By J. W. Bridge

Triaxial compression tests at various confining pressures and temperatures, as well as tangent modulus tests using ultrasonic waves, were conducted for wax-coated granular composite materials. The material used is a surface for Thoroughbred horse racing. The purpose of these tests is to examine how track shear strength and tangent modulus at a range of loads respond to changing temperatures. Previous work has shown that a wide range of operational temperatures are experienced which have been reproduced in the lab. Using differential scanning calorimetry, it is confirmed that these operational temperatures correspond to distinct thermal transition regions for the wax that is used to coat the sand in these surfaces. Preliminary results show that both shear strength and tangent modulus are sensitive to temperature changes with maximum strength and modulus correlating with major DSC wax transition regions.

Jan 1, 2010

By John A. Clark, Danylo Oryshchyn, Casey Carney, Stephen Gerdemann, Cathy Summers, Thomas Ochs

"Limited analysis of combustion gas streams where carbon capture is not of interest is done mainly to ascertain operation parameters. Stringent regulations on acid gases and particulates promote careful flue gas analysis. Unregulated components are typically not analyzed. Typically not more than four points (two in the boiler, and one each in the flue and the stack) are sampled. A successful oxy-fuel process with carbon capture and compression is anticipated to require as many as 12 sample points with analysis for water, nitrogen, oxygen, argon, NOx, SOx, and carbon monoxide. Carbon dioxide captured for beverages produces a high value product and the cost associated with analysis is warranted. However, carbon capture for disposal must keep all costs to a minimum. This paper will compare alternative approaches for cost-effective sampling and analysis of the carbon dioxide product streams from oxy-fuel combustion, through all stages of production through compression and pipeline/vessel delivery.IntroductionAnalysis of gases in an oxy-combustion process with carbon capture is essential to the operations of the oxy-fired boiler and the subsequent collection, compression, and purification of carbon dioxide. The process is charged with pure oxygen and not-so-pure carbon in the form of coal at the front end, generating a product of mainly carbon dioxide with traces of argon, nitrogen, sulfur compounds, nitrogen compounds, oxygen, hydrogen, and mercury. It is possible that hydrogen chloride and hydrogen sulfide may also be present in trace amounts [1]. The trace components primarily come from impurities contained in coal such as water, sulfur, nitrogen, and volatile organic compounds. Coal also contains a good deal of mineral matter that is transformed into ash during combustion, becoming particulates that can complicate the analysis regimes utilizing standard analytical equipment."

Jan 1, 2010

By Gabrielle Gaustad

For aluminum, substitution of primary with secondary resources decreases energy consumption; this energy advantage creates a strong economic incentive to recycle. Several authors have raised concerns that the current sinks for secondary materials may soon be saturated, impeding subsequent expansion of recycling. This work combines dynamic material flow analysis with optimal batch planning models to quantify the significance and drivers of these pending limits under several scenarios, and thereby explore potential opportunities to increase recycling. An aluminum recycling system case was developed that includes containers and packaging, automotive, and construction products and scraps. The impacts on aggregate scrap utilization and materials cost are explored in the context of changing alloy demand and lifetime. Insights drawn from this specific case study could be applied to multi-stakeholder, systemic models.

Jan 1, 2010

By Lucas Lopes da Costa

In this work, a natural foam extracted from the Amazon buriti palm tree is investigated as possible substitute for synthetic foams. The basic physical and mechanical properties of this biofoam were evaluated. Its sponge-like structure was characterized by the amount of pores and morphological aspects. It was found that the buriti biofoam displays a very low density of the order of 0.1 g/cm3 with a relatively good compressive strength. This would be suitable for several engineering applications and as a new material with the potential for replacing currently applied synthetic polymeric foams.

Jan 1, 2010

By Karel Van Acker

The automotive is a sector where energy consumption during the use phase prevails over the production and the end-of-life phase. Therefore, a lot of research and innovations at replacing classical steel parts by lighter materials like light metals and polymer composites. While composites are very attractive for the use phase of cars, their introduction suffers from the limited end-of-life options for composite structures. An extensive life cycle analysis for a reference car design has been conducted to study the effects of replacement of conventional steel structures by lightweight carbon fibre composite alternatives. The study also takes second order effects in the design of the car into account. The opportunities and treats of the trend towards more intensive use of carbon-fibre composites in car design are identified. A discussion on the potential of other types of composites for the automotive in terms of sustainability considerations is added.

