By A. J. Griest, A. P. Young, P. D. Frost

A study was made of the effect of ß grain size on the tensile ductility of a-ß titanium alloys haet treated to strengths in the range 165,000 to 180,000 psi. It was concluded that the primary cause of $ embrittlement is the large grain size which is obtained so rapidly in many a-ß titanium alloys when heated into the ß field. It was also found that grain-boundary a and acicular intragranular a in the microstructure are not necessarily detrimental to the tensile ductility if the prior ß grain size is sufficientlv fine. BETA embrittlement occurs in a-ß alloys when the finish hot-working or stages of the subsequent heat treatment have been done at temperatures in the ß field. In order to avoid this embrittlement, for-gings must be finished at temperatures under the ß transus. For better workability, it would be desirable to forge at temperatures in the ß field. For this reason, research has been conducted to determine the cause of ß embrittlement. Although ß grain size has been considered as a possible contributing factor to ß embrittlement, only limited research has been done to evaluate its effect. The effect of addition elements on ß grain growth in unalloyed titanium has been studied by Liu.' Complete mechanical property data, however, were not obtained for correlation with grain size. Ogden and coworkers2 have investigated the effect of both a and ß grain size and grain shape in Ti-Cr-Mo alloys. Their data indicated that tensile ductility was relatively insensitive to ß grain size at annealed strength levels (140,000 psi ultimate). No study has apparently been made to determine the relationship between ß grain size and ß embrittlement in a-ß alloys heat treated to high strength (180,000 psi ultimate). The high-strength condition is that in which ß embrittlement is particularly severe. Beta grain size is not easily varied through the use of a range of annealing times and temperatures in the ß field, because of the rapidity with which ß grain growth occurs. Short-time heating techniques are needed to obtain the smallest ß grains. EXPERIMENTAL PROCEDURE In this research, the experimental procedure was as follows: 1) Tensile and microimpact specimen blanks were resistance heated to produce a range of ß grain sizes. 2) The tensile and microimpact blanks were then solution-treated in the a-ß field and aged to produce predetermined ultimate tensile strengths in the range 165,000 to 180,000 psi. Tensile and impact ductility were then correlated with a grain size for constant strength levels. Materials—The alloys Ti-6A1-4V, Ti-4A1-4Mn, and Ti-16V-2.5Al are representative of the heat-treatable a-ß types in which ß embrittlement can be severe. The compositions and ß transi of the heats studied are given in Table I. The Ti-16V-2.5Al heat was melted and fabricated to 1/4 in. round at Battelle; the other alloys were obtained as 1/4 in. round rolled from commercial heats. The micro-structures of the as-rolled alloys were fine a-ß mixtures. This structure is typical of titanium alloys hot-worked extensively in the a-ß field. Resistance-Heating Treatments to Establish ß Grain Size—For direit resistance heating, a 1/4-in.-diam s~ecimen was heated with a 3000-watt transformer rated for 1000 amp with adjustable secondary voltage. The apparatus included a spray quench fixture. Both heating and quenching periods could be automatically controlled. For temperature measurements, 28-gage Chromel-Alumel wires were tack-welded to the specimen at its midpoint. A high-speed recorder-controller was used to control the heating cycle.

Jan 1, 1960

By W. Mitchell, B. H. Bergstorm, C. L. Sollenberger

A unique compression testing machine was constructed to load individual 1/8 to I-in. spheres of glass, etc., at rates from 100 to 100,000 lb per min. During loading the applied load was continuously plotted us the deformation of the sphere-platen system. The load-deformation curve conforms to the theory of elasticity. The spheres were surrounded by steel retaining rings or by gelatin (to prevent secondary fracture). The product size modulus was determined from screen analyses. The data shows: 1) Energy input per unit mass is inversely proportional to the product size modulus (or directly proportional to the surface area per unit mass). 2) Increased loading rates slightly increase the energy input per unit mass required for fracture without affecting the preceding relationship. Theory and experiments show that much of the input strain energy is transformed into kinetic energy of fragments at fracture, this being a reason efficiencies based on "surface energies" are exceedingly small. This large kinetic energy component is usually dissipated as heat but may be partially reclaimed because impact of fragments against the surface of steel retaining rings causes additional comminution. There are currently several theories of crushing, all of which can be derived from the general energy equation of Gillilandl as was pointed out by Mitchellet al in 1954'and more recently by Rose and Sullivan. If the exponent of the equation dE-x-"dx is assigned values of 2,1, or 3/2, one obtains by intergration between suitable limits, the equations of Rittinger, kick,' and Bond,' respectively. Other investigators prefer to let the exponent be a variable parameter. To help resolve the controversy, the Allis-Chal-mers Research Laboratories set up a series of carefully controlled experiments in which the level of energy input required to induce the comminution of a single particle by slow compression loading was very accurately measured. The energy input requirement, in conjunction with the size analysis of the fragments produced at fracture, yielded an accurate energy-product size relationship for the conditions studied. APPARATUS The experimental apparatus was designed to apply a compressive load on opposite sides of an "ideal particle." Spherical shapes were chosen, because point contact loading is typical of the mechanics of conventional crushers. The bulk of the experimental data was obtained with glass spheres because glass is a fairly homogeneous, brittle material for which the properties follow definite statistical distributions. The spheres ranged from 1/8 to 1-in. diam. The compressive load was applied to the specimen at a uniform rate by a loading mechanism (Fig. 1) which acted through a system of levers. The uniform rates, ranging from 100 to 100,000 lb per min, were obtained by metering water into a bucket suspended at the end of the secondary level. Point contact was made with the sphere through tungsten-carbide platens. This latter material is extremely hard and has a high modulus of elasticity, thereby having a minimum of distortion when loaded. The actual load on the sphere was measured independently of the lever system by a load cell, Fig. 2, which was designed so that the voltage output of the load cell would be proportional to load. The deformation of the specimen was indirectly measured by a pair of transformers which were attached to opposite edges of the upper platen. The cores of the transformers, which were attached to the lower platen, moved relative to the transformer so that the voltage output was proportional to the deformation of the sphere-platen system. The load was plotted against the deformation on an X-Y recorder. The area under the curve, as shown on Fig. 3, was proportional to the energy input of the

