Search Documents

By Pierre R. Hines

The first progress in American ore dressing practice was made in the mills of the Mother Lode in Calif., the Comstock Lode in Nev., and Gilpin County in Colo., during the years 1861 to 1870, when the ancient wooden stamp battery, with square wooden stems, was converted into the 'California' stamp made of wrought and cast iron, with round stems which rotated. Eli Whitney Blake invented the jaw crusher in 1858 for stone crushing, and it was soon used for crushing ore. F. W. Gates' gyratory crusher followed twenty years later. S. R. Krom, Thomas A. Edison, and others improved the Cornish rolls by increasing their size and spring pressures; the Symons Brothers made horizontal and vertical disc crushers; W. Ball and E. T. Leavitt designed powerful steam stamps for Lake Superior native copper ores; and jigs were mechanized. William B. Frue, a mill superintendent in the Lake Superior copper district, invented the vanner in 1874. Arthur F. Wilfley built his riffled concentrating table in 1895, just after Dr. Robert H. Richards commenced his Ore Dressing. The Wilfley table so changed concentrator flow sheets that Dr. Richards was compelled to revise his text, and its publication was delayed until 1903. The value of sizing or classifying before concentration was recognized. Dr. Richards had persuaded the Anaconda Copper Mining Co. to install round tables with special surfaces to catch the 'extremely fine free mineral.'l Gravity concentration had achieved almost every refinement for recovering or separating minerals by the difference in their specific gravities. However, one serious problem remained unsolved, i.e., how to retrieve the enormous loss of the extremely fine mineral in the slime portion of the ore. Slime, then, as now, was not a precise term due to the variation in the mineral composition of the ores and the different requirements in crushing, grinding, sizing, and classifying. At that time, slime was considered to be fine sand and colloidal material passing 100 mesh.2 Most sulfide ore minerals are more friable than their associated gangue minerals, so that crushing and grinding increased the proportion of the extremely fine ore minerals in the slime. Sparkling specks of galena, chalcopyrite, argentite, or ruby silvers, according to the ore, floating away on the tailing stream from vanners and slime tables, were familiar sights in the old gravity concentrators. Gravity concentration practice was aimed at recovering the ore minerals at the coarsest possible size because the recovery was higher and unnecessary

Jan 1, 1962

By J. M. Dahl, R. J. Warrick, O. K. Riegger, H. Van Vlack

A liquid which is rich in oxygen (and silicon) develops at steel rolling temperatures in resulfurized and plain-carbon steels. This liquid fluxes solid manganese sulfide. The composition of the liquid and the resulting microstructures vary with the manganese/silicon/oxygen ratios in the steel. The observations and conclusions zuhich are presented are used 1) to suggest a mechanism for MnS deformation in resulfurized steels, and 2) to rationulize hot-shortness anomalies between plain-carbon and resulfurized steels. 1 HIS is a summary of the dependence of sulfide inclusion microstructures upon steel composition, and an interpretation of the behavior of sulfide inclusions at steel-rolling temperatures. Sulfide inclusions are known to have several metallurgical effects upon steel. Their effects upon hot-shortness are best appreciated. Although hot-shortness is well known, it is questionable whether its mechanism is fully understood because there are several anomalies in our interpretation. For example, why should not high sulfur contents produce extensive hot-shortness in free-machining steels ? A second metallurgical consequence of sulfide inclusions appears because sulfide inclusions improve machinability. Furthermore, globular inclu- sions are to be desired over elongated inclusions. To date, we know that lower silicon contents (< 0.010 pct) favor the globular sulfides, but we do not know why this interrelationship between silicon content and inclusion shape exists. Finally, the evidence is strong that the surface quality of a hot-rolled steel is particularly sensitive to the sulfur content. SUMMARY OF PREVIOUS WORK The role of sulfur in hot-shortness was first suggested during the past century. It is uncertain who was the first to conclude that sulfur was less deleterious in the presence of manganese, and that manganese altered the sulfide phase from a liquid FeS to a solid MnS at steel-rolling temperatures. However, Urban and chipman&apos; emphasized that liquid FeS may accumulate as an interdendritic film during solidification. More recently, Keh and Van lack&apos; showed that the intergranular liquid does not completely surround the metal grains at all rolling temperatures. Rather, a small finite dihedral angle exists when geometric equilibration is attained at

Jan 1, 1962

By A. J. Jacobs, G. Katz

MANY of the studies of intermetallic compounds containing uranium were performed during the early 1940&apos;s under the aegis of the Manhattan Project. Subsequently, much of this work was declassified and published after 1949. In some instances this early work, completed with relatively impure materials, represents the only source of X-ray diffraction powder data available in the literature. In the case of the intermetallic compound U,Fe some discrepancies in the powder pattern exist in the literature. Since this compound has been prepared in this laboratory, it is believed that the publication of the indexed powder pattern would help clarify the conflict in the literature. In studies of the U-Fe system, Gordon and Kauf-mannl and Grogan and Clews2 independently reported the intermetallic compound U,Fe in 1950. The crystal structure was described by Baenziger, Rundle, Snow, and Wilson3 in 1950. It is isostructural with U,Mn, U,Ni, and U,Co and crystallizes in a body-centered tetragonal lattice. The lattice constants determined by Baenziger et al. are: giving an X-ray density = 17.7 g cm-3 for 4 mol per unit cell. The compound used in this study was prepared by melting a stoichiometric mixture of the constituent metals in an argon-arc furnace using a nonconsum-mable tungsten electrode. Before the argon of 99.98 pct purity was introduced into the furnace, it was passed through CaC1, to remove water vapor and afterwards through a stainless steel tube containing calcium turnings heated at 600°C for the removal of nitrogen and oxygen. The purity of the uranium used was better than 99.9 pct and that of the iron was 99.97 pct. Before and during melting a zirconium getter was used to further purify the argon atmos-

