By Baozhong Ma, Yonggang Wei, Shiwei Zhou, Bo Li, Chengyan Wang, Hua Wang

The effects of additives with Na2S, Na2SO4 and CaSO4 on phase transformation of nickel laterite ore in low-temperature reduction roasting process using carbon monoxide were investigated. The results showed that diffraction peaks of forsterite increased with increasing reduction temperature for 30min with the addition of 10wt% Na2SO4 and 50vol% CO, and diffraction peaks of forsterite increased with increasing the content of Na2SO4 at 900°C for 30min. Comparing the above three additives, phase transformation of nickel laterite ore were strongly influenced with the addition of 10 wt% Na2SO4 and 10 wt% Na2S. Calcium sulphide from the thermal decomposition of CaSO4 was carried out in the reaction product. SEM-EDS analysis result deduced that increasing the dosage of Na2SO4 from 10wt% to 15wt% could promote the polymerization of ferronickel and improve the grade of nickel in ferronickel.

Jan 1, 2015

By Makoto Ohlsuka

The ternary Ni2MnGa intermetallic compound is an intelligent material which has both a ferromagnetic property and a shape memory effect (SME). The use of the shape memory alloy films for an actuator of micro-machines is very attractive because of its large recovery force. The purpose of the present study is to investigate the effects of fabrication conditions and to clarify the relationships between these properties and fabrication conditions of the Ni-Mn-Ga films. The Ni-Mn-Ga films with a thickness of nearly 5 um were deposited with a radio-frequency magnetron sputtering apparatus using a Ni50Mn25Ga25 or Ni52Mn24Ga24 target. They were heat-treated at various temperatures between 873 and 1273 K for homogenization and ordering and then cooled in a furnace. The composition of the films depended on the sputtering power. The as-deposited films were crystalline and had columnar grains. After the heat treatment the grains widened and the grain boundary became indistinct with the increasing heat treatment temperature. The martensitic transformation temperature of the heat-treated films increased with increasing nickel content. Furthermore the effect of plastic deformation and constraint aging on SME is also investigated. After plastic deformation, the two-way SME was shown through the martensitie transformation and its reversion, The intensity of X-ray diffraction peaks from stress-induced martensitie phase was found. The constraint-aged films also showed the two-way 3ME by thermal cycling.

Jan 1, 2003

By Tao Xuea

Gold frequently occurs in nature in the form of a gold-silver alloy. Thus, investigation of the electrochemical behavior of gold-silver alloys in cyanide solution has practical significance. In this paper, the potentiodynamic method is used to determine the anodic polarization curves of gold-silver alloys (Au-10% Ag and Au-50% Ag) in cyanide solutions. To facilitate the interpretation of the results, complementary experiments conducted in NaOH solution in the absence of cyanide are also reported. The results for the Au-Ag alloys are compared with the polarization behavior of pure gold and pure silver. With the aid of potential-pH diagrams for the Au- and Ag-CN-H20 systems and electrochemical kinetics concepts, the dissolution mechanism of gold-silver alloys, the effect of the presence of silver on the cyanidation of gold, as well as the factors which control the anodic reaction rate are clarified.

Jan 1, 1998

By Suchun Zhang

The alkaline oxidation of refractory gold concentrates containing arsenopyrite and pyrite at ambient temperatures and pressures has been found to be accompanied by the simultaneous dissolution of gold without the addition of cyanide. A detailed study has been made of the kinetics of the oxidation of the pure minerals and of several concentrates. The reaction products of the oxidation of arsenic and sulphur have been monitored using chromatographic techniques. In the case of arsenopyrite, thiosulfate, monothioarsenate, arsenate and sulfite are the principal products while thiosulfate has been confirmed to be the dominant product of pyrite oxidation. Gold, either as added powder or as a constituent of the concentrates has been found to dissolve simultaneously during the alkaline oxidation of both arsenopyrite and pyrite, and this appears to be associated with the in-situ formation of thiosulfate as a lixiviant. The effects of temperature, stirring speed, oxygen partial pressure, alkalinity and pulp density on the oxidation of arsenopyrite and the dissolution of gold have also been investigated. Keywords: Gold, dissolution, arsenopyrite, pyrite, alkaline, oxidation, thiosulfate, thioarsenate

