By T. F. Kassner

The dissolution kinetics of type 304 stainless steel in the Bi-Sn eutectic alloy have been investigated under the well-defined hydrodynamic conditions produced by the rotating-disc sample geometry. In addition, the mutual solubilities of iron, chromium, nickel, and manganese from 304 stainless steel in the eutectic alloy were determined over the temperature range 450" to 985°C. The convective -diffusion model for mass transport from a rotating disc was used to interpret the experinlental dissolution data. The dissolution process was found to be liquid-diffusion-controlled under specific conditions of temperature and Reynolds number. Liquid penetration into the 304 stainless steel resulted in a reduction of the di,ffusion-controlled mass flux and thus precluded the calculation of the diffusion coeficients of the four components from 304 stainless steel in the Bi-Sn eutectic alloy. The convective-diffusion model for diffusional limitations of electrode reactions and mass transport at the tationssurface of a rotating disc set forth by Levich 1,2 has found wide applicability in the investigation of electrochemical and dissolution phenomena in aqueous systems. Riddiford 3 and Rosner have reviewed the model and also include numerous references on work of this nature. More recently the rotating-disc system has been applied to the investigation of hetereogeneous reactions in liquid-metal systems. Shurygin and Kryuk 5 have measured the dissolution rates of carbon discs in molten Fe-C, Fe-Si, Fe-P, and Fe-Ni alloys. Shurygin and shantarin6 also studied the dissolution kinetics of iron, molybdenum, chromium, and tungsten, and the carbides of chromium and tungsten in Fe-C solutions with a rotating-disc sample geometry. In these systems it was possible to distinguish between diffusion and reaction control mainly through experimental confirmation of the velocity dependence of the dissolution rate predicted by the model. However in the absence of dependable solubility data and the virtual lack of diffusion data in these systems, a quantitative check of the magnitude and the temperature dependence of the rate was not possible. In many instances, estimates of the activation energy for solute diffusion and the diffusion coefficient based upon the experimental dissolution data are not credible. A recent study by this author7 has resulted in a critical test of the model in a liquid-metal system. The solution rates of tantalum discs in liquid tin were measured over a wide range of temperature and velocity conditions. In addition, the solubility and diffusion coefficient of tantalum in liquid tin were determined as a function of temperature. The latter data were used with the model to predict both the magnitude and the temperature dependence of the dissolution flux. In that work it was also deemed necessary to reevaluate the solution to the convective diffusion equation to incorporate the effect of the lower range of Schmidt numbers encountered in liquid-metal systems. Good agreement between the model and the experimental dissolution data in the region of diffusion control was obtained in the Ta-Sn system. The Bi-Sn eutectic alloy is used as a seal between the reactor head and the reactor vessel in the Experimental Breeder Reactor-11. The alloy is fused periodically prior to fuel-handling operations. In that connection, it was necessary to investigate the compatibility of the liquid alloy with the type 304 stainless-steel containment material. The results of a rotating-disc study in this multicomponent system are presented. EXPERIMENTAL METHOD The 5.08-cm-diam discs were machined from 0.317-cm-thick plate. Chemical analysis information for the type 304 SS material is given in Table I. The discs were ground flat on metallographic paper and given a final polish on Linde B abrasive. A thin support rod was threaded into the disc and the region around the threads was fused under an inert gas. The support rod was fitted with a quartz protection tube and then was attached to a supporting shaft which passed through a rotary push-pull vacuum seal. The disc and supporting shafts were dynamically balanced prior to insertion into the furnace tube. The apparatus is shown schematically in Fig. 1. The 58 pct Bi-42 pct Sn eutectic alloy melts were prepared from 99.995 pct pure Bi and Sn by fusing the components in a 7-cm-ID Pyrex crucible. The system in which the melts were made was evacuated to a pressure of 1 x 10-6 Torr and back-filled with purified argon several times before melting the charge. The ingot was reweighed and placed in a slightly larger-diameter Vycor crucible used in the dissolution runs. A run was started by lowering the disc into the liquid

Jan 1, 1968

By L. C. Brown, E. B. Hawbolt

The formation of grain boundary precipitates has been studied in Ag-5.64 wt pcl Al alloys at 688°C. Large-grain specinzerzs were used and the boundary misorientation measured by X-ray diffraction. At low-angle grain boundrrries Primary sideplates form. u)hile abore a 17-deg misorientation lenticular precipitates predominate. Growth of the lenticular precipitates was studied on individual grain boundaries using a statistical technique. The thickening and lengthening rates appeared to be independent of &apos;pain boundary misorientation, indicating that grain boundary diffusion was not significant in this system. The precipitates grew urith constant shape, with both the length and thickness increasing parabolically with time. The parabolic lengthening rates were unexpected since previous theory and experimerztal results had indicated linear growth. By approximating the shape of the precipitate to that of an oblate spheroid grouling with constant shape an equivalent diffusion coefficienl was calculated. The zlalue obtained was in good agreement with nleasurements obtained fron, diffusiorz couples. IF a single-phase alloy is heated or cooled to a temperature such that the phase becomes supersaturated, there is a tendency for a second phase to precipitate from it in order to remove the supersaturation. Precipitation takes place initially on grain boundaries due to preferred heterogeneous nucleation, but subsequently Widmans kitten plates may form in the grain interiors if the grain size and supersaturation are sufficient. The type of grain boundary precipitate formed depends on the nature of the boundary. Aaronson1 and clark2 have shown that grain boundary misorientation can be characterized by the simple parameter R, where and X, Y, and Z represent the minimum rotations about three orthogonal axes required to bring the two lattices forming the grain boundary into coincidence. The maximum value for R is 60 deg. In using this parameter the orientation of the grain boundary itself is, of course, neglected. However it was found in both Fe-si3 and A1-Ag2 that the precipitate shape depended only on the parameter R. Clark found that the vast majority of precipitates formed were allo-triomorphs— lens-shaped precipitates that grew along the grain boundaries. At low-angle boundaries, however, (R < 15 deg) Widmanstatten sideplates nucleated at the grain boundaries and grew into the adjacent grains. It has been reported that the rate of growth of grain boundary precipitates is controlled by diffusion within the supersaturated phase.&apos; The theories which have been developed for growth rates have assumed the diffusion coefficient constant over the composition range of the supersaturated phase. This is a fairly good approximation if the composition range involved is not large. Thickening rates have been calculated using the theory developed by Zener4 and by Frank5 for the growth of planar precipitates. A parabolic growth law