Jan 1, 1961

By D. P. Pope, T. Vreeland

Observations of dislocations in zinc using Berg-Barrett X-ray micrography confirm the validity of a dislocation etch for (1010) surfaces. A technique for measurement of the depth in which dislocations can be imaged in X-ray micrographs is given. This depth on (0001) surfaces of zinc was found to be 2.5 µ using a (1013) reflection and CoKa radiation. BUCHANAN and Reed-Hill (B & RH) have recently questioned the ability of a dislocation etch to reveal all of the basal dislocations which intersect (1010) surfaces in annealed zinc crystals.' This etch was developed by Brandt, Adams, and Vreeland who conducted a number of different experiments to check its ability to reveal dislocations.2,3 B & RH prepared (0001) foil specimens for transmission electron microscopy from annealed crystals and observed dislocation densities of about l08 cm per cu cm in the foils, while the etch indicated densities of the order of l04 cm per cu cm in their annealed crystals. As this etch has been used in a number of studies of dislocations in zinc, it is of considerable importance to reassess its validity in the light of the B & RH results. The X-ray work reported here was undertaken to check the ability of the etch to reveal dislocation intersections on (1070) surfaces of zinc. The X-ray technique was chosen for this check because it could be applied to the as-grown crystals with a relatively small amount of specimen preparation. We believe that the possibility of accidental deformation in preparation of the bulk specimens is considerably less than that for thin foil specimens suitable for transmission electron microscopy. Unfortunately, basal dislocations are not visible on Berg-Barrett topo-graphs of (1010) surfaces, which are the surfaces on which the etch is most effective. Therefore, a one-to-one correspondence between the etch and X-ray observations could not be made. Basal dislocations near (0001) surfaces have been observed by Schultz and Armstrong4 using the Berg-Barrett technique, but they did not report the as-grown dislocation density observed in their crystals. We have applied the X-ray technique in this study to surfaces oriented from 1 to 2 deg of the (0001) to determine the basal dislocation density, and have compared this density with that observed using the etch on a (1070) plane of the same crystal. The X-ray observations permit determination of the depth in which basal dislocations can be observed under the diffracting conditions used. SPECIMEN PREPARATION High purity zinc crystals are very soft, so a good deal of care must be exercised in the preparation of observation surfaces. As-grown crystals approximately 2.5 cm in diam and 20 cm long were acid cut into 1.25 cm cubes. A thin slab was cleaved from an (0001) surface to produce an accurately oriented reference surface on the specimen. Some of the cubes were examined in the as-machined condition while some were annealed in argon at 410°C for 2 hr. Heating and cooling rates were less than 2°C per min. Some of the specimens were scratched on a (0001) surface with a razor blade to produce fresh dislocations. Approximately 2 mm of material was acid lapped from one face of a cube to produce a surface oriented between 1 and 2 deg from the basal plane and parallel to the [1210] direction. A (1070) surface was also acid lapped. The lap used a 1 to 3 pct solution of HN03 in water to saturate a soft cloth which was backed by a stainless steel plate. The cloth was moved over the crystal surface at a rate of 20 cm per sec while a normal force of about 4 g was maintained between the cloth and the specimen. As-lapped surfaces were examined as were surfaces which were chemically and electrolytically polished after lapping. The small angle between a lapped surface and the (0001) plane was measured to 0.1 deg using a Unitron microgoniometer microscope (the cleaved surface was used as a reference in this measurement). The microscope was modified so that the intensity of reflected light could be continuously monitored on a meter. This modification produced nearly a ten-fold increase in the reproduceability of orientation readings. OBSERVATIONS The Unitron Microgoniometer observations indicated that the lapped surfaces had a terraced structure with the terraces quite rounded and spaced about 0.1 mm in the [1010] direction. The maximum change in slope between terraces was 0.25 deg, indicating a terrace height of about 0.1 µ. A Unitron measurement of the average angle between (0001) and a lapped surface was checked by micrometer measurement of the specimen and found to agree within 0.1 deg. The Berg-Barrett micrographs using (1013) reflections and CoKa radiation5 revealed subboundaries, short dislocation segments, spirals, and loops near the surfaces which were oriented from 1 to 2 deg of the (0001). Micrographs of surfaces prepared by lapping appeared very similar to those of the chemically and electrolytically polished surfaces. The loops and spirals were not extinct in (1013) or (0002) reflections, indicating that they have a nonbasal Burgers vector. Extinctions of the short, straight dislocations indicated that they belonged to an (0001)(1210) system. Fig. 1 is an example of a micrograph which shows a subboundary, and dislocation segments which are pre-

Jan 1, 1970

By A. E. Dwight

Lattice parameters were determined for eighteen equiatornic alloys of the CsCl-type structure, ten of which were previously un-reported. It was found that fomation of the CsCl-type structure in binary alloys of the transition elements is largely dependent on position of the elements in the periodic table. The relative size of the two elements was not found to be a controlling factor. A recent paper by Beck, Darby, and Arora1 corre-lates the occurrence of CsC1-type ordered structures with the position of the constituent elements in the periodic table for the first long period. It was also suggested that a definite increase in relative bond strength between unlike atoms occurred when, in binary alloys of iron-group elements, the other component is changed from a chromium-group element, to a vanadium-group element, to titanium. A later paper by Philip and Beck2 noted that the lattice contraction increased in the order CrFe, VFe, and TiFe. It was also noted by Philip and Beck2 that the lattice contractions of CsC1-type alloys decreased in the order: TiFe, TiCo, and TiNi, which is an apparent reversal of the contractions expected from the position in the periodic table. It was suggested that the increasing lattice contraction is an indication of increased stability, i.e., greater A-Bbond strength. The present investigation was carried out to determine whether the relation of the position in the periodic table to the formation of the CsC1-type structure was also correct for alloys involving the second and third long-period elements. A systematic search was made for CsC1-type structures among equiatomic alloys and for those found, the lattice contraction was determined. EXPERIMENTAL TECHNIQUE The elements Y, Gd, Ti, Zr, Hf, V, and Cb are designated the A group and the elements Mn, Re, Fe, Ru, Os, Co, Rh, Ir, Ni, Pd, Pt, Cu, Ag, and Au are designated the B group. Equiatomic alloys were prepared for 57 AB combinations. The alloys were arc melted in a multicrucible furnace3 in buttons ranging from 5 to 20 g. Chemical analyses were not made, as the charge weights agreed closely with those of the buttons after melting. The alloy buttons were homogenized at 800° to 900°C. Metal log raphic and X-ray specimens were prepared and heat treated at temperatures from 600° to 1200°C. Specimens for X-ray diffraction were usually ground to a powder in an agate mortar; however, needle-shaped solid specimens were used when the alloy was sufficiently ductile to permit their preparation. Diffraction patterns were taken with a Straumanistype Debye-Scherrer camera using filtered Cu or Co radiation. The lattice parameters were obtained in A by plotting the calculated a0 values against the cos29/sin 0 + cos2?/? function and extrapolating linearly to ?= 900. Metallographic control specimens were polished on cloth wheels with diamond paste and etched with various phosphoric and nitric acid reagents. RESULTS The eighteen equiatomic alloys listed in Table I gave evidence of a cubic structure with two atoms in the unit cell, although two of these cubic structures exist only at elevated temperatures and transform to a tetragonal structure on quenching. Nine of these eighteen alloys gave diffraction patterns with super-lattice lines showing that the structure is of the CsC1-type. The lack of superlattice lines in patterns of the other nine alloys may be attributed to the small difference in atomic scattering power of the components. Metallographic study indicates the occurrence of nine narrow single-phase fields at the AB composition. Any or all of these nine may also have a CsC1-type structure. The VFe alloy was found to have a CsCl-type structure by Philip and Beck2 through the use of CrKa radiation (for which the scattering factor of V is anomalously low), whereas the Cu radiation used

