Search Documents

By H. F. Bishop, F. A. Brandt, W. S. Pellini

The solidification mechanism of experimental steel ingots (7x7x20 in.) was studied by thermal analysis. It was determined that solidification proceeds in wave-like fashion at rates which are determined by the carbon level, superheat, and mold thickness. The thermal cycles of the mold walls were related to the course of solidification. ESPITE marked advances in the field of solid state transformation, metallurgical research has contributed comparatively little exact quantitative data on the mechanism of solidification of metals. There is, therefore, a great need for such data in the various metallurgical industries. The mechanics of solidification of ingots have been investigated in the past primarily by studies of the rate of skin formation as indicated by bleeding or "pour out" tests. The "pour out" method, however, is a tool which gives only approximate information. In the case of alloys with wide solidification ranges, such as irons and certain nonferrous alloys, the method will not work at all; in the case of alloys of intermediate solidification ranges, such as commercial steels, the information may be misleading. Thus, the general adoption of this method has resulted in divergent conclusions regarding the solidification process. Chipman and Fondersmith1 by means of bleeding tests have shown that the linear growth of a solidifying ingot wall follows a parabola of the general form, D = K C, with the start of solidification delayed until superheat is exhausted, as indicated by the constant C. These tests were carried only to a wall thickness of about 5 in. using an ingot of approximately 17x39 in. in cross-section; hence the latter stages of solidification were not studied. Matuschka2-3 indicated that linear solidification of ingots is rapid at first, then slow, but toward the end of solidification the rate becomes extremely rapid again. Spretnak's4 bleeding studies indicated that, wall growth is expressed more rigorously by two parabolas, and that their point of intersection corresponds to a change of solidification mode from columnar to equiaxed. Spretnak also showed that the K values of the first parabola are always the same regardless of superheat. Nelson bled ingots of square cross-section and found that linear wall growth is initially rapid but decreases continually until the end of solidification. He also concluded that rate of solidification in ingots of square cross-section increases 2.15 pct for every 10 pct increase in cross-sectional area of the mold. The mold ratios considered (ratio of cross-sectional area of the mold to cross-sectional area of the ingot) were all less than 2 to 1. The subject of solidification has also been treated mathematically in many cases, but because of the lack of accurate thermal constants and the simplifying assumptions required, as their authors generally acknowledge, they represent only approaches to the actual conditions of ingot solidification. A third method of studying solidification is the electrical analogue method promulgated by Pasch-kis6-7 and by Jackson and coworkers.8 This method treats solidification as a heat transfer problem with the solidification cycle synthesized on an electrical circuit. Paschkis in his treatment of solidification considered the fact, which was generally ignored, that solidification of steel is not simply the growth of a plane solid wall but a more complex process occurring over a temperature range as indicated by the constitution diagram. Undoubtedly, the anomalous results obtained by bleeding tests arise from the inability to measure quantitatively this mushy condition. The shape of Paschkis' solidification curves are more nearly in accord with those of Matuschka, in that they indicate rapid linear solidification at the beginning and end of solidification with intermediate solidification occurring at a slower rate. Paschkis indicates a definite lengthening of solidification time with increasing superheat. Thermal analysis is a direct method providing exact information for all types of metals regardless of solidification range and was thus adopted in the present program to follow the entire course of solidification from the surface to the centerline of the ingots. The method has the added advantage of being adaptable to following the thermal cycle of the ingot mold during the course of solidification. Test Methods The ingots studied were of square cross-section, 20 in. long, tapered from 71/4 in. at the top to 63/4 in. at the bottom, and fed with a hot top 7 in. in diam and 12 in. high. The molds were uniform in wall

Jan 1, 1953

By W. Rostoker

A STUDY of the titanium-oxygen system' involved an associated series of measurements of the lattice parameters of the a and TiO phases. The results permit some interesting deductions which are herein reported. A comprehensive survey of the physical PI-operties of the phases in this alloy system has been made by Ehrlich.2 However, only impure titanium was available at that time, so that some revision of his measurements is to be expected. The lattice parameters were calculated from the high angle lines of Debye-Scherrer patterns taken in a 14 cm camera and using filtered CuKa radiation. The specimens were prepared largely by crushing and screening of lump samples which had been quenched from elevated temperatures. Only in the case of low oxygen contents was it necessary to resort to filing and annealing. The results of the lattice parameter studies are graphically presented in Figs. 1 and 2. It will be seen that oxygen produces a pronounced distortion of the c parameter of the a phase (hexagonal close-packed). The trend is in general agreement with Ehrlich's work, although the divergence of actual parameter values strongly suggests that his titanium was very impure. It will be noted that the a phase of titanium can tolerate the unusually high saturation solubility of about 34 atomic pct 0. By virtue of this unique effect, it is possible to make a calculation of the effective atomic diameter of oxygen when dissolved in a lattice with metallic bonding. This has not been possible before. Ehrlich's2 density measurements demonstrated that oxygen occupies interstitial positions in the a lattice and the trend of the lattice parameters would certainly support this. In a hexagonal close-packed unit cell the largest interstitial positions lie at (2/3, 1/3, 1/4) and (2/3, 1/3, 3/4). Accordingly, if both of these positions were occupied, the ratio of titanium to oxygen would be 1:1. The extrapolated c parameter may be taken as between 4.93 and 4.99?. The a parameter appears to reach a constant value of 2.955? at low oxygen contents. The distance of the center of a titanium atom site from the [vc2/16+a2/3-1.448] Then the atomic diameter of the oxygen atom is represented by the function: where the radius of the titanium atom is 1.448A,

