By H. Landsberg

THE curriculum presented here is an outgrowth of discussions by the Committee on Geophysics Courses of the A.I.M.E. in previous years. It had to be a compromise between the desires voiced by employers of geophysicists, professional geophysicists and the possibilities at an average college. There one has to face the questions of the available teaching staff, the inertia of administrators and teachers set in their ways, and the red tape involved in modernizing antiquated curricula. It is, of course, not ideal to have colleges and universities lag 10 years behind the times. Rather, instead of being prodded by industry, -they should be ahead of industrial needs. There should also be a certain amount of leeway for the student in any college curriculum. All these points had to be considered in drawing up a curriculum, which, instead of being narrowly termed "geology" or "geophysics" was rather called "earth science." It gives the student a chance to specialize in one of the various branches represented by teachers on the faculty of The Pennsylvania State College, giving as options Geology (with subdivisions of Mineralogy and Paleontology), Geophysics, Geography, and Meteorology. Table IA. represents the option of geophysics in the curriculum that envisages that a student may want to make his career in any of the fields encompassed by the American Geophysical Union or in geoexploration. This is, of course, only the start of an education that in most cases will have to be followed by graduate work for complete professional training. The outlined curriculum is definitely of an engineering type and is identical for all of the four options mentioned for the first two years. Specialization will start in the junior year but even thereafter the branches are kept as closely allied as feasible in order to permit a student to change from one to the other (e.g., because of a different aspect in the employment situation) with a minimum of additional work. Table IB shows the geophysics option according to subject matter, indicating the considerable amount of work in the fundamentals of mathematics, physics and chemistry with a liberal number of geology courses, and some engineering. The courses in the field of geophysics are limited-just two lecture courses as a general introduction and one field course, to permit the student a visualization of the correlation between mathematically analyzed physical data and the geological realities. Thesis work is considered essential to teach the student, while he is still in college, some things S. F. Kelly has mentioned as desirable: (I) following of instructions for somewhat independent work; (2) organizing of material, and (3) producing a readable report. This, together with the personal contact with the advising faculty member, will help in forming a student's personality. The seminar course attempts to get the student into the habit of reading current literature, so that he can keep abreast of the times.

Jan 1, 1941

By Francis Foley

FROM the point of view of the metallographist, the adaptation of x-rays to the study of the crystal structure of metals is of the greatest importance. While one may hardly consider the findings resulting from x-ray study as revolutionary, their positive nature, compared with the deductions we have been forced to accept from the work that had gone before, gives firmer ground on which to build and furnishes new fields for speculation. Prior to the advent of the crystallogram, the best work on the crystal structure of steel was that of Osmond and Cartaud.1 They concluded, from their investigation with percussion figures formed at various temperatures, that alpha, beta, and gamma irons belonged to the cubic system and that they showed well-marked specific characteristics and could not have the same internal structure. What the internal structures were, they had no direct method of determining; but from a consideration. of the fact that the 001 plane (that parallel to the cube face) is a plane of perfect cleavage and minimum hardness in alpha iron and that the 111 (octahedral) plane is by far the most important in the crystallography of gamma iron, they were led to suggest the simple cubic arrangement as that of alpha and the face-centered cubic arrangement as that of gamma iron. They suggested the body-centered cubic arrangement as that of beta iron. The atomic arrangement of the various crystal forms of iron has been quite definitely determined in recent years by means of x-rays and the work of Westgren2 and Westgren and Phragmèn3 has been rather conclusive. They not only determined the atomic arrangement of alpha, beta, and gamma iron but also that of the high-temperature modification delta.

