By T. Y. Yan

SUMMARY Laboratory high pressure column tests have shown that the presence of 1-20 ppm of aluminum ion effectively prevents permeability loss during uranium leaching with leachates containing sodium carbonate. If added after permeability loss has occurred, aluminum ion can restore the permeability to nearly its original value. No deleterious effect was observed on uranium leaching performance and the technique should be quite compatible with all field operations. INTRODUCTION The recovery of uranium values from underground deposits by in situ leaching or solution mining has become economically viable and competitive with conventional open pit or underground mining/milling systems (Merrit, 1971). In situ leaching processes are particularly suitable for small, low-grade deposits located in deep formations and dispersed in many thin layers. Many such ore bodies occur along a broad band of the Gulf Coastal Plain (Eargle et. al., 1971). The advantages of the in situ leaching processes have been reviewed (Anderson and Ritchi, 1968). In the in situ leaching process, a lixiviant containing the leaching chemicals is injected into the subterranean deposit and solubilizes uranium as it traverses the ore body. The pregnant lixiviant or leachate is produced from the production well and is then treated to recover the uranium. The resulting barren solution is made up with the leaching chemical to form lixiviant for re-injection. Upon completion of the leaching operation, the formation is contaminated with leaching chemicals and other species made soluble in the leaching operation and has to be treated to reduce the concentration of these contaminants in the ground water to levels acceptable to the regulatory agencies (Witlington and Taylor, 1978). Restoration is accomplished by injecting a restoration fluid, which could be the fresh water or water containing chemicals, into the formation. As it traverses the leached formation, the restoration fluid picks up the contaminants and is then produced at the production well. This produced water is either disposed or purified for recycle. In both phases of operation, formation permeability or well injectivity is one of the most important parameters which determines the viability of the in situ leaching process. Low formation permeability limits production rates, leading to uneconomical operations. The formation is said to be sensitive if there is a sharp loss of permeability on contact with water and other fluids. Many uranium bearing formations, for example, the Catahoula formation of the Texas Coastal Plain, contain significant amounts of clay minerals which are water sensitive. Serious permeability losses can occur when the pH and chemical composition of the lixiviant is significantly different from that of the formation water. Jones has investigated the influence of chemical composition of water on clay blocking of permeability (Jones, 1964) and Mungan studied permeability reduction through changes in pH and salinity of the water (Mungan, 1965). Various mechanisms of permeability damage have been proposed and reviewed (Jones, 1964; Mungan, 1965; Gray and Rex, 1966; and Veley, 1969). When large amounts of swelling clays are present, a significant fraction of the flow channels in the formation can be reduced due to swelling. However, in most cases, swelling need not be the main cause of permeability losses. Particle dispersion and migration or clay sliming can be more important causes for formation damage. Clay particles entrained in the moving fluids are carried downstream until they lodge in pore constrictions. As a result, microscopic filter cakes are formed by these obstructions, plugging the pores, effectively restricting fluid flow and reducing the formation permeability. Moore found that as little as 1-4 percent clays present in a fine grained sandstone could completely plug the formation if they are contacted by incompatible injected fluids (Moore, 1960). It has been found that injection of NaHC03/Na2CO3 lixiviant into formations with significant clay content often leads to loss of formation permeability and well injectivity. To alleviate this problem a change of the lixiviant composition to KHC03/K2CO3 has been proposed. At present, however, many in situ leaching operations employ NH4HC03/(NH4)2C03 mixtures as a source of carbonates. This approach has been successfully used in South Texas by Mobil, Intercontinental Energy, Wyoming Minerals and U.S. Steel, etc. The use of ammonium carbonates solutions, however, contaminates the formation and requires a time-consuming restoration operation. The other approach to reduce the permeability loss is to pretreat the sensitive formation with chemicals which prevent clay dispersion and migration. Such chemicals include hydroxy-aluminum (Reed, 1972 and Coppel et. al., 1973), hydrolyzable zirconium salts (Peters and Stout, 1977), hydrolyzable metal ions in general (Veley, 1969) and polyelectrolyte polymers (Anonymous). Still another approach, is to minimize the "shock" caused by sudden injection by gradually changing the chemical composition of the injected fluids from that of the formation water. THE APPROACH Since permeability loss can be an important factor limiting the efficiency and economic viability of the in situ leaching process, a study was initiated on

