By Josef Intrater

A dilatometric determination of the a + ß region temperature limits was performed on vacuum melted Zircaloy-2. The temperature of transformation for a-a+ß and a+ß — ß on heating and cooling as a function of rate of heating and heat treating history was studied. The limits were found to be 815° to 830°C to 975° to 995°C on heating and from 960° to 930°C to 785° to 770°C on cooling. A 5° to 15°C increase was observed for a- a + ß with increased rate of heating and a 20° to 30°C decrease for ß - a + ß with increased rate of cooling. 1 HE transformation temperature for pure zirconium has been determined by many investigators1-5 using metallography, electrical resistivity measurements, and dilatometry. The effect of the rate of cooling on the transformation temperature of zirconium has been studied by Hayes and Kaufmann6 and Duwez,7 and the effect of alloying elements by pfei18 and McGeary.13 Since the development of Zircaloy-2, the limits of the a + ß region for that alloy have been also determined. The first reported temperature for the a — a + a transformation in Zircaloy-2 was 900°C and for a + ß - ß 1000C Subsequent studies by Picklesimer and damson" indicated the beginning of the transformation at 810°C, and the metallographic study by the Technology Group of the Special Materials Section at the Westinghouse Bettis plant1' suggested that 820°to 830°C is the temperature of transformation. The dilatometric investigation by the latter group yielded 830°C for the beginning of the transformation. Thomas and Forscher12 set the beginning of the transformation at 900 °C on heating and the end of the transformation at 870°C on cooling. The above investigators stated in their paper that the dilatometric curve exhibits features caused by a eutectoid reac-

Jan 1, 1962

By W. C. Leslie

The textures of cold-rolled and of annealed iron are compared with those of an iron-0.8 pct copper alloy in which the amount of precipitation after cold rolling was controlled. Previously published pole figures -for cold-rolled and for annealed iron are confirmed. The effects of precipztatiotz after cold rolling are to retain the cold-rolled texture after annealing, to inhibit the formation of the usual allnealing texture, and to produce elongated recrys-tallized ferrite grains. It is suggested that the inhibition of new textures by precipitation after cold rolling is a general phenomenon. A great deal of attention has been paid to the development of texture during the secondary or tertiary recrystallization of ferritic alloys, but very little work seems to have been done on the control of texture during primary recrystallization. If such control were attained, it might be possible to simplify the processing of oriented materials or to change the characteristics of current cold-rolled and an-nealed products. From previous experience, it seemed likely that texture could be controlled by recrystallizing a supersaturated solid solution. Green, Liebmann, and Yoshidal found that the formation of preferred orientation in aluminum (40 deg rotation about <111> relative to the deformed matrix) was inhibited when iron was retained in supersaturated solid solution in the strained aluminum. The authors attributed this inhibition to iron atoms in solid solution. There is, however, an alternative explanation. Green et al, took a highly supersaturated solution of iron in strained aluminum and heated it to an unspecified temperature for recrystallization. It is probable that precipitation occurred prior to and during recrystallization, and it is proposed that the inhibiting agent is this precipitate, rather than the iron atoms in solid solution. It is important to note that precipitation before cold work is ineffective; the effective precipitate is that formed after cold working and either before or during recrystallization. The location and distribution of the precipitate are critical. Precipitation in such a manner has been found to have profound effects upon kinetics of recrystallization and the microstruc-ture of the recrystallized alloys.2-4 It would be surprising, indeed, if this were accomplished with no change in texture. Because of the relative simplicity of the system, and because of previous experience,4-7 it was decided to determine the effect of precipitation on texture in an alloy of iron and copper. Bush and Lindsay5 found an unspecified change in texture in cold-rolled and annealed low-carbon rimmed steel sheets when the copper content exceeded 0.1 pct. MATERIALS In earlier work, the rate of recrystallization of a low-carbon steel was greatly decreased by 0.80 pct copper, and, after the proper treatment, the recrystallized ferrite grains were greatly elongated.4 Accordingly, it was decided to investigate the effect of precipitation on texture at this level of copper content. The iron and the iron-copper alloy were made from high-quality electrolytic iron and OFHC copper, vacuum-melted in MgO crucibles, cast, hot-rolled to 0.2 in., then machined to 0.150 in. The compositions are given in Table I. The plates were heated to 925°C and brine quenched, twice. This produced a ferrite grain size of ASTM 0 in the iron and ASTM 1 in the Fe-Cu alloy. Disk specimens were cut from the heat-treated plates, repeatedly polished and etched, then used to determine (110) and (200) pole figures by reflection. Despite the complication of large grain size, these pole figures strongly indicated a random texture. PROCEDURES The copper content in solid solution in ferrite before cold rolling and recrystallization, and hence, the amount that could precipitate during the recrys-tallization anneal, was controlled at three levels by heat treatment. The specimens as quenched from 925° C were presumed to have all the copper, 0.80 pct, in solid solution. Other samples of the quenched alloy were aged 5 hr at 700°C to retain about 0.5 pct Cu in solid solution.6 A third set of quenched specimens was reheated to 700°C, then slowly cooled in steps, to reduce the amount of copper in solid solution to a very low level. All specimens were cold-rolled 90 pct, from 0.150 to 0.015 in. thick. The rolling was done in one direction only, i.e., the strip was not reversed between passes, with a jig on the table of the mill to keep the short specimens at 90 deg to the rolls. The rolls were 5 in. in diameter and speed was 35 ft. per min. Machine oil was used as a lubricant. In a supersaturated alloy, the maximum effect of the copper precipitate on microstructure and on recrystallization can be developed by a treatment at 500°C, after cold rolling and before recrystallization.&apos;

