By B. C. Allen

Grain boundary grooving has been studied in chromium, molybdenum, and tungsten under a variety of conditions using high vacuum techniques and tantalum -gettered argon. The average surface free energy of solid chromium, and the chromium-liquid silver interface free energy were respectively found to be 2200 ± 250 and 500 i 130 ergs per sq cm from groove formation kinetics and estimates of pertinent volume difffusion coefficients. The results for chromium were unffected by variations in interstitial content ranging from 0.003 to 0.09 pct C, or 0.003 to 0.03 pct O. Surface diffusion is the primary mechanism of groove formation in chromium under 1 atm argon at 1200" to 140O°C, and is essentially unaffected by 0.003 to 0.09 pct C, 0.003 to 0.03 pct O , metastable nitrogen contents up to -0.01 pct, and up to 2 torr Ag vapor. At higher temperatures, the major mechanism is volume diffusion in argon or evaporation-condensation in stutic vacuum. Surface diffusion occurs in molybdenum at 0.5 to 0.96 and in tungsten at 0.5 to 0.9 of the absolute melting tempera -ture by a single mechanism, possibly by the migration of single adatoms or vacancies. Results were slightly affected by up to 23 tory Sn vapor, and in molybdenum were essentially unaffected by 0.5 Ti or carbon in the range 0.002 to 0.02 pct. Volume difffusion through the liquid is the mechanism of groove formation in chromium-liquid silver at 1200" to 1400°C and in molybdenum-, Mo-0.5Ti-, and tungsten-liquid tin at 1200" to 2000°C. The solid-liquid interface free energies involved were estimated from grooving kanetics. WHEN a grain boundary intersects a solid surface, a groove tends to form along the line of intersection at temperatures above about half the absolute melting point (0.5 TM). The groove progressively grows by preferential atomic migration either by diffusion or evaporation. Establishment of a groove angle occurs in accordance with the grain boundary and surface free energies involved. The motivation for groove formation is a reduction in the total surface free energy of the system. This study is a continuation of previous work on thermal grooving of chromium, molybdenum, and tungsten.&apos; The temperature ranges were extended, and the effect of metallic and interstitial impurities was evaluated. The results were such that certain interface free energies and surface self-diffusion coefficients were deduced from the grooving kinetics. EXPERIMENTAL WORK Materials and Preparation. As indicated in Table I, the 0.05-0.08-cm-thick chromium, molybdenum, and tungsten sheet used was nominally 99.99 pct after recrystallization. Two lots of molybdenum with about the same analysis, Mo-0.5Ti,* and tungsten were ob- *Alloy compsitions are expressed in weight percent . tained commercially. Extruded chromium rod,&apos; prepared from iodide process crystals, was warm rolled to sheet at 700°C. Sheet of three Cr-0 impurity alloys containing up to 0.03 pct 0 was prepared by warm rolling arc melted, extruded, and swaged rod. Two Cr-C impurity alloys containing up to 0.09 pct C were made by equilibrating unalloyed chromium with a known amount of CH4 for 24 hr at 1150°C in previously evacuated quartz capsules. Chromium containing nominally 0.015 and 0.06 pct N was similarly prepared by equilibration with NH3. The sheet was recrystallized to give a stable grain size about equal to the sheet thickness. Molybdenum and Mo-O.5Ti were recrystallized in a tantalum resistance furnace 1 hr at 1 x lo-5 torr at 2300" and 220O°C, respectively. Tungsten was similarly annealed for 1 hr at 2500°C. Chromium and its impurity alloys were outgassed at 1100°C and recrystallized 1 hr at 1700°C under 1 atm Ar. Except for nitrogen, the impurity content stayed roughly constant. Nitrogen in both alloys was reduced to <0.001 pct. In fact, over 80 pct of the added nitrogen was lost after outgassing at llOO°C and annealing sheet 1 hr at 1300°C in argon in the presence of tantalum. Such a rapid loss can be rationalized since -2 torr N are required for equilibrium with 0.04 pct N in solution,3 while the equilibrium pressure is ~10-5 torr over tantalum at 1300°C.4 The recrystallized sheet was cut into small coupons which were metallographically ground and polished on one side with a minimum of grain boundary relief. The surface roughness was on the order of 0.01 µ. The tin and silver used were nominally 99.999 spec-trographically pure. After being outgassed at 1100°C and equilibrated in a molybdenum crucible for 0.5 hr at 1800°C in argon, the tin contained 3 ppm 0, <0.3 ppm N, and 0.1 ppm H. Following outgassing at 900°C and equilibration in a chromium crucible 1 hr at 1400°C in argon, the gas content of the silver was 1 ppm O, <0.5 ppm N, and 0.3 ppm H. Grooving Under Argon or Vacuum. All specimens were placed in unsealed containers made from rod or sheet of the same alloy, thereby enabling the polished surface to achieve gas-solid equilibrium. The annealing fixtures are shown in Fig. 1. The specimen was placed in a resistance furnace with a tantalum or Ta-10W heating element plus tantalum fixtures or radiation shields. Chromium was outgassed at 1100°C, and molybdenum and tungsten were outgassed at 1900°C to 1 x l0-5 torr or at the grooving temperature, whichever was lower. In vacuum anneals, the specimen was then heated directly to the intended grooving temperature. In argon anneals, 99.996 Ar was admitted

Jan 1, 1970

By C. E. Lundin, M. Hansen, D. J. McPherson

PRIOR work on the Zr-Cu phase diagram by Alli-bone and Sykes,&apos; Pogodin, Shumova, and KUGU cheva,&apos; and Raub and EngeL3 as confined largely to copper-rich alloys. The investigations of Raub and Engel were the most recent and seemingly the most complete of these. Alloys from 0 to 68.3 pct Zr were studied principally by thermal analysis and microscopic examination. These authors reported an inter metallic compound ZrCu, (1116°C melting point) and two eutectics, one at 86.3 pct Cu (977°C mp) and the other at 49 pct Cu (877°C mp). The solubility of zirconium in copper was reported to be less than 0.1 pct at 940°C. The zirconium melting stock consisted of Westing-house "Grade 3" iodide crystal bar (nominally 99.8 pct pure). It was treated by sand blasting and pickling (HF-HNO, solution) to remove the surface film of corrosion product, resulting from grade designation tests. The crystal bar was cold rolled to strip, lightly pickled again, and cut into pieces approximately 1/32 in. thick and 1/4 in. square. These were cleaned in acetone, dried, and stored for charging. The high-purity copper (spectrographic grade) was supplied by the American Smelting and Refining Co. with a nominal purity of 99.99 pct. These copper rods were rolled to strip, cut into squares the same size as the zirconium platelets, cleaned in acetone, dried, and stored. Equipment and Procedures The equipment used for melting and annealing the zirconium binary alloys and for the determination of solidus curves has been described in connection with previous work on the Ti-Si system&apos; and in recent papers in this series describing the studies on eight binary zirconium systems.5-&apos; Techniques employed for preparing and processing the alloys were also similar to those used in the above references. Ingots of 20 g were melted under a protective atmosphere of helium on water-cooled copper blocks in a nonconsumable electrode (tungsten) arc furnace. The ingots were homogenized and cold-worked prior to isothermal annealing to aid in the attainment of equilibrium. The specimens were heat-treated in Vycor bulbs sealed in vacuo or under argon, depending on the temperature of the anneal. Quenching was accomplished by breaking the Vycor bulbs under cold water. Temperature control was within ±3OC of reported temperatures. Thermal analysis was primarily relied on to determine eutectic levels, peritectic levels, and compound melting points. The induction furnace incipient melting technique was also used but did not provide the accuracy obtained by thermal analysis in this system, which involves much lower solidus temperatures than the other zirconium systems. A special technique for the determination of characteristic temperatures was employed in the case of several intermediate phases and their eutectics which displayed very small differences in melting temperatures. Specimens were sealed in Vycor bulbs and annealed at a series of very accurately controlled temperatures. Metallographic examination was then employed to reveal incipient melting. Furnaces and techniques in general were described previously.&apos; The echant used was 20 pct HF plus 20 pct HNO3 in glycerine unless otherwise stated. Results and Discussion The chemical analyses of the majority of alloys prepared for the determination of phase relationships in this system are given in Table I and a brief summary of the equilibrium anneals employed is given in Table 11. In a preliminary program, alloys containing 1, 4, and 7 pct Cu were annealed for three different times at each of the temperatures 700°, 800°, and 900°C. No change in the relative amounts of phases present was detected after 350, 150, and 75 hr at the above temperatures, respectively. The times listed in Table II were accordingly chosen as a result of these preliminary tests. Zirconium-rich alloys containing from 0.1 to 10 pct CU were reduced by cold pressing from 58 to 8 pct, depending upon thk alloy content, homogenized for 7 hr at 900°C, and then reduced 80 to 13 pct by cold rolling, again depending upon copper content. Other alloys were studied in the cast, or cast and annealed conditions. The contracted scope of investigation for this system included the range 0 to 50 atomic pct Cu. This approximate region is shown in Fig. 1. Due to evidence of phase relationships departing considerably from those proposed by Raub and Engel" in the 50 to 100 atomic pct range, the investigation was extended to cover this composition area rather thoroughly also. Fig. 2 is a drawing of the entire diagram. The labeling of some phase fields was omitted in Fig. 2 for the sake of clarity. An expanded view of the zirconium-rich region, with the experimental points necessary for its construction, is given in Fig. 3. The generally accepted value of Vogel and Tonn8 or the allotropic transformation a + 862&apos; ±5OC, was employed in the construction of these diagrams. A careful study revealed that the "Grade 3" crystal bar used in this investigation actually transforms over the approximate range 850" to 870°C, due to impurities. It must be expected that this two-phase field in unalloyed zirconium will cause some departures from binary ideality in the very dilute alloys. Zirconium-rich Alloys: The a + ß transformation temperature is decreased from 862" to about 822°C by increasing amounts of copper. Thus, a eutectoid reaction, fi ß a+ Zr,Cu, occurs at a composition of about 1.6 pct Cu. The eutectoid level was determined to lie between the alloy series annealed at 815" and 830°C. The placement of this eutectoid temperature