Jan 1, 1968

By T. E. Scott, D. H. Sherman, C. V. Owen

It has been established&apos; that vanadium exhibits a ductile to brittle transition temperature which increases with increasing hydrogen content. Optical microscopic examination at room temperature revealed no evidence of hydride precipitate in fractured specimens containing 100 ppm H, but hydrides were present in samples with 800 ppm H. More recently2 the strain rate and temperature dependences of the ductility drop in vanadium containing 6 ppm H were reported. It was argued that the ductile-brittle transition, while dependent on the presence of hydrogen, probably could not be explained by the precipitation of hydride. The bases of the argument were that 6 ppm H would not produce sufficient hydride to alter the ductility to the extent observed and no visual evidence of hydride was obtained. However, the data were not sufficient in these investigations 1,2 to define accurately the ductile-brittle transition temperature. Also, no information was available concerning the terminal solubility of hydrogen in vanadium at the low concentrations employed. westlake 3 has studied the electrical resistivity of vanadium at several hydrogen concentrations. He was able to detect the precipitation of hydride and to extend the hydrogen solvus to the composition and temperature range pertinent to the observed ductile-brittle transition behavior, Westlake compared his

Jan 1, 1968

By H. C. Fiedler

THE development of the cube-on-edge secondary re-crystallization texture in Si-Fe strip depends upon the ability of inclusions to restrain normal grain growth. This ability is determined by the number and size of inclusions, which, for a given composition, is controlled by the thermal history of the material during the prior processing.&apos; It has been shown2 that increasing the silicon content decreases the solubility of sulfur, and it is the purpose of this note to show the consequences of this decreased solubility for secondary recrystallization. Heats were made as previously described and cast into graphite molds.&apos; The compositions are shown in Table I. Slabs 1 in. thick were cut from the ingots and either hot-rolled from 1000°C in the as-cast condition or after one of the heat treatments described later. The processing to the final gage of 12 mils followed the previous procedure.&apos; To avoid cracking, the 5.2 pct Si alloy was cold-rolled at 150" to 200°C rather than at room temperature. The percent cube-on-edge texture developed by isothermal heat treatments was determined by dividing the maximum torque measured on disk sam-

Jan 1, 1968

By A. W. Schlechten

The proposition is advanced that edutcation specifically for exlractive metallurgy is desirable not because the course content is cmique but rather as a means of indoctrinating the student with a backgrocmd that will give him an interest and pride in the profession. Factors that have caused the decline in enrollment in metallurgical engineering courses emphasizing extractive processes are being overcome. There is a need to distinguish between the sciences of metallurgy and the engineering applications to avoid confusion both in and out of the profession. AS a first step in preparing the 1967 EMD Lecture I searched the literature to determine what my predecessors had done hoping thereby to gain some clues for my own performance. The Transactions of the Metallurgical Society show that the first EMD Lec- turer in 1959 was Dr. W. J. Kroll, known chiefly today for his pioneering work on the production of titanium and zirconium, but equally respected by an earlier generation for his contributions to lead refining. He has been followed by a series of well-known and competent metallurgists all possessing specialized knowledge that has served as a basis for their lectures. The EMD Lectures have in general been a review of the development of a certain aspect of the extractive metallurgical industry or a preview of a particular area of science or technology that has applications in extractive metallurgy. The usual format is to describe developments of the past, summarize the present state of knowledge, and make predictions for the future. There has been great variation in the relative amount of time devoted to these three subdivisions, the past, the present, and the future. For example, Professor Gaudin, the 1961 EMD Lecturer, in speaking of Separation Engineering on the Moon, did not have too many examples of past practice and so had to emphasize the future. It is cheering to observe that all of these authorities were optimistic in their predictions. Despite the fact that four of the previous EMD Lecturers have been educators, Professors Gaudin, Pidgeon, Schuhmann, and Kellogg, none of them discussed the subject of education for extractive metallurgists. I might say parenthetically that lecturers in other divisions, such as B. M. Larsen, J. B. Austin, F. D. Richardson, John Chipman, and R. F. Mehl, have commented with concern on the present state of training for extractive metallurgy. What can you say that is new about extractive metallurgy education? Certainly nothing new can be said about the educational process itself. Professional educators do have new approaches to teaching and learn-