Jan 10, 1925

By Robert I. Jaffee, Bruce W. Gonser, Eugene M. Smith

There has been little investigation of the gold-germanium binary alloys. Haughtonl does not mention any work on the system. In a review article commemorating the fiftieth anniversary of the discovery of germanium, E. Einecke2 mentioned a gold-germanium eutectic at 24 atomic per cent Ge (10.4 weight per cent) melting at 359°C., but did not give the source of his information. From measurements of electrical conductivity, J. 0. Linde3 estimated that at least 0.6 weight per cent germanium is soluble in gold. The recent availability of germanium in this country in commercial quantities has led to interest in its properties and its alloys. This study is part of a program of investigation on germanium alloys; work on ternary alloys involving germanium and gold will be reported later. In this investigation, the composition and melting point of the Au-Ge eutectic reported by Einecke has been found to be substantially correct. Eutectic composition has been placed at I2.0 per cent germanium, however. An alloy of 10.4 per cent Ge, Einecke's value, was found to have a few gold dendrites in it. The cutectic temperature has been determined as 356.0 6 ± 0.5°C., slightly less than the temperature of 359°C. reported by Einecke. The liquidus curves and the solid solubility of ger- manium in gold have been determined, and are shown in Fig. I. Materials and Alloying The germanium used in this investigation was prepared by the Eagle-Picher Lead Co. from pure germanium oxide, by reduction in clay crucibles with sodium cyanide. The regulus is quite pure, assaying over 99.9 per cent Ge. High-purity gold obtained from Handy and Harmon was used. Alloying was carried out in graphite crucibles in an atmosphere of purified hydrogen. The temperature was brought up to 1050" to iioo°C., and the metal was allowed to freeze in the crucible. Prepared in this way, the gold dendrites in hypoeutectic alloys were somewhat segregated at the bottom and sides of the ingot, and on the hyper-eutectic side the lighter primary germanium tended to gather at the top. Most of the alloys were made from virgin metal. Low-germanium heats were made by alloying pure gold with the eutectic. Melting losses were consistently a few milligrams or less, and the composition could safely be taken from the intended analysis. The 30 per cent and 50 per cent germanium heats for thermal analysis were made in part from remelted higher germanium heats, and they may be OR composition as much as one per cent. Because of the high cost of materials, the weight of heats for thermal analysis were 15 to 20 grams and heats for metallo-graphic, X-ray, and hardness specimens were 2 to 4 grams.

Jan 1, 1945

By Franklin Moeller

Discussion of the paper of FRANKLIN MOELLER, presented at the New York meeting, February, 1916, and printed in Bulletin No. 110, February, 1916, pp. 343 to 354. K. A. PAULY, Schenectady, N. Y.-I read with interest Mr. Moeller's paper descriptive of the mechanical parts of the new electric hoist at the Granite Shaft of the North Butte Mining Co. and as the paper treats largely of the mechanical equipment I have little discussion to offer. There is, however, one question which I would like to ask and that is, why the discrepancy in hoisting cycles between the curves given in the paper read by Mr. Sykes for the American Institue of Electrical Engineers at San Francisco and those given in the paper under discussion? In Mr. Sykes' curves the acceleration period is shown to be 16 sec. for all depths from 2,000 to 4,000 ft. inclusive, while Mr. Moeller in Fig. 2 shows 25 sec. throughout the range and in Fig. 4 shows 35 sec. Mr. Moeller's curves also show the following reductions in the peak load during acceleration: Level, Feet Mr. Sykes, Horsepower Mr. Moeller, Horsepower 2,060 3,500 3,130 3,000 3,800 3,480 Fig. 2 4,000 4,100 3,800 2,250 1,595 Fig. 4 As the purchaser's specifications called for 15 or 16 sec. I would like to know whether or not any modifications have been made in the requirements since the equipment has been installed.

Jan 5, 1916

By E. F. Poncelet

Forty years ago A. A. Griffith developed a theory explaining why brittle materials displayed such low tensile strengths.' He based his views on two points. First, he found himself compelled to assume that all brittle materials are replete with flaws, cracks, and other defects that act, although quite invisible, as large stress raisers. Second, he applied the "theorem of minimum potential energy," which says that the total potential energy of a system must pass from the unbroken to the broken condition by a process involving a continuous decrease in potential energy. By this means he satisfactorily accounted for the noted low strength of such solids and also for the wide spread obtained in experimental measurement of these strengths. So successful has the theory been that it is favored by some to this day. Unfortunately this theory is of limited use beyond the explanation of these two noted phenomena and it is keenly felt that a better theoretical insight into the physics of the fracturing process is needed as the volume of experimental evidence accumulates. The author proposes in the following to build on the fundamentally sound concepts of Griffith and, with the help of increased theoretical knowledge over that available to Griffith, develop a mechanism for frac-ture which will provide far greater understanding of the experimental evidence accumulated to date than is possible from the original Griffith idea. THE GRlFFlTH THEORY Very little progress indeed can be made without accepting the first postulate of Griffith which supposes all brittle solids to be full of microcracks. It would be difficult indeed to find a better mechanism for the small strength of such brittle materials, in conjunction with the fact that the energy that must be expended for comminution is by no means small. The postulate of the existence of the microcracks permits the breakup of the various bonds a few at a time by concentrating the stress at the tip of the progressing crack, while the total energy expended is the same as if they all had been ruptured simultaneously. The only flaw in the argument is that no reasonable explanation has been proposed to account for the genesis of such cracks. Indeed their very presence is in violation of the Griffith second postulate, the potential energy theorem. This theorem is straightforward for isothermal processes, and, in spite of Griffith, there is some doubt that treating the problem isothermally is legitimate. The surface energy of bodies is a free energy, not a potential energy as stated by Griffith, and the production of new surface free energies is not necessarily an isothermal process. There is ample evidence to the contrary. Generally speaking, if heating a body increases its surface area, then, by virtue of Le Chatelier's principle, any increase of that area by other means will tend to lower its surface temperature. Lord Kelvin calculated the actual cooling that resulted in drawing out a film of liquid.2 R. A. Houston calculated the surface cooling that resulted in stretching a metal wire.3 These calculations were made by applying the Carnot cycle to the process and evaluating the thermodynamics thereof. IRREVERSIBILITY OF THE FRACTURING PROCESS While Griffith was very careful not to say so, the impression gained from studying his papers is that he considered the fracturing process as reversible, that is, a succession of quasi-equilibrium states. There is ample evidence that it is not. The indication that the new surfaces produced by the propagation of a crack are cooler than the original body points to an irreversible heat flow from the interior to the new surfaces to equalize the temperatures. If the process be reversible, any crack accidentally formed should immediately close up as, in the absence of any strain energy, the potential energy would thereby be lowered. The fact that they do not, constitutes a paradox. Such paradoxes are nothing new where certain phenomena that propagate from minuscule nuclei are assumed to be reversible. Such is, for instance, the condensation of a pure saturated vapor that is suddenly chilled by adiabatic expansion. At the beginning the tiny droplets that are formed should be only a few angstroms in size, but the vapor pressure at such droplets is so high that they should evaporate at once. A similar situation arises if a saturated pure solution becomes super-saturated upon cooling; the first tiny crystal nuclei should dissolve as fast as

