Search Documents

By R. O. Williams

A recent article by Chernock, Singer, Mueller, and Beck 1 which supports the use of the integral of I sin $ d$ for comparing fiber texture data does not settle what happens to I sin ø as ø approaches zero, where I is the diffraction intensity for poles oriented 0 deg from the fiber axis. They indicate that they believe that it should approach some constant value (that is, I increases without bound) and the fact that in reality it does not was a result of the diffraction

Jan 1, 1960

By J. R. Mihalisin, J. S. Iwanski

The response of Inconel "700" to heat treatment has been studied by light and electron microscopy combined with X-ray and electron diffraction techniques. A heat treatment which vesults in low ductility for this alloy appears to be associated with the formation of MC carbide in a Widmanstdtten distribution. This type of precipitation can be suppressed by suitable heat treatment with concurrent increase in ductility. Various other phases precipitated in this alloy are also identified. RECENT studies of commercial nickel base su peralloys have demonstrated the importance of the morphology of carbide phases upon physical properties.' For example, empirical heat treatment studies applied to Nimonic "80" and Inconel "X" have resulted in prescribing double aging treatments for optimum physical properties. These treatments have subsequently been related micro-structurally to grain boundary carbide morphology.2 The purpose of this study was to obtain information about the morphology and identity of some of the phases precipitated in Inconel "700" after heat treatment. It was hoped that some correlation could be made of micro structure with heat treatment similar to that observed with Inconel "X" and Nimonic "80." EXPERIMENTAL PROCEDURE Specimens were obtained from a hot-rolled bar of Inconel "700" of the following composition: C Mn Fe S Si 0.10 0707 0.42 0.007 0.12 Cu Cr -A1 -Ti- Co Mo Ni 0.02 -14.90 TM 2.22 27.61 2.92-- Bal. Specimens were prepared in the following heat-treated conditions: (A) 2275°F for 2 hr WQ (B) 2275°F for 2 hr WQ + 2000°F for 1 hr (C) 2275°F for 2 hr WQ + 1600°F for 48 hr. (D) 2275°F for 2 hr WQ + 2000°F for 1 hr + 1600°F for 48 hr. Empirical stress-rupture studies had shown that treatment (D) resulted in optimum stress-rupture life and ductility. Treatment (C), although giving a good aging response, resulted in low ductility. Treatments (A) and (B), respresenting individual. steps in treatments (C) and (D) were added here for microstructural comparison studies. The procedure was to make an optical and electron microscopic investigation supplemented by X-ray diffraction analysis of electrolytically extracted residues. Electron diffraction studies were made utilizing selected area diffraction techniques with extraction

Jan 1, 1960

By C. G. Dunn, J. L. Walter

SILICON-iron .under certain conditions of processing and annealing will form a cube texture. The occurrence of this texture in thin tapes of silicon iron was first reported by Assmus, Detert, and Ibe.' They concluded that the cube texture in their material formed by a secondary re crystallization process. In the course of present investigations on the development of the cube texture and the mechanisms involved in its formation by secondary re-crystallization it was found that under certain conditions the cube texture was replaced by a cube-on-edge or (110) [001] texture. We call this phenomenon tertiary re crystallization since it follows secondary recrystallization. The secondary recrystallization occurs after primary recrystallization and a substantial amount of normal grain growth. It is the purpose of this paper to describe briefly the occurrence of tertiary recrystallization and the structure and texture prior to and after tertiary recrystallization. The primary and secondary recrystallization structures and textures are the subject of another study and will be referred to briefly in the discussion of results. Evidence will be presented for the view that the dominant driving force for tertiary recrystallization is derived from the surface free energy which depends on the crystallographic planes presented to the gas-metal interface. In the absence of boundary restraining forces (dispersed phases, thermal grooves, and so forth) a sufficiently large difference in surface free energy across a grain boundary would produce boundary migration away from the center of curvature of the boundary intersection line in the surface of the sample according to risher.2 Therefore, particular attention was paid to observation of the direction of motion of these surface boundary lines. Furthermore, measurements of the actual boundary curvatures could be used to estimate the driving force supplied by surface free energy. EXPERIMENTAL PROCEDURE Samples were prepared by hot and cold-rolling vacuum-melted ingots of iron containing 3 pct Si to strips 0.012 and 0.006 in. thick. The ingots contained less than 0.005 wt pct impurities. The rolled strips were cut into samples approximately 1 in. wide by 3 in. long and were electropolished to remove surface imperfections. All samples were annealed in a vacuum at a pressure of approxi-

Jan 1, 1960

By G. R. Wilms

In a recent investigation1 on the properties of chromium, and of Cr-10 wt pct W and Cr-5 wt pct Mo alloys at elevated temperatures, it was found that intercrystalline cavities developed in all of these materials during tensile creep at 950°C, and that the cavities led to intercrystalline fracture. There were some interesting differences, however, between the cavities produced in the pure metal and those in the alloys; these differences, moreover, were associated with a difference in ductility. The relevant conditions of creep testing are specified in the captions to Figs. 1 and 3. Chromium showed the presence of quite large intercrystalline cavities, Fig. 1, and these were more or less randomly distributed around the boundaries. The chromium alloys, on the other hand, showed the presence of both small cavities and cracks at the grain boundaries, Fig. 3; it is apparent that the cracks are formed by the linking together of the small cavities. Moreover, the cavities and

