Search Documents

By M. Z. Mubarok

Effect of single addition of a lignin-based biopolymer additive, DP 2782, at various dosages as well as in combination with thiourea on cathode polarization during copper deposition was investigated by performing potentiodynamic and galvanostatic measurements using a potentiostat. The result of electrochemical measurements was compared with the behaviour of cathode deposition with glue and thiourea additives. Surface micro-appearance of the copper deposit after 1 h galvanostatic scan under current density of 330 A/m2 and various additive type and dosage was evaluated by scanning electron microscopy (SEM) examination. It was found that the addition of 2.5 mg/l biopolymer gave sufficiently polarizing effect of copper deposition. SEM examination of the cathode surface after galvanostatic scan revealed that the combination of the biopolymer with thiourea (2.5 and 3.5 mg/l) resulted in a compact deposit which is comparable with that resulted from the test with glue and thiourea.

By Daniel Kim, Justin McAllister, Shijie Wang

"At the Kennecott Utah Copper Refinery, impurities in the electrolyte are being precipitated in the circulation system and form a hard scale in the piping. This scale must be removed periodically for proper electrolyte flow. Distinct layers of differing composition form as the operating conditions of the tank house change. Scale samples from the inlet and outlet pipes were analyzed to discover the nature of the precipitates. Each sample was sectioned and examined under optical microscopy and SEM. The composition of the scale was analyzed using ICP, XRD, and SEM/EDX mapping. The rate of deposition was determined by measuring the amount deposited on new pipes after elapsed time intervals. In order to determine how to minimize the formation of the scale, the mechanism was studied and the results are presented in this paper.IntroductionIn copper electrorefining, impure copper anodes are refined into pure copper cathodes. The impurities from the anodes are either insoluble and report to the slimes or soluble and dissolve concentrating in the electrolyte. These impurities are controlled by bleeding electrolyte from the system. Over time, the impurities combine to precipitate a hard scale on the surfaces contacted by the electrolyte. The scale causes problems with tank house circulation systems. In order for the refinery to operate properly, the scale must be removed periodically from the walls of the pipes. The first step to control the buildup of scale on the pipes is to understand the composition and the phases that are present in the scale."

Jan 1, 2012

By Ji-He Wei

The ESR of Cu-Cr-Zr alloy has been experimentally investigated. The remelting experiments have been carried out with different slag fluxes in the Cal, + Nal, CaF2 + ZrO2 and CaF2 + NaF + ZrO2 systems on an ESR furnace of 25kg capacity; using a water-cooled copper mould of 96.5 mm diameter, with the forged square bar electrodes of 50x50 mm2. The slag amount was taken to be 1.5 kg. The remelting current and voltage used were 1600-1800A and !5-25K, respectively. The influence of the slag composition on the stability of the remelting process and the losses of alloying elements (2r and Cr) has been considered and examined. The technologies of hot working and heat treatment of the ES ingot have been described and discussed. Some physical properties of the slag in a CuF2 + NaF + ZrO2 system and the remelted Cu-Cr-Zr alloy have been determined. The results indicated that with the slag flux of CaF2 + NaF + l0 mass % ZrO2 and the other operation parameters employed, a high quality ingot of Cu-Cr-Zr alloy may be obtained at the considerably high yields of Zr and Cr by means of ESR. For the remelted Cu-Cr-Zr alloy with a specified composition of 0.5 mass % Cr and 0.1 mass % Zr, the appropriate electrical conductivity, hardness and softening temperature are as high as 45-46S/m, HRB 82-84 and 550°C. respectively. The properties of the Cu-Cr-Zr alloy products are in accordance with and superior to the requirements and specifications of ISO5l82-l99l(E).