Jan 1, 1964

By B. Ladanyi

The problem of rock behavior under concentrated loadings has been the subject of a number of studies in the past and has been receiving increasing attention by rock mechanics investigators in recent years. Its application covers various fields, but main interest in its solution has arisen in connection with the problems of drilling, bearing capacity, and rock testing. These widely different purposes and fields of interest probably have been one of the reasons why, in spite of the large amount of published experimental data and several theoretical studies, there are still many points which need further clarification. Another reason for this situation undoubtedly is due to the fact that the rock behavior in indentation is complicated by a great number of influencing factors. Experimental evidence shows that, depending on the rock type (mechanical properties, porosity), environment (ambient effective pressure, pore fluid, temperature), and the type of loading (indenter shape, initial embedment, load level, loading rate), the rock response to indentation may vary within very large limits. The widely different rock behavior has made it impossible up to now to treat the problem with a consistent single mathematical theory, but has required instead a series of simplified models covering only certain most important events in the failure sequence. As far as the theory of rock indentation is concerned, this chapter does not add much new information. Its main purpose is, however, to state the indentation problem in a general manner and to indicate which points need to be studied in more detail before its definite solution is attempted. Also, since excellent reviews of the state-of-art of rock indentation in drilling have recently been given,1-4 this will not be repeated here, and only references pertinent to the points of the problem under study will be quoted. The theoretical part of this study attempts to give a quantitative evalu-

Jan 1, 1972

By A. C. Milner

In a gold standard world which possesses insufficient metal to meet the every-day needs of all, confidence becomes the vital factor, the very foundation upon which the machinery for the expansion of gold into currency, and credit, rests. The gold supply, affected by many influences, moves constantly from one point to another, but not always to that point where it is most needed. In the period 1928-1930, the combined gold holdings of the United States and France increased $1,370,936,-000, and this with new gold adding only $600,000,000 to the monetary gold stock.Theref ore, the gold stocks of other countries must have been depleted during the period by $770,936,000. This uncontrolled shifting throws the delicately adjusted instrumentalities of both credit and commerce out of equilibrium. If a given nation's gold stock shifts so as to bring it substantially below the legal reserve ratio set up against it for currency issues, the effect can easily extend to the currency issues and banking credit volume of one or more nations which may have based their gold exchange standards upon the gold stock of such nation. Thus the substitution of paper based on gold in place of the actual gold is an inflation of the currency, which carries through into an uncontrolled pyramiding upon the entire machinery of credit based on gold. In 1929 Europe, South America, Africa and Asia had overissued currency based on gold. America, Oceanica and Japan, which have not overissued their gold currencies, would in normal times require their entire present gold stocks and, as Continental Asia is largely upon a silver credit basis, from a domestic standpoint, it would appear that the gold problem is not so much one of maldistribution, as it is one of inadequate supply. It would appear that some method of increasing greatly the velocity of gold, within the safe reserve point, should be devised, or that silver, of which estimates indicate that 7,000,000,000 oz. are available for

