By Robert E. Green, Wolfgang Sachse

Simullaneous ultrasonic attenuation measurements of both quasishear waves propagating in single cryslals of aluminum indicate that, in the undeformed annealed state, the dislocation density is generally not uniform on all slip systems. Change oof attenuation measurements made during plastic defortnation of crystals , which possessed specific orientations ideal for studying the orientation dependence of dislocation damping, indicate that, for low strain levels, dislocation motion occurs on additional slip systems besides the primary one, even for crystals oriented for plastic deformation by single slip. THE sensitivity of internal friction measurements permits such measurements to be used successfully in studying the deformation characteristics of metal crystals. On the basis of experimental observations, T. A. Read1 was the first to associate internal friction losses with various dislocation mechanisms. Since that time further work2-' has been performed and a dislocation damping theory has been formulated by Granato and Lucke.6 In the amplitude independent region, this theory predicts the attenuation a to be dependent on an orientation factor O, a dislocation density A, and an average loop length L. if is a constant, independent of crystallographic orientation. For a given crystallographic orientation, changes in dislocation density and loop length give rise to the observed attenuation changes accompanying plastic deformation. The Granato-Liicke theory suggests the investigation of the orientation dependence of attenuation measurements in hopes of obtaining information to separate dislocation motion losses from other losses.7 An experimental study of the orientation dependence of attenuation in undeformed annealed single crystals should yield an insight into the uniformity of dislocation distribution throughout the entire specimen. A similar study on crystals plastically deformed in a prescribed fashion should give information about the alterations in the dislocation distribution on the slip systems activated during plastic deformation. The possible modes of elastic waves which can be propagated in aluminum,8 copper,9 zinc,10 and other hexagonal metals" have been calculated. Associated with each mode of wave propagation are dislocation damping orientation factors, which are based on the resolution of the stress field of that particular elastic wave onto the various operative slip systems in the material. These orientation factors have also been calculated as a function of crystallographic orientation in the papers cited above. Einspruch12 obtained agreement between predicted and observed attenuation values of longitudinal and shear waves in (100) and (110) directions of two undeformed aluminum crystal cubes. He ascribed the slight deviations between predicted and observed values to a nonuniform dislocation distribution, or to other loss mechanisms. In shear deformation of zinc crystals, Alers2 found that the attenuation of shear waves having their particle displacements in the slip plane was very sensitive to the deformation, while the longitudinal wave attenuation was affected only when the wave propagation direction was not normal to the slip plane. Using aluminum single crystals oriented for single slip, Hikata3 et al. found that during tensile deformation the change of attenuation of the shear wave (actually quasishear) having particle displacements nearly perpendicular to the primary slip direction exhibited the easy-glide phenomena, while longitudinal waves did not. Similar results were reported by Swanson and Green5 during compressive deformation of aluminum crystals. These results are in qualitative agreement with the calculated orientation factors for specimens of this orientation. In well-annealed, undeformed aluminum crystals, the damping is expected to be due to dislocations vibrating on all twelve slip systems. The orientation factors associated with this initial damping will be designated by O2 and O3, where a, represents the average orientation factor for the slow shear (or quasishear) wave and O3 represents the average orientation factor for the fast shear (or quasishear) wave. The calculation of these values for aluminum crystals by Hinton and Green8 shows that they vary very little as a function of crystallographic orientation—at most, by a factor of 2.47. If the dislocation density and loop length are uniform, then in the initial undeformed state, Here the subscript zero refers to the initial value of the attenuation. Also for aluminum, the calculations8 show that the orientation factors for primary slip only, associated with each shear wave, exhibit a sharp minimum for particular crystallographic orientations. A composite plot of the two shear wave orientation factors for primary slip only is shown in Fig. 1. Since these orientation factors are associated with dislocation motion occurring on the primary slip system only, the proper condition to check these factors might be attained by slightly deforming a single crystal oriented for primary slip. For dislocation motion on the primary slip system only,

Jan 1, 1969

By B. B. L. Seth, H. U. Ross

A generalized rate equation for the reduction of iron oxide was derived from which two particular equations were obtained: one for rate controlled by the transportation of gas, the other for rate controlled by the phase-boundary reaction. Pellets of pure ferric oxide having diameters of 8.5 to 17.5 mm and a density of 4.8 g per cm3 were prepared and reduced by hydrogen at 750° to 900°C. From the analysis of data obtairzed, it was observed that neither the phase-houndarv reaction nor the transportation of gas controlled entirely the rate of redziction. Rather, the mechanism of reduction can he divided into three stages. In the beginning, the process seems to depend predominantly on the surJrce reaction, hut after a layer of iron is formed the diffusion of gas becomes the controlling factor. Towards the end, however, the rate falls sharply due to a decrease in porosity. The times predicted by the generalized equation for a certain degree of reduction showed an excellent agreement with those obtained experinmentally for pellets of varying sizes. WIDE interest in iron oxide reduction has resulted in many valuable studies pertaining to thermody-namical properties, equilibrium diagrams, and chemical kinetics. Although the thermodynamical properties and equilibrium diagrams are now known with a fair degree of accuracy, the mechanism and rate-controlling step in the reduction of iron oxides presents a problem to research workers which is still unsolved. This is because the field of chemical kinetics is so highly complex. Besides the chemical reaction between oxide and reducing gas, several other processes are occurring simultaneously such as solid-state diffusion of iron through intermediate oxides (FeO and Fe3O4), the diffusion of reducing gas inwards and of product gas outwards, and the sintering of iron if reduction is carried out above the sintering temperature of iron. Furthermore, there is a large number of variables, including the nature and flow rate of the reducing gas, the chemical composition and physical properties of the ore, the temperature of reaction, particle size, and so forth, all of which can affect both the mechanism and the kinetics of reduction. Despite the controversy and diversity of opinion about the mechanism of iron oxide reduction, three main schools of thought have emerged. According to the first, the rate is controlled by the diffusion of gas through the boundary layer of stagnant gas; the second claims that the rate is proportional to the area of the metal-oxide interface, while the third believes the transportation of reducing gas from the main stream to the metal-oxide interface and of product gas from the metal-oxide interface to the main stream to be the rate-controlling step. 1) The boundary-layer theory is true mainly for packed beds where the flow of gas through the bed is important. For a single particle, the boundary layer may be prevented from being the rate-controlling step if a gas flow rate of reducing gas above the critical flow rate is used. 2) Several workers have reported a linear advance of the Fe/FeO interface which provides excellent support for the belief that reduction is controlled by the surface area. McKewanl has given formal shape to this concept with mathematical derivation and has shown it to be valid for reduction of several iron ores, hematite, and magnetite, both by H2 and H2, H2O, N2 mixtures. Some other investigators, however, do not find this theory to be entirely valid. Deviations have been observed2 and further confirmedS3 Hansen4 also agrees that deviations do occur, at least in the latter stages of reduction, while from the data of several investigators summarized by Themelis and Gauvin,5 it is clear that the theory is not always applicable and further that, when it is applicable, it does not hold in the final stages of reduction. 3) Among those who claim the transportation of gas to be the rate-controlling step are Udy and Lorig,6 Bogdandy and Janke,7 and Kawasaki el a1.8 The validity of the theory has also been acknowledged indirectly by other research workers who show that the sintering and recrystallization of iron cause a decrease in reduction rate, for it is only if the transportation of gas is important that this sintering has any bearing. However, the theory has been rejected by some because they have failed to obtain

