By Fred C. Bond

DISCUSSION Milton C. Shaw and Donald R. Walker (Massachusetts Institute of Technology)—For many years the two empirical rules of comminution bearing the names of Rittinger and Kick have been applied to grinding processes to account for the energy required to crush brittle materials. The basis for Rittinger's rule was the thought that the energy to grind a substance went largely into supplying the additional energy associated with the new free surface, while Kick's law was prompted by the concept of dimensional similarity and is a special statement of the concept of constancy of strain energy to cause rupture. According to Rittinger the energy to grind a given volume varies as the change in the square of the mean particle size, v - A (D2), while according to Kick this energy varies

Jan 1, 1953

By J. P. Denny

The constitution of the Ga-In system was determined by thermal methods. An experimentally determined metastable equilibrium line (an extension of the indium-rich liquidus) was obtained. The various alloys were studied metallographically using polished samples obtained by a casting method. These low melting alloys required a special dry-ice assembly to maintain a suitable temperature. RECENT interest in alloys that are liquid at room temperature has led to rather extensive investigation of gallium-base alloys. Widely distributed over the earth, gallium could be produced in substantially larger quantities than at present, if a significant demand existed.' One study' has established its presence in 12 out of 14 zinc blends, in all of 15 aluminum ores, in 4 out of 12 manganese ores, in 35 out of 91 iron ores, and in all of 7 magnetite ores. It occurs as a rule in minute amounts, however, leading to high extraction costs. Recent quotations run from $2.50 to $7.50 per g. During the course of the present investigation, portions of the system Ga-In have been redeter-mined, and the results of this study are presented herein. Thermal and metallographic methods have been employed. Lecoq de Boisbaudran, the discoverer of gallium, conducted the first investigation" on Ga-In alloys in 1885. The temperatures of incipient melting, and of completion of melting, were determined at four alloy compositions. In 1936, Hansen' constructed a eutec-tic-type phase diagram for the system Ga-In, based on . work. The existence of a Ga-In compound was regarded as improbable by Hansen, and subsequent investigations are in agreement. French, Saunders, and Ingle3 conducted a more complete study of the system in 1938, using thermal methods. Their phase diagram is a eutectic type, containing a unique concave-upward liquidus. The solid-solution range of gallium in indium was reported as 9.5 pct by weight, and that of indium as less than 1 pct, at the eutectic temperature. The eutectic composition, determined as being bracketed by the compositions showing a true horizontal at the eutectic temperature (16°C), was reported as 76 5-0.5 pct Ga and 24 i 0.5 pct In. Experimental Procedure The preparation of Ga-In alloys is simplified by the low melting points involved. Various compositions were prepared by melting in pyrex tubes, using a cover of distilled water or parafin to prevent the alloys from wetting the glass wall. In all cases, the melts were homogenized. by stirring. Where possible, both cooling and melting curves were determined. The extensive undercooling of gallium was found to prohibit a satisfactory cooling-curve analysis of gallium-rich alloys, however, and transition points on the gallium side of the eutectic could be determined only by melting curves. The inverse rate method of thermal analysis proved to be most satisfactory and was used to a great extent. Various heating and cooling rates were used, ranging from 0.2" to 5.0°C per min. Low temperature melting analyses were conducted within a constant temperature bath, maintained at about 70 °C. The alloys were solidified (under water or paraffin) within a pyrex tube, using dry ice; the tube was then sealed within a cold Dewar flask, the unit transferred into the constant temperature bath, and periodic temperature readings taken. The high temperature melting-curve determinations and all cooling-curve determinations were made in a vertical tube furnace. At near-eutectic compositions, the furnace was placed within a refrigerated room held at —20°C. Accordingly, the furnace on cooling approached —20°C asymptotically and permitted the determination of those phase transitions occurring below room temperatures. Temperatures were measured with a 30-gage iron-constantan thermocouple, immersed directly in the alloy. To prevent contamination of the melt, the leads and junction were coated with Lucite, applied by painting with a solution of Lucite in ethylene dichloride. Electromotive force measurements were made with a Leeds and Northrup precision potentiometer, type 8662. The couples were calibrated against the boiling point. of water and, at lower temperatures, against a calorimeter thermometer having a Bureau of Standards certificate. The melting points of gallium and indium used in the present investigation were determined as 29.-77° and 156.1°C, in good agreement with previously reported values of 29.78°C° and 156.4"C.' The spec-

Jan 1, 1953

By W. Rostoker

PART of a program of research on the Ti-A1 system1 involved a study of the lattice parameters of the titanium-rich a solid solution, which has a hexagonal close-packed structure. For this work, a 14 cm Debye-Scherrer powder camera and filtered CuK, radiation was used. For each pattern, the parameters were calculated by a least squares solution of the five strongest high angle lines. This provides an accuracy of i0.005A or better. The results are shown graphically in Fig. 1. It will be seen that an unusual change of slope occurs in the curve for the C parameter at high aluminum contents. Such anomalous changes in slope have been recorded by RaynorV or several magnesium-rich solid solutions. The effects were interpreted in terms of a special contribution to the lattice distortion due to factors of electronic origin predicted by Jones." Jones' theory, in substance, suggested that an unusually large expansion of the lattice would begin when the electron per atom concentration in the alloy was increased to a value at which an overlap just began from one Brillouin zone to another. Con-

