By Eduard Ouerra, Nuo Jin

"The use of polytetrafluoroethylene, PTFE, as a solid sorbent for elemental sulfur during pressure oxidation of chalcopyrite was investigated. The effects of agitation, PTFE particle size and lingin sulfonate addition were evaluated using leaching conditions that were otherwise similar to those employed in the CESL process. The effects of these factors and their interactions on chalcopyrite oxidation are explained in terms of interfacial forces and solid-solid interactions. Using relatively fine PTFE powder with vigorous agitation resulted in about 100% copper extraction in less than 90 minutes without the need for grinding of the flotation concentrate.IntroductionThe extraction of copper from sulfide ores has always been dominated by the conventional pyrometallurgical smelting process. Though much effort has been made to develop various hydrometallurgical processing routes, smelting remains as the dominant process, treating approximately 80% of the chalcopyrite concentrates worldwide [1]. However, some of recently emerged techniques for treating chalcopyrite through hydrometallurgical routes are showing results that are competitive with smelting in terms of economical feasibility. Representative methods include: Activox Process, CESL Process, Anglo/UBC Process, High Temperature Pressure Oxidation, and Bio-Oxidation. Among these, the CESL processes operate at a medium temperature range (typically 140-150GC) and oxygen pressure of 100 psi, with chloride as a catalyst, and reportedly achieve copper extractions of about 95% with a light regrinding of flotation concentrate to a p95 of 45 ìðé [2]. In spite of this satisfactory extraction result, the leach residues contain significant amounts of conglomerates which contain a small amount of unreacted concentrate [2], The conglomerations are formed because the elemental sulfur generated is liquid and sticky (melting point of sulfur being 119°C), and has a tendency to wet the sulfide mineral surface, a fact which inhibits the oxidation of the minerals. The overall process chemistry of the CESL process may be summarized as follows [3]:"

Jan 1, 2012

By Jean Igor Margem, Rômulo Loiola, Sergio N. Monteiro, Foluke S. de Assis, Frederico M. Margem

"Fibers extracted from the ramie plant have been traditionally used in textile and are now being considered as polymeric composite reinforcement owing to their superior strength. Recently the mechanical behavior of ramie fiber reinforced polyester composites was investigated but no significant improvement was found. Therefore, the objective of this work was to carry out a similar investigation by changing the type of polymeric matrix. Specimens with up to 30% in volume of ramie fibers incorporated into epoxy were bend-tested until fracture. The results showed a moderate improvement with a tendency of decreasing stress for higher amounts of ramie fibers due to the weak interface developed with the epoxy matrix.IntroductionThe engineering application of natural fibers extracted from cellulose-containing vegetables, also recognized as lignocellulosic fibers, is presently considered an environmentally correct alternative to replace more expensive, non recyclable and energy-intensive synthetic fibers [1-3]. In fact, composites reinforced with traditional fibers such as coconut, sisal, jute, hemp, etc ... are already on the market in substitution for common glass fiber automobile components [4-6]. Even less known fibers like curaua from the Amazon region are being industrially used [7]. Economical and environmental reasons sustain a promising future trend for natural fiber composites. In comparison with the less expensive glass fiber among energy-intensive synthetics, lignocellulosic fibers are approximately five times cheaper. For the current situation of our planet, natural fibers are regarded as ""green"" environmentally friendly materials. They are abundant, renewable, biodegradable, and recyclable, above all, neutral with respect to carbon dioxide emission, associated with global warming.Several relatively unknown lignocellulosic fibers such as piassava [8], sponge gourd [9], sugar cane bagasse [10], buriti [11] and ramie [12], with simple and limited applications, or just byproducts, are now being investigated for their potential as composite reinforcement. This could widen the offer of new lignocellulosic fibers for composite reinforcement. The banana fiber, in particular, has a tensile strength around 700 MPa [13], which is comparable to the strongest lignocellulosic fibers used as composite reinforcement.In addition to polyester, the epoxy is another relatively strong polymer used as composite matrix. Therefore, the objective of the present work was to assess the mechanical properties obtained by flexural test, for epoxy composites reinforced with different amounts of banana fibers."