Jan 1, 1931

By Donald B. Gillies

The fundamentals of human nature don't change much from generation to generation, or even from century to century. Except for the spur of necessity and the lure of reward and ad venture, few of us would bestir ourselves unduly. The general welfare has little appeal to the average individual. Its promotion comes about mainly as a by-product to individual efforts directed at more personal benefits and satisfactions. In discussing incentives for the mining industry, we really are talking about incentives for people who devote their energies and resources to mining. The vigorous and productive mining industry as we have known it was the product of the varied incentives we have known in the past: the lure of great financial reward if you struck it rich; the thrill of romance and adventure in the search for mineral wealth, usually along the frontiers 'of civilization; the satisfaction of developing a great, productive enterprise by the application of skill, courage, and determination in the face of obstacles. Back of the prospector and engineer were other venturesome persons willing to take a flyer with their savings in a grubstake, or in stock in a promising mining venture, hoping for large returns, but reconciled to take a loss and try again with the next opportunity. It is free enterprise-a chance for high profits, but a chance also of total loss-that created the great mining industry of this country and of the world. Free enterprise has given us, in the United States, the greatest productive system in the world, the highest standard of living, the most abundant life. The lure of gold-whether from the ground or merely incidental to the discovery and development of our mineral resources-pushed our frontiers westward across the country and northward into Canada and Alaska far in advance of the staid course of agriculture and commerce. No one guaranteed success to our forebears as they risked life and fortune in developing a new country. Self-reliance was the backbone of our economic and spiritual Progress and achievements. Our neighbors had little time to spare from their own problems. And though there was a willingness among the pioneers to help one another, they didn't lean too much on one another.

Jan 5, 1950

By R. V. Smith, E. J. Dewees, R. H. Williams

Before this paper was presented, the terms "f" and "v1/f in flow equations had been called "friction coefficient" and "friction factor," respectively. However, many authors have used the names for the terms interchangeably, with the result that considerable confusion has existed in the literature on flow of fluids. In an effort to establish a clear and concise terminology for these terms, the authors have designated f as "resistance coefficient" and dm as "transmission factor." Transmission factors for the flow strings of gas wells were determined by tests on wells in six fields of Oklahoma, Texas, and Louisiana. Data were collected on 14 gas wells while gas was flowing through 1 1/4, 2, 21/2, and 3-in. tubing and 51/2 and 7-in. casing. The transmission factors developed from these data were found to follow the resistance equation published by Nikuradse1 for turbulent flow in "rough" pipes with an average absolute roughness of 0.000,65 in. This average absolute roughness is believed to be representative generally of the flow strings of gas wells with the exception of those that have been exposed to corrosion or other conditions causing undue roughness. Also, use of an absolute roughness of 0.000,65 in. probably will result in transmission factors that are more representative of gas-well conditions than those in common use today, provided that the transmission factors are calculated by the methods outlined in this report. The authors believe that use of these transmission factors will permit calculation of more accurate subsurface pressures in gas wells than those in use today. Engineers use transmission factors in flow equations to compute subsurface pressures in flowing gas wells from measured wellhead pressures. These subsurface pressures are necessary for determining the productivity of gas wells from "back-pressure" tests. The methods of calculating pressures in flowing gas wells, as outlined by Rawlins and Schellhardt2 in Bureau of Mines Monograph 7, are based on the transmission factors in the well-known Weymouth formula" Natural gas engineers have realized that errors introduced by using transmission factors as given by the Weymouth formula are relatively unimportant in testing low-capacity gas wells; but they also know that such factors are important considerations in testing large-capacity wells. Accordingly, the research described in this report was undertaken to fulfill the need for more accurate means of calculating subsurface pressures in gas wells. This report is part of the Bureau's study of the flow of natural gas through pipe and commercial pipelines. Several of the conclusions regarding flow in the flow strings of gas wells were influenced by the results of the study of flow in horizontal pipelines. These instances are mentioned in the text of this report. METHODS OF COMPUTING TRANSMISSION FACTORS Methods and procedures for computing transmission factors for turbulent flow in circular pipes from test data taken on gas wells have been derived and explained in detail in a paper by Smith4. As these methods were used to calculate the transmission factors presented in this report, a summary is included. Starting with

Jan 1, 1955

By W. C. Meyer

In an effort to conserve and extend oil resources, the use of powdered coal-in-oil mixtures (COM) as an alternate fuel in oil-fired boilers is receiving increasing attention. For the approach to be successful, some degree of stability of the suspension against settling is needed. The variety of means available to achieve stability of this nonaqueous slurry is reviewed along with some of the physical and chemical concepts which underlie each method.

Jan 1, 1983

By J. P. Hammond, C. J. McHargue, J. R. Holland

IT has been reported that both berylliumL and zirconium&apos; developed the same basic textures during rolling at temperatures up to 1475 °F as at room temperature, differing only by an increase in the spread of basal planes toward the transverse direction as the temperature of deformation was increased. Iodide titanium&apos;&apos; rolled at 1050°F has a texture similar to the cold-rolled texture, {000l}, 25° to 30" from the rolling plane toward the transverse direction, <1010>, Rolling iodide titanium at 1450°F produced a more random condition with the basal planes parallel to the rolling plane and no direction strongly aligned with the rolling direction.

