Search Documents

By W. C. Hagel, H. J. Beattie

Seven austenitic alloys of varions base compositions and minor-alloy additions were solution-treated, aged systematically between 1200oand 1800oF, and examined by X-ray and electron metallography. Intragranular preczpitations of µ, Laves, s, ?', Ni3Ti, and x phases were observed as a function of composition and aging time and temperatwre. Phase solubility limits were detevtnitzed within 100Fo intervals. These inter metallic compounds fall into two distinct general classes, and whichever class predomznates depends on base composition. It has become increasingly evident that multicom-ponent austenitic alloys are well characterized by their precipitation processes. Since certain groups of elements act as one, the relationships among these processes are reasonably simple; complete identification of such processes is usually attainable by a systematic aging study with a combination of techniques centered on microscopy and diffraction. Several nickel- and cobalt-base alloys illustrating cellular precipitation and its interaction with general precipitation were reported previously.1 The group of alloys covered in the present paper demonstrates precipitation-hardening reactions involving two distinct classes of intermetallic compounds where the predominating class appears to depend on base composition. This dependency ties in with a crystal-chemistry regularity first observed some twenty years ago by Laves and Wallbaum but never amplified to our knowledge. Results of electron-microscope and X-ray diffraction studies on systematically aged hot-rolled alloys known commercially as S-816, S-590, Rene-41, Incoloy-901, M-308, and M-647 are reported here. Some of these alloys have previously undergone minor-phase analyses by other investiators. Alloy S-816 was investigated by Rosenbaum, Lane and Grant,3 and Weeton and Signorelli.4 Rosenbaum found only CbC in hot-rolled bars. Lane and Grant found CbC and a small amount of M6C in the cast structure and stated that both carbides form during aging, most of the precipitation being CbC. Weeton and Signorelli found CbC, M23C6 and a weak indication of a phase after a slow step-down cooling cycle from 2250°F. Rosenbaum also investigated hot-rolled samples of S-590 and identified CbC and M6C. Preliminary information on Rene-41, gained partly from the present work, was reported by Morris.5 Long-time precipitation phenomena in Incoloy-901 at 1350°Fwere investigated by Clark and Iwanski.B heir raw data re- semble those of our present heat with 0.1 pct B, while their interpretation of these data resembles our interpretation of data from another heat with only 0.001 pct B; they made no statement as to boron content. No previous minor-phase studies of alloys M-308 or M-647 have been reported. EXPERIMENTAL METHODS Table I gives alloy compositions in both weight and atomic percent. Specimens were solution-treated from 1700º to 2200ºF, aged at logarithmic-time intervals up to 1000 hours between 1200 and 1800 F, and examined in accordance with procedures previously described in detail. ' ' Phase extractions were carried out in electrolytic cells containing 800 ml of either 7 pct HC1 in denatured ethanol or 20 pct H3PO4 in water. After electrolysis for 48 hr at 0.1 to 0.2 amp per sq inch, residues were separated by filtration or centrifuging. X-ray powder patterns of residues were recorded on a diffractometer for accuracy and on film for sensitivity. Lattice parameters were calculated by least-squares analyses of indexed sin 8 values, and relative abundances were estimated from intensities of strongest lines of each phase. These phase abundances denote relative amounts with respect to each other rather than to the alloy. Mechanically polished specimens were etched in a freshly mixed solution of 92 pct HC1, 5 pct H2SO4, and 3 pct HNO3. Parlodion replicas for the electron microscope were chromium-shadowed in high vacuum at a glancing angle of 20deg. All electron micrographs are reproduced here with the shadowing source above. The correspondence betweenelectronmicrostructures and phases identified by X-rays was established by a high redundancy of correlation between relative amounts at different stages of aging and examination above and below critical transformation or solubility temperatures. EXPERIMENTAL RESULTS S-816 and S-590—The phases found in S-816 and S-590 after various aging and solutioning treatments are listed in Table 11. These data and the observed

Jan 1, 1962

By T. Toda, R. Maddin

A study has been made of the microstructure and mechanical properties of splat-cooled aluminum-base gold alloys with gold concentration from 0.25 to 5.0 wt pct. These alloys have been quenched from the liquid state by a torsion-catapult technique, which has made it possible to pepare specimens suitable for mechanical property measwements. From the electron micrographs it has been shown that the solid solubility of gold in aluminum can be extended to 2.5 wt pct (0.35 at. pct) by splat-cooling, while the maximum equilibrium solubility is known to be less than 0.3 wt pct (0.04 at. pct). The very fine grain size (several tenths of a micron), the extended solid solubility, and the fine dispersion of a second phase (AuAl2) contribute concurrently to a substantial strengthening effect. In Al-5 wt pct Au splat-cooled specimens of less than 50 thickness, the yield strength is 17 kg per sq mm or 6 times as large as the strength of bulk specimens. For the Al-1.0 to 2.5 wt pct Au solid solution obtained by splat-cooling, the yield strength reaches 7.5 kg per sq mm after an aging treatment (for 10 hr at 200°C), while it is 3.7 kg per sq mm for the corresponding bulk specimens. A great deal of research has been done in recent years on the structure and the properties of metals and alloys rapidly quenched from the liquid state.' The term "splat-cool" has been used with the meaning of a rapid quenching from the liquid state., The splat-cooling techniques have produced large numbers of new structures, which are expressed in terms of metastable phases,3 concentrated solid solutions,4 amorphous phases,5'6 new phases,7 and so forth. Nearly all previous studies have concentrated on the physical properties; i.e., crystallography, structure, electrical resistivity, magnetism, and so forth, of the splat-cooled metals and alloys. The mechanical strength of splat-cooled metals and alloys has hardly been investigated except for some recent work by MOSS' on A1-V alloys. The principle common to all experimental techniques developed to obtain very rapid quenching rates is based on the heat transfer by conduction. Liquid must be in good thermal contact with a substrate of high heat conductivity. Both of the published devices known as the "gun" and the "piston and anvil" techniques suffer from certain shortcomings. For example, the specimen obtained by the gun technique is very small and flaky, and hence inadequate for mechanical properties measurements. On the other hand if the material is forced to yield a continuous speci- men by the piston and anvil technique, it is probable that some plastic deformation occurs during the quench. A novel method for rapid quenching of a liquid metal or alloy, the "torsion-catapult", has been devised by Roberge and Herman9 at the University of Pennsylvania. In the apparatus the melt is thrown out of a curved furnace by a catapult and impinges on a copper substrate. The apparatus has the advantage of producing a continuous foil which is relatively large in size and of a quality suitable for the measurements of mechanical properties. The quenching rate is estimated to be of the order of l05 to l06 ºC per sec, (comparable to rates achieved by the piston and anvil technique). In selecting an alloy to be studied we were made aware of the fact that gold was believed to be "insoluble" in in and consequently age hardening in the A1-Au system appeared to be interesting. Quite recently Heirnendahl13-15 revealed that the solid solubility, as determined by transmission electron microscopy, was 0.3 wt pct Au at 640°C and 0.25 wt pct Au at 600°C, decreasing with decreasing temperature. In an A1-0.2 pct Au alloy after quenching from a solution treating temperature of 600°C the yield stress was 2 kg per sq mm, and it increased up to 6 kg per sq mm after aging for 1 to 10 hr at 200°C. The precipitation occurred in the form of platelike particles mainly on (100) matrix planes. The intermediate phase n', the equilibrium phase n (AuAl2), and lattice relationships between both precipitates and the matrix were also investigated by electron microscopy. One of the purposes of the present research is to determine whether or not the solid solubility in this system, in which gold has a very small solubility in

