By J. E. Tobey

THERE are a lot of good things about this great industry of ours. Let us stop commiserating and consider some of the things that are right in this business. Coal is number one in the basic material industries. Our civilization owes more to it than to any other basic commodity. We are literally immersed in the benefactions of coal. In cur man-made world it is indispensable and we are constantly surrounded by objects, materials, and services which owe their existence to coal. Practically all the important materials, such as iron, steel, brick, cement, lime, rubber, glass, cotton, and wood have felt its magic touch.

Jan 1, 1939

By E. W. Johnson, M. L. Hill

Cold working of iron-carbon alloys was found to increase greatly the hydrogen solubility and to decrease the diffusivity at temperatures up to 400° C. These effects are increasing functions of both the carbon content and the degree of deformation. The hydrogen behavior is consistent with the idea that cotd working creates "traps", which are concluded to be microcracks in which the hydrogen is chemisorbed. Hydrogen embrittlement is explained by the Petch theory of metal crack surface energy loss due to hydrogen adsorption. HYDROGEN embrittlement of steel has been studied for many years and has been the subject of an extensive literature, but the mechanism of the effect has not been completely understood. The embrittlement is unusual in that the ductility loss is not accompanied by an increase of the yield strength, being primarily a decrease of the fracture strength alone. The loss of fracture strength is usually most severe in the temperature range between 0°and 100°C. Here the solubility of hydrogen in the iron lattice at ordinary H2 pressures is extremely low while the diffusivity is still quite high. From the relationships between the ductility and the hydrogen content, test temperature and strain rate, it is apparent that the hydrogen atoms causing the ductility loss difbse to and concentrate in small regions of the metal which are especially susceptible to the initiation and propagation of fracture. This hydrogen segregation apparently occurs after plastic straining has begun. Below 0°C the ductility loss persists only at low strain rates in confirmation of the view that the embrittlement is diffusion .controlled. The tendency of the embrittlement to disappear above 100°C can be explained by the increasing lattice solubility of hydrogen with rising temperature. A common view of hydrogen embrittlement of steel is that the hydrogen initially dissolved in the metal lattice diffuses to structural discontinuities and there precipitates as H2 gas at very high pressures which assist the external stress in causing premature failure.1,2 The idea of a high H2 pressure in equilibrium with ordinary amounts of hydrogen in steel at room temperature is due to observations of hydrogen behavior in fully annealed material, for which the Sieverts' law constant relating solute concentration to H2 pressure is extremely small. Hydrogen-embrittled steel, however, is always plastically deformed to some extent, and therefore it is important that hydrogen embrittlement be explained primarily in terms of hydrogen behavior in plastically deformed material. Such an explanation is attempted in this paper. Previous studies of hydrogen in cold-worked steel have shown that both the solubility and the diffusion rate are significantly chaned when the steel is cold worked. Darken and Smith discovered that the amount of hydrogen absorbed from acid by cold-rolled steel at 35°C is many times greater than that absorbed by hot-rolled steel. They found also that the hydrogen permeability of the steel is unaffected by cold working. Keeler and Davis4 confirmed the high apparent solubility of hydrogen in cold-worked iron-carbon alloys at temperatures up to and even beyond the recrystallization temperature. They also found that this solubility increase accompanying cold work is a sensitive function of the carbon content, being absent when no carbon is present. The present experimental study was undertaken primarily to obtain an improved understanding of the behavior of hydrogen in cold-worked steel. Data were obtained on the effects of temperature, H, pressure, carbon content, and degree of cold work on the hydrogen solubility and diffusivity in iron-carbon alloys. These data have been helpful in elucidating the nature of the cold-worked steel structure as well as in providing information on the mechanism of hydrogen embrittlement of steel. EXPERIMENTAL Cylindrical specimens for hydrogen absorption and diffusion rate measurements were prepared from three iron-carbon binary alloys and a commercial SAE 1010 steel. The iron-carbon alloys were prepared by vacuum melting electrolytic iron with graphite in a magnesia crucible. The alloys were cast in vacuum as 2 1/2-in. sq ingots weighing about 20 lb each. The ingots were hot rolled (above 1900°F) to 5/8-in.-diam round bars and then cooled in air to room temperature. The resulting metallographic structure consisted of islands of fine pearlite surrounded by free ferrite. Chemical analyses of the materials are given in Table I. The 5/8-in. diam bars were turned to diameters such that cold reduction to the desired final specimen diameters would result in either 30 or 60 pct reduction in area (RA). The machined bars were then cold worked by swaging at room temperature

