By M. L. Holzworth, Joseph C. Kremer, Paul A. Beck, L. J. Demer

FOR alloys which are in practice heat treated to obtain increased strength, such as steels, duralumin, copper-beryllium, and others, the treatment usually involves heating to a relatively high temperature. At such temperatures the grain size of the product is largely determined by grain growth. Even in metals and alloys annealed merely to relieve work hardening, recrystallization is generally followed by a certain amount of grain growth. Thus, effective grain size control, which is often of great practical importance in manufacturing processes, depends on the grain growth behavior of the material used. Despite its importance, grain growth has been the subject of few investigations of a fundamental nature. The term "grain growth" has been used to designate a group of related, but distinctly different, phenomena. The two most important and best known of this group are illustrated by the following example. Curve a in Fig r shows the increase of the average grain size of a copper-beryllium alloy, containing 2 pct Be and 0.15 pct Co, with increasing annealing temperature. The time of annealing was 2 hrs. The grain size was quite uniform in all specimens. The results of a similar experiment with an alloy containing 2 pct Be and 0.31 pct Co are shown by curve b. It is seen that for any annealing temperature below T. the grain size was smaller than in the previous case. Grain growth became slower with the higher Co content. This "inhibiting" effect of the higher Co addition was associated with the appearance in the microstructure of fine, light blue particles of the CoBe phase. Up to temperature T. the structure of the inhibited alloy (curve b) was just as uniform as the structures represented by curve a. However, after annealing at T, or at higher temperatures, the inhibited alloy showed some extremely large grains (much larger than the grain sizes developed by the uninhibited alloy with low Co content) mixed with the small grains according to curve b. The presence of these mixed or "duplex" structures is indicated in Fig 11 by the vertical lines branching off curve b. The type of grain growth occurring in uninhibited Cu-Be alloys (curve a) has has been most frequently and best investigated in brass. This type has been designated as "normal grain growth," while the grain growth phenomena occurring in inhibited materials were, at times, referred to as "abnormal grain growth." However, since the latter term has been applied occasionally to the phenomenon of critical recrystallization, which also results in large grains although by an entirely different mechanism, in the present paper a different nomenclature has been adopted in order to avoid confusion. Typical of the grain growth in uninhibited metals and alloys is the continuous

Jan 1, 1947

By F. A. Veer, W. G. Burgers, B. H. Kolster

Starting-- from Cu-Si diffusion couples a study of diffusion in the intermetallic compound Cu3Si of the Cu-Si system has been made. Mmker experiments showed copper to be the diffusing element. From the rate of growth of the Cu3Si phase diffusion coefficients were derived. The activation energy for diffusion is 18.6 kcal per mole. The couples show some interesting microscopic features, for which a tentative explanation is given. THE synthesis of dimethyldichlorosilane, (CH3)2SiC12, an important compound in the manufacture of methyl-silicones, takes place at the surface of a thin Cu3Si layer deposited on a mass of silicon particles."' By passing CH3C1 vapor at about 350°C, silicon atoms are consumed from Cu3Si in forming the volatile silane molecules, thus leaving copper atoms at the surface. It is well-known that copper acts as a poison for the above-mentioned reaction by catalyzing the dissociation of methylchloride.' However, no poisonous effect is observed, at least not before most of the silicon from the particles is converted into silane.3 This would be understandable, if either the copper atoms diffuse through the Cu3Si deposit to the underlying silicon or silicon atoms diffuse in the reverse direction to the copper, both processes resulting in the formation of new Cu3Si and so ensuring the proceeding of the reaction. In this paper experiments are described, demonstrating copper to be the diffusing element. Also a very low activation energy for the diffusion is observed. EXPERIMENTAL The silicon used contained 1 ppm Mg and 1 ppm Cu; the copper was spectroscopically pure (Fe: 2 ppm; Ag, Mg, Si: 1 ppm). The copper and silicon samples were prepared in the form of blocks of approximately 10 by 10 by 5 mm with two parallel sides by spark-machining. The blocks were ground on emery paper (grit 600), etched (copper with nitric acid, silicon with a 4:l nitric acid:hydrofluoric acid mixture), and cleaned with alcohol. As the brittleness of the silicon did not allow a welding procedure to prepare the diffusion couples, the copper and silicon blocks were pressed together in a steel clamp. The pressure exerted by the clamp brought about contact between the parts of the couple and so ensured proceeding of the diffusion. The couples were heated in a vacuum furnace (about 10"5 Torr). The temperature was stabilized within 1 pct. After a heat treatment a section parallel to the direction of diffusion was examined in the microscope and in the X-ray scanning microanalyzer. To determine whether copper or silicon is the diffusing element marker experiments were carried out using tungsten wires with a 20-p diam. EXPERIMENTAL RESULTS Figs. 1, 2, 3, and 4 give micrographs of diffusion zones of Cu/Si couples. Analysis by the electron mi-croprobe of the Cu/Si samples after a definite heat treatment revealed the existence of only one intermetallic phase as can be seen from the line scan shown in Fig. 5. From the X-ray diffraction pattern it could be deduced that this phase was CU 3 Si.4 Even when diffusion zones of considerable width (up to 600 p) were obtained, no other phases occurring in the Cu-Si system could be detected, neither by the electron microprobe nor by X-ray diffraction analysis. The optical anisotropy of the Cu3Si phase made it possible to observe the columnar shape of the crystal-