Jan 1, 1962

By A. L. Mular

lnput energy-size modulus relation at small reduc-tion ratios is expressed by Et = (M, -Mt) k;. In some cases 13 is close to Schuhmann&apos;s distribution modulus a in value. Experimental results in conjunc-tion with the equation demonstrate the fact that energy input which produced fracture is not expended on unbroken starting material inside the mill at any time. Recently, schuhmann1 derived the Charles equation2 using the postulate that complex com-minution operations can be considered as a summa- tion of many comminution events. The fragments resulting from each event are assumed to follow the Gaudin-Schuhmamn distribution. In his derivation, Schuhmann implies that the size distribution of the total mass of a material is determined by the fraction of that mass actually subjected to comminution. Consider a feed to contain a volume, Vo, of uni- formly sized homogeneous material. After t seconds of grinding, let the volume of broken material be Vo - Vt where Vt is the volume of starting material not yet broken. The size distribution of the broken material is given by: where V is the cumulative volume less than size X, and k, is the size modulus of the broken material at time t. The distribution for the total volume at this

Jan 1, 1962

By J. A. Cahill, A. D. Kirshenbaum

Using an alumina or zirconia crucible with an alumina sinker or a molybdenum sinker coated with zirconium dioxide, the density of liquid iron was determined by the immersed-sinker method over the temperature range of 1800" to 2500°K. The density, with respect to temperature, is ex-Dressed by the equation Dg/cm = 8.523 - 8.358 X 10 T&apos;K The molar Volumes and thermal coefficients of expansion were calculated. Iron, upon me1ting, was found to expand 3.5 pct. A basic knowledge of the physical properties of materials at high temperatures is becoming increasingly important. A check of the literature shows, that in spite of the importance of iron, very few measurements have been made of its physical properties in the liquid state. Density measurements have been made by Benedicks and his collaborators1g using the method of balanced columns, by Desch and smith4 using the immersed sinker method with an alumina sinker, by Lucas using the maximum bubble method5 and by Stott and endall&apos; who used an alumina pyknometer. In the method of balanced columns, the difference in level of molten iron in two arms of a U-tube, together with the corresponding difference of pressure had to be measured. The formation of gas bubbles in one or both arms was a great source of error. These values are very erratic. They vary from 6.83 to 7.45 g per cm3 at the melting point (1805"~) and from 6.45 to 7.15 g per cm3 at 1890°K. Stott and Rendall determined the density at 1837"K, with a reproducibility of *0.2 pct. They used an alumina pyknometer fired to 1973°K. The vessel was filled in a vacuum furnace by immersion in the liquid metal. When thermal equilibrium was attained, the pyknometer was withdrawn, cooled, the ingot removed and then weighed. The chief disadvantage of the method was the difficulty of inserting the pyknometer without cracking it. The authors have been able to determine the density of liquid iron from its melting point up to 2500°K, by using the immersed-sinker method, with A1203 or ZrOz crucibles and A1203 or molybdenum sinkers coated with Zr02, Fig. 1. EXPERIMENTAL Apparatus. In these studies the source of heat was the carbon tube resistance furnace with an argon atmosphere described previously.7 Experimental runs were made using either Ala3 or ZrOz crucibles. The sinkers used were 1) pure A1a3 and 2) molybdenum coated with ZrOz. The crucible, 2 1/8 in. in diam and 3 in. high, was centered in the furnace on an Ala3 of Zr02 pedestal. The sinker, 1/2 in. in diam and 1 1/2 in. long, together with a counter weight, was suspended from an analytical balance into the melt by a molybdenum wire. Procedure. The procedure, as described previously,&apos; consisted in measuring the weight loss of the sinker in the liquid iron while determining simultaneously the liquid iron temperature by means

Jan 1, 1962

By R. J. Wasilewski

Axial expansion has been determined by X-ray diffraction up to 600° to 760°C in a titanium and four high-oxygen alloys. Expansion data cannot be fitted to the usual quadratic expression and anomalies observed are believed indicative of the changes in the bonding configuration of the valence electrons. Furthermore, there is significant disagreement between data obtained on poly crystalline and single crystal powder specimens. The major disagreement occurs within the temperature range (-470°C) where both mechanical and electrical properties also show markedly anomalous behavior. X. HIS work forms part of an investigation of physical properties of pure titanium and its osolid solutiono alloys with oxygen and nitrogen. In view of the anomalies observed in both the electrical resistivity&apos; and the susceptibility behavior it was decided accurately to determine the thermal expansion behavior of the pure and alloyed a titanium. PREVIOUS WORK The axial expansion coefficients reported for pure titanium are listed below. As can be seen, there is a marked discrepancy between the axial expansion and the experimentally determined coefficients on poly crystal line material. Thus, if we take the most recently reported axial expansivities3,4 we obtain perature interval of 25o to 700°C. The experimental value reported for polycrystalline metal is, however, of the order of 9.7 x 10o6 per OC. EXPERIMENTAL I) Pure Titanium. High purity titanium powder of -325 mesh was used throughout most of this work. The only significant impurities present were the interstitials, oxygen and nitrogen, which analyzed respectively 650 and 80 ppm. The purity of the ma-

