By E. Goldin, H. J. Juretschke

THE electrical properties of porous conductors have been studied ever since such materials, usually prepared by pressing and sintering of metallic powders, obtained practical importance. In most cases, however, the results have not been easy to interpret because of the great number of independent variables such as powder size, pressure, pressing rate and temperature, subsequent thermal history, porosity, and so on, which enter into the fabrication of industrially desirable materials. In recent years an interpretation of these properties has become of interest because the electrical properties of many new substances, prepared as fine powders by crystallization from the vapor phase or by reactions in the solid state at high temperatures, have to be determined on porous samples formed from the powder. Since theoretically significant information must refer to the fully dense state of the material, it is important to relate the electrical properties measured on such porous samples to those expected for a sample of 100 per cent density. A simple theory for the porosity dependence of the electrical conductivity and the Hall effect was recently proposed by Juretschke, Landauer, and Swanson.' Their model, assuming a distribution of pores of equal size and shape, sufficiently far apart so that each pore is embedded in a region of uni-

Jan 1, 1959

By D. D. Pollock, D. I. Finch

PREVIOUS work' on a four-component system (Cu-Mn-Ni-Fe) resulted in the development of consistent relationships between the chemical composition and the electrical properties of these manganin-type alloys. The present study was undertaken to develop alloys with temperature coefficients of resistivity and thermoelectric properties more desirable than those of the manganin type, and to determine whether the relationships which had been found for the Cu-Mn-Ni-Fe alloys could be extended to five-and six-component alloy systems. PREPARATION OF ALLOYS The five- and six-component alloys were made from OFHC copper rod, ARMCO iron, electrolytic nickel, manganese cathode chip, and special high-purity aluminum and indium. A Cu-Mg master was used for deoxidation. The compositions of these materials are given in Table I. The alloys were melted and cast as indicated previously,' except that no cover was used and the melts were teemed. EXPERIMENTAL PROCEDURE The finished wire size of 0.0808 in. diam was again selected for the reason that the test specimens would be self-supporting, thus eliminating any extraneous effects which might have been introduced by winding smaller diameter wire on spools or forms. The following tests were performed on the finished wires: A) Chemical Analyses—All of the components of these alloys were determined by premium gravimetric methods. The principle residual impurity contained in these alloys is 0.008 pct Mg (by weight), maximum. Tables II and 111 present the mean analyses computed from at least four determinations of each constituent. B) Electrical Characteristics—The test procedures forthe determination of the thermal emf vs copper, resistivity, and the resistance-temperature relationship are given in detail in Ref. 1. It was also shown that the resistance-temperature relationship is of the form Pt = P,n + At -B/2, [1] where P, is the resistance at t C expressed in percent of a given standard resistance, P, is this per- 0 centage at 0°C, and A and B are constants for a given, properly treated, composition. The results of the electrical tests are also given in Tables II and 111. INTERPRETATION OF DATA The modified Linde2 formula, known to be valid for dilute binary solid solutions, was applied to the complex Cu-Mn-Ni-Fe type alloys. This relationship is of the form where Ap is the increase in resistivity. Zb the valence of the solute, Zn the valence of the solvent, and K and K are designations assigned by Robinson and Dorn3 to the constants for the periodic group to which solute element belongs. The units of K, are -cm per valence difference squared per at. pct; those of K2 are pa-cm per at. pct. For the sake of brevity, these units are not repeated in the following discussion. Calculations were made to determine if this formula was accurate for five-component systems. No experimental studies were made of the Cu-In and Cu-A1 binary systems. The effects of indium additions upon the resistivity of copper are given by Linde. These data, along with those of the effects of Mn and Fe, permitted the calculation of the effects of Al.

