By J. O. Mogalanyane, N. Naudé, A. M. Garbers-Craig

The fines produced is not suitable as feed material for the subsequent rotary kiln and the electrical arc furnace. The need for briquetting the ferronickel ore is premised on the minimisation of fine particles in the rotary kiln as well as improving charge permeability in the furnace, and improving overall process safety. Briquetting may be defined as an agglomeration method in which fine particles are compressed under pressure. It consists of three different technologies: vibropressing, roller pressing and stiff extrusion. The current study focuses on evaluating the performance of ferronickel briquettes generated, using roller-pressing technology. Physical properties, chemical properties and metallurgical properties of the briquettes were used to evaluate their performance and quality. Standard ISO tests for iron ore pellets were used. Size degradation as a result of reduction was measured using the ISO 4696-1 test. The decrepitation of the briquettes at the point of entry into the rotary kiln was evaluated using the ISO 8371 test method at a temperature of 700oC. The degree of reduction was evaluated using the ISO 4695 test procedure. Average green briquette compressive strength of 559 N was reported at a moisture content of 16% with an average drop number of 19.1. Increasing the moisture content has a detrimental effect on both the compressive strength and the green briquette yield. The drop number is expressed as the number of drops until breakage, when a briquette is dropped from a 1 m height, decreased with an increase in moisture content. At a moisture content of 16% an average green briquette yield of 85.1% was reported. Keywords: Ferronickel briquettes, moisture content, curing conditions, physical properties, chemical properties

Jan 1, 2020

By G. Akdogan, C. Dorfling, L. Bumhira

Hydrometallurgical recovery of rare earth elements from phosphors obtained from end-of-life fluorescent lamps involve leaching followed by extraction of dissolved metals from solution. The similar properties of rare earth elements make selective recovery of individual elements challenging. The aim of the paper was to investigate the extraction of primarily Ce and Tb from a hydrochloric acid leach solution also containing other REEs (Y and Eu) as well as impurity metals (Ca and Al). Batch solvent extraction tests were performed with di-(2-ethylhexyl) phosphoric acid (DEHPA) at various extractant concentrations, pH conditions and organic-to-aqueous ratios. Extraction isotherms and separation factors for the range of conditions tested in the project are presented in the paper. Separation of individual REEs was not possible at the conditions investigated, but a mixed REE product can be obtained in a single extraction stage operated at a pH of 0.5 using 1 M extractant at an O/A ratio of 1; these conditions resulted in complete Y and Eu, 95 % Ce and 99 % Tb extraction with Ca and Al coextraction below 7 %. A better quality mixed REE product can be produced by operating at lower pH and extractant concentration conditions, but this would require a larger number of extraction stages. Keywords: Cerium, fluorescent lamps, phosphors, rare earth elements, solvent extraction, terbium

Jan 1, 2020

By Y. Qin, L. Han, P. Gao, Y. Han, Y. Lia

In the present study, an innovative comminution technology of high-voltage pulse discharge was proposed for galena to weaken the mechanical property. The results of pre-treatment experiments indicated that the optimal operating conditions of spherical gap spacing 25 mm, pulse numbers 120, and loading voltage 25 kV were obtained, where the relative grindability of pretreated products was improved significantly, although with the prolonging of grinding time, the superiority of high-voltage electric pulses was gradually weakened. The galena ores were subjected to a high-voltage pulse discharge, and then the crack generating along the boundary between galena and gangue was observed under an optical microscope, and the surface burning which appeared in the ores. The scanning electron microscope (SEM) results indicated that the pretreated products were in a state of melting and then condensation, accompanied by some pore formation. Pulsed discharge pre-treatment not only produced more micro-cracks and cracks in the sample but also extended the original crack. Keywords: High-voltage pulse discharge; galena; relative grindability; micro-crack

Jan 1, 2020

By M. M. Makhofane

Anhydrous zirconium tetrafluoride can be used as a precursor for the manufacturing of nuclear-grade zirconium metal. This can be done by fluorinating plasma-dissociated zircon with ammonium bifluoride in a batch reactor. This paper describes the batch process. It was proved that anhydrous zirconium tetrafluoride can be manufactured by this route as confirmed by X-ray diffraction. The process shows potential for scaling up to the kilogram scale and possibly the tonnage scale.