Jan 1, 2013

By Robert Fritzsch, Ragnhild E. Aune, Mark William Kennedy, Behzad Mirzaei

"The quantitative particle concentration can give important information about the cleanliness of melts for quality control in primary and secondary production of aluminum. Manual quantification of the particle concentration is normally a time consuming process and human control can bias the acquired images and particle count.The present paper explains the automated image-processing steps for the quantification of SiC-particles, with equivalent diameters from 2 to 25 µm, in solidified A356. A total of 700 micrographs, acquired with a standard white light microscope with 10 x magnification, were analyzed. The applied software (Image Pro-Plus 7.0 from MediaCybemetics®) allows for programming of macros which in tum provides the user with a higher degree of control. The automated results are compared with the results obtained by manually counting the particles in the same micrographs. The impact of the automated results on the estimated filtration efficiency was established to be only -3%.IntroductionInclusions are both indigenous and exogenous particulates that are present in commercial metals such as aluminum. If large individual or large numbers of inclusions are present, they can have a significant negative impact on the appearance, mechanical and chemical behavior of products produced from the metal. Aluminum is known to contain large numbers of inclusions: =50 µm in size, e.g. typically <l ppm by volume or <100,000 inclusions of>20 µm per kg of metal as detectable using a Liquid Metal Cleanliness Analyzer, LiMCA [1]. Depending on the final application of the aluminum, inclusions can render the metal 'not fit for purpose', and result in serious economic consequences to metal producers.It is not surprising that the aluminum industry has developed a number of treatment processes to improve metal cleanliness, given the large number of high value products whose quality can be adversely affected by inclusions. CFFs are the most commonly applied filtration process and have been used to filter >50% of the world production of aluminum since the 1990's [2].Inclusions in aluminum may be particles, bifilms [3] or clusters of: oxides (Al2O3 , SiO2), spinels (MgO· Al2O3), carbides (SiC, Al4C3), nitrides (AlN), borides (TiB2), sulfides, phosphides and intermetallics [ 4]."

Jan 1, 2013

By Ray Y. Lin

Chemical vapor deposition of tungsten carbide on the surface of steel has been investigated at temperatures between 400 and 550C in an atmosphere containing tungsten hexafluoride, hydrogen and benzene. The tungsten fluoride flow rate was maintained at 20 ml/min. The hydrogen flow rate was at 100 ml/min. The benzene concentration varied from 1.15 to 5.56% in the reaction gas. It was observed that the higher the temperature, the faster the deposition rate for tungsten carbide. But the dependence of the deposition rate on the benzene concentration was not systematic. From the x-ray diffraction analysis, it was observed that W, W2C and WC are all presented in the coating. The amount of each phase presented in the coating depends on the temperature and, to a less extent, on the benzene concentration. The microhardness measurement has also been done for all CVD carbide coatings obtained in this study.

Jan 1, 1992

By J. Brent Hiskey, Rebecca Grace Copp

The solvent extraction of yttrium and neodymium from copper pregnant leach solutions (PLS) using Primene JM-T, a primary aliphatic amine, has been studied. Effect of contact time, pH, sulfate concentration, and extractant concentration were investigated using synthetic and actual PLS systems. Standard experimental conditions were 5 minute contact time, pH ~2.5, and 10 % v/v Primene JM-T concentration. Distribution isotherms were constructed for the pure systems and for actual copper leach solutions. Synthetic solutions contained 100 ppm Y and ~75 ppm Nd. Samples of PLS contained 2 - 10 ppm Nd and 14 - 30 ppm Y. Results showed that complete extraction of both yttrium and neodymium occurred within five minutes and at pH values greater than 1. It was also found that sulfate concentration does not inhibit extraction at any concentration. Additionally, the distribution isotherms created show that extraction for these metals can operationally take place in one stage.