Jan 1, 1982

By A. H. Larson, R. J. McClincy

Laboratory-scale decopperizing experiments with multiple sulfur addifions were conducted at 330°C on ternary Pb-Cu alloys containing, as the third elenlent, Sn, Ag, As, Sb, Bi, Zn, and Au, common impurities in lead blast-furnace bullion. For silver and tin, an increased rate and extent of 'cofifier removal was obsert3ed. The elements As, Sb, Zn, Au, and Bi had no effect or less effect as compared to sulfur additions with no i)npurily additions. THE production of primary lead in the blast furnace yields an impure lead frequently containing such impurities as copper. antimony. arsenic. tin, gold, silver iron, oxygen. and sulfur. By cooling this lead to a temperature near its melting point. most of the iron, sulfur, and oxygen and part of the other impurities are removed in the form of a dross. With incipient solidification of the lead, the copper concentration wil have been reduced to 0.02 to 0.05 pct. depending upon the concentration of the other impurities. according to Davey.' Since copper interferes with the treatment of silver after the desilverizing process, it is desirable to decrease the copper content of the lead still fur-ther before the lead is desilvered. The decopperizing of the lead is accomplished by stirring a small quantity. approximately 0.1 pct. of elemental sulfur into the lead at a temperature near its melting point, 330" to 360°C. The copper is removed as a copper sulfide which constitutes a small fraction of a voluminous dross consisting mostly of lead sulfide and entrained metallic lead. The residual copper concentration following the decopperizing operation is frequently as low as 0.001 to 0.005 pct. Thi fact has aroused considerable interest because the equilibrium copper concentration of lead in contact with solid PbS and solid Cu2S is at least an order of magnitude greater, 0.05 pct Cu at 330C. 1, 2 Most investigators have suggested that various impurities in the lead bullion are responsible for the very low copper concentrations frequently encountered in practice. There is little agreement, however? as to which of the impurities are helpful and which are not.3"11 Also. few investigators have sought to explain the mechanisms responsible for the removal of copper to very low concentrations. Willis and Blanks9 have proposed that a nonstoichiometric copper-deficient cuprous sulfide forms in place of the supposed Cu2S. Being copper-deficient, this sulfide phase would possess a low copper activity, and the diffusion of copper dissolved in the liquid lead into this phase would be greatly facilitated. Pin and wagner2 have investigated the removal of copper from liquid lead by studying the effect of impurity-doped lead sulfide on the decopperizing of pure Pb-Cu alloys. Samples of the doped PbS were held in contact with copper-saturated lead for 1 week at 33'7°C. They reported a beneficial effect on decopperizing with bismuth and antimony and no effect with tin or silver. which is directly opposite to the results observed in practice and those reported by Davey 3 and this studv. The purpose of this paper is to describe the effects of certain additive elements on the extent to which copper can be removed fro111 liquid lead by successive additions of sulfur. The impurity elements were added individually to prepared Pb-Cu alloys. The resulting ternary alloys as well as a binary Pb-Cu alloy were then decopperized with repeated additions of sulfur. EXPERIMENTAL Materials. Granulated test lead with a purity of 99.999 pct and the additive elements Cu. Ag. Sb. Bi. Zn. Sn. and Au with purities of 99.99 pct were American Smelting and Refining Co. research-grade materials. The major impurities in the lead were 1 ppm each of iron and copper. all others being less than 1 ppm. The arsenic used was a technical-grade arsenic of 98+ pct purity. Reagent-grade flowers of sulfur were melted under argon to provide small pieces free of fines. Apparatus. The decopperizing experiments were carried out in a 25-mm-OD by 375-mm-long Pyrex tube sealed at one end. The tube was mounted vertically in a resistance-heated. hinge-type tube furnace controlled to within ±lcC. Temperature measurement was accomplished by means of a standardized chromel-alumel thermocouple sealed into the base of a silica. paddle-type stirring rod. All decopperizing experiments were carried out under an argon atmosphere. Procedure. A Pb-Cu starting alloy containing 0.05 pet Cu was prepared under carbon and poured into cold tap water to produce shot. The ternary alloys were prepared by melting together 100 g of the starting alloy and a sufficient amount of the impurity element to yield the desired concentration. The resulting alloy was then homogenized in a Pyrex tube at 450C with continuous stirring. The furnace temperature was then lowered to the operating temperature of 330°C. When thermal equilibrium had been obtained at the operating temperature, individual additions of 0.2 pct (0.2 g) of solid sulfur were added to the melt and stirred in. Stirring was continued for a period of 3 min. discontinued for 5 min. and resumed for the remaining 2 min of a 10-min cycle. This cycle was repeated for as many sulfur additions as desired. When the decopperizing experiment had been completed the lead bullion was quenched and samples of the bullion and dross phases were taken for analysis. Results. The results obtained in the decopperizing

Jan 1, 1970

By J. J. Jakosky

The strategic importance of the metallic minerals in our industrial economy, and the declining rates of discovery have focused attention on means of exploration for new mineral deposits. A consideration of exploration techniques leads to an attempt to evaluate the effectiveness of geo- physics as a tool for mining exploration. One means of evaluation will be to compare the use of geophysics in petroleum exploration with its possible uses in mining.

Jan 1, 1949

By H. H. Klepfer, M. E. Snyder

UNTIL very recently, the commercial availability of the rare earths as metals has been very limited. Fabrication of mill products from these metals has not been studied in most cases. This note reports the results of the development of fabrication techniques for thulium. Thulium has a melting point of about 1550°C and a hexagonal close-packed crystal structure. It oxidizes in air to give a black oxide (TmzO,). The procedures for producing thin thulium foil were developed on one ingot weighing about 220 g and were subsequently applied in processing about a pound of metal to foil. Several alternates for the various fabrication steps were investigated and will be discussed. The metal fabricated was in the form of commercial chill-cast ingots 1 in. in diam and 2 in. long weighing approximately 220 g. Impurities in the ingots were reported by the vendor to be 4000 ppni tantalum, 2000 ppm calcium, 200 ppm nickel, 100 to 200 ppm iron, 100 ppm europium, and less than 100 ppm copper, lutetium, and ytterbium. In addition to these impurities, several salt-like inclusions as large as l/8 in. in diam were revealed along the center line of the one ingot sectioned. Preliminary tests indicated that small wafers cut from the as-cast ingot would not fabricate readily by rolling. Forging of copper-jacketed wafers was therefore attempted. At 1550"F forging was satisfactory but an apparent reaction of copper with thulium demanded investigation of lower temperatures. Therefore, the remainder of the test ingot was forged at 1450°F—with only minor cracking. All ingots forged were inserted into copper tubes of 1 in. 1D and 0.125-in. wall thickness. The jackets were sealed by flattening the ends of the tubes and welding under helium. Heating time at 1450°F was 30 min. Press forgings of 1/8 in. per pass were used, followed by 10 min reheats. When the ingots had been squared and reduced to 0.250 in. in thickness, the original copper jacket was stripped off and replaced by a new jacket in preparation for hot rolling. Hot rolling at 1450" F without edge cracking was readily accomplished after forging. Excellent results were obtained with 10 pct reductions of thickness followed by 5 to 10 min reheats. After reduction of thickness from 0.250 to 0.100 in. the copper jacket was removed. It was found, in fact, that hot rolling in air was possible. A tenacious black oxide similar to that seen on zirconium was formed during 3 min reheats at 1450°F. Reduction in air to 0.010 in. foil was possible taking 10 pct reductions per pass. The oxide coat formed during hot rolling in air could best be removed by sand blasting and pickling. Common pickling solutions containing polar solvents were found to attack the metal too rapidly and a concentrated nitric-hydrofluoric acid mixture attacked neither the oxide nor the metal. The most satisfactory pickling solution was 52 vol pct concentrated nitric acid-48 vol pct glacial acetic acid. After forging to 0.250 in., vacuum annealing and cold rolling was found to be another satisfactory alternate to hot rolling in copper jackets. After forging. a hardness of Rockwell B76 was found. Annealing in vacuum (2 X l0-5 mm of Hg) for 1 hr at 1200"F did not alter this value. Annealing at 1470"F for 1 hr brought the hardness down to R;]63. With cold rolling (5 pct per pass) the hardness returned to about R,1:76 after 20 pct reduction and edge cracking became noticeable. However, cold rolling to a total of 40 pct reduction in thickness (RI,,83) was possible before edge crack propagation became serious. Good surface finish was obtained, and the metal loss due to oxidation was minimized by cold rolling and vacuum annealing. Using this procedure the yield of 1.25 in. wide by 0.010 in. thick foil from a 1-in. diam ingot was about 40 pct.