Jan 1, 1968

By C. C. Harris

A critical literature review leads to a descriptive model of tumbling mill operation based upon energy partition concepts and the necessary requirements for particle fracture. As grinding proceeds into the ultra-fine region, conditions which are of little significance during normal operations gradually become controlling. These involve increasing resistance to fracture and an increasing tendency to aggregate as particles become smaller, and a growing fraction of the power input being consumed fruitlessly. The result is that fineness asymptotes to a maximum value as comminution proceeds indefinitely; thus where t is time, p and n are experimentally determined parameters, and Ø is a measure of fineness, which is presumed to be proportional to specific surface area, or proportional to the reciprocal of the size modulus (provided that the distribution modulus remains constant with time), or both. Ø, is the asymptotic value of Ø and is a measure of the grind limit. A method for its graphical determination is given. In a previous paper1 the physical and mathematical principles requisite to a study of the role of energy in comminution were reviewed. The micro-process of comminution — or the comminution event — can be investigated in terms of (a) the magnitude of the force-field localized around the individual particles which gives rise to the stresses generated in the particles, which in turn induces their fracture, and (b) the distribution of fragment sizes, should the event prove fruitful. The entire fragmentation operation can be considered to be the totality of its individual events, and in order to obtain a single independent variable of the process it is necessary to transform and sum the local stresses in terms of energy.1 This energy, however, will account for only a fraction of the energy input to the comminution process, the actual magnitude depending upon the kind of mill and several related factors. From the comminution viewpoint the primary function of a mill is that of stressing as many as possible of the individual particles of the charge to failure, with the maximum economy of energy expenditure. This is difficult indeed to achieve, for stressing a particle does not always break it, while the overwhelming portion of the energy input is involved with various internal mill processes which — almost incidentally — determine the magnitude, frequency, and manner in which the forces are applied to the particles. Essentially, these processes depend upon the mill dimensions, loading and speed, and they may be little affected whether fracture occurs or not. These processes must be delineated if a complete description of the role of energy in comminution is to be given; the energy account sheet1 (Fig. 1) in showing how the energy is partitioned for the requirements of the several functions it performs, provides a framework for the development of a model of the comminution process. Actual numerical values for the variables appearing in Fig. 1 will depend upon the mill, materials, and operating conditions. A possible general relationship between the variables will be suggested in this paper. Before proceeding further, a cautionary note must be issued. It was pointed out in an earlier paper&apos; that while energy input is not changed by increasing the power and decreasing the time in the same proportion, and vice versa, the results of the process in terms of particle fineness may be different. Thus, although energy is chosen as the independent variable of a comminution process, it is not absolutely independent, and care must be exercised to ensure that it is used within its range of valid application. Time has the necessary independence, and it will be used in place of energy where it is appropriate. The residence time in a mill is usually of the order of minutes. Under these conditions the particles are subjected to "... a relatively constant fracture producing environment".2 However, under the more rigorous conditions of greatly extended time, which pertain in ultra-fine grinding, indications are that the fracture producing environment no longer remains constant; this is the major subject of this paper. At this extreme limit the mill is probably taxed to its utmost, and at the same time the bulk material properties are becoming closer to ideal, while the physico chemical effects associated with surfaces, edges and corners are multiplying. (The edge length per unit volume is proportional to the square of the specific

Jan 1, 1968

By Frank W. Dickson, George Tunell

Five hot spring areas of the western United States show evidences of present day deposition of HgS; two also show evidences of accompanying Sb2S3 deposition. Sulfide minerals are depositing at or near the surface from hot waters that differ for each spring ai:ea in amount and kinds of dissolved matter. All the springs contain dissolved substances that act as buffering agents and that cause increased alkalinity with increasing temperature. Transport of Sb2S3 is possible in H2O and in boron and sulfide solutions. Increasing alkalinity and temperature enhance stibnite solubility. Quantitatively important transport of HgS appears restricted to alkaline sulfide solutions that contain HgS2=. Elemental mercury probably forms in deep hot waters because HgS breaks down into mercury and sulfur above 200°C, and free S is removed by reaction with water. Elemental mercury should accompany HgS2= in solutions that were at 200°C or higher. Cinnabar deposits from saturated alkaline sulfide solutions because of combinations of temperature decrease, dilution, oxidation, and reactions with wall rock: Amedee Hot Springs, Boiling Springs, and Coso Hot Springs are areas in which HgS is the only sulfide deposited. Hot waters at Amedee and Boiling Springs are supersaturated with HgS or transport colloidal HgS. Steamboat Springs waters deposit mainly silica and stibnite, but they have deposited HgS recently. Sulphur Bank waters deposit mostly stibnite and some HgS. The hot-spring waters of all springs represent highly modified deep water. Field and laboratory studies support the concept of transport of HgS in moderately alkaline sulfide solutions as HgS2=. Fluctuating deposition of stibnite and cinnabar reflects availability of sulfide or variations in deep-source HgS and Sb,S,. Silica and HgS dissolve mutually in alkaline sulfide solutions, and cinnabar and quartz would be expected to deposit simultaneously. Free mercury given off by hot-spring waters would impregnate country rocks.

