By W. A. Tiller, S. O’Hara

Grain refinement in stirred melts has previously been shown to arise from dendrite segmentation. The present work discusses experiments capable of distinguishing between remelting and mechanical effects which result from fluid motion. Nucleation of still un-dercooled Sn-1 pct Pb melts with a single-crystal seed shows that the grain size of the resulting ingots decreases as the undercooling at nucleation increases up to about 1Z0C, then increases again for larger undercoolings. Pure melts exhibit little refinement as a result of nucleation at any undercooling up to 12°C. The presence of fluid motion gives rise to grain multiplication in pure melts, but the magnitude of this effect is partly obscured by solid-state pain growth. The results indicate that two grain-multiplication pvocesses can operate, one which involves dendrite remelt ing, and another associated with fluid motion. Small ingot experiments indicated that an equiaxed transition can be caused by fluid motion. THE presence of forced convection during recales-cence of undercooled Sn-1.3 pct Pb melts has been shown to give rise to extensive grain refinement during solidification of small ingots of this alloy.''2 In Ref. 2, this refining was shown to result entirely from dendrite fragmentation and not from any nucleation mechanism. The purpose of the present work is to establish what processes lead to dendrite segmentation. Experiments were therefore carried out to determine the resulting structure of both pure tin and Sn-1 pct Pb melts, nucleated at various undercoolings by single-crystal seeds in the absence of forced or natural convection. By comparing the information obtained from these experiments with the results of Refs. 1 and 2, the effects of fluid motion on the ingot structure, and the details of the segmentation mechanisms, should become clear. The results of these experiments should also be helpful in understanding the solidification structures of larger ingots since natural convection, which is known to play an important role in determining ingot structure13 differs only in degree from the fluid-motion effects studied here. I) EXPERIMENTAL PROCEDURE The apparatus shown in Fig. 1 was constructed to permit controlled nucleation of stirred or unstirred supercooled melts using a seed oriented in the tin dendrite growth direction. Because the melts, in all cases, were capable of larger supercoolings than the one used in each experiment, the structure observed always resulted from a single nucleation event at the surface. The sequential procedure was as follows: Tin was melted under purified hydrogen and the oxide removed at a temperature of 450°C . Electromagnetic stirring was then used to clear the surface completely and during this time the guide tube was lowered underneath the melt surface. A pointed Czochralski-like crystal was then propagated from a specially prepared tin dendrite seed4 inside the guide tube while the temperature of the bulk melt was held just above the melting point, ensuring a perfectly clean seed which was epitaxial with the original dendrite. The dendrite and epitaxial seed, still in the guide tube, were withdrawn from the melt which, in turn, was undercooled to 2C° below the temperature at which the nucleation experiment was to be performed. The melt was held there for several minutes, both in stirred and in still-melt experiments. The temperature was next raised to the required value and the melt nucleated by the carrot seed inside the guide tube, the heater power being shut off just after nucleation. In experiments where quenching after nucleation was required, a high-density graphite crucible was used, but otherwise the procedure was as described above. The temperature gradient in the melt before nucleation was kept below 1C° per cm by carrying the experiment out just below the center of the heater shown in Fig. 1.

Jan 1, 1968

By Sheldon Rideout, E. L. Kamen, B. S. Lement, Paul A. Beck, W. D. Manly

The 1200°C isothermal sections of the following ternary phase diagrams were investigated: Cr-Co-Nil Cr-Co-Fe, Cr-Co-Mot and Cr-Ni-Mo. In all these systems the u phase was found to form extended solid solutions. Two new ternary phases of unknown structure were identified. The existence range of intermediate phases of transition elements was correlated with 3d electron vacancy concentrations. THE occurrence of extensive ternary d solid solutions in the Cr-Co-Ni and in the Cr-Co-Fe systems was described in a brief note.' More recently d- solid solutions were also found in the Cr-Fe-Mo system by two independent groups of investigators.2,3 The existence of binary d phases in the V-Co and V-Ni systems, predicted in ref. 1, was experimentally discovered recently by Duwez and Baen and independently by W. B. Pearson, J. W. Christian, and W. Hume-Rothery.5 Duwez and Baen stated two general conditions for the occurrence of the d phase in alloys of the transition elements: "(1) The atomic diameters of the two metals do not differ by more than 8 per cent. (2) One of the two metals has a body-centered cubic structure while the other is face-centered cubic, at least in one of its allotropic forms." In the course of an extensive research program conducted at this Laboratory under the sponsorship of the NACA, several ternary systems, containing d solid solutions and also certain new ternary phases, were investigated. The present report describes the investigated portions of the 1200°C isothermal sections of the following ternary phase diagrams: Cr- Co-Ni, Cr-Co-Fe, Cr-Co-Mo, and Cr-Ni-Mo. It was found that the range of existence of the d phase in these four ternary systems, as well as in one of two ternary systems which were investigated by others, can be fairly consistently described in terms of electron vacancy concentrations. This supports the suggestion of Sully and Heal" that the d phase is an electron compound. Experimental Procedure The ternary alloys were prepared by vacuum induction melting in zirconia and alumina crucibles. Lot analyses of the metals used are given in Table I. Specimens of all alloys were annealed at 1200°C in an atmosphere of purified 92 pct helium and 8 pct hydrogen mixture. Alloys consisting mainly of

