Search Documents

The first production on the Island of Trinidad was discovered 29 years ago; 13,275 acres were proved for oil and gas to the end of 1937, and 145,076,700 bbl. was produced from 2661 wells, or 10,928 bbl per acre. The production of oil in 1936 was 13,237,030 bbl. and in 1937 a new peak of 15,498,350 bbl. was reached. During November 1937, the daily average production was 43,350 bbl., or 35 bbl. per well, while the maximum gas production was 45 million cubic feet daily. Two hundred fifty wells were completed during 1937 and 15 abandoned. At the end of last year, 800 wells had been temporarily shut down, 1235 were producing oil and gas, and 2 were producing gas only. Six hundred seventy-nine dry wells had been drilled to the end of 1937. At the end of November 1937, the following oil-producing methods were in use: 395 wells flowing, 491 pumping, 97 on air-gas lift and 252 wells miscellaneous. There were no flooding operations. The oil is produced from the Miocene and Eocene and is of both asphalt and paraffin base. The gas produced averaged approximately 1050 B.t.u. per cu. ft. with 0.8 gal. of gasoline per 1000 cubic feet.

Jan 1, 1938

By W. C. Winegard, J. R. Carruthers, A. Plumtree, L. R. Morris

The unidirectional solidification of dendrites containing central twin planes was studied in A1-Ti alloys. Once nucleated, the twinned dendrites are a Twore ejficient form for solute redistribution and therefore grow in preference to the normal columnar dendvites. Comparison of these twinned dendrites to adjacent colunmar dendrites by means of decanting experinzents and electron-probe rnicvoarmlysis indicates that these special dendrites grow with less undercooling than normal dendrites. These findings are further supported by the effect of forced convection on the dendrite morphologies. COMMERCIAL semicontinuous cast ingots of most aluminum alloys frequently exhibit large grains which appear to be composed of hundreds of parallel, continuous, thin lamellae. This structure has been termed "basaltic",' "fiederkristall", or, commonly, "feathery grain". The lamellae are 'about 100 p thick, several inches long, and each lamella contains a central (111) coherent twin boundary. The feathery grain has been reported to have a (112) direction2 and a (110) direction4 in the twin plane parallel to the casting direction, in contrast with the usual columnar structure where a (100) direction predominates. Aust et uZ.~ proposed that the twin boundaries were growth twins nucleated by stacking faults on the octahedral planes. chalmers6 has suggested that feathery grain may grow by a re-entrant edge mechanism, as proposed by wagner7 for twinned dendritic growth in germanium. Cahn et ~1.~ have concluded that the occurrence of feathery grain is evidence of some form of lateral layer growth rather than the atomically continuous growth normally observed in metals. The postulates by Chalmers and Cahn would seem to be contradicted by the work of Nakao~"' who showed that feathery grain only occurs when growth rates are high and the aluminum contains some solute. Specifically, Nakao found that in order to obtain feathery grain, in small castings solidified unidirec-tionally upward, the rate of growth must be above 2.4 cm per min and a critical solute concentration must be present. Below this solute concentration the grain structure was totally columnar. The critical solute concentration was found to be approximately: 0.04 wt pct Ti, 2 wt pct Cu or Mg, and 8 wt pct Zn. As pointed out by Chalmers it is not obvious why a twin-plane re-entrant edge mechanism would occur in aluminum which is thought to have a diffuse solid-liquid interface. The present experiments were undertaken to determine the growth mechanisms in- volved and to study the solute segregation in more detail. EXPERIMENTAL PROCEDURES Alloys ranging in composition from 0.05 to 0.23 wt pct Ti* were prepared from 99.9 pct pure Ti and 99.993 pct pure Al. Two-hundred-gram samples of A1-Ti binary alloys were solidified unidirectionally and vertically upward from a water-cooled copper base, in a heated insulated mold. The 1-in.-diam, 6-in.-length mold was made of Marinite (manufactured by Johns-Manville Co.). The mold was attached to a 24-in. pivoted arm such that by dropping a weight the mold was rotated 180 deg, throwing the liquid metal from the solid. In this way, the solid-liquid interface was revealed by decanting. A sketch of the decanting mold is shown in Fig. 1. The alloy was poured into the mold at temperatures ranging from 680" to 750°C, partially solidified by water cooling from the base, and decanted after a measured time interval. Growth rates for each metal-pouring temperature were calculated from solidification-time vs length solidified curves. Temperature gradients in the melt were measured using four No. 34 gage thermocouples which protruded into the mold cavity. Grain orientations were determined by X-ray diffraction using Laue back-reflection techniques. Grain substructures were examined metallographically, using polarized light, by applying a thin epitaxial anodic film to polished sections after the method of Hone and pearson." Titanium micro segregation was measured by electron-probe microanalysis using a NORELCO AMR/~ with a mica crystal and proportional-flow counter. Several of the cast samples exhibited feathery and columnar dendrites growing in the same direction and

Jan 1, 1967

By B. Fagerberg, P. H. Fahlstrom

Crushing and grinding practice in Sweden follows closely the international pattern. Certain special circumstances, however, have had an influence on its development. Most mines are worked underground. These mines are either quite small or very large. Sulfide ores are commonly treated by custom milling and, apart from the cement industry, the rock species treated are hard and abrasive. Another important factor is the increasingly strict requirements placed on the mechanical condition of different products, especially lump ores and coarse iron-ore concentrates. Increasing requirements are being placed on the concentrate grade to suit the new steel processes. As a result, iron ore beneficiation has expanded considerably for the production of fine pelletizing concentrates. This applies especially to magnetite ores in the intermediate phosphorus range 0.1-1% P. In 1969, about 5.5 million tons of pellets will be manufactured. It should be pointed out, however, that fairly large quantities of coarse products are still being made at mills where the right conditions are available. Crushing and grinding is also of great importance in the production of rich concentrates at high recovery from sulfide ores. In fact, a large part of the development work on the concentration of sulfide ores has been devoted to the crushing and grinding processes. Boliden has played an important role in this connection.