Jan 1, 1965

By T. L. Chu, G. A. Gruber

Silica films hare been rleposited 011 silicon substmtes at 400° to 600°C by a chemical-transport technique using hydrogen fluoride as the transport agent ill a closed system. This transport takes place from a source materia1 1071: temperature to substrates at higher temperatures, as indicated by the thermochemistry of the transport reaction. The experimental variables of- the transport process, such as the substrate temperature, the pressure pi the transport agent, and so forth, have been studied. The rate -determining step of the transport process appears to he the ),ale of chemical reaction in the source region. The transported films are similar to thermally grown silica films in physical proper-ties with the exception of 'some what higher dissolrrtion rates. SILICA films deposited on suitable substrates serve many purposes in electronic devices. They are used for the fabrication of tunneling devices, the surface passivation of devices, and the shielding of devices from nuclear radiation: and as selective masks against the diffusion of specific impurities into semiconductors. Doped silica films can also be used as sources for the diffusion of impurities into semiconductors. Several oxidation and deposition techniques for the preparation of silica films have been developed to meet the requirements of these applications. The therma1 oxidation of silicon by oxygen or steam at temperatures above 900 C is commonly used in silicon technology. The deposition techniques are perhaps more advantageous since they usually require lower temperatures and are not limited to silicon substrates. Silica films have been deposited on silicon and other substrates by reactive sputtering and chemical reactions. The sputtering of silicon in an oxygen atmosphere is capable of depositing good-quality silica films on silicon' and gallium arenide. Many chemical reactions are known to yield silica at room temperature or higher. These reactions may involve intermediate steps. However, the final step yielding silica should take place predominately on the substrate surface in order to produce adherent films. When silica is formed in the gas phase by volume reactions, no adherent deposit can be obtained. Generally, the experimental conditions of a reaction can be varied so that the surface reaction predominates over the volume reaction. The chemical reactions which have been used successfully for the deposition of silica films are briefly as follows. The pyrolysis of alkoxysilanes in an inert atmosphere or under reduced pressure has been employed to deposit silica films on germanium3 and silicon4 at 650" to 750°C in a flow system. The deposition of silica films from alkoxysilanes has also been achieved at nearly room temperature by a low-pressure plasma. Device quality silica films have been deposited on germanium and gallium arsenide by the deposition of an amorphous thin silicon film followed by oxidation at 600" to 700" . Silica films for high-temperature capacitors have been produced by the hydrolysis of silicon tetrabromide at 950°C in argon and hydrogen atmospheres.7 We have developed a chemical-transport technique for the deposition of silica films on semiconductor substrates at relatively low temperatures. The thermochemistry of the transport reaction, the experimental variables of the transport process, and the properties of the transported silica films are described in this paper. THERMOCHEMICAL CONSDERATIONS The transport of solid substances by chemical reactions in the presence of a temperature gradient has been used for the preparation of films and crystals of many electronic materials. In this technique, a gaseous reagent is chosen so that it reacts reversibly with the solid substance under consideration to form volatile products. Since the equilibrium constants of most reactions are temperature-dependent, the transport of these products to regions of suitable temperature in the reaction system would cause the reverse reaction to take place. depositing the original solid. When the equilibrium is shifted toward the formation of the solid as the temperature is decreased, the solid is transported from a high-temperature zone to a lower-temperature region, and vice versa. This chemical-transport technique can be carried out in a closed or gas-flow system. In a closed system, chemical equilibrium is presumably established in the different temperature regions of the system, and the transport agent regenerated in the deposition region repeats the transport process in a cyclic manner. The local chemical equilibrium may not be approached in a flow system: however, this system offers a greater degree of flexibility. Silica reacts reversibly with hydrogen fluoride and this reaction was chosen for the transport process. The over-all reaction between silica and hydrogen fluoride may be written as: SiO2(s) + 4HF(g-) = SiF4Ur) + 2H2O(^)

Jan 1, 1965

By A. McLean, D. W. Gomersall, R. G. Ward

An experimental study has been made of the solubility of nitrogen in liquid iron and liquid Fe-C alloys using levitation melting and a rapid quenching device. Iron alloy droplets were equilibrated with nitrogen gas at 1 atm pressure, quenched, and analyzed. Previous techniques for studying the Fe-C-N system have produced data which me in marked disagreement. This disagreement is due largely to errors caused by reaction between the molten alloy and the crucible material. With the levitation procedure, errors from this source have been eliminated and precise solubility data obtained for temperatures between 1450° and 1750°C. C-N interactions in molten iron have been expressed in terms of first- and second-order free energy, enthalpy, and entropy parameters. ALTHOUGH the solubility of nitrogen in iron base alloys is in general small, the effects of nitrogen on the properties of steel may be quite profound. For most purposes nitrogen in finished steels is undesirable, particularly in the low-carbon grades, since on cooling to room temperature the solubility limit of nitrogen in the steel may be exceeded and this can lead to embrittlement and loss of ductility on aging. On the other hand, nitrogen can improve the work-hardening properties and machinability of steels while in certain stainless grades nitrogen is important in order to stabilize the austenite phase. It is, therefore, desirable that one should be able to predict the solubility of nitrogen in liquid iron alloys. To do this, information is required concerning the interactions between nitrogen and the various alloying elements which may be present in liquid iron. There have been several investigations of these effects in recent years1"7 and the interactions between nitrogen and many elements dissolved in liquid iron are now known to a high degree of precision at steel-making temperatures. Unfortunately, a number of iron alloy systems which are of interest in steelmaking have been difficult to deal with by the experimental techniques generally used for this type of investigation. Among the most important of these are the Fe-C alloys. In the past, two methods have been widely used for determining nitrogen solubilities: the Sieverts' technique, in which the amount of nitrogen required to saturate a given mass of liquid metal at a particular temperature and pressure is measured volumetrically, and the sampled-bath technique in which liquid metal held in a crucible is equilibrated with a gas phase containing a known partial pressure of nitrogen, and samples drawn from the melt are quenched and analyzed. These two methods have been discussed in detail elsewhere.5,8 With the Sieverts' technique, errors may be introduced from the following sources: i) Gas adsorption on metal films which have condensed on the cooler parts of the reaction chamber. ii) Uncertainty in the determination of "hot volume" calibrations. iii) Crucible-melt interaction, particularly if a gaseous reaction product is formed or if the melt becomes contaminated with material from the crucible walls. The sampled-bath method may also suffer from errors due to reaction between the melt and the crucible material. In addition, there is the possibility that gas may be lost from the sample during solidification and cooling. In the present investigation, the solubility of nitrogen in liquid iron alloys has been studied by means of a new technique based on the use of levitation melting equipment and a rapid quenching device. In addition to the fact that problems of the type outlined above are avoided, this particular approach has the following advantages: i) The high-frequency current induces vigorous stirring within the levitated droplet so that gas-metal equilibration is rapidly attained. ii) The gas phase surrounding the melt can be changed very quickly and is easily controlled. For example, a droplet may be levitated in helium, deoxidized in hydrogen, equilibrated with nitrogen, and quenched, within a period of 15 min. ii) Melts can be readily under cooled or superheated, thus extending the effective temperature range of an investigation and allowing temperature-dependent data to be determined with a high degree of precision. Excellent reviews of levitation melting techniques and their application to physical-chemistry studies at high temperature have been published recently by Jenkins et al.,9 Peifer,10 and Rostron.11 In the present investigation a levitation melting technique has been used to obtain data for the solubility of nitrogen in pure liquid iron and liquid Fe-C alloys at temperatures between 1450° and 1750°C. The solution of nitrogen in liquid iron can be described by the reaction:

