Search Documents

By G. M. Gay, R. L. Perrine

This paper describes a method of numerical computation for three-dimensional, unstable, miscible displacement behavior useful for heterogeneous systems, as well as for more ideal conditions. In the method, flow equations are first linearized by a perturbation approach. The basic flow process is separated and a solution for its behavior readily obtained. The remaining problem of deviations from the basic flow caused by non-ideal conditions is then subjected to numerical analysis. Results obtained from use of the method are also presented. Although conditions assumed in the test cal-culations were severe, results show the type of dispersing flow expected and appear quite satisfactory. The method has eliminated or reduced in importance problems of oscillating values near steep fronts, excessive computer smoothing, etc. A unique advantage of the method is that the source of variations from ideal behavior can be observed. ,The one serious drawback results from the algebraic complexity of the perturbation approach, and the need for second-order terms to be retained in calculations of interest. Fewer array points are available and more computer time is required than would be desired. However, these difficulties are also experienced with other approaches to the solution of three-dimensional dispIacement problems. INTRODUCTION Prediction of behavior of the miscible displacement process within a porous medium for any system of engineering importance is plagued by a number of difficulties. With typical fluid properties the displacing fluid has the lower viscosity, and there is a natural tendency toward flow instability. The problem of predicting instability is compounded by the fact that every real system is heterogeneous. Permeability will vary from point to point — not entirely systematically, and yet not in a random fashion leading to a readily defined average. Furthermore, permeability is unlikely to be isotropic. These permeability properties, which are characteristic of any real porous medium, accentuate the effects of flow instability. Another factor to be considered is that flow dispersion accompanies the displacement process in a porous medium. Mechanistically, dispersion is due to the fact that flow between any two points in the medium follows multiple tortuous paths, each characterized by slightly different flow properties. The fact that the coefficient characterizing dispersive properties of the real medium JS a tensor with variable elements complicates matters. Further difficulties arise because the parabolic influence, while not negligible, is small. Thus, there is a tendency toward steep and uneven displacement fronts along which dispersion smoothing must be represented accurately. Yet frequently used numerical analysis schemes may tend toward either instability, oscillation or excessive smoothing, none of which gives the desired accurate picture of flow behavior. Thus, while many experimental and analytical studies of the process have been made, predictions of actual performance are still subject to considerable uncertainty and possible improvement. This paper reports on part of a study which attempts to develop improved methods for solution of the flow equations describing the miscible displacement process. Of necessity, the calculations were performed on a large digital computer. A three-dimensional system is represented, and the coefficients defining dispersion and permeability can be varied in a manner representative of a real system. Because the differential equations are nonlinear, a first step is to linearize them using a perturbation approach. Objective of this approach has been to separate the basic flow which would occur in an ideal system and for which predictions are readily made. Then the numerical analysis, which is necessarily complex, is directed toward solution of the perturbation equations. These equations state how the basic flow is modified

Jan 1, 1967

By R. G. Aspden

Crystals with an (001) [loo] initial orientation of an iron-base alloy containing 3 pct Si were cold rolled with and without the use of constraints. A major difference in the rolling and annealing textures was observed between crystals rolled with and without constraints. These data show that the contribution of constraints at grain boundaries in a poly crystalline sheet should be considered in applying textural data on single crystals to grains in an aggregate. SILICON-iron alloys with a cube texture have been recently developed and their magnetic characteristics reported.1-4 Of interest in the development of this texture were the textural changes of single crystals accompanying rolling and annealing and the influence of constraints at grain boundaries in an aggregate on the behavior of individual grains. The present study was primarily concerned with the effect of constraints during rolling on the textures of 3 pct Si-Fe crystals initially (001)[100]. Barrett and Levenson5 were among the first to observe an influence of constraints at grain boundaries on the textural changes of individual grains during deformation. They tested Taylor's6 theory of plastic deformation of face-centered-cubic metals in which deformation textures were predicted. About one-third of the grains in poly crystalline aluminum did not rotate as predicted. Grains of the same initial orientation were observed to rotate in different directions under the influence of applied stress and anisotropic flow of neighboring grains. Recently, the various inhomogeneities of flow of crystals in an aggregate have been studied7'8 and reviewed.9-11 Barrett and Levenson" rolled (001) [loo] iron single crystals inserted in close-fitting holes in copper to limit lateral flow and to simulate rolling of grains in an aggregate. Deformation bands were formed after a 90 pct reduction in thickness, and the cold-rolling texture contained two components described by rotating the (001)[100] about 35 deg in both directions around the normal of the rolling plane. No annealing textures were reported. Chen and Maddin13 rolled molybdenum single crystals initially (001) [loo]. The crystals were mounted between two hardened silicon-iron plates and 96 pct reduced in thickness by rolling at a low rate of reduction, about 0.0001 in. per pass. The deformation texture had the mean orientation of (001) [loo], and the azimuthal spread included orientations described by rotating (001) [loo] about 35 deg in both directions about the pole of the rolling plane. The presence of deformation bands were not reported by Chen and Maddin or detected in subsequent work of Ujiiye and Maddin.14 The ideal orientation of the annealing texture was (001) [loo]. Recently, Walter and Hibbard 15 reported on the textures of 3 pct Si-Fe alloy crystals initially near (001) [loo]. Each crystal was in an aggregate cut from a columnar ingot. After 66 pct reduction by rolling, the texture consisted of two symmetrical components which had the orientations described by rotating (001) [loo] about 30 deg in both directions about the pole of the rolling plane. Annealing texture was near (001) [loo]. In the above work, the textures of body-centered-cubic crystals were studied after rolling under the influence of constraints. The deformation textures varied from (001) [loo] to near the (001) [110] type and appeared sensitive to the manner in which the crystals were rolled. No textural data were available on the effect of rolling (001) [loo] crystals with and without constraints. The purpose of the present work was to evaluate the influence of constraints during rolling on the textures of 3 pct Si-Fe crystals initially (001) [loo]. Rolling and annealing textures were studied for a) crystals rolled with no constraints at different rates of reduction, and b) crystals rolled with constraints imposed by neighboring grains and by plates between which a crystal was "sandwiched". PROCEDURES AND EXPERIMENTAL TECHNIQUES Data are presented on four crystals which are representative of several crystals studied. The orientation of each crystal prior to rolling was (001) [loo] as determined by the Laue X-ray back-reflection method," i.e., each crystal had an (001) within 3 deg of the rolling plane and [100] within 3 deg of the rolling direction. These crystals were obtained from two iron-base alloys containing 3 pct Si by weight which were prepared by vacuum melting electrolytic iron and a commercial grade of silicon. Crystals 1, 2, and S-1 were cut from a large single crystal grown from the melt of one alloy by the Bridgman technique17 in an apparatus described by

Jan 1, 1960

By A. T. Chatas

A description of the geometrical characteristics of spherical reservoir systems, a discussion of unsteady-state flow of such systems and examples of engineering applications are presented as backgmund material. The fundamental differential equation, a description of average spherical permeability and the introduction of the Laplace transformation serve as theoretical foundations. Engineering concepts are investigated to indicate particular solutions of interest, which are analytically obtained with the aid of the Laplace transform. These are numerically evaluated by computer, and presented in tabular form. INTRODUCTION A tractable mathematical analysis of unsteady fluid flow through porous media generally requires incorporation of a geometrical symmetry. The simplest forms include the linear, cylindrical (radial) and spherical. Most analytical endeavors have concentrated on cylindrical symmetry because it occurs more often in petroleum reservoirs. Nevertheless, some reservoir systems do exist that are better approximated by spherical geometry. Review of technical literature revealed but a single reference to unsteady spherical flow in petroleum reservoirs.l The motive and purpose of the present work was to remove this gap in technical information, and to provide the practicing engineer with some useful analytical tools. The mathematical details associated with the particular solutions of interest involved use of the Laplace transformation. Hurst and van Everdingen previously demonstrated the efficacy of this operational technique, and in many respects the present treatment was patterned after their earlier work.2 PRELIMINARY CONSIDERATIONS GEOMETRICAL CHARACTERISTICS Geometrically, a spherical reservoir system is defined at any instant of time by two concentric hemispheres whose physical properties of interest vary only with the radial distance. Every physical property is thus restricted to be a space function of only one variable: the distance along a radius vector emanating from the center. Such a system is composed of an outer region and an inner region, separated by a defined internal boundary. The inner region simply extends inward from this boundary, whereas the outer region extends outward from it to an external boundary. The position of the internal boundary is presumed fixed, so that the size of the inner region remains constant. On the other hand, the position of the external boundary at any given instant of time is determined by the distance into the system that a sensible pressure reaction has occurred, Thus, the external boundary may change position with time. It initially emerges from the inner region and advances outward to its ultimate position. When this ultimate position coincides with a geometric limit, the reservoir system is said to be limited. When it coincides with points subject to pressure gradients furthest removed from the internal boundary, yet short of a geometric limit, the system is said to be unlimited. In this investigation two different boundary conditions are imposed at the ultimate boundaries of limited systems. The first requires that no fluid flow occur across this boundary; the second that the pressure remain fixed at this boundary.3-5 UNSTEADY-STATE FLOW In a strict sense virtually all flow phenomena associated with a reservoir system are unsteady-state. The transient behavior of these phenomena requires accounting, however, only when time must be introduced as an explicit variable. Otherwise, steady-state mechanics may be used. Analytically, steady-state conditions prevail in a reservoir system only over that portion of its history when this relation is satisfied:

Jan 1, 1967

By U. C. Tainton

The paper reviews the evolution of electrolytic zinc, describing some of the major obstacles that have been encountered and overcome. The chief remaining limitations of present-day standard practice are: Difficulty of obtaining high extractions, especially from low-grade and complex ores; filtration troubles, if ores contain much soluble silica; and irregularities in electrolysis, if more than certain limited amounts of antimony, arsenic, cobalt; etc., are present in the ores. These factors dictate a relatively high-grade plant feed, thus subjecting the electroytic-zinc process to the same kind of limitations as the zinc smelter. The "high acid process," in which both acid strength and current density are raised to about four times the usual figures, is described. This system concentrates both plant and operations, allows a simple type of flow sheet, and. minimizes some of the difficulties above mentioned. The large-scale operation of the process is described. SOME time ago, at a meeting of the Institute Prof. J. W. Richards1 said, "I take exception to the statement that all the factors in the production of electrolytic zinc were known long ago. There is possible in my opinion an improvement of perhaps 50 per cent. in the new electrolytic processes." An examination of the literature of the subject will show the justness of Professor Richards' contention. The work of the earlier investigators was carried on in the shadow of difficulties that, today, are hardly more than memories. We seldom hear now of zinc sponge, that bête noir of the electrolytic-zinc pioneers. Zinc sponge, was the name given to a peculiar, soft, black, non-adherent form of zinc deposit that was utterly useless for melting into ingot form. At the big plant at Cockle Creek, New South Wales, in 1897, Edgar Ashcroft2 said that the solution in the plant would suddenly, and without ascertainable cause, go "bad" and begin to deposit spongy zinc. The most delicate, even spectroscopic, methods of analysis were unable to detect any difference between "good solution and "bad" solution; either form might change to the other on being kept for a while. When it is added that an outbreak of this insidious disease (which. appeared to

Jan 2, 1924

By C. Laird, C. E. Feltner

An investigation into the effect of a material's slip character on its high strain fatigue properties has been carried out using copper and Cu-7.5 wt pct A1 as representative wavy and planar slip mode materials, respectively. In copper, the constant term and exponent in the Coffin-Manson equation, ?EpNf1/2 = const, are unaffected by the temperature of testing or the history of the metal. On the other hand, in Cu-7.5 wl pcl Al, while the exponent is invariant, the constant is increased with respect to copper and increased further with decrease in temperature. The life in Cu-7.5 wt pct A1 is double that of copper at room temperature and about four times at 78°K. Fractoflaphic studies indicate that these diffevences in life are associated with the early stages of cracking. In copper, severe surface rumpling provides crack nuclei at pain boundaries independent of' testing temperature or the history of the metal. In Cu-7.5 wt pct Al, the planar slip mode of deformation prevents grain boundary folding; crack nucleation is therefore mainly transgranular and the increase in life with respect to copper is associated with a prolonged linking-up stage of such transgranulay cracks. At the lower temperature the increased difficulty of cross slip inhibits multiplication of trans-granular cracks and retards the linking-up process, giving a further enhaancement in life. It is expected that such behavior will be found general in materials of wavy and planar slip mode, respectively. STAGE II crack propagation in high strain fatigue takes place by a repetitive process of crack tip blunting in the tension part of a fatigue cycle followed by resharpening of the crack in the compression part.1-3 This mechanism has come to be called the "plastic relaxation process".3 At very high strains (lives to failure less than 103 cycles), most of the life of a specimen is spent in crack propagation by the plastic relaxation process.4,5 Since the differences in the cyclic strain hardening behavior of metals and alloys are comparatively small in this strain range,6,7 the amount of blunting at a crack tip depends primarily on the applied strain amplitude. The rate of crack propagation in this life range is therefore nearly constant with respect to material and temperature of testing. In the longer life portion of the high strain fatigue range (l03 to 103 cycles to failure), a considerable fraction of the lives is spent in crack initiation and Stage I growth. Grain boundaries have frequently4,5,8 been found to be the sites for this growth which is also associated with a surface folding process.4'5 Such folding behavior may also be general in any material having a grain structure and capable of plastic deformation. It has therefore been suggested475 that the universality of the Coff in-Manson law,9'10 constant,* where ?Ep is the plastic strain range and Nf the number of cycles to failure, is reflected in the approximate invariance of both the crack initiation and propagation behavior. It happens that, in most investigations of the phenomena associated with failure,4,5,8 materials with a wavy slip mode have been used as vehicles for the studies, or else "normally" planar slip mode materials have been tested under conditions giving rise to wavy glide deformation, e.g., stainless steels cycled at high temperature.'' The purpose of the present investigation was to determine whether or not different cracking phenomena would occur when the slip mode of a material is planar and if the associated life to failure would be different than that of a wavy slip

Jan 1, 1968

By E. P. Polushkin, Henry L. Shuldener

This paper describes the results of microscopic examination of a series of brass pipes removed from apartment and office buildings in New York City, adjacent localities on Long Island, and Philadelphia. They were selected as typical of approximately four hundred pipe specimens obtained over a period of five years during an investigation of corrosion in hot-water installations. A part of the investigation is reported in this paper and includes a brief history of the pipes, a description of their inside surface and microstructure, and a study of the effects of corrosion, with particular reference to the structural aspects of local and selective dezincification. Although the bibliography on the corrosion of brass pipes is quite extensive, it refers almost entirely to corrosion in sea water. The authors believe that their examination of this series of pipes, which had been subjected to the corrosive action of fresh water for various lengths of time, may throw some additional light on the problem of corrosion. Pipes Examined The pipes were made by different manufacturers and their sizes range from 3/4 in. to 4 in. nominal inside diameter, the majority being within I to 2 in. They can be divided into two groups according to chemical composition: (I) with a copper content of 60 to 62 per cent and (2) with a copper content of 65 to 68 per cent. The first group (pipes made of Muntz metal) comprises 22 pipes and the second (pipes made of high brass) comprises 18 pipes. The pipes had been in service in various locations in the hot-water systems of the buildings involved. Some were taken from horizontal lines in the basement, some from overhead distributors and some from vertical risers. The distance, in terms of feet of pipe, of the specimens from the hot-water generator was no less than 75 ft. and often IOO to 300 ft. In the majority of cases the water-heating equipment was provided with a regulator to limit the temperature of the hot water supply. The normal range of temperature in pipe systems of this kind is Ioo° to 160°F. Water Supples The average chemical composition of the water supplies carried by the pipes is shown in Table I. In evaluating the corrosiveness of a natural water, four factors are considered of prime importance: namely, hardness, alkalinity, pH and silica content. The waters listed in Table 1 are characterized by relatively low hardness, 10, alkalinity, low pH and low silica content. The waters of lower pH and higher CO2 content are more corrosive. A characteristic of all of these waters is that they do not deposit a protective mineral coating as do waters with high bicarbonate of lime content, which would be reflected