Jan 10, 1969

By R. Stickler, A. Vinckier

An optical and electron microscope study was made on a commercial 302 stainless steel heat treated for massive carbide precipitation. Convincirg evidence was obtained that the grain boundary precipitate does not grow away from the grain boundary into the matrix, but grows as a network of large thin dendrites in between the grains. IN austenitic stainless steels the carbon in supersaturated solution precipitates when the steel is heated in the temperature range 450" to 1000°C. During such heat treatments the chromium-rich carbide occurs primarily at the grain boundaries and has adverse effects on the corrosion resistance and low-temperature ductility of the material. It has been shown that the morphology of the precipitated particles differs widely depending on the time and temperature of the heat treatment, the nature of the boundary, the misfit between the grains, and so forth.1"5 It was assumed by Mahla et al.,' Streicher,' and Mc Nutt' that the carbide particles which nucleate in the grain boundary grow in various geometric or dendritic forms away from the boundary into the matrix. However, Kinzel,' Hatwell et a, and Plateau et aL4 found that the particles nucleate in the grain boundary and grow as a network of thin dendrites in the grain boundary interface. We have made a comprehensive studyg of the precipitation occurring in a commercial 302 austenitic stainless steel heat treated for times ranging from 0.15 to 1500 hr at various temperatures from 480" to 1065"~. This study was made to elucidate the influence of heat treatments on both the mechanical and the corrosion properties of this steel. Part of this investigation which is pertinent to the morphology of the grain boundary carbides referred to above is separately reported here. We found that the particles which nucleated in the boundaries grew in the interface of these boundaries, thus supporting the viewpoints of Kinzel,' Hatwell et al.,3 and Plateau et al.4 Furthermore, when carbide particles nucleated in the matrix very close to the boundaries, they possessed a morphology distinctively different from the particles growing in the grain boundaries. MATERIAL A study of metallographic samples and of fracture surfaces of a 302 stainless steel is reported in this paper. The composition and heat treatments are listed in Table I. Polished and etched samples were examined und813r the optical microscope, and carbon extraction replicas of etched micrographic samples and various fracture surfaces3'8'9 were examined under the electron microscope. RESULTS AND DISCUSSION A representative optical micrograph of the 302 steel, condition A, is shown in Fig. l(a). Particles can be seen on the grain boundaries but no traces can be found of particles which grow from the grain boundaries into the matrix. A carbon extraction replica of this sample shows numerous large thin dendrites, Fig. l(b). The lateral dimension of such carbide particles vary up to 100 p, and their thickness estimated from the amoun! of electron penetration i:; between 500 and 1000A. Such large dendrites are extracted from almost all grain boundaries and, if they had grown into the grains, they would definitely be revealed by etching traces in the matrix, Fig. l(a). The reason why these large dendrites on the extraction replica appear to be grown into the grain is due to the mechanism of the extraction replica process. Thus, these dendrites are supported by the carbon replica film only at the edges originally along the grain boundary trace A-A, Fig. l(b), in the polished metal section and have subsequently fallen over onto the carbon replica film during handling. Although such dendrites generally fall only to one particular side of the grain boundary trace, one finds occasionally that parts of a dendrite have fallen to both sides, as shown in Fig. l(b). Further evidence for the growth of carbide in the grain boundary can be obtained from the appearance of fracture surfaces. A small impact specimen of the 302 steel, condition A, was broken at liquid nitrogen temperature. The fracture path follows the

Jan 1, 1962

By H. E. Cline, E. F. Koch, J. L. Walter

It has been postulated and, in a few instances shown, that some kind of dislocation structure will be present at semicoherent interfaces to accommodate small lattice mismatches. In the present study of the NiAl-Cr eutectic, regular arrays of interface dislocations are observed at the boundary between the chromium-rich rods and the NiAl-rich matrix. The networks were examined by transmission electron microscopy and selected area diffraction. The rods and the matrix have a crystallographic relationship in which all directions and planes of the two phases are parallel. The dislocation networks are cmposed of a<100> dislocations lying on the intersections of the cylinders with (100) planes. Dislocations forming hexagonal rather than square arrays are also observed at certain areas of the network. The morphology of the network is consistent with the interpretation of mismatch being accommodated by interface dislocations in the cylindrical geometry. The measured spacing between dislocations was used to calculate an apparent lattice mismatch between the phases (˜0.35 PCt)interface network energy (-140 ergs per sq cm), and network strengthening (-10,000 psi). It has been proposed by Frank and Van der Merwe1 that dislocations should be present at the boundary between two semicoherent crystallographically related phases. The role of the interface dislocations would be to reduce the internal stresses, caused by the mismatch in atomic spacing across the interface. Such dislocations have been observed at the interface between expitaxially grown films and Substrates.2-4 Interfacial dislocations have also been observed at precipitate-matrix interfaces.&apos;-&apos; Directionally solidified eutectics have been shown to have semicoherent phases1&apos; and would, therefore, be expected to have interfacial dislocations as found by Weatherly at a lamellar fault in A1-A12Cu.11 The NiAl-Cr eutectic appeared to be a promising system to examine because both phases are cubic, the lattice mismatch is small, and the phases are crys-tallographically related. Furthermore, the eutectic is easily thinned for transmission microscopy. Indeed, interfacial dislocations were observed and this report describes the nature of the dislocation networks in the boundary between the NiAl-rich ma-trix-phase and the fine chromium-rich rods.21 I) EXPERIMENTAL PROCEDURE Ingots, 3/4 in. in diam and 6 in. long were made by melting in vacuum and casting under argon using 99.9 pct pure material. The composition, in at. pct, was 33 pct Ni, 33 pct Al, and 34 pct Cr. The ingots were then placed in A1203 crucibles on a water-cooled base, melted by means of induction, and withdrawn from the hot zone at the rate of 1 in per hr under argon.* * T his material was first directionally solidified in this laboratory by E. R. Stover Slices were taken perpendicular to the growth direction of the directionally solidified ingot for metallography and for transmission electron microscopy. The electron transmission samples were thinned mechanically, then thinned electrolytically in A-2 electrolyte* *A-2 electrolyte: 62 ml perchloric acid, 700 ml ethanol, 100 ml butylcellosolve, 137 ml distilled H20. until a hole appeared in the foil. 11) EXPERIMENTAL RESULTS A) Optical Microscopy. The microstructure, viewed on a plane perpendicular to the growth direction, is shown in Fig. 1. The structure consists of cells or colonies of parallel chromium-rich rods in the NiAl matrix. The cells occur when there are impurities present12 or, in a ternary eutectic, if the composition is slightly off the eutectic composition. The axis of the chromium-rich rods is parallel to the growth direction except near the cell boundaries. Here the rods may assume angles to the growth direction; however, examination shows that the crystallographic relationship between the rod and the matrix remains the same. Fig. 1 includes cell boundaries where the rods formed at a large angle to the growth direction. The variation of rod position across the cells made it possible to Fig. 1-Structure on plane perpendicular to growth direction. Rods near cell walls are at large angle to growth direction. Magnification 315 times.