Jan 1, 1952

By C. Y. Garber

INTEREST in the sink-float plant operated by the Bunker Hill and Sullivan Mining and Concentrating Co. at Kellogg, Idaho, has recently been largely confined to the preparation and reconditioning of the galena medium. The ease and simplicity of these operations in a concentrating mill producing a flotation lead concentrate has occasioned enough comment to possibly justify a brief description. The subject is treated from an operator's viewpoint only; no effort is made to discuss it in a theoretical or technical manner. PLANT AT BUNKER HILL The sink-float plant was first operated in December 1941. It was built for the purpose of quickly increasing mill capacity with a minimum of equipment. It is the Huntington-Heberlein sink and float process using galena medium and is operated under license from the Sink and Float Corporation, New York city. Lead-zinc ore from the Bunker Hill mine is crushed to pass a I ¼ in. screen and is then washed and separated on vibrating screens having 4 ½ -mm. round-hole punched plates. The screen undersize, amounting to 33 per cent of the mill feed, is dewatered and sent to the ball-mill feed bins. The screen oversize goes to the sink-float plant, where 50 per cent of the oversize, or 33 per cent of the mill feed, is float, which is washed free of medium and disposed of as a tailing. The remaining 33 per cent is sink, which, after washing, is crushed to pass ½ in. and joins the undersize in the ball-mill feed bins. The normal plant capacity is 1700 tons per 24 hr. About 1.7 per cent of the total lead and 3.3 per cent of the total zinc in the feed is lost with the sink-float tailings (Table I). [ ] More complete descriptions of the H. H. process and Bunker Hill sink-float plant are given in several recent articles, listed at the end of the paper. PREPARATION OF MEDIUM AT BUNKER HILL New medium is made intermittently as needed, usually 12 hr. in each 6 days. A small portion of the current mill flotation concentrate is diverted from the lead cleaner cells to a I-in. vertical sand pump and pumped to a two-cell 36-in. Agitair flotation machine, where NaCn and ZnSO4 are added and the grade of concentrate is improved as shown in Table 2. Tailing from this operation is returned by gravity

Jan 1, 1946

By W. A. Krivsky, R. Schumann

Relaxation calculations were made to find the temperature distribution in the refractory wall surrounding a tuyere pipe. One set of boundary conditions approxiwated those of a standard copper converter while a second set represented a hypothetical,thermally insulated tuyere pipe. The pvonounced cooling effect of the tuyere is related to the problem of tuyere accretions and tuyere bunching. PARTICULARLY severe service conditions are encountered in the tuyere zone of a basic copper converter during the matte blow. High-temperature gradients result from the juxtaposition of the hot charge and the tuyere pipe carrying cold air. Refractory temperatures near the tuyere mouth vary rapidly with time when the blast is turned on or off. One of the most serious problems is the formation of magnetite accretions around the tuyere mouth, which occurs very rapidly under some operating conditions. As a result, continual punching of the tuyeres is necessary to maintain a satisfactory rate of converting. Thus, if some means could be devised for keeping the tuyere pipes fully open without necessity for punching, a considerable saving should result from reduction in labor cost, maintenance of full capacity operation, and reduction in refractory costs. Recent quantitative studies of the FeO-Fe,O,-SiO, system1 have shown that the solubility of magnetite in iron-silicate slags decreases rapidly with de- creasing temperature in the range of copper converting temperatures. Data taken from the previous work are shown in Fig. 1. Thus the formation of "horns" and accretions around the tuyere mouth can result simply from the freezing out of magnetite on the cooler areas of refractory immediately adjacent to the tuyere pipes. One might expect to find a correlation between the severity of magnetite formation and the area of refractory surface which is cooled below the freezing point of the slag (corresponding to magnetite precipitation). Magnetite itself has a very high melting point (1597°C) so that the accretions are for all practical purposes infusible. The accretions might be dissolved by increasing the silica content of the slag and at the same time raising the temperature, but this approach is not feasible because it results in rapid corrosion of the basic refractory lining of the converter as a whole. In order to understand better the problems involved in tuyere design and operation, it seems essential to have at least a semiquantitative idea of the thermal conditions in the tuyere zone. Accordingly, this paper presents results of thermal calculations for an idealized copper converter tuyere. These calculations follow the so-called relaxation