Jan 1, 1962

By C. H. Li, R. J. Stokes, T. L. Johnston

A portion of the Ni3Cr-Ni3Al phase dzagram has been investigated, including the precipitation of 1 (Ni3Al) as well as the existence of ordered Y (Ni matrix), Extensive metallographic studies by electron microscopy have been carried out and X-ray diffraction diagrams have been taken at both elevated and ambient temperatures, No long-range ordering of the phase was found above 893°C (1639°F) in the compositional range investigated. The high rate of formation of the ordered ?1 phase upon quenching has been confirmed, a phenomenon which up to the present Lime has retarded the understanding of this phase diagram, Specimens with controlled amounts of ?1 exhibited up to a six-fold improvement in yield and creep strength compared with single-phase Ni-Cv-A1 alloys. MOST of the important high nickel heat-resistant alloys are related to the nickel-chromium-aluminum system. One of the important functions of the aluminum, often accompanied by titanium, is to produce a precipitate of the very fine ?1 phase (Ni3A1, X) where X may be Ti, Cr, or other elements. A number of investigators1-" have demonstrate the presence of y&apos; in these alloys but most of their materials contained large amounts of other elements resulting in appreciable amounts of con- fusing phases such as carbides. Further clouding of the precise role of y&apos; has been the suspected existence of an ordering reaction in the y matrix itself, ro-3,12-17 It appeared from these investigations that aluminum in Ni-Cr alloys would raise the ordering temperature of the matrix from 540°C at NisCr to 1300°C at Ni,Al. In support of this possibility, the matrix phase in the parallel Ni-Fe-A1 system is ordered to very high temperatures.1 OBJECTIVES OF THIS RESEARCH From this survey of the literature it appeared desirable to conduct an investigation of the simple Ni-Cr-A1 system using the alloys of the highest available purity to avoid the complication of foreign phases and thereby isolate the structures in the Ni-Cr-A1 system. Procedures were developed to study ? - ?o and ? - ?1 equilibria. Preliminary mechanical tests at elevated temperatures were also conducted.

Jan 1, 1962

By F. R. Brotzen, J. Taranto

SEVERAL investigators have computed stacking-fault concentrations from X-ray diffraction data.&apos;-&apos; The method generally employed relates the line shift to the stacking-fault probability. In this investigation platinum filings of 99.99 pct purity screened to -325 mesh were studied after having been subjected to various annealing treatments. The lines were measured on a General Electric XRD-5 spectrogoniometer using CuK, radiation. The centroid of the broad reflections was determined by the method proposed by pike.&apos; The stacking-fault probability was calculated by the formula given by Warren and warekois,3 with the assumption that all stacking faults were on the (111). Various high-angle reflections were used, but most data collected refer to the shift in the (400) reflections. When the filed platinum powder was annealed at 1200°C for 20 min the stacking fault concentration was too small to be detected. The stacking-fault probability in freshly filed specimens, as determined by the line shift relative to the annealed specimen, was about 0.016, Fig. 1. If the faults would be created only by extended dislocations, the dislocation density in the filed specimen would be about 3X1012 cm-2. The average stacking-fault width of about 21 which was used in this computation, is that given by Thornton and Hirsch.7 The mechanism by which stacking faults are annihilated during annealing is not yet fully understood. The isothermal results obtained do not seem to support the simple hypothesis of a first-order decay. On the other hand, the analysis by Kuhlmann, Masing, and Raffelsieper8 for the loss of dislocations during recovery agrees much better with the experimental data of this investigation. This analysis yields an activation energy of 29 ± 8 kcal per mol for the disappearance of stacking faults in cold-worked platinum during annealing. Even if one takes into account the lack of accuracy inherent in this X-ray method, the activation energy found is substantially less than that of self-diffusion in platinum, i.e., 61.6 kcal per mol.9 The results therefore suggest that processes other than dislocation climb, which involves the activation energy of self-diffusion, are responsible for the loss of stacking faults in platinum during annealing. The broad reflection lines became sharper early in the recovery process, Fig. 1. The sharpening occurred well before the stage during which stacking faults disappear. This lends support to Nowick&apos;s10

Jan 1, 1962

By E. P. Abrahamson II

The effect of transition element binary solid-solution additions upon the recrystallization temperature of vanadium has been investigated. Cr, Fe, Co, Ni, Mo, Ru, Rh, Os, and IY lower the recrystallization temperature, while Ti, Mn, Zr, Cb, Pd, Hf, Ta, W, Re, and Pt raise it. The majority of elements have their greatest effect in less than 0.15 at. pet. Both the rate of change of recrystallization temperature with atomic percent solute and the limit of initial linearity are found to Correlate with the free atom grozdnd state outer electron configuration of the sollte element. THE work of Abrahamson and Grant1 and Abraham-son and Blakeney2 has shown that the solute&apos;s elec- tron configuration appears to be a prime determinant of both brittle-to-ductile transition and recrystallization temperature in dilute binary alloys. It has also been shown by Abrahamson3 that the limit of linearity, i.e., the limit of initial linear change of recrystallization temperature with atomic percent solute, is also a function of the electron configuration of the solute in iron base alloys. Because of the systematic nature of the solute electron configuration correlation, it is to be expected that some systematic variation might be observed upon changing the solvent. Thus, this study of recrystallization in vanadium base alloys is the first of a series aimed at defining the role played by the electron configuration of solute in determining the recrystallization characteristics of dilute transitional alloys. PROCEDURE All alloys were made using 99.8 pct V containing 0.011 C, 0.024 N, 0.08 0, 0.006 H, 0.035 Ta, and

