By S. B. Lement

THE nature of the carbides that form during the tempering of martensite is a subject of continuing controversy. The only direct methods of identification available are X-ray and electron diffraction. These methods are subject to several difficulties. Only a relatively few diffraction lines of appreciable intensity emanate from carbide phases that are formed at low tempering temperatures. Furthermore, some overlapping of carbide and matrix lines occurs. There is also the problem that numerous lines in the patterns of possible carbide phases that may be present have about the same d-spacings. Increasing the number of carbide lines and eliminating the matrix lines can be accomplished by extraction techniques. However, there is always the possibility that a change in carbide structure will occur as a result of removal from the parent matrix. Therefore, such techniques as electrolytic extraction and making extraction replicas should be checked by other methods. For identifying small amounts of carbide in a tempered martensitic matrix, electron diffraction carried out in reflection is more advantageous than X-ray diffraction. To properly prepare a specimen for reflection electron diffraction, an etchant that will selectively attack the matrix and thereby cause the carbide particles to stand in relief should be used. With an electron beam directed at a grazing angle to the specimen surface, the major contribution

Jan 1, 1960

By L. Delisle

This work represents the first step of an attempt to test the applicability of the electron microscope to the study of subgrain structures in copper. Observations on annealed and deformed single crystals and polycrystalline samples of copper are described. IN the course of study of the structure of fine tungsten wires and tungsten rods with the electron microscope, well defined subgrain structures were observed. The size, size distribution, and orientation uniformity of the etch figures varied widely in different samples. Figs. 1 and 2, electron micrographs of a tungsten wire and of a tungsten rod, respectively, are illustrations of the difference in size and size distribution of the etch figures in different samples of the same metal. The observed differences, as pointed out in a previous paper,' appeared to be related to the heat and mechanical treatments of the samples. They were also consistent with the results reported in the literature on the mosaic structure of metals.' For that reason a program of research was initiated in an effort to obtain more systematic evidence of the possible relation of heat and mechanical treatments to the subgrain structure of metals as observed in the electron microscope. The purpose of this paper is to present observations made on the effect of cold work on the subgrain structure of copper. Procedure Starting Materials: Copper was the metal studied because it can be obtained in a high degree of purity, much information is available in the literature on its properties and its response to cold work and heat treatment, it shows no allotropic change, and it is sufficiently hard to be handled without great difficulty. Two groups of specimens were used: 1—single crystals cast from spectroscopically pure copper and 2—polycrystalline samples of oxygen-free high conductivity copper. Single crystals were studied because it was hoped that the elimination of a number of variables, such as grain boundaries, orientation differences, degree of purity, would simplify the problem and perhaps permit a better understanding of the phenomena that would be observed. The polycrystalline samples were designed to give a general picture of the changes considered. The single crystals were made of copper which analyzed spectroscopically to better than 99.999 pct Cu. They were cast in vacuum, by the Bridgman method, in crucibles made of graphite with a maximum ash content of 0.06 pct. The mold design is shown in Fig. 3. It permitted casting crystals of the size and shape required for the experiments, so that the danger of introducing cold work in the original samples by cutting or other machining would be eliminated. The polycrystalline samples were pieces, 3/4 in. long, cut from a rod of oxygen-free high conductivity copper, % in. in diameter. A flat surface, 1/4 in. wide, was milled along the rods, polished, and etched. The samples were then annealed in vacuum at 850°C for 1 hr. Polishing and Etching: Work previously done on tungsten,' polished mechanically and etched chemically," had shown that: 1—the general appearance of the etch figures of a given sample was not altered by repeated polishings and etchings under similar conditions; 2—variations in the time of etching and the concentration of the etchant changed the definition of the etch figures, but did not alter their general size nor orientation distribution within the limits of observation. Further work confirmed the reproducibility of the subgrain structures observed in, 1—single crystals and polycrystalline samples of copper when polishing and etching were repeated under similar conditions, and 2—specimens of tungsten and polycrystalline copper when electrolytic polishing and etching were substituted for mechanical polishing and chemical etching, respectively. On the strength of these observations, it was felt that, if conditions of polishing and etching were kept constant, changes observed in the subgrain structure of a sample upon deformation and annealing would be attributable to such treatments. For that reason the conditions of polishing and etching were kept as constant as possible. The single crystals were polished electrolytically in a bath of orthophosphoric acid in water, in the ratio of 1000 g of acid of density 1.75 g per cc to 1000 cc of solution, under a potential drop of 1.6 to 1.8 V. Electrolytic polishing was selected to prevent the formation of distorted metal in polishing. The same samples were etched by immersion in a 10 pct aque-