Jan 1, 2000

By Jiu-ju Cai, Wen-caho Liu, Fei Liu

"With the northern cities of China as study objects, and to confirm Ground-source heat pump system of the environmental benefit and the developing direction. In this paper LCA was applied to the environmental benefit Ground-source heat pump System from raw materials acquisition to system production, utilization and disposal. The conclusion shows that Ground-source heat pump system of the environmental benefit in the northern cities of China. The result showed that Ground-source heat pump system had remarkable environmental benefit. 1. Introduction Life cycle assessment Originate in the sixties of last century, what it paid close attention to is to obtain processing from products raw materials, the processing of products produces, products transportation, products use and maintain to the influence to environment of course. It is a products -oriented environmental management style, it is the environmental management mode of meeting the needs of sustainable development strategy [1]. The research object was in the city and lie in the North of China, would undertake Beijing Olympic Games some football matches in the second half of 08, in order to improve the local environment, adjust the energy structure, reduce the heating consumption of urban coal in the centre, eliminate the coal-burning boiler under 10 tons, since 2005, the local government promotes and utilizes actively the heat pump technology in the source substitute the heating of coal-burning boiler. At present, this area is adopted the technological heating area of heat pump of source reach 20 million square meters, account for this area heat 11.2% of area always, it is estimated, by 2010, adopt the technological heating area of heat pump of source will reach 65 million square meters, the proportion of the area rises to about 30% to account for this area and always heat [2 ]. Study to the whole lifespan of heating system of heat pump of ground source of this area on the basis of LCA method, obtain the products impact on environment of different stages and environmental benefit, find out and reduce or dispel the measure of the influence, improve the environmental benefit of the ground source heat pump heating system.2. MethodologyThe research approach used in this research is the Life cycle assessment, the frame of the research approach is goal and scope definition, the inventory analysis, impact assessment, interpretation.[3][4][5]"

Jan 1, 2008

By Esperidiana A. B. Moura, Elizabeth Carvalho L. Cardoso, Glauson Aparecido F. Machado, René R. Oliveira

Plastics global annual production exceeds 250 million tons and more than 40% of the total plastic production is used as packaging materials. In recent years polymeric materials derived from biomass have received great attention due to scarce petroleum resources and environmental concerns. PLA is one of the most extensively studied bio-based and bio-compostable aliphatic polyesters; nevertheless, high brittleness and low toughness limits its application. Blending PLA with PBAT (Poly(butylene adipate-co-terephthalate)), an aliphatic-aromatic copolyester, was the solution found due to its high toughness and biodegradability. Differences between PLA and PBAT solubility parameter values lead to the formation of immiscible blends as well as reduction in their mechanical performance besides a poor morphology; so, 5% of pre-irradiated PLA and a previous compatibilized PLA/PBAT (EcovioTM) were added to PLA/PBAT blends in order to improve miscibility phases. Investigations were accomplished on phase morphology (SEM), mechanical properties, thermal behavior and X-ray diffractions (XRD).

Mar 1, 2017

By Xinhua Wang, Xuefeng Liu, Die Yang, Lifeng Zhang, Wen Yang

"CSP thin slab continuous casters are well used in recent years. The control of heat transfer in the mold is very important because it is correlated with several slab defects. The mean heat flux of CSP mold was studied based on the plant production data of LCAK steel and weathering steel. The effect of various operation conditions on the heat flux was analyzed and discussed. The results showed that the heat flux was 2.1-2.6 MW/m2 on the wide face and 1.2-2.2 MW/m2 on the narrow face for the casting of LCAK steels. During the casting of weathering steel, the heat flus was mostly 2.05-2.5 MW/m2 on the wide face and was 1.1-1.8 MW/m2 on the narrow face. The heat flux depended largely on the casting speed. The heat flux on the wide face increased obviously with increasing casting speed when the casting speed was relatively low; however, at high speed, the heat flux increased slowly or kept constant. At low casting speed, the heat flux depended little on the superheat of the molten steel. The mean heat flux depended little on the level fluctuation at continuous casting mold.IntroductionCSP thin slab continuous casters are used more frequently in recent years for its low cost of construction and manufacturing. The structure of CSP mold is very different from that of conventional thick slab casting mold, inducing the difference of heat flux between them. There have been some studies about the heat flux of thick and medium slab casters [l, 2]. Heat transfer in the mold is very important for the solidification of molten steel because it is correlated with several slab defects such as slab break-out, longitudinal crack, and surface depression. Moreover, higher casting speed is desired to improve the productivity. The control of solidified shell is extremely important. The heat flux is largely influenced by several casting parameters such as the cooling intensity of the mold, the casting speed[3], the mold flux powder [3, 4] and the carbon content of steel as well [5]. The investigation on the heat flux and affecting parameters can help to understand the solidification of molten steel in the mold."

Jan 1, 2013

By Mariana H. Staia

Thermodynamic calculations based on the free energy minimization method were performed for the system Ti-Fe-Mn-0-C1-C in order to evaluate the chemistry associated with the chlorination of an ilmenitic concentrate using CCl4. In the calculations various weight ratios of FeTi03/ CC14, a , were considered, which varied between 0.32 to 0.98 at temperatures ranging from 673 K to 1273 K , at atmospheric pressure. The results obtained indicated that the operating conditions for a process in a packed bed reactor, which implies the chlorination of both Fe and Ti, are 0.39 < a < .49 at T 1173 K.