Jan 1, 1970

By J. E. Andersen, J. Halpern, C. S. Samis

In the presence of oxygen, galena is oxidized in an aqueous medium containing sodium hydroxide, in accordance with the following reaction: PbS + 2O2 + 3OH ? HPbO2 + SO4 = + H2O A novel method was devised for following this reaction which takes place in an autoclave under oxygen pressure, by measuring the concentration of HPbO2- in the solution with a cathode ray polarograph employing stationary platinum electrodes. Using this procedure a study was made of the kinetics of the reaction, in which the effect of a number of variables, including temperature, oxygen pressure, NaOH concentration, and agitation, on the rate, were determined. The results of this study are described and discussed, in terms of possible mechanisms for the reaction. IT is known that sulphide minerals can be oxidized in aqueous media in the presence of oxygen under pressure. Reactions of this type can be classified in two categories depending upon whether the products of oxidation are insoluble or soluble in the aqueous medium. An example of the first type of reaction is the oxidation of pyrite in alkaline solutions, giving rise to an insoluble iron oxide. The kinetics of this reaction have been investigated and its mechanism established.&apos; It has been applied in the oxidation of iron sulphides present in refractory gold ores to improve the subsequent recovery of gold by cyanida-tion.&apos; The second type of reaction finds application where it is desired to recover the metal by leaching during oxidation. In this case a medium is selected in which the oxidized mineral is soluble. For example, nickel, copper, and cobalt sulphide ores can be treated by oxidation in the presence of a solution of ammonia dissolving the nickel, copper, and cobalt as the metal ammine sulphate salts.:&apos; A similar treatment has also been reported to apply to zinc sulphide ores.&apos; It is known that lead sulphate is soluble in solutions of sodium hydroxide or ammonium acetate. It should therefore be possible to dissolve the lead from galena ores by aqueous oxidation with oxygen under pressure using either of these solutions. The applicability of the ammonium acetate treatment has been investigated and confirmed in a recent study.&apos; The present paper describes the results of a similar study in which the kinetics of the oxidation of galena in sodium hydroxide solutions have been investigated. The object of this investigation was pri- marily to obtain information of a fundamental nature relating to the kinetics and mechanism of this reaction. The use of pulps of comminuted ore in a study of this type is undesirable because of the difficulty in controlling and measuring the surface area. The measurements were therefore made using galena crystals of measured surface area and in this way absolute reaction rates were obtained. The reaction was found to proceed as follows: PbS + 2O2 + 3OH ? HPbO2 + SO4 + H2O [I] The products are sodium plumbite and sodium sulphate salts which dissolve in the aqueous solution. The reaction studies were carried out in an autoclave in which a desired pressure of oxygen was maintained. The reaction was followed by measuring the concentration of lead in the solution with a cathode ray polarograph. The results obtained in this investigation are presented and discussed in the present paper. Experimental Materials: The crystals of galena were obtained from Violamac Mines, Sandon, B. C. The following impurities were indicated by spectrographic analysis carried out by the Provincial Assay Office, Victoria, B. C.: Sn, 0.02 to 0.2 pct; Sb, 0.07 to 0.7; Zn, 0.01 to 0.1; Si, Fe, Mg, As, less than 0.05 pct; Ag, 126 oz per ton, the latter determined by standard fire-assaying procedure. After cutting a specimen measuring approximately 5x7x12 mm, the crystal surfaces were ground parallel to the 100 axes using No. 2 emery, washed with water, and the dimensions were measured with a micrometer. Oxygen gas was of commercial grade and supplied in cylinders by Canadian Liquid Air. Solutions were made up with chemicals of chemically pure grade and distilled water. Equipment: Autoclave: The autoclave used in these studies was constructed of stainless steel and

Jan 1, 1954

By P. S. Kotva

Dislocation substructures in superalloy matrices of varyzng co)npositions have been studied. In general, it has been found that the alloys can be classified into &apos;&apos;high", &apos;&apos;medium", and "low" stacking fault energy classes based on the type of dislocation substructure observed in the matrix and that the substructure can be correlated to the stacking fault energy. The effect of different types of dislocation substructure and dislocation reactions on the intragranulur precipitation of carbide phases has been studied. In a Ni-Cv-Mo-Fe matrix, precipitation of MC carbides in association with stacking faults has been observed. In most superalloys, solid-solution strengthening and precipitation hardening are the chief mechanisms employed to achieve strength. The latter contribution to strength is usually achieved by the precipitation of / in certain wrought alloys. Insufficient attention has been given to the problem of obtaining strength in su-peralloys by controlling precipitation of carbides on imperfections within the matrix. The present work was undertaken to investigate the dislocation substructure in various superalloy matrices, to study the effect of such substructure on subsequent precipitation of carbides in the matrix, and to investigate whether certain modes of precipitation of carbide phases found in austenitic stainless steels2"4&apos;6 would occur in nickel-base alloy matrices with dislocation substructures of the same type as those found in austenitic steels. 1) EXPERIMENTAL TECHNIQUES Five-pound heats of the various alloy compositions reported here were vacuum-cast. The ingots were given light deformation by rolling to break up the as-cast structure and then homogenized for 24 hr. HASTELLOY alloy X (nominal composition: Ni-2OCr-17Fe-8Mo-0.05C) was homogenized at 2150°F and In-cone1 625 (nominal composition: Ni-20Cr-5Fe-8Mo-3.5Cb-0.05C) was homogenized at 2280°F. Fabrication of 0.004-in. sheet was achieved by cold rolling with intermediate annealing treatments being carried out at the same temperature as those used for homogeniza-tion. Each solution anneal was followed by quenching. The aim of this procedure was to redissolve as much of the primary carbide phase as possible. Samples of the 0.004-in. sheet were cut and encapsulated in quartz capsules and then heat-treated in the tube furnaces. Thin foils were prepared using an ethanol-10 pct perchloric acid bath at 32°F and at a voltage of 22 v. A "window" technique was employed. Observations were made on a JEM-7 electron microscope operating at 100 kv. 2) EXPERIMENTAL RESULTS a) Types of Dislocation Substructure. Fig. 1 shows a schematic correlation between stacking fault energy, SFE, and the type of dislocation substructure observed in various matrices of nickel- and cobalt-base alloys. A precise quantitative determination of stacking fault energy is not implied in the figure but the correlation between stacking fault energy and the type of dislocation substructure obtained allows alloys to be divided into three classes in analogy with the classification employed by Swann and ~uttin~&apos; for binary alloys of copper. Class I alloys are associated with a "high" SFE and show a cellular substructure of dislocations as typified by the micrograph of a thin foil of pure nickel deformed 4 pct at room temperature in Fig. 2. With decreasing SFE the tendency toward cell formation is lessened and dislocations tend to be arranged in coplanar groupings. Examples of this class of alloys with "medium" SFE are provided by the mi-crostructure of solution-heat-treated, quenched, and deformed thin foils of HASTELLOY alloy X, "Waspaloy" (prior to any aging), and Inconel 625. Fig. 3 shows a thin-foil micrograph of an alloy of Inconel 625 composition, solution-heat-treated, quenched, and deformed 5 pct at room temperatures. No evidence of any cell structure can be obtained in materials of "medium" stacking fault energy, Fig. 3, even after severe deformation. The stacking fault energy of the alloy shown in Fig. 3 is, however, not low enough to make the dissociation of dislocations visually obvious. As stacking fault energy decreases further, with successive addition of solute in the matrix, there is an increased tendency toward dissociation of dislocations and cross slip becomes progressively more difficult. Eventually, when the stacking fault energy is "low" enough, complete dissociation of dislocations is seen to occur as shown in Figs.