Jan 1, 1970

By R. M. N. Pelloux

This study of aluminum-copper alloys had two aims: 1) To determine the effect of the amount and distribution of a second phase, CuAl2, on the creep-rupture strength, ductility, and fracture characteristics of the alloys. The work of Gemmell and grant' on single-phase aluminum-copper alloys provided a basis for the present study. 2) To attempt to provide a relation between the microstructure and strength of two-phase alloys deformed at comparatively high temperatures (greater than 0.45 T,). The creep behavior of the two-phase magnesium alloys Mg;Ce and Mg-A1, has been treated by Roberts. 9 In work reported by Sully and Hardy4 and by Underwood, Marsh, and Manning~ on A1-Cu two-phase alloys, and also in a portion of the work of Gemmell and grant,' aging took place during the creep tests. 'In the present work, overaged aluminum-copper alloys were subjected to creep deformation at two temperatures, 500 and 700OF. The overaging treatments to produce the precipitate dispersions were performed prior to the test, at temperatures which were the same as the ultimate respective test temperatures. Hence, the present study is concerned with the creep behavior of stable (in contrast to "underaged") two-phase A1-Cu alloys, i.e., alloys in which no depletion of the solid-solution matrix occurred during: creep. MATERIALS AND PROCEDURE A 2 and a 3 pct Cu alloy, supplied by Alcoa, were studied; Table I shows the compositions. The grain size of the specimens, 0.9 to 1.0 mm, was achieved by annealing the machined test bars for 2 hr at 1000°F, followed by furnace-cooling to 900°F, and homogenizing for 4 hr. Both compositions are in the single-phase condition at 900°F. Two types of overaged dispersions, termed "over-aged I" and "overaged 11" were prepared after the grain size and the homogenization anneals. The overaged I alloys were prepared by quenching to room temperature after homogenization, aging at either 500' or 700°F for 72 hr, and air-cooling to room temperature. The overaged I1 alloys were prepared by furnace-cooling after homogenization, to either 500' or 700°F, and holding at the necessary temperature for 72 hr. The times for furnace-cooling from 900°F to 700° and 500°F were, respectively, about 2 and 3.5 hr. The structures of the A1-2 pct Cu alloys are shown in Fig. 1 (overaged I) and in Fig. 2 (overaged 11). A comparison of Figs. 1 and 2 shows that in the overaged I alloys the precipitate particles along the grain boundaries are much more closely spaced and the grain boundaries are straighter than they are in the overaged I1 alloys. Further, the particle size and spacing in the grains are smaller than in the overaged I1 alloys. Microstructures of the A1-3 pct Cu alloys have not been shown; the structures of these alloys differed from those of the A1-2 pct Cu alloys only in that the distribution density of the particles was greater. The creep specimens had a gage section 1 in. long with a diameter of 0.155 to 0.195 in. Before testing, specimens were electropolished in a solution of 100 cc glacial acetic acid, and 30 cc of 60 pct perchloric acid, at 40' to 50°F, at 24 v. The specimens were kept refrigerated prior to testing to avoid precipitation at room temperature. Constant stress creep tests were conducted; the load was applied 75 min after heating of the specimens to test temperature had begun. EXPERIMENTAL RESULTS Creep-Rupture—Fig. 3 shows the log stress-log rupture life plotfor the overaged alloys studied, and also for the underaged A1-2 pct Cu alloy.' At 700°F, the stress-rupture life relationship is nearly independent of both the amount of precipitate (i.e., composition) and of the type of overaging treatment (i.e., precipitate dispersion). At 500°F it is apparent that the increase in rupture life that was ex-

Jan 1, 1960

By N. Tiner

THE mechanical properties of magnesium-alloy castings are greatly improved by grain refinement, and at present considerable attention is being paid to methods of obtaining fine-grained castings. One method of achieving this end is the use of proper melting and superheating techniques. These have been employed commercially to a great extent, but no comprehensive study of the subject appears to have been published at present. Numerous investigations found in the literature include some reference to superheating techniques, 1-4 and Achenbach, Nipper and Piwowarsky,5 based principally on thermal analysis, ascribe the grain-refining action of superheating to the influence of solid foreign particles or dissolved gases present in the melt upon the course of crystallization. The primary purpose of this paper is to present the principal facts concerning the effect of superheating on grain size of magnesium alloys. Attempts are also made to explain the experimental results in terms of a general hypothesis. The investigations are limited chiefly to common commercial casting alloys. In order to carry on this work, it was necessary to determine the factors influencing grain size and to develop a proper technique for the preparation of samples. The preliminary tests made by the author indicated that the grain size of magnesium alloys resulting from the solidification of a melt is determined by alloy composition, presence of impurities, rate of cooling during solidification, thermal history of the melt and to some extent the structure of the charge used. The rate of cooling is in turn dependent upon the mass of the melt, pouring temperature, and dimensions, properties and temperature of the mold into which the melt is poured. The final grain size of the alloys is still further modified by heat-treatment subsequent to casting. It is not within the scope of the present paper to discuss all of these factors, and it would suffice to note here that when equal amounts of magnesium alloys are prepared from the same alloying materials, melted in graphite crucibles under the same thermal conditions, then cast into graphite molds at a constant temperature, the .resultant solids have the same grain size. By maintaining all other factors constant, it is thus possible to vary thermal conditions of a melt and to examine the grain size of resultant castings. PREPARATION OF SAMPLES AND GRAIN-SIZE TESTING The alloys investigated in this paper were taken from ingots made by Permanente Metals Corporation or prepared by the author with pure carbothermic magnesium and necessary alloying elements. Melting was carried out under a flux in a graphite crucible heated uniformly by an

Jan 1, 1945

By P. W. Rainier

THE Chivor emerald field is situated on the eastern slope of the Andes in the Department of Boyacá, at an elevation of about 8000 ft. above sea level. It overlooks the Llanos (plains) of the Orinoco and is watered by many streams flowing into the Rio Meta, the Orinoco's largest tributary. The Rio Meta is navigable from the Orinoco to a point within about 50 miles of the Chivor district and may eventually prove to be the reasonable outlet for the future development of this part of the country. The topography of the district is extremely rugged and mountainous (Fig. 1), the difference in elevation between two points on a mining claim 1 km. square being sometimes as much as 4000 ft. The ground is covered with dense forest growth and the available timber is suitable and sufficient for mining purposes, but it is becoming gradually depleted by Indian clearings as the country around the mines becomes settled. The many streams combined with the rough topography give good possi-bilities for hydroelectric power. The center of population nearest to Chivor is Bogota, the capital of the republic and a city of some 300,000 inhabitants; the distance is two and one-half days' travel. The first stage of the journey from Bogota, is accomplished by rail to Chocontá, some 4 hr. travel. From Chocontá the journey is made in the saddle, one night being spent in Guateque. The latter is a small town and the nearest post office to the mines, being some 10 hr. ride distant. The roads are mere bridle paths, in parts hazardous and almost impassable in the wet season. All supplies brought to the mines, other than those produced locally, are carried by pack mule; mule freight from Chocontá costs 3 centavos1 per pound. The climate of the Chivor district is healthful and bracing. The wet season begins in March and concludes in November, the remaining months being dry. The annual precipitation is about 150 in. The temperature throughout the year is nearly constant, varying from about 45° F. to about 65° F. shade temperature. The rains are cold and unpleasant, and for the greater part of each day in the wet season the country is shrouded in dense mist. A fire can with comfort be kept burning in a living room all the year round. There are a few slight