Jan 1, 2012

By R. L. Setsepu, S. O. Bada, J. Abdulsalam

The utilization of biomass as a solid fuel for co-firing has received great attention from boiler manufacturers as a clean coal technology (CCT) option. This research aimed to produce biocoal pellets, as a clean energy fuel, using hydrochar from trees planted to rehabilitate acid mine drainage (AMD) water and fine coal discards. The hydrochar was synthesized by hydrothermal carbonization of Searsia lancea harvested from AMD-contaminated land at a temperature of 280°C and a residence time of 90 minutes. It was blended with discard coal (–1 mm) at ratios of 25% and 50% hydrochar to produce different forms of solid pelletized biocoal (BC). The physicochemical and mechanical properties of each of the biocoal pellet blends were determined. The 100% hydrochar had the highest calorific value of 29.99 MJ/kg, while the raw discard coal had a calorific value of 16.73 MJ/kg. The ash content decreased from 42% in the discard coal to 25% in the blend of 50% coal and 50% hydrochar biocoal pellets. Biocoal pellets comprising 25% hydrochar and 75% discard coal (BC25 HC/75 COAL) displayed the best mechanical properties (compressive strength 3.06 MPa) of all the fuels, but the physicochemical properties were inferior to the BC50 HC/50 COAL pellets. This research has demonstrated that hydrochar synthesized from a tree species planted for hydraulic control of AMD has the capability to act as a binder for improving the mechanical properties and energy characteristics of fine discard coal.

Dec 1, 2021

By M. R. L. Blackwell

Over the period 1964 to 1969 Conzinc Riotinto of Australia undertook and completed an evaluation of a large low-grade copper orebody on Bougainville Island in the Territory of Papua and New Guinea. From the outset it was clear that the geographic, climatic and topographic characteristics of the area would necessitate a heavy capital outlay on production and support facilities. Both the physical problems and the magnitude of the investment amplified the need for a thorough and rigorous evaluation of the various strategies for exploiting the orebody. In view of the number of independent and inter-related variables and the flow of new data, a computer-based evaluation process extended the scope and depth of the analysis considerably. The system used permitted an iterative assessment and re-assessment of the various strategies with the results becoming increasingly refined with time. This process encompassed the modelling of the orebody, the simulation of alternative operating strategies and the determination of the financial profitability of the project,

Jan 1, 2014

By V. V. Getman, V. A. Chanturiya, T. N. Matveeva

Most of the Au and PGM ores in Russia are characterised by a thin mineral impregnation of noble metals in sulfide minerals, and a large variety of mineral forms that lead to high loss of precious metals with fine fractions during flotation. In modern flotation technology, the rational choice of reagents is one of the main trends for selective separation of minerals and effective metals recovery. New data on the selectivity of the thermo-sensitive polymer with specific functional groups (TMPPh) as a flocculant and collector of Au and Pt fine fractions are available. The selective modified collector (DEDTCm) for the recovery of Au and Pt from complex ores is discussed in this paper. Scanning electronic microscopy (SEAM), laser SIM and AFM microscopy, UV and IR spectroscopy were applied to study the adsorbed layer of new reagents on the mineral surface. Flotation tests of TMPPh on the gold-bearing ore of the Olimpiada deposit showed an increase in Au extraction and Au content in the concentrate of the rougher flotation. Using a combination of reagents TMPPh and ButX, the quality of the Au and Pt concentrates increased in 1.7 time with an increase in recovery up to 15 % compared with the traditional reagent mode. Testing of TMPPh polymers in flotation of Pt-Cu-Ni ore at Norilsk Nickel has shown the ability to obtain a concentrate with a higher Pt content. Recovery of platinum is 17% higher than recovery in an experiment without polymer. Application of DEDTCm helped to achieve higher technological parameters in flotation of lowgrade Rt-Cu-Ni ore. Compared to the basic mode Pt recovery was plus 13%, Pd recovery was plus 9% and the content of precious metals in the rougher flotation concentrate increased in 2,5 - 4 times. The studies have been supported by Grants of the President of RF “Scientific School of Academician V.A. Chanturiya” NSh-220.2012.5, NSh-748.2014.5. Keywords: Au and Pt complex ores, flotation, flocculation, thermo-sensitive polymer TMPPh, modified collector