Jan 1, 2016

By Haydar Güneş

In this study, a hydrometallurgical process was evaluated for the recovery of Nd from a Nd-Fe-B magnet. Each leaching test was performed at the solid (weight) to liquid (volume) ratio of 1:50 and was mixed at 400 rpm at ambient temperature. The effects of 3 different acids (HCl, HNO3, and H2SO4) on the extraction of Nd were investigated and H2SO4 was found to be more effective than other acid solutions. Under the optimal conditions, pregnant leach solution was produced with H2SO4 for subsequent Nd precipitation testing. Each precipitation test was carried out using 100 mL of feed solution mixed at 600 rpm at 25°C. NaOH and H2C2O4 were used for Nd precipitation. The highest Nd was precipitated as Nd2(C2O4)3, 10H2O with C2H2O4 at 20 min.

By T. J. White

A synthetic Mineral Immobilization Technology (SMITE) has been developed for stabilizing municipal and hazardous waste incinerator ash. Tailored additives are introduced to the ash in a&apos; first stage that pre-stabilizes all the toxic metal components in non-volatile forms. and in a second pyrometallurgical stage, these are converted to insoluble mineral analogues. It has been found that a combination of apatitie. spinal, anhydrite and monazite can immobilize all the ash components at high waste loading and high density. Typically the stabilized products contain in excess of 50 wt% ash and have densities of 2.5- 3.0 g.cc-1. Toxicity Characteristic Leach Procedure (TCLP) testing has demonstrated that the products well satisfy regulatory requirements. The cost of production and disposal of SMITE waste forms in 2-5 less expensive than. convential methods of solidification/stabilization. This paper will describe the principles of SMITE design for ash stabilization, outline the fabrication procedure, and present comprehensive microstructural and chemical data to validate waste form performance.

Jan 1, 1996

By Takeo Fujino, Nobuaki Sato, Yarong Wang, Kohta Yamada

"Ternary mixed sulfides of some transition metals MTS3 (M=Ba, ·Pb, T=Ti, Zr) were synthesized by a relatively low temperature process using sulfur melt. The mixture of starting materials, such as, metals and/or binary sulfides and a large excess of sulfur was reacted in a vacuum-sealed Pyrex or quartz ampoule at 350- 600 °C for one to three weeks. After the reaction, the remaining sulfur was completely removed by a process composed of filtration of sulfur melt and followed dissolution in CS2• The binary sulfides impurities coexisted in the products were removed by rinsing the products in water and acetone. By using the above method, BaTiS3, PbTiS3 and BaZrS3 'Were obtained in pure form. The effect of addition of halides on the yields of these ternary sulfides were also discussed.IntroductionThere have been a vast number of studies on the preparation and physical and /or chemical properties of mixed metal oxides. As is well known, some of such compounds exhibit excellent materials properties, causing them for use in mechanical, electronic, magnetic and chemical devices. Not a few mixed metal sulfides show similar physico-chemical properties to those of the corresponding mixed metal oxides. However, the study of the mixed sulfide crystals is rather sparse mainly due to difficulties in preparing these compounds. In various methods which have been adopted for preparing mixed sulfides, the simplest method would be the solid-solid reaction of the component binary sulfides or elements. However, there are always diffusional constraints with regard to the reactions in solid phases causing it necessary to heat the reactants at sufficiently high temperatures, viz. 800-1200°C. On the other hand, some mixed sulfides are unstable at high temperatures or to change their materials properties due to sulfur nonstoichiometry and structural modification depending on temperature, i.e., synthesis of such compounds needs to be made at lower temperatures. Processing in alkali halide melts is hopeful to overcome the above problems but to obtain the halide melts the temperatures above ~ 600 °C is needed. Low temperature reaction has been carried out for the preparation of Hg1.24TiS4, which was formed by the ·combination of TiS2 and molten Hg metal at 320°C[l]. Reaction of WS2 with LiBH4 melt at 350°C yielded LixWS2[2]. These sophisticated methods, however, can be applied only to the vary special cases."