Jan 1, 1953

By R. S. Archer

THE name molybdena was employed by Pliny to denote various substances resembling lead. Later this name was applied to galena-the naturally occurring sulfide of lead-or substances of similar appearance. By the middle of the eighteenth century, it was applied to graphite and to the mineral sulfide of molybdenum (MoS2) now called molybdenite. This confusion is quite understand- able inasmuch as these substances look and feel very much alike. In 1778, the Swedish chemist Scheele published a treatise in which he pointed out essential differences between graphite and molybdenite. On treatment with nitric acid, molybdenite, unlike graphite, produced a peculiar white earth with acidic properties which he called molybdic acid. Since the same mineral gave off sulfurous fumes on heating, he concluded that it was a sulfide of molybdenum. In 1790, there appeared an account of the isolation by P. J. Hjelm of the new element molybdenum, as a metallic powder, by heating the oxide with carbon. It was not until Bertelius conducted the necessary experiments, about 1818 to 1825, that the foundation of the chemistry of molybdenum was laid. The only recorded use of molybdenum during the first century after its isolation was as a chemical reagent, primarily for the determination of phosphorus. It was not until the last decade of the nineteenth century that the use of molybdenum in steel appears to have been investigated. A

Jan 1, 1953

By C. G. Dunn, M. Sharp

HE orientations of 137 crystals of copper pro-T duced by secondary recrystallization in a cube texture matrix have recently been obtained. Although the crystals were not prepared for the purpose of determining a secondary recrystallization texture, the orientations obtained proved to be rather interesting, as they confirmed, in part, published results and also disclosed additional preferred orientations in the texture. The investigation of Dahl and Pawlek,&apos; Bowles and Boas,&apos; and Kronberg and Wilson3 showed respectively that the orientations of secondary grains growing in a cube texture matrix were related to those of the primary grains by a rotation of approximately 30" about [001], the rolling direction, by 30" about a <111> direction, and by either 22" or 38" about a <111> direction. Kronberg and Wilson also obtained a component of the texture similar to that of Dahl and Pawlek except the angle of rotation about [001] was 19". When the cube texture matrix was deformed a small amount, Kronberg and Wilson also obtained large grains on subsequent annealing corresponding to a rotation of 15" about the normal to the sheet, but these grains should not be classified as secondary recrystallization grains since they were produced subsequent to mechanical straining. The particular texture obtained, of course, depends on the composition of the copper and the processing schedule employed, since these factors markedly affect the primary recrystallization texture and the sharpness of any cube texture produced. In the present investigation, pieces of OFHC copper in the form of M in. round bars were cold forged to a thickness of about 0.40 in., annealed 1 hr at 350°C in an atmosphere of hydrogen, and cold rolled crosswise to a thickness of 0.200 in. These pieces were given a penultimate anneal of 1 hr at 350°C in hydrogen and a 90 pct cold-rolling reduction lengthwise to a thickness of 0.020 in. Indentations generally were put in one end of the as-cold-rolled strips to promote earlier formation of secondary grains.

Jan 1, 1953

By E. E. Donath

THE coal hydrogenation process is well known as a means for production of liquid fuels from coal. In this paper, the possibilities of the coal hydrogenation process as a source of chemical raw materials will be discussed. The recovery of chemicals from coal hydrogenation products necessitates some modifications and additions to the equipment used for the production of fuels. The conversion of coal into liquid fuels such as gasoline requires two steps: liquid-phase and vapor-phase hydrogenation. Intermediate oils obtained in the liquid phase contain oxygen and nitrogen compounds, especially aromatic compounds, since the coal itself is composed mainly of cyclic compounds. These oils are the raw material for the separation of high-molecular-weight aromatics and of tar acids and tar bases. The relative amounts of heavy and middle oil-boiling above and below 325ºC, for instance-can be influenced by temperature, residence time, and catalyst of the liquid-phase hydrogenation. In vapor-phase hydrogenation, a solid bed catalyst is used to convert the intermediate oil from the liquid-phase operation into hydrocarbons of the gasoline boiling range. Essentially pure hydrocarbons with a low content of sulphur, oxygen, nitrogen, and olefines are obtained. Depending mainly on the catalyst, the high ring-compound content of the liquid-phase oil can be preserved and gasoline rich in aromatics obtained. However, with other catalysts, these ring compounds can be split into gasoline with a high content of isoparafhns.3 Again, depending on the operating conditions, products of varying boiling range can be obtained. Selection of catalyst and operating conditions therefore makes possible the production of different grades of motor fuel and also variations in the relative amounts of benzene, toluene, and xylene when aromatic hydrocarbons are produced. The schematic flowsheet, Fig 1, shows the main steps of the coal hydrogenation process, and the product streams used for the recovery of chemicals are indicated. In the liquid-phase stage, coal is made into a paste with re- cycle heavy oil. The coal paste is mixed with hydrogen and preheated at a pressure of 300 to 700 atm in heat exchangers and preheaters. The coal paste and hydrogen enter high-pressure converters where the liquefaction of coal, conversion of the high-boiling liquid materials initially obtained, into intermediate oils is performed at a temperature around 470ºC. The reaction products enter the hot catchpot in which oil vapors of lower boiling point