Jan 1, 1969

By E. F. Thomas

THE late George S. Rice was active in the inves--I- tigation of bumps, particularly in the last ten years of his career as chief mining engineer of the U. S. Bureau of Mines. Since most of his investigation was carried out in Great Britain, continental Europe, and—to a lesser extent—Canada, his thinking on prevention was influenced considerably by the experience of those countries. It is not surprising, therefore, that when he was called upon a few years before his retirement to investigate bumps in the U. S. and suggest ways to prevent them, he turned to longwall mining. A longwall method had been most successful in combating the bump hazard in mining coal under deep cover, especially in Great Britain, but the prevailing method there at the time was advancing longwall mining, which he knew was uneconomical under U. S. mining conditions. For this reason he proposed a modified retreating longwall system that he believed included the best features of the advancing method. As brought out by Rice,' if the cover is 2000 ft and 50 pct of the coal is extracted, the static load on the remaining pillars will be about 4000 psi, which exceeds the ultimate crushing strength in most instances. If the pillar coal is overloaded before a pillar line is established, then the abutment zone preceding a line of extraction is no place to split pillars or extract them by any method other than an open-end system. Rice therefore advocated open-end mining, preferably by longwall, but he was willing to compromise with long-face mining if the longwall method was not acceptable. Rice's system was put into operation in a mine in Harlan County, Kentucky,3 but subsequent experience has shown that it did not take into account two important factors—avoidance of pillar-line points and maintenance of adequate development in advance of the pillar-line abutment area. For ten years after Rice's retirement the USBM did little investigation and research on bumps, chiefly because so few were occurring that there was not much cause for alarm. But in 1951 there were three occurrences involving fatal injuries, and the Bureau began a statistical survey in that year. C. T. Holland, head of the department of mines at Virginia Polytechnic Institute, was retained as a consultant. The resulting study' of 117 case histories brought out these important conclusions: 1) Almost invariably the bump occurred in a locality affected by the abutment zones of one or more pillar lines. 2) In most cases the locality of the bump was influenced by the abutment zones of more than one pillar line. The term pillar-line point has been used for many years in the Appalachian region for such a situation. Point is used in the geographical rather than the mathematical sense. 3) In pillar-line extraction the following practices are safest in preventing bumps: a. The mine layout should provide for pillars of uniform size and shape along the extraction line. b. The mine layout should be planned so that no development need be done in the abutment zone of a pillar line. c. The layout should permit open-end extraction of pillar lines from the next goaf, so that it will not be necessary to resort to pocket mining, splitting pillars, or any practice that will involve driving in the direction of the goaf within the abutment zone. d. Pillars should be large enough to support area without undue roof and floor convergence before establishment of a pillar line. These are, of course, generalities, and while they are useful in laying out areas where bumps can be expected, they are of limited help in many mines that were committed to a system of mining before it was realized that they were subject to bumps. Under such conditions it becomes necessary to choose between the following alternatives: 1) Abandon the territory, except for pillars that offer no extraction problems. 2) Through experience select the pillars that are most heavily loaded, and, by augering, induce bumps from a safe vantage point so that impinged loads are relieved. This method was first developed at the Gary, W. Va. mines of U. S. Steel Corp. and later adapted to mining thick coal beds at Kaiser Steel's Sunnyside mine in Utah. No scientific method is available to determine where to drill within a loaded pillar. Although this method of unloading has worked very successfully at Gary—with one exception—

Jan 1, 1959

By O. W. Simmons, L. W. Eastwood, C. M. Craighead

H. Schwartzbart and W. F. Brown, Jr.—The authors have divided the effects of recovery on the true stress-true strain curve into two types; metarecovery, which effects only the first part of the curve or the yield strength, and orthorecovery, which effects the flow stress at any strain. Both of these are said to be true recovery effects, involve no recrystallization, and are explained by the removal of two different types of imperfections caused by work hardening. However, there seems to be some question as to whether the data are sufficiently conclusive to exclude, as an explanation of the authors' results, a mechanism based on the relief of residual stresses between the grains or slip bands and recrystallization. It appears that metarecovery could be interpreted in the same fashion as a customary interpretation of the Bausch-inger effect. The balanced system of internal stresses which exists between grains in a strained specimen due to varying orientation and, hence, yield strengths, of the different grains is responsible for a reduced yield strength in compression following pre-tension, and, similarly, for an elevated yield strength in tension following pre-tension. If the specimen is now heated so that the internal stresses are relieved by creep, then the yield strength in tension following tension will have been reduced and in compression following tension will have been raised. There seems to be a very strong case for the lack of recrystallization in the aluminum investigated by the authors, if one defines recrystallization as the presence of visually detectable new grains or accepts the X-ray evidence as conclusive. One must remember, however, that the appearance of spots on the back-reflection X-ray patterns cannot be taken as the time when recrystallization first started. The areas of recrystallized strain-free material must first have grown to a size large enough to give distinct spots on the patterns and this may take some time. Averbachl7 in an investigation of brass has shown that recrystallization can be detected by extinction measurements at temperatures lower than those based on hardness or X-ray line width determinations. It can be seen from fig. 10 that the rate of recrystallization is extremely low over a considerable time period at the onset of the process. Observations on the rate at which small amounts of recrystallization effect the flow stress would have given further insight as to whether undetectably small amounts of recrystallization might have been responsible for orthorecovery. Also, the question arises as to whether the effects observed in fig. 6 for various times and temperatures could not have been obtained if the time at 212°F were sufficiently long. In addition, the argument that the curve in fig. 10 is not sigmoidal seems weak in view of the scattering of the points. It is conceivable that an accurate determination of the curve for the first 100 hr would exhibit a relationship other than the one drawn. There is one point we would like to raise about the condition of the starting material. The authors annealed their material at 750°F for 15 min to remove the effects of any previous work hardening or machining strains. Reference to the work by Anderson and Mehl shows that this treatment may not have completely recrystallized the aluminum, so that the starting material may have had some strained areas. Higher temperatures or longer times may have been required to remove the effects of any small strains. We would like to mention some results of tests being conducted at the Lewis laboratory of the National Advisory Committee for Aeronautics in an investigation of the Bauschinger effect in relation to fatigue. Tests were performed on annealed electrolytic copper and several annealed brasses. Specimens were pre-strained 1 pct in tension and then tested in compression or tension with and without intermediate stress-relieving annealing treatments at 500°F for various times. Specimens heated at 500°F for 10 1/2 hr showed an elevation of the flow curve in compression and an approximately equal lowering of the flow curve in tension when compared with the curves for the un-heat treated specimens. After approximately 0.8 pct strain, all flow stresses coincided and were equal to the flow stress of the virgin material at this strain. This behavior is consistent with the metarecovery observed for aluminum by the authors and for which a residual stress model can be used. On the other hand, increas-