Jan 1, 1960

By F. C. Langenberg, J. Chipman

New data on the distribution of silicon between slag and carbon-saturated iron at 1600oand 1700oC are presented which, in combination with previously published data, permit the determination of silica activities over a broad range of compositions in the CaO-Al2O3-SiO2 system. The distribution of silicon between graphite-saturated Fe-Si-C alloys and blast furnace-type slags in equilibrium with CO has been described in previous publications.1"3 In this past work the silica-silicon relation was established at temperatures of 1425" to 1700°C for slags containing up to 20 pct Al2O3. This paper presents the results of additional studies at 1600" and 1700° C which extend the silicon distribution data at these temperatures for CaO-A1203-SiO2 slags over a range from zero pct A12O3 to saturation with A12O3, or CaO.2A12O3. The upper limit of SiO, is set by the occurrence of Sic as a stable phase when the metal contains 23.0 or 23.7 pct Si at 1600" or 1700°C, respectively. The activity of silica over the expanded range is determined directly from the distribution data.3 Recently, 4-7 other investigators have studied the activities of SiO, and CaO, principally in the binary system, using different methods and obtaining somewhat different results. EXPERIMENTAL STUDY The experimental apparatus and procedure have been fully described in previous publications.1, 3 Six new series of experimental heats have been made, four at 1600° and two at 1700°C. Master slags of several fixed CaO/A12O3 ratios were pre-melted in graphite crucibles, and these were used with additions of silica to prepare the initial slag for each experiment. Slag and metal were stirred at 100 rpm and CO was passed through the furnace at 150 cc per min. The initial sample was taken 1 hr after addition of slag at 1600°C or 1/2 hr after addition at 1700°C. The run was normally continued for 8 hr at 1600°C or 7 hr at 1700°C, and the final sample was taken at the end of this period. Changes in Si and SiO2 content indicate the direction of approach to equilibrium, and in a series of runs where the approach is from both sides this permits approximate location of the equilibrium line. Fig. 1 shows the results of such a series of 15 runs at 1600°C for slags of CaO/Al2O3 = 1.50 by weight. Figs. 2 and 3 record other series at 1600°C and Fig. 5 a series at 1700°C with fixed CaO/Al2O3 ratios. The results of the experiments at 162003°C have been reported in part in a preliminary note.3 In the experiments recorded in Figs. 4 and 6, the slags were saturated with A12O3 (or with CaO.2A12O3 within its field of stability) by suspending a pure alumina tube in the melt during the course of the run. The final slag analyses were used to establish the liquidus boundaries8 in the stability fields of CaO.2Al,O3 and of A120,. ACTIVITY OF SILICA The free-energy change in the reaction has been calculated by Fulton and chipman2 from recent and trustworthy data including heats of formation, entropies, and heat capacities. The more recent determination by Olette of the high-temperature enthalpy of liquid silicon is in satisfactory agreement with the values used and therefore requires no revision of the result which is expressed in the equation: SiO, (crist) + 2C (graph) = Si + 2CO(g.) [1] &F° = + 161,500 - 87.4T The standard state for silica is taken as pure cristobalite and that of Si as the pure liquid metal. Since the melts were made under 1 atm of CO and were graphite-saturated, the equilibrium constant for Eq. [I] reduces to K1 = asi /asio2 The value of this constant is 1.77 at 1600°C and 16.2 at 1700°C. Through K1, the activity of silica in the slag is directly related to the activity of silicon in the equilibrium metal.