Jan 1, 1968

By B. H. Kear, B. J. Piearcey

The orientation and temperature dependence of the tensile and creep propevties oj Mav-M200 crystals halle been determined. Crystals oriented for single slip exhibit ,maximum ductility, minimum work hardening, and least creep resistance, whereas crystals in multiple slip orientations show nzinimu~n ductility, strongest work hardening, and greatest creep resistance. At 1400" and 1600°F there is a marked improzlenzent in creep strength for orientations approaching [001] and [111], indicating that interactions between dislocations gliding in intersecting octahedral slip systems play an important role in creep resistance. At 1800°F the creep strength is much less dependent on orientation, which is rationalized in terms of slip in cube planes as well as octahedral A frequent mode of failure in high-strength cast nickel-base superalloys is by intergranular fracture, particularly along those grain boundaries oriented transverse to the major stress axis. VerSnyder and ~uard&apos; demonstrated that this problem could be overcome by eliminating transverse grain boundaries through unidirectional solidification. Piearcey and versnyder2 made use of this principle in the development of unidirectionally solidified gas turbine blades and vanes, where the growth direction of the columnar grain structure coincides with the axis of principal stress under operating conditions. The present investigation was undertaken to determine if further improvement in properties may be obtained by eliminating grain boundaries altogether, so as to take advantage of the well-known dependence of mechanical properties of single crystals upon the orientation. 1) EXPERIMENTAL PROCEDURE Single crystals of Mar-M200* were grown from the melt under vacuum by a modified Bridgman method. The melt was poured into a preheated alumina mold, and crystal growth was promoted from one end by appropriate gradient cooling. Tensile and creep specimens (2 in. diam by $ in. gage length) were prepared by a series of operations involving electrical discharge machining, precision grinding, and electropolishing. The orientations of the specimens were determined by the Laue X-ray back-reflection method. Tensile tests were carried out in aWiedemann machine with furnace attachment, using a strain rate planes. In all orientations imzpvouement in the strength charactevistics of the material can be induced by heat treatment. Creep ad stress rupture data for (001) oriented crystals are compared with similar data obtailted previously joy random polycvystalline material, and also columnar grained material having a prejevved (001) orientation. The single-crystal )material exhibits both longer rupture life and lower minimum creep rate at all temperatuves, and the rupture elongation is comparable with that in the columnar grained material. From these results it is concluded that single crystals should and useful application in gas-turbine blades and tanes. The optimum orientation for a blade is considered to be with its axis of principal stvess parallel to (001) ou (111). of 0.0001 sec-&apos;. Load and extension were recorded directly on an X-Y recorder. The strain measuring device consisted of extension arms attached to the grips at one end and leading out of the furnace to an LVDT (linear variable differential transformer) at the other. Creep tests were performed using a standard constant load creep frame. 2) DISCUSSION OF RESULTS 2.1) Structure of Alloy. The structure and segregation in as-cast and heat-treated Mar-M200 has been described in detail else where.~ The main features are as follows: the as-cast material is heavily cored, due to pronounced dendritic segregation during solidification; the dendrites are rich in tungsten and cobalt whereas the interdendritic regions are rich in chromium, titanium, nickel, and carbon. The structure consists of -60 vol pct coherent precipitate of y&apos;, basically Ni3(A1,Ti), in a matrix of y (nickel-base solid solution), interspersed in the interdendritic regions with minor MC carbides and -y&apos; eutectic. The y&apos; particles, and y-y&apos; eutectic, contain more titanium, aluminum, and nickel, and less tungsten, cobalt, and chromium than the y matrix. Heat treatment partially removes segregation, eliminates the eutectic, refines the y&apos; dispersion in y, and gives additional partially coherent M23Cs carbide. An as-cast crystal, therefore, is composed primarily of two oriented phases (y + y&apos;), whereas the normally heat-treated crystal consists of three oriented phases (y + y&apos; + MZ3Cs). Typical electron transmission micrographs of the y + y&apos; structure are shown in Fig. 1. Crystals grown in the (100) orientation develop a simple unidirectional dendritic structure, Fig. 2, since (100) happens to be the preferred direction of growth for dendrites in this material. Crystals grown in the {110) and (111) orientations, however, tend to promote equal growth, generally in separate colonies, in the two and three geometrically favored (100) growth directions, respectively. In other orientations of growth, a single (100) dendrite direction generally pre-

Jan 1, 1968

By E. Miller, J. M. Eldridge, K. L. Komarek

Aclivilies of magnesium in liquid Alg-Si alloys have been delermined between 5 and 60 at. pcl Si, close to the melling point of Mg2Si, by an improved isopieslic melhod. Silicon specinrens, held in alumina crucibles and graplrile conlainevs of special design, were healed in a letrlpevalure gvadient and equilibrated with mag-nesilcrrl rapor in a closed lilanium system. The ther-madynamic Junctions were calculated and compared with the thermodyuamic properties of the other three mg- Gvoup IVB systems. Lattice paramelers of three Mg2X compounds were measured. The bonding in the Mg2X compounds is largely covalent with small and uarying amounts of metallic and ionic conlvibutions. The Mg-Si phase diagram1 has one congruent melting compound, Mg2Si, of essentially stoichiometric composition, two eutectics, and very limited terminal solid solubilities. Little information is available on the thermodynamic properties of this system. The free energy of formation of Mg2Si has been determined by the Knudsen cell technique2 in the range 572" to 680oC, by the transportation method3 between 858" and 950oC, and by the electromotive-force method4 in the range 400o to 600°C. Kubaschewski and villa5 and caulfield6 have measured the heat of formation of Mg2Si. An electromotive-force study of magnesium-rich liquid alloys was recently published by Sryvalin el al.7 The present investigation was undertaken to complete a general survey of the thermodynamic properties of the homologous series of Mg-Group IVB systems, i.e., Mg-Pb,a9,Mg-Sn,10,11 mg-Ge,12and Mg-Si. An isopiestic technique, previously developed for similar measurements on liquid Mg-sn11 and Mg-Ge alloys,12 was modified for the Mg-Si system. Specimens of the nonvolatile component, silicon, were contained in dense alumina crucibles placed inside covered graphite crucibles which were heated in a temperature gradient in an evacuated and sealed titanium reaction tube and equilibrated with magnesium vapor of known vapor pressure. The alumina crucibles prevented contact between the highly corrosive liquid Mg-Si alloys and graphite. The graphite cruci- bles effectively preserved the high-temperature equilibrium composition of the liquid alloys containing highly volatile magnesium on termination of the experiments during the quench to room temperature. EXPERIMENTAL PROCEDURE Silicon of semiconductor-grade purity (E. I. du Pont de Nemours and Co., Brevard, N.C.) and 99.99+ pct Mg (Dominion Magnesium Ltd., Toronto, Canada) were used. Graphite crucibles with press-fitted lids were machined from high-density (1.92 g per cu cm) rods (Basic Carbon Corp., Sanborn, N.Y.) which had a maximum ash content of less than 0.04 pct. The alumina crucibles had a purity of 99.7+ pct (Triangle RR grade, Morganite, Inc., Long Island City, N.Y.). In preliminary runs the liquid alloys were contained in graphite crucibles following the exact procedure developed for the Mg-Ge system.&apos;2 These runs failed due to appreciable reaction between the molten Mg-Si alloys and graphite, and the results have been discarded. The procedure was then modified and the Mg-Si alloys were subsequently held in alumina crucibles. For most of the runs alumina crucibles of known weight and approximately 6.3 mm ID, 12.5 mm height, 1.0 mm wall thickness were loaded with weighed amounts of silicon and encapsuled in tightly covered weighed graphite crucibles 5/16 in. ID, 2 in. helght, 3/32 in. wall thickness). The graphite crucibles were machined from rods which were 85 pct of the theoretical density. These crucibles were therefore sufficiently porous so as to permit magnesium vapor to effuse through the silicon under the experimental conditions of approximately 970O to 1220°C and 1 day equilibration time. However, negligible magnesium was lost from the crucible during the quench due to the slow effusion rate through the pores of the graphite. The inner alumina crucible prevented the liquid alloys from contacting the graphite, and the very tightly fitting graphite crucible lids served to retain any magnesium vaporizing from the alloys inside the crucibles during the quenching step.12 The loaded silicon-alumina-graphite cells were positioned, one above another, on a 16-in.-long titanium thermocouple well and tied securely to the titanium tube with thin molybdenum wires held in grooves around the circumference of the graphite crucibles. A thin (0.005-in.) molybdenum strip prevented contact between the graphite crucibles and the titanium. This assembly was lowered into a titanium reaction tube (la in. ID, 16 in. long, $ in. wall thickness) closed on one end which contained a 11/2-in.-long cylinder of magnesium at the bottom. The inner titanium thermocouple well was positioned eccentrically in the large tube because of the eccentric mounting of the cells on the well. Appropriate modifications of the titanium cap"&apos;12 were made to join the inner and outer titanium

