By S. M. Purdy

Under certain conditions of hot rolling and air cooling from the hot-rolling temperature, bars of a high carbon (0.40 pct C) chrome-nickel austen-itic alloy were found to show magnetism even though no ferrite or martensite could be detected by microscopic or X-yay methods. The appearance of magnetism in such alloys may come from chromium impoverishment of the austenite grains near the precipitated carbide particles. SPORADICALLY, hot-rolled bars of Silchrome 10, an exhaust valve steel, have been found to be magnetic. Because of the analysis of the alloy—0.40 pct C, 18 pct Cr, 8 pct Ni, 3 pct Si —magnetism is unexpected. Preliminary investigation showed neither martensite nor ferrite to be present; only austenite and Cr23C6. Since a literature search was fruitless, a brief study was made of the appearance of magnetism in this alloy. The only basic difference between the two heats is the nitrogen content. Permeability was measured using a Severn magnetic gauge. This instrument consists of a magnet mounted on a counterbalanced arm. A set of calibrated plugs is placed in contact with one pole of the magnet. The specimen is placed close to the other pole of the magnet. If the specimen pulls the magnet away from the plug, it has a permeability greater than that marked on the plug. This technique is swift and reproducible. Previous experience has shown that the permeabilities obtained corresponded to those obtained on a permeater with a field strength of 100 oe. Specimens from both heats were annealed at temperatures between 1700 and 2300°F. One set of specimens was water cooled and another furnace cooled. All the water-quenched specimens were non-magnetic; the furnace cooled ones were magnetic as shown in Table I with no difference being observed between the two heats. Microstructural examination of the specimens showed the expected increase in carbon solubility with increasing temperature. Carbide solution was complete at 2200°F. The specimens heated to 1900°F or below showed some carbide precipitation from the hot-rolled structure. A furnace cooled specimen from a given temperature showed less carbide out of solution than the water-quenched specimen from the next temperature below; e.g., the specimen furnace cooled from 2100°F showed less carbide out of solution than the water-quenched specimen from 2000" F. These studies indicated that the appearance of magnetism was not related to the quantity of carbon in or out of solution and it was related to precipitation at temperatures below 1700" F. A set of samples annealed and water-quenched from 2100° F was aged for 4 hr at temperatures between 1000" and 1600°F; all were non-magnetic. A second set of samples, similarly annealed, was aged 1 to 24 hr at 1200°F with the results shown in Table II. None of the latter set of specimens showed magnetism until they had been aged about 8 hr. Magnetism was quite strong after aging 24 hr. X-ray diffraction studies on several of the magnetic specimens showed that the austenite had a lattice parameter of 3.58A and that the carbide was Cr23C6. Several of these samples were electrolytically digested in 10 pct HCl in ethanol, with a current density of 0.1 amp per sq cm. None of the particles in the residue were magnetic. Accidentally, one cell was run at 1 amp per sq cm; e.g., magnetic particles were found in this residue. After careful separation, the magnetic particles were mounted on a quartz fiber and their diffraction pattern determined using a 5.73-in. Debye-Sherrer camera with CrK radiation. These particles showed a fcc structure with a lattice parameter of 3.57A. Prolonged exposure, up to 16 hr, produced no other lines on the film. The following facts seemed to be established at this time: 1) Austenite was the magnetic phase. 2) Neither ferrite nor martensite could be detected. 3) Magnetization could be produced by aging at 1200°F. One explanation of these data is that the carbide precipitation impoverishes the region immediately around the carbide particle of carbon and chromium and increases the proportion of nickel. All of these serve to increase the Curie temperature of the region around the carbide particle. If the composition change is enough, the Curie temperature will rise above room temperature. If the volume of the affected region is great enough, the magnetism will become detectable. At low aging temperatures, composition changes are great enough but the overall volume of impoverishment is quite small

