The editorial expenses for the preparation of the manuscript of the second edition, as for the first, were provided by grants of the Engineering Foundation and the Open Hearth Steel Committee of the Iron and Steel Division, AIME ; the Seeley W. Mudd Memorial Fund again sponsored the publication of this volume. The companies and research or educational institutions with which the authors, reviewers, and editors are connected also contributed much to the writing and editing of this book through their generous donations of time and travel and office expenses. And finally, the authors and others have given countless hours of their own time with no recompense but the satisfaction of a job well done. In order to give credit to the companies or educational institutions which made it possible for the members of the Editorial Board to devote considerable time to the revision of this book, the names of these members and their affiliations are recorded here as follows : W. O. Philbrook, Carnegie Institute of Technology M. B. Bever, Massachusetts Institute of Technology H. B. Emerick, Jones and Laughlin Steel Corporation B. M. Larsen, United States Steel Company A number of individuals suggested desirable changes in the book before rewriting was started. Almost all manuscripts were gone over critically by reviewers, and the resulting criticisms led to the correction of errors and omissions and greatly contributed to the accuracy and completeness of the text. Other people have supplied additional data or illustrations or assisted in other ways. While some of these contributors must remain anonymous because they are not known to the Editors, the cooperation of the following individuals is gratefully acknowledged : R. D. Allen, Republic Steel Corporation, Chicago Isadore Amdur, Massachusetts Institute of Technology Mary Baeyertz, Armour Research Foundation S. P. Bahmer, Republic Steel Corporation, Massillon E. C. Bain and Associates, United States Steel Company, Pittsburgh C. W. Briggs, Steel Founders' Society of America H. W. Briske, Wisconsin Steel Works

Jan 1, 1964

The editorial expenses for the preparation of the manuscript of the second edition, as for the first, were provided by grants of the Engineering Foundation and the Open Hearth Steel Committee of the Iron and Steel Division, AIME ; the Seeley W. Mudd Memorial Fund again sponsored the publication of this volume. The companies and research or educational institutions with which the authors, reviewers, and editors are connected also contributed much to the writing and editing of this book through their generous donations of time and travel and office expenses. And finally, the authors and others have given countless hours of their own time with no recompense but the satisfaction of a job well done. In order to give credit to the companies or educational institutions which made it possible for the members of the Editorial Board to devote considerable time to the revision of this book, the names of these members and their affiliations are recorded here as follows W. O. Philbrook, Carnegie Institute of Technology M. B. Bever, Massachusetts Institute of Technology H. B. Emerick, Jones and Laughlin Steel Corporation B. M. Larsen, United States Steel Company A number of individuals suggested desirable changes in the book before rewriting was started. Almost all manuscripts were gone over critically by reviewers, and the resulting criticisms led to the correction of errors and omissions and greatly contributed to the accuracy and completeness of the text. Other people have supplied additional data or illustrations or assisted in other ways. While some of these contributors must remain anonymous because they are not known to the Editors, the cooperation of the following individuals is gratefully acknowledged: R. D. Allen, Republic Steel Corporation, Chicago Isadore Amdur, Massachusetts Institute of Technology Mary Baeyertz, Armour Research Foundation S. P. Bahmer, Republic Steel Corporation, Massillon E. C. Bain and Associates, United States Steel Company, Pittsburgh C. W. Briggs, Steel Founders' Society of America H. W. Briske, Wisconsin Steel Works

Jan 1, 1951

By L. Grånäs, B. Aronsson

In a recent study of Fe-Si alloys Walter and Koch' observed pairs of dislocations in Fe-6.25 pct Si crystals rolled to reductions of 10 pct and subsequently annealed for 1 hr at 650°C. They interpreted these pairs as being due to stacking faults. From the spacing of the dislocations a stacking-fault energy of 15 to 19 ergs per sq cm was calculated. These authors did not pay any attention to the order -disorder phenomena in Fe-Si alloys. It is the purpose of this communication to report some preliminary results from a study of ordering and its influence on the plastic deformation of Fe-6.0 pct Si alloys. Our results suggest that the dislocation pairs observed by Walter and Koch may have been due to long-range order rather than to stacking faults. The alloys used in this investigation were prepared from pure electrolytic iron and silicon and were melted in argon. After hot working, strip tensile specimens were machined to a gage length of 70 mm and a thickness of 1 mm. The specimens were heat- treated for 2 hr at 1000°C, furnace-cooled, and subsequently deformed 2 pct in tension at 400°C. The strain rate was 5.6 X lo-' sec-'. Thin foils of the deformed specimens were prepared by means of the Bollman technique and examined in a Siemens Elmis-kop I at an accelerating voltage of 100 kv. In the Fe-Si system long-range ordering occurs at a silicon content of about 6 pct Si. In our alloys evidence for ordering is given by selected-area diffraction patterns which show extra reflections consistent with a super lattice of the D0 9 type. In addition, the dislocation arrangement in deformed specimens indicates that long-range order is present. A typical mi-crophotograph of a thin foil is shown in Fig. l. The dislocations are usually straight and parallel and laying in distinct directions. In the commonly observed (111) zone the projections of the dislocations are close to (113) and (oil). Observation of the image position indicates that the two dislocations in a pair have the same Burgers vector and hence constitute a superlattice dislocation.~ According to theory3 a superlattice dislocation in the DO3 structure consists of four ordinary dislocations connected by two types of antiphase boundaries as shown in Fig. 2. In our specimens only two dislocations in each pair have been observed, Fig. 1. The problem is to decide whether the area between these is a NN or a NNN antiphase boundary. Dark-field images using the (200) reflexion (the indices are defined with respect to the DO3-type superlattice) can