Jan 1, 1957

By Robert I. Jaffee, Bruce W. Gonser, Eugene M. Smith

THERE has been little investigation of the gold-germanium binary alloys. Haughton1 does not mention any work on the system. In a review article commemorating the fiftieth anniversary of the discovery of germanium, E. Einecke2 mentioned a gold germanium eutectic at 24 atomic per cent Ge (10.4 weight per cent) melting at 359°C., but did not give the source of his information. From measurements of electrical conductivity, J. 0. Linde3 estimated that at least o.6 weight per cent germanium is soluble in gold. The recent availability of germanium in this country in commercial quantities has led to interest in its properties and its alloys. This study is part of a program of investigation on germanium alloys; work on ternary alloys involving germanium and gold will be reported later. In this investigation, the composition and melting point of the Au-Ge eutectic reported by Einecke has been found to be substantially correct. Eutectic composition has been placed at 12,0 per cent germanium, however. An alloy of 10.4 per cent Ge, Einecke&apos;s value, was found to have a few gold dendrites in it. The eutectic temperature has been determined as 356.0 ± 0.5°C., slightly less than the temperature of 359°C reported by Einecke. The liquidus curves and the solid solubility of germanium in gold have been determined, and are shown in Fig. I. MATERIALS AND ALLOYING The germanium used in this investigation was prepared by the Eagle-Picher Lead Co. from pure germanium oxide, by reduction in clay crucibles with sodium cyanide. The regulus is quite pure, assaying over 99.9 per cent Ge. High-purity gold obtained from Handy and Harmon was used. Alloying was carried out in graphite crucibles in an atmosphere of purified hydrogen. The temperature was brought up to 1050° to 1100°C., and the metal was allowed to freeze in the crucible. Prepared in this way, the gold dendrites in hypoeutectic alloys were somewhat segregated at the bottom and sides of the ingot, and on the hypereutectic side the lighter primary germanium tended to gather at the top. Most of the alloys were made from virgin metal. Low-germanium heats were made by alloying pure gold with the eutectic. Melting losses were consistently a few milligrams or less, and the composition could safely be taken from the intended analysis. The 30 per cent and 50 per cent germanium heats for thermal analysis were made in part from remelted higher germanium heats, and they may be off composition as much as one per cent. Because of the high cost of materials, the weight of heats for thermal analysis were 15 to 20 grams and heats for metallographic, X-ray, and hardness specimens were 2 to 4 grams.

Jan 1, 1945

By H. W. Camp

Although the situation in the oil industry during the past year has not been conducive to large expenditures for development and research, there is little indication that such expenditures have been curtailed. While few outstanding achievements have been reported, considerable progress has been made in the development of new product,s and the adaptation of petroleum derivatives to new uses. The most important question facing the refiner today is the antiknock quality of his gasoline. This year has seen the widespread adoption of the term "octane number" as a measure for anti-knock values, and in the latter months of the year the public has been made acutely aware of this condition through competitive advertising. Gasoline is no longer priced on volatility and gravity alone, but on octane number as well; and premiums are being paid for material of relatively high octane rating. The situation has grown more and more competitive and has forced refiners continually to raise the octane rating of their regular and competitive grades, and at this writing the same situation exists for premium grades which have possessed relatively high anti-knock properties for some time. Straight-run gasoline produced from paraffin-base or semiparaffin-base crudes has an inherently low anti-knock value, and in order to convert this material to a higher quality it has been found necessary to crack an increasing percentage of the crude oil charge. By completely cracking the heavier portions of the crude and blending back with the straight-run gasoline, it has been possible to produce an average of 63 to 65 octane number gasoline on average Mid-Continent crude. This operation carried to the fullest extent does not suffice, however, and the recent and rapid development of the so-called &apos;(reforming unit," has resulted. The straight-run gasoline fraction is cut into two parts: a light, low boiling point gasoline; and a heavy gasoline or naphtha. The latter containing the low anti-knock portions of the gasoline, is sent through a re-forming unit and subjected either to high temperature or pressure, or both, which materially increases its octane number. On average Mid-Continent the blend of low boiling point straight-run,

