectivity were higher for the chlorination of spent catalysts than results obtained by the hydrometallurgical processing of the same sample. Results of the scale-up of the oxychlorination of the unroasted sample confirmed those of the laboratory scale. The global recovery rates were about 88 pct of cobalt, 93 pct of molybdenum and 76 pct of vanadium. The carbochlorination was applied to the recovery of W and Ti from Denox catalyst that is a carbon and sulfur free one. Recovery rates higher than 99 pct at temperatures lower than 500 °C could be obtained. This may indicate that the chlorination process can be applied to the treatment of various industrial wastes or by-product containing transition and/or refractory metal compounds A flow - sheet for the pretreatment of these materials is proposed.

Jan 1, 1995

By J. C. Agarwal

Slags produced by modern smelting furnaces contain copper values which are unacceptably high for discard. The electric arc furnace is employed commercially to clean copper from flash furnace slags but the addition of highly oxidized converter slags to an electric furnace has created operational problems. Highly oxidized Noranda Reactor slags have not been processed successfully in a pyrometallurgical process. These slags, which contain large concentrations of copper (5 to 10 per cent), are treated in slag concentrators (controlled cooling, crushing and milling, and flotation) which produce a copper concentrate that must be resmelted. Though commercially operable, it will be shown that the slag concentrator has important process and cost disadvantages as compared to a pyrometallurgical process. In this paper an economic comparison is made between a pyrometallurgical process and the slag concentrator. For the analysis, five hypothetical smelting plants are considered. Each plant treats 1200 tons of copper concentrate per day and produces 109,000 tons of copper annually. The plant configurations used in this study are:

Jan 1, 1976

By Y. Yang, S. Peelman, J. Sietsma, Z. H. I. Sun

The rare earth elements (REEs) present in the Kiruna iron ore mine tailings are being considered as a new REE resource for the EU. These tailings, after beneficiation, contain approximately 5000 ppm of rare earths, concentrated in apatite and monazite minerals. To economically extract the REEs from these tailings the phosphorous contained within the apatite must also be extracted and the waste production of the process should be minimal. To achieve the extraction of REEs and phosphorous HCl and HNO3 were investigated as possible leaching agents. Based on the results a leaching process using HNO3 is proposed. This process produces H3PO4 from the apatite while simultaneously dissolving the REEs. The resulting leach liquor is then cooled to remove the unwanted Ca as Ca(NO3)2. Analysis of the leach liquor reveals extraction ratios of between 75% and 100% for the heavy REE (e.g. Y, Eu, Dy, …) and below 40% from the light REEs (i.e. Ce, La). Full phosphorous extraction was also achieved.

Jan 1, 2016

By Daniel Bennett

There are few methods currently applied towards on-line bulk mineralogical analysis. Yet on-line knowledge of process mineralogy could potentially provide large benefits, such as increased extraction efficiency or resource optimization. The work described in this paper involves the development of radio frequency methods for bulk mineralogical analysis. Some resonances that occur in the radio frequency spectrum are mineral specific, and potentially allow quantitative estimation of mineralogy in an ore stream. Results will be presented on the specific detection of chalcopyrite. Initial quantitative measurements investigating matrix effects have indicated the feasibility of on-line mineralogical estimation using radio frequency techniques.

Jan 1, 2006

By P. A. Olubambi1

Representative samples of the hydrothermal vein deposits of the bulk complex sulphide ore deposit, 10 km south of Ishiagu, in Ebonyin State, South Eastern part of Nigeria were collected from two small scale mining companies. The samples were mixed and successively crushed in a jaw crusher and cone crusher, and ground in a rod mill. Characterization was carried out with SEM, EDX, XRD, XRF and ICP-OES. Mineralogical analysis revealed the presence of sphalerite, galena, siderite, pyrite, quartz and chalcopyrite. X-ray Diffractometry showed that sphalerite mineral in the ore occurs as sphalerite ferrous with varied percentage of Zn and Fe within the various sizes while chalcopyrite occurs as a chalcopyrite group mineral with chemical formula Cu2MnSnS4. Results of the elemental analysis showed variations in elemental composition within the different sizes.

Jan 1, 2006