Jan 1, 1960

By Gen-ichi Nakazawa, Masamichi Fujimori, Ichiro Doi

INTRODUCTION The major products of nickel industry in Japan are the electrolytic nickel (E-Ni), the ferro-nickel (Fe-Ni) and the nickel oxide sinter (NOS), totaling in production to 90 - 100 X 103 tons/year in terms of pure nickel content, and sharing approximately 20% for E-Ni, 10% or less for NOS, and the rest for Fe-Ni. The raw materials to be used for these products depend totally upon the imports from abroad; matte, the raw material used in the production of E-Ni, is from Australia and Indonesia; matte for the NOS is from Indonesia and New Caledonia; and garnierite, the raw material for Fe-Ni, is imported in bulk from New Caledonia, Indonesia and the Philippines. This report describes the acquisition of these raw materials, the production processes, trend of supply-demand, problem areas and the measures taken, and so forth, in connection with the nickel industry in Japan. ELECTROLYTIC NICKEL 1. History The nickel industry in Japan began in 1939 by the Sumitomo Metal Mining Co., Ltd. (SMM) with 150 tons E-Ni/month under the blast furnace smelting and the metal anode electrolysis. This was temporarily suspended after the end of last World War II, but resumed in 1952 with garnierite of New Caledonia as a raw material. Since then, the production capacity has been expanded incidentally to the increase of demand. However, since the smelting of garnierite contained about 2% nickel was very costly, the smelting process had been changed to smelt the briquettes of the mixture of garnierite and nickel sulfide concentrate imported from Canada and Australia. In 1975, this smelter was closed, and SMM's nickel refinery used matte from Western Mining Corp. (WMC) of Australia as a raw material. The refining process had been the metal anode one. The crude nickel oxide derived from roasting the high grade nickel matte had been melted and reduced with coke in the electric furnace and cast into anode. In 1970, a new refinery was constructed to produce 1,000 tons Ni/month under the matte anode process, and further, in 1976, the old refinery was converted into the matte anode process, thus resulting in the total production capacity of 1,690 tons Ni/ month today under the matte anode process. Shimura Kako Co., Ltd. began in 1951 to produce a little of E-Ni, and in 1955, they constructed a shaft furnace smelter with New Caledonian garnierite as a raw material to begin the E-Ni production under the matte anode process. Its monthly production reached 400 tons in 1957, but it discontinued its smeltering in 1963 to convert to the matte import from S. Le Nickel, WMC and INCO. In 1979, it changed the source of matte supply from the above to Soroako of Indonesia, discontinued the E-Ni production in 1979, and arranged for a total toll contract with Sumitomo. Meanwhile, SMM has developed a very distingished process for nickel-cobalt separation and refining by a solvent extraction method from nickel and cobalt mixed sulfide generated as a by-product in the nickel recovering process from laterite under the Nicaro process. Nippon Mining Co., Ltd. (NMC) also developed its own process. The plants under these processes were constructed in 1975, with the monthly production capacity of 230 tons of nickel and 130 tons of cobalt by SMM, and 300 tons of nickel and 110 tons of cobalt by NMC. SMM imports the raw material from the Marinduque Mining and Industrial Corp. of the Philippines, while NMC from Queensland Nickel Pty. Ltd. of Australia. 2. Production Status 2.1 Producers and materials Today, SMM holds the monthly E-Ni production capacity of 1,920 tons, of which 1,690 tons are from the matte anode process, and the remaining 230 tons are from the mixed sulfide as a raw material. NMC also uses the mixed sulfide as a raw material for a production of 300 tons/month. [ ] Most of SMM's raw material, nickel matte, is imported from WMC of Australia, partly using the Soroako matte from Indonesia. An example of material analysis is given in Table 1. Matte is a raw material for E-Ni and NOS, and the major sources of matte supply at present are Australian WMC and Indonesian Soroako, occupying ap-

Jan 1, 1982

By G. T. Hahn, C. N. Reid, A. Gilbert

An evaluation is made of the possible cautsal relationship between twinning and fracture in molybdenum. For both single and poly crystalline material no instance of twin-induced fracture was observed. Instead brittle fracture was found to be slip-induced at heterogeneities. For single-crystal material, the yield stvess in compression and the fracture stvess in tensiow obey a similar angular- relationship which follows approximately a 1/cos2 ? law. where 0 is the angle between the specimen axis and the nearest (100) plane. This sittlilarity between yield and fracture behavior casts doubt on the interpretations made previoltsly that a 1/cos2? relationship supports a critical normal fracture stress criterion. SINCE fracture in brittle materials takes place at stresses an order of magnitude lower than the theoretical strength of the lattice, it must be postulated that some stress-concentrating effect is operative during the fracture-initiation process. Several mechanisms have been proposed whereby the necessary stress concentrations could be produced. The well-known Cottrell mechanism1 describes a dislocation interaction which can lead to the formation of an incipient cleavage crack on a cleavage plane, and both zener2 and stroh3 have discussed models which predict the stress concentration at the intersection of a slip band with a grain boundary. When twinning occurs twin/twin intersections and twin/grain boundary intersections represent another possible means of fracture initiation. Although still controversial, the concept of twin-induced fracture is supported by a weighty mass of evidence, which has been reviewed in a recent paper.4 This investigation was conducted in order to assess the extent to which the brittleness of molybdenum can be ascribed to this cause. Emphasis was placed on seeking direct metallographic evidence for twin-induced fracture such as arrangements of twins located at the fracture origin. EXPERIMENTAL PROGRAM Materials. The experimental materials are described inTable I. From the chemical analyses and estimates of the amounts of interstitials likely to be retained in solution,5 it is concluded that all were mul-tiphased systems. X-ray diffraction experiments6 showed no evidence of preferred orientation in the polycrystalline materials. Single crystals were grown from Molybdenum X and Y using the floating-zone technique,' in a vacuum of better than 3 x 10-5 Torr. However difficulties were experienced with Molybdenum X due to violent gas evolution from the molten zone, and additional crystals (Crystals 3 to 6) were produced by annealing for 5 1/2 hr at 2300°C under a vacuum of 10-4 Torr. Techniques. A series of tension, compression, and bend tests was conducted. Tension tests were used to demonstrate brittle behavior, to measure brittle-fracture stresses, and to provide fractured specimens for metallographic inspection. Compression tests were employed in order to obtain some ductility and a measure of the yield stress. Furthermore, it was considered that compression loading would permit the study of crack nucleation in the absence of propagation. The bend tests were conducted to facilitate identification of the fracture origin, which would be expected to be at, or near, the tensile surface of the sample. Tests were carried out at temperatures between 78" and 298°K attained by means of a liquid-nitrogen evaporator of modified Wessel design.' Specimens were fashioned by mechanical grinding, and, prior to heat treatment, were electropolished at 10 v in a 3:l mixture of ethyl alcohol and sulfuric acid, using a stainless-steel cathode. Except where noted, a strain rate of 4 pct per min was used. All specimens had a gage section 0.75 in. long; diameters of 0.10 and 0.20 in. were adopted for the tension and compression specimens, respectively, the former of single shoulder design, the ends being gripped in split collets with a conical bearing surface. In the bend test, electropolished specimens measuring 0.080 by 0.25 by 1.25 in. were deformed at 78°K by four-point loading. The bending device had spans of 1 in. between the outer and 4 in between the inner fulcra; it was stressed between the compression anvils of the Instron machine at a constant deflection rate. EXPERIMENTAL RESULTS Polycrystals. Tension and Compression Tcsls. It is apparent from Fig. 1(a) that above 170°K fracture of Molybdenum X takes place at stresses equal to or greater than the compressive yield stress whereas