Jan 1, 1968

By Falih Ergunalp

REGULAR production of chrome in Turkey started in 1860 with the operation of the Bursa deposits (5, Fig. I). Others were discovered at Makri, near Fethiye (3, Fig. I). For 33 years Turkey remained the principal source of this mineral. While new discoveries were coming in elsewhere, Turkey's output declined until 1921, as a result of four successive wars, which ruined the economics of the country. In 1927 a revival came with the production of 18,000 tons. In that year the Société Minière de Fethiye was formed. This company now operates mines in the Vilayets of Aydin, Denizli, Burdur and Mentese, and it has reached a maximum production of between 80,000 and 90,000 tons annually. The Turkish output therefore increased from 29,000 tons in 1930 to 55,000 tons in 1931; and to 119,009 tons in 1934. The second phase in the increase in chrome production in Turkey came about in 1935, when the Government decided to reorganize and control the mineral industry of the country according to the principles of "government control" of the present regime. Up to that time the mineral resources of the country had been exploited by private concerns. In 1935, the M.T.A. (Maden Tetkik ve Arama) Institute (Institute of Mining Research and Geological Survey) was established by the Government to do the geological and geophysical survey work and discover new mineral resources for the country. Before the establishment of the M.T.A. Institute, the chief chrome-producing region was Fethiye (3 and 4, Fig. I). As a result of the extensive work of this bureau, many new chrome deposits have been discovered and are now in production. The operational field of the mineral industry was given to Eti Bank, another Government-sponsored and Government-controlled establishment. Eti Bank gradually took over the exploitation of existing mines by purchasing them from privately operated companies. Attention was first given to the Zonguldak collieries and to the different chrome deposits scattered over the country. The Guleman mines (14, Fig. 1) were developed and put in operation in 1936. Since then the bulk of Turkish chrome output has come from this mine, which yields the highest grade ore in the world (averaging 52 per cent Cr2O3). In 1939, the recently discovered chrome deposits to the north of Eskisehir went into production, yielding ore having a Cr2O3 content of 51 to 52 per cent. Today, more than ever, the efforts of both the M.T.A. Institute and the Eti Bank are concentrated on finding new deposits and placing them in operation. There are still many promising regions of the country that merit systematic surveying and prospecting for chrome ores. Thus it is probable that Turkey will continue to make noteworthy progress in chrome output. As the annual chrome production of

Jan 1, 1944

By M. E. Fine, A. A. Hendrickson

The critical resolved shear stress and the strain rate dependence of the .flow stress are reported for Ag base A1 single crystals up to 6 at. pct A1 over a temperature ralzge of 4.1° to 470°K. At room temperature the solid solution strengthening is attributed brinciballv to an increase in the dislocation density on alloying. At 42°K the alloys are relatively stronger because the dislocations widen on alloying and are more difficult to cut. In a previous paper, the authors reported the characteristics of strain aging in Ag base A1 alloys.' The variation of the magnitude of the strain-aging yield drops on aging time, aluminum content, and testing temperature strongly indicated that the phenomenon is due to the Suzuki mechanism. In the present paper, the critical resolved shear stress (CRSS) and the strain rate dependence of the flow stress are reported for Ag base A1 single crystals as functions of testing temperature (4.2" to 470") and A1 content (0 to 6 at. pct). Observations on the substructure and measurements of the effect of crystal growth rate are also given. The experimental re- sults appear explainable considering that aluminum additions increase the dislocation density and dislocation width. EXPERIMENTAL METHOD The methods of specimen preparation and tensile testing were described previously.' Briefly, single crystals were grown from the melt in a vacuum (1 x lom5 mm Hg), shaped into tensile samples by a combination of abrading and acid etching, annealed at 850°C in a vacuum (1 x 10" mm &Z) for several days, and furnace cooled to 200'. The testing was done on a model TM Instron using friction grips and a strain rate of about 5 x 106 per sec unless otherwise noted. The various testing temperatures were obtained by immersing the specimens in the following media: 1) 4.2': liquid helium using the apparatus of G. Byrne;' 2) 77°K: liquid nitrogen; 3) 200"K: dry ice and acetone; 4) 415' K: ethylene glycol; 5) 460' \ to 480' : molten Stanalax. In the determination of the CRSS above 296' K, a ratio method was used; the crystals were strained initially at the higher temperature, 0.1 pct shear strain, and then tested at 296' . The ratio of the flow stress between the two temperatures was then multiplied by the average CRSS at 296' K to obtain the value of the CRSS at the high temperature. (The test at 296' showed a yield point resulting from strain aging; the flow stress at 296' K was taken as the lower yield stress.) The ratio method, we believe, is more accurate than using different crystals since