Jan 1, 1953

By R. E. Collins, Paul B. Crawford

Mathematical equations have been derived to show the effect of the slippage phenomomenon (Klinkenberg effect) on unsteady-state gas flow through porous media. The assumption is made that the slippage may be represented by an equation of the type It is pointed out that most of the existing data on unsteady gas flow may be corrected for slippage by a simple change in definition of the dimen-sionless groups. INTRODUCTION Several solutions to the various problems associated with the unsteady-state flow of gas through porous media have been recently presented in the literature.','" The cited publications have resented solutions for flow under ideal conditjons. The principal assumptions involved include: (a) the density of the gas obeys the perfect gas law; (b) the viscosity of the gas is constant; and (c) the gas permeability is constant. Few, if any, actual gases under reservoir conditions are believed to conform with the above, but the ideal solutions do provide the basis for making improved estimates on the performance of gas reservoirs. The purpose of this paper is to show the performance characteristics when assumption (c) is corrected for the slippage phenomenon or the Klinkenberg effect. This is believed to be a step nearer to reality. MATHEMATICAL DEVELOPMENT Case 1. Gas Flow — Ideal Conditions The equations describing the flow of gas under ideal conditions have been clearly presented in the cited literature; however, for completeness of this work they are repeated here. The basic differential equation describing the flow of gas is Equation (6). It may be derived as follows: The continuity equation, the perfect gas law and Darcy's law are combined to give: Manuscript received in the Petroleum Branch office Aug. 3, 1963 or If — is constant, Equation (5) is rewritten to form the basic Equation (6). or for the linear case A dimensionless equation is obtained by dividing through by (pl)z and making the substitutions shown below: The resulting equation is A similar procedure for the radial case leads to the following equations: where and Equations (11), (12), and (13) are those used by Bruce, et al., and Jenkins and Aronofsky for their computational work.

Jan 1, 1953

By H. E. Stauss, J. Hino

INTEREST in silicon has arisen again in the past decade as a result of improvements in crystal rectifiers.' Although the preparation of silicon was first reported by Berzelius in 1880, the early product was of relatively low purity, and only the need for rectifiers in World War II led to the production of a 99.9+ pct pure powder. This material in crystalline form was consolidated into massive silicon for use, and the method developed was to melt it with selected added constituents as "doping" agents. Melting techniques, therefore, are of great importance. There are two basic problems in producing silicon ingots free of doping additions; one is the prevention of spitting and the other is prevention of cracking of the ingot during freezing. The most satisfactory arrangement yet developed for producing massive silicon is to melt and freeze in a cylindrical quartz crucible surrounded by a concentric heating element and concentric radiation shields or insulation. For example, use can be made of a tubular heater with a high frequency generator as the source of power and reflecting shields of alundum cylinders. The spitting of silicon is related to gas evolution, and the gas comes from two primary causes—adsorbed gas and the reaction products of silicon and the crucible. Gas is also released from bubbles contained in the quartz crucible walls. Improved removal of adsorbed gas can be achieved by means of controlled melting and freezing. The seriousness of the problem in vacuo is reduced with an electrically operated mechanical movement of the high frequency power coil. The upper portion of the powder charge is melted first and the high frequency coil lowered until the powder is completely molten. During cooling the high frequency coil is raised slowly. These means also reduce the final nonviolent extrusion of large beads of metal through the ingot top during freezing. Better control of spitting and bead extrusion is obtained when melting is done under helium at. atmospheric pressure instead of in vacuo. The problem of reaction between silicon charge and crucible in practice is confined to the reaction between silicon and quartz. This2 apparently is: Si + SiO2 + 2SiO The part that this reaction plays in spitting has not been isolated for separate study. SiO is a volatile vapor at the melting point; of silicon and is released freely during melting in vacuo, but hardly at all in helium at atmospheric pressure. The cracking of ingots is a major difficulty in melting silicon, and its prevention requires special melting techniques or the addition of "toughening" agents such as aluminum or beryllium.' The cracking of the ingots has been explained as being the result of the expansion that occurs upon freezing; although direct observation of freezing ingots reveals visible cracks on the surface only after a red heat has been reached, suggesting that cracking is the result of differential contraction of silicon and quartz. Silicon wets quartz, and the ingot adheres tightly to the crucible. Therefore as ingot and crucible cool, the two either have to pull apart, or at least one must crack. Surprisingly, in spite of the relative thinness of the quartz and the thickness of the ingot, the ingot and the crucible both crack. Microscopic and X-ray4 studies fail to show any plastic flow other than twinning in the ingots. Slow cooling fails to prevent cracking. Another possible solution to cracking is to weaken the crucible. Use of thin-walled crucibles finally led to success with fused quartz crucibles with a wall thickness of 0.25 to 0.50 mm. With such thin-walled fused quartz crucibles consistently uniform success is secured in producing sound ingots 30 mm in diam from the purest available grade of silicon (99.9+) without the use of any type of addition. Melts are made in the size range of 50 to 100 g. Omission of a deliberately added doping agent is not sufficient to insure pure ingots. The reaction of silicon with crucibles and the resultant solution of impurities in the silicon is well-established." In this laboratory, the presence of Al, Be, and Zr has been found spectroscopically in ingots melted in contact with alumina, beryllia, and zircon. The best crucible materials reported in the literature are MgO and SiO2. Use of MgO in this laboratory has resulted in a heavy deposit of magnesium on the furnace walls, showing that a reduction of the magnesia occurred and the resulting magnesium removed from the melt by volatilization. In the case of quartz, the silica is reduced and SiO liberated to deposit on the equipment walls. There probably is real danger that oxygen is dissolved in the ingot when either magnesia or silica is used as the crucible material. Preliminary analyses by Dean Walter in his vacuum unit in this laboratory6 indicate the presence of oxygen in undoped silicon melted in quartz.