Jan 1, 1962

By Donald Warren, J. F. Libsch

HIS investigation originated as a result of a pre-vious experimental study' of the magnetic properties of Fe-Co alloys fabricated by the powder metallurgy technique. Densities of powder compacts prepared for the magnetics investigation varied from 7.45 to 7.70 g per cu cm or from 93 to 95 pct of the experimental value of 8.08 g per cu cm for a fused alloy of the same composition.' While this range of density is considered sufficiently high for most applications, the highest possible density is to be desired for maximum magnetic properties. By applying a technique similar to the one described above to a pure electrolytic iron powder, Rostoker³ was able to achieve a density of 7.895 g per cu cm, which is the highest density ever reported for sintered iron. While Rostoker's work involved the sintering of an elemental powder rather than a mixture, it was believed that higher densities should also have been obtained for alloys using the above technique because of the recoining operation and the high sintering temperature. Consequently, it was decided to investigate the various factors affecting the density of this alloy with the idea that such a study might lead to higher densities and, as a result, powder alloys having magnetic properties identical with those of the fused alloys. It was believed that the principal reason that near-theoretical densities for the powdered alloy were not obtained was the interference of gases with the normal sintering mechanism. When present during the sintering operation, gases can exert several harmful effects: they can remain on the particle surface and interfere with surface diffusion and plastic flow; they can be released and, under certain conditions, expand the void spaces through gas pressure; or they can remain trapped in the pores and exert a hydrostatic pressure that retards elimination of the pores. Jones,4 Rhines,5 Goetzel," and others have given the effect of gases in the sintering of powder compacts an extensive treatment. Among the more important sources of gases in the sintering process are dissolved gases, adsorbed gases, air entrapped during pressing, and gaseous products of chemical reactions. During sintering adsorbed gases are partly released at a relatively low temperature, while those gases entrapped during pressing cannot escape until their pressure is increased sufficiently through increasing temperature to expand the interpartjcle openings. The remaining adsorbed gases, gaseous reduction products, and dissolved gases produce a similar effect at the higher temperatures. If, in the sintering process, gas evolution occurs after the interpore channels have been sealed, an exaggerated expansion of the void spaces results. This is particularly true if the temperature is high enough for extensive plastic flow. In his fabrication of powder bars from tantalum, Balke7 had to consider the effect of adsorbed hydrogen and provide for its escape during sintering by limiting the compacting pressure to a maximum of 50 tons per sq in. The effect of gases entrapped during pressing was first noted by Trzebiatowski8 when he found that gold and silver powders decrease in density with increasing sintering temperature if pressed at 200 tsi, while they exhibit the usual increase when pressed at 40 tsi. Recent investigators9-11 have also noted that entrapped gases have an effect on the expansion of copper compacts during sintering. Proper provision for the escape of gaseous products of reduction must be made in order to avoid deleterious effects. Myers" states that in the sintering of electrolytic tantalum powder, the temperature was gradually raised to 2600°F with a pause at 2000°F to permit reduction of the oxides. Experimental Details For the present study, 50 pct Co-50 pct Fe compacts in the form of circular disks 1½ in. in diam and 0.15 in. thick were fabricated by the pressing and sintering of a mixture of the elemental powders. It was decided to follow the sintering process by means of liquid permeability measurements, because it was thought that such measurements might serve as a measure of relative pore sizes, as well as a possible indication of the point at which most of the interpore channels become sealed. However, since the permeability as measured by the flow of a liquid, such as ethylene glycol, does not give an absolute indication of the point where the pores have become isolated, a method for determining the percentage of pores connected to the surface was set up. As an additional cross check on the permeability measurements, metallographic methods were used to study the relative pore size. Finally, the property of ultimate interest, the density, was measured. Raw Materials: The powders used consisted of an annealed, 99.9 pct pure, —150 mesh grade of electrolytic iron powder, and a 98 pct pure, —200 mesh grade of reduced and comminuted cobalt powder. The cobalt powder was not further processed either by hydrogen reduction or annealing. The screen analyses for the iron and cobalt powders are given in Table I, while the chemical analyses for each type of powder are listed in Table 11. Table 111 gives the hydrogen loss measurements for the powders according to the M.P.A. Standard Method and for a higher temperature as well. Preparation of Compacts: Equal amounts of the elemental powders were mixed by rotation for 1 hr and then pressed into compacts approximately 0.15

Jan 1, 1952

By A. B. Stickney

UPWARDS of 200,000 engineers in this country are sufficiently interested in engineering as a profession to have joined a society, but not over 10% of them belong to any one society. There is a widely-felt need of an over-all organization of all the societies to act as spokesman for all engineers on matters of common concern. On a local basis, over 100,000 engineers in 35 metropolitan areas have organized themselves into local councils, and are doing an effective job of intersocietal co-operation within their sphere of activity. In the last few years much has been said and written about a similar organization on a national scale. Everybody wants iteverybody is talking about it-it's in the air-it's coming-it's inevitable. Although it is no longer necessary to talk about why or whether there should be such an organization, there is no such unanimity about what it should be like. This paper outlines a proposed organization by answering four questions-who, how, what, and who will pay for it.