Jan 1, 1962

By F. A. Crossley

The key to disagreements between Blackburn's findings and mine is the word equilibrium". My work attempted to define the equilibrium diagram of the titanium-rich end of the Ti-A1 system. It can readily be shown that Blackburn's conclusions are based primarily on the examination of structures substantially removed from equilibrium. The diagram presented in Fig. 16 is properly labeled a "phase diagram". However, it appears that Blackburn either does not understand or does not accept the difference between "phase diagram" and "equilibrium diagram" as defined in the Metals Handbook.17 The conflict lies not in Blackburn's data but in his interpretation of it, and his use of "transformation", "phase diagram", and "equilibrium diagram" as synonymous terms. I share his view that the light microscope is much inferior to the transmission electron microscope for the study of transformations; but this fact does not render the light microscope useless or untrustworthy. The difficulties experienced with the Ti-A1 system have not been due to the limitations of the light microscope, but rather to the extreme sluggishness in achieving equilibrium at temperatures below 1000° C. Were it not for the light microscope employed with polarized light, the twin phase syndrome' might still be unrecognized and, as a consequence, still adding to the confusion of Ti-A1 investigations. (Ref. 1 should read ... Contract No. N161-25952 ... vol. 236.) Other, more sophisticated techniques, including electron transmission, simply confirm the erroneous tentative conclusions drawn from observations of structures due to the twin-phase syndrome. By the standards of most of the investigations of the Ti-A1 systems, seven of the fifteen compositions investigated by Blackburn were seriously contaminated with oxygen. The writer has found that 0.1 wt pct 0 shifts the a + Ti3A1 boundary to 1 at. pct lower A1 content at 700°C. At constant aluminum content, this corresponds to a temperature shift of the boundary of +25°c.18 Blackburn advises that the first group of alloys contained 0.1 to 0.15 wt pct 0, bur he does say whether the analyses were performed on as-received material or on specimens in their final state of heat treatment. This is especially important considering the 20-mil-thick starting materials. If specimens had been annealed in the two-phase a + 6 region it would have provided an indication of the final degree of oxygen contamination since up to about 12 at. pct A1 the boundaries of this region are well-defined for low-oxygen alloys. Blackburn questions the capability of light microscopy in determining phase boundaries in the Ti-A1 system. I submit that the a/a + Ti3A1 boundary in Fig. 1 of Ref. 1 over the composition range from 10 to 18 at. pct A1 was determined by dilatometry and supported by electron diffraction. Specimens of alloys containing 8, 10, 12, and 14 at. pct A1 were aged at 550°C for 1000 hr (under stress of 5000 psi to accelerate the tendency to equilibrium) and then fractured in tension at room temperature. Collodion was applied to the as-fractured (unetched) surface and, when stripped, carried away particles identified by electron diffraction as Ti3A1. Perhaps Blackburn will explain why these electron diffraction data were ignored. At this time, a technique for revealing or indicating

Jan 1, 1969

By AIME AIME

JANUARY saw the completion of the 237-ft. Upper-Narrows hydraulic debris dam on the main Yuba River in northern California. This project which is the key unit in a series of four similar structures on the Bear, American, and Yuba Rivers, removes the last obstacle to the revival of California's vast hydraulic gold-mining industry. The Upper-Narrows dam is a single-arch type of structure, and embodies the latest developments in that type of construction. One of the principal innovations used is the series of air vents in the crown (that part over which the water spills) which serve to break the vacuum caused by the spilling water, thus reducing vibration to a minimum. Electric strain gages were also embedded in the concrete of the dam, and it is hoped that by careful study of these instruments true stresses can he determined.

Jan 1, 1941

By Glenn R. Zellars, J. P. Morris

The carrier gas method was used to measure the vapor pressure of copper over liquid copper and Fe-Cu alloys. From these results, the activity of copper in the alloys was determined at 146°, 1550°, and 1600°C. Calculations of the activity of iron were made from the results for copper. The activities of copper and iron show strong positive deviations from Raoult's law. KNOWLEDGE of vapor pressures of liquid metals has both practical and theoretical value. Fuming of metal baths is directly related to vapor pressure, and the data should bc particularly important to the technology of vacuum metallurgy. Theoretical applications include determinations of heats of vaporization, heats of solution, and activity coefficients in alloys. Methods for measuring vapor pressures of metals have been reviewed by Speiser and Spretnak.' High-vacuum procedures, such as the Langmuir and Knudsen methods, have been used most widely in recent years. However, these methods are not applicable to vapor pressures greater than lo-' mm Hg and often cannot be used in the temperature range of greatest interest. The purpose of this investigation was to develop a procedure for measuring vapor pressures of pure metals and alloys that would be applicable to pressures greater than lo-' mm Hg. The transportation or carrier gas method has been used. Copper was chosen for the initial work because its vapor pressure has been established fairly well and the reliability of the technique could be ascertained. Applicability to alloys was studied by determining the vapor pressure of copper over liquid Fe-Cu alloys. Experimental Procedure The tests were carried out in a graphite-spiral resistance furnace. The charge consisted of 50 g of metal contajned in a covered sintered-alumina crucible 1/2 in. deep and 13/8 in. ID. Two sintered-alumina tubes led from outside the furnace to within the crucible, passing through close-fitting holes in the crucible cover and radiation shield. The arrangement of the crucible and the two alumina tubes is shown in Fig. 1. The small-bore tube (1/16 in. ID by 5/16 in. OD) served as the inlet for the carrier gas. The tip of this tube touched the metal surface and the flow of gas imparted a rippling motion to the metal. In this manner the gas was brought into close contact with the metal and became saturated with metal vapor. In most of the tests the flow rate of the carrier gas was 560 ml per min, measured at room temperature. Approximately half of this saturated gas was allowed to escape from the crucible through the second alumina tube (3/16 in. ID by 5/16 in. OD) and was discharged to the atmosphere through a