Jan 1, 1953

By S. F. Reiter

The paper presents isothermal recrystallization curves for 0.08 and 0.15 pct C steel at subcritical temperatures following small amounts of plastic deformation. The effects of deformation, temperature, and aging on nucleation and growth rates ore described. The free energy of activation for grain boundary migration in steel is given. SEVERAL excellent reviews of the literature have appeared concerning the recrystallization of metals.'-' The present investigation follows the approach advanced by Mehl, Stanley, and Anderson,6-7 in which the rate of recrystallization was analyzed in terms of N, the rate of nucleation, and G, the rate of growth of recrystallization nuclei. Two lots of low carbon, capped steel of the analysis given in Table I were studied. Each lot consisted of a 150 lb coil which had been hot rolled to 0.083 in. and then cold rolled to 0.042 in. at the mill. Strips 0.930 in. wide were sheared perpendicular to the rolling direction. Both steels were normalized before studying their recrystallization characteristics. The strips were cleaned, painted with a magnesia-acetone paste, and made into packs of equal weight, wrapped in 0.002 in. copper foil. The packs were placed in a salt bath at 900°C for 30 min and air cooled. A relief anneal followed in a second salt bath for 15 min at 650°C. The relief anneal was found necessary from early tests in which a longer incubation period and slower rate of recrystallization were observed in relief-annealed lot A steel than in similar material which was strained and recrystallized directly after being normalized. This effect, which indicates the presence of transformation and/or cooling stresses in steel air cooled from above the A, temperature, has also been observed by Samuels8 and Masing.9 Figs. 1 and 2 show the microstructure of lot A and B materials and illustrate the rather uniform No. 8 ASTM grain size produced by this heat treatment. Winlock and Leiter10 observed that strip specimens which had their sharp edges removed elongated more uniformly than those which were not polished. Similarly, when the sheared edges were removed on a belt grinder, it was found in the present investigation that such samples recrystallized more uniformly than did unpolished strips. Therefore, all strips were carefully rounded prior to their extension. The approximate strain limits for the production of large recrystallized grains are from 6 to 12 pct extension." It was found that for the purpose of this investigation, 8 and 9 pct elongation were suitable deformations. The strain rate employed was 0.01 in. per in. per min and produced a yield point elongation of 4 pct. Winlock and Leiter found that mild steel of No. 8 ASTM grain size gave the same yield point elongation when extended at 0.012 in. per in. per min. All of the lot A and B strips extended in tension developed a straight, stretcher strain line at each grip when the upper yield point was reached. The lines were parallel and made an angle of 55" with the edge of the strip. They approached each other with increasing strain and met near the center of the sample at the end of the yield point elongation. Immediately thereafter, a small drop in load was observed and then the load increased in a regular manner with increasing extension. The grips were initially 8 in. apart. After extension, the 6 in. gage length was carefully cut into 1 in. samples. The remainder of the strip was discarded. After a flash pickle in hot 50-50 hydrochloric acid, six samples, each of which had been taken from a different strip, were placed in a basket and submerged in a lead pot for isothermal recrystallization. Although no recovery effect was observed, strain aging did occur after extension. Therefore, samples were always recrystallized within 24 hr after their cold deformation. After recrystallization, the samples were etched with a solution comprised of one part by volume of nitric acid with three parts of water. Bromide printing paper was exposed directly at low magnifications and later used with a mask to measure the desired quantities. First, the average diameter of the largest grain visible in each sample was determined using dividers. Next, the number of recrystallized grains per unit area was counted and recorded as n. Then, for each sample, the combined area of the recrystallized grains was measured by transcribing the grain outlines to standard graph paper. Many determinations of the area of the recrystallized grains were repeated five times and indicated a standard error that was not greater than 25 pct. The average area for six samples was divided by the area of the mask to yield the percentage recrystallized. Recrystallization of 0.08 Pct C Steel The progress of recrystallization at 670°C after 8 pct elongation of lot A steel is shown in Fig. 3, a through f. The shapes of the growing crystals are approximately equiaxed, as is assumed in the

Jan 1, 1953

By J. E. Burke

THE origin of recrystallization textures continues to be a matter of controversy. One explanation is that a recrystallization texture occurs because only grains having a limited range of orientations ever appear in the deformed matrix—the oriented nuclea-tion* hypothesis. Another explanation is that grains essentially having all orientations are nucleated but that those having certain orientations grow much more rapidly than any others in the deformation texture, and thus only the rapidly growing grains survive when recrystallization is complete. There has recently appeared a great deal of evidence'- indicate that recrystallized grains of face-centered cubic metals are frequently related to their parent grains by rotations of 20" to 40" about a common [lll] direction. Furthermore, it has been observed that the growth rate of the new grains depends upon their orientations with respect to the matrix, and that the most rapidly growing grains lie within the stated range of orientations. In a recent note, Beck7 has concluded from observations of this type that oriented growth alone is responsible for the appearance of preferred orientations in re-crystallized metals. It should be pointed out. however, that many of the available data indicate that oriented nucleation operates in addition to oriented growth. Thus, while oriented growth may permit a selection to be made among nuclei of several orientations, only a limited number of orientations are available in the first place for such selection.

Jan 1, 1953

By Orville R. Lyons

This paper presents a method whereby the amount of misplaced material and the difficulty of the separation can be used to compare coal cleaning equipment of all types, from effectiveness and capacity standpoints. The correlations presented do not include all types of equipment currently available, but the method can be used to evaluate any make or type of coal cleaning equipment, both old and new. THE relative performance of coal washing equipment, or the effectiveness with which any type or make of equipment removes impurities from coal, has been most difficult to evaluate in the past. The most widely used yardstick is the Frazer and Yancey efficiency formula developed in 1922,' but Yancey in a later article states that "washers treating coals of different density composition or operating at different densities of separation cannot be compared directly on the basis of this criterion."' Prior to and since 1922, a variety of other methods has been used for comparison purposes, including the distribution curve, the error area, and the "ecart probable" or probable error. Yancey and Geer in discussing these methods conclude, "Performance can be evaluated in a number of different ways, with the choice of the proper method to use being dictated by the objectives of the investigation and the data available."' It is true that performance can be evaluated in a variety of ways, but if the equipment is to be evaluated on an effectiveness basis, there should be only one universal comparison method. Varying methods have been used because one universal comparison method has not been found or developed. In the article previously quoted, Yancey and Geer state in clear terms the primary concept for a universal comparison method: "One of the simplest, and certainly one of the most obvious evaluations of washery performance is the quantity of sink material in the washed coal and the float material in the refuse. If the washery products are tested at the density at which the washing unit is operated, the sink in the washed coal and the float in the refuse represent material that has been misplaced." The quantity of misplaced material was used as a criterion of washery performance by Lincoln in 1913," by the United States Bureau of Mines in 1938,' by Hancock in 1947," and by the national French research agency Cerchar in recent years.' In 1950 Andersone proposed the use of this criterion as an efficiency value to replace the Frazer and Yancey formula. However, none of the above-mentioned investigators used the misplaced material concept in a manner that would provide universal coal-cleaning equipment comparisons. The Correlation Theory The ideal coal cleaning process would treat all sizes and would make a perfect separation at any given specific gravity. All material lower in density than the desired value would report in the coal product and all material higher in density would report in the refuse product. Unfortunately, no known cleaning process achieves this goal and there seems little likelihood that any process yet to be invented will do more than approach it. When coal is treated in volume under operating conditions, it is impossible to avoid mechanical entrapment, fluctuations in throughput and effective gravity of separation, and the creation of turbulent currents, even when a true heavy-liquid bath is used and the feed is closely sized and contains little intermediate gravity material. This being so, it is possible to appreciate the difficulties inherent in trying to obtain a perfect separation when treating a wide range of sizes and a feed containing high percentages of intermediate material, using turbulent currents to help create the effective separation gravity, under operating conditions which normally tend to be on the overload side. When coal is separated from refuse in any coal cleaning equipment, some refuse always reports to the coal and some coal to the refuse; the writer therefore assumed that there should be a relationship between the total amount of misplaced material produced by any given piece of equipment and the difficulty of separation as represented by the percentage of near gravity material in the feed. With small amounts of near gravity or k0.1 material in the feed there should be less misplacement of material than would occur with large amounts of near

