By Mehdi Asadi, Heinz Palkowski

"In recent years, the increased demand for advanced high-strength steels (AHSS) mainly had been driven by the need of the automotive industry to reduce weight and to improve safety. Beside good ductility and high strength, those steels have a high bake hardening (BH) effect, giving additional contribution to the strength of structural parts, subjected to the paint baking process. In this paper we concentrate results gained for hot rolled dual phase (DP) steels.For the simulation of changing process conditions within the final hot rolling the specimens were hot deformed using different schedules of temperatures and reductions, selected according to the non-recrystallization temperature (TnRX). It was possible to refine the DP steel structure by control-ling the deformation temperature and the amount of strain below TnRX during the thermo-mechanical controlled processing (TMCP). This structure refinement resulted in an improvement of the strength and BH behaviour. A wide spectrum of mechanical properties could be obtained depending on the different hot deformation schedules. The best strength and BH levels were recorded for the deformation below TnRX at the highest amount of strain.IntroductionDP steels are characterized by a good formability, high strength and a good compromise between strength and ductility [1]. Moreover, the DP steels exhibit a continuous yielding behaviour, low yield point and a high strain-hardening coefficient [2]. Furthermore, the DP steels often show a large potential for bake hardening (BH). BH refers to the increase in yield strength as a result of the paint baking treatment of the shaped auto-body parts. The primary mechanism that causes the additional strengthening is the immobilization of dislocations by the segregation of interstitial atoms, known as classical static strain aging [3]. The increase of strength thus achieved allows a further reduction of sheet thickness and improves the crash safety and the dent resistance. The BH of special steel qualities is technically used in DP, where e.g. the increase in strength is realized in the final heat treatment [4]. Previous own investigations [5-6] stated that the BH effect of DP is much stronger than that one for conventional BH steels."

Jan 1, 2012

By David G. Dixon

Although the kinetics of leaching processes are of paramount importance in the design and analysis of nearly all hydrometallurgical flowsheets, these concepts remain poorly understood and, as a result, are only rarely applied to mass and heat balance models. In this second of two papers, we demonstrate how simple yet powerful models of leaching kinetics and other rate processes may be added to mass and heat balance models, and apply these concepts using a spreadsheet model of a simplified pyrite autoclaving flowsheet. In particular, we focus on the interpretation and scale-up of batch leaching data, and on simple means for modeling other phenomena commonly associated with leaching, such as reagent depletion, gas-liquid mixing, and the precipitation of oxides and basic salts.

Jan 1, 2002

By Joerg Hammerschmidt, Marcus Runkel, Andreas Wirtz, Kent Pope

"Fluidized bed reactor systems in the minerals industry have been progressively developed and widely implemented over a period of more than sixty years for a multitude of process applications. Their versatility is manifested in calcining, roasting and combustion treatment of minerals including solid fuels. Experiences from metallurgical processes have expanded to new applications in the oil shale processing, biomass combustion and renewable energy sector. This paper focuses on the most important aspects of fluidized bed technology for a variety of Outotec processes. Energy recovery is a major topic for all applications and will be addressed, as well as environmental aspects, particularly regarding the off-gas treatment. Outotec is one of the pioneers of roasting and the fluidized bed process including gas cleaning and sulphuric acid production where applicable. Process development is strongly supported by significant investment in R&D, thus enabling process adaptation and scale-up to meet specific customer/market requirements.Introduction to Fluidized Bed TechnologyThe early days of fluidized bed technology were characterized by the use of bubbling fluidized bed reactors (BFB). This technology was popular for roasting zinc and copper ores. The introduction of circulating fluidized bed technology led to increased plant capacities and improved process control for the traditional processes. Furthermore, the technology has been applied in many other industries, including the renewable energy industry, which will be part of this design and process comparison. The paper starts out with the fundamentals on particle fluidization as the main common design parameter, leading to the importance of heat recovery and offgas treatment.In fluidized reactor systems, the particle concentrations can reach several hundred kilograms per cubic meter of fluidization gas. This high solid concentration leads to large surface areas and enables direct contact of gas molecules with particle surface molecules. Excellent conditions for enhanced heat and mass transfer thus provide nearly ""ideal"" heat exchange conditions and better reaction kinetics. The bubbling bed exhibits a better heat transfer coefficient within the bed in comparison to the circulating fluidized bed (CFB). The different conditions of gas velocities and solid concentrations allowing the classification of fluidization reaction regimes are shown in the Reh diagram in Figure 1."