Jan 1, 2020

By O. T. Konina, V. A. Masloboev, A. V. Svetlov, E. A. Krasavtseva, D. V. Makarov, A. A. Goryachev

Dusting phenomena have been examined at the tailings storage facility of Apatit JSC Kirovsk, a mining operation located in the far north of the Russian Federation. The material composition of the tailings was identified. Existing dust suppression methods were examined. Field observations were undertaken and official data was obtained from the Murmansk Administration for Hydrometeorology and Environmental Monitoring, and analysed. A database was built for forecasting dusting according to critical scenarios in order to estimate the peak MPCs of suspended solids in the atmospheric air. Mitigation measures were formulated and recommended to the mining operation. Keywords: Mineral dust particles, apatite-nepheline ore concentration tailings, suspended solids MPC, climate change

Jan 1, 2020

By Y. Qin, X. Fu, T. Qi, H. Tang

"The FASTMELT ® process was developed as an alternative to blast furnace ironmaking; in this process, high-quality molten iron is produced using direct reduction followed by high-temperature slag/metal separation. In this study, iron recovery and phosphorus removal from oolitic highphosphorus haematite using the FASTMELT® process was investigated. The performance of two reducing agents, coal and wood char, was compared. Direct reduction experiments indicated that with optimized reductant addition, the ore-char and ore-coal briquettes attained metallization values of 82% and 78%, respectively, and residual carbon contents of 0.24 and 2.35%, respectively. The slag/metal separation experiments revealed that molten iron containing 0.41% phosphorus and 0.021% silicon (by mass) was produced from optimally reduced ore-char briquettes, and molten iron containing 0.78% phosphorus and 0.91% silicon from optimally reduced ore–coal briquettes. The study indicates that carbonaceous materials with high CO2 reactivity are suitable for use in the FASTMELT ® process for phosphorus removal and iron recovery from oolitic high-phosphorus haematite. IntroductionIn China, the general depletion of iron-rich mineral reserves has led to many efforts to exploit low-grade and refractory ironcontaining resources for ironmaking (Liu et al., 2014). The efficient utilization of the highphosphorus oolitic haematite resources in central China has received considerable attention. The available resources of this material total approximately 3.0 billion tons. The oolitic units in the ore exhibit an onionlike structure with phosphorus-containing gangue layers of 2–10 µm thickness. The best concentrate produced from these resources contains approximately 50% iron (Fe) and 0.8–1.2% phosphorus (P) (by mass) (Ai, Yu, and Wei, 2009; Song et al., 2013; Wu, Wen, and Cen, 2011). Further removal of phosphorus from these ores using conventional beneficiation methods is not possible."

