Search Documents

By H. E. Strauss

The time-to-fracture test has been applied to pure platinum and to two alloys of platinum under the special conditions of small cross-sectional area of the specimens and of a test temperature above the annealing temperature. While the results are similar in character to those secured with large specimens of steel at temperatures below the annealing temperatures, two differences are noted: (I) an upward inflection in the curves for log stress vs. log time for the alloys, and (2) a sharp break in the curve for log stress vs. log time for pure platinum when single crystals filled the wire. The experiments showed that: (I) platinum and 10 per cent rhodium-platinum maintained their strengths at IIOO°C. better than did to per cent iridium-platinum, and (2) the rhodium-platinum after a time exceeded the iridium-platinum in strength at IIOO°C. Platinum alloys in their service at high temperatures encounter conditions somewhat similar to those that exist in the usual form of the "time-to-fracture"l test with steel. This paper is intended primarily to present results obtained by a "time-to-fracture" test under conditions approximating actual service for platinum (at the temperature IIOO°C. under oxidizing conditions) with three materials, pure platinum (99.99 per cent), a platinum alloy with 10 per cent iridium, and a platinum alloy with 10 per cent rhodium. The experimental procedure differed from that previously used in this type of measurement in that the samples were of small diameter (0.010 in.), were fully annealed, and were tested at a temperature definitely above their annealing points (600°C., IOOO°C. and 1050°C., respectively, for 60 per cent cold reduction and 15 min. heating time2,3). The experimental arrangement was similar to that previously described,' using as heating unit a small, horizontal, platinum-wound furnace, ½ by 12 in., maintained at constant temperature by an automatic controller. The samples were 0.010-in. wires, which had been annealed at 1200°C. by drawing them slowly through the furnace. The time-to-fracture was measured electrically. Elongation was not determined because of the difficulties inherent in the experimental arrangement. Life—that is, the time-to-fracture—was considered the important property in these first tests. No attempt was made to measure the reduction in area, but the types of fracture were noted qualitatively; in the text they are referred to as (I) the normal, plastic, or necked fracture, (2) the knife-edge fracture, and (3) the brittle or intercrystalline fratture with small reduction of area. Results for different constant applied stresses are plotted in Fig. I. In all cases at least two trials were made for each stress, although they cannot always be indicated separately on the curves. The breaking Stresses drop very rapidly to a small frat-286

Jan 1, 1943

By H. E. Strauss

The time-to-fracture test has been applied to pure platinum and to two alloys of platinum under the special conditions of small cross-sectional area of the specimens and of a test temperature above the annealing temperature. While the results are similar in character to those secured with large specimens of steel at temperatures below the annealing temperatures, two differences are noted: (I) an upward inflection in the curves for log stress vs. log time for the alloys, and (2) a sharp break in the curve for log stress vs. log time for pure platinum when single crystals filled the wire. The experiments showed that: (I) platinum and 10 per cent rhodium-platinum maintained their strengths at IIOO°C. better than did to per cent iridium-platinum, and (2) the rhodium-platinum after a time exceeded the iridium-platinum in strength at IIOO°C. Platinum alloys in their service at high temperatures encounter conditions somewhat similar to those that exist in the usual form of the "time-to-fracture"l test with steel. This paper is intended primarily to present results obtained by a "time-to-fracture" test under conditions approximating actual service for platinum (at the temperature IIOO°C. under oxidizing conditions) with three materials, pure platinum (99.99 per cent), a platinum alloy with 10 per cent iridium, and a platinum alloy with 10 per cent rhodium. The experimental procedure differed from that previously used in this type of measurement in that the samples were of small diameter (0.010 in.), were fully annealed, and were tested at a temperature definitely above their annealing points (600°C., IOOO°C. and 1050°C., respectively, for 60 per cent cold reduction and 15 min. heating time2,3). The experimental arrangement was similar to that previously described,' using as heating unit a small, horizontal, platinum-wound furnace, ½ by 12 in., maintained at constant temperature by an automatic controller. The samples were 0.010-in. wires, which had been annealed at 1200°C. by drawing them slowly through the furnace. The time-to-fracture was measured electrically. Elongation was not determined because of the difficulties inherent in the experimental arrangement. Life—that is, the time-to-fracture—was considered the important property in these first tests. No attempt was made to measure the reduction in area, but the types of fracture were noted qualitatively; in the text they are referred to as (I) the normal, plastic, or necked fracture, (2) the knife-edge fracture, and (3) the brittle or intercrystalline fratture with small reduction of area. Results for different constant applied stresses are plotted in Fig. I. In all cases at least two trials were made for each stress, although they cannot always be indicated separately on the curves. The breaking Stresses drop very rapidly to a small frat-286