Jan 1, 1960

By R. E. Morgan, D. L. Douglass

The determination of phase relationships and solid-solubility limits can be performed by quantitative metallography in addition to the usual X-ray and metallographic techniques. For example, Beck and smith1 redetermined the ß/ß + ?, ß + ?/?, a/a + ß and a + ß/ß boundaries in the Cu-Zn system by measuring the volume fraction of second phase of several alloys and extrapolating the volume fraction-composition curves to 0 and 100 pct. A modification of this technique is suggested for certain alloy systems, in which it is not necessary to use several alloy compositions but merely one. A single two-phase alloy may be used to determine terminal solubilities in the following manner. The method consists of equilibrating samples of the alloy in a two-phase region adjacent to the desired solid solution, at three or more temperatures, quenching, measuring the volume fraction of second phase present, and applying an analytical treatment to calculate the unknown solid solution. However, two restrictions are inherent in this technique. They are: 1) only certain types of alloy systems are amenable to it, and 2) the general features of the system must be known. The first drawback to the new technique, i.e., that only certain types of systems may be studied, necessitates that the composition at one end of the tieline must either be constant with temperature or well established as a function of temperature. Either a pure metal or some intermetallic compounds fulfill the former. If it is assumed that the volume per gram-atom of a dilute solution is unchanged by the addition of element B to element A, the composition of the solid solution in equilibrium with the second phase may be determined by a material balance and is given by where X, = volume fraction of B in a solid solution Xc = volume fraction of B in compound c X = volume fraction of B in alloy f = volume fraction of second phase The composition by weight may then be determined by the use of tables in the Metals Handbook2 when the density ratio of the solid solution constituents is known. A possible alternative treatment involving the use of the lever rule is less precise than the above tech- nique. This may be used when the density of the solid solution is either known or may be calculated from X-ray data for several compositions. The following analysis is then made. The ratio of compound to solid solution (by weight) may be expressed as follows: x0 - x wc = xr-x = x0 - x r2i Xc -X where Wc = weight of compound w = weight of solid solution x, - alloy composition, weight percent x = unknown composition Xe = compound composition but where V, = volume of compound VA = volume of solid solution pc = density of compound p, = density of solid solution fc = volume fraction of compound fB = volume fraction of solid solution and fs = l -fc then If pc and xc are known, and f, is measured, then pB is the only unknown on the right side of Eq. [4]. The known densities of the solid solution can be plotted for various compositions and can then be expressed mathematically as a function of composition. The use of an expression of pB = f(x)reduces the equation to one unknown—the desired solubility. In the event that the densities are unknown, they may be calculated for various compositions from Vegard&apos;s law. The calculated values are then plotted and expressed analytically. The most accurate results are obtained for Eq. [4] when fc<< 1, i.c., when (x, -x,) - 0, &/l-f, - m; but as fc/l -fc - 0, (xl-x,)- (x, - x), and x - x,,. However, the accuracy with which fc can be measured decreases as f, decreases.3 Alloys for investigation must be selected by a compromise, which is based upon an error analysis of Eq. [4] and knowledge of the accuracy of volume fraction measurements. An examination of phase diagrams in the literature showed many which were amenable to the technique described here. The zirconium-copper system was selected in order to determine the solubility of copper in beta zirconium. Pieces of an alloy which was arc-melted three times were wrapped in tantalum foil and sealed under an argon atmosphere in Vycor tubes. The sealed samples were equilibrated at temperatures from 850" to 960°C for 3 weeks and quenched to room temperature by smashing the capsule in water. Several planes of polish were examined, and

Jan 1, 1960

By J. Chipman, J. C. Fulton

Reduction of Si from slag to carbon-saturated iron is a very slow reaction. The rate is nearly independent of stirring but is accelerated markedly by increased temperature. In a slag containing 45 pct SiO2, 38 pct CaO, 17 pct Al2O3, the energy of activation is approximately 130 kcal. AT temperatures of 1450" to 1600°C occurring in the hearth of the iron blast furnace, chemical reactions are normally expected to proceed with great rapidity. Many of the reactions of iron making are indeed quite rapid and attain a condition corresponding roughly to a state of equilibrium before metal and slag are tapped from the furnace. The one conspicuous exception is the reaction by which carbon in the coke or metal reacts with silica in the slag to deliver silicon to the metal. From the practical viewpoint the slowness of this reaction is indeed fortunate, for if it were fast enough to reach equilibrium during the time of contact, it would be difficult to produce pig iron of the desired low silicon content. The one other reaction which under certain circumstances can also be very slow is the transfer of sulfur from blast-furnace metal to slag. In their laboratory exeriments on this reaction, Hatch and Chipman found that at least 5 hr were required for the attainment of equilibrium in a small crucible and that the reaction was not accelerated by increasing the rate of stirring. Subsequently it was shown2 that the presence of a reducible oxide MnO greatly inhibited sulfur removal, and finally that SiO2 itself3 under some conditions has sufficient oxidizing Dower to interfere with sulfur transfer. The kinetics of sulfur removal are now rather well understood,4 and it has been shown3,5 that when the silicon content of the metal is high enough to prevent reduction of SiO,, the desulfurizing process is rapid. Thus the observations of slow removal of sulfur are associated with the coincident slow reduction of SiO2, a process which transfers both silicon and oxygen to the metal phase. It is, of course, the oxygen which interferes with sulfur removal. An explanation of the slowness of the silica reduction reaction has not been obtained. The sulfur transfer process has been shown by the authors5 to be at least partially transport-controlled in the absence of interference by silica. Under the experimental conditions. 99 pct of the total transfer at 1600" was accomplished within an hour. Under similar conditions the reduction of silica may not proceed half-way to equilibrium6 in 8 hr. It is scarcely imaginable that silica reduction could be transport-controlled when the slag contains 44 pct SiO2 and the metal about 1.4 pct C. The experiments reported here show definitely that it is controlled by a slow step or steps in the chemical reaction. One might expect to find such a slow step in the breaking of SiO bonds or in the slow removal of oxygen by carbon at the slag-metal or metal-crucible interface or by bubble formation. EXPERIMENTAL PROCEDURE The experimental procedure used in this investigation was similar to that used in the study of the kinetics of desulfurization.5 A sketch of the graphite crucible and stirrer used in the current work is shown in Fig. 1. The quantity of metal and slag used was adjusted so that the slag-metal interface was located between the top and bottom blades on the stirrer; the top of the slag layer was above the top blade. The stirrer shaft was hollow down to the metal level and served as thermocouple well or optical pyrometer target. Stirring speeds of 0 to 500 rpm were used. A carbon monoxide atmosphere was maintained in the furnace by flushing the gas over the slag surface, except in run No. 220 when it was bubbled

