By R. M. Treco

The effect of small additions of oxygen on the hardness, density, and lattice parameters of high purity zirconium has been investigated. Precision parameter values and density of oxygen-free zirconium are given as: a,, - 3.2258 kX units, C = 5.1373 kX units, O23 = 6.507 g per cc. THE effect of oxygen on the hexagonal-phase lattice constants of pure zirconium is of interest for several reasons. The extensive hardening effect of oxygen noted by previous investigators' must be due in part to the lattice distortion accompanying its introduction and possibly to the preferred position of the oxygen atoms. De Boer and Fast' have shown that oxygen is taken into solid solution in large amounts, appearing to occupy an interstitial position. These authors also found that expansion of the lattice was not uniform since the a axis attained a constant value after the addition of 10 atomic pct while the c axis continued to expand. It was thought in the present work that this expansion of the zirconium lattice with increasing amounts of oxygen

Jan 1, 1954

By F. D. Rosi, C. A. Dube, B. H. Alexander

The slip and twinning planes have been determined in deformed crystalsof titanium by an X-ray method of analysis. The slip planes are of the type {1010} and {1011}, while the twinning planes are of the type {1072}, {1121}, and (1122). In the case of the predominant (1010) slip, a type I digonal axis of indices <1120> was the effective slip direction. Microscopic observations on the appearance of the three twin types disclosed a distinct difference in their shapes, and an attempt was made to correlate this difference with the amount of twinning shear. The slip mechanism was discussed on the basis of the difference in c/a ratios for the common hexagonal close-packed metals. IT is a general rule that slip in metals occurs most easily on the planes of greatest atomic density and of the largest interplanar spacing, and that the direction of slip is a close-packed direction. Thus, of the hexagonal close-packed metals which have been investigated by the German school in the decade 1925 to 1935 (cadmium, zinc, and magnesium), it has been found that slip occurs on the basal plane (0001) and in a <1120> direction.&apos; In the case of magnesium above 225oC, slip occurs on a first-order pyramidal plane (1011) as well as on the basal plane.&apos; The hexagonal metals, moreover, deform in part by twinning, and, again with the exception of magnesium at elevated temperatures, the twinning plane has always been reported to be a second-order pyramidal plane {1012).&apos; In view of this consistency in the plastic behavior of these metals, it has been supposed that the same slip and twinning elements would be operative in the other important hexagonal close-packed metals (titanium, zirconium, and beryllium), although there are some reasons why this may not be so. Referring to the tabulation in Table I of the axial ratios of the important metals in this structural class, it may be seen that they can be categorized into three distinct groups depending on the value of their c/a ratios. In the first group are cadmium and zinc with large positive deviations from the ideal ratio for closest packing. This expansion in the direction of the c-axis would be such as to accentuate the basal plane as the slip plane, because it increases the interplanar spacing. The second group includes cobalt and magnesium, which closely approximate the ideal ratio. In the third group are zirconium, titanium, and beryllium whose axial ratios are decidedly less than the ideal. The lattice of the elements in this group is compressed along the c-axis which, in effect, tends to make the basal plane less favorable for slip inasmuch as it reduces the interplanar spacing and the atomic density of this plane. Thus, for metals in the third group, it may be said that there is a certain indefiniteness about the glide plane, in that planes other than the basal plane may be expected to operate. The fact that magnesium begins to exhibit planes other than the normal slip and twinning planes at elevated temperatures may indicate that this behavior will become more pronounced in metals of lower axial ratios. For this reason it might be expected that the slip and twinning behavior of zirconium, titanium, and beryllium would be different from that found in cadmium and zinc. One indication that there is a difference is reflected in the recent work which has been done on the deformation textures of these metals."&apos; As will be shown later, there is a significant difference between the rolling textures of cadmium, zinc, and magnesium on the one hand, and zirconium, titanium, and beryllium on the other, and this difference suggests that the mechanism of plastic flow is not the same in these two groups of metals. From these considerations, therefore, it may be seen that there are good reasons why it cannot be concluded that titanium will have the same crystal-lographic elements of slip and twinning as those exhibited by zinc and cadmium. For the complete determination of these elements it would be most advantageous to have single crystals. However, much valuable information can be obtained by using coarse grained polycrystalline specimens, provided the grains are sufficiently large to permit X-ray

Jan 1, 1954

By John F. Knudsen

Following the flowsheet from the primary crushing plant of Ray mines division through the final products sample mill, there are eight exhaust systems ranging in size from 12,000 to 30,000 cfm. Where possible, hood face velocities are kept around 500 ft per min, permitting branch velocities of 2500 ft per min. Tight-fitting enclosures are provided over all ore drops, crushing operations, and vibrating screens. All enclosures are exhausted either primarily or secondarily, except those around conveyor head-pulleys where the ejector effect of the falling ore creates sufficient indraft to abate dust dissemination. IN 1947 an Industrial Hygiene Department was organized to represent and assist the four western mining divisions in industrial hygiene problems. Department headquarters are located at the Utah Copper Division, Magna Plant, Magna, Utah, with a branch office at the Chino Mines Division, Hurley, N. M. The headquarters staff includes a director, a department secretary, an industrial hygienist, a supervising ventilation engineer, and two ventilation designers. To be in closer association with work at the Southwest properties, a field engineer at the branch office conducts field studies which include ventilation problems at the New Mexico and Arizona properties;i.e., the Chino and Ray mines divisions. Functions of the department are to discover and evaluate existing hazards and to develop protective measures, either by personal protective devices or by proper ventilation, depending on the nature of the contaminant. Other than dust counting, all air samples collected at the four properties are processed at the home office. If through plant surveys or by suggestion of management some type of ventilation or air conditioning is required, the problem is usually handled by the ventilation section of the headquarters department, where general arrangement or line drawings are prepared, showing hoods, ducting, and equipment. Some hood and special parts detailing is done at headquarters; otherwise, required detailing is done by the respective plant engineering departments. Prior to the design of industrial ventilation, either new projects or the revamping of old ones, a thorough survey is made of existing conditions. In so far as possible weighted average exposures are determined and adequate ventilation provided on the basis of maximum allowable concentrations of the contaminant in question, as well as medical case histories, if these are available.