Jan 1, 2017

By G. M. Evans, S. Mitra, A. V. Nguyen

As an alternative to the conventional flotation method, there has been continual research in an effort to enhance base metal ores and combustibles recovery using ultrasonics. These studies however were largely limited to the pre-treatment of ores for the removal of surface contaminants while the effect of ultrasonics on the bubble and pulp-phase interactions remained somewhat unexplored. Noting this deficiency, this study aimed to investigate the mechanistic effect of an ultrasonic field in an impeller less flotation cell specifically focusing on the bubble-particle interaction dynamics. A lab-scale flotation cell (capacity 1 litre) was designed, involving a vertically oriented ultrasonic probe (20 kHz, rated at 1.2 kW) and operated in the output power range from 1 to 20% with continuous liquid recirculation. Particle suspension was achieved by the combined action of recirculation and ultrasonic pulses. Interactions of coarse size glass ballotini particles (D32 = 314 μm) with bubbles (< 1 mm diameter) in the presence of a surfactant were studied, using high-speed imaging. Application of an ultrasonic pulse in the aqueous medium resulted in the generation of numerous microbubbles which increased with increasing input power and duration of the ultrasonic pulse time. Such periodic pulses introduced at a high level of turbulence in the pulp phase facilitated adequate bubble-particle contacts. Microbubbles played a key role in forming particle clusters which were observed to be floatable even in the absence of any carrier bubbles. When carrier bubbles were introduced, some of these particle clusters attached to the bubble surface and conveniently floated. It was noted that a favourable state of bubble-particle interaction was achievable to produce stable bubble-particles aggregates by suitably controlling the input power and period of the applied ultrasonic pulse. Keywords: Flotation, bubble-particle interactions, collision, attachment, detachment, ultrasonic pulse

Jan 1, 2020

By I. V. Filippova, Y. Foucaud, M. Badawi, L. O. Filippov, S. Lebègue

To optimize the flotation of Ca-minerals, their separation contrasts were investigated by coupling experimental and theoretical techniques. We showed that they mainly rely on structural properties such as the Ca-Ca distance on their exposed surfaces but also on the ability to control the intermolecular interactions. An optimized composition of the carboxylic collector by calculating the collector-mineral and the intermolecular interactions was developed. Blending the saturated acids and non-ionic molecules with a fatty acid collector significantly increases the flotation selectivity between scheelite (CaWO4) and fluorite (CaF2). The theoretical results were validated by experimentally improving the separation contrast between Ca-minerals. After the tests of several depressants and collectors, the best depression of gangue Ca-minerals (fluorite, apatite and vezuvianite) was found by combining sodium silicate and sodium carbonate. Keywords: Ca Minerals, Fluorite, Scheelite, Carboxylic acids, Unsaturated Acid, Fatty acids

Jan 1, 2020

By E. L. J. Kleynhans, J. I. J. Fick, J. P. Beukes, P. G. van Zyl

"Ferrochrome (FeCr) is vital for the production of stainless and high-alloy ferritic steels, since it is the only source of new Cr units. FeCr production is an energy-intensive process. The pelletized chromite prereduction process is most likely the FeCr production process with the lowest specific electricity consumption (SEC), i.e. MWh/t, currently in operation. However, due to increases in costs, efficiency, and environmental pressures, FeCr producers are attempting to lower their overall energy consumption even further. Recently, it was proven that pre-oxidation of chromite ore prior to pelletization and prereduction significantly decreases both the SEC and lumpy carbonaceous reductants required for smelting. This paper presents the first attempt at conceptualizing the technoeconomic feasibility of integrating chromite pre-oxidation into the prereduction process. Financial modelling yielded a net present value (NPV) at a 10% discount rate of approximately R900 million and an internal rate of return (IRR) of approximatelyy 30.5% after tax, suggesting that the implementation of pre-oxidation prior to pellet prereduction may be financially viable. Sensitivity analysis indicated that the parameter with the greatest influence on project NPV and IRR is the level of prereduction. This indicates that the relationship between maintaining the optimum pre-oxidation temperature and the degree of prereduction is critical for maximium process efficiency. IntroductionStainless steel is a crucial alloy in modern society. Virgin chromium (Cr) units used in the manufacturing of stainless steel are obtained from ferrochrome (FeCr) – a relatively crude alloy consisting predominantly of Cr and iron (Fe) (Murthy, Tripathy, and Kumar, 2011; Beukes, van Zyl, and Ras, 2012). FeCr is produced mainly by the carbothermic reduction of chromite ore in submerged arc furnaces (SAFs) and direct current arc furnaces (DCFs) (Neizel et al., 2013; Beukes, Dawson, and van Zyl, 2010; Dwarapudi et al., 2013). The energy required to heat, smelt, and reduce the chromite ore to the metallized state is supplied by electricity (Pan, 2013). FeCr production is an energy-intensive process, with a specific electricity consumption (SEC) varying from 2.4 MWh/t to more than 4.0 MWh/t FeCr produced, depending on the process applied (Pan, 2013; Neizel et al., 2013). Daavittila, Honkaniemi, and Jokinen (2004) stated that the typical operational costs of FeCr smelters can be divided into four categories, i.e. chromite ore (30%), carbonaceous reductant (20%), electricity (30%), and other production costs (20%). This makes electricity consumption the joint largest factor that influences operational costs in FeCr production."