Jan 1, 1932

By J. K. Stanley

Knowledge of the diffusivity of carbon in the low temperature form of iron (alpha iron existing below 910°C) is at the moment of considerable interest in the study of the decomposition of austenite and martensite, the elastic after-effect,123 the magnetic after-effect4 and the decarburization of steel below 910°C. Information on the solubility of carbon in iron, and to a lesser extent its diffusion, is also important in consideration of such phenomena as blue-brittleness, temper-brittleness, "magnetic" aging, quench-aging, strain-aging, and possibly the yield point. In order to obtain more information on these subjects more fundamental knowledge is necessary. It is the purpose of this work to present data on the diffusion and solubility of carbon in the alpha iron. The high temperature form of iron (gamma; face-centered cubic) existing above 910°C is capable of dissolving relatively large amounts of carbon, up to 1.7 pet at 1130°C, while the low temperature form (alpha, body-centered cubic) existing below 910° dissolves only a limited maximum amount of less than 0.02 pet carbon at 725°C, according to data obtained here. Since the solubility of carbon in the face-centered or gamma iron is large, relatively speaking, no great analytical difficulties have been encountered in the determination of the solubility lines5 or of the diffusion of carbon.0 The limited solubility of carbon in alpha iron offers difficulties because experimental procedures and analytical methods for low carbon contents below say 0.01 pet have to be more refined than techniques used for work with gamma iron. Because of the difficulties of applying conventional methods to the determination of the diffusion of carbon in alpha iron, virtually no work has been done on this subject. However, by proper refinement of the analytical method for small amounts of carbon, the determination of the diffusion coefficient can be made readily using modified procedures. The solubility of carbon in alpha iron has been determined over a temperature range by various investigators, but the agreement among them is poor. The present investigation establishes the limits quite accurately. Information of this kind is useful in establishing the correctness of equilibrium diagrams but, more significantly, such information on maximum solubilities, especially when extended to alloyed ferrites, should be extremely important in the study of aging and related phenomena. Literature The literature existing on the diffusion, in particular, and on the solubility of carbon in alpha iron is not extensive. The data which exist are not of a high order of accuracy, much of them being in the realm of conjecture. THE DIFFUSION OF CARBON IN ALPHA IRON Whiteley7 made the qualitative ob- servation, using metallographic techniques, that the rate of diffusion of carbon at the A1 (725°C) point was very rapid and that its diffusion was still rapid at 550°C. Snoek,4 studying the magnetic aftereffect in high purity iron, arrived at the conclusion that the after-effect could be explained by the presence of small amounts of carbon diffusing under the influence of magnetostrictive strain (lattice distortion due to magnetic interaction). In later work, Snoek8 made an estimate of the ratio of carbon diffusion in alpha to its diffusion in gamma iron, and concluded that for a temperature of 910°C the ratio of Da/D? was 2600. Polder,9 basing his calculations of D on relaxation phenomena in the elastic after-effect, estimated that Da is about 1/3 of D? at 910°C (1183°K) and is about 1/12 of Dy at 727°C (1000°K). Polder&apos;s equation for the diffusion of carbon in alpha iron was calculated to be 18000 D = 5.2 X 10-4 e-RT cm2 per sec Ham10 obtained data for the diffusion and solid solubility of carbon in alpha iron at two temperatures by using one technique similar to that employed in this study. He found a D of 8.0 X 10-7 cm2 per sec at 702°C and of 2.7 X 10-7 at 648°C. THE SOLUBILITY OF CARBON IN ALPHA IRON Although pearlite is absent in steels containing 0.06 pet,11 0.05 pet,12 or 0.045 pet C,13 it appears that the carbon in these steels cannot be in solution in ferrite. The solubility of carbon at the A1 (725°C) point was first determined by Scott14 on the basis of cooling curves, and was found to be between 0.03 and 0.04 pet C. Tamura15 by interpolating between the solubility of carbon in delta iron at 1400°C and in alpha at room temperature (assuming zero solubility) ar-

