By L. R. Jackson, W. T. Lankford, K. F. Smith

ComMercial steel sheet is prepared by a combination of hot and cold rolling and annealing. This treatment usually results in more or less pronounced anisotropy. The anisotropy may manifest itself both as preferred orientation and in the manner in which impurities, segregations, and the like, are aligned in the sheet. The type of preferred orientation and the organization of impurities or segregations may affect the elastic moduli, the yield strength, the tensile strength, and almost always the amount of ductility in different directions. In any case, the most important directions concerned in the anisotropy are along the rolling direction, along the width direction, and along the thickness direction. Considerable data exist on the anisot-ropy of sheet steel as demonstrated by conventional tensile tests; however, few attempts have been made to measure the constants of plastic anisotropy and use them to describe the flow of anisotropic sheet under combined stresses. In this paper, evidence is presented indicating that plastic flow in anisotropic sheet can be described by the shear-strain energy flow theory provided that the anisotropy is properly taken into account. Materials Used in the Investigation Table I lists the sheet materials used in this investigation and describes the condition in which materials were tested. Direction, of Tests and Test Methods Two types of tests were run—tensile tests and hydraulic-bulge tests. Characteristic parameters of anisotropy were determined from the tension tests by methods which will be described later. In all cases, the tensile test pieces were cut from the same quarter line and adjacent to the bulge test pieces in the sheet in order to minimize

Jan 1, 1949

By W. J. Babyak

The habit planes for hydride precipitation in large grains of alpha zirconium and Zircaloy-4 were determined in specimens containing 161 and 136 ppm hydrogen, respectively. In zirconium, the hydride platelets precipitated on various pyramidal planes inclined to the basal plane at angles ranging from 10 to 50 deg and 75 to 90 deg. Hydrides were most frequent at inclinations of about 20 deg and 90 deg. In Zircaloy-4, hydride plates were inclined to the basal plane at angles vanging from 5 to 25 deg with the predominant inclinatioiz equal to 12 deg; no platelets were found near the prism plane position. In both zircoinium and Zir-caloy-4, hydrides were principally, but not exclusively, parallel to (1011) type planes. When the Zircaloy-4 gmins were subjected to tension stresses of 12,100 psi and 19,400 psi during hydride precipitation, the hydride habit was unchanged except that precipitation favored those habit planes which were inore nearly perpendicular to the stress direction. The stress-orientatioiz effect increased with the magnitude of the stress. THE hydride habit plane in a zirconium has been determined by several investigators. Langeron and Lehr1 in 1956 found platelets parallel to (1010) slip planes. In 1962, Westlake and Fisher2 confirmed these findings and showed that hydride precipitation on twin planes, as reported by Kunz and Bibb,3 was probably due to incomplete removal of worked metal from specimen surfaces. Secondary habit planes, ( 1011) and (1015), were also found by Westlake and Fisher under particular charging conditions where a hydride layer may have existed at the hydrogenation temperature. Most recently, walters4 and westlake5 again observed the (1010) habit exclusively in zirconium. Louthan and hgermans have reported that hydrides precipitate on various ( 101l ) and (112l) planes positioned 31.5 to 90 deg to the basal plane in Zircaloy-2. The present investigation was concerned with the hydride habit in Zircaloy-4 in relation to that in zirconium and the possible change in habit when precipitation occurs under stress. The latter consideration was prompted by the stress-orientation phenomenon originally reported by Marshall and Louthan.7, 8 I) EXPERIMENTAL Materials and Specimens. Chemical analyses of all materials are given in Table I. The zirconium specimen was a 1 by 4 in. section cut from wrought crystal bar that was hot-rolled at 790°C to 0.300 in. and cold-rolled to a final thickness of 0.095 in. All surfaces were mechanically polished and then chemically polished with a solution of H2O, HNO3, and HF (10:10:l by volume) prior to annealing. Grains as long as 0.25 in. were grown by thermally cycling the specimen three times (in 10-5 mm Hg vacuum) between 825" and 1000°C at approximately 125°C per hr. The specimen was isothermally annealed at 825°C for 24, 40, and 120 hr after each cy-

Jan 1, 1968

By R. A. Nadler and

Specimens of Ti-155A (Ti-5Al-1.3Fe-1.3Cr-1.2Mo), Ti-6Al-4V and Ti-4Al-3Mo-1V were hydrogenated, aged to high strength levels, and subjected to notched stress-rupture tests and tensile tests at two strain rates. Both Ti-6Al-4V and Ti-155A were relatively unaffected by hydrogen in amounts exceeding those found in commercially -produced material. Inconsistencies in the data and a relatively low initial level of ductility prevented an accurate determination of the hydrogen tolerance for aged Ti-4Al-3Mo-1V, but there was no evidence that this alloy was any more susceptible to hydrogen embrittlement than Ti-155A and Ti-6A1-4V. THE metallurgical literature has been considerably enriched in the past five years by the publication of the results of many investigations which were concerned with the effects of hydrogen on titanium and its alloys. Although it is not the authors' intention to provide a complete literature survey of this vast field, it is worthwhile to summarize briefly some of the important factors which influence the embrittling phenomenon in a - B alloys. Some of the influencing factors are those of strain rate, temperature, and composition. Hydrogen embrittlement in a - B titanium alloys is now believed to be a strain-induced phenomenon, and whether or not embrittlement occurs at high hydrogen levels depends largely upon whether sufficient time is available for hydride precipitation. This condition is fulfilled by tensile testing at very slow strain rates or by rupture testing smooth or, preferably, notched specimens over relatively long periods. Conveniently, maximum embrittlement occurs at or near room temperature. The presence B - stabilizing elements, in amounts sufficiently small to prevent an all -B or nearly all -P condition, promotes hydrogen embrittlement and this tendency is believed to be related to the amount of a - B interfacial area present. Aluminum, by increasing the solubility of hydrogen in A titanium, greatly reduces the danger of hydrogen embrittlement, while oxygen has been shown to have detrimental effects.' The preceding discussion is based on experimental work performed on annealed a - P alloys. This early work has shown that annealed Ti-6A1-4V and Ti-155A are relatively insensitive to the embrittling effects of hydrogen.' Although no work has been reported on annealed Ti-4A1-3Mo-lV, the alloy would be expected to exhibit somewhat the same insensitiv-ity as Ti-155A. In sharp contrast to the voluminous literature on annealed titanium alloys is the paucity of reported investigations on materials receiving commercial heat-treatment cycles. To date, the most notable contributions in this field have arisen from two separate investigations on Ti-3Mn-1Fe-1Cr-1V-lMo, the so-called 3Mn comple~. These investigations