Jan 1, 1960

By H. M. Howe

PART I. INTRODUCTORY. § 24. INTRODUCTION.-This paper discusses the chief existing data as to the temperature, in iron-carbon alloys, of Ae.3, the upper limit of the transformation range when in equilibrium, as distinguished from Ac3, the temperature at which the end of the transformation is noted in heating up, and from Ar3, that at which its beginning is noted in cooling down. The former is in fact carried above Ae3 and the latter below Ae3 by lag. I touch incidentally on the influence of manganese on Ae3 (§ 29, p. 1102). The sections, tables, and illustrations, are numbered consecutively with those in the accompanying papers by Howe and Levy on Determination of, the Position of Ae3 in Carbon-Iron Alloys, and by Burgess, Crowe, and Rawdon on Thermal and Microscopical Examination of Professor Howe's Standard Commercial Steels, to which the present paper forms a sequel. § 25. The contradictoriness of our present evidence is shown by grouping it together in Fig. 14. For instance, both Goerens and Meyer (Series 2) and Meuthen (Series 12) used practically stationary temperature, and thus reduced the influence of lag very greatly; yet Ae3 for 0.32 carbon steel according to the former investigators is 894°, but according to Meuthen it is at or below 770°, a discrepancy of 124° or more. In view of our ability to measure these high temperatures within a few degrees, the existence of such a discrepancy is as unwelcome as it seems needless. I attack the thankless task of bringing some order out of this chaos.

Jan 6, 1913

By Lawrence A. Roe

Talc, when it can be isolated as a pure mineral, has a composition of 63.36% SiO2, 31.89% MgO, and 4.75% H2O. However, as an industrial commodity, talc rarely approaches theoretical purity. Nevertheless, the impure talc products of commerce find a multitude of uses and few substitutes in many industrial applications. Minerals commonly associated with and sold together in talcose mixtures are tremolite, chlorite, dolomite, mica, and magnesite. Steatite was originally a mineralogical name applied to pure talc. In today's commerce steatite generally refers to the massive variety of talc suitable for electrical insulator manufacture. Block steatite ore can be machined into various shapes. Impure varieties of massive or block talc are still commonly referred to as soapstone. Soft massive talc, suitable for crayon manufacture, has been referred to as French chalk. It has been common practice to discuss talc, soapstone, and pyrophyllite under the same general heading. In the case of soapstone and talc, this is a natural thing since many different types of platy, soft minerals exhibiting a high degree of lubricity (commonly referred to as "slip") have been grouped together and called soapstone or talc. Further, there is a mineralogical relationship of pyrophyllite to montmorillonite and talc to hectorite. Thus, talc and pyrophyllite are sometimes referred to as clay minerals. When finely divided talc or pyrophyllite are combined with water in proportions to make a slurry, the end product does have the appearance of a clay-water mixture. Soapstone for utensils and ornaments was mined by prehistoric Indians on Santa Catalina Island, Calif. In the mid-1800s, soapstone from deposits along the western foothills of the Sierra Nevada mountains was used by white settlers for building and ornamental stone and in the linings and foundations of furnaces (Anon. 1956). Previous to 1916, the annual recorded production in California did not exceed 2000 tons. In the period 1912 to 1918, output rose sharply when the Talc City, Western, and Silver Lake mines were put into operation. From 1916 to 1935, the state's annual output of talc was in the range of 9,000 to 20,000 tons. In the mid-1930s, the use of talc in wall tile grew rapidly. In California, the production of talc grew to 63,000 tpy in 1943. The post-war building boom helped California production to grow to 120,000 tons in 1951. In 1968, production was 165,000 tons, 1969 was 145,000 tons, 1970 was 185,000 tons, and 1972 was 155,000 tons. Talc mining in New York state dates to about 1878 when a Colonel Palmer and associates opened the first commercial talc mine on the Nelson Freeman farm near Talcville, New York. In 1893, this operation was sold to the International Pulp Co. which changed its name to the International Talc Co. in 1944. Total production from seven New York mines, in 1948, was 130,000 tons. A new talc operation, the Gouverneur Talc Co. owned by the R.T. Vanderbilt Co., began operations near Balmat, N.Y., in 1948. The initial capacity of the processing plant was 200 tpd (Gillingham, 1950). Subsequent expansions have increased capacity to over 600 tpd. The Vermont talc industry began just after the start of the 20th century. Talc was discovered in the area of the present Johnson, Vt., talc mine in 1902. The American Min¬erals Co. initiated plant operations at Johnson in 1904. The Magnesia Talc Co. opened a plant at Waterbury, Vt., in 1913 (Burmeister, 1963; Trauffer, 1964) and acquired American Minerals Co. in 1923. The Waterbury mine has a long history as a producer of talc crayons. The Eastern Magnesia Talc Co. was formed in 1924 by a merger of the Eastern Talc Co.

Jan 1, 1975

What has happened to the basic coal industry during the past year? Has it been a better year for coal than 1961? What striking new developments have occurred in mining, preparation and utilization? Are there positive signs that production will go up? What has happened in the utility market, the metallurgical market and the export market? Is the controversial question of coal transportation nearer to a solution? What progress has research made for coal during the year? The answer to these and many other important questions are offered in the following review of the Coal Industry-1962.

