Search Documents

By Alden B. Greninger

Many recent contributions in the field of theoretical metallography have been concerned with crystallographic definitions or descriptions of various phenomena. The lattice orientation of the crystal being studied must be known before such definitions can be made. Practically all the metallic crystals used do not have crystal faces—other than the unknown "plane of polish"; hence resort must be had to other means of determining orientations. Some use has been made of etch-figures, slip bands, optical properties, etc., for this purpose; but for accurate results, and because of the fewer restrictions to their use, the various X-ray methods have been the most satisfactory.' The methods that have been used may be divided into two general classes: (1) oscillation methods, and (2) transmission Laue methods.² The disadvantages of these methods are numerous, chief among them being the time required to determine a complete orientation. No method proposed so far is wholly satisfactory for determining the orientation of a small macrograin within a polycrystalline aggregate.

Jan 1, 1935

By G. B. Walker, S. J. Swainson, S. A. Falconer

DURING the past few years much interest and attention has been focused on a relatively new method of ore concentration, which utilizes the principles of sink and float and employs as the heavy medium a suspension in water of a finely ground solid, such as galena or ferrosilicon. Although a relatively recent development, much progress has already been made in applying heavy-media separation processes to a considerable number of ores. Eight plants in this country and abroad -are now treating approximately 10 million tons of ore annually by heavy-media separation (sink-float) processes, including lead-zinc, lead, iron, garnet, tin and tungsten. At the annual meeting of the A.I.M.E. in 1941, three interesting papers (unpublished) dealing with heavy-media separation (sink-float) processes of ore concentration as practiced in four commercial units in the United States were presented by Victor Rakowsky, Grover Holt, Elmer Isern and Robert Ammon. These papers gave an excellent exposition of the principles of sink and float, as well as the operating practice in two iron-ore-beneficiation plants, the Harrison and the Merritt, of Butler Brothers, in Minnesota; the Central mill of the Eagle Picher Mining and Smelting Co.; and the Mascot mill, of the American Zinc, Lead and Smelting Co. Augmented by pictorial descriptions and a working model demonstrating the processes, these papers evoked a great deal of interest and discussion. In fact, in reporting the high lights of the meeting in the April 1941 issue Of MINING AND METALLURGY, Professor Taggart made the statement that "preconcentration by heavy suspension was Miss A.I.M.E. 1941 so far as milling is concerned." Although to date the greatest application of heavy-media separation from the tonnage point of view has been for the treatment of lead, zinc and iron ores, these processes have a much wider field of usefulness. In this regard, it is to be noted that recently new heavy-media separation plants for treating cassiterite ore and garnet ore have been placed in successful operation. Moreover, numerous other types of ores have been found to respond well to these processes when tested on a semi-commercial scale, and it is expected that in the near future a considerable number of new plants will be erected. In view of the fact that heavy-media separation processes offer such attractive possibilities, particularly now, when the mining industry is being called on for an even larger production than ever before has been attempted, despite shortages of labor and supplies, it was felt that a description of some of the successful separations that have been worked out during the past year in the Ore Dressing Laboratory of the American Cyanamid Co. on a variety of ores of strategic importance would be of interest. The purpose of this paper, therefore, is to present the essential data relating to investigations of heavy-

Jan 1, 1943

By J. D. Miller, A. Cortez, J. Hupka

The separation efficiency of the hot water digestion-flotation technique used for bitumen recovery from various domestic tar sands was evaluated. Bitumen viscosity was found to be the most important tar sand property in determining the success of the bitumen separation. Bitumen viscosity of the tar sand war controlled by changes in digestion temperature and/or changes in diluent (kerosene) addition. Complete and uniform dilution of the bitumen phase was achieved by providing a sufficient presoaking, or penetration time, for a given tar sand type. For all the tar sand samples tested, an excellent correlation was obtained between the coefficient of separation and the bitumen viscosity. To achieve a satisfactory coefficient of separation, it was found that the bitumen viscosity must be reduced below 1.5 Pa.s (16 P) at the temperature of digestion. This was the case regardless of the tar sand type, grade, or origin.