Jan 1, 1969

Jan 1, 1880

By W. P. Evans, R. W. Buenneke

Warren and Averbach's multiple order, Fourier method was applied to solid specimens of SAE 1045 steel. The material was hardened to three hardness levels and specimens of each hardness were shot peened to three intensities. Particle size, root-mem-square strain, mean strain, md macro residual stress were determined for each. Microstrains caused by either hardening or peening varied markedly over microregions. In general, increasing the hardness or peening intensity increased the rms strain and decreased the particle size. Similar effects were observed by varying hardness and peening intensity independently. At a Rockwell hardness of C 50, peening had little effect on line broadening, but both mean strain and macro residual stress increased. Mean strain was independent of column length. Induced macro residual stress by peening was affected most by initial hardness, but not by specific peening intensity. The purpose of this work is to establish the state of residual strain and particle size by X-ray diffraction in hardened and cold-worked plain carbon steel and attempt to relate these X-ray measured parameters to fatigue performance. X-ray line broadening (and its micro implications), along with X-ray residual stress (and its macro implications), may be basic indicators of the inherent fatigue resistance of the material. X-ray line broadening is caused by variable lattice strains and small particle size. Both are a result of plastic deformation which accompanies hardening or cold working processes. Therefore, X-ray line broadening is a good measure of both. warren1 has recently reviewed the Warren and Averbach2,3 Fourier analysis of line broadening. Strain and particle size effects can be separated because broadening due to particle size is independent of order of the diffraction peaks, while broadening due to strain is not. Microstrain is obtained as a root-mean-square strain averaged over discrete distances within the crystals causing diffraction. These distances are quite small, varying from 10 to 10081, and may be interpreted as the gage length over which the strains are averaged. Because of their variable nature, the X-ray line is broadened. The plot of rms strain vs distance (or column length) within the specimen gives a measure of their variability. Small particles also cause X-ray line broadening as already mentioned. A particle is interpreted as a region within a crystal or grain which diffracts X-rays coherently. This region is one of given orientation and may be bounded by a small angle grain boundary, dislocations, a twin boundary, or a stacking fault. The present work covers measurement of X-ray line broadening and macro residual stress on an SAE 1045 steel, quenched and tempered to various hardnesses. Various amounts of cold working were produced by shot peening the surfaces to various Almen intensities. Particle size, root-mean-square strain, and mean strain were calculated from the Fourier coefficients of the X-ray diffraction profiles in a direction normal to the peened surface. No effort was made to separate the various causes of particle size broadening. Macro residual stresses were reported in directions parallel to the peened surface. I) X-RAY METHOD The Fourier coefficients were determined for the 110 and 220 X-ray profiles. They were corrected for instrumental broadening by the method of Stokes,4 using an annealed reference specimen of similar geometry presumed to be free from broadening due to small particles and distortions. The nth Fourier cosine coefficient, A,, is related to a particle size coefficient, Ap, and a distortional coefficient, ADn, by the equation:

Jan 1, 1963

By Edward F. Winter, C. E. Ruoff

A silicon solid-state array image scanner is described. This paper deals with structural and performance properties of the array which basically consists of PIN photo and gating diodes, and low capacitance isolation diodes. Each chip of the array is composed of an 8 by 9 matrix of photo detector cells; each cell contains one each of the three diode types mentioned. This x-y matrix is read a column at a time with an access delay of approximately 100 nsec per column. It is designed to detect the presence or absence of illumination within 10-mil diam image spots located on a 15- by 15-mil grid. Radiant power level of an illuminated spot is low; of interest is the range around I uw with a of 8400g Structural improvements to the original array which will result THE purpose of this paper is to describe the results of a solid state scanner exploratory development activity. The scanner is intended to sense the presence or absence of low-level illumination falling upon a matrix of 10-mil wide squares arranged on a 15- by 15-mil x-y grid pattern. The light of interest has a wavelength of 8400, characteristic of radiation emitted from a GaAs lasing diode. This wavelength matches well the spectral absorption of silicon,' thus the well-developed silicon processing technology can be applied to fabricating large integrated arrays of PIN photocells to sense the radiation. The illumination state of the cells of the array is read, one column at a time, by addressing a drive line of the particular column in question and examining the state of those sense lines which are orthogonal to the drive Lines of in greater sensitivity at various wavelengths, both above and below 8400Å, and in greater speed are presented. These include variations in diffusion depth, resistivity of N and P regions, isolation techniques, and packaging. Trade-offs between access speed, cycle frequency, and sensitivity are discussed. A packaging approach to achieving an array composed of several chips is described. Requirements on this package are: 1) maintenance of 15- by 15-mil pitch of the light sensitive cell position, therefore positional accuracy of mounted 8 by 9 cell photo detector chips; 2) maintenance of inherent high array speed even though signal levels are low through high density close proximity mounting of monolithic sense amplifier circuitry. the array. One bank of N sense amplifiers is required, where N is the number of photodiode cells in each column of the array. CELL AND CHI" STRUCTURE A photograph of a single monolithic cell is shown in Fig. 1. Each cell is composed of three junctions, an isolation junction, a logic or blocking diode junction, and a photodiode junction; all of these junctions are connected electrically by a common N region. An electrical schematic of four cells of the array is shown in Fig. 2 with the associated driver and sense amplifier circuits in block diagram form. Note the common cathode configuration of the three diodes of each cell. Fig. 3, a diagram of the cell vertical struc ture, illustrates how the electrical configuration of