Jan 1, 1961

PERSONAL (Members are urged to send in for this column any notes of interest concerning themselves or their fellow-members.) Members and guests who registered at Institute headquarters during the period Oct. 10 to Nov. 10, 1914: Jintaro Kojima, Ashio, Japan. E. R. Hinckley, Seoul, Korea. J. Homer Stover, Trenton, N. J. S. A. Taylor, Pittsburgh, Pa. Kirby Thomas, New York, N. Y. Lawrence Addicks, Douglas, Ariz. Keijiro Nishio, Tokyo, Japan. Noel Cunningham, Bethlehem, Pa. Alexander K. Hamilton, Chicago, Ill. E. C. Vigeon, London, England. Harold N. Lawrie, Portland, Ore. S. E. Fairchild, Jr., Philadelphia, Pa. C. Spence Thomas, Cardiff, Wales. W. C. Schmidt, Jr., New York, N. Y. Henry Tackmann, New York, N. Y. Kenneth C. Browne, New York, N. Y. Dr. David T. Day has resigned his position with the U. S. Geological Survey and opened an office at 1331 F Street, N. W., Washington, D. C., for practice as a consulting engineer.

Jan 12, 1914

By Michael Hoch, Seong Kwan Rhee

The ternary system Zr-Cr-0 was investigated at 1200°, 1500°, and 1700°C. The isotherms at these temperatures were determined by metallographic and X-ray diffraction analysis of carefully selected alloys. AS a part of a series of investigations1-4 of the ternary and quaternary phase diagrams on refractory metals and their compounds, the ternary system Zr-Cr-O was investigated at 1200°, 1500°, and 1'700°C. The binary diagrams Zr-Cr, Zr-O, and Cr-0 as reported by Hansen5 and Levin et a1.' and the existence of a ternary coompound ZrsCrsO (q-carbide structure a. = 11.96A) provided a good base for this investigation of the Zr-Cr-O phase diagram. MATERIALS The materials used and their suppliers were: Zirconium powder, 99.4 pct pure, Charles Hardy, New York; Zirconium dioxide, Fairmount Chemical Co., Newark, N.J.; Chromium powder, 99.85 pct pure, Fairmount Chemical Co., Newark, N.J.; Chromium sesquioxide, 99.86 pct pure, J. T. Baker Chemical Co., Pillipsburg, N.J. Though the materials used were not "hyperpure", the impurities present do not affect the results (lattice parameters, phase boundaries) within the experimental accuracy. EQUIPMENT AND PROCEDURE The detailed procedures and equipment used for this investigation were similar to those described elsewherel' "ith the exception that in this study an induction-heated argon-atmosphere furnace was used. The latter furnace was used to prevent the vaporization of chromium metal in samples in the higher temperature range (above 1200°C). The tungsten crucible was induct ion-heated in a vertical quartz tube filled with argon gas. The quartz tube was 1-1/2 in. in diameter and 10 in. long; it was connected at the top and bottom to water-cooled copper plates. The argon gas of a purity 99.995 pct was further purified by being passed through zirconium metal chips which were maintained at 800°C in a silica tube 1 in. in diameter and 30 in. in length. The furnace was flushed with argon gas for an hour before starting heating; during heating, a slight (3 cm oil) overpressure of argon was maintained in the system. Power was supplied by a 20-kw Ther-Monic Induction Generator. The samples rested on a tungsten-wire basket; the wire basket was connected to a tungsten wire which passed through the tungsten crucible lid, and entered the system on top through a Wilson-type seal. By pulling on the wire, the sample was removed from the crucible and dropped to the water-cooled copper base of the furnace. Because of the presence of argon gas, the cooling of the sample was even more rapid than in the vacuum furnace.' EXPERIMENTAL RESULTS AND DISCUSSION 1) Isothermal Section at 1200°C. The compositions investigated have been numbered within the phase diagram, Fig. 1, and all the pertinent information about the samples can be found in Table I. This table lists the composition of the samples, the phases present in the room-temperature diffraction patterns, the phases detectable in the microstruc-ture, and calculated lattice parameters of the a-zirconium phase. The shapes of the various phase