Jan 1, 1959

By James M. Schopf

Gilbert H. Cady (Senior Geologist, Head of Coal Division Emeritus, Illinois State Geological Survey, Ur-bans)— Those coal mining and preparation engineers and operators who read this article will probably be most concerned with those parts which deal with the applied aspects of coal petrology in the fields of mining and technology. Actually the two categories overlap to such a degree that they are essentially one. The article appears to suggest that there are two points of veiw in the field of applied coal petrology. From one viewpoint the interest is in the attributes of the various macerals (Fig. 4)—vitrinite, exinite, and inertinite—-in terms of utilization (when the coal is burned, coked, gasified, hydrogenated, etc.). From the other point of view, assuming that the macerals do possess individuality in behavior, interest attaches to the possibility that coal of a particular type (maceral composition) can be prepared by discriminating methods of preparation and blending. Most of the 29 items listed for mining and technology can be assigned to one or the other of these two categories. Somewhat the same simplicity that resides in the items of the proximate chemical analysis is desirable for the petrologic analysis. This simplicity appears to be fairly well achieved by the group maceral device provided mineral matter is also included. At present, without fully adequate experimental substantiation, the three types of material represented by the group macerals vitrinite, exinite, and inertinite are regarded as sufficiently different in composition and properties so that the preponderance of any one type gives the coal distinctive properties provided it is not too high in rank. This appears to be increasingly true with coals of decreasing rank from medium volatile bituminous coals downward. The article reflects the great emphasis placed on the technique of descriptive coal petrology in America. Such description has resulted in a good understanding of the nature of the fundamental variability in the physical composition of bituminous coals. Such understanding has been attained very largely by the thin section technique used in coal bed profile analysis introduced by R. Thiessen after the manner suggested by the data assembled in Table 11. In contrast, the group maceral concept of coal analysis in terms of the categories indicated on the left hand side of Fig. 4 is particularly useful for broken coal analysis and applied coal petrology, in which evaluation is largely based on quantitative concepts. It is inadequately emphasized in this article that although the Thiessen procedure is suitable for the purpose of petrologic description in which texture and orientation are of critical importance, it is less well adapted to the technological uses of applied coal petrology. No doubt those persons whose interest may have been aroused in the possibilities of more refined coal preparation by this and other recent contributions to the literature of coal petrology will understand that certain technical aspects of coal petrology, particularly in the field of descriptive petrology, are still a matter of some controversy among the coal petrologists, but they will also appreciate that Schopf has made an important contribution to the field of coal petrology in America by pointing out that such petrology requires consideration of disoriented or broken coal samples and that results are expressed less in descriptive terms than in quantitative values with respect to the four types of material composing coal—-vitrinite, exinite, inertinite, and mineral matter. Unfortunately because so much American coal petrology has been descriptive of the coal in the bed there is a dearth of literature on applied coal petrology. Research and experimental data in this field are greatly needed.

Jan 1, 1959

By J. Halpern, D. R. McKay

SOME of the most important hydrometallurgical developments in recent years relate to processes involving the oxidation of sulfide minerals in aque- ous suspension at elevated temperatures by air or oxygen under pressure. Among these is the acid pressure-leach process which has been developed, particularly for the treatment of pyritic uranium ores.1-5 In this process, an aqueous suspension of the ore is digested in an autoclave, in which an overpressure of air or oxygen is maintained, at temperatures above 100°C. Oxidation of the pyrite (FeS,)

Jan 1, 1959

By R. T. Hukki

John F. Myers (Consulting Engineer, Greenwich, Corm.)—Since the art of comminution has lain practically dormant for many years, it is very interesting that R. T. Hukki approaches the subject with a new concept. One is reminded of the research carried on by A. W. Fahrenwald of Moscow, Idaho, a few years ago. Fahrenwald mounted a steel bowl on a vertical shaft. The balls and ore placed in the bowl were rotated at fast speeds, thus simulating the supercritical speeds used by Hukki. The rolling action of the balls against the smooth shell liner has pretty much the same effect. The action is horizontal in one case and vertical in the other. Both researchers report good grinding activity. It is also constructive that such able investigators give to the students of comminution their interpretation of their laboratory results in terms of large-scale operation. History shows that it takes a lot of time for such radically new ideas to be absorbed by the industry. Typical of this is the present-day activity of cyclone classification in primary grinding circuits. The idea of cyclone classification has been kicking around for 30 or 40 years. Certainly we all suspect that the ponderous grinding mills of today, and their accessory apparatus, large buildings, etc., will ultimately give way to small fast units, just as this has occurred in other industries over the past 50 years. At the moment there is no evidence that ball and liner wear is prohibitively high. In fact, at the time Fahrenwald was demonstrating his high-speed horizontal machine at the meeting of the American Mining Congress, several years ago, he assured this writer that the balls retained their shape much longer than they do in conventional tumbling mills. Rods and balls that slide (as some operators in uranium plants are experiencing) get flat. Apparently the balls have a rolling action. Mr. Hukki's references to the processing capacity of the Tennessee Copper Co. mills is adequate. Those studying this subject will be greatly interested in the paper presented by Richard Smith of the Cleveland-Cliffs Iron Co. at the annual meeting of the Canadian Institute of Mining and Metallurgy in Vancouver April 24, 1958. This paper will be published during the latter part of 1958 in the Canadian Institute of Mining and Metallurgy Bulletin. Hukki's pioneering spirit is to be commended. R. T. Hukki (author's reply)—It has been heartening to read the objective discussion by J. F. Myers. The sincerity of his opinions is further strengthened by the fact that the article he has discussed contradicts in a major way the parallel achievements of his life work. Myers is right in his opinion that in general it takes a long time before new ideas are accepted by the industry. On the other hand, revolutions usually take place at supercritical speeds. There are many indications at present that both the unit operation of grinding and the related subject of size control are now just about ripe for a revolution. In grinding, brute force must ultimately give way to science. Rapid progress can be anticipated in the following fields: 1) Autogenous fine grinding at supercritical speeds will be the first advance and the one that will gain recognition most easily on industrial scale. At this moment, little Finland appears to be leading the world. Crocker recently made a statement that in nine cases out of ten, your own ore can be used as grinding medium more effectively and far more economically than steel balls. This is true. The present author would like to introduce a supplementary idea: In eight cases out of the nine cited above, it can be done at the highest overall efficiency in the supercritical speed range. Fine grinding must be based on attrition, not impact. The path of attrition may be vertical, horizontal, even inclined. 2) In coarse grinding, the conventional use of rods is sound practice. However, even the rods can be replaced by autogenous chunks large enough to offer the same impact momentum as the rods. To obtain the momentum, the chunks must be provided with a free fall through a sufficient height in horizontal mills operated at supercritical speeds. Coarse grinding must be based on impact. Detailed analysis of the subject may be found in a paper entitled "All-autogenous Grinding at Supercritical Speeds" in Mine and Quarry Engineering, July 1958. 3) All conventional methods of classification, including wet and dry cyclones, are inefficient in sharpness of separation. Continuous return of huge tonnages of finished material to the grinding unit with the circulating load is senseless practice. In the near future the present methods will be either replaced or supplemented by precision sizing. These three fields are also the ones to which J. F. Myers has so admirably contributed in the past. Fine Grinding at Supercritical Speeds. By R. T. Hukki (Mining EnGineERInG, May 1958). Eq. 9, page 588, should be as follows: T , c, (a — 6') n D Ltph On page 584 of the article the captions for Figs. 4 and 5 have been placed under the wrong illustrations and should be interchanged.