Jan 1, 1943

By E. T. Turkdogan, P. Grieveson, J. F. Beisler

Jan 1, 1963

By Northcutt Ely

This volume- summarizes mining and petroleum legislation in 18 European jurisdictions. Within these jurisdictions, primary attention is given to requirements that must be met in each country for acquisition of rights to permit development of mineral resources. Coverage includes: First, identitication of the controlling laws or statutes governing minerals acquisition and reference to the administrative authority; second, analysis; of the laws governing mines and quarries and their products; third, analysis of laws applicable to natural gas, petroleum, and related materials; and fourth, mention of laws regulating offshore operations. Where pertinent, sections dealing with historical background or administration have been added in countries where minerals are subject to control of States or Provinces, those areas are considered separately from the central government.

Jan 1, 1974

By Gerald A. Crawford

"1880s - Unmasking the Sudbury Basin Falconbridge Ltd. turned 60 in 1988 but its roots go back more than a century to the discovery and development of the mineral resources of the Sudbury Basin. Nickel was first identified in the area in 1856 but sustained exploration awaited the early 1880s and the advance of the CPR westward from Sudbury. Rock was laid bare in the right-of-way and by forest fires and logging. Reddish oxidized outcropping or ""gossan"" were exposed, heralding the presence of nickel as the shape of this astounding geological formation gradually began to emerge. Many great mines of the area were opened up in this period on the south rim of the Basin west of Sudbury. To the east the ore dips below overburden, however, and Falconbridge remained a mere dot on the map until the turn of the century when Thomas Edison detected a magnetic occurrence by dip needle."

Jan 1, 1999

Titanium and Zirconium Industries Pty. Ltd. separates rutile and zircon from heavy mineral concentrate recovered from sand dunes on the east coast of North Stradbroke Island, Queensland. Separation plant feed is delivered to Dunwich, on the west coast, by a seven mile aerial ropeway traversing the island. Mining and concentration is effected by two floating dredge-concentrators now operating on the beach 31; miles from the aerial ropeway terminal. Heavy mineral concentrate is transported hydraulically from the dredges to the ropeway through a 6 in. pipeline. Six pumps in series deliver 24 ton/hr of dry solids in a pulp containing 13 per cent solids. For maximum economy the transfer pumping system is controlled deliberately to cause transportation in the zone of incipient settlement of solids, ieat velocities below the limit deposit velocity for the particular pipe diameter, pulp density, and specific gravity of solids. Automatic density control, based on a combination of power consumption and pipeline pressure, eliminates the danger of plugging the line but periodic flushing is necessary to remove gradual accumulation of solids in the bottom of the pipe. After 15 months operation the pipeline was descaled with hydrochloric acid to remove severe blistering with rust nodules, regrowth of which is now prevented by continuous injection of inhibitors. After transporting 100,000 tons of heavy mineral the average wear on the steel portion of the pipeline was 0·01 in. and indications are that wear on the asbestos cement portion is less.DESCRIPTION OF OPERATIONSGeographyTitanium & Zirconium Industries Pty. Ltd. (T.A.Z.I.) operates on North Stradbroke Island, some 30 miles southeast of Brisbane, Queensland. The island is approximately 25 miles long and eight miles wide, and is bounded on the east by the Pacific Ocean and on the west by Moreton Bay (Fig. 1). With the exception of a small outcrop of volcanic 1. Manuscript received at The Institute. 8th May. 1962. This paper was presented at the Annual Conference of The Institute. 5th-11th August. 1962.