Jan 1, 2014

By D. W. Lawler

Prior to the manufacture of sulphuric acid in metallurgical plants, the SO2 rich gas from the smelter, roaster, or furnace must be cleaned to removed particulates, volatile contaminants, SO3, and water. Cleaning is accomplished by contacting the. gas with cooled weak acid. The system is designed so that all the contaminants, originally in the gas are captured in the weak acid, which then becomes an effluent from the plant. Historically, the entire weak acid effluent stream has been treated for disposal, with no attempt to recycle or recover any part if it. This is becoming increasingly environmentally unacceptable, and operators must consider better methods of treatment and recovery. In this paper, Kvaerner Chemetics discuss a number of options that allow the contaminants to 'be separated from the acid' value. This will result in an acid byproduct that can be sold or used elsewhere, and will minimize the volume of hazardous byproducts that must be discharged.

Jan 1, 1998

By Denise Nascimento, Alice Barreto Bevitori, Felipe Perissé Duarte Lopes, Renan Carreiro, Sergio Neves Monteiro, Isabela Leão Amaral da Silva

"Natural fibers obtained from plants have increasingly been used as reinforcement of polymeric composites in engineering applications. This is the case of the fiber extracted from the piassava palm tree, a native of the southeast region of South America, which for a long time has been used in simple items like brooms and brushes. Recently it was reported that the tensile strength of the piassava fiber varied inversely with the equivalent diameter. Following that previous work, the elastic modulus and the density dependence on the diameter of stiffer piassava fibers of the Attalea fiinifera species was investigated. Precise measurements with a profile projector and Weibull analysis of the experimental results indicated that both the elastic modulus and the density of piassava fibers also follow an inverse correlation with the diameter. Scanning electron microscopy observations of the microstructure and fracture surface showed that defects and participation of microfibrils are responsible for this correlation.IntroductionIn the past decades, both the increase in the price of the petroleum and climate changes due to greenhouse gas emissions are motivating the use of renewable and low cost natural materials as a substitute for energy intensive and CO2 contributor synthetic materials [1]. A typical case is that of natural cellulose-based fibers extracted from cultivated plants in comparison to glass fibers, which are extensively used for composite reinforcement. In fact, these natural lignocellulosic fibers are increasingly being investigated [2-6] as possible reinforcements of polymeric composites, and in some cases, successfully replacing glass fiber composites in engineering applications [7]. The automobile industry has remarkable examples of lignocellulosic fiber composite substitutions [8-10]. Not only do some of these fibers display specific mechanical properties comparable to glass fibers but their composites also contribute to lower equipment wear and better finishing of molded components [6]."

Jan 1, 2012

By Jose Hector Figueroa P.

Mexicana de Cananea, S.A de C.V. is a major copper producer mining a large deposit of the disseminated porphyry type considered one of the largest copper resources of the world with 2.7 billion tons of 0.60% copper for the mill plus 4.1 billion tons of averaging 0.26% copper for leaching. Mining of low grade sulfide leach ore, has been an important part of the overall production of the open pit mine which started in 1944. Before this time all the mining in Cananea was by underground methods. The leaching process in Cananea began on the 1920's with in situ operations in the underground mine and small dumps up to the 1950's. Large scale leaching operations began in 1960 and the copper solutions produced were treated in precipitation plants until 1,980 when the first SX/EW Plant was put in operation in Cananea. Leaching action is essentially ferric-bacterial, with no fiesh acid added to the leaching solutions. Traditionally, 5540% copper extraction is recovered fiom ROM, 70- 120 meter high leach dumps in 80 months of leaching. Cananea has successfully improved copper recoveries by implementing several actions that include: 1. Stripping of old dumps. 2. Leaching of old dumps through slotted casing. 3. Crushing conveying leach ore to minus 8 inch and stacking it in 30 meter lifts. As result of these actions, copper recovery has been increased' to about 70% of total copper with actions 1 and 2 and up to 85% in half the time by crushing-conveying the leach ore, based on the same solubility index of the run-of-mine ore. This paper describes the above actions that were implemented to enhance the leaching recoveries from. sulfide leach dumps and the economics of such actions.