Jan 1, 1951

By Robert Baschwitz, John Chipman

The distribution of silicon between liquid silver and Fe-Si-C alloys has been studied at 1420oand 1530°C. The data are consistent with earlier studies. New data of Hager on the liquidus lines of the system Ag-Si and the distribution data are used to obtain the activity coefficient of silicon in both liquid phases. Data on the heat of mixing in iron permit accurate extension to 1600°C. Equilibrium data involving SiO2 and silicon in liquid iron together with revised data on the free energy of SiO2 are used to fix the activity of silicon in the infinitely dilute solution. The binary system exhibits strong negative deviation from ideality. At infinite dilution ? Si at 1600" is 1.25 x 10'3, and at concentrations up to NSi = 0.4 the slope d InySi/dNSi has a constant value of r; = 13. It is found that logysi in the ternary solutzon is approximately but not exactly the same function of Nsi + NC as of NSi in the binary. The results are consistent with currently available data on the free energy of Sic and its solubility in molten iron. LIQUID solutions of the system Fe-Si-C have acquired considerable importance as the laboratory prototypes of blast furnace hot metal. Equilibrium studies involving such solutions and slags approximating those of the blast furnace have yielded useful information concerning the thermodynamic properties of blast furnace slags. In studies of this kind great importance attaches to a knowledge of the thermodynamic activity of silicon in the solution as a function of temperature and composition. An attempt was made by Chipman, Fulton, Gokcen, and askey' to evaluate all of the pertinent data on this system and to deduce the desired relation between activity, composition, and temperature. These authors published data on the solubility of graphite and Sic in molten Fe-C-Si solutions and on the distribution of silicon between liquid iron and liquid silver. They showed further how the activity of silicon in very dilute solutions in liquid iron could be calculated from equilibrium data involving the molten alloy and solid SiO,. These calculations rested on the published thermodynamic properties of SiO, in- cluding its heat of formation which at that time was recorded as -209.8 kcal. This value has been under suspicion for some time and has recently been replaced by the concordant results from two independent laboratories2,3 which place the heat of formation of a-quartz at -217.6 kcal. This revision necessitates a re-evaluation not only of the activity of SiO2 in slag but also of silicon in molten iron. It is the purpose of this paper, therefore, to recalculate the activity of silicon, and in furtherance of this objective to present new data on its distribution between liquid Fe-Si-C alloys and liquid silver. HEAT OF SOLUTION OF SILICON IN IRON In order to determine the effect of temperature upon the activity coefficient it is necessary to know the heat of solution of silicon in iron as a function of composition. This is found in the data of Korber and Oelsen4 shown in Fig. 1. The curve corresponds to the following equation, which is of a form suggested by Wagner:5 Here AH is the heat absorbed in kilocalories in forming one gram atom of molten alloy from its molten elements and the N's are atom fractions. The relative partial molal enthalpies of the components, each referred to its pureliquid state and defined as zFe = aFe - PFe and zsi = HSi — -psi, are shown graphically. At low concentrations zSi = -28.5 kcal, in agreement with Kijrber and Oelsen's computation. This is in good agreement with the value of -29.3 kcal obtained by Chipman and Grant6 using an entirely different method. ACTIVITY AT INFINITE DILUTION From the known free energy of SiO, it is possible to obtain the activity of silicon in dilute solution in liquid iron from equilibrium studies. The heat of formation of a-quartz is —217.6 kcal and the heat capacity and entropy data are given by Kelley and ~ing.' The free energy of formation of ß-cristo-balite at temperatures above the melting point of silicon is expressed by the following equation: Si(Z) + O2(g) = SiO2 (crist); AF" =-226,500 + 47.50T [I] The value of the deoxidation product for silicon [%Si] x [%O]2 at 1600°C according to Gokcen and chipmans is 2.8 x 10"5, in agreement with results of Hilty and Crafts.9 More recent works of Matoba,