Jan 1, 1984

CLEAR sunny skies that prevailed all through the 175th General Meeting of AIME were not the 1east of the details that resulted from the many months and man-hours of p1anning by the Southern California Local Section. Some 2600 persons left the 1953 Annual Meeting technically enlightened, having had a choice of over 300 papers presented by 400 authors to listen to, learn from, and criticize. During the meeting, Mike Haider turned over the Presidency of AIME for 1953 to Andrew (Drew) Fletcher.

Jan 4, 1953

By R. T. Keyes, R. B. Clay, L. L. Udy, V. O. Cook, M. A. Cook

Based on compressibility and stress wave velocity in rock, initial explosive loading conditions, the thermochemistry of the explosive and reasonable description of the pressure-distance relations behind the shock front, the distribution of energy between the products of detonation and the burden are estimated as a function of time for various loading conditions. These include 'powder factor', loading density A (fraction of borehole occupied by explosive), and the explosive itself. Factors responsible for rock fragmentation are discussed in terms of: 1) 'release wave fracturing', 2) 'shear wave fracturing', and 3) 'release of loading fracturing' or 'rock bursting'. Release wave fracturing appears to occur only in the immediate vicinity of free faces, and shear wave fracturing only adjacent to the borehole under normal blasting conditions. Rock bursting is thus considered to be the most important means of rock fracturing in blasting. Means for maximizing it are considered. The most important factors to consider include maximum available energy A, explosive density p1, loading density A and 'powder factor'. Maximum efficiency is attained in general by maximizing the A . p1 product. This is achieved by using high density explosives at a loading density of unity (A = 1.0). Ways for achieving this condition are discussed. The bulk-handled aluminized slurry blasting agents have the desired properties for achieving optimum conditions for high blasting efficiency based on the theory outlined herein. Factors considered most important in the blasting of rock are: 1) The maximum available energy A, determined by the heat of explosion Q and the mechanical efficiency ?, a factor intimately associated with the mode of application (A = Q at highest gas concentrations). 2) The 'borehole pressure', pb, or the maximum pressure developed in the borehole after passage of the detonation wave and before the burden has had time to move or become compressed appreciably. (Owing to the short duration of the detonation wave at any particular point in the borehole, the fact that the explosive may not always fill the borehole completely and the further fact that the burden may not actually see the detonation pressure, the borehole pressure is considered more significant than the detonation pressure p2 as a performance factor in borehole blasting.) The borehole pressure is determined by the explosion or adiabatic pressure, p3 , and the loading density, A, or the fraction of the borehole filled by explosive. 3) The physical conditions important in the application of the explosive are: a) The 'powder factor,' (We/Wr), or the ratio of the wt of the explosive to that of the rock being blasted expressed as lb per ton or more generally in lb/cu yd. b) The bulk density, p1 ?. c) The 'burden' or 'line of least resistance,' the spacing between boreholes, the geometry of the borehole pattern and sequence of firing. d) The physical and chemical properties of the rock, most significant of which are possible heterogeneties, such as faulting, prefracture, and greater than micro-scale chemical heterogeneities. (This factor is not considered here but deserves a great deal of careful consideration.) All of these factors need to be carefully considered in the most economical engineering of a blast. Here is considered firstly an outline of the present status of dynamic rock mechanics, particularly as it pertains to blasting. The factors pertaining to the most efficient application of blasting agents are also considered, followed by a discussion of methods of application to achieve optimum explosives performance. ROCK MECHANICS Dynamic rock mechanics is currently a rapidly developing science contributing greatly to a better understanding and consequently the more effective application of explosives in blasting of rock.1-22 Basic to the development of the science of dynamic rock mechanics were the advances of Goransen23 and the Los Alamos and NOL groups24-28 concerning rock and stress wave phenomena and the transmission and reflection characteristics of stress waves at interfaces between different media. Basing considerations on this new knowledge as well as new experimental methods of study (ultra-high speed streak and framing cameras and electronic timers) the theory of fracture and failure of solids under impulsive loading by stress waves developed rapidly.14,16,27-29 Also the