Jan 1, 1929

By S. J. Burns, W. W. Webb

The dislocation arrangements formed during unsteady propagation of cleavage fractures on (010) planes in LiF have been investigated by high-resolution etch-pit techniques and by X-ray diffraction topogvaphy. In impurity-hardened crystals, cracks propagating in any direction on (010) planes at velocities of about 103 cm per sec are usually accompanied by light plastic deformation which is enhanced wherever the crack is allowed to hesitate. Dislocations with [011] type Burger's vectors are often formed looped around the crack tip. They are dragged along with the crack tips leaving edge dislocations lying nearly parallel with the clearage surface about 5µ from it. These dislocations are easily overlooked since they may initially intersect with the cleavage surface infrequently and later may disappear from the crystals due to image forces during aging at room temperature. Although the plastic work associated with these dislocations is only comparable with the reversible (010) surface energy, an instability in crack propagation appears due to a limit of the velocity with which dislocations can be dragged along with the crack. Transition to a fully brittle nonplastic fracture mode occurs when the crack velocity exceeds the velocity with which dislocations can be moved by the stress field of the crack. TRANSITIONS between brittle and ductile modes of fracture appear to be common processes in the behavior of materials in which the flow stress is close to the stress at which brittle cracks can propagate. High-strength engineering alloys fit into this category and the transition from ductile to brittle modes of crack propagation may be associated with catastrophic failures in these important materials. The methods of theoretical mechanics indicate the geometrical conditions in which these processes may occur but the detailed mechanisms controlling the generation of dislocations in the initiation of the plastic mode and the process by which the loss of plasticity occurs on transition to the brittle mode are not yet clear. Since these mechanisms are not amenable to direct observation in engineering alloys we have chosen a semi-ductile alkali halide LiF as a model system in which to observe transition mechanisms between plastic and brittle modes of crack propagation. Cleavage cracks in this system are known to undergo a plastic-elastic transition at velocities between 103 to 104 cm per secl and dislocation configurations in LiF are amenable to study by optical-microscopic observation of dislocation etch pits2 and by X-ray diffraction topography.3 We have been able to identify a dislocation mechanism responsible for the transition from brittle to slightly plastic modes of crack propagation in LiF. A model based on this mechanism permits calculation of the critical crack-propagation velocity for this transition and indicates the importance of the stress dependence of dislocation velocity in determining the critical crack velocity. Of course, this model cannot be carried directly over to more complex materials but it is quite possible that its qualitative features are generally applicable. Dislocations intersecting fresh cleavage surfaces in LiF were reported by Gilman,4 by Forty,5 and by Wash-burn et a1.6 Such dislocations were construed to have been nucleated where the cleavage crack hesitated or stopped, near stress concentrators, such as cleavage steps, on the crystal face. The loci of such dislocations deposited On the cleavage plane in bands were called "stop lines" or "deformation zones". Gilman, Knudsen, and walshl measured the velocity of cleavage cracks in lithium fluoride by evaporating thin resistive strips on the crystal side and recording

Jan 1, 1967

By Morris Muskat

A theory is presented for calculating the performance history of complete water-drive systems producing from idealized stratified formations. The general equations are applied to systems where the permeability stratification is either of the exponential or linear type. Calculations were carried through for different degrees of permeability stratification, but with special emphasis on the effect of the mobility ratio between the produced oil and the invading water on the resultant performance. These results are also expressed graphically as curves for the initial water breakthrough recovery, for the different degrees of stratification, as a function of the mobility ratio, and of the composition of the produced fluid stream as a function of the cumulative oil recovery. For several typical cases the latter has also been plotted as a function of the cumulative oil and water throughflow. The general result is that when the mobility of the oil is lower than that of the invading water the channelling tendency resulting from the permeability stratification becomes aggravated as the higher permeability zones become flooded out. Situations of this type would obtain when producing low gravity or highly viscous oils. Conversely, if the mobility of the oil is high compared to that of the invading water, the flooding of the high permeability zones will lead to a retarding and choking effect, and the gross bypassing phenomena will be partially suppressed. These conditions would correspond to those of flooding high gravity or low viscosity oils. A discussion is given of the various basic assumptions made in the analysis, including that of ignoring the stripping phase of the production history as implied by relative permeability concepts. INTRODUCTION The physical ultimate recoveries from oil reservoirs are basically determined and limited by the physical oil displacement processes associated with the reservoir producing mechanism. In practice, however, the economic ultimate recoveries are further limited by the mobility of the reservoir fluids and the uniformity and continuity of the producing formation. In fact, it is the differential depletion between the component parts of the composite reservoir which ultimately determines the total recovery at the time of field abandonment. While this observation applies to both the solution gas drive and gravity drainage mechanisms, in which use is made only of the energy contained within the original oil-bearing reservoir, it is of even more paramount importance under operations wherein the energy associated with extraneous fluids provides the ultimate oil expulsion mechanism. Whether the invading fluid is the water from an edgewater drive, water injected for pressure maintenance, gas injected for pressure maintenance, or gas returned to the formation in a cycling program, it is often the continuity and uniformity of the producing section which will control the economic efficiency of the operations. The importance of the problem of reservoir non-uniformity does not, of course, lessen its complexity or the difficulties of its solution. In fact, these are inherently such that the concept of a "general" solution is virtually meaningless. About all that can be reasonably hoped for is the analysis of specific and well-defined types of non-uniformity which may give some degree of approximation to actual reservoir conditions. Since variations in the nature of the reservoir which depend only on the position along the streamlines will not lead directly to major differential depletion development within the reservoir, the types of non-uniformity considered thus far have involved stratification assumptions. That is, the producing section has been replaced by a multi-layer "sandwich," each uniform areally, and differing from the others only in its basic physical constants as to thickness, porosity and permeability. The fluid motion in the composite system is thus approximated by a parallel superposition of the independent fluid movements in the individual strata. For the specific application to cycling operations the theory of the effect of permeability stratification has been developed for both discontinuous' and continuous types of permeability stratification. Among the latter, treatments have been given of systems in which permeability distributions are governed by exponential, linear' or probability3 functions. In all these studies complete dynamical equivalence was assumed between the injected dry gas and the displaced wet gas. The overall effective permeability of each stratum was therefore considered as constant and independent of the degree of invasion of the injected fluid. In the case of the displacement of oil by water, the assumption of dynamical equivalence between the water and oil will be strictly valid only by accident. Even if the oil viscosity should be the same as that of the water, the effective permeability to the oil in the presence of the connate water will in general be quite different from that of the water behind the water-oil interface flowing past the trapped residual oil. As a result the effective permeability for the stratum as a whole and rate of water invasion will change with time as the intrusion continues. The differential fluid motion in the individual strata will thus also vary with time. Qualitatively, it is easy to predict the resultant effects. If the permeability to viscosity ratio of the invading fluid exceeds that of the fluid displaced, the stratification and bypassing effect of the perme-