Jan 1, 2017

By L. Gutierrez, R. Yepsena

Enargite in porphyry copper deposits is an important mineral as it displays good floatability under the presence of the collectors usually used in the flotation of copper sulfides. As a result, copper concentrates grades are reduced. As scarcity of water resources is a problem relevant to Chilean mining, the use of seawater is a feasible solution. The behaviour of copper sulfides and molybdenite in the process of flotation in seawater was previously studied but not for enargite. The objective of this research is to study the behaviour of the enargite in different conditions of electrochemical potential during the process of flotation using seawater. The study was carried through micro-flotation tests using pure samples of enargite, at Eh values ranging from -300 to 500 mV(SHE), both in seawater and aqueous solutions containing calcium and magnesium. The results show that at pH 10.5 in seawater, the enargite and chalcopyrite recoveries are reduced throughout the whole range of Eh studied. At pH 9 in seawater, enargite and chalcopyrite are depressed under reducing and slightly oxidising conditions. The recovery of both minerals drastically decreases at Eh values lower than -100 mV and greater than 400 mV. The behaviour of enargite in seawater flotation differs from that observed in conventional water, since in the latter case the recovery of enargite decreases at higher potentials close to 500 mV. Keywords: Enargite, flotation, seawater, redox potential

Jan 1, 2020

By M. Rudolph, A. van Hall, G. Öktem, S. G. Özkan, A. Hassanzadeh

Despite the four-decade study on ultrasound’s (US) impact on mineral’s floatabilities, there is still not clarity regarding its role in mineral surface wettability. For this purpose, the present investigation endeavours ……the hydrophobicity and floatability characteristics of a chalcopyrite-pyrite-quartz (Cp- Py-Qtz) system in the presence and absence of an ultrasonic pre-treatment. The ultrasonic process was carried out by a sonopuls at a constant frequency of 20 kHz with an adjustable power level from 30 to 200 W. Initially, the impact of sonication time (15, 30, 45, 60 and 90 s as well as 10, 20 and 30 min) and power magnitude (30, 60, 90, 120 and 180 W) were evaluated while the dissolved oxygen, temperature, conductivity and pH were also monitored. Collector-less micro-flotation tests were carried out on the non-pre-treated and the US pre-treated samples at 60 W and 15 s. The samples’ hydrophobicities were determined by the drop shape analysis approach. The dissolved-oxygen level was varied using a mini bench pressurised water reactor to study the effect of O2(aq) concentration on the chalcopyrite and pyrite wettability characteristics. The results showed that the minerals’ hydrophilicities were relatively more sensitive to the sonication’s time than its power that resulted in reducing all three minerals’ hydrophobicities. In addition, it was found that the dissolved-oxygen content and creation of sub-micron sized bubbles led to an improvement on chalcopyrite and pyrite hydrophobicities. Finally, we proved that the Cp’s floatability increased and Qtz’s recovery reduced while being subjected to the ultrasonic irradiation (15 s at 60 W); however, Py’s recovery remained constant. This conclusion confirmed the possibility of a selective separation in ultrasound-assisted copper ore flotation. We recommend that further advanced investigations be conducted, using an X-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM) to thoroughly understand the surface modifications induced by the ultrasonication