Jan 2, 1963

By Harold B. Fell

MANY oil producers are in disagreement with the idea held by some that an increase in the price of crude oil would be unlikely to stimulate much production and that we will be obliged to draw upon foreign sources of petroleum to supplement our domestic production as the years go by. Supporting our con trary opinion are numerous facts and figures. The most recent official estimate of the maximum efficient rate of production from the oil wells of the United States is 5,271,000 bbl per day. The Economics Advisory Committee of the Interstate Oil Compact Commission estimates, assuming certain supplies from imports and from natural gasoline and benzol, that crude oil require-

Jan 1, 1947

By Hans Lundberg, Basil T. Wilson, H. Steuart Scott

FOR the benefit of those readers who may not be in close touch with present practices in the geophysical prospecting for ore, brief reference will fiat be made to the advantages and shortcomings of the methods to be discussed. Magnetic and electric methods are generally accepted as the most useful for ore prospecting. By magnetic methods, magnetic intensities that are not normal may be recorded and outlined. From these can he located concentrations of such highly magnetic minerals as magnetite or pyrrhotite, which sometimes occur in such large masses that they are of economic value in themselves. More often. however, these magnetic min¬erals are associated with others, such as copper, zinc, lead, gold, and silver, which, if existing in sufficient concentration and quantity, may constitute valuable ore bodies. It is therefore only when pyrrhotite and magnetite are present in these bodies that the magnetic method can be used to indicate their presence.

Jan 1, 1945

By W. F. Carew, F. A. Crossley

Tensile, creep-rupture, and stability tests were employed to evaluate the effect of a-strengthening and ß-complexing additions on the base composition Ti-6Al-3Mo. The ultimate objective was to produce an alloy of greater strength than the Ti-7A1-3Mo alloy. Strengthening of a was accomplished by additions of 2 and 4 pct Ge, 4 pct Sn, 4 pct Zr, and 2 pct Sn-2 pct Zr. Making the ß more complex while keeping the total of ß-stabilizing additions constant at 3 pct resulted in higher tensile strengths but lower creep and rwpture strengths, especially at 1000°F. None of the more complex versions of the base alloy offers greater promise than the Ti-7A1-3Mo alloy. However, some improvement in the strength of the latter may follow from additions of zirconium perhaps up to 4 pct. PREVIOUS work directed at the development of titanium-base alloys with: 1) minimum room-temperature tensile elongation of 10 pct in 1 in., 2) high creep resistance at elevated temperature, and 3) the ability to retain original room temperature tensile ductility following exposure to creep conditions at elevated temperatures, demonstrated Ti-Al-Mo ternary compositions in the range 5 to 7 pct Al-3 to 6 pct Mo to be the most promising. Of this group the Ti-7Al-3Mo alloy was the strongest.'-= The objective of the present work was to determine if alloys of this type could be further strengthened by making additions which dissolve preferentially in the a-phase and by making the ß-phase more complex. For this study the base composition Ti-6Al-3Mo was selected rather than Ti-7Al-3Mo in order to minimize the possibility that in a more complex alloy with a-strengthening additions, low ductility might obscure the strength contribution. The metals

Jan 1, 1959

By S. Floreen

Seven iron alloys ranging from 5 to 12 pct Ni and 5 to 14 pct Cr were studied. All alloys transformed to bcc massive martensites. Tempering increased the strengths , probably because of relief of residual stresses generated by the martensite transformation. The major strengthening mechanism appeared to be solid-solution hardening by nickel and chromium. Studies of the work-hardening behaviw, of the effects of prior austenite grain size, and of the effects of changing strain rate and test temperature gaue results very similar to iron or low-alloy steels. Increasing nickel contents markedly improved the toughness at subzero temperatures. Studies of the flow properties did not, however, indicate the reason for the beneficial effect of nickel on toughness. The marine atmosphere corrosion resistance of the alloys was improved primarily by chromium additions, but increasing nickel contents were also beneficial at low levels of chromium. J\ number of maraging and PH stainless steels are strengthened by precipitation hardening in a low-carbon Fe-Ni-Cr martensite matrix. To some extent the resultant properties of these steels must depend upon the properties of this matrix. The present study therefore was conducted to evaluate the transformation characteristics and mechanical properties of a series of Fe-Ni-Cr martensitic ternary alloys. A limited evaluation of the corrosion resistance of the alloys in marine atmosphere was also made. ALLOY PREPARATION Seven 100-lb air induction melts were prepared using electrolytic iron, nickel, and chromium metal additions. The initial Fe-Ni charge also contained 0.05 wt pct graphite to produce a carbon boil during melt down. After melting of the base charge, the heats were refined with 0.1 wt pct additions of manganese, silicon, aluminum and titanium and poured into cast-iron molds. The ingots were homogenized at 1250°C and uni-directionally hot-rolled to 2-in. plate. They were then homogenized another hour at 1250°C, and unidirection-ally hot-rolled to %-in. plate at a finishing temperature of approximately 1050°C. The compositions of the heats are given in Table I. Two additional heats were prepared as 40-lb vacuum-induction melts using electrolytic iron, nickel, and chromium metals, and commercially pure molybdenum chips. A carbon boil, and 0.1 wt pct additions of aluminum and titanium were again employed, but manganese and silicon were not added. The heats were converted to %-in. plate using the procedure described above. The compositions of these heats are included in Table I.