Jan 1, 1950

By A. J. Garnier, N. H. van Lingen

Rock downhole is known to be lesc. drillable than when brought to the surface. This must be ascribed mainly to the presence under downhole conditions of a pressure differential across already made chips, which hinders their being lifted. The pressure differential has partly a static and partly a dynamic origin. Balling-up of bits is another consequence of this pressure differerztial. Reduction in penetration rate owing to an increase in the strength of the rock is governed by the difference between the mud pressure and the pressure of the for/nation pore liquid. Rotationally symmetric geostatic stresses have 170 effect on drillability. Fracture of rock when drilling will be brille in most cases. The above is supported by laboratory drilling experiments with drag bill and roller bits an elevated mud, pore, and confining pressures On rocks differing in strength and permeability. INTRODUCTION In oil well drilling drillability of rock is found to decrease with increasing depth of the hole. Naturally deep rock will be more compacted and, therefore, harder to drill than shallow rock of the same type. However, apart from this the drillability of a sample of deep and compacted rock brought to the surface is generally much higher than in its original location downhole. In view of the economic implications of this reduction in drillability, it seems worthwhile to analyze its causes. The origin clearly has to be sought in the difference of environment. The only conceivable factors would seem to be the presence of mud under pressure, the pressure of the formation pore liquid, and the overburden of the rock. Down the borehole the rock is compressed triaxially by mud pressure and overburden. It is well known that the strength of rock is increased when confined by external pressure1. Various authors have, therefore, ascribed the difference in drillability mainly to the strengthening of rock by triaxial compression. Another factor, mentioned by Bobo and Hoch5, is that forces. including "pressure differential forces", tend to hold a dislodged particle in place. However, the conditions determining their magnitude are not clarified nor is their effect on drilling rate assessed. In the laboratory, drilling experiments on pressurized samples of rock yielded evidence that pressure differential forces holding the chips down are the major factor in reducing rate at depth. This paper describes the experiments and shows how the results enable both a qualitative and a quantitative interpretation of the factors determining the effect of chip hold-down on drilling rate. The implication with respect to balling-up and jet action is also discussed. The greatcr part of the experiments were performed in the pressure vessel shown in Fig. 1. The spacc between the sample of rock and the vesscl is divided by "0" rings into three separate chambers. The rock sample is confined laterally by pressurized oil in thc middle chamber. Penetration of oil into the sample is prevented by partly jacketing it with brass foil. Thc pressure of the drilling fluid in the hole can be adjusted via the upper chamber. Permeable rock specimens arc water saturated before being drilled. With a properly plastering mud as drilling fluid the pressure of the pore water can be adjusted independently via the lower chamber.

By R. V. Sara

Determination of the Hf-C phase diagram was conducted primarily by metallographic and X-ray diffraction studies on appropriate alloys. The only intermediate phase observed in this binary system was HfC. This phase was found to be homogeneous between 34.0 and 48.0 at. pct C at 2200°c and between 36.0 and 49.3 at. pct C at 3150°C. The lattice-parameter variation was also determined for HfCI-, compositions prepared at 2200° and 3150°C. The most most refractory composition, with a melting point of 3830°c, was established at 47.5 at. pct C from melting-point data. Solidus temperatures of 2240' and 3150°C occur on the high-kafnium and high-carbon sides of the monocarbide, respectively. The invariant point between HfC and carbon is located at 66.0 at. pct C, whereas the 2240°C solidus corresponds to the peritectic temperature at which hafnium is formed from HfC and hafnium-rick liquid. Hafnium has a melting temperature of 2208°C and is capable of taking carbon into solution to the extent of 10.5 at. pct at this temperature. ALTHOUGH the Hf-C phase diagram has not been previously evaluated experimentally in its entirety, the belief has been that the general configuration would resemble the chemically similar Group rV carbide systems, Ti-C and Zr-c.' These binaries are characterized by a single carbide phase with a simple NaC1-type structure which is maintained over wide compositional ranges. This family of carbides has high thermal stability that increases substantially as the atomic number of the metal component increases. This trend characterizes HfC as one of the highest melting materials. According to Agte and Alterthum,2 the melting point for this monocarbide is 3890°C, a value that has been quoted quite extensively for the past several decades. Recently, in repeating the work of Agte and Alter-thum, Adams and Beall3 determined the melting point of HfC to be 3895°C. A significant departure from the commonly accepted version of the Hf-C system was reported by Avarbe and his coworkers,4 who proposed that there is an extreme stabilization of a hafnium in a narrow field to 2820°C, above which it melts peritectically to form HfC and liquid. Their study was also concerned with the melting temperature of various HfCI-, compositions, but the peak melting point was taken from the work of Agte and Alterthum. Avarbe and his associates were not concerned with the high-carbon region of the system. However, three widely varying temperatures have been reported for the HfC-C solidus by other investigators. Cotter and Kohn5 observed approximately 2800°C; Portnoy et al.' reported 3260°C; and, more recently, Krikorian7 indicated 2915°C. Equally as uncertain is the solidus between hafnium and HfC. As noted above, Avarbe et al. report a peritectic temperature of 2820°C, Krikorian7 measured 2150°C, and Benesovsky and Rudy' estimated 2000°C on their diagram. I) EXPERIMENTAL PROCEDURE The starting materials for this study consisted of reactor-grade hafnium hydride obtained from Fair-mount Chemical Co., Newark, N.J., hafnium carbide supplied by Wah Chang Corp., Albany, Ore., and Union Carbide spectroscopic-grade graphite, SP-1. The graphite analysis indicated impurities at levels of only 0.5 ppm or less. According to the suppliers, the hydride and carbide contained the typical impurities listed in Table I. The samples required for these studies were prepared by dry blending either graphite and hafnium hydride or hafnium hydride and hafnium carbide powders for approximately 5 min in a "Spex Mixer Mill". The latter combination was used only for preparing several samples in the HfC1-, melting-point studies. Small pellets, varying between 3/16