Jan 1, 1961

By William P. Blake

At the August meeting of the Geological Society of America, I presented a paper on the occurrence of alunogen and bauxite upon the Upper Gila river, about 40 miles north from Silver City, New Mexico, together with observations upon the geology of that region." Inasmuch as the subject is specially interesting to metallurgists and mining engineers, and as our Transactions contain recent important papers, by Dr. Hayes, M. Laur, of France and others, upon bauxite, I venture to offer to the Institute, in more condensed form, an account of the deposits described in the paper above referred to. The only other published account of the alunogen locality which I have been able to find is a prospectus-pamphlet, issued in a small

Jan 1, 1895

By C. E. Lesher

THE Disco* process for the production of low temperature coke and its immediate predecessor, the Wisner or Carbocite process have been described in the voluminous literature of low temperature carbonization.1 This paper will describe the development of the process from the first attempt at commercial operation by the American Gas and Electric Co. at Philo, Ohio, Yn the 1920's to the successful operation in 1949 by the Disco Co., a division of the Pittsburgh Consolidation Coal Co., of the 1000-ton per day Disco plant near Pittsburgh, see Figs. 1-2. In the 1924 coal industry depression following the hectic post World War I expansion, the northern Appalachian, unionized bituminous coal fields were affected first and foremost, and Western Pennsylvania as hard as any. Competitive market pressure was heaviest on the lower grades of steam coals, notably the from the Panhandle district where ash and sulphur are inherently higher than in the same Pittsburgh coal bed to the east along the rivers. The firm structure of Panhandle coal while favoring the prepared sizes, depressed the usefulness and value of the finer sizes. Panhandle slack and nut slack were marketed with difficulty at consistent, and at times considerable, loss. Many solutions were suggested, and the Pittsburgh Coal Co. investigated all. Lower delivered prices through lower mine costs and more advantageous freight rates were obvious goals, but equally obvious were the difficulties of self attainment of either in any substantial measure. Selling Btu's in pipes was abandoned as an idea after a thorough study of the economics of distribution of what was then, and is even now, the only developed continuous process of complete gasification of bituminous coal-producer gas. Although the coal company purchased huge blocks of electric power, it sold not a car of coal to the central power stations. Public utilities controlled the markets for electric current, and it was found that no matter at how low a cost current might be put on the bus bars by the coal company, distribution to its widely scattered coal mines made such an enterprise practically impossible. Consolidation of underground operations and a huge modernization program of mining operations in the 1920's were but preparation for the introduction of mechanical cleaning of the coal for market, particularly the smaller sizes of steam, gas, and by-

Jan 1, 1953

By C. E. Lesher

THE Disco* process for the production of low temperature coke and its immediate predecessor, the Wisner or Carbocite process have been described in the voluminous literature of low temperature carbonization.1 This paper will describe the development of the process from the first attempt at commercial operation by the American Gas and Electric Co. at Philo, Ohio, Yn the 1920's to the successful operation in 1949 by the Disco Co., a division of the Pittsburgh Consolidation Coal Co., of the 1000-ton per day Disco plant near Pittsburgh, see Figs. 1-2. In the 1924 coal industry depression following the hectic post World War I expansion, the northern Appalachian, unionized bituminous coal fields were affected first and foremost, and Western Pennsylvania as hard as any. Competitive market pressure was heaviest on the lower grades of steam coals, notably the from the Panhandle district where ash and sulphur are inherently higher than in the same Pittsburgh coal bed to the east along the rivers. The firm structure of Panhandle coal while favoring the prepared sizes, depressed the usefulness and value of the finer sizes. Panhandle slack and nut slack were marketed with difficulty at consistent, and at times considerable, loss. Many solutions were suggested, and the Pittsburgh Coal Co. investigated all. Lower delivered prices through lower mine costs and more advantageous freight rates were obvious goals, but equally obvious were the difficulties of self attainment of either in any substantial measure. Selling Btu's in pipes was abandoned as an idea after a thorough study of the economics of distribution of what was then, and is even now, the only developed continuous process of complete gasification of bituminous coal-producer gas. Although the coal company purchased huge blocks of electric power, it sold not a car of coal to the central power stations. Public utilities controlled the markets for electric current, and it was found that no matter at how low a cost current might be put on the bus bars by the coal company, distribution to its widely scattered coal mines made such an enterprise practically impossible. Consolidation of underground operations and a huge modernization program of mining operations in the 1920's were but preparation for the introduction of mechanical cleaning of the coal for market, particularly the smaller sizes of steam, gas, and by-