Jan 1, 1953

By Charles W. Oxford, R. L. Huntington

During the past 20 years (1932-1952), many condensate reservoirs have been discovered in the United States, particularly in the Gulf Coast region. Most of these reservoirs have been produced by a combination of gas cycling and slow pressure depletion in order to recover the liquefiable components from the single-phase fluids originally existing within the Although a record of the composition of the produced fluids has been kept on some of these reservoirs, very little laboratory work has been done on small scale replicas so as to obtain some idea of the effect of such variables as fluid flow withdrawal and cycling rates, pressure, temperature, percentage of liquid hydrocarbon and water saturation within the reservoir. Weinaug and Cordell have shown experimentally that condensates can be revaporized within a sand reservoir; however, they studied only the effect of fluid withdrawal rate. In this investigation the above mentioned variables were studied experimentally in small scale reservoirs both in the case of vaporization of condensate by batchwise pressure deple-

Jan 1, 1953

By D. J. DeLazaro, W. Rostoker, R. E. Riley, M. Hansen

KNOWLEDGE of the isothermal transformation behavior and the TTT chart method of graphically summarizing such information has been of invaluable aid to the ferrous metallurgist in understanding and developing heat treatments intended to provide specific mechanical properties. It is to be expected that similar lines of study directed to titanium-base alloys will be as profitable. This paper summarizes, on conventional TTT charts, the isothermal transformation products and pertinent reaction rate data for binary alloys of titanium containing 1, 3, 5, 7, 9, and 11 pct Mo, respectively. The results so presented were derived from metal-lographic examination. Some X-ray diffraction work was done to clarify certain points of question. Ti-Mo System To the authors&apos; k.nowledge, TTT charts have only been used to describe the reaction rates of eutectoidal decompositions. It would seem that the kinetics of decomposition of any unstable solid solution might be conveniently described in this manner. The equilibrium diagram of the Ti-Mo system&apos; is shown in Fig. 1. The similarity with the Fe-Ni system will be recognized. Additions of molybdenum serve to stabilize the /3 phase to increasingly lower temperatures. The solubility of molybdenum in the a phase is restricted to less than 1 pct at 600°C. Under normal conditions. a homogeneous ,8 structure quenched to a, temperature in the a f & field will reject a of invariant composition. The rate at which this occurs depends on the degree of undercooling and the degree of supersaturation of /3. The structural character of the rejected phase may also be expected to be related to the undercooling. Materials and Experimental Methods A sponge titanium was used which has a nominal impurity content as reported in Table I. The nominal composition of the molybdenum used is also included. The alloys were prepared in 150 g melts by arc melting in an evacuated water-cooled copper crucible of the type reported in an earlier paper.&apos; The pancake-type ingots were forged to 1/4x1/4 in. bars and homogenized for 24 hr at 1000°C in evacuated Vycor bulbs. Specimens Vi in. thick were cut from these bars for heat treatment. The heat treatment cycles followed an invariant procedure. The specimens were soaked at 1000°C for 20 min under a helium protective atmosphere prior to quenching into a lead bath held at a temperature corresponding to a chosen degree of undercooling. After a prescribed period of time at this temperature, the specimen was removed and water quenched. A series of specimens so treated for progressively longer periods served to establish the times for initiation and completion of the decomposition of the /3 phase at a particular temperature. Although heat treatment of unprotected specimens in a lead bath does permit surface contamination by lead diffusion, this method is necessary to insure sufficiently rapid quenching rates. As long as the bath treatments were of less than 1 hr duration. the contaminated surface was not unduly deep and could be removed without excessive grinding. Metal-lographically, the contaminated zone could be readily distinguished from the pure binary alloy. Transformation Characteristics of Ti-Mo Alloys Metallographic examination showed that a supersaturated p phase may decompose by one of two processes. Alloys containing 1 to 9 pct Mo, when quenched in water from the homogeneous /3 field,

Jan 1, 1953

By F. E. Streigert, J. H. Mallery, A. H. Geisler

The existing data on precipitation in Cu-Be alloys have been reconciled with some new data to present a more complete and rational analysis of the atomic rearrangements involved in the process. Two different coherent precipitates were proposed. Each is responsible for a type of diffuse X-ray diffraction effect. THE nature of the atomic rearrangement involved in the precipitation of the compound y-Cu-Be from supersaturated solid solutions of the copper-base alloys has been the subject of two extensive investigations.&apos;-" he precipitate in this alloy system has a rather simple structure; at equilibrium it has a body-centered cubic unit cell with copper atoms on the corner sites and beryllium atoms on the center site. While a simple mechanism would be expected to obtain for the precipitation process, those which have been proposed do not adequately explain all of the reported data. The purpose of the present report is to rationalize some of the previous observations and to contribute new data on the subject obtained by the usual techniques of structure analyses. The Cu-Be system of alloys represents one of the most extensively investigated precipitation systems, so a detailed review of the pertinent literature on structure is in order. Striations: Since one of the important features of the mechanism—the habit plane—is determined by microscopic examination, microstructural features that have been observed should be considered at this time in order to assess their role in the precipitation process in Cu-Be alloys. One of the most prominent features appears as regularly oriented markings or stripings (ripples or striations) across the crystals on a suitably polished and etched sample of the aged alloy. These have been observed and interpreted by many workers. Masing and Dah14 observed striations in both the a and /3 phases of a 2.5 pct Be alloy, and attributed them to the beginning of the precipitation of very fine y crystals along favored planes of the a matrix and to the local decomposition of the £ crystals into a plus y. These markings were apparent in both the a and /3 phases of the micrographs given by Smith5 for a 2.75 pct Be alloy, while Moore" detected them in the a matrix phase using polarized light. Desch7 attributed the markings to fine precipitate particles lined up on a family of matrix planes like Masing and Dahl had done, and he identified the planes as those of the (111) family, the slip planes of the matrix. The striations were presumably the structure which Northcott- eferred to as "martensitic." He found that this structure was present in samples that had been aged under widely different conditions with hardness values ranging from 160 to 400 VHN. Later Guinier and Jacquet&apos; also found striations in both the a matrix and secondary /3 phase. Their analyses showed that the striations were along (110) planes of the matrix phase, apparently in contradiction of the results of Desch. They found that the striations were developed during aging on the surface of a specimen that had been polished prior to aging.&apos; On this basis they concluded that the striations represented mechanical deformation by slip along (110) planes of the matrix resulting from precipitation stresses.&apos;" Similar but fainter striations were observed in the same manner on an A1-Cu alloy sample, in which the change in volume was much less than for Cu-Be alloys and