Jan 1, 1964

By N. Mungan

Laboratory water floods were performed in oil-wet and waterwet alundum and Torpedo cores, displacing a refined oil with n-hexylamine or Triton X-100 solution. Also, some floods were performed in which a sucrose solution was displaced with n-butyl alcohol. The Purpose ot the tests was to see if the oil recotlery could be increased and to examine what role the inter-facial tension reduction and wettability change play in the recovery mechanism. it was found that the chromatographic transport of amine was influenced by core wettability. In oil-wet cores, the rate of advance of the amine band could be predicted from equilibrium chromato-graphy, while in water-wet cores the amine band moved faster than predicted, indicating a non-equilibrium process. By reducing the interfacial tension to 1.1 dyne/ cm, oil recovery was increased. More oil was recovered from Dri-filmed cores than from water-wet cores. Reversing the wettability of the porous media from oil-wet condition also resulted in some additional oil recovery. Neutral wettability floods did not increase oil recovery. INTRODUCTION Interfacial forces in petroleum reservoirs are responsible for retention of large quantities of residual oil. Increasing exploration costs have created an incentive to attempt recovery of this residual oil by new and novel processes. One novel process involves changing the interfacial forces by introducing a chemical into the reservoir during water flooding. Recently, several investigators have carried out laboratory displacement tests using amines. lt3.4 The amines adsorbed onto initially water-wet core surfaces, changing them to oil wet. Additional oil was recovered when the cores were flooded in a manner reversing the. wettability from oil-wet conditions. In all these studies, the wettability reversal was considered responsible for increased oil recoveries although it was noted that amines also reduced oil-water interfacial tension. In the present study, displacement experiments were performed in water-wet and Dri-filmed cores. The purpose was to separate the effects of lowering the interfacial tension from changing the wettability. LABORATORY STUDY All experimental data given in this paper have been obtained at a temperature of 70F + 1 and prevailing atmospheric pressure. FLUIDS AND MATERIALS The oil used in these experiments* was washed with H2S04 and passed through two 100-200 mesh silica-gel beds to remove unsaturates and surface active impurities. Normal hexylamine** of practical purity was used, and the alundum cores*** were composed of nearly pure A1203. Fused quartz (SiOi) and Lucalox (A12 )t plates were used in the contact angle measurements. DISPLACEMENT TESTS Displacement tests were performed in alundum and Torpedo cores. Before displacement runs, cores were acidized with 0.1 normal HCI, flushed with distilled water and fired at 1,200F to make them water wet. This procedure also reduced water sensitivity of the Torpedo cores. Oil-wet cores were prepared from water-wet cores by flowing several pore volumes of 1 per cent by weight Dri-film SC-87 solution in heptane through the cores, flushing the cores with nitrogen, evacuating, and finally heating the cores at 300F for 4 or 5 hours. Between floods, cores were cleaned by conventional procedures and treated again as above.

Jan 1, 1965

Agnico-Eagle Mines Ltd. comprises a Gold Division at Joutel, Quebec, and a Silver Division at Cobalt, Ontario. In 1979 the Silver Division milled 41,700 mt (46,000 st) of ore at a recovered grade of 139 g per mt (4.06 oz per st) for a production of 5,816 kg (187,000 oz) of silver. The 100 -year -old mining, camp of Cobalt has long been noted for its high-grade silver ores, and now seems to be on the threshold of being revived with several companies operating in the area. In 1979, the Gold Division milled at the rate of 27,200 mt per month (30,000 st) and processed 333,000 mt (367,000 st) at a grade of 6.58 g per mt (0.192 oz per st) with a mill recovery of 91.670 to produce 2,013 kg (64,700 oz) of gold. The average total cost per ton milled was $22.10 per mt ($20.05 per st) which was $3.66 per g ($1 13.90 per 0s). These figures make Agnico-Eagle one of the lowest cost producers in North America. Gold occurrence in the Joutel ore is fine-grained and contained within sulfide facies composed mainly of pyrite with minor pyrrhotite. Two underground mining methods are employed with long hole stoping accounting for about 75% of the ore mined and shrinkage stoping the remainder. Ore from underground is hoisted into a 545 mt (600 st) coarse ore bin from where it is conveyed to a 45 mt (50 st) surge bin ahead of the 10-51 Hydrocone crusher. Crushed ore is then screened to make a 13 mm (112 in.) product with the oversize being recrushed in a 7-60 Hydrocone. Mill feed is conveyed to two 900 mt (1,000 st) fine ore bins. The Hydrocones were installed as part of a new crushing plant in March of 1980 and have contributed substantially to an increase in mill capacity. Space has been left to install a third crusher in the future. The fine ore bins discharge to a 2.75 m by 3.66 m (9 ft by 12 ft) rod mill, followed by a 3. 7 m by 5.5 m (12 ft by 18 ft) ball mill in closed circuit with a Krebs 380 mm (15 in.) cyclone to produce a 7070 minus 37 micron (400 mesh) .flotation feed. This pulp is first treated in a 34 cu m (1, 200 cu ft) Maxwell flotation cell and then in an additional twelve 2.8 cu m (100 cu ft) cells. Combined flotation concentrates are reground to 9070 minus 37 microns (400 mesh) in a 1.8 m by 4.9 m (6 ft by 16 ft) ball mill in closed circuit with a single Krebs 254 mrn (10 in.) cyclone. Flotation tailings are sent to the tailings dam. Reground concentrates are then aerated with lime to a single Pachuca and thickened in a 16.75 m (55 ft) diameter thickener with the addition of diesel fuel to render any activated graphite inert to adsorption of

Jan 1, 1981

By H. J. Wasson

With the close of 1932 and the third year of the depression, the activity of oil production presents, amidst the general wreckage and chaos of industrial society, a somewhat unique picture of rationalized economic effort. How long it will continue to present such a picture, however, is a subject for conflicting surmises. East Texas still dominates the contemporary horizon, but it has become, at least for the time being, a definitely known factor. With its 9500 wells it is approximately 90 per cent drilled up. So long as production control obtains, it is merely one important factor of the national oil reserve. Domestic Production The notable new discoveries in the United States were less numerous than for several years. Elsewhere in the world the record is much the same. The Conroe field in Montgomery County, Texas, lying in an intermediate zone that might be classified either as Gulf Coast or East Texas, represents perhaps the single example of a truly major discovery during the year. Elsewhere in Texas the new pool discoveries, about a dozen or so in number, were nearly all in the region known as Southwest Texas. Oklahoma contributed seven or eight new pools of the routine "run-of-mine" caliber, and the opening up of a few deeper oil pays also were of some significance. Continued expansion of the proved and semiproved reserves in Kansas added an important increment to the oil resources of that state. In California not a single new field was added to the roster, though deeper pay zones equivalent to or of greater importance than many new fields in other parts of the country were discovered or indicated. The new deep zone in the Belridge field is considered by some to underlie the prolific Temblor and may thus forecast the widespread distribution of a potentinl oil horizon underlying many San Joaquin Valley fields below the depths thus far exploited. Aside from the routine operations in connection with settled production, the Eastern fields were decidedly inactive. Further new develop-