Jan 1, 1999

By S. N. Sinha

The distribution coefficients of lead and silver between copper and matte phases have been measured at two different temperatures. Experiments covered the ranges of 0.009-1.8, 0.07-0.13, and 0-11 wt pct lead, silver, and iron in matte, respectively. The distribution coefficients of lead have been measured at 1405 and 1505 K and correlated with lead and iron concentrations in metallic copper and matte. The values of the distribution coef¬ficient of lead between copper and iron-free matte, at infinite dilution of lead, have been determined to be 3.60 and 4,06 at 1505 and 1405 K, respectively. The distribution coefficient of silver between copper and iron-free matte is independent of silver concentrations and has been measured to be 2.13 and 2.21 at 1400 and 1500 K, respectively. For an iron-bearing matte, the distribution coefficient of silver has been correlated with iron concentration in the matte at both 1400 and 1500 K. From the measured values of distribution coefficients, the Raoultian activity coefficients of PbS and AgS0.5 in copper-saturated matte have been calculated. At infinite dilution, the following equations correlating the Raoultian activity coeffici¬ents of PbS and AgS0.5 with matte- composition and temperature have been obtained: log Y° PbS =1.515 + 1080/T 0.14 NFes lbS Fog YAgS = -0.074 - 425/T + 0.09 NFes. - 0.5

Jan 1, 1983

By Xuewei Lv, Guibao Qiu, Jiaqing Yin, Chenguang Bai

"The iron ore sinter is one of the main raw materials for the blast furnace (BF) process. In the production of iron ore sinter, the cooling speed of the sinter determines its quality. In addition, the heat recovery devices are installed in the cooling machine for energy saving. The cooling parameters like gas flow rate and the size of sinter should be optimized for getting the gas with a higher temperature and a good quality of sinter simultaneously. In this study, the commercial simulation software COMSOL was used to establish a model for simulating the cooling process of the iron ore sinter. Moreover, three different gas flow rate (1.5, 3, 5m/s) and three different diameter of sintered particles (50, 70, 100mm) were investigated with the model. As a result, in certain porosity, a higher cooling speed was achieved when smaller size or larger gas flow rate was used. And lower gas flow rate was beneficial for the heat recovery. The model could intuitively present the exchange of heat between the sinters and air, as well as the flow and temperature fields during the cooling process.IntroductionIron ore sinter plays a great role in iron and steel industry for many Asian countries such as China, Japan and India. As a part of the sintering procedure, the impact of cooling process on the quality of iron ore sinter couldn't be neglected. On the other hand, the massive iron ore sinters which were at high temperature contain extremely large amount of heat. However, it was reported that there's very few of them recovered in China with an average recovery rate of nearly 10.5% at 2004 [1]. Thus, more reasonable cooling procedure should be developed to get high quality product and heat recovery rate simultaneously."

Jan 1, 2011

By Xun Hu, Jian Pan, Hongbin Yu, Deqing Zhu, Yanhong Luo

Lump ores are one kind of important burdens for blast furnace (BF), their metallurgical properties have significant influence on BF performance. In this paper, the relationships between the mineralogy of five natural lump ores and the metallurgical performance have been studied. The mineralogy study includes mineral compositions, microstructure and porosity, and the metallurgical performance covers reducibility index (RI), low-temperature reduction degradation index (RDI) and decrepitation index (DI). The results show that the complex lump containing hematite, and goethite has better overall metallurgical performance. For single lump, the RI of goetihte ores is higher, the RDI and the DI is strongly influenced by porosity. The hematite and magnetite ores have good anti-decrepitation and anti-RDI, but generally the RI is lower due to lower porosity, and the RI is related to the grain size, the smaller grain size is, the better reduction will be.

Jan 1, 2015

By Julian Johnson

The effect of changing redox potential (Eh) on the high temperature sulfuric acid leaching of Western Australian dry-land nickel laterite ores has been investigated. In particular, the effect of added reductant (sulfur, sodium sulfite) or oxidant (potassium chromate) on Eh, leaching kinetics, metal extractions, acid utilisation and leach residues has been determined. Three separate ores - nonhonitic ores from Murrin Mumn and Bulong, and limonitic ore from Cawse - were used in the study. Sulfur addition varied from 0 to 7.8 kg/t ore. The total acid loading was kept constant at 430 kg/t (Murrin Murrin ore) and 330 kglt (Cawse ore), whilst acid loading for Bulong ore was varied according to the presence of either reductant or oxidant. The extraction of both nickel and cobalt from limonite ore remained unaffected when small amounts of sulfkr were added, but addition of even small amounts of reductant to nontronitic ore decreased both nickel and cobalt extraction. Increased manganese and iron dissolution were observed as the levels of reductant increased, accompanied by a decrease in chromium dissolution. As the iron dissolution increased, free acidity decreased, with a subsequent decrease in nickel extraction. In contrast, addition of oxidant lead to reduced iron and manganese dissolution and slower extraction of nickel and cobalt. Keywords: Limonite, Nonhonite, Eh, Nickel Extraction