Jan 1, 1960

By Michael P. Richardson

INTRODUCTION This paper is intended to be a summation of the state-of-the-art i n draw theory and draw- point spacing. Knowledge of this very important factor in the successful design and operation of a block caving mine is scarce and nonconclusive. It is hoped that the presentation of this paper will stimulate interest and discussion which will lead to a stronger understanding of these a1 1 important factors. Please note that block caving as used here- in refers to block, panel, and mass caving systems in general, not just to the specific system of block caving where discrete blocks of ore are prepared and caved as a unit. DRAW THEORY The knowledge of draw theory as related to the practice of block caving mines is, unfortunately, very limited. In recent years much work in draw theory has been done in respect to sublevel caving systems and an understanding of draw mechanics relating to sublevel caving seems to be emerging. This work is certainly helpful to those of us interested in block caving but the question of "what goes on up above" still hounds us since we are more interested in the region of draw which begins just above the area where sublevel caving interest ends. Herein is presented a brief summary of draw theory with an attempt to look at the factors which can help our understanding of the area of draw influence in block caving mines. Nature of Gravity Flow An understanding of the flow of granular material (rock, sand, grain, or prill as examples) is the first step toward understanding block caving draw. If we take a supported column of granular material and allow gravity flow through an aperture at the bottom of the column, an ellipsoidal shaped zone of disturbance of the in-place material will form and grow with extraction of material through the aperture. The volume of this zone of disturbance or loosening is about 15 times the volume of material extracted at any given time (Kvapil, 1980). Figure 1 shows the development over time of the zone of disturbance. The ellipsoid of disturbance represents a future ellipsoid of extraction which will equate to the volume of materia1 extracted by that future time. Extraction involves the movement of the particles located vertically over the drawhole directly downward while material outside this direct vertical volume moves radially inward and down toward the drawpoint as shown in Figure 2a. Figure 2b shows the result of this motion on originally horizontal strata within the ore column. Increased draw increases the eccentricity of the ellipsoidal volume or, in other words, the ratio of the height over the width of the disturbed area increases as ore is withdrawn from the column (Kvapil , 1980). This becomes important to block caving since eventually a vertical cylinder of draw will be approximated as this ratio increases without bounds. Figure 3 shows this result. The width of this draw cylinder is a critical dimension for the determination of draw point spacing in relationship to block caving mine design. McCormick (1968) for one, felt that within this cylinder of draw, mass flow would take place. This is the

Jan 1, 1981

By G. Sandoz

A simple diffusion-couple experiment was carried out for the purpose of determining whether chromium in sufficient amounts would cause the cementite phase in cast irons to become thermodynamically stable with respect to graphite and austenite at 1750°F. The implications of the results to some current theories on graphitization mechanisms are discussed. The literature abounds with evidence that chromium retards the decomposition of cementite to graphite and austenite or ferrite, for example during first-stage and second-stage graphitization in malleabilizing white cast irons and the subcritical graphitization of steels. Efforts to explain this retarding action of chromium have been conjectural, however, because the mechanisms controlling graphitization kinetics in the absence of chromium have never been clearly established. Concerning rate control, there are basically two schools of thought: 1) that graphitization rates are limited by diffusion potential (the stability of cementite relative to graphite, and 2) that graphitization rates are limited by diffusivity of Fe, C, Si, vacancies, and so forth.5'10 Chromium then, is thought either to increase the stability of cementite or to retard some critical diffusion process.

Jan 1, 1960

By E. W. Lithgow, E. G. Williams, R. R. Holbrook, B. R. Wilson

The mineralogy and geochemistry of Pennsylvanian shales and underclays were studied to determine their suitability for lightweight aggregate and refractory ladle brick. Eighty percent of the variation in bloating of shales and clays was explained by the variation of Si02, A1203, and fluxes (Fe203, MgO, CaO, Na20, and K20); 60% by variation in quartz, kaolinite, illite, and chlorite. The best bloating was exhibited by marine shales, whereas freshwater shales and underclays experienced little or no expansion. Regional paleogeographic maps o f Pottsville and Allegheny shales permit bloating to be geographically predicted. It was found that clays meeting the specifications for refractory ladle bricks were obtained from underclays having over 34.5% mica, over 40% kaolinite and less than 15% quartz. Underclays of this composition are confined to the lower Allegheney outcropping along the near-margins of the coal basin. The best clay is that underlying the Lower Kittanning coal. Porosity of the first fired brick was found to be inversely correlated with reheat expansion.