Jan 1, 1962

By G. A. Calboreanu

One way of cost reduction is attained when using materials with improved erosion ? corrosion resistance. For many years hard irons successfully answered the Mining Operation needs however application ranges were limited due to the low chemical resistance of such alloys. Corrosion resistance of any hard iron increases when microscopically homogenizing chromium and generating passivation conditions throughout and between all metallographic phases. Chromium distribution of the new material called Max10 was analyzed with EDS ? energy dispersive spectroscopy. At critical depleted chromium carbide ? matrix interfaces chromium increased to 31.72% which is well within passivation levels. Generally the corrosion resistance of high chromium hard irons provided by Metal Casting Industry is limited to 0.5% sulfuric acid and 28 PPM ionic chlorides. Such restrains increased when using Max10 to 2.0% sulfuric acid and 100 PPM ionic chlorides. Max10 contains 35% carbide volume fraction, has excellent corrosion resistance within pH = 1.15 ? 13.6 while fracture toughness under plain - strain conditions and Mode I opening is KIC = 20 KSI.(inch)1/2. Wear rate was calculated with the pin-on-disk apparatus using a diamond indenter per ASTM G99 recommendation. After years of research, experimentation and implementation the Max10 castings were service installed in slurry pumps and mixing equipment. In some applications the life time of slurry pumps manufactured in Max10 tripled versus previously used materials.

Jan 1, 2012

By Liqun Liang

Various nondestructive testing (NDT) inspection methods are available to evaluate the structural integrity of cast-in-place shafts. The widely used methods include Cross Hole Sonic Logging Testing and Low Strain Testing. Due to its advantages such as low cost, easy operation, quickness and flexibility (no need to plan ahead and prepare inspection tubes or other devices), Low Strain Test is frequently specified in quality assurance programs of many countries or when doubts arise as to the integrity of the finished shafts/piles. The method is well suited for small to middle sized shafts. However it is an indirect NDT testing method and has certain limitations. Data interpretation requires proper training, experience and judgment and, therefore, inconsistent conclusions and reporting may be provided by different testers. To avoid or reduce such inconsistencies, it is best to follow a standardized data interpretation and record classification system. In this paper, a new classification method is presented with examples. A step-by-step data evaluation and interpretation procedure is proposed with examples of real cases to help understand the LST data. The paper also makes recommendations for measures to be taken when anomalies are detected in tested production piles.

Jan 1, 2011

By S. Parada, P. T. Jones, M. Guo, S. Smets

The corrosion behaviour of a high-quality rebonded magnesia-chromite refractory in contact with a vacuum oxygen decarburization (VOD) slag with high Al2O3content (15?20 mass per cent) is investigated under VOD process conditions by rotating finger tests in a vacuum induction furnace. The refractory degradation mechanisms are studied by the characterization of corroded microstructures using scanning electron microscopy, equipped with energy dispersive spectroscopy. The influence on the refractory wear of the process temperature and the Al2O3content in the slag is discussed. Keywords: corrosion, magnesia-chromite refractory, VOD slags, vacuum induction furnace

Jan 1, 2004

By D. Pillay

Outsourcing? and ?sub-contracting? have become buzzwords in recent years, as SA industry becomes increasingly exposed to the global economy, and global competitiveness. In its effort to ?catch up? after years of relative isolation, there is a concerted effort to learn from global ?best practice?, in order for South African companies, and the SA economy, to become ?winners?. There seems nothing wrong with this approach at face value. Companies need to compete and be profitable if they are to remain in business. Failure will in the end mean bankruptcy, and the loss of jobs. However, if one interrogates the precise practices, and their implications for all concerned?not just shareholders and employers, but workers, communities, the environment, future generations, the national economy?then the picture can change dramatically. ?Best practice? for whom?

Jan 1, 1999

By Christopher Mark

Pillar recovery continues to be one of the more hazardous activities in underground coal mining. Safety requires that the roof above the intersection remain stable until after the pillar has been extracted. Artificial supports (timbers and Mobile Roof Supports) arc essential to roof stability, but so is the final remnant stump or pushout. Traditional mining practices usually called for the complete extraction of the final stump, but the recent trend (both in the U.S. and internationally) seems to be towards mining plans that leave a remnant stump. For this study, a sample of roof control plans from the Mine Health and Safety Administration (MSHA) Coal Districts were analyzed to determine current pillar recovery practices. Both full- and partial- extraction plans were included. Special attention was paid to whether plans require that a final stump be left, and whether requirements regarding the dimensions of the remnant stump are included. Foreign experience with final stumps is also summarized. It seems that the risk of major pillar falls can often be reduced by leaving final stumps that are large enough to protect the intersection, but small enough that they do not inhibit the caving of the gob. Because final stumps are often irregular in shape, a new approach for estimating their strength is described. Analyses were conducted to assess the effect of seam height and depth of cover on the potential variation in the size of remnant stumps.