Jan 1, 2004

By Shengli Wu, Fengjie Zhang, Feng Chang, Hua Lu, Kaiping Du

In order to make a complete understanding of steel plant metallurgical dusts and to realize the goal of zero-waste, a study of their properties was undertaken. For these purposes, samples of two sintering dusts (SD), two blast furnace dusts (BFD), and one electric arc furnace dust (EAFD) taken from the regular production process were subjected to a series of tests. The tests were carried out by using granulometry analysis, chemical analysis, X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectroscopy via SEM (EDS), and Fourier transform infrared spectroscopy (FTIR). The dominant elements having an advantage of reuse are Fe, K, Cl, Zn, C. The dominant mineralogical phases identified in sintering dust are KCl, Fe2O3, CaCO3, CaMg(CO3)2, NaCl, SiO2. Mineralogical phases exist in blast furnace dust are Fe2O3, Fe3O4, with small amount of KCl and kaolinite coexist. While in electric arc furnace dust, Fe3O4, ZnFe2O4, CaCO3, CaO, Ca(OH)2 are detected.

Jan 1, 2015

By Ivo André

Sorption of copper ions from aqueous solutions by dried biomass of the aquatic plant Potamogeton luscens was studied at laboratory scale. The aquatic plant was collected in water resources in Brazil, washed, dried at 60°C and ground in a bladed mixer. Sorption experiments were conducted in agitated flasks and in a packed bed column. Maximum copper removal was obtained between pH 5.0 and 6.6 when copper was present in the ionic form Cu'. Sorption followed the Langmuir isotherm with saturation attained at 35 mg/g. Free energy of sorption was found, to be of the order of -25 kJ/mol. Sorption kinetics data were better described by a second order reaction and rate constants were calculated in 0.030 1/(min.mg) for - 4.0 mm particles and 0.081 1/(min.mg) for - 0.59 mm particles. Removal of metal ions in a packed bed column showed that Potamogeton luscens biomass can be used in several sorption/dessorption cycles. After sorbent saturation, copper ions can be recovered from the loaded biomass by elution-with H2SO4, solution. Main mechanism responsible for heavy metal uptake was found to be ion exchange. Results are discussed in terms of the surface properties of the biomaterial, solution chemistry of copper ions and thermodynamics parameters.

Jan 1, 1995

By Jun Lu, Min Chen, Wei-jian Su, Jian-zhong Luo, Yu-tao Lei

"In the case of treating phosphatizing wastewater containing zinc, zinc had an impact on the solution chemistry, especially on pH. Fe2(SO4)3 and CaCl2 were used as precipitators to remove phosphate from zincic phosphatizing wastewater and the optimum pH was investigated. Zinc ion had a significant effect on the optimum pH. The optimum pH ranges were 12.10(inlet concentration of 15.67mg/L, outlet concentration of 9.53mg/L), 3.04-5.50(inlet concentration of 11.97mg/L, outlet concentration of 0.44-0.26mg/L), and more than 10.72(inlet concentration of 12.24mg/L, outlet concentration of less than 0.47mg/L) under the conditions without precipitator, with Fe2(SO4)3 and with CaCl2 respectively.Introduction Phosphate coating is commonly used for protective coating of machine elements. Including oil removal by caustic washing, rust removal by acid washing, phosphatization and inactivation, the phosphatization process produces wastewater containing inorganic salt of high concentration, especially the phosphate, beyond the environmental standards and polluting environment seriously. What’s more, the wastewater from zincic phosphatizing technology also contains another pollutant, zinc. At present, Chemical Precipitation (CP) and Biological Nutrient Removal (BNR) are two of most common technologies of phosphate removal. BNR, such as A/O, A2/O and UCT technology, is suited for wastewater containing organ phosphorus of low concentration and CP for wastewater with phosphate of high concentration [1]. Researches on CP treating wastewater containing phosphate of high concentration, mainly focus on adding quantity of precipitators[2-5] and coagulants[2-4] and the choice of technologies[3-9]."