Jan 1, 1969

By H. L. Hartman

The drop tester has proved an invaluable tool for the investigation of percussion drilling in the laboratory in "slow motion". It has allowed the process of rock penetration by impact to be studied a single blow at a time. In the present work, the relation of cratering to indexing has been determined under conditions simulating those in the bottom of the hole at atmospheric pressure. Indexed blows form craters which are influenced by others adjacent to them. Two unique effects are involved: (1) the provision of additional free faces in proximity to the point of impact and (2) the creation of subsurface damage by the previous blow(s). Both have a pronounced influence on the volume of rock removed per blow, which governs the rate of penetration in actual drilling. The emphasis in this study was placed on determining effects of index distance and impact energy on crater volume when blows were struck on a previorusly "drilled" or damaged surface, a situation most representative of down-hole conditions. The results indicated that (I) the optimum index distance on a damaged surface is greater than on a fresh, undamaged rock surface; (2) the volume of rock broken at optimum index distance is about the same for both surface conditions with die-shaped chisels but tends to be greater on a cratered surface with wedges; (3) the optimum index distance and maximum crater volume are proportional to the energy level; (4) at a given energy level, the volume of rock broken by dies generally exceeds that by wedges; and (5) maximum crater volume varies, approximately, inversely with width of die but is nearly independent of included angle of wedge. INTRODUCTION This is the third of a series l,2 of papers reporting on one phase of a continuing program of drilling research being conducted in the Rock Mechanics Laboratory at The Pennsylvania State U. The phase under consideration is crater geometry — blow energy relations in percussion drilling. While the previous papers have discussed mainly craters produced by single blows, indexed-blow studies are the subject of this paper. The basic mechanism of drilling under study here — that of penetration of a chisel-shaped bit subjected to impact — is the one employed in probably 90 per cent of all rock drilling in mining, percussion drilling. It also forms the fundamental action in nearly all oil well drilling with the so-called rotary (roller-bit) method. Here, the action is more complex, however, and may in actuality comprise rotary-percussion drilling. Certainly, the down-hole air and mud hammer drills, which superimpose percussion on rotation, belong in this latter category. In any event, impact blows constitute one of the principal mechanisms in the vast majority of drilling, mining or petroleum, and it is essential in drilling research to study percussion in all its basic aspects. Percussion drilling can be simulated in the laboratory by means of an impact drop tester. Striking one blow at a time with chisel-shaped bits, the drop tester permits study of most of the parameters in the drilling process except blow frequency and the interrelationship of certain variables. Single-blow craters, the simplest to produce, allow the determination of basic relationships, such as volume vs blow energy; while indexed craters most closely resemble the action in real drilling and provide data for the establishment of optimum operating criteria. Indexed-blow craters are those which are influenced by others in proximity. The simplest case to visualize, and the one studied in detail here, is that in which a given crater is formed adjacent and parallel to a previous crater, such that the second crater breaks into the first. A more complex situation usually exists downhole, where indexing is achieved by rotation of a radial-winged or rolling-cutter bit. But, admittedly, the phenomenon of indexing is more likely to be understood eventually if it is first studied in its simplest form, that related to parallel craters. Limited research has been conducted on indexed blows. The most complete study was that by Simon, 3,4 who proposed universal indexing curves to relate the important variables. His work, however, was conducted entirely with rows of craters formed on a

By W. Rostoker

Single isothermal sections were constructed for the titonium-rich corners of the systems Ti-Fe-O, Ti-Cr-O, and Ti-Ni-0 with a view to locating the shape and disposition of the ternary intermediate-phase fields for the compounds isomorphous with Fe3W3C. IN a previous note,&apos; it was reported that a group of ternary intermediate phases existed which occurred in the general composition range Ti,X,O-Ti&O where X was one of the following elements: copper, nickel, cobalt, iron, or manganese. In two instances, binary intermediate phases occurred (Ti²Cu and Ti²Ni) which appeared to be isomorphous. The X-ray diffraction patterns of the phases could be indexed on a cubic lattice whose cell edge was of the order of 11 kX. Karlsson2 stated that the line extinctions and line intensities indicated that these phases were isomorphous with Fe³W³C and therefore belonged to the space group Oh. This author also noted that no unique phase of this type occurred at the composition Ti,Cr,O. This latter statement was accepted as true at the time the previous technical note was written.&apos; However, work continued along these lines and that reported here has shown that a phase isomorphous with Fe³W³C does exist in the vicinity of the composition Ti³Cr³O but not at or near Ti4 Cr²O. The lattice parameter of this phase was found to be 13.01 kX. Metallographic examination of both as-cast and annealed specimens of these supposed ternary oxide phases disclosed structures which were far from single phase in many instances. It was considered a point of some interest to locate more positively the composition coordinates of the single-phase fields. To this end, single isothermal sections for the systems Ti-Fe-O (1000°C), Ti-Cr-0 (1000°C), and Ti-Ni-0 (900"C) were constructed. Phase relationships were studied by both X-ray diffraction and metallotrra~hic methods. Allovs were prepared as 10 g buttons by melting in a noncon-sumable electrode, water-cooled copper crucible arc-melting furnace using a helium atmosphere. Oxygen was introduced quantitatively by the use of weighed amounts of TiO² or TiO. Iodide titanium and the purest available alloying metals were used. All results are discussed in terms of the nominal composition of the melts. Previous experience with making oxygen-rich alloys had shown that oxygen losses were not significant if a homogeneous melt was produced. Weight-loss measurements were used to check loss in metallics during melting. Anneals were conducted in evacuated Vycor bulbs, and annealing times ranged from 24 hr at 1000 °C to 48 hr at 900°C. To achieve equilibrium in certain sluggish alloys, seven-day anneals were used. Debye-Scherrer powder patterns were taken in a 14 cm diam camera using filtered CuK radiation (K² = 1.541232 kX; K., = 1.53739 kX). Specimens were prepared by crushing and screening previously annealed buttons. In general, the X-ray diffraction results were used to identify the major phases, while the metallographic examinations were more useful in indicating the number of phases present. By the use of the combined results and general fundamental rules governing ternary equilibrium, it was possible to construct isothermal sections in good detail. In some instances where auxiliary lattice-parameter data were available, it was possible to lay down tie lines and to locate more positively corners of three-phase fields. Isothermal Section of the System Ti-Fe-O at 1000°C The binary systems Ti-O³ and Ti-Fe4 have been published. Binary phases, TiO, TiFe, and TiFe2, are likely to be encountered in the titanium-rich corner of the system. The structures are NaCl (Bl), CsCl (B2), and MgZn, (C14) types, respectively. Although preliminary X-ray diffraction studies indicated the presence of a ternary phase in the composition range Ti,Fe,O-TiJ?e,O, metallographic examination of two specimens at these compositions revealed the presence of other phases. Thirty-eight alloys were used to delineate the phase boundaries of the isothermal section illustrated in Fig. 1. The five almost single-phase ter-

Jan 1, 1956

By L. S. Cates

THE war is now behind us. We in the mining industry feel a just pride in the part that our industry and our men and our products played in defeating the enemy on the fighting fronts around the world. In five years of mobilization and actual combat, our mines and oil wells produced over 3 billion tons of coal, a billion tons of petroleum, 500 million tons of iron ore, 21/4 million tons of lead, 31/2 million tons of zinc, 5 million tons of copper, 14 million tons of bauxite, 17 million tons of sulphur, 68 million tons of salt, and 3 million tons of potash. It was an unparalleled performance. But what of today? Why the present low production and high costs? Among the black clouds in the mining sky none are so black as that presented by the labor situation. We know it is the result of the legislation and the interpretation of that legislation in the past ten or fifteen years. Since the passage of the Norris-LaGuardia Act in 1932, we have had nothing but a succession of laws, regulations, and decisions that have intensified the strength of the unions and made the operators of the mines and the sources of their financing prartirally impotent