Jan 1, 1954

By W. R. McMillan, E. A. Gulbransen, K. F. Andrew

Annealed and electrolytically polished pure iron was oxidized between 650° and 850°C at oxygen pressures of 0.1 to 2 microns Hg. Electron optical studies showed that oxidation occurs discontinuously over the surface and orients crystallographically with the substructure of the metal grains. IN previous papers', " the authors described the formation of oxide films on high purity iron at norrnal pressures and at temperatures below 300°C. Electron optical studies showed that the oxide film consisted of many individual oxide crystallites having nearly random orientation on each metal grain. The size of the oxide crystallites depended upon the temperature and upon the extent of oxidation. In these studies the crystallite size varied from 250 to 1800Å. Recently, Bardolle and Benard3 studied the crystal habit of the oxide crystallites formed on Armco iron between 650" and 850°C in what might be defined as a "poor vacuum" atmosphere in which the pressure could be varied between 10-1 to 10-3 mm of Hg. Their results showed that, at 850°C and a vacuum of l0-2 to 10-3 mm of Hg, a few well oriented nuclei of oxide were formed on the metal grains. At pressures between l0-1 to 10-2 mm of Hg, many oriented nuclei of oxide were formed. At 750°C the metal surface was bright although an oxide was present. Unfortunately, the extent of oxidation, the oxygen pressure, and the influence of carbon in the metal were not determined, and it was, therefore, impossible to give a theoretical interpretation to the very beautiful light micrographs. Bardolle and Benard used the light microscope to determine the crystal habit of the oxide and X-ray diffraction to determine the orientation relationships. It was believed that the use of controlled amounts of oxidation at high temperature is an important method for the study of the initial stages of oxidation of metals at high temperatures. This paper presents the first results of an electron optical study of this problem for iron. Since the electron microscope and electron-diffraction methods using stripped oxide films and surface replicas yielded finer details of the crystal habit and structure of oxide film, these methods were used in this study. Two types of iron having different carbon contents were used: Puron and Armco* iron. A com- parison of the results for these materials made possible a study of the influence of the surface oxide-carbon reaction on the initial stages of oxidation. Before discussing the experimental results, the thermodynamic equilibria of 1—the oxidation reaction, 2—the surface oxide-carbon reaction, and 3—the solubility of oxygen in iron, will be considered. In addition, it is important to consider the kinetic-theory predictions on the rate of collision of oxygen with the iron surface. Thermodynamic and Kinetic-Theory Calculations Only one type of reaction is usually considered in the oxidation of iron at normal pressures at high temperatures: Fe(a) + 1/2O2(g) = FeO(s) 3Fe(a) + 2O2(g) = Fe3O4(s) 2Fe(a) +3/2O2(g) = a-Fe2O3(s). [11 However, two other reactions may occur: FeO(s) + C (solid solution in Fe) + Fe(a) + CO(g) [2] and Fe(a) + O2(g) e Fe(a) (solid solution of 0,). [ 3 ] In addition, iron will react with the higher oxide at certain temperatures to form FeO. For a complete interpretation of the oxidation of iron at low pres-

Jan 1, 1955

By R. Casting, J. Philibert, and C. Crussard

APPARATUS described in this paper uses the properties of X-radiation, emitted by substances under electron bombardment, as a means of rapid chemical point analysis. The method is based upon the principles of emission X-ray spectrography pioneered by Moseley in 1913. A very finely focused beam of electrons—the electron probe—is projected on the surface of a sample, which has a very large area compared with the beam diameter, at the point where it is desired to know the chemical composition. The minute volume of the sample which is thus irradiated emits a complex X-ray spectrum consisting principally of the characteristic radiations of the elements present in the volume. Measurement of the wavelength and intensity of each component of this spectrum thus affords a simple method of determining the chemical identity and concentration of these elements. The volume of sample which is analyzed at each position of the beam is limited by the diffusion of electrons in the sample. For an accelerating potential of the electron beam of about 30 kv, which is a convenient value for producing the characteristic radiation, this diffusion extends over a diameter of about 1 µ normal to the beam, and about 2 µ in the direction of the beam. Thus a beam of 1 µ in diameter leads to a volume of about 2 µ in diameter being irradiated. The limits of the analyzed region are thus considerably smaller than those obtained by using spark or arc emission spectrometry, which must extend to about 50 µ at right angles to the beam, and those obtained in X-ray fluorescence analysis, where the penetration of the specimen is considerably greater. The apparatus itself consists of three main parts: an electron optical system. an X-ray spectrograph and an optical microscope. The electron opticai system consists of a tungsten cathode emitting the electrow and a pair of magnetic lenses which focus the electron beam on the specimen to be analyzed. The specimen is prepared in the usual way, as in optical micrography. The X-radiation, emitted at the focal spot where the electrons strike the sample, is analyzed with a curved crystal, Geiger-Müller counter, vacuum spectrograph. The light microscope, designed to observe the surface of the sample in the region to be analyzed, is provided with a reflecting objective placed on the axis of the second magnetic lens. Its magnification is X450. The quantitative determination of an element A in the analyzed region is made by measuring the intensity I, of a strong characteristic line of the element, as emitted from the sample, and then the intensity I (A) of this same line as emitted from a