Jan 1, 1967

By J. L. Taylor, Pol Duwez

THE present knowledge of the Ti-Al system is limited to the portion of the diagram extending from pure aluminum to the intermetallic compound TiAl3' A preliminary investigation of the titanium-rich Ti-A1 alloys revealed that the solubility of aluminum in titanium is quite extensive and that the transformation temperature of titanium is raised by alloying with aluminum. From an X-ray diffraction study of alloys containing up to 75 atomic pct Al (TiAl3), the phase boundaries at 750°C were located as follows: the a titanium solid solution extends from 0 to about 36 atomic pct Al, a two-phase region exists from 36 to 46 atomic pct Al, and an intermediate phase of varying concentration extends from 46 to 62 atomic pct Al. The purpose of the present paper is to describe the crystal structure of this new phase. The alloys were prepared by melting in a helium arc furnace on a water-cooled copper plate, using a furnace essentially the same as that described in ref. 2. The titanium metal was of the iodide type furnished by the New Jersey Zinc Co., and a piece of pure aluminum (99.99 pct) was obtained through the courtesy of the Aluminum Co. of America. After melting, the samples, weighing approximately 5 g, were sealed in evacuated fused silica tubes and homogenized for 4 hr at 1000°C. The specimens were then held for 10 days at 750°C and rapidly cooled to room temperature. Filings were then taken from each sample, sealed in evacuated vials, annealed at 750°C for 4 hr, and rapidly cooled to room temperature by quenching the vials in water. Powder diffraction patterns were obtained with a 14.32 cm diam camera, using K copper radiation filtered through a nickel foil. Structure Determination The X-ray diffraction patterns of the alloys containing 46, 50, 55. 60, and 62 atomic pct Al were identical, except for a slight shift in the positions of the reflections. The alloy containing 55 atomic pct Al was chosen far structure determination. The powder pattern contained 37 reflections and the a, doublets were well resolved in the back-reflection range. The relatively small number of reflections and the sharpness of the pattern were considered as an indication of a simple atomic arrangement in a relatively small unit cell of high symmetry, and an attempt was therefore made to solve the structure without single crystal work. A satisfactory fit was found on a large scale Hull-Davey tetragonal chart for an axial ratio of approximately 1.45. All the reflections were readily indexed and the tentative unit cell dimensions were computed to be a - 2.81 kX, c - 4.07 kX, and c/a = 1.448. The indices (hkl) and the values of d and sin2 A are given in Table I. The agreement between observed and computed sin2 is quite satisfactory. Once the unit cell was known, the details of the structure were readily found. First, it is obvious that the number of atoms per unit cell cannot exceed two, since more than two atoms would lead to a density greater than that of pure titanium. The next logical step is to assume that the two atoms occupy the corner and center of the cell. If this assumption is correct, the structure may be described as follows: space group D1, - P 4/mmm; one titanium atom in a: 000; one aluminum atom in d: 1/2 1/2 1/2: and no extinctions. Assuming this structure to be the correct one. intensities were computed by means of the usual equation: sin2 0 cos 0 where F is the structure factor; 8, the Bragg angle. and p, the multiplicity factor. The calculated values of intensities are compared in Table I with the visually estimated intensities. The agreement is quite satisfactory and the structure is therefore confirmed. The crystal structure of TiAl just described is the same as that of AuCu ordered. The AuCu ordered

Jan 1, 1953

By P. S. Rudman

The allotropic volume changes of the ,metallic elements are reviezoed with the conclusion that in general atomic volume is conserved to better than 1 pct in such transformations. A table of the atomic volumes of the metallic elements is given and its use in considering the size factor in alloys is discussed. The importance of the concept of atomic-size factor, due to Hume-Rothery and coworkers,' is firmly established. Most attempts at quantitative formulations of this concept have employed the atomic radius (half some interatomic distance) as the measure of size and innumerable tables of such radii exist. This is probably, however, an unfortunate choice of parameter. Firstly, discussion in terms of interatomic distances requires a knowledge of the crystal structure. While this is known, except for a few cases, for the elemental structures, there are still many undetermined alloy structures. Secondly, except for the simpler structures, face-centered cubic (Al),* body-centered cubic (A2),* and hexagonal-close-packed (A3).* with ideal axial ratio, there is no unique in- teratomic distance, an m y decision must be made as to which distance, or which average of the distances, should be used. However, the most important point is that for metals the dominant bonding parameter can generally be expected to be atomic volume and not interatomic distance. This is perhaps most explicitly stated in the Wigner-Seitz cellular method.' In this approximation, cellular polyhedra of atomic volume v are replaced by spheres of radius Y,: 4/3 ?rs3 = v. That is, there is no reference to the interatomic distances. If atomic volume is in fact the dominant parameter, then in allotropic transformations we might expect to find atomic volume approximately conserved. For example, in the A1 ? A2 transformation we would thus have