Jan 1, 1970

By S. A. Mersol, C. T. Lynch, F. W. Vahldiek

The room-temperature microhardness of as-grown and annealed MoaC single crystals was measured on the (0001), {2110), and1012) planes using Knoop and Vickevs indenters at loads ranging front 25 to 1000 g. The orientatimz dependence of hardness with respect to crystal axes was also studied. The average random hardness of as-grown crystals was determined to be 1520 kg per sq nm. Annealing to 2000°C decreased. the average hardness by 150 units. An increase in hardness after annealing at 2200 ;C was noted. Optical and electron microscopy revealed slip and twin traces on all planes studied, as produced by mi-cvohavdness indentations. Basal (0001)(2i10) slip was determined to be the primary slip system and was substantiated by electron transmission microscopy. A secondary {1010)(2110) slip was produced by mi-crohardness indentations. The lattev also produced twinning- of the {10i2)[0001] type, as proven by electron diffraction. Electrical resistivity and elastic-modulus anisotropy were found and correlated with hardness anisotropy and Mo2C crystal structure. Elastic-modulus values were obtained by microhard-uess and ullrasonic methods. Bonding mechanism of Mo2C is discussed. ROOM-TEMPERATURE microhardness indentations are useful for studying hardness anisotropy, slip, and twinning in brittle materials. Slip has previously been produced in this manner in and WS~~.~ Recently, the authors5 reported slip of the {10i0)(11~0) type produced by high pressure and microhardness indentations on hexagonal TiBz (c/a = 1.066) single and polycrystals. This slip system was also reported by French and ~homas' and Taka-hashi and ~reise~ for hexagonal WC (c/a = 0.976) crystals. These results suggest that prismatic rather than basal slip is favored in hexagonal nonmetallic materials having a c/a ratio considerably less than the ideal (1.633). Buerger precession and cylindrical X-ray rotation patterns were previously' taken on cleaved sections of the Mo2C single crystals studied in this work. Th~y were found to be hexagonal MoaC with a. = 3.0233A, co = 4.7344A, and C/O = 1.5660. The latter ratio is close to that of the beryllium metal (c/a = 1.57), which slips primarily on the (0001) plane: but also slips on the (1010) planes.'0 ~irconium" (c/u = 1.59) and titanium12 (c/o = 1.59) deform mainly by slip on nonbasal planes which contain a close-packed direction. This is due to the fact that for these two metals the initial resolved shear stress for slip on the (10i0) prismatic planes is lower than that on the (0001) plane. The prominence of basal rather than prismatic slip in metals of high c/o ratios is shown by cadmium (c/a = 1.89), zinc (c/a = 1.86), and magnesium (c/a = 1.62) which deform mainly by basal slip. However, in case of the latter, by stressing magnesium crystals in tension or compression parallel to the basal plane, slip on (10i0) planes can also be produced.13 Several hardness values for polycrystalline Mo2C are reported in the literature: Biickle ' and Samsonov'~ give a value of 1800 and 1479 kg per sq mm, respectively, at a 100-g load; and Kieffer and Benesovsk~'~ report a value of 1950 kg per sq mm at a 50-g load. ~ott'~ reports a Vickers hardness value of 2000 kg per sq mm, with the load unspecified. A Rockwell A hardness value of RA = 88 has also been reported.'' In the present work, for comparison with single-crystal Mo2C hardness values, a Khnloo value of 1600 It 150 kg per sq mm was found on 99.6 pct pure and 99 pct dense hot-pressed Mo2C. This work was undertaken partly to explain the considerable differences in hardness values reported for polycrystalline Mo2C. EXPERIMENTAL The Mo2C single crystals investigated were prepared by a Verneuil-type process using an electric arc by the Linde Co. of the Union Carbide Corp.lg The largest specimens grown were boules 7 mm in diam by 40 mm in length. The crystals had an average density of 9.04 g per cu cm, with a Mo + C content of 99.8 wt pct. The major impurities were: 100 ppm each Na, Zr, and Ca; 85 ppm 0, 55 ppm Fe, and 10 ppm each Cr and Ta. The crystals were found to be carbon-poor, the average carbon content being 5.73 wt pct (stoichiometric value is 5.89 pct). The molybdenum content was found to be 94.08 pct, which is nearly stoichiometric. Electron-microprobe traverses of selected specimens were done with a Phillips-AMR microanalyzer. Thin-film and carbon replicas were used to prepare electron micrographs. This work was done with a JEM-6A electron microscope. Prior to optical and electron-optical studies, specimens were mounted in Lucite and polished on a vibratory polisher using diamond-paste grades ranging from 9-1 p and Linde A powder for up to 48 hr. Dilute nitric acid was used for thin-section polishing and chemical etching for 1-15 min. Electrical-resistivity measurements at room temperature were taken with a Rubicon bridge, using gold contacts. For hardness measurements, a Tukon Microhardness Tester Type FB with Knoop and Vickers indenters was used. Measurements were taken at loads ranging from 25 to 1000 g; however, the 100-g load was chosen as the standard load. All measurements were taken at room temperature. Indentations of cracking classes 1 and 2 only were considered for hardness determinations.20)21 (There are six cracking classes, ranging from "class 1" for a perfect inden-

Jan 1, 1967

By A. Kelly, S. Sato

Tensile tests have been performed on aluminum single crystals of 99.99 pct purity at 196°K. The resolved shear stress when the stress-strain curve becomes concave to the strain axis depends on orientation, being always higher for crystals with an initial orientation close to the sides of the unit triangle. Observations have been made, with the optical microscope, of the appearance of slip lines on polished surfaces of the crystals. Particular attention has been paid to the first appearance of cross-slip. It is confirmed that marked cross-slip is first seen when the stress-strain curve becomes concave to the strain axis. Measurements are reported of the lengths of the slip lines observed on top and side faces of the crystals at various stages of the deformation. The lengths of the slip lines vary inversely as the flow stress for all crystals, independent of crystal orientation. From measurements of the lengths and separations of the slip traces it is possible to estimate the number of dislocations which are annihilated at each cross-slip site. It is concluded that the annihilation of screw dislocations of opposite sign is the most important cross-slip process occurring. FRIEDEL1 recently pointed out that the stress-strain curve of many pure metals of face-centered-cubic structure can be considered as composed of three stages. Plastic flow commences with a region showing a small rate of hardening which is approximately linear. This has been called "easy glide*. It is followed by a region of more rapid hardening in which the slope of the curve is again approximately constant and this, in turn, is superseded by a final part of the curve which is concave to the strain axis. Following Diehl2 we may designate these regions as stages I, II, and III respectively. The onset of stage 111 occurs at lower stresses at higher temperatures. The appearance of the slip lines formed during these various stages has been described by a number of workers?-5* The object of the present work was to make detailed observations of the lengths and separations of slip lines for a number of crystals of different orientations deformed at the same temperature and strain rate. Although much previous work has been published on the deformation of aluminum single crystals the importance of measurements of these quantities has only recently been realized—they are essential for experimental tests of recent theories of work hardening.' 9 In aluminum, deformed at room temperature, stage 11 of the stress-strain curve is very weakly marked, as the stress for the onset of stage 111 is attained soon after the end of easy glide. In the present experiments it was decided to use a temperature lower than room temperature so that stage II of the curve was better developed. However, at temperatures as low as 90°K slip lines are not measured easily with the optical microscope.5 For this reason 1960k was chosen as a suitable temperature. Even at 1960k however, stage III of the curve commences at glide strains of 6 to 10 pct and hence