Jan 1, 2000

By Gennadiy M. Poletayev, Mikhail D. Starostenkov, Alexandra S. Starostenkova

"The process of the combustion synthesis was modeled by computer simulation using the molecular dynamics method. The set of the critical parameters regulating the velocity of the reaction was found from these computer experiments. It was established that the character of structure-energetical transformations at the combustion synthesis in the systems Ni-Al and TiAl depended on the type of boundaries used for the phases delimitation in the bimetal thin films.IntroductionProducing new materials and products, based on the combustion synthesis (CS), is the objective of scientific investigations as one of the most perspective one for industrial applications. But there are several problems connected with theory and experiment. It allows us to forecast the properties of materials. First of all, the main problems are stipulated by structure-energetical transformations taking place at high velocities of the reaction and at high temperatures. It prevents the analyzing of the transformation mechanisms in materials, taking place at microscopic, atomic levels in details.It is evident, that computer simulation allows to decide some problems and to approach to more exact theoretical presentation of structure-energetical reactions taking place at CS. It is known, that the most typical systems, where CS is observed, are bimetals Ni-Al and Ti-Al. The investigation of interphase boundary stability in the systems of Ni-Al and Ni-Fe was made by the method of molecular dynamics in [1]. The bimetal thin film was presented by the packing of atoms in the plane (111) of FCC lattice. It was found that the discrepancy in the sizes of atoms A and B of bimetal was compensated by the formation of 60° top dislocations, set against interphase boundary in the absence of point defects and free volume. The density of top dislocations was proportional to the factor of size discrepancy of atomic components of the bimetal. Diffusional reconstruction of the interphase boundary and areas, situated near it, was observed only at definite concentration of point defects - vacancies, inculcated in the structure of the bimetal at the definite temperature. The atoms of the bimetal component of less size penetrated in the area of the second component with higher velocity. The clusters of intermetallic germs began to form. It led to the growth of the system temperature and acceleration of the process of the diffusional reconstruction of thin film. The following transformations were found: top dislocations splitted into single ones, which climbed from interphase boundary into the zone of more plastic component; the formation of sub grain structures took place."

Jan 1, 2001

By Fatma Arslan

The lateritic nickel ore sample subjected to this experimental study was taken from Çalda ore deposit (Turkey) and contains 1.43% Ni and 0.105% Co. Mineralogical investigations showed that the ore sample contains asbolane, chromite, limonite, hematite, goethite, lepidocrocite, magnetite, serpentine, and clay type minerals together with chalcedon, quartz, calcite, and chlorite. In the acidic leaching experiments, the effects of temperature, acid (H2SO4) concentration, and leaching time on nickel leaching recoveries were investigated. Leaching recovery versus time curves showed a parabolic trend and increasing the temperature shifted that curves to the higher values. The dissolution of nickel from lateritic ore can be explained by a shrinking core model and the apparent activation energy was found as 47.34 kJ/mol in the range given by the literature. The highest Ni and Co leaching efficiencies as 90.2% and 96.8% respectively were obtained at 80°C temperature, 200 g/L H2SO4 concentration, and 8 hours of leaching time.

Jan 1, 2006

By Gretel Parker

In situ Raman spectroscopic investigations of copper iron sulfides in leach solutions have been undertaken. Coupling potentiodynamic techniques to Raman spectroscopy produces a powerful tool for studying mineral surface response to changing conditions, while ESEM and high-vacuum techniques provide complementary ex-situ information on surface structure and composition. Oxidative acid leaching of chalcopyrite at ambient temperature yielded a product with S-S bonds that were shifted from those seen with covellite, with little evidence of elemental sulfur formation. Leaching of chalcopyrite led to non-homogeneous product distribution. Raman spectroscopy was able to identify the products formed on the mineral surfacein situ while leaching was occurring. Raman mapping and imaging demonstrated a surface distribution of the products which can be related to composition and structure changes of the mineral surface. The surface formed on chalcopyrite after anodic oxidation at 0.570 V vs. Ag/AgCl in 0.1 mol dm-3 HCl undergoes laser-induced transformation.