Jan 1, 1945

By N. S. Stoloff, R. C. Ku, R. G. Davies

The stress-strain behavior of Fe-Co and Fe- V alloys containing up to 25 pct solute have been studied in the temperature range 25° to - 196°C. The microyield stress is independent of temperature for all alloys studied, while the temperature dependence of the ordinary yield stress is large and comparable to that for unalloyed iron. An alloy-softening phenomenon is observed for many alloys relative to unalloyed iron, and appears to be a consequence of removal of inter-stitials from solution and their subsequent agglomeration. The ductile to brittle transition temperature is increased markedly by both cobalt and vanadium. Transmission electron microscopy observations reveal that cross slip and cell formation are restricted with increasing solute, which can account for many aspects of yielding and fracture behavior. IRON and other metals of bcc structure slip on many planes of the (111) zone at moderate and elevated temperatures, giving rise to wavy glide. At low temperatures, however, there is a tendency for slip to be restricted to planes of only one or two crystallographic types; in the case of Fe-Si alloys for example, (110) glide predominates, giving rise to planar slip bands."' Restriction of cross slip at low temperatures in iron has been linked by Brown and Ekvall3 to increased strain hardening in the preyield microstrain region, leading to an apparently large temperature dependence of the yield stress. Support for this view has been provided by Lawley and Gaigher4 from a transmission electron microscope study of molybdenum. They concluded that dislocations at lower temperatures, by virtue of their inability to change planes readily, are unable to interact and annihilate, leading to an increase in internal stress and work-hardening capacity. Restriction of cross slip at low temperatures has also been suggested to be an important factor in determining the ductile to brittle transition of single-phase solids, including metals of bcc structure.5 It is pertinent to note that most solute elements tend to raise the ductile to brittle transition temperature of poly crystalline ferrite,6,7 although in some cases, e.g., Fe-Cr7 and Fe-Al,8 the dilute alloys may actually yield at lower stresses than unalloyed iron. It appears, therefore, that solute elements may have an effect analogous to lowering the test temperature with regard to restricting cross glide. Such an effect has indeed been observed in the ionic alloy system KCl-KBr,9 in which bromine atoms, although causing little misfit and consequently little effect on the yield stress of KC1, have a pronounced effect in restricting wavy glide and inducing brittleness. The purpose of the present investigation was to determine the effects of selected solute atoms on the yield stress and fracture behavior of iron, and to elucidate in turn how the slip character was related to these properties. Since it is known that interstitial atoms exert a strong influence on the mechanical behavior of iron, the solute elements chosen for study were vanadium, which reacts strong with interstitials,10 and cobalt, which does not form highly stable interstitial compounds." EXPERIMENTAL PROCEDURE Four-pound ingots of each of the following alloys were vacuum-melted in zirconia crucibles: Fe-1, 5, 10, 25 at. pct Co, and Fe-1, 4, 10, 20 at. pct V. An ingot of unalloyed iron from the same original stock as that used for the alloy was remelted under similar conditions to eliminate variations in interstitial content arising from differing thermal histories. Chemical analyses of the iron, cobalt, and vanadium melt stock are listed in Table I. All ingots were rolled and swaged, commencing at 850°C, to 1/4-in.-diameter bar. The bars were then annealed at 850°C for 1 hr (except that the 10 and 20 pct V alloys were heated for 2 hr) to give a uniform equiaxed grain size of about 0.05 mm. Tensile samples of 0.125 in. diameter by 0.8 in. gage length were utilized for studies of the ductile to brittle transition. A second set of tensile samples were utilized for microstrain experiments in which strain sensitivity of 1 x 10"6 was achieved by a capacitance method.3 Cylindrical compression samples 0.250 in. diameter by 0.4 in. long also were prepared to study the influence of composition on the macroscopic yield stress, and for metallographic analyses of defor-

Jan 1, 1965

By J. L. Bruce

AFTER six years of war-enforced idleness, Cyprus copper mines are operating again. This relatively long shutdown seems infinitesimal when compared with something like seventeen hundred years of inactivity that followed the important operations of the ancient Romans, and continued until the twentieth century. The historical records of the ancient operators are scarce but full of interest to those who realize that Cyprus copper production was important more than two thousand years ago. This paper, however, will give only a brief review of the ancient history and the evidence of ancient mining which have been quite fully covered in other publications.1-6 The purpose of this paper is to give a general sketch of the Cyprus Mines Corporation's enterprise in the Island of Cyprus, with special emphasis on those conditions and practices which are unusual. The picture is not intended to be complete, and many interesting details will be omitted. Some of these may be described in subsequent papers covering departmental practices. The principal operations of Cyprus Mines Corp. are in Cyprus, where it has leasehold concessions from the Cyprus Government covering about 50 square miles. It holds additional areas under "Prospecting Permits." The consideration for the concessions is a royalty on production, coupled with minimum annual rentals. Cyprus is a British Colony in the Eastern end of the Mediterranean with an area of about 3000 square miles and a population of about 400,000, of which 65 pct may be classed as Greeks on the basis of language, religious training, and traditions. About 25 pct are Moslems, principally of Turkish extraction. Prevailing languages are Greek and Turkish. A large proportion of the supervisory and administrative staff and practically all of the skilled and unskilled craftsmen and laborers are drawn from the native population. The "overseas" staff constitutes not more than 2 pct of the employees. The majority of these are from the United Kingdom, the British Dominions and Colonies. About one-third are from the United States of America. The topography of the Island is rugged, with mountains and foothills covering more than two-thirds of the area. Between the Kyrenea range rising to 3000-ft elevation, along the north coast, and the Troodos range (maximum elevation 6400 ft) occupying the southwest half of the Island, lies a cultivated rolling plain, the "Mesaoria," dry in summer and watered only by the winter rains and by scanty irrigation from small mountain streams and wells in the spring and summer. Climate and natural vegetation are characteristic of semi-arid conditions. The "urban" population, about one-fourth of the total, lives in the five port towns, Famagusta, Larnaca, Limassol, Paphos and Kyrenia, and in the capitol Nicosia, near the center of the Island. The suburban population lives almost entirely in villages or small towns, with very few people residing in isolated country homes.

Jan 1, 1947

By D. A. Elgillani, S. Atak, D. A. Rice, M. C. Fuerstenau, R. B. Bhappu

Quartz and feldspar cannot be floated with sulfonate at any pH; spodumene floats over a narrow acid pH range, while beryl responds moderately over a broad pH range. After wet-grinding in a steel mill, beryl, quartz, and spodumene float well with sulfonate below about pH 7, whereas the improvement in the response of feldspar is not so marked. A mechanism by which iron can be adsorbed on these minerals is presented. Also, the responses of leached, natural, and wet-ground beryl to amine, sulfonate, and oleate flotation are shown and related to the measured zero-points-of-charge of these materials. Earlier work with leached beryl showed that good flotation could be obtained with alkyl aryl sulfonate over a rather wide pH range using a Fagergren flotation cell.' When a similar response was observed with leached quartz, it was decided that unintentional activation was being obtained from the metallic components of the Fagergren cell. To obviate this difficulty, a microflotation cell was designed, and an experimental technique was devised. These have been described elsewhere. Experiments conducted with the small cell showed that leached quartz could not be floated at any pH with any sulfonate addition,3 which is in agreement with the observations of Kraeber and Boppel.4 Similarly, it was also found that leached beryl responded to sulfonate flotation only over a narrow pH range rather than the broad range reported earlier.1 This early work,1 however, revealed the important effect that wet-grinding in a steel mill has on the flotation response of certain silicates. That is, it was found that quartz and especially beryl floated well over an unusually wide pH range after wet-grinding in a steel mill. Microcline, however, floated poorly below pH 4, even though wet-ground under the same conditions. The work of Eigeles6 on adsorption of oleic acid on leached quartz and iron-contaminated quartz at constant pH is in agreement with these flotation data. Other research has shown that ferric iron, added as a salt to the system, functions as an activator in the narrow pH range in which Fe +++ iron hydrolyzes to its hydroxy complexes.3,5 These phenomena indicate that iron functions differently in flotation systems depending on its method of introduction. The object of this paper is to determine the mechanism by which iron is adsorbed on certain minerals, the mechanism of collector adsorption after iron abstraction, and the role that Fe++ and Fe+++ assume in the selective separation of these minerals. EXPERIMENTAL MATERIALS AND METHODS Sodium alkyl aryl sulfonate, mol wt 450,7 pure potassium oleate, and pure dodecylamine were used as collectors. All other chemicals were reagent grade in quality, i.e., n-amyl alcohol as frother; HC1, H2SO4, and KOH for pH adjustment; and ferric chloride as activator. Conductivity water, made by passing distilled water through an ion exchange column, was used in the experimental work. All minerals used in the investigation were hand-picked specimens. Sample Preparation: Each of the minerals was crushed through 8 mesh, and the product was divided into two groups, one to be ground dry and the other wet. Dry grinding was accomplished with an alumina mortar and pestle. The product was dry-screened to 48 x 150 mesh, cleaned magnetically, deslimed in conductivity water, and dried. Preparation of the samples by wet-grinding involved grinding a 200-g charge of the mineral (-8 mesh) at 60% solids with natural water in a mild steel rod mill for four minutes. This charge was then wet-screened immediately with natural water to 48 x 150 mesh, dried, and cleaned magnetically. Some experiments were also conducted with leached beryl and quartz. These products were prepared by leaching the sized sample (48 x 150 mesh) with concentrated HC1 with a percolation technique until no iron could be detected in the leach liquor. Following this step, the sample was rinsed with conductivity