Jan 1, 1960

By N. G. W. Cook

The conventional cyclic system of deep-level mining by drilling and blasting gives rise to an inadequate degree of stope sorting when mining thin reefs. This results in poor utilization of the capital facilities of a mine in the form of shafts, haulages, airways, and associated equipment. Continuous and controlled removal of the thin gold-bearing portion of the reefs would permit better stope sorting and hence greater utilization of capital facilities. Results of experiments to develop hard-rock cutting machines for mining are reported and the benefits which could be derived from their use are discussed. Mining, from exploration through refining, is essentially a process of sorting in which the payable mineral, or metal, is progressively separated from the other constituents of the earth's crust with which it was originally associated. This takes place more distinctly at each step of the operation. What is it that determines the degree to which sorting should be carried out at each of the several steps comprising a whole mining operation? The formal answer is that degree of sorting at each step which results in the lowest overall cost for the complete separation. In practice, individual steps are chosen from those available in current technology, each of which effects a degree of sorting such that the quantity of material which must be sorted in the succeeding step is economically acceptable. It follows that any new technological development has repercussions throughout the whole mining operation and, more important, that the solution to excessive costs in any one step of the operation may lie not in improving the costly operation itself so much as in increasing the degree of sorting preceeding that operation. This concept, particularly in relation to deep-level mining of thin, tabular gold-bearing reefs in South Africa, is discussed here, and the most recent results achieved in the development of hard-rock cutting machines for stoping more selectively than is possible with explosives are presented. Deep-Level Mining Deep-level mining involves operations which are either not encountered, or are of only trivial importance, in near-surface mining. Near-surface, the major operations are those of rock breaking, transport, and milling. In deep-level mining, hoisting, environmental control, and strata control assume major importance. Some idea of the relative magnitude of these operations may be gained by comparing the separate amounts of energy which are required, or which must be controlled, to effect the various operations when, say, mining a tabular deposit 40 in. thick at 8000 ft below surface, Table 1. It is true that the costs of handling a given quantity of energy are not the same for each operation. Nevertheless, Table 1 does emphasize the fact that the operations of hoisting, strata control, and environmental control are of unique and major significance in deep-level mining. In particular, hoisting and environmental control place a heavy load on the reticulation system of the mine—the shafts, haulages, and airways. Typically, a new, deep gold mine with an annual revenue of about $35 million requires a total capital expenditure of about $140 million of which some $100 million is invested in developing and equipping this reticulation system. The ratio between annual turnover and capital invested of about one-quarter is exceptionally low, and it typifies the poor utilization of capital by the current technology of mining hard rock at depth. The average thickness of the reefs in the new South African goldfields varies from 10 to 30 in.,l and even in the thicker reefs the gold is often confined within a small fraction of the nominal thickness. Nevertheless, it is universal practice to mine these reefs at a stope width of about 40 in. or more, so that the quantity of rock broken in the stopes and hoisted out of the mine is between two and ten times the quantity of rock actually carrying a significant amount of gold. The reason for the adoption of such excessive stope widths is to be found in the method of rock breaking by drilling and blasting. The only free surface to which a blast hole can break is the stope face. It follows2 that each hole cannot have a burden in excess of the height of the free face if it is to break satisfactorily. To

Jan 1, 1971

By M. E. Shank, J. Wulff

At the present time, the designer of dies for metal powder pressing is handicapped by relative ignorance of stress distribution and frictional effects at the interior surface of the die. Unckell was the first to develop a method for the study of wall friction. He used three Brinell balls on which the die rested during pressing. The total frictional wall force was determined by the size of impression these balls left on a soft metal plate. Since the method does not give radial pressures, or distribution of such pressures, coefficients of friction could not be determined. Although Unckel measured density distribution, he was not able to determine radial or shear stresses. Shaler2 has proposed theoretical expressions for the stress and density distribution within cylindrical compacts during pressing, in accordance with the experimental results of Kamm, Steinberg, and Wulff.3 By application of Siebel's method,4 Kamm et a13 plotted stress trajectories for two compacts. From the stress trajectories they calculated coefficients of friction from point to point along the die wall. As pointed out by Shaler in the discussion of Ref. 3, these values are based on progressive point-to-point calculations on finite size grid squares across the compact. In the region of the die wall such calculated values may therefore have considerable cumulative error. The purpose of the present paper is to develop an experimental method by which the nonhydrostatic pressures and shears acting on the interior wall of a cylindrical die can be measured. Such measurements can then he correlated with existing data to aid in the explanation of the pressing process. The method used is based on the elastic: properties of the thick-walled tube used as the die. The principle of super-position of force systems on an elastic body is assumed to hold. Electric strain gauges were mounted in adjacent positions on the exterior die wall in order to get an exact measurement of the variation of tangential strain over the length of the die during pressing. While in this paper, measurements in terms of only tangential strains are considered, it is well to note that similar calculations may be set up for axial strains. The latter are not preferred, since they tend to be smaller than the tangential strains and therefore permit less sensitive measurements. Discussion in this work is restricted to compacts pressed from both ends, since the elastic deformation of the die is then more amenable to analysis. Before choosing the electric strain gauge method, a more direct line of attack was considered and discarded. The discarded idea was the insertion of a pressure gauge through a hole in the die wall.* The gauge would have been in the form of a small piston. If pressure were exerted against such a gauge, it would move outward along a radius of the die. One disadvantage of the scheme is its inability to measure shears along the die wall. Another more serious disadvantage is the disturbance caused by the device itself. It would serve to change the forces it was designed to measure. No matter how small the movement of the gauge, when pressure is applied a discontinuity would exist in the wall surface at that point. Due to the stress concentration caused by the hole, abnormal deflections of the die wall would occur around the gauge. During pressing, powder would be forced into the resulting depression. The depression would then become larger with increasing compacting pressure. Powder, not being a fluid, is capable of supporting shear. The ease with which it would flow into the die wall depression to further move the piston is an indication, not of the radial pressure at that point, but of the state of shear retarding the movement. Thus the "pressure" gauge is really a criterion of flowability, and of the capability of the powder to support shear. For these reasons, it was decided that the electric strain method, herein employed, was more reliable, if more indirect. The gauges and lead wires, mounted on the external die wall do not in any way affect the behavior of the metal powder or the die during pressing. Theory of the Method THE EFFECT OF RADIAL PRESSURE ON THE DIE WALL Effect of a Single Small Band of Hydrostatic Pressure Consider a die which is a thick-walled cylinder of outer radius R. and inner radius Ri. If over a small finite length L there is a normal pressure P, a tangential strain distribution at the outer wall results. This is shown schematically in Fig 1. The exact shape of the curve may he predicted by an extension of the theory of a semi-infinite beam on an elastic foundation.6 This