Jan 1, 2010

By Thomas Niehoff

"Oxyfuel combustion systems are state of the art for many melting operations. Airfuel systems have been stepwise modified to oxygen enrichment, oxygen lancing and oxyfuel. Every change of the melting process will have consequences with regards to emissions and energy usage. The uniqueness of many operations requires unique skills to resolve potential issues. This paper will give some examples of how airfuel systems can successfully be converted to oxyfuel.IntroductionOxyfuel technology – meaning the combustion of fossil fuels such as natural gas, oil or coal with technical oxygen instead of air for industrial melting or heating processes is widely used in many industries these days. Even though oxygen production, storage and handling has been state of the art for decades other opinions exist. Often oxyfuel is regarded with fear and potential hazards like: “Oxygen makes the process too hot.”, “Oxygen will melt away the refractory.”, Liquid oxygen is dangerous.”, “Oxygen will cause explosions.”, ……etc.Typically a more detailed discussion about a specific industrial process and how oxygen can be applied in a safe and economic way the seeming issues go away."

Jan 1, 2010

By David Bequette, Ray D. Peterson, Cynthia K. Belt

"With a need to cut production costs in the metals industry, cost savings from energy efficiency improvements are critical. Opportunities can be found by reviewing furnace systems and practices so that the melting and holding processes operate at the highest energy efficiency. Many of the changes can be implemented with a minimum of expense or capital investment. This paper will review several low cost methods to optimize energy efficiency on reverberatory melting or holding furnaces. These five methods (furnace utilization, idle procedures, fire rate, controls, furnace pressure) will be explained and information given to implement these changes. Included are several rules-of-thumb and benchmarks for aluminum reverb furnaces.IntroductionEnergy can be a significant portion of the total manufacturing costs for metals and materials manufacturing involving thermal processing such as heat treating, melting, and high temperature processing. Natural gas prices have dramatically varied over the last few years. While no one can foresee the future, prices are expected to increase from the current low prices. More recently, emphasis is being put on the reduction of greenhouse gases with the potential of additional costs to industry.One of the first steps in an energy management program is to measure the energy usage of the process [1]. The results are typically understood in relation to the mass melted in kWh / mT [BTU / lb]. For the purposes of this paper, furnace energy efficiency is calculated over a month or even a year and thus includes hold times. This efficiency is typically different from the values quoted by furnace manufacturers. Those values are for limited short term tests at highutilization.Once you know the performance for your furnaces, these should be compared to industry benchmarks. For aluminum melt furnaces with cold air burner systems, a benchmark value or goal is 1800-2000 BTU/lb [1160-1290 kWh/mt], though some of the best have reached 1600 BTU/lb [1030 kWh/mt]. Furnaces with regenerative burners can attain 1100-1200 BTU/lb [710- 775 kWh/mt]. There are some designs of multi-chamber furnaces or oxygen furnaces that have improved on these numbers, perhaps as low as 950 BTU/lb [615 kWh/mt]. Typically, as the degree of sophistication and energy efficiency of the furnace increases, so does the cost."

Jan 1, 2010

By Hector Carreon

Due to elevated temperatures, excessive stresses and severed corrosion conditions, turbine engine components are subject to creep processes that limit the components life such as a turbine bucket. The failure mechanism of a turbine bucket is related primarily to creep and corrosion and secondarily to thermal fatigue. As a result, it is desirable to assess the current condition of such turbine component. By using eddy current images, it was shown that the eddy current technique could be used to monitor creep damage in a nickel base super-alloy. The eddy current results also show a significative variation in the electrical conductivity on the creep damage zone with respect to the background zone in nickel-base super-alloy samples. In addition, the absolute thermoelectric power coefficient show also a strong dependence associated with creep damage in nickel base super-alloy samples using a copper hot tip reference. The eddy current and thermoelectric power techniques seems to show promise as nondestructive evaluation tools for monitoring the level of creep damage in metallic alloys.