Jan 1, 1953

By E. P. Peleider

DIAMOND drill research work was initiated at the School of Mines, University of Minnesota, in late 1949. The Drilling Symposium held in Duluth that spring highlighted the problem of high cost and core recovery and the need for controlled testing. An advisory committee made up of informed representatives of both mining companies and drilling companies was formed to suggest and advise on a program of drill research. A Hy-Mac hydraulic drill unit, see Fig. 1, especially designed for experimental testing, was obtained for this work by the School of Mines through the courtesy of the Carboloy Co. It is an extremely flexible unit, capable of exerting a forward thrust of about 1750 lb and turning at speeds from 650 to 2200 rpm. The feed arrangement is so designed that the advance can be set either at a constant rate or permitted to vary at a fixed Pressure, see Fig. 2. The

Jan 1, 1953

By Earle E. Schumacher

THE elements silicon and germanium are not metals within the usual, intuitive association of the word, nor are they so within a stricter definition based on the electronic binding. Two properties associated with metals are plasticity and high electrical conductivity. These elements crystallize in the diamond cubic structure, an arrangement apparently not very favorable to slip, and are therefore brittle rather than ductile. Their electrical conductivity is not like that of metals the atoms are locked together by the covalent bond, which in pure and perfectly arranged material leaves but few electrons free to act as electrical carriers.† In further contrast to metals, their electrical conductivity can be greatly increased by raising the temperature. Yet silicon and germanium are not ideally nonmetallic. They are hard, solid, and possess a metallic luster. They exhibit that peculiar brand of electrical conductivity conveniently termed "semi- conduction," wherein, as shall be seen, lies much of their importance. Both, but silicon in particular, are important components in real metallic alloys and the methods of their reduction and preparation lie clearly in the province of the metallurgist. From their duality of physical and chemical properties, silicon and germanium, along with such elements as boron, diamond, gray tin, selenium, antimony, and arsenic, are considered semimetals or metalloids. Because of their importance to metallurgy and the im-

Jan 1, 1953

By G. G. Gunther, C. L. Boeke

THE zinc deleading processes at the Parral and Santa Barbara mills are described separately to provide a basis for comparison. Although the two procedures are fundamentally alike, there are some differences in application to meet specific conditions. The Asarco mill at Parral in the State of Chihuahua is a flotation plant treating 1450 metric tons per day of complex sulphide copper-lead-zinc ores. In general, the procedure used for selective separation of the minerals into a copper, a lead, and a zinc concentrate follows the usual practice. First, a bulk copper-lead concentrate is floated and then separated into a final copper and a final lead concentrate by the sulphurous acid process. A small tonnage of high grade gravity lead concentrate is tabled from the bulk copper-lead cleaner tailing before it is reground so as to avoid undesirable over-grinding and sliming of this portion of the lead mineral. Next, a zinc concentrate is floated from the lead rougher tailing and, as described later, is separated into a final lead product and a final zinc concentrate. Finally, the zinc rougher tailing receives a strong scavenger float to remove all recoverable middling values for regrinding and return to the flotation circuits. The slime is separated from the scavenger flotation product, and only the sand portion goes to the regrind section. The minerals in the separated slime are extremely resistant to all methods of selective separation and pose one of the major problems awaiting solution. Nevertheless, the slime shows a profit when mixed with either the lead or the zinc concentrate, except when metal prices are very low, so it is accepted as a final product for lack of a more profitable method of handling it. In contrast, the minerals in the reground sands of the

Jan 1, 1953

By Carl Wagner

This paper contains solutions of the differential equation of diffusion in binary alloys if the diffusion coefficient is an exponential function of the concentration of one of the components. THE general differential equation for one-dimensional diffusion in a binary system can be written as: where c is the concentration of one of the two components in any suitable units; x, the distance from a reference plane; t, time; and D, the diffusion coefficient. Hartley and Crank&apos; have pointed out that eq 1 with conventional length units for measuring the distance x holds only if the alloy can be regarded as a rigid framework. In general, this is not the case, especially if the lattice parameter varies appreciably with composition. If a modified coordinate system is used instead of an orthodox system based on the centimeter a:: length unit, eq 52 is obtained, which has the same general form as eq 1 and is generally valid. The necessary transformations are presented in the appendix. If&apos; D is independent of concentration, analytical solutions of eq 1 are known for numerous boundary conditions. If D depends on concentration, solutions based on known analytical functions are not available. Among others, Boltzmann2 and Matano3 have shown that the concentration c depends only on (x/t1/2) in the case of diffusion between two semi- infinite spaces with uniform initial concentrations: c = c, for x < 0, t = 0, i.e., x/tl/2 = — x [21] c = c2 for x > 0, t = 0, i.e., x/tl/2 = + a Moreover, Boltzmann and Matano have shown how D may be calculated as a function of concentration over the whole range of composition from c -c, to c = c2 if c as a function of (x/t1/2) for the initial conditions stated in eq 2 has been determined experimentally. Thus, for instance, in principle, the diffusion coefficient in silver-gold alloys may be calculated as a function of concentration for the whole range of composition from only one diffusion experiment with a couple of pure silver and pure gold welded together. If the diffusion coefficient D as a function of concentration c is known, a solution of eq 1 for boundary conditions as stated in eq 2 with arbitrarily chosen values of c, and C2 may be wanted. For instance, if the diffusion coefficient in an alloy A-B as a function of concentration has been derived from an experiment with a diffusion couple involving 0 and 30 pct B as initial. concentrations, the calculation of the concentration distribution in a diffusion couple involving other initial concentrations, e.g., 5 and 20 pct B, may be desired. This problem may be solved by numerical or graphical integration of eq l. The solution of an ordinary differential equation of second order, which results from using (x/t1/2) as an independent variable, can be computed quite rapidly if two conditions for the same value of the independent variable are given. In eq 2, however, two conditions are given for two