Jan 1, 2003

By F. Sakurai

The enlarged Mitsubishi process in Naoshima has been in steady operation since. May 1991. However, the sulfuric acid plants have been in operation for more than 30 years. The acid plants were modernized between 1999 and 2001 by renewing some of main equipment such as the drying tower and gas heat exchangers, and introducing new technology. At the same time, as an electric energy saving measure, the electric power consumption in the sulfuric acid plant was vastly improved by decreasing the volume of gas treated the installation of low temperature activity catalyst in the 1st pass of the converter and optimization of main gas blower runner. Furthermore, last year, the oxygen plant was replaced and enlarged, and anode production increased from 240,000 to 280,000 tonnes per year with an associated increase of sulfuric acid from 550,000 to 660,000 tonnes per year. This paper describes these recent improvements in the acid plant at Naoshima smelter.

Jan 1, 2002

A study of iron-removal from copper leachate by limestone precipitation followed by direct eltctrowinning of copper has been conducted. The influence of the process parameters: amount of precipitant, contact time, temperature, agitation intensity, solution acidity, and initial iron concentration on iron-removal was investigated. The effects of electrowinning time, cell voltage, solution acidity and temperature on electrowinning of copper were also investigated. The leachate contained 1.20 g/l cu2+ and 7.41 g/l total iron at pH 2.27. After contacting with 14 g/l precipitant for 2 hours, 97.5 % of the iron was attenuated and 98.4 % of the copper was recovered. With the following electrowinning conditions: 3 lead anodes, 3 stainless steel cathodes, 2.5 V, 39.41 A/m2 and 10.7 g/l H2S04, copper recovery-was 98.4 %. Purity of copper powder produced was greater than 99.0 %.

Jan 1, 1999

By Jozef Zmik, Sergey Dobatkin, Martin Fujda, George Raab, Libor Kraus

"The present work, likewise, deals with grain refinement of medium carbon steel AISI 1045 having different initial microstructure resulting from thermal and/or thermomechanical treatment (TM) applied prior severe plastic deformation. In case of TM treated steel, structure refinement was conducted in two steps. Preliminary structure refinement has been achieved due to multistep open die forging process which provided total strain Eef ~ 3. Uniform and fine recrystallized ferrite structure with grain size of the order of 2-5 µm and with nest-like pearlite colonies was obtained. The further grain refinement of steel samples having different initial structure was accomplished during warm Equal Channel Angular Pressing (ECAP) at 400°C. The microstructure development was analyzed in dependence of effective strain introduced ( Eef ~ 2.5 - 4). Employment of this processing route resulted in extensive deformation of ferrite grains where mixture of subgrains and ultrafine grain was found regardless the preliminary treatment of steel. As straining increases the dynamic polygonization and recrystallization became active to form mixture of polygonized subgrains and submicrocrystalline grains having high angle boundaries. The intensive straining and moderate ECAP temperature caused the partial cementite lamellae fragmentation and spheroidization as straining increased. The lamellae cementite spheroidization was more extensive in TM treated steel samples. The deformation behavior of for both steel structural state confirm the strength increase; however the work hardening behavior was modified with respect to initial structure of steel prior SPD processing.IntroductionIn the last years, ultrafine grained materials have attracted considerable research interest because they tend to possess high strength without sacrificing toughness and ductility. Microstructural refinement of steel is usually achieved by alloying and/or by thermomechanical treatment process, which modifies phase transformation. Recently, advancement of severe plastic deformation (SPD) techniques provides another efficient access for grain refinement of metals and alloys. The fabrication of bulk materials with ultrafine grain sizes has attracted a great deal of attention over the past two decades because of the materials' enhanced properties [ 1, 2]. In last decade a worldwide effort in manufacturing process to obtain ultrafine grain structures in steels is persisting."