Jan 1, 1957

By B. C. Allen

Surface free energy and surface self-diffusion of solid molybdenum were studied in the temperature range 1600" to 2400°C using pressure-sintered bi-crystals. Comparison of groove angles formed in various surfaces perpendicular to the grain boundary indicate a maximum of 1 pct variation in surface free energy with crystallographic mientation. This anisotropy tends to decrease with increasing temperature. The surface diffusion of the bicrystals is equivalent to that of sheet with a mild (100) Preferred orientation. Anomalously low values found for bi-crystals with surface orientations of (OOl), (012), and (011) are rationalized in terms of anisotropy in surface free energy. THE effect of crystallographic orientation on surface free energy1,' and surface self-diffusion3,4 has been primarily studied in fcc metals. The object of this work was to study the effect of orientation on surface diffusion and surface free energy of bcc molybdenum using pressure-sintered bicrystals. EXPERIMENTAL WORK Materials and Crystal Preparation. Arc-melted molybdenum rod was obtained commercially and electron beam zone refined at 50 cm per hr at 10- 5 torr to form single crystals about 8 cm long and 0.65 cm diam. Three crystals were prepared with axial orientations about 1 deg from [001.], [011], and. [111]. To reduce the carbon content, the crystals were annealed 2 hr in 1.4 atm flowing wet hydrogen at 2050°C. Then the oxygen content was reduced by annealing for 2 hr in -30°C dewpoint hydrogen at 2020°C. The resulting impurity analysis is given in Table I. Bicrystal Preparation. The single crystal rods were cut into transverse slices with a thin silicon carbide abrasive wheel to produce specimens about 0.6 cm long. They were mounted in epoxy and surrounded by stainless steel washers. Cutting in half was done longitudinally at various angles to known crystallographic planes containing the cylinder axis according to Fig. 1. To reduce surface deformation resulting from the cutoff wheel and thus reduce parasitic grain boundary formation on subsequent annealing, about 0.003 cm was manually ground off each cut surface with 600 grit paper. Care was taken to keep the surface flat. After removal from the mounts, one half was generally ro-tated 180 deg with respect to the other to give a po- tential symmetrical tilt grain boundary between the two halves. In the other cases when low misorienta-tion angles were desired, the crystals were not rotated. On the basis of symmetry, sufficient bicrystals were prepared to cover the entire range of misorientations for symmetrical tilt boundaries. The misorientations, +, ranged from 0 to 45, 0 to 90, and 0 to 60 deg for [001], [011], and [111] bicrystals, respectively. One [Ill] twist bicrystal was prepared from 2 single crystal discs rotated 17 deg relative to each other. Each specimen consisted of two pieces which were placed in a cylindrical tantalum can. Sharp edges were rounded and the fit was made as snug as possible to reduce subsequent deformation during bonding. The assembly and crystals generally were vicuum outgassed at 900" or 1700°C and then electron beam welded in the can at l x 10-4 torr. After being leak checked, the samples were placed in an autoclave and hydrostatically gas-pressure bonded5 in four batches under helium at 10,000 to 18,000 psi at 1650°C for 3 hr. Satisfactory bonds were obtained in many cases, and most of the crystals bonded after two exposures. The results did not appear to be affected by the various pressures used, preannealing conditions, crystal orientation, or time-pressure-temperature route taken to the final bonding condition. After bonding, the tantalum cans were selectively removed in cold concentrated HF. Measurements indicated overall deformation was under 1 pct. The bicrystals were metallographically ground and polished flat and perpendicular to the axis. Examination showed the boundaries were straight and almost free of parasitic grains caused by extraneous local deformation. Annealing. In preparation for thermal grooving, the bicrystals were cleaned and annealed by outgassing at 10-5 torr at 1900°C and heating at 2300°C under 1 atm 99.996 Ar for 0.5 hr. The crystals were held in a closed 4-deck box made of molybdenum sheet, and were heated in a Ta-1OW resistance furnace. The ar-