Jan 1, 1975

By C. S. Smith

QUANTITATIVE methods were used to good effect in the earliest days of metallography1-3 but they mysteriously passed into virtual disuse until the important paper4 by Howard and Cohen in 1947. Various devices for the measurements of integrated linear intercepts have been constructed, primarily by petrographers. The hydraulically operated stage designed by the writer5 was satisfactory, but prolonged use caused air bubbles to become entrapped, which introduced back-lash. A new stage has been constructed which avoids this defect and provides better integration when measuring directional structures. This utilizes a circular traverse, and integration is achieved by counting electrical pulses produced by a photocell and a light chopper.* The stage is shown diagramatically in Fig. 1 and in photograph, Fig. 2. It is of simple construction. Mounted on a plate with clamps to fit the stage of a standard metallurgical microscope is a worm and 100-tooth worm gear, the latter supporting the specimen to be measured. The worm is manually actuated by a knob which contains inside it three

Jan 1, 1961

(Members are urged to send in for this column any notes of interest concerning themselves or their fellow-members.) Members and guests who registered at Institute headquarters during the period July 10 to Aug. 10, 1915: William H. Rettie, Yonkers, N. Y. Paul S. King, Wilmington, Del. A. J. Eveland, Pachuca, Mexico. E. E. R. Tratman, Chicago, 111. Chang Fu Wang, Shanghai, China. Courtenay Dekalb, Tucson, Ariz. F. H. Fovargue, Terlingua, Tex. Emil Gathmann, Baltimore, Md. W. W. Elmer, Tuttletown, Cal. Henry S. Drinker, E. M., LL. D., has just completed 10 years' service as President of Lehigh University. A notable gathering of alumni, with their wives and daughters, numbering more than 1,000 persons, met in South Bethlehem on June 5. In accordance with the request of Dr. Drinker, no formal celebration was held, but, nevertheless, a spontaneous and enthusiastic expression- of appreciation and affection was voiced by alumni, students and faculty, testifying to the regard felt for Dr. Drinker and extolling the progress made by the University under his guidance.

Jan 9, 1915

Prof. Henry M Howe, New York: It is extremely probable that this efflorescence of silica is due to the liquation either of silicon or of a silicide, and the subsequent oxidation of the silicon to silica. As Mr. Fackenthal says, it is very hard to see why silicon should liquate from an iron containing so little silicon, and it seems more probable that some silicide of some volatile element has liquated, and has dissociated on reaching the air, and that the volatile element has volatilized, leaving the silicon to oxidize to silica. The volatile elements present which might thus liquate in combination with the silicon are sulphur, zinc, and lead. It is hard to see why sulphide of silicon should have liquated from an iron containing so little of either sulphur or silicon. At first, one naturally thinks that either the zinc or the lead present in this furnace might have liquated as silicide. It is true that they are both volatile at the temperature within the furnace, but then the vapor-tension* of each of them within

Jan 1, 1901

By Freeman Bishop

Senator Henry M. Jackson t D. Wash.) recently tossed a live grenade into the hardrock mining industry with proposed legislation to change provisions of the law governing Federally owned mineral values. Title Two of the measure would place hardrock mining agreements on a leasing basis similar to that which has applied to oil and gas since 1920. Known as the "Public Domain Lands Organic Act 01 1971" or S.921, the bill would monitor exploration by heavy machinery which ran destroy fragile ecology without any requirement for restoration or rehabilitation." Jackson said. Abandoned mining claims, lie continued, dot the public domain, "casting clouds upon the title to property which belongs to all the people.” and a minerals leasing system is "the most practical way of achieving the proper balance."

Jan 1, 1971

By P. Payson

Intergranular corrosion in corrosion-resistant chromium-nickel steels has been widely discussed in the last few years. So far as the author knows, nothing has been published which definitely shows that this tendency can be eliminated, although suggestions have been made that a remedy is possible if certain specifications are satisfied. Strauss, Schottky and Hinnüberl suggested an increase in chromium content to an extent that would prevent the impoverishment of chromium on carbide precipitation sufficient to cause impaired corrosion resistance in the matrix. Pilling2 suggested an increase in nickel, so that the stability of the austenite matrix would be increased. Aborn and Bain3 say that "intergranular attack—may be eliminated by preventing carbide precipitation (e. g., by lowering the carbon content or somehow raising its solubility) or by precipitating it permanently under conditions which will not remove chromium from solid solution so drastically at any points." In a later paper Aborn and Bain4 state that many different metallic elements, tungsten, vanadium, copper, aluminum, molybdenum, titanium and zirconium, have been added in small percentages to increase the stability of these alloys, but that it has been reported that according to the copper sulfate test these added elements act only to retard the intergranular corrosion. and that increased nickel and chromium contents have similar effects. Newell5 showed that the lower the quenching temperature before reheating, the less severe was the intergranular attack.