Jan 1, 1958

By H. A. Domian, H. Biloni, G. F. Bolling

Jan 1, 1965

By V. A. Phillips

Transmission-electron micrographs of electro-thinned samples of bulk-aged Cu-3.1 pet Co alloy show an aging sequence, supersaturated solid solution — coherent particles — quasi -coherent particles — noncoherent particles. Hardening is due to precipitation of coherent spherical fee coball-rich particles showing coherency strain fields, which are resolved at between 15 and 30A diameter. Loss of- full coherency did not occur until well into the overaged region, even with the assistance of deformation after aging. Different average particle diameters of 123, 92, and 149 ± 10Å were observed in samples aged to peak yield strength at 600°, 650°, and 700°C, respectively, indicating that there is no critical size for peak hardening. Noncoherent particles tended to develop (111) faces and became octahedral in shape. Dislocations tended to nucleate spherical coherent particles which eventually grew together forming large elongated particles. The surface energy of a noncoherent (low-angle) inter-phase boundary is estimated to he about 50 ergs per sq cm. A number of particle lining-up phenomena were observed. Overaging is principally attributed to increase in particle spacing, progressive loss of coherency, and increase in amount of discontinzdous precipitation. COPPER dissolves about 5.6 at. pet (5.2 wt pet) of cobalt at 1110oC1 and the solubility decreases to 0.75 at. petl (0.54 at. pet)2 at 650°C and to 0.1 at. pet or less at lower temperature.' It has been known for many years3-5 that Cu-Co alloys are capable of age hardening. Since cobalt is fee above 417°C and its atom size is only about 2 pet smaller than that of copper, precipitation of coherent particles would be expected. The equilibrium phase precipitated at 700°C and below contains about 10 pet Cu in solution which tends to stabilize the fee structure, lowering the transformation temperature to 340oc.l The alloy is known to undergo discontinuous precipitation in addition to general precipitation; while the former can be seen with an optical microscope, the latter precipitates are not visible except in the grosly overaged condition.5, 6 Extensive use has therefore been made of the ferromagnetic properties of the precipitate in order to follow the course of aging, and it has proved possible to measure the average particle size, spacing, approximate shape, and volume fraction and to determine that the particles are coherent without ever seeing a particle (see for example Refs. 2, 7, and 8). The magnetic measurements of particle size are limited to diameters below about 120Å.7 The present study was undertaken using the techniques of transmission-electron microscopy in order to check the above conclusions, to extend the previous magnetic work to larger particle sizes, and to attempt a more detailed correlation of properties and structure. A portion of this work has already been published.9-11 The present paper is concerned with the metallographic features of precipitation in relation to aging curves. Bonar and Kelly12'13 have published preliminary results of a similar study on single crystals of Cu-2 at. pet Co. EXPERIMENTAL Preparation of Alloy. A Cu-Co alloy, containing 3.12 wt pet (3.36 at. pet) Co by analysis, was prepared from 99.999 pet purity oxygen-free copper and electrolytic-grade cobalt. The alloy was melted and cast in vacuo in a high-frequency furnace using a graphite crucible and mold: Analysis showed chat 0.004 pet C was picked up during melting. The 1-1/2-lb ingot was homogenized in hydrogen for 24 hr at 1000°C. Slices were cold-rolled to 0.005 or 0.003 in. thickness, with an intermediate 650°C anneal in hydrogen at 0.080 in. thickness. Batches of six to ten strips were solution-treated in sealed-off quartz tubes in high vacuum in a vertical furnace and quenched by dropping into iced brine containing a device which snapped off the nose of the tube. Solution treatment consisted of 1 hr at 990°C or 2 hr at 965°C. The latter was employed for all mechanical-property studies, since a tendency was noted for the higher temperature to give porous material. Strips were usually aged individually in a horizontal vacuum furnace, inserting into the hot zone and withdrawing into a cold zone without breaking the vacuum. This method gave a rapid heating rate, permitting the use of short aging times. In some cases, particularly for the longer aging times at the higher temperatures, samples were sealed individually in quartz tubes in high

Jan 1, 1964

By J. L. Brimhall, R. A. Huggins

The structure of deformed internally oxidized alloys of siluer- cotztcrining magnesium and copper-containing aluminum in was studied by thin-film transrrzissiotz electron microscopy. With low to moderate amounts of stvain, the deformation structure in t11e dispersion-hardened alloys was found to consist of a high density of dislocations arranged it a random distribution or in a very fine, but poorly defined, cell stucture, depending on the fitness of the dbsbersion and amount of deformation. 112 contrarst, both pure copper and silver show relative1y Large, distinct cell structures. The particular structures in the alloys are believed to result from particles acting as both dislocaliot~ sources and deflector-s. The Inck of a pvorzolrr~ced deformation texture tr~ regiotzs qf' seoere loctll plastic curvature after heavy deformation can also be traced to the formation of clislocntions on many slip systemes and a lack 01 local concentrations of dislocations of predominantly one sign. THE presence of fine dispersions of a second phase has long been known to have a strong influence upon the mechanical properties of solids. Until recently, the influence of particles on the deformation mechanisms has been assumed to be solely that of barriers to dislocations. This is seen in the classic models of edge dislocations being restrained by the particles.1 4 There is, however, considerable evidence that this is not their primary effect, and that the particles can have a large influence on the defect structure generated by plastic deformation. The presence of particles causes changes in the surface topography observed after deformation. In overaged precipitation-hardened materials containing hard, noncoherent precipitates, fine intersecting slip lines are found after deformation of single crystals. indicating the activation of many slip systems. This has been extensively observed in the A1-Cu systen;, both by optical microscopy and replica electron microscopy.'"13 In some of the observations. the slip lines were seen to extend between the particles. Similar observations of extremely fine slip lines or the apparent absence of normal slip lines have also been found in A~-M~."

Jan 1, 1965

By John D. Verhoeven, Edward E. Hucke

An experimental technique has been developed for the measurement of the rate of electrotransport to a precision of 1 pct in the molten Bi-Sn system. Results are presented across the phase diagram from 30°C above the liquidus to 520°C. A phenomenological description is presented and the data on Bi-Sn are thereby converted to the effective charge, Analysis of the data indicates the true charge of the migrating tin species in bismuth to be +1.8 at 500°C. The data agree well with the recent work of Belashchmko. fieldintensity. The resistivity of the molten Bi-Sn system is also presented. WHEN an electric field is applied to a metal, a relatively large current is produced due to the ease with which electrons move within the metal. The electric field also produces a force on the ions which might cause them to migrate. Such a migration of metallic ions has been detected under certain conditions. This electromigration of the metallic ions will be referred to herein as electrotransport. The study of electrotransport in metallic systems has a rather long history dating back to the initial work of Gerardin1 in 1861. General reviews of electrotransport in liquid and solid metals have been published by Schwarz,2 Jost,3 Seith,4 and Heumann.5 In reviewing the literature it is apparent that the theoretical developments are not yet complete. The difficulty arises in describing the momentum transfer between the migrating ions and the electrons. In addition, there is a lack of good quantitative electrotransport data at high temperatures, especially in liquid metal systems. This work was undertaken to establish quantitative electrotransport data in a liquid metal system which might serve as a critical test of the theoretical developments. The Bi-Sn system was chosen for analysis, and the rate of electrotransport was determined as a function of temperature and composition. THEORETICAL CONSIDERATIONS If all of the atoms of a metal are considered to be positively charged due to the loss of electrons to the