Jan 1, 1960

By A. E. Dwight

Lattice parameters were determined for eighteen equiatornic alloys of the CsCl-type structure, ten of which were previously un-reported. It was found that fomation of the CsCl-type structure in binary alloys of the transition elements is largely dependent on position of the elements in the periodic table. The relative size of the two elements was not found to be a controlling factor. A recent paper by Beck, Darby, and Arora1 corre-lates the occurrence of CsC1-type ordered structures with the position of the constituent elements in the periodic table for the first long period. It was also suggested that a definite increase in relative bond strength between unlike atoms occurred when, in binary alloys of iron-group elements, the other component is changed from a chromium-group element, to a vanadium-group element, to titanium. A later paper by Philip and Beck2 noted that the lattice contraction increased in the order CrFe, VFe, and TiFe. It was also noted by Philip and Beck2 that the lattice contractions of CsC1-type alloys decreased in the order: TiFe, TiCo, and TiNi, which is an apparent reversal of the contractions expected from the position in the periodic table. It was suggested that the increasing lattice contraction is an indication of increased stability, i.e., greater A-Bbond strength. The present investigation was carried out to determine whether the relation of the position in the periodic table to the formation of the CsC1-type structure was also correct for alloys involving the second and third long-period elements. A systematic search was made for CsC1-type structures among equiatomic alloys and for those found, the lattice contraction was determined. EXPERIMENTAL TECHNIQUE The elements Y, Gd, Ti, Zr, Hf, V, and Cb are designated the A group and the elements Mn, Re, Fe, Ru, Os, Co, Rh, Ir, Ni, Pd, Pt, Cu, Ag, and Au are designated the B group. Equiatomic alloys were prepared for 57 AB combinations. The alloys were arc melted in a multicrucible furnace3 in buttons ranging from 5 to 20 g. Chemical analyses were not made, as the charge weights agreed closely with those of the buttons after melting. The alloy buttons were homogenized at 800° to 900°C. Metal log raphic and X-ray specimens were prepared and heat treated at temperatures from 600° to 1200°C. Specimens for X-ray diffraction were usually ground to a powder in an agate mortar; however, needle-shaped solid specimens were used when the alloy was sufficiently ductile to permit their preparation. Diffraction patterns were taken with a Straumanistype Debye-Scherrer camera using filtered Cu or Co radiation. The lattice parameters were obtained in A by plotting the calculated a0 values against the cos29/sin 0 + cos2?/? function and extrapolating linearly to ?= 900. Metallographic control specimens were polished on cloth wheels with diamond paste and etched with various phosphoric and nitric acid reagents. RESULTS The eighteen equiatomic alloys listed in Table I gave evidence of a cubic structure with two atoms in the unit cell, although two of these cubic structures exist only at elevated temperatures and transform to a tetragonal structure on quenching. Nine of these eighteen alloys gave diffraction patterns with super-lattice lines showing that the structure is of the CsC1-type. The lack of superlattice lines in patterns of the other nine alloys may be attributed to the small difference in atomic scattering power of the components. Metallographic study indicates the occurrence of nine narrow single-phase fields at the AB composition. Any or all of these nine may also have a CsC1-type structure. The VFe alloy was found to have a CsCl-type structure by Philip and Beck2 through the use of CrKa radiation (for which the scattering factor of V is anomalously low), whereas the Cu radiation used

Jan 1, 1960

By C. H. Li, R. J. Stokes, S. H. Bendel, J. A. Sartell, T. L. Johnston

The mechanism of the oxidation of high-purity copper has been studied at temperatures from 500° to 981°C employing gravimetric, high-temperature microscopic and inert marker techniques. An investigation of the adhesion of copper oxides was also made. The oxidation of copper is found to be parabolic at all temperatures. It is concluded that the controlling mechanism is the outward diffusion of CU+ ions through the Cu2O layer, but the mechanism of diffusion is modified by the state of compressive stress in the oxide layer at the oxidation temperature. At temperatures below the transition from elastic to plastic behavior of Cu2O the growth stresses reach a value sufficiently high to cause CuO whiskers to be extruded. The extrusion of whiskers results in the injection of a large number of vacancies into the CuO. The Cu20 layer grows by the advance of the CuzO/CuO interface into vacancy-rich CuO. Since there is an adequate supply of non -thermally created vacancies, the activation energy for oxidation is that required to move the Cu+ ion through the appropriate saddle point to a neighboring vacancy, which has been determined to be 20,000 cal per mole. At temperatures at which the Cu20 can deform plastically the stresses are never high enough to cause whiskers to form. thus vacancies must be supplied by themal activation and as a result the activation energy increases to 40.000 cal per mole. ALTHOUGH extensive studies of the oxidation kinetics of pure copper have been made in the past. the mechanism has received relatively little attention. As a result, certain features of the kinetic data have not been satisfactorily explained&apos; For example, several workers1,2 have reported that the activation energy for oxidation in the range from 500° to 700° C was about 20,000 cal per mole whereas that above