Jan 1, 1953

By T. E. Watkins, M. D. Nelson

INTRODUCTION Deeper drilling for oil is becoming more and more the rule rather than the exception. With deeper drilling come additional problems, perhaps the greatest being those brought on by the higher temperatures encountered down the hole. particularly in the Gulf Coast region of Texas and Louisiana. Temperature gradients of the order of 1.8° to 2.0°F/100 ft are not unusual, and a gradient of 2.3"F.'100 ft is found in some areas of Texas. With a mean surface temperature of 74oF, the following temperatures could be expected for a geothermal gradient of 2.0°F; 100 ft: at 10,000 it. 271°F. 12,000 ft, 314°F: 14,000 ft, 354,oF; and 16.000 ft. 394°F. Severe gelation of lime-base drilling fluid in wells that have high bottom hole temperatures has become perhaps the most serious difficulty enconntered in drilling under such conditions. Lime-base drilling fluids have been very succesefully and widely used in the drilling of wells in the Gulf Coast region because of their inherent stability toward contaminants. their ability to suppress the swelling dispersion of bentonitic shales, and their ease of maintainance. The gradual recognition: during the past few years, that these muds were. in themselve. the cause of many difficulties experienced in drilling has led to wide-pread efforts by the drilling industry. to determine the reasons for the failure of these mud systems and to develop mud systems capable of performing satisfactorily under high-temperature conditios. MANIFESTATIONS OF HIGH-TEMPERATURE GELATION it is generally possible to recognize the symptons of high-temperature gelation early enough that advance predictions can be made of serious difficulties. in mud control, and the useful life of the drilling fluids can be extended by proper treatment. Following i.; a list of the manifestations of high-temperature gelation: (1) The drill string 'takes weight' while going in the hole after a trip. In early stages of high-temperature gelation it is possible to notice a slight reduction in drill string weight as the drill pipe is lowred near the bottom of the hole. (2) Excessive pump pressure is required to .tart the circulation of drilling fluid at or near the bottom of the hole when going hack to bottom after a trip. As the severity of the gelation increases it may be necessary to break circulation a number of times when going in the hole. (3) The drilling fluid from the bottom of the hole is thick and often granular or lumpy when pumped up after making a round trip. In a severely gelled drilling fluid system such a condition may be irreversible; that is, it cannot be stirred or chemically treated to produce a satisfactory drilling fluid. (4) Completion tool.. such as logging tools or perforating guns will not sink to the bottom of the hole. On some occasions completion tools will become stuck and require a fishing job to retrieve them if the wire line attached to them is broken. It is often difficult to determine whether the condition of the drilling fluid is responsible for sticking the tool or whether the wire line becomes key seated in a crooked hole and causes the allow difficulty. When there are 110 other symptoms of high-temperature gelation. then the difficulty may usually be attributed to the latter cause. (5) In extreme cases of high-temperature gelation it is necessary to "wash" and "ream" when going back to bottom after coming out of the hole. (6) In many -instance. it has been found to be extremely difficult and expensive to 1111 production packers 2nd tubing in moderately deep oil wells which had been drilled with a lime-base drilling fluid. In such instances-the original mud had apparently "set" to a consistency approaching that of a weak cement. CAUSES OF HIGH-TEMPERATURE GELATION Extensive test; have indicated that a lime-base mud does not develop a highly gelled condition at temperatures below 250°F. whereas above that temperature such condition often develops rapidly. (Fig. 1) concurrently. the following changes are evident ill the mud: (1) The alkalinity of the mud decreases to a very low value. with both caustic soda and lime being consumed. (2) The quartz content of the mud decreases sharply. (3) The bentonitic content of the mud decreases or di-appears, with concurrent decrease or loss of base exchange capacity of mud solids. (4) New compounds formed in the mud have been found to be cal-cium silicate, calcium aluminum silicate, and calcium sodium aluminum silicate. (5) The mud loses the ability to form a filter cake of low permeability. The above characteristics have been discussed, in part. by other authors