Jan 1, 1950

By W. R. McMillan, E. A. Gulbransen, K. F. Andrew

Annealed and electrolytically polished pure iron was oxidized between 650° and 850°C at oxygen pressures of 0.1 to 2 microns Hg. Electron optical studies showed that oxidation occurs discontinuously over the surface and orients crystallographically with the substructure of the metal grains. IN previous papers&apos;, " the authors described the formation of oxide films on high purity iron at norrnal pressures and at temperatures below 300°C. Electron optical studies showed that the oxide film consisted of many individual oxide crystallites having nearly random orientation on each metal grain. The size of the oxide crystallites depended upon the temperature and upon the extent of oxidation. In these studies the crystallite size varied from 250 to 1800Å. Recently, Bardolle and Benard3 studied the crystal habit of the oxide crystallites formed on Armco iron between 650" and 850°C in what might be defined as a "poor vacuum" atmosphere in which the pressure could be varied between 10-1 to 10-3 mm of Hg. Their results showed that, at 850°C and a vacuum of l0-2 to 10-3 mm of Hg, a few well oriented nuclei of oxide were formed on the metal grains. At pressures between l0-1 to 10-2 mm of Hg, many oriented nuclei of oxide were formed. At 750°C the metal surface was bright although an oxide was present. Unfortunately, the extent of oxidation, the oxygen pressure, and the influence of carbon in the metal were not determined, and it was, therefore, impossible to give a theoretical interpretation to the very beautiful light micrographs. Bardolle and Benard used the light microscope to determine the crystal habit of the oxide and X-ray diffraction to determine the orientation relationships. It was believed that the use of controlled amounts of oxidation at high temperature is an important method for the study of the initial stages of oxidation of metals at high temperatures. This paper presents the first results of an electron optical study of this problem for iron. Since the electron microscope and electron-diffraction methods using stripped oxide films and surface replicas yielded finer details of the crystal habit and structure of oxide film, these methods were used in this study. Two types of iron having different carbon contents were used: Puron and Armco* iron. A com- parison of the results for these materials made possible a study of the influence of the surface oxide-carbon reaction on the initial stages of oxidation. Before discussing the experimental results, the thermodynamic equilibria of 1—the oxidation reaction, 2—the surface oxide-carbon reaction, and 3—the solubility of oxygen in iron, will be considered. In addition, it is important to consider the kinetic-theory predictions on the rate of collision of oxygen with the iron surface. Thermodynamic and Kinetic-Theory Calculations Only one type of reaction is usually considered in the oxidation of iron at normal pressures at high temperatures: Fe(a) + 1/2O2(g) = FeO(s) 3Fe(a) + 2O2(g) = Fe3O4(s) 2Fe(a) +3/2O2(g) = a-Fe2O3(s). [11 However, two other reactions may occur: FeO(s) + C (solid solution in Fe) + Fe(a) + CO(g) [2] and Fe(a) + O2(g) e Fe(a) (solid solution of 0,). [ 3 ] In addition, iron will react with the higher oxide at certain temperatures to form FeO. For a complete interpretation of the oxidation of iron at low pres-

Jan 1, 1955

By G. R. Speich, Morris Cohen

The growth rate of bainite has been determined by hot-stage metallography in five hypereutectoid high-purity iron-carbon, iron-carbon-chromium, and iron-carbon-nickel alloys. The studies have been confined essentially to lower bainite. The growth rate is independent of time at constant temperature, but both the edgewise and sidewise growth rates increase with increasing temperature. Increasing the carbon content, or adding chromium or nickel, decreases the growth rate without greatly affecting the temperature dependence. The results lead to separate diffusion-controlled models for the edgewise and sidewise growth rates. ALTHOUGH bainite has been subject of many detailed investigations,1,2 the growth mechanism of this intermediate transformation product of steel remains unclear. One difficulty has been that practically all the kinetic measurements have been restricted to studies of the overall reaction rate. Only a limited amount of information3, 4-6 is available on the growth process itself. The purpose of the present work was to investigate the effect of time, temperature and composition on the growth rate of bainite using hot-stage metallography. This method makes it possible to observe continuously the isothermal growth of individual bainitic units because of the surface upheavals accompanying their formation.3 This information is needed to test the existing growth models and to obtain a better understanding of the factors controlling the bainitic transformation. EXPERIMENTAL PROCEDURE Alloys—The compositions of the alloys used in the present work are shown in Table I. The five alloys were vacuum-melted and cast, and were prepared from high-purity materials. The three iron-carbon alloys were available from the work of Roberts et al.7 in the form of 3/8-in. diam rods.* To facilitate machining, the rods were ing. The rods were then tempered for 3 hr at 650°C to allow machining. The iron-carbon alloys in Table I were selected for investigating the effect of carbon on the bainitic growth rate. Due to the rapidity of the transformations involved, it was not feasible to measure the growth rates in iron-carbon alloys having carbon contents much less than 0.9 pct C. The iron-carbon-chromium and iron-carbon-nickel alloys were selected to study the influence of chromium and nickel on the growth rate at a carbon level of about 1.1 pct C, since this carbon content was intermediate among the iron-carbon alloys. The concentrations of chromium and nickel were chosen to match isothermal trans formation diagrams in the literature.8&apos;9 Hot-Stage—Since the iron-carbon alloys had such low hardenabilities, it was necessary to quench the hot-stage specimens drastically from the austentiz-ing temperature to the isothermal transformation temperature to prevent the formation of pearlite or proeutectoid constituents. A rapid-quenching metal-lographic hot-stage was built for this purpose. A maximum temperature of about 1100°C and quenching rates up to 500°C per sec could be attained with this equipment. The details of the apparatus are described in a recent publication. After being polished and mounted on the hot-stage, the specimen (0.020 in. thick) was protected from oxidation and decarburization during austenitizing by a vacuum of 10-4 to 10-5 mm. The quench to the reaction temperature was accomplished with a helium blast, and the isothermal run at this temperature was conducted in a helium atmosphere. A fine-wire thermocouple spot-welded to the sample and a high-speed

Jan 1, 1961

By Robert B. Sosman

ONE of the most neglected fields for physicochemical education as well as for research is that of high-temperature phenomena. Few universities or technical schools give instruction in the physical chemistry of substances at high temperatures. On the contrary such instruction is almost entirely confined to the region between the freezing and boiling points of water. This field should be extended to a much wider range of temperatures, both low and high. Such an extension is logical, sound, feasible, and practical.