Jan 1, 1967

By L. D. Jaffe, F. W. Cotter, E. Cordon

The hardenability of titanium-base alloys was studied by metallographic examination and hardness survey of Jominy specimens end-quenched from the B range. Analyses of the data led to the equation log J = -0.57 + 0.25 @ct Fe + pct Mn + pct Mo) + 0.19 @ct Cr) +0.16 @ct V) + 0.03 @ct Zr). Here J is the distance, in sixteenths of an inch, from the quenched end of a Jominy hardenability specimen in the position of peak hardness, for material quenched from the B range. This equation fitted the experimental data with a standard deviation of approximately 0.29. The effects of the elements Al, Sn, W, Cu, Ni, B, C, N, 0, and H, and of pain size, were not statistically significant or not practically significant. A check against hardenability measurements in the literature showed agreement within the stated standard deviation. The equation should be useful in estimating hardenability of new or modified titanium alloys. HARDENABILITY in a titanium-base alloy is the ability of the alloy to retain the B structure on quenching. An alloy with high hardenability will retain the /3 structure even when cooled relatively slowly from a temperature at which B or P plus a is stable. A low hardenability material will retain P only if quenched extremely rapidly from the range of p or 0-plus-a stability, or will not retain it at all, at room temperature. High hardenability is desirable in titanium alloys to be heat-treated to high-strength levels. Its value is by no means limited to large section sizes. With high hardenability, a material can be solution-treated and cooled at a variety of rates, either to give high strength directly or, more generally, to give a soft ductile condition from which high strength can be obtained by subsequent aging. With low hardenability, high strength can be obtained, if at all, only by very rapid quenching, and there will generally be little increase in hardness on subsequent aging; an alloy of this type is limited in its applicability. On the other hand, alloys of very low hardenability have some advantages in weldability; essentially, they are always in the annealed condition, after welding as well as before. For commercial alloys, hardenability data are usually available, in the form either of property data after cooling from the solution temperature at various rates, with or without subsequent aging, or of results of a standard hardenability test, such as that originally developed for steels by Jominy and Boegehold.' When modifications of an available alloy are considered, or preparation of new alloy compositions, it would be Very convenient to be able to estimate the hardenability of the new material without having to make and test it. A method of estimating hardenability of titanium alloys from their composition was suggested by one of the authors some time ago, on a preliminary basis, utilizing scattered data found in the literature.' It seemed worthwhile to carry out a systematic experimental study of the effect of composition upon hardenability. EXPERIMENTAL PROCEDURE Approximately fifty heats of various compositions, weighing 8 to 10 Ib apiece, were melted in a small inert-gas tungsten-arc furnace with water-cooled copper walls. The starting material was 110 Brine11 titanium sponge, with high-purity metals added for alloying. Each heat was bottom-poured under vacuum through a molybdenum burnout strip into a cold graphite mold, to form an ingot approximately 4-1/2 by 3-1/2 by 3 in.* From each ingot were cut *The material was melted and cast by Pitman-Dunn Laboratory, Frankford Arsenal, to whom the authors must express their thanks. two pieces 4-1/2 by 1-1/2 by 1-1/2 in. These were forged, at temperatures adjusted to the composition, into 1-1/4-in. rounds, from which standard 1-in.-diam hardenability specimens3 were machined. A number of small samples were also prepared from forged materials of each heat, annealed, quenched from various temperatures, and examined metallographically. The P-transus temperature was determined by observation of the degree of resolution of primary a in these pieces. samples for chemical analyses were also taken from the forgings. One hardenability specimen of each heat was solution-treated for 1 hr approximately 50°F above the measured transus temperature, and the other for 1 hr approximately 250°F above the transus. (An additional hour was allowed for the specimens to reach furnace temperature.) These are not necessarily the temperatures that would be selected for

Jan 1, 1964

By J. D. Defilippi, E. M. Gilbert, K. G. Brickner

FCC chromium-manganese-nitrogen (Cr-Mn-N) steels differ from most other fcc materials in that these steels undergo a ductile-to-brittle transition. Transformation to martensite is considered to be responsible for this behavior in some metastable Cr-Mn-N steels. However, very stable Cr-Mn-N steels also exhibit a ductile-to-brittle transition. The results of this study indicate that deformation faulting is the probable cause of the brittle behavior of stable Cr-Mn-N steels. Deformation faulting accounts for the ductile behavior of these steels in a tension test at -320°F and brittle behavior in an impact test at -320°F. Deformation faulting also accounts for the toPological features observed on the fracture surfaces of impact specimens of these steels. FACE- centered- cubic chromium-manganese-nitrogen (Cr-Mn-N) steels differ from most other fcc materials in that these steels undergo a ductile-to-brittle transition. Many Cr-Mn-N steels transform to martensite during deformation,l-5 and several investigatorsl-3 have suggested that the brittle behavior of these steels is caused by martensite formation. However, very stable Cr-Mn-N steels also exhibit brittle behavior. Schaller and Zackeyl reported that a very stable Cr-Mn-N steel (less than 3 pct martensite formed at -320°F) exhibited a transition temperature higher than that for steels in which large volume fractions of martensite formed during testing. The explanation given by Schaller and Zackey for this observation was that in the very stable steel the martensite, because of its higher interstitial content, was more brittle than that formed in their other steels. This explanation was questioned by Tisinai and samans4 and Baldwin.6 Moreover, because the toughness of stainless martensite at cryogenic temperatures is generally very low, this explanation does not account for Thompson's7 observation that small additions of nickel (1 to 3 pct) greatly improve the toughness of high nitrogen (0.35 pct) Cr-Mn-N steels. The present paper summarizes the results of an investigation of the low-temperature brittleness in very stable Cr-Mn-N steels. The importance of the mode of deformation on the toughness of these steels is discussed. Table I. Compositions of the Steels Invertigated, Pet Steel C Mn P S Si Ni Cr N - A 0.09 14.70 0.018 0.011 0.47 0.22 18.40 0.54 B 0.12 14.90 0.001 0.008 0.48 0.14 17.80 0.38 C 0.12 14.95 0.004 0.005 0.62 3.95 18.43 0.38 MATERIALS AND EXPERIMENTAL WORK The compositions of the steels investigated are shown in Table I. Steels A and B had compositions within the limits of a proprietary Cr-Mn-N stainless steel,* whereas Steel C was similar in composition to the proprietary steel except for its 3.95 pct Ni content. All steels were hot-rolled to 1/2-in. thick plate. The plates were subsequently annealed for 1 hr at 2000°F and water-quenched. Standard longitudinal and transverse Charpy V-notch impact specimens were machined from the annealed plates. Duplicate longitudinal and transverse impact specimens were tested at 212", 80°, 32", 0°, -100°,-160°,-200°,-256", and -320°F. Longitudinal tension-test specimens were also machined from the plates and tested at a crosshead speed of 0.05 in. per min at the aforementioned temperatures. The fractured impact and tension-test specimens of all three steels were examined to determine whether martensite had formed during testing. Magnetic, X-ray, electron-diffraction, and electron-microscopy techniques were used to detect the presence of martensite in the highly deformed areas of these specimens. Metallographic examination of highly deformed areas of impact and tension-test specimens revealed the presence of dark-etching bands, such as those shown in Fig. 1. These bands were observed only in deformed samples and were thought to be associated with the low-temperature brittleness of the Cr-Mn-N steels. Accordingly, a sample 1 in. wide by 3 in. long was cut from the 1/2-in.-thick plate of Steel C. This sample was surface-ground to a in. and then cold-rolled 60 pct at -320°F. Thin foils were prepared from the cold-rolled sample and examined in a JEM electron microscope. Brightfield, dark-field, and selected-area diffraction techniques were used to determine the cause of the dark-etching bands. Fractographic experiments were also performed. Impact specimens Of Steels A, B, and C were broken at -320oF, and the fracture surfaces of these specimens were immediately shadowed with carbon. The carbon replicas were examined in a Siemens electron microscope, and attempts were made to correlate the topological features of the fracture surfaces with the deformation mechanisms that could be occurring during an impact test of these steels.