Jan 1, 1970

By L. C. Brown, C. St. John, C. C. Sanderson

The diffusion rate in Cu-Te couples is very sensitive to compressive stress, with a load of 20 psi making a significant difference to the width of the diffusion zone. At zero stress, two phases appear in the diffusion zone (Cu4Te3 and CuTe). Under compressive loading the third stable phase (Cuz Te) also appears, and its thickness increases progressively with increasing stress. The results are explained on the basis of an incipient Kirkendall porosity which restricts the transfer of atoms from the copper into the diffusion zone. DURING a study of the Kirkendall effect in Cu-Te couples prepared by clamping together the two components, it was found that the diffusion-zone width and shape in the plane of contact were not reproducible. Although the stresses involved in clamping are not normally sufficiently high to affect diffusion rates, preliminary tests established that the Cu-Te system is particularly stress-sensitive. The phase diagram for the system Cu-Te given in Hanssen1 shows that there is practically no solid solubility at either end of the phase diagram. Many areas of the diagram are not fully substantiated, but there appear to be three intermediate phases: Cu,Te—hexagonal in structure, having a grey luster; Cu4Te3—a tetragonal defect structure, having a red-purple luster; CuTe—orthorhombic in structure and having a golden-green luster. The existence of a fourth phase, the X phase at 37 at. pct Te, is considered doubtful. The composition ranges of the three stable phases are small, and are not accurately known. The phase diagram changes little with temperature up to 305°C, at which temperature a polymorphic transformation takes place in Cu2Te. The nature of the Cu-Te phase diagram indicates that the diffusion zone in a Cu-Te couple would consist of a series of layers of intermediate phases. The relative thickness of any one phase will depend on its diffusion coefficient and composition range.' In this type of diffusion couple it is often found experimentally that some phases are not visible at all in the diffusion zone due either to a small diffusion coefficient or to a restricted composition range.3 Since the composition ranges of the phases in Cu-Te are not known, it is not possible to determine diffusion coefficients in this system from a knowledge of the phase thicknesses. Several investigations have been carried out to determine the effect of compressive stress on diffusion rates in multiphase systems. Diffusion couples of Ni-A1 have been investigated by Storchheim et al.4 and by Castleman and Seigle.5 Two phases (ß and ?) appear in the diffusion zone under zero stress and the thickness of both phases is progressively reduced with increasing stress. According to Storchheim et al.4 a stress of 25,000 psi reduces the thickness of the diffusion zone by 50 pct. In a-brass—?-brass couples the thickness of the 0 phase formed in the diffusion zone was reduced by 20 pct at a stress of 20,000 psi.6 In other investigations the compressive load has been observed to increase the width of the diffusion zone. In A1-U, several investigators3,8 have found the width of the whase UA13 to increase with stress. According to casileman,8 the rate of formation of UA13 at 520°C is 75 pct faster at a stress of 20,000 psi as compared with a stress of 2500 psi. In Cu-Sb the effect of stress is greater than in the other systems described. According to Heumann9,10 only one phase (y) appears in the diffusion zone at a stress of 500 psi, but at a stress of 850 psi two phases (y and k) are present. If a diffusion couple containing both y and k phases is annealed at a low stress level, the y phase grows at the expense of the k phase. EXPERIMENTAL The diffusion couples were prepared from electrolytic copper bar stock with a nominal purity of 99.92 pct and from tellurium of 99.7 pct purity. The tellurium proved difficult to machine because of its brittleness and a technique was developed for casting the tellurium into a graphite slab mold and spark-machining specimens from this slab. Both the copper and tellurium were produced in the form of discs 2 in. diam by approximately 1/4 in. thick with surfaces ground flat to 3/0 emery paper. The diffusion apparatus is shown in Fig. 1. Auni-axial compressive stress was applied to the system through a simple lever system. A stainless-steel rod actuated by the lever arm lay inside a stainless-steel tube. The diffusion couple lay on top of the steel rod, and pressure was applied to the couple between the rod and a plug welded into the center of the tube. To ensure a uniform stress across the couple, a hemispherical boss and cup were used to transmit the load to the diffusion couple. A 400-w tube furnace with a uniform hot zone 3 in. long slid around the stainless-steel tube and maintained the assembly at temperature. A thermocouple situated 3 in. from the specimen operated a proportional temperature controller which maintained the specimen temperature constant to ±2°C. Most diffusion runs were carried out at 250C although a few tests were made at other temperatures in the range 235° to 300°C. The specimens were inserted and removed with the furnace at operating temperature, and took only 2 min to reach diffusion temperature—a time small compared with the total diffusion time. All the diffusion experiments were carried out in a hydrogen atmosphere, since consistent results were obtained in hydrogen and nitrogen atmospheres and in