Jan 1, 1932

The Howe Memorial Lecture, in memory of Henry Marion Howe, Past President of the Institute, was authorized in April, 1923, as an annual address to be delivered by invitation under the auspices of the Institute by an individual of recognized and outstanding attainment in the science and practice of iron and steel metallurgy or metallography, chosen by the Board of Directors upon recommendation of the Iron and Steel Division. The following were the Howe lectures and lecturers for the years indicated 1924 What is Steel? By Albert Sauveur. 1925 Austenite and Austenitic Steels. By John A. Mathews. 1926 Twenty-five Years of Metallography. By William Campbell. 1927 Alloy Steels. By Bradley Stoughton. 1928 Significance of the Simple Steel Analysis. By Harry D. Hibbard. 1929 Studies of Hadfield's Manganese Steel with the High-power Microscope. By John Howe Hall. 1930 The Future of the American Iron and Steel Industry. By Zay Jeffries. 1931 On the Art of Metallography. By Francis F. Lucas.

Jan 1, 1923

An appropriation of $4000 was made to the United Engineering Society for the support of the work of the Engineering Council. It was resolved that the proposed amendments to the Constitution, regarding requirements for membership, be sent to the membership without comment thereon by the Board of Directors. Forty-one members, and three associates were elected. The status of two junior members was changed to member. The resignation of one member was accepted. The dues of nineteen members who are engaged in active duty with the Allied armies were remitted. B. B. Thayer was elected a member of the Board of Trustees of the United Engineering Society for a period of three years, to succeed himself. John H. Janeway was elected a member of the Library Board for a period of four years, to succeed himself. George C. Stone was elected a member of the Library Board in place of E. F. Roeber, deceased. E. Gybbon Spilsbury was elected representative of this Institute on the John Fritz Medal Board of Award, to succeed himself. J. Parke Channing was elected a member of the Engineering Council for a period of three years, to succeed himself.

Jan 1, 1918

By H. K. Work

THE Bessemer process is one of the most interesting methods of making steel. At one time it was by far the most important. In recent years, however, it has steadily lost ground to the open-hearth process. The forces working against this method of steelmaking are partly economic and partly metallurgical.' In this paper, dealing as it does with the control of the process, the metallurgical factors alone will be considered, although it is obvious that economic factors must play a part in determining the ultimate status of the Bessemer process. This discussion has been limited in another respect-it deals primarily with the acid Bessemer process in bottom-blown converters, although much of the information is applicable to basic and side-blown converters. The fact that open-hearth steel has superseded Bessemer steel to a large extent has tended to create an impression that Bessemer steel is inferior. As a matter of fact, Bessemer steel is actually superior to open-hearth for many applications.2 There are, however, definite metallurgical limitations to the use of Bessemer steel, resulting largely from two factors: (I) the physical properties conferred by nitrogen and phosphorus, and (2) the variability from blow to blow. These, of course, are not entirely independent, since some of the variability covered in the second item is undoubtedly due to nitrogen. But the variability is also caused by other factors. One of these is the relatively small size of the Bessemer heats. Because of this, a given shipment of Bessemer steel is more likely than a shipment of open-hearth steel to contain the product of several heats, each with its own distinctive and slightly different characteristics. Added to this is the fact that the refining of Bessemer steel proceeds so rapidly that the timing of the end point is limited to a matter of seconds, whereas the finishing period in the open hearth extends over a period of one or two hours and the timing of the end point may vary by several minutes without seriously affecting the product. There is no doubt that this has contributed to the variability of Bessemer steel and has led to the use of open-hearth steel in many optional applications. That Bessemer steel may vary is not necessarily objectionable, and it may even prove an advantage, providing a precise control is available to secure the desired qualities for any specific application. With this in mind, a comprehensive research program was undertaken, one phase of which was directed toward securing more accurate control of the blow. The results have been encouraging, and it is the purpose of this paper to describe a method in which modern scientific instruments, based on photocells, are currently being employed to assist the blower. THE CONTROL PROBLEM In this day of scientific control of technical processes, where the operating