Jan 1, 1954

By Ramachandra Rao

THE occurrence of copper ores at Garimenapenta, 14 59 min 30 sec N Lat., 79 33 min 10 sec E Long., in Nellore district, Madras State, India, has been examined and investigated on numerous occasions during the past two centuries.&apos; No tangible orebody was ever located as a result of all the ex- tensive trenching and shafting done in the area by various agencies. However, during 1933 Messrs. Piepmeyer & Co., a German firm engaged by one of the leaseholders of the area, carried out an electrical survey using inductive methods.&apos; On the basis of certain strong indications found in their survey, they recommended that the prospect be proved by drilling or shafting. But for want of financial backing no further work was carried out. When the Madras government more recently proposed investigation, Dr. Krishnan, then Supt. Geologist of the Madras Circle, urged that before further costly ventures were carried out a test geo-

Jan 1, 1954

By C. W. Thompson

Paul D. Suloff (Goodyear Tire and Rubber Co., Inc., Akron, Ohio)—I would like first to comment on problems of the conveyor belt discussed in Mr. Thompson&apos;s excellent paper, since that is what we hope we know most about. Twists in relatively wide conveyor belt unavoidably produce a lateral maldistribution of tension, raising tension at belt edges and reducing it at the center. They also produce a lateral collapsing force on the belt at the center of the twist owing to the inherent tendency of all the longitudinal elements of the belt to try to pass through a point at the twist center. Calculation of the twist geometry by the methods shown in Mr. Thompson&apos;s paper keeps these extraordinary forces within limits which the belt designer can tolerate. No reduction in belt life due to twisting need be contemplated when this geometry is maintained. There is a minor exception that belts of extreme lateral flexibility will tend to curl laterally at the center of the twist. However, any ordinary fabric construction will perform satisfactorily in this respect. These twists are always made in regions of low tension in the conveyor so that even in the edges of the twist, belt tension does not exceed the average tension found in highly stressed regions of the conveyor. Offsetting these out-of-ordinary belt stresses is the advantage that Mr. Thompson has brought out of getting the return run up out of the dirt where it can be seen. This not only makes it easier to train, but also, in the event that it is not properly trained, frees it of the normal return run edge wear hazard. It is well known that return run edge wear is a prominent cause of belt mortality underground. An interesting aspect of this two-way conveyor is that the belt may be made what is known as a Mobius Strip. A Mobius Strip is obtained by splicing a belt after turning one end of it 180" about its longitudinal axis. In other words, one end is turned upside down before splicing. A belt spliced in this fashion turns itself upside down every time it comes around, but the twist which has been put in the splicing, of course, stays at one location on the conveyor, in this case one of the twist sections at the end. Turning the belt over every revolution might have advantages in some cases. Belts could be made with equal covers and the two sides worn equally and simultaneously. In this case there would be no problem of getting belts on upside down by mistake. However, the two-way conveyor does not have to be a Mobius Strip. It can be twisted in such fashion that the same side is up on both runs. It is simply a question of which way the final 90" twist is made before joining the ends. Another interesting aspect of the two-way conveyor is the problem of operating two-way conveyors in series. Here the sequencing of starting brings up some new problems. It will be recognized, although not always at first glance, that if the starting sequence is planned for one run of the conveyor the reverse will result on the other run. With the two runs carrying bulk material in both directions a reverse sequence on one run would be intolerable. In this situation the only solution appears to be a simultaneous starting of all conveyors in the series. However, with the coal in one direction and intermittent supplies in the other it would be entirely practical to sequence the conveyors for the coal run and accept a reverse sequence on the supply run. The two-way conveyor also lends itself to new driving possibilities. First, it is quite possible to drive at the head end of each run, which of course, means a drive at each end of the two-way conveyor. Driving in this way a given belt can be extended to substantially greater lengths than a conventional conveyor with drive at one end only. In addition to this, under certain conditions the conveyor can be extended to extreme length by driving at one end and at some intermediate point on the most heavily loaded run. As a particular case, a belt carrying coal downgrade and supplies back upgrade could be extended to extreme lengths by driving at the head of the coal run and at an intermediate point of the supply run. Mr. Thompson has been a pioneer in belt conveyor transportation underground and his accomplishment here with the first two-way conveyor of any consequence is another notable addition to the art.

Jan 1, 1954

By J. Chipman, H. Towers, M. Paris

A simple radioactive tracer technique is used to measure the diffusion coefficient of calcium ion in molten slags. In a slag of 40 pct Ca0-40 pct Si0,-20 pct Al203, Dc " at 1450°C is 1.3x10-6 cm&apos; sec-&apos;. THE application of the principles of thermodynamics to steel and iron making problems has proved so fruitful that the kinetic approach has tended to be neglected. It seems probable that in some reactions the rate-determining step is the dif-fusivity of the reactants or of the products. But knowledge of the diffusion coefficients of the constituents of liquid slag and metal is singularly lacking. The present work was undertaken as a first step toward supplying such data for slags. Furthermore, any additional information on the physical properties of liquid slags might be expected to help in elucidating their structure. It is essentially a preliminary investigation, the course of which was determined more by the necessity of establishing a method than by the immediate intrinsic interest of the results. For example, the selection of calcium ion to be studied was dictated by the suitability of the isotope Ca45 in that it is a simple emitter with a long half-life. Of the other ions commonly encountered in slags, the isotopes of iron and manganese have relatively complex radiations as well as the normal disadvantage of requiring control of the oxygen potential of the atmosphere; Mg27 and Al29 have half-lives measured only in minutes; Si3&apos; has a simple decay process but its half-life of 2.8 hr is too short for preliminary studies; the only useful oxygen isotope is the stable O18; and there remain only sulphur and phosphorus both of which have suitable isotopes but were rejected as being of less fundamental interest than calcium. Similarly a lime-alumina- silica slag was used in preference to calcium silicate primarily because of its low melting point and its capacity to form a glass on fairly rapid cooling. Literature Review Very few studies of diffusion in liquid silicate systems have been reported. In order to determine the origin of diopside inclusions in felspathic rocks, Bowen1 investigated the diffusion between diopside and various mixtures of albite and anorthite. Platinum crucibles were used with diopside, the heavier of the two liquids, forming the lower half of the cell and diffusion taking place against gravity. Change in concentration along the diffusion path was found by measuring the refractive index of the quenched glass. Nearly thirty years later McCallum and Barrett2 used essentially the same method to determine the diffusion coefficient of lime in lime-alumina-silica slags. In this case the interest was to find the rate-determining step in the process of slag attack on refractory materials. In an investigation of the kinetics of the sulphur reaction, Derge, Philbrook, and Goldman8 determined the diffusion coefficient of sulphur in a typical blast furnace slag by the simple procedure of melting a slag containing 2 pct S over an identical slag sulphur-free. They make no claim to a high degree of accuracy but suggest that D, is of the order of 10-6 cm2 sec-l. Other high temperature liquid diffusion studies have been concerned with metals. Holbrook, Furnas, and Joseph4 determined the diffusion coefficients of silicon, phosphorus, sulphur, manganese, and carbon in liquid iron by immersing a small carbon crucible containing pure iron-carbon alloy in a large vessel containing iron with a high concentration of the particular element. Their results were confirmed by Paschke and Hauttmann5 using a similar method. Diffusion coefficients in silicates in the glassy state have been studied by Johnson, Bristow, and Blau6 Both Na24 and Ca45 were used as tracers but only the