Jan 1, 1960

By Oliver Bowles

Slate is a fine-grained rock that has a more or less perfect natural cleavage, permitting it to be split readily into thin, smooth sheets. According to a definition established by the American Society for Testing Materials, slate is "a microgranular crystalline rock derived from argillaceous sediments by regional metamorphism and characterized by a perfect cleavage entirely independent of original bedding, which cleavage has been induced by pressure within the earth." Origin and Character Slates have originated from sedimentary deposits consisting largely of clay. Such materials were carried by streams and deposited in seas or lakes in successive horizontal beds. Other materials such as calcium carbonate, sand, or gravel may have been deposited over the clays, and the pressure of these superimposed materials gradually consolidated the materials below into bedded deposits of shale. Shale is a stratified rock formed by recrystallization of the clay plus adsorbed potash into the mica, sericite. Shale has neither the strength nor the splitting properties of slate since the mica is fine and the flakes unoriented, and the quartz grains do not interlock. Many shales, however, have been subjected to intense metamorphism. Mountain-building forces ever at work in the earth&apos;s crust may crumple, squeeze, and fold the shales. At the same time, accompanying high pressures and temperatures changed the original minerals into mica, interlocking quartz, or chlorite. Both mica and chlorite consist of minute tabular sheets or flakes with perfect cleavage. The intense pressure and movement tend to orient these flakes in parallel positions normal to the direction of pressure. The parallelism of the flakes results in the tendency to split with ease in one direction, which has been termed "slaty cleavage," and which is the outstanding characteristic of slate. Actually, the cleavage is through the cleavages of the individual micaceous plates. The original bedding of the slate is often folded and contorted, and the slaty cleavage commonly cuts across it at sharp angles. Composition MINERALOGICAL COMPOSITION The most abundant mineral in most slates is white mica (sericite), a hydrous silicate of potash and aluminum. It is present in very small flakes recognizable only with a microscope. Small grains of quartz (silicon dioxide) are also abundant and are regularly distributed among the mica flakes. The mica-like mineral, chlorite, is usually present in considerable quantities. Chlorites are of several kinds, the more common being hydrous silicates of aluminum and iron or magnesium. Other common minerals present in small quantities are rutile, clay, hematite, pyrite, carbonaceous matter, feldspar, zircon, tourmaline, calcite, dolomite, and siderite. The general range of the chief constituents is about as follows: Sericite, 38 to 40; quartz, 31 to 45; chlorite, 6 to 18; hematite, 3 to 6; and rutile, 1 to 1 ½ pct. CHEMICAL COMPOSITION Results of many analyses indicate that clays, shales, and slates differ little in chemical composition. The changes that take place during metamorphism are confined largely to rearrangement of the elements into new minerals with accompanying changes in physical properties such as hardness and cleavage. The general

Jan 1, 1960

By H. C. Rogers

It has been shown previously&apos;- 3 that when a mild steel or iron is charged with hydrogen, the normally observed yield point is eliminated or considerably

Jan 1, 1960

By R. P. Smith, L. S. Darken

FOR a high-purity iron-carbon alloy, the phases existing at equilibrium at temperatures slightly above the temperature of the metastable eutectoid are austenite and cementite (hyper-eutectoid) or austenite and ferrite (hypo-eutectoid) and those below the eutectoid temperature (carbdn content > 0.02 pct) are ferrite and cementite. Such an alloy, held in a carefully controlled and measured temperature gradient (about 1 cm per deg) which includes the eutectoid temperature, then quenched and examined metallographicall.y, provides a precise measure of the eutectoid temperature. The samples were hollow cylinders approximately 1.3 cm OD, 0.63 cm ID, and 2.5 cm long, which had been carburized to the desired carbon content at 1000°C with an appropriate hydrogen-methane mixture. In order to cool the samples to room temperature with a minimum change of carbon content and absence of cracks they were quenched in a Cerro Bend bath at 480°C, followed by a water quench to room temperature. Three cylinders were suspended in the furnace1 in a purified helium atmosphere, by a closed end, thin wall, silica tube which also served as a thermocouple well. The top and bottom cylinders served only as a means of making the temperature gradient along the center cylinder more uniform. The temperature was determined with a platinum-platinrhodium thermel calibrated by comparison with a thermel certified (* 0.5OC) by the National Bureau of Standards. After holding in the temperature gradient for 24 to 72 hr the samples were quenched in Cerro Bend at 480°C, followed by