Jan 1, 1965

By L. Weyher, H. L. Lovell

This discussion is restricted to a very specific application of the cyclone - its use as a hydro-cyclone in the cleaning of fine coal. It is hoped that the development of the present data will assist in the further elucidation of existing qualitative models, and also in an enhanced application of the hydrocyclone and provide a base for further research. Discussed are the mechanisms of gravity separation in hydro-cyclones, test procedures, experimental observations, and industrial applications from these studies. Within the general area of unit operations, a considerable effort has been expended in theoretical and empirical research associated with cyclone operations. The motivation involves the industrial requirement for devices and techniques to manipulate small particles at low operating costs, a situation required in coal preparation. There are good reasons why the cyclone helps to satisfy this demand, because it combines operational simplicity (no moving parts) with versatility and high throughput capacity per unit area. The cyclone is one of the most widely applied tools in the process technologies. There are areas for potential cyclone application which have been only meagerly explored or not considered at all. This discussion is restricted to a very specific application of the cyclone - its use as a hydrocyclone in the cleaning of fine coal. It represents an initial presentation of a more comprehensive report. Coal preparation can appropriately claim the hydrocyclone since most of its predominant industrial uses have originated in this area and have spread into other applications, including the broad field of ore dressing, the petroleum industry, chemical processing, nuclear engineering and food technology. There is one operational principle common in all cyclones: A fluid is tangentially introduced into a cylindrical or conical container under pressure. A predominantly irrotational flow field1 is established within the cyclone (Fig. 1). The uniqueness of this flow is indicated by the variation in tangential velocity across the cyclone radius, which reaches a maximum a short distance from the center and decays toward the cyclone wall. In contrast, the tangential velocity in a centrifuge increases uniformly toward the wall. Usually two products are discharged from the cyclone. They differ in that one discharge consists predominantly of that portion of the feed fluid which moves along the wall axially away from the feed inlet, while the other consists predominantly of fluid spiralling along the central regions of the cyclone, in an axial direction opposite to that of the wall current. Fig. 2 indicates these discharge points schematically. The latter product may be termed the vortex-product, since it is discharged with the central vortex-current. In the case of conical cyclones, the former product may be referred to as the apex-product. Although the names "over- and underflow" are widely used, many cyclones are operated from extreme angular positions thus the proposed terms are less ambiguous. The cyclone feed fluid can be laden with solid particles or nonmiscible fluid drops. Such a feed component is discharged from the cyclone, after some residence time, into the one or the other product. Yet, the orifice through which a particle will leave the cyclone is dependent upon a number of factors. These factors, in a statistical sense, determine the path of the particle within the cyclone. Thus, different separation phenomena are possible and different process results attainable by the controllable variation of the particle path. It is then, to attain a fuller understanding of this particle path, to which this study is ultimately directed. It is anticipated that the detailed study of the data being developed will allow further elucidation of existing qualitative models. However, the development of a quantitative description of cyclone operation in terms of a mechanism is not currently feasible. The flow conditions in a cyclone are not fully understood even for a pure fluid, without the added complexity of the inclusion of multiple size-density particles. It is hoped that the development of the present data will also assist in an enhanced application of the hydro-cyclone and provide a base for further research. Some practical applications drawn from the data are suggested. Cyclone operations have been classified according

Jan 1, 1967

By Richard H. Olson, Lawrence A. Roe

Talc, when it can be isolated as a pure mineral, has a composition of 63.36% Si02, 31.89% MgO, and 4.75% H20. However, as an industrial commodity, talc rarely approaches theoretical purity. Nevertheless, the impure talc products of commerce find a multitude of uses and few substitutes in many industrial applications. Minerals commonly associated with and sold together in talcose mixtures are tremolite, chlorite, dolomite, mica, and magnesite. Steatite was originally a mineralogical name applied to pure talc. In today's commerce steatite generally refers to the massive variety of talc suitable for electrical insulator manufacture. Block steatite ore can be machined into various shapes. Impure varieties of massive or block talc are still commonly referred to as soapstone. Soft massive talc, suitable for crayon manufacture, has been referred to as French chalk. It has been common practice to discuss talc, soapstone, and pyrophyllite under the same general heading. In the case of soapstone and talc, this is a natural thing since many different types of platy, soft minerals exhibiting a high degree of lubricity (commonly referred to as "slip") have been grouped together and called soapstone or talc. Further, there is a mineralogical relationship of pyrophyllite to montmorillonite and talc to hectorite. Thus, talc and pyrophyllite are sometimes referred to as clay minerals. When finely divided talc or pyrophyllite are combined with water in proportions to make a slurry, the end product does have the appearance of a clay-water mixture. Soapstone for utensils and ornaments was mined by prehistoric Indians on Santa Catalina Island, CA. In the mid-1800s, soapstone from deposits along the western foothills of the Sierra Nevada mountains was used by white settlers for building and ornamental stone and in the linings and foundations of furnaces (Anon. 1956). Previous to 1916, the annual recorded production in California did not exceed 2000 tons. In the period 1912 to 1918, output rose sharply when the Talc City, Western, and Silver Lake mines were put into operation. From 1916 to 1935, the state's annual output of talc was in the range of 9,000 to 20,000 tons. In the mid-1930s, the use of talc in wall tile grew rapidly. In California, the production of talc grew to 63,000 stpy in 1943. The post-war building boom helped California production to grow to 120,000 tons in 1951. In 1968, production was 165,000 tons, 1969 was 145,000 tons, 1970 was 185,000 tons, and 1972 was 155,000 tons. Talc mining in New York state dates to about 1878 when a Colonel Palmer and associates opened the first commercial talc mine on the Nelson Freeman farm near Talcville, New York. In 1893, this operation was sold to the International Pulp Co. which changed its name to the International Talc Co. in 1944. The company was acquired by R.T. Vanderbilt Co., Inc. in 1974. A new talc operation, the Gouverneur Talc Co. owned by the R.T. Vanderbilt Co., began operations near Balmat, NY, in 1948. The initial capacity of the processing plant was 200 stpd (Gillingham, 1950). Subsequent expansions have increased capacity to over 600 stpd. The Vermont talc industry began just after the start of the 20th century. Talc was discovered in the area of the present Johnson, VT, talc mine in 1902. The American Minerals Co. initiated plant operations at Johnson in 1904. The Magnesia Talc Co. opened a plant at Waterbury, VT, in 1913 (Burmeister, 1963; Trauffer, 1964) and acquired American Minerals Co. in 1923. The Waterbury mine has a long history as a producer of talc crayons. The Eastern Magnesia Talc Co. was formed in 1924 by a merger of the Eastern Talc, Co.

Jan 1, 1983

By A. C. Freeze

The first use of electric punched card accounting machines as an aid in calculating reserves at the Sullivan mine in Kimberly, B.C., was made in January, 1948. At that time their use was limited to totalling individual reserve blocks for the various reserve classes and for calculating total metal content. The immediate objective was to increase speed, improve accuracy, and to effect some savings in labor that could be employed more usefully elsewhere. It was recognized also that the potential for achieving even greater advantages was excellent. The initial experiment proved so successful that it was inevitable that the use of the method would expand. Thus, for the past nine years assay data from core hole and development headings have been processed by these machines and the results integrated with the program of calculating reserves. It was also learned that the machines could store and classify a large amount of other information concerning the mining characteristics of each reserve block in addition to tonnage and metal content. This has proven very useful for the preparation of monthly production reports as well as in long term planning, in forecasting production schedules, and in analysing the results achieved.