Jan 1, 1962

By H. R. Gardner

The heat treatmmt of plutonium was studied using the Jominy end-quenching technique commonly used for determining the hardenability of steel. Plutonium specimens were end-guenched from temperatures in each of the ß, y, d, d&apos;) and E phases. One series of specimens with a low-iron content, 165 pprn Fe, and another gvoup with a high-iron content, 678 pprn Fe, were used in order to study the effect of a Pu-Pu,Fe eutectic network on the hardness and micro-structure. Hardness traverses indicated no significant variations in hardness with either cooling rate or quench temperature. Metallographic studies indicated major effects on microstructure. Grain size was found to vary markedly with quenching temperature and cooling rate. It was determined that the Pu-PueFe eutectic network could be modified extensively by heat treatment, including spheroi -dization in the y phase and 6 phase below 413°C. An unidentified spheroidal inclusion was observed to go into solution in the delta and higher temperature phases. 1 HE element plutonium is unique among metals in that it has six allotropic forms in the solid state.&apos; These have been designated&apos; as the a, ß, y, d, d&apos;, and phases. The respective phase transformations occur at approximate temperatures of 122", 210°, 319°, 450°, and 480°C with a melting point at 640°C. With this number of phase transformations it becomes pertinent to consider the effect of heat treatment and cooling rate in the various phases on the microstructure and hardness of plutonium. To determine; the effect of a wide range of cooling rates, the Jominy end-quenching technique was applied to cylindrical plutonium specimens. In addition, since the presence of iron in amounts greater than 500 pprn is common in plutonium and results in a network of the Pu-Pu6Fe eutectic, it was decided to study heat treatment effects on two bomb reduced plutonium buttons with different iron contents. A low iron button containing 165 ppm Fe and a high iron button containing 678 ppm Fe were selected for this comparison. EXPERIMENTAL PROCEDURE Experimental Material. The cylindrical bars for Jominy quenching were cast from button stock in vacuo in MgO coated graphite molds. Metal pouring temperature was approximately 950°C and the molds were preheated to 300°C. The castings were machined to 0.5 in. diam. by 2.5 in. long cylinders. Chemical analysis and density data for the two groups of Jominy specimens containing different iron contents are presented in Table I. Except for iron, heats 19-12-1 and 20-2-1 are comparable within the limits of analytical accuracy. Representative specimens from the low-iron and high-iron bars were taken for metallographic examination. The low iron specimen was found to have extensive microcracking, Fig. 1. In addition, numerous unidentified spheroidal inclusions were present, Fig. 17. The average grain size of the low-iron plutonium is 0.068 mm, Fig. 4. In the high-iron plutonium, a Pu-Pu6Fe eutectic network is prominent, Fig. 7. The average size of the network is 0.100 mm. Unidentified spheroidal inclusions were also common in the high-iron plutonium. The average grain size of the high-iron plutonium is 0.036 mm. Experimental Technique. A Jominy end-quenching fixture was fabricated for glove box use. A 2.5 in. water height was used with an orifice of 0.250 in. ID. The orifice to specimen distance was maintained at 0.5 in. Annealing temperatures of 160°, 265°, 400°, 465°, and 535°c were chosen for the study of the effect of quenching from ß, y, d, d&apos;, and e phases on microstructure and hardness. During quenching, cooling curves were obtained from the Jominy specimens at distances from the quenched end of 1/16, 1/8, 3/8, 3/4, 1-1/4, and 2 in. Cooling rate calculations were made from the cooling curves for temperature intervals of 100° to 110° 160" to 170°, 330" to 340°, 420° to 430°, and 490° to 500°c. These temperature intervals were chosen