Jan 1, 1965

By D. S. G. Hanson

The Flin Flon Mine has been in production for over fifty years, and current mining is dependent on pillar and remnant recovery. One of the last major blocks of ore, and an important economic entity to the Mine, is the North Main Shaft Pillar. A rock mechanics program was initiated through under' ground instrumentation and other subsequent analyses, to establish the degree of instability as min¬ing progressed. Several studies have been and will be undertaken to evaluate the general stability, and possibly improve the chances of stability during pillar recovery. The North Main Shaft Pillar is immediately bounded by cemented cut and fill supporting rib stopes which inturn are bounded by slag and waste filled stopes. The min¬ing method involves a modified longhole open stoping and slag fil¬ling sequence for each mining block in a general mining upwards scheme.

Jan 1, 1983

By Jack A. Simon, M. E. Hopkins

Coal is defined as a combustible rock that originated in the accumulation and physical and chemical alteration of vegetation. Coal can be ignited and burned like the wood that was man's earliest fuel, but coal gives more heat than the same amount of wood and has many industrial uses. Unlike wood, coal is not generally found on the surface of the ground but is mined from the solid rock of the earth. Before taking up the occurrence, formation, and the unique character of coal in the rock sequence, let us briefly consider the general character of all rocks in the crust of the earth. Relatively little is known about the very earliest history of the earth, although a number of logical theories have been developed. Manned exploration of the moon and the rocks returned to earth continue to provide some answers to questions concerning the earth's origin and history. The period of earth history with which we concern ourselves here begins after great areas of water had evolved on earth and substantial land areas of once molten (igneous) rock existed. Weathering and other processes that attacked the surface of the rocks reduced them to small particles. Water provided by rainfall transported this material, ultimately, to large bodies of water where it was deposited. Thus was initiated the geologic sequence of sedimentary rocks that lie above the once molten igneous rocks. The crust and upper mantle of the earth are made up of several large plates along which differential movement (primarily horizontal) takes place. Such movements, although small, are occurring today. These horizontal movements are accompanied by vertical movements causing important changes in the relative position of the continents and oceans. Low-lying coastal swamps with favorable climates are ideal locations for coal accumulation and burial by river-borne sediments, and large areas

Jan 1, 1981

By Henry F. Hebley

This paper brings within the compass of one comparatively brief article a general description of the situation concerning the nation's water resources. It touches upon the phenomenal growth in the demand for water supply and emphasizes the problems facing the coal industry both with regard to acid mine water drainage discharged from active and abandoned mines and the suspended solids discharged to the stream system from wet coal preparation plants.

Jan 4, 1953

By Leslie F. Tedsen, John E. Dorn, Alan E. Flanigan

It is necessary occasionally to use aluminum-alloy sheet where moderately elevated temperatures are encountered. Considerable attention has been directed toward determining the influence of "artificial aging" on the room-temperature properties of the precipitation-hardenable alloys, as testified by numerous company reports and by references I to 4. Investigations on the properties at elevated temperatures are few, however, and have not always covered the range of times and temperatures of greatest interest. The present investigation was instituted to overcome this deficiency. The work was done for the Office of Production Research and Development of the War Production Board, under the supervision of the War Metallurgy Committee, as a part of the "restricted" Project NRC-548. It has been released for publication by the Office of Production Research and Development. AS is well known, the high-strength aluminum alloys achieve their remarkable properties as a result of precipitation-hardening. In production they are subjected to a solution heat-treatment followed by quenching, to retain the supersaturated solid solution. The solution treatment is followed by "aging" (precipitation-hard- ening) either at room temperature or at a suitable elevated temperature. A considerable increase in tensile and compressive yield stresses results from precipitation at room temperature ("natural aging"). Through the elevated-temperature process ("artificial aging") it is possible to obtain values of yield stress considerably higher than those attainable by natural aging. The increase in yield stress is accompanied by a smaller gain in ultimate tensile stress and by a decrease in elongation. During the first stages of artificial aging the yield stress increases steadily until it reaches a maximum value. In this condition the material is said to be "fully aged." Further exposure results in "averaging," attended by a steady decrease in yield stress. In the production of the artificially aged materials, temperatures and times are selected to achieve full aging. The following important characteristics are associated with the process: 1. The higher the temperature, the more rapidly is the fully aged condition attained. :7