Jan 1, 2010

By Aline Maria dos Santos Teixeira

Serpentinite is an ultra basic and metamorphic rock consisting mainly of magnesium, calcium and silicon oxides. The rock under study is a host rock of chromite mine located in Andorinha, BA. The objective of this paper is to evaluate the rock's physical and chemical characteristics to be used as an additional fertilizer of acid soils. After comminution, rock samples were submitted to chemical analysis, XRD, SEM-EDS and TGA. Afterwards, particle size distribution was determined. Result analysis confirms that our rock consists mainly of dolomite, calcite and diopside. According to the result obtained, it can be said that the serpentinite rock has promising applications in agriculture for the correction and additional fertilization of acid soils. However, it is necessary to study the characteristics of the rock such as its dangers and toxicity as well as evaluate them according to the legislation for corrective acidity.

Jan 1, 2010

By Mohamed Ahmed, A. Kawy

"Smelting of scrap copper and residual anodes and cathodes carried out in a reverberatory type furnace. In this, deoxidation process is carried out by wood, which acts as a resource of reduction gases such carbon monoxide, hydrogen and methane. Use of wood causes the formation of soot pollutants and efficiency of oxygen removal from copper is low leading to added costs in removing contaminants. This expensive problem was solved by using of reformed natural gas as a source of reduction gases (CO+ H2).IntroductionThree reverberatory furnaces were used for smelting of scrap copper and residual anodes and cathodes. Each furnace had a 7tpd capacity and was operated at 1183 °C.In this furnace, Step1-compressed air supplied by tubes from the side of the furnace to remove sulfur from copper matte by oxidation .The copper is also oxidized to copper oxide .[1]Step 2- copper from matte is deoxidized by a reductant. Typically deoxidation process is carried out using wood as a resource of carbon monoxide, hydrogen and methane which are the reduction gases. Use of wood causes the following:1- Forms soot pollutants2- Oxygen removal efficiency from copper is low; more contamination in copper matte increased energy in deoxidation3-the process is highly expensive.In the recent trends, this problem has been solved by using reformed natural gas as a source of reduction gases (CO+ H) .This results in 1-Reduced pollution during smelting.2- High efficiency in the removal of oxygen from copper to produce oxygen free copper. The surface of copper produced from this method is smooth which helps in forming and machining.3- Low cost and natural gas is more readily available in Egypt than wood."

Jan 1, 2010

By Xiaobing Yang, Animesh Jha, Greg Doughty

"Successful use of inert anodes should reduce the CO2 footprint in aluminum production. The search for a “holy grail” inert anode for metal electro-winning from constituent oxides using molten salt bath as an electrolytic medium is continuing. In this article we demonstrate the engineering approaches for the fabrication of intermetallic anodes, based on a quaternary Al-Ti-Cu-M (M:Ni, Fe) system for primary aluminium production. In particular, we examine the microstructural and electrochemical properties of alloys, based on the quaternary compositions. We explain the aspects of phase stability under anodic potential, which leads to the loss of anodic materials in the temperature range of 850-1050oC. The results are analysed in the context of oxidation reaction and formation of oxide layers which readily dissolve in the cryolite melt and prevent passivation. The paper also describes the conditions under which the reduction of aluminium at the graphite cathode occurs which also strongly depends on the molten salt chemistry for the nucleation of molten aluminium at the cathode.1. IntroductionOxygen-evolving inert anodes are an alternative to the conventional consumable carbon anodes for the production of primary aluminium. In this paper the materials selection criteria chosen for the engineering of anode is based on the understanding of the thermodynamic stabilities of aluminide intermetallic phases, some of which are formed and remained stable in fluoride melts. For example, the formation Al3Ti dispersed in aluminium metal via molten-fluoride flux reaction is well known in the context of aluminium casting and grain refining [1-3]. It is for this reason in our research we concentrated on the engineering of stable intermetallic phase mixture in the Al-Ti-Cu ternary system, shown in Figure 1 [4]. In this figure two compositions in the Al3-0.5zTi1-0.5zCuz family are shown with the substitution of 7 atomic % and 11 atomic % copper. However initial investigations showed that these two compositions were unsuitable due to the formation of low-temperature liquid (~540oC) and intermetallic phase, Al2Cu along the Al-Cu binary edge during solidification. The Al2Cu phase segregated along the boundaries of Al3Ti and Al5Ti2Cu, and dissolved away when electrolysis was carried out using these anodes above 800oC. The presence of consequential porosity in the anode material increased the corrosion of the alloy through local heating due to high current density at 0.8 A cm-2. The early tests were carried out with cryolite melts, shown in Figure 2, having 3 weight percent of Al2O3 in the bath at 850oC."