Jan 1, 1943

By Pual M. Tyler

BLIZKRIEG tactics in the present war have consumed metals on such a profligate scale that some of the best-laid procurement plans for civilian and military needs of even a year ago seem in retrospect incredibly meager. Conservation of raw materials has reached an all-time climax in Germany, where metals are worth more than human life and throwing away an empty toothpaste tube may be legally punished by death. Even the United States and the British Empire, proud masters of nine tenths of the world?s known mineral reserves and processing plants, are being driven to metals and feverishly expanding production facilities that not long ago were deemed overbuilt. After the war is over and inevitable postwar readjustments are completed, it is reasonable to expect that purchasing power ? or at least the ability to procure the comforts and luxuries of life ? will be distributed among vastly larger population than ever before, accelerating the rising trend in demand for industrial raw materials in ever greater quantity and variety.

Jan 1, 1942

By H. S. Price, J. C. Cavendish, R. S. Varga

This paper presents a new technique for solving some of the partial differential equations that are commonly used in simulating reservoir performance. The results of applying this technique to a simple problem show that one obtains accurate pressure values near wells, as well as accurate pressure pdients, which can be explicitly calculated. The method is completely rigorous in that convergence of the discrete numerical solution to the continuous solution for both pressure and pressure gradient is established. High-order, piecewise-polynomial approximations are used near the wells where pressure gradients are steep, while low-order, piecewise-polynomial approximations are used elsewhere to reduce greatly the calculation time. This combination is shown to give a uniformly good approximation to the solution. These approximations, obtained by using a Galerkin process with suitable Hermite subspaces, are shown to be theoretically and numerically superior to the usual approximations obtained from standard finite-difference techniques. Not only are much greater accuracies obtained, but computer times are also greatly reduced. The application of this technique to multiphase flow problems (e.g., single well coning problems) would have considerable practical interest, but such extensions of this technique with full mathematical rigor have not been made as yet. However, the numerical methods presented here are general, and in principle extend to multidimensional, multiphase flow. Moreover, the preliminary results given in this paper are sufficiently encouraging that we feel the effort in attempting these extensions is justified. INTRODUCTION The problem of obtaining accurate pressure distributions and pressure gradients around wells is of considerable importance in the numerical simulation of reservoir performance. The most common approach to solving this problem is to use finite difference techniques (see McCarty and Barfield9 or Peaceman and Rachfordl0). This approach, however, has many disadvantages, the major one being that many grid points are generally necessary for accurately describing the pressure distribution and the pressure gradient around wells. This need for a fine grid results in large computer times and often in prohibitively high costs. Besides investigating the method of finite differences, some authors, such as Welge and weber17 and Roper, Merchant and Duvall,13 have considered a combination of analytical and numerical techniques with some success. These approaches, however, are all nonrigorous and quite often cannot even be applied. In this paper, we present a numerical formulation of high-order accuracy, based on the Galerkin method, for solving this problem. We treat here only the partial differential equation that describes steady-state, single-phase flow. However, the methods presented are general and in principle extend to multidimensional, multiphase flow. Specifically we treat special cases of the problem in two dimensions described by: where G is a rectangle (with sides parallel to the coordinate axis) with boundary ?G, ?/?n denotes the outward normal, and y and B are non-negative constants such that y + B > 0.

Jan 1, 1970

By F. B. Plummer

THE physical properties of oil-producing sands, such as grain size, porosity, and permeability, are becoming more and more important in petroleum production engineering as oil fields are being repressured and rejuvenated. A number of excellent papers have been published recently on all three of these properties. Faucher, Lewis and Barnes1 give a com-plete survey of the work done through 1932 and contribute also much information on sands that they themselves have examined. Muskat and Botset,2 Wykoff, Botset, Muskat and Reed,3 Hurst,4 and Muskat5 have contributed a great deal to the theory and actual measurement of flow of liquids and gases through porous media. Muskat and Botset have measured the permeabilities of different sands with gases and liquids. They find that the radial is always slightly under the linear permeability. However, in most of the previous experiments small samples of the sand were used, and the method of production of fluid or gas through the sands has not been very close to actual oil-field conditions. In addition, so far as the authors are aware, no measurements of linear and radial permeabilities have been made simultaneously under exactly the same conditions. The multiple permeability apparatus described here is a part of the equipment being acquired by this laboratory for thorough investigation of the physical properties of producing sands. It possesses certain advantages for comparative studies of liquid flow. Additional data and descriptions of other instruments will follow in papers to be written later on. The essential features of the permeability apparatus are as follows:

Jan 1, 1934