Jan 1, 1953

By E. C. Burke, W. R. Hibbard

G. B. Craig (University of Toronto, Toronto, O,nt., Canada)—The advent of pyramidal slip at room temperatures in a magnesium crystal (M2,) and the very low value reported for the critical shear stress are puzzling. Table I1 shows the calculated values (approximate) for sin x cos I in this specimen if all the (10l) planes are considered. If So is the shear stress resolved in the direction of glide, on the glide plane, and U, is the stress operative in yield point tests, then: S,, — 325 (0.169) 55gpersqmm (approximately) for 1101: S,, = 325 (0.465) = 151 gpersqmm (approximately) for (0001): S,, — 325 (0.101) - 32.8 gpersqmm (approximately) Thus, we see the pyramidal plane in which the minimum shearing component operated. Barrett"' stated: "Experiments have repeatedly shown that, when there are several crystallographically equivalent slip systems in a crystal, the one having the greatest resolved shear stress will become active. ..." It does not appear to me that the measurements given are conclusive proof that pyramidal slip operated. E. C. Burke and W. R. Hibbard, Jr. (authors' reply) —Although the low value for the critical resolved shear stress for pyramidal slip may be puzzling, there does not appear to be any basis for questioning the validity of the measurements. Under the influence of constraints, slip systems having decidedly lower shearing components may become operative, e.g., "cross-slip" or the "forced glide" in magnesium reported by Bakarian. Since we believe that pyramidal slip occurred in the specimen because basal slip was inhibited, it is not too surprising to find an operative plane with a lower shear stress. -7 C. S. Barrett: Structure of Metals U94jl p. 2J6. New York. McGraw-Hill Book Co.

Jan 1, 1953

By R. Maddi, I. R. Kramer

The delay time for the initiation of slip was studied in single crystals of a brass, aluminum, and ß brass. A delay time for slip was found in ß brass when the specimens were tested below room temperature; however, one was not found for a brass or aluminum. A general theory for the existence of the brittle transition temperature is proposed. A LTHOUGH a considerable amount of effort has A been devoted to the study of the deformation and fracture of single crystals, the vast majority of the work was concerned with static tests or with tests carried out at relatively slow strain rates. The necessity for the study of a possible incubation time for slip becomes apparent when the various theories which have been postulated for the elucidation of the mechanism of slip are considered. The existence of an incubation period would strongly indicate that slip occurs by a process of nucleation and growth; whereas the absence of an incubation would present rather convincing evidence that slip occurs by a cataclysmic process. In addition to shedding light on the process of plastic deformation, an understanding of the early stages of plastic deformation may be helpful in finding an explanation for the brittle behavior of the body-centered metals under certain conditions. It is well known that these metals, such as iron, molybdenum, tungsten, ß brass, etc., will become brittle as the test temperature is lowered or the strain rate is increased. In spite of the fact that this subject has received considerable attention since the turn of the century, no adequate theory exists today which explains the phenomenon. In the ductile temperature range the metal breaks with a "fibrous" fracture after considerable slip has taken place. In the brittle temperature range the metal fails essentially by cleavage on the {loo) planes: however, some plastic flow is always present even in the most brittle fractures. It is possible, as will be explained later, to ascribe this brittle behavior to the length of the incubation time for slip. Clark and Wood,' using polycrystalline metals, showed that a delay time existed for the yield point in mild steels and that the delay time depended upon the applied stress. These authors stated that the delay time was observed only with those materials for which the stress-strain curve showed a definite yield point. In their work only the mild steel specimens exhibited a delay time at the yield point, while the other materials studied-type 302 stainless steel, SAE 4130 normalized steel, SAE 4130 quenched and tempered steel, 24s-T aluminum—did not show a delay time. These authors' in an extension of their work, found that as the temperature was lowered the delay time was increased. It is, then, the purpose of this investigation to measure or to set an upper limit on the delay time for plastic flow in single crystals of a brass, aluminum, and ß brass. The delay time will also be studied as a function of temperature. The incubation time may be measured by determining the length of time the specimen will support a stress without slip occurring when the stress is greater than the static critical resolved shear stress. In order to accomplish these measurements use was made of a pendulum which was so designed that a single crystal specimen could be placed at various positions along its length. When a pendulum is struck by another pendulum of the same length, an elastic wave is transmitted down the bar with the velocity of sound in the material and is reflected from the far end of the bar. The reflected wave then travels back and unloads the stress until it reaches the impacted end of the bar and the two pendulums separate. The length of time that the specimen is subjected to the stress is equal to the time it takes for the stress wave to travel twice the distance from the specimen to the end of the bar. The stress applied to the specimen is governed by the velocity of impact of the two pendulums. The stress at which the specimen first suffers plastic: deformation was determined in these experiments by examining the specimen under the microscope for the first appearance of slip lines and by measuring the residual strain after each impact. In these experiments the critical resolved shear stress was approached from the low stress side and no attempt was made to determine it exactly. To determine it exactly, it would have been necessary to find that stress at which slip would have just started. However, since the stresses were increased in rather small increments the critical stress is believed to be approached rather closely, as will be seen from the experimental results. The critical stress will be taken as the highest stress obtained before the onset of plastic deformation. The stresses

Jan 1, 1953

Jan 1, 1953

By A. E. Nehrenberg

IN an earlier publication' it was shown that the.. shape assumed by a volume of growing austenite is inherited from the prior structure. The matrix grains of pearlitic microstructures are equiaxed, and austenite grows in an equiaxed manner in these prior structures. Martensite and bainite, on the other hand, have an acicular grain structure, and the austenite produced in such structures grows in an acicular manner. In the discussion of this paper' it was pointed out that in cold-rolled tempered martensite, austenite grows in an equiaxed, rather than an acicular manner. The results of an experiment carried out to arrive at an understanding of this behavior are illustrated by the micrographs. Fig. 1 shows the acicular microstructure produced by heating tempered martensite to a temperature within the Ac1-Ac3 range, 1350°F. When tempered martensite is cold rolled, then heated to the same temperature, the equiaxed structure shown in Fig. 2 is produced. A sample of cold-rolled tempered martensite heated at 1350°F just long enough for the formation of a small amount of austenite is shown by Fig. 3 to have an equiaxed (recrystallized) ferrite grain structure. The small particles of. austenite which formed at 1350°F in the equiaxed ferrite matrix are likewise equiaxed. Thus, the equiaxed growth of austenite in cold-worked tempered martensite is not a contradiction of the principles described in the previous paper, for the growth pattern reflects the matrix grain structure existing at the time of austenite formation. References A. E. Nehrenberg: The Growth of Austenite as Related to Prior structure. Trans. AIME (1950) 188, pp. 162-174; Journal of Metals (January 1950). 2 J. R. Vilella and R. A. Grange: Discussion of ref. 1. Trans. AIME (1950) 188, pp. 1378-1381; Journal of Metals (November 1950).