Jan 1, 2010

By Jewel Andrew Gomes

Arsenic is considered as one of the toxic materials being controlled by Environmental Protection Agencies in several developed and developing countries. It is found in the nature as constituents of the soil, minerals and also in various organic forms. It enters the air, water, and land from wind-blown dust and gets into water from runoff, leaching, soil erosion and anthropogenically from chemicals used for wood preservation, insecticides, medicine, military purpose, pigments, and electronic circuitries. There are several techniques available for removal of Arsenic, such as coagulation/filtration, lime softening, ion exchange, reverse osmosis, nanofiltration, wet chemical, and electrochemical. Electrocoagulation has been found as one of the most efficient techniques to remove inorganic arsenic with more than 99% efficiency. In this paper, we present our work on electrochemical treatment of both the inorganic and organic arsenic from water using various sacrificial electrode materials, i.e., iron, aluminum, copper, and combination of them. The floc produced by this method has been also characterized using XRD, SEM/EDS, FTIR, and cyclic voltammetry.

Jan 1, 2010

By Mark Jolly

"Instead of using the traditional batch casting process, the CRIMSON [1] (Constrained Rapid Induction Melting Single Shot Up-Casting) method employs a high-powered furnace to melt just enough metal to fill a single mould in a closed crucible. The crucible is transferred to a station for computer-controlled counter gravity filling of the mould for optimum filling and solidification. The CRIMSON method therefore holds the liquid aluminium for a minimum of time drastically reducing the energy losses attributed to holding the metal at temperature. With the rapid melting times achieved, of the order of minutes, there isn’t a long time at temperature for hydrogen to be absorbed or for thick layers of oxide to form. The metal is never allowed to fall under gravity and therefore any oxide formed is not entrained within the liquid. Thus higher quality castings are produced leading to a reduction in scrap rate and reduced overall energy losses.IntroductionEngineers at the University of Birmingham, England, with local company, NTec, have invented a new casting process that will reduce the energy costs of light-metal foundries. The technology, entitled CRIMSON, means that foundries need only heat the quantity of metal required to fill a single mould rather than large batches that use unnecessary energy and create waste. The complete concept of CRIMSON requires a change of philosophy in the approach to casting and requires the user to think holistically in order to reap the full benefits from the process. This paper will discuss the various aspects of energy wastage within the foundry sector and discusses the processes whereby the energy can be reduced. Primarily the author focuses on the aluminium sector but CRIMSON can be applied to many of the non-ferrous “light” alloys. Ferrous materials and non-ferrous “heavy” alloys can also benefit from some of the ideas but not necessarily directly from the application of CRIMSON."

Jan 1, 2010

By P. K. Narasimhargahavan

This paper discusses briefly the major reasons associated with the growth and its impact on the energy requirement and Environmental imbalance. A projection based on the present global Alumina and Al requirement indicate a substantial further growth of at least 30% over the next 10 years. It is indicated that the main factors which are likely to influence investments are the environmental factors such as the Climate Change and global response to the growing energy prices and sustainable development. Each of the developed / developing nations must find response to the GHG emissions which will encourage the Al Industry to make an effective contribution to global warming while preserving the international competitiveness of the industry - a challenging task. The efforts shall concentrate on improving energy efficiency in the industry possibly of the order of 25% over the next 10 to 20 years. The developments in this line are discussed.

Jan 1, 2010

By Hamed Mirzadeh

The hot working behavior of 17-4 PH stainless steel was studied using the hot compression test at temperatures of 950-1150 °C with strain rates of 0.001-10 s-1. A step by step procedure for data analysis in hot compression test was given. The work hardening rate versus stress curves were used to reveal whether or not dynamic recrystallization (DRX) occurred. At low Zener- Hollomon (Z) parameter, this material showed a new DRX flow behavior, which was called Multiple Transient Steady State (MTSS). At high Z, as a result of adiabatic deformation heating, a drop in flow stress was observed. The general constitutive equations were used to determine the hot working constants of this material. Moreover, after a critical discussion, the deformation activation energy of 17-4 PH stainless steel was determined as 337 kJ/mol.