Jan 1, 1967

By P. R. Swann, J. G. Parr

Quenched structures were studied in alloys containing up to 12.5 pct cobalt. The subsequent decomposition of a 10 pct cobalt retained-ß phase alloy was investigated using metallographic and X-ray diffraction methods. Hardness measurements also were made during the decomposition process. Precipitation of Ti2Co is by nucleation and growth; and an activation energy of 50,000 cal per mole was determined. The values of the coefficient ß suggest that the precipitate is pearlitic at temperatures between 450 and 475°C, and spheroidal between 500 and 525°C. THIS paper describes part of a series of invesligations into phase transformations in binary alloys of titanium with transition elements. The general approach is similar to that taken in work on titanium-iron and titanium-nickel alloys.' Previous investigators'' have established the titanium-rich end of the titanium-cobalt phase diagram, reproduced in Fig. 1. Orrell and Fontana' showed that alloys containing more than about 6 pct" cobalt quenched from the ß range, produced 100 pcl retained-p phase. The isothermal decomposition of alloys containing between 0.8 pct Co and 15.5 pct CO was investigated by the same workers in the temperature range 650 to 1000°C. They reported that these alloys transformed into a or Ti,Co depending on the cobalt content, but no quantitative data were given. In the work to be described a series of alloys containing 0.8 pct Co to 12.5 pct Co was examined in the quenched condition. The 10 pct Co alloy (the lowest cobalt content to retain 100 pct ß on quenching) was selected for further work on the tempering kinetics of the ß decomposition. Experimental Procedure Since our own melting equipment was not installed at the outset of this work, the Physical Metallurgy Division of the Department of Mines and Technical Surveys (Ottawa, Canada) prepared the alloys. These were made of Japanese sponge, (which when melted had a value of 103 DPH, using a 1-kg load), and electrolytically prepared cobalt. The al- loys, made up to contain 0.8, 1.6, 3.3, 5.8, 8.3, 10.0 and 12.5 pct Co, were homogenized by swaging into rods at 900°C. Filings were taken from the rods, and any iron chips from the file were separated magnetically. Size fractions of both plus and minus 200 mesh (about 75p) were shown by their constitution, after annealing just below the eutectoid temperature, to contain the same cobalt content. Consequently, it was permissible to use the —200-mesh fraction, knowing it to be representative of the rod composition. Quenching in argon was carried out in a newly designed furnace, whose features include (1) an Inconel furnace tube, (2) a positive pressure of argon maintained at all times in the furnace—even when a sample is removed or inserted. The furnace is shown in Fig. 2 and is described in the Appendix. The tempering processes were carried out on powder samples sealed in evacuated quartz capsules. Since the highest tempering temperature was 525OC, no protection against reaction with the quartz was necessary. (Tests were made on filings of iodide titanium and showed no hardness increase after equivalent heat-treatments.) A thermocouple was attached to the capsule, which was heated to the

Jan 1, 1959

By J. J. Gilman

Examination showed that characteristic cleavage step patterns are observed on the cleavage surfaces of undeformed, slipped, bent, twinned, compressed, and indented zinc crystals; and the effect of temperature is discussed. Dimples were seen to produce cleavage steps in a treelike pattern in otherwise undeformed crystals. The steps seem to originate when cracks intersect screw dislocations. IT has been known for a long time that the path of fracture in polycrystals may be discontinuous (see Jaffe, Reed, and Mannl for review). Recently, Kies, Sullivan, and Irwin2 have proposed, and given evidence, that crack propagation is discontinuous within individual crystals as well. Other evidence has been given by Low.' When discontinuous cracks within a crystal join together to make a macrocrack, the lamellae between each set of two cracks are torn somewhere, forming small cliffs. These cliffs appear as lines when the cleavage surface is observed microscopically.4,5 The lines have been called vein, tree, and riverlike markings by various authors, and they have sometimes been mistaken for fissures. The descriptive term cleavage steps is used in this paper. Cleavage steps vary in height over a wide range of values, from molecular dimensionsG to lor. and larger. Kies, Sullivan, and Irwin,2 as well as George,' have shown that the gross cleavage step patterns for plastics, polycrystalline metals, and for mono-crystals are sometimes similar. Thus, they depend mostly on the mechanical variables that prevail during cleavage and are relatively insensitive to the structure of the material. For example, parabolic markings2,7,8 sometimes result when cracks open up ahead of, and not coplanar with, the main crack front. If the advance crack has the same velocity as the main crack, their intersection line is a parabola, otherwise it is a hyperbola or an ellipse. The patterns are strongly affected by differences in crack velocities. This results in chevron patterns which point to the place of origin of the main crack. It is the purpose of this paper to demonstrate the existence of a mechanism of cleavage step formation which is a continuous rather than a discontinuous process. Also, certain characteristic step patterns are described, and the strong effect of temperature is shown. The specimens were zinc monocrystals (grown from 99.999+ pct pure metal). These were cleaved at room temperature and at — 196°C. Results and Discussion Cleavage step patterns are highly variable from point to point on a given specimen, as well as from one specimen to another. Although the patterns shown in the photographs are typical, they have been selected for graphic illustration. Figs. la and lb compare undeformed crystals that were cleaved at —196 °C and room temperature, respectively. Cleavage at room temperature (Fig. lb) resulted in a higher density of high steps (dark black lines) and enhanced the visibility of the fine background markings. Deformation by simple slip caused no marked change in the step patterns until the glide strain reached about 1.0. But, as Fig. lc shows, the density of high cleavage steps was greatly increased by large glide strains. Corrugations lying perpendicular to the slip direction may also be seen in Fig. lc. These are caused by deformation bands. The cleavage resistance of the crystal of Fig. lc was very high compared to undeformed crystals (estimated by the force on a needle required for cleavage). Striking and varied cleavage step patterns were observed on bent crystals. Two characteristic patterns that were observed on crystals bent at 25°C, and cleaved by reverse bending at —196°C, are shown in Figs. 2a and 2b. The first, Fig. 2a, consists of V-shaped lines similar to the parabolas of other materials2,7 Fig. 2b shows a pattern that is the equivalent of Fig. la, consisting of faint background lines with a few higher step markings. Cleavage of bent crystals at room temperature resulted in Figs. 2c and 2d. Now, the cleavage step lines show a strong tendency to follow one of two perpendicular paths. In Fig. 2c (bent once), many of the cleavage step components that lie parallel to the bend axis are assembled into irregular lines. In Fig. 2d (bent twice), the cleavage steps again tend to consist of two perpendicular components, but neither of the components is assembled into lines. Also, the step density is higher.