Jan 1, 1968

By Cyril Jones

13.9-1. Introduction. Any mining venture or project is undertaken with a view of gaining some benefits, which, with the modern limited corporation, means earning a return to the stockholders for the use of their funds. Thus, any manager, when confronted by an opportunity of expending funds, must realize that the funds should generate a satisfactory return. The problem then becomes one of how the manager should best expend, if he should expend, funds for opportunities that become available to him. In the evaluation of a mineral property, or of a project within an operating mineral property, there must be cognizance of the fact that the final return is dependent on many factors that are not present in other industries. The primary factor in mining operations is the orebody, which has a diminishing life. This diminishing life gives the decision maker a range of choices; for by expending more capital for a larger plant, he can work the deposit out in a shorter period (16). This may, in fact, maximize the return on the investment. Alternatively, he may wish to maximize the total profits, a course which usually requires a lower capital investment and allows a longer working life for the deposit before final depletion. Other factors that have great importance in the evaluation of mining projects are the taxation treatment of mining profits from the viewpoint of depletion, depreciation, and investment credit. Investment opportunities involve expending funds at the present time in return for future benefits. These future benefits have a degree of risk in that the annual amounts of benefits and their duration cannot be fore- cast accurately. The treatment of risk in economic analysis involves the quantification of the degree of variability of the expected future benefits and also of the initial capital expenditure. This treatment in mineral exploration may be extended to cover the initial search for an orebody

Jan 1, 1968

By B. E. Terkelsen, B. J. Piearcey

A study has been made of the effect of unidirectional solidification on the creep behavior, stress-rupture properties, and thermal shock resistance of four nickel-base superalloys. The alloys Mar-MZOO, B-1900, IN 100, and TRW 1900 show improved rupture ductility and thermal shock resistance when tested with the columnar grains parallel to the major stress axis during test. The relative improvement in creep-rupture properties depends on the intrinsic strength of the alloy, a property which depends on composition, heat-treatnient, and crystallographic orientation. The data clarifies some of the factors affecting the properlies of the cast nickel-base superalloy. COMPONENTS designed for high-temperature use have, in recent years, been fabricated by precision casting techniques using nickel-base alloys developed specifically for use in the conventionally cast condition. This development was a result of both the increasing complexity of the component and the recognition that high-temperature strength was incompatible with workability. The use of castings can be economically favorable, but, more important, the recent complex designs of air-cooled gas turbine blades and vanes in alloys which possess the necessary high-temperature strength cannot be forged. Common modes of failure of high-temperature components are excessive creep, creep rupture, and thermal fatigue. If rupture occurs then the mechanism is usually by inter crystalline cracking along those grain boundaries oriented transverse to the major stress axis. In the stronger alloys, rapid propagation of intercrystalline cracks result in apparent premature failure demonstrated by the absence of third stage creep in a creep-rupture test and low rupture ductility. Tensile ductility shows a similar trend, that is, decreasing ductility with increase in strength. It is not surprising, therefore, that increases in creep strength have only been obtained with a loss in resistance to thermal shock, a property which shows a dependence on tensile ductility. VerSnyder and ~uard&apos; showed that the application of unidirectional solidification to a brittle Ni-Cr-A1 alloy both improved the rupture life of the alloy and increased rupture ductility. Since this casting method results in columnar grains, it appeared that the solution to the lack of ductility in nickel-base alloy components was the elimination of the source of failure, namely the transverse grain boundaries. This concept was recently developed2 to produce cast-to-size gas-turbine blades and vanes consisting entirely of columnar grains oriented parallel to the major stress axis of the component. Not only did the process impart increased rupture life and ductility to the components, but it also increased their resistance to thermal shock. During this development, the effect of unidirectional solidification on the properties of several alloys was investigated. The resulting data allows certain conclusions to be drawn regarding the factors affecting the creep and stress-rupture properties of the cast nickel-base superalloy and also its resistance to thermal shock. Detailed information was obtained on the alloys Mar-MZOO, B-1900, In 100, and TRW 1900. The composition of the alloys studied are shown in Table I. MATERIAL PREPARATION AND TESTING The conventionally cast alloys are cast as +-in.-diam bars in innoculated shell molds under conditions designed to maintain control of grain size. Unidirec-tionally solidified casting were produced in the form of 3-in.-diam ingots. Specimens from the latter were machined such that the axes of the columnar grains were parallel with the axis of the test bar, except in certain cases where the transverse properties of the material were being evaluated. The specimens were tested in an axial loading creep machine.&apos; Temperatures were measured with thermocouples, attached just outside each end of the gage length, to assure uniform temperature along the entire specimen. Chromel/alumel thermocouples were used up to 1800"F and Pt/Pt-10 pct Rh thermocouples above 1800"F. The specimen temperature was recorded and maintained within i2"F throughout the test. Creep extensions were measured automatically with extenso-meters attached to ridges on the specimen and recorded continuously using linear variable differential transformers and multipoint recording equipment. MICROSTRUCTURE The microstructures of transverse sections of the four alloys studied are shown in Figs. 1 and 2. Fig. 1 shows optical micrographs of the alloys, both in the conventionally cast and unidirectionally solidified conditions. Each alloy displays a cored dendritic structure, a distribution of MC carbide, and the presence of the y — y&apos; eutectic constituent.~ In the case of IN 100 and B-1900, Fig. 1 indicates that in these specimens the eutectic is degenerate. That is, it consists only of y&apos; pools indicating that the y constituent has been solutioned during the cooling period after solidification. The major effect of unidirectional solidification on the microstructures of the alloys is a tendency to promote a more dendritic form of MC carbide and an increase in dendrite arm spacing, both effects being a result of the slower solidification rate in the unidirectional solidification technique. V, lec tron micrographs of transverse sections of the four alloys in the two cast conditions are shown in