Jan 1, 1962

By W. M. Albrecht, W. D. Klopp, R. I. Jaffee, B. G. Koehl

Kinetic studies were made of the reactions of tantalum with oxygen, nitrogen, and air at 400o to 1500°C. The tantalum-oxygen reaction is linear from 500° to 1250°C. The tantalum-nitrogen reaction follows a cubic rate law at 400° to 700°C and a parabolic rate law at 800" to 1475°C. The reaction behavior in air is initially parabolic followed by a transition to linear behavior. In the search for high-temperature materials, considerable interest is being shown in the refractory metal, tantalum. It is the third highest melting metal with a melting point of 2996°C. Also, tantalum has excellent ductility, making it one of the most workable refractory metals. In considering high-temperature applications of tantalum, the oxidation kinetics of the metal must be known. Such information also serves as a basis for the development of corrosion resistant tantalum-base alloys. Therefore, this study was made to investigate the reaction of tantalum with air, nitrogen, and oxygen. LITERATURE Several oxides of tantalum have been reported. The pentoxide, Taz05, is the only oxide of tantalum whose identity has been established. A high-temperature modification, aTa2Os, has been reported by several investigators.1-4 A low-temperature phase, ßTa2O5, undergoes an allotropic transformation at 1320o to 1350oC. 5-8 Four other oxides of tantalum have been reported. The oxides TaO2, TaO, and Ta4O have been reported by schonberg.9 A suboxide Ta2O, was observed by Wasilewski 6. However, the presence of oxides lower than Ta2O5 is questioned by Lagergren and Magneli.7 In oxidation studies, vermilyeal0 and Peterson, et al.,12 reported one possible phase intermediate between Ta and Ta2O5. Only Ta2O5 was formed in the tantalum air reaction, as reported by Michae1.l3 Several studies have been made on the kinetics of the tantalum-oxygen reaction. vermilyeal4 investigated the range 50° to 300°C and found that the rate of growth of a thin adherent oxide film could be described by the Cabrera-Mott theory. Gulbransen and Andrew15,18 studied the reaction kinetics of tantalum in oxygen pressure of 1/10 atm at 250° to 450°C. At all temperatures the reaction followed the parabolic rate law for periods up to two hours. The oxidation behavior in the range 500" to 1000°C was found to be linear at oxygen pressures of 0.2 to 600 psi according to Peterson. et al.l1 At very low pressures (1 x 10-3 to 2 X lo-&apos; mm of Hg) Gebhardt and seghezzi17 reported linear oxidation at 800° to 1500°C. The reaction of tantalum with air is similar to the reaction with oxygen. Studies have been made by Waber, et a1.,12 and Michae1.l3 Two nitrides of tantalum, TaN and Ta2N are known. Their structures have been determined by Brauer and Zapp 18,19 The tantalum-nitrogen reaction kinetics have been investigated by Gulbransen and Andrews. 15, 16 The reaction follows the parabolic rate law at 500° to 850°C at a nitrogen pressure of 1/10 ,atm. At the same temperature, the tantalum-nitrogen reaction is much slower than the tantalum-oxygen reaction. EXPERIMENTAL TECHNIQUES Material— The material used in this study was high-purity, electron-beam-melted tantalum obtained from the Temescal Metallurgical Corp. The hardness of the as received ingot was 76 Vhn. The analysis of the material is given in Table I. Methods—Cylindrical specimens of tantalum approximately 0.9 cm in diam and 0.5 cm in length

Jan 1, 1962

By P. Greenfield, C. C. Smith, A. M. Taylor

J. E. Harris (Berkeley Nucclear Laboratories, England)—Greenfield et al.11 attribute abrupt changes in slope of their log o/log i curves for heat-treated Mg/0.5 pet Zr alloy (zA) to &apos;atmosphere&apos; locking. It is proposed here that a more reasonable explanation of the apparent strengthening at low rates of strain can be based on precipitation either during the preanneal or during the creep tests. All the tests were carried out above 0.5 Tm where solute atmospheres are likely to be largely evaporated2 and can migrate sufficiently rapidly so as not to impose any &apos;drag&apos; on the moving dislocations. McLean3 has derived an expression for determining the temperature Tc above which, due to the high-migration rate of the atmospheres, Cottrell or Suzuki locking can play no part in determining creep strength. This expression, which holds for an applied shear stress of not greater than 5 X 107 dynes per sq cm is: Tc/Tm= 7/6.8 - log10? where i = secondary creep rate The values for T, corresponding to the maximum and minimum reported creep rates at each temperature have been calculated from the data of Greenfield et al. These are given in Table VII. All the test temperatures were above T,, the margin being greater for the higher temperatures and for the lower strain rates where the breaks in the log s/log ? curves occurred. Dorn and his collaborators14, 17 have studied systematically the effect of solute hardening on the creep properties of an A1/3.2 at. pet Mg alloy. In the temperature range where strain aging occurred in tensile tests, abnormally high-activation energies for secondary creep were obtained but at temperatures above 0.43 Tm, solute alloying did not have any effect on the creep parameters. Moreover, there have been no reports of any strain aging phenomenon during elevated temperature tensile tests with ZA material.18 Instead of the observed strengthening being due to atmosphere locking, it is now proposed that precipitates play an important role in enhancing the creep strength of the material. There are two possibilities—precipitation of zirconium hydride during the high-temperature preanneal and/or precipitation of the hydride or a-zirconium during creep. On the basis of the former the results can be interpreted in terms of a critical stress being necessary to force the dislocations through or over preexisting precipitates. From the latter, if the strengthening is due to pre- cipitation during the test then hardening should be associated with a critical strain rate. At low rates of strain, time is available during the tests for precipitation to occur either directly onto dislocations (thus pinning them) or generally throughout the matrix (which would impede dislocation movements). Examination of the data of Greenfield et al. suggests that both mechanisms may be operative since they observed precipitation during creep and also found that their alloys exhibited high-creep strength in the early stages of the low-stress tests, i.e., before creep-induced precipitation had time to occur. It is not easy to understand why they considered that precipitation of zirconium hydride is unlikely to occur at 600°C while it can take place in tests in air at as low a temperature as 200°C. Precipitation of the hydride during the preanneal cannot be ruled out merely on the basis of metallographic examination. Hydride precipitates in ZA type alloys are very small and can only be accurately resolved in the electron microscope.9 For example, in this laboratory20 hydride platelets with major dimensions <(1/10) µ have been observed by electron transmission through thin film specimens of hy-drogenated ZA material. Complex interactions between dislocations and such particles are illustrated in Fig. 12. Additional evidence for precipitation during pre-annealing is provided by the data presented in Greenfield&apos;s Fig. 1 and Table IT. These show that the creep strength at 200o and 400°C increases with the time of preanneal at 600°C. Such increases cannot be explained on the basis of increases in grain size alone for further improvements in strength were observed when the material was annealed for longer times than that required to stabilize the grains. Although the main discussion is confined to ZA material, similar arguments can be used against the strain aging hypothesis proposed to explain the binary Mg/Mn alloy data. In this case no precipitation is possible during the preanneal, but precipitation-hardening during creep can occur.