Jan 1, 1954

By P. Gordon

An isothermal jacket microcalorimeter, supplemented by metallographic, microhardness, and X-ray measurements has been used to study the isothermal annealing of high purity copper after room temperature tensile deformation. The amount of stored energy released during annealing has been measured as a function of deformation in the range 10.8 to 39.5 pct elongation. The data have shown the major heat effect to be associated with recrystallization and have allowed an analysis of the recrystal-lization kinetics and the calculation of activation energies of recrystallization. WHEN a metal is deformed plastically, some of the energy expended is dissipated as heat during the working process, while the remainder is stored within the metal in the form of lattice distortions and imperfections. During subsequent heating of the metal, the distortions and imperfections can be largely annealed out and the associated stored energy released as heat. It is apparent that measurements of the evolution of stored energy during such annealing may produce important information concerning the nature of the annealing mechanisms and the imperfections involved. Some excellent studies of this type have been made in the past, notably those of Taylor and Quinney,&apos; Suzuki,2 Bever and Ticknor,3 Borelius, Berglund, and Sjöberg,4 and Clarebrough et al.5,6 None of this work, however, employed isothermal techniques, with the exception of the Borelius studies&apos; in which only the early annealing stages were investigated. Since isothermal measurements, as compared with heating or cooling curve, have the merits that 1—they reveal the kinetics of a process more clearly, 2—the results obtained are more easily applied to theory, and 3—most fundamental investigations of annealing using techniques other than calorimetry have been carried out isothermally, it was considered important to apply calorimetry to the study of the isothermal annealing of metals. Accordingly, an isothermal jacket calorimeter of the Borelius type,&apos; supplemented by metallographic, hardness, and X-ray measurements, has been used to study the annealing of high purity copper after room temperature tensile deformation. Experimental The microcalorimeter has been described fully elsewhere." Briefly, the specimen to be studied is placed in a constant temperature environment of virtually infinite heat capacity achieved, as shown in the drawing of Fig. 1, by means of a vapor thermostat. A high thermal resistance is provided between the sample and the environment and a sensitive differential thermopile (see Figs. 2 and 3) arranged with half its junctions in contact with, and thus at the constant temperature of, the environment, and the other half in contact with the sample. A reaction in the sample develops a small difference in temperature, AT, across the thermopile, which is followed by a recorder-galvanometer set-up as a function of time, t, and is converted to reaction heat per unit time, P, by the use of the equation AT P=a?T + b AT dt The constants, a and b, in Eq. 1 are determined by a simple calibration, making use of the Peltier heat developed by a small current run through the junction of a thermocouple located in an axial hole in the specimen (Fig. 2). In its present form, the limit of sensitivity of the calorimeter is a heat flow of 0.003 cal per hr. The copper used was the spectroscopically pure metal supplied by the American Smelting and Refining Co. in the form of 3/8 in. diam continuously cast rod, reported to be 99.999+ pct Cu. A small amount of the copper was available at the start of this work and is referred to hereafter as lot A. A second batch, lot B, was obtained later, most of the results described subsequently being for this lot. As will be seen, there is some indication that lot A was somewhat purer than lot B, but it is not known whether this difference was present in the as-received metal or arose during subsequent handling. The two lots of copper were remelted and cast into two 1½ in. diam ingots in vacuo, using high purity graphite crucibles and molds. The ingots were upset several times to break up the large cast grains, and then rolled and swaged to rods 0.391 in. in diameter, using several intermediate anneals with about 40 pct reduction in area between anneals. The penultimate anneal was 2 hr at 350°C. X-ray examination showed no marked general preferred orientation in the resulting rods. The grain structure typical of the two rods is shown in the micrograph of Fig. 4." It was found to be virtually im- possible to get an unambiguous measure of the absolute grain size in the two annealed rods because of the profusion of annealing twins and the lack of regularity of the grain boundaries. However, counts of the number of boundaries intersected per unit length along a random line on a polished section, making a correction for the proportion of boundaries (about half) estimated to be twin boundaries, gave a figure of about 0.015 mm for the average grain diameter. The grain size of the rod from lot A was about 5 pct smaller than that from lot B. The rods were cut into 1 ft long bars and these deformed in tension at room temperature to various total elongations in the range 10.8 to 39.5 pct. A strain rate of 1 pct per min was used. The deformed bars were then stored in a dry ice chest until such time as samples were to be cut from them. Five bars deformed as indicated in Table I were used for the subsequent tests. In all cases, all the calorimeter.

Jan 1, 1956

By J. Walter Snavely

PRESENT-DAY processing in many industries, calcining, sintering, briquetting, beneficiation and nodulizing, increasingly calls for the handling of large volumes of hot bulk materials. Various types of conveyors have been employed. This discussion will cover the factors governing their selection. For temperature ranges up to 400°F, or approximately 200 °C, a wide range of conveyors is available. Special constructions of rubber conveyor belts, steel conveyor belts, vibrating and shaker conveyors, apron conveyors, and drag chain conveyors, all are used successfully. As temperatures go well above 400 2F, however, choice of conveyors is narrowly limited. This paper will consider the problem of handling bulk materials only where the temperatures exceed 400°F. The arbitrary selection of 400 °F as a dividing point undoubtedly can be challenged, as special conveyor belting constructions are available which are suitable for temperatures in excess of 400°F. However, when the relatively short life of such belts and the cost of their replacement, with the attendant down time, are balanced against the reliability and long service life of the properly designed steel constructed units to be discussed, there is little question in any operator&apos;s mind that the special belts are more expensive to use. Because the conveyors under study are for the handling of bulk materials, inevitably including a high proportion of fines, obviously wire mesh belts cannot be included for consideration. Even though this type of conveyor is widely used at high temperatures, i.e., for carrying glassware through a lehr, it is unsuited for the conveying of bulk materials, and therefore will be excluded from further discussion in this paper. Preliminary to the study of the conveyor itself is the determination as to whether the material is to be cooled while it is being handled, or whether the processing requires retention of all heat and the maintenance of a given temperature range. In the majority of cases cooling is incidental to or part of the handling process, when the handling, for example, follows completion of sintering, roasting, calcining, refining, or some other process. To meet such operating conditions successfully, the conveying medium used must have: 1—a construction capable of withstanding maximum initial temperatures of the material being handled. 2—a construction providing efficient heat transfer for cooling. 3—a construction providing dependable operation and long life with minimum service requirements, and 4—a construction providing controlled and efficient conveying. Under the usual conditions of cooling during the handling, the construction selected to withstand the initial maximum temperatures does not necessarily involve using alloys, as excellent results can be achieved with normal carbon steels and cast irons, when they are properly applied and proportioned. The earliest and simplest type of conveyor for handling very hot materials is the cast steel drag chain conveyor, still widely used for handling hot cement clinker, as illustrated by Figs. I and 2. Because of the rugged and generous proportions of the chain link design, low carbon steels are entirely suitable for the links. The pins, however, must be alloy steel. The simple, rugged construction of this type of conveyor makes it readily capable of withstanding high initial temperatures, even though the chain is operating buried in the material. The drag-chain type of conveyor has advantages and limitations. Although the efficiency of the heat transfer is relatively poor, the life of the conveyor is reasonably long, and because of its crude simplicity it does not require much servicing. However, as a conveyor, it is limited in capacity, and largely limited to horizontal runs. Furthermore, because of the crude design, heavy weight, and the chain operating at the temperature of the material, greatly reducing permissible operating chain pulls, this type of conveyor is limited to relatively short centers. Another type of conveyor that has been used for very hot materials is the cast pan conveyor. Because of its very generous proportions the cast pan, which is made of either cast iron or malleable iron, can withstand initial maximum temperatures. It also provides efficient heat transfer for cooling. Further, it is on efficient conveyor construction, which can be used for inclines. Because the chain employs rolling friction instead of sliding friction, and is not in the maximum temperature zone, much longer centers are possible. It is this type of conveyor that is frequently used in the casting of various metal pigs, pig iron, and aluminum; it is obvious, therefore, that very high initial temperatures are being handled. With this kind of conveyor the return run is frequently sprayed with water to accelerate heat transfer. The build-up of residual heat in the very heavy cast pans is thus overcome. The outboard roller steel pan conveyor is an improved pan conveyor&apos; which provides high rates of heat transfer and substitutes formed steel pans for the heavy cast pans. It is a very efficient conveying medium. The details of this particular construction are clearly shown in Fig. 3. An early application of this type of conveyor is shown in Fig. 4. In this case the conveyor units are handling roasted phosphate rock at average temperatures of 1000" to 1500°F, and frequent maximum temperatures as high as 1900°F. Several widths are used. The capacity of the unit at a speed of 50 fpm is approximately 30 tph per inch of width at peak loadings, average capacity being about 1/3 of peak loading. The assembled conveyor is shown in Fig. 5, with views of both the top and the underside to show all the construction details. In particular, the following general design principles were carried out in this construction:

Jan 1, 1954

By V. Koump, T. F. Perzak, R. H. Tien

A series of experiments were carried out in which the rates of propagation of the liquidus and the eutectic fronts Mere measured during essentially one-dimensional freezing of Al-Cu alloys. The dimensions of the ingots were 3 by 5 by 6 in. Three different alloys containing 0.1, 4.5, and 17 pct Cu were used in these experitments. For each alloy the rate of heat removal was varied to give a total jreezing time in the range 3 to 30 min. The results of these measurements cowlpared favorably with the theoretical model of freezing of binary alloys with time-dependent surface temperature. IN engineering analysis of solidification of commercia1 steels and nonferrous alloys it is a common practice to assume that an alloy freezes by propagation of an isothermal solidification front, i.e., essentially as a pure metal. In two recent theoretical investigations&apos;j2 the present authors explored the possibility of a more realistic approach to the problem of solidification of alloys. In the proposed model the freezing of an alloy is assumed to take place by propagation of two isothermal fronts, i.e., the liquidus front and the solidus (or eutectic) front. The region between the two fronts contains both liquid and solid and is referred to as the solid-liquid region. The width and the solid content of the solid-liquid region vary with alloy type, solute concentration, and cooling rate. For a given alloy system, initial concentration of solute, and the mode of heat removal, the proposed model yields the temperature distribution within the solid skin, temperature, solid fraction, and concentration distributions with the solid-liquid region, and the rates of propagation of the liquidus and the solidus fronts. This model is obviously of considerable practical importance in engineering analysis of solidification processes, since it gives a more realistic estimate of skin strength during solidification and a better estimate of the total freezing time. Before the new model can be used with confidence, however, it is necessary to test this model experimentally. The experimental testing of the proposed model is a relatively simple matter since the effects to be measured are large and a relatively simple experiment will suffice. The theoretical model predicts, for example, that during freezing of an alloy containing substitutional type solute (negligible diffusion in the solid during freezing) the solid-liquid region occupies an appreciable portion of the ingot, even at low concentration of solute.&apos; Another prediction of the theo- V. KOUMP, formerly with U. S. Steel Corp., is now with Research and Development Center, Systems and Process Division, Westinghouse Electric Corp., Pittsburgh, Pa. R. H. TlEN is Senior Scientist, Fundamental Research Laboratory, U. S. Steel Corp., Research Center, Monroe ville, Pa. T. F. PERZAK, formerly with U.S. Steel Corp., is now with Fiber Industries, Greenville, S. C. Manuscript submitted March 6, 1968. IMD retical model, easily verifiable by experiment, is that the rate of propagation of the solidus (or eutectic) front increases as the solidus front approaches the center of the slab. This prediction is contrary to well-known behavior of the solidification front during freezing of pure metals, where the rate of propagation of the solidification front decreases with time and freezing is completed at the lowest rate. A rather severe test of the proposed model is provided by comparison of theoretical predictions and experimental measurements of the effects of cooling rate and composition on the rates of propagation of the liquidus and the eutectic fronts. In order to test the soundness of the formulation and the method of solution of the problem of solidification of alloys a series of experiments were carried out in which the rates of propagation of the liquidus and the eutectic fronts were measured during essentially one-dimensional solidification of A1-Cu alloys. The A1-Cu system was chosen strictly as a matter of convenience. Three different alloys containing 0.1, 4.5, and 17 pct Cu were used in these experiments. For each alloy the rate of heat removal was varied to give the total freezing time in the range 3 to 30 min. The results of these measurements are compared with the predictions of the theoretical model of solidification of binary alloys, with time-dependent surface temperature.&apos; Before the experiments described in this paper were undertaken, a serious attempt was made to utilize the measurements of previous investigators to test the theoretical model. In the course of this preliminary study a careful review was made of experiments of Pellini and coworkers3 and Doherty and Melf~rd.~ The measurements in Pellini&apos;s work were carried out using a steel containing at least four major components. Evaluation of the solid fraction-temperature relation for this steel (required in the theoretical model) is difficult and uncertain. Doherty and Melford, on the other hand, measured the solid fraction-temperature relation experimentally, but did not give sufficient data to explore the effects of composition and the cooling rates on solidification. Hence it was not possible to utilize these measurements to test our theoretical model. EXPERIMENTAL METHOD The experimental technique used in this investigation differs somewhat from the more conventional techniques employed in solidification studies. This technique was developed primarily to eliminate con-vective mixing in the molten metal caused by pouring of molten metal into the mold. In our experiments A1-Cu alloys were melted directly in the mold. The mold assembly used in solidification experiments is shown in Fig. 1. The mold was fabricated from *-in. stainless-steel sheet. The dimensions of