Jan 1, 1956

Jan 1, 1935

By G. W. Reimers, S. E. Khalafalla

A colloidal solution of a ferrimagnetic material, such as magnetite, in a liquid that is immiscible with and lighter than water is projected for use in selective separation of particles according to their density spectrum. Magnetic levitation forces can be created as an antigravity field when the fluid is properly placed in an inhomogeneous magnetic field. When the gradient of the magnetic field is directed downwards, the levitation force in the fluid will be in an upward direction to float sinking nonmagnetic bodies by counterbalancing their density mismatch with the magnetic fluid. Several nonmagnetic objects with densities ranging from 2.50 to 11.35-g cm' were made to float or submerge at will in a 0.96-g cm' density fluid placed in vertical magnetic field gradients ranging from 0.1 to 1 kilo-oersted cm-'. The magnetic levitation force in dyne cm' was found to vary linearly as a function of the object-fluid density mismatch with a slope equal to one g, the acceleration due to gravity.

Jan 1, 1974

By Y. Ueda, F. Noguchi, T. Yanagase

The rate of CaO dissolution into slag melts is of great importance in the field of pyrometallurgy. In this study the mechanism of CaO dissolution has been investigated by observing the melt heated on Pt-filament directly through microscope together with a help of X-ray micro analyser to find out a distribution of each element around CaO crystal. The direct observation reveals that the CaO dissolution tends to proceed by the action of molten slag entering between CaO crystal and newly formed 2Ca0. Si02 layer through cracks. The effect of slag composition on the formation of 2CaO- SiO2 layer will be shown as well as the effect of halogenides addition on the destruction of this compound layer.

Jan 1, 1976

By A. D. K. Laird, C. A. Johnson

Drag coefficients for a cylinder being towed through water at constant velocity and also at constant linear acceleration were measured. Drag coefficients for constant velocity towing showed reasonable agreement with previous results. The drag coefficients found for constant acceleration showed little correlation with either the magnitude of the acceleration or the value of the modulus AD/V2 and tended to be slightly lower than those for constant velocity. INTRODUCTION For the design of offshore structures, wave forces acting on immersed cylinders are of importance. Several investigations have been made of these forces and of how they can be predicted from wave theories. A paper by Crooke' summarizes much of the work already done. More recent research by the Wave Research Laboratory at the University of California, Berkeley, has added much to the body of data collected under ocean wave conditions, but has not found a reliable method of force prediction from basic theories of wave motion. The present investigation is part of a long-range program to collect data with which to test current and future theories and correlations. The immediate objective was to measure drag forces on a circular cylinder subjected to linear accelerations over the range of Reynolds numbers between l04 and 105 where the drag coefficient was a constant for constant velocities. In particular, the effect of constant acceleration from rest and from uniform motion was to be investigated. The effect of acceleration may be evaluated in terms of drag coefficients. A useful resistance coefficient, C, is defined by the equation for total drag force, D, exerted by the fluid on the cylinder. DT =CSp V2/2.........(1) The coefficient C may be plotted as a function of the parameter AD/V2. Here D is the diameter and S is the projected area of the cylinder. The acceleration and velocity are A and V. The mass density of the fluid is p. An alternate drag coefficient, C, corresponds to the total force of the fluid opposing the motion minus the virtual mass force. This drag coefficient, arising from the velocity of the fluid, may be compared with that for the same cylinder in uniform motion. The similarities and differences between this coefficient as calculated for accelerated and for steady motion are of interest in the inverse process of predicting drag forces on cylinders under arbitrary conditions. One serious difficulty in this method is the specification of the virtual mass which depends also on the flow picture about the cylinder.1 EXPERIMENTAL EQUIPMENT The experiment was performed in the combination wave and towing tank at the Engineering Field Station of the University of California. The tank is 200 ft long, 8 ft wide, and 6 ft deep. The tow carriage is externally propelled by a cable, and the velocity of the carriage is maintained essentially constant by means of an am-plidyne. For the purpose of the present investigation, the speed control of the amplidyne was modified by inserting a linear speed control rheostat, which was rotated at a constant speed by a small d-c motor equipped with a slip-clutch. Accelerations which were constant over a reasonable length of time were thus produced. The magnitude of the acceleration depended upon the speed of the d-c motor and the limiting speed of the carriage. Data were obtained for a range of accelerations of 2 to 10 ft/sec,2 and a range of velocities of 2 to 15 ft/sec. An accelerometer (Statham Type C-2-350) with a range of ±2g was attached to the carriage and connected to a Brush analyzer and penmotor. A continuous coil of wire with 10 turns/ft wound around a fixed wooden form extending for a distance of 40 ft along the length of the tank was connected by an electrical contact mounted on the carriage to a Brush analyzer and penmotor, to give the time-position history for each run. The test cylinder was machined from solid aluminum alloy, 17-ST. to a diameter of 1.250 in., and could be