Jan 1, 1959

By P. G. Shewmon

THIS paper is concerned with the redistribution of a second phase when a 2-phase solid alloy is annealed in a temperature gradient. An examplewhich is discussed in detail is the redistribution of carbides in a low-carbon steel annealed in a temperature gradient below the A, temperature. As a result of such a treatment, the carbides at the cooler side disappear, while those at the hotter side grow in size. In a 2-phase zirconium-hydrogen alloy, the amount of hydride will tend to be increased at the cold end and decreased at the hot end. That such an effect can occur in solid metals is not generally appreciated. However, with the trend toward higher operating temperatures in several fields, this phenomenon will become more important in the future. Actually, such effects should be rather common in the core of nuclear power reactors where the op- erating temperatures are high and temperature gradients are an order of magnitude higher than in previous high-temperature applications of alloys. The purpose of this paper is to point out the existence of such an effect, to discuss the manner in which one predicts whether a redistribution of the second phase will occur in a given system, whether the second phase will go to the hot or cold face, and how rapidly the redistribution will occur. One aspect of this problem has been discussed by pfam and Wernick2who considered the migration of a small liquid region through a solid. In their case, the diffusivity in the liquid is much larger than in the solid and they have interpreted their results successfully by using Fick's first law as the flux equation in the liquid, and taking the concentration gradient from the phase diagram. For all the cases they have studied, this type of analysis predicts that the liquid region migrates from the cold end to the hot end, and this is what was found ex-

Jan 1, 1959

By M. V. Nevitt

THE Cr,O-type, or P-tungsten, structure having the space group (Oh2— Pm,n) is one of the most widely occurring structures found among the intermediate phases involving transition metals. Including the phases reported here for the first time, the total number of these A,B phases now known is 39. Greenfield and Beck' have correlated the lattice parameters of these phases with the Goldschmidt radius of the close-packed chains of A atoms. Laves' discussed the apparent size of the A and B atoms in this structure. Gel1er" proposed a scheme for reproducing the lattice constants of the phases by the use of a list of effective C.N. 12 radii for the component elements. Reported here is a survey of the A,B combinations which appeared favorable for the stability of the Cr,O-type phase but which, at the time the investigation was begun, either had not been reported upon or had conflicting reports as to the existence of the structure. Seventy systems were investigated, and 8 Cr,,O-type structures were found. Six of these also were reported by other investigators in the interval between the start of this investigation and its completion. This survey yielded information as to the influence of the relative sizes of the A and B atoms on the stability of the phase and, for the various families of Cr,O-type phases, the effects of the sizes of the A and B atoms on the lattice constant. Likewise, a somewhat clearer picture of the connection between the position of the A and B elements in the Periodic Table and their Cr,O-type phase-forming tendencies has become apparent. Experimental Procedure Alloys were prepared in the form of arc-melted 3-gram buttons in all cases where the vapor pressure of neither component was high enough to cause