Jan 1, 1963

By J. F. Martin, L. M. Melnick, R. Rapp, R. C. Takacs

Recent studies on the determination of hydrogen in steel have shown that the hot-extraction method for removing hydrogen from a solid sample is preferable to its removal from a molten sample by vacuum fusion or by fusion in vacuum with tin. A number of techniques are available, however, for determining the hydrogen so extracted. They include: thermal conductivity, gas chromatography, pressure measurement before and after catalytic oxidation of the hydrogen to water and removal of the water, and pressure measurement before and after diffusion of the hydrogen through a palladium membrane. These techniques have been evaluated on the basis of initial cost, maintenance, speed and accuracy of analysis, and applicable concentration range. The results of this study showed that the palladium-membrane technique is best suited for routine use. FOR some time investigators have been concerned with the origin, form, and effect of hydrogen in steel. In such stdies', the analysis for hydrogen constitutes one of the most important phases. It is quite apparent that the results for hydrogen concentrations in a given steel are dependent on the method of obtaining the sample, storage of the sample until analysis, preparation of the sample, and analysis of the sample, including all the facets inherent in the calibration and operation of an apparatus for gas analysis. There are a number of means available for determining hydrogen. This is a critical study of some of the more common techniques in use today. In most conventional melting and casting methods, hydrogen concentrations of 4 to 6 parts per million (ppm) in steel are quite common. Because of the undesirable effects of hydrogen on steel there has been increased use of techniques such as vacuum melting,' vacuum casting, and ladle-to-ladle stream degassing, which lower the hydrogen content to levels on the order of 1 to 2 ppm. Therefore, the method used for determining hydrogen in steel must be sensitive and precise. In any analytical procedure for gases in metals there are two distinct operations—the extraction of the gas from the metal and the analysis of the extracted gas. To extract the gas from the steel, three methods have been employed: 1) fusion of the sample with graphite at high temperature; 2) fusion with a flux, such as tin, at a lower temperature; and 3) extraction of the hydrogen from the solid sample at a temperature below the melting point of the steel. Fusion with graphite is the least-acceptable method. The blank in this method is higher and more variable than in either of the other two methods. The hydrogen fraction of the total gas composition usually is between 10 and 50 pct; thus, a larger analytical error is possible. The vacuum-tin fusion4 extraction of hydrogen is probably the most rapid method in use today; the extraction time is usually about 10 min. However, with this system a bake-out of the freshly charged tin for 2 hr is necessary and a change of crucible and a charge of fresh tin are required after each day of operation whether one or thirty samples have been analyzed. In addition, frequent checks of blank rates are required since CO and Na are continually being given up by the steel samples dissolved in the tin bath. The composition of the gas in this method lends itself readily to analysis; although the hydroge concentration may fall to as low as 50 pct, more often it is above 90 pct, thus allowing a more precise analysis (because of less interference from other gases). In 1940 ewell' published the hot-extraction method for extracting hydrogen from the solid sample, comparing analysis for hydrogen extracted at 600°C with similar analysis for the gas extracted at 1700°C by fusion with graphite. Good agreement for hydrogen was obtained between these two methods, provided sufficient time was allowed for extraction at the lower temperature. carsone obtained good results in his comparison of this hot-extraction method with vacuum-tin fusion. Subsequent work by Geller and sun7 and Hill and ohnson' has shown that steel samples should be heated to at least 800°C to effect the release not only of the diffusible hydrogen but also of the "residual" hydrogen that may be present as methane. Since the rate of evolution of hydrogene9l0 depends on such factors as sample size and composition, thermal history, and extent of cold work, a fixed extraction time is not possible. Extraction times of 30 min are normal, but 2 hr are not unusual. Induction or resistance heating may be used in the hot-extraction method. With resistance heating the

Jan 1, 1964

By T. A. Read, M. S. Wechsler, D. S. Lieberman

A theoretical analysis of the austenite-martensite transformation is presented which predicts the habit plane, orientation relationships, and macroscopic distortions from a knowledge only of the crystal structures of the initial and final phases. THIS paper presents a new theory of the formation of martensite. This theory makes possible the calculation of the austenite planes on which the martensite plates form, the orientation relationship between the austenite and martensite crystal axes, and the macroscopic distortions which are observed. The only input data needed are the crystal structures and lattice parameters of the austenite and martensite. Considerable effort has been devoted over the past thirty years to the development of an understanding of the crystallographic features of martensite reactions. Much of this work has been done on steels and iron-nickel alloys, for which a great deal of data has been accumulated concerning the shape and orientation of the martensite plates, the relative orientations of the austenite and martensite crystal axes, and the observable distortions which result from transformation. These observations are reviewed in refs. 1, 2, and 3. The first major step toward an understanding of these phenomena was made in 1924 by Bain,' who showed that the a body-centered cubic structure can be produced from the 7 face-centered cubic structure by a contraction of about 17 pct in the direction of one of the austenite cube axes and an expansion of 12 pct in all directions perpendicular to it. Since that time, most of the efforts at further interpretation have been made by investigators who have worked from the phenomenological data, incorporating some of the information from the lattice properties, and have sought an analysis into likely deformations which would produce the observed results."- "11 but the three most recent papers on the subject have already been reviewed in some detail." Machlin and Cohenl0 measured the components of the distortion matrix and verified that the habit plane is a plane of zero distortion and rotation for the (259) case. They showed that the measured distortion matrix, when applied to the parent lattice, does not yield the product lattice and hence some inhomogeneous distortion must occur. Frank,u working from the lattice properties and taking some clues from the observations, considered the correspondence of close-packed rows and planes in the austenite and martensite. He predicted substantially the observed lattice relationship and habit plane for certain steels which have a (225) habit. Geisler12 suggested that there is a natural tendency for the habit plane to be a (111) and postulated certain slip processes to account for the fact that the experimentally observed habit plane is irrational and deviates from the assumed one. The present work differs from previous treatments of martensite formation in that it permits calculation of all the major manifestations of the process. Habit plane indices, orientation relationships, and observable distortions are all calculated from a knowledge of the crystal structures of the initial and final phases alone. The calculations contain no adjustable parameters. The agreement found between calculated results and the observations reported in the literature constitutes powerful evidence in favor of the mechanism of martensite formation proposed. The theory is applicable to systems other than steel (as is discussed later in this paper) which exhibit a diffusionless phase change but because of the wide-spread interest in the austenite-martensite transformation, particular attention will be given to the iron-base alloys. For other systems which undergo a similar face-centered cubic to face-centered tetragonal transformation, the mathematical treatment is identical with that presented here. Hence the theory successfully describes the transformation in the indium-thallium alloy.'" Homogeneous Transformation to Martensite The distortion which any homogeneously transforming volume of austenite undergoes in order to become martensite is shown in Fig. 1, as was first suggested by Bain.' (This distortion will hereafter be referred to as the "Bain distortion.") This specification of a contraction along one cube axis ;ombined with an expansion in all directions perpendicular to this axis describes what is properly called the "pure" distortion associated with this transformation. The distinction between a "pure" and an "impure" distortion plays an important part in the discussion which follows. A "pure" distortion is characterized by the existence of at least one set of orthogonal axes fixed in the body which are not rotated by the distortion. (These are called the "principal axes" of the distortion.) No such set of axes exists in the case of an "impure" distortion. On the other hand, an impure distortion can always be represented as the result of a pure distortion combined with the rotation of the specimen as a rigid body. For a given impure distortion the corresponding pure distortion