Jan 1, 1962

By L. Adler

Some estimate of the geologic pressures existine at the site of a proposed underground opening is essential for its economic design and construction. Regardless of the size of such an opening, drill hole, or mine stope, these primitive stresses need evaluation; at present a number of techniques are available for this purpose. However, a new method of analysind stresses is proposed in this paper. Some estimate of the geologic pressures existing at the site of a proposed underground opening is essential for its economic design and construction. Regardless of the size of such an opening, drill hole or mine stope, these primitive stresses need evaluation. At present a number of techniques are available for this purpose, and another one is to be proposed. These may be grouped into three general methods: 1) precedent, 2) instrumentation, and 3) theoretical analysis. The first two are covered in the literature where their advantages, as well as limitations, are discussed.&apos;9&apos; Generally a theoretical approach combines structural geology with engineering mechanics. The former deals with the geodynamic causes of residual stresses (stresses not related to overburden weight) and presents interesting, but controversial, views.&apos;" A general and useful conclusion, however, can be drawn - vertical residual stresses are much less prevalent than horizontal. However, if for some reason, the values and effects of horizontal pressures were better known to engineers the following analysis

Jan 1, 1962

By W. C. Hagel, J. H. Westbrook

Usittg a sectioning technique with Agl10 as the tracer, the diffusion of silver in silver-excess (45.8 at. pct Mg), near-stoichiometric (49.8 at. pct Mg), and magnesium-excess (52.0 at. pct Mg) cylinders of CsCl-type AgMg was determined from 500" to 700°C. Diffusion coefficients conform to the expression D = Do exp (-q/RT) where the respective Do values are 1.53, 0.280, and 0.134 sq cm sec-I and the Q values are 41.3, 40.6, and 38.0 kcal g-atom-&apos;. Lnttice-parameter and density measurements were performed on a more numerous assortment and wider range of compositions. Substitutional defects were found on both sides of stoichiometry. Activation energies for other rate processes in these alloys show related trends with changing composition, although silver may not be the rate-detemining species. KNOWLEDGE of diffusion coefficients is necessary for a quantitative understanding of the many rate processes (e.g., grain growth, precipitation, sintering, oxidation, or mechanical deformation) occurring in solids. Although these data are available for most metals and common alloys, they are quite limited for intermetallic compounds—a group of materials whose unique physical and mechanical properties are presently attracting great interest. From a fundamental viewpoint, diffusion in intermetallic compounds also offers several engaging aspects owing to: their ordering, the possibility of introducing large, stable concentrations of lattice defects, and the variety of bonding types and crystal structures which can be found. In the case of CsC1-type compounds, some previous work has been directed at examining the role of vacancy defects by changing their concentration compositionally. The diffusion of Co60 was measured in 0 NiAl1- and in P COA., Except for the results of Smoluchowski and Burgess, isothermal diffusion coefficients were found to pass through a minimum at the stoichiometric composi- they decreased sharply on what was reported by Bradley and co-wrkers&apos; to be the vacancy-rich (aluminum excess) side of stoichiometry. This investigation of the diffusion of Agl110 in AgMg was undertaken both as an adjunct to a concurrent study of its deformation behavior and for the purpose of obtaining information on the influence of lattice defects and temperature on diffusion in another CsC1-type intermetallic compound. Bcc AgMg remains ordered up to and melts congruently at 820°C. Solubility limits at 300°C are about 41 at. pct Mg and 53 at. pct Mg. It is one of the Hume-Rothery electron compounds with a 3/2 electron-atom ratio. Previous investigations of its properties include hardress,&apos; tenile,&apos;-&apos; electrical reistivity, and thermodyna-mic1&apos;,14 studies. Indications of a high bonding strength may be found in the large heat of mixing1&apos; and in the 6-pct vol contraction on compound formaticp, as calculated using atomic radii of l.40 and l.55a for Ag and Mg. EXPERIMENTAL PROCEDURE Alloys were prepared by the induction melting of selected fine silver (99.95) and low-iron magnesium (99.95) in magnesia crucibles under 1 atm of A. Supplied by the Handy and Harmon and Dow Chemical Cos., respectivelv. Melts were poured under argon into graphite molds providing 1 1/8-in.-diarn. by 4-in.-long ingots. These were homogenized in evacuated and argon-filled fused-silica capsules by heating for 16 hr at 750&apos;. Three 1 in.-diam. by 3/4-in.-long cylinders were machined from the mid-portion of each ingot for diffusion measurements. Three alloys, analyzing 45.8, 49.8, and 52.0 at. pct Mg were taken as representing the extremes of interest, with 49.8 at. pct Mg being very close to the stoichiometric composition of 50.0 at. pct Mg.