Jan 1, 1967

By H. E. Cline, E. F. Koch, J. L. Walter

It has been postulated and, in a few instances shown, that some kind of dislocation structure will be present at semicoherent interfaces to accommodate small lattice mismatches. In the present study of the NiAl-Cr eutectic, regular arrays of interface dislocations are observed at the boundary between the chromium-rich rods and the NiAl-rich matrix. The networks were examined by transmission electron microscopy and selected area diffraction. The rods and the matrix have a crystallographic relationship in which all directions and planes of the two phases are parallel. The dislocation networks are cmposed of a<100> dislocations lying on the intersections of the cylinders with (100) planes. Dislocations forming hexagonal rather than square arrays are also observed at certain areas of the network. The morphology of the network is consistent with the interpretation of mismatch being accommodated by interface dislocations in the cylindrical geometry. The measured spacing between dislocations was used to calculate an apparent lattice mismatch between the phases (˜0.35 PCt)interface network energy (-140 ergs per sq cm), and network strengthening (-10,000 psi). It has been proposed by Frank and Van der Merwe1 that dislocations should be present at the boundary between two semicoherent crystallographically related phases. The role of the interface dislocations would be to reduce the internal stresses, caused by the mismatch in atomic spacing across the interface. Such dislocations have been observed at the interface between expitaxially grown films and Substrates.2-4 Interfacial dislocations have also been observed at precipitate-matrix interfaces.&apos;-&apos; Directionally solidified eutectics have been shown to have semicoherent phases1&apos; and would, therefore, be expected to have interfacial dislocations as found by Weatherly at a lamellar fault in A1-A12Cu.11 The NiAl-Cr eutectic appeared to be a promising system to examine because both phases are cubic, the lattice mismatch is small, and the phases are crys-tallographically related. Furthermore, the eutectic is easily thinned for transmission microscopy. Indeed, interfacial dislocations were observed and this report describes the nature of the dislocation networks in the boundary between the NiAl-rich ma-trix-phase and the fine chromium-rich rods.21 I) EXPERIMENTAL PROCEDURE Ingots, 3/4 in. in diam and 6 in. long were made by melting in vacuum and casting under argon using 99.9 pct pure material. The composition, in at. pct, was 33 pct Ni, 33 pct Al, and 34 pct Cr. The ingots were then placed in A1203 crucibles on a water-cooled base, melted by means of induction, and withdrawn from the hot zone at the rate of 1 in per hr under argon.* * T his material was first directionally solidified in this laboratory by E. R. Stover Slices were taken perpendicular to the growth direction of the directionally solidified ingot for metallography and for transmission electron microscopy. The electron transmission samples were thinned mechanically, then thinned electrolytically in A-2 electrolyte* *A-2 electrolyte: 62 ml perchloric acid, 700 ml ethanol, 100 ml butylcellosolve, 137 ml distilled H20. until a hole appeared in the foil. 11) EXPERIMENTAL RESULTS A) Optical Microscopy. The microstructure, viewed on a plane perpendicular to the growth direction, is shown in Fig. 1. The structure consists of cells or colonies of parallel chromium-rich rods in the NiAl matrix. The cells occur when there are impurities present12 or, in a ternary eutectic, if the composition is slightly off the eutectic composition. The axis of the chromium-rich rods is parallel to the growth direction except near the cell boundaries. Here the rods may assume angles to the growth direction; however, examination shows that the crystallographic relationship between the rod and the matrix remains the same. Fig. 1 includes cell boundaries where the rods formed at a large angle to the growth direction. The variation of rod position across the cells made it possible to Fig. 1-Structure on plane perpendicular to growth direction. Rods near cell walls are at large angle to growth direction. Magnification 315 times.

Jan 1, 1970

By Richard A. Queeney, Lance G. Peterson

ESTIMATES of the stacking fault free energy of copper reported in the literature show an extensive divergence of results. Based on measurements of dislocation node radii, Thornton et al.7 find the lower limit of stacking fault energy to be 60 ergs per sq cm: Jossang and coworkers4 estimate the same value should be less than 40 ergs per sq cm. Assuming stacking fault free energy to be twice the coherent twin boundary free energy, Valenzuela8 reports 72 ergs per cm, while Inman and Khan2 cite a value of 24 ergs per sq cm. which can no doubt be accounted for by almost complete absence of interstitials in solution. However, the minute concentration was sufficient to permit observable recovery of dislocation damping. Assuming a dislocation density of 1010 CM -2 and an average loop length of 0.5 , a concentration of interstitials as low as 0.01 at. ppm is sufficient to reduce dislocation damping by more than a factor of ten. The concentration of interstitial solute atoms in Ferrovac E-0.15 pct Ti was thus estimated at 0.01 at. ppm < (C + N) < 2 at. ppm. The absence at elevated temperature of strengthening due to interstitials, Fig. 1, was therefore anticipated in the titanium alloy. The temperature dependence of the flow stress below 300°K was unaffected by addition of either titanium&apos; or zirconium.&apos; Observed, however, was an initial difference in the absolute value of the flow stress below 320oK, Fig. 1. Grain size may account for the difference; the grain diameter of Ferrovac E was 30 to 45 µ and that of Ferrovac E-0.15 pct Ti 65 to 90 µ. Although second phase particles in the form of titanium carbides and nitrides precipitated in the Ferrovac E-0.15 pct Ti alloy, the spacing was too large to produce any strengthening effect. The mechanical properties measured, therefore, were inherent to the bcc lattice. 1W. C. Leslie and R. J. Sober: Trans. ASm, 1967, vol. 60, pp. 99-111. 2 H. Conrad: Journal of Metals, 1964, vol. 16, pp. 582-88. 3 A. S. Keh and W. C. Leslie: Materials Science Research. H. H. Stadelmaier and W.W.Austin, eds., vol. 1.pp. 208.50, Plenum Press, New York, 1963. 4A. S. Keh, Y. Nakada, and W. C. Leslie: Dislocation Dymmics, Rosenfield, Hahn, Bement, Jr., and Jaffe, eds., pp. 381-406, McCraw-Hill Book Co., New York, 1968. &apos;W. J. Bratina, J. T. McCrath, and H. E. Rosinger: Can. Met. Quart., in press. 6 W. J. Bratina, J. T. McGrath, and D. Mills: Suppl. Trans. Japan Inst. Metals. 1968, vol. 9, pp. 436-43. &apos;H. E. Rosinger and C. B. Craig: Can. Met. Quart., In press. %. Mills. J. T. McGrath. and W. J. Bratina: ScriptaMet,, 1968, vol. 2, pp. 311-13. The purpose of this note is to present the results of a direct measurement of the stacking fault free energy in copper. The present method avoids both the question of interaction forces of nodal dislocations and the assumption that the coherent twin boundary free energy is one-half that of a stacking fault. Fig. 1 shows a transmission electron micrograph of a stacking fault intersecting a high angle grain boundary in copper: Fig. 2 is a schematic representation of the intersecting interfaces. To produce the specimen, pure copper was rolled to 0.002 in. thickness and annealed for several hours at 875°C. These foils were strained in tension to l04 µ in. per in., and rean-nealed to 8 min. Recrystallization and/or grain growth were not observed during the second anneal, indicating that intersections such as Fig. 1 are equilibrium configurations. Many such stacking faults were observed, but few were noted as intersecting grain boundaries in well-illuminated areas. The intersection of Fig. 1 was well away from the specimen edge. Since similar defects have not been observed in fully recrystal-lized and annealed copper, it is felt that this defect is due to the tensile straining. Electron transmission