Jan 1, 1963

By E. J. Whittenberger

OVER the past two decades, the Cr-Ni stainless steels, popularly termed 18-8 steels, have been used in ever increasing amounts in the aircraft, automotive, chemical, transportation, and building industries.' The contribution of nickel to these steels is associated with its strong austenite forming tendencies which assure good hot and cold forming characteristics, and with its beneficial influence upon corrosion resistance, especially in oxidizing acids. The adjustment of the chromium and nickel contents has been used advantageously in controlling the rollability and the response of the mechanical properties of these steels to cold reduction. With the advent of the jet age and the government stockpiling of nickel, considerable emphasis has been placed upon the development of satisfactory low nickel or nickel-free substitute austenitic stainless steels, especially for nonmilitary applications.2 Fer-ritic 17 pct Cr (AISI Type 430) stainless steel has been effectively substituted for the austenitic grades in applications with mildly corrosive exposure. However, the limited formability and ferromagnetic behavior of this grade do not permit its satisfactory use for many applications. To achieve better formability in a nenmagnetic steel and conserve nickel, a number of low nickel substitute austenitic grades of stainless steel have been developed in recent years. In most of these steels, manganese and nitrogen have been substituted for a portion of the nickel content, for example, 17 pct Cr-4 pct Ni-6 pct Mn (AISI Type 201), 18 pct Cr-5 pct Ni-8 pct Mn (AISI Type 202), and 16 pct Cr-1 pct Ni-17 pct Mn, all of which contain approximately 0.15 pct N.1 The precipitation of ferrite when large ingots of these Cr-Ni-Mn-N steels are heated to temperatures high enough for conversion to slabs on conventional universal slabbing mills has seriously affected the hot workability of these steels. This has been especially true in the case of the 16 pct Cr-1 pct Ni-17 pct Mn (sometimes referred to as 15 pct Cr-1 pct Ni-15 pct Mn) composition." Because it is possible that little, if any, nickel will be available for nonmilitary stainless steel applications in the event of a national emergency, a need has existed for a nickel-free austenitic stainless steel containing hot and cold forming characteristics similar to 18-8 steels and corrosion resistance at least comparable to the 17 pct Cr ferritic steel. The aforementioned deleterious effect of ferrite upon the hot working characteristics of the 16 pct Cr-1 pct Ni-17 pct Mn, steel indicates the importance of establishing the austenite-austenite plus ferrite phase boundaries as the first step in the development of nickel-free or low nickel substitute steels. This paper presents the data collected in an elevated temperature constitutional study of the Cr-Ni-Mn-N system at the South Works of the United States Steel Corp. Experimental Procedure The 300 compositions used in the investigation were melted in a 26 Ib induction furnace and cast in 3 14 in. diam by 18 in tall hot-tcpped ingot mo1ds.

Jan 1, 1958

By W. L. Phillips

The plastic properties of lithium fluoride and magnesium oxide under compression were investigated in the temperature range 25° to 1000°C. At the higher test temperatures, the critical resolved shear stress and the rate of work-hardening of both materials decreased. At the same time, the number of stress lines decreased and the individual stress lines became wider. The density of dislocations decreased for a given strain the higher the test temperature for lithium fluoride. The decrease in the critical resolved shear stress as a function of temperature could be fitted by the equation 7 = Toe-KT. THE influence of temperature on the stress-strain curves of a variety of metal single crystals has been studied for a wide range of temperature.1"5 In general, it has been found that both the critical resolved shear stress and the rate of work-hardening decrease rapidly with increasing temperature and fall to a value of essentially zero well before the melting point is reached. AS the test temperature is increased, the density of slip lines has been found to decrease, while the width of the individual lines increases. Recently, Gallagher,' Graf et al.,7 and Pate1 and Alexander8 have found that single crystals of germanium and silicon, which have a covalent bond, can be plastically deformed at elevated temperatures. In compressing germanium it has been found that the strain-hardening coefficient decreased very rapidly as the temperature was increased. The coefficient did not tend to zero, however, as the melting point was approached. The plastic properties of ionic crystals at elevated temperatures have not been extensively investigated. In the only work previously reported Tamman and salge9 and Theile10 have shown that the yield point of sodium chloride single crystals tested in tension and compression decreased slowly with increasing temperature, falling to zero at the melting point. As the temperature was increased, they found a substantial increase in the amount of plastic deformation that could be sustained before fracture; and at temperatures above 400°C in tension tests there was an obvious necking which produced local extensions of up to 3000 pct. The purpose of the present work is to extend the knowledge of high-temperature deformation to the ionic crystals, lithium fluoride and magnesium oxide. The following were investigated: 1) The gross shape of the stress-strain curve at several temperatures. 2) The change in the critical resolved shear stress as a function of temperature. 3) The appearance of slip bands and the density of dislocations as a function of strain and temperature. EXPERIMENTAL TECHNIQUES The lithium fluoride and magnesium oxide used in this investigation were purchased from the Harshaw