Jan 1, 1933

By W. A. Backofen, G. Y. Chin, W. F. Hosford

The effect of machine stiffness on discontinuous flow and fracture of the 2024 aluminum alloy was studied in tension at 4.2OK. An increase of machine stiffness was found to decrease the amount of elongation and drop in load during discontinuous flow, thereby postponing fracture to larger strains and higher stresses. The possibility of utilizing stiffened tools in deformation processing to suppress shear fracture originating from unstable flow was indicated. The problem of nucleating discontinuous flow and the role of the effective mass of the system in discontinuous flow were also considered. AT low temperatures the plastic flow of metals is often discontinuous, with sudden load drops and elongations.1,3 Basinski1,4 has presented strong evidence that discontinuous flow, at least in aluminum alloys, occurs under nearly adiabatic conditions. During testing the load may drop suddenly and flow become localized when the thermal softening, due to heat generated in plastic straining, is greater than the strain and strain-rate hardening. This instability criterion is more easily satisfied at low temperatures because 1) the volume specific heat is reduced so that relatively large temperature increases are possible in straining, and 2) the flow stress is relatively temperature-dependent. The important role of adiabatic shear in ductile fracture processes has been emphasized,5-1 and consideration has already been given to the influences of thermal and mechanical properties on the tendency of a material to undergo adiabatic shear.17677 By focusing attention on how the mechanical loading system influences low-temperature discontinuous flow, additional insight into adiabatic shear and its effect on fracture may be gained. EXPERIMENTAL PROCEDURE Because of its low thermal conductivity, the 2024 aluminum alloy exhibits a highly consistent discon- tinuous-flow behavior at 4.2°K and was therefore chosen as the material for study. Machined specimens of 0.113 in. diam and 1.125 in. gage length were solution heat-treated at 490°C for 3 hr, quenched into cold water, and immediately immersed in liquid nitrogen until just before testing. Testing was done at 4.2°K by immersion in liquid helium at a crosshead drive rate of 0.03 in. per min. As normally used (hard-machine basis), the spring constant of the testing machine was k = 25,000 lb per in. By inserting beam springs in series with the specimen, this value could be lowered by a factor of about 100. Details can be found elsewhere.? As a result of variable machine stiffness, the actual strain rate ranged from about 3 x 10 5 to 3 x 10-4 per sec from one test to another, as well as within any one test. However, preliminary tests had established that the tensile curves were not altered significantly by this strain-rate variation. Fig. 1 shows a typical load vs plastic-elongation curve for a solution heat-treated 2024 aluminum alloy specimen pulled in the standard hard machine (k = 25,000 lb per in.) at 4.2"K. The elastic extension has been subtracted. Plastic flow proceeded smoothly from yielding at approximately 22,000 psi (load = 220 lb) to a strain of about 4 pct at which point the flow became discontinuous. The magnitude of the load drops as well as the plastic elongation per drop increased with increasing strain until the specimen finally broke abruptly. The load-elongation behavior of a sample tested with a relatively soft machine under otherwise identical conditions is given in Fig. 2. In general, there

Jan 1, 1964

By Herman Dykstra, R. L. Parsons

A numerical method for solving partial differential equations in steady state fluid flow is described. This method, known as the "relaxation method," has two advantages over analytical methods: (1) practically any problem can be solved, and (2) a solution can be obtained quickly. A disadvautage is that the solution is not general. The method is applied to core analysis and relative permeability measurement to calculate constriction effects and to calculate the true pressure drop measured by a center tap in a Hassler type relative permeability apparatus. Further applications are suggested. INTRODUCTION Many problems in fluid flow cannot be solved analytically because of the nature of the boundary conditions. For many problems, however. an exact answer is not necessary because boundary conditions are not exactly defined or the parameters describing the porous medium are not accurately known. The relaxation method can be used to obtain an approximate answer easily and quickly for the flow of incompressible fluids in porous media. The method can also be used for other types of problems, such as determining the stress in a shaft under load. or the temperature distribution during steady state heat flow. In this discussion only calculations concerned with the flow of fluids in porous media will be considered. The method was introduced by R. V. Southwell in 1935.' THEORY The treatment given here follows that given by Enimons.2 Consider a porous medium to be replaced entirely by a net of tubes of equal length and uniform cross-sectional area as shown in part in Fig. 1. Assume that the net of tubes behaves exactly like the porous medium which it replaces; that is, the net can be made fine enough to reproduce exactly the porous medium. Assume also that Darcy's Law can be used to calculate the flow from one point to another point through these tubes. The flow from point 1 to point 0 is KA . ------ P-P) .......(11 where a is the distance between points: K is the "permeability" of a tube; A is the cross-sectional area of a tube; is the viscosity of the liquid in the porous medium; and (P1 — P0) is the pressure difference between point 1 and point 0. In like manner the flow can be calculated from points 2, 3, and 4 to point 0. The net flow into point 0 is Qo = KA/µa (P1 + P2 + P33 + P4-4P0) . . (2) MB For an incompressible fluid the net flow into point 0 will be zero or, Q. = 0. This says that at point 0 fluid is neither being accumulated nor depleted. 'Therefore. P1 + P2 + P3 + P4 - 4P0 = 0 .... (3) . If. now. with specified boundary conditions. the pressure i.; known at a finite number of points in a given region, as at the points shown in Fig. 1, Equation (3) will be satisfied at every point. If, on the other hand, the pressure is not known, the pressure can be guessed at these points. Then. unless the guess is perfect. Equation (3) will not be satisfied at all of the points. When Equatiol~ (3,) is not satisfietl. let d = P1 + I?, + P, + P, - If' .,....(4) where 6 is an apparent error and is called the residual at point 0. Equation (4) shows how much the pressure guess is in error at point 0 with respect to the surrounding points. A positive residual means that the pressure is too low, and a negative residual means that the pressure is too high. To bring the residual, 6. to zero in order to satisfy Equation (3). it is necessary to make changes in the pressure guesses. Equation (4) shows that a +1 change in Po will change the residual at point 0 by -4. A +1 change in the pressure at any of the four surrounding points will change the residual at point 0 by +l. Thus it can be seen that a change at any point will affect the residual at that point and the four surrounding points. By changing the pressure from point to point, all of the residuals can eventually be brought nearly to zero and the problem will be solved. This procedure is the essence of relaxation methods and is used to relax the residuals so that Equation (3) is satisfied at every point. The procedure can be most easily explained in detail by solving a simple problem. as Southwell says, "To explain every detail of a practical technique is to risk an appearance of complexity and difficulty which may repel the reader. A