Jan 1, 1970

By A. R. Calawa, T. C. Harman, M. Finn, P. Youtz

A study has been made of the growing, annealing, and diffusion parameters in PbSe, Pb1-ySnySe, and Pb1-xSnxTe. Single crystals of these materials have been grown using the Bridgman technique. For all of the above materials the as-grown crystals are p type with high carrier densities. To reduce the carrier concentration and increase the carrier mobility, the samples are annealed either isothermally or by a two-zone method. From isothermal anneals, the liquidus-solidus boundary on the metal-rich side of the stoichiometric composition has been obtained for some alloys of Pb1-xSnxTe and on both the metal- and seleniunz-rich sides for PbSe and alloys of Pbl-ySnySe. In Pbo.935 Sno.065 Se carrier concentrations as low as 5 x1016 Cm-3 and mobilities as high as 44,000 sq cm v-1 sec-1 at 77°K have been obtained. Inter diffusion parameters mere also studied. The ddiffusion experiments mere identical to the isothermal or two-zone annealing experiments except that the samples were removed prior to complete equilibration. The resulting p-n junction depths were determined by sectioning and thermal probing. Inter diffusion coefficients for various temperatures were calculated for both PbSe and Pb0.93Sn0.0,Se. RECENTLY, there has been considerable interest in the PbTe-SnTe and PbSe-SnSe alloys with the rock salt crystal structure. The unusual feature of these systems is the variation of energy gap EG with composition. Several investigations1-3 have shown that EG for the lead chalcogenides decreases as the tin content increases, goes through zero, and then increases again with further increase in tin content. The possibility of obtaining an arbitrary energy gap by selecting the composition is an especially attractive feature of these alloys for applications involving long-wavelength infrared detectors and lasers. In addition, some unusual magneto-optical, galvanomagnetic, and thermomag-netic effects should occur for alloys with low band gaps. If uncompensated low carrier density crystals can be obtained, then a small carrier effective mass, a large dielectric constant, and the resultant high carrier mobility should yield enormous effects at low temperature in a magnetic field. The relative variation of the energy gap with pressure should also be very large for these low gap materials. The primary purpose of this paper is to provide some information concerning the preparation of low carrier concentra- tion, high carrier mobility, and homogeneous single crystals with a predetermined alloy composition. I) DETERMINATION OF ALLOY COMPOSITIONS In all of the work described in this paper, the composition of lead and tin chalcogenides in the alloys was determined by electron microprobe analysis. Separate X-ray spectrometers are used to make simultaneous intensity measurements of the Pb La1 and Sn La1 lines emitted by the sample under excitation by a beam of 25 kev electrons focused to a spot about 2 µm in diam. These intensities are compared to the intensities of the same lines emitted by standards under the same conditions. The standards used are the terminal compounds of each pseudobinary system, i.e., PbTe and SnTe for Pbl-xSnxTe alloys, PbSe and SnSe for Pbl-ySnySe alloys. The composition of the sample is then obtained from theoretical calibration curves which relate the weight fractions of lead and tin in the alloy to the measured ratios of X-ray intensities for the sample and the standards. The lead and tin calibration curves for each alloy system were calculated by using corrections for backscattered electrons,4 ionization,5 and absorption,6 and assuming that the atom fraction of tellurium or selenium in the sample and standards is exactly +. Results obtained by using the microprobe are in good agreement with those obtained by wet chemical analysis. II) CRYSTAL GROWTH FROM THE VAPOR Early work on the vapor growth of PbSe was carried out by Prior.7 He used small chips of Bridgman-grown single crystals as the source material and frequently converted the whole charge of a few grams into one crystal. In the present work, vapor growth occurred using a metal-rich or chalcogenide-rich two-phased alloy powder as the source material. Small, nearly stoichiometric crystals are formed on the walls of the quartz tube. The procedure will now be described in detail. Initially, a 100-g charge containing (metal)o.51(chalco-genide)o 49 proportions or (metal)o.49(chalcogenide)o. 51 proportions of the as-received elements in chunk form are placed in a fused silica ampoule. After the ampoule is loaded, it is evacuated with a diffusion pump and sealed. The sealed ampoule is placed in the center of a vertical resistance furnace. The region containing the ampoule is heated to about 50°C above the liquidus temper-ature for the particular composition used. After about one-half hour at temperature, the elements are reacted and the molten material homogenized. The ampoule is quenched in water. The quenched ingot is crushed to a coarse powder for vapor growth experiments and to a fine powder for the isothermal annealing experiments which are discussed in a later section. Vapor growth experiments were carried out using the powdered, metal-rich or chalcogenide-rich alloys

Jan 1, 1969

THE metal iron has physical and chemical properties which are somewhat different from those of steels, but a knowledge of the pure metal is a useful starting point in studying the behavior of steels. Solid iron exists in two different crystalline forms, called alpha (a) and gamma (?) iron, the former being the ordinary form at room temperature. When heated above the "A2 point," 768 C (1414 F), the metal becomes nonmagnetic, and at the "A, point," 910 C (1670 F), it undergoes a change in crystalline form to become gamma iron. In the range 768 to 910 C, it is sometimes called beta (ß) iron to distinguish it from the magnetic alpha, but the two are identical in crystal structure. When gamma iron is further heated to 1400 C (2552 E), it changes into delta (d) iron, which is identical with beta or non- magnetic alpha iron. Pure iron melts (in an inert atmosphere) at 1537 C (2800 F); the melting point is generally lowered by alloys or impurities. PROPERTIES OF IRON AT HIGH TEMPERATURES Many of the properties of iron undergo abrupt changes at the transition temperatures.1 For example, in heating through the A, point, a sudden shrinkage in volume occurs. Similarly, melting is attended by sharp physical changes such as an increase in volume. Table 16-1 contains a summary of the measured physical properties of pure iron at several temperatures. Usually the properties change smoothly within the range of stability of a given form, but this is not always true. For example, the specific heat reaches a sharp maximum at the A2 point although no trans- formation occurs. (See Fig 14-1.) Solvent Powers of Liquid Iron. Liquid iron is capable of dissolving most of the other metals and many nonmetallic elements as well. Of the metals that are liquid at the melting point of iron, only lead, silver, and bismuth refuse to dissolve to an ap-