Jan 1, 2001

By Paul M. Tyler

Graphite occurs in many places in the United States, but previous to 1914 the domestic production amounted to only 15 to 20 per cent of the natural graphite consumed in this country. Including artificial, graphite, the proportion was about 25 per cent. During the World War the production of both natural and artificial graphite increased until, in 1918 it, contributed more than one-half of the available supply, and since 1919 the proportion has not fallen below 40 per cent. Except during the war period, however, this apparently increasing independence has not been due to any large increase in production from domestic mines. It simply reflects a larger output of artificial graphite and reduced imports of Ceylon lung and chip, grades which have never been produced in substantial quantity in the United States. DOMESTIC DEPOSITS3 American graphite deposits, though numerous and often large, are characteristically low-grade. They constitute an abundant source of potential supply, but in normal times they have proved relatively costly to work, and even at the same price the various products have never been able wholly to displace certain imported qualities, notably crucible grades from Ceylon and pencil graphite from Mexico.

Jan 1, 1929

By W. H. Schiffbauer

The protection of miners, equipment, and infrastructure is discussed. While the primary focus of the described technology is to prevent miners from being injured, struck-by, or crushed by heavy equipment; another major benefit realized is also the protection of equipment and infrastructure. An attempt is made to define and classify the systems used to provide proximity detection and warnings as well as collision detection and avoidance. Information about the speed of vehicles and human operator response time can be a factor in the choice of what type of system and what features are needed to properly address the needs. How the technology adjusts to compensate for various vehicle speeds, while maintaining the same level of protection is noted. The statistics which justify the need of miner protection are provided. The primary system components required, what attributes they feature, and how they respond in the environment, is briefly highlighted. The physics behind the danger zone marker technology and what makes it so robust and reliable is established. Examples of a few mining applications and specific operational modes are provided for both surface and underground.

Jan 1, 2011

By Eleanor Abshire

[THE INCREASING use of hafnium as a vital component in atomic power reactors has brought this metal into recent prominence. A literature survey was made and this bibliography was compiled to provide research and production groups with a ready source of reference to this important metal anti its compounds. This service is rendered by the Zirconium Information Center, which is sponsored by the Department of the Navy, Bureau of Ships, and the F .S. Department of the Interior, Bureau of Mines, tit the Bureau's Northwest Electrodevelopment Experiment Station, Albany, Oreg. The following reference sources have been reviewed for this compilation : Chemical Abstracts; Industrial Arts Index; Crerar Metals Abstracts; Nuclear Sciences Abstracts; Bureau of Mine; Information Cicular 7771, Bibliography of Zirconium; anal Bureau of Mint' Information Circular 7830, Bibliography of Zirconium, suppllement to Information Circular 7771.]

Jan 1, 1960

The Role of Mineral Processing in the Development of Cement with Low Carbon Emissions

Sep 13, 2010

By Brian P. Waagner

Construction law in general and the law of deep foundations in particular continues to develop rapidly, particularly in the areas of risk allocation. Public and private owners are increasingly using contractual disclaimers to shift the risk of differing site conditions to contractors, and courts are increasingly willing to enforce these contractual devices. Perhaps also in an effort to control costs, public and private owners are turning to design-build contracting techniques. While design-build offers many advantages over traditional project delivery systems, it does not answer all of the risk-allocation questions that frequently arise. Even in design-build, problems with unanticipated subsurface conditions and defective design are not easily addressed. Finally, developments in electronic commerce present the potential to transform the construction industry.