Jan 1, 1954

By Robert C. Emmett, Donald A. Dahlstrom

FOR many years gravitational classification has been employed as a basic tool in beneficiation of minerals and coal. While improvements have been made to increase efficiency and fields of application, the basic flow pattern has remained relatively unchanged in most gravitational classifiers. Feed slurry is introduced into a settling pool wherein the coarser solids settle against either an upward or horizontal fluid current, or a combination of both, and are withdrawn in a concentrated underflow stream. The finer solids below the classification point possess too low a settling velocity and thus are primarily swept out through a weir overflow by the bulk of the fluid. Because of its simplicity, efficiency, and low power and maintenance costs, gravitational classification finds a wide acceptance for separations in the range of 20 to 325 mesh. Two factors resulting from the basic flow pattern employed in gravitational classification present difficult problems for certain installations. If classification at 60 to 200 mesh of separation is desired, capacity in terms of gallons of overflow per minute per square foot of settling pool area must be low to allow required solids to settle to the underflow. If a thousand or more gal per min of feed slurry must be handled, either a very large classifier or a number of smaller units must be employed, taking up floor space and head room. Examples of this are the large classifiers, wetting tanks, or settling tanks used in the coal industry for recovery of process water from fine solids. Units as large as 50 or 60 ft in diam and 60 ft high, requiring substantial amounts of steel, are not uncommon. A second factor is the lack of self-regulation in gravitational classification. As overflow rate increases, mesh of separation increases correspond-ingly. This normally heightens difficulties of bene-ficiation. If a fine mesh of separation is required at varying feed rates, the problem is more than doubled in complexity. One of the primary advantages of gravitational classification is low power requirement. Gravity feeds or very low pressure heads are employed. However, fluid energy is still present in the inlet stream and provision must be made to dissipate it properly to obtain uniform upward or horizontal currents. Rather than waste this energy, it would be desirable to utilize it to secure a greater degree of self-regulation and simultaneously increase classification capacity per square foot of area. A free vortex could be realized by a tangential entry of feed, resulting in generation of centrifugal force to complement force of gravity in its action. With greater force it should be possible to gain finer separation at any overflow rate per square foot of settling pool area as compared with conventional gravitational classification. Furthermore, as feed rate increases, centrifugal force will also increase and at least partially offset faster currents sweeping solid particles to the overflow. A more stable classification point should result. The liquid-solid cyclone is the most common application of a free vortex in the beneficiation field.&apos; Many previous papers have emphasized uniformity of flow pattern within the cyclone which is largely responsible for the sharp classification that can be obtained.&apos;-4 If a free vortex can be maintained in a non-pressurized vessel with a free surface it may be possible to realize a third advantage of sharper classification. This open-top cyclone would then achieve a minimum energy loss comparable to that with conventional classifiers, and a mesh of separation coarser than 150 mesh, extending the range of application of the free vortex. This is not presently possible with ordinary cyclones. To test the applicability of the free vortex to gravitational classification, a 30-in. diameter open-top cyclone was constructed at Northwestern University. The cylindrical section was 30 in. high and the conical section included an angle of 60". The feed nozzle was a standard 4-in. pipe entering tan-gentially, with centerline 17 1/2 in. below the top of the cyclone. The conical section was flanged near

Jan 1, 1954

By Arthur Baker III

The orebodies are long bedding-plane lenses of chalcopyrite and sphalerite, associated with garnetite masses. Most of the orebodies are within a 50-ft thickness of Cambrian limestone; other Paleozoic limestones and dolomites are locally metamorphosed but only slightly mineralized. Pre-mineral faults are numerous, but shallow folds were the main ore-localizing structures. JOHNSON camp is in the northwestern part of Cochise County, Ariz., about 50 miles east of Tucson. The nearest major mining districts are Tombstone and Bisbee, respectively 27 and 50 miles to the south, and the Superior-Miami-Globe-Ray porphyry copper group, about 90 miles northwest. Like many mining camps of the Southwest, Johnson camp is said to have been worked by the Spaniards. The first production on record was in the early 1880&apos;s, when an unknown amount of oxidized copper-silver ore in the Peabody mine was mined from replacement orebodies in the Pennsyl-vanian Naco formation. From 1904 to 1911 outcropping oxidized ores in the Cambrian Abrigo formation were worked, and an estimated 100,000 tons of copper ore were shipped. In 1912 the first large sulphide orebody of the district, the Republic Manto orebody, was discovered, and in the following few years some 250,000 tons of predominantly sulphide ore were shipped. The average grade of this ore was approximately 4.5 pct Cu, 6 pct Zn, 0.8 oz. Ag, and 0.001 oz Au. The Republic, Copper Chief, and Mammoth mines were the principal producers during this period. Mining ceased in the district after 1920, and until 1943 only small-scale leasing operations were carried on. In 1943 all the mines that had been productive were acquired by the Coronado Copper and Zinc Co., the present operators, and in the 10 years since that time the district production has amounted to approximately 350,000 tons of milling ore averaging 2 pct Cu and 6 pct Zn. Most of this ore was produced from the Republic and Mammoth mines, but since 1950 a large part of the production has been from the new Moore mine. The total known production from the district, then, is about 3/4 million tons of copper and copper-zinc ore of low grade. All of this ore was produced from orebodies associated with garnetite in the middle member of the Cambrian Abrigo formation. In addition to this known production, an unknown tonnage of ore was extracted from the Peabody mine orebodies that lie in the Pennsylvanian Naco formation. Published information on the geology of the district is limited. Aside from brief references in various mining journals, only three papers on the district have been published.1-3 One of these is a U. S. Bureau of Mines report on a diamond drilling program, one is a brief paper on the general geology of the district, and the third is a report on geochemical experiments, with a section on the occurrence of the orebodies. The last two are by John Cooper, of the United States Geological Survey, who has done much detailed work in the area. Stratigraphy The rocks of the mineralized area are Paleozoic sediments ranging in age from Cambrian to Penn-sylvanian. Several disconformities are present in the stratigraphic column, the most important one being between the Cambrian Abrigo formation and the Devonian Martin formation. There are no angular unconformities. Within the district, the Paleozoic sediments lie in a fairly uniform monocline, striking northwest and dipping 30" to 50" northeast. This local monocline is part of a domal struc-ture centered in the Little Dragoon mountains to the southwest. The Texas Canyon stock, a quartz monzonite body intruded probably during the Laramide revolution, lies south of the mineralized area (Ref. 2, p. 33). The Paleozoic rocks dip away from the stock, and on the surface are separated from it by at least 1500 ft of Pre-Cambrian rocks. The outcrop pattern of the northeastern edge of the stock suggests that it may dip gently northeastward, passing below the mineralized area at moderate depth. No quartz monzonite has been found in mine workings or diamond drill holes, which reach to depths of 1000 ft. The only igneous rock found in the mineralized area is a lamprophyre dike cutting the Naco limestone in and near workings of the Peabody mine. With the exception of the lowermost beds—the Bolsa quartzite and the shaly lower member of the Abrigo formation—the Paleozoic sediments are predominantly carbonate rocks, Fig. 1. The middle member of the Abrigo formation, which contains the principal ore-bearing beds, is limestone, with thin shale partings throughout most of its 250-ft thick-ness. Near the top of this member is a sandy bed some 25 ft thick. The upper member of the Abrigo formation and the lower half of the overlying Devonian Martin formation are dolomitic, with num-