Jan 1, 1970

By R. D. Nelson, J. C. Shyne

The ß and a ß transformations in plutonium were studied with particular emphasis on the transformation kinetics and microstructure. Significant observations are: 1) The kinetic data show conclusively that the ß — a transformation in high-purity plutonium can proceed isothermally with no athermal component. 2) Plastic deformation of the stable (3 phase retards the subsequent (3 — a transformation. 3) Plastic deformation of the stable a phase accelerates the a — ß transformation; the acceleration is attributed only to residual stresses. 4) The a and a?a volume changes occur anisotroPically in textured plutonium. 5) An apparent crystallogvaphic relationship exists between the parent and the product phases of the and (3 — a transformations. 6) Both applied uniaxial compressive stresses and uniaxial tensile stresses raise the starting temperature for the ß — a transformation. 7) A given uniaxial tensile stress favors the a — ß transformation more than an equivalent applied uniaxial compressive stress opposes the transformation. These observations of the (ß —a and a — ß phase changes in plutonium are consistent with known mar-tensitic transformations. ThIS paper elucidates some of the characteristics of the a— ß and ß —a transformations in plutonium. Because considerable conjecture exists about the mechanisms by which the phase transformations occur in plutonium, experiments have been performed to provide indirect information concerning the mechanisms responsible for the a —ß and ß -a transformations. Indirect information is of particular value in the study of plutonium because of the experimental difficulties presented by the metal. Single crystals have not been produced in any of the allotropes. The large density results in high X-ray and electron-absorption factors and consequently complicating X-ray and electron diffraction. The kinetics of ß — a and a — ß transformations of plutonium and the behavior of the transformations under a variety of conditions have been investigated in detail. Information about the mechanisms of the allo-tropic transformations of plutonium was obtained indirectly from three sources: 1) the effect of plastic deformation of the stable parent phase upon the transformation kinetics; 2) the behavior of the metal transforming under applied stresses; and 3) the microstruc-tural and crystallographic features between parent and product phases. PHASE-TRANSFORMATION CHARACTERISTICS In characterizing solid-state phase transformations in metals and alloys, it is useful to define several types of transformations. An aim of the present work was to identify the low-temperature transformations in plutonium by type, i.e., as martensitic or nonmar-tensitic. Practical definitions for these terms follow. The terms commonly used to categorize phase transformations lack universally accepted definitions. This confusion arises doubtlessly because some terms specify crystallographic or morphological character while other words have a kinetic or a thermodynamic connotation. For example, martensitic specifies certain definite crystallographic restrictions. Unfortunately, martensitic is sometimes used in an ill-defined way to imply kinetic characteristics. Further confusion attends the use of such expressions as nucleation and growth, diffusional, and massive. From time to time new systems of phase-transformation nomenclature are suggested; unfortunately none of these has gained general acceptance.1,2 The authors of the present paper have no intention of entering the controversy. We recognize that some readers may object to the nomencliture used here. For exampie, the terms military and civilian have recently been used in much the same way as martensitic and non-martensitic are used in this paper. This paper is intended to describe several specific details of the low-temperature phase transformations in plutonium. The authors have found it useful to identify these transformations as martensitic; the term was chosen as the best available to describe the experimentally observed features of the transformations studied. A martensitic transformation is one that occurs by the cooperative movement of many atoms; the rearrangement of atoms from parent to product crystal structure occurs by the passage of a mobile semico-herent growth interface. The geometric features characteristic of a martensitic transformation are a specific orientation relationship between the product and parent phase lattices, a specific habit-plane orientation for the growth interface, and a shape change with a specifically oriented shear component. There is no alloy partition between the parent and product phases in a martensitic transformation. Martensitic transformations may display either athermal kinetic behavior or thermally activated isothermal kinetic behavior. Some martensitic transformations occur isothermally, although more commonly martensitic transformations are athermal. Isothermal martensitic transformations are suppressible by rapid cooling. In athermal martensitic transformations, nucleation and growth are not thermally activated and the transformations are essentially time-independent. Nucleation, growth, or both can be thermally activated in isothermal martensitic reactions. Transformation of the parent phase into a marten-

Jan 1, 1967

By J. H. Waxweiler, L. C. Ikenberry, R. J. Bendure

Carbon which is present as insoluble carbides in austenitic stainless steels can be measured quantitatively by dissolving the steel in iodine-methanol and analyzing the residue for carbon. Severe sen-sitization was observed in Type 302 due to precipitation of only 0.003 pet carbon. Both cold work and the presence of delta ferrite caused a marked acceleration in rate of carbide precipitation. Carbide precipitation rates in 17-7 PH were stzulied for the austenite conditioning and also the aging heat treatment. CARBON and its compounds exercise a major influence on the properties of stainless steels and their response to thermal treatment. Sensitization in 18-8 type stainless steels has been the subject of numerous investigations throughout the years. Bain, Aborn, and utherford," and Binder, Brown, Frankss all studied the effects of heating austenitic stainless steels in the temperature range of 1000° to 1500°F. The primary purpose of most of these studies was the investigation of susceptibility to in-tergranular attack in acids due to these sensitizing heat treatments. Intergranular precipitation of carbides was always associated with intergranular attack but it was recognized2 that severe attack could occur with but minute quantities of precipitated carbide. Mahla and ielsen utilized the electron microscope to make a significant contribution in illustrating the appearance and method of growth of chromium carbides during sensitizing heat treatments. However, as they stated, their studies of residues could not be used to obtain a quantitative measurement of the amount of carbon which was actually precipitated. The aim of the present investigation was to devise a relatively fast, simple method for the quantitative measurement of carbides in stainless steel. EXPERIMENTAL WORK The initial investigations were made to determine the best means of separating carbides from the matrix. A number of dissolving media were tried using both chemical and electrolytic attack. Qualitative examination of the extracted residues by X-ray diffraction indicated that solution in iodine-methanol would furnish a good means of separation. Consequently, further work was pursued along this line. The method is quite simple. The sample in the form of millings or nibblings is dissolved in iodine-methanol solution at room temperature (6-g iodine, 25-ml methanol per g of sample). The insoluble residue containing the carbides is separated by suction filtration through an ultra-fine glass filter disc. This is a very fine filter medium that will retain particles as small as 0.1 to 0.2 p in diameter. After washing with methanol and drying, the filter disc and residue are placed in a conventional combustion carbon-tube furnace and the carbon determined gravimetrically. Using this technique it was found that reproducible insoluble carbon values were obtained. However, since such small amounts of insoluble carbon were obtained on Type 302 after sensitizatipn at 1250°F and 1500°F, the values were confirmed by a second method. In the second method the sample was dissolved with copper potassium chloride and filtered through a millipore paper. This treatment dissolves the matrix but leaves undissolved practically all of the carbon irrespective of how it is present in the steel. The amount of insoluble carbon present as chromium carbide is determined by calculation from the analysis of the residue for chromium and iron. The derivation of the formula used for this calculation is discussed later. The values obtained by the indirect copper-potassium-chloride method were in agreement with those obtained by the iodine-methano1 method. See Table I. It should be pointed out that the sensitivity of the direct combustion method is not too high when the amount of carbide present is small. This is due primarily to inherent blanks and to analytical errors such as weighing. For this reason it cannot be stated with any degree of certainty that there is a significant difference between values of 0.002 and 0.005 pct. Having confirmed that the iodine-methanol extraction gave a quantitative measurement of the precipitated carbides in Type 302, exploratory tests were conducted on Armco 17-7 PH stainless steel. Samples from commercial Heat 54807 were solution annealed at 2000°F, water quenched and heated at 1250" and 1500°F, and water quenched. The analysis of Heat 54808 is as follows:

Jan 1, 1962

By John E. Hockett

The need for basic information about the relationship between resistance to dejormatim (flow stress), temperature, strain, and strain rate, for the solution of metal-fovming problems, is pointed out. Some early attempts to satisfy the need are mentioned. A brief description of a machine called a Cam Plastome-ter is given, including the processing of results of testing in the machine. Next, a program of testing aluminum in compression over a wide range of constant true-strain rates (0.1 to > 200 sec-1) and a modevately broad range of temperatures (223° to 673°K) is described. The results of this program are presented in the form of true-stress us true-strain cuvves. The data in these curves are presented in the form of relationships between true stress and true-strain rate in sermilogarithmic and log-log form, as functions of temperatures—for several true strains. Finally, true stress, for a given true strain, is displayed as a function of log true-strain rate and absolute temperature, i.e., a surface. SINCE the publication of Hill's book1 on plasticity theory, increasingly rapid advances have been made in analytical solutions to forming problems. Methods in common use are the slab method, the uniform deformation energy method, the limit analysis method, the slipline field method, and the semiexperimental method called "visioplasticity". These approaches, and examples of their use, are covered in detail by Johnson and Melloor2 and by Thornsen, Yang, and Kobayashi.3 unfortunately, practically all of the above work has had to rely upon a number of basic assumptions, e.g., homogeneous deformation and Coulomb (sliding) friction; and virtually no dependence of the mechanical behavior of the deforming metal, upon temperature, strain, and strain rate, has been included. It is with this dependency that this paper is concerned. Loizou and sims4 looked at the above relationship for lead using both a constant compression-speed Cam Plastometer and a constant true-strain-rate Cam Plastometer designed by Orowan.5 Alder and Phillips8 investigated the relationships for aluminum, copper, and steel in the same constant true-strain-rate Plastometer. cook7 tested twelve steels at temperatures ranging from 1170° to 1473°K in the same Plastometer over a range of true-strain rates of 1.5 to 100 sec-'. The writer tested commercially pure aluminum at room temperature and depleted uranium at temperatures from 573" to 873°K at strain rates from 10-3 to 1.0 sec-1 in a Cam Plastometer designed and built at Los Alamos Scientific Laboratory.8 During the past few years the Cam Plastometer at Los Alamos has been used for a number of relatively minor experiments on brass, mild steel, duralumin, Armco iron, and depleted uranium. In this time the machine has been continually modified and improved. It was decided to utilize fully the wide range of strain rates now available with the machine by testing a material about which some information was already in the literature. Prior work on commercially pure aluminum6 appeared to deserve confirmation and expansion. So it was decided to explore the resistance to compression of this material over the currently available range of constant true-strain rates and a convenient range of temperatures. This paper is a report of that exploration. I) EQUIPMENT AND PROCEDURE The principal item of equipment is, of course, the Cam Plastometer, the working part of which is shown in Fig. 1. In this figure, an aluminum specimen may be seen between two tungsten carbide platens, in position for a room-temperature test. Above the upper carbide platen is a load cell. Output from the load cell is amplified and applied to a galvanometer in a recording oscillograph. Auxiliary equipment includes the oscillograph, the control console, a counter, and a time-mark generator. The counter is first used in adjusting the time base. Then it registers the count, of sixty pips per revolution generated by the rotating cam, in each second. These pips and the time base are also applied to galvanometers in the oscillograph. Thus, load, time, and cam position are recorded simultaneously. Heating of a specimen prior to compression is done

Jan 1, 1968

By J. Szekely, G. P. Martins

A formulation is given for describing the rate of expansion of spherical bubbles rising in liquids the freeboard of which is evacuated. The computer solution of the resultant differential equations has shown that, for low freeboard pressures (less than about 5 mm Hg), on approaching the free surface the bubbles expand much less rapidly than predictable from equilibrium considerations. In other words, in this region the pressure inside the bubbles will be significantly larger than the static pressure in the liquid corresponding to the position of the bubble. These theoretical predictions were confirmed by experimental work, using two-dimensional air bubbles rising in mercury. The important consequence of these findings is that the expansion of gas bubbles in vacuum degassing operations will be a great deal less than expected from hydrostatic considerations. This would lead to a significant reduction in the available interfacial area and may explain the apparent poor efficiency of many vacuum degassing units. VACUUM degassing as a treatment for liquid steel has gained widespread popularity in recent years; the number of known installations exceeds several hundred at the present time.' Although much information is available on both the thermodynamics of the system and the overall performance of various industrial units, much less is known about the fundamental aspects of the process kinetics.2-4 The basic physical situation common to virtually all vacuum degassing operations is the interaction between gas bubbles (swarms of bubbles) and the surrounding molten metal, held in a container, the freeborad of which is at a low absolute pressure. Once formed (or introduced from an external source) the bubbles will ascend, due to the buoyancy forces, and, during this ascent, a significant increase in their volume will occur. This progressive increase in the bubble volume is due to two factors: a) the continuous reduction in the static pressure acting on the bubble during its rise; and b) mass transfer into the bubble from the surrounding molten steel. In a recent paper Richardson and Bradshaw developed equations5 for describing mass transfer into gas bubbles from molten metals at reduced pressures. However, in deriving these expressions it was assumed that the pressure inside the bubble was identical to the static pressure in the adjacent liquid. In other words, the volume of the bubble was considered to be in equilibrium with the pressure of the fluid adjacent to it. This assumption, thus their analysis presented, was thought to be reasonably accurate for most of the bubble's ascent; however, it was unlikely to be valid in the immediate vicinity of the free surface, held at a low pressure. It was pointed out in the discussion6 that the region close to the surface may be of considerable importance as both the driving force and the interfacial area available for mass transfer are at their highest value here. The ' 'anomalous" behavior of gas bubbles when approaching a free surface at low pressures was recently confirmed in a preliminary investigation by Szekely and Martins. ?1 Here high-speed motion photography was used to study air bubbles rising in a column of n-tetradecane with a freeboard pressure of 0.1 mm Hg. It was found that significant distortion of the bubbles occurred on approaching the free surface; furthermore, the expansion observed was much less than what one could expect from hydrostatic considerations, i.e., factor a previously discussed. It follows from the foregoing that a detailed study of these phenomena would be justified both from fundamental considerations and because of their potential relevance to technology. The purpose of the paper is to present a more realistic formulation for the expansion of a gas bubble approaching a low-pressure region, together with a comparison of the theoretical prediction with experimental measurement. An inert bubble will be considered in the first instance; it is thought that the understanding of the fluid mechanics is an essential first step toward the realistic formulation of the mass transfer process. This latter problem will be the subject of a subsequent publication. FORMULATION The Physical Model. Consider a spherical bubble, of initial radius Ro, rising in a fluid, having a density pL. Initially let the bubble be at a distance H from the free surface, and at a pressure Pgo, as illustrated in Fig. 1. Pgo, the initial pressure in the bubble, is given by the following equation: pgo = Po = Ptp +pLgH [ la] where Po is the pressure in the liquid corresponding to the initial position of the bubble and Ptp is the pressure at the free surface. The fluid pressure at