Jan 1, 1969

By F. W. Bryan, D. H. Lynch

Introduction This paper is a general description of current central Florida phosphate mining, beneficiation, and product transportation. It is directed and believed to be of interest to engineers not familiar with this industry. Deposit: The phosphate deposits of central Florida are generally located in a five county area which includes Polk, Hillsborough, Hardee, Manatee, and DeSota counties. Geologically, the deposit is of marine origin and is identified as the Bone Valley formation. This formation is Pliocene to Recent in geological age and overlies a Miocene limestone formation known as the Hawthorn. The Bone Valley formation sediments are regionally characterized by equal proportions of apatite, quartz, and clay. The clay is predominantly of the mont-morillonite family. On a local scale, however, the proportions of these three major constituents vary considerably. The phosphate occurs as the apatite mineral (Ca 10F2(PO4)(6) and with the clay and sand, the minable ore is commonly referred to as matrix. This matrix is overlain by unconsolidated overburden of sand and sandy clays, ranging in depth from 10 to 45 ft. The matrix usually occurs in fairly horizontal continuous beds from 3 to 25 ft in thickness. The bedded limestone formation lies directly below the matrix and is generally well defined. The phosphate particles range from 3/4 in. to 200 mesh (Tyler) in size. The phosphate particles coarser than 14 mesh are called pebble phosphate and those less than 14 mesh are termed flotation feed which, when beneficiated, subsequently become concentrates. Through mining and beneficiation, phosphate quality is measured in BPL percent which stands for bone phosphate of lime units. In subsequent chemical manufacturing, the quality is indicated by P205 content. The deposit is economically characterized by various ratios such as tons of product per acre and cubic yards handled per ton of product. Magnesium, iron, and aluminum content are also considered in evaluating ore reserves. These elements are often critical to the chemical fertilizer processes. Presently, an ore body is considered economically minable if it meets the criteria shown in [Table 1]. These, of course, are general guidelines and specific costs and returns on investment must be considered in each case for acquiring reserves. On a new grass-root venture, a 20-30 year life is generally expected with a mineral recovery of 80%. History and Uses Phosphate mining in central Florida began around the turn of the century. However, in the early days, only pebble phosphate was produced until about 1930 when technology was available to beneficiate the -14 + 150 mesh particles. The -150 or -200 mesh material was discarded as it is today. The basic processes for beneficiation are washing, scrubbing, desliming, sizing, and flotation. These basic unit processes are essentially the same today although many improvements have been developed since the early days. Phosphate is used primarily in the production of high analysis fertilizer chemicals, typical of which are triple superphosphate, monoammonium phosphate (MAP), and diammonium phosphate (DAP). Phosphate is also used in the production of food preservatives, dyes for cloths, vitamin and mineral capsules, steel hardeners, gasoline and oil additives, toothpaste, shaving creams and soaps, bone china dishes, plastics, optical glass, photographic films, light filaments, water softeners, insecticides, soft drinks, road fill, and livestock feed supplements. Florida produces over 80% of the nation&apos;s marketable phosphate rock and one-third of the world production, according to the US Bureau of Mines. This amounted to approximately 35 million tons in 1975. Exports of Florida phosphate rock were to such countries as Canada, Japan, West Germany, Italy, and India, with Canada and Japan being the major users. Almost 95 o of all outbound cargo shipped through the port of Tampa is phosphate rock or related products. Beneficiation Following is a description of Agrico&apos;s new Fort Green beneficiation plant which is typical of the newer large capacity plants being built in the field. Agrico&apos;s Fort Green mine was completed in 1975 and is located in the southwest corner of Polk County and is directly adjacent to Manatee, Hillsborough, and Hardee Counties. With some minor differences, Fort Green is typical of a modern central Florida plant. The rated capacity is 3,000,000 plus tons of product per year and this varies according to the richness of the ore being handled. A simplified flowsheet is presented in [Figs.1 and 2]. This plant is served by three draglines of the 40-cu-yd class. The phosphate beneficiation is usually divided into three major functional steps: (1) washing and screening to produce a pebble product and flotation feed, (2) feed preparation and (3) flotation to produce concentrates. The typical plant is similarly divided into these three functional areas. Washer: Briefly, the slurried matrix is pumped from two draglines simultaneously at a combined rate of about 20,000 gpm at 2000 tph (solids) to rotary trommel screens sized to make a 7/8-in. separation. ([See Fig. 1]-) The trommel oversize is sent to hammermills where it is crushed and returned to the trommel screens, or pumped to tailings if minor impurities (Fe203, A1203, MgO) are too high. The trommel undersize is pumped to 14 mesh stationary (static) flat screens. The flat screen over¬size is subjected to three stages of 14 mesh vibrating screening and two stages of log washing in order to produce a final pebble product. The pebble product (+ 14 mesh material) is conveyed by belt conveyor to a large on-ground storage pile. Pebble product is reclaimed through a tunnel and loading system below

Jan 1, 1980

By Jacques Steininger, Robert E. England

Single crystals of ZnTe and ZnTe1-,Sex with x up to 0.13 have been grown from the elements by temperature gradient solution zoning using excess tellurium as a solvent. Best results have been obtained with charges with the compositions 45/55 at. pct Zn, Te, for ZnTe and increasing amounts of selenium for ZnTe1-xSex. The temperature in the molten zone was maintained at about 1070°C with a gradient of about 10°C per cm. Chemical analyses of quenched ZnTe ingots show tellurium concentrations in the molten zone as high as 70 pct with concentration differences across the zone of 1 to 2 at. pct Dark dots which are observed by transmitted light microscopy in as-grown crystals can be removed by annealing in zinc vapor at 900 C. INTEREST in wide band gap semiconductors has led to a new study of ZnTe and ZnTel-xSex crystal growth. ZnTe is the only II-VI compound with a wide band gap (2.3 ev) that can be made p type with low resistivity. Attempts to make it n type with low enough resistivity to be useful for p-n junctions have so far been unsuccessful.1 ZnSe has a band gap of 2.65 ev but can be made n type only. However, ZnTel-xSex solid solutions with x as low as 0.36 have been made both highly n and p type2 with a minimum band gap around 2.12 ev3 at room temperature and appear to hold the best promise for efficient injection electroluminescence in the visible. ZnTe has the lowest melting point of the zinc chal-cogenides (1295°C) and consequently attempts have been made to grow crystals from both the liquid and the vapor phase.4 Complicated apparatus is required for growth from stoichiometric melts because of the high vapor pressures of the elements at the melting point of ZnTe and because of the problem of quartz devitrification. Small crystals have thus been grown in high-pressure equipment by Fischer5 and by Narita et a1.6 with pressures of the order of 50 atm of argon to prevent excessive evaporation from the melt. Large crystals of ZnTe can be obtained by growth from the vapor phase4 but they often present numerous dislocations and inclusions. An improvement in the quality of vapor- grown ZnTe crystals was reported by Albers and Aten7 by equilibration of mixtures of small crystals with compositions lying on either side of the solid single-phase field at fixed temperature. The same technique was later applied by Aten8 to the growth of ZnTe1-xSex crystals with less than 1 pct inhomo-geneity. Because of the higher liquidus temperatures of the solid solutions and the high vapor pressure of selenium, previous attempts to grow ZnTel-xSex from the melt have been limited and unsuccessful.9 The phase diagram of the Zn- Te system is reproduced in Fig. 1, based on data from Kobayashi10 and Kulwicki.11 Carides and Fishher12 have reported lower liquidus temperatures on the tellurium-rich side, but their data would require confirmation. The liquidus temperature on the tellurium-rich side decreases rapidly with increasing tellurium concentration and the Te2 vapor pressure over the liquidus also decreases accordingly.&apos;3 The decrease in liquidus temperature and vapor pressure therefore makes it possible to use conventional apparatus if there is a sufficient excess of tellurium in the melt. Single crystals of ZnTe have thus been grown by Kucza,14 in a modified Bridgman technique, from solutions containing up to 60 at. pct of Te by lowering unsupported quartz ampoules through a temperature gradient at about 1200°C. Under these conditions, the phase diagram indicates that the entire charge is initially molten. Crystal growth can therefore proceed by normal freezing and rejection of excess tellurium into the melt. The modified Bridgman technique has several major limitations. Because of the rejection of excess tellurium into the melt during freezing, the melt composition and the temperature at the growth interface vary continuously. They tend to follow the liquidus until the eutectic which is very close to pure tellurium (447°C, >99 pct Te). Since the solidus composition also varies with temperature,15 crystals grown by this method are inhomogeneous. They present small variations from stoichiometry which may affect their structure and physical properties. The simultaneous increase in tellurium content and decrease in melt temperature also combine to reduce the rate of diffusion of tellurium away from the growth interface, thereby causing constitutional supercooling and possibly dendritic growth. To minimize these effects, the initial melt composition is in practice kept relatively close to stoichiometry (less than 60 pct Te). This however limits the possibilities of operating at low temperatures and pressures. This paper describes a modified method of crystal growth by temperature gradient solution zoning (TGSZ) which is an adaptation of the temperature gradient zone-melting technique developed by pfann16 and of the traveling solvent method of Mlavsky and weinstein.I7 The TGSZ method now applied to the growth of ZnTe and ZnTel-xSex crystals is characterized by its very simple experimental arrangement and sample preparation technique. Unlike the modified Bridgman technique, there is no increase in the tellurium concentration in the melt and therefore it is possible to operate at lower temperatures and pressures. This method is also suitable for maintaining a constant temperature at the growth interface.