Jan 1, 2010

By Ulises Crossa Archiopoli

We describe a technique that allows rapid imaging of the thermal diffusivity of the sample by a modified photo-thermal technique. The thermal diffusivity in hardened steels strongly correlates to the hardness. Hence in a noncontact manner and with optical microscope resolution, a 2D map exhibiting the crystallographic phases and hardness of the sample can be retrieved. Two almost collinear laser beams scan the surface, one as a modulated pump and a second as a CW probe. The deflection of the probe carries information on the thermal expansion of the sample and with it, on the thermal diffusivity. It is shown that a single determination of the time delay of the modulation of the probe beam can be used to retrieve the thermal diffusivity.

Jan 1, 2010

By Shirleny Fontes Santos

Muscovite mica crystals lower than 15 mm diameter are discarded as waste in the mining area of Borborema-Seridó (BRAZIL). The objective of this work was the ore dressing and purification of this waste to be used in the preparation of pearlescent pigment. Muscovite was dry ground using knife mills and an ultrasound treatment. It was possible to achieve 67% of mica with particle size lower than 100 µm. This product was used in the preparation of brilliant pigments based on muscovite flakes covered with rare earth oxides (CeO2, PrO2, Ce0,95Pr0,05O2). The pigments were characterized by X-ray diffraction, thermal analysis and scanning electronic microscopy. The color of the resulting pigments was analyzed using the CIELAB method and it showed the following colors: muscovite-CeO2 ? yellow, muscovite-PrO2? black and muscovite-Ce0,95Pr0,05O2 ? orange. Those results have shown that ?trash mica? is suitable for use in pigment preparation.

Jan 1, 2010

By Tian Sugui

By direct aging treated, creep properties measurement and microstructure observation, the influences of the direct aging treatment on the creep behaviors of Hot Continuous Rolled GH4169 superalloy are investigated. Results show that the creep resistance of Hot Continuous Rolled GH4169 superalloy may be obviously improved by directly aged treatment. Under the applied stress of 700MPa at 660, the creep lifetime of the alloy is enhanced to 126h from 60h. During hot continuous rolling, the deformation features of the alloy are the twinning and the double orientations slipping of the dislocation activated within the twinning regions. After direct aging treated, the alloy displays a smaller grain size, and the finer g² phase is dispersedly precipitated in the matrix of the alloy, which is thought to be a main reason of enhancing creep lifetime of the alloy.

Jan 1, 2010

By M. S. Borges

The need for the waste management industry to reach environmental patterns, technological innovation, and a technological demand of the productive sector is covered by this study. The environmental care and responsibility in the industrial sector and the necessary cultural changes for companies and entities is also emphasized. A collaborative tool was developed to help all partners involved in the environmental administration. This tool focuses on the interaction among residue generators in the productive chain. It was developed for a vehicle assembler company supported by entities or institutions with emphasis in the research, development and innovation, with expertise and capacity for new products creation, as well as reuse, recycling and reduction of by-products generation. The work aims to establish a tool for socio-environmental management, focusing on promotion and interaction between industrial waste generators sectors.

Jan 1, 2010

By S. Y. Tan

The thermal stability of fully silicided NiSi with arsenic doping on silicon was investigated. The aims of the work were to investigate the Ni silicide phase-related issues associated with arsenic dopant and thermal annealing on Ni-FUSI/HfO2/Si and Ni-FUSI/HfSiO/Si gate stacks. It was found that arsenic-incorporation demonstrated some improvement in both morphology and phase stability of nickel silicided films at high processing temperatures regardless underlying gate dielectrics. The correlations of Ni-Si phase transformation and arsenic doapnt with their electrical and physical changes were established by sheet resistance measurements, X-ray diffraction (XRD), atomic force microscopy (AFM), and X-ray photoelectron spectroscopy (XPS) analysis. Furthermore, the modulation of the work function (WF) of Ni fully silicided gates by arsenic impurity is presented, comparing the effects of dopant (As) on the WF and silicide phases (NiSi and NiSi2). It confirmed that the work function of NiSi can be tuned by implanting arsenic dopant, but it ineffective for NiSi2 phase.

Jan 1, 2010