Jan 1, 1962

By Hsun Hu

Three single crystal strips of a 3 pct Si-Fe alloy with approximately (110) [001], (210) [001], and (100) [001] orientations were rolled at room temperature to 30, 50, and 70 pct reductions in thickness. Their deformation and annealing textures were studied. In most cases, the change in texture upon recrystallization and subsequent growth can be described as rotations around the <I10 > axes. A < WO > rotational relationship was also observed. The temperature dependence of recrystallization textures was discussed. WhILE considerable data have been published on the rolling and annealing textures in silicon-iron crystals, very little study has been made on the texture formation at various stages of rolling deformation, and during the process of recrystallization. Dunn&apos; in some of his early works had studied the orientation of recrystallized grains in crystals cut out from lightly rolled (10 to 20 pct reduction) large grained sheets. He found that in most cases a third-order twin relationship exists between the crystal and the recrystallized grains. This orientation relationship actually corresponds to rotations around the <110> axes. The more recent studies of Dunn &apos; and of Dunn and Koh &apos;5 on the rolling and annealing textures in various silicon-iron crystals were concerned mostly with a cold-rolling reduction of 70 pct and annealing at 980OC for recrystallization. Reductions of similar magnitude were also employed by Walter and Hibbard in rolling columnar crystal aggregates of a silicon-iron ingot. A systematic study of the effect of rolling reduction on the deforma- tion and annealing textures is still lacking. Regarding the effect of annealing temperature on the texture formation, Dunn3 has observed a change in therecrys-tallization texture by annealing a 70 pct rolled (1 10) [001] crystal first at a low temperature then atahigh temperature. But the details of texture formation during the annealing treatments were not thoroughly investigated. The present investigation was undertaken to study the texture developments at various stages of rolling deformation and of the recrystallization process, so that a better understanding on the texture formation in silicon-iron crystals may be obtained. EXPERIMENTAL PROCEDURE The three single crystals used in the present investigation were selected from the group of single crystal strips previously prepared7 from a high grade commercial Si-Fe alloy with 3 pct Si. The thickness of these single crystal strips was 0.040 in. The orientations of the three crystals as determined by the X-ray back-reflection Laue technique are shown in Table I. Each of the three crystals was rolled at room temperature along the strip direction to 30, 50, and 70

Jan 1, 1962

By G. M. Schwartz, J. N. Gundersen

John W. Gruner (Professor Emeritus, College of Science, Literature, and the Arts, Dept. of Geology, University of Minnesota, Minneapolis) — It is surprising that two men as well acquainted with the taconite rocks of the Mesabi District as Drs. J. N. Gundersen and G. M. Schwartz should have concluded that the taconite of the Eastern Mesabi before the intrusion of the Duluth gabbro consisted largely of quartz and magnetite. These minerals were "locally reconstituted" into "a wide variety of silicate mineral assemblages" by the gabbro. It is well known, of course, that the silicate mineralogy of the Eastern Mesabi (&apos;about 14 miles in length) is quite different from that of the Main Mesabi which is over 60 miles long. The change from one to the other is abrupt and cannot be attributed to any other cause than the thermal effects of the gabbro. Are we to assume or believe that the taconite of the Eastern Mesabi was radically different from that of the Main range before the gabbro metamorphosed it?

Jan 1, 1962

By C. H. Li, R. J. Stokes, T. L. Johnson

The effect of alumina particles on the nucleation and growth of cracks through a silver- chloride matrzx has been investigated. It has been found possible to promote fibrous cracking in dispersion-strengthened silver, chloride under notch-impact conditions at temperatures at which silver chloride alone cleaves brittlely The modification) of fracture beIzavzor is thought to be due to the relaxation of hydrostatrc stress beneath a notch by the nucleation of cavities near alumina particles. In recent years, composite or dispersion-strengthened materials have been studied primarily to understand their high resistance to plastic flow particularly at elevated temperatures. Dislocation models have been developed with which it is possible to deduce with fair success the effects of interparticle distance, particle size, temperature, upon yielding and creep behavior.l-4 Much less attention has been paid to the fracture behavior of these materials (with the notable exception of common structural steels) and little is known experimentally about the manner in which inclusions affect the nucleation and growth of cracks through a matrix. Nevertheless a beginning has been made in connection with fibrous cracking in ductile matrices where inclusions appear to play an essential ro1e.5-7 During the severe localized plastic deformation which accompanies necking in a tensile test, cavities are believed to develop at inclusions; these cavities subsequently grow and coalesce by plastic flow until separation is complete. It is of interest to consider whether inclusions can affect fracture behavior under loading conditions which restrict the plasticity of the matrix itself (for example, cleavage under conditions of a high imposed strain rate at low temperatures). It is particularly interesting to study these effects in a solid which shows a spectrum of behavior ranging from fully ductile to semi-brittle behavior. Such a solid is silver chloride whose mechanical behavior depends sensitively upon temperature and strain rate.&apos;," The present paper is concerned with a study of the influence of inclusions (in the form of alumina particles) on the fracture behavior of silver chloride loaded uniaxially at low strain rates at room temper- ature and also under notch impact conditions over a wide range of temperature. In particular, it will be shown that the alumina particles can exert a startling effect on the ductile-brittle transition temperature of notched silver chloride and that the magnitude and nature of the effect depends upon both the quantity of alumina and the shape of the alumina particles. 1. EXPERIMENTAL PROCEDURE 1.1 Materials Used. Silver chloride powder of analytical reagent (AR) quality having an average particle size 6 was supplied by the Mallinckrodt Chemical Works (st. Louis, MO.). Acid washed 900 mesh alumina powder, designated A38-900, was supplied by the Norton Co. (Cambridge, Mass.). This powder was added to silver chloride in two forms: a) the as-received condition in which the individual particles were of random irregular shape; their statistical average size was 7; b) in a condition in which each particle was spherically shaped by a fusion technique. In this case, the statistical average particle size determined with the optical microscope was approximately the same (about 5p) but electron micrographic evidence indicated that many ultra fine particles were present in the spheroidized powder. 1.2 Preparation of Composite Materials. Silver chloride-alumina composites containing 2.5, 5, and 15 pct by volume of alumina were produced by the extrusion of mechanically mixed powders blended in a ball mill for 24 hr at room temperature. The mixtures were compacted at 50,000 psi at room temperature in the form of billets 3/4 in. in diameter and 1 in. long which were then extruded with a 16:l reduction ratio at 370°C through a radius-type steel die having a 5 deg lead-in angle. An extrusion temperature of 370°C was selected to ensure that all composites had sufficient plasticity to be extruded. Apart from this general requirement, the choice was arbitrary. 1.3 Microstructure of Composites. Attempts were made to check the distribution of alumina metallo-graphically by polishing transverse and longitudinal sections of the extruded rod. Specimens were wet-ground to 600 emery paper and lapped successively with 5 and 0.25-p grades of diamond paste. They were etched for 10 sec in 10 pct sodium thiosulfate solution and lightly polished in concentrated ammonium hydroxide. The most effective way to render the alumina particles and grain boundaries visible was to radiate the surface with intense white light to decorate the grain boundaries and the particle-matrix interfaces photolytically.