Jan 1, 1946

By W. E. Keck

THE flotative properties of the principal minerals in Michigan's potential iron ores have been investigated to develop methods of bene-ficiation for the ores. One of these minerals, magnetite, is of considerable importance as a source of iron. Study of its flotation was similar to that of hematite1, another iron mineral in these potential ores. The present research consisted essentially of: (1) a survey of the literature on mag-netite flotation, (2) the preparation of pure magnetite, (3) the develop-ment of laboratory procedure and (4) flotation experimentation. Literature an Magnetite Flotation.-For the purpose of this discussion, the results of previous work on the flotation of magnetite can be sum-marized as follows. The mineral has been floated with pine oil2, and it has also been separated from synthetic mixtures with silicates by the use of the same reagent2. Magnetite and apatite in iron-ore slimes have been separated by flotation of apatite with sodium palmitate3. These data were utilized in the present investigation. Preparation of Magnetite.-The pure mineral was prepared from the magnetic-separator concentrate of an iron ore (obtained from the Wither-bee Sherman Corporation, Port Henry, N. Y.). This concentrate was slowly comminuted with laboratory rolls and pulverizer to pass 65 mesh and was then tabled several times. Tabling yielded a relatively coarse magnetite concentrate, tailing and slimes. The two latter materials were rejected insofar as the present work is concerned, and treatment of the magnetite (table concentrate) was continued by separating it into -65 + 200 and -200-mesh sizes. Separation of the sizes was made by first dry screening and then wet screening. The -200-mesh material was rejected to eliminate possible introduction of error into flotation

Jan 1, 1937

By Charles Hardy

ACTIVATED alumina is an aluminous material which may be 1 classified chemically as a partially dehydrated aluminum trihydrate having a high porosity and a perma¬nent physical structure. In general, it may be employed effectively and economically for the complete removal of water vapor from gases and vapors; for the selective adsorption of certain as especially those of the higher boiling points, and as a catalyst or catalyst carrier. Other forms of alumna are available and may be employed similarly but not so effectively nor can reactivation be accomplished with uniformity over many cycles without deterioration. The adsorption-reactivation cycle of activated alumina can be repeated many times without any apparent depreciation ill

Jan 1, 1934

By W. R. Ingalls

THE paramount subject of interest and concern at the present time is the readjustment in economic conditions following the cataclysmic disturbance produced by the war and the misconceptions leading to an orgy of extravagance that prevailed during two years following the armistice he, time is too short for me to undertake to review the nature and extent of the upheavals occurring between August, 1914, and October, 1920. Bulky volumes will be written about them. . But I shall have to refer to some of the results in order to outline a prognosis. It is the future, not the past;' that is of most interest to us. Let me be so bold as to say, without further preface, that I am not optimistic as to the near future. .We shall, indeed, have revivals in trade, but they will be delusive if their nature be not 'understood. We shall build hopes and expectations upon political maneuvers and events, only to find in the end that they were folly. In the meanwhile fundamental economic influences will continue to exert their steady and irresistible pressure. The new administratiow at Washington has no magic wand with which to kindle the fires in our idle steel furnaces, or create a million new houses for the people; nor can the premiers of Europe put into motion the spindles of the cotton and woolen mills, or by any incantations compel the people of the Orient to buy goods. The people of the Orient, and of, Europe, and of the two Americas are in the grip of the same economic forces. The readjustment has proceeded further in some parts of the world than in others. In the United States I do not think we, have gone more than over the threshold. I shall tell you why 1 think thus, but in telling you I shall be limited, in view of the immensity of the subject, to a series of bald statements, without much elucidation.