Jan 1, 2002

By Jaeheon Lee, Junmo Ahn, Jiajia Wu

In this project, low grade copper ore samples were obtained from two mining sites in the US, and they were chalcopyrite-rich (sample A) and conichalcite-rich (sample B) ore. Copper grades were 0.6% and 0.4% for the two samples, A and B, respectively. Leaching experiments were conducted by bottle roll tests for 24 hours, and various lixiviant systems were applied. Methanesulfonic acid (MSA) and glycine were used as alternative lixiviants to sulfuric acid. Oxidants including ferric ion and hydrogen peroxide were tested. The results showed the copper extraction of sample A increased after adding 1 g/L ferric ion in sulfuric acid and MSA solution, from 20% to 36%, but further increase was not observed with higher ferric ion concentration. The copper recovery increased significantly with H2O2 concentration, and over 80% copper recovery was obtained with 10% H2O2. For sample B, the copper dissolution kinetics were relatively fast and reached the maximum value in five hours. Around 60% copper were extracted in sulfuric acid and MSA solution. Copper recovery slightly increased after adding ferric ion and H2O2. Glycine is a weaker lixiviant for both samples, the copper extractions were 36% and 4% respectively. INTRODUCTION Chalcopyrite is the most abundant copper sulfide mineral on earth, and it is one of the most refractory copper minerals regarding chemical processing. The declining copper grade and depletion of copper oxide deposits stimulate the development of hydrometallurgical process to extract copper from chalcopyrite. The dissolution of chalcopyrite by ferric ion is normally illustrated as Equation (1) and (2) (Dutrizac & MacDonald, 1974): CuFeS2 + 4Fe3+ → Cu2+ + 5Fe2+ + 2S0 (1) CuFeS2 + 4Fe3+ + 3O2 + 2H2O → Cu2+ + 5Fe2+ + 2H2SO4 (2) However, slow kinetics are usually observed from chalcopyrite leaching at ambient temperature and pressure. Researchers attribute the slow kinetics to passivation during chalcopyrite dissolution, and different passivation products are also proposed (Klauber, 2008). In recent years, many efforts have made to develop new methods to extract copper from chalcopyrite, such as utilizing bacteria or stronger oxidant (Zhao et al., 2015; Ruiz-Sánchez & Lapidus, 2017).

Jan 1, 2019

Market confidence is on the rise and industry leaders turning toward the vast and diverse region of Latin America are faced with abundant, yet daunting, opportunity. From the iron orebodies of Brazil to the renowned copper mines of northern Chile, drilling teams in Latin America are often faced with abrasive, broken ground. These types of ground conditions tear up coring bits rapidly, making it extremely difficult for even the most seasoned drilling teams to maintain effective productivity. The drilling challenges faced in this rich and opportune region are being met today by advanced coring technology, bringing with it the potential for increased productivity in Latin American mineral exploration.

Jan 3, 2010

This Bureau of Mines publication contains five papers pertaining to the effective grounding of mine power systems, as follows: Ground-check monitor types and safety characteristics; ground wire monitors for surface coal mines; ground bed design and measurement; electrical ground rod corrosion; and a continuous ground bed resistance monitor.

Jan 1, 1979

By Gabriel Gonçalves Pessoa de Castro

O trabalho teve por objetivo produzir uma liga Al AA1070 com granulometria fina a partir de um material com granulometria grosseira, por meio de deformação plástica severa (DPS) aplicada por prensagem por canais equiangulares (ECAP) via rota C, bem como esclarecer e avaliar os mecanismos responsáveis pela evolução microestrutural durante este processo de prensagem. O processo empregou a rota C com 5 passes consecutivos a frio e acumulou uma deformação ?5 = 5,95. O material de partida é proveniente de um processo de laminação a quente, com uma microestrutura de grãos grosseiros com tamanho de grão de 16 ± 18 µm. Foi realizada a caracterização microestrutural com o auxílio das técnicas de microscopia eletrônica de varredura (MEV) e de difração de elétrons retroespalhados. O refinamento microestrutural foi realizado eficientemente alcançando uma microestrutura fina, observou-se uma redução de 80% alcançando um tamanho de grão de 3,38 µm, e um aumento da fração de contornos de alto ângulo passando de 23% a 46%. A partir dos resultados obtidos nas análises conclui-se que os mecanismos responsáveis pela evolução microestrutural foram os processos de subdivisão por meio de fragmentação e rotação de grãos, recuperação e recristalização dinâmica.

Aug 16, 2017