Jan 1, 1946

By Leslie F. Tedsen, Alan E. Flanigan, John E. Dorn

It is necessary occasionally to use aluminum-alloy sheet where moderately elevated temperatures are encountered. Considerable attention has been directed toward determining the influence of "artificial aging" on the room-temperature properties of the precipitation-hardenable alloys, as testified by numerous company reports and by references I to 4. Investigations on the properties at elevated temperatures are few, however, and have not always covered the range of times and temperatures of greatest interest. The present investigation was instituted to overcome this deficiency. The work was done for the Office of Production Research and Development of the War Production Board, under the supervision of the War Metallurgy Committee, as a part of the "restricted" Project NRC-548. It has been released for publication by the Office of Production Research and Development. AS is well known, the high-strength aluminum alloys achieve their remarkable properties as a result of precipitation-hardening. In production they are subjected to a solution heat-treatment followed by quenching, to retain the supersaturated solid solution. The solution treatment is followed by "aging" (precipitation-hard- ening) either at room temperature or at a suitable elevated temperature. A considerable increase in tensile and compressive yield stresses results from precipitation at room temperature ("natural aging"). Through the elevated-temperature process ("artificial aging") it is possible to obtain values of yield stress considerably higher than those attainable by natural aging. The increase in yield stress is accompanied by a smaller gain in ultimate tensile stress and by a decrease in elongation. During the first stages of artificial aging the yield stress increases steadily until it reaches a maximum value. In this condition the material is said to be "fully aged." Further exposure results in "averaging," attended by a steady decrease in yield stress. In the production of the artificially aged materials, temperatures and times are selected to achieve full aging. The following important characteristics are associated with the process: 1. The higher the temperature, the more rapidly is the fully aged condition attained. :7