Jan 1, 1969

By A. E. Lee

THE Blackwell Zinc Co., Inc., a subsidiary of the American Metal Co., Ltd., operates a horizontal retort zinc smelter at Blackwell, Okla. The plant has 14 furnace blocks of 800 retorts each, fired with natural gas on a 48 hr cycle. Over 13,000 tons of zinc-bearing material, chiefly sulphide flotation concentrates, are treated monthly to produce slab zinc and high lead-cadmium fume. In 1942 a program of rebuilding and modernizing the smelter was started. By 1947 furnace smelting capacity had been increased to a point where roasting and sintering facilities were inadequate, and it was necessary to purchase oxidized materials to supplement sinter production. The seven 210 ft Ropp roasters and three 42 in. x 44 ft Dwight-Lloyd machines then in use had been in service at least 20 years and were in need of major rebuilding. Thus it was entirely practical to consider all new equipment and a change of method rather than rebuilding and repairing obsolete units. A study of the problem indicated that roasting as such could be eliminated and roasting and sintering accomplished in one step by a modification of the Robson process,&apos; which had been used since the early 1930&apos;s by the National Smelting Co., Ltd., at their plants at Avonmouth, England, and Swansea Vale, South Wales. Francis P. Sinn, General Manager, Zinc Smelting Operations, The American Metal Co., Ltd., who was familiar with the practice in England, suggested the use of one large machine for the entire operation from concentrate to sinter. One step sintering appeared to best meet Blackwell&apos;s plant requirements and indicated substantial savings in labor, gas, coal, and repair costs. Choice of Machine Size The sinter machine size was set at 12x168 ft for a rated capacity of 540 tons per day. This tonnage, produced on a five day week, would meet the seven day requirements of the 14 furnace blocks. The one large machine was quoted at a lower cost than two or more 6 ft wide machines of similar total capacity. Further, the larger machine could be housed in a smaller structure and only one set of equipment for charge preparation and delivery and for disposal of sinter cake was needed. One machine on a five day week made possible a concentration of the skilled operating personnel and required less men than a plant including two or more machines and related equipment circuits. Fewer units of equipment meant less maintenance, and the two down days weekly allowed ample time to repair and, if necessary, to make up lost production. Experience had indicated better sintering quality and rates with larger masses of material, not only on wider machines, but also in deeper beds. The ratio of windbox perimeter to area for the 12x168 ft machine is 0.179, compared to 0.353 for a 6x102 ft machine and 0.617 for a 42 in. x 44 ft machine. This meant less air leakage with resulting fan power savings and less spoilage of charge along the pallet sides. Performance Initial operation of the new sinter plant was made in November 1951 and regular production attained late in December. The average product sinter output during 1952 and the first half of 1953 has been 18.2 tons per hr. The average for one month has been as high as 22.4 tons per hr. Considerable experimenting with varied operating conditions accounts in part for the below capacity — 24 tons per hr — average output, and work to further improve production rate continues. A typical sinter analyses is 66.0 pct Zn, 0.3 pct Pb, 0.1 pct Cd, 0.3 pct S, 8.0 pct Fe, 2.0 pct SiO,, 0.8 pct CaO, and 0.2 pct MgO. Use of this material has made possible increases in furnace burden and improved furnace operation over the former practice using sinter made from Ropp roasted concentrates. Better lead and cadmium elimination in sintering has permitted the furnace production of slab zinc lower in lead and cadmium. Anticipated economies of operation have largely been gained. The sinter plant is operated by seven men per 8 hr shift — one head operator, three equipment operators and three sweepers — plus one oiler on day shift only. While it has been necessary at times to operate seven days a week to produce the required sinter tonnage, the five day work week usually has been adequate. Consumption of natural gas for sinter bed ignition is 200,000 to 300,000 cu ft per day. Green Ore Sintering Practice The 30 to 31 pct sulphur content of the —200 mesh zinc concentrates is the fuel used to sinter the charge, no coal addition being required. In the feed to the machine, sufficient concentrates are added to crushed return sinter fines containing 0.3 to 0.5 pct sulphur to produce a charge averaging 5.0 to 6.5 pct sulphur. Since the return sinter used in Blackwell&apos;s practice is varied from — 1/2 to — 1/8 in., the actual sintering mixture of fine sinter and concentrates is somewhat higher in sulphur. The coarser sinter particles are too large to resinter and merely aid porosity in the sinter bed. The ratio of concentrates to return sinter in the charge ranges from about 1:4 to 1:5.5. Variations are based on the appearance of pried up bed sections, bed exit gas temperature trends, windbox suctions, and return sinter size. Sufficient sulphur must be used to obtain fritting of the charge into a soft sinter cake and to aid in the elimination of lead and cadmium. Excessive feed sulphur will result in partial slagging of the cake impairing porosity and prolonging sintering time.

Jan 1, 1954

By C. Wert, G. Mah

A relaxation peak thought to be due to the presence of C-C pairs in cobalt has been observed. It exists both above 420"C, where cobalt has the fcc structure, and below 420"C, where cobalt has the hcp structure at equilibrium. The effect is thought, however, to be caused by motion of C-C pairs in the fcc phase in both instances; enough retained fcc phase was deduced to be present at temperatures below 420°C to make the phenomenon possible. Measurements of the aniso-tropy of the effect in single crystals of various orientations of fcc phase showed the effect to have a maximum value in longitudinal strain for a [loo] crystal and a minimum value for a [Ill] crystal. This observation seems to rule out the possibility of (110) nn pairs being responsible for the effect. From measurements of the strength of the relaxation in the alloys, we reach the conclusion that both the binding energy of the pairs and the specific relaxation per pair are smaller than corresponding quantities for interstitial pairs in bcc metals. DETERMINATION of the details of atom placement of small atoms such as carbon, nitrogen, oxygen, and hydrogen in metals has been a difficult problem. In certain alloys such as martensite extensive departure from random placement of the interstitials can be deduced from X-ray diffraction off the atoms of the host metal, but such diffraction techniques are of small help for small departures from randomness. A technique which does offer promise in the latter instance is the anelasticity of these interstitial alloys. Most previous investigations using this property have utilized alloys in which the solvent is one of the bcc metals, alloys such as These studies have been interpreted to show that an interaction exists between interstitials which causes them to form clusters in more than random numbers; the binding energy of interstitials in such clusters has been deduced to be about 0.1 ev per atom (for small clusters of size two to four atoms). Similar investigations have been carried out on close-packed solvent metals, Ni-C by and Diamond and Ag-O by Papazian.8- In both of these svstems. no relaxation of the singly dissolved interstitial is expected, so an-elastic behavior of the interstitials must be caused by their association in some cluster or complex of non-cubic symmetry. Since relaxations in these alloys were observed to have a strength which varied about as the square of the interstitial concentration, the effect was deduced to be caused predominately by motion of i-i pairs in the crystal. A striking difference is observed in relaxation strength of interstitial alloys between the bcc and fcc systems. The specific effect per interstitial atom is much larger for the alloys in the bcc crystals than for those in fcc crystals. Comparing clusters of size two in the Nb-O system4 and the Ni-C system,7 one finds the magnitude of the anelastic effect per interstitial atom in the former to be some 100 times greater than that in the latter. Such a difference in relaxation strength might be caused by a difference in concentration of the pairs (this means a higher binding energy in the bcc crystals). It might also be caused by a large difference in shape factor of the elastic strain field about the pairs between the two cases (a much more noncubic shape factor would be required for the bcc crystals). This investigation was undertaken to examine the possibility of C-C pair formation in alloys of cobalt and carbon using anelastic effects. Since cobalt has both fcc and hep phases, it seemed to offer the chance that measurements over a range of frequency might permit comparison of properties of pairs in the two crystal types. Although this goal was not reached, several significant facts were deduced from the observations. 1) An anelastic phenomenon believed to be associated with the presence of C-C pairs in cobalt exists. It has many features in common with that observed in nickel. 2) The effect is thought to be caused by pair motion in the fcc phase. 3) Calculations of the relaxation strength A, which includes as a parameter the product of the pair concentration, C, and the square of the shape factor &apos;, show that this parameter is much smaller in the CO-C alloy system than in the interstitial alloys in the bcc systems. 4) From this finding, we reach the conclusion that both the binding energy of C-C pairs in cobalt and the specific relaxation strength per pair are small compared to corresponding values for such pairs in the bcc systems. 5) The crystalline anisotropy of the effect permits the identification of reasonable geometrical models of close C-C pairs. I) EXPERIMENTAL PROCEDURE A) Method of Measurement. The anelastic measurements-—all of which were constant frequency measurements of internal friction—were designed to study the expected phenomenon in both the hcp and fcc structures in cobalt. Knowledge of similar measurements in Ni-C alloys led us to believe that the damping peak should occur below the transformation temperature for frequencies near 1 cps and above for frequencies near 100 kcps. This surmise was correct. The low-frequency measurements were made on wire specimens using a vacuum torsion pendulum; the damping peak was found at about 2&apos;70°C at a frequency of 1 cps. Because of large superimposed damping of magnetic origin at this temperature, a longitudinal magnetic field of about 1500 oe was applied to the