Jan 1, 1954

By C. N. Garman

Homestake-New Mexico Partners operate a 750-tpd carbonate leach uranium concentrate mill near Grants, N.M. The highly mineralized water available as process water leaves much to be desired. The 628 ppm as CaCO 3 makes the use of raw water very troublesome in pipes and on filter cloths. However, the residual sodium carbonate in the final filter cake going to tails makes an ideal softening agent. To take advantage of this fact, all makeup water used in the mill is first used as tailing slurry dilution water and comes to the mill from the tailings pond. The 5-acre tailings pond serves as a thickener and 100 to 150 gpm of nearly clear solution is decanted to a pump to be returned to the mill. Since this tailings water has small quantities of uranium in the solution an ion exchange scavenger unit was installed to remove as much uranium as possible. The ion exchange raffinate is then used as final filter wash ahead of the tailings slurrying step. In spite of the large settling area this return water is not clean enough for ion exchange feed. The solids present are very fine and composed of approximately 15 pct (by weight) burnable carbonaceous material common to the sandstone uranium ores in the area, 40 pct SiOz plus 45 pct CaC03. Laboratory work showed that this material responds very well to flotation. Before deciding to use flotation, various clarifying systems such as pressure leaf filters, sand filters, and continuous vacuum pre-coat filters, were considered. Each of these could have solved the problem but with much more operating labor, more reagents and greater installation costs than the flotation step. About 100 to 150 gpm of fouled water is fed to two 66-in. Fagergren cells, in series. Reagents used at the beginning were Arquad 2HT75 and Arquad C50, at the rate of about 1% lb per 8-hr shift, or about 0.0053 lb each per ton of ore. This did not completely remove the solids but does an acceptable job. Approximately 75 pct of the slimes are a size that can be caught on a 41-Whatman Paper are removed. Removal of these slimes also allows much better settling of the coarse nonfloatable material. Advantage is also taken of this fact in a small settling tank ahead of precipitation. Removal of this amount of the slimes makes the ion t:xchange feasible. PREGNANT SOLUTION CIRCUIT The carbonate? leach-caustic precipitation method of uranium concertration does not provide for any process purification step ahead of precipitation. Therefore, any fine solids getting into the pregnant solution through the filter cloth show up in the final concentrate. This, of course, lowers the grade, and, at times, the slimy nature of these very fine solids rendered final filtration of the concentrate difficult if not impossible At Homestake-New Mexico Partners a 75-ft thickener was available for gravity clarification of 100 to 120 gpm of this pregnant solution. However this did not sufficiently remove the slimes. Laboratory investigation of the whole range of flocculants that were suggested by literature, salesmen, and friends failed to turn up anything of consequence. A continuous vacuum pre-coat filter would do the job and was investigated. The capital cost and the operating labor and materials made this a last chance choice. Following work done in the metallurgical laboratory on the tailings return water, it was found that some changes in the reagent strengths and combinations made a very definite decrease in the solids in the pregnant solution. Concentrate grade improved about 5 pct anti the final product after drying had an appreciably greater bulk density. Compared to a cost of about 2.2e per ton for pre-coat filter opelation for cleaning just one circuit, flotation costs less than 1.0 per ton of ore for cleaning two circuits. While a pre-coat filter would do a more thorough job, the flotation does all that is required for either circuit. Gravity causes the froth produced to run back into the leach circuit. This does not appear to result in a build-up of objectionable slime. No extra manpower is required; the operators in the separate areas can observe the operation of the cells and mix the small quantities of reagents as needed. Normally the 66-in. Fagergren cell requires 15 hp per cell, but this very dilute slurry needs only 10 hp for both cells. Originally, a combination of the two Arquads mentioned previously served as frothers and promoters. As further testing

Jan 1, 1962

By L. L. Swift

AT the present time there are four base metals being used for automo-tive bearing alloys. Of course there are numerous variations in the amounts of alloying elements added to each base metal and nearly all of these alloys have the conventional, if not classical duplex structure; that is, they are composed of a hard constituent embedded in a soft matrix. The well-known theory is that the former will wear well, while the latter will be plastic enough to allow the bearing to be broken in and conform to the contours of the shaft. The requirements of the modern bearing have been most aptly described by W. M. Corse: In order to meet the engineering demands of today a good bearing metal must be able to carry the weight of the shaft and stand up under steady or suddenly applied loads, or even blows in some types of service. A certain amount of plasticity is desired to compensate for minute irregularities in the shaft or bearing surface, and to permit yielding, thereby avoiding dangerous stresses in bearing and shaft and pre-venting overheating and rapid wear of parts. Less plasticity is required in a bearing metal if the surfaces of bearings and journals are machined accurately, aligned, and kept in alignment. It is desirable, of course, that a bearing metal have a low coeffi-cient of friction. Under most operating conditions the friction depends on the unit pressure of the bearing, the speed, the temperature, and the properties of the lubricant. A good bearing metal must have a low rate of wear to reduce the necessity for frequent replacements, and adjustment of the bearings. It must wear more rapidly, however, than the journal or shaft running on it, because replacement of the journal or shaft is more difficult and costly than replacement of the bearing.1 The hardness of the bearing alloy is a property closely related to several of the foregoing. With a duplex microstructure, the measure-ment of hardness with any of the usual commercial devices means little. The Bierbaum method of measuring the hardness of the individual constituents was developed to fill this need.

Jan 1, 1938

By C. O. Worden, C. A. Zapffe, F. K. Landgraf

SUMMARY FOLLOWING the discovery of Parke and Ham that deoxidation control of cast molybdenum can be predicated upon simple fractographic examination, a special study of that metal was undertaken to investigate those patterns ascribed to forgeability and nonforgeability. An elaborately developed system of cleavage patterns immediately rewarded the study; and they are reported here as a necessarily preliminary contribution calling attention to information which is both new in type and in origin. In general, the present observations confirm those of Parke and Ham, and Woodside; but they also disclose a wealth of detail and correlated phenomena which greatly expand the earlier information. For example, the oxide pattern of nonforgeability is found to be complex, perhaps involving as many as three distinctive patterns. And the nature of the carbide seems to be at least twofold. In addition, transgranular facets are here shown for the first time. Elaborately complex, but in a characteristic manner, these facets depict distortion in original crystal growth which provides truly extraordinary patterns. No carbide and oxide forms display themselves transgranularly, except in profile as exceedingly thin superficial films at the grain boundaries. Crystallographic features are also rare-a condition undoubtedly resulting from the great substructural distortion; but occasionally registrations are found of cleavage on {001}, and faulted areas believed to be Neumann-type deformation on {112}. INTRODUCTION Parke and Ham, 1 and again Woodside, 2 have reported that the forgeability of molybdenum cast by their vacuum-electric-arc process can be predicted with great dependability by a simple fractographic observation. They state that nonforgeability is the result of a grain boundary oxide which can be readily identified on the fracture facet at high magnification; and they convert the nonforgeable condition to a forgeable one by increasing the carbon content of the melt until the oxide structures subsequently observed in the fractograph become replaced by a second strongly marked pattern characteristic of carbide and coincidentally indicative of forgeability. Considerable importance immediately attaches to such observations: (I) because of their direct commercial application to one of metallurgy's inviting and relatively unexplored metals; (2) because of a general scientific curiosity regarding the nature of these characteristic markings; and (3) perhaps more important, because of