Jan 1, 1954

By R. I. Jaffee, H. R. Ogden, D. J. Maykuth, W. L. Finlay

Titanium with up to 7.5 pct Al forms single-phase a alloys that are work hardening, not heat treatable, and ductile as welded. The high aluminum Y phase alloys are not usefully ductile, despite their low hardness, but they have excellent oxidation resistance and hot hardness. LITTLE has been published on the effect of aluminum on the mechanical properties of titanium, despite the fact that two of the first four commercial alloys released by titanium alloy producers contained aluminum as an important alloying ingredient. These were both a-ß type alloys, one containing 4 pct A1 and 4 pct Mn and the other containing 3 pct A1 and 5 pct Cr. However, neither of these alloys reflects the true alloying nature of aluminum, since each contains important amounts of the ß-stabilizing addition, manganese or chromium. In a previous publication on the constitution of Ti-A1 alloys,&apos; the authors showed that aluminum had a high solubility in a titanium and was strongly a stabilizing in nature. About 25 wt pct A1 is soluble in a titanium at room temperature. With as little as 5 pct added aluminum, the a transus temperature is increased from 882" to 970°C, and the correspond- ing ß transus to 995°C. The first intermediate phase in the Ti-A1 system is the ordered face-centered tetragonal TiAl phase, which extends from 34 to 46 wt pct Al. The present paper presents hardness data over the entire titanium-rich region of the system, through the TiAl phase, and mechanical property data on the alloy range capable of being fabricated. Methods of Investigation The materials used and general preparation of alloys, as well as experimental techniques used in the investigation of Ti-A1 alloys, have been adequately described.&apos; Briefly, the preparation consisted of arc-melting the desired amount of high purity aluminum (99.99 pct purity) and iodide titanium (maximum hardness 100 Vickers, as deposited) together on a water-cooled copper hearth under a partial pressure of argon. The resulting button ingot was of such form that it could be fabricated without further treatment. All work was done using ingots weighing 10 to 15 g, which were hot-rolled to strip form whenever possible. Tensile samples were 3.25 in. long, 0.5 in. wide, and 0.040 in. thick, with a reduced section 1.25 in. long by 0.250 in. wide. The gage length used was 1 in. Electrical strain gages mounted on the

Jan 1, 1954

By Y. C. Liu, W. R. Hibbard

Based on pole figure data and microstructural observations, the re-crystallization orientation found in a copper strip previously cold-rolled 99.5 pct from a single crystal with an initial (110) [112] orientation may be described as: a 30° rotation, clockwise and counterclockwise, about octahedral poles of the cold-rolled texture such that all four poles function at a low annealing temperature (400°C) and only three of them function at high temperatures (500&apos; to 1050°C). The relative intensity of deformation stresses on various slip planes can be correlated with the choice of poles affecting the rotations found in the recrystallized orientations. ROTATIONAL reorientation about the poles of densely packed crystallographic planes is an important characteristic of secondary recrystallization" in face-centered cubic metals. Some evidence has also been interpreted to show that such a rotational relationship also exists in the primary recrys-tallization process." In an investigation of the crystallographic relationships in the recrystallization process, several aspects of the experimental procedure should be considered. With cold-rolled poly-crystalline metal as the initial material, pole figure analysis leaves many ambiguities as to whether or not simple indices can be assigned to adequately represent its orientation. The rolling texture does not consist of a single texture. Minor deformation textures are usually present. In all cases, twin textures are present. The presence of both minor and twin deformation textures influences the recrystallization texture. In order to study the recrystallization mechanism, a more precise knowledge of the history of the material before recrystallization is necessary. Tensile deformation of a single crystal usually produces residual stresses which are concentrated at slip bands. Since the exact nature and orientation of these potential nuclei sites cannot be experimentally evaluated, the tensile deformation of a single crystal was not considered adequate. From the work done by Barrett and Steadman6 n copper, it appeared that cold rolling of a single-crystal specimen with an initial (110) [112] orientation would yield a specimen which fulfills the conditions required for the present investigation, namely a highly preferred single rolling texture with relatively homogeneous stress distribution. By investigating the recrystallization texture of this material, additional details of reorientation during recrystallization might be obtained. The purpose of this paper is to describe such an investigation. Experimental Procedure Copper used in the present investigation was cathode sheet with a purity of 99.94 to 99.97 pct. A copper single-crystal specimen, 1.15x0.8720x0.5322 in. (thickness) was cut from a cylindrical crystal which was grown in a Bridgman furnace.&apos; The cutting was accomplished on a horizontal milling machine operated at a very slow speed to obtain a (110) plane in the rolling plane and a [112] direction in the rolling direction. The disturbed surface was removed by electrolytic polishing in dilute orthophos-phoric acid (H3PO4) with a specific gravity of 1.14, and a current density of about 1 to 2 amp per sq cm. A 3-min polishing was needed to eliminate the disturbed surface causing Debye-Scherrer rings and a 45-min polish produced a surface which yielded sharp rounded Laue spots. It was estimated that about 1/16 in. of metal was removed from the original cut surface. The final orientation of this specimen before rolling was about 2" from the (110) plane in the rolling plane with a [112] direction aligned in the rolling direction. It is possible that a small amount of strain was still present in the cube despite the fact that the Laue spots seemed very sharp. It is doubtful, however, that this would be an important factor after a subsequent rolling reduction of 99.5 pct. This copper specimen was rolled on a laboratory rolling mill with two highly polished rolls 37/8 in. in diam in the following manner: 0.010 in. per pass to 50 pct reduction, 0.005 in. to 70 pct, 0.002 in. to 85 pct and, finally, 0.001 in. per pass to a 99.5 pct reduction. Specimens, about 1 in. sq with the rolling edges intact, were cut from the rolled strip by the electrolytic method previously described, after the strip