Jan 1, 1960

By S. L. Lopata, E. B. Kula

A variation of yield and tensile strength with direction has been noted in heat-treated 4340 steel which had been warn-worked by rolling in the austenitic condition prior to quenching. Measurements by X-rays showed a preferred orientation of martensite crystals. Various ideal preferred orientations of martensite were calculated by assuming a preferred orientation for austenite and transforming this to martensite by the Kurdjumov -Sachs and Nishiyama relationships. Comparison with the measured preferred orientation showed that the ideal rolling texture for austenite in 4340 steel could be expressed as a (112) [111] texture with a component of (110) [112]. No evidence was found for any fiber axis in the rolling direction, or fop- a (123) [412] texture. The observed martensite pole figures can be adequately accounted for by these ideal austenite textures and by the Kurdjumou-Sachs or Nishiyama transformation relationships between austenite and martensite. ALTHOUGH preferred orientations are found in cold-rolled steel sheet and in many nonferrous metals, they are not generally encountered in wrought, heat-treated high-strength steels, since such steels are generally not cold worked sufficiently to develop a strong texture, and any texture that is present is removed during heat treatment by the phase transformations taking place. This report gives details on a preferred orientation found in warm-rolled and hardened 4340 steel. In a recent study, a special combination heat-treating and working technique was used in which 4340 steel was deformed in the austenitic condition, and before re crystallization of the austenite could occur, quenched to form martensite.&apos; Since the austenite was unrecrystallized, it was cold worked and hence could have contained a preferred orientation which could be transmitted to the martensite on quenching, and this in turn could be manifested as a directionality of mechanical properties. Such a directionality of properties was found as a result of working, and this prompted an X-ray study of the preferred orientation. Literature Survey— Rolling Texture in Face-Cen-tered-Cubic Austenite—M a preferred orientation is found in a rolled and hardened steel, it is first appropriate to consider what texture existed in the austenite as a result of the rolling but prior to the transformation to martensite. The changes taking place as a result of the austenite-martensite transformation are then considered. In view of the instability of austenite in 4340 steel at low temperatures, no direct determination of the austenite texture was made. However, an estimate of the texture for austenite in 4340 steel may be made by considering the textures found for other face-centered-cubic metals. Barrett&apos; has reviewed the rolling textures for many materials. The most common orientation in face-centered-cubic metals has the (110) planes parallel to the rolling plane and the [112] directions parallel to the rolling direction, or (110) [112]. Other orientations found are (112) [111], as well as (100) [001], (110) [001], and others. Beck and his co-workers, using quantitative pole figures, report that (123) [121],3 later corrected to (123) [412],4 better describes the ideal orientation. smallman5 reported that the ideal preferred orientation for high-purity face-centered-cubic metals is (123) [121], but that there is a transition to (110) [112] as solid solution elements are added. The latter texture tends to occur more readily at lower temperatures. This transition between the two textures was explained by differences in the slip characteristics with concentration or temperature. More recently, Jones and Fell6 concluded that the (123) [412] texture for face-centered-cubic metals could equally well be represented by a mixture of (110) [112] and (112) [111] textures, and hence it had no physical reality. From the above results it can be seen that there is no agreement on the "ideal" texture for fcc metals and, hence, no firm basis for assuming a texture for austenite in 4340 steel. Therefore, the orientations (110) [112], (123) [412], and (112) [111] have been considered in the following.* *The (123) [4121 is identical to the (123) [121] rotated 90 deg. Orientation Relationship between Austenite and Martensite—When martensite forms from austenite, certain crystallographic planes of the martensite are parallel to planes in the austenite. This orientation relationship was first determined by Kurdjumov and

Jan 1, 1960

By F. N. Rhines, A. S. Nemy

The mode of high-temperature tertiary creep of 523-0 aluminum alloy was found to be strongly stress dependent. The occurrence of necking and/or fissures during tertiary creep exhibited a sequence with varying stress, wherein fissures with no necking occur at a minimum stress and necking with no fissures occur at a maximum stress. At an intermediate stress, tertiary creep begins without necking but with fissures in a region just beneath the external surface, followed by necking and the development of fissures along the axis of the specimen. The results are interpreted in terms of grain boundary gliding and the hydrostatic stresses produced by restraints to grain boundary gliding. THERE appear to be two possible reasons for the existence of a period of accelerating elongation prior to rupture during high-temperature creep in metals; namely, 1) a change in the structure of the metal itself, leading to a change in its response to loading, and 2) a reduction in the cross section of the metal resulting in a higher unit loading. Howe,&apos; by annealing and retesting broken low-temperature creep specimens, found that irreparable damage is done once a metal is subjected to creep. Andrade2 first pointed out the association between the reduction in cross section and the increase in creep rate. The present research was designed to investigate both of these factors by retesting specimens machined from material which had been subjected to high-temperature creep testing short of rupture. EXPERIMENTAL METHOD An aluminum alloy, 52s-0, was selected for these studies because it is constitutionally simple, is strong enough to be relatively insensitive to mechanical damage during machining,3 and undergoes accelerating creep in a convenient temperature range. This alloy is hardened by 2.6 wt pct Mg in solid solution and is not subject to overaging effects; it has a very small quantity of an insoluble impurity phase, Mg2Si, finely dispersed throughout its micro-structure. Creep specimens, similar in design to ASTM 0.252-in. tensile specimens, were machined from 3/4-in. round stock and the surfaces were electro-polished. A 24-hr anneal at 500°C was then applied to stabilize the grain size to an average diameier of 0.27 mm. Subsequent heating for as long as 700 hr at the intended test temperatures produced no change in the tensile properties, indicating a well-stabilized state of the material. Corresponding to each of the typical testing conditions listed in Table I, one creep specimen was tested to destruction and this test was employed as a guide in the selection of times for subsequent tests. Duplicate creep tests were then run to various points along the creep curve to produce specimens which were used to determine changes in mechanical properties and microstructures. The latter were examined at the midsections of the specimens. Other specimens were tested to various stages of tertiary creep, after which they were remachined to new cylindrical test specimens, electropolished and re-tested in creep. RESULTS The major findings of this investigation may be illustrated by a comparison of the results of three sets of creep tests. These were run at 400°C at three stress levels, namely 750, 1000, and 1500 psi. In presenting these results in Figs. 1, 5, and 8, the creep curves are given in pairs: That curve of each pair which is drawn through filled circles corresponds to the initial test, and the curve drawn through open circles (and designated by - R) represents the result of retesting the same specimen after machining to a new cylindrical surface. The load was readjusted to the original unit stress at the beginning of each retest.