Jan 1, 1951

By L. B. Slichter

It has been estimated that rock exposures in most mining districts aggregate less than 1 per cent. of the total surface area.1 Conclusions concerning the hidden 99 per cent. necessarily have been based on knowledge of only a small fraction of the surface, and from this limited information the geologist has been obliged to deduce the approximate and general nature of the underlying formations. In the search for ore it is necessary to supplement this general picture with greater detail. Fairly accurate knowledge of relatively small zones is required. This knowledge is carefully sought in many different ways—detailed interpretations of geological history, the tracing of float, the use of test pits, of trenching, of drilling, and of other methods. Practical ingenuity, scientific brilliance, great perseverance and patience, and the expenditure of large sums of money have all been a part of this search. The problem of exploring beneath cover with economy, and of obtaining essential information which this cover hides, is obviously a difficult one. It is also a very important one, for geologist&apos;s inform us that already the story of the 1 per cent. exposed outcrops has been largely read.V here remains the nearly virgin field comprised in the hidden 99 per cent.: and the importance of this zone is bound to increase continually. In recent years, the problems connected with the exploration of this "99 per cent. zone" have attracted a constantly enlarging group of investigators and at present greater efforts than ever before are being made to resolve them. This work, in it&apos;s various special aspects, has enlisted, beside geologists, the cooperative efforts of chemists, physicists, and mathematicians. The progress made in this development should be kept before those directing explorations in order that due advantage may be taken of a changing situation. My subject concerns certain aspects of one of the older physical methods of exploration, the magnetic method. This method is familiar in principle to most of us, arid because of its age., is especially suitable for

Jan 1, 1929

By I. A. Ettlinger

THE formation that the writer has chosen to call "The Central Arizona Batholith" is included in the Globe, Miami, Ray, Pioneer, Troy, and Silver King mining districts. Its extension to the southeast is in the Banner mining field. Basing his argument on what is known of batholithic intrusions, the author offers reasons for considering all these granitic outcrops as parts of a single great mass of plutonic rock. The United States Geological Survey has subdivided this area into three -quadrangles-the Globe, the Ray, and the Florence. Of the first two, geologic atlases1 have been published, but of the last, the topographic map alone is available. These mining districts include such prominent present-day producers as Inspiration, Miami, Old Dominion, Arizona Commercial, Iron Cap, Superior and Boston, Magma, Belmont, and Ray Consolidated. Among those well known in the past are Silver King mine and Gibson mine. Fig. 1 is a geologic map of the Central Arizona Batholith region. F. L. Ransome&apos;s excellent work on The Copper Deposits of Ray and Miami, Arizona,&apos; is of great value to all workers in those districts. His geologic map for the Ray and Globe quadrangles has been incorporated in Fig. 1, and the stratigraphic names employed are those first applied and defined by him in his pioneer work in this region. The purpose of this paper is to show that the ores are related to post-Carboniferous granitic intrusions; that while there does not seem to be any adequate explanation for the distribution of all the igneous stocks, a preexisting structure does appear responsible for at least the location of the largest igneous stock of the region; that the principal producing vein mines are located in the sedimentary rocks in the roof of this batholith, while the disseminated copper deposits are found bordering the lower portions of the batholith exposed by erosion; that primary zoning is illustrated not only on a broad (district) scale but also on a small (individual

Jan 1, 1928

By C. A. Heiland

A. INTRODUCTION (C. A. HEILAND) I. PRINCIPLES OF TEMPERATURE COMPENSATION IN MAGNETIC INSTRUMENTS The principle underlying the majority of magnetic intensity variom-eters is a comparison of the force to be measured with another force of known magnitude. The known force may be (a) of a magnetic nature, such as magnetic fields produced by magnets or coils, or (b) of a mechan-ical nature, such as (1) the elastic forces of wires, or (2) the force of gravity, such as employed in bifilar magnetometers and magnetic balances. In instruments of such type, usually a magnetic system is employed, free to move about either a horizontal or vertical axis, on some sort of a suspension. If the earth&apos;s magnetic field alone were present, such a system would adjust itself into the direction of the field or that of its components. Owing to the simultaneous action of the comparison force, however, the magnetic needle assumes a position that differs from the direction of the magnetic force; for all such instruments, the angle of deflection a is given by tan a = F/X, where F is the known and X the unknown earth magnetic force component. In other words, the magnetic system merely serves as an "indicator" for the position of balance of the two forces. Considering the matter from this point of view, it is not immediately obvious why the temperature of such a magnetic system should modify the results. In magnetic instruments, we may distinguish two different effects of temperature: (1) a magnetic effect and (2) a mechanical effect. The first is due to the fact that the magnetic moment of a magnet drops with an increase in temperature. This drop is characterized by the temperature coefficient of the magnetic moment µ (see equation 1). The second effect is due to the change in the .torsion of suspension wires with temperature or to the expansion of lever arms of masses acting on magnetic balances.