Jan 1, 2011

By Selvin Yesilay, Munevver Caki, Canbora Bayraktar, Bekir Karasu, Rahmi Imrak

"In this study, the utilization capability of the solid wastes taken from a commercial roof tile and brick factory in Eskisehir of Turkiye has been investigated in the production of stoneware bodies which can be formed by slip casting. At the first stage, X-ray fluorescent (XRF) and X-ray difractometer (XRD) analyses of the wastes were performed. Depending upon the results, a body recipe with an optimum casting concentration was adjusted. The bodies obtained from prepared slips were fired at 1160 oC as glazed and unglazed forms. Then, they were undergone certain tests in order to determine their firing shrinkage values, water absorption levels and optical parameters. To establish what kind of phase formations occurred after firing as a result of waste incorporations into bodies XRD analysis was conducted. Additionally, effects of such a compositional modification on the microstructure of the bodies were examined by a scanning electron microscope (SEM). Consequently, it was concluded that fired roof tile and brick wastes could be evaluated in both glazed and unglazed stoneware bodies. Introduction Stoneware is the general name applied to many wares fired between 1150 and 1300 °C. It has a different and denser structure than those of ceramics produced at lower temperatures. Fired stoneware possesses a lower water absorption value. When matured at a high temperature, it gives a possibility for the use of feldspar as a main ingredient [1-2]. Colors of stoneware can be brown, red, white and most of the times beige. Firing usually takes place in oxidation atmosphere but also reduction can be rarely used. This naturally has an effect on the body colors [3]. Earth, which contains clay minerals, becomes plastic mud when mixed with water, has a capability to be easily shaped and can be hardened without cracking if fired at 900-1000 °C, is referred as one of the brick and tile raw materials [4]. Natural and aesthetic appearances of buildings obtained with brick and tile products, which make them preferable especially for construction sector, are of importance. Because clays being main raw material of that type of productions generally do not exist as pure materials in nature, their usability depends on their mineralogy and impurities they contain [5]."

Jan 1, 2008

By Nicola Baldo, Marco Pasetto

"The paper discusses the results of a laboratory study, aimed to evaluate the suitability of the bottom ash from Municipal Solid Waste Incineration (MSWI), obtained from different Italian plants, to be recycled in the lithic skeleton of bituminous mixtures, for base layers of road and airport pavements. The research involved a preliminary study of the physical and geotechnical properties of the bottom ash by itself; it was followed by a mechanical characterization of the bituminous concretes. The traditional Marshall methodology was used to identify the optimum bitumen content; the mixtures were also mechanically checked by means of the stiffness modulus test, repeated load axial test and fatigue test. Because the requisites for acceptance in the Italian Specifications and Standards have been satisfied and given the positive mechanical performances, it has been verified that the MSWI bottom ash can be used as substitution of the lithic materials in the road bases, also with very high contents (up to 81% on the weight of the aggregate). Introduction The incineration of Municipal Solid Wastes (MSWs) provides for by-products which can be mainly classified as bottom ash and fly ash. The first one, corresponding to the 25% on the weight of the wastes to be incinerated, so resulting the principal product of the process, is mainly composed by Silica (Si), Iron (Fe), Calcium (Ca), Aluminium (Al), Sodium (Na) and Potassium (K) oxides, so presenting a composition similar to that of different natural materials. Its metallic fraction can be recovered; the remaining part is usually stocked in dumping or, less frequently, recycled. Bottom ash can be re-utilised in the construction of new infrastructures, especially in bitumen bounded mixtures, because of the inert properties of the binder which covers the grains with a subtle film, that prevents the release of heavy metals. The paper describes a study aimed to design new bituminous mixes for flexible road and airport pavements, realised with the highest content of 4 types of bottom ashes, deriving from different MSWI plants of the Northern Italy. The ashes will be named as BA1, BA2, BA3, BA4 respectively (the origin cannot be specified)."