Jan 1, 1969

By Michael Tenenbaum

THE importance of semikilled steel as a high tonnage grade has long been recognized. The increasing severity of the applications for which semikilled steel is used makes it desirable to obtain further information regarding the features of open hearth practice and ingot structure that can affect steel performance in subsequent rolling and fabricating operations. Accordingly, an investigation is being carried out studying the structure of various types of semikilled steel ingots. This paper reviews some of the observations made and information gathered in this investigation. By definition, semikilled steel may be considered to include all nonrimming steels in which the natural shrinkage occurring during ingot solidification is offset to an appreciable degree by gas formation. Accordingly, this type of steel includes the entire range intermediate between rimmed and fully killed steel. The resultant ingot structures range from those of steels that have been capped to suppress a weak rimming action to those steels that have been killed in the furnace or ladle to the extent that no mold deoxidizer is required. A survey reported to the 1946 AIME Open Hearth Conference&apos; reviewed the practices being used at 28 major plants for the deoxidation of semikilled steel. It was found that most plants divide the deoxidizing additions between the ladle and the mold many of the plants adding only minor amounts of deoxidizer to the bath or none at all. Silicon, aluminum and titanium were the only elements used for ladle and mold deoxidation. Mold deoxidizers were added as capping additions or as uniformly fed additions. Several practices were reported in which the steel was deoxidized in the ladle to the extent that little or no mold deoxidation was needed. No reference was made to grades capped by using special mold designs or special closures over the top of molds. Accordingly, specific examples of this type of practice will not be considered in this paper. It appeared from this survey of deoxidation practice that semikilled steel can be divided into three types, namely, capped semikilled, in which aluminum is added near the end of pour or after shut-off, intermediate semikilled steels, in which aluminum is fed uniformly throughout the pour, and semikilled steels requiring no mold deoxidation. In an attempt to cover the ingot structures obtained by the range of practices reported in the preceding survey, three series of experimental heats were made using increasing amounts of aluminum, silicon and titanium for ladle deoxidizers. The ladle deoxidizers were added as stick aluminum, 50 pct ferrosilicon and 20 pct ferrotitanium (4 pct carbon), respectively. Two methods of studying ingot structures were used. Ingots were removed from production, burned longitudinally and machined to allow observation of the central pipe and coarse blowholes. During the machining operation much of the finely porous subsurface structure was obliterated. Accordingly, observations were also made

Jan 1, 1947

By Michael Tenenbaum

The importance of semikilled steel as a high tonnage grade has long been recognized. The increasing severity of the applications for which semikilled steel is used makes it desirable to obtain further information regarding the features of open hearth practice and ingot structure that can affect steel performance in subsequent rolling and fabricating operations. Accordingly, an investigation is being carried out studying the structure of various types of semikilled steel ingots. This paper reviews some of the observations made and information gathered in this investigation. By definition, semikilled steel may be considered to include all nonrimming steels in which the natural shrinkage occurring during ingot solidification is offset to an appreciable degree by gas formation. Accordingly, this type of steel includes the entire range intermediate between rimmed and fully killed steel. The resultant ingot structures range from those of steels that have been capped to suppress a weak rimming action to those steels that have been killed in the furnace or ladle to the extent that no mold deoxidizer is required. A survey reported to the 1946 -AIME Open Hearth Conference&apos; reviewed the practices being used at 28 major plants for the deoxidation of semikilled steel. It was found that most plants divide the deoxidizing additions between the ladle and the mold—many of the plants adding only minor amounts of deoxidizer to the bath or none at all. Silicon, aluminum and titanium were the only elements used for ladle and mold deoxidation. Mold deoxidizers were added as capping additions or as uniformly fed additions. Several practices were reported in which the steel was deoxidized in the ladle to the extent that little or no mold deoxidation was needed. No reference was made to grades capped by using special mold designs or special closures over the top of molds. .Accordingly, specific examples of this type of practice will not be considered in this paper. It appeared from this survey of deoxidation practice that semikilled steel can be divided into three types, namely, capped semikilled, in which aluminum is added near the end of pour or after shut-off, intermediate semikilled steels, in which aluminum is fed uniformly throughout the pour, and semikilled steels requiring no mold deoxidation. In an attempt to cover the ingot structures obtained by the range of practices reported in the preceding survey, three series of experimental heats were made using increasing amounts of aluminum, silicon and titanium for ladle deoxidizers. The ladle deoxidizers were added as stick aluminum, 50 pct ferrosilicon and 20 pct ferrotitanium (4 pct carbon), respectively. Two methods of studying ingot structures were used. Ingots were removed from production, burned longitudinally and machined to allow observation of the central pipe and coarse blowholes. During the machining operation much of the finely porous subsurface structure was obliterated. Accordingly, observations were also made

Jan 1, 1949

By Michael Tenenbaum

The importance of semikilled steel as a high tonnage grade has long been recognized. The increasing severity of the applications for which semikilled steel is used makes it desirable to obtain further information regarding the features of open hearth practice and ingot structure that can affect steel performance in subsequent rolling and fabricating operations. Accordingly, an investigation is being carried out studying the structure of various types of semikilled steel ingots. This paper reviews some of the observations made and information gathered in this investigation. By definition, semikilled steel may be considered to include all nonrimming steels in which the natural shrinkage occurring during ingot solidification is offset to an appreciable degree by gas formation. Accordingly, this type of steel includes the entire range intermediate between rimmed and fully killed steel. The resultant ingot structures range from those of steels that have been capped to suppress a weak rimming action to those steels that have been killed in the furnace or ladle to the extent that no mold deoxidizer is required. A survey reported to the 1946 -AIME Open Hearth Conference&apos; reviewed the practices being used at 28 major plants for the deoxidation of semikilled steel. It was found that most plants divide the deoxidizing additions between the ladle and the mold—many of the plants adding only minor amounts of deoxidizer to the bath or none at all. Silicon, aluminum and titanium were the only elements used for ladle and mold deoxidation. Mold deoxidizers were added as capping additions or as uniformly fed additions. Several practices were reported in which the steel was deoxidized in the ladle to the extent that little or no mold deoxidation was needed. No reference was made to grades capped by using special mold designs or special closures over the top of molds. .Accordingly, specific examples of this type of practice will not be considered in this paper. It appeared from this survey of deoxidation practice that semikilled steel can be divided into three types, namely, capped semikilled, in which aluminum is added near the end of pour or after shut-off, intermediate semikilled steels, in which aluminum is fed uniformly throughout the pour, and semikilled steels requiring no mold deoxidation. In an attempt to cover the ingot structures obtained by the range of practices reported in the preceding survey, three series of experimental heats were made using increasing amounts of aluminum, silicon and titanium for ladle deoxidizers. The ladle deoxidizers were added as stick aluminum, 50 pct ferrosilicon and 20 pct ferrotitanium (4 pct carbon), respectively. Two methods of studying ingot structures were used. Ingots were removed from production, burned longitudinally and machined to allow observation of the central pipe and coarse blowholes. During the machining operation much of the finely porous subsurface structure was obliterated. Accordingly, observations were also made

Jan 1, 1949

By F. Keller, J. D. Edwards

The anodic treatment of aluminum presents problems of scientific as well as of commercial interest.l-3 Of particular interest is the fact that, during the anodic oxidation process, the oxide continues to form at the metal-oxide interface under any oxide previously formed. This has led to speculation as to the mechanism involved in the formation of the relatively thick oxide coatings that are used commercially for decorative or protective purposes. Furthermore, the ability of certain types of oxide coatings to adsorb dyes and other substances has stimulated research to determine the actual structure of these adsorptive coatings. It has been found that anodic oxide coatings on aluminum are composed essentially of aluminum oxide. They are formed by the action of oxygen ions penetrating to the metal surface during the electrolytic oxidation treatment. These coatings can be formed in a number of different electrolytes, as for example, those which contain sulphuric acid, chromic acid, oxalic acid, or boric acid. These are the commonest and most useful electrolytes employed commercially. Except for certain specific conditions of formation, the coatings in general have been found to be amorphous alumina, as far as can be determined by X-ray or electron-diffraction methods. Anodic oxidation processes can be arranged in three rather general classes if they are grouped in relation to the solvent action of the electrolyte on the coating.4 In the first class, the electrolyte has little or no solvent action on the coating that is formed. In general, coatings produced under such circumstances are nonporous and non-adsorptive. In the second class, the electrolyte exerts an appreciable solvent action on the coating. These coatings are porous and adsorptive. Finally, for the third class, the electrolyte tends to dissolve the coating about as rapidly as it is formed. This action produces electrolytic brightening or anodic polishing of the aluminum surface and at most leaves only a very thin film of oxide. The nonporous and nonadsorptive type of oxide film is represented by the coatings that are formed when solutions of boric acid are employed as the electrolyte. It is especially significant that these impervious films are formed in electrolytes that exert little or no solvent action on the coating. Where a boric acid electrolyte is used, the coating tends to form rapidly, with the result that the flow of current is soon reduced to substantially zero. This indicates that the growth of the coating has stopped. As a rule, the thickness of the coating is roughly proportional to the voltage employed for formation and the coatings of this type are exceedingly thin. In an electrolyte of this type, the coating has a high resistance when the aluminum is made anode; consequently, any current that may flow (leakage current) is very