Jan 1, 1948

By W. A. Anderson

IN the pressure die-casting of zinc alloys it is customary to force the molten alloy under high pressure into a permanent steel die by means of a plunger moving in a bushing that has a clearance on the diameter of the order of 0.002 in. Successful operation of the plunger type of machine requires the presence in the zinc alloy of certain percentages of aluminum. Without these aluminum additions, the normal reaction of molten zinc on ferrous materials causes sticking of the plunger and a complete shutdown of the equipment. All of the zinc alloys used for pressure die-casting today contain approximately 4 per cent of aluminum, which is more than sufficient to make plunger operation feasible. The clearance between the plunger and its bushing is an important matter. As the space becomes larger, there is a loss in effective metal pressure. Ordinary gray cast iron served fairly well and is still used in some machines. However, the rate at which the plunger clearance increases with this material is considered by many to be far too great. There is, therefore, a serious interest in finding new materials more capable of retaining the desired clearance during long periods of use. Today many die casters are using special materials for plungers and bushings selected by the somewhat expensive and time-consuming test of actual experience. An analysis of the problem reveals two possible end points of plunger operation: (1) the building up of zinc-alloy plunger-material reaction products in sufficient bulk to cause sticking and (2) rapid solution, wear or erosion, all of which will increase the clearance to an undesirable extent. If neither of these takes place, the plunger will operate for a long time, of course. The authors have developed a laboratory apparatus in which the action of a plunger moving in a bushing immersed in molten zinc alloy could be simulated closely. Such a machine made possible a more rapid and less expensive survey of the available construction materials and an analysis of the specific alloying reactions taking place in the clear-ance area.

Jan 1, 1939

By Frederick Laist

About six years ago the Anaconda Copper Mining Co. decided to investigate the possibility of extracting zinc from the ores of certain mines in the Butte district. These ores are of a complex character and contain so much iron and lead that the concentrate contains only 33 to 35 per cent. zinc. Investigations showed that while a high-grade concentrate could not be obtained by ordinary methods, such as tabling and magnetic treatment, a fair grade could be made by the Horwood process. In this method, the concentrate resulting from the flotation of all of the sulfides is given a light roast and this calcine is subjected to flotation in the presence of a large amount of sulfuric acid; the resulting concentrate contains most of the zinc and a residue contains most of the iron. The fact that the lead, copper, and silver are divided approximately equally between the zinc concentrate and the iron residue and the large consumption of acid, which ranged from 50 to 100 lb. (22 to 45 kg.) per ton of concentrates, were serious objections to this plan. The zinc recovery, moreover, was low, as a considerable percentage invariably accompanied the iron. While a profit might be made on the ores by the use of this process, it was thought that other and more promising methods might be devised. After carefully studying the field and doing some laboratory work on various processes that had been suggested, it was decided that the electrolysis of sulfate solutions was the most promising. We soon found, as have other investigators, that the only way to obtain a good zinc deposit is to have the electrolyte free from all metals more electronegative than zinc, such as copper, cadmium, lead, arsenic, antimony, etc. Arsenic and antimony are particularly injurious, causing very poor current efficiency and small yield per horsepower when present in amounts so small as almost to defy detection—1 mg. or less per liter. A pure zinc is soluble only with difficulty in sulfuric acid; an impure zinc dissolves very readily. Electrolytic zinc deposited from pure solutions is, of course, extremely pure and dissolves only about one-fiftieth

Jan 1, 1921

By A. H. Geisler, R. F. Mehl, S. Barrett

The studies of the mechanism of pre= cipitation and of the resulting property changes in aluminum-silver alloysl-3 have presented some new concepts of the aging reactioxl—concepts that may be fundamental in establishing a complete quantitative theory of age-hardening. With both aluminum-copper and aluminum-silver alloys, thin platelike aggregates form parallel to the Widmanstätten planes of precipitation.l,4 These platelets grow in lateral dimensions and in thickness with aging time until they arc thick enough to produce an X-ray diffraction line pattern. Their structure is that of a transition lattice which is coherent with the matrix, since the atomic spacings in the matrix and the precipitate are the same on each side of their common interface.2,4 The equilibrium precipitate forms later from and at the expense of the transition lattice. Since age-hardening occurs during the formation and growth of the transition lattice, the major contributor to the hardening no doubt is the stress condition in the matrix resulting from the matrix holding the precipitate in the coherent condition. The development of these stresses also appears to be responsible for an increase in the electrical resistance superimposed on the normal decrease resulting from a change in the concentration of the matrix during aging.3 The two consecutive reactions constituting the aging process are accompanied by characteristic microstructural alterations. The initial precipitation process results in the formation of a Widmanstatten figure, while the later transformation of the transition lattice to the equilibrium lattice is accompanied by a coalescence, in the case of aluminum-copper alloys,5 and by the appearance of light areas at the grain boundaries with aluminum-silver alloys showing a structural rearrangement of matrix and precipitate.3 This latter reaction is similar microscopically to the so-called "discontinuoils precipitation." Possibly discontinuous precipitation is a process that often if not always follows true precipitation of a coherent lattice and during which the transformation of the coherent transition lattice to the equilibrium lattice takes place accompanied by matrix recrystallization.3 Expermental Procedure The alloys were made using 99.97 per cent A1 or distilled magnesium, with

Jan 1, 1943

By R. F. Mehl, A. H. Geisler, S. Barrett

The studies of the mechanism of pre= cipitation and of the resulting property changes in aluminum-silver alloysl-3 have presented some new concepts of the aging reactioxl—concepts that may be fundamental in establishing a complete quantitative theory of age-hardening. With both aluminum-copper and aluminum-silver alloys, thin platelike aggregates form parallel to the Widmanstätten planes of precipitation.l,4 These platelets grow in lateral dimensions and in thickness with aging time until they arc thick enough to produce an X-ray diffraction line pattern. Their structure is that of a transition lattice which is coherent with the matrix, since the atomic spacings in the matrix and the precipitate are the same on each side of their common interface.2,4 The equilibrium precipitate forms later from and at the expense of the transition lattice. Since age-hardening occurs during the formation and growth of the transition lattice, the major contributor to the hardening no doubt is the stress condition in the matrix resulting from the matrix holding the precipitate in the coherent condition. The development of these stresses also appears to be responsible for an increase in the electrical resistance superimposed on the normal decrease resulting from a change in the concentration of the matrix during aging.3 The two consecutive reactions constituting the aging process are accompanied by characteristic microstructural alterations. The initial precipitation process results in the formation of a Widmanstatten figure, while the later transformation of the transition lattice to the equilibrium lattice is accompanied by a coalescence, in the case of aluminum-copper alloys,5 and by the appearance of light areas at the grain boundaries with aluminum-silver alloys showing a structural rearrangement of matrix and precipitate.3 This latter reaction is similar microscopically to the so-called "discontinuoils precipitation." Possibly discontinuous precipitation is a process that often if not always follows true precipitation of a coherent lattice and during which the transformation of the coherent transition lattice to the equilibrium lattice takes place accompanied by matrix recrystallization.3 Expermental Procedure The alloys were made using 99.97 per cent A1 or distilled magnesium, with