Jan 1, 1932

By M. T. Hepworth, T. P. Papazoglou

Hydrogen diffusion in hcp and bcc titanium in the temperature range 610° to 900°C was measured by reacting cylindrical specimens of high-purity titanium at constant temperature with small constant pressures of hydrogen of the order of a few Torr. In the range 0 to 6.7 at. pct H in hcp titanium, the diffusion coefficient D in sq cm per sec is given by: where T is in °K and R in cal per g-atom OK. Only three measurements of diffusivity in bcc titanium were made: at 900&apos; : the diffusivity in ß titanium was found to be 1.8 x 10-4 sq crn per sec. McQUILLAN1 has studied the constitution of the Ti-H system and reported the concentration of hydrogen as a function of pressure of hydrogen and temperature. He found hydrogen absorption was reversible and rapid at temperatures above 500°C in both crystallographic modifications, the a (hcp) phase and the ß (bcc) phase, with the latter phase stabilized by hydrogen additions. Wasilewski and Kehl 2 measured the diffusivity of hydrogen in hcp and bcc Ti-H alloys. For bcc alloys, they reacted cylindrical specimens of titanium with hydrogen gas at 1 atm pressure. They measured the rate of absorption of hydrogen isothermally on specimens ranging from zero hydrogen content when above the transformation temperature to hydrogen contents sufficient to stabilize the bcc phase when below the transformation temperature. By integrating Fick&apos;s second law for a cylindrical geometry, assuming a diffusion coefficient independent of composition, they calculated diffusivities as a function of temperature. In the range 650" to 1000°C their results in bcc titanium yielded the expression: where D is in sq cm per sec, T in OK, and R the gas constant in cal per g-atom-OK. Their studies on the hcp a phase were conducted by exposing long cylindrical titanium specimens to hydrogen at a sufficiently high pressure to establish a surface layer of fl phase 80 to 120 u thick for the duration of an isothermal experiment. Concentration profiles were then determined by hydrogen analysis from chips obtained upon machining quenched specimens. The diffusivity of hydrogen was then calculated yielding the expression: The present investigation was undertaken principally to redetermine the diffusivity data on a titanium by a direct absorption from the gas phase at sufficiently low hydrogen pressures to avoid the presence of a surface bcc phase and also to check the diffusivity data at low hydrogen concentrations in the bcc stmcture. EXPERIMENTAL PROCEDURE High-purity electrolytic sponge titanium (99.9 pct) of BHN 91 was arc-melted, forged, rolled, and machined into cylinders of final hardness, upon annealing, of BHN 92. Cylindrical specimens of two sets of dimensions were used: 1.524 by 2.931 cm and 1.905 by 3.663 cm diam and length, respectively. The experimental apparatus used for annealing specimens and for admitting known amounts of hydrogen at constant pressure is shown in Fig. 1. In a typical experiment, a specimen was lightly abraded with fine-grain silicon carbide, washed with water and detergent, and then thoroughly degreased with reagent-grade tri-chlorethylene and acetone. The specimen was suspended by a Chrome1 wire in the center of a quartz furnace tube, without contact with the tube, and heated to 925°C (as measured by a thermocouple adjacent to the specimen, outside the tube) for a period of at least 4 hr under a vacuum of from 10-6 to -7 Torr as measured by an ionization gage. The furnace temperature was then adjusted to the temperature chosen for the particular diffusion study and the specimen allowed to equilibrate thermally. Hydrogen was then ad-

Jan 1, 1969

By A. D. Schwope, L. R. Jackson, K. F. Smith

Burghoff and Blank1 have pointed out that the creep properties of hard-drawn coppers are closely associated with their individual softening characteristics and have further shown that the creep resistance of various types of copper is improved, under certain circumstances, by cold stretching. In the design of certain types of electrical machinery, it is important to have the creep resistance as high as possible; furthermore, short-time creep strength is important since in many cases stresses are large only during warming-up and cooling-down periods. In this paper, data are presented showing the effect of cold work on the short time creep strengths of various types of commercial copper under several conditions. It is shown that trends from short-time creep tests are evident at longer times. Materials Used in the Investigation The coppers used in this investigation were commercial grade and of two basic types, oxygen free high conductivity (OFHC) and tough pitch. Additions of silver in amounts of 15 and 25 oz per ton were added to each of the two coppers. The analyses of these six coppers are given in Table 1. Originally, they started as wire bars 4 X 4 X 54 in. A. square rod was made by hot rolling the wire bars to 9/16-in. rod in 8 passes. This rod was then cold drawn to 0.445-in.-diam rod and annealed for 3 1/2 hr at 1000°F. It was then cold drawn to 0.325-in. rod and again annealed at 1000°F for 3 1/2 hr. Hard square rods were then made by cold rolling to 0.257 X 0.257-in. rod. Soft wire was made from the hard- drawn material by annealing at 650°F for 3 hr. The final rolling was performed using a set of 9-in. grooved rolls revolving at 30 rpm, which produced square wires. Reductions of approximately 5, 20, 30, and 40 pct were obtained using several passes in the same direction for the large reductions. The 5 pct reduction by drawing was accomplished using a steel die having 2 parallel bearing surfaces. The die angle was 7 1/2 degrees and the wires were lubricated with a paste of ceresin wax dissolved in carbon tetrachloride. The speed of drawing was 13 fpm. Since work was done on only two sides of the wire simultaneously, it was necessary to rotate it 90 degrees each pass to insure uniform deformation. The room-temperature tensile properties of the various tempers are given in Table 2. The grain size of the an- nealed 0.257-in. wires was uniform and averaged about 0.035-0.045 mm. Experimental Procedures for Short-time Creep Tests Standard creep-test frames (Fig 1) were used for the testing. Special fixtures were designed to apply axial compressive and tensile loads to the copper wires. The compression specimens were 1 in. long and the ends were ground flat and parallel. The creep in compression was indicated by the movement of reference marks s-ratched on intersliding platinum strips attached to the moving heads of the fixture. The movement was measured with an optical micrometer fitted with a filar eyepiece on which the smallest division was 0.00005 in. The tensile creep specirriens were 4 in. long which provided ample gripping surface for the jaw-type grips. The platinum strips were attached to a one-inch gauge length of the wire and the creep measured as previously described. The single-specimen furnaces were connected to individual power and control sources. The controlling equipment consisted of Foxboro controllers

Jan 1, 1950

By J. J. Gilman

RECENT experiments have shown that the mar-tensite reaction in a standard tool steel is influenced by the history of the reacting austenite. The martensite reaction proceeds to a given extent at a higher temperature in austenite formed from an annealed spheroidal structure than it does in austenite formed from tempered martensite: that is to say, a prequench lowers the temperature range of the martensite reaction in this steel. Furthermore, a prequench alters the appearance of the martensite as compared to martensite formed from "virgin" austenite. The steel used for this work was a manganese nondeforming tool steel of the following composition: C, 0.85 pct; Mn, 1.43; Si, 0.23; Ni, 0.12; Cr, 0.59; and W, 0.59. A piece from a rolled bar was forged to Vz in. sq and annealed to a spheroidal structure. Disks 1/8 in. thick were used in the experiments. Several sets of the specimens were prepared and austenitized in lead at 1475°F. Three sets were held at 1475°F for 15 min, quenched in water, and immediately reheated to 1475°F. After this quench the three sets were held for 5 min, 30 min, and 3 hr, respectively, at 1475°F and then the individual specimens in each set were quenched in molten baths to 325", 300°, and 275ºF, respectively, and held for 15 sec. Immediately after the quenching treatments? the specimens were tempered at 600°F for 30 sec to darken the martensite and then were quenched in water. The holding times were short enough to avoid isothermal transformation. Three other sets of specimens were given the same final quenching treatments as the first three, but they were austenitized at 1475°F for 20 min, 35 min, and 3 hr and 15 min, respectively, without an intermediate water quench. The two individual specimens from each set were quenched together in order to eliminate quenching errors. Several experiments were run in this way but only the six sets referred to are described in detail because they all yielded essentially the same results. By means of the stated heat treatments the martensite reaction was investigated for: 1—austenite formed from an annealed structure, and 2— austenite formed from tempered martensite. The martensite reactions of the two types of austenite differed significantly. This is shown by Figs. 1 and 2. Comparison of the photographs on the left in Figs. 1 and 2 with those on the right shows that less martensite was formed by a quench to a given temperature from prequenched austenite than from austenite formed from an annealed structure, that is, the prequench suppressed the martensite reaction. The effect was observed for specimens austenitized 20 min, 35 min, and 3 hr and 15 min. A comparison of Figs. 1 and 2 shows that the martensite reactions in both sets of specimens occurred at lower temperatures with increased austenitization time. This was caused by the increased dissolution of residual carbides with time at 1475°F. However, the difference in amount of martensite formed in prequenched austenite as compared to virgin austenite was approximately the same for all three austenitization times. One further observation should be noted. The needles of the martensite formed from virgin austenite are somewhat longer on the average and show less of a tendency to cluster than those of martensite formed from prequenched austenite. This causes the martensite on the right in Figs. 1 and 2 to have a more acicular appearance than the martensite on the left. Since the sets of specimens used in this work were austenitized for identical total lengths of time and the effect of a prequench on the martensite reaction existed for specimens held at the austenitizing tem-