Jan 1, 2020

Dr Hanekom I would like to thank Dr Hanekom for a very valuable -contribution; it summarizes careful statistical test work which was an omission from the original paper. Minor manipulative details, the application of a finer measuring graticule and the reproducibility of the procedure are described and the author accepts with gratitude this ready-made answer to the first and second points of Dr Finkelstein&apos;s comments. Mr Williamson The author is indebted to Mr Williamson for historical background to early experiments with captive bubbles and it is conceded that the original paper described another avenue to an old flotation goal. The field of application is restricted and we would not work with all the material illustrated by Klassen and Mokrousov.1 The particles in Figure 74(a) are far too large and irregular; material in Figures (b) through (d) could be employed for semi-quantitative work in spite of obvious disadvantages; Figure 74(f) represents ideal conditions. We have studied this mineral-collector association in the size range given and results were satisfactory. For larger pick-up values than that illustrated an induction period of more than 0.01 second was required (actually 90 seconds for a maximum bubble load at pH 7.2 with 25 g/t oleic acid!). REFERENCE 1. KLASSEN,V. I. ANDMOKROUSOV,V. A., &apos;An Introduction to the Theory of Flotation,&apos; Butterworths, London, 128, Figure 74, (1963). Mr Slander and Mr Kooij Researchworkers in a practical mineral development laboratory may well ask what contribution yet another micro-technique can make to the problems of large scale ore flotation. The obvious answer is that there can be little or no direct translation of results obtained with a static system comprising air bubble and pure mineral concentrate to a dynamic multicomponent operation. However, for the rapid study of one mineral or variable some small scale apparatus must be employed. In the Anglo American Research Laboratory, the described semi-quantitative pick-up technique has filled a niche and requirement. For ourselves, the system represents a definite advance over the contact angle approach in that samples of minerals conventionally prepared in laboratory or plant may be used, which is a desired step nearer flotation. We bracket this pick-up apparatus with the Hallimond tube1,2 and evidence is now to hand that pick-up curves may often be related to flotation recoveries obtained from this tube with pure mineral samples and from the Fuerstenau glass cell3 with the total ore at low pulp densities. We would not wish to push the comparison of pick-up results past this stage for there is much published development work relating the Hallimond and Fuerstenau equipment to flotation on a larger scale. At the Anglo American Research Laboratory for example, a test in a Fuerstenau cell is often the final integrated step in laboratory investigations into the TORCO process. As these contributors rightly point out, pick-up tests can offer nothing towards the determination of optimum reagent dosage for large scale flotation. This is the function of bench-type flotation cells with up to 2 kg batches of ore. At this level, collector performance and consumption and physical properties of the froth are more comparable with large scale operation. The pick-up cell, Hallimond tube and Fuerstenau cell are essentially equipment from which the effect of control parameters can be derived. For the assessment of collector behaviour, the pick-up approach is rapid and economic and we offer here a pick-up contribution towards the flotation of Witwatersrand uraninite with anionic sulphonate collectors (Fig. 1). A large crystal of the local mineral was not available for contact angle measurements and owing to its low concentration in Witwatersrand gold-bearing reef, a small sample was laboriously obtained by tabling, superpanning and heavy medium separation. The pick-up values of a sized portion were determined by the described procedure in the presence of nine petroleum sulphonate collectors. Responses fell into two categories; "normal" curves (dotted lines) and a group of collectors which were very active at low concentration but showed depression of pick-up at the higher levels. The similarity in form of curves for collectors 1 and 3 was apparent and reagent 3 was found to be simply a diluent of 1. Otherwise, collector performance could not be related to either sulphonate content or molecular weight of the active constituent. However, reagent 2 gave the best performance in a bench flotation cell with regard to overall uranium distribution but, as predicted, reagent 1 yielded the best grades. Later pick-up tests with a similar class of collector have suggested that depression at high reagent concentrations may be due to "bubble armouring" whereby an hydrophilic air-liquid interface is produced which rejects mineral attachment. Prolonged investigations with the same mineral sample have not been required except for the study of uraninite which lasted for more than a year. Variation in pick-up response could not be detected over this period during which the mineral was stored under distilled water. The only visible change was a small efflorescence of lead sulphate, readily removed and decanted off after stirring with a glass rod in the sample tube. In its main role as a "trouble-shooter", the pick-up method is applied to fresh mineral samples taken from a flotation plant and soon discarded or from a current run in the ore-dressing laboratory. After production of a concentrate, a solvent cycle, as described in the original paper, may be required to remove heavy organics or other contaminants as when a sample has been taken from circuits containing detergents, grease or return flotation solutions. This solvent cycle will not remove chemisorbed collectors and we prefer not to work with minerals from flotation tailings or with pick-up cell discards. It has been thought preferable to answer the contributors&apos; other apprehensions with regard to sample preparation, activators, depressants and the physical properties of reagents in another paper on offer to this Journal. It covers pick-up investigations relating to the flotation of nickeliferous pyrrhotite at two Anglo American Corporation Mines, which approach seemed the correct orientation for a reply to another contributor to this paper.