Jan 1, 1941

By Luther B. Eames

J. V. N. DORR, New York, N. Y.-I have read Mr. Eames' excellent paper on this' subject with great interest, for besides being connected with the design and installation of the first modern countercurrent decantation plant, he was associated with me in the development of the thickener in the Black Hills some years earlier, and has now been operating the largest plant that has used this method of treatment. His, discussion, of the influence of different factors on the results obtained is quite thorough, but several features I think may not be apparent to the reader who has not studied the subject carefully. 1. Grade of Ore That Can Be Treated.-Mr. Eames has shown graphically that' the assay of all solutions increases directly as the grade of the ore treated. He has not emphasized, however, the fact that, as most operators prefer to keep the assay of pregnant solutions down below a certain figure in order to insure complete precipitation, an increase in ore value beyond a certain point means a proportional increase in solution precipitated and therefore not only an increase in the percentage of dissolved gold recovered, but an actual descrease in tailing loss. The importance of the influence of the percentage of moisture in the underflow on loss is made clear, and I. may add that unless it is quite evident that pulp can be safely settled to 50 per cent. solids, or more, it is usually advisable to use a continuous filter at the end of. a decantation plant to reduce losses in cyanide and gold. Dissolution in Thickeners.-The influence of a change of solution on silver dissolution has long been emphasized and most gold operators have. recognized the annoying way in which a gold ore after being agitated until nothing more can be dissolved will loosen up again when almost ready for the dump after the dissolved metal has been removed by decantation or filtration. Continuous decantation gives favorable conditions for this additional dissolution and a chance to recover most of what is thus dissolved. This is especially true if an extra tank is used in the series and barren solution added at the second tank from the end instead, of the first, as shown in Mr. Eames' Fig. 1. It can be calculated that the use of this tank will reduce the mechanical loss of cyanide by one-third and cut the gold loss as well; but the saving in gold or silver that may dissolve when the pulp is first diluted with weak solution may be as important.

Jan 4, 1917

By G. S. Cole, H. Biloni, G. F. Bolling

An experimental investigation of sovlze low .melting point alloys sJtows that a substvucture of isolated depressions can be the first manvestation of constitutional supercooling on solid-liquid interjaces veuealed by decanting. Electron-tni cvop vobe and wletallo gvaplic esanzinations, in tlze bulk belzind the interjace, oj the segregation associated with these isolated areas substantiate tlzei&apos;v depressed nature, since a solute of ko < 1 is enriched, and a solute of ko > 1 depleted. In contrast, the pox structuve, a set of projections often veported in the literature, leaves no trace oj. segvegation. These obserl;atims, accovlrpanied by a brief review of recent literature, point to inconsistencies between experirrental obsevvation and the idea that the fornzation of a projection is a causal step in the development of a cellular substructure. An argument is presented to show instead how it is plausible for substantial depvessiom to form in the pvesence of constitutional supercooling at dislocations threading the solid-liquid interjace. THE development of constitutional supercooling during growth from the melt leads to the formation of the cellular solidification substructure. This well-founded association between structure and instability has been basic in understanding cellular substructure and micro segregation; however, the initial formation of structure seems unclear. Rutter and Chalmers,&apos; in definitive experiments and theory, noted that in the presence of constitutional a planar interface might break down: "resulting in the formation of a small projection on an initially plane or uniformly curved interface." That is, the breakdown from a planar to a cellular interface was implied to be initiated via a projection into the unstable liquid. Later, Walton et (11. found that a structure of isolated projections, termed "pox", appeared at solid-liquid interfaces decanted under growth conditions near the onset of constitutional supercooling; the pox were taken as the indication of the instability promoted by the supercooling. Tiller and Rutter4 in their extensive work studied the shape transitions at decanted interfaces which were generally observed to proceed as— pox, "irregular cells", elongated cells, regular (hexagonal) cells, and so forth. The pox varied in size from lo-&apos; to 1CT4 cm, and tended to disappear as cells increased in number and regularity, but as noted,4 the first real array of cells did not seem to be a development from the pox. In fact these authors implied a lack of connection because they stated that the pox are denser on "irregular cells", and as cell boundaries increase in number (i.e., the cells become smaller) there is less need for the pox which do dis- appear. Thereafter, most authors dealing with either experiment or theory have accepted the reality of pox and have used them as a criterion for the onset of constitutional supercooling. In contrast, Spittle, Hunt, and smiths have now suggested that pox are irrelevant artifacts comprised of such things as entrapped oxide. This proposal invokes the observations of weinberg6 and chadwick7 each of whom have shown that the act of decanting leaves a residual liquid on a decanted interface; the remnant solid layer of the order 10 p may thus contain particles that might have been transported from the external surfaces, or elsewhere, during decanting. With the incentive of this suggestion,= some further experiments and a reexamination of the literature have been conducted, in order to question the validity of pox as evidence of an instability and to examine the initial development of the cellular substructure. 1) EXPERIMENTS Single crystals of zone-refined tin (-99.9999 pct) were grown from the melt in a controlled fashion with various, small concentration additions of lead and antimony, for which ko < 1 and > 1, respectively. The crystals were decanted at conditions near the onset of constitutional supercooling and were thus appropriate for observation of slight perturbations. It was possible to observe two types of small departure from smooth or "planar" interfaces in both cases of lead or antimony additions. Some were projections and others, if in regular array of any type, were depressions. The crystals were etched with suitable reagents progressively dissolving the decanted interface surface; projections left no record, but depressions were continuously associated with spotlike areas contrasting with the rest of the interface. Traverses were made with the beam of an electron microprobe across the regions of contrast; with lead addition the persistent spots were lead-rich, and with antimony addition the persistent spots were antimony-poor. This is consistent only with a dominant role for depressions, because if the projections had left spots but were incorrectly catalogued, a reversed observation should have been made; that is, the Pb(ko < 1) should have been depleted and the Sb(ko > 1) enriched. In the work of Cole and inegard, and elewhere, regular arrays of structure associated with the initial stage of instability have been shown, in photographs and represented as pox or projections. We believe this to be erroneous, by inference, since whenever a regular array was observed, in the present examination, it consisted of depressions, regardless of the nature of the solute, ko 1. Fig. 1 is reproduced8 as an ideal example of the possible optical illusion involved; the observer can satisfy himself from the distribution of illuminated areas that the markings are depressions. Fig. 2 from the present investigation is an interference photograph of an interface similar to that in Fig.