Jan 1, 1970

By A. Ghosh, T. B. King

The kinetics of the discharge reaction: 20'- (in silicate melt) = O,(g) + 4e- at a platinum anode in lithium silicate melts have been studied al 1350°C by galvanostatic methods. Plots of the sleady-state overpotential, q, as a function of the logarithm of the current density, i, showed injlections and were linear only at high current densities. The value of the overpotential was influenced by bubbling gas through the electrolyte. The ocer potential was also studied as a function of time. The rise and decay of overpotential were very slow processes. At low current densities transport is the likely rate-controlling process but at high current densities passivation of the electrode, Presumably by an oxide film on the surface, seems to be a contributory functor. IT is well-established that molten silicates behave as electrolytes'5 and, except in a few cases,6 conduction is entirely ionic. Moreover, it is supposed that a possible, and perhaps predominant, mechanism for phase boundary reactions between metals and slags is similar to that in corrosion whereby anodic and cathodic processes occur at unrelated sites, the metal serving to conduct electrons.1'8 Thus electrochemical studies of some slag-metal reactions would seem to be a useful way to diagnose the rate-controlling steps in the overall reaction. The electrochemical method is, in principle, a better diagnostic tool than the direct chemical method for the following reasons: 1) The partial electrochemical reactions, which are simpler than the overall reaction, may be studied individually. 2) The rate of reaction can be controlled at will and independently of the concentrations of reactants. 3) Fast reactions can be studied by relaxation methods.' Esin and his coworkers5'10"12 have pioneered such studies in silicates and have deviloped some ingenious techniques. Not all of their findings, however. can be accepted without a good deal of further work. In this investigation, the kinetics of the oxygen discharge reaction: 202- (in silicate melt) = Oz(g) + 4e- [I] at a platinum electrode were studied by both steady-state and transient galvanostatic techniques. Interest in this reaction was first developed as a result of the findings of Fulton and chipman13 that the reduction of silica, in a silicate slag, by carbon, dissolved in liquid iron, is a very slow reaction. Subsequent work, for example, by Rawling and ~lliott,'~ has demonstrated that the reaction under these conditions must be slow, because the rate is limited by diffusion of oxygen in the iron to the metal-crucible phase boundary at which a CO bubble may be nucleated. Further work by Tarassof,'~ in which the reduction of silica by aluminum dissolved in copper was studied, has shown that under these conditions, where carbon monoxide evolution is not involved, control of the reaction rate resides in diffusion of silica in the slag phase. However, there is no practical way of inducing sufficient convection in the system to make it clear that the phase boundary reaction is indeed fast. The overall reaction of silica reduction involves the discharge of silicon ions at cathodic sites and oxygen ions at anodic sites. In the examples cited, the discharged ions are dissolved in a liquid metal. In the present study of oxygen ion discharge, gaseous oxygen may be evolved at high current densities or oxygen may simply dissolve, possibly as oxygen molecules, in the silicate at very low current densities. The discharge of an oxygen ion at an anode must, in silicates less basic than the orthosilicate composition, be preceded by a reaction in the vicinity of the electrode, such as: which makes oxygen ions available. Platinum was chosen as the working electrode since it is comparatively inert to oxygen and is, therefore, expected to come rapidly into equilibrium with the electrolyte and with gaseous oxygen. Minenko, Petrov, and Ivanova16 have measured the electromotive force at a platinum electrode in molten silicates as a function of the partial pressure of oxygen in the atmosphere, the concentration of oxide ions in the melt, and the temperature. They found platinum to behave as a reversible oxygen electrode. At two different oxygen pressures, Po2 (I) and Pq (11). the electromotive force is given by: where F is the Faraday constant, equal to 23,060 cal per v equivalent, indicating that the electrode reaction is as written in Eq. [I.]. Platinum has been similarly used in molten silicates by other inve~ti~ators. "'~~ In this investigation platinum was used only as an anode, since a current deposits other elements on its surface and changes its characteristics.

Jan 1, 1970

By W. A. Young

Polynomial functions of temperature were obtained for the specific heats, thermal diffusivities, and thermal conductivities of zirconium hydrides containing 4 at. pct U. Three hydrides (H/Zr atom ratios of 1.58, 1.65, and 1.70) were studied over the range a" to 900°C and a fourth (H/Zr = 1.81) was studied over the range 0° to 760°C. The specific heats were determined from enthalpy measurements which were obtained using a unique drop calorimeter specifically designed for use with materials in which high temperature phase transitions and/or high dissociation pressures occur. Thermal diffusivities were measured by the flash method using a pulsed laser. The thermal conductiuities were obtained as the product of specific heat, thermal diffusivity, and density. The specific heats agree, within 10 pct, with values derived using a theoretical model in which the hydrogen and zirconium atoms are treated as Einstein and Debye oscillators, respectively. RELIABLE values of the thermophysical properties of the fuel are required to predict the operating temperatures and temperature response of SNAP nuclear reactors. Among the most important of these properties are the thermal conductivity, specific heat, and thermal diffusivity. A considerable number of investigations1-4 have been made of these properties for the Zr-H and Zr-H-U systems.* However, little of the drides, however, this direct method cannot yield meaningful results, since the hydrogen will redistribute under the influence of the thermal gradient, thus forming a concentration gradient; hence, one has a spectrum of compositions, rather than a homogenous alloy. Although the "average" composition of the material may be identical to the initial uniform concentration, the directly measured value of conductivity will be dependent on the thickness of the specimen, due to the highly sensitive dependence of transport properties on hydrogen content. This dependence is strikingly illustrated by the work of Bickel,5 who found that the electrical conduction of zirconium hydrides ranges from primarily hole conduction to primarily electronic conduction, depending upon the hydrogen content. Fortunately, the direct measurement of thermal conductivity is unnecessary, since it can be expressed as the product of the specific heat, thermal diffusivity, and density, all of which can be directly measured with considerable accuracy. EXPERIMENTAL Specimen Preparation. The combined fuel-moderator material used in SNAP reactors is a hydrided zirconium-uranium alloy containing -10 wt pct U. The alloy used in this work was representative of that used in nuclear reactors except that normal uranium was substituted for the enriched uranium required for reactor usage. It was produced by a triple-arc-melt and double-extrusion process. All specimens were prepared from a single cylindrical extrusion which contained 10.30 pet U, 89,35 pct Zr, and 0.35 pct impurities, The specimens for each composition were hydrided simultaneously with ultrapure hydrogen (10 ppm total impurities) using standard fuel production techniques which routinely yield homogeneous, crack-free fuel with negligible increases in the impurity levels. The hydrogen content of each specimen was determined from its weight gain and the density was measured by liquid displacement, Chemical analyses yielded hydrogen concentrations which agreed with the weight gain data within ±0.02 in H/Zr atom ratio) the concentrations of all other elements agreed almost exactly with the initial values after adjustment for the added hydrogen. The specimens used for the determination of specific heat were centerless ground to 2.00 cm diam after hydriding. A thin slice was carefully removed From each end for metallographic examination. In every case, this examination revealed a uniform structure as evidenced by the appearance and distribution of the two phases present in the fuel at the hydrogen concentrations used. TWO specimens (H/Zr = 1.600 and 1.632) appeared to be entirely 6 phase with equi-axed grains; the specimen with H/Zr = 1.756 showed

Jan 1, 1970

By H. Groeneveld, C. A. Connally, P. J. Hoenmans, J. J. Justen, W. L. Mason

A miscible displacement pilot using a slug of LPG driven by separator gas was conducted in the Cardiurn reservoir of the Pembina field. The injection pattern was a 10-acre, inverted, isolated five-spot. Upon completion of the LPG-gar phase, an experiment was conducted using a slug of water followed by gas. Calculated performance of the pilot is compared with actual performance. Equations are developed to calculate the distribution of LPG into zones of varying permeability, to estimate the progress of the flood at different times in the various zones and to estimate gas rates after breakthrough. The analysis indicates that permeability stratification was a dominant factor in controlling oil recovery and that oil was completely displaced from the swept pore volume. The results of the pilot indicated that miscible flooding is a practical means of pressure maintenance in this reservoir. The total recovery from the pilot area was good in spite of the early breakthrough of LPG. The effects of stratification were reduced by injecting a slug of water into the partially swept reservoir. INTRODUCTION The Pembina field,' located in Alberta, is the largest oil field in Canada and one of the largest in the North American continent. The reservoir is a stratigraphic trap producing from the Cardium sand. Neither bottom water nor free gas has been found. The recovery of oil by the natural depletion mechanism has been estimated at 12.5 per cent. Pressure maintenance studies of various areas have indicated that the recovery can be increased 21/2 times by water flooding, and a large area of the field is presently under water flood. However, reservoir studies of the North Pembina area indicated that miscible flooding might be competitive with water flooding. A pilot test was conducted to evaluate the performance of a miscible flood. A 10-acre, inverted, isolated, five-spot pattern was selected for the pilot. The pattern area was large enough to minimize wellbore fracturing effects and contained sufficient oil to provide significant working numbers. The performance of each of the four producers could be evaluated individually and compared. In the event of breakthrough in one direction, the effect would be isolated from the other producers. The use of a single injector minimized the volume of LPG required, and, because of the high mobility of gas, one well was sufficient to inject the necessary daily volume to replace the high rate of production. With four producers, the test could be completed in time for results to be evaluated, additional engineering studies to be made and a unit to be formed before the reservoir pressure in the North Pembina area declined below the bubble point. The pilot was located in an area developed on staggered, 80-acre spacing. The injection well was drilled at a regular location, while the four producers were drilled 467-ft north, east, south and west of the injector. Each quadrant and its associated producer were identified according to their direction from the injector— that is, north, east, south or west. The eight surrounding producers on 80-acre spacing were shut in to isolate the pilot area and provide for reservoir pressure observation. The pilot wells were completed using permanent-type completion techniques. After coring, casing was run through the pay section and cemented. Inside 51/2-in. casing, 2 1/2-in. tubing was hung. The wells were perforated opposite the Upper Cardium sand and lightly fractured. Fracturing volumes, rates and pressures were low to minimize the extent of the fractures. The fracturing treatments average 1,000 lb of 20-40 mesh sand in 700 gal of a low fluid-loss sand-carrying agent. Feed rates and wellhead fracturing pressures averaged 5.5 bbl/min at 2,535 psig, respectively. After fracturing, the productivity index was measured in each of the five pilot wells. The average PI of the four producers was 0.41 BOPD/psig drawdown. The measured PI'S were approximately the same as PI'S calculated from core analysis data, indicating that the fracturing treatments were just sufficient to overcome