Jan 1, 1944

By F. Keller, J. D. Edwards

The anodic treatment of aluminum presents problems of scientific as well as of commercial interest.l-3 Of particular interest is the fact that, during the anodic oxidation process, the oxide continues to form at the metal-oxide interface under any oxide previously formed. This has led to speculation as to the mechanism involved in the formation of the relatively thick oxide coatings that are used commercially for decorative or protective purposes. Furthermore, the ability of certain types of oxide coatings to adsorb dyes and other substances has stimulated research to determine the actual structure of these adsorptive coatings. It has been found that anodic oxide coatings on aluminum are composed essentially of aluminum oxide. They are formed by the action of oxygen ions penetrating to the metal surface during the electrolytic oxidation treatment. These coatings can be formed in a number of different electrolytes, as for example, those which contain sulphuric acid, chromic acid, oxalic acid, or boric acid. These are the commonest and most useful electrolytes employed commercially. Except for certain specific conditions of formation, the coatings in general have been found to be amorphous alumina, as far as can be determined by X-ray or electron-diffraction methods. Anodic oxidation processes can be arranged in three rather general classes if they are grouped in relation to the solvent action of the electrolyte on the coating.4 In the first class, the electrolyte has little or no solvent action on the coating that is formed. In general, coatings produced under such circumstances are nonporous and non-adsorptive. In the second class, the electrolyte exerts an appreciable solvent action on the coating. These coatings are porous and adsorptive. Finally, for the third class, the electrolyte tends to dissolve the coating about as rapidly as it is formed. This action produces electrolytic brightening or anodic polishing of the aluminum surface and at most leaves only a very thin film of oxide. The nonporous and nonadsorptive type of oxide film is represented by the coatings that are formed when solutions of boric acid are employed as the electrolyte. It is especially significant that these impervious films are formed in electrolytes that exert little or no solvent action on the coating. Where a boric acid electrolyte is used, the coating tends to form rapidly, with the result that the flow of current is soon reduced to substantially zero. This indicates that the growth of the coating has stopped. As a rule, the thickness of the coating is roughly proportional to the voltage employed for formation and the coatings of this type are exceedingly thin. In an electrolyte of this type, the coating has a high resistance when the aluminum is made anode; consequently, any current that may flow (leakage current) is very

Jan 1, 1944

By J. E. Burke, Y. G. Shiau

SEVERAL attempts have been made to account for the fact that grains in a fully recrystallized metal will coarsen on annealing Two fundamentally different hypotheses have been advanced; with several variations of each. One school considers that the cause of grain growth is the surface energy of the grain boundary The theory of Jeffries1 that grain size and grain size contrast control growth is an example The second school considers the primary cause to be a difference in the lattice energy on either side of the grain boundary The more perfect grains are considered to grow at the expense of their less perfect neighbors, with a decrease in free energy, and a consequent increase in the stability of the system. Burgers2 presents the case for the strain or lattice imperfection theory of grain growth quite completely The latter theory is attractive, since there is no doubt that differences in lattice energy or lattice perfection can cause grain boundary migration A recrystallization nucleus grows for this reason as was beautifully demonstrated by van Arkel and Ploos van Amstel3 Although it is generally stated that grain growth does not precede recrystallization, several workers4,5 have shown that small strains may induce a single crystal in an aggregate to grow, or at least may cause some&apos; grain boundary migration The origin and nature of the imperfections that are considered to be responsible for normal grain growth have never been clearly described, but it is generally agreed that they are a consequence of the difficulty of atomic reorientation in the solid state, and that they do not seriously differ from the type of imperfection that-can be introduced by mechanical deformation An object of the present work was to determine whether the introduction of mechanical deformation would cause grain growth in a specimen which would not otherwise show it under the conditions used It was also planned to determine the effect of such deformation the rate of growth in a specimen which would show - growth in the unstrained condition Recently Maddigan and Blank6 have indicated that slightly strained specimens of alpha brass can undergo considerable growth prior to recrystallization if annealed at low temperatures French7 has reported that at deformations less than 17 pct it is very difficult to detect the beginning of recrystallization in the same material. It was therefore planned to broaden this work to include a complete study of the microscopic behavior of alpha brass under conditions of temperature, time, grain size and deformation such that recrystallization would not occur or would occur to only a small extent EXPERIMENTAL PROCEDURE The brass was prepared by melting cathode copper and commercially pure zinc

Jan 1, 1947

By S. W. Poole, J. A. Rosa

THE object of this investigation was to determine the distribution of chemical elements within a large, killed alloy-steel ingot, by sulphur printing and quantitative chemical analysis. With regard to segregation in steel ingots, the factors of melting practice, pouring temperatures, mold design, etc., and the mechanics of solidification and its attendant functions, have been the subject of intensive study over a period of years by many investigators. Notable among these is the Sub-Committee of the No. 5 Committee of the British Iron and Steel Institute. For an exposition 0f the many problems awaiting the researcher on the heterogeneity of steel ingots, the methods of attacking these problems, together with some of the answers, the reader is referred to the nine reports and numerous papers of that committee and its membership. STEELMAKING DATA Melt.-The heat was made in a 70-ton direct arc-type basic electric furnace. Furnace charge consisted of nickel-chromium-molybdenum steel, most of it in the form of heavy mill scrap. All of the scrap was charged cold. The standard double-slag method was employed, the heat being finished under a strong carbide slag. Aluminum was used as the deoxidizing agent. Tapping temperature, as observed with an optical pyrometer, was 3000°F. Detail of Mold and Ingot Size.-Details of the ingot mold and the ingot itself are given in Fig. I. Teeming.-Teeming temperature of the subject ingot as observed with an optical pyrometer was 2830°F. The ingot was top-poured directly through a 1 ½ in. nozzle and required 7 min., 44 sec. to fill up to the hot top. An additional 2 min., 30 sec. were required to fill the hot top. The ingot was stripped hot and charged with the remainder of the heat into an annealing furnace. There it was given the standard annealing cycle used for these ingots. Subsequent heat-treatments are described elsewhere in this paper. SECTIONING AND PREPARATION FOR SULPHUR PRINTING Because of previous favorable experience in sectioning ingots up to 21 ½ in. square with an oxyacetylene torch, it was decided to use this method to section the subject ingot. The ingot was preheated to 900°F. for 12 hr. It was then placed on a steel bed in a horizontal position so that the longitudinal axis was level and parallel to the track of the motor-driven torch carrier. Two cuts were made, one 2 in. above the longitudinal axis and the other 2 in. below. The time required to make each cut was approximately 75 min. The cutting operation is shown in Figs. z and 3. The 4-in. thick slab was mmediately charged into a furnace standing at 1200°F.