Jan 1, 1943

By R. M. Brick

THE Institute of Metals Division Lecture in 1936, given by R. F. Mehl, on diffusion in solid metals1, was introduced with the statement that "the phenomena of diffusion are intimately related to many basic prob-lems of the metallic state, but in addition to this the process of diffusion is of first importance practically." In view of the scope of that lecture, it does not seem necessary to review the importance, history or present status of diffusion problems. One aspect of the subject of diffusion that has received little attention became of some immediate importance in the course of a study on segrega-tion. When a solid solution alloy freezes, the familiar mechanism of solidification requires that the first nuclei formed be low in solute con-centration, with a resultant normal segregation or coring effect during freezing. Theoretically, diffusion of solute atoms during solidification should result in a homogeneous solid solution. Actually, of course, it is impossible in most binary alloys to obtain a cooling rate that will permit diffusion to eliminate coring in the freezing dendrites. For a given alloy, the extent of diffusion attained up to the point of final solidification will determine the degree of enrichment in solute atoms of the final liquid phase. The flow of this liquid into dendritic contraction channels and the solute concentration of the liquid seem to be the determining factors as to whether the final gross segregation is normal, inverse or absent. The purpose of the present study of diffusion was to determine to some extent the separate diffusion rates of copper and magnesium into pure aluminum with a view to clarifying previous results on segregation in these alloys; i.e., the fact that under similar freezing conditions alumimum-copper alloys segregate inversely and aluminum-magnesium alloys segre-gate normally. Of concomitant interest were the questions of the homogenization times required for segregated ingots or partially melted, i.e., "burnt," structures, and the solution heat-treatment times required for cast, hardenable aluminum-copper and aluminum-magnesium alloys, for worked and annealed structures, and so forth.

Jan 1, 1937

By Oscar Glaeser

THE mine and plant of the United Verde Copper Co., located in Yavapi County, at Jerome, Arizona, have been described in various technical publications and, therefore, a brief outline of its essential features will suffice. The orebodies are of the schist replacement type, the main sulfide mass being a large lens-shaped body approximately 7 acres in cross-sectional area. In general, the mineralization is found along the iron-schist contact, with the orebodies extending-about 1000 ft. along this contact and varying from a few feet to 250 ft. in width. The mine is located on a mountain slope and has openings into it on three horizons, as follows: 1. Raises and ore passes open vertically into the shovel pit. These extend down to the 1000-ft. level, where they terminate as loading bins in the Hopewell adit. The main fan intake air shaft, which also extends vertically down to the 1000-ft. level, has its surface opening on the hillside at the extreme north end of the shovel pit, and the main mine air return exhausts through a raise at the extreme south end of the shovel pit. 2. The 500-ft. level adit. 3. The Hopewell adit on the 1000-ft. level. The mine has a vertical downward extent of 2000 ft. below the 1000-ft. level. Underground operations are carried on through two main shafts, both of which are wholly underground. Shaft 5 is the ore-hoisting shaft. It has three compartments and extends from the 800 to the 3150-ft. level. Shaft 6 is the service shaft, and is used for lowering and hoisting men and material. It has a large cage compartment and three smaller compartments for counterweights, ladderway, and pipe and power lines. This shaft extends from the 500 to the 2550-ft. level, and is now being extended to the 3000-ft. level. An air shaft for the downward movement of fresh air from the fan has been provided, and extends to the 2550-ft. level at this time. Work has been started to extend this air shaft to the 3000-ft. level. A return airway for vitiated mine air, in the form of raises and short connecting drifts, extends downward to the 2100-ft. level.

Jan 1, 1929

By W. E. D. Stokes

The application of aviation to mining and petroleum operations, on the basis of economy and attainment, has become a demonstrated fact. According to Dominion Government rccords, 30 Canadian companies engaged in air transportation with northland mining camps, carried 13,000 tons of freight in 1935, and in 1936 carried 16,000 tons. In addition, many mining companies used planes to transport prospectors with canoes, outboard motors, gasoline drums and supplies to remote locations, and one company maintained a plane to take radium-bearing ore from its mine on Great Bear Lake nearly 1000 miles south to the railway at Waterways, Alberta. Heavy pieces of mining machinery weighing 2 tons are being carried by Ford trimotor planes over the Andes, at an altitude of not less than 15,000 feet. At Bulolo, New Guinea, 17,500 tons of disassembled gold-dredging equipment has been flown over inaccessible terrain, while supplies and building materials for a community of 1000 whites have been transported by airplane. A 31/2-ton shaft was carried on one notable trip, while at another time an automobile, 2 tons of rice and a large safe went over the mountains in one plane. Fig. 1 shows an electric generator that was carried by plane to Bulolo. Many large American oil companies operated fleets of planes during 1936, ranging from fast, luxurious air liners for executives to elaborate geological prospecting units, ambulance planes, freight carriers and pipe-line repair crews. According to the U. S. Geological Survey, commercial firms photographed 16,291 square miles during 1935, while the Government compiled from aerial photographs by the Geological Survey in the United States 85,544 square miles. It was found that information could be determined in a fraction of the time required by surface methods. However, sounding a word of caution, a Commonwealth of Australia government report on aerial survey operations had this to say: It is necessary to repeat ad nauseam that aerial photographic survey is in no sense a substitute for geological investigation, though it is a very valuable adjunct thereto, and greatly facilitates and aceeleratcs geological mapping. There are many details

Jan 1, 1937

By Clarence A. Seyler

The technical difficulties of cutting thin sections of coal for examination by transmitted light have hitherto restricted the investigation of the important subject of the microstructure of coal to the few possessed of the requisite skill and time. Apart from this, the method fails with anthracites and other coals rich in carbon, owing to the opacity of the material. Occasional use of the method of polishing a surface, with or without etching, has been made, but it was not until Winter' published an account of his results that attention was seriously directed to the method. In May, 1923, a specimen of dull anthracite came into my hands; I tried Winter's method on it and the presence of megaspores and other vegetable structures became clearly visible. A preliminary notice was published by me;2 but I soon abandoned the use of Schulze's solution, having found that a mixture of chromic and sulfuric acids gave far better results. In the meantime Turner and Randall, in America, had independently developed the method of flame etching, as applied to anthracite, with great success. I have spent a year studying the method of chromic etching, which gives excellent results with bituminous coals and camels, as well as with anthracite. For anthracites, I have used the chromic method and Turner's method of flame etching, whichever was the more convenient or as a check one on the other. The polishing is done, according to metallurgical practice, by the use of a polishing machine and successively finer emery paper, followed by polishing on cloth moistened with a suspension of levigated green oxide of chromium, and a final rubbing on "selvyt" (a cotton velvet polishing cloth) moistened with alcohol. The polished sample is examined by reflected light with a 2/3 and 1/6 in. objective. Bituminous coals usually show considerable structure, and even anthracites show it faintly in places. The sample is then etched by immersion in a boiling solution made by adding 10 c.c. of concentrated sulfuric acid to 30 C.C. of a saturated solution of chromic acid; enough water is then added to dissolve

Jan 1, 1925