Jan 1, 1953

By R. B. Burt, J. A. Barr, I. S. Tillotson

THE pumping of solids in water suspension is an important part of many metallurgical and mining operations. In most cases, it is still in the rule of thumb category for which no universal formula has been developed, and much research is needed. Because of the limited and incomplete data available, this article may be classed as an experience paper, which is presented with the hope that some contribution will be made toward the development of the so-called universal formula. This formula, if and when developed, may be evolved from several factors, many of which are not now available for general application. The designing engineer is interested in obtaining accurate forecasts on: 1—the minimum velocities needed to prevent choke-ups in the pipeline, which in turn dictates pipe sizes, 2—power required for pumping, 3—pump selection. The basic factors for a given problem will include: 1—weight per unit of time of solids to be handled, 2—specific gravity of solids, for calculation of volume, friction and power, 3—screen analysis of solids with the colloidal acting, i.e., the slime fraction, a very important factor, 4— shape of particle or some means of determining a friction constant, 5—effects of percentage of solids, 6—development of a viscosity factor to be used in the overall calculations, 7—calculation of the lower limits of pipeline velocities permissible, 8—calculation of total head, pump horsepower, and 9—setting up of pump specifications. In certain limited cases horsepower and total heads and minimum velocities may be computed and a suitable pump selected from basic data, but in many cases, as in mining of Florida pebble phosphate, experience rather than a hydraulic formula still should be used as a basis of selection. Pumping Florida Pebble Matrix Pumping at the Noralyn mine of International Minerals and Chemical Corp. will be used as an example. Other areas will vary as to the characteristics of the matrix, especially the slime content. A typical screen analysis of this matrix is: +14 mesh, pebble size,* 2.1 pct; —14 +35 mesh, 11.4 pct; -35 +I50 mesh, 60.5 pct; -150 mesh, 25.0; total, 100 pct; moisture in bank, 20.0 pct; weight per cu ft in bank, 120 lb. The —150 mesh fraction may increase to as much as 35 pct in adjacent areas. When thoroughly elutriated, the matrix has a relatively slow settling rate, which is an important factor in permitting lower pipeline velocities without choke-ups. Exact data is not available to evaluate settling rates. For a factor of 100 a suspension of clean building sand in water is suggested. When pumping long distances, a quick settling matrix allows the coarser solids to settle out along the bottom of the pipeline, causing drag, turbulence, and increased friction. With a slow settling matrix as at Noralyn, turbulence acts to keep the solids in suspension at a lower friction head, regardless of the pumping distance. When the pebble content of the matrix, i.e., the + 14 mesh fraction, is in excess of 10 pct of the total solids, trouble may be expected from settling out even in normal pumping distances. To prevent choke-ups and maintain tonnage, an additional pump must be added in the long runs, where one pump would otherwise be satisfactory. A typical pulp handled is: total volume, 7800 gpm; water, 4500; solids pumped per hr, 4200 lb; sp gr pulp, 1.4; percent solids in pulp, 46.; pipe size, 16-in. ID; pulp velocity, 12.85 fps; probable critical velocity, 10 fps, as below this minimum velocity choke-ups would be numerous. In calculating friction heads the Armco handbook is used where a roughness factor based on 15-year-old pipe is set up. Because the pipe used in pumping matrix is smooth and polished because of the scouring action of the phosphate and its silica content, the head losses in the Armco table for water are practically the same as in pumping the Noralyn matrix through smooth pipe, plus the fact that conditions vary widely over short periods, making accurate determinations difficult to obtain. New pumps and pump changes are being tested continuously and a wealth of data built up. This has resulted in a substantial improvement and lower relative costs in pumping matrix. The Florida phosphate industry is constantly seeking to offset higher wage and material costs with improved technique. Until a few years ago a 12-in. discharge pump was commonly used, with heads as low as 80 ft. Sizes have gradually increased and heads more than doubled. For example, the following pump was placed under test at the Noralyn mine: make, Georgia Iron Works; size, suction 16 in., discharge 14 in.; impeller, 39-in. diam; motor, 600 hp, slip ring; full load speed, 514 rpm. The results were increased head, higher capacity than the older design, with fewer pumps in the line from mine to washer.

Jan 1, 1953

By R. Maddi, I. R. Kramer

C. S. Roberts (Dow Chemical Co., Midland, Mich.)— In this study we have seen another example of how modern electronic instrumentation can be of great value to metallurgical research. The authors have shown much ingenuity in their experimental work. However, I wish to point out that anelasticity theory tells us that we must be cautious when we use pulse methods for measurements which are to be correlated with knowledge of static stress-strain behavior. The basic stress calibrations used by the authors depend on the use of static moduli combined with the pulsed strains. No recognition of a possible modulus defect has been indicated. The general agreement of critical resolved shear stresses may indicate that a