Jan 1, 1944

By L. C. Brown, E. B. Hawbolt

The formation of grain boundary precipitates has been studied in Ag-5.64 wt pcl Al alloys at 688°C. Large-grain specinzerzs were used and the boundary misorientation measured by X-ray diffraction. At low-angle grain boundrrries Primary sideplates form. u)hile abore a 17-deg misorientation lenticular precipitates predominate. Growth of the lenticular precipitates was studied on individual grain boundaries using a statistical technique. The thickening and lengthening rates appeared to be independent of &apos;pain boundary misorientation, indicating that grain boundary diffusion was not significant in this system. The precipitates grew urith constant shape, with both the length and thickness increasing parabolically with time. The parabolic lengthening rates were unexpected since previous theory and experimerztal results had indicated linear growth. By approximating the shape of the precipitate to that of an oblate spheroid grouling with constant shape an equivalent diffusion coefficienl was calculated. The zlalue obtained was in good agreement with nleasurements obtained fron, diffusiorz couples. IF a single-phase alloy is heated or cooled to a temperature such that the phase becomes supersaturated, there is a tendency for a second phase to precipitate from it in order to remove the supersaturation. Precipitation takes place initially on grain boundaries due to preferred heterogeneous nucleation, but subsequently Widmans kitten plates may form in the grain interiors if the grain size and supersaturation are sufficient. The type of grain boundary precipitate formed depends on the nature of the boundary. Aaronson1 and clark2 have shown that grain boundary misorientation can be characterized by the simple parameter R, where and X, Y, and Z represent the minimum rotations about three orthogonal axes required to bring the two lattices forming the grain boundary into coincidence. The maximum value for R is 60 deg. In using this parameter the orientation of the grain boundary itself is, of course, neglected. However it was found in both Fe-si3 and A1-Ag2 that the precipitate shape depended only on the parameter R. Clark found that the vast majority of precipitates formed were allo-triomorphs— lens-shaped precipitates that grew along the grain boundaries. At low-angle boundaries, however, (R < 15 deg) Widmanstatten sideplates nucleated at the grain boundaries and grew into the adjacent grains. It has been reported that the rate of growth of grain boundary precipitates is controlled by diffusion within the supersaturated phase.&apos; The theories which have been developed for growth rates have assumed the diffusion coefficient constant over the composition range of the supersaturated phase. This is a fairly good approximation if the composition range involved is not large. Thickening rates have been calculated using the theory developed by Zener4 and by Frank5 for the growth of planar precipitates. A parabolic growth law

Jan 1, 1968

By W. J. Carlson, S. M. Parmerter, I. Iwasaki

This article discusses the effect of physical and chemical modifications of starches on the anionic and cationic flotation of silica from oxidized iron ores and magnetite-taconite concentrates. It also deals with the results of the interaction of starch, pH, and calcium ions on the flocculation, clarification, and filtration of iron ore slimes and magnetite-taconite tailings. Starches, particularly when an-ionically modified, were found to be effective depressants in anionic silica flotation. British gums and dextrins were beneficial for oxidized iron ores, but none of the starches or starch derivatives appeared to have any effect on magnetite-taconite concentrates. The flocculation and filtration of iron ore slimes were affected most strongly by the level of starch, to a lesser degree by the pH, and virtually not at all by the level of calcium chloride. The clarification of iron ore slimes was complexly dependent on these three factors. The flocculation of magnetite-taconite tailings depended mainly on the level of starch, whereas their clarification depended on the level of lime. As previously reported in the literature, selective flocculation and partial upgrading of a semitaconite could be readily attained with starch and calcium chloride. A previous article discussed some of the parameters that are important when various corn starches are applied to the soap flotation of activated silica from iron ores and to the flocculation of iron ore slimes.&apos; Methods of solubilizing the starches and the molecular size after mechanical and thermal treatments, as inferred from the viscosity measurements, were shown to influence the adsorption characteristics on iron ores, and the residual concentrations of both calcium ion and starch in the pulp liquor were in direct correlation with the flotation and flocculation behavior.2-4 The present article summarizes the results of more recent tests conducted to ascertain the role of starches and starch derivatives in various phases of iron ore beneficiation. The scope of this investigation has been extended to include not only anionic and cationic flotation, but also the flocculation and filtration of iron oxide slimes, the selective flocculation and partial upgrading of semitaconites, and the flocculation and clarification of magnetite-taconite tailings —all problems that are of vital importance to the iron ore industry of Minnesota. By combining a practical approach with adsorption studies and by using single-mineral systems5 in these research efforts, it is believed that the ultimate goal of developing a suitable modification of starch structure may be realized. The topics covered in this article are limited to the empirical aspects of the research program on the depressant activity of starches and products in the cationic and anionic flotation of silica and of their role in flocculation, water clarification and filtration. ANIONIC SILICA FLOTATION In the soap flotation of activated silica from iron

Jan 1, 1970

By E. P. Polushkin, Henry L. Shuldener

THIS paper describes the results of microscopic examination of a series of brass pipes removed from apartment and office buildings in New York City, adjacent localities on Long Island, and Philadelphia. They were selected as typical of approximately four hundred pipe specimens obtained over a period of five years during an investigation of corrosion in hot-water installations. A part of the investigation is reported in this paper and includes a brief history of the pipes, a description of their inside surface and microstructure, and a study of the effects of corrosion, with particular reference to the structural aspects of local and selective dezincification. Although the bibliography on the corrosion of brass pipes is quite extensive, it refers almost entirely to corrosion in sea water. The authors believe that their examination of this series of pipes, which had been subjected to the corrosive action of fresh water for various lengths of time, may throw some additional light on the problem of corrosion. PIPES EXAMINED The pipes were made by different manufacturers and their sizes range from ¾ in. to 4 in. nominal inside diameter, the majority being within I to 2 in. They can be divided into two groups according to chemical composition: (I) with a copper content of 60 to 62 per cent and (2) with a copper content of 65 to 68 per cent. The first group (pipes made of Muntz metal) comprises 22 pipes and the second (pipes made of high brass) comprises 18 pipes. The pipes had been in service in various locations in the hot-water systems of the buildings involved. Some were taken from horizontal lines in the basement, some from overhead distributors and some from vertical risers. The distance, in terms of feet of pipe, of the specimens from the hot-water generator was no less than 75 ft. and often 100 to 300 ft. In the majority of cases the water-heating equipment was provided with a regulator to limit the temperature of the hot water supply. The normal range of temperature in pipe systems of this kind is 100° to 160°F. WATER SUPPLIES The average chemical composition of the water supplies carried by the pipes is shown in Table I. In evaluating the corrosiveness of a natural water, four factors are considered of prime importance: namely, hardness, alkalinity, pH and silica content. The waters listed in Table I are characterized by relatively low hardness, low alkalinity, low pH and low silica content. The waters of lower pH and higher CO2 content are more corrosive. A characteristic of all of these waters is that they do not deposit a protective mineral coating as do waters with high bicarbonate of lime content, which would be reflected

Jan 1, 1944

By Carl J. McHargue

Rods of 99.99 + pct Al which had initial orientatzons of <001>, <118>, <115>, <111>, and random were swaged at room temperature. Changes in orientation as a function of deformation were studied on axis distribution charts. The <001> orientation appeared to be relatively stable due to the inhomogeneity of the deformation process. near the <100> zone were quickly reoriented towards <001>. Orientations on the <110> zone between <118> and <115> appeared to be stable to reductions of about 50 pct, then were reoriented toward <001>. At very high reductzotzs. movement away from the <111> orientation was observed. the requirement that a circular cross section be maintained. In addition to these mechanical factors, there are grain-boundary effects in poly crystalline materials which are not yet understood. Hartmann and Macherauch conclude, for example, that multiple slip occurs for all orientations in fine-grained aluminum and copper and that the choice of operative slip systems has no simple relationship to orientation.? Many investigators have attempted to avoid problems of interpretation caused by an initial texture by treating the starting material to obtain as ran- IT has been generally accepted that the deformation texture obtained at high reductions, e.g. 90 pct, will not be noticeably affected by a prior texture; whereas, that obtained at reductions of 40 to 50 pct may be significantly influenced by the specimen history.&apos; Some recent studies, however, have been interpreted as showing that an initial texture strongly influenced the deformation textures in rods at reductions greater than 90 pct. Freda and Cullity suggested that the <001> texture in a heavily cold-worked copper rod was due to a <001> texture in the original casting. McHargue, Jetter? and Ogle concluded that the <001> component in an aluminum rod extruded at liquid nitrogen temperature was remanent from a <001> texture in the cast extrusion billet.3 Most of the published work on the effect of initial orientation on deformation textures has been for cold-rolled or compressed single crystals,4-6 The primary interest in these studies was to examine various orientations with regard to their stability under flow? thus determining the possibility of such orientations being stable end orientations. There appears to be no published studies on the effect of initial orientation on fiber textures in polycrystalline specimens. A recent study, however, is concerned with the reorientation of individual grains in polycrystalline specimens pulled in tension.? Although the reorientation of single crystals loaded in simple tension is well known, the movements in the forming of wires and rods would be expected to be different due to the circular array of radial-compressive stresses exerted by the die walls or the rolls, and to

Jan 1, 1962