Jan 1, 2005

By P. Lussiez

Precipitates consisting of amorphous ferrihydrite and crystalline goethite have been prepared by aging hydrolyzed Fe (III) solutions at room temperature. The precipitates have been characterized by x-ray diffraction and differential thermal analysis. The amorphous ferrihydrite transforms to goethite with time. The ferrihydrite to goethite transformation is affected by the presence of small amounts of copper or nickel coprecipitated with the iron. .The addition of copper decreases the amount of goethite at a given aging time and increases the amount of coprecipitate which is initially dissolved in sulfuric acid, but it does not seem to affect the dissolution of the crystalline part'. It is proposed that adsorption of copper hydroxo species on goethite nuclei delays the ferrihydrite to goethite transformation. The effect of nickel is less dramatic than that of copper. Apparently a portion of the added nickel is adsorbed on the goethite crystallite surface rather than incorporated into the goethite lattice.

Jan 1, 1981

By W. Gutmannsbauer

Thin films of TiO2 nanoparticles have been prepared by different reactive deposition methods, such as electron evaporation, ion plating and ion beam sputtering. Many properties especially the optical properties, are strongly related to the film morphology and surface roughness. Scanning force microscopy was employed to obtain information on the surface structure of as-deposited Ti(h thin films. The influence of the deposition conditions and the film thickness on the optical and structural properties has been investigated. The as-deposited films were found to be amorphous or polycrystalline with anatase structure.

Jan 1, 1995

By I. Gaballah

Decontamination of synthetic solutions of copper acetate, chloride, nitrate and sulfate containing 10, 100 and 1000 ppm of copper, using chemically treated barks has been studied. Metal percent removal from solutions depends on the pH and the initial concentration and to some extent on the salt used. It varies from 40 to 99 % of the solution initial metallic ion's content. The maximum retention capacity of the treated bark varies from 31 to 43 mg of Cu per gram of dry modified bark. Bark loaded with copper had been analysed by Scanning Electron Microscopy and lnfra Red spectroscopy. Cu is uniformally distributed in the bulk of the bark. No copper segregation is observed. It seems that copper is bound to the acidic sites of the bark. Anions are not detected on the copper loaded bark neither with the SEM or with the IR spectroscopy.

Jan 1, 1993

By M. D. Stephens

A new, one-step process for extracting titanium from titaniferrous materials has been demonstrated. In the process, depleted uranium tetrafluoride (DUF 4), a solid, is mixed with ilmenite (FeTi03) and heated to 900°C. Titanium is extracted in the vapor phase as titanium tetrafluoride (TiF4) and the DUF4 is converted to uranium-iron oxide. The process has been found to selectively fluorinate the titanium in ilmenite and is capable of producing high purity TiF 4 with very low iron content. TiF 4 can be collected by condensation or through reaction with a fluoride salt such as NH4F, KF, or NaF. The TiF4 produced from the process can be used to make titanium metal, titanium oxide, or fluorotitanate compounds. Since the fluorination process is highly selective for titanium, it avoids many of the separations and waste issues common to other titanium extraction processes.

Jan 1, 2001

By Dietrich Gross

This paper describes an advanced oxy-fuel combustion technology for re-melting aluminum that significantly reduces energy consumption and emissions. This oxy-fuel combustion technology developed by Jupiter Oxygen is a patented process for combustion of fossil fuels with pure oxygen while excluding air, thereby creating an undiluted high flame temperature and increased efficiency for process heating in industrial furnaces. This unique process has led to improved heat transfer and longer residence time while maintaining the same process temperatures as with air combustion. The energy efficient combustion process allows aluminum companies to operate at a substantially lower cost due to a dramatic fuel savings of up to 70% for natural gas and waste oil (1). The results of more than 10 years of day-to-day experience utilizing the Jupiter Oxygen Corporation oxy-fuel combustion technology licensed to Jupiter Aluminum Corporation in the aluminum re-melting business are discussed.