Jan 1, 1959

By J. O. Betterton, W. M. Spicer

The solubilities of antimony in the a and ß-forms of zirconium were determined between 750" and 1300°C. The a-phase forms by a peritectoid reaction, and the a/(a + ß) and ß/(a + ß) phase boundaries rise in temperature with in- ' creasing antimony. Impurities in the 99.95 pct zirconium were sufficient to influence the phase boundaries and the variation reported is approximate. The restricted solid solubility of the terminal zirconium phases, which is especially characteristic of this system, is thought to result from the low free energy of the Zr2Sb phase. ZIRCONIUM-antimony alloys are important in zirconium alloying studies since antimony is one of the highest valent elements which can be used to make zirconium alloys. The dilute alloys are of further interest as they have somewhat better corrosion resistance' than pure zirconium. The first investigation of the phase diagram was made by Russi and wilhelm2 who found a eutectic reaction, liquid (- 17.5 at. pct Sb) = ß zirconium (- 11 at. pct Sb) + Zr2Sb, at 1430°C'. The Zr2Sb phase was of complicated hexagonal structure, and by thermal analyses of the relatively impure alloys then available, Russi and Wilhelm found evidence for the peritectoid formation of the a-phase. EXPERIMENTAL In the present work, the phase diagram was re-investigated in the region 0 to 5 at. pct Sb and 750" to 1300°C using iodide-zirconium alloys. Details of the procedure have been described earlier. Essentially the alloys were prepared by arc casting and were then examined by the annealing and quenching method. The times of annealing varied from 1 hr at 1300°C to 30 days at 760°C. As in other zirconium phase-diagram studies1"5 the impurities in the zirconium were still sufficient to affect the results, and the experiments will therefore be described in 3 parts. The results from the first 2 parts of the work are shown in Fig. 1. Here the ß/(ß + Zr2Sb) and a/(a + ZrzSb) phase boundaries were determined with alloys made from 99.9 pct zirconium,* and cast under such conditions that the Vickers hardness of a alloys extrapolated to 95 to 110 VPN at 0 at. pct Sb. Such alloys were not suitable for investigations of the (a + ß) region, and the results shown in Fig. 1 near the (a+ ß) and (a +ß + Zr2Sb) regions were determined with purer alloys. These alloys had an extrapolated hardness range of 75 to 85 VPN and were made from 99.95 pct zirconium. A deviation from binary equilibrium occurs in Fig. 1 as indicated by the (a + ß) region of pure

Jan 1, 1959

By R. Bakish

A. B. MICHAEL and F. J. Huegel1 recently re- ported on dislocation configurations in are-cast columbium. This communication discusses observations made in our laboratory on etch structures believed to be associated with dislocations

Jan 1, 1959

By M. T. Simnad, R. F. Mehl, L. Yang

Techniques for studying marker movement in K-Rb interdiffusion have been worked out. The results indicate that Rb diffuses faster than K and that the ring mechanism of diffusion cannot be the dominant one operating in this case or probably in cases involving other alkali metals, despite their low ion core repulsive energies. SEVERAL theoretical attempts have been made in the past decade to elucidate the mechanism of diffusion in body-centered-cubic metals. No general agreement, however, has been reached by different authors. Zener,1 and later LeClaire,2 on the basis of a correlation between the entropy of activation for self-diffusion and the temperature dependence of the elastic constants, predicted that a ring mechanism should operate in the diffusion of body-cen-tered-cubic metals. Paneth3 calculated the activation energies of various ring, vacancy, and interstitial mechanisms for the self-diffusion in alkali metals and concluded that the most likely one was based on the linear motion of "crowdions," which is in fact a different form of interstitial diffusion. Fumi,1 however, showed that the experimental values of the activation energies for self-diffusion in the alkali metals could be better accounted for if the diffusion process in these metals was assumed to follow a vacancy mechanism. The same conclusion was reached by Kojima5 for the self-diffusion in lithium. Experimental evidences published during the past few years seem to exclude the ring mechanism as the predominating one in the diffusion of body-centered-cubic metals. For instance, maker movement has been observed in ß-brass, first in this laboratory" and later by Resnick and Baluffi.5 Shewmon and Bechtoldh also found marker movement in the body-centered-cubic system Ti-Mo and showed that the argument which led Zener and LeClair to favor a ring mechanism was not incompatible with a vacancy mechanism. In spite of this, it seemed to the authors that further experimental tests should be made by studying the Kirkendall effect in body-centered-cubic systems that characteristically have small ion core repulsion, such as the alkali-metal systems. Since the ion core repulsion term constitutes the main part of the activation energy needed for the rotation of a ring, such a test should be the most critical of all. The system K-Rb was chosen for experimental study because these metals form a continuous series of solid solutions. Experimental Investigation Owing to the extremely active nature of these two metals, a brass dry box (18 x 11 x 10 in.) was built for making the diffusion couple. It had a big lucite window on top, two side ports through which neo-prene-rubber gloves were inserted, and another side port covered with an optically flat-glass window for microscopic examination of the sample. Inside the box there were a circulating fan driven with a rotating horse-shoe magnet located outside the box, a heater used to generate potassium vapor for getter-ing the box, and a cold trap for keeping the inside of the box cool. Chemically pure grade K and Rb were triple distilled before they were transferred in vacuum into cylindrical steel molds kept in pyrex-glass ampules, Fig. 1. The latter together with the tools needed for making the diffusion couple were put into the dry box. After the box was flushed with purified argon and gettered with potassium vapor, generated from a heated steel crucible inside the box, the glass ampules were broken and the mound on the top of the alkali-metal ingot was cut off with a razor blade to yield a flat surface. To make the diffusion couple, one K ingot and one Rb ingot were pushed out of the molds together with their steel supports by screwing a metal plunger into the bottom of each mold. They were then laid on a brass cradle inside the assembling carriage (shown separately in Fig. 2) with the flat faces opposite to each