Jan 1, 1954

By N. A. Gokcen

THE data of Chaudron,1 Tonosaki,2 and Collins³ on the thermodynamic properties of MOO, disagree widely. These authors, by using essentially similar methods, studied the following reaction: 1/2MoO2(s) + H2(g) == i/2Mo(s) + Ph,o H2O(g),K = —----- [1] Ph2 Tonosaki used a vacuum system consisting of a furnace containing MOO, and a water saturator whose temperature was kept at 25 °C with a thermostat. After repeated evacuation, hydrogen was admitted slowly into the system. The experiments were based upon the fact that at a constant furnace temperature and constant partial pressure of water, the total pressure of gas mixture over MOO? + Mo is constant. Any attempt to vary the pressure by external forces would vary only the amounts of MoO2, and Mo, after which the pressure should return to the equilibrium value in accordance with the equilibrium constant of reaction 1. The actual value of K was determined from the total equilibrium pressure (sum of Ph2o + Ph2) at each temperature. The total pressure of gas was varied within the range of 80.2 to 125.4 mm Hg, within a temperature range of 645" to 823 °C. The results were summarized as log K = 0.9413 — 1444.6/T for reaction 1. The ratio of H2O/H2 was considered to be uniform in spite of the presence of a thermal gradient across the static gas phase. It was shown by Rosenqvist and Cox,&apos; however, that in somewhat similar circumstances the error resulting from thermal diffusion may be large. Collins³ improved Tonosaki&apos;s method by attempting to avoid thermal diffusion errors. His equilibrium data were obtained at 700°, 800°, and 900° C, and the result for reaction 1 was expressed as log K = 1.258 — 1822/T. The purpose of this investigation was to study reaction 1, avoiding the thermal diffusion errors, and to obtain equilibrium data in a considerably wide temperature range for the reliable extrapolation of the resulting thermodynamic functions. Experimental Procedure The diagram of the apparatus is shown in Fig. 1. Tank hydrogen was passed through a tube containing platinized asbestos at 425 °C in order to convert a trace of oxygen into water vapor. The flow rate was carefully controlled with a capillary-type flow-meter B and a bubbling column D. The gas was then presaturated sufficiently at P and led into a condenser system immersed in a thermostat, controlled to within ±0.002C. The temperature of the thermostat was measured with a thermometer calibrated against a certified standard. The temperature of P was adjusted to avoid the condensation of unduly large amounts of water as judged from the rate of flow out of the capillary tube M. Argon was purified by passing it through magnesium chips kept at 630°C. After passing through the flowmeter B&apos;, it was mixed with moist hydrogen emerging from the thermostat. The resulting gas mixture was then led into the hot zone of the furnace through the heated glass tubing and the silica tube S, thus insuring the same ratio of PII2o/Ph2 from the condenser to the reaction chamber, thus avoiding thermal diffusion. The entire gas system was of all-glass construction, except at the magnesium train. The furnace comprised a glazed alumina tube over which a 15-in. platinum coil was wound. The lower end of the alumina tube was tightly closed with a brass bottom and a silicone rubber gasket, and the upper end with two glass disks, each with a hole of 1/16 in. in diameter, through which the gas mixture escaped into the atmosphere. A back-up coil of kanthal wire facilitated the temperature control of the furnace. A coil of annealed molybdenum strip of 99.99 pct purity, 0.005 in. thick and 0.050 in. wide, and weighing 17 g was hung in the furnace with a 0.010-in. platinum wire attached to one end of a sensitive analytical balance. The temperature of the furnace was measured with a Pt-Pt-10 pct Rh thermocouple checked against a standard. The experimental procedure consisted of heating the gas purification trains, adjusting the gas flow rates, attaining a constant thermostatic temperature, flushing the entire system for 2 hr while heating the furnace to well above the expected equilibrium temperature and then cooling it at a rate of 0.3°C per min during which time the change in the weight of molybdenum was observed on the balance. For a given thermostatic temperature, i.e., a constant Prr,o/Px,, molybdenum oxidized upon cooling slightly below the equilibrium temperature. The procedure was then repeated by heating the furnace and thus reaching a temperature slightly above the equilibrium value. The average of the two temperatures, differing by 2" to 3"C, was considered to be the true equilibrium temperature. In order to determine the stoichiometric composition of the oxide phase present in this investigation,

Jan 1, 1954

By Edward L. Clark, Garrett A. Muilenburg

THE first record of the discovery of iron ore in Missouri was Marquette&apos;s observation in 1673 of brown iron ore, or limonite, in the Mississippi River bluffs just north of the mouth of Apple Creek in southeastern Perry County. There is no record of any attempt to mine or smelt Missouri iron ores until 1815, when the Ashebran furnace was erected at the Stouts Creek shut-in near Arcadia, Iron County. Some limonite was treated in this furnace, the first iron furnace west of Ohio, but most of the ore was hematite from Shepherd Mountain and adjacent deposits. Eight years later, in 1823, the Perry furnace five miles north of Caledonia, Washington County, was constructed to smelt limonite ore. It was not until 1890 to 1900, however, that these ores attracted considerable attention. Nearly 300,000 tons had been produced by 1911, and this production had come from 24 counties in the Ozark region. For the next two decades, until 1931, essentially all activities ceased. During the depression years of the thirties when employment was low many people turned to the brown ores for subsistence; consequently production was increased. World War II produced another stimulus to the industry. The availability of risk capital in the past three years has revived interest in these deposits, although no appreciable increase in production has resulted.