Jan 1, 1951

By R. L. Parsons, Herman Dykstra

A numerical method for solving partial differential equations in steady state fluid flow is described. This method, known as the "relaxation method," has two advantages over analytical methods: (1) practically any problem can be solved, and (2) a solution can be obtained quickly. A disadvautage is that the solution is not general. The method is applied to core analysis and relative permeability measurement to calculate constriction effects and to calculate the true pressure drop measured by a center tap in a Hassler type relative permeability apparatus. Further applications are suggested. INTRODUCTION Many problems in fluid flow cannot be solved analytically because of the nature of the boundary conditions. For many problems, however. an exact answer is not necessary because boundary conditions are not exactly defined or the parameters describing the porous medium are not accurately known. The relaxation method can be used to obtain an approximate answer easily and quickly for the flow of incompressible fluids in porous media. The method can also be used for other types of problems, such as determining the stress in a shaft under load. or the temperature distribution during steady state heat flow. In this discussion only calculations concerned with the flow of fluids in porous media will be considered. The method was introduced by R. V. Southwell in 1935.' THEORY The treatment given here follows that given by Enimons.2 Consider a porous medium to be replaced entirely by a net of tubes of equal length and uniform cross-sectional area as shown in part in Fig. 1. Assume that the net of tubes behaves exactly like the porous medium which it replaces; that is, the net can be made fine enough to reproduce exactly the porous medium. Assume also that Darcy's Law can be used to calculate the flow from one point to another point through these tubes. The flow from point 1 to point 0 is KA . ------ P-P) .......(11 where a is the distance between points: K is the "permeability" of a tube; A is the cross-sectional area of a tube; is the viscosity of the liquid in the porous medium; and (P1 — P0) is the pressure difference between point 1 and point 0. In like manner the flow can be calculated from points 2, 3, and 4 to point 0. The net flow into point 0 is Qo = KA/µa (P1 + P2 + P33 + P4-4P0) . . (2) MB For an incompressible fluid the net flow into point 0 will be zero or, Q. = 0. This says that at point 0 fluid is neither being accumulated nor depleted. 'Therefore. P1 + P2 + P3 + P4 - 4P0 = 0 .... (3) . If. now. with specified boundary conditions. the pressure i.; known at a finite number of points in a given region, as at the points shown in Fig. 1, Equation (3) will be satisfied at every point. If, on the other hand, the pressure is not known, the pressure can be guessed at these points. Then. unless the guess is perfect. Equation (3) will not be satisfied at all of the points. When Equatiol~ (3,) is not satisfietl. let d = P1 + I?, + P, + P, - If' .,....(4) where 6 is an apparent error and is called the residual at point 0. Equation (4) shows how much the pressure guess is in error at point 0 with respect to the surrounding points. A positive residual means that the pressure is too low, and a negative residual means that the pressure is too high. To bring the residual, 6. to zero in order to satisfy Equation (3). it is necessary to make changes in the pressure guesses. Equation (4) shows that a +1 change in Po will change the residual at point 0 by -4. A +1 change in the pressure at any of the four surrounding points will change the residual at point 0 by +l. Thus it can be seen that a change at any point will affect the residual at that point and the four surrounding points. By changing the pressure from point to point, all of the residuals can eventually be brought nearly to zero and the problem will be solved. This procedure is the essence of relaxation methods and is used to relax the residuals so that Equation (3) is satisfied at every point. The procedure can be most easily explained in detail by solving a simple problem. as Southwell says, "To explain every detail of a practical technique is to risk an appearance of complexity and difficulty which may repel the reader. A

Jan 1, 1951

By John Greenawalt

IN view of the increasing importance of sintering in the beneficiation of iron ores preparatory to their reduction in the blast furnace, the writer believes the time is opportune for an up-to-date, though brief, discussion of the general principles of sintering, as well as a discussion of some of the recent improvements and mechanical developments that have been achieved in this industry, its present trend and future possibilities. Sintering may be defined as the agglomeration of fine mineral particles into a porous mass by incipient fusion caused by heat produced by com-bustion within the mass itself. Its first successful application, in connec-tion with the treatment of lead sulphide ores, was known as blast roasting. In this process the lead ore was given a preliminary roasting in a reverber-atory furnace, then the incandescent mass was placed in a pot with a grate and an updraft was applied. It was soon discovered that much better results were obtained by cooling the ore, moistening it, and placing it upon an incandescent layer of fuel previously placed upon a grate, and then applying the updraft blast of air until the charge was converted into a more or less agglomerated mass. The fuel was sulphur and the process one of desulphurization, which was the principal result desired. The application of downdraft to blast roasting brought about tremen-dous results; the principal one of which was that an air blast of high pressure could be passed through a layer of ore deposited on a grate, or on a grate covered by a layer of coarse porous material, without disturbing the particles of which the layer is composed. The air current is compelled to filter through the pores of the charge, whereas if the same pressure applied to the top surface of the charge with downdraft were applied to the bottom of the charge with updraft, the charge would be completely blown off the grate. Another result of reversing the draft was that a flame could readily be applied to the top surface of the charge for ignit-ing purposes.