Jan 1, 1959

Jan 1, 1959

By D. W. Lillie

It has been demonstrated that considerable bend ductility exists in bulk specimens of polycrystalline high-purity silicon. The possibility of hot-forming at 1200°C is suggested. EXCELLENT corrosion resistance in many media and low cross section for absorption of thermal neutrons (0.13 barn) would make silicon of interest to nuclear engineers were it not for extreme brittle-ness and the difficulty of fabrication by any reasonable means. The use of silicon for structural purposes also has been considered in view of its light weight and oxidation resistance. Johnson and Han-sen' have investigated the properties of silicon-base alloys and concluded that there was no way of making pure silicon or silicon-rich alloys ductile at room temperature. In view of reports of appreciable ductility in germanium single crystals above 550°C'." and some plastic deformation in single-crystal silicon above 900oC,' the present investigation was undertaken to define more precisely the limits of high-temperature ductility in pure silicon. After this investigation was begun torsion ductility in both germanium and silicon was reported by Greiner." Through the courtesy of F. H. Horn, a small bar of cast extra high-purity silicon was obtained and small bend specimens were made from it by careful machining and grinding. All of the reported tests results were obtained from samples from this bar (bar No. 1) and one other of similar source (bar No. 2). No complete analysis was obtained but, based on analysis of similar semi-conductor grade material, metallic impurities were under 0.01 pct total. Vacuum-fusion analysis for oxygen showed a value of 0.0018 2 0.0003 pct for the first bar tested and metallographic analysis showed no evidence of a second phase. Bend tests were carried out on an Instron tensile machine using a bend fixture with a 1 -in. span loaded at the center. Supporting and loading bars were 0.250 in. round and the load was applied by downward motion of the pulling crosshead of the machine. Specimen thickness and width were approximately 0.10 in. and % in. respectively. Loading rate was controlled by holding crosshead motion constant at 0.02 ipm. In some cases a smaller specimen was used on a 5/8-in. span with a 0.129-in.-diam loading bar. The entire bend fixture was surrounded by a hinged furnace and all heating was done in air atmosphere. Temperature measurement was made with thermocouples fastened directly to the bend fixture within less than 1 in. from the specimen. Autographic stress-strain curves were recorded during each test, and breaking load, total deflection, and plastic strain could be obtained from these curves. Stress was calculated from the beam formula S = 3PL/2bh2, where P is the load in pounds, L the span in inches, b the specimen width in inches, and h the specimen thickness in inches. This formula is strictly correct only in the elastic range but has been used to calculate a nominal stress for convenience in the plastic range. The stress given is the maximum stress in the specimen. Results The results of the complete series of tests are shown in Table I. The first group of tests (specimens Nos. 1-6) showed the beginning of plastic flow at a test temperature of 900°C, so two additional tests (Nos. 8 and 9) were made at 950°C on small-size specimens from bar No. 2. Specimen No. 8 was tested in the as-machined condition, and No. 9 was heat-treated in hydrogen at 1300°C for 2 hr, cooled to 1200°C and held 1 hr, cooled to 1000°C and held 1 hr, cooled to 900°C and held 1 hr, and finally cooled to a low temperature before removal from the hydrogen. It is apparent that the heat-treatment had a significant effect on yield strength and ductility. In addition, the magnitude of the yield point was conslderably reduced in the heat-treated specimen as is shown m Fig. 1 by tracings of the stress-strain curves. After obtaining a furnace capable of reaching higher temperatures specimens Nos. 10 to 13 were tested at 1100 and 1200°C. Strain rate was increased by up to a factor of 10 to see whether the ductility observed was excessively strain sensitive. Specimen NO. 10, strained at 0.02 ipm and 1100oC, was still bending at a deflection of 0.322 in. when the load rate was increased to 0.2 ipm, resulting in immediate