Jan 1, 1953

By N. A. Gokcen, John Chipman

D. C. Hilty (Union Carbide and Carbon Research Laboratories, Niagara Falls, N. Y.)—This paper is a very nicely detailed analysis of a difficult problem. I would like to point out that the results that Mr. Crafts and I published a few years ago had no reference to activity, or anything else of a similar nature; our results were strictly empirical. It is quite gratifying that we now have a case where results involving activity coefficients and results derived from direct observations on actual steel melts are practically identical. When two different laboratories, working from two entirely different approaches, come out with results in such good agreement in their major significance, that is an achievement. It is something that was not possible 15 or 20 years ago. There is one question I would like to ask Dr. Chip-man. It has to do with a very minor point of disagreement in these results. When we reported the kink in the Si-O solubility curve I think you may recall that it came at the different temperature levels at about the order of 0.015 to 0.03 pct 0 and 0.03 to 0.07 pct Si—we also pointed out that we had difficulty in obtaining data at that level, although we finally did get some. I note in going through the data for the present paper, that there are no samples in those particular silicon and oxygen ranges. I wonder if that was purely accidental or was there a reason for it. D. E. Babcock (Republic Steel Corp., Youngstown, Ohio)—Mr. Hilty, do you have any explanation for that discrepancy between Dr. Chipman&apos;s curve and your own Mr. Hilty—Our explanation for it at that time was that for some reason our system probably was not in true equilibrium with SiO, that is, in equilibrium with the silica crucible at that level. We did observe, however, that that was the level at which both the metal and the slag became saturated with SiO,. On the average, in studying inclusion formation in small ingots permitted to solidify normally from the molten state, we observed pure silica inclusions at silicon contents over about 0.05 pct and FeO type inclusions at silicon

Jan 1, 1953

By Jun Hino, P. G. Shewmon, P. A. Beck

THE investigations of Crussard,&apos; of Guinier and Tennevin,&apos; and of Dunn and Daniels," indicate that the subgrains formed in a cold worked and annealed metal are capable of growing at each other&apos;s expense during annealing, if the temperature of annealing is sufficiently high and the time is long enough. The results of Dunn and Daniels are particularly convincing in showing that subgrain growth is essentially the result of the free surface energy associated with the subboundaries. In subgrain growth, as in ordinary grain growth, energy is gained as a result of the decrease in total subboundary surface area per unit volume. Recently, Wood and Scrutton4 found that the rate of subgrain growth upon annealing increased very considerably, if simultaneously a creep strain was applied to the specimen at a low strain rate. Working with 99.98 pct pure fine-grained aluminum, these investigators found that the continuous X-ray diffraction back-reflection rings of material strained at room temperature remained continuous after heating for ten days at 250 °C. However, when heated at the same temperature under a stress of 1000 psi even for only three days, the formerly continuous X-ray diffraction rings broke up into numerous dots, which were fairly clearly separated from each other. The continuous X-ray diffraction rings were interpreted as indications of a very small subgrain size, not resolved by the X-ray diffraction method used. The breaking up of the continuous X-ray diffraction ring during annealing under stress was taken as an indication of a great increase in subgrain size, so that the individual subgrains could then be resolved. The effect of simultaneous strain at a low strain rate in accelerating subgrain growth, discovered by Wood and Scrutton and designated by them as "cell growth," is of fundamental importance. The experiments described in this note were carried out in order to confirm Wood and Scrutton&apos;s results by direct metallographic observation. Also, information was sought as to the minimum creep strain necessary to produce this effect. A fine grained high purity aluminum strip was prepared by alternate 33 pct rolling and annealing treatments for 1 hr at 350°C. Specimens cut from this strip were subjected to a relatively fast creep strain of 7.2 pct in 3.5 min at 300°C under a constant load initially corresponding to 1185 psi. The subgrains set up were large enough (about 0.015 to 0.03 mm) to be clearly observed (Fig. 1) at X200 magnification with polarized light, after electrolytic polishing and anodic etching, producing a fine oxide film." The corresponding X-ray diffraction pattern is shown in Fig. la. After the fast creep strain treatment a portion of the specimen was subjected to a creep strain of 8.3 pct in 44 hr at 350°C under a constant load initially corresponding to 320 psi. Another portion, annealed under the same conditions, but not strained, served as control specimen. The subgrain size of a typical area of the specimen annealed under strain and of the one annealed without strain is shown in Figs. 2 and 3 (X-ray diffraction patterns, Figs. 2a and 3a). Annealing without strain produced clearly observable subgrain growth (subgrain size: about 0.03 to 0.05 mm). The effect of simultaneous strain was to increase greatly the rate of subgrain growth (resulting in a subgrain size of approximately 0.05 to 0.13 mm), in accordance with Wood and Scrutton. In another experiment, the effect of the amount of simultaneous strain was studied. The initial subgrain structure was set up by fast creep, as described previously. The specimen was then heated at 350 °C under a constant load initially corresponding to 320 psi, as above, for 2.2 hr (0.24 pct strain), and 8.8 hr (0.58 pct strain). Comparison with the corresponding unstrained control specimens by means of X-ray diffraction showed that 0.58 pct strain definitely had an effect, but the effect of 0.24 pct strain was doubtful.