Jan 1, 1946

By R. W. Gould, B. G. LeFevre, A. G. Guy

The resistivity anomaly known as the K state was studied in Ni-Mo alloys containing 10.5 and 14.0 at. pct Mo. Both these alloys exhibit a large K effect which depends on the mechanical and thermal treatment. On the basis of X-ray diffuse scattering studies which were correlated with resistivity measurements, it appears that the K state in dilute Ni-Mo alloys can be associated with changes in the degree of short-range order within the a phase. An interesting phenomenon that has received much attention in recent years is the K state. The K state is marked by anomalous changes in some of the physical properties of certain alloys without the occurrence of observable microscopic structural changes. One of the early pieces of work in this area was by Thomas&apos; who studied alloys of Ni-Cr, Ni-Cu, Ni-Cu-Zn, Fe-A1, Fe-Si, and Ni-A1. Upon annealing specimens which had been previously cold-worked or quenched from an elevated temperature he found an anomalous increase in resistivity over a certain temperature range. He also found that specimens which had been appropriately annealed to develop the K state showed a decrease in resistivity upon subsequent cold working. These effects are opposite to those found in normal alloys. Although the resistivity anomaly has been rather arbitrarily taken as the "definition" of the K state, there are several other interesting effects which accompany the resistivity increase. In Ni-Cr alloys,2, 3 for example, it was found that the hardness increases with increasing resistivity. It was also found that specimens which have been treated to develop the K state can be cold-worked for as much as an 80 pct reduction of area without an increase in the hardness. In Fe-A1 and Fe-Si alloys4 the K state is accompanied by an increase in flow stress and by a lattice contraction. In Ni-A1 alloys,5 specimens which have been treated to develop the K state also show an increase in elastic modulus. In Ag-Pd alloys6 the increased resistivity observed on annealing a cold-worked specimen is accompanied by an increase in the thermoelectric power and an increase in the Hall coefficient. The explanations of the K state phenomena are varied and depend upon the particular alloy in question. Several theories have been advanced to explain the increased conductivity with cold work on the basis of changes in the electronic configuration of the alloy as a result of local lattice distortions.7"9 Most investigators, however, believe that some type of local order in the solid solution, either short-range order (SRO) or clustering, is responsible for this effect. Theories concerning the relationship between ordering and the K state have for the most part been speculative, since there is little direct X-ray evidence that can be correlated with the above property changes. Much of the previous work on the K state was done in the Ni-Cr system where the small difference in the X-ray atomic scattering factors of the components nickel and chromium makes it very difficult to use X-ray diffuse-scattering measurements to determine the role of local order. In the Ni-A1 system, however, Starke et al.10 succeeded in detecting a connection between local order and the K state. It was found that a small but measurable K effect correlated with increasing SRO in the nickel-rich a phase. The manner in which local order might increase the resistivity of K state alloys is not completely clear. Since most of the known K state alloys contain at least one transition element, significance has frequently been attached to the presence of an unfilled d shell. It has been suggested that during the formation of the K state the number of conduction electrons decreases as a result of the transfer of s electrons to the d shell where they are more tightly bound.1&apos;11&apos;12 Koster and Rocholl13 have proposed that SRO can cause an increase in resistivity for alloy systems in which the number and mobility of charge carriers are reduced when the percent solute is increased. According to this hypothesis, the local environment of a given solvent atom changes in the same manner with increasing percent solute as it does with an increasing degree of SRO; hence the change in physical properties should tend in the same direction. In this hypothesis, SRO is considered only in a statistical sense, and the increased resistivity of the K state is attributed to a change in the mean distribution of electrons and holes in the s and d states as a result of SRO. From the work of Chen and Nicholson on Ag-Pd alloys,6 it appears that the K state can occur in systems for which the d shell is completely filled. These investigators explained the increased resistivity by picturing the SRO as small domains of some form of long-range order (LRO). According to ~ibson,&apos;~ the number of effective electrons can be reduced by the creation of a new Brillouin zone boundary near the Fermi surface of an alloy as a result of the changing crystallographic symmetry that accompanies the formation of a superlattice. This idea may be expressed in terms of the superzone concept.15 In the present work the role of local order in the formation of the K state in Ni-Mo alloys was investigated. The principal tools used in this study were X-ray diffuse scattering and electrical resistivity measurements; however, these data were supplemented by electron microscopic and field-ion microscopic data. The purpose of the work was to determine whether or not the K state in Ni-Mo alloys can indeed be attributed to the formation of SRO as has been proposed by previous investigators.

Jan 1, 1969

By W. T. Nightingale

The three gas-producing "pools" discussed in this paper are in Sweet-water County, southwest Wyoming, and Moffat, County, northwest Colorado. Hiawatha, North Baxter Basin and South Baxter Basin gas fields became economically important in 1929 when a 330-mile gas line connected them with Salt Lake City, Ogden and towns en route. This development immediately focussed attention on the gas-producing fields and the efforts of the producing company to develop them in an orderly, economical manner. Several outstanding interests were acquired and working agreements made with others. Thus the interference of natural drainage areas was avoided, the pernicious practice of drilling direct

Jan 1, 1930

By W. M. Johns

The word "Flatland" should read "Flathead" in the title of the paper by Willis M. Johns on page 184 of the June 1962 issue. The correct title is "Belt Series in Lincoln and Southwest Flathead Counties, Montana." In the same paper, reference 12 on page 191, the publication is Bulletin 12, Montana Bureau of Mines and Geology, rather than Bulletin 17.

Jan 1, 1962

By D. H. Baldwin, R. E. Reed-Hill

WITH the polarized-light microscope, the basal-plane trace may be located on hcp crystal surfaces to an accuracy of approximately 1 deg. This determination can also be made on very small crystalline areas, approaching a micron in width. Measured basal-plane trace distributions on selected specimen surfaces can yield1,2 valuable texture information. However, the polarized-light microscope is probably best suited to orienting