Jan 1, 1960

By D. Argyriades, G. Derge, G. M. Pound

The electrical conductance of molten FeS was studied as a function of temperature and composition. It was found that stoi-chiometric FeS (36.5 pct S) shows a minimum specific conductance of 400 ohm-1 cm-1. For the Fe-rich melts the conductivity increases with increasing amount of iron to about 4850 ohm-1&apos; cm-I at 26 pct sulfur. For the sulfur-rich melts the conductivity increases with increasing amount of sulfur until it reaches a maximum of 1300 ohm1 cm-1 for 37.4 pct S and decreases to 800 ohm-1 cm-1 for 38.3 pct sulfur. It is concluded that molten stoichiometric FeS is an intrinsic semiconductor in which the forbidden gap in the electron energy level diagram is quite narrow. Excess sulfur acts as an acceptor impurity in providing a component of positive hole conduction, while excess iron acts as a donor impurity to increase the n-type conduction. K. Bornemann and G. von Ftauschenplatl used a four-terminal, direct-current cell to study the electrical conductance of molten copper sulfide. Their measurements showed a high conductivity, of the order of 100 ohm-1 cm-" and a positive temperature coefficient. From electrolysis studies, Savelsberg2 concluded that molten Cu2S and molten FeS are electronic conductors. Further. he found that molten FeS has a high specific conductance, of the order of 1500 ohm-&apos; cm-&apos;, and a small negative temperature coefficient. Pound, Derge, and Osuch,3 using an ac Kelvin circuit and a four-terminal cell, measured the specific conductance of molten Cu,S, molten FeS, and various mixtures. They found that the specific conductance of the solutions followed a roughly additive rule of mixtures. Yang, Pound, and Derge4 showed from electrolysis measurements that the mechanism of electrical conduction in molten Cu2S, FeS, and mattes is primarily electronic. Further, they observed that small additions of CuCl suppress the electronic conduction whereupon the system behaves ionically.

Jan 1, 1960

By G. S. Ansell

RCENTLY, in investigating the high-temperature creep properties of an aluminum, SAP-type alloy, MD 2100, fabricated by Professor F. V. Lenel of Rensselaer Polytechnic Institute, Ansell and Weertman1 found unusually low creep rates. These creep rates are 4 or 5 orders of magnitude lower than is predicted by the slowest creep mechanism based upon dispersion-hardened alloy theory. They ascribed these results to a lack of both normal active dislocation sources and a continuous three-dimensional dislocation network. If one couples these results with the following factors of production and microstructure: 1) The compacted and sintered aluminum powder compact is hot-extruded, with an extrusion ratio of 25:1.2 2) The alyminum oxide particles are approximately 140A units thick, and have a spacing varying from 0.05 to 1.5 1. 3 3) The alloy has plate-shaped grains with minor axes of about 5 X 10 -3 mm and major axes several orders of magnitude greater than this.&apos;

Jan 1, 1960

The following rules, upon approval by the Board of Directors, shall serve as guides in the practical applications of the Bylaws for the operation of the Institute and have the full power and effect of Bylaws, however, these rules may be changed, modified, re¬pealed or amended when deemed necessary by the Board of Directors Any change or alteration of these Rules shall be published in the Journals of the Institute within three months after such alteration is adopted ARTICLE I-ORGANIZATIONS OF THE INSTITUTE Section 1-Societies Rule 1-Governing Body Each Society shall form its own governing body composed of an Executive Committee, or similarly designated executive body, duly elected officers, and a Nominating Committee for the nomination of Institute officers as provided by the Bylaws of AIME and of each Society approved by the Board In all correspondence and printed matter the Society Boards of Directors shall be specifically identified For ex¬ample, the Mining Board of Directors or the Board of Directors of the Society of Mining Engineers Using simply the "Board of Directors" could cause confusion