Jan 1, 1968

By R. W. Smashey, B. J. Piearcey

The structure, composition, and morphology of the carbide phases present in the nickel-base superalloy, Mar-M200, hare been determined and three carbide phases observed. The MC carbide is a solidification product, and the M23 Co and M6C carbides are both prod~icts of solid-state precipitation. The identity of each phase usas determined by both X-ray and electron-diffraction techn~ques. Compositions of all three carbides were studied using the electron beam micro-probe analyzer and by unalyszs of electrolytically extracted residues. Optical and electron microscopy were employed in order that the time/temperature -dependent behavior of the carbides might be observed. Supplementary studies were completed on thin foils and oriented single crystals to determine the mor-phology and orientation relationship of each phase with that of the matrix. MAR-M~OO* is a high-temperature, creep-resistant superalloy designed for use in the as-cast condition. The "as-cast" microstructure consists of a solid-solution matrix, referred to as gamma (y), which contains a general, coherent precipitate of the inter-metallic Ni3(A1,Ti) referred to as gamma prime (?). As a result of dendritic segregation during solidification, a degenerate, spherulitic ? -?&apos; eutectic constituent is present at the grain boundaries and the in-terdendritic regions, which is nucleated by the y on the dendrite tips. A primary carbide phase, a solidification product, is also present at the grain boundaries and in the interdendritic areas, and an additional carbide appears at the grain boundaries as a fine discontinuous precipitate. The alloy is particularly susceptible to heat treatment. For example, the mechanical properties of the columnar grained mater- ial are substantially improved by solution heat treatment, followed by an intermediate temperature age. Metallographic examination of heat-treated material reveals, however, that exposure to elevated temperatures has a marked effect on the microstructure of the alloy; in particular, it is observed that precipitation of considerable amounts of various carbide phases occur. The following investigation was carried out to determine the morphology, composition, and behavior of the carbides in Mar-Ma00 as an aid to the determination of their effect on the mechanical properties and stability of the alloy. THE PRIMARY MC CARBIDE The MC carbide phase appears in the interdendritic interstices and the grain boundaries. In directionally solidified Mar-M200 the carbide appears as very small particles in the chilled region, Fig. l(a), whereas in material less affected by the chill, it becomes larger and develops a dendritic morphology, Fig. 1(b). Step polishing of metallographic specimens from this region shows that in directionally solidified material the individual carbide dendrites are connected in a dendritic network within the metallic interdendritic interstices, whereas in material from the chilled region and in conventional Mar-M200 they are discontinuous, isolated dendrites. No orientation relationship exists between the primary carbide and the matrix.

Jan 1, 1968

By Wilbur S. Burbank, Robert G. Leudke

The impressive western San Juan Mountains of Colorado were carved by Pleistocene and Recent erosion from a thick blanket of Tertiary volcanic rocks that rests upon a basement of metamorphic, sedimentary, and igneous rocks ranging in age from Precambrian to Tertiary. These rocks record a long, complex, and fairly complete sequence of geologic events that have affected the region through much of geologic time. The geologic history of the region includes several periods of deformation, erosion, and igneous activity; closely associated with two of these periods were two periods of mineralization. The older of these was related to Late Cretaceous-early Tertiary (Laramide) intrusive activity, and its deposits occur in the older sedimentary units. The younger, of later Tertiary age and related to the widespread middle Tertiary extrusive and intrusive activity, is the chief concern of this paper. Tertiary volcanism built a great plateau surrounding the San Juan volcanic depression, a complex of subsided crustal blocks in the vent areas. The Silverton and Lake City cauldrons, nested within the larger depression, were domed by resurgent magma that created keystone grabens along the distended crests of the domed floors and many postcauldron radial and concentric fractures, dikes, and intrusive plutons within and marginal to the cauldron sites. The postvolcanic evolution of large quantities of gases, chiefly carbon dioxide and water, propylitically altered the rocks in and around the volcanic depression prior to the younger period of ore deposition. The ore deposits, localized mainly in the radial and concentric fractures about the cauldrons and in the associated graben faults, include fissure veins, chimneys, replacements, and disseminations in volcanic and underlying basement rocks. Fissure veins, constituting the major economic source, yielded precious- and basemetal ores. Most veins are compound with sphalerite, galena, and chalcopyrite; some veins contain silver-bearing arsenical sulfosalts and free gold. These minerals occur in predominantly quartz gangue. However, gangues composed of several manganese silicates and carbonates and relatively· barren of metals are abundant locally and probably originated by alteration of rocks at roots of faults and fissures during evolution of carbonatic solutions. The bulk of the ores are hypogene and probably had their source in deep parent magmas of the shallow eruptive rocks. Total production since the early 1870's has exceeded half a billion dollars in recovered metals, with a ratio of precious- to base-metal values of about 3 to 2. Since 1930, improvements in metallurgical treatment and mining techniques have increased the base-metal yield.