Jan 1, 1946

By R. W. Cahn, C. D. Graham

Two predictions of the oriented growth theory of recrystallization textures have been tested by measuring the orientation dependence of the rate of growth of a single grain into a strained single crystal of aluminum, and determining the orientations of artificially and spontaneously nucleated grains growing preferentially into strained aluminum single crystals. Growth rates are found to be insensitive to orientation, except that new grains with orientations similar to the matrix or to a twin of the matrix have very low mobilities. Similarly, new grains growing preferentially into a strained crystal have random orientations, except that orientations near that of the matrix or its twins are avoided. The predictions of oriented growth theory are thus not confirmed. BASICALLY, the oriented growth theory of re-crystallization textures1 rests on the assumption that the rate of growth of a recrystallizing grain depends strongly on the orientation of the growing grain relative to the strained matrix into which it grows. In particular, the theory holds that in face-centered-cubic metals the orientation which corresponds to maximum growth rate is one in which the growing grain and the matrix are related by a rotation about a common <111> direction. The amount of rotation, as derived from several kinds of experiments,2-1 has been assigned various values, generally in the range between 20" and 40". (A <111> rotation of 60" is a twin relationship.) The conclusion that boundary migration rates depend strongly on orientation is based almost entirely on indirect evidence; there have been very few direct measurements of boundary migration rates as a function of orientation.* " The present investigation was undertaken to provide such measurements, to help make possible a decision between the oriented growth and oriented nilcleation theories of recrystal-lization textures. The basic experimental program consisted of measuring the rate of growth of a single recrystal-lizing grain consuming a strained single crystal, with the orientations of both grains preselected so that the effect of orientation on growth rate could be determined. A prerequisite for such an experiment is a strained single crystal which will support the growth of a new grain but which will not spontaneously nucleate new grains on heating. That is, the crystal must support the growth of a grain nucleated artificially, but contain no recrystalliza-tion nuclei which will become active at the testing temperature. Beck was apparently the first to note that such a condition could exist," and to make use of the condition for am experiment of the type described here.&apos; The present work was actually suggested, however, by a report of Tiedema". " that an aluminum single crystal strip, oriented with a (111) plane in the plane of the strip and a < 112> direction parallel to the tensile axis, would not recrystallize after 20 pet extension even when heated almost to the melting point, provided that the strip was heavily etched before being heated. This result could not be duplicated in the present work. In fact, it was found that any crystal which deformed in multiple slip (<100>, <112> and <111> orientations) underwent spontaneous nucleation after 15 pet extension, even if etched. However, crystals which deformed in single slip, and which did not develop heavy deformation bands, could be extended 15 pet without showing spontaneous nucleation at temperatures up to 600°C. Crystals oriented within about 10o of <110> which developed heavy deformation bands could be extended 10 pet without showing spontaneous nucleation. In all cases a heavy etch was required to prevent nucleation. Etching was necessary because of the presence of an oxide layer on the crystal surface at the time of straining, which leads to preferential nucleation at the surface.&apos;&apos; Grain Growth Rates Experimental Procedure and Results—Aluminum strips of 99.6 pet purity (principal impurities 0.19 pet Fe and 0.12 pet Si), 1 mm by 1 cm in cross section, were grown into single crystals of controlled orientation by the strain-anneal method of Fuji-wara.&apos;"&apos; " A sharp temperature gradient was maintained in the strips during growth by lowering them into a salt bath controlled at 650°C. Crystal orientations were determined by the etch-pit method of Barrett and Levenson" to an accuracy of ±2O. The crystals were extended by 10 or 15 pet in a simple hand operated tensile machine. Crystal orientations were rechecked after extension, and were found to be in agreement with the orientations predicted by the formula of Schmid and Boas." After extension, the grip ends of the single crystal specimen were cut off with a jeweller&apos;s saw, and the crystal heavily etched (at least 20 pet wt loss) in hot 10 pet Na or KOH solution. A region of severe local deformation was then introduced at one corner of the strip, usually by cutting off the corner with shears. Heating this end of the strip caused a large number of new grains to nucleate at the sheared edge. One of these grains grew to occupy the full width of the strip. The appearance of the strip at

Jan 1, 1957

By J. H. Nead

OBJECT THE experiments herein described were undertaken with a view to investigating thoroughly the influence of carbon on the tensile and impact physical properties of carbon steel. The original comprehensive plan included investigation of a series of steels with varying carbon contents over a wide range of heat treatments. These were to be studied as to their static tensile qualities, and also their resistance to shock as measured by the Charpy impact bending test. A thorough metallographic examination was likewise included in the schedule. The Charpy tests and the metallographic examination have not been completed to date, and are accordingly withheld for another report. All heat treatments, however, have been made, and the static tensile tests have been completed. A description of the procedure of the experiment and the results thus far obtained are therefore reported herein. CONCLUSIONS No attempt is made to draw general conclusions from these experiments, but the curves and the data are submitted as being of general importance and wide applicability.

Jan 12, 1915

By B. T. Brady

Rock mechanics, like all engineering disciplines, must have a theoretical foundation. The subject of this chapter is the formulation of analytical methods that may aid in the rational design and determination of the stability of engineering structures in competent brittle rock materials. By an engineering structure in rock, we mean any (1) excavated sub- surface opening, (2) open surface structure, or (3) system of openings in rock that is virtually self-supporting-that is, not requiring artificial systems to carry structural stresses.

Jan 1, 1970

By Harmel A. Dawson, Robert A. Wilson

First the basic steps to determine the values present and the minerals involved which are the basis for the metallurgical testing are presented in this paper. Next, choosing the process or processes indicated for treating an ore are discussed. This is followed by the test procedures used, the results of which will indicate amenability to treatment. These test procedures have been developed, used and proven effective in laboratory evaluations relative to plant processing. Special, uncommon processing is beyond the scope of the paper. Evalutation of test results and incorporation into the preliminary and final flow sheet for plant design are discussed. The value of a flow sheet, with material and water balances, to plant design is shown.