Jan 1, 1961

By C. A. Bruch, W. E. McHugh, R. W. Hockenbury

Commercially pure molybdenum specimens were irradiated in the Materials Testing Reactor for an estimated exposure of 1.9 to 5.9x10 20 thermal nvt. Prior to irradiation, the material was ductile in the tension test; whereas after irradiation, it was brittle. The results of tension tests conducted at various temperatures revealed that the transition temperature for this material had been increased from —30' to +70°C as a result of the radiation exposure. From metallographic studies, it is concluded that the embrittlement is due to submicroscopic changes which raise the flow stress-temperature curve of the material. PRIOR to ten years ago, the bombardment of metals with high speed heavy particles such as protons, deuterons, a particles, and neutrons was primarily of academic interest. These particles existed in extremely small numbers in a few laboratories and only under very special conditions. With the introduction of the nuclear power reactors, these particles are now available in enormous quantities and it has become important from a practical standpoint to learn how well metals withstand severe reactor radiations. The principal radiations of concern in reactors are neutrons and y rays, since the heavier charged particles exist only in limited regions of reactors. Seitz,' in a theoretical approach, has shown that all of these high energy particles, except y rays, have enough energy to knock atoms from lattice sites and that these knocked-on atoms have enough energy to cause additional displacements of neighboring atoms. The result of this process would be a lattice containing many imperfections in the form of interstitial atoms and vacancies. Hence, it would be expected that the properties of metals can be changed by reactor radiations, and such has been found to be the case. Only a limited amount of data have been published in the open literature,2,3 and these data have been for relatively low integrated-neutron-flux exposures. In general, one effect of reactor radiations on the mechanical properties of metals has been to increase strength and decrease ductility. It is now possible to irradiate specimens in the Materials Testing reactor at much higher fluxes and to higher integrated exposures than previously possible.' The data which are being presented here describe the effects of a relatively high exposure on some mechanical properties of molybdenum. Experimental Procedures Material: The molybdenum used in this investigation was obtained from the Climax Molybdenum Co. The two heats from which the material originated were melted under a vacuum of 5 to 30 microns and cast in 7 in. diam water-cooled copper molds. One ingot contained 0.061 pct C and the other 0.066 pct. Both ingots were hot worked by extrusion and rolling into % in. diam rods, after which they were annealed and straightened. The rods were subsequently heated to 1100°C in a hydrogen atmosphere and swaged to ½ in. diam rods at the Research Laboratory of the General Electric Co. The resulting material had an average hardness of 264 VPN, or 99.2 Rb, and had an average of 5000 grains per sq ml in the transverse section, Test Specimens: Substandard-size tensile specimens were prepared according to the specifications shown in Fig. 1. These specimens were used also for hardness measurements. The metallographic specimens were small disks which were polished, etched, and photographed at X1000 prior to irradiation. The field studied was

Jan 1, 1956

By W. H. Class

The embrittling effects of oxygen, ozone, nitrogen, air, and surface residues, on NaCl has been investigated. The embrittlement by ozone and oxygen was found to be associated with the formation of a NaClO3 surface compound. In these cases the initial crack that was responsible for fracture (in a bend test) always nucleated at the corners between the tension and side faces. The behavior of air was very erratic and on certain days did not produce enzbrittlement. During these periods, crystals that had become embrittled by the ozone treatment completely recovered their ductility after a short exposure to the ambient atmosphere, It was established many years ago1 that considerable ductility could be obtained in NaCl single-crystal specimens if the crystal surfaces were dissolved in water either during or immediately prior to the test. The original interpretation of this effect by Joffe attributed the enhanced ductility to the removal of surface microcracks by dissolution. Later investigations2'3 have suggested that the exclusion of air from the specimen surface is the criterion for extensive plastic flow prior to fracture. The air em-brittlement in this later work was attributed to the diffusion of gaseous atoms into the surface layers of the crystal, thereby impeding the movement of dislocations. This model satisfactorily accounts for the reembrittlement observed after further air exposure subsequent to the water dissolution treatment. However, the situation has recently become more complex by the observations in several laboratories4-t that under certain conditions air exposure does not impair the ductility of NaC1. It has also been recognized5 that improper drying operations after water dissolution can leave surface precipitates that lead to embrittlement. Cleavage defects on as-cleaved crystals can often be another source of embrittlement. In the present work the effect of the gaseous atmospheres nitrogen, argon, air, oxygen, and ozone, on the ductility of rock salt was studied extensively. The embrittlement resulting from oxygen and ozone exposures was found to be associated with the formation of a NaC1O3 surface film. It is suggested that certain atmospheres, one of which often can be ambient air, which inhibit the formation or favor the decomposition of this compound, can promote ductility. Thus one aspect of the Joffe effect is certainly related to the removal of surface compounds or complexes by water dissolution. The effect of surface precipitates that remain after drying operations and of cleavage defects were also studied. In neither of the latter cases was the embrittlement as severe as that found with a NaClO3 surface layer. PROCEDURE AND SPECIMEN PREPARATION The nature of the embrittlement produced by the agents mentioned above was studied by means of microscopy, mechanical testing, and X-ray diffraction. Specimens were cleaved from large crystals of optical quality sodium chloride obtained from the Harshaw Chemical Co., and, except for those tested in the as-cleaved condition, were given a 15- to 20-sec immersion in distilled water followed by a rinse in absolute methyl alcohol. The specimens were then blotted on a soft, absorbent paper, and dried by a few seconds exposure to a stream of warm, dry air. Such a procedure was found to give a control surface which was microscopically free of residues. (A few crystals were intentionally painted with a concentrated NaCl solution in order to investigate the effect of surface residues). All specimens were of 0.140 sq in. cross-section. Crystals prepared in the above manner were immediately placed in a gas train where they could be exposed to the desired gases for preselected periods of time. For the oxygen and nitrogen exposures, pure reagent-grade gases were employed. The ozone was provided in the form of an ozone-oxygen mixture (approximately 10 pct ozone) prepared by passing commercial grade oxygen over a strong ultraviolet light source. All gases were dried prior to their introduction into the train. Since argon was found to be completely inert in its behavior (i.e., residue-free specimens that were exposed to argon were not embrittled), it was periodically utilized to check the control specimen surfaces as well as the condition of the gas train used for aging the specimens. After exposure to the gaseous media in question, the crystals to be used for the measurement of the strain to fracture were transferred from the gas train to a protective oil bath (without further exposure to the atmosphere) where the tests were conducted in three-point bending. The apparatus was so adjusted that the load could be applied at a constant, continuous rate. Other Snecimens from the gas train were deformed