Jan 1, 1962

By D. L. Wood, J. H. Westbrook

The tensile behaviors of the CsCl structure compound AgMg are extensively documented in terms of strain, strain rate, temperature, composition, and metallurgical processing treatment. The observations lend themselves to presentation in terns of three regimes of deformation behavior; 1) low temperatures where deformation is primarily by slip; 2) intermediate temperatures where the deformation mode is also slip but with the detailed behavior dominated by dislocation interactions with solute atoms; 3) high temperatures where defomation is primarily by diffusion controlled processes. Of all the material groups of potential interest as high-temperature structural materials, the inter-metallics have been the least studied, particularly with respect to their mechanical behavior. Moreover, the application and processing of intermetallics for uses which exploit their often unique physical properties have been impeded by a lack of understanding of their mechanical properties. Previous work in this area* has been largely *For a recent review, see Westbrook.&apos; exploratory, aimed on the one hand at the direct empirical development of materials of engineering utility and ,on the other at identification of the important parameters affecting the mechanical behavior of inter metallics. As a consequence, there has not been available, heretofore—for any inter-metallic—data, sufficient in extent or precision to provide an adequate phenomenological description of the effects of metallurgical variables on deformation behavior. Such documentation is prerequisite to intelligent application or processing design and is also necessary for testing present and future theoretical analyses of mechanical behavior. It was therefore an objective of the present investigation to document the deformation behavior of a simple ordered intermetallic over as wide a range as possible of all the usual metallurgical variables. The compound AgMg was chosen as the subject of this investigation because it met all of a group of desired criteria, namely: 1) congruent but moderate melting point; 2) simple crystal structure; 3) ordered structure persisting to the melting point; 4) broad solubilities for the component elements. The first and last criteria were expected to aid in the preparation of homogeneous single-phase specimens: the second and third to help simplify the

Jan 1, 1962

By J. A. Elias, R. H. Heyer, J. H. Smith

Plastic anisotropy determined by the ratio of width strain to thickness strain in tensile specimens of low-carbon steels is strongly related to crystallographic preferred orientation. Using(222) Pole figures, a method was developed which permits rapid Predictions of plastic anisotropy for any crystallographic texture or orientation. The method is applied to low-carbon steel sheets in which four different crystallographic orientations were produced by variations in cold rolling and annealing treatments. AnISOTROPIC behavior of metal sheets during plastic deformation has long been evident. A familiar example is earing in cup type draws. During tension testing of sheet specimens, anisotropy results in a difference in width strain as compared with thickness strain. Carpenter and Elam1 observed this phenomenon in single crystals of aluminum for both sheet and rod samples. Lankford, Snyder, and Bauscher2 made tension tests on sheet samples of aluminum-killed low-carbon steel to determine the ratio of the width-to-thickness strains, and showed that this ratio was related to drawing performance. Burns and Heyer3 calculated theoretical ratios of width strain to thickness strain for two specific orientations of the bee system, using <111> as the operative slip direction. These calculated values were in fairly good agreement with the ratios determined by tension tests of low-carbon steel sheets in which these preferred orientations existed. The high degree of plastic anisotropy of silicon steel sheets could also be predicted from their crystallographic structure by these calculations. The present study has been made to show that the anisotropy observed in plastic tensile straining is strongly orientation dependent and can be adequately predicted for many orientations and textures. PLASTIC STRAIN RATIO R In the region of uniform elongation of a tension test specimen the plastic deformation may proceed at different rates in the width and thickness directions. Such anisotropy has been described in the past by the plastic strain ratioR:

Jan 1, 1962

By R. W. Fountain, John Chipman

The solubility of nitrogen in Fe-B alloys (0.001 to 0.91 pet B) is determined by the Sieverts&apos; technique for temperatures of 950° to 1150°C. The activity coefficient of nitrogen is decreased by boron. The three-phase equilibrium between ? iron, BN, and gas is established and also the four-phase equilibrium between iron, BN, Fe2B, and gas. The above equilibria are calculated for a iron. The relation of these data to hardenability and strain aging of boron-treated steels is discussed. BORON additions are known to enhanbe the hardenability of heat-treatable steels and to assist in the control of strain aging in sheet steel for deep drawing. The increase in hardenability is explained by the theory that adsorption of boron on austenite grain boundaries reduces their free energy and thus retards ferrite and upper bainite nucleation.l,2 Digges and Reinhart3 have shown that the full effectiveness of boron in commercial steels is achieved only when strong nitride formers such as titanium and zirconium are also present. The influence of nitrogen on eliminating the boron contribution to hardenability was also demonstrated by Shyne and Morgan.4 These workers prepared Ni-Mo steels containing either nitrogen or boron or nitrogen plus boron. The nitrogen-plus-boron steels showed the lowest hardenability which was attributed to the presence of stable nucleating particles, presumably nitride. Morgan and Shyne5-7 have shown that boron in the amount of 0.007 pet will completely eliminate strain aging due to nitrogen in low-carbon, open-hearth steels. In addition, by proper control of the boron additions, a rimming steel can be produced. Since the effectiveness of boron on hardenability and eliminating strain aging is influenced by the amount and distribution of the nitrogen in the steel, the present study was. undertaken to determine the influence of boron on the solubility of nitrogen in iron. EXPERIMENTAL PROCEDURE The solubility of nitrogen in Fe-B alloys was measured by the method of Sieverts, which consists of determining the amount of gas dissolved by the metal in a constant volume system. The apparatus employed in this investigation and the experimental details have beendescribed previously.B AMcLeodgage was added to the apparatus to allow measurements at very low pressures. The alloys were melted at reduced pressure in a basic-lined induction furnace using electrolytic iron and ferroboron. Ferroboron was added after the primary deoxidation of the iron with carbon. Since it was difficult to attain a constant low level of oxygen by this procedure, silicon was added after the carbon deoxidation and prior to the ferr obor on addition. The alloys were castas 2-in. sq ingots, heated in argon at 1050loC, and forged to 1/4-in. plate. After forging, 1116 in. was machined from each side of the plate to remove any possible contamination, and it was then cold-rolled to 0.010-in. sheet. The sheet was cut into approximately 1/4-in. squares and pickled in an inhibited H2SO4 solution to ensure a clean surface. In the case of the boron alloys, a hydrogen treatment could not be used for surface cleaning because boron losses resulted. The composition of the alloys is given in Table I. For a solubility determination, a 75-g sample was inserted in a quartz tube and sealed in place in the apparatus. The entire system was evacuated at room temperature and leak tested for 24 hr. If no leaks were observed, the system was heated to the temperature of measurement and again leak tested for 24 hr. If no leaks were detected, the hot volume and solubility determinations were begun. The hot volume was determined at a constant temperature for each run by admitting successive amounts of argon and recording pressure vs volume, which, in all cases, resulted in a straightline relationship. The argon was then removed and the procedure repeated with nitrogen. Successive additions were made until the desired nitrogen content of the metal and equilibrium pressure of the system were obtained. The

Jan 1, 1962

By Colin C. Harris, Nathaniel Arbiter

The flotation operation can be analyzed in terms of three groups of variables. The first, largely independent of control by the operator, embraces the fixed physical and chemical properties of the ore minerals. The second includes all chemical and physical effects imposed on an ore after mining that influence its floatability. These can be either purposefully or accidentally applied. The third embodies the flotation-machine characteristics which realize the potential floatability of selected ore minerals in terms of grade and recovery levels. The machine effectiveness thus depends not only on its own contribution, but on the prior influence of all other variables on floatability. HISTORICAL DEVELOPMENT From the earliest days, flotation mills used many types of machines. Hoover 20 in 1914 mentioned as then important the Potter-Delprat tank for gas generation by acid, the DeBavay cones for skin flotation, the Elmore mixer and separation chamber for vacuum flotation, and his own modification of the Mineral Separation cell for the agitation froth process. Less important at the time were the MacQuisten tube and the Hyde cell. By 19274~ scores of machines had been developed and dozens had found their way into mills. From then on, however, under the scrutiny of competitive tests, many fell into disuse. Taggart in 19454~ classified processes broadly as skin flotation and froth flotation, dividing machines for the latter into the three categories: bubble column, pulp body, and combination.* Under &apos;bubble column&apos; he listed all pneumatic, cascade, and subaeration cells; and under &apos;pulp body&apos; those cells in which gas was generated by boiling, chemical action, and pressure reduction, as well as the agitation-froth type. At that writing skin flotation, the cascade machines, and all pulp body and combination machines were said to be extinct, leaving pneumatic and subaeration types dominant (u. S. practice). The process of elimination has continued to the present, with almost all pneumatic cells succumbing to the pressure of competition from subaeration machines. The only new machines to appear in recent years have been double-impeller types f and these have met with only limited acceptance.

Jan 1, 1962

By Harry A. Lipsitt, Rollins E. Hook, Attwell M. Adair

A necessary condition for a uniaxial stress distribution in compression testing is that the specimen end surfaces make full contact with the apparatus compression plates. In addition all compression surfaces must be machined perpendicularly to the loading axis. In general this condition is not sufficiently fulfilled in a simple apparatus. Therefore on application of the load the compression plate may first touch the specimen at one point only. This may cause crumbling of the specimen if the material under investigation is brittle (e.g., ionic crystals). It also precludes a precise study of the beginning of deformation as the effective cross sectional area is unknown. In addition a complex stress state is set up which renders quantitative work impossible, e.g., on dislocation density and arrangement as a function of stress. To overcome these difficulties a "self-adjusting" upper compression plate is required. A simple and reliable method of achieving this is shown in Fig. 1: A steel hemisphere is placed on the specimen. As soon as the compression plate (which no longer needs precise machining) makes contact with this hemisphere the load is uniformly distributed over the whole specimen surface, and a homogeneous uniaxial state of stress results. An advantage of the method is that the loading is always central, even when the specimen surface is not parallel to the compression plate (Fig. 1, dashed line). Therefore to a first approximation a uniaxial state of stress is maintained if the misorientation of the specimen end surface is small. Two typical stress strain curves of identically prepared sodium chloride crystals are shown in Fig. 2; curve 1 was taken without and curve II with the hemisphere under otherwise identical conditions. The improvement in the accuracy of defining the beginning of elastic and plastic deformation is clearly indicated. The writer wishes to thank the Deutsche Forschungsgemeinschaft for financial support, and Professor P. Haasen for providing facilities for this work.