Jan 1, 1938

By A. R. Jr. Amos

LOG washers have been used for many years in the washing of clay iron ores, phosphate rock and manganese ores, but not until the past 15 years have they been employed to any extent in the preparation of aggregate materials and fluxing stone. For a machine of such importance where tenacious clay or soft rock must be eliminated, there are few data generally available. The purpose of this paper is to set forth the results obtained from several operations, together with a few suggestions for planning a specific installation. Where the material to be washed out consists of loose surface soil, silt, or small amounts of quickly soluble clay, there is little competition with other forms of washers, because greater power and maintenance are required for the operation of log washers, but where the foreign matter is a stiff clay, such as occurs with high-calcium limestones and in marginal gravel deposits, the ability of other kinds of washers to eliminate com-pletely the hard clay balls is at least uncertain. Then the log washer comes into its own field, for with the breaking and churning action of the logs it will clean out the toughest clay. Even with material from the hydraulic dredge, if it contains tough clay, the log washer is desirable unless the gravel is subjected to a costly soaking and rehandling process. Recently there has been a considerable development in other types of machines to accomplish these results but it is not within the scope of this paper to make comparisons between competitive types, but to present the best obtainable data on log washers only. From the primitive design that gave it its name, a long log hewn from a tree, with paddles forged to shape from strap iron and attached by lag screws, the log washer has gradually been developed to the present all-steel type. As now manufactured, the log washer consists essentially of two built-up logs on which are mounted a series of paddles, carried by shafts fitted at the ends of the logs on bearings fastened outside the enclosing steel box, or trough, which is set at an angle of about 5° to 10° and into which the material is fed. Stuffing boxes at the places where the shafts pass through the box at the lower end are equipped with water-

Jan 1, 1936

By Donald Barton

THIS paper outlines a time-saving graphical method of calculation for application to the interpretation of observations with the Eötvös torsion balance. Preliminary to the treatment of this short cut method which has been found practicable, the principal formu-las by which the student of interpretation can calculate the gradient and differential curvature produced by different types of bodies in different types of situa-tions are presented and discussed. It is necessary to split most geologic bodies into a series of simpler ones for which not too complicated formulas are avail-able. The gradient and differential curvature effects are calculated for each of the simple bodies and then summed to the total effect for the whole body. The calculations are considerable in number and, though more tedious than difficult, should be' entrusted to an experienced calculator. Considerable facility in qualitative interpretation can be acquired by the geophysicist from experience and from a thorough study of the types of gradient and differential curvature anomalies produced by the dif-ferent types of possible structural situations. How-ever, semi-quantitative calculations' of the probable structure bring out many relations that are not evident in a simple inspection of torsion balance results ; it throws out as impossible or improbable certain of the alternative structural possibilities that may seem equally probable under simple inspection of the results; it will determine more accurately the position of the crest of the structure; and reduce considerably the un-certainty in the interpretation and it is necessary to intelligent interpretations. The calculation of such cross-sections consists of a trial-and-error calculation of a body that will give gradient and differential curvature effects as closely as possible the same as those observed. From his knowledge of the gradient and differential curvature produced by different types of bodies, the geophysicist sketches a tentative cross-section of the structure as indicated-to him-by the observed results of the torsion balance survey, and the calculator then splits the struc-ture into blocks, and calculates the gradient and differ-ential curvature block by block. If, as rather usual, the calculated .gradient and differential curvature pro-files diverge considerably from, the respective observed ones, it is necessary to add and subtract blocks from the cross-section until a close agreement is obtained .between the calculated and observed profiles. The com-plete calculations have to be gone through for each block that is added or subtracted.

Jan 9, 1928

By A. R. Jr. Amos

LOG washers have been used for many years in the washing of clay iron ores, phosphate rock and manganese ores, but not until the past 15 years have they been employed to any extent in the preparation of aggregate materials and fluxing stone. For a machine of such importance where tenacious clay or soft rock must be eliminated, there are few data generally available. The purpose of this paper is to set forth the results obtained from several operations, together with a few suggestions for planning a specific installation. Where the material to be washed out consists of loose surface soil, silt, or small amounts of quickly soluble clay, there is little competition with other forms of washers, because greater power and maintenance are required for the operation of log washers, but where the foreign matter is a stiff clay, such as occurs with high-calcium limestones and in marginal gravel deposits, the ability of other kinds of washers to eliminate com-pletely the hard clay balls is at least uncertain. Then the log washer comes into its own field, for with the breaking and churning action of the logs it will clean out the toughest clay. Even with material from the hydraulic dredge, if it contains tough clay, the log washer is desirable unless the gravel is subjected to a costly soaking and rehandling process. Recently there has been a considerable development in other types of machines to accomplish these results but it is not within the scope of this paper to make comparisons between competitive types, but to present the best obtainable data on log washers only. From the primitive design that gave it its name, a long log hewn from a tree, with paddles forged to shape from strap iron and attached by lag screws, the log washer has gradually been developed to the present all-steel type. As now manufactured, the log washer consists essentially of two built-up logs on which are mounted a series of paddles, carried by shafts fitted at the ends of the logs on bearings fastened outside the enclosing steel box, or trough, which is set at an angle of about 5° to 10° and into which the material is fed. Stuffing boxes at the places where the shafts pass through the box at the lower end are equipped with water-

Jan 1, 1936

By Henry Fernald

THE accounting system or bookkeeping methods of any company are principally the concern of that company and of those who are in control of its affairs. Its published financial report is, however, primarily intended for those who are not already fully informed regarding its operations and finances. Whatever may be the advantages of standardization of accounting and bookkeeping methods, it must be admitted that a company has a certain right to handle its accounts and keep its books and records in whatever manner may seem to it best adapted to its affairs, even though such methods may differ materially from those generally adopted by others. In its financial reports it should not, however, either ask or expect that the statements it makes or the terms which it uses will be given in its case a meaning and interpretation different from that which they are ordinarily considered to have in similar reports and statements of other companies. The particular form and arrangement of such reports is a matter concerning which there may be much difference of opinion. It is of little importance whether current assets come first or last in the Balance Sheet, but it is important that there should not be included under this designation any items which are not properly current assets within the generally accepted meaning of that term. The extent to which stockholders or others interested are to be made acquainted with the full details of a company's business is a question which the proper authorities must in each case decide. It should, however, be recognized that there are certain facts regarding a mining com-pany which must be set forth in a financial statement if it is fully to cover the conditions and affairs of the company. For example, a financial, statement which does not include or is not accompanied by a statement, of the ore reserves of the company does not fully set forth its financial condition. This is true whether the absence of such a statement of ore reserves is because it is not desired to make public the figures or whether it is because the ore reserves themselves are not definitely known, or accurately measured.