By Verne E. Hooker, Robert M. Becker

The evaluation of in-situ rock stresses from measurements of the change in diameter of a borehole that is stress-relieved by overcoring has become a common practice. Generally the stress evaluation has been based on isotropic relations whereas rock in varying degrees is aniso tropic. A plane elasticity solution fora circular hole along one axis of an orthotropic medium has been adapted to evaluation of in situ stress. The necessary elastic parameters for this evaluation may conveniently be obtained from static tests on the overcore in conjunction with a consistent orthotropic thick-wall cylinder solution. The method and equations for the laboratory and field evaluations are summarized and illustrated. The determination of in-situ rock stresses from boreholc deformation measurements has gained widespread acceptance. Hastl measured the change in diameter of a borehole that was stress-relieved by drilling a larger concentric core; this overcoring method has produced a major portion of the field data for recent stress evaluations in rock. These evaluations are based on the elastic properties of the rock, which are conveniently determined by testing the overcore.6-8 The stress evaluation and the overcore testing procedures generally assume isotropic relations whereas rock is anisotropic in varying degrees. Recently, an anisotropic plane stress solution was adapted for evaluation of in-situ stress9 and a related plane strain solution was developed for the testing of stress-relief core. 10 The present paper unifies the stress evaluation and overcore testing procedures for a general class of anisotropic rock. Equations are presented for calculating the state of stress in a plane normal to the borehole, and a consistent thick-wall cylinder solution is given for determining the necessary elastic properties. In addition, a complete example of stress evaluation from laboratory and field data is presented, and the order of error in computing the state of stress from isotropic relations is illustrated. Several limitations of the results should be emphasized. All results assume small linearly elastic deformations of a homogeneous medium. Rock characterized by orthotropic, transversely isotropic, and isotropic elasticity is considered; however, the anisotropic results assume a special relation among certain elastic constants in addition to geometric orientation with respect to a plane of elastic symmetry. For some stress determinations in rock, these may be severe limitations. On the other hand, the anisotropic evaluation procedure involves little additional effort and is much more flexible than the corresponding isotropic evaluation procedure. The collection of field data is identical. The laboratory determination of elastic parameters is no more difficult and time-consuming for the anisotropic than for the isotropic model. Only the calculations require some additional effort for the anisotropic evaluation, and this additional effort is eliminated by use of a small computer. The flexibility of the anisotropic procedure is greater because more than two independent elastic constants are available in fitting rock data. For the special relationship assumed among orthotropic constants, five independent elastic constants are available for the determination of in-situ secondary principal stresses as compared with two independent elastic constants for the isotropic model. Much of the material presented is either directly from the literature or adapted from the literature through superposition or the usual transformations. Consequently, only enough detail for clarity of presentation is included. RELATIONS FROM ANISOTROPIC ELASTICITY Materials that have three mutually orthogonal planes of elastic symmetry are called orthotropic. By directing the axes of the coordinates perpendicular to these planes, Hooke's law for an orthotropic solid 11 is

Jan 1, 1970

By Kun Li, Alex Simkovich

The rate of dissolution of alumina in carbon-saturated liquid iron has been studied experimentally in a system where alumina was in the form of a cylindrical rod immersed in an iron bath contained in a graphite crucible. Data obtained consisted of the concentrations of aluminum in the melt as a function of time. In the case of static experiments, the data are shown to agree with theoretical prdictions based on the diffusion of aluminum.. The rate of dissolution was greatly increased by the rotation of the alumina rod. It is concluded that the diffusion of aluminum from the alumina/metal interface is the rate-controlling step. In the past, thermodynamic investigations of systems encountered in ferrous process metallurgy have received widespread attention. More recently, considerable work has been devoted to the study of kinetics associated with these systems in an effort to determine their rate controlling mechanisms. The alumina-iron system is of great importance in ferrous metallurgy. Yet information concerning kinetics of reaction in this system is seriously limited. The present study was made in order to establish the rate-controlling step for dissolution of solid alumina in liquid iron. LITERATURE REVIEW A number of papers concerning dissolution of solid metals in liquid metals have been reported in the literat~re. Generally, for these simple systems, dissolution is controlled by mass transfer of the dissolving species. Complex systems involving dissolution of solid metal carbides and oxides in liquid metals and slags have been studied to a much lesser extent. Skolnick5,6 reported on the reaction between liquid cobalt and poly-crystalline cylinders of tungsten carbide, in which the cylinders were dissolved while being rotated about their longitudinal axes at various speeds and temperatures. As a result of unexpected preferential grain boundary attack by the liquid cobalt, large errors in the measured dissolution rates occurred because of loss of tungsten carbide grains to the liquid cobalt. Nevertheless, it was possible to establish that the liquid Co-W carbide reaction was not controlled by mass transfer. In a similar approach, cooper7 was able to show that artificial sapphire rods, (alumina single crystals) dissolving in lime-alumina-silica slags obeyed a mechanism of mass transfer control. Here, again, the rods were rotated at various speeds and temperatures, and the process was followed as a function of these variables. Forster and Knacke8 took a practical approach to reaction between slags and refractories. By blowing argon through refractory cylinders of silica, silli-manite, or dolomite and directing the gas to rise along the slag-refractory interface, it was possible to increase the rate of mass transfer. Although the method was admittedly crude, it nevertheless permitted an evaluation of the relative stabilities of refractories with respect to slag attack. Data were interpreted on the basis of mass transfer control. EXPERIMENTAL TECHNIQUE Apparatus. An illustration of the apparatus used in this study is shown in Fig. 1. The furnace consisted of a Morganite recrystallized alumina tube wound with a molybdenum coil. A secondary molybdenum heater was mounted around the upper half of the primary coil to aid in controlling the thermal gradient within the furnace. The primary heater tube was 3 in. in ID and 30 in. long. A reducing mixture of 95 pct N and 5 pct H was maintained around the heating elements. Thermal insulation was provided by alumina powder. The chamber within the primary combustion tube contained a boron nitride block near the top to assist in controlling the thermal gradient to the furnace and also to provide a bearing surface for the rotating graphite shaft. The outside diameter of the graphite shaft was $ in. A separate threaded graphite specimen holder was screwed into the end of the shaft. The holder contained a tapered hole drilled into the end to guide the oxide specimens as they were pressed into it for mounting. Additional guidance for the rotating graphite shaft was furnished by a water-cooled bronze bushing attached to the top of the furnace. A steel clamp was fastened to the upper end of the graphite shaft and rested on a thrust bearing; the shaft and clamp were driven by a dc motor through a set of gears. Two O-rings located immediately above the bronze bushing maintained a gas-tight seal about the graphite shaft. The lower half of the alumina tube housed the crucible and charge, which were placed on a 3/4-in. diam movable alumina support tube. With this arrangement, charges could be inserted into or removed from the furnace while the hot zone was maintained at or above 1000°C. To control the temperature of the furnace, the thermocouple was mounted inside the support tube and in contact with the crucible bottom. Stray electric fields in the furnace were of sufficient intensity to cause erratic indications by the thermocouple. By enclosing the thermocouple protection tube in a molybdenum sheath and grounding this shield, the problem was eliminated. Output of the thermocouple went to an automatic continuous balance controller. Procedure. A typical run was as follows. First, electrolytic iron was premelted in graphite crucibles and cast into graphite molds with the same configura-

Jan 1, 1970