Jan 1, 1954

By T. M. Allen, W. H. White

THE Greenwood-Grand Forks area of southern central British Columbia, known as the Boundary District, has a long history of mining exploration and production. At the turn of the century this was the premier copper mining camp in the British Empire, its total production amounting to some 20 mil- lion tons. Most of this ore came from the great Granby mines at Phoenix, but the Motherlode mine at Deadwood camp, 6 miles to the west, and several mines in Summit camp, 5 miles north of Phoenix, made important contributions. The large deposits were exhausted in 1918 and the district since has seen only desultory exploration and salvage operations. The orebodies are mineralized skarn zones in limestone members of a thick series of Upper Paleozoic sedimentary and volcanic strata. Chalcopyrite is the primary ore-mineral. Copper carbonates and silicates occur sparingly in outcrops, but the oxidized zone generally is very shallow. Much of the surface is mantled by glacial drift which in most places ranges in thickness from 2 to 15 ft. In some of the hanging valleys, however, the glacial drift may be as much as 100 ft thick and may assume drumlin-like forms.

Jan 1, 1954

By F. D. Rosi

IN the production of single crystals by the Bridg-man method of solidification from the melt in vacuum at a crucible lowering rate of 0.25 in. per hr, a cellular structure was frequently observed in copper and copper-base alloys at the terminal surface of the as-cast crystals (i.e., the surface representing the last portion of the crystal to solidify). The geometrical form of this structure varied from crystal to crystal, but, in general, could be classified as either hexagonal or quadrilateral. Fig. 1 shows examples of this cellular structure, which is similar to that reported by Buergerl and, more recently, by Pond and Kessler&apos; and Rutter and Chalmers. In the micrographs of Figs. lb and c, the cubic structure in the alloy crystals is obscured somewhat by excessive surface evaporation in the final stages of solidification. X-ray orientation studies indicate that the traces outlining the various geometrical forms correspond to octahedral planes, which are the planes of greatest reticular density in the face-centered cubic lattice. It would appear from this that the view first propounded by Bravais,4 that the surface energies and normal growth velocities of the different crystal planes are inversely proportional to their reticular densities, applies to this cellular structure, since those surviving are the planes of greatest atomic density. Thus, the observed variation in the geometrical form of this structure in crystals of different orientation is readily understandable from the distribution of the (111) planes in the standard {111}, (1101, and (1001 stereographic projections. Depending upon whether the crystal axis (i.e., the direction of crystallization) coincides with a <111>, <111>, or <100> direction, the cellular structure viewed from a surface perpendicular to the crystal axis will consist of a network of regular hexagons, skewed hexagons (with interfacial angles of 110" and 125"), or cubes, respectively. It follows, moreover, that off-orientations from these principal directions will yield modifications of these three basic geometric configurations. In this connection, it is interesting to note that the bounding planes of the hexagonal structure observed in tin by Rutter and Chalmers3 showed no preferred orientation.

Jan 1, 1954

By J. P. Martin, A. H. Geisler, J. H. Crede, E. Both

The investigation of a 50 pct Co alloy was undertaken to determine whether there was any direct correlation between the structure and properties of Co-Fe alloys which were given various magnetic heat treatments. The magnetic anisotropy and texture of the 0.002-in. cold-reduced 98 pct material tend to decrease and change in nature with increasing temperature of the recrystallization anneal. Annealing samples in a magnetic field had little effect on either the magnetic properties or texture. However, cooling them in a magnetic field greatly improved their magnetic properties. THE beneficial influence of a magnetic field applied during the heat treatment of certain soft magnetic materials has been known for a long time. Early work showed that the presence of a magnetic field of a few oersteds during the heat treatment of Fe-Ni alloys will cause a large increase in maximum permeability. A pronounced increase in the residual induction which is produced by the magnetic anneal causes the hysteresis loop to approach the shape of a rectangle. Such results are beneficial since the desired properties are high permeability, high induction at maximum permeability, high residual induction, and low coercive force. More recently Libsch and coworkers1 studied the effect of magnetic annealing on the hysteresis properties of a series of Co-Fe alloys prepared from powders. They observed good response for the 35 and 50 pct Co alloys but little response for the 42 pct Co alloy. They pointed out that this was somewhat surprising since the 42 pct alloy has a high linear magnetostriction and zero crystal anisotropy and similar conditions in Fe-Ni alloys give excellent response to magnetic annealing. They found optimum properties to be at the 50 pct composition with residual induction, Br = 19,000 gauss and coercive force, Hc = 0.68 oersteds after the magnetic anneal. Before the magnetic anneal these values were B, = 12,600 gauss and Hc = 1.15 oersteds. The optimum treatment consisted of cooling from above the y-a transformation temperature to 900°C in a field of 20 oersteds, holding 11/2 hr at 900°C, then cooling at a rate of 20° to 25°C per min in the field to below 230°C. Cooling rate mainly affected coercive force with the value decreasing from 1.09 to 0.88 oersteds as the rate was increased from 3° to 48°C per min. Cooling from 1020" to 900°C in a field followed by further cooling to 230°C without the field gave properties decidedly inferior to those for samples annealed with the field applied throughout the cooling. They concluded that to get the best properties the samples must be cooled in a field to a threshold temperature above which the alloy is plastic enough to be affected by magnetostriction. In this respect the holding temperature must be high enough so that the alloy exhibits good plasticity to permit the optimum orienting of magnetic domains by relaxation of magnetostriction. In contrast, the holding time was of less significance for there was little improvement when the time exceeded 1/2 hr. The improvement in properties effected by magnetic annealing has usually been attributed to the establishment of a domain texture caused by the "freezing in" of magnetic strains. On the other hand, Smoluchowski and Turner2,3 apparently found that a magnetic field applied during recrystallization could alter the crystal texture. If this effect is real, improved properties would also be expected when

Jan 1, 1954

LOCAL SECTIONS (There are 60 Local Sections in the United States, 4 Foreign ) ADIRONDACK Established June 18, 1952 Paul W Allen, Chairman William Webb, Vice-Chairman Edwin Briggs, Secretary-Treasurer National Lead Company Mac Intyre Development Tahawus, New York Paul W Allen, Section Delegate R G Fleck, Alternate Section Delegate