Jan 1, 1921

By John Wulff, J. H. Hollomon

Service failures in brass condenser tubes are often due to corrosion. One of the commonest types of corrosion reveals a surface structure of redeposited copper.' The study of the effect of alloy addition agents in preventing this kind of corrosion has received impetus from the extensive publication of Bengough and May.2 The mechanism of such inhibition gauged from immersion corrosion,2 cell corrosion,3 and electrolytic potential4 measurements is controversial. This controversy may be attributed in part to a lack of definite knowledge5 of the actual nature of the initial films formed in corrosion experiments. In our own corrosion work on copper and 70-30 brass this lack became apparent and necessitated an examination of surface films by X-ray and electron diffraction methods. The present paper is but an introduction to the subject of inhibition and reports the structure of films formed in active corrodents. Experimental Procedure The arsenical coppers and brasses used in this investigation were made by one of the writers* in the plant of the Revere Copper and Brass Co. at Rome, N. Y. Standard commercial melting practice was followed. O.F.H.C. copper and electrolytic zinc were used and all arsenic additions were made by additions of a master copper alloy. The final analyses are given in Table I. Likewise, the extrusion, cold-rolling, and intermediate anneals employed followed standard usage. Final heat-treatments were given to all materials to produce a similar grain size (0.035 to 0.045 mm. for brass and 0.015 to 0.025 for copper) for the alloys containing various percentages of arsenic. Samples 1/2 by M by 1/4 in. were cut from sheet material resurfaced and finished with 0000 metal-lographic papers. The surfaces were all degreased in alcohol and benzine before immersion. After immersion in the corrodent, they were washed gently in tap water, dipped first in alcohol and then in pure benzine and allowed to dry in the diffraction apparatus. The reflection electron diffraction apparatus used has been described by Burwell and Wu1ff.6 Fig. I is typical of the photo-grams obtained. The X-ray apparatus was

Jan 1, 1941

By John Wulff, J. H. Hollomon

Service failures in brass condenser tubes are often due to corrosion. One of the commonest types of corrosion reveals a surface structure of redeposited copper.' The study of the effect of alloy addition agents in preventing this kind of corrosion has received impetus from the extensive publication of Bengough and May.2 The mechanism of such inhibition gauged from immersion corrosion,2 cell corrosion,3 and electrolytic potential4 measurements is controversial. This controversy may be attributed in part to a lack of definite knowledge5 of the actual nature of the initial films formed in corrosion experiments. In our own corrosion work on copper and 70-30 brass this lack became apparent and necessitated an examination of surface films by X-ray and electron diffraction methods. The present paper is but an introduction to the subject of inhibition and reports the structure of films formed in active corrodents. Experimental Procedure The arsenical coppers and brasses used in this investigation were made by one of the writers* in the plant of the Revere Copper and Brass Co. at Rome, N. Y. Standard commercial melting practice was followed. O.F.H.C. copper and electrolytic zinc were used and all arsenic additions were made by additions of a master copper alloy. The final analyses are given in Table I. Likewise, the extrusion, cold-rolling, and intermediate anneals employed followed standard usage. Final heat-treatments were given to all materials to produce a similar grain size (0.035 to 0.045 mm. for brass and 0.015 to 0.025 for copper) for the alloys containing various percentages of arsenic. Samples 1/2 by M by 1/4 in. were cut from sheet material resurfaced and finished with 0000 metal-lographic papers. The surfaces were all degreased in alcohol and benzine before immersion. After immersion in the corrodent, they were washed gently in tap water, dipped first in alcohol and then in pure benzine and allowed to dry in the diffraction apparatus. The reflection electron diffraction apparatus used has been described by Burwell and Wu1ff.6 Fig. I is typical of the photo-grams obtained. The X-ray apparatus was

Jan 1, 1941

By Oliver C. Ralston, Foster Fraas

INTRODUCTION ELECTROSTATIC methods of separation are used only when some peculiar advantage is gained. Such cases are minerals that are not separable by differences in specific gravity or magnetic response and that are desired in particles as large as 10-mesh, a size on which flotation separation is inefficient. This paper covers several separations of this type and others. It includes studies in the electrostatic behavior of kyanite, sillimanite, and zircon, simple silicates that cannot be called either acid or basic but are more nearly neutral. Kyanite and sillimanite are both desired in 10-mesh size and are difficult to beneficiate from low-grade ores to give that type of concentrate. A separation of garnet from diopside was studied because this mixture had been removed from a wollastonite product by drying and magnetic separation, and no special or extra-preparation for electrostatic separation was necessary. THE SEPARATOR The separator used in these tests is of the nonhomogeneous field type shown in Fig I[a]. It consists of a 11.4-cm-diam rotating metal roll 2 at ground potential over which the dry mixture of minerals is fed. The roll serves as one electrode of the separating field, and the other electrode is that of 3, a smaller 5-cm-diam rotating metal cylinder which is held at a high direct-current potential. In this paper the term "electrode" will be confined to the electrode at 3, roll 2 being designated only as "roll." [ ]