Jan 1, 1962

By J. M. Markowitz

The movement of hydrogen in two-phase Zircaloy-2 under the influence of a thermal gradient was studied in specimens of cylindrical geometry. A gross displacement of hydrogen toward the cooler regions of the specimen was observed with consequent copious precipitation of 6-ztrconium (ZrH) there. The kinetics of the diffusion are analyzed and discussed. X HE temperature-gradient redistribution of hydrogen in a-Zircaloy-2 has been treated both theoretically and experimentally Hydrogen moves toward the cold side of the temperature gradient until a steady state has been established; tendency for further hydrogen movement because of temperature differences is nullified by the tendency to move in the reverse direction because of the concentration gradient. The steady state condition is described by the equation in which iV is the concentration of hydrogen at a point in the specimen corresponding to absolute temperature T, R is the gas constant,k is a constant of integration, and Q is a parameter called the heat of transport, characteristic Of the particular system. The value of Q has been determined for hydrogen in Zircaloy-2 by several investigators, using Eq. [11. There is considerable variation in the results, the cause of which has not been resolved; reported values lie in the range 3 to 6 kcal per mole. The physical situation for two-phase thermal migration is much more complex. The -phase boundary for the solubility of hydrogen in Zircaloy-2 ranges from a concentration of 25 ppm at 200°C to a maximum of about 600 ppm at 550°C.4a Thus, if the concentration of hydrogen in Zircaloy-2 is sufficiently great (>600 ppm), the specimen will be entirely two-phase, consisting of a matrix of a-Zircaloy-2 surrounding particles of zirconium hydride. At time zero, with a temperature gradient imposed, the relative amounts of hydride and a-phase in each infinite-simally thin isothermal section of the specimen can be determined from the phase diagram by the lever rule. Moreover, the concentration of hydrogen in the matrix phase varies from point to point, following the a solubility line. Over most of this temperature range (<450°C) 6 phase, Fig. 3, has a constant concentration.5 The diffusion rate toward the cold side should be governed by 1) the slope of the a solubility line and 2) the temperature gradient, The extra complication of two-phase thermal diffusion lies in the fact that migration of hydrogen would leave the a-phase concentration gradient unaffected, since it is fixed at any temperature only by the solubility; gross concentration changes would reflect only the relative amounts of matrix and hydride, which could vary continuously at every point. Migration of hydrogen out of a region would lead to dissolution of hydride, and

Jan 1, 1962

By R. W. Heckel

The conzpaction of metal powders is analyzed through density-pressure curves as a three-stage process — die filling, individual particle motion, gross compact deformatim. The densification occurring during each of these stages is evaluated quantitatively. The amount of densification in the first and second stages is primarily a function of particle geometry. The densification taking place in the third stage is dependent mainly upon the material. AT the present time the densification of powders during compaction is usually described by terms such as "compactibility," "compressibility," and "compression ratio." Schwarzkopfl has proposedthat compactibility be defined as the minimum pressure needed to produce a given green strength, while compressibility be used to indicate the extent towhichthe density of a powder is increased by a given pressure. Compression ratio is generally defined as the ratio of the compact density obtained at a given pressure to the apparent density of the loose powder. 13alshina found that the pressure imposed on a compact affects the relative volume of the compact according to the following relation: hP= - LV + C [ll where: P is the applied pressure, V is the relative volume of the compact, Ratio of the specific volume of the compact to that of the material without porosity. Lisa constant described as the modulus of pressing and is determined by the slope of a plot of h P vs V, and C is a constant which is determined by the intercept of a plot of InP vs V. Several drawbacks of the Balshin analysis may be noted from Fig. 1, which is a plot of pressure (loga-