Jan 1, 1962

By W. F. Carew, F. A. Crossley

IT has been reported that the Ti-8 pct A1 alloy is ductile as water quenched from 800°C but brittle as annealed at 650 °C." The present, somewhat limited, investigation was undertaken to discover the cause of the embrittlement. In order to evaluate to some extent the continuity of the embrittling phenomenon, alloys of 6, 8, and 10 pct A1 were studied. Subsequent to the completion of most of this work, Ence and Margolin reported that a Ti,A1 phase exists and that two or more unidentified compounds may exist in the Ti-A1 system.' Materials, Equipment, and Techniques The alloys were prepared using Kroll process sponge of 124 Bhn hardness. In addition, some 8 pct A1 material was made with iodide titanium. The sponge-base alloys were prepared as melts of 4 lb or more by double arc melting. The iodide Ti-8 pct A1 alloy was prepared as 200-g buttons. The alloys were forged at temperatures of 980" to 1150°C. Results of chemical analyses are given in Table I. A Baldwin-Southwark 60,000-lb capacity tensile machine, equipped with an autographic stress-strain recorder, was used for the tensile tests. Standard tensile test specimens, 0.252 in. diam, were used. Standard Charwy V-notch impact specimens were tested using a -kiehle machine. specimens were sealed in evacuated Vycor bulbs for heat treatment. Powder samples for Debye-Sherrer anal- ysis were prepared by filing and screening through 325 mesh. The —325 mesh fraction was taken in an effort to concentrate a microstructural constituent assumed to be less ductile than the a phase. The powder samples were stress relieve2 by annealing

Jan 1, 1958

By James R. Cost

The increasing emphasis upon the use of refractory metals has resulted in a closer look at some of the properties of these materials. In the course of a study of the Nb-N system it became necessary to re-examine one such property, the spectral emissivity, e. Experiments were performed in order to determine e for solid niobium as a function of both temperature and nitrogen content. The results of these experiments, which indicate a small but significant correction to the spectral emissivity of pure niobium, are reported herein. In addition, data on the total emissivity, et, of niobium and the spectral emissivity of the nitride Nb2N are given. To this author's knowledge, neither of these emissivities are as yet reported in the literature. Previous studies of the spectral emissivity of niobium have been few. In 1915, Burgess and Waltenburgl obtained a value of 0.49. Whitney? in 1935, used a Mendenhall V to obtain the commonly accepted value of 0.374. A recent investigation of sintering of niobium graphically reported a value of about 0.36= using a solid block of the metal with a blackbody hole drilled into it. In the present experiment a method similar to that of Worthing4 was used. An 8-in. long and 3/16 in. diam hollow tube was formed from smooth surfaced 0.0013-

Jan 1, 1962

By C. H. Li, R. J. Stokes, T. L. Johnston

Sodium chloride crystals are brittle in the presence of surface microcracks. Water immersion leads to an enhancement of ductility which is retained indefinitely in dry air providing the crystal is dried without leaving a surface precipitate. Storage in a damp atmosphere results in a surface reaction and consequent rembrittlement. Although elimination of surface flaws in ionic solids does not necessarily enhance ductility, there is always a change in the location of the fracture origin. EVER since the original experiments of Joffel there has been controversy over their interpretation and no satisfactory generalized explanation has yet been given. It is generally admitted that when sodium

Jan 1, 1961

By James A. Roberson

THE mechanical behavior of molybdenum has become a matter of considerable interest in recent years because it has a reasonably high strength at high temperatures. Various aspects of its fatigue behavior have been investigated previously,1-3 and the results can be summarized as follows. Recrys-tallized molybdenum exhibits a fatigue limit which decreases continuously with increasing temperature. The ratio of fatigue-limit stress to ultimate tensile stress is high (0.6 to 0.8) and reasonably constant. The present work was undertaken to determine the effect of variations in environment on the fatigue of molybdenum stressed in fully reversed axial tension compression. In order to provide a basis to which these data could be compared, a complementary series of fatigue tests were made in vacuum. All of the specimens used were made from one mill lot of unalloyed molybdenum which had been vacuum-arc melted, worked down to 1-in.-diam bar, re-crystallized, then warm-worked to 5/8 in. diam. The interstitial content by weight was as follows: C—0.022 pet, 02-0.0026 pet, Hz-0.0001 pet, and N20.0002 pct. The average grain diameter in the transverse direction was about 0.035 mm, and the average grain length was about 0.15 mm. Typical tensile-test data are shown in Table I. None of the specimens tested exhibited an upper yield point.