Jan 1, 1947

By Donald L. Ball

The equilibrium of boron nitride, gaseous nitrogen, and solute boron was investigated in Fe, Fe-C, and Fe-Si rnelts by the Sieverts technique. The free ellergy of dissociation of boron nitride, involving -the implied standard states, was evaluated in the range 1400" to 1600°C as: ?Fo = 38,000 - 23.5T, cal ber mole The solute-solute interaction coefficients eBB, ecB , and eg were determined as 0.058, 0.22, and 0.078, respectively. BORON is an important ingredient in some types of steel and cast iron. It was employed at a particularly high level, 0.01 wt pet, in the as-cast malleable iron "CentraSteel".1 In this material, the boron concentration was critical in order to assure graphite, and avoid primary cementite, in the as-cast structure. One possible function of the boron in this alloy was the nucleation of graphite through the agency of boron nitride, which, conceivably, precipitated from the melt during cooling. A research program was instituted to assess the validity of this proposed mechanism. The first undertaking, reported here, was a determination of the thermodynamic possibility of boron nitride precipitation. Data available in the literature on the activity coefficient of solute boron in iron-base melts are inadequate for the present purpose. They will be reviewed briefly, however, so that comparison can be made, when

Jan 1, 1968

By G. Derge, W. Peifer, J. H. Richards

INTRODUCTION A WIDE variety of metallurgical defects in steel have commonly been attributed to the presence of excessive amounts of hydrogen. These defects include flakes in rails and forgings, cracks in welds, and blisters in enameled ware. They have been related to hydrogen largely by circumstantial evidence because the proper sampling and analysis of steel for hydrogen has been known to be difficult and because no general agreement has existed with regard to the relative suitability and accuracy of available methods. The need for a direct approach to these problems has been widely recognized. This general situation has been well described in the publications of the British Committee on the Heterogeneity of Steel Ingots,1 and current approaches to the problem were reviewed in a recent symposium of the AIME.12 The plans described by the present authors at that meeting have now matured satisfactorily and will form the basis of this paper. The principle object of this paper will be to describe the methods of sampling and analysis which have been developed and to illustrate the usefulness and limitations of these methods by citing their application to a specific problem. The first problem selected for investigation was the behavior of hydrogen in rail steel. This was chosen because the occurrence of shatter cracks in rails has received a great deal of study over a long period of time. The defect can be controlled by the expensive procedure of slow cooling. However, it may be hoped that a better understanding of the factors influencing the hydrogen content of rails will lead to a more efficient control of this problem. Rails provide a good starting point for a more general study of hydrogen in steel because they provide a cross section large enough to develop cracks, yet small enough for convenient handling and sampling. Rails were also selected because they are made from plain carbon steel and it was felt that the initial work should not be complicated by the effects introduced by alloying elements. The considerations which determined the original planning of this study should be reviewed. The inherently complex nature of most hydrogen problems requires that a large amount of data must be collected for any particular case. This in turn means that any analytical procedure should be as rapid and simple as possible. The same objective of speed is indicated by the fact that it may finally become desirable to use hydrogen analysis in process control. It is also known that hydrogen is highly fugitive and that any procedure which facilitates early analysis of the sample without prolonged or irregular storage has distinct advantages. The most important previously reported methods of analysis may be classified into three general groups: (I) Vacuum fusion. (2) Vacuum extraction (without melting). (3) Total combustion.