Jan 1, 1968

Jan 1, 1968

By Paul F. Kerr, Donald M. Hausen

Fine colloidal gold near Carlin, Nevada is disseminated in leached carbonate strata of the Roberts Mountains Formation in the Lynn "window" of the Roberts Mountains thrust fault. The ore body is generally stratiform and is more or less conformable to altered beds near the top of the formation, underlying Devonian limestones. Two sequences of mineralization are recognized: ( 1) an earlier base metal-barite assemblage related to early Cretaceous intrusives (121 ± 5 m.y.), and (2) a later low temperature Au-As-Hg-Sb assemblage of near surface emplacement. The earlier sequence consisting of sparse galena and sphalerite in barite with anomalous amounts of zinc, lead, nickel and copper, associated with dikes of dacitic composition, is of little economic importance. The later sequence of gold, realgar, cinnabar, and stibnite associated with extensive silicification and argillic alteration of limestone beds, has resulted in important deposits of gold. Argillic alteration of hydrothermally leached carbonate strata has provided the environment in which the most prominent gold deposition took place. Carbonate minerals in the limestone host rock have been replaced by microcrystalline quartz and chalcedony to form stratiform silica masses and recrystallized lenses of euhedral quartz. Zones of porous silicification are light gray to white, elliptical in shape, and more or less follow bedding. Silicification is bordered by argillic alteration and pyritization. Deposition of gold usually lies in a zonal pattern that encircles chimney areas of silicification.

Jan 1, 1968

By P. Chiotti, R. J. Hecht

Vapov pressure data of solid and liquid alloys along with phase diagram data WERE employed in calculating the thermodynamic properties for the Ca-Zn system. The relative excess partial molal free energy for zinc in the liquid alloys was fitted to the relation wnvre i is we tvmpvrutiirc in ucgrees neivtu ana in is the tr~ole fvaction. Relations for the standard free energy of fortnation for the eight cornpounds were developed. ThE phase diagram for the Ca-Zn system as determined by Messing et a1.&apos; is reproduced in Fig. 1. Earlier work on the phase diagram has been summarized by Hansen and Anderko2 and the very limited thermodynamic information for this system has been reviewed by Hultgren et a1.3 The heat of fusion for the compound CaZn2 has recently been determined to be 9260 cal per mole.4 Solubility data for calcium in zinc for the temperature range of 650" to 725°C were fitted by the relation and reported by Johnson and Dilloon5 In the present investigation zinc vapor pressure data were obtained by both the dewpoint and Knudsen methods in order to calculate the thermodynamic properties for liquid and solid alloys. The dewpoint method as employed in this work requires that only one of the components be significantly volatile, in this case zinc, and that the vapor pressure of pure zinc be known. For calculation purposes the vapor pressure data for pure zinc3 were fitted to the relations; for temperatures below 692.7K, the melting point of zinc. The corresponding free-energy relations for vaporization and sublimation of pure zinc are respectively. Some of the calculations also required knowledge of the free energy of fusion of zinc and calcium and the free energy for the 721°K allotropic transformation of calcium. The free energy of fusion of zinc was taken to be the difference between Eqs. [4] and [5], or The free energy of fusion and transition for calcium were based on the enthalpy values of 2040 and 222 cal per g-atom, respectively, as reported by Chiotti et al. 4 and the heat capacity data given by Hultgren et a1.3 and are represented by the relations, In the latter expression the difference in heat capacity between the a and 0 forms of calcium was neglected. MATERIALS AND EXPERIMENTAL PROCEDURES The metals used in preparing the alloys were Bunker Hill slab zinc, 99.99 pct pure, and Ames Laboratory calcium. The average impurities in the calcium in parts per million by weight, ppm, were N-17, H—77, Ba—216, Mg-15, Si—7, C—157, and Fe—9. The zinc was cleaned in dilute nitric acid and the calcium was used as received. The calcium was stored and handled in an argon-filled glove box and when removed from the dry box it was kept in an argon-filled desiccator. Tantalum was found to be a suitable alloy container. The alloy components were contained in a 1-in.-diam cylindri-

Jan 1, 1968

Jan 1, 1968

By T. L. Berger, M. C. lnman, M. F. Rose

AFTER shock loading, mechanical twinning has been observed by several authors1-4 for a variety of fcc metals and alloys. It has been shown2,3 that low stacking fault energy materials deform primarily by the formation of mechanical twins and stacking faults during dynamic loading. Further, Inman, Murr, and Rose2 have shown that a correlation exists between the average hardness and the volume percent of mechanically twinned material in stainless steel. It has been observed in nickel&apos; that mechanical twins are produced during shock deformation if the peak pressure associated with the shock wave is greater than 350kbar. It is the purpose of this work to discuss shock-hardening mechanisms in nickel and to determine to what extent the initial condition influences the final response. The "flying plate technique" was used to generate planar shock waves with peak pressures as high as 710 kbar. The details of the technique5" have been discussed elsewhere and will not be repeated here. The material used in this study was polycrystalline nickel of 99.98 pct purity and had an initial grain size of 0.18 mm. Prior to any deformation, all samples were given a stress-relief anneal of 6 hr at 600°C in a vacuum furnace. After annealing, the initial condition of the samples was changed by cold rolling individual samples from 0 pct to a maximum of 80 pct reduction in thickness. This provided samples with controlled initial histories for shock deformation. Immediately after shock loading, the specimens were slowed and quenched by suitable arrangement of buffer material and water bath. This technique minimized specimen damage and the effects of shock heating on the samples. Since deformation twins in high stacking fault energy fcc metals are only produced at high stress levels, the initial defect configuration prior to mechanical twinning should greatly influence the number of twins formed. In fact, Zukas and Fowler7 have found that prestraining in iron and steel greatly suppresses the formation of mechanical twins during the shock deformation process. Following the methods of Warren and warekois8 and Cohen and Wagner,9 X-ray diffraction profile analysis was performed to determine the incidence of stacking faults and mechanical twins in the deformed nickel. Analysis was made on samples in the annealed, cold-rolled, shock-loaded, and cold-rolled—shock-loaded states. The estimated accuracy of the peak position measurements is *0.01 deg in 2?. Therefore the accuracy in the measurement of the relative peak shifts between the (400) and (222) diffraction line profiles is on the order of *0.04 deg in 2?. None of our measurements indicated peak shifts greater than 0.04 in 28. This would correspond to a fault density of -1 pct and sets the limit on the sensitivity of our instrument. Similarly, analysis of the shift in the center of gravity of the diffraction line profiles yields the minimum measurable value of the twin fault probabilitya to be -0.002. Fig. 1 shows mechanical twinning in nickel shock-loaded to 400 kbar. In this photograph, fault intersections are clearly visible. The thickness of the individual fault lamellae was determined from the image widths of their lines of intersections by the