Jan 1, 1967

By H. E. Mauck

The many factors that control bumping must be carefully studied for each coal seam where bumps occur, and specifications known to exclude bumping should be incorporated in the mining plans. This calls for complete knowledge of the seam&apos;s characteristics and its adjacent strata, and in many instances these characteristics are not revealed until the seam is actually mined. Pressure and shock bumps, the two general types, occur jointly and separately. In this discussion no differentiation will be made. Whether pressure or shock, they are treated as bumps, and both must be eliminated. Bumps in mines have occurred in several places throughout the coal fields of the world. A study of many of these occurrences indicates that geologic characteristics, development planning, and mining procedure have contributed. But more specifically, there are conditions usually associated with bumps: thickness of cover, strong strata directly on or above the seam, a tough floor or bottom not subject to heaving, mountainous terrain, stressed and steeply pitching beds, and the proximity of faults and other geologic structures. Mine planning should incorporate these known factors (not necessarily in order of importance): 1) Main panel entries should be limited to those absolutely necessary to ventilate and serve the mine. This reduces the span over which stresses may be set up that will later throw excessive pressures on barrier and chain pillars when they are being removed. 2) Barrier pillars should be as wide as practicable so that they will be strong enough to carry the loads thrown on them when final mining is being carried out. 3) Pillars should never be fully recovered on both sides of a main entry development if the barrier and chain pillars are to be removed later. The excessive pressures placed on the main chain and pillar barriers by arching of the gob areas can result in bumping when these barriers are being removed. 4) Full seam extraction is better accomplished by driving to the mine boundary and then retreat-drawing all pillars. If there are natural boundaries in the mine—such as faults, want areas, and valleys —retreat should be started there. 5) Pillars should be uniform in size and shape. The entire development of the mine should call for uniform blocks with entries driven parallel and perpendicular. Only angle break-throughs should be driven when necessary for haulage, etc. 6) For better distribution of rock stresses and reduction of carrying loads per unit area, both chain and barrier pillars should be developed with the maximum dimensions. 7) Pillars should be open-ended when recovered. If they are oblong, the short side should be mined first. Both sides of a block should not be mined simultaneously, but under no circumstance should the lifts be cut together. 8) Pillar sprags should not be left in mining. If they are not recoverable, they should be rendered incapable of carrying loads. 9) Pillar lines should be as short as practicable. (Three or four blocks are adequate). Experience has shown that rooms should be driven up and retreated immediately. The longer a room stands, the more unfavorable the mining conditions. This contributes to bumping. 10) Pillars should not be split in abutment zones (high stress areas lying close to mined out areas) and if slabbing is necessary, it should be open-ended. 11) Pillars should be recovered in a straight line. Irregular pillar lines will allow excessive pressures thrown on the jutting points. Experience has shown that the lead end of the pillar line can be slightly in advance. 12) Pillar lines should be extracted as rapidly as possible. This appears to lessen pressures on the line and render abutment zones less hazardous. 13) Extraction planning should call for large, continuous robbed out areas. Robbing out an area too narrow to get a major fall of the strata above the seam tends to throw excessive pressures on a pillar line. 14) Timbering in pillar areas should be adequate but not excessive. Too heavy timbering or cribbing is likely to retard roof falls and throw excessive weight on the pillar line. 15) Experience has shown that when pillar lines have retreated 800 to 1000 ft from the solid, bumps can occur. Because this distance may vary in different seams, impact stresses should be studied for each individual condition. In any event, extra precautions should be taken against bumps in this area. This list of controlling factors may or may not be complete. It probably is not, but it covers most of the problem&apos;s significant aspects. The question is whether or not bumping can be eliminated. The answer is that bumping can be minimized and possibly eliminated if these and other established factors are thoughtfully considered and incorporated in the mining and extraction plans. If a mine has already been developed or the pattern set so that little change can be made, then it will be necessary to adjust to the most nearly practicable system that can incorporate the known factors.