Jan 1, 1978

HARRY B. BARREN Harry B. Barren, born in Cleveland, Ohio, May 31, 1888, died in Indiana Harbor, Ind., on Mar. 18, 1918. After graduating from the Case School of. Applied Science of Cleveland, class of 1910, he spent a year at the Youngstown, Ohio, plant of the Carnegie Steel Co. and the following two years with the National Tube Co. in Lorraine, Ohio. In 1913, he went to Indiana Harbor as assistant superintendent of the blast furnaces of the Inland Steel Co. Four months later, he was made superintendent. On Feb. 11, 1914, he was married to Miss Anna E. Jones in Cleveland and is survived by his widow and two sons, and by his parents Mr. and Mrs. H. A. Barren, of Cleveland, and a brother Kenneth, a lieutenant in the 309th Engineers, stationed at Camp Taylor, Louisville, Ky. CHAS. H. JOHNSON Charles Harmany Johnson died Dec. 10, 1918, at his home in New Castle, Pa., after an illness of more than four weeks brought about by a complete nervous collapse. He was born near Clinton, Lawrence Co. Pa., July 9, 1870, a son of George W. and Elizabeth A. Johnson. His parents moved to New Castle when he was two years old, where he attended the public schools of New Castle. He then attended Allegheny College, and later Massachusetts Institute of Technology where he graduated as a mining engineer. For a year and a half after completing his work at Boston he was connected with the Mesaba Ore Range in Minnesota, and then returned to New Castle and became associated with his father in the operation of the old sheet mill, which was converted into a tin mill and later sold to the American Sheet and Tin Plate Co. Since that time he has been actively engaged with his father in the limestone business and other industries. At the time of his death Mr. Johnson was general manager of the Pittsburg Limestone Co., the G. W. Johnson Limestone Co., the Lawrence Limestone Co., the Keystone Limestone Co., and the Mahoning Limestone Co., all of which have quarries in Lawrence, Butler, Blair and Armstrong counties and also in Maryland and West Virginia. He was president of the Johnson Bronze Co., the National Stone Co., and the

Jan 3, 1919

By Carle R. Hayward

The growing importance of metallography has caused a corresponding interest in the improvement of apparatus for preparing specimens of metals and alloys for microscopic examination. The purpose of this paper is to describe an electric heating-furnace, a grinding- and polishing-machine, and a device for mounting specimens, which are used in the metallographical work at the Massachusetts Institute of Technology. These three pieces of apparatus were designed and made in the laboratory of the Institute, and each possesses some original features which may be of interest. Electric Heating-Furnace. The accurate control of heat necessary for metallographic work is best obtained by the electric-resistance furnace. Uufortunately, however, even the platinum-wound furnaces cleteriorate with use and ultimately burn out, while the cheaper resistance-materials are often short-lived. Since the resistance-coil must be replaced from time to time, it is of advantage to be able to make this change with as little trouble as possible, and this is an important feature in the furnace shown in Fig. 1. A is a cylindrical galvanized-iron can, with two handles, B. A porcelain tube, C, passes through the central hole in the cover of the can and rests upon the asbestos disk, D; the bottom of the tube is held in place by the asbestos ring, 3. The space, F, around the tube is filled with powdered magnesia. G is an ordinary assay-crucible, with the cover inverted so as to present a smooth top for supporting a second porcelain tube, H. The latter is wound with " Excello " resistance-tape, 0.014