Jan 1, 1953

By R. B. Burt, J. A. Barr, I. S. Tillotson

DISCUSSION Howard Howie (Knoxville, Term.)—The authors are to be congratulated on the presentation of a paper containing so much valuable information on the pipeline transportation of phosphate, as there is very little literature on the subject. The writer is especially interested in the paper, as he conceived the arrangement of the Akin and Godwin plants and was in charge of the design work and the engineering incident to their construction. The Akin and other phosphate deposits in the Tennessee phosphate area lie on beds of limestone that are very irregular. The limestone beds, after the phosphate matrix has been removed, are similar in appearance to land severely eroded by the action of water and denuded of top soil. Depressions in the limestone, called cutters, are irregular in depth with vertical or overhanging walls, having the general appearance of cracks in dried clay. They change abruptly in direction, width, and depth, and vary on the Akin tract from 1 to 25 ft in depth and from 1 to 50 ft in width. Pinnacles of limestone commonly occur in the cutters which appear, when exposed, like small clifflike islands in a river. Limestone floats also occur. The phosphate matrix fills the cutters and covers the uncuttered areas, the thickness of the cover varying continually and sometimes rather abruptly. It occurs generally as stratifications of phosphate rock and clay of varying thickness. The phosphate rock in the matrix varies in hardness and in percents of silica, lime, iron oxides, and fluorine, and the clay varies in toughness. In some places the deposit consists of narrow strata of rock almost devoid of clay streaks. In other nearby locations the clay will predominate. When it is excavated, the phosphate rock breaks into thin irregular lumps, locally known as plate rock. Limestone lumps are also excavated with the matrix. Akin plate rock is generally much softer than that occurring in other deposits in the area. Because of the above described physical and chemical variations of the excavated material, the resultant slurry varies in size distribution, specific gravity, and percent of slimes. When the rock is soft or when there is an increase of clay, the slime fraction is greatly increased as it passes through pumps and pipelines, resulting in reduced pipe friction. It is obvious that the longer the pipeline the greater the reduction of coarse fractions into fines, causing a decrease in pipe friction that cannot be accurately evaluated. The matrix is mined with a dragline that drops it into a hopper with a grid composed of 9-in. parallel bar spacings located above the hammer mill. The matrix on, and passing through the grid, is subject to the action of powerful sprays which wash it down to the hammer mill, together with any limestone lumps that are not removed before passing through the grid. The hammer mill reduces the feed to lumps of plate rock and clay, most of which will pass through the 8-in. pump suction. The mixture discharges into a pool containing the pump suction pipe. Water from a hydraulic nozzle moves the mixture to the pump suction intake. The pump, driven by a variable speed motor, is the same size as the pumps mentioned on p. 279. Provision is made to remove any lumps that lodge in a bend in the suction pipe in a manner similar to that used in the Florida phosphate fields. The hammer mill and pump units are mounted on wide steel skids so that they can be moved as the mining operation progresses. The discharge from the pump flows through an abrasion-resistant spiral welded steel pipe 81/4 in. actual inside diam, 8 in. nominal diam, for a maximum distance of 2200 ft, which is the limiting pumping distance for one pump. This pipeline, referred to hereafter as pipeline A, discharges into a ball mill without balls, which in turn discharges into a rotary screen attached to it that separates the slurried matrix into 11/4-in. oversize and undersize fractions. The oversize is returned to the mill for further reduction; the undersize is pumped to a Dorrco washer and then flows into a hydroseparator 160 ft in diam. In spite of the size reduction in the hammer mill and the blunging and washing of the slurry in its passage through the pump, pipeline, mill, and washer, the discharge to the hydroseparator frequently contains mud balls almost perfectly spherical. Sometimes the discharge from the 16,000-ft pipeline at Godwin contains mud balls the size of bird shot and smaller. This pipeline will be referred to subsequently as line B. Liquid caustic is added to the slurry at the Akin plant before its passage through the hydro-separator, which decreases the size of particles in the overflow by dispersion. In passing through pumps 1, 2, and 3 and pipeline B, the slime fraction in the underflow is increased by abrasion and blunging and also by continuing dispersive action of the caustic. The matrix for use in the experimental tests referred to on p. 279 was obtained from three small surface openings on the Akin tract that were made previous to the purchase of the tract by the Authority. Matrix used in the 2 and 4-in. experimental pipeline tests was taken from the three openings and proportioned to obtain a sufficient quantity that would be fairly representative of the average in the Akin deposits. Prospecting samples of matrix had been obtained from drill holes which showed no small variation in physical and chemical properties. Some of the physical variation is evident from the size distribution of solids in samples taken during the tests covering line B flows so thoroughly made by the Authority und&apos;er the direction of Mr. Burt, see Table V, p. 280. Hydraulic gradients for a pipe of 8-in. diam were derived from the 2 and 4-in. pipeline tests using the so-called representative matrix as above described, and plotted on the profile of pipeline B. Gradients of other materials in slurry form passing through pipelines that bore some similiarity to the Akin matrix slurry were also plotted. After a study had been made of the hydraulic gradients plotted on the profile and the varying slurry flow that would probably occur during actual operation, three pumps were ordered, referred to as No. 1, 2, and 3 on p. 279. No. 1 and 2 pumps were installed and the third kept in reserve should the operation of 1 and 2 pumps prove satisfactory, since installation of the third pump would require an attendant, as well as the laying of 5400 ft of pipe to supply it with seal-water from the Akin plant. Subsequently, it was found desirable to install the third pump to maintain capacity when the slime fraction was low and the coarse fractions were large. Reference to Fig. 6 will show that the flow in B line goes upgrade in three locations. At the outlet at Godwin, the slurry flows between two 45" bends for an approximate distance of 18 ft to rise above the ground a sufficient height to discharge into a launder feeding the first classifier. This condition requires extra energy, which is taken care of by keeping the hydraulic gradient a sufficient distance above the high points. Although there are rather heavy upgrades in the line, the choking condition that might occur at the