Jan 1, 1967

By R. A. Wolfe, H. W. Paxton

Self-diffilsion coefficients for cr51 and Fe55 in 12 pct Cr-Fe and 17 pct Cr-Fe for Fe55 in chromium, and for Cr51 in vanadium have been measured. The results are compared with other values for the Fe-Cr system, and with the various theories of diffusion in hcc metals. Some empirical correlations are discussed between Do and Q in hcc systems, or, expressed differently, the constancy of ?G*/T solidus for seveval bcc metals and alloys is noted. It appears very probable that a vacancy mechanism is operative in bcc metals, hut this cannot he stated with certainty. THE great bulk of work on diffusion in metals, both experimental and theoretical, was for many years concentrated on those with close-packed and, in particular, fcc lattices.1,2 There appears to be little doubt that the mechanism of diffusion in these solids is vacancy migration, leading to mass transfer and in substitutional solid solutions to a Kirken-dall effect.3,4 For bcc metals, the picture is much less clear. The Kirkendall effect certainly occurs in several alloys.5-10 However, attempts to understand the factors contributing to the pre-exponential in the usual expression for the diffusion coefficient D =D, exp {-Q/RT) by extension of ideas useful in close-packed lattices have not always been successful. Zener,11 Leclaire,12 and Pound, Paxton, and Bitlerl3 have suggested that various forms of ring diffusion may be important in some bcc metals. For close-packed metals, Do is usually about 1 sq cm per sec and Q - 35Tm kcal per mole (Tm = melting temperature in OK). The theory of Pound et al. suggests for ring diffusion that Do may be about 10-4 and Q, although difficult to calculate with any precision, would be significantly less than 35 T,. The experimental results on self and solute diffusion in ? uranium14,15 and ß zirconium,10 and for solutes in 0 titanium,17 and possibly for self-diffu- sion in chromium below about 0.75 T,," gave some credence to this theory. However, not all bcc materials display low values of DO and Q, and the exceptions were not predicted by any theory. Furthermore, it has recently become apparent that, in bcc materials, log D is not always linear with T-l if a sufficiently wide range of temperature is studied.16,18 This variation may be such that Q may increase18,19 or decrease20 with increasing temperature. The present work was undertaken in an attempt to provide further diffusion data on bcc metals, and to try to understand the factors which contribute to differences in behavior between the various elements. For part of this work, the Fe-Cr system was chosen since it is of considerable technological importance, and data on 12 pct Cr and 17 pct Cr alloys appeared well worthwhile to supplement that existing for the remainder of the stern.18,22 The diffusion of Fe55 in chromium was studied as an example of a more or less "normal" tracer element in a possibly abnormal host lattice. Finally, no data were available for vanadium, the neighbor of chromium in the periodic table, because of lack of a suitable isotope so cr55 was used as a tracer in a few preliminary experiments. For convenience, we shall refer to elements whose Do and Q are low compared to those predicted by Zener's theory as "anomalous". PROCEDURE This investigation determined self-diffusion rates by means of radioactive tracers and the integral-activity method first utilized by Gruzin.23 In this method a thin layer of radioisotope of the diffusing element is plated or coated onto a planar surface of the diffusion sample, which is then given an isothermal-diffusion annealing treatment. The determination of an activity-penetration curve involves measuring the residual activity of the specimen after each successive layer or section has been removed parallel to the original planar surface. The method used here is essentially the same as that used by Gondolf18 and Kunitake.21 Two radioactive tracers, cr51 and Fe55, were used in this investigation. Diffusion coefficients were determined for the diffusion of one or both of these tracers in four different materials, viz., Fe-12 wt pct Cr alloy, Fe-17 wt pct Cr alloy, chromium, and vanadium. The diffusion samples had nominal dimensions of 1.5 cm diameter and 0.5 cm thickness. The grain size was several millimeters for the Fe-Cr alloys and at least 1 mm for the chromium and vanadium samples. Accurately planar surfaces