Jan 1, 1965

By E. Miller, J. M. Eldridge, K. L. Komarek

The thermodynamic properties of liquid Mg-Ge alloys have been determined between 1000°and 1500°K by an isopiestic method. Germanium specimens, heated in a temperature gradient and contained in covered graphite crucibles of special geometry, were equilibrated with magrtesium vapor in closed titanium tubes. The crucible design allowed free access of magnesium vapor to the samples during the equilibration to form alloys of magnesium and germanium, but prevented magnesium losses from the crucibles on quenching the titaniuin tubes to terminate the experimental runs, thus preserving the equilibrium alloy compositions. The activities and partial molar enthalpies of magnesium and the integral thermodynamic properties of the system were calculated from the experimental data. THE Mg-Ge phase diagram&apos; shows one congruent melting compound, Mg2Ge, of essentially stoichio-metric composition, two eutectics, and very limited terminal solid solubilities. Very little information is available on the thermodynamic properties of the Mg-Ge system. The free energy of formation of Mg,Ge was recently deter-mined2 by a Knudsen cell technique in the temperature range 610° to 760°C. The standard enthalpy of formation of Mg,Ge was measured calorimetrically by Bever and coworkers.3 The present study was undertaken as part of a general investigation of the thermodynamic properties of the homologous series of Mg-Group IVB systems, i.e., Mg-Pb,4 Mg-Sn,5 Mg-Ge, and Mg-Si. An isopiestic technique was used which was developed by the authors5 for investigating the thermodynamic properties of liquid Mg-Sn alloys. Specimens of the nonvolatile component, contained in covered graphite crucibles, are heated in a temperature gradient in an evacuated and sealed titanium reaction tube, and equilibrated with magnesium vapor of known pressure. The method employs crucibles of special geometry which preserve the high-temperature equilibrium composition of liquid alloys having a highly volatile component such as magnesium on termination of the experimental runs by quenching the crucibles to room temperature. EXPERIMENTAL PROCEDURE First reduction germanium of 99.999+ pct purity (Eagle-Pitcher Co., Cincinnati, Ohio) and 99.99+ pct magnesium metal (Dominion Magnesium Ltd., Toronto, Canada) were used. The graphite crucibles were machined from high-density (1.92 g per cu cm) graphite rods (Basic Carbon Corp., Sanborn, N.Y.) which had a maximum ash content of less than 0.04 pct. The non-reactivity of graphite with germanium at the temperatures used in this study had been previously established by Scace and Sleck.6 The experimental procedure has been previously described in detail.5 The selection of a particular crucible geometry for a run was determined by a combination of imposed experimental conditions, the principle being that more tightly covered crucibles were required to preserve alloy compositions during quenching when higher magnesium pressures and higher specimen temperatures were used. Depending upon the composition range of the equilibrated alloys the source of the magnesium vapor was either pure magnesium or a two-phase mixture of Mg2Ge + Ge-rich liquid of known magnesium pressure. The experimental runs can be divided into the following three groups on the basis of crucible geometry and magnesium source material. Crucibles with Small Holes and Pure Magnesium Reservoirs. The crucible dimensions were identical to those of the Mg-Sn investigation5 except that the hole diameters were reduced to 0.010 in. because of the higher temperatures and higher magnesium pressures involved in the Mg-Ge system. During an equilibration run, magnesium vapor diffused from the reservoir to each specimen through the small holes, one drilled through the crucible lid and two others drilled through graphite baffles positioned vertically inside the crucible between the lid hole and the specimen. Since the magnesium pressure was high, i.e., in the range 117 to 277 Torr, during the equilibration time of approximately 24 hr, equilibration was not impeded by these holes. A specimen composition at equilibrium was fixed by the relative temperatures of the specimen and the reservoir, and by the thermodynamic properties of the system. Upon brine quenching the titanium reaction tube to end a run the vapor pressure of magnesium above the liquid alloys decreased exponentially with decreasing temperature, and the small cross-sectional areas of the holes (4.9 x 10"* sq cm) drastically reduced magnesium losses from the crucibles. Because of its low vapor pressure, germanium losses from crucibles during a run were at most 0.2 mg for pure germanium and correspondingly less for the alloys. This crucible geometry satisfactorily retained the equilibrium alloy compositions on quenching for magnesium-rich (from 3 to 33 at. pct Ge) alloys provided their temperatures were below the melting

Jan 1, 1967

By A. Gatti, R. L. Fullman

A very fine dispersion of aluminum oxide is produced by internal oxidation of solid-solution alloy of 0.14 pet A1 in Ag. The particle size of the aluminum oxide is approximntely 50 to 100A in radius. The yield strength of the alloy is increased markedly by internal oxidation. A further increase in strength is produced by cold working the internally oxidized alloy. Recrystallization is retarded by the finely dispessed aluminum oxide particles, so that the strength increase resulting from cold work is retained on annealing at temperatures 14 to about 700°C. MANY workers&apos;-3 in the past have studied various aspects of the internal oxidation of aluminum-silver alloys. This paper is an extension of these studies with emphasis placed on the effect of time and temperature of annealing on the strength of these alloys after oxidation and subsequent cold working. Two general conditions are necessary to internally oxidize an alloy. First, oxygen must diffuse through the base material more rapidly than does the addition; otherwise oxidation will take place as a surface layer. Secondly, the affinity of oxygen for the addition must be greater than for the base material. After internal oxidation of certain alloys takes place, a marked increase in hardness accompanied by higher yield stress and improved creep properties is noted, presumably as a result of the highly dispersed oxide within the base material. Meijering and Druyvesteyn1 also noted that the internally oxidized portion of a partly oxidized alloy failed to recrys-tallize under annealing conditions that led to coinplete recrystallization of the unoxidized part. EXPERIMENTAL-METHODS AND PROCEDURES Few alloys can be made to contain a second phase that is extremely stable at high temperatures. Silver plus aluminum in solid solution was chosen for these internal oxidation studies because of the high rate of oxygen diffusion through silver and the very stable nature of aluminum oxide. Two alloys were vacuum cast. The nominal compositions were: Alloy A—1 pct Al, balance Ag; Alloy B—0.1 pct Al, balance Ag. Chemical analysis, which does not distinguish between aluminum and aluminum oxide, showed the conlposition to be: Alloy A—1.6 pct Al, and Alloy B—0.14 pct Al. The ingots were machined for surface cleaning, swaged and drawn to 0.020-in. diam wire. A sample 20 ft long of the 0.020-in. dianl wire of each composition was annealed 24 hr at 800°C in pure dry hydrogen. Each wire was then cut into two equal pieces. Photomicrographs of the 0.14 pct A1 alloy are shown in Fig. 1, the annealed 0.020-in. wire at the left and the oxidized wire to the right. The oxidation treatment for the first set of data was 1000 hr at 800°C in air. After this treatment the 1 pct A1 proved to be brittle. It is assumed that high alunlinum oxide concentration at the grain boundaries was responsible. The 0.14 pct Al wire remained ductile and all further data were derived using this alloy. One-half of this wire, about 5 ft, plus 5 ft of as-homogenized wire, was then drawn cold to 0.005 in. diam. All tensile tests were conducted with an Instron Engineering Corp. tensile-testing machine, Model TT-B. Unless otherwise indicated, the tests were made at room temperature with a strain rate of 0.1 per min. All metallographic samples were etched with an aqueous solution of 2 pct each of CrO3 and H2SO4 . EXPERIMENTAL RESULTS AND DISCUSSION PARTICLE SIZE DETERMINATION A study was made of the particle size of the aluminum oxide produced in the samples of Ag + 0.14 pct Al, oxidized 1000 hr at 800°C. A cross section of the as-oxidized wire was mounted in bakelite, polished, and etched with an aqueous solution of 2 pct each of CrO3 and H2SO4. The specimen was then thoroughly cleaned by stripping successive coatings made by applying 10 pct nitrocellulose in amyl acetate. The final replica of the cross section was made by applying 2 pct nitrocellulose in amyl acetate. The replica was stripped, transferred to a copper screen, shadow cast with chromium at 10 deg and photographs taken using a Phillips Metallix electron microscope at an accelerating potential of 100 kv. A photograph of an etched sample of the as-oxidized material is shown in Fig. 2. We believe the pits in the photograph are places were A12O3 inclusions were sitting in the matrix. By inspection, it appears that the volume fraction ob-