Jan 1, 1960

By W. F. Dietrich

Mineral fillers are relatively inert chemically under the conditions of use but have physical properties* that modify those of the materials • The properties. uses, and other data on 15 classes of important *The pro listed in the second edition of Industrial Minerals and Rocks.l A third edition of this reference is in preparation. in which they are incorporated. The mineral fillers considered in this article are asbestos, barite, clays, diatomite, crushed limestone, limestone whiting and lime, mica, silica, talc and soapstone, and pyrophyllite. Slate and stone, other than limestone and its derivatives, are excluded because, even though used in large quantities, they are exceptionally low-cost materials generally produced close to the area where they are used. Carbon black is excluded because it is manufactured from natural gas and more than 90 pct of the output is used in rubber; hence the factors for estimating requirements are easily evaluated. OVERALL GROWTH FACTORS Table I gives the population, retail sales, and value added by manufactures in the U. S. and in the eleven western states in 1954. These data are rough guides to the proportionate part of total U. S. markets for products containing mineral fillers that may be expected in a given area. For example, the population of the eight Mountain states in 1954 was 3.6 pct, and retail sales in these states were 3.8 pct of the U. S. total, but the value added by manufactures was only 1.3 pct of the U. S. total. On the other hand, the three Pacific Coast states, with 10.3 pct of the total population, had 12.0 pct of the retail sales and produced 9.6 pct of the value added by manufactures. On an industry-by-industry basis the correlation between the three guideposts will not be as close as shown in the 1954 data for the Pacific Coast states, but in the long-term view the continuing rapid population growth in the western states is certain to result in expanded industrial production at an even more accelerated pace, which will shorten the gap between local consumption and production in most major groups of manufactured consumer goods. Of course, there will always remain favorable areas for production of specific products. Such special situations must be individually analyzed. Fig. 1 compares the population trends in the U. S., the western states, and California with Real Gross National Product from 1910 to 1957, with forecasts to 1970. It is estimated&apos; that the U. S. Real Gross National Product, as measured by the value of goods and

Jan 1, 1960

By A. J. Jacobs, J. W. Spretnak, R. Speiser

The activities of nickel in liquid iron-nickel solutions containing from 10 to 90 at. pct Ni were measured over the temperature range .1510° to 1600°C. A special function was devised whereby activities can be computed by a graphical integration using the results of chemical analyses on the vapor phase alone. The liquid solutions studied exhibit negative deviation from Raoult&apos;s law, but they approach ideality as the temperature is raised from 1510° to 1600°C. The maximum heat of solution is less than -8.0 kcal per mole. The entropy of solution is less than —2.5 kcal per mole deg at 1510°C, and changes negligibly as the temperature is raised. The liquid iron-nickel solutions do not follow regular solution behavior. THE activities of the components of a liquid alloy system can be determined in favorable cases from the partial pressure of the vapor in equilibrium with the liquid alloy.&apos; Assuming that the vapor over the alloy behaves as an ideal gas, the activity of component i is given by the expression, Where the superscripts 1, v, and o signify the liquid, the vapor, and the pure component, respectively; the f&apos;s are the fugacities, and the P&apos;s, the pressures. The quantities Pi and Pi can be determined by the

Jan 1, 1960

By V. A. Phillips, M. Safdar Ali

The tensile properties of Cu-0.20 pct Al, Cu-0.45 pct Mg, Cu-0.27 pct Cr, and Cu-0.22 pct Be solid-solution alloys were studied at -196°, 18°, 2509 and 500°C on wires internally oxidized at 900°and 1000°C. Internal oxidation produced marked increases in yield strength relative to pure copper, particularly at low temperature. The yield strength decreased with increase in temperature to a much greater extent than predicted by current theories of dispersion hardening. The strengthening effect of internal oxidation persisted throughout the entire stress-strain curve, but since a marked loss of ductility occurred at all test temperatures, only modest increases in tensile strength were realized. INTERNAL oxidation involves the preferential oxidation of a baser solute in a relatively noble solvent by diffusion of oxygen into the solid. Since the process is diffusion controlled, it is expedient to carry it out at a high temperature often approaching the melting point. The amount of solute is limited and the oxidation conditions adjusted so that oxygen diffuses inwards to meet the solute causing reaction to progress inwards and form subscale instead of only sur face scale. The reaction can be made to occur throughout the thickness of thin material producing a fine dispersion of oxide inside the metal. C. S. Smith1"3 appears to have been the first to recognize the true nature of the process of internal oxidation. Although extensive kinetic and metal-lographic studies followed by Rhines and coworkers,4-5 Chaston7 andMeijering and Druyvesteyn8 working independently were the first to report hardening effects due to internal oxidation. These results prompted detailed studies of the effects of internal oxidation on the hardness, tensile, creep, and fatigue properties of a number of alloys by G. C. Smith and coworkers9-12 in England, on hardness by Gottardi13 in Italy, and on hardness and tensile properties by wood14 in the U.S.A. Publications dealing with other aspects of internal oxidation will not be reviewed here. Internal oxidation of solutes having a high affinity for oxygen provides a means of obtaining very fine dispersions stable in a suitable atmosphere at temperatures well above those at which most age harden ing precipitates coalesce. The process therefore offers a method of producing thin sheet and wire of possibly outstanding creep resistance. The size limitation might be overcome by internally oxidizing porous powder compacts made from alloy powder before final sintering. PREPARATION OF ALLOYS The alloy ingots, which were approximately 5 1/2 in. long by 1 in. diam, were made up in a high-frequency furnace, using as raw materials OFHC copper, 99.99 + pct Al, high-purity magnesium, and master alloys of Cu-4.19 pct Be and Cu-10 pct Cr. The alloys containing aluminum and magnesium were melted ii closed high-purity graphite crucibles and solidified in the crucible which was lowered partly Out of the coil to give a hot-top effect. The alloys containing beryllium and chromium were made by melting in vacuo in alumina-lined sillimanite crucibles. The magnesium, chromium, and beryllium

Jan 1, 1960