Jan 4, 1961

By Charles S. Barrett, Robert F. Mehl, Dana W. Smith

The Widmanstatten figures found in the steels have been long recognized and in some aspects carefully studied,' especially as they occur in cast hypoeutectoid alloys. Aside from the practical importance of the structures obtained in the steels by various heat treatments, a study of the characteristics of these figures is interesting because of the rich opportunity the system affords to obtain new data on the mechanism of segregation from solid solutions. This opportunity is twofold: first, by changing composition within the austenite range the proeutectoid precipitate may be changed from that of ferrite to that of cementite, thus offering the same opportunity for changing the type of precipitate while maintaining the same basic lattice as that afforded by the Cu-Zn alloys;2 and second, the eutectoid inversion leads upon drastic quenching to the formation of martensite, a Widman-statten figure of unique interest from the crystallographic viewpoint, particularly in comparison with those formed on slow cooling.3 We have, therefore, two types of structure to study: that formed on slow cooling of hypoeutectoid and hypereutectoid alloys, and that formed on quenching hypoeutectoid, eutectoid, and hypereutectoid alloys. For each of these types of structure we require the crystallographic plane in the mother austenite along which the precipitate forms (we shall see that the precipitates in these alloys are invariably platelike in form), and also the orientation of the precipitate upon this plane. Some of these

Jan 1, 1933

By G. V. Jere, V. Krishnan, C. C. Patel

Standard free energy and standard enthalpy changes as a function of temperature have been calculated for the chlorination reactions of different oxides constituting columbite and tantalite. The tallies of standard lee-energy change (F) indicate the possibility of pvefeential chlorination of different oxides but the ease 0.f chlorination of columbium pentoxide at about 250°C and the chlorinating tendency of columbium pentachloride in promoting the chlorination of tantalum and other metal oxides, p7-evetzt the separation of columbiu?n and tantalum from other oxides and pom each othel.. It is likely that low temperatuves of chlorination and continuous 1err2oval of columbium pentachloride from the ..eaction zone may help partial separation of columbium from tantalum as well as from titanium. The standavd enthaply change (AH?) values shotr that 1ou.-temperature chlorination around 300" to 500°C is likely to sustain the chlorination , without external heating. COLUMBIUM (niobium) and tantalum metals, their alloys and interstitial compounds are finding extensive uses in nuclear reactors and high-temperature equipment.la-3 These metals also find uses in chemical process plants, electrical rectifiers and capacitors and as "getters" in electronic tubes.la With the development of Kroll process of reduction of volatilized titanium tetrachloride by magnesium for the production of titanium metal, chlorine metallurgy is receiving greater attention. Chlorine metallurgy has several advantages, the foremost amongst them are: the ease of chloride formation, separation of the different constituents of minerals by selective chlorination, and the reduction of the chlorides in vapor phase to the respective metals. Recently, Si-bert, Kolk, and Steinberg4 have considered a number of methods for the preparation of columbium metal and the most promising is found to be the halide reduction. Since the minerals columbite and tantalite are comparatively abundant in nature, the future of the metallurgical processes depends on the utilization of these minerals for the production of columbium and tantalum chlorides by chlorination. In this paper, an attempt has been made to interpret thermodynamically the chlorination of individual oxides constituting columbite and tantalite, with the help of the recent thermodynamic data.5-8 For this purpose, standard free energy and standard enthalpy changes of the chlorination reactions of the oxides with chlorine, both in absence and presence of carbon as the reductant, have been calculated as a function of temperature and represented graphically. Similar calculations for the reactions employing carbon tetrachloride and carbonyl chloride as chlorinating agents have also been incorporated in this paper. REPORTED WORK ON CHLORINATION Cuvelliezg has patented a process for the separation of columbium and tantalum from their concentrate, wherein 75 pct Cb05 is claimed to be chlorinated at 1050°C in the course of 7 hr using chlorine or chlorine containing nonreducing gases, the products of reaction being CbC1, or CbOC1,. At this temperature, Ta,05 is claimed to remain unaffected. It is further claimed1° that at higher temperatures, the proportion of Ta205 chlorinated increases while that of Cb205 diminishes. During the studies on the action of chlorine on individual metal oxides, Kangro and Jahn" have observed that Ta,05 is not chlorinated even at 1200" in the stream of chlorine, while 75 pct of Cb,05 is converted into CbOC1, around 900 to 1100°C. The chlorination of Cb205 by chlorine in the presence of carbon, investigated by Lind and Ingle,' and

Jan 1, 1962

By S. Feuerstein, L. Rice

The effect of low pressures on the flow and fracture behavior of molybdenum is described. For poly crystalline samples, room-temperature tensile tests indicate greater ductility under 10 Torr than under intermediate pressures up to and including atmospheric pressure (760 Torr). In addition, tests conducted at 760 Torr under atmospheres of air, dry nitrogen, and purified argon exhibited no apparent difference in mechanical properties. Critical tests involving baking in situ as well as those involving single-crystal deformation further imply that the ductility effect is a pressure-dependent phenomenon related only to the fracture process. This dependency is discussed in terms of adsorption and diffusion contributions. THE effect of very low pressures on material properties has heretofore been presumed to be important only for substances possessing relatively high vapor pressures at ambient temperatures. Research has therefore been concentrated primarily on organic solids and liquids, and in some instances on metals such as zinc and cadmium. Most vacuum-effect studies' on the mechanical behavior of metals have been performed under conditions of either cyclic loading or creep rupture at elevated temperatures, i.e., over extended time periods. These studies were not restricted to high vapor pressure materials but also encompassed such metals as gold, copper, and nickel. Very little concern, however, was placed upon the importance of a vacuum environment on the mechanical behavior of metals subjected to a simple unidirectional deformation at ambient temperatures. A tension test is generally of short duration as compared to a creep test, and at room temperature vacuum effects if any would be expected to be surface-limited. In early 1963, Kramer and podlaseck2 reported a change in the bulk flow behavior of aluminum single crystals during room-temperature tension tests. The deformations were performed under pressure conditions of 760 to 3.4 X 10-8 Torr and indicated for the first time a vacuum surface effect contributing to the bulk tensile behavior of metal specimens. As a consequence, an experimental program was initiated in this Laboratory to study the effects of ultrahigh-vacuum conditions on the mechanical behavior of metals. The results of a preliminary study on poly-crystalline molybdenum3 revealed, unlike Kramer's observations of changes in the stress-strain behavior, only an increased ductility under ultrahigh vacuum. Flow behaviors were nearly identical for all tests re- gardless of pressure. This paper presents comprehensive results obtained in this area of research. 1) EXPERIMENTAL PROCEDURE Three material categories were used in this study: sintered and are-cast polycrystalline molybdenum of nominal purity 99.93+ pct and single-pass electron-beam zone-refined molybdenum single crystals having a nominal purity level of 99.99+ pct. The interstitial levels (weight percent) as determined by the Materials Testing Laboratories, Division of Magnaflux Corp., were as follows: sintered molybdenum (C— 0.005, H—0.0004, O—0.015, N—0.008); and arc-cast molybdenum (C-0.0038, H-0.0003, O-0.015, N-0.023). Single-crystal molybdenum obtained from Materials Research Corp. had a typical interstitial analysis of C-0.0015, H-0.00007, O—0.00045, and N-0.0001. Tensile specimens having a 5 mm diam by 50.8 mm length were prepared from these materials. An average grain diameter of 0.059 mm was obtained for the sintered specimens following a 4-hr, 1600°C heat treatment. Grain sizes from 0.019 to 0.149 mm were obtained in the arc-cast specimens following heat treatments from 1100° to 1600°C for 1 hr. This series of specimens was used exclusively for the grain-size effect studies. All samples were electrolytically polished in 97 pct sulfuric acid solution prior to testing. Experiments were performed at room temperature in an ion-pumped ultrahigh-vacuum system positioned in an Instron tensile machine, Fig. 1. A constant strain rate of 4.2 x 10-4 sec-1 as derived from crosshead displacement was assumed for the deformations. Starting vacuums ranged from 2 to 0.5 X 10-10 Torr. These pressure measurements were made using corrected values4 of an NRC Redhead gage. Comparative readings were also made against a G.E. triggered dis-