Jan 1, 1953

By J. H. Henderson, H. J. Ledbetter, N. B. Gove, J. D. Griffith

INTRODUCTION The results of a series of laboratory flood tests using liquid Iso-butane to displace refined oils from test cores are pre- ented and interpreted on an empirical bask. The study Revealed the similarity of the miscible liquid displacement to that of the immiscible-fluid displacement mechanism. The efficiency of the iso-butane flood decreased markedly as the oil Viscosity increased. but the effect of injection rate on the effectiveness of the primary production stage was negligible over the range investigated. The presence of free-gas saturation prior. to iso-butane breakthrough increased the volume of iso- Butane required to recover a given percentage of the oil present. Injection of liquid i.e.-butane prior to water follicle sculpted in a marked improvement in oil recovery by the water flood. INTRODUCTION The production of petroleum is often enhanced by the injec-1i1)n of extraneous fluids into the reservoir. It has been suggeited that the injection or cycling of a wet gas or a liquefied petroleum gas would he instrumental in increasing the effic.ienr!; of oil recover! to a greater degree than the commonly injected fluids. dry pas and water. Although instances of injection of light liquid hydrocarbons are not unknown, a systrmatic recording of the result is unavailable and superfi- cially, the practice gives the impression of being economicaIIy unsound. For specific types of displacement, analytic: solutions have been advanced which aid in understanding the physical mechanisms involved. However, there is no generalized theoretical concept which permits adequate prediction of displacement efficiency from a knowledge of readily measured reservoir rock and fluid properties. The Buckley-Leverett approach to oil displacement by an immiscible phase is an admirable analysiy of that type of mechanism. Dykstra and Parsons have introduced a useful concept in their evaluation of the role of the mobility ratio and its merit in rationalizing displacement phenomena. Everett, Gooch and Calhoun3 in their report on the effect of viscosity ratio and miscibility have pointed out the lack of a comprehensive theoretical approach and the desirability of investigating the mechanism of miscible-miscible displacement. In lieu of a well-developed theory concerning miscible-111isci1)le displacement and in view of the scarcity of engineering information on actual LPG injection trials, the limited program of laboratory experimentation described below was undertaken. OBJECTIVES The original broad objectives of the program, to study the oil recovery process using LPG as the displacing phase, defined the direction and scope of the laboratory tests. The specific objective. of the experimentation were to evaluate

Jan 1, 1953

By E. W. Filer, L. S. Darker

ONE of the primary purposes of this investigation was to determine how far blast-furnace metal and slag depart from equilibrium, particularly with respect to sulphur distribution. In studying the equilibrium between blast-furnace metal and slag, there are two approaches that can be used. One method is to use synthetic slags, as was done by Hatch and Chipman;&apos; the other is to equilibrate the metal and slag from the blast furnace by remelting in the laboratory. In the set of experiments here reported, metal and slag tapped simultaneously from the same blast furnace were used for all the runs. The experiments were divided into two groups: 1—a time series at each of three different temperatures to determine the t.ime required for metal and slag to equilibrate in various respects under the experimental conditions of remelting, and 2—an addition series to determine the effect of additions to the slag on the equilibrium between the metal and slag. An atmosphere of carbon monoxide was used to simulate blastfurnace conditions. The furnace used for this investigation was a vertically mounted tubular Globar type with two concentric porcelain tubes inside the heating element. The control couple was located between the two porcelain tubes. The carbon monoxide atmosphere was introduced through a mercury seal at the bottom of the inner tube. On top, a glass head (with ground joint) provided access for samples and a long outlet tube prevented air from sucking back into the furnace. The charge used was iron 6 g, slag 5 g for the time series, or iron 9 g, slag 7 % g for the addition series. This slag-to-metal ratio of 0.83 approximates the average for blast-furnace practice, which commonly ranges from about 0.6 to 1.1. A crucible of AUC graphite containing the above charge was suspended by a molybdenum wire in the head and, after flush, was lowered to the center of the furnace as shown in Fig. 1. The cylindrical crucible was 2 in. long x % in. OD. The furnace was held within &3"C of the desired temperature for all the runs. The temperature was checked after the end of each run by flushing the inner tube with air and placing a platinum-platinum-10 pct rhodium thermocouple in the position previously occupied by the crucible; the temperature of the majority of the runs was much closer than the deviation specified above. The couple was checked against a standard couple which had been calibrated at the gold and palladium points, and against a Bureau of Standards couple. The carbon monoxide atmosphere was prepared by passing COz over granular graphite at about 1200°C. It was purified by bubbling through a 30 pct aqueous solution of potassium hydroxide and passing through ascarite and phosphorus pentoxide. The train and connections were all glass except for a few butt joints where rubber tubing was used for flexibility. The rate of gas flow was 25 to 40 cc per min. As atmospheric pressure prevailed in the furnace, the pressure of carbon monoxide was only slightly higher than the partial pressure thereof in the bosh and hearth zones of a blast furnace—by virtue of the elevated total pressure therein. Simultaneous samples of blast-furnace metal and slag were taken for these remelting experiments. The composition of each is given in the first line of Table I. There is considerable uncertainty as to the significant temperature in a blast furnace at which to compare experimental results. This uncertainty arises not only from lack of temperature measurements in the furnace, but also from lack of knowledge of the zone where the slag-metal reactions occur. (Do they occur principally at the slag-metal interface in the crucible, or as the metal is descending through the slag, or even higher as slag and metal are splashing over the coke?) The known temperatures are those of the metal at cast, which averages about 2600°F, and of the cast or flush slag, which is usually about 100°F hotter. To bridge this uncertainty, remelting temperatures were chosen as 1400°, 1500" (2732°F), and 1600°C. For the time series the duration of remelt was 1, 2, 4, 8, 17, or 66 hr; crucible and contents were quenched in brine. The addition series were quenched by rapidly transferring the crucible and contents from the furnace to a close-fitting copper "mold." Of incidental interest here is the fact that the slag wet the crucible