Jan 1, 2008

By G Hope, C Young, R. N. Gow

"The presence of enargite (Cu3AsS4) is problematic in gold processing as it is refractory, increasing cyanide and oxygen consumption, and enviromnentally hazardous. Selective leaching and treatment of the arsenic would prove advantageous to conventional gold leaching methods. The reactivity of enargite samples from Montana, US and Quiruvilca, Peru were studied under alkaline conditions, pH range of 8-13, using a cyclic voltammetry corrosion cell setup. Raman spectra of the surface were taken during and after cycling to compare surface species against theoretical predominance diagrams. Under slightly oxidizing conditions, covellite (CuS) peaks were found on the surface in a short matter of time, above - 200m V vs SHE for pH 9-13, suggesting arsenic leaching, but for longer conditioning times, elemental sulfur peaks were also found, which created a passivating surface layer. By operating above pH 12, under reducing conditions, ~-500mV vs SHE, arsenic can be leached as a thioarsenate (AsS4-xOx3-), without sulfur formation.IntroductionEnviromnental limitations on pyrometallurgical processing of arsenic has pushed the desire to process enargite-, Cu3AsS4, bearing concentrates towards a hydrometallurgical solution. Attempts to process can be broken down into two categories - the co-dissolution of arsenic and copper under acidic conditions or the selective leaching of arsenic under basic conditions. The selective leaching of arsenic would preferably leave behind a chalcocite, Cu2S, or covellite, CuS, phase that would be more amenable to conventional processing methods of the copper and gold industries. These methods employ bi- or poly-sulfides to leach arsenic as Assl· [1-4], hypochlorite leaching [5-7], ammoniacal leaching [8] or fine grinding to mechanically activate the enargite surface and increase normally slow reaction kinetics[9]. This study looked into the surface formations of an enargite electrode under alkaline conditions, in a pH range from 8-13, as it cycled from -1000 mV to 1000 mV vs SHE. The understanding of the formations and under what conditions they form will be helpful in further development of any of the aforementioned processes."

Jan 1, 2012

By Beatriz Ribeiro Nogueira, Vijaya Kumar Rangari, Esperidiana A. B. Moura, Anne Chinellat, Arifa Parveen, Angel Visentim Ortiz

"Composite consisting of ethylene vinyl alcohol (EVOH) with short piassava fibers were prepared by extrusion process and their thermal and morphological behavior were investigated. The EVOH reinforced with 5 and 10 % of pi as sa va (Attaleafunifera Mart) fiber particle, based on the percentage weight ratio (wt %), untreated and treated with a commercial silane coupling agent, were prepared and the influence of fiber loading and the effect of chemical treatment on their thermal and morphological behavior were evaluated by SEM, DSC and TG analyses. Melt flow index (MFI) of the composites have been determined to evaluate the effects of fiber reinforcement on dynamic viscoelastic melt of the EVOH. In addition, piassava fibers characterization by SEM, FTIR, and organic and inorganic composition have also been carried out. The SEM results of the composites showed surface micrographs without microvoids and a good distribution, dispersion and compatibility between the fillers and the EVOH matrix. Concerning the piassava fibers characterization, the results showed that piassava has higher lignin content than cellulose and hemicelluloses, and around 0.7 % of ash with 52 % of silica (Si02). This high concentration of silica is consistent with the SEM analysis of the fiber that showed a large amount of ""silica rings"" encrusted on their surface.IntroductionLately, great worldwide interest has arisen in developing new technologies that enable the use of products with less environmental impact. Effort has been put into seeking natural modifier applications, particularly regarding the use of natural fibers. Special attention has been given to the use of natural vegetable fibers, because of the huge variety of species available. Such vegetable fibers are usually referred to as lignocellulosic materials [1]. This work evaluated the effects of piassava (Attalea funifera Mart.) fiber incorporation in an ethylene and vinyl alcohol copolymer (EVOH). The EVOH belongs to a family of copolymers with excellent gas barrier properties and resistance to organic compounds, which allow its application in different segments, from food packaging to gas tanks. However, EVOH is very sensitive to moisture, and in conditions of high humidity its gas barrier properties, thermal and mechanical properties are affected."