Jan 1, 2008

By Shengqi Chen

The reduction smelting of nickel laterites produces slag, consisting principally of the chemical components MgO, "FeO", SiO2, and A12O3, and ferro-nickel alloy. Despite the fact that the phase equilibria for the ternary MgO-"FeO"-SiO2 up to 1500°C is well established limited experimental data are available in the MgO-"FeO"-SiO2-Al2O3 system, which is relevant to commercial operation of the process. A methodology has been developed for the experimental investigation of the liquidus temperatures for the multi-component system MgO-"FeO"-SiO2-Al2O3-Cr2O3 in equilibrium with metallic iron. Experiments have been carried out using high temperature equilibration, quenching, followed by electron probe X-ray microanalysis (EPMA). Liquidus temperatures have been determined in the silica primary phase field in the composition ranges directly relevant to the Cerro Matoso S.A. ferro-nickel smelting slag. Liquidus isotherms have been determined for temperatures between 1450 to 1600°C. The study enables the liquidus to be described for a range of MgO/FeO ratios. It was found that liquidus temperatures in the silica primary phase field decrease significantly with the addition of AI2O3. Keywords: Liquidus temperature, ferro-nickel, pyrometallurgy, smelting

Jan 1, 2004

By Michael Zinigrad

The quality of metallic materials depends on their composition and structure and these are determined by various physico-chemical and technological factors. To effectively prepare materials with required composition, structure and properties it is necessary to carry out a research in two parallel directions: Comprehensive analysis of thermodynamics, kinetics and mechanisms of the processes taking place at the solid-liquid-gaseous phase interface during welding processes and development of mathematical models of the specific welding technologies. We have developed unique method of mathematical modeling of phase interaction at high temperatures. This method allows us to build models taking into account the thermodynamic characteristics of the processes, the influence of the initial composition and temperature on the equilibrium state of the reactions, the kinetics of heterogeneous processes, the influence of the temperature, composition, hydrodynamic and thermal factors on the velocity of the chemical and diffusion processes. The model can be implemented in the optimization of various technological processes in welding, surfacing, casting as well as in manufacturing of steels and non-ferrous alloys, materials refining, alloying with special additives, removing of non-metallic inclusions.

Jan 1, 2003

By P. N. Anyalebechi

"The as-cast microstructure of two commercial-size ingots of aluminum alloy 3004 produced by the electromagnetic casting process was quantitatively characterized. This involved the quantitative determination of through-thickness and across-width variations in dendrite cell size, grain size, macrosegregation of alloying elements, interparticle spacing, and the types, volume fractions, and sizes of the constituent or second phase particles. More than ninety-five percent of the constituent phases in the ingots consisted of the A16(Mn,Fe) phase; the desirable a-Al 12(Fe,Mn)3Si phase was not detected in any of the ingots by Guinier X-ray diffraction analyses or electron probe X-ray microanalyses. A significant microstructural heterogeneity through the thickness and across the width of both ingots was observed. For example, macrosegregation, and the sizes of the constituent phase particles, dendrite cells, and grains increased concomitantly from edge to mid-width and from surface to center of the ingots. There was a -20% depletion (negative macrosegregation) of Mg and a +54-87% enrichment (positive macrosegregation) of Ti in the center of the ingots. With the exception of grain size, there was no significant microstructural difference between the two ingots examined. The causes and practical implications of the observed microstructural heterogeneity in the ingots are discussed.IntroductionThe first step in the fabrication of majority of wrought products of aluminum and its alloys is the casting of large ingots or billets of simple shapes (round or rectangular). The sizes of the ingots vary from 10 mm to 450 mm diameter or 25 mm to 780 mm thick. The quality of the finished products is established at the ingot casting stage. This is because the microstructural characteristics, such as secondary dendrite cell size or arm spacing, amount of alloying elements retained in solid solution, macrosegregation, and the characteristics of second phases, produced during casting cannot be reversed by subsequent processing. Up until twenty-five years ago, the effect of as-cast microstructure of large ingots on the structure and behavior of thin sheets (0.34 mm thick) during drawing and ironing processes was incorrectly assumed to be minimal or nonexistent. This was based on the erroneous notion that the thermal treatments and large reduction (>99.94%) and strain that the ingot undergoes during production of the sheets completely destroys the original ingot structure and its inherent heterogeneity. However, the effects of ingot structure can, a priori, be deduced from the observed effects of constituent phase particle size, type and volume fraction on recrystallization, development of texture during annealing and deformation, and earing. In fact, careful examination of the behavior of products produced from different size ingots or castings have shown that the original microstructure of the ingot has a direct impact on the properties and performance of the end products."