Jan 1, 1928

By P. W. Gilles, B. D. Pollock

THE pioneering work of Steinitz1 and Steinitz, Binder, and Moskowitz2 has shown conclusively the existence at high temperature of two additional phases in the molybdenum-boron system and thus brings to a total of six the number of structures appearing in this system. To the structures Mo2B, MOB, and Mo2B5 they have added MO3B2, a new -MOB form, and have shown that MOB,, which has the same range of composition as Mo2B5, is only a high temperature structure of the latter. This solid solution, interestingly enough, includes neither of the compositions corresponding to the stoichiomet-ric compounds, MOB, or Mo2B5, but rather at all temperatures has intermediate values of composition. These workers have also, in the course of their work, measured melting points, transition temperatures, eutectic and peritectic points in the system and have shown that Mo3B2, because of its dispro-portionation at low temperature to Mo2B and MOB, is stable only in a limited high temperature range. During the course of the present work on the vaporization properties of the molybdenum-boron compounds, a few transition temperatures were observed. When the report of the other workers appeared, it was decided to repeat, in part, their study of the system. As a result, considerable evidence has been obtained that substantiates the specific kinds of melting processes they report as well as the general features of their diagram. However, a marked difference was found between the temperatures they report and the ones observed in this study, with the latter being higher. The purposes of this paper are to present the evidence obtained in this laboratory that verifies their diagram of the system, to give some important temperatures in the system, to compare them with those previously published, and to seek an explanation of the difference. Samples The metal starting material was 400 mesh molybdenum powder with a purity stated by the manufacturer to be 99.9 pct. The initial treatment, designed to remove volatile contamination, consisted of heating in a vacuum for 10 min to a temperature of from 800" to 1000°C during which a loss of 0.3 to 0.4 pct occurred. An assay following this treatment showed it to be 99.4 pct pure, with the principal impurity probably being oxygen. The boron starting material was obtained from the Cooper Metallurgical Laboratories and the Fair-mount Chemical Co. as 325 mesh powder with manufacturers' analyses of 99 pct or better. Initial treatment consisted of heating in molybdenum in a vacuum at about 1700°C for 10 min. During this time a loss of 3.5 pct occurred. An assay following this treatment showed the different samples to have purities ranging from 95.5 to 99.0 pct with iron and carbon as the principal impurities. Following the initial treatment, the elements were combined to form stocks of Mo2B and MOB by heating pressed mixtures in a vacuum to 1100" to 1200°C to accomplish reaction and to 1500" to 1900°C for a few minutes to evaporate the more volatile impurities. Analysis of the two compounds for boron by a modification of the method of Blumenthal3 and for molybdenum by the lead-molybdate method indicated them to have purities greater than 99 pct. The individual samples to be studied had compositions in the Mo2B-MOB range and consisted of mixtures of the stock compounds. Procedure As is usually the case in high temperature work the selection of containers for the samples posed some problems. For vapor pressure studies tantalum crucibles, allowing little contact with the pressed samples, were used and some of the observations made during these experiments are pertinent to the study of the phase diagram. Most of the experiments, however, were performed in graphite containers, as were those of the previous authors. Two kinds of spectroscopic grade graphite crucibles were used. One was a % in. cylinder, 3/4 in. high, containing seven 3/16 in. holes drilled 1/2 in. deep into which were packed samples of the different mixtures weighing 250 to 500 milligrams. The other, consisting of separate crucibles, was prepared by drilling 3/16 in. holes, 1/2 in. deep into 1/4 in. graphite rods % in. long. The 7/8 in. cylinder was heated directly by induction while the small crucibles were packed in a tantalum heating element for induction heating. All heating was done in a high vacuum system in which the pressure was generally less than 1x10-5mm and never rose above 2x10-5mm when the samples were hot. The general pattern of the heating in graphite was to heat rapidly to a temperature somewhat below the desired one, then to raise the temperature slowly. The samples were held for 2 to 5 min at the maximum temperature, which in all cases was far higher than that needed to produce reaction. The short time was employed to reduce possible contamination by the crucible material and to reduce composition changes that would occur because of vaporization. After examination following the heating, the samples were reheated to a higher temperature. Temperatures were measured with a Leeds and Northrup disappearing filament optical pyrometer, certified by the National Bureau of Standards, by sighting through a window at the top of the vacuum