Jan 1, 1993

By Denise Corrêa de Oliveira

Common dry batteries use zinc as the negative electrode. Producers commonly use additives such as mercury to prevent corrosion and to increase the mechanical resistance of the zinc anode. Alkaline batteries also contain it, as an anti-corrosive agent. When mixed with the common municipal solid waste, heavy metals as zinc and mercury pollute soil and ground water supplies, moving to the food-chain and affecting human health. Due to these possible damages, this kind of waste must be properly disposed, or recycled. Thus, even in low amounts (ppm) in batteries, mercury has to be eliminated or, at least, its content should be reduced. This work presents the use of pyromettalurgical processes, to reduce mercury content and recover zinc. The tests involved batteries treatment at temperatures from 300° to 1000°C. Mercury is eliminated up to 650°C, and zinc is evaporated at higher temperature treatment. C

Jan 1, 2001

By D. A. Meyn, R. L. Holtz, C. S. Pande, M. A. Imam, D. J. Singh

"Various theoretical and experimental techniques used to search and develop new metal hydride systems suitable for hydrogen storage are described. The main theoretical technique under study makes the use of electronic structure of the candidate materials. Microstructural characterization techniques like transmission electron microscopy are being used to study the hydride formation. Novel processing techniques for material preparation such as those needed to produce thin films or amorphous phases are also being utilized. The techniques are illustrated with results from Pd, FeTi and Mg2Ni systems.IntroductionOf the four methods of hydrogen storage, compressed gas, cryogenic liquid, metal hydrides, and gas-solid adsorption, the metal hydride storage method is more attractive from the point of view of high volumetric density and safety. Compressed gas storage has disadvantages of extreme pressure, weight, and volume requirements, whereas storage of hydrogen as cryogenic liquid is unattractive due to the requirements of extremely low temperatures and high consumption of primary energy. Moreover, the number hydrogen atoms present in a volume of 10- 22 Cm3 (nH) in liquid hydrogen state (- 20K) is 4.2 whereas number of hydrogen atoms that can be accommodated in a free volume of 10-22 cm3 of various hydrides are as follows: LiH--5.9, TiH2--9.2, ZrH2--9.2, VH2--l0.2. High hydrogen concentration is usually associated with a large H/Metal atomic ratio but is also a function of structure."

Jan 1, 1994

By Charles I. Richman

Aquispirillum magnetotacticum (AM) is gram-negative hetrotrophic bacteria that belongs to a class ,of magnetotactic bacteria that have an ecological niche in marine marches and fresh water swamp sediments. Thiobacillus Ferrooxidans (TF) is a Gram-negative, acidophillic chemoliths that may have similar chemical conditions within the cytoplasmic membrane as Aquaspirillum M. to support growth of Magnetosomes. Magnetosomes are cellular bodies that accumulate under slightly aerobic conditions. Magnetotactic motion occurs in an external magnetic field and depends on the medium viscosity. The Atomic Force Microscope equipped with a magnetic tip shows the presence of Magnetosomes in these bacteria strains. The size, shape of magnetosomes in AM and TF strains are characterized.