Jan 1, 1962

By W. O. Philbrook, A. E. El-Mehairy

The reduction by hydrogen of individual particles of dense hematite implanted in beds of inert spheres is controlled by single-particle kinetics. No evidence of reagent starvation was found down to low flow rates established by pressure gradients as low as 0.01 in. H2O per- in. of depth in beds of spheres as small as 3/16 in. diam. The optimum size for most rapid reduction of beds of homogeneous ores results from the effect on reducing potential of the gas of competing factors of supply and consumption. A recent publication1 presented the results of a study of the rate of reduction of iron ore in a fixed bed by hydrogen introduced at constant pressure differential. Under these conditions the reagent flow rate varied directly with the bed permeability, which was a function of particle size and shape and bed voidage, and inversely with the temperature-dependent viscosity of the gas. The present note adds data from supplementary experiments designed to reveal whether or not any partial reagent starvation arising from a flow-dependent transport resistance in the gas phase might have been operative. Kinetic studies were made of the reduction of individual spheres of iron oxide inserted into beds of inert spheres, so that the reagent flow rate and aerodynamic conditions were again determined by bed characteristics and temperature. The experimental techniques and apparatus were similar to those previously described.&apos; The synthetic iron ore spheres were wet-rolled by hand from powdered, reagent-grade* Fe2O3 and subsequently dried and then fired in air at 1250°C. The indurated pellets has almost no porosity as indicated by their specific gravity of 5.10. The beds were made of dense alumina spheres, closely sized to the same dimension as the iron oxide spheres, in the following diameters: 3/16, 1/4, 5/16, and 3/8 in. Each bed was hand-packed of particles of a single size to a controlled voidage of 0.32 and depth of 3 in. within a capsule having an internal diameter at least 10 times the particle diameter. A few weighed iron oxide spheres were individually planted in the central plane of the bed of inert spheres at points away from the wall. Reduction was carried out at atmospheric pressure by purified hydrogen at 670°, 800°, and 985°c. The reagent was supplied at precisely controlled pressure differentials of 0.01, 0.02, and 0.03 in. of water per in. of bed depth. This gave a range of flow rates similar to that used in the study of beds of ore and comparable with blast-furnace practice in terms of mols of reducing gas per hr per sq ft of cross-section. Viscous flow prevailed in all beds under the experimental conditions of this study. The reduced particles were checked for loss in weight and then sectioned for metallographic examination. Occasional particles were found to have contained minute internal cracks that interfered with the concentricity of the reduction interfaces, and data for such particles were rejected. An experimental rate constant for the reduction of the imbedded Fe2O3 spheres was calculated on the assumption that the rate was proportional to the metal-oxide interface area by an equation that has been found by McKewan2 to describe the reduction of single spheres

Jan 1, 1962

By F. C. Schora, H. P. Meissner

Iron ore from Cerro Bolivar, Segre&apos;, and Sierre Grande was reduced in fluid beds at about SOOT, using gas analyzing 20.5 pct CO, 41 pct Hz, and 38.5 pct N2. Except in the early stages of reduction, the rate of oxygen loss from the bed was directly proportional to the oxygen concentration in the bed, independent of gas composition as long as the gas was reducing, and little affected by temperature. The percentage reduction of the bed solids at any time was independent of particle size. I HE reduction of spheres or cubes of dense iron ore in a slowly moving stream of either pure H, or pure CO has been found to take place at distinct interfaces between well defined layers of iron and the iron oxides.&apos;y4 These interfaces generally penetrate the ore lump in topochemical fashion, remaining parallel to the original contours of the specimen. Thus in the earlier stages of reducing hematite, the specimen&apos;s core is Fe,O, surrounded by successive shells of the lower oxides, and finally by an exterior shell of iron. McKewan5 assumed that the rate limiting step occurred at the Fe-FeO interface, with reducing gas penetrating up to this interface through the external porous iron shell, and reduction of the higher oxides within the ore lump occurring by diffusion of iron through the dense FeO shell. He developed an analytical expression based on this model relating the amount of oxygen removed from

Jan 1, 1962

By N. Jaffe, J. E. Dorn

The effect of stress on the creep rate of high-purity poly crystalline aluminum in the intermediate temperature range was investigated by conducting creep tests at a series of different stresses and by decreasing the stress abruptly during the course of primary and secondary creep. Three series of decreases in stress tests were conducted: the stress was decreased in primary and secondary regions of creep at 347.5°K and the stress was decrensed in primary creep at 327°K. The results demonstrate the effects of structure and temperature on the stress dependence of the creep rate. The trends in the creep rate after a drop in stress are complicated and show that recovery takes place. The experimental results were compared with Friedel&apos;s theory for cross-slip, the experimentally determined energy for a constriction being in good agreement with the theoretical estimate proposed by Stroh. PREVIOUS investigations have shown that the ap-- parent activation energy for creep of polycrystalline aluminum, over the range from about 250° to 380°K, is approximately 27,400 cal per mole,&apos; a value that is to a first approximation insensitive to the applied stress, the creep rate, and the creep strain. Several facts strongly support the thesis that creep, in this temperature range, is controlled by the rate-determining mechanism of cross-slip: 1) Recovery of the cold-worked state can take place by a number of mechanisms prominent among which is climb and cross-slip. Astrom2 reported rapid recovery of cold-worked polycrystalline aluminum at 340° to 370°K giving an activation energy of 28,000 cal per mole and additional recovery at the higher temperatures of 455° to 478°K giving an activation energy of 36,000 cal per mole. Whereas the latter process was clearly identified with the climb mechanism, the former process. which has an activation energy in good agreement for that of creep in the same temperature range, is most likely due to recovery by thermally-activated cross-slip. 2) Single crystals of aluminum exhibit sharp slip-

Jan 1, 1962

By W. L. Korbee, P. Hazebroek, M. Prats, E. E. Allen, C. A. 225-000-000-017 Verbraak, H. C. van Elst