Jan 1, 1950

By Bernard Kopelman

The particle size of tungsten metal powder used to make tungsten wire for use in radio tubes and incandescent lamps must be closely controlled if the highly desirable feature of nonsagging is to be achieved. Our knowledge of factors affecting the particle size of tungsten powder has been limited by lack of any extensive literature on the subject. There are no publications in the English language discussing this problem in any but the most general terms. In this paper the published experimental information on this subject is reviewed. Based on the published data and some experimental data obtained by the author, a general theory of factors affecting the particle size of tungsten metal powder obtained by reduction of the oxides in hydrogen is offered. The various forms of the tungsten oxides and tungsten metal used in the experiments described were those prepared by commercial processes, so that the experimental results obtained on a laboratory scale would be more directly applicable to actual commercial reduction conditions. The effects of time of reduction, temperature. and concentration of water vapor in the hydrogen were observed by counting microscopically the particle distribution obtained. Such a method is very time-consuming, but the data obtained by this method are more reliable and more fundamental than those obtained by any of the several instruments available for measurement of particle size. Review of the Literature Until the year 1912, tungsten powder was prepared commercially by reducing tungstic oxide in the presence of carbon or one of its compounds (such as glycerin or ethylene glycol), usually by firing the mixture in a closed fire-clay crucible. The resultant powder contained about 95 per cent tungsten.' When reduction of tungsten oxides by H² was introduced Commercially,²,³ several investigators became concerned with the equilibria between tungsten metal and its several oxides in an atmosphere of hydrogen and water vapor.4-l3 While these many investigations were in fair agreement on the equilibria WO³ + H2 = WO2 + H2O and WO2 + 2H2 = W + 2H2O there arose considerable controversy as to the chemical composition of the oxide between WO³ and WO², because of very poor agreement on the equilibrium constant of this intermediate oxide reduction reaction. The controversy on this intermediate oxide has been in progress for more than 100 years. Thus Malguti,14 in 1835, decided it was WO2.56 In 1857, Riche15 proposed the formula W³O8. Usler,16 in 1865, confirmed the existence of WsO8 and further proposed W1O1l. In 1897, Desil7 agreed upon W²O8 but also found W5O14.

Jan 1, 1947

By Bernard Kopelman

The particle size of tungsten metal powder used to make tungsten wire for use in radio tubes and incandescent lamps must be closely controlled if the highly desirable feature of nonsagging is to be achieved. Our knowledge of factors affecting the particle size of tungsten powder has been limited by lack of any extensive literature on the subject. There are no publications in the English language discussing this problem in any but the most general terms. In this paper the published experimental information on this subject is reviewed. Based on the published data and some experimental data obtained by the author, a general theory of factors affecting the particle size of tungsten metal powder obtained by reduction of the oxides in hydrogen is offered. The various forms of the tungsten oxides and tungsten metal used in the experiments described were those prepared by commercial processes, so that the experimental results obtained on a laboratory scale would be more directly applicable to actual commercial reduction conditions. The effects of time of reduction, temperature. and concentration of water vapor in the hydrogen were observed by counting microscopically the particle distribution obtained. Such a method is very time-consuming, but the data obtained by this method are more reliable and more fundamental than those obtained by any of the several instruments available for measurement of particle size. Review of the Literature Until the year 1912, tungsten powder was prepared commercially by reducing tungstic oxide in the presence of carbon or one of its compounds (such as glycerin or ethylene glycol), usually by firing the mixture in a closed fire-clay crucible. The resultant powder contained about 95 per cent tungsten.' When reduction of tungsten oxides by H² was introduced Commercially,²,³ several investigators became concerned with the equilibria between tungsten metal and its several oxides in an atmosphere of hydrogen and water vapor.4-l3 While these many investigations were in fair agreement on the equilibria WO³ + H2 = WO2 + H2O and WO2 + 2H2 = W + 2H2O there arose considerable controversy as to the chemical composition of the oxide between WO³ and WO², because of very poor agreement on the equilibrium constant of this intermediate oxide reduction reaction. The controversy on this intermediate oxide has been in progress for more than 100 years. Thus Malguti,14 in 1835, decided it was WO2.56 In 1857, Riche15 proposed the formula W³O8. Usler,16 in 1865, confirmed the existence of WsO8 and further proposed W1O1l. In 1897, Desil7 agreed upon W²O8 but also found W5O14.

Jan 1, 1947

By David Russell, Courtland Lee

FOREWOHD-Americans have been able to create wealth from the nation's natural resources to an extent unprecedented in recorded history, thanks largely to the existence of a free market and of a rational body of laws. The General Mining Law of 1872, for instance, by establishing the rules of the game, was quite effective in channeling the ability of Americans to discover and develop mineral deposits. Another example was the Mineral Leasing Act of 1920 which made available the more easily discovered mineral deposits by spelling out the conditions and rules under which miners could obtain leases on federal lands.

Jan 5, 1977

By Adrien Berton

For nearly a century, the Corocoro deposit has been renowned among geologists from the fact that it shares with the Lake Superior deposits of the United States the distinction of being the only important copper districts where native copper is worked commercially. The Corocoro district, named after the city of Corocoro, the capital of the Province of Pacajes (Department of La Pas, Bolivia) is situated towards the western edge of the Bolivian high plateau, at an altitude of a little over 13,000 ft. The most interesting part of the district is that immediately surrounding the city of Corocoro, at a distance, by railway, of 65 miles from La Paz and 210 miles to the Chilean port of Arica on the Pacific Coast. The climate of the region is that of the semi-desert, dry and relatively cold, with big differences of temperature between day and night. The rainy season begins in December and ends in March. The cupriferous lodes of Corocoro have not attracted as much interest as the silver mines of Potosi but they have been known for a long time. In the precolonial period the Indians were using the charquis, or natural native copper sheets, to make small brass objects, and the beautiful pale green brochantite of the outcrops as a source of green pigments. During the colonial period, the oxidized ores of the outcrops were worked for copper, which was used by the mint at Potosi for making currency. The native copper ores were neglected because the Spanish miners were at a loss how to concentrate and smelt them. About 1830, work by rudimentary processes, which were improved little by little, was begun on the native copper ores. The total production of native copper in the following hundred years amounted to 100,000 tons. This native copper, which was remarkably pure, was much appreciated on the European markets before the introduction of electrolytic copper. It was useful for making special ornamental brass or bronze and the granular concentrates of native copper, called barrilla, containing 80 to 85 per cent copper were suitable for making copper sulfate by direct oxidation and subsequent leaching with sulfuric acid.