Jan 1, 1953

By Nicholas J. Grant, H. C. Chang

Microscopic observations during creep tests were made on AI-20 pet Zn, 80 pet Ni-20 pet Cr, and 25 and 3S aluminum specimens. All these materials failed in an inter-crystalline manner under certain stress and temperature conditions. Particular atten-tion was given to the initiation and propagation of intercrystalline cracks in coarsegrained AI-20 pct Zn specimens. The geometry of the grains and grain boundaries in these specimens was known before the tests. On the basis of the observations and a knowledge of the interaction between grains and grain boundaries, a mechanism of intercrystalline fracture and propagation of the fracture has been proposed. METAL, and alloy fracture occurs essentially in two ways: transcrystalline and intemrystalline. In the past most of the work done in this field was centered on the determination of stress criteria for fracture. The specimens used for these studies were tested under varying conditions of stress state, temperature, and strain rate. Unfortunately, very little attention was given to the initiation and propagation of the fracture, whereas the nature of fracture was examined closely only after failure. Several extensive reviews of these studies have been published by Orowan, Smith, Barrett, and Petch.1, 4 It is well known that a material which exhibits a ductile and transcrystalline fracture can be made to exhibit a brittle and intercrystalline fracture by modifying its composition and by heat treatment. This modification may or may not result in microscopically observable precipitation in the grain boundaries." In the creep of any one alloy the transition of transcrystalline to intercrystalline fracture is a function of stress, strain rate, and temperature." The tendency for intercrystalline fracture to occur increases as the strain rate decreases and the testing temperature increases. Extensive work on high purity aluminum (99.995 pet) under creep conditions showed the importance of the interaction between grains and grain boundaries, and the different responses of grain and grain boundaries to the variables: stress, strain rate, and temperature.7, 8 It was also shown that grain boundary deformation necessarily has to be accommodated in the grains by various deformation means as. for example, fold formation. The type of fracture resulting from the creep of high purity aluminum was invariably found to be transcrystalline. On the other hand, 2S and 3s aluminum were, under certain conditions, found to fracture in an intercrystalline manner." One reason given for this was that the grains could accommodate to a lesser extent the deformation of the grain boundaries.19 It was decided to examine this line of reasoning in greater detail and to investigate the particular interactions between grains and grain boundaries that result in the incidence and progression of inter-ct,ystalline fracture. It is also the purpose of this paper to show where and how intercrystalline cracks start and how they propagate to result in fracture. Several alloys—Al-20 pct Zn, 80 pet Ni-20 pet Cr, 2S and 3s aluminum-— were used for this study, but attention was paid mainly to the behavior of an A1-20 pet Zn alloy, since its general creep behavior has been established." From the results of this study a mechanism of intercrystalline fracture is proposed. Experimental Procedure The experimental procedure was similar to that used in previous work and has been detailed elsewhere.&apos; Two parallel flat surfaces were milled from an originally round specimen, giving a gage portion which was 1x0.09X0.17 in. Some round specimens, 1/4 in. round by 1 in., were also tested. The A1-20 pet Zn specimens. which were annealed at 1030°F for 24 hr, showed two to four grains across the width of the test bar, and most of the grains occupied the whole thickness of the specimenu. Before some of the specimens were subjected to creep, the grain arrangement was mapped out in a development drawing, Fig. 1. The initiation and

Jan 1, 1957

By M. Oka, C. M. Wayman

It has been known for some time1 that (110)b twinning is possible in bct martensite.* Any plane of the form (110) not parallel to the fourfold axis of tetra-

Jan 1, 1969

By J. W. Downey, A. E. Dwight, R. A. Conner

In a previous paper&apos; we have reported the existence of a number of AB2 Laves phases in which A is a member of the scandium group (including the 1an-

Jan 1, 1967

By Ramesh Malhotra, Hubert E. (Deceased) Risser

THE WORLD Coal, as a source of energy and as a source of coke for the smelting of iron ore, has contributed significantly to the development of every major industrial nation of the world A number of other materials-oil, natural gas, wood, waste materials, water, and, in some applications, nuclear materials -can be used satisfactorily for the generation of heat and energy, but no generally acceptable and economic substitute has been found to supplant coke in iron ore smelting in conventional blast furnaces. In the development of many nations, coal provided the initial source of energy for industrialization Although coal provided more than 60% of the world&apos;s energy each year between 1902 and 1929, oil and natural gas have surpassed it as a source of energy in more recent years (Ref. 38, pp. 439, 441). Despite the rapid rise in importance of other fuels, a considerable amount of the total energy consumed is still supplied by coal. In 1972, coal supplied 32.1 % of the total world energy (Ref. 49, pp. 2-3). To produce this energy, 2.4 billion metric tons of coal were consumed-a 16.0% increase over the amount consumed in 1962. A further worldwide increase in the amount of coal used to supply energy is projected. According to Dr. Karlheinz Bund (Ref. 37, p 145), by the year 2000 world coal consumption could amount to 5 billion mt. Coal Resources and Production The world&apos;s coal resources are estimated to be about 10,872 billion mt. Of this amount, 1,297 billion mt are classified as measured reserves (Ref. 50, p. 57). In Table 13.A.1 the estimates of measured reserves and total resources, recent production, and the ratio of measured reserves to production of major coal-producing countries are shown. About 90% of the world&apos;s total coal resources are estimated to be in the USSR, the United States, and China. The United States ranks second in the world in coal resources, but in measured reserves, it ranks first. Because of the difference in rate at which available coal resources are being exploited, the ratio of measured reserves to actual production varies widely among areas and countries. France and East Germany have the lowest reserve to production ratios, 49.5 and 60.1, respectively. In Mexico, where currently less than 5 million mtpy of coal are produced, the ratio is 1257 For all countries producing more than 200 million mtpy of coal (except East Germany), the ratio ranges from 350 to 670. For the United States, the ratio is 669.7. In Table 13.A.2, distribution of the world&apos;s coal resources by area is shown. More than 97% of the total resources lie in the northern hemisphere, with Asia, including European USSR, having 63.4%. Only 1.9% of the total coal resources are estimat-

Jan 1, 1976