Jan 1, 1959

By L. W. Berger, R. I. Jaffee, D. N. Williams

The effects of hydrogen on the properties of binary Ti-A1 alloys containing 2.5, 5, and 7 pct aluminum and ternary alloys of the same compositions with added interstitial elements oxygen, nihrogen, and carbon were studied. Aluminum increases the apparent hydrogen solubility of the a-phase, resulting in a marked increase in resistance to impact embrittlement. In the Ti-5Al and Ti-7Al alloys, for example, the addition of 180 and 305 ppm hydrogen, respectively, did not cause embrittlement, while unalloyed titanium was embrittled by as little as 75 ppm. The role of aluminum in increasing hydrogen solubility of the a-phase probably accounts for the excellent hydrogen tolerance of a-ß alloys containing considerable amounts of aluminum. There is some evidence that aluminum retards the rate of hydride precipitation. If so, these alloys may be susceptible to slow-strain embrittlement. UNALLOYED a-titanium is extremely sensitive to small amounts of added hydrogen in that there is a marked decrease in notch properties. For example, as little as 100 ppm hydrogen is sufficient to lower the room-temperature notch-impact strength from over 100 to less than 20 in.-lb.' This loss of impact Strength has been associated with the Presence of hydride phase in the microstructure. Hydrogen in the amounts encountered in commercial practice

Jan 1, 1959

By P. D. Zemany, G. W. Sear, B. W. Roberts

Vanadium metal is embrittled by hydrogen at a temperature as low as 250°C when held in the presence of manganese metal and water vapor in a rough vacuum. It is established that the property changes are caused by the catalytic decomposition of water vapor at the vanadium surface and the diffusion into and solution in the vanadium of the resultant hydrogen. It is found that manganese is a necessary component of the catalyst. The manganese is transported in the vapor phase by an unknown molecule. A deuterium tracer experiment demonstates the role of water vapor in the embrittle-ment process. VANADIUM metal foils were observed to become embrittled' at a temperature of about 300 °C when held in the presence of manganese metal and a small amount of moist air, This paper describes the investigation to find the embrittling agent and an understanding of the relatively low temperature reactions that are involved. Experimental The vanadium metal foil used was prepared by cold-rolling and pack-rolling 32 mil sheet" in a series of steps down to 1 mil foil. The original observation was confirmed by sealing vanadium foils of 3 x 10 sq cm into individual Pyrex tubes with manganese powder† and a con- trol tube containing only the vanadium foil. These tubes were evacuated to 10 -5 mm Hg without baking and sealed. After heat treatment for 200 hr at 300°C, the control foil showed no change in duetility, whereas the foil contained in the manganese— containing tube was embrittled. The visual appearance of each was unchanged. A series of Pyrex sample tubes, about 2.5 cm diam and 25 cm long, were prepared, each containing a 3 x 10 sq cm piece of foil and 5 g manganese powder at the lower end of the tube. By reducing the time of anneal and the temperature of these samples, it was found that embrittlement could be created at 250°C in a time as short as 1 hr. Since the vanadium metal used here has been drastically cold-worked by rolling, it is assumed that it contains a maximum number of dislocations. To check the possible necessity of dislocations in this low temperature reaction, a vanadium foil sample was annealed in Vycor for 2 hr at 800°C to re crystallize and reduce the dislocation concentration. Metallographic examination showed grains which were not visible before annealing. The embrittlement procedure was carried out at 300°C and 3 hr. Upon checking the foil no embrittlement was observed. Further experiments demonstrated that about 6 hr at 300°C are required to create embrittlement in the foil. This delay in the onset of embrittlement in the vanadium foil suggests but does not prove that dislocation channels play a role in the embrittlement phenomena. If manganese metal is necessary for this low temperature embrittlement, do other elements in the transition metals group yield the same result? To check this qualitatively, a group of elements of similar atomic radii were obtained and sealed as before into Pyrex tubes with a sheet of vanadium foil. These tubes were annealed at 250°C for 6 hr and included (with radii)-2 A1 (1.4A), As (1.25A), Be (1.2A), Co (1.25A), Cr (1.45A), Cu (1.25A), Fe (1.25A), Ga (1.2A), Ge (1.25L%), Mn (1.3A), Ni (1.25A), Si (1.2A), Ti (1.45A), Zn (1.3A), air, H,O, 10 cm Hg of dry hydrogen, and MnO, powder. Upon testing the above sample foils for brittleness, only the manganese-containing tube yielded a brittle foil. Manganese Transport—To eliminate contact of manganese metal powder and vanadium foil, sample tubes were prepared with fritted glass barriers. The embrittlement reaction was still found to occur. Thus, the mode of transfer of manganese is certainly vapor transport. A vanadium foil was embrittled by this mechanism in an evacuated Pyrex tube for 8 hr at 300°C. By means of X-ray fluorescence analysis,' the amount of manganese added to the surface was established at 5 ±2 x 10 -6 g per sq cm. Since the average rate of manganese deposition is known, an effective average pressure of an assumed carrier compound can be computed. ___ P = M/T v2p mkT