Jan 1, 1965

By H. Warlimont

Precipitation of cementite plates from carbon-rich austenite gives rise to localized formation of martensite in the matrix next to the precipitate upon quenching. The growth of this martensite is urmsually restricted. A distinct lattice relationship is found between this martensite and the cementite phase. It is concluded that the martensite is nacleated in the region of lowest carbon concentration at the austenite-cementite integace, with low-energy matching to the cementite lattice. The restriction of the growth of the martensite phase to the vicinity of the cementite plates can be explained by misfit in the austenite -martensite glissile interface and the uphill carbon gradient in the austenite. The investigation was carried out by light- and electron-microscopy and by electron-diffraction of thin foils. THE precipitation of cementite from carbon-rich austenite gives rise to a localized formation of martensite in the matrix next to the precipitate upon quenching. This behavior has been described previously by A. B. Greninger and A. R. Troiano1 for a 1.78 pct C steel ("pseudomorphic martensite"), and by A. Hultgren2 for a Fe-0.99 pct C—5.20 pct Mn steel. By measuring the axial ratio of the martensite phase,' it was found that the carbon content of this martensite was lower than that of the martensite which formed without prior partial transformation to cementite. Therefore, it was concluded that lowering of the carbon concentration in the matrix next to the precipitate raised the M, temperature locally and thus led to nucleation of martensite at the ce-mentite-austenite interface. However, the restriction of the growth of the martensite phase to the vicinity of the cementite plates cannot be explained by localized carbon impoverishment alone. Under ordinary conditions a martensite plate which has been nucleated in a favorable site can continue to grow until it encounters a physical barrier, or until it encounters a compositional barrier in the matrix, where the total free-energy change for the reaction is not negative, since it has been shown by numerous experiments that the activation energy for growth of ordinary martensite is virtually zero.' An investigation was conducted by transmission electron microscopy and electron diffraction to study this extraordinary martensite. It was expected that crystallographic in addition to compo- sitional conditions caused this abnormal mode of martensite formation. MATERIAL AND PROCEDURE An Fe-C-Mn alloy containing 1.15 pct C and 5.1 pct Mn was used for most of the experiments. For metallographic work, specimens 15 by 15 by 3 mm were used. For preparation of thin films, the initial specimen size was 15 by 15 by 0.7 mm. The heat treatment of each specimen consisted of austenitizing for 1/2hr at 1100'~ in an argon atmosphere, subsequent isothermal holding in a lead bath at one of a series of different temperatures, and, finally, quenching into brine at room temperature. For metallographic examination, the specimens were mounted in bakelite (slight tempering effects resulted from the heat in the mounting press) ground, polished, and etched in nital. Thin films for transmission electron microscopy and electron diffraction were obtained by grinding the specimens to approximately 0.2 mm thickness and subsequent electrolytical thinning. The orientation relationships were evaluated from sets of electron micrographs and selected-area electron diffraction patterns of single units of the transformation products and the adjacent matrix. RESULTS In the alloy which was used for the experiments, proeutectoid carbide precipitates over a wide tem-

Jan 1, 1962

By R. G. Hudson, L. Yang

In electrochemical separation of metals, it is necessary to control the potential applied between the electrodes so that only the desired electrode reactions can occur. A knowledge of the minimum potential needed for a given electrode reaction to take place continuously is therefore pertinent to the success of the process. In molten chloride systems at high temperatures, activation polarization is believed to be small,1,2 so the minimum potential needed for the electrolytic decomposition of a molten metal chloride MC1n (n = valence of the metal ion) is therefore essentially the equilibrium electrode potential E of the metal-chlorine galvanic cell in the solution. If the decomposition products are pure M and chlorine at a pressure of p atm, E*Eo-rt/nf in [i] Since EO (the standard electrode potential of MCln) is a constant at a given temperature and R (the gas constant), and F (the Faraday's constant) are all constants, the variation of E with the electrolytic bath conditions is largely determined by the effect of the latter on the activity of the metal chloride amcln (standard state = pure MC1,). Measurement of E and study of how amCin varies with temperature and concentration, the nature of the solvent, and that of the coexisting solutes are therefore pertinent in the selection of optimum operating conditions for the electrochemical separation of metals. Because of its low melting point, high decomposition potentials of its components, and the low solubility of heavier metals in it, the LiC1-KC1 eutectic melt is a useful solvent and has been used in the electrodeposition of Mo,3Ce,4 and u5 metals. Senderoff and Brenner3 measured the potentials of Zn/Zn++, Fe/Fe++, Cu/Cu+, Mo/Mo+++, and Ag/Ag+ against an Ag/AgCl (pure) reference electrode at 600°C and a concentration of 4.1 mole pct of each chloride and came to the conclusion that complex ion formation occurred in some of the melts. Laitinen and LiUe gave an electromotive force series at 450°C for a number of {Metal/Metal ions (unit activity)) electrodes in LiC1-KC1 eutectic melt, the {pt/pt++ (unit activity)) electrode being chosen as the reference. Walker and Danly7 studied the ther-modynamic properties of NiC12 in LiC1-KC1 eutectic melt over a wide range of temperatures and concentrations by measuring the electrode potential between a nickel electrode and a chlorine electrode in the melt. Since potential measurements made by using the chlorine reference electrode are of more direct significance both in the study of electrochemical separation and in the evaluation of the thermodynamic properties of the melt, it is therefore decided to measure the electrode potentials of cells of the type {M/MCin (mole fraction = N) in LiC1-KC1 eutectic melt/Cl2 over a range of N values and temperature for a number of metal chlorides. The results should indicate the order by which the various metals plate out on the cathode and how this order is affected by temperature and the concentration of the metal chloride in the solu-