Jan 1, 1912

By R. F. Hehemann, R. H. Goodenow

Thermal arrest, hot-stage microscopy, and transtnission electron microscopy techniques have been employed to study the transformations in low-carbon iron and Fe-9 pct Ni alloys. In continuous cooling experiments, each alloy transforms at an essentially constant temperature for cooling rates below the critical rate required for martensite formation. However, high-tenzperature transformation in pure iron takes place by a different mechanism than that in the 9 pct Ni alloys. Pure iron exhibits an equi-a a structure with a low and random dislocation density while the 9 pct Ni alloy exhibits a cell or lathlike substructure analogous to that of low-carbon martensite. This same substructure characterizes upper bainite in higher-carbon inaterials. UNTIL relatively recently, diffusionless transformations have been considered to take place by the same mechanism and have been termed mar-tensitic transformations.l-3 The most characteristic feature2 of this mode of transformation is the shape change produced by a shear deformation and growth of the product phase frequently occurs at an extremely high velocity approaching that of an elastic wave.4&apos;5 A different mechanism of diffusionless transformation was recognized first in Cu-Ga and other copper-base alloys.6,7 From the absence of surface tilting in these alloys, it has been concluded that transformation is not accomplished by the cooperative shear displacements that occur in mar-tensitic reactions. Transformation presumably takes place by the rapid movement of an incoherent interface which is capable of propagating across parent grain boundaries. Although the transformation is diffusionless in the macroscopic sense, advancement of these interfaces is accomplished by an atom by atom rearrangement. Transformations of this type therefore require thermal activation and are generally operative only at high temperature. Although requiring short-range diffusion at the interface, propagation still occurs so rapidly that the reaction cannot be suppressed with normal cooling rates.7 The resulting microstructures exhibit large, irregular-shaped regions of the product phase, which are essentially free of crystallographic features. Consequently, these reactions have been termed massive transformations. Transformation by the massive mechanism has been reported to occur in ferrous systems involving pure iron and binary alloys of iron with nickel, chromium, and silicon by Gilbert and owen.&apos; The Fe-Ni system is of special interest in that the massive transformation was observed in alloys with less than 15 pct Ni while alloys having more than about 28 pct Ni transformed by the conventional mar-tensitic mechanism. By employing cooling rates substantially higher than those used by Gilbert and Owen, Swanson and Parr have been able to suppress the massive transformation in alloys with 0 to 10 pct Ni9 and produce martensite as revealed by surface relief. The massive transformation in the alloys having less than 15 pct Ni was identified by the lack of surface relief and an irregular rather than clearly acicular microstructure.&apos; Speich and Swann, using thin-foil electron microscopy, identified three distinctly different structures10 in quenched binary Fe-Ni alloys. From 0 to 4 pct Ni the structure consisted of blocky grains of a with a low and random dislocation density. Alloys with 4 to 25 pct Ni exhibited a cell structure with a high dislocation density; and at greater than 25 pct Ni the structure consisted of internally twinned plates. The structural change at approximately 4 pct Ni suggests that alloys with low nickel content transform by a different mechanism than those with intermediate nickel contents and the transition from the cellular to the internally twinned structures at approximately 25 pct Ni is analogous to the transition from needles to internally twinned plates that occurs over a narrow range of carbon contents in Fe-C martensites.11,12 Conventional bainitic and martensitic modes of austenite decomposition operate in ternary Fe-C-Ni alloys having less than 10 pct Ni. This investigation was conducted in order to explore the conditions under which the massive, bainitic, and martensitic transformations occur and the relationships between these modes of decomposition.

Jan 1, 1965

By A. A. Bauer, F. A. Rough, G. H. Beatty

AS a result of recent studies, the constitution of the zirconium-uranium system has been fairly well defined. A diagram for the system is shown in Fig. 1. However, both oxygen and nitrogen are known1-3 to have a pronounced effect on the limits of both ß- and e -phase regions. It has been shown that small amounts of oxygen severely constrict the compositional limits of these phase regions in the ternary zirconium-uranium-oxygen system. A previously published tentative diagram shown in Fig. 2 illustrates the ß-phase constriction resulting from oxygen additions. Generally, iodide zirconium has been used in constitutional studies of zirconium-uranium alloys. While this is the highest purity material available, cast iodide zirconium-uranium alloys will generally average from 200 to 300 ppm 0 and from 50 to 60 ppm N. Thus, while the constitution of the zirconium-uranium system is fairly well defined, it must be realized that this definition applies to alloys containing in the vicinity of 250 ppm 0 and 50 ppm N. The present investigation was undertaken to accurately determine the boundary between the ß-plus-P and ß phases at a single temperature in the binary zirconium-uranium system by quantitatively

Jan 1, 1959