Jan 1, 1953

By H. C. Chang, N. J. Grant

REEP studies and measurements in most in-V> stances are based on a relatively gross gage length. Even in some recent theoretical studies on the mechanism of creep, changes were followed by means of X-rays and metallography without regard for the behavior of the individual grains and grain boundaries.'" Analytical studies of creep have frequently indicated that more than one competing process is operative and that the ultimate creep performance depends on the effects of temperature, time, and strain rate as well as grain size.'-" he grains and grain boundaries are known to respond differently to these variables but the extent of the response is still little known, especially in poly-crystalline materials where the relative orientations of grains and grain boundaries are important. This paper reports some experimental observations of the behavior of the grain boundaries and their effect on the deformation in the grains. High purity aluminum was used to avoid complications of aging reactions, second phase, inclusions, etc. Experimental Procedure A small vertical nichrome wound furnace was built to permit direct loading on the test specimen. This furnace is capable of operating up to about 1300°F with reasonable temperature distribution. A ground rectangular quartz window, 1.25x0.5 in., is imbedded in the external stainless steel tube to permit observations of the creep process with a microscope. An argon atmosphere ,was provided to prevent oxidation. The quartz window caused a temperature gradient between the back and front surfaces of the specimen of 15" at 700°F. The temperature gradient could be cut down to 3°F along the length of the specimen by adjusting shunts across the furnace windings. An ordinary metallurgical microscope with a working distance of 14 mm was rebuilt so that it could be moved in three mutual perpendicular directions. Visual examination could be made with either a 30X eyepiece or a 15X filar eyepiece. Using an objective of focal length 24.3 mm and a numerical aperture 0.20 a total magnification of 120X or 240X could be obtained. High purity aluminum rated at 99.995 pct was supplied by the Aluminum Co. of America as % in. then the gage portion was further machined to 3/16 in. diam. The ends were Y4 in. diam and threaded to fit available specimen holders. Two opposite flat surfaces of the gage portion were obtained by milling, giving final dimensions of the gage portion of 3/4x3/16x3/32 in. Machined specimens were first electropolished in Jacquet's solution.' Reference marks were produced by pressing a thin sewing needle into the surface of the specimen. The specimen was then annealed at 900°F for 24 hr and at 1150°F for 12 hr. Typical macrostructures of specimens treated in this manner are shown in Fig. 1. The range of the grain size was 1 to 5.5 mm (see Fig. l), but most of the grains were of 2.5 mm and went through the whole thickness of the specimen. The specimen was re-electropolished and etched electrolytically to reveal the grain boundaries. In order to reveal the orientation difference of the grains, etch pits were produced on the surface of the grains by etching in a mixture of hydrochloric and nitric acids (HC1, 45 pct; HNO,, 10 pct; H,O, 45 , by volume). The specimens were very carefully put into the holders and furnace; yet even with this care, fine slip lines were developed on the specimen surface.

Jan 1, 1953

By Tell Ertl

THE Piceance Creek Basin in northwestern Colorado is believed to contain the richest large deposit of oil shale in North America. The major portion, about 1650 sq miles, is bounded by the White River on the north, the Grand Hogback, which runs from Meeker to Rifle, on the east, the Colorado River to the south, and the drainage basin of Salt and Douglas Creeks on the west. The Basin is a plateau 7000 to 9000 ft high, composed of 3000 ft of the Green River series of Eocene age and surrounded by a steep escarpment of 1000 to 3000 ft. From the escarpment the beds dip gently toward the center. Although oil shale is found in all members of the Green River series, the rich thick beds are found chiefly in the Parachute Creek member. This is normally capped by 100 to 200 ft of the Evacuation Creek, the youngest member of the Green River series. Actually the Piceance Creek Basin oil shale is not a shale, nor does it contain oil. It is magnesium marlstone holding solid organic matter capable of being broken down by heat into gases, some of which can be condensed into oil. The marlstone is resilient nonporous rock, difficult to sample by pick or hammer and moil. Many companies and individuals prospected the Colorado oil shale shortly after the first World War,' see Fig. 1, but because of the discovery of large quantities of petroleum in the late 1920's in Cali- fornia, Oklahoma, and East Texas, interest in oil shale development waned and did not revive until World War 11. In 1944 the writer, employed by the Bureau of Mines, prospected the high grade oil shale in numerous places along the southern outcrop of the Piceance Creek Basin. Several channel samples about 100 ft in length were cut, see Fig. 2. An eight-man crew needed a week to cut a satisfactory channel 80 ft long in the cliff face. The Phillips Petroleum Co., the Union Oil Co. of California and others also prospected the oil shale outcrop. In 1945 the Bureau of Mines initiated a core drilling program for the purpose of obtaining accurate samples from the Piceance Creek Basin. The U. S. Geological Survey set up a program for the geological study of the Basin that is still going on." Until the end of 1951 a total of 31 holes was drilled for core with diamond drills, and, in addition, cuttings through the oil shale have been obtained from 4 gas wells drilled by standard rotary oil well rigs. The Bureau of Mines drilled 12 of the holes, the Union Oil Company of California 8, the Standard Oil Company of California 6, the Sun Oil Company 3,

Jan 1, 1953

By F. W. Glaser, W. Ivanick

A pressure-sintering method was used to produce binder-free and very dense TiC specimens. Some physical properties of these TIC bodies were determined and found to compare favorably with those of certain cemented Tic grades. It was also observed that the hot transverse rupture strength of TiC bodies remained substantially the same regardless of the amount or type of binder material used. STUDIES of the structure and physical properties of refractory materials have been intensified recently because of the urgent need for nonstrategic materials that retain their strength at high temperatures. Research aimed at determining and improving the physical properties of cemented carbides and borides has been accelerated with a view toward possible use of such materials in connection with turbine blades, rocket nozzles, and other high temperature applications. On the hypothesis that the strength requirements in connection with some of the above applications could be met only by proper choice of cementing agents for such refractory materials, the literature describing the physical properties of borides or carbides was reviewed. However, with a few exceptions,'-" references were found only to compositions containing at least one or more auxiliary binder metals. Cobalt and nickel are among the most frequently employed cementing agents. The melting point of Tic (approximately 3250°C) and therefore the sintering temperature, at which notable densification of a cold pressed Tic powder compact could be expected in the absence of a liquid binder phase, is relatively high. The present study makes use of a high temperature, pressure-sintering procedure, recently described by one of the authors in connection with the sintering of binder-free ZrB,," to produce dense bodies of sintered Tic—free of any cementing agent. During the course of this sintering study, some physical properties of dense Tic bodies produced by this method will be discussed. Materials, Preparation of Samples, Testing Methods The procedure for the forming of Tic powder consisted of mixing graphite and TiH, powders in stoi-chiometric proportions, and heating this mixture in a H, atmosphere and carbon crucible by high frequency, to temperatures ranging between 1900° and 2100°C (3452" and 3812°F). The powdered carbide was then comminuted and screened to the desired particle size. Table I shows the chemical analysis of the two grades that were employed for the production of samples during this work. Bodies of Tic, approximately 2.5xlx0.5 cm were produced in graphite molds that were heated by direct conduction. Sintering was carried out at temperatures for time intervals ranging from approximately 0 to 30 sec under a constant pressure of about 1.3 tons per sq in. An alternate method for the production of samples consisted in cold pressing the individual Tic grades at pressures ranging from 4 to 10 tons per sq in. and sintering in a hydrogen atmosphere in graphite crucibles heated by high frequency induction. Sintering temperatures ranged from 2600° to 2900°C (4715° to 5255°F). Electrical testing was done by measuring potentiometrically the voltage drop over a length of 1.5 cm for a current of 10 amp at room temperature. Cross-sectional areas as well as densi-