Jan 1, 2008

By Toshiki Kabutomori

In fuel cell powered automobiles, hydrogen is required to be stored in materials that have a hydrogen storage density of over 4 mass%; further, these materials should be capable of supplying hydrogen by using the waste heat from a fuel cell, which is at a temperature of 373 K, in order to match the mileage of gasoline-powered vehicles. A Ti-Cr-V alloy, which exhibits a BCC structure and forms a solid solution, is a promising candidate for onboard hydrogen storage materials. Although it has a large hydrogen storage capacity of over 3.9 mass%, the rechargeable hydrogen capacity is limited to approximately 2.6 mass%. In this study, the effects of fine pulverization of the alloy on PCT (hydrogen pressure-composition-isotherm) characteristics were investigated in order to improve the rechargeable hydrogen storage capacity of the alloy. From the PCT measurements of the finely pulverized samples of the alloy, a plateau in the absorption curve was observed to begin at a hydrogen concentration of 0.5 mass%; further, a rechargeable hydrogen storage capacity of 3.3 mass% was obtained. This was greater than that obtained from the sample that was not finely pulverized, i.e., 2.5 mass%. However, the plateau width in the desorption curve was 2.5 mass%, which was the same as that observed for the sample that was not finely pulverized. The increase in the rechargeable hydrogen capacity during absorption is attributed to the precipitation of the -hydride phase (MH~2) directly from the metal phase (phase). The precipitation of the phase (MH~0.5), which should be formed in low hydrogen concentrations, is suppressed as a result of a possible reduction in the internal defects such as dislocations, vacancies, and grain boundaries by fine pulverization and annealing of the alloy.

Jan 1, 2006

By Huimin Lu, Zegao Sun, Zhijiang Gao

The traditional Ti6Al4V alloys were obtained by the smelting reduction of V-Ti bearing beach placer by rotary hearth furnace and aluminothermic reaction in laboratory. First, it gets he lp from combined rotary hearth furnace and grinding magnetic separation process to prepare titanium slag containing vanadium. In this study, a neural network model was used. The comparisons between experiment results and neural network simulation results show that genetic algorithm (GA)-based on back propagation (BP) method can predict the degree of reduction and separation of iron and slag with higher prediction accuracy. Then by aluminothermic reaction process, the optimized process parameters for Ti-V-Al alloys were searched. Al can deoxidize metal V and Ti from the metal oxides of artificial rutile containing vanadium. Finally, traditional Ti6Al4V alloy can be obtained by remelt and adjust the constituents.

Jan 1, 2016

By Baojun Zhao, Zhixiang Cui, Zhi Wang

"Bottom blown oxygen copper smelting process has been developed in Dongying, China by Dongying Fangyuan Nonferrous Metals Co., Ltd. in commercial scale. This is the first modem copper smelting technology developed in China with the advantages of high oxygen enrichment, low temperature and autothermal operation. Production capacity of more than 100,000 tonnes per year of copper has been achieved through a single bottom blown oxygen furnace with instantaneous feed rates reaching up to 90 t/h. The main features of the bottom blowing smelting process are that high grade matte (up to 72 wt% Cu) can be produced at relatively low temperatures with 2-3 wt% Cu remaining in the smelting slag. Analyses of quenched smelting slag show that significant amount of magnetite crystals are present in the slags at operating temperature which indicates that the operating temperature was much lower than the liquidus temperature of the slag. After four years operation this new technology has shown great potential for expanding production capability and energy saving. Process development continues on the first commercial scale bottom blown furnace at Dongying Fangyuan Nonferrous Metals and a larger bottom blown smelting furnace is under construction.IntroductionFlash and bath smelting technologies are the major processes used in modem copper making industry [l]. Ausmelt/Isasmelt using top blown and Noranda/Teniente using side blown are typical and common bath smelting technologies. In 1980s-1990s Hunan Shuikoshan Mineral Bureau, jointly with China Nonferrous Engineering and Research Institute (now China Enfi Engineering Corp.), developed the concepts of the bottom blown oxygen processes for both lead and copper smelting [2]. After the pilot test on 3000 ton copper per year scale in 1991, it was not progressed to industrial scope."

Jan 1, 2013

By C. Takano

The integrated iron and steelmaking industry generates large amounts and many types of solid dusts and sludge, at different phases of the production. Within these are: sludge of the Blast Furnace; coke fines; fine and coarse fractions from oxygen converters; sludge from water treatment at rolling mill unit; and others. In this paper the above dusts and sludge were physically and chemically characterized. The obtained results allowed defining self-reducing pellets using these materials. The high temperature behavior of the pellets were evaluated. Good results, with no decrepitation and swelling, and high yield of reduction, show that it is feasible to recycle them, as self-reducing pellets, in oxygen steelmaking converter.