Jan 1, 1960

By H. C. Chao, L. H. Van Vlack

Small MnS inclusions with known crystallographic orientations were placed inside powder compacts of low-carbon steel. After the metal was axially campressed with negligible end friction, the deformstions for the metal and the inclusions were compared. The MnS inclusions deformed more when the [100] direction was aligned with the compression axis than when the [111] direction was parallel to this axis. The deformations of the inclusions in the two principal radial directions were equal for each of the above orientations. Inclusions with [110] compression alignments did not deform with radial symmetry. The relative deformation of the inclusion and metal was closely dependent upon the relatiue hardness of the two phases. The relative deformation of the two phases was not sensitive to the rate of deformation. RECENT studies by the authors1.&apos; suggested that the plastic deformation of MnS in steel would probably be highly sensitive to the orientation of the inclusions and to the temperature of the metal. This paper reports an investigation of these factors upon MnS behavior within steel. Manganese sulfide (MnS) possesses an NaCl-type structure and typically has extensive (l10) {110} slip as a separate (noninclusion) crystal.&apos; A secondary slip system, ( l 10) { l l l}, has also been observed where the major slip system is restricted. In general, MnS inclusions must be rated as a highly deformable second phase.3 The amount of sulfide deformation varies, however, with several composition and processing factors. Some of these have been only partially assigned. For example, it is known that minor amounts (<0.01 pct) of silicon within free-machining steels will increase the amount of MnS deformation,4 but the mechanism of the added deformation can only be surmised at the present. Manganese sulfide and steel have sufficiently comparable deformation characteristics so that slip which is started in steel may be continued through the sulfide inclusions and back into the steel if the crystal orientations are favorable.5 A more detailed discussion of previous work on the plastic deformation of NaC1-type crystals and on the plastic deformation of inclusions within a metal is given in Chao&apos;s work.6 EXPERIMENTAL PROCEDURE The manganese sulfide which was used in this study was prepared by previously described methods.&apos; Single crystals of MnS, both as cleavage cubes and as spheres, were oriented within steel powder compacts so that the desired crystal directions were parallel to the direction of axial compression. A four-stage hydrostatic compaction procedure was used and involved the following steps. In the first stage part of the powder was placed in a metal die 1 in. in diameter with a thick (1 in. OD, 5/8 in. ID) rubber liner which had one end plugged. The steel powder was hand-rammed, making it as dense as possible before placing a carefully sized MnS crystal (either as a sphere or as a cube) near the center. The crystal was oriented with the chosen direction vertical; viz., [001], [011], or [111], with the aid of a X10 microscope. A pair of tungsten wire threads 0.020 in. in diameter was inserted along the side of this (&apos;core compact" to locate the desired plane after the compression tests. After the crystal was positioned in the center of the die, more powder was added and carefully rammed by hand. The die was then capped with a rubber plug of the same hardness and thickness as that of the liner. The whole assembly as shown in Fig. 1 was compacted by a ram load of 54,000 lb (about 70,000 psi). In the second stage a smaller, 3/4-in, rubber-lined die was used to give a stress of approximately 120,000 psi. The above process was repeated with the initial compact serving as a core for a larger compact. The final product after sintering was a cylinder 1 cm long and 1 cm in diameter, having a density of 7.54 g per cu cm. This was close to the theoretical density since the metal contained a non-metallic phase. There was no evidence of MnS deformation during the hydrostatic compaction or subsequent sintering. Elevated-temperature hardness data were obtained by procedures previously described.2 Compression tests for inclusion deformation utilized the cylinders which were described above. The critical problem in these tests was the lubri-

Jan 1, 1965

By M. Shelef, A. W. Fletcher

The effect of alkali sulfates in promoting the sul-fation of nickel and copper in a bulk sulfide flota -tion concentrate by fluidized bed roasting has been studied in the laboratory, and it was shown that the various alkali sulfates promote sulfation to approximately the same extent. The sulfation of a mixture of synthetically prepared iron and nickel oxide and of nickel ferrite has also been studied. Nickel sulfation was promoted by high ratios of Fe:Ni and by the presence of sodium sulfate. THE work described in this paper was a continuation of earlier studies into the role of alkali sulfates in promoting the sulfation roasting of nickel sulfides1,2 in an endeavor to determine how the system was affected by the presence of compounds of iron and copper. The earlier work1 showed that, in the sulfation of NiO at 680°C, the reaction was limited by the formation of an impermeable film of nickel sulfate on the oxide surface. The relative effect of the various alkali sulfates in promoting nickel sulfation varied in the order: Li > Na >Cs > Rb > K A study of alkali sulfate/ nickel sulfate interactions at high temperatures showed that the promoting action was due to the fact that the nickel sulfate product layer sintered and agglomerated only when the more active additives were present. This resulted in the formation of discontinuities in the nickel sulfate layer so that diffusion of the sulfating gases to the NiO surface was no longer impeded and the reaction could proceed to completion. A similar explanation was used for the observation that sodium and lithium sulfates promote the oxidation of NiS to NiO at temperatures below 750°C since small amounts of nickel sulfate were formed during oxidation.2 It was of interest to study the effect of alkali sulfates on the sulfate roasting of a sulfide flotation concentrate which is typical of material treated commercially. In order to control temperature it is essential to roast sulfides in a fluidized bed and this technique was therefore used, although the batchwise operation of a small-scale laboratory reactor does not reproduce all conditions which prevail in full-scale continuous plant. The results obtained are therefore only comparative, and cannot be used for predicting the optimum conditions for metal extraction. The sulfation of synthetically prepared mixed oxides of nickel + copper and nickel + iron and of nickel ferrite was also studied to evaluate the relative effects of alkali sulfates with more complex systems. SULFATION ROASTING OF A SULFIDE FLOTATION CONCENTRATE The bulk sulfide flotation concentrate used in this work contained 7.92 pct Ni, 1.74 pct Cu, 35.66 pct Fe, and 31.28 pct S. The sulfide minerals present in order of abundance were pyrrhotite FeS, pyrite FeS2, pentlandite (FeNi)S, and chalcopyrite CuFeS2. Two samples described as coarse and fine were used. The coarse sample, which was a flotation concentrate (58 pct plus 300 mesh), was ground to 100 pct minus 350 mesh to produce the fine sample. Before roasting, the sample of sulfide concentrate was agglomerated by wetting witli a solution of the alkali sulfate (or water), thoroughly mixing, and drying at 110°C. This gave a cake which was gently crushed and screened, the -18 +100 mesh fraction being used for fluidized bed roasting. A similar-size fraction had been used by the authors in pilot plant work with a 4-in.-diam fluidized bed reactor.&apos; In this work it was found that the molar ratio of additive to the total iron + nickel + copper content of the sulfide sample should be adjusted to a value of approximately 0.06, as this was the optimum amount necessary for nickel sulfation. Experimental. The fluidized bed reactor consisted of a quartz tube approximately 60 cm long and 30 mm in diameter resting in a vertical tube furnace. The sulfide bed (30 g) was supported on a bed of -4 +12 mesh quartz particles 3 cm high, which rested on a sintered quartz disc welded to the tube. The temperature of the furnace was controlled with a variable transformer to give a final bed temperature of 680°C. The bed was fluidized with air or mixtures of air + 10 pct v/v SO2, at a total apparent gas velocity of 60 to 65 cm per sec at 680°C. The SO2 was introduced into the fluidizing air stream only when the oxidation of the sulfides was completed. At the end of the roasting period the calcine was leached with boiling water and the