Jan 1, 1967

By Larry Kaufman, Martin Schatz

The effect of pressure on the extension of the ? loop in the FeSi system has been determined by means of metallogvaphic studies and hardness measurements performed on a series of high-purity Fe-Si alloys containing 7.5, 11.0, and 13.9 at. pct Si, respectively. These mensurements, performed at 42 kbar and temperatures up to 1200oC, indicate that the ? loop is expanded to about 10 at. pct Si at 42 kbar as opposed to a maximum extension of 4 at. pct Si at 1 atm. Comparison of the experimental results with thermodynamic predictions of the pressure shifts yields satisfnctory results. DURING the past few years, several studies have been performed in our laboratory1-' in order to determine the effect of high pressure on phase equilibrium in pure iron and iron-base alloys. The purpose of these studies has been to elucidate the effects of high pressure experimentally and to compare the observed results with predicted pressure effects derived on the basis of known thermody-namic and volumetric data at 1 atm. These studies have included work on pure iron2,5,7 as well as Fe-Ni,1,5 Fe-cr,l,5 and Fe-c4-6 alloys. In addition, Tanner and Kulin3 have reported results of pressure studies on two Fe-Si alloys containing 2.0 and 6.25 at. pct Si. At the time of this latter study, no detailed information was available concerning the difference in volume between the a (bcc) and ? (fcc) phases in the Fe-Si system as a function of silicon content. In order to compare their observations with calculated pressure shifts, Tanner and Kulin were forced to assume that silicon had no effect on the difference in volume between a and ? iron. The resulting discrepancy between their calculation of the a/? phase boundary at 42 kbar and the observed results led them to the conclusion that silicon additions probably decrease the difference in volume between a and ? iron. Recently: Cockett and Davis8,9 have reported de- tailed studies of the lattice parameters of a series of Fe-Si alloys at temperatures ranging from 20" to 1150°C. These measurements, performed on alloys in the bcc and fcc range, show that silicon does indeed decrease the difference in volume between a and ? iron. By correcting the calculations of Tanner and Kulin in line with the observed effect of silicon they were able to show improved agreement between computed and observed pressure shifts.' The present measurements were undertaken to provide additional corroboration of this effect, by extending the range of composition, in addition to exploring a situation where large extensions of a ? loop could result in impingement of the ? field with an ordered bcc phase (based on Feo.75Sio.25). I) EXPERIMENTAL PROCEDURES AND RESULTS The alloys investigated were obtained from Dr. F. Kayser of M.I.T. They were prepared at the Ford Scientific Laboratory by vacuum melting electrolytic iron and high-purity silicon. The melts were poured under an argon atmosphere into hot-topped steel molds. Subsequently the ingots were hot-worked down to 1/2-in.-diam rods. Three alloys containing 7.5, 11.0, and 13.9 pct Si were studied. Carbon, regarded as the principal impurity, analyzed at, or below, 0.001 wt pct for all of the alloys. Prior to pressure-temperature treatment, the rod was annealed for 24 hr in vacuum at 1000°C, water-quenched, and subsequently machined into 0.100-in.-diam by 0.100-in.-long specimens. Subsequent to machining, the specimens were again annealed and then examined metallographically. They were found to exhibit a clear coarse-grained ferrite similar to Figs. 10 and 110 of Ref. 1 and Fig. 2 of Ref. 3. Subsequently, specimens of each alloy were equilibrated at 42 kbar at various temperatures in supported piston apparatus.1,3,4,6 Three specimens, one of each alloy, were wrapped in platinum and exposed simultaneously. The pressure-temperature cycle consisted of increasing the pressure from ambient to 42 kbar at 25oC, heating rapidly to the desired temperature, holding for 15 min, and quenching to 100°C, followed by slower cooling to 25°C and pressure release. The temperature was measured with a Pt/Pt-13 pct Rh thermocouple which was not corrected for pressure effects. Subsequently, specimens were examined metallographically and by

Jan 1, 1964

By C. D. Stahl, R. Sandrea

This investigation was made to evaluate the comparative effects of the viscosity and the phase behavior of the buffer fluid in the composite solvent displacement of Bradford crude from waterflooded sandstone cores. Buffer slugs of propane, naphtha and other refined hydrocarbons exbihiting increasingly favorable viscosity ratios and decreasing solubility relationships, respectively, with Bradford crude, were used in long Berea sandstone cores. The secondary slug was isopropyl alcohol. The results indicate that higher oil recoveries are obtained for increasingly favorable phase relationships even when these are accompanied by unfavorable viscosity ratios within the range studied. Moreover, when propane is used as a buffer slug with an adverse viscosity ratio of 36, it gives higher oil recoveries than at a similar size slug of an any1 alcohol having a viscosity ratio of 1.09. The investigation was extended to the study of the effect of flooding rate on oil recovery. Residual Bradford crude was displaced from a 6-ft Berea sandstone core at rates varying from 0.3 to 30 ft/ day. The results show that as flooding rates were increased above or decreased below a minimum range of 1 to 2 ft /day, displacement efficiency increased considerably. INTRODUCTION In recent years, the alcohol slug process as a means of tertiary recovery has been the subject of many investigations. Gatlin and Slobod showed the advantages of the combination solvent slugs over the previous single-slug process.1 The combination slugs require less total slug material to obtain similar oil recoveries. The basic combination process involves injecting a primary or buffer solvent which is preferentially oleophilic, followed in turn by a water-driven slug of isopropyl alcohol. This procedure ensures that the buffer slug, which is miscible only with the reservoir oil, displaces and replaces the oil and is in turn displaced, together with the water, by the isopropyl alcohol slug miscible with both fluids. Likewise, for those reservoir oils that show some degree of phase incompatibility with isopropyl alcohol, as does Bradford crude, a proper buffer solvent can artificially make the alcohol process technically feasible. From an economic standpoint, propane or LPG would be the most appropriate primary solvent to be used in the field; however, Taber, et a12 have indicated that the alcohol process becomes highly inefficient in the displacement of light hydrocarbons because of the entrapment of these hydrocarbons during the stabilized bank formation. Moreover, since materials such as propane have such low viscosities, adverse viscosity ratios with most reservoir oils would be penerated, thereby possibly further reducing the efficiency of the buffer solvent. This paper presents the results of an experimental study of the comparative effects of viscosity ratio and phase relationships on the displacement efficiency of Bradford crude by means of dual solvents. The work was extended to include the effect of flooding rate on oil recovery. Rates within the range of field and laboratory values were used. EXPERIMENTAL PROCEDURE APPARATUS The porous media used in this study consisted of two 10-ft and one 6-ft Berea sandstone cores, 3-in. in diameter. These were cast in galvanized steel pipe of 31/2-in. ID and the annulus was filled with Armstrong cement. The 10-ft cores were assembled by connecting two 5-ft units, which were joined together by 8-in. steel flanges fitted to the pipe. Intimate contact between the two sections was obtained by inserting a thin disk of the same sandstone between the core faces. The outlet and inlet ends of the cores were covered with threaded pipe caps. The injected fluid was gravity fed to two variable-rate positive-displacement pumps. The fluids were filtered before entering the core and the effluent was collected in an automatic fraction collector and