Jan 1, 1953

By B. L. Averbach, Morris Cohen, L. L. Seigle

Free energies, enthalpies, and entropies of mixing of Ni-Au solid solutions containing 5 to 95 atomic pct Ni have been determined by the electromotive force method at 700° to 900°C. The thermodynamic activities exhibit large positive deviations from Raoult&apos;s law, and the entropies of mixing are almost twice those of ideal solutions. The enthalpies of mixing are positive (heat is absorbed) and are attributable to the lattice distortional energy resulting from the size difference between the nickel and gold atoms. This factor appears to be responsible for the miscibility gap at lower temperatures. IN the thermodynamic study of metallic solid solutions, most interest has been directed toward systems with negative deviation from Raoult&apos;s law, namely, those exhibiting superlattice or compound formation. The results of previous investigations are summarized in recent publications.&apos;-&apos; Relatively little experimental work has been carried out on solid solutions which manifest a positive deviation, possibly because the range of solubility in such cases is usually quite limited. Nevertheless, the relationship of the thermodynamic properties of these solutions to diffusion, nucleation, and precipitation in the solid state are of considerable importance. The binary Ni-Au alloys are particularly suited to an investigation of these relationships. Despite the presence of a miscibility gap at lower temperatures, Fig. 1, indicating a large positive deviation from Raoult&apos;s law, complete solid solubility is found above 840°C. Moreover, the difference in the atomic scattering powers of nickel and gold is sufficiently great to permit X-ray diffraction studies of atomic arrangements and pre-precipitation phenomena. Radioisotopes of both nickel and gold are available for diffusion work, and finally, a large difference in nobility between the two elements facilitates measurement of the thermodynamic properties. The present paper describes the experimental determination of the free energies, enthalpies, and entropies of mixing of solid Ni-Au alloys. Table I gives a list of the symbols used in the paper. Experimental Method The stability of nickel chloride relative to gold chloride" indicated that the galvanic cell method could be used for determining the thermodynamic properties of Ni-Au alloys. An electrolytic cell (Fig. 2) was constructed, similar to that of Weibke and Matthes,7 in which the electrodes were solid nickel and Ni-Au alloys, and the electrolyte was a fused mixture of alkali chlorides containing NiCl,. The cell electrodes were made from fine gold granules and carbonyl nickel shot melted together under argon, chill cast, swaged to 1/16 in. diam rod, and annealed for one week at 850°C. Commercial reagent and chemically pure grade salts, purified by dehydration, were used for the electrolyte. The cell, operating in an atmosphere of purified argon, was heated in a resistance-wound cylindrical furnace whose temperature was controlled to within ±0.5ºC. The potential developed between the pure nickel and the alloy electrodes, which is related to the thermodynamic properties of the alloys by standard equations to be presented later, was measured with a potentiometer and a mirror galvanometer sensitive to 10-7 v. Dehydration of the electrolyte was carried out in the assembled cell by evacuating at 100°C for about

Jan 1, 1953

By R. S. Busk

A PREVIOUS paper1 has summarized the effect of A all metallic elements on the lattice parameters of magnesium. The present paper deals with the effect of temperature on the lattice parameters and the way in which that effect is modified by alloyed elements. The experimental techniques for sample preparation, exposure to the X-ray beam, measurement of line diameters, and calculation of the parameters were the same as reported in the previous paper. The temperature of the specimen was raised by surrounding the mounted compact with a conical Glas-Col,* the base of which was sealed with Saran film. In this way the temperature of the specimen could be raised to 200 °C, which was the maximum desired in the present study. Control of temperature was effected by maintaining a constant, desired voltage to the resistance coils of the Glas-Col through a Variac. Temperature was measured by an iron constantan thermocouple embedded in the body of the specimerl so that the thermocouple bead was within 1/16 in. of the surface exposed to the X-ray beam. Variation of temperature during an exposure was less than + 1/4 oF. A series of eight alloys, consisting of pure Mg, Mg+Ag, Mg+Al, and Mg+Sn were studied. All percentage values are in atomic percent. The results are given in Table I. The density values given in Table I were calculated from the lattice parameters, using an equation due to Foote and Jette:"

Jan 1, 1953

Most of the production of germanium in the U. S. is from byproducts of smelting Tri-state zinc ore. Only in England has commercial manufacture been reported from coal.

Jan 1, 1953