Jan 1, 1960

By C. A. Siebert, D. J. Girardi

PRACTICALLY every metallurgical process in-volves, at some stage or another, the contact of a metal with a gas. Because of this, gas-metal re-actions are of great practical importance and have been subjected to numerous investigations. It has long been recognized that the presence of cuprous oxide in liquid copper has an important effect on its casting characteristics and .physical properties. This has led to the desirability of determining the quantitative relationships between cuprous oxide in the liquid copper and the usual gases present during processing. Such data are not only of practical importance but also of a theoretical interest in that they provide a means of applying the principles of physical chemistry to problems in applied metallurgy. The object of this investigation was to determine the quantitative relationship at equilibrium between the gases carbon monoxide and carbon dioxide and the cuprous oxide content of liquid copper. The reaction and its equilibrium constant may be expressed as follows: 2 Cu (liq) + CO2 (g) = Cu2O + CO (g) acu2o X aco/a2 cu X aco2 Here the underlined symbol Cu2O designates cuprous oxide dissolved in liquid copper and (a), the activity of the various constituents. The activities of carbon monoxide and carbon dioxide are assumed to be directly proportional to their re- spective partial pressures and the activities of cuprous oxide and copper are taken to be proportional to their respective mol fractions. The equilibrium constant may then be expressed as follows: K2 = Ncu2o X Pco [Ncu]2 X Pco2 where N = mol fraction The solubility of carbon monoxide and carbon dioxide in liquid copper is a rather controversial subject.'-' A review of the literature is given by 0. W. Ellis.' It appears that carbon monoxide and carbon dioxide are both only very slightly, if at all, soluble in liquid copper. Volskii and Slobodskoi5 determined the equilibrium between carbon monoxide, carbon dioxide, and liquid copper at 1100°C. Their results show a higher cuprous oxide content for a given CO/CO2 ratio than found in the present work. The system hydrogen, water vapor, and liquid copper was investigated by Allen and Hewitt8 over the temperature range of 1090" to 1350°C. Equilibrium values for the system carbon monoxide, carbon dioxide, and liquid copper calculated from these data agree reasonably well with the present work. Materials and Procedure The copper used was oxygen free, designated as OF and analyzed as 99.98 pct copper with no appreciable amount of any one impurity based upon spectrographic determinations. The carbon dioxide was cylinder gas averaging about 99.95 pct CO2 with air as the major impurity. The carbon monoxide was produced by passing carbon dioxide over heated charcoal. Alundum combustion boats were used as containers for the liquid copper. No appreciable reaction took place between the copper and the alumina. This was evident from the fact that the copper sample after a run did not ordinarily adhere to the bottom of the boat and that the

Jan 1, 1951

By Benny J. Nelson

AS a part of the fundamental research program of Aluminum Research Laboratories, some data were obtained on the ternary system Mg-Al-Mn. As very little information on the magnesium corner of this diagram has heretofore been published, it seems desirable to make available the values found for the liquidus and solidus surfaces of this system. Procedure The settling procedure was used for the determination of the liquidus compositions. Metallo-graphic examination of quenched samples, and stress-rupture upon incipient melting, were used for the solidus determinations. The settling procedure has been described in a previous paper.' Briefly, this method involved saturating the alloy with manganese at a temperature substantially above that at which the sohbility was to be determined, then cooling the melt to the latter temperature, and holding it at that temperature for a substantial period of time. Samples for analysis .were carefully ladled from the upper portion of the melt at hourly intervals during the holding period. After the ladling of each sample, the melt was stirred to redistribute some of the manganese that had already settled, because it appeared that when the latter particles of manganese again settled, they aided in carrying down more of the manganese and thus hastened the attainment of equilibrium. The melts were prepared and held in a No. 8 Tercod crucible holding approximately 4 lb of metal. The manganese was added either in the form of a prealloyed ingot (Dow M) containing about 1.5 pct Mn or by the use of a flux (Dow 250) containing manganese chloride. In calculating the flux additions, it was assumed that the manganese introduced would be equal to 22 pct of the total weight of the flux. Temperatures were measured with an iron-constantan thermocouple enclosed in a seamless steel tube, the lower end of which was welded shut. This protection tube also served as a stirring rod. The samples ladled from the upper portions of the melts at the various intervals were analyzed for aluminum, manganese, and iron. When making the alloys which were to be used for the determination of the solidus, 2½ in. diam tilt mold ingots were cast, scalped to 2.0 in. in diam, and extruded into ? in. diam wire. The principal impurities in the melts for this investigation were iron and silicon; their total not exceeding 0.03 pct. Portions of the wire, approximately 2 in. in length, were enclosed in stainless steel capsules for protection from the atmosphere. Bundles of these capsules, with a dummy capsule containing an iron-constantan thermocouple, were heated inside a large steel block (acting as a heat reservoir) in a closed circulating-air type electric furnace. At ap- propriate times, the capsules were removed and quenched in water. The wires were examined metallographically to determine the temperature of initial melting. Short times at temperature were used at the beginning for wire specimens of all alloys to obtain quickly the approximate temperatures at which melting could be first observed. When approximate solidus temperatures had thus been determined, equilibrium heating was attempted. This equilibrium heating consisted of an 8 or 16 hr period at a temperature, about 50 °F below the lowest temperature at which melting occurred when short heating cycles were used, followed by further heating for 1 hr periods at consecutive 10" higher temperatures. The theory for the method of stress-rupture at incipient melting has been well covereda and its limitations are recognized. Thus, if the interfacial tensions are such that the first minute quantity of liquid is "bunched up" at the grain boundary junctions instead of spreading out along the grain boundaries,³ temperatures higher than the solidus are required before melting will be manifested by rupture of the specimen. This point will be elaborated later. Specimens of the wires with a reduced section (approximately 1/16 in. diam) were suspended vertically in a tubular furnace. The setup used is shown in Fig. 1. The clamp holding the specimen was made from alumel thermocouple wire and the thermocouple was thus completed across the specimen by attaching a chrome1 wire to its lower end. Temperatures were read from a Speedomax recorder used in conjunction with a calibrated thermocouple. The small weight attached to the specimen and a vibrator attached to the furnace tube, to aid in distributing the molten constituent along the grain boundaries, were used to bring about rupture at a temperature closely approximating the solidus. The specimens were heated at a rate of about 5°C per min. The rupture of the specimens was indicated both by sound and by the action of the recorder. An argon atmosphere containing a small amount of SO² was used for protection of the specimen. The assembly was taken out of the furnace immediately following rupture and the specimen removed. Some of the broken specimens were examined metallographically and will be referred to later. Results and Discussion Fig. 2 shows a set of typical time-composition curves for liquid samples of the Mg-Al-Mn alloys used for the settling tests. The data as presented

Jan 1, 1952