Jan 1, 1937

By W. R. Kanne, P. R. Strutt, R. A. Dodd

A study has been made of the creep behavior of ß-NiAl of stoichiometric composition in the temperature range 475" to 775°C. Single crystal tensile specimens were deformed under a constant applied load. From slip line studies and tensile axis rotations it was concluded that the crystals deformed by pencil-glide on (100) and (110) planes with a (100) slip direction. Electron microscope thin-film studies showed evidence for profuse cross-slip, and the dislocation Burgers vector was determined to be (100). There was no tendency for the dislocations to lie in definite slip planes, although a strong alignment of segments of edge dislocations was frequently seen. The activation energy for creep in the temperature range 475" and 775°C was judged to be much lower than that for creep at temperatures above 775°C. It is possible that the rate-controlling process is the thermally activated cross-slip of screw dislocations. In recent years considerable interest has developed in the possible use of high-melting-point intermediate phases for high-temperature applications necessitating good creep resistance. Ordered alloys such as Ni3A1, modified by alloying additions, have received particular attention, culminating in the recent development by Pratt and Whitney of single crystal turbine blades.' The intermediate phase NiAl has considerable theoretical interest from a creep standpoint because not only is it ordered up to the melting point (-1650°C at stoichiometry) but it contains a high concentration of structural vacancies on the aluminum-rich side of stoichiometry. These vacancies are known to exert a strengthening effect under some conditions,' but in addition they might be expected to affect high-temperature creep rates through dislocation climb. The present paper deals with the slip line and dislocation structures developed during creep of stoichiometric NiAl between 475" and 775C, and with possible attendant creep mechanisms. MATERIALS AND TEST TECHNIQUES NiAl ingots of stoichiometric composition were prepared by induction melting 99.996 pct A1 and 99.98 pct Ni (kindly provided by the Kaiser Aluminum Co. and the International Nickel Co., respectively) in 100 cc pure alumina crucibles in a helium atmosphere. No chemical melting flux was used in order to avoid con- tamination of the alloy. Each ingot was slowly direc-tionally solidified to avoid porosity and to produce very large grains up to 2 in. in length. In this way, ingots were obtained which were suitable for sectioning into single crystal creep specimens. Chemical analysis indicated that all alloys were within the range 49.6 0.3 at. pct Ni. For the present investigation, identical rectangular single crystal blanks were cut vertically from one particularly large crystal in an ingot using a series of three diamond cut-off wheels with appropriate spacers. Thus, all sliced crystals had the same orientation with the tensile axis parallel to the long side of the rectangle; the initial orientation of the tensile axis is shown as S, in Fig. 1. The blanks were homogenized at 1250 to 1300°C for 48 hr and subsequently cooled slowly to room temperature. A gage length of rectangular cross section and about 0.75 in. in length was prepared on each specimen using an electrolytic lathe and a dilute nitric/phosphoric acid electrolyte. The gage length cross section was 0.250 0.0005 in. by 0.040 ± 0.0005 in. Holes to accommodate tensile grips were electrolytically machined using a rotating acid jet. After creep testing, this same technique was used to cut discs for transmission electron microscopy. Thus, all shaping was done electrolytically, the only exception being that (122) sections were spark-machined from some speci-

Jan 1, 1970

By J. D. Verhoeven

In the past 15 years a considerable amount of experimental and theoretical work has been done concerning the onset of convection in liquids as a result of interm1 density gradients. This work, which has been doue in many different fields, is reviewed here and extended slightly to give a rrlore quantitative understanding to the probletrz of conzection in liquid metal dlffusion experinletzts. In liquid metal systems the capillary reservoir technique is currently used, almost exclusively, to measure diffusion coefficients. In this technique it is necessary that the liquid be stagnant in order to avoid mixing by means of convection currents. Convective mixing may result from: 1) convection produced as a result of the initial immersion of the capillary; 2) convection produced in the region of the capillary mouth as the result of the stirring frequency used to avoid solute buildup in the reservoir near the capillary mouth; 3) convection produced during solidification as a result of the volume change; and 4) convection produced as a result of local density differences within the liquid in the capillary. The first three types of convection have been discussed elsewhere1-a and are only mentioned for completeness here. This work is concerned only with the fourth type of convection. Local density differences will arise within the liquid as a result of either a temperature gradient or a concentration gradient. It is usually, but not always, recognized by those employing the capillary reservoir technique that the top of the capillary should be kept slightly hotter than the bottom and that the light element should be made to migrate downward in order to avoid convection. In the past 15 years a considerable amount of work, both theoretical and experimental, has been done in a number of different fields which bear on this problem. This work is reviewed here and extended slightly in an effort to give a more quantitative understanding of the convective motion produced in vertical capillaries by local density differences. The Stokes-Navier equations for an incompressible fluid of constant viscosity in a gravitational field may be written as: %L + (v?)v = - ?£ + Wv - g£ [1] where F is the velocity, t the time, P the pressure, p the density, v the kinematic viscosity, g the gravitational acceleration, and k a unit vector in the vertical direction. A successful diffusion experiment requires the liquid to be motionless, and under this condition Eq. [I] becomes: where a is the thermal expansion coefficient [a =-(l/po)(dp/d)], a' is a solute expansion coefficient [a' = -(l/po)(dp/d)], and the solute is taken as that component which makes a' a positive number. Combining with Eq. [3] the following restriction is obtained: Since there is no fixed relation between VT and VC in a binary diffusion experiment, Eq. [5] shows that the condition of fluid motionlessness requires both the temperature gradient and the concentration gradient to be vertically directed. Given this condition of a density gradient in the vertical direction only, it is obvious that, as this vertical density gradient increases from negative to positive values, the motionless liquid will eventually become unstable and convective movement will begin. The classical treatment of this type of instability problem was given by aleih' in 1916 for the case of a thin fluid film of infinite horizontal extent; and a very comprehensive text has recently been written on the subject by handrasekhar.' It is found that convective motion does not begin until a dimensionless number involving the density gradient exceeds a certain critical value. This dimensionless number is generally referred to as the Rayleigh number, R, and it is equal to the product of the Prandtl and Grashof numbers. For the sake of clarity a distinction will be made between two types of free convection produced by internal density gradients. In the first case a density gradient is present in the vertical direction only, and, since the convection begins only after a critical gradient is attained, this case will be called threshold convection. In the second case a horizontal density gradient is present and in this case a finite convection velocity is produced by a finite density gradient so that it will be termed thresholdless convection. Some experimentalists have performed diffusion experiments using capillaries which were placed in a horizontal or inclined position in order to avoid convection. These positions do put the small capillary dimension in the vertical direction and, consequently, they would be less prone to threshold convection than the vertical position. However, if the diffusion process produced a density variation, as it usually does, it would not be theoretically possible to avoid thresh-

Jan 1, 1969

By Thomas L. Garwood, F. C. Menk

I T is generally accepted that no method of coal cleaning except froth flotation is effective in cleaning dust. In the majority of coals mined in the United States the dust sizes contain a high percentage of impurities, hence the removal of the dust from the coarse sizes lowers the impurity content of these sizes. Dedusted coal is desired as a means of providing a better feed to cleaning plants because of increased efficiency in both dry and wet plants. In dry-cleaning plants, a dedusted feed makes for a pervious and uni¬form bed. With a dusty feed the fines tend to segregate in the feed stream and pass en masse over the air separators, causing a lack of uniform aeration and fluidity of the bed necessary to efficient cleaning. In wet-cleaning plants deducting of the feed often decreases the sludge problem to the point of eliminating the necessity of wasting wash water. It may be advantageous to eliminate sludge-settling equipment in favor of dedusting equipment, to provide the advantages of a dedusted feed to the wet-washing process. Dedusting advantages may include: (1) the removal of fusain, especially advantageous in plants washing coal intended for metallurgical coke; (2) prevention of the gradual build-up of solids in the wash water, with a consequent variation in the washing ability of the system; (3) prevention of the loss of dust to the sludge ponds, providing instead a fuel for local consumption or special markets.