Jan 1, 1959

By T. N. Dixon, J. E. Briggs

A study was made of numerical techniques for solving the large sets of simultaneous equations that arise in the mathematical mode ling of oil reservoir behavior. It was found that noniterative techniques, such as the Alternating Direction Implicit (ADI) method, as well as some other finite difference approximations, produce oscillatory or unsmooth results for large time steps. Estimates of time step sizes sufficient to avoid such behavior are given. A comparison was made of the Point Successive Over-Relaxation (PSOR), Two-Line Cyclic Chebyshev Semi-Iterative SOR (2LCC), and iterative ADI methods, with respect to speed of solution of a test problem. It was found that, when applicable, iterative ADI is fastest for problems involving many points, while 2LCC is preferable for smaller problems. INTRODUCTION With the advent of high speed, large memory, digital computers, there has been an increasing emphasis on the development of improved methods for simulating and predicting reservoir performance. Two-dimensional, three-phase reservoir models with various combinations of PVT effects, as well as gravity and capillary forces, are common throughout the industry. Such models are also available through consulting firms, to anyone desiring to use them. Three-dimensional models will probably be practical in only a few years. We conducted a study of some of the numerical methods used for solving the large sets of simultaneous equations that arise in such models. A typical set of equations for a reservoir model is shown below:

Jan 1, 1969

By N. F. Schulz, H. A. Lex, J. D. Zetterstrom

A green ball of iron ore faces many perils from the time it is formed until it finally emerges from the pelletizing furnace as a hardened pellet. For instance, if the rate of heat transfer into a ball is sufficient to produce vapor from either the free or combined water more rapidly than it can escape at a tolerable pressure, the ball may split, spall, or even explode, a failure commonly known as decrepitation. To avoid such failures, one must either limit the rate of heat transfer during the drying and preheating stages, at the expense of production rates, or improve the decrepitation resistance of the green balls. The latter remedy may often be accomplished through changes in ore preparation, balling procedures, or the judicious use of binders or other additives. INTRODUCTION Pelletization has become established as an especially desirable method for the agglomeration of fine taconite concentrates and it promises to be equally satisfactory for improving the physical structures of certain natural ores. A high-quality pelletized iron ore consists of uniformly sized spheres, usually about 1/2-in. diam, which are strong enough to resist abrasion and breakage during handling and which reduce well without disintegration in the blast furnace. The unfired agglomerates, "green balls", are subject to several destructive effects that must be avoided or minimized if a high-quality product is to be obtained by pelletization. Among these are abrasion and impact deformation or breakage during handling of the wet green balls, deformation and breakage by compressive forces in the bed of ore in the pel-letizing furnace, decrepitation during drying and preheating, wind erosion, and radial cracking at firing temperatures. Moisture condensation from the warm saturated gases downstream from the drying zone on wet, cool balls may cause bed collapse if it becomes excessive. Decrepitation is defined as the sudden disintegration of green balls, usually with an audible pop, that occurs when they are heated too rapidly during the drying or preheating stages of the pelletization process. The extent of ball disintegration may vary from merely splitting off a small fragment to almost total disintegration into the original ore particles making up the ball. Such ball destruction results in a decreased yield of pellets, and the fragments, which also tend to interfere by obstructing the gas flow through the bed, must eventually be screened from the fired product and recycled. The closely related type of ball failure that sometimes occurs during the high temperature firing stage, resulting in radial cracks without fragmentation, was not considered to be decrepitation for the purpose of this investigation. Failure by decrepitation is not usually a serious problem in the pelletization of taconite concentrates. The problem is significant, however, in the pelletization of some natural ores, especially those containing hydrous iron oxides. In some instances, economicd production rates cannot be maintained if the drying and preheating rates are slowed down enough to avoid decrepitation. OBJECTIVES This investigation was undertaken to: (1) Develop a practical laboratory means for quantitatively measuring the tendency for green balls to decrepitate in iron ore pelletizing furnaces, and (2) Investigate the causes and cures of ball decrepitation. MATERIALS Two iron ores were used in the work reported here: a taconite concentrate at 90% minus 325 mesh, containing 65.0% Fe, 8.4% SiO2, and no loss-on-ignition; and a crude oxidized ore at 54% minus 325 mesh, containing 59.1% Fe, 3.6% SiO2, 1.1% A12O3, and 9.5% loss-on-ignition. For a special test of effect of particle size distribution on decrepitation, two other

Jan 1, 1967