Jan 1, 1966

By A. Lubinski, J. L. Logan, W. S. Althouse

A4ost gas twells and flowing oil wells are completed and treated through a string of tubing and a packer. Changes in temperature and in pressure inside or outside the tubing will: (I) if free motion of the tubing inside the packer is permitted, increase or decrease the length of the rubing; or (2) if free motion is prevented, induce forces in the tubing and on the packer. If pressure inside the tubing is greater than outside, the tubing may buckle helically even in the presence of a packer-to-tubing tension. The tubing will always buckle, and much more severely, if free motion is permitted. The buckling may be prevented by pulling the tubing in sufficient tension. The prediction of these forces and tubing movement has here to fore been based upon calculations that did not inciude helical buckling. This paper preseitts means with which these length or force changes can be calculated while taking into account the effect of helical buckling. To avoid damaging formations, failure of remedial operations, or damage to the tubing or packer, application is made to practical problems involving calculations of the required length of seals, amount of sluckoff or tension, and prevention of permanent corkscrewing. INTRODUCTION Leakage of a packer may result in costly failures of such operations as squeeze cementing, hydraulic fracturing, etc. To avoid such failures, the authors are often asked questions pertaining to the length of necessary seals, the amount of necessary slackoff, etc. Published work' does not take into account helical buckling of tubing. Investigation of helical buckling was prompted by the fact that allowance must be made for this phenomenon in order to provide relevant answers. In the past, theoretical work on helical buckling was confined to conditions for which such buckling does not The mathematical treatment of behavior in a buckled condition, given in the Appendix, is novel. Assumptions upon which this investigation is based are listed and discussed in a special section. The following are a few of the many kinds of problems which may be solved with this paper. 1. Consider a packer in which tubing may move. Such movement will occur after pressures and temperature are changed. The paper provides means for: (a) calculating the amount of such movement and, therefore. the required length of seals; and (b) calculating the necessary amount of initial slackoff, for which there is no danger of unsealing the packer, if the length of seals is given. Such calculations, as well as those which follow, tully take into account the fact that part of the movement ib due to elastic helical buckling of the lower part of the string. This buckling may occur even in tubing under tension. Insufficient initial slackoff for a given length of seals, or insufficient length of seals for a given slackoff, may result in costly failures. A field case of such a failure will be given further in this paper. 2. In the case in which tubing cannot move in the packer, changes of pressure and temperature result in tubing-to-packer forces and forces in the tubing above the packer, both of which may be calculated. This knowledge is important because, if these forces are too large, the) could damage the packer or the tubing. 3. For wells in which wireline tools are to be run through the tubing, the paper provides means to keep the tubing from buckling, thereby permitting free passage of tools. 4. In deep wells, mainly in the presence of large casing, tubing may become "corkscrewed", i.e., take a permanent helical set. A field case is described further in the text. Using this paper, one may calculate in advance conditions under which permanent corkscrewing would occur, and then take preventive steps. HELICAL BUCKLING Consider a string of tubing, freely suspended in the absence of any fluid inside casing, as shown in Fig. I(a). Now consider an upward force F applied at the lower end of this tubing. This force compresses the string; and if the compression is large enough (which is always the case in actual problems), the lower portion of the string will buckle into a helix, as shown in Fig. 1 (b). The lower end of the tubing is subjected to a compression F. This compression decreases with the distance from the bottom and becomes nil (neither compression nor ten-

By P. D. Merica

The remarkable phenomena exhibited by the aluminum alloy known as duralumin were discovered during the years 1903-1911 by A. Wilm1,2 and have been described by him and by others. 3 4 5 6 The unusual feature of this alloy is the fact, as was shown by Wilm, that it can be hardened quite appreciably by quenching from temperatures below its melting point followed by aging at ordinary temperatures, which consists merely f allowing the material to stand at these temperatures. The hardness is not produced by the quenching alone but increases during the period of aging, which may be from one to three days. Cohn3, 5 gives data showing the increase of hardness of duralumin during aging, after quenching in water from about 450° C. Upon annealing, the alloy so hardened by aging is softened exactly as is hardened steel. The composition of this alloy usually varies within the following limits: Copper, 3 to 4.5 per cent.; magnesium, 0.4 to 1.0 per cent.; manganese, 0 to 0.7 per cent.; aluminum, balance; iron (as impurities), 0.4 to 1 per cent.; silicon, 0.3 to 0.6 per cent. Its density is about 2.85. It is used only in the forged or rolled condition. This alloy has been produced for some years commercially and is in demand for the fabrication of parts for which both lightness and strength are required, such as for aircraft. Its tensile strength will average 50,000 to 60,000 lb. per. sq. in. (3515 to 4218, kg. per sq. cm.) after appropriate heat treatment, such as that described by Wilm.

Jan 6, 1919

By R. T. DeHoff, L. J. Buteau, J. Kronsbein

Network topology is introduced and used to describe sinter bodies at various stages of the sintering process. The matrices of incidence, loop-branch. tree-branch, and cut-branch are constructed and their relationship to the three-dimensional void space and the common two-dimensional bounding surface is established. The sintering body is assunzed to remain connected but this is not so with the void space. The topological invariants known as Betti numbers are related to this observed fact and provide parameters which measure the progress of the sintering process. They are extracted from the matrices by means of known algebraic operations. Experimental procedures are given which permit actual construction of the various matrices and determination of the Betti numbers by serial sectioning of the sinter bodies. A sinter body is produced by exposing a large number of metallic particles (0.00001 to 0.3 in. diam) to a temperature that is near but below their melting point. When these particles are maintained at such a temperature for a sufficient length of time, it is found that the interparticle contacts become welded. As time increases, these welds, often referred to as necks, grow. All of the space between the particles constitutes a single connected void; an ultimate consequence of sintering is the breaking up of the void into separated parts. A mathematical apparatus for describing the geometric characteristics of a sinter body at each stage of the process was first proposed by F. N. Rhinesl when he introduced the application of topology to this problem. He described the sinter body in terms of one of its topological invariants, the genus. The most important advantage of a topological description is invariance with respect to continuous deformations. This means that particle sizes and shapes need not be considered, resulting in considerable simplification and generalization of the geometric description. In the case of a sinter body, wherein the internal geometry is particularly complex, the simplification provided by topological concepts is absolutely essential. The important parameters in the Rhines model are the number of particles and the interparticle contacts. The invariant considered called genus is given by Euler's formula for the connectivity of two-dimensional surface of the sinter body. This surface includes the pore-solid interface. The Euler formula is G = C - P + 1 [1] where C = number of interparticle contacts, P = number of particles, and G = genus of the surface bounding the sinter body. In topology the term genus may be used to mean the number of self re-entrant cuts that can be made on a closed surface without dissecting it into more than one connected surface. Its use is restricted to the surface and does not apply to the three-dimensional volume enclosed or excluded by it. In the case of sintering, the volume enclosed by the surface is defined as the sinter body; the volume excluded will be referred to as the void space. There is an intrinsic reason for using genus as a characteristic number associated with a sinter body. The genus is related to the Gaussian curvature by the integral of the product of the principal curvatures taken over the entire surface of the sinter body, as given by

Jan 1, 1965