Jan 1, 1998

By Defeng Zhou, N. Trubaki, Jian Meng, Fanzhi Menga, Xiaojuan Liu, Yanjie Xia

"The microstructure and the electric conductivity of (Ce0.9Nd0.1)1 xMxO2 d (M=Mo, W) solid solutions were investigated. It has been found that their conductivity containing the grain (s gi ), the grain boundary (s gb) and the total conductivity (s t ) at 300°C- 700°C can be ranked as: (Ce 0. 9Nd 0. 1 ) 0.99 W 0.01 02- d (s gi = 0.065 S.cm·1, (s gb = 0.265 S.cm·1, s t = 0.039 S.cm-1) > (Ce0.9Nd0.1)0.99Mo0.01O2- d (s gi = 0.053 S.cm·1, s gb = 0.142 S.cm·1, s t = 0.029 S.cm-1) > Ce0.9Nd0.1 s 2- d (s gi 0.045 S.cm-1, s gb = 0.091 S.cm-1, s t = 0.018 S.cm-1) measured at 700°C. The highest conductivity is obtained in (Ceo.9Ndo.1)0.99W0.01O2 d. These results indicate that (Ceo.9Nd0.1)0.99W0.01O2- d is the most promising electrolyte materials of intermediate-temperature solid oxide fuel cells among (Ce0.9Nd0.1)1-xMxO2- d. IntroductionRare-earth (e.g. La3+, Nd3+, Gd3+ and Sm3l doped ceria-based ceramic materials have been acknowledged to be attractive electrolytes for solid oxide fuel cells operating below 600°C due to their high ionic conductivity [1, 2]. In order to improve ionic conductivity of these electrolytes further, in recent reports [3-6], some aids such as Mo03 [3] etc. in a limited amount can be used which causes extremely high conductivity. For example, Zhou et al. found that with MoO3 doping, the grain boundary conductivity of Nd3+ doped CeO2- d increased notably especially at lower temperatures due to the effect of severely undersized do pants [3]. It is well known that the size of W6+ (rw6+ = 0.60 Å) is close to Mo6+ (rMo6+ = 0.62A) because of lanthanide shrinkage. Thus, rare-earth doped ceria e.g. Nd3+ doped CeO2g with WO3 in a limited amount will be probably good and even better electrolytes. However, much less information is available about these materials. Therefore, in our paper, (Ce0.9Nd0.1)0.99 1-xMxO2- d (M=Mo, W) solid solutions have been prepared and characterized. Much higher conductive electrolytes are found in the series of (Ce0.9Nd0.1)0.99 M0.01O02- d particularly (Ce0.9Nd0.1)0.99W0.01O2- d"

Jan 1, 2012

By A. R. G. Azevedo, G. C. Xavier

"The search for technological innovations in the Civil Construction takes as an objective the reduction of costs and increase of the productivity. However, these technologies demand analysis and studies of parameters of control that provide the quality of the products. With the intention of improve the knowledge on industrialized mortars used in mechanized projection machines, a characterization was done in the state anidro, fresh and hardening of three mortars, being each one of a State, Rio de Janeiro, Sao Paulo and Bahia. The tenors of water/ mortar was obtained through tests done in built environment, it varied from 0,17 to 0,26. From these results, the mortars were projected by his respective consistency, analyzing its compressive strength, and traction adherence resistance, in this way, the good performance of the revetments was provided.IntroductionThe market competitiveness of Construction has led companies to invest in construction processes and techniques in order to rationalize and optimize the buildings. Thus, changes emerged in coating system providing improvements in conventional materials and novel construction techniques, such as mortar industrialized and mechanized projection.Adopting projection equipment mortar is flagged as one of the solutions to reduce the interference of hand labor in construction, optimizing the performance of internal and external coatings, as well as streamline the production process and transportation, reducing lossesMaterials and deadline for execution of the casing(l)The process has been used due to its benefits, however, studies are necessary parameters for quality control of these mortars used in the projection to greater knowledge of mixing and market acceptance. It is therefore quite relevant information processing techniques available on the subject, as necessary to carry out research aiming at defining specific indicators of quality."

Jan 1, 2013

Gas-liquid contacting in the packed bed is a common operation in metallurgical reactors. Research has shown that, unlike wetting flow, non-wetting liquid flows in the form of discrete droplets or rivulets. Thus, modeling of the liquid phase as a continuum is in contradiction to the observations. Also, for the non-wetting case, continuum models have failed to describe liquid flow path when the liquid source is a point source. The aim of the current work is to put forward a combined Lagrangian-Eulerian approach to model the liquid and gas flow in the packed bed. Liquid is assumed discrete and modeled using a force balance approach. Gas is assumed to be interpenetrating continua and modeled using k-emodel for turbulent flow. Structured packing is assumed and x- ray imaging technique is used to visualize liquid flow lines in the bed. Simulation results for liquid flow path compared with the experiments.

Jan 1, 2006

By Chen Song

In the experiments of purifying the solution of chlorine leaching from nickel concentrate with N235, the effects of organic phase composition on purifying efficiency have been studied. From the results obtained, the optimal organic phase composition is found to be 25%N235+12%isomerous alcohol +63%sulfonic kerosene (VIV) and the saturated content of cobalt in organic phase is7.95 g*dm3. And then the serial experiment is carried out. The results show that at the given organic phase composition, the purified solution contains p(Ni) >200 gm dm3, p(Ni)l p(Co) >50000 and the contents of Cu, Fe, Mn, Zn meet the technical criterion of standard nickel electrolyte. The cobalt chloride solution contains p(Co) >I10 g L-1, p(Co) lp(Ni)>50000 and the enrichment of cobalt has been achieved.