Jan 1, 1943

By J. D. Sudbury, J. E. Landers, D. A. Shock

The external corrosion of casing is one of the most important problems facing the present day production man. A 1953 NACE report' estimated the annual cost of casing corrosion at $2,200,000 in 22 fields studied. The fields represented only 10 per cent of the wells in the United States. It was significant that 77 per cent of the failures reported were due to external corrosion. A variety of means for combatting the casing corrosion problem have been discussed in papers such as the NACE survey' mentioned previously. No attempt to revicw these will be made in this paper. Thc scope of this paper has been limited to a discussion of the following major items: (I) an instrument for studying external electrolytic corrosion; (2) use of this instrument to determine the quantity of protective current required to prevent corrosion of casing; and (3) problem of accelerated external corrosion of the oil string at the base of the surface string. ELECTROCHEMICAL MECHANISM OF CORROSION It IS gcncrally belleved that one major cause of external corrosion is the existence of electrolytic cells operating between various formation waters. A theoretical discussion of the role of earth potentials in casing corrosion has been presented by L. de Witte and F. J. Radd.2 A brief picture of the electrolytic corrosion action between two differcnt formations (A and B) is presented in Fig. I. This picture is a review to many but is given to insure clarity. In the anode area, oxidation takes place as iron ions go into solution in formation A as a product of corrosion. In the cathode area. reduction takes place and hydrogen atoms are formed at the boundary between the pipe and formation B. The flow of electrons. as indicated. is into the pipe at the anode or corroding area and out of the pipe into the formation at the cathode. In order to conform with regulations of this journal, the flow of a conventional current (I! is also indicated in this sketch. All subsequent references will be to this so-called conventional current flow and will be indicated by the symbol (I). As this action takes place the layer of hydrogen developed on the cathode offers a resistance to the flow of current in the cell. It is said (hat the cathode has been polarized. This polarizing film can be rcmoved by addition of a so-called dcpolarizing agent which reacts with and removes this hydrogen film. Such an agent must be present in ordcr for this corrosion reaction to go at a rate sufficient to cause a severe corrosion problem. The two common depolarizing agents are: (I) oxy-sen. which readily reacts with hydro gen to form water, and (2) certain bacteria which use atomic hydrogen as part of their life process. It is not difficult to explain the presence of these agents. Oxygen may be present in some very shallow formations. Sulfate reducing bacteria are found to exist in nearly any ground where mud pits might be dug. THE CASING POTENTIAl-PROFILE Instrumentation A sketch of the equipment* uscd in determining casing potential profiles is shown in Fig. 2. The tool is run in the hole using a hoist truck with a three-conductor cable. This tool must be run with tubing and rods out of the hole and should be run with the flow line disconnected. By proper choice of electrode size it can be run in any size casing. The electrodes must be run in an open hole or a hole filled with oil. Measurements cannot be made while immersed in water. The tungsten carbide-tipped knives serve as the electrical robes and arc spaced 25 ft apart. The potential difference along a 25-ft section of casing is measured with a potentinmeter to an accuracy of about 5 mv. Current flowing in the pipe can then

Jan 1, 1956

By John W. Tieman

Coal is a term applied to vegetable matter which, through geological processes of heat and pressure, has had both its physical and chemical properties changed. Because its chemical composition is variable, geologists classify coal as a rock rather than a mineral. Peat represents the initial stages in the development of coal, although not classified as coal itself. PHYSICAL PROPERTIES OF COAL The physical properties are concerned with the characteristics of coal in its natural state, or prior to its end use as a fuel. For example, the hardness of coal determines the maintenance cost on coal handling equipment; the specific gravity of coal determines the coal preparation techniques used in a cleaning plant as well as the capacity of coal bins, boats and size of cargo, and other coal storage facilities. The physical properties are, of course, dependent upon the chemical constituents that make up coal, and thus all properties are interrelated. Specific Gravity The specific gravity of a body is the ratio of the weight of the body in air and the weight of an equal volume of water. The specific gravity of pure coal ranges between 1.25 and 1.70, generally increasing with rank. The most important use of this physical characteristic is the part that it plays in the cleaning of coal by wet wash methods. The basic principle on which these operate is that the specific gravity of coals differs from their associated impurities and that there is a relationship between the velocity of the fall of particles in water and their density. Since the specific gravity of slate is around 2.5 and pyrite is about 5.0, pyrite and slate will fall to the bottom of a container filled with water more rapidly than coal. If the water is given a pulsating motion by