Jan 1, 2012

By M. Fafard, R. Ahmed, O. Dion-Martin

"The optimization of aluminum sheet and tube forming needs the use of large strain finite elements software. The precision of the predicted results from those simulations depends mainly on the quality of constitutive law of the material used. In order to improve quality of these simulations, Barlat has suggested a new yield function named YLD2000-2d. This criterion describes the anisotropic behavior of the rolled aluminum plates. This work consists of characterizing the AA5754 alloy and estimating the material parameters needed for the YLD2000-2d criterion in LS-DYNA. In order to get these parameters, various mechanical testing were performed such as bulge and tensile tests. Moreover, the bulge test was also used to obtain an estimation of work hardening curve in large strain condition, up to 50%. The objective of this paper is to share the experimental results of the characterization of AA5754 aluminum alloy.IntroductionResearchers from National Research Council Canada's Aluminium Technology Center (NRCATC) and Aluminium Research Centre - REGAL, are working on aluminium tube hydroforming processes of AA-5754-0 alloy, used in automotive industries. Hydroforming process presents several difficulties such as wall thinning and section changes. In order to control them, some parameters can be set during the process like pressure rate and end feed level [1]. Given the complexity of the parts and the variability of the control parameters, the use of finite element method (FEA), like LS-DYNA, based on large strain theory is thus necessary. The accuracy of predicted results depends mainly on the quality of the constitutive law used to model the behavior of material. FEA results seem to be valid with the von Mises yield criterion used in some cases. But, given the anisotropic properties of the AA-5754 alloy, a more appropriate criterion could be used. The *MAT_ BARLAT YLD2000 shell material criterion, developed by Barlat [2], who's taking into account the anisotropic behaviour, was chosen due to its large flexibility and its good adaptation to particular elastoplastic behavior of aluminum. However, the use of this criterion needs to determine some material parameters by experimental way."

Jan 1, 2013

By Che Xin, Liu Tianlong, Bi Hongyun, Chen Lijia

"High-cycle fatigue experiments were conducted at 800°C in laboratory air for three ferrite stainless steels including 15CrNbTi, 15CrMoNbTi and 18CrNbTi, where the stress ratio of 0.l was adopted. The experimental results show that at 800°C, the fatigue limit of the 15CrMoNbTi steel is the highest, the fatigue limit of the 15CrNbTi steel is slightly lower than that of the 15CrMoNbTi steel, and the fatigue limit of the 18CrNbTi steel is the lowest. At the same maximum stress, the 15CrMoNbTi steel has longer fatigue lives than the 15CrNbTi steel in the low stress area, while the 18CrNbTi steel has the shortest fatigue life. In addition, the observations on the fracture surfaces of fatigue specimens reveal that the fatigue cracks initiate transgranularly at the free surface of the specimens and propagate in a transgranular mode.IntroductionIn modem automotive industry, the manufacturers have paid great efforts to clean exhaust gas and to improve fuel economy. It is thought an effective way to increase the temperature of combustion chamber in automotive engine. And thus, the manifold closed to the engine in automotive exhaust system can suffer high temperature up to approximately 1000°C. Because of their relatively low thermal expansion coefficient, high yield strength at elevated temperature and good fatigue resistance, ferrite stainless steels, especially added with alloying elements such as Mo, Nb and Ti, are increasingly used for automotive exhaust systems [1-3]. In fact, exhaust manifold operated under high frequency vibration and exposed to high temperature exhausting gas also requires good fatigue resistance at elevated temperature. Some studies on the high temperature fatigue characteristics of stainless steel have been documented. It has beeen found that the fatigue limit of four ferrite stainless steels including 409L, 436L, 429EM and 444 (18Cr- 2Mo) reduces significantly with increasing temperature [4, 5]. In the research concerning the effect of a-phase embrittlement on fatigue behavior in a high-chromium ferrite stainless steel, it is noted that the precipitation of brittle a-phase will reduce the crack initiation and growth resistances and result in a decrease in fatigue limit [6]. In this investigation, the high-cycle fatigue behavior of three ferrite stainless steels including 18CrNbTi, 15CrNbTi and 15CrMoNbTi at 800°C have been studied to address the mechanical aspect of high-cycle fatigue behavior for ferrite stainless steels and to provide the theoretical reference for the safe design of automotive exhaust system."

Jan 1, 2013