Jan 1, 1957

Discussion of the paper of W. C. PHALEN, presented at the Pittsburgh meeting, October, 1914, and printed in Bulletin No. 93, September, 1914, pp. 2249 to 2265. DAVID T. DAY, Washington, D. C.-Consider the United States broadly and the distribution of the salt industry. Think of the old solar-evaporation process up in New York State, then of the more recent processes in Michigan and Kansas and Louisiana, where the rock salt furnishes a large industry, then of the solar-evaporation process at Salt Lake, then turn to the crucial place in the United States, where there is an embarrassment of salt, and that is California. I am not forgetting' the immense body of salt east of that in the Virgin River country of Utah; but in California the situation is interesting. There are very large quantities of salt in the Searles Marsh region; again, in Southern California, at the southern end of Death Valley, there are two or three mountains of salt which have been explored recently, where the salt is sufficiently pure to be used at once. There is also a large deposit of gypsum, and it would be possible there, by extremely cheap means, to produce an amount of salt sufficient to furnish the United States' greatest needs. The principal reason that capital has been deterred from developing such a large mass is not the fact that solar evaporation produces a great deal of salt around San Francisco, but the fact that if potash salt is to be produced in connection with the salt in the borax region a, great deal of ordinary salt must be disposed of. It cannot be dumped, for it would get back into the brine again; the first rains would bring that salt back into solution again. It must be sold, given away, or hauled to a distance, which would mean a considerable freight charge. The salt will be going begging. E. G. SPILSBURY, New York, N. Y.-The remark of Dr. Day's regarding the likelihood of the production of a large amount of waste salt brings to my mind the condition that obtains in Germany in all of the potash fields. In Germany salt is a government monopoly. In the development of the potash deposits, it becomes a grave question as to how much salt they may be allowed to extract and bring to the surface.

Jan 4, 1915

By G. R. Wilms

In a recent investigation1 on the properties of chromium, and of Cr-10 wt pct W and Cr-5 wt pct Mo alloys at elevated temperatures, it was found that intercrystalline cavities developed in all of these materials during tensile creep at 950°C, and that the cavities led to intercrystalline fracture. There were some interesting differences, however, between the cavities produced in the pure metal and those in the alloys; these differences, moreover, were associated with a difference in ductility. The relevant conditions of creep testing are specified in the captions to Figs. 1 and 3. Chromium showed the presence of quite large intercrystalline cavities, Fig. 1, and these were more or less randomly distributed around the boundaries. The chromium alloys, on the other hand, showed the presence of both small cavities and cracks at the grain boundaries, Fig. 3; it is apparent that the cracks are formed by the linking together of the small cavities. Moreover, the cavities and

Jan 1, 1960

By D. E. Moore

The strength of a natural serpentinite gouge was measured at 400°C and an effective pressure of 100 MPa. The strength of the gouge decreased with increasing pore pressure to 50 MPa and then was nearly constant between 50 and 125 MPa. The samples at 50-125 MPa pore pressure slid stably, whereas those at 3-25 MPa pore pressure showed stick-slip behavior. Lengthening the pre-heating time to 72,000 s of samples at 100 MPa pore pressure led to increases in both the strength and the likelihood of sliding unstably. With still longer pre-heating times, the strengths decreased again and sliding once more became stable. The strength of the gouge at 3 MPa pore pressure was unaffected by changes in pre-heating time. A possible explanation for the results is that excess pore pressures are being generated in the gouge, causing the true effective pressure to be lower than the apparent value.

Jan 1, 1984

By K. U. Snowden, J. N. Greenwood

EARLY studies by Gough and sopwith' have shown that the fatigue resistance of certain metals increased when the test was carried out in a partial vacuum; lead showed this effect to a marked degree. This communication describes surface deformation differences between high-purity lead fatigued in air and in a vacuum of approximately 5 X l0-3 mm Hg. Both air and vacuum tests were carried out by the same alternating flexure machine at a frequency of 500 cpm. Flat cantilever-bend specimens with tapered sides were cut from strip, annealed at 100°C, and chemically polished.

Jan 1, 1959