Jan 1, 1953

By H. E. Stauss, G. Sandoz

AN increase in the value of magnetostriction1 * is known to result from the annealing of some ferromagnetic alloys in a magnetic field. Similar increases may be anticipated in the value of the magnetostriction of alloys that are of interest because of their normal high values. Two were selected for trial, 87 pct Fe-13 pct Al(Fe,Al) and 69 pct Co-31 pct Fe, the latter being used as a representative of the Co-Fe alloy series. The influence of a magnetic field present during annealing is explained by the domain theory of magnetism." The field orients the domain vectors in its own direction when the alloy is at or below the Curie temperature, and holds them there until the metal is cold. During cooling the interaction stresses between neighboring grains are largely relaxed. Interaction stresses will reappear, however, if the state of magnetization of the specimen is changed in any way, and will be larger the more the new state of magnetization differs from the one existing during the magnetic anneal. In this connection the 180" reversal of a magnetization vector is not considered a change because a simple reversal does not tend to produce a change in shape of a magnetized region. When the field existing during the anneal is removed after the metal is cold, the domain vectors can turn back only to the nearest crystallographic directions of easy magnetization because return to random

Jan 1, 1953

By C. G. Dunn, M. Sharp

IN twinned crystals of the face-centered cubic metals the lattice of one twin is a mirror image of the other in a common twin boundary. When several twins appear within large grain in a sheet specimen, the twin one boundaries form a set of lines at the surface of the specimen which coincide with (111) planes of the large grain. Furthermore, for twins of the same orientation, these lines are parallel. Generally, the presence of identically oriented regions with straight parallel boundaries coinciding with a (111) plane of the surrounding crystal is strong evidence for identifying the island regions as twins of the parent crystal. However, Fig. 1, which shows the macrostructure of a large grain of copper with island regions that satisfy these conditions. is not an illustration of (111) twins. Since the reverse side of the specimen has much the same appearance, it was thought at first that these regions, which appear dark in the macrograph, actually were twins. According to X-ray data, however, these regions are second-order twins of the large crystal. With regard to their formation, these second-order twins formed by secondary recrystallization in a cube texture matrix. Growth occurred in the direction of the arrow (see Fig. 1) as the specimen moved slowly into a gradient temperature furnace as described previously.' Nucleation of the second-order twins occurred, therefore, on the ends facing opposite the arrow. If the origin of the second-order twins were due to repeated twinning, some first-order twin structure should be visible on these ends. This proved to be the case, as very small twins were readily found with the aid of a microscope, and probably could have been seen, in some instances, under ideal lighting conditions without aid of a microscope. Fig. 2 shows a cross-section view taken perpendicular to both the surface and the (111) trace of the parent crystal (visible as a straight boundary in Fig. 1) at the beginning point of growth of a second-order twin and where one first-order twin was relatively thick. In the micrograph, A is the large parent grain; B is the first-order twin of A; and C, which is a first-order twin of B; is a second-order twin of A. Between A and B and between B and C the major straight portions are traces of common (111) twin boundaries. The straight portion of boundary between A and C, however, is not a common crystallographic plane to the two lattices; it is a (111) plane of A and a (115) plane of C. Without considering the mechanism of twinning itself, the origin of the second-order twins may be accounted for in terms of repeated twinning and special growth characteristics. After each nucleation, a selective growth process can be thought of as favoring growth of the first-order twin in local spots only and favoring growth of the second-order twin to an extent comparable with that of the parent grain over relatively large areas in a way similar to that described for twinning in aluminum.' It has already been pointed out that the boundary between the large grain (A) and the second-order twin (C), which is responsible for the straight boundary portions in Fig. 1, involves a (111) plane of A and a (115) plane of C. The same combination of planes is not only possible in first-order twins, but actually appears quite frequently.3 Their prevalence in first-order twins and their presence here in second-order twins, together with the necessary occurrence of a large number of common lattice sites at the boundary, is an indication that this combination produces an "energy cusp"' boundary. (Energy cusp boundaries have been described by Shockley and Read.") The configuration of atoms near a {Ill), (115) boundary in first-order twins is of course different from the configuration near the same type of boundary in second-order twins. References 1 M. Sharp and C. G. Dunn: Secondary Recrystallization Texture in Copper. Journal of Metals (January 1952) Trans. AIME, p. 42. 2W. G. Burgers and W. May: Stimulated Crystals and Twinning in Recrystallized Aluminum. Recueil des travaux chimiques des Pays-Bas (1945) 64, p. 5. aD. Whitwham, M. Mouflard, and P. Lacombe: Discussion of W. C. Ellis and R. G. Treuting, "Atomic Relationships in the Cubic Twinned State." Trans. AIME (1951) 191, p. 1070; Journal of Metals (October 1951). 4 W. Shockley and W. T. Read: Dislocation Models of Crystal Grain Boundaries. Physical Review (1950) 78, p. 275.

Jan 1, 1953