Jan 1, 2011

By G. Van Weert

The pellet reactor was developed approximately 20 years ago in the Netherlands for softening drinking water. Since then, some 35 plants have been built, ranging in capacity up to 8500 m3/h. Applications now also include removal of phosphates and fluorides and the production of metal carbonates and sulphides from waste streams. The pellet reactor consists of a fluidized bed, wherein the process solution is thoroughly mixed with the precipitation reagent at special inlet nozzles to give over-saturation of the compound to be precipitated. In water softening applications, the compound is CaCO,. In the case of nickel or other metal waste streams, Na2CO3 solution is added in sufficient amounts to precipitate metal (hydroxy) carbonate on the fluid bed particles. These grow typically to dense spheroids, which are removed when they reach 0.8 to 1.0 mm diameter. These spheroids are easily dewatered, free flowing and low dusting. The latter property is becoming an attractive advantage in connection with new plant hygiene regulations. The operation of a 60 cm diameter pellet reactor on nickel containing plating waste is described and the properties of the produced nickel carbonate spheroids are discussed.

Jan 1, 1993

By Gerardo Fuentes

The stoichiometry and kinetics of the hydrothermal reaction of enargite in copper sulphate solutions was investigated in the range 140–300 °C, and particle size under 15 and 50 μm. The stoichiometric experiment was performed at 300 °C, using one gram of sample (96% enargite, 4% tennantite) and 100 mL of copper sulphate solution (10 gpl) at 1.2 pH. Enargite reacted completely after 80 min. A solid product was obtained and characterized by XRD. The main product was chalcocite (M) and some traces of djurleite and chalcocite (Q). Tennantite did not react under these conditions. The kinetic experiments were conducted at 140 °C, 190 °C, 250 °C and 300 °C. From fitted data and Arrhenius equation the calculated activation energy (Ea) was 51 kJ/mol. According to the hydrothermal transformations studied, the reactivity of different phases found in the copper concentrates was bornite > chalcopyrite > covellite > sphalerite > pyrite > enargite > tennantite.

By James B. Pfeiffer

TETRA Technologies, Inc., has applied its HDS? metals precipitation system to control a mine drainage problem. The effluent from the mine contains primarily zinc, manganese and iron, plus varying small amounts of cadmium, copper and lead. The flow from the mine averages 350 gpm, and varies considerably depending on season and weather conditions. The plant was designed to treat 1000 gpm of the water and generate a dense sludge suitable for recycling. The HDS? system contains a number of reactors, followed by post filtration and meets stringent metals discharge criteria as specified by New Source Performance Standards.

Jan 1, 1994

Al2O3,-WC Composite powder for cutting tools was synthesized by self-propagating high-temperature synthesis using A1 powder as a reducing agent. WC, W2C and Al2O3 were concurrently formed in WO3Al-C system. It was found that the complete reaction was achieved with excessive addition of carbon and appropriate processing parameters such as degree of dilution, particle size of aluminum, compaction pressures of green pellets and carbon source. The final product which was leached by 50% HN03+HF diluted solution was consisted of Al2O3-55wt% WC having 2-3um of mean particle size.

Jan 1, 1999

By Huimin Lu, Liyuan Zhao, Zhijiang Gao

The aluminum matrix composite reinforced by graphene was successfully fabricated using high pressure torsion (HPT). With only 0.5wt% graphene, the grain size was reduced to 100nm while that of pure Al was about 500nm. The hardness of the composite increased from the center (64HV) to the edge (120HV) of the sample. Moreover, the tensile strength of this composite reached 197MPa, while that of pure Al was 157MPa. The enhancement in mechanical properties was induced by grain refinement, load transfer from the matrix to the reinforcement and dislocations piled up at the grain boundaries.

Jan 1, 2015

By Michele L. Bustamante, Gabrielle Gaustad

In recent years, t h e future supply of tellurium has been called into question due to the anticipated rapidly increasing demand from thin film cadmium telluride photovoltaics. Since tellurium is produced as a byproduct of other extractive processes – principally, the electrolytic refining of primary copper sulfide ore – it is important to explore the dynamics of the parent metal extraction and processing – in this case copper – when attempting to answer this question. This research explores the changing landscape of global copper production; introducing system diagramming and the concept of byproduct intensity (BPI) to illustrate concerning downward trends in tellurium supply potential. Upon closer inspection, it is concluding that, while a likely contributor to these downward trends, the increased use of non- traditional copper production techniques alone are not responsible; other factors include market substitution and incomplete data reporting. Additionally, a review of literature on tellurium recovery processing reveals a promising outlook for future supplies; highlighting potential for improvements in yield, which allow producers to make better use of what is available, even in the face of suppressed BPI.