Jan 1, 1959

By R. D. Pehlke

THE impending commercial importance of iron-aluminum alloys has served as a stimulus for re- search on the preparation and properties of these alloys. However, the activities of the components of the binary system remain undetermined. The experimental determination of the thermodynamic properties of binary solutions of iron and aluminum has been hindered by the high liquidus temperatures

Jan 1, 1959

Jan 1, 1959

By C. Crussard, R. Tamhankar

It is the policy of The Metallurgical Society to provide, in the TRANSACTIONS OF THE METALLURGICAL SOCIETY OF AIME, a prompt and accurate medium for publication of reports of significant new research in both the scientific and engineering aspects of metallurgy. Papers submitted to the Society are judged by competent reviewers accord-ing to established criteria for technical merit, accuracy, originality, and presentation. STAFF: Editor, Gerhurd Derge Carnegie Institute of Technology Schenley Park Pittsburgh 13, Pa. Editorial Assistant, M. A. Redmerski Staff Coordinator, James J. Burke THE METALLURGICAL SOCIETY: W. R. Hibbard, Jr., President; J. C. Kinnear, Jr., Past-President; John Chiprnan, Vice President; T. D. Jones, Treasurer; R. W. Shearman, Secretary. PUBLICATIONS COMMITTEE OF THE METALLURGICAL SOCIETY: A. W. Thornton, Chairman; Dennis Carney, John Chip-man, J. C. Fulton, J. H. Hollomon, H. H. Kellogg, A. E. Lee, R. Maddin, J. D. Sullivan, and D. Swan. Review and selection of manuscripts is under the supervision of the following Publications Committees: Extractive Metallurgy Division: T. B. King, Chairman; S. J. Dickenson, R. P. Hermsdorf, R. Schuhmann, Jr., and P. T. Stroup. Institute of Metals Division: Robert Maddin, Chairman, F. Lincoln Vogel, Jr., Vice-chairman, W. A. Backofen, R. W. Balluffi, J. H. Bechtold, M. B. Bever, R. S. Busk, C. G. Goetzel, Paul Gordon, C. D. Graham, .Jr., Robert F. Hehemonn, R. I. Jaffee, F. E. Jaumot, Jr., Irving R. Kramer, A. J. Lena, Harold Margolin, C. J. McHorgue, Russell A. Meussner, J. B. Newkirk, H. W. Paxton, G. E. Pellissier, I. S. Servi, Alan U. Seybolt, A. J. Shaler, and Jack Washburn. Iron and Steel Division: J. C. Fulton, Chairman; T. B. King, F. C. Langenberg, W. 0. Philbrook, and T. 0. Winkler. Published bimonthly by the American Institute of Mining, Metallurgical, and Petroleum Engineers, Inc., 29 West 39th Street, New York 18, N. Y. Telephone: PEnnsylvania 6-9220. Subscription $20 per year for non-AIME members in United States and North, South, and Central America; $25, foreign; $5 for AIME members. Single copies, $4.00, single copies foreign, $5.00. The AIME is not responsible for any statement made or opinion expressed in its publications . . . Copyright 1958 by the American Institute of Mining, Metallurgical, and Petroleum Engineers, Inc. . . . Registered cable address, AIME New York ... Indexed in Engineering Index, Industrial Arts Index, and Chemical Abstracts... Second class postage paid at New Yark, N. Y., and Ann Arbor, Mich. Volume 212, Number 6.