In a recent paper,&apos; one of us has presented some experimental evidence on the relationship between twinning and brittle fracture in steel. From metallographic examinations of brittle fracture it could be derived that mechanical twins and microcracks are formed already in front of a running brittle fracture. A tentative explanation based on the evaluation of the statistical distribution of mechanical twins vs various angles to the fracture was given in the above mentioned paper. It was suggested that these twins are caused by stress waves emitted by a running brittle fracture. With the aid of high-speed photography and the use of photo-stress sheet we are now able to study in more detail the propagation of a brittle fracture and the emittance of stress waves connected with fracture. A typical example is given in Fig. 1. In this figure a running brittle fracture in an ordinary Thomas steel is shown. The experiment was performed on a Robertson apparatus and the stress waves caused by the fracture were made visible with photo-stress

Jan 1, 1962

By Molly Gleiser

The standard free energies of formation of some gaseous metal oxides together with those of their condensed oxides have been plotted against temperature. The heats of formation of the gaseozcs oxides are tabulated. An explanation is given of the use of the data to predict the importance of the gaseous metal oxides at high tenzperatures. RECENT mass spectrometric work1 has resulted in the detection of several hitherto unknown gaseous oxides and the measurement of their free energies of formation. Of especial interest is the fact that several of the refractories in common use either as crucibles or furnace tubes, and metals used in Knudsen cells and in furnace windings, have been found to have one or more stable gaseous oxides. In view of the present emphasis on high-temperature techniques, the development of vacuum metallurgy.z heating by electron bombardment and plasma jets, and the resultant shift to ever higher temperatures, it is no longer possible to plan experiments without taking into consideration the significance of the presence of these gases in the system, the reactions they undergo. and their contribution to the vapor pressure. A good example of what went wrong in earlier work, when the existence of these gaseous molecules was not yet known, is presented by the work of Hoch, Nakata, and Johnston. Hoch and coworkers attempted to measure the vapor pressure of solid ZrO2 by letting the vapor in equilibrium with zir-conia effuse from a tantalum Knudsen cell. The free energies of formation of solid zirconia and tantala are such that a short calculation showed that the reaction

Jan 1, 1962

By M. Schwartz, S. K. Nash, R. Zeman

Knoop hardness in the rolling plane and in the longitudinal plane of hot-rolled and cold-rolled sheets of sublimed magnesiu?w was measured as a function of the angle between the long axis of the indenter and the rolling direction. These measurements were correlated with similar data taken on the (0001) and (1010) planes of a single crystal of magnesium where the hardness was measured as a function of the angle between the long axis of the indenter and the [1120] direction. The results were analyzed for compliance with the hypothesis of Daniels and Dunm to account for slip, and with a similar hypothesis to account for twinning. Some hardness anisotropy data are also presented for magnesium-indium and magnesium-lithium solid solution alloys. It is well known that the hardness of a crystalline specimen is different for its different surfaces, and also that the hardness is a function of direction within a single surface. Variations in hardness for single crystals have been found to be much larger than those for polycrystalline materials. Also, materials having low crystal symmetry were found to have a greater anisotropy of hardness than those of high symmetry. 0&apos;Neill1 and Pfeil,2 using a 1-mm Brine11 ball, studied single crystals of aluminum and iron, respectively; and they found a variation of hardness of about 10 pct between readings taken along the principal crystallographic faces. Daniels and Dunn3 found that the Knoop hardness number varied about 25 pct as the long axis of the indenter rotated on the basal plane of a zinc single crystal. The variation on the (1450) plane was about 100 pct, and the average hardness on this plane was about twice that of the basal plane. They also studied the variation of hardness within the (loo), (110), and (111) faces of a single crystal of silicon ferrite and found variations of about 25 pct although the average values for these planes were almost identical. Single crystals of zinc were also studied by Meincke.4 He found that the Vickers hardness numbers varied about 30 pct depending on whether the axis of the indenter was parallel or perpendicular to the (1010) and (1110) planes. Mott and Ford,5 using a Knoop indenter, found a 25 pct variation in hardness on the basal plane of zinc. Crow and Hinsley6 studied heavily cold-rolled bronze, steel, brass, copper, and other metals. They found that the difference in hardness numbers based on the difference in the length of the diagonals of the Vickers indenter was from 5 to 12 pct. Some minerals and synthetic stones show a very large anisotropy of hardness. Robertson and Van Meter7 found the Vickers hardness of arsenopyrite to vary from 633 to 1148 kg per mm2. stern8 using the double-cone method on synthetic corundum found the hardness number to vary from 950 to 2070. And winchell9 reported a variation of hardness number from 184 to 1205 in kyanite. The variation of hardness as a function of direction in a given crystallographic plane in single crystals possesses a periodicity which is related to the symmetry of the lattice. Daniels and Dunn3 found a six-fold periodicity of hardness in the (0001) plane of zinc. They found that the hardness curves of silicon ferrite had a four-fold symmetry in the (100) plane, a two-fold symmetry in the (110) plane, and a six-fold symmetry in the (111) plane. Mott and Ford5 also reported a six-fold symmetry of hardness in the basal plane of zinc. And vacher10 found two-, four-, and six-fold periodicities of hardness in copper on the (110), (100), and (111) planes, respectively. The purpose of this paper is to report the results of an investigation on the anisotropy of hardness as a function of orientation in single crystals of mannes-ium, and samples of rolled magnesium, magnesium-indium, and magnesium-lithium solid solution alloys. The anisotropy of hardness of pure magnesium which had been hot rolled, and then cold rolled various amounts to fracture, was studied by means of Knoop indentation hardness numbers; and the results were correlated with the preferred orientation as determined by quantitative X-ray pole-figure data. A comparison was made of the hardness data obtained from the rolled sheets and those of single crystals of magnesium. In order to obtain a more fundamental understanding of the variation of hardness and of Knoop hardness testing, the data were analyzed by