Jan 1, 1973

By T. G. Digges, C. L. Vold, M. R. Achter

A study was made of the effect of the growth conditions on the perfection of single crystals of niobium (columbium). Dislocation densities, determined by means of double-crystal diffractometer measurements , were not greatly affected by the method of crystal preparation but could be reduced by annealing treatments. However, the size, sharpness, and tilt angles of the substructures, observed with X-ray reflection macrograph, were sensitive to variations in growth procedures as well as to subsequent thermal treatments. Although the dislocation density was the same in both types, there were more low-angle bound-aries in crystals grown by zone melting than in those prepared by strain anneal. Mechanisms to account for these observations are discussed in terms of dislocation movements. A planned study of the structure-sensitive properties of refractory metals required the use of single crystals of a high degree of structural perfection and, for ease of handling, of large cross section. It appeared that the strain-anneal technique could satisfy both of these requirements. First, crystals grown in the solid state have been reported to be more perfect than those obtained from the melt.' Second, the diameters of rods which may be produced by zone melting should have a theoretical limit determined by specific gravity, thermal conductivity, and surface tension, while the diameter of strain-annealed rods is limited only by practical considerations. Previously it was shown that niobium (columbium) single crystals of 1 in. diam2 may be grown by strain anneal, compared to the 0.5 in. maximum diameter achieved by zone melting, as reported for molybdenum by Belk.3 The current research was undertaken to investigate and optimize the effect of various process variables on the perfection of 1/4 and 1/2-in.-diam niobium single crystals grown by strain annealing and to compare their perfection to those grown by zone melting. Characterization of these crystals was more conveniently accomplished by means of X-ray than by metallo-graphic techniques. EXPERIMENTAL PROCEDURE Specimen Preparation. Zone-melted crystals of 1/4 in. diam were produced by the standard electron-beam zone-melting technique. The swaged and cleaned rods were outgassed, in the solid state at a temperature near its melting point, at a rate of 12 in. per hr, and single crystals were grown by making two molten passes at 2 in. per hr. By maintaining a zone length of 4 to % in., very uniform single crystals several inches long were obtained. For the strain-annealed crystals, an induction heater was used, in preference to other types of heating, to take advantage of the good penetration of large sections. A five-turn coil, 1 in. long, operating at 10 kc and powered by a motor generator, was contained in a vacuum chamber. The rod, suspended from the upper end, was raised through the coil for both recrystallization and crystal growth. In preliminary work single crystals of the same material were also grown with single and multiturn coils powered by a 450-kc generator. A vacuum of 2 X 10-6 Torr was maintained at temperatures up to 2400°C. Starting with electron-beam-melted ingots of 21/2 in. diam, the analysis for which is given in Table I, the material was cold-swaged to the desired cross section of 1/4 and 1/2 in. diam and then recrystallized. The rods were then strained in a tensile machine and converted to single crystals by passing through the induction coil. As with zone melting, control of orientation is possible by the use of special procedures. Other investigators, see for example Williamson and smallman,4 have reported that orientation control may be achieved by a bending technique. In the present work the strained rod is partially lowered through the coil to start the growth of the crystal. Then it is removed and bent at a point in the poly crystalline portion. Finally, it is returned to the chamber and growth is continued "around the corner". This procedure has certain limitations. If the bending operation exceeds the critical strain, recrystallization may take place. Also, the amount of bending which can be imparted to the rod is limited by coil geometry, and up to now has been 10 deg. However, by repeating the bending and growing operations it should be possible to attain any desired orientation. In preparation for X-ray examination, single crystals were sectioned and planed by means of the spark-erosion technique. To obtain the maximum reflected intensity, the (110) plane was exposed for examination. They were then etched 3 to 5 min in a mixture of con-

Jan 1, 1967

By J. D. Hunt, D. T. J. Hurle

A uariety of eutectic structures are formed in faceted/nonfaceted eutectics. The various structures are explained in terms of the absence or presence of small facets in the liquid groove. Regular structures are produced when, for purely geometric reasons facels cannot form. The presence of a facet in the liquid groove leads to the formation of an irregular or a cell-like complex regular structure, due to the relative immobility of the groove. A classification of eutectics was proposed by Hunt and jackson, based on the presence or absence of facets on the primary phases (the absence of facets may be predicted from the dimensionless entropy of melting2). Eutectics were divided into three groups: 1) eutectics in which both phases grow in a nonfaceted manner; 2) eutectics in which one phase grows faceted, the other nonfaceted; 3) eutectics in which both phases grow faceted. It was suggested that regular1 rodlike or lamellar structures1 should be formed in the first group, that irregular or complex regular structures1 should be formed in the' second, and that irregular structures1 should be formed in the third. Recently it has been shown that the structural classification is incomplete. Regular rodlike structures (InSb-NiSb eutectic3), or broken lamellar structure (Bi-Zn eutectic, Fig. 8), are formed in alloys of the second group when the faceted phase has a large volume fraction. Hunt and jackson' argued that regular structures could form in faceted/nonfaceted systems, but that such structures would be unstable in the presence of microfacets on the lamella of the faceting phase, because the growth rate at a point on such a facet would depend on the kinetic undercooling at the point of nu-cleation on the facet, and not on the local kinetic undercooling. In these circumstances it would not be possible to consistently balance the compositional and kinetic undercooling over a lamellar structure and thus obtain a stable isothermal interface. In this paper we discuss in detail the origin of the various structures formed in faceted/nonfaceted systems, pointing out that the most important factor promoting the formation of a regular structure is the absence of a facet in the liquid groove. 1) FACET FORMATION IN SINGLE-PHASE MATERIALS Facets form when there is an energy barrier for the addition of a new solid layer on an existing solid. When a barrier is present,2 growth proceeds by the lateral movement of steps across a crystallographic plane. The rate-controlling stage of the process occurs when the step is first formed. Hulme and Mullin6 have shown that faceting in single-phase materials can only occur when both interface curvatures are convex with respect to the solid and when the surface is tangential to the facet plane. When even one of the curvatures is concave a facet does not form because new layers of solid from adjacent regions can always feed the facet plane, Fig. 1. Growth under these conditions is then as easy as elsewhere. Similar considerations will apply to eutectic growth; consequently the shape of the faceted phase is extremely important. 2) LAMELLAR SPACING CHANGES IN EUTECTICS Jackson and Hunt7 have shown that the interface undercooling AT of a growing lamellar interface (neglecting kinetic undercooling) is related to the lamellar spacing, A, and growth velocity, v, by an expression of the form: where m, Ql, and nL are constants of the system given in Ref. 7. Eq. [I] is plotted for fixed v in Fig. 2. Jackson and Hunt postulate that a regular eutectic grows near, but to the right of the minimum in the AT vs A curve. They argue that the spacing cannot be to the left of the minimum because the interface is then unstable to fluctuations in A. It cannot grow too far to the right, because when the spacing becomes too wide an isothermal interface can no longer be maintained over the large-volume-fraction phase.7 It is argued that during any change in growth rate the lamellar spacing remains in the permitted range by the movement of lamellar faults. When the spacing is too wide, the fault, shown in Fig. 3, moves to the left; when the spacing is too narrow it moves to the right. The faults, however, have to be formed. heir formation has been shown to occur when local regions deviate considerably from the spacing defined by the lamellar When the spacing is locally too narrow (it passes to the left of the minimum, Fig. 2), pinching off of the narrow phase occurs. When the spacing is locally too wide, the interface on the large volume-fraction phase can no longer be maintained as an iso-

Jan 1, 1969