Jan 1, 1959

By J. Doig, A. A. Bauer, F. A. Rough

AN investigation of the phase relationships between the 6 phases of the uranium-molybdenum and uranium-titanium systems was conducted by studying alloys ranging in composition from uranium-31.5 at. pct Mo to uranium-34 at. pct Ti. A ternary cut showing these phase relationships is presented upon the basis of thermal-analysis data obtained and upon the basis of metallographic and X-ray examination of heat-treated and quenched specimens. Isothermal ternary sections, inferred from phase relationships determined between the two 6 phases, are presented for the uranium-molybdenum-titanium system. In the compositional range investigated, a y-ura-nium solid solution exists at elevated temperatures. At about 900°C the 6-U2Ti phase, with limited molybdenum solubility, forms. Epsilon, a molybdenum-titanium-rich solid solution appears at the same temperature and appears in all phase regions that exist below this temperature except in the terminal 6-phase regions. The y phase is stable to approximately 660°C in titanium-rich alloys; the y and 6-U,Ti phases decompose at this temperature to a uranium in a peritectoid reaction. The y phase in molybdenum-rich alloys of the ternary cut studied decomposes in an apparent eutectoid reaction, at about 593°C, to the 6-uranium-molyb-denum and a-uranium phases. The e phase while present, presumably plays a negligible role in these reactions. Titanium was found to markedly decrease the stability of retained y in these alloys. Age-hardening characteristics developed in titanium-contain ing uranium-molybdenum alloys quenched from 900°C and aged at 500°C are ascribed to decomposition of Y to the a and E phases. INTRODUCTION Alloys of uranium with molybdenum, titanium, and zirconium, respectively, are of great interest because of their potential use as reactor fuels. As a result, this interest extends to the constitution of these alloys, particularly in view of their uniqueness of constitution. In these systems, alone, among known uranium-alloy systems, an intermediate phase forms by direct decomposition of the high-temperature y-uranium phase. As a prelude to possible future alloy development, an investigation has been undertaken of the phase relationships that occur between the intermediate phases of these systems. These phase relationships have already been reported for the intermediate 6 phases of the uranium-zirconium and uranium-titanium systems.' The results of an investigation of the phase relationships between the 6 phases of the uranium-molybdenum and uranium-titanium systems are reported here. The phase relationships that occur in the binary systems pertinent to this investigation are shown in Fig. 1. Phase nomenclature appearing throughout this report is as shown in these diagrams; the crystal structure of the phase is given in Table I. EXPERIMENTAL PROCEDURE Alloys were cast and fabricated to flat plate. Specimens were heat treated and examined metal-

Jan 1, 1959

By H. L. Armstrong

SOLID-STATE diffusion is an important technique in certain aspects of metallurgy, and especially the metallurgy of semi-conductors and semi-conductor devices. If the diffusion is carried out under constant conditions for a time, t, the concentration, C, of the diffusant at a depth, x, below the surface from which the diffusion is carried out is given by an expression of the form. C = Cof(x,Dt) [I] Co being a constant, and D the diffusion constant of the diffusant in the material and at the temperature

Jan 1, 1959

By M. J. Sinnott, J. C. Tobin

A technique for collecting and analyzing the small quantities of gases desorbed on heating metal powders has been developed. The gases collected from copper powders of various types of manufacture have been analyzed and found to contain H2O, CO2, and SO2. The quantities of gas evolved vary from 0.05 to 1.0 milliliter, under standard con-ditons of temperature and pressure, per gram of powder. The source of the gas has been traced to surface films on the powder. IN the powder-metal industry it is recognized that the presence of gases in the powders affects the processing and resulting properties of the sintered product. Several sources for these gases are possible; namely, chemical reactions with the sintering atmospheres, inclusion. of gases during compacting, dissolved gases in the metal powder, and sorbed gases on the metal-,powder surfaces.1, 2, 3 Since the quantities of the gases are relatively small, no direct attempt has been made to collect and analyze them nor to isolate their source. The work that has been done has been concerned with the dimensional stability of the product., its porosity, density, or mechanical and physical properties. Conclusions are drawn on the basis of studies of this type as to the probable effect of gases on these properties. 4, 5, 0 In the present investigation an attempt has been made to obtain quantitative data on the analysis and quantities of gases associated with copper powders manufactured in different ways. Apparatus was constructed to collect gases evolved from loosely packed powder samples on heating to various temperatures under a reduced pressure of helium. The powders were outgassed thoroughly in a vacuum prior to starting the collection operation in order to eliminate mechanically entrapped gases and to prevent the possible reaction of the powder with these gases. Experimental Procedures Materials—The major portion of the investigation was carried out on a single heat of water-atomized, oxygen-free, high-conductivity copper. A relatively coarse fraction of this powder, 20 to 100 mesh, was tested as a mixed powder and as various graded size fractions. The microstructure of this powder showed equiaxed grains and was clean and free from oxides and oxide eutectic. The particle size, as determined

Jan 1, 1959