Jan 1, 2006

By Hai-Xing Fang, Bing Xie, Hong-Yi Li

"In the duplex melting process, chromium forms chromium spinels, the study of which will help to exploit the Hongge ores (rich in chromium) in the Panzhihua-Xichang area in China. Mimicked chromium slag was synthesized. The oxidation and decomposition mechanism of the Fe-Cr spinels contained was studied in a sodium roasting process. The effects of temperature, roasting time, amount of soda added and filling reagents were investigated. The leaching-reduction-precipitation-calcination procedure to extract Cr2CO3 was optimized. The results showed that the optimized roasting temperature was 1000~1020°C with a stoichiometric Na2CO3 addition and without any filling reagents. Roasted materials were leached with distilled water and were filtered to obtain a chromium-containing solution, which was adjusted to pH 1.60-1.80. A reducing reagent, NaHSO3, was added in a stoichiometric ratio and the solution was then adjusted to pH 7.25~8.25. Maximum Cr2O3 precipitation was obtained and the precipitate was calcined at 1050°C for 2h to obtain Cr2Ü3 with recovery rate over 96%.IntroductionChromium is widely applied in the metallurgical industry, in refractory materials and in the chemical industry with its particular properties of hardness, wear-resistance, high temperature resistance and corrosion resistance [1]. There is no free state of chromium in nature and chromite is the main chromium containing mineral [2], China is poor in chromium resources, despite its large demand, and there are few deposits of high grade of chromite ores except in some regions in Tibet and Xinjiang province [1, 4]. Hongge, one of largest titanomagnetite mines in Panzhihua-Xichang area, is a polymetallic deposit mainly containing iron and titanium; it is also associated with various beneficial elements such as chromium, copper, nickel, etc. [3]. As investigated in Reference 3, the chromium reserves of Hongge ores are so large that it is of great importance to study how to extract the chromium from them."

Jan 1, 2012

By Guolin Zheng, Jian Pan, Deqing Zhu, Xianlin Zhou

"In ferronickel production, nickel oxide and part of the iron oxide are reduced to metal by agglomeration and smelting in blast furnace. Due to the physical and chemical properties of the laterite ores, a large fraction of fines is generated during the pre-treatment stages and the strength of agglomeration is weakened, which results in low productivity and bad quality. In this paper, the process of pelletization of nickel laterite was developed, and some parameters to strengthen the pelletization of nickel laterite have been optimized. The results show that the compressive strength of fired nickel laterite pellet can reach over 2000 Newton per pellet while firing at the temperature of 1220 °C~1250 °C in 12 min. The product pellet can be used as high-quality burden for blast furnace to manufacture ferronickel.IntroductionIn recent years, the global stainless steel market was developed exuberantly, which greatly promoted the needs of the basic raw material of stainless steel smelting - metal nickel. Currently nickel sulfide ores are only 40% of global nickel reserves, but offer 60% of all the nickel production. However, with the deficit of resources, the nickel sulfide ore (high grade ore) is depleting, so there is an increasing focus on the utilization of low-grade nickel laterite. Recent research has focused on the wet treatment process to utilize nickel laterite, and less on the use of other technologies [1-8]. The economical and efficient technology relies on the reduction of nickel oxide and part of the iron oxide metal by agglomeration and smelting in blast furnace in China. Some domestic steel companies have adopted this process [9, 10]. Unfortunately a large fraction of fines is generated during the pre-treatment stages and the strength of agglomeration is weakened, which results in low productivity and bad quality of fired pellets. In this study, the process of pelletization of nickel laterite was developed firstly, and some parameters to strengthen the pelletization of nickel laterite have been optimized, and the product pellet can be used to produce stainless steel and ferronickel alloy by blast furnace."

Jan 1, 2011

By Patricia Negrini Siqueira Poveda, Leonardo G. A. Silva

Thermoplastic materials are sensitive to ultraviolet radiation (UV), which can cause structural changes, causing variation in mechanical properties and appearance. UV range between 250 and 400 nm is considered the most aggressive to polymers, and prolonged exposure to it results in breakage and/or crosslinking chains. Light stabilizer additives, blockers or absorbers are added to the polymers for protection in order to extend the life of the final product. The choice of the adequate light stabilizer additive system depends on factors such as resin final application, thickness, geographic location of exposure, presence of fillers in the composition, contact with chemicals, among others. This study evaluates different additive systems: conventional organic, inorganic nanotechnologyc base and the synergy between them when applied to polyethylene considering carbonyl index and UV/VIS results after aging by QUV chamber.