Jan 1, 1948

AARONS, J. BOYD, Major. AGNEW, FRANK VANS. ALLEN, HERMAN H., Private, D Co., 8th -Reserve Engineers. BAINS, THOMAS M., Major, Engineer Officers' Reserve Corps. BANKS, H. R., Lieutenant, Canadian Engineers, B. E. F. BARBOUR, PERCY E., Deputy Supt. (Captain), New York State Troopers; Captain, 22d Regiment, N. Y. N. G. BARLING, H. B., Ist Lieutenant', Engineer Officers' Reserve Corps. BIGELOW, BRAXTON. BLOOMFIELD, E. C., Lieutenant. , BORROW, F. K. BROCK, R. W., Major, 19th Reserve Battalion of Canadians. BROOKS, ALFRED H., Captain, Engineer Officers' Reserve Corps. BROWNE, DE COURCY, 1st Lieutenant, Ordnance Dept., Fortress Monroe, Va.

Jan 9, 1917

By Kichizo Niwa, Toshio Yokokawa, Mitsuo Shimoji, Yoshihiko Watanabe, Satoshi Kado

A LTHOUGH a systematic research on diffusion in liquid metals has not been carried out, partial studies have been developed by various workers in several systems. A few recent papers among them have shown that this line of approach is quite useful for understanding the structure of the liquid state. Furthermore, it has been found in kinetic

Jan 1, 1958

By Samuel Thomas

The specimen of anthracite coal which I hold in my hand, insignificant as it may appear to the casual observer, speaks volumes to me and to the initiated, as it suggests and represents the entire evolution of the use of anthracite coal in the manufacture of pig-iron, the growth and development of which it is my purpose to review here to-day. During our recent visit to the Mountain Copper Co.'s works at Keswiek, I picked up this piece of coal from a pile of anthracite lying in the yard, asked Mr. Edwards, the manager, a countryman of mine, where it came from, and, to my surprise and delight, discovered that it had been brought all the way from Wales, and had come out of the identical vein which my father opened near Yniscedwin, about eighty years ago. I had no idea, before this incident, of contributing to the already full and complete programme of the day; but, being requested by our distinguished President and Secretary to do so, I consented to relate here the story which this remarkable find naturally brought back to my mind.

Jan 1, 1900

By Albert F. Hill

The manufacture of structural shapes in steel of uniform quality, which shall command the full confidence of the engineer, is a problem in practical metallurgy which is beginning to attract much attention in this country. The progress of the past fern years in the improvement of plant and processes has placed it within the power of the steel-maker to supply a material of such chemical composition as will meet the requirements; but this solves only in part the difficulties of the constractor. It is well understood that the influence of shop manipulations is a most decisive one upon the mechanical properties of the finished product; in many cases so great, in fact, as to cause an entire transformation in the character of the material, and to render it unfit for the service for which it was intended. On the other hand, mechanical treatment is frequently resorted to as an efficient corrective of certain undesirable properties, which may be due either to chemical composition or previous manipulation. This understood and accepted, it is evident that careful investigation of the effects of mechanical treatment is fully as necessary to the successful use of steel in engineering structures, as the investigation of the influence exerted by its chemical composition. All structural material has to undergo more or less mechanical treatment, such as shearing, punching, upsetting, etc. Each of these operations produces effects which are far more marked and decisive in steel than they are in iron, and means must therefore be adopted to counteract, or at least to modify, these effects before the material is permitted to enter the structure. The fact that both shearing and punching affect the tenacity and elasticity of steel has long been recognized; bat, through more recent investigations, it has been established that these effects are purely local, and are therefore susceptible of correction by other and simpler means than annealing. The importance of this discovery to the use of steel in structures is very great. The impracticability of

Jan 1, 1883

By R. W. Diamond

THREE mills are now operated by the Consolidated Mining & Smelting Co. of Canada, Ltd.: (1) The Sullivan Concentrator, Chapman Camp, B. C. (near Kimberley, B. C.), (2) the, St. Eugene Concentrator, Moyie, B. C., and (3) the. Tadanac (Customs) Concentrator,Trail, B. C. Differential flotation is the only concentration method employed in all three plants. Tables are used for pilot work only. Values in all ores treated are as minerals of some or all of the metals -lead, zinc, gold or silver. Occasional customs ores contain small amounts of copper. Sulfide iron content of ores treated varies from a FIG. 1.-THE SULLIVAN CONCENTRATOR, CHAPMAN CAMP, B. C. (NEAR KIMBERLEY, B. C.). low figure in some ores to 38 per cent. iron in Sullivan ore. Gangue minerals vary considerably. A few customs ores are somewhat oxidized and as a result present difficulties. Flotation equipment and control are similar in the three mills, and the flow sheets at the St. Eugene and Tadanac mills, while much simpler, are modeled after that of the Sullivan Concentrator. In this paper I will not detail treatment nor equipment in any of our plants but will describe special features in, or in connection with, all of them. I will then deal with flotation reagents, describing our use of each of them, particularly where differing from general practice. I will conclude with comments on special subjects related to differential-flotation.