Jan 1, 1962

By G. D. Cody, D. S. Beers, B. Abeles

The thermal diffusivity (thermal conductivity divided by specific heat) of Armco iron has been measured over the temperature range 30º to 1025ºC. The results are in good agreement with the thermal diffusivity computed from published values of thermal conductivity and specific heat, except near the Curie point and at the a to y phase transition, where the measured diffusivity undergoes rabid variations. The differences observed are ascribed to a rapid variation in the electronic thermal conductivity near the Curie point, and a decrease in the lattice thermal conductivity, at the a to ? phase transition. A major difficulty in measuring the thermal conductivity of materials at high temperatures is the determination and elimination of radiation losses. It has been shown, however, that in measuring thermal diffusivity D (thermal conductivity/specific heat) radiation losses can be taken into account exactly.&apos; In order to test the performance of a newly designed apparatus for measuring thermal diffusivity of solids,&apos; we measured Armco iron to an accuracy of 2 pct in the temperature range 30" to 1025°C. This material was selected since both the thermal conductivity,3&apos;4 k, and specific heat,5 C, are known accurately in this temperature range and thus the measured values of D could be compared with D computed from the pub-

Jan 1, 1962

By J. Gordon Parr, G. R. Purdy

The phase boundaries of "TiNi" have been accurately determined by high-tewperature X-ray diffraction and metallo-graphic techniques. The phase (centered at 51 pct Ni) has a restricted range of homogeneity at 500°C, and a much greater range at 800°C. "TiNi" in all alloys containing less than 51 pct Ni decomposes rapidly and reversibly at 36°C to form a previously unreported phase. ThE region of the titanium nickel system corresponding to the phase "TiNi" has been the subject of several investigations.1,2,4-7 Laves and wallbaum1 reported "TiNi" as a body-centered cubic (a2) Phase, and Duwez and Taylor2 determined its para- meter to be 2.986. Duwez and Taylor also reported that "TiNi" decomposed into "Ti2Ni" and "TiNi3" on prolonged heating at 650" and 800°C, which led McQuillan3 to suggest a sluggish eutectoid reaction between "TiNis" and "Ti2Ni". Margolin, Ence, and Nielsen,&apos; working with higher purity alloys, found no evidence of this decomposition. They showed the "TiNi" phase region extending from 49 to 54 pct*

Jan 1, 1962

By David A. Thomas, John F. Peck

Sam Leber (General Electric Refractory Metals Laboratory)—I think that the authors should differentiate between the curved grains obtained by swaging and the crumpled grains produced by drawing. This can be seen most easily in the transverse sections of Fig. 2d, and is also apparent in Fig. 2c. This difference in structure indicates that the mode of deformation shou1d affect the texture, since the cylindrical texture should be maintained or even increased by the curved grains developed by swaging. Drawing, on the other hand, crumples the grains. This should convert the cylindrical texture into a normal fiber texture. This has been substantiated by a comparison of tungsten wires fabricated by similar drawing and swaging schedules. Although cylindrical textures have been detected in drawn iron wires, they were weak in comparison to tungsten wires which included swaging as part of the fabrication process. It should also be noted that large curved surfaces developed by swaging are concentric with the surface. The postulated (100) surface of these crystals would be confirmed by a (100) cylindrical texture, as was observed in tungsten. The preservalion of the (100) cylindrical texture by swaging would maintain the <100> direction in the radial position required for easy flow. This might provide a partial explanation for the decreased rate of work hardening observed in the swaged wire. J. F. Peck and D. A. Thomas (authors&apos; reply) — The authors appreciate Dr. Leber&apos;s comments on the differences in textures, microstructures, and properties of swaged and drawn wires. The evidence of the prominence and persistence of the cylindrical texture in swaged bee wires seems quite consistent with our microstructural observations and interpretations. We are presently engaged in further work to correlate the development of texture and micro-structure in drawn bee metals.