By S. Moodley

In the chloride process for TiO2 pigment production, various titania feedstocks (i.e. rutile, synthetic rutile, slag, and upgraded titania slag (UGS)) are chlorinated in a fluidized bed reactor with petroleum coke at temperatures between 1000°C and 1100ºC to yield gaseous metal chlorides. Although feedstock preference is largely based on TiO2 content, feedstock physical properties (i.e. density, sphericity, size distribution, and porosity) differ; these differences will affect fluidization behaviour and can inadvertently affect conversion efficiency. For example, a high carryover from the reactor reduces particle residence time and decreases conversion rates. Owing to dwindling rutile reserves in the world, most chloride producers are forced to feed blends of feedstocks to their chlorinators; and so it becomes important to understand whether blends have an effect on the hydrodynamic properties of the bed. This paper describes the physical characterization of different feeds and the determination of the elutriation constants for slag, rutile, synthetic rutile, and a blend (i.e. 50 wt% rutile, 50 wt% slag).A common feature of the tests was that particles finer than 75 µm tended more than any other size to be elutriated. The tested rutile, classified as a Geldart Group B material, had the lowest carryover, whereas the slags had the highest. Interestingly, the elutriation constant ([ki]) of the blend is lower than those of either of its individual components.

Jan 1, 2012

By I. Mitov, A. Stoilova, D. Krastev, B. Yordanov

We present three technological scenarios for the recovery of valuable components from gangue, stored in the tailings dam at Kremikovtzi metallurgical plant in Bulgaria, into marketable iron-containing pellets. In the first approach the iron concentrate was recovered through a two-stage flotation process, desliming, and magnetic separation. In the second proposed process, the iron concentrate was subjected to four sequential stages of magnetic separation coupled with selective magnetic flocculation. The third route entails the not very common practice of magnetizing roasting, followed by selective magnetic flocculation, desliming, and magnetic separation. The iron concentrate was pelletized in a laboratoryscale pelletizer. Each technology has been assessed with regard to the mass yield of iron concentrate, the iron recovery. and the iron, lead, and zinc content in order to identify the most effective route.