Jan 1, 1954

By George W. Mitchell

THE property of Eureka Corp. Ltd. is located in the approximate geographic center of Nevada, 2 miles from Eureka, the county seat. The great sources of power, the Colorado, Snake, and Salmon Rivers and the rivers of northern California, are 300 to 500 miles distant, and no lines serve areas closer than 150 miles. Fuel for diesel and steam generation is available in Utah, 300 to 400 miles to the east. Eureka&apos;s railhead is 80 miles north where two trunk lines cross the county. A spur line serves Ely, 77 miles east. Good highways connect Eureka to the railheads. Activity in the Eureka mining district began in the early 1870&apos;s. The oxidized high grade lead-sil-ver-gold ore terminated against the footwall of the Ruby Hill fault, and in 1890 the main operations ceased. In 1938 Eureka Corp. Ltd. discovered ore in the hanging wall of the fault by diamond drilling. The history of Eureka in the late 1800&apos;s indicates that there was some water at 600 to 800 ft in the old workings, probably accumulations above the water table which did not seriously interfere with mining operations. Both the Locan and Richmond shafts were sunk to a level below the table, but apparently the only serious difficulty with water occurred in the Locan. The steam pump used when the last work was done on the 1200 level in 1923, many years after exhaustion of the main orebodies, is still installed on the Locan 900 level. The capacity was about 500 gpm, lifting 750 ft to the 100 level, which connected with the surface. In addition to this. bailers were used to keep the 1200 level free of water. It is said that pumping in 1923 lowered the water in the Holly shaft, about a mile and a half away, but this seems doubtful. The pumping was of short duration because no ore was found. When work at the new Fad shaft was started in 1941 Eureka Corp. Ltd. engineers were fully aware of the probability of encountering water in large volume. Their primary exploration and development had to be carried on at the 2250 level. The first water was encountered at 300 ft. This was undoubtedly surface drainage in the bedding of the Pogonip limestone and was less than 100 gpm. The fractured, loose Hamburg dolomite at the water table was not well cemented, and relatively little water, 300 gpm, percolated through it with difficulty. At 1350 ft well-cemented dolomite containing some open fractures was encountered. These fractures produced the first water of consequence, 750 gpm. At 1700 ft the volume was 1000 gpm increasing to the maximum during shaft sinking, 1600 gpm, at the 2000 level. Secret Canyon shale, a dry formation, was entered at 2100 ft, where a concrete water ring was placed to catch all of the water. The volume decreased rapidly to a constant flow of 1200 gpm. Below 2100 ft the shaft and stations remained in the shale and water was not a problem. Several faults of moderate displacement, including the reverse Martin fault, had been intersected during the traversing of 1000 ft of wet Hamburg, but no undue quantities of water were encountered. Observations in the diamond drill holes in the ore zone area showed a rapid lowering of the water table. The shaft was flooded when it left the dry shale and entered the water-bearing Eldorado dolomite on the 2250 level, crossing a fissure which paralleled the Martin fault. High pressure water doubled the volume then being pumped. Pipe failure through a water door bulkhead was a contributing factor. Immediately following this flooding in March 1948 preparations were made to recover the shaft as rapidly as possible by increasing power and pump capacities as needed. Measurements before flooding indicated the water could be lowered at a fast rate. However, the water table did not recede as rapidly as expected and volumes required to lower the water in the shaft were higher. Obviously the size of the main water channel on the 2250 level was increasing because of erosion, allowing greater volumes to enter the workings and draining beyond the cone originally being drained during shaft sinking. Eroded material was being deposited in the shaft below the 2250 level in serious proportions. In December 1948 a second flooding of the Fad shaft was allowed for the purpose of reassessing existing conditions and studying alternate methods of attack. The detailed geology of the Eureka mining district, see Fig. 1, has been described during the past 75 years by many geologists.&apos; Only the general features and those which seem to affect the drainage problem will be discussed. The old ore zone, mined between 1870 and 1890, is located in a wedge-shaped block of Eldorado dolomite between the footwall of the Ruby Hill fault and the underlying Prospect Mountain quartzite, see Fig. 2. Production of high grade oxidized lead ore containing high values in gold and silver has been variously estimated at $50 to $90 million. The tonnage mined was probably close to 1,500,000, nearly all of which was found above the water table. The new ore, discovered by diamond drilling in the hanging wall of the Ruby Hill fault, is a flat-

Jan 1, 1954

By K. E. Beu

IN the measurement of retained austenite concentrations in steels using the integrated intensity method,1 Averbach has pointed out" that the absorption factor A(0) for a flat sample making a glancing angle 4 with the incident X-ray beam can be combined with his constant factor R to obtain our constant factor" G provided that "1—There is no preferred orientation in the sample, and 2—The geometric requirements [for the sample, film, and X-ray beam] have been met precisely."&apos; If A(0) can be combined with R to give G according to the equation G = R . A(0) [14] then the possibility for making non-compensating errors in the austenite determination has been eliminated. This has been described previously in a technical note." Because of the brevity of the previous note,3 it was impossible to emphasize the fact that the two conditions on preferred orientation and geometry can be easily met experimentally, contrary to Aver-bach&apos;s statement that: ". . . the necessary conditions must be tested experimentally for each determination, and this is done most easily by observing whether the apparent absorption has the form of Eq. 2 [the theoretical equation for A(0)]."" he way in which these two conditions can be met experimentally will be discussed briefly to help clear up this point. In addition to these two conditions, other factors such as sample shape, homogeneity, and grain size which also affect A will be included in this discussion. A (0) depends on sample shape. The theoretical function for A was derived originally for a flat surface.&apos; In general we have found that a flat sample surface is readily obtainable." If such a surface can * The effect of surfaces which are not flat on the measurement of retained austenite will be discussed later. be obtained, it has the following advantages: 1—it is easily reproducible from sample to sample, 2—it is the form required for metallurgical examination —this type of examination being frequently desirable for this work, and 3—it is an efficient shape for diffraction purposes. Perhaps the most important of these features is that a flat sample surface is easily reproducible; hence, this requirement on the repro-ducibility of A from sample to sample is met for all such samples. Fig. 1—Schematic diagram of the quartz crystal monochromator diffraction unit. The centerline of the main beam is at 6&apos; to the target face. The tangent to the crystal face is at 16.8&apos; to the moin beam. The centerline of the monochromatic beam is at 33.6 to the main beam. The sample surface can be rotated in its own plane. The angle of the sample surface and the monochromatic beam can be adjusted by rotating about the vertical axis, The film holder can also be rotated about B so that the film can be exposed over the desired angular range. For Fe K, X = 1.932A. 1011 planes of quartz have d = 3.35A. A(0) depends on homogeneity and grain size. If the sample is badly segregated or the grain size is large, the effect of micro-absorption and primary extinction1. &apos; must be considered. It has been shown, however, that for most plain carbon or low alloy hardened steels, neither micro-absorption nor primary extinction effects are present.&apos; A (0) depends on camera geometry. For a given angle 0, A remains theoretically constant from a geometrical viewpoint only if the following factors are kept constant: 1—the angle of inclination .+ of the sample to the X-ray beam, and 2—the centering of the sample with respect to the film cylinder. These are mechanical problems which can be solved readily if the facilities of a good machine shop are available. The arrangement used to insure that the angle 4 remains constant and the centering of the sample is reproducible is indicated schematically in Fig. 1. The sample is clamped against a thin plate with a hole in it by means of a spring-loaded pres-