Jan 1, 1962

By R. J. Allio, C. H. Randall

An automatic system for the quantitative analysis of microstrulcture has been developed. The method is based upon a statistical model of microstructure and employs phase intercept fractions as fundamental random variables. Structure-sensitive properties can be related explicitly to parameters derived from the distribution of phase intercept fractions in a matevial. THE properties of mechanical dispersions and of multiphase alloys art: intimately related to the amount, distribution, and intrinsic properties of the dispersed material. In many instances, the amount and distribution of the dispersed substances have greater influence on the over-all system properties than do the properties of the dispersed substance-Such properties as average particle size, particle size distribution, homogeneity of dispersion, volume per cent of dispersed phase, and mean free path between dispersed particles thus become critical in any evaluation of the properties of a dispersion. Unfortunately, techniques for evaluating quantitatively the microstructural characteristics of dis~ersions rapidly and accurately have not been available. If necessary, qualitative or semiquantitative devices can be utilized. Some such devices are based merely upon comparison of the specimens in question with arbitrary standards. Other techniques involve superposition of grids and tabulation of particles observed in different portions of the grid. Still other methods based upon lineal analysis entail counting lines or points at random upon the specimen to be examined; the number of intersections of the line with a given phase, the proportion of line or number of points which are covered by given phase are variously recorded. The mathematical basis for most of the techniques of quantitative metallography have been amply reviewed in the literature.&apos;l2 without exctption, however, the standard techniques for quantitative metallography are either imprecise or are exceedingly tedious to apply. For example, tranverse integrating stage for rapid manual areal fraction measurement has been designed by Smith.3 Howerer, as in the case of any device based upon visual eslimation, operator bias may cause appreciable error. Various flying spot devices, on the other hand register particle size distributions in 2-dimensions, from which it is difficult to derive other properties of the dispersion. Thus, e.g., the 3-dimensional distribution cannot be inferred unless certain rather broad assumptions are made concerning the randomness of distribution and geometrical configuration of dispersed phase. Many limitations to the application of quantitative structural analysis can be overcome by the use of the microdensitometer, which is essentially an automated areal analysis device. Data obtained in the form of a distribution of phase intercept values are

Jan 1, 1962

By D. W. Rudd, D. W. Vose, S. Johnson

The permeability of Mo-0.5 pel Ti to hydrogen was investigated over a limited range of temperature and pressuire (709° to 1100°C, 1.i and 2.0 atm). The resulting permeability, p, is found to obey the The experimental data justifies the permeation mechanism as a diffusion contl-olled pnssage of Ilvdrogen atoms through the metal barrier. 1 HE permeability of metals to hydrogen has been investigated by a number of workers and their published results have been tabulated by Barrer&apos; up to 1951. Since most of the work on the permeability has been accomplished prior to this date, the compilation is fairly complete. Mathematical discussion of the permeability process has been reported by Barrer, smithells, and more recently by zener. From these efforts several facts are observed. First, the permeability of metals to diatomic gases involves the passage through the metal of individual atoms of the permeating gas. This is evidenced by the fact that the rate of permeation is directly proportional to the square root of the gas pressure. Second, the gas permeates the lattice of the metal and not along grain boundaries. It was shown by Smithells and Ransley that the rate of permeation through single-crystal iron was the same after the iron had been recrystallized into several smaller crystals. Third, it has been observed that the rate of permeation is inversely proportional to the thickness of the metal membrane. Johnson and Larose5 verified these phenomena by measurirlg the permeation of oxygen through silver foils of various thicknesses. Similar findings were noted by Lombard6 for the system H-Ni and by Lewkonja and Baukloh7 for H-Fe. Finally, it has been determined that for a gas to permeate a metal, activated adsorption of the gas on the metal must take place. Rare gases are not adsorbed by metals, and attempts to measure permeabilities of these gases have proved futile. ~~der&apos; found negative results on the permeability of iron to argon. Also, Baukloh and Kayser found nickel impervious to helium, neon, argon, and krypton. From what was stated above concerning the dependence of the rate on the reciprocal thickness of the metal barrier, it is seen that although adsorption is a very important process, at least in determining whether permeation will or will not ensue, it is not the rate determining process for the common metals. A case in which adsorption is of sufficient inlportance to cause abnormal behavior has been noted in the case of Inconel-hydrogen and various stainless steels.&apos;&apos; APPARATUS The apparatus used in this study is shown in Fig. 1. The membrane is a thin disc (A), but is an integral part of an entire membrane assembly. The entire unit is one piece, being machined from a solid ingot of metal stock. When finished, the membrane assembly is about 5 in. long. Two membrane assemblies were made; the dimensions of the membranes are given in Table I. The wall thickness is large compared to the thickness of the membrane, being on the average in the ratio of 13 to 1. There exists in this design the possibility that some gas may diffuse around the corner section of the membrane where it joins the walls of the membrane assembly, If such an effect is present, it is of a small order of magnitude, as evidenced by the agreement of the values of permeability between the two membranes under the same temperature and pressure. A thermocouple well (B) is drilled to the vicinity of the membrane. The entire membrane assembly is then encased in an Inconel jacket and mounted in a resistance furnace. The interior of the jacket is connected to an auxiliary vacuum pump and is always kept evacuated so that the membrane assembly will suffer no oxidation at the temperatures at which measurements are taken. The advantages of this configuration are: 1) there are no welds about the membrane itself, so that the chance of welding material diffusing into the membrane at elevated temperatures is remote. 2) It is possible to maintain the membrane at a constant temperature. Since the resulting permeation rate is very dependent upon temperature, it is advisable to be as free as possible from all temperature gradients. 3) It is possible to obtain reproducible results using different specimens. The only disadvantage to this configuration is the welds (at C) in the hot zone. The welding of molybdenum to the degree of per-

Jan 1, 1962