Jan 1, 1964

By H. R. Ogden, E. S. Bartlett, A. G. Imgram

Unmodified disilicide coatirigs were applied to sheet-tensile specimens ofCb-Dg3 and Mo-TZM veJractovy- metal alloys. Coating thickness, degree of coating-substrate interdiffusion, and specimen geonzetry (notched and plain were included in the variables studied. Tensile tests were made to determine the ductile-lo-brittle transition temperature. The disilicide coating modestly increased the transition temperatlre of TZM, but had no effect on 043. Neither material condition (recrystallized or stress-velieved) nor specimen geometry (notched or unnotched) significantly altered the effects of coatings on the transilion temperatures of. the alloys. Cracks in the brittle coatings did not propagate into the substrate, and fracture modes appeared to be the same for both un-coated and coated specimens. MOST potential structural applications for refractory metals and alloys involve exposures to oxidizing environments at elevated temperatures. The general lack of oxidation resistance of these metals will require protective coatings to allow fulfillment of their potential. Currently preferred coatings for the oxidation protection of refractory metals are brittle intermetallic aluminides or silicides. These are typically formed on the surface of the refractory-metal substrate by a diffusion reaction between the substrate and a gaseous or liquid medium that is rich in aluminum or silicon. Because of the brittleness of these coatings, they will sustain no plastic deformation at low temperatures. They are frequently cracked by cooling from the coating temperature because of the thermal-expansion mismatch with the substrate alloy. Even if they survive cooling intact, they crack rather than sustain deformation under load at low temperatures. Thus, when a coated refractory metal is strained beyond the elastic limit of the coating at low temperatures, the mechanical environment of the substrate would include both static and dynamic cracks. These might be expected to influence the flow and fracture behavior of the substrate. This could be manifested in an altered fracture mode and/or an increase in the normal ductile-to-brittle transition temperature of the refractory-metal substrate. This paper presents the results of a research program that was conducted to determine the influence of the presence of a brittle surface coating on the low-strain-rate tensile behavior of typical refractory metals at low temperatures. EXPERIMENTAL PROCEDURES Material Preparation. Thirty-mil-thick sheets of molybdenum TZM alloy (Mo-0.5Ti-O.1Zr) and colum-bium D43 alloy (Cb-IOW-1Zr-O.1C) were obtained commercially. These alloys were selected as substrate materials representing two classes of materials important in current refractory-metal technology. The TZM was in the stress-relieved condition, and exhibited a heavily fibered grain structure. The D43 had been processed by the duPont "optimum" fabrication schedule,&apos; and exhibited slightly elongated grains typical of this process. Tensile specimens of two geometries were prepared from these materials: 1) plain specimens with 0.2-in.-wide 1.0-in.-long gage sections; 2) specimens similar to above, but with a 0.06-in.-diam hole drilled in the center of the gage section, providing a stress concentration factor, Kt, of 2.5. The "notch" geometry was selected to represent a typical condition of a rivet hole or other geometric discontinuities as might be encountered in various applications. Machined specimens were degreased, with a final rinse in acetone, prior to the application of coatings. Specimens of each substrate and configuration were pack-siliconizedin a particulate mixture of 80 pct A1203, 17 pct Si, and 3 pct NaF. Specimens were embedded in this mix (contained in graphite retorts) and coated in an electrically heated argon-atmosphere furnace under time-temperature conditions to effect nominal 1- and 3-mil-thick silicide coatings: Coating Thickness, mils Thermal Treatment 0.6 to 1.4 24 hr at 982°C 2.4 to 3.2 48 hr at 1093°C Coating kinetics were similar for both the TZM and D43 substrates. These treatments had little or no visible effect on the substrate microstructure as determined by optical metallography. The coatings on TZM were essentially single-phase unmodified disilicides, while those on D43 showed substantial evidence of modification by proportionate reaction with the respective substrate elements or phases, as shown in Fig. 1. It was recognized that these coatings might not be particularly desirable regarding protective capability. However, it was desired to circumvent possible inter -ferring chemical interaction with the substrate by pack additives such as chromium, titanium, boron, aluminum, and other elements that typify the better protective coatings for these materials.&apos; Thus, the results presented apply specifically to the simple silicide coatings investigated. They may not be rep-

Jan 1, 1967

By G. H. F. Gardner

The velocity and attenuation of elastic waves in sandstones were measured as a function of both pressure and fluid saturation. A large change occurs in these quantities if water is added and the rock is not compressed, but the change is small if the rock is subjected to a large overburden pressure. Measurements were made by vibrating cylindrical samples in both the extensional and torsional modes at frequencies up to 30,000 cycles/sec. Formulas were derived which enable the attenuation of dilatational waves in dry rocks to be deduced from the data. Similar experimental methods were used to investigate the properties of unconsolidated sands. Velocities were found to vary with the 1/4 power of the overburden pressure and attenuations to decrease with the 1/6 power. The effects of grain size, amplitude and fluid saturation were studied. Formulas by which the effects produced by a jacket around the sample may be calculated were derived. The practical application of these results to formation valuation is discussed. INTRODUCTION The attenuation of elastic waves in the earth has been of interest to the seismologist and geophysicist for many years, but only recently to the petroleum engineer. Engineering interest has been brought about by the success of velocity logging devices, for it is possible by modification of these instruments to measure the attenuation of sound waves in addition to their velocity and, hence, deduce the mobility of formation fluids as well as the porosities of the rocks which contain them. The main problem is to decide whether field measurements can be made with sufficient accuracy to be of practical use. This problem can only be solved after we know the magnitude of the attenuations which are typical of the earth at various depths. The logarithmic decrement of a fluid-saturated rock is the sum of a "sloshing" decrement and a "jostling" decrement, the former caused by the mobility of the fluid contained within the rock and the latter by the granular framework of the rock. Sloshing decrements can be calculated&apos; using Biot&apos;s theory, but the jostling losses are less well understood. The present paper reports an experimental investigation of jostling losses in consolidated and uncon- solidated sands, particularly with respect to the effect of overburden pressure and fluid saturation. Born&apos; showed that the decrement of a sandstone may increase dramatically when only a few per cent by weight of distilled water is added, and that the additional loss is proportional to the frequency of vibration. His measurements were made with no compressive stress on the framework of the rock. M. Gondouin3 investigated similar phenomena for fluid-saturated plasters but also did not compress the samples. In the present paper it is shown that compression of the framework reduces this effect, so that at depth the jostling decrement of a sandstone may be expected to be almost independent of fluid saturation and frequency. Decrements for many sedimentary rocks have been given by Volarovich,4 but all for the state of zero overburden pressure. Anomalously low velocities have been logged in shallow unconsolidated gas sands. Results of the present investigation confirm that these velocities are not caused by correspondingly high attenuations, because the jostling decrement in a packing of sand grains is small and much less than in a consolidated sandstone at the same depth. Velocities in sands have been measured by Tsareva5 and by Hardin6 as a function of pressure, but the corresponding decrements do not appear to have been measured previously. The widely used "resonant bar method" of measuring velocities and decrements was employed. Comments on variations of this technique have recently been published by McSkimmin.7 The main novelty of the present technique was the application of pressure to the samples. It was found possible to do this by placing the apparatus inside a pressure vessel, provided the conditions leading to large additional losses were avoided. These conditions are discussed below. EXPERIMENTAL TECHNIQUE Cylindrical samples were caused to vibrate in both the extensional and torsional mode of vibration and the amplitude of vibration was measured as a function of frequency in the neighborhood of a resonant frequency. The resonant frequency, fr, is related to the corresponding elastic modulus by the formulas where E and N are Young&apos;s modulus and the modulus of rigidity, p is the density of the sample, and A the wavelength of the vibration.

Jan 1, 1965