Mar 1, 2017

By Cleusa Cristina Bueno Martha de Souza

Hydrometallurgical techniques for processing metals are becoming an efficient method for recovering metals. Although batteries&apos; manufacturers have got rid of mercury content, some efforts have been made for recovering other metals enclosed in the battery formula. This paper discusses the bench scale experiments in the purification process of leached solutions from alkaline spent batteries. After leaching process using sulfuric acid as leachant, the solutions containing Fe, Cd, Pb, MIl, Zn and K were neutralized to precipitate iron hydroxide. In a second step, the purification experiments were carried out with excess of zinc dust to try to remove Cd while Mn and Zn still remain in the solution to be recovered in an electrolysis stage. The purification experiments procedures were conducted at different temperatures and times to find out properly conditions from the viewpoint of metals removal After filtration the solutions were submitted to chemical analysis to certify the metals content extracted.

Jan 1, 2001

By Lucas L. Costa, Luiz F. Lopes, Ludy C. Motta, Felipe P. D. Lopes, Sergio N. Monteiro, Lara S. Vasconcellos

"Environmentally correct materials like the lignocellulosic natural fibers, which are renewable and biodegradable, are being extensively investigated as possible substitutes for synthetic fiber in polymeric composites. Several natural fibers have never been thoroughly investigated as possible composite reinforcement. The fiber obtained from the leaves of the buriti (Mauritia flexuosa) palm tree is one example. Therefore, the objective of this work was to study the properties of buriti waste fibers, in amounts of up to 30%, reinforcing polyester composites.IntroductionIn the past century, the technological development gave priority to new synthetic materials with energy intensive methods of production. Today, there is a concern that conventional energy source such as petroleum, natural gas and coal are the main responsible for global warming. Therefore, the use of natural materials is gaining attention not only for the saving in process energy but also the renewable and biodegradable characteristics that make them environmentally correct. The lignocellulosic natural fibers extracted from cultivated vegetables like jute, sisal, hemp, coconut, flax, ramie and many others are typical examples. This type of fiber is being extensively investigated as a possible substitute for synthetic ones, especially the glass fiber, as composite reinforcement [1].A relevant example of lignocellulosic fiber substitution is nowadays occurring in vehicles. The automobile industry is applying composites reinforced with natural fibers to replace parts such as panels and seat cushions made of fiberglass or polymeric foams [4], as illustrated in Fig. 1. The practical reasons for this preference are that natural fiber composites present less damage to tools and molding equipments as well as relatively better finishing and less abrasive surface than corresponding parts made, for instance, of glass fibers. On top of these advantages, low cost is probably the main motivation for the industrial interest for natural fiber composites, especially in the case of residual fibers [5] or post-used fabrics such as jute sackcloth [6]. Natural fibers, however, are hydrophilic and will not form strong bonding with a hydrophobic polymer, normally used as composite matrix [1-3]. Another disadvantage is the heterogeneous characteristics of a natural fiber, which is typical of biomaterials. This results in a relatively great dispersion of dimensions and properties values such as the mechanical strength [1-3]."

Jan 1, 2008

By Wei-Tong Du, Zheng-Lei Guo, Yu Wang, Shu-Chao Wang

The influence of bottom blowing a CO2–O2 mixture on the bath temperature of a vanadium extraction converter was studied by using the characteristics of CO2 with weak oxidizing. It was studied in two aspects: oxygen content and temperature. The experiments showed, when the ratio of the mixture of CO2–O2 was 2:8 at 1300 °C, the bottom blowing of the converter inhibited the heating up of the hot metal, thus keeping the temperature below the carbon vanadium transition temperature. At 1360 °C, the sensible heat absorption by CO2 was 1.44 times that absorbed by O2 per mole. Meanwhile, at 1300 °C, 20% CO2 released the chemical heat of 13.58 kJ. So with the increase of the CO2 ratio, the bath temperature was reduced. The research showed that the bottom blowing of a CO2–O2 mixture had an advantageous effect by decreasing the temperature of the vanadium extraction converter.

Mar 1, 2018