Jan 1, 2001

By G. Diáz

The PLACID process applied to the recycling of spent lead-acid batteries is being developed by an European Consortium within the Brite-Euram II programme. The status of the project entitled "Lead Recovery from Lead Oxide Secondaries" is described in this paper. The main laboratory and batch experimental results and the preliminary feasibility study are summarised. The description of the demonstration pilot plant and continuous campaigns programme for 1995 are also included. An interesting global approach is proposed, integrating the Placid process in the existing spent battery recycling pyrometallurgical facilities. This yields important improvements in the overall process. Grids would be easily treated by the conventional pyrometallurgical route, obtaining lead alloys,, while battery pastes, slags and fumes would be fed to the Placid process, obtaining pure electrolytic lead (>99.99 %), ideal for battery paste manufacturing. The implementation of the Placid process into the existing battery recycling pyrometallurgical facilities is analyzed from technical, environmental and economical viewpoints. Greater overall lead recovery, lower operating costs, reduced waste production, environmentally safer residues and much better lead product quality are the key advantages. The authors draw the following final conclusion : Integration of the Placid process with conventional pyrometallurgical treatment is a feasible and very attractive alternative route for spent lead-acid battery recycling.

Jan 1, 1995

By W. -S. Hwang, R. A. Stoehr, P. Ingerslev

"The flow of molten metal entering complex two-dimensional foundry molds has been modeled using the Simplified Marker and Cell (SMAC) and Solution Algorithm (SOLA) techniques. The molds were for a series of four and three-spoke wheel designs. The computer calculations were compared to physical experiments in which molten cast iron was poured into C02-bonded sand molds. The metal was photographed with a high speed motion picture camera focused through a Pyrex glass window on one face of the mold. To get good agreement between the calculations and the experiments, it was necessary to accurately represent the velocity through the ingate. This was calculated by application of the Bernoulli equation to flow through the feed system. Some difficulties were experienced with mathematical instability, expecially in the three-spoke design with a narrow ingate. This was overcome by using 100% upwind differencing, and over relaxation parameter near 1.0 (i.e. no over relaxation), and variable mesh spacing.IntroductionModeling the flow of molten metal entering molds has the potential for making significant contributions to the design of feed systems. It will supply information to the computer-aided-design systems of the future that will enable the designer to optimize the placement of gates, dimensioning of passages, and designation of casting speeds. Such design criteria have generally been based on application of energy balance (Bernoulli equation) principles to flow in the sprues, runners, and gates. Indeed, this is the easiest way to determine the proper dimensions to give a suitable filling time for a casting of a given size. A number of computer programs, including one by some of the present authors, have integrated such calculations into CAD systems. l Modeling the flow of metal inside the mold cavity requires other techniques that will handle free-surface transient flow. Stoehr and Hwang reported on the application of the Marker-and-Cell (MAC) technique to mold filling problems at the previous conference in this series at Hennicker, N.H. in 1983. 2 Although considerable progress has been made since that time in improving the accuracy, stability, and convenience of these techniques, the shapes to which they were applied remained limited. Also, physical verification of the results of the calculations was limited to water models.The work to be reported in this paper was undertaken with two objectives: (1) to apply these techniques to more complex and realistic shapes, and (2) to verify the results by comparison with flow patterns observed in molten metal poured into actual sand molds."

Jan 1, 1986

By D. Majuste

This paper describes an experimental approach to evaluate the effect of organic impurities or even additives on metal electrowinning and product quality. In addition to electrowinning tests and electrochemical measurements, the approach includes organic analysis by Fourier Transform Infrared spectroscopy and gas chromatography; video monitoring of the reaction interface; and product characterization by using scanning electron microscopy, crystallographic texture and bending tests. The mechanical behavior of metal cathodes was assessed with a customized bending device that is able to bend the cathodes up to angles similar to that of the stripping machine. In this work, the effect of a potential organic impurity, lubricating oil, on the production of electrolytic zinc is taken as a case study. The findings of the investigation allowed a better understanding on the role of this organic on energy consumption and product quality and a qualitative prediction for the behavior of Zn cathodes during the stripping operation. Simple control and optimization procedures resulted in significant energy savings.