Jan 1, 1964

By G. Ansel, J. P. Doan

THE important literature concerning zirconium in magnesium-base alloys is predominantly contained in patent references. Sauerwald, Eisenreich, and Holub1-4 discovered the profound grain-refining influence of small amounts of zirconium on cast magnesium and the attendant increases in strength, and ductility. They extended their work to reveal that limited amounts of certain other elements, including zinc, could be added for further improvement in strength and hardness. British. Patent 5111376 relates to the parent discoveries of Sauerwald, Eisen¬reich, and Holub. All of these references deal primarily with casting characteristics and properties in the cast state. Minor mention is made of desirable tensile strength, ductility, and toughness of wrought Mg-Zr alloys* modified by one or more additional elements. No extensive reference in the literature" has been found to the particular characteristics of wrought Mg-Zn-Zr alloys, with which the present paper is concerned. - The work to be discussed represents essentially an extrusion study of the Mg-Zn-Zr alloys and indicates that this system is highly interesting in the wrought state both academically and commercially. Accordingly, an important aim of this paper is to describe the hot-workability, tension and compression properties, metal¬lography, and toughness of these alloys. Compositional variations are limited to the ranges o to 7 per cent Zn and o to I per cent Zr. EXPERIMENTAL PROCEDURE Alloying and Casting Alloying ingredients were cell mag¬nesium, commercial zinc (intermediate grade), and a chloride salt containing approximately 50 per cent ZrCl2 and 50 per cent alkali chlorides. This salt is produced by Titanium Alloy Manu¬facturing Company. Melting, alloying, and pouring procedure essentially followed the crucible process as described by Nelson.6 The magnesium was melted using Dow No. 310 flux, and the temperature raised to 1350° to 1400°F for the alloying operations. After alloying of the zinc, the zirconium containing salt was added in small portions with vigorous stirring. This is an adaptation of the method described in British Patent 533264.7 The alloying efficiency of zir¬conium was approximately 30 per cent. During the alloying of zirconium, fluorspar was added in amount required as a flux¬inspissating agent. Next the melt was refined with Dow No. 310 flux and held quietly for 15 min. Finally billets were cast in a book-type permanent mold

Jan 1, 1946

By E. DeGoyler

The Furbero oil field lies in the Gulf coastal plain of Mexico between the important ports of Tampico and Vera Cruz and about one-third of the distance between the two points from the latter (Lat. 20" 22' N., 97" 30' W. Gren.). It is in the State of Vera Cruz, about 14 miles west by south of the village of Papantla in the canton of the same name, and is the most southern of the developed oil fields of the Tampico-Tuxpam region being a distance of 50 miles south by east from the Potrero del Llano field and 42 miles in the same direction from the Alamo field. The field has been developed by the Oil Fields of Mexico Co. and is in the midst of a large block of lands owned or leased by them. Communication is through the port of Tuxpam with which it is connected by a narrow-gauge railway and 6-in. pipe line some 52 miles in length. This field is of more than ordinary interest since it represents a type of oil deposit hitherto unknown. So far as I am aware, no other commercially valuable deposit of oil is known to occur under conditions of accumulation similar to those found here. The igneous nature of the so-called 'sand' encountered in drilling was not recognized until a number of wells had been drilled; and it was not until recently that the geological relations of the sill or laccolith, which gives rise to the accumulation of oil, were known and the so-called 'anticline' was known to be, in part at least, the result of igneous intrusion. Geological surveys in this general region were made in 1900-1901 by W. H. Dalton and in 1907-1909 by P. C. A. Stewart, F. W. Moon, Leonard V. Dalton, and Dr. Max Muhlberg. More recent surveys have been made, however, under the direction of the author, by E. L. Ickes, B. C. Belt, B. Hartley, and Harve Loomis. Notes of the earlier examinations were not available with the exception of the report by Dr. Muhlberg who apparently first recognized the true nature of the Furbero intrusion. This paper is indebted to his work and that of the more recent surveys for much of the detail regarding stratigraphy and to Messrs. Percy Furber and Arthur C. Payne, President and General Manager of the Oil Fields of Mexico Go. for permission to publish, and for much of the in-