Jan 1, 1927

By D. S. Newton

Introduction Historically the production of zinc dust has been based upon residual and secondary zinc. Using horizontal retorts filled with diecasting scrap, galvanizers drosses and sweater billets, dust has been produced by condensation into static condensers on a 24 hour cycle. Although fairly flexible as regards input materials the process is not amenable to close control of the product, is labour intensive and unless carefully run can cause fume problems. With a steadily increasing demand for zinc dust of consistent properties and higher quality there is a demand for an improved method of manufacture in which dust can be produced continuously and which is capable of close control thus ensuring a minimum amount of oversize or unsaleable material. The Process in use in the works of Imperial Smelting Corporation (Alloys) Ltd. in England, and in Canada and Holland, satisfies the criteria stated above, and has proved to be easy to control with a minimum labour demand.

Jan 1, 1970

P. Herasymenko (New York University, New York) —The authors' experiments on equilibria between water vapor and liquid synthetic slags represent a valuable contribution to our knowledge of the nature of liquid slags. They can be regarded as a proof of ionic splitting of water molecules dissolved in slags. The assumption that water dissolved in slag was com- pletely ionized was made in my report on hydrogen equilibria in steelmaking as early as 194010. In that paper, the first systematic data were given on the content of ionized hydrogen in acid and basic open-hearth slags. The paper probably escaped the notice of the authors, although they mention the articles published later by other investigators who reported erratic and

Jan 1, 1958

By C. H. Jr. Herty

DURING the past few years frequent reference has been made to a certain type of iron known generally as "bad iron," "dirty iron," etc., both by steelmakers and producers of iron castings.1 Open-hearth operators have claimed that such iron was entirely within the specified limits as to ordinary analysis but it was difficult to make good steel from it. It has been suggested that unreduced material in the iron is responsible, also that most trouble is experienced with the iron when the blast furnace is delivering a product whose analysis is more or less variable. Other reasons suggested are the use of scrap or borings, unsintered flue dust in the burden, a cold hearth, too high a proportion of unsuitable grade of ore, or the form of the carbon in the iron. Accordingly, a subcommittee was appointed at the fall meeting of the Open-hearth Committee of the American Institute of Mining and Metallurgical Engineers held in Pittsburgh in October, 1926, to investigate the reasons for the occurrence of this bad iron and suggest methods for preventing its appearance. This committee enlisted the cooperation of the U. S: Bureau of Mines Experiment Station at Pittsburgh in undertaking a study of pig-iron quality as affecting the open hearth. The following is a report of the findings to date:

Jan 1, 1929

By C. Norman Cochran, James L. Brandt

ALTHOUGH gas in aluminum and its effect on aluminum products have been the subject of a number of papers, not many quantitative determinations of the hydrogen content of solid aluminum and its alloys have been recorded in the literature. For solid aluminum samples, four investigators have reported hydrogen contents which appear reasonable compared with the hydrogen solubility of 0.7 ml per 100 g, STP, in molten aluminum at 660°C established by Ransley and Neufeld' and verified by Opie and Grant' and Ransley and Talbot. Sloman," who used a vacuum fusion procedure, reported the hydrogen content of some high purity aluminum as 0.66 ml per 100 g, STP. Griffith and Mallett, employing the tin fusion method, reported the internal hydrogen content of six different aluminum alloys as ranging from less than 0.1 ml per 100 g, STP, for 1100 alloy to 0.7 ml per 100 g, STP, for 4043 alloy (previously 43S, a 5 pct Si alloy). Eborall and Ransley," using a solid extraction of the gases at 600°C, reported hydrogen contents ranging from 0.1 ml per 100 g, STP, to 1 ml per 100 g, STP. Ransley and Talbot reported that several thousand analyses on 99.2 pct and higher purity aluminum as well as Duralumin type alloys indicated hydrogen contents ranging from 0.1 ml per 100 g, STP, to 0.5 ml per 100 g, STP.

Jan 1, 1957