Jan 1, 1954

By J. L. Huitt, B. B. McGlothlin

The introduction of new fracture propping agents that are brittle but much stronger than sand created the problem of what loading strength is required for a propping agent to be effective in a given formation. It is shown that the load at which the propping agent crushes should exceed the load at which total embedment in the fracture faces is possible. Simple laboratory tests to determine loading strength of the propping agent and embedment in the fracture faces, and use of these data in selecting a propping agent for a given formation, are discussed. INTRODUCTION One of the most important factors in the design of hydraulic fracturing treatments is the selection of a propping agent that can effectively provide the fracture flow capacity needed for stimulation of a well. Sand, once generally accepted as being synonymous with propping agent in hydraulic fracturing, is now recognized as having limited effectiveness in many formations because of its low resistance to crushing. Sand particles are brittle and have relatively low strength. Because of this property, sand particles are crushed in rocks that offer high resistance to the penetration of fracture faces by the proppant particles when the fracture attempts to close under the action of the overburden load. For rocks that offer a high resistance to penetration, deform able particles are more effective propping agents than sand. However, for this same type of rock, a propping agent that does not deform, yet does not crush, is often more effective. Thus, a rigid propping agent with sufficient strength to prevent crushing is desirable. A method for determining the strength required for a rigid propping agent to function effectively in given formations is discussed. BEHAVIOR OF RIGID PROPPANTS AND FRACTURE FACES RELATED STUDIES An early qualitative description of the reaction of propping sand in fractures was given by Hassebroek et al.' In discussing fracturing in deep wells, the authors mentioned that even though propping sand entered the fractures, a high flow capacity did not result due to crushing or embedding of the propping sand. Dehlinger et al.2 in discussing the reaction of propping sand surmised that, because of the hardness of sand particles, deformation occurred in the fracture faces contacting the propping sand. In later studies,3,4 methods of determining the embedment of propping sand in fracture faces of soft rock and the critical load at which propping sand is crushed by the fracture faces in hard rock were discussed. In working with de-formable proppants, Kern et al. considered proppant particles to be deformed into cylindrical disks by action of the overburden and then pressed slightly into the fracture faces by further action of the overburden. Rixie et al.'0 reported on embedment pressure and presented a method of selecting a propping agent for use in given formations. The propping agents included sand, walnut shells and aluminum pellets. All these studies have contributed materially to a better understanding of propping agent behavior; however, the strength of brittle proppants (sand, glass and ceramics) required to result in embedment rather than crushing has not been discussed. This topic will be covered in the ensuing discussion. PROPPANT PARTICLE CRUSHING—-EMBEDMENT For this discussion, a rigid propping agent is considered to be one that is brittle and fails under tensile stress when loaded to a critical value. In an earlier study4 it was shown that the Hertzian4 loading theory could be applied to a spherical brittle propping agent if the propping agent and fracture faces behaved elastically. At the failure of the proppant, the ratio of the load to the square of the diameter of the particle should be constant for a given material combination, or: Lc/dp2=C ............(1) A partial derivation of this equation from proppant and formation properties is included in the Appendix. Should a rigid particle not be crushed as a load is applied, it embeds in the fracture faces. A study3 of particle embedment in fracture surfaces has been published. The embedment can be described by an equation based on Meyer's metal penetration hardness relationships: d1/dp=B 1/2[L/dp2]m/2..........(2) In Eq. 2, B and m are constants that are characteristic of the rock; the significance of the other terms is shown in Fig. 1. A STANDARD DEFINITION FOR PROPPANT LOADING STRENGTH Eq. 1 is useful in appraising propping agent strength," but it is strictly applicable only when the area of contact between a particle and a fracture face (or loading plate)

Jan 1, 1967

By Alfred Weiss

The Daniel C. Jackling Award, established in 1953, is presented for significant contributions to technical programs in mining, geology, and geophysics. This year's recipient, Alfred Weiss, was cited "For his pioneering achievements in applying systems analysis, operations research, and computer methods in exploration, mining, and environmental control; and in disseminating the new technology to the worldwide mining community; and for his lecture, “New Concepts and Tools in Decision-Making.”

Jan 1, 1979

By R. G. Wheeler, J. W. Goffard

The Larson-Miller parameter was used to correlate time, temperature, and indentation creep of magnesium, aluminum, and some of their alloys. In the temperature range 300" to 450°C, the short-time Meyer hardness of pure magnesium was less than that of the magnesium alloys tested, but for long times the pure magnesium has greater indentation creep resistance. Aluminum (1100 alloy) had 1.5 to 2.5 times more indentation creep resistance than magnesium at 300" and 450oC, respectively. Hardening of aluminum with a dispersion of Al2O3 was effective in the time and temperature ranges studied. New technologies have required the development of new materials and the utilization of the more familiar materials for new and unusual applications. The use of magnesium and aluminum and some of their alloys, because of their desirable nuclear characteristics, light weight, low cost, and ready availability, has been extended to the 300" to 450°C temperature range. In this temperature range the basic consideration of these materials must be their rate of plastic flow rather than offset yield strengths. The indentation testing reported here arose from a need for design data for the load-holding ability of supports made of these materials. Test Procedure—Hardness indents were made with a 0.275-in.-diam quartz indentor and a 10.65-lb load. The indentor was made by fire-polishing a spherical surface on the end of a fused quartz rod. The samples were held at temperature in a graphite crucible controlled to ±2°C. A thermocouple was attached to the sample and test temperatures were recorded. The diameter of the spherical indentation was measured at the end of a test period and the compression stress (Meyer Hardness) was determined by: H___________load__________ m = projected area of indent Samples were 1 in. in diam and at least 1/4 in. thick. It was observed that at the higher temperatures and longer times, the quartz indentor would stick to the magnesium sample. The quartz indentor was, therefore, frequently inspected and fire-polishing repeated when necessary. The area of sticking was always a small fraction of the area of indent and was therefore considered to have an insignificant effect on results. Correlation of Hot-Indentation Test Data with Time-Temperature Parameter—Sherby and Dorn' have correlated creep or tensile data of a' solid solutions of aluminum with a temperature and strain-rate parameter suggested by Zener and Holloman. underwood2 used this parameter to correlate creep properties of some steels with hot hardness, and upon the basis of this correlation a means of obtaining creep properties from short-time (and inexpensive) hot hardness tests has been demonstrated. Since the validity of the correlation of creep properties with a time-temperature parameter and the correlation of creep properties with hot hardness have been shown, it follows that hot hardness may correlate with the time-temperature parameter. The hot-indentation data obtained was expressed as Meyer hardness, and was shown to be time and temperature dependent. Correlation of Meyer hardness, time, and temperature with the parameter was made using the relationship: Hm = Meyer hardness t = time, hours T = absolute temperature, OK K = constant A value for the constant K was calculated by equating In l/t + K/T at different temperatures and times but at the same hardness. The correlation was tested by plotting Hm vs the parameter, In 1/t +K/T. Since materials are being sought which have high hardness at low indentation creep, i.e., a high Meyer hardness for long time at high temperatures, low values of the parameter are ofthe most interest. TEST RESULTS Magnesium—Pure magnesium (99.98 pct) cut from extruded rod was indentation tested perpendicular to the rod axis at temperatures of 300°, 350°, 400°, and 450°C for times ranging from 6 sec to 112 hr. Fig. 1 shows the time dependency of Meyer hardness at the four constant temperatures. Fig. 2 shows the correlation of the Meyer hardness of pure magnesium with the time-temperature parameter using a K of 22,720 in Eq. [I]. At the bottom of Fig. 2, the effect of doubling the time of indentation t2 = 2(t1), on the abscissa for any time is shown graphically. This effect is of constant magnitude. Also shown graphically are the magnitudes of the effects on the