Jan 1, 2014

By N. M. Komkov

The main operation of obtaining zinc from sulfide raw materials by hydrometallurgical technologies is the oxidation roasting of zinc concentrates in fluidized bed furnaces. The technical-economic parameters are determined by the parameters of the roasting process, which depend on the composition of the initial raw materials, the temperature of the bed and on other factors. The predetermined roasting temperature is maintained due to the change of specific efficiency as well as to the quantity of the heat removed from the bed. The efficiency of caissons depends at a high degree on the composition and the thickness of the accretion formed on the surface of the caissons. Forecasting the roasting results is impossible unless we know the mechanism of the accretion formation. The aim of the present paper is the thermodynamic analyses of the behavior of the charge compositions under roasting and the determination of the potential mechanism of the accretion formation. The thermodynamic analyses show that under conditions of the oxidation roasting the thermodynamic probability of the formation of zinc sulfate is higher than the probability of the oxide formation until a temperature of873 OK is reached. The thermodynamic probability of the formation of the lead sulfate is higher than the probability of oxide formation in the entire temperature range of roasting. The probability of formation of ferrites and silicates of zinc decreases only insignificantly the sulfate stability. The results of the investigation of the accretions composItion formed under roasting of concentrates with particle sizes less than 0.02 J..lm (60%), containing 65% of sphalerite (ZnS), 12% of pyrite and chalcopyrite (FeS2 and CufeSz) each, 3% of galenite (PbS), 7% of silica and other non-ore minerals, have shown that the composition of accretion varies depending on the depth of the accretion layer. The accretions on the caissons and the thermo-siphons consist mostly of zinc sulfate (more than 50%). The accretions of forehamber consist mostly of zinc oxide. They also contain ferrites and silicates. The formation of the sulfate zinc accretion in the cold parts of the fluidized bed furnace (the caissons and thermo-siphons) may be explained by a lower temperature on the surface and probably by a catalytic influence of the present oxides in the formation of S02 and sulfates. The nature of the structure of the accretion in the hotter parts of the furnace may supposedly be explained by the formation of elemental vaporous zinc during roasting.

Jan 1, 2003

By John M. Gaines

Lead concentrates from the Viburnum Trend in the Southeast Missouri Lead district are sintered prior to smelting to bind the particles together homogenize the feed, and reduce the sulfur content. Good sinter forms competent masses about 4 to 6 inches across, that hal!e about 15% porosity and good mechanical strength to withstand transport and the weight of the overlying load in the smelter. Bad sinter has poor mechanical strength and forms fine fragments that retard the circulation of reducing gases in the furnace and lengthen the time required for reduction. The productivity of the lead smelter depends on good sinter feed. Because some lead sinter plants produce bad sinter about 20% of the time, this applied mineralogy study has been undertaken to determine the mineralogical and microtextural differences between good and bad sinter. A reflected light microscopic study of 130 polished sections has shown that good and bad sinters differ distinctly in their mineralogy, tex1ure. and character of, porosity. Good sinter consists of hardystonite, franklinite. lead-zinc-bearing magnesium-calcium silicate, lead silicate matrix, and large crystals of calcium-magnesium-iron silicate, together with minor amounts of lead oxides, lead-zinc silicate, metallic lead, specular hematite, magnetite, lead-iron-bearing zincite and zinc-Iead-magnesium-bearing wustite in a tightly intergrown mesh of crystals and with an evenly distributed porosity of 15% to 20%. Electron microprobe analyses show that the principal phases contain lead (or zinc): hardystonite (4-20% Pb) franklinite (2-14% Pb) and lead silicate matrix (65-74% Pb). Bad sinter differs from good sinter in the greater abundance of lead silicate matrix, galena metallic lead, and lead oxides and the lesser abundance of hardystonite, franklinite and calcium-magnesium-iron silicate. Bad Sinter is characterized by a lack of an intimate intergrowth of the constituent phases. Its porosity is much lower commonly 0 to 5% and those pores are concentrated in local areas rather than distributed evenly throughout the sinter.

Jan 1, 1991