Jan 1, 1968

By Raymond F. Gray, Victor J. Hoffman, Richard J. Bagan, Harold L. McKinley

The first indication of tungsten in the Bishop area was the discovery of scheelite concentrations in a gold placer operation in the ( since named) Tungsten Hills in 1913. After early intermittent production, the deposits of the district were slowly discovered and developed. The Pine Creek mine, located in 1916 and under the direction of Union Carbide Corporation since 1935, became the principal producer in the district. By the end of 1965, the total production of the district had reached 3,450,932 units of WO3, 17,071,242 pounds of molybdenum, and 19,599,110 pounds of copper. The topography of the district is characterized by its extreme relief, ranging in elevation from 13,986 feet to about 4400 feet in the Mount Tom quadrangle. The present topography is the result of the uplift and erosion of the Sierra Nevada and the great subsidence of the Owens Valley with its related deposition and volcanism. The general structure of the pre-Tertiary rocks consists of a series of tightly-folded metasedimentary and metavolcanic rock remnants surrounded by exposed plutons ranging in composition from hornblende gabbro to alaskite. The metasedimentary rocks consist of low- to intermediate-grade metamorphic equivalents of fine-grained sediments deposited during the Paleozoic era in a miogeosynclinal environment. Later volcanics were deposited in a eugeosyncline. The ore bodies in the Bishop district consist of scheelite-bearing tactite formed by the pyrometasomatic replacement* of calcareous sediments along the contact with an acidic granitic intrusive. A number of the metasedimentary remnants have had tungsten deposited along their edges.

Jan 1, 1968

By C. E. Brukl, E. Rudy, St. Windisch

The ternary-alloy system Nb-Mo-C was investigated by means of X-ray, melting point, DTA, and metallo-graphic techniques; a complete phase diagram for temperatures above 1500°C was established. Above 1960°C, niobium monocarbide and the cubic (Bl) high-tenzperature phase in the Mo-C system form an uninterrupted series of solid solutions. The ternary range of the pseudocubic q MoCl-, is very restricted. Dimolyb-denum carbide dissolves up to 44 mol pct Nb2C (2240°C), whereas the maximum solid solubility of MO2C in Nb2C does not exceed 5 mol pct. The order-disorder transformation temperatures in Mo2C and Nb2C are lowered by the mutual metal exchanges. Six invariant (p = const) reactzons occur in the ternary system; three correspond to class 11-type four-phase reactions involving a liquid phase, one to a class I (eutectoid)-type, and two further isotherms are associated with limiting tie lines. The results of the Phase diagram investigation are discussed, and the thermodynamic interpretation identifies the low relative stability of the binary sub-carbides in conjunction with the large stability diflerences between niobium and molybdenum carbides as the cause for the formation of a stable equilibrium between the monocarbide and the metal phase in the ternary reson. Due to their refractoriness, the carbides of the high-melting transition metals have received increased interest in recent years as base materials in composite structures for aerospace applications at high temperatures and for the development of self-bonded cutting tool materials; other novel fields of application include power reactors, where operation at high temperatures becomes essential for attaining high power efficiencies. In these applications, the increased reaction rates at high temperatures require a close consideration of the chemical interactions between the alloy constituents. As a consequence, a detailed knowledge of the phase relationships in the alloy systems is required in order to provide a sound basis for developmental -type work. Partly as a result of the considerable experimental difficulties associated with the investigation of this high-melting alloy class, no complete studies of ternary metal-carbon systems have been performed until recently. Even the high-temperature phase relationships in the binary transition metal-carbon systems have been delineated only during the past few years to a degree of accuracy required for a more detailed study of ternary or higher-order alloys. In recent investigations of binary and ternary systems of refractory transition metals with carbon, boron, and silicon,&apos; alloys from the ternary systems Nb-Mo-C became of interest because of the demonstrated possibility2,3 of obtaining compatible composites based on metal + monocarbide combinations. In the meantime, however, studies in other, but related, ternary metal-carbon systems, such as Ta-W-C, have shown that the solid-state equilibria may change significantly toward higher temperatures (>2000°C), and that extrapolations based on low-temperature equilibrium data are, in general, not very reliable. Although the lower-temperature (<2000°C) phase relationships in the Nb-Mo-C system are similar to those found in Ta-W-C, a cursory thermodynamic analysis of the equilibria indicated4 that complete solid-solution formation between Mo2C and Nb2C should not occur at higher temperatures. The present work was conducted in order to experimentally verify these expectations and, in addition, to provide phase equilibrium data in the melting range of the alloys. In the boundary systems, niobium and molybdenum are known to form a continuous series of solid solutions.576 The continuous solubility was also confirmed by Kornilov and Polyakova,7,8 who also observed a minimum melting point at 22 at. pct Mo and 2345°C. The phase diagram investigations of the Nb-C system by Storms and Krikorian9 and Kimura and Sasaki10 were recently supplemented by Rudy et al.11,12 The system contains a high-melting monocarbide with the B1 structure, Table I, and a subcarbide, Nb2C, which exists in at least two different states of sublattice order at low temperatures47"-&apos;3 and a disordered state above approximately 2500°C.11,12 The melting-point measurements by Rudy et al .11,14 are in close confirmation of the data by Kimura and Sasaki.10 The rather complex phase relationships in the Mo-C system were only recently Clarified.15,18 The system is characterized by three congruently melting, intermediate phases, MozC, ? MoC1-x and a Mol-,, Table I, of which only Mo2C is stable at temperatures below 1650°C. Substoichiometric MozC exists in several states of sublattice order which interconvert in homogeneous phase transitions. Hyperstoichiometric compositions cannot exist in the ordered state. Upon cooling through a critical temperature range, the

Jan 1, 1968