Jan 1, 1954

By E. J. Dulis, R. M. Fisher, K. G. Carroll

IT is well known that ferritic steels containing more than 15 pct Cr when subjected to temperatures in the range of 700" to 1000°F exhibit increasing hardness and decreasing ductility. The phenomenon has been widely termed the "885 °F embrittlement," after the temperature of most marked effect.&apos;.&apos; In view of the excellent review articles available in the literature3-6 only a brief account of experimentally established facts need be given here. The extent of changes in physical characteristics during embrittlement depends on chromium concentration and time at temperature, higher alloy content and longer time both promoting more rapid and extensive changes. In a 27 pct Cr steel, changes in impact strength and in angle of fracture in bending can be detected after only a 1 hr exposure at 885°F; after 50 hr this steel becomes quite brittle. Hardness increases slowly with time during thousands of hours exposure and may attain a maximum hardness number twice as large as that of the unexposed steel. Microstructural changes accompanying embrittlement have been described as an initial widening of grain boundaries followed by eventual darkening of ferrite grains. Embrittled steels etch more readily, e.g., the weight loss of a 27 pct Cr steel in acid solution may occur at a rate one hundred fold greater following exposure at 885 OF. Marked changes which accompany embrittlement have been observed in electrical resistivity, specific gravity, and magnetic coercive force. Changes in physical properties may be readily removed by heating at temperatures above the embrittling range, such as a treatment at 1100°F for 1 hr. It has frequently been noted that the 885 °F embrittlement suggests precipitation on a submicro-scopic scale of a chromium-rich constituent, the nature of which has not been revealed by X-ray diffraction. Progressive broadening of the body-centered cubic diffraction lines during embrittlement has been observed," and recent observations by Lena and Hawkes&apos; upon single crystals have shown early asterism in X-ray photographs, disappearing within an hour at 900 °F. Many workers have ascribed8-13 the phenomenon to a precipitation of a phase (FeCr), which is known to cause embrittling effects at temperatures much higher than 885°F. Two general observations, however. suggest that a precipitation cannot be responsible for the 885°F phenomenon: 1—prior cold work greatly enhances a formation, whereas it scarcely affects the 885 °F embrittlement, and 2—the presence of an alloying element such as nickel or manganese may have an effect on the 885 °F embrittlement which is opposed to its effect upon a formation. The slight enhancement of a formation and 885°F embrittlement observed in the presence of elements with strong carbide and nitride forming tendencies&apos; is probably a consequence of lessened chromium depletion of the matrix. The bar graph in Fig. 1 shows a typical example, taken from two 27 pct Cr steels used in this work, of the hardness after exposure for 10,000 hr at 900°, 1050°, and 1200°F. Steel A (0.03 pct C, 3.13 pct Mn) showed marked hardening at 900" and 1200°F, whereas steel B (0.12 pct C, 0.63 pct Mn) exhibited only the 900°F hardening. The cr phase was found in steel A at the higher temperatures but not in steel B. Presumably a formation is enhanced by the low-carbon and high-manganese concentrations in A," Thus there are two distinctly different hardening phenomena present which cannot both be ascribed to v precipitation without invoking a transition phase possessing remarkable properties. Materials A number of chromium steels exposed for long periods (5000 to 34,000 hr) at 900°F, as well as unexposed samples of one of the steels, were available for this investigation. Table I gives the chemical compositions and aging treatments of these steels. In addition to these steels exposed in the elevated temperature test furnaces of the National Tube Division, a number of high-chromium steels were heated for short periods in small laboratory air furnaces and lead baths. Supplementing these commercial steels, a sample of high-purity (0.018 pct C, 0.002 pct N) 28 pct Cr iron, exposed 1000 hr at 887°F. was furnished by the Union Carbide and Carbon Corp. In addition, an alloy of iron and chromium of high purity containing 46 pct Cr was used. This

Jan 1, 1954

By D. S. Eppelsheimer, D. N. Williams

The cold rolled textures of iodide titanium and of three samples of commercial titanium were examined using the Schulz-Decker Geiger counter technique. The iodide titanium and two of the three samples of commercial titanium showed a (0001) [1010] texture rotated 30&apos; toward the transverse direction about an axis in the rolling direction. The third sample of commercial titanium showed a double texture. THE metals of the hexagonal system tend to deform similarly if the c/a ratios are similar. Thus titanium, zirconium, and beryllium, with c/a ratios of 1.601, 1.590, and 1.570, respectively,l should have similar cold rolled textures. The cold rolled texture of high purity iodide titanium has been described as (0001) [1010] rotated 30" toward the transverse direction about an axis in the rolling direction.&apos; The texture of zirconium has also been reported as (0001) [1010] with a transverse rotation from the ideal position of approximately 30" about an axis in the rolling direction." This texture differs from that reported for titanium however since a continuous spread of (0001) poles toward the transverse direction was reported rather than distinct (0001) maxima 30" from the rolling plane normal. Beryllium has a texture similar to that of zirconium although the angle of transverse rotation of the (0001) poles is much less.&apos; These three metals thus show a common type of cold rolled texture, as yet unexplained, which can be described as (0001) [1010] with various degrees of rotation toward the transverse direction about an axis in the rolling direction. Since titanium showed the greatest degree of rotation from the (0001) [1010] position, the cold rolled texture of titanium was re-examined using a semiquantitative Geiger counter X-ray technique to obtain more accurate experimental data from which a theoretical interpretation of this new type of hex- agonal rolling texture could be developed. The cold rolled textures of iodide titanium and of three samples of commercial titanium were determined. Table 1 gives the analyses of the titanium samples. Experimental Procedure Preparation of Samples: Prior to the final rolling operation each of the samples was given an initial reduction of approximately 50 pct and annealed to remove the gross effects of any previous treatments. Samples were annealed in vacuum, high purity helium, and air to determine whether annealing atmosphere had any effect on the cold rolled textures developed. All samples were annealed 1 hr at 800°C. Grain size determinations were made using the formula, 1.075 in which n is the number of grains counted in an area A (in sq mm) and M is the magnification of the area counted.&apos; This formula gives the diameter between opposite flats assuming hexagonal grains. At least three areas containing more than sixty grains each were counted in each grain size determination. Rockwell B hardness readings were made on the annealed samples. The results of the measurements of

Jan 1, 1954