Jan 1, 1962

By T. C. Shelton, W. M. Huang

One of the problems arising from the use of modern machines and systems in coal mining is increased emission of explosive gases into the mine passageways. Interest in degasification of coal seams has grown. The authors summarize the results of coal permeability tests done at Virginia Polytechnic Inst. on one of the fundamental aspects of the problem. There are undoubtedly many factors that affect the emission of gas from coal but the permeability of coal to gas flow would seem to be fundamental. However, there is very little information on coal permeability to gas flow available in the U.S. at the present time, despite the fact that such knowledge would appear to be significant in any degasification effort. Studies made recently in the mining engineering laboratories at Virginia Polytechnic Inst. have determined values of permeability on 1-in. cubes of selected coals. COAL PERMEABILITY The permeability values given in this paper are based on adaptations of Darcy&apos;s law formulated by Henry Darcy in I856 from experiments with fluid flow in porous media.&apos; Using air as the gaseous fluid, they were obtained by employing similar methods as are used to dete1:mine the permeability of petroleum and gas reservoir rock specimens. Permeability is. a measure of the ease with which fluids flow through a porous substance, and it is governed by the connected pores within a porous medium. If a few large-sized pores, fractures or channels are present within the medium, the medium can have great permcnability without significant porosity. It is reasonable to assume, therefore, that the permeability of coal, due to its structure, is based on fractures connecting the pore space left as the result of some degree of devolatilization or other changes of the substance from which coal was formed. The results of this irvestigation tend to validate this assumption in that the values obtained indicate a close relationship between the rank and permeability of coal. COALS TESTED AND PROCEDURE The coals whose permeability values were determined in this investigation are given in Table I.

Jan 1, 1962

By I. F. Jackson, H. L. Hartman

Hard-metal inserts have received considerable attention in the mining industry recently for a variety of excavating and penetrating purposes. Their use in percussive drilling and in coal cutting machines is well known, but attempts to utilize them in cutting materials such as dimension stone have been discouraging because of excessive tool wear and failure. Particular attention is given to those properties of hard-metal inserts that affect their resistance to wear. A consideration of the actual wear mechanism shows the importance of correct mounting of the inserts and of the selection of suitably powered driving motor so as to achieve minimum tool wear and maximum tool life. Comparisons are made between the performances of types of hard-metal inserts, relating their inherent properties with results obtained in laboratory tests. As part of a broad program to improve the quarrying and processing of industrial minerals, The Pennsylvania State University has been investigating the machinability of slate under laboratory and field conditions. It should be emphasized that the results of the research presented in this paper are also applicable to other natural structural materials, and particularly to the more workable ones such as limestone and sandstone. Improvements which accrue in cutting and sawing should prove of benefit to all the dimension stone industry. Further, it may be pointed out that the results reported here are applicable to rotary drilling (with drag bits) as well as to cutting and sawing of rock. INVESTIGATIONS IN RELATED FIELDS The investigation was initiated with an extensive survey of available literature related to metal cutting and to rotary drilling. The following similar features between metal cutting and slate cutting became evident: 1) Hard-metal inserts are widely used as a cutting tool in both cases. 2) The forces acting on the tool may be resolved into normal and tangential components. 3) Rate of penetration and tool wear are important criteria in each case. On the other hand, important differences also exist: 1) Most metals, exhibit plastic behavior, while slate (and most rock) is a brittle material under normal conditions. 2) In metal cutting the component of force acting parallel to the surface of the workpiece is considerably greater than the force holding the tool against the workpiece. 111 slate cutting, this situation is reversed. Similarities between drag-bit rotary drilling and slate cutting are as follows: 1) In both casts, a tool, usually of the hard-metal insert type, is used to penetrate a brittle material. 2) The drilling forces and related variables, such as rotation speed, are similar. 3) Chip formation in each case is essentially the same. 4) The shape of the tool is similar in rotary drilling and slate cutting. Important differences are also apparent: 1) The objective of drilling is to produce a directed hole, while in cutting it is to form a kerf. In core drilling, however, a kerf is also produced. 2) The horizonta1 component of force in rotary drilling decreases from the center to the outside of the tool, whereas in slate cutting the component is almost uniformly distributed across the width of the tool. 3) The power absorbed in the drill rod is greater in rotary drilling. 4) The clogging action of chips, if excessive power is applied to the tool and if flushing is insufficient, is more serious in rotary drilling. Because of the striking similarities between metal cutting and slate cutting, and between rotary drilling and slate cutting, it was considered that the findings of investigators in those fields would serve as a guide for experimental studies of slate cutting. The following is thus devoted to a discussion of those aspects of metal cutting and rotary drilling pertinent to