May 1, 2021

By R. Kumar, N. R. Mandre

"The beneficiation of iron ore slimes by selective flocculation was studied. Polyacrylamide (PAM) and guar gum were used as flocculant, along with sodium hexametaphosphate (SHMP) as a dispersant. The samples collected were initially subjected for chemical and mineralogical studies. The mineralogical studies indicated the presence of haematite and goethite as the principal iron-bearing minerals, with quartz and kaolinite as gangue minerals. The selective flocculation tests showed that the Fe grade can be enhanced from 58.24% to 64.60% Fe at a recovery of 66.33% using polyacrylamide as the flocculant. A Fe grade of 63.20% at a recovery of 68.04% was obtained using guar gum as flocculant. The efficacy of the studies was analysed using a separation index, which indicated that the higher separation index was obtained with the tests employing polyacrylamide as the flocculant. IntroductionIndia is endowed with huge reserves of highgrade iron ore and is one of the prominent producers in the world. As the high-grade iron ores have been exhaustively mined, it has become imperative to use low-grade iron ores, fines, and slimes to meet the growing demand. Also, generation of fines and slimes during mining and processing contributes to loss of minerals to the extent of 30% of the total value (Mandre and Panigrahi, 1997). These fines/slimes are often discarded as waste into tailing ponds, containing considerable amounts of iron. Therefore beneficiation of tailings/slimes has become necessary for optimal utilization of the resources.In recent years, interest in recovery of valuable minerals from low-grade ores, slimes, and tailings has increased worldwide. These activities are initiated not only to recover minerals but also to address various environmental issues associated with fine particle treatment. The literature reveals that several technologies have been employed in this regard, including flotation, advanced gravity separation, and high-intensity magnetic separation. However, these processes are found to be ineffective for fine particle treatment due to lower collision probability in flotation, decreased gravitational effect in gravity separation, and reduced drag force in magnetic separation, among other factors (Batisteli and Peres, 2008; Das et al., 2007; Dworzanowski, 2012; Rocha, Caneado, and Peres, 2010). Therefore, it is in this regard that selective flocculation has gained importance in treating slimes in recent years."

Jan 1, 2017

By B. D. H. Knights

In November 2009 Mintek installed the FloatStar? advanced flotation stabilization system on Vale&apos;s Cauê iron ore beneficiation plant in Brazil. In September 2010 the system was upgraded to include flotation optimization. The circuit consisted of two parallel cleaner circuits producing final concentrate. The tailings from the cleaner section passed through a scavenger circuit. Large, well-instrumented feed sumps played an important role in circuit stability, presenting a good opportunity for advanced control. Previously the plant was controlled using distributed control system (DCS) level control only. The flotation circuit processes roughly 30kt/day. The FloatStar system provided advanced control of the flotation circuit as well as of the sumps feeding the circuit. The system underwent a lengthy trial to assess the benefit that it provided. Two data sets were analysed, showing performance under advanced stabilization and optimization respectively. Several validation and consistency criteria were employed to ensure the quality of the analysis. Iron recovery and iron tailings grade were used to measure system performance. The analysis showed that the system increased recovery by up to 2.7%. In addition, the system decreased the iron tailings grade by between 1.2% (from 23.5% to 22.3%) and 4.3% (from 31.3% to 27.0%) during different test campaigns. The analysis also showed that the entire FloatStar stabilization system was active for 72.7% of the time from first activation to the end of the first data set (approximately 200 days). From the analysis it was concluded that under similar conditions for &apos;ON&apos; and &apos;OFF&apos; tests, the system provides a clear benefit. It was also found that over the longer term, the system continues to provide a benefit. This finding suggests that the results were not simply due to a short-term advantage. The size of the data set, as well as the magnitude of the recovery improvements, lends considerable confidence to these results. Therefore, it can be concluded that the FloatStar control system provides substantial benefit to operations at this site.

Jan 1, 2012

It is well known that the ability to influence project value reduces significantly as planning progresses and decisions regarding project parameters are made. However, at the prefeasibility stage in particular, where one of the main aims should be to evaluate a wide range of options in order to select the best for more detailed further study, there is often a reluctance to spend the time and money needed to do this rigorously. This paper demonstrates, by a number of case study examples, how significant increases in value may be obtained by fully evaluating the combinations of alternatives for various project design parameters, including (though not limited to) mining methods, haulage methods, mining rates, processing methods and rates, sequencing of mining, and cut-off grades, with changes and upgrades over time where applicable. The additional value unlocked is typically orders of magnitude greater than the additional cost of the more comprehensive study. The dangers of misuse of simplistic sensitivity analyses and failure to identify how strategies might change in response to changes in external factors are also illustrated, and the importance of selecting the best `grade descriptor&apos; is discussed.

Jan 1, 2007