Jan 1, 1916

By A. S. Yue

The movphology of the Mg-32 wt pct Al eutectic has been studied as a function of freezing- rate and temperature gradient. At slow freezing rates a lamellar eutectic was formed; whereas, a rod-like eutectic was generated at fast rates. The inter-lamellar spacing increased as the freezing rate decreased in aggreement with theoretical predictions. Lamellar faults, morphologically similar to edge dislocation models in crystals, were responsible for the subgrain structures in the eutectic mixture. A linear increase in fault density with freezing rate was observed. Fault concentl-ations of the order of 10 per sq cm for a range of freezing rates from 0.6 to -3.0 x 10 cm per sec were estimated. The transformation from lamella?, to rod-like morphologies was determined experimentally to be dependent on the freezing rate and independent of the temperature gradient. Moreover, the number of rods formed per- unit cross-sectional area increased exponentiallv with increasing freezing rote. BRADY' and portevin2 classified eutectic structures into lamellar, rod-like, and globular according to the morphology of the solid phases present. Although this classification is quite descriptive, very little has been reported on the details of the mechanism by which the eutectic structures are formed. Recent work by Winegard, Majka, Thall, and chalmers3 and by chalmers4 on lamellar eutectic solidification suggest that the maximum thickness of the lamellae decreases with increasing rate of solidification due to inadequate time for lateral diffusion. scheilS and Tiller' have shown theoretically that the lamellar widths indeed depend on the solidification rate. However, there has been no experimental evidence to support the theory. Chilten and winegard7 have studied the interface morphology of a eutectic alloy of zone-refined lead and tin. They found that the lamellar width decreased as the freezing rate increased in agreement with the theoretical predictions of scheils and Tiller.' More recently, Kraft and Albright' have investigated the microstructures of the A1-CuA12 eutectic as a function of growth variables. They observed lamellar faults present in the lamellar eutectic, similar to edge dislocation models in crystals. Furthermore, Kraft and Albright reported that they could not designate which extra lamellar was responsible for the formation of a lamellar fault even under electron microscopic magnification. In this paper, the morphology of the Mg-A1 eutectic structure is described. The effects of freez- ing rate on the interlamellar spacing and on the lamellar fault density are presented in detail. The transformation from lamellar to rod-like eutectics is discussed in terms of the freezing rate and the temperature gradient. EXPERIMENTAL PROCEDURE The experimental details of alloy preparation, the decanting mechanism and the determinations of the freezing rate and the temperature gradient have been reported elsewhere. Measurements of plate-edge angles were made with a microscope. The true angles used to determine the interlamellar spacings were determined by a two surface analysis technique.'' Since the decanted interface structure does not represent the true eutectic morphology on the solid,g all measurements were made from an area in the solidified bar behind the interface. Measurements of the apparent interlamellar spacings between the two phases of the eutectic were made on a photographic negative by means of a calibrated magnifier. Each value listed in Table I represents the average of thirty measurements on one negative. In general, these measurements are approximately equal with an error of less than pct. The average rod diameter for each specimen was also measured on a magnified photomicrograph. Each value of the diameter represents the average of fifty measurements. RESULTS AND DISCUSSION The experimental observations and their discussion to be presented here are restricted to the morphology of the eutectic structure and to the effects of the freezing rate and the temperature gradient on the solidification of eutectics. INTERLAMELLAR SPACING It has been shown previouslyg that the micro-structure of the decanted interface and the longitudinal section of the Mg-A1 eutectic is characterized by the presence of both lamellar and rod-like morphologies. The lamellae become more regular as the freezing rate is decreased. A three-dimensional photomicrograph representing a perfect lamellar morphology is illustrated in Fig. 1. The lamellae of the top and longitudinal sections of the specimen are regularly spaced while those in the transverse section are not quite straight and parallel. Their parallelism is slightly distorted because fault lines producing a discontinuity are present. A method for calculating the interlamellar spacings A, is described in Appendix 1. The true

Jan 1, 1962

By Akio Suzuki, P. G. Wahlbeck

AS a part of a study of the vaporization of transition metal-chalcogen systems, the vaporization reactions for the Ti-Se system have been studied. In order to establish vaporization reactions it is important to determine the identity of vapor species in equilibrium with the condensed phases. In some cases, it is possible to deduce the identity of vapor species through observations of composition change of the condensed phase with which the vapor is in equilibrium. Determination of vapor species in equilibrium with condensed phases should precede vapor-pressure measurements and is necessary for proper thermodynamic analysis of vapor-pressure data. Bear and McTag-gart' reported that vacuum heating ot TiSea at 950°C produced a residue with a composition of 1.7 Se/Ti atomic ratio units. Analyses of condensed phases existing for the Ti-Se system have been performed by Bernusset,2"4 Gron-vold and Langmyhr,5 Hahn and Ness,' and Ehrlich.~ Results and conclusions of two types of experiments are described herein: 1) experiments where samples of known composition were vaporized followed by chemical analysis of residues and 2) experiments where the vapor species were identified by means of a mass spectrometer. Experimental Section. Sarnple Preparation. Samples of TiSe2 were prepared in a sealed, evacuated quartz ampule by heating to 1000°C stoichiometric amounts of selenium of 99.999+ pct purity obtained from the American Smelting and Refining Co. and titanium of 99.2 pct purity obtained from A. D. Mackay, Inc. After heating, the sample was ground and reheated to insure homogeneity. Samples containing less selenium than TiSez were prepared by mixing amounts of titanium powder and TiSez appropriate for the desired composition; the titanium and TiSez mixture was heated in the same manner as described for TiSe2. Analyses of titanium selenide samples contained in quartz crucibles were performed by gravimetric oxidation in oxygen at 800°C; the products of the oxidation were solid TiOz and gaseous Se02. The mass of the original sample and the mass of TiOn determined the Se/Ti atomic ratio. The sample of TiSen used in these experiments had a composition of 2.04 Se/Ti atomic ratio units. The compositions for all samples reported were analyzed by this method. Va/!orization Experiments. Samples of titanium selenides were vaporized in tungsten Knudsen crucibles. Some vaporization experiments were carried out in glass vacuum lines followed by chemical analyses of residues, and some vaporization experiments were performed with a Bendjx mass spectrometer as described previously.8

Jan 1, 1967

President Howe: It is, of course, not easy to discuss off-hand the paper which Mr. Becker has presented with so much lucidity. I will only make one remark, which is outside of the line of his argument, and concerns merely a passing allusion in his paper. Mr. Becker speaks of the fact that glass breaks with a flat or conchoidal fracture, and that steel shows a rough or " cupped " surface of frac-

Jan 1, 1895

By Frederick Laist

0. C. RALSTON, Salt Lake City, Utah.-I have merely glanced over this paper, consequently, I am hardly in a position to discuss it intelligently. There is one thing, however, that is of interest, that is, the claim that the oil mixture which they have chosen is the best adapted to the work at hand. I would like to ask Mr. Mathewson if they still feel that that is the case-if that really does give the best grade of concentration and the best extraction for the same money, compared to any particular oil mixture which they could get. E. P. MATHEWSON, Anaconda, Mont.-We are still using that mixture, and we consider it the most economical mixture used. DAVID COLE, El Paso, Texas.-I would like to ask Mr. Ralston if there are some other mixtures that would be better? E. P. MATHEWSON.-We are open to suggestions. 0. C. RALSTON.-My own paper on oils* calls attention to the fact that certain hardwood oils, especially the tars, are now being burned or wasted. A great deal of hardwood tar is available as low as 4 or 5 c. per gallon, that being its value as fuel under the boilers. As a matter of fact, a great deal of testing has been done with only the commercial products that are as a usual ride sold on the market. Very little hardwood tar is sold on the market. In asking a great many people who have tested flotation oils, I have not heard hardwood tar mentioned very often. I think I would add to that that the hardwood tars can probably be bought in quantity comparable with the sludge acid at Anaconda, and. should contain a greater proportion of the frothing constituent, and at a price fairly commensurate with what they pay for the sludge acid. E. P. MATHEWSON.-I would like to make a correction in one statement I made that there has been no change made in the mixture. This change has been made: We found that the amount of wood creosote in treating the sand from tables was extremely small, and we tried some experiments on a large scale, dropping it out and using simply the sludge acid and sulphuric acid. We found that this gave practically as good results as wood creosote. We use wood creosote in treating the slimes. We find it necessary in that operation. DAVID COLE.-I would like to ask, what is sludge acid?

Jan 10, 1916

By Thomas T. Read

REVIEWING the events of the year in mineral industry education, a certain amount of either amusement or irritation, depending upon one's viewpoint, can be derived front the section dealing with mining engineering in Walter B. Pitkin's "New Careers for Youth" which appeared during the summer. On p. 102 Prof. Pitkin says "The mining engineer is disappearing .. . because . . . the profits of mining decline rapidly with the age of the mine." In his "Are Too Many Students Taking Mining Courses?" published in the May issue of this journal, W. B. Plank presents statistics showing that there was some decline in student enrollment in mining and metallurgical courses in 1932-3 and 1933-4, compared with 1930-31, but that the decline was proportionate to that in all lines of engineering study combined. Informal reports from Institute officials that have visited tinning schools during the fall indicate that nearly all schools showed an increase in enrollment for the current school year. Pre else statistics will be made available by Prof. Plank at the Annual Meeting. His study last year provided, for the first time, accurate and complete information on the enrollment in mining schools, as well as the number of various courses and the degree granted, and it will be interesting to have comparable figures for this year. Prof. Pitkin's views on the future opportunities for mining engineers were discussed at some length - on pages 439-4.40 of the November issue of MINING AND METALLURGY.

Jan 1, 1935

Discussion of the paper of Dorsey A. Lyon and Robert M. Keeney, presented at the Butte meeting, August, 1913, and printed in Bulletin No. 80, August, 1913, pp. 2117 to 2149. C. D. WOODWARD, Butte, Mont.:-We constructed a small blast furnace, and used first carbon electrodes and an alternating current of about 50 to 75 volts. We were able to smelt the material which was fed to the furnace, but we did not carry on experiments far enough to see just exactly what the power consumption was and compare it with the amount of material treated. We found that the blast seemed to help materially in reducing our charge and cutting down our power consumption. There were several other experiments tried at the time, and I do not call to mind now just what they were. We were trying to do away with the carbon electrode and replace it with an iron one, and it also seems to me we tried to use the ore for an electrode; but I believe that the electric furnace in the reducing end is simply a question of British thermal units per kilowatt-hour compared with British thermal units in a pound of coke. Now, if a pound of coke costs us 0.5 c. and a kilowatt-hour costs us in the neighborhood of 1.5 c., I think there is a big advantage in using coke instead of the electrical current for copper reducing. We tried steam, and a number of other methods, to throw copper down, but it has been some time ago and I am not very familiar with them now. The outlook of the experiments did not seem to be very promising, and we took it more as a thermal problem than an electrical one. PROF. JOSEPH W. RICHARDS, South Bethlehem, Pa.:-Mr. Woodward has spoken of the question as a thermal problem. I would call attention to the fact that electric furnaces usually utilize the heat of the electric current at from four to ten times the efficiency with which the heat generated by fuel is utilized; so it will not do simply to compare by thermal units generated. Your total thermal units may cost much less from coke than from electricity, yet you will find the electrically generated thermal units utilized in a properly designed furnace from three to ten times more efficiently than in the combustion furnace. You must make that allowance is comparing the cost of thermal units generated electrically and thermal units from coke.

Jan 11, 1913

By D. A. Woodford

A number of observations have now been reported where the steady-state creep rate is apparently linearly dependent on the applied stress at high temperature and low stresses. This results in a creep rate greater than that predicted by extrapolation of high-stress data and has obvious practical implications. However, some of these observations are open to question. For example, the analysis by Harris and Partridge17 of the data of Greenfield et a1.18 was dependent on strain rates which, according to the original authors, were too low to be measured. Dr. Bernstein appears to have demonstrated a linear stress dependence at low stresses in two zirconium alloys. There are, however, a number of discrepancies in his treatment of the data and the subsequent theoretical analysis which require clarification. 1) It is incorrectly stated that steady-state conditions are revealed by a slope of unity on a plot of log i vs log (time). This objection is trivial if the author meant to say a slope of zero, although it is unclear how subsequent extrapolation was made to determine the steady-state creep rates at low stresses for the zircaloy-2. If the plot used was actually log c vs log (time), it is unlikely that a slope of unity would represent a constant creep rate. A plot of log (c - co) vs log (time), where c0 is the extrapolated intercept sf the steady-state creep rate on the strain axis, would have a slope of unity during steady-state creep. However, eo cannot be determined unless is is already known. 2) The author chooses to interpret his results based on the equation: where A, and B, are structure-sensitive parameters, Ql and Q, are the activation energies for the particular creep process, and n describes the sensitivity of the creep rate on stress. The first term represents a slip creep process and the second a diffusion creep process. However, it is stated later that "two distinct processes acting in parallel are involved". Eq. [I] surely represents two processes in series since each reacts to the total applied stress and t, is the sum of the individual creep rates. If the processes are acting in parallel, then the effective stress in each would be less than the applied stress. The component stresses would be given by sl + s2 = a but it is not clear how the magnitude of either, or the corresponding stress exponent, could be determined.

Jan 1, 1969

By E. P. Mathewson

A Discussion of the Paper of E. P. Mathewson, presented at the New York Meeting, April, 1907, and printed in Bi-Monthly Bulletin, No. 13, January, 1907, pp. 7 to 14. PROF. HENRY M. HOWE, New York, N. Y. (communication to the Secretary *) :-The results presented in Mr. Mathewson's paper are of very great interest. Perhaps the most interesting is that shown in Table I. and Fig. 1, in which the arsenic decreases in 10 min, from 0.22 to 0.07 per cent. This is such a large decrease that it is to be hoped that Mr. Mathewson will verify it by repeating his tests with a matte of similar composition. This is particularly to be desired, because the simultaneous removal of sulphur appears to be very small. All three blows further agree in showing that the removal of arsenic is in the very early part of the blow. The fact that the removal of arsenic then ceases abruptly cannot be explained completely by the fact that the arsenic has fallen so low as by its lowness to resist further removal, because in the first blow the arsenic becomes stationary at 0.06 per cent., whereas in the third blow it does not become stationary until it has fallen to 0.034 per cent. The abrupt ending of the re¬moval of arsenic is more likely to find its explanation in the composition of the slag, and it is to be hoped that. Mr. Mathewson will supplement these extremely valuable data with others in which the composition of the slag at the same time shall be given. The sudden rise of arsenic toward the end of the third blow I suppose must be referred to an error in sampling or analysis. Mr. Mathewson speaks on page 14 of the "percentages of iron . . . volatilized during the first period." Is it his meaning that all this iron is really volatilized, or does he mean that the iron is scorified and the sulphur volatilized ?

Jul 1, 1907