Jan 1, 1953

By C. E. Lesher

THE Disco* process for the production of low temperature coke and its immediate predecessor, the Wisner or Carbocite process have been described in the voluminous literature of low temperature carbonization.1-4 This paper will describe the development of the process from the first attempt at commercial operation by the American Gas and Electric Co. at Philo, Ohio,' in the 1920's to the successful operation in 1949 by the Disco Co., a division of the Pittsburgh Consolidation Coal Co., of the 1000-ton per day Disco plant near Pittsburgh, see Figs. 1-2. In the 1924 coal industry depression following the hectic post World War I expansion, the northern Appalachian, unionized bituminous coal fields were affected first and foremost, and Western Pennsylvania as hard as any. Competitive market pressure was heaviest on the lower grades of steam coals, notably those from the Panhandle district where ash and sulphur are inherently higher than in the same Pittsburgh coal bed to the east along the rivers. The firm structure of Panhandle coal while favoring the prepared sizes, depressed the usefulness and value of the finer sizes. Panhandle slack and nut slack were marketed with difficulty at consistent, and at times considerable, loss. Many solutions were suggested, and the Pittsburgh Coal Co. investigated all. Lower delivered prices through lower mine costs and more advantageous freight rates were obvious goals, but equally obvious were the difficulties of self attainment of either in any substantial measure. Selling Btu's in pipes was abandoned as an idea after a thorough study of the economics of distribution of what was then, and is even now, the only developed continuous process of complete gasification of bituminous coal-producer gas. Although the coal company purchased huge blocks of electric power, it sold not a car of coal to the central power stations. Public utilities controlled the markets for electric current, and it was found that no matter at how low a cost current might be put on the bus bars by the coal company, distribution to its widely scattered coal mines made such an enterprise practically impossible. Consolidation of underground operations and a huge modernization program of mining operations in the 1920's were but preparation for the introduction of mechanical cleaning of the coal for market, particularly the smaller sizes of steam, gas, and by-

Jan 1, 1952

By Cyril Stanley Smith

Jan 1, 1949

By Cyril Stanley Smith

Jan 1, 1949

By R. L. Ash, R. R. Rollins, C. J. Konya

An investigation was performed to determine conditions for optimizing the spacing of simultaneously initiated multiple explosive columns. This was done by using models of mortar, dolomite, and Plexiglas with 10-grain mild detonating fuse as the explosive charge. It was desired to simulate blastholes with multiple primers initiated by detonating fuse or when high-velocity explosives are used in low-velocity materials. It was found that optimum spacing between multiple charges was strongly influenced by charge length. At less than optimum charge length, the spacing at which complete shearing was possible between adjacent charges decreased exponentially with a subsequent loss of broken material volume. For charges fired simultaneously, larger burdens and spacings were possible as compared to those necessary for single-crater charges. For each material studied, there was a characteristic optimum charge length and a maximum attainable spacing at any given burden. Proper selection of the spacing distance between charges is fundamental to successful blasting. Its value directly affects the cost of drilling and explosives used per unit of broken material. In addition, the choice of a spacing that is Compatible with a given set of blasting conditions aids in the control of fragmentation sizing, ground vibrations, overbreak, and throw which in turn, influence other production costs. For example, normally loaded blastholes that are spaced too closely invariably promote overbreak and usually give coarse fragmentation. Unless care is taken, airblast and violent flyrock will occur and under certain conditions cutoffs and misfires may result. Too large a spacing, on the other hand, frequently leads to conditions that form bootlegs or toes. The choice of a particular spacicg to use, however, is largely a matter of individual experience and judgment, usually based on trial and error. Very little is known or can be found in the literature with regard to how the spacing between charges is related to field conditions and charge geometry. As a general rule, the firing time sequence of adjacent charges and properties of a material are thought to have the most significant influence on the spacing distance best suited for any given field condition. For example, delayed initiation of adjacent charges usually always requires a closer spacing than when charges are fired at the same time. This should be expected if one considers that the energy normally dissipated and lost in the surrounding ground from charges fired independently would be captured and utilized for breaking material between charges when they are initiated together. Spacing can be extended also when charges are aligned with structural planes of a material, such as jointing, along which shearing is relatively easy. It is customary to relate the spacing (S) between charges to their common burden (B) in the form of a spacing ratio, or SIB. The burden normally is considered as the optimum depth or distance from any single charge perpendicular to the nearest free or open face at which the desired fragmentation and maximum crater yield are obtained. For production blasting, value of the ratio is generally considered to vary from 1 to 2, depending on conditions.1-6 When adjacent charges are fired independent of one another, the value varies from 1 to about 1.4, the closer amount being employed to square corners or produce craters having the ideal 90" apex angle. The larger ratio is the geometric balance value for craters having an apex angle of 135". The basic ideal crater forms in the plane of the charge diameter for charges fired independently are shown in Fig. 1. In the event charges are fired simultaneously, geometric balance in the plane of their charge diameters suggests that a spacing ratio near 2 would be appropriate, as illustrated by Fig. 2. In practice, however, some compromise ratio value must be selected to conform with the specific ground conditions. An example would be where the jointing planes tend to produce 60° or 120° crater angles, the appropriate geometrically balanced charge arrangement being given by Fig. 3. In this condition, the spacing ratio is 1.15, not 1 or 1.4 as suggested for the 90° cratering of independently fired adjacent charges. In view of the foregoing, it would seem logical to assume that whenever charges all having the same burden are fired at the same time, spacing distances always can be greater than those permitted by charges fired independently. In practice this is not the case, however.

Jan 1, 1970

By P. W. Andrews, R. B. Toombs

ECONOMIC STRUCTURE OF MODERN INDUSTRIAL ECONOMIES The role of minerals in modern industrial economies may be examined in several ways. There are relationships with the various sectors of the economy: the primary, secondary, and tertiary industrial groupings and activities. Mineral supply and demand activities can be measured in terms of national accounts criteria. The economic policy objectives of the modem industrial economy are based to a considerable extent on the needs of the nation for economic supplies of miner- al materials. There is an important role for minerals relative to national security in peace and in wartime and many national policies are directed toward ensuring adequate sup- plies of minerals. Environmental control in the modem industrial economy is increasingly concerned with matters related directly to the production and use of minerals and these matters, in turn, bear importantly on conservation in mineral supply and demand. Mineral polices include specific provision for research and development activities concerned with the production and the use of minerals. In all, national policy objectives will be shaped in considerable part by the circum- stances of mineral supply and demand: the relative degree of availability from domestic and foreign sources, the state of the mineral-processing industries, and the degree of development of the mineral-using industries, and per capita and total changes in requirements. Goods made from mineral raw materials are the basis of all advanced societies and although this is taken for granted, every country is continually dealing with problems of mineral supply and demand. Considering that in the first 50 years of this century the consumption of mineral materials in a highly Industrialized country such as the United States increased by six times while the population was doubling, it becomes apparent that if a country is to enjoy rapid economic growth it must have access to huge and ever-growing supplies of mineral materials at lowest possible cost. Adequate supplies of mineral materials and wise usage of mineral resources have always been among the most important determents of a nation's survival The importance of access to adequate mineral supplies is increasing every year and this has significant international, as well as national, implications because of the unique locational characteristics of mineral resources. It is generally acknowledged that no particular type of natural resource is essential to a high level of national income or to economic progress. A country's endowment of natural resources need not exercise a determining influence on the course of its national income over time, provided it is able to trade. What is required for economic progress is the availability of a substantial quanti-

Jan 1, 1976

By R. D. Schoone, J. T. Michalak

Recovery, recrystallization, and texture development of a cold-rolled aluminum-killed steel have been studied during simulated box annealing. Two different initial conditions existed prior to cold rolling: 1) essentially all of the nitrogen in solid solution and 2) most of the nitrogen precipitated as AlN. The combined effect of nitrogen and aluminum in solid solution before annealing was to inhibit recovery and sub-grain growth at temperatures above about 1000°F and to raise the recrystallization temperature range on continuous heating at 40°F per hr from 1000"-1050°F to 1065"-1085°F. For the material with nitrogen and aluminum initially in solution there was an inhibition in the nucleation of the (001) [110] texture component and an enhancement of the (111) [110] texture component. The differences in annealing behavior mzd texture development are attributed to preprecipitation clustering of aluminum and nitrogen at subboundary sites developed by prior cold working. THE annealing of cold-worked aluminum-killed steels has been the subject of numerous investigations.'-'2 These studies have been concerned with kinetics of recrystallization, with microstructure and texture development, and with the individual and combined effects of composition, thermal history prior to cold rolling, and heating rates during subsequent annealing. It has been shown that the inhibition of recrystallization, and the development of the pancake-shaped grain and recrystallization texture characteristic of aluminum-killed steels, can be associated with the precipitation of A1N particles during a recrystallization anneal involving heating rates in the range 20" to 80°F per hr. If the AIN is precipitated before cold rolling or if more rapid heating rates are employed, the cold-rolled steels recrystallize more rapidly to an equiaxed grain structure and texture comparable to that of rimmed low-carbon steel. The retardation of recrystallization, the development of the elongated grain structure, and the pronounced (111) texture have been attributed to: 1) precipitation of A1N at prior cold-worked grain boundaries to form a mechanical barrier to grain boundary migration;' 2) precipitation on the boundaries of the growing recrystal-lizing grains as well as on cold-worked grain boundaries;'" and 3) preprecipitation clustering or precipitation on subboundaries to retard recovery, nucleation, and growth. The present study was undertaken to study in more detail recrystallization and texture development during commercial box annealing of cold-rolled aluminum-killed steels. Comparison of the annealing be- havior after cold rolling, for two different conditions prior to cold rolling, was made in an attempt to define more clearly the role of aluminum and nitrogen in forming the recrystallization texture. A) MATERIAL AND PROCEDURE The material used in this investigation was a commercial low-carbon aluminum-killed steel which was hot-rolled with a finishing temperature of about 1565"F, then coiled at about 1020°F. The composition, in wt pct, was: 0.050 C, 0.30 Mn, 0.007 P, 0.019 Si, 0.03 Cu, 0.02 Ni, 0.02 Cr, 0.045 Al, and 0.004 N. Two 4.5 by 13 by 0.078 in. sections were cut from the center section of a hot-rolled panel and one of these was reheated to provide two different conditions prior to cold rolling: low AlN: as commercially hot-rolled, with aluminum and nitrogen in solid solution; and high AlN: as commercially hot-rolled, then reheated at 1300°F for 3.5 hr to precipitate most of the nitrogen as AlN. ~etallc&a~hic examination indicated that the reheating did not change grain size nor carbide distribution (some spheroidization of pearlite was noted). Texture analysis at half-thickness level showed that both sections had the same substantially random as-hot-rolled texture. The results of check chemical analysis of each sample are given in Table I. Both sections were cold-reduced 65 pct on a laboratory rolling mill to a final thickness of 0.027 in. Cold rolling, in one direction only, was in the direction of the prior hot rolling. Specimens 1.0 by 1.25 in. were cut from the cold-rolled sheets and given a simulated box anneal in an atmosphere of 2 pct HZ-98 pct He. Specimens were heated at a constant rate of 40°F per hr from room temperature to various temperatures in the range 750" to 1300°F and cooled immediately by withdrawal to the water-cooled end of a tube furnace. The temperature in the 6-in. uniform hot zone of the furnace was controlled within 3"F. Selection of the individual specimens was made to give a random distribution of annealing temperatures with respect to location in the cold-rolled sheet. At least two specimens of each condition were annealed to the same temperature and smaller specimens for light microscopy, transmission electron microscopy, and X-ray studies were prepared from each of these. Rolling-plane sections for each of these studies were taken at half thickness. Light microscopy and transmission electron micro-

Jan 1, 1969

By E. S. Tankins, G. R. Belton

A simple solution model, based upon the formation of molecular species, is developed for strongly electronegative dilute solutes in liquid binary-metallic solvents. Two approximations are considered for the relative concentrations of the species: the random and the quasi-chemical. Equations are presented for the partial molar free energy, enthalpy, and entropy of mixing of the solute. An experimental study has been made of equilibrium in the reaction H2 6) +0 (dissolved) = H2O(g))for the liquid Cu-Co alloys. The standard free energy of solution of oxygen is presented as a function of composition for the alloys at 1550°C and as a function of temperature for five of the alloys. The experimental results for these alloys and also for Cu-Ni alloys are shown to be in reasonable agreernent with the theory in the random approximation. A knowledge of the thermodynamic behavior of dilute solutes in liquid metals and alloys is of importance in understanding and designing refining and alloy-making processes. Accordingly, several attempts have been made to derive suitable solution models to forecast the effect of a third component on the activity coefficient of such a solute in a metal. Alcock and Richardson' reviewed the literature prior to 1958 and also showed that a regular solution model gave a reasonable description in the case of metallic solutes but failed to account for the behavior of the more electronegative solutes sulfur and oxygen. These same authors2 later modified their model by using the quasi-chemical approximation3 to calculate the average composition of the first coordination shell surrounding each solute atom. This modified model was shown to lead to a better qualitative description of the behavior of the electronegative solutes; however, quantitative agreement with experimental data for oxygen in alloys could only be achieved by assuming a very small coordination number. The authors concluded that the major source of error in the model was the assumption that pairwise interaction energies were independent of composition. Substitutional and interstitial random solution models by Wada and saito4 are essentially similar to the first model except that the required interchange energies were derived from the modified solubility parameter equation of Mott, instead of from experimental binary data. Most recently Hoch5 has presented a statistical model for interstitial solutions and has applied the model to the Fe-C-O system. However, as the various interaction energies needed in the model had to be derived from the ternary data, the model does not promise well as a means of forecasting ternary behavior. Each of the above models carries the assumption that the strongly electronegative solutes have the same configurational environment as metallic solutes; i.e., the solute can be treated as a substitutional or interstitial atom in a quasi-crystalline lattice and is surrounded by a normal coordination shell of solvent atoms. There are, however, a number of facts which suggest that this is unlikely. First, the heats of solution are large, being more typical of molecule formation rather than alloying. For example, the heats of solution of monatomic oxygen and sulfur in liquid iron are -90 kea16,8 and -74 kea1,7, 8 respectively. These are to be compared with maximum heats of solution of metallic solutes in liquid iron of about -13 keal (silicon is an exception with -28.5 kea17). The large depression of the surface tension of liquid iron by trace amounts of the electronegative solutes oxygen, sulfur, and selenium9 suggests, by analogy with aqueous systems, the possible existence of polar molecules in the liquid. The effect of these solutes is at least three orders of magnitude greater than normal metal solutes.10 As has been pointed out by Richardson,11 the electron affinities and ionization potentials of oxygen and sulfur are such that it is likely that they exist in metallic solution as negatively charged ions. If this is so, and it is assumed that electrostatic forces play an important role in determining the configuration, it is unlikely that the stable configuration will be that of an isolated ion surrounded by a symmetrical coordination shell of solvent ions. It is more likely that the energy of the system would be lowered by the formation of solute-solvent screened dipoles. The above arguments suggest the formation of "molecular species" between solute and solvent atoms. The idea of the existence of molecular species in such solutions is not new, however', for Marshall and chipman12 have explained in a semi-quantitative manner the C-O equilibrium in liquid iron by postulating the species CO. Chen and Chip-man13 interpreted their measurements on the Cr-O equilibrium in iron in terms of the species CrO. Zapffe and sims14 have also postulated the existence of such species in liquid-iron alloys.

Jan 1, 1965

By Ian MacGregor

As I drove in from the airport on Sunday somebody said 'On the right you will see Duntroon, which is the military training school of Australia.' So I asked the driver, where did they get that name? 'Oh,' he said, 'from some people who built a house there. That was it's name- Duntroon.' It strikes a note with me because, that's the name of a 12th century castle on the west coast of Scotland where I spend what leisure hours I have and, therefore, it establishes the long connection between Australia and my native land. There is also a story I should tell you about the oil industry and its upsurge in Scotland recently which has resulted in great prosperity. And in Edinburgh, the walls of the banks are bulging-because of the incursion of foreign exchange and other resources. Charlotte Square, as some of you know, is the centre of the Scottish financial world and at one of the corners of Charlotte Square, where ho streets intersect, there are three stores-three emporia on the ground floor. Two of them at opposite corners are banks: The Royal Bank of Scotland, and not to be beaten by that, The Bank of Scotland. But the third building is occupied, or was occupied, by a furniture store over many years-very high-grade, high quality furniture that the elite of the Edinburgh society always supported. And suddenly, the store was cleared out and in came a bunch of carpenters and other people busily engaged in rebuilding the store, and finally the new tenants arrived on the scene.

Jan 1, 1978

By C. V. Millikan

THE year 1930 in the petroleum industry has been characterized by the establishment of large potential production of crude oil. This has resulted in closer cooperation between companies by proration and unit operation agreements in order to afford an equitable outlet to all, and to prevent a flood of oil being forced on the market with attendant tremendous material and economic waste. Drilling wells in proved areas and wildcat wells are fewer than in the past several years. Restricted production and low prices have caused greater effort to increase producing and recovery efficiencies. Increased refinery efficiencies have amplified the effect of overproduction. Pipe line departments have been especially busy. New oil lines have reached more refineries by new and shorter routes. Establishing greater gas reserves by new fields has justified new gas lines to industrial centers, and has brought this fuel to thousands of new domestic consumers. Two long gasoline lines, a new venture in pipe lines, are being built to obtain a lower cost of transportation and less loss between the refineries and their distribution centers. The chairmen of the various divisions have discussed the developments of their respective branches more fully in the following reviews.

Jan 1, 1931

By H. W. Gillett

Unlike most previous Howe lecturers, I had not the good fortune to be associated with Henry Marion Howe, nor to be directly one of his students. Yet, through his writings, he has been my teacher, as he has of all American metallurgists. Instructive as his writings are—I use the present tense because Howe thought so keenly and reasoned so surely, seeing clearly, as if by intuition, what was hazy to lesser minds, that his writings are still vital—it is not those books and papers, nor even the minds he trained in his classes, that were his most outstanding service. It was the spirit of Howe in his approach to the problems of metallurgy, his broad-mindedness and fairness, his recognition of the need for theories and hypotheses to explain metallurgical phenomena, his willingness to use them as servants, as well as his questioning attitude—his refusal to accept them as masters—that comprise his greatest service. This most thoroughly warrants the honor the Institute pays each year to his memory. These traits I so respect and honor in any man that I glory in this opportunity to do reverence to him in whom they were so notably united. Howe's Discussion of a Creep Problem I have often wished that Howe were still with us to turn his keen insight upon the problems of the use of metals at high temperatures, a field much studied but still very hazy. Indeed, 53 years ago, in a paper1 before this Institute, Howe stated a problem closely allied to some that still perplex metallurgists and engineers dealing with the high-temperature field. Howe was intrigued by a report2 from another old master, Robert Henry Thurston, on the behavior of annealed vs. cold-drawn iron wire, and in order to broaden the foundation for metallurgical generalization, Howe made experiments of his own on copper and silver. In these tests by Thurston and by Howe, the wires were rapidly loaded to determine the

Jan 1, 1939

By H. W. Knott, M. H. Mueller

The crystal structures of Ti2Cu, Ti2Ni, Ti4Ni2O, and Ti4Cu20 have been determined using powder specimens examined by X-ray and neutron diffraction. Lattice constants have been determined for all four phases using X-ray powder diffraction films. Atom positional parameters of all four phases have been determined from observed neutron intensities. X-ray diffraction calculated intensity data have been presented also for the phase Ti2Cu to point out the particular suitability of neutron diffraction in this case. Interatomic distances have been determined using the positional parameters obtained from neutron diffraction. ALTHOUGH some investigations of the crystal structures have been made of these four compounds previously,'-13 it was the purpose of the present investigation to expand the previous work in order to locate the various atoms, determine their coordinates, and to confirm or to correct some of the previous work. It was convenient to group these four compounds together since they are related chemicallv and/or structurally. The compound Ti2Cu is tetragonil; and Ti2Ni, Ti4Ni2O, and Ti4CU2O are all large fees of the same space group. Ti2Cu has been previously reported as a fee phase by Laves and Wallbaum;1 and Rostoker2 which was possibly the oxide phase, Ti4Cu20. Joukainen, Grant, and Floe;3 and Trzebiatowski, Berak, and Ramotow-ski4 have also reported a phase of this composition. karlsson5 has reported a small fct phase of the composition Ti3Cu which may be the presently discussed Ti2Cu phase. More recently Ence and Margolin6 have reported a small fct phase for Ti2Cu and the present authors7 together with Nevitt8 have briefly reported it to be a bet related to the fct with a co three times the length of the co of the fct and have also reported that this phase has a very limited composition. Further refinements will be reported which have varied some of the parameters of this bct structure slightly. Ti2Ni has been reported as a fee phase by Laves and wallbaum;1 Duwez and taylor;9 Rostoker;2 Poole and Hume-Rothery;10 and Yurko, Barton, and parr.11 In a later paper Yurko, Barton, and parr12 have given the complete structure of this phase based on an X-ray diffraction study which was independently confirmed with neutron diffraction by Mueller and knott.7 Additional crystal structure information will be given. Ti4Ti2O, Ti4Cu2O, and a number of other compounds including Ti4Fe2O have been reported as fcc phases by Rostoker,2 and more recently Nevitt13 has confirmed the Ti4Ti2O phase. Rostoker,2 however has reported diffraction lines for Ti4Fe2O which do not have all odd or all even indices. These lines, therefore, cannot be observed if this compound has a fee structure. This same error has crept into the diffraction results reported for TiNi2O and Ti4Cu20 in the ASTM powder data which has been credited from Rostoker's data. Complete crystal structures of these two phases will be presented. Although all four of these structures have large unit cells and hence do not lend themselves for completely resolved neutron powder patterns, a sufficient number of individual reflections was observed for solving the structure. They also serve as good examples of some of the advantages to be gained by using both neutron and X-ray diffraction techniques. EXPERIMENTAL PROCEDURE All of the alloys were prepared by arc melting. The starting metals had the following purity: Cu 99.999 pct, Ni 99.83 pct, and Ti 99.92 pct. Oxygen was introduced into the two oxide phases as chemically pure TiO2, with the remainder of the titanium coming from the above mentioned metal. All of the sample buttons were annealed in evacuated Vycor tubes, the two binary phases for 5 days at 700°C and the two oxide phases for 3 days at 900°C. Oxygen analyses were performed on all four phases by two independent laboratories with the following amounts of oxygen present in atomic percent; Ti2Cu-0.06, Ti2Ni-1.03, Ti4Ni2O-13.95, and Ti4Cu20-13.87. The stoichiometric amount for the oxide phases is 14.29 at. pct. Since all of the samples were very brittle they were easily reduced to a powder for diffraction measurements. The lattice constants given in Table I were determined for the four compounds from X-ray diffraction patterns of powder samples exposed to filtered copper radiation using a 114.59 mm diam Debye-Scherrer type camera using the Straumanis loading. None of the patterns showed a detectable amount of a second phase. The lattice constants were obtained from an IBM 704 computer program employing a least squares treatment with systematic correction terms as previously reported.14

Jan 1, 1963

By D. J. McAdam, G. W. Geil, R. W. Mebs

As shown in previous papers by the authorsg-17t the resistance of a metal to fracture, like its resistance to plastic deformation, is a function of all three principal stresses. A technical cohesion limit is the technically determined resistance to fracture under a specific stress system. The technical cohesive strength thus comprises an infinite number of technical cohesion limits corresponding to the infinite number Of possible com-binations of the principal stresses. The technical cohesive strength, therefore, may be represented by a surface in a diagram with the three principal stresses as coordinates. As shown in previous papers,'-'' the technical cohesive strength increases with plastic deformation, with decrease in temperature, and with increase in the strain rate. The technical cohesion limit, therefore, is affected by the same factors that affect the flow stress,$ namely, the stress system, plastic deformation, temperature, and the strain rate. More- over, the influence of each of these factors on the technical cohesion limit has been shown to be qualitatively similar to the three of the same factor on the flow stress.9-18 Advance of knowledge about the conditions determining fracture of metals has been retarded by the reluctance of some investigators to abandon preconceived ideas about how metals ''should,, behave. The incorrect idea is still prevalent that the conditions determining resistance to fracture are very different from those determining the flow stress. Attempts are still being made to express resistance to fracture in terms of a single parameter, such as a limiting value of the greatest principal stress, the maximum shearing stress, or the volume stress (one-third the algebraic sum of the three principal stresses). In these attempts, a sharp distinction is sometimes made between a ductile or ,plasticdeformation, fracture,, and a "brittle frat-ture.H In making this distinction, however, the meaning attached to the term "brittle fracture" sometimes is not made clear. The term could mean fracture after very little plastic deformation or it could be used to designate the type of fracture. An ordinary fracture of a ductile metal at room temperature starts as a cleavage, generally transverse to the direction of the greatest principal stress, but eventually changes to a shearing fracture' In some conditions, however, the metal fractures entirely by cleavage, with no evidence of plastic deformation during the fracture; the surface of such a fracture may have a

Jan 1, 1948

By R. W. Mebs, G. W. Geil, D. J. McAdam

As shown in previous papers by the authorsg-17t the resistance of a metal to fracture, like its resistance to plastic deformation, is a function of all three principal stresses. A technical cohesion limit is the technically determined resistance to fracture under a specific stress system. The technical cohesive strength thus comprises an infinite number of technical cohesion limits corresponding to the infinite number Of possible com-binations of the principal stresses. The technical cohesive strength, therefore, may be represented by a surface in a diagram with the three principal stresses as coordinates. As shown in previous papers,'-'' the technical cohesive strength increases with plastic deformation, with decrease in temperature, and with increase in the strain rate. The technical cohesion limit, therefore, is affected by the same factors that affect the flow stress,$ namely, the stress system, plastic deformation, temperature, and the strain rate. More- over, the influence of each of these factors on the technical cohesion limit has been shown to be qualitatively similar to the three of the same factor on the flow stress.9-18 Advance of knowledge about the conditions determining fracture of metals has been retarded by the reluctance of some investigators to abandon preconceived ideas about how metals ''should,, behave. The incorrect idea is still prevalent that the conditions determining resistance to fracture are very different from those determining the flow stress. Attempts are still being made to express resistance to fracture in terms of a single parameter, such as a limiting value of the greatest principal stress, the maximum shearing stress, or the volume stress (one-third the algebraic sum of the three principal stresses). In these attempts, a sharp distinction is sometimes made between a ductile or ,plasticdeformation, fracture,, and a "brittle frat-ture.H In making this distinction, however, the meaning attached to the term "brittle fracture" sometimes is not made clear. The term could mean fracture after very little plastic deformation or it could be used to designate the type of fracture. An ordinary fracture of a ductile metal at room temperature starts as a cleavage, generally transverse to the direction of the greatest principal stress, but eventually changes to a shearing fracture' In some conditions, however, the metal fractures entirely by cleavage, with no evidence of plastic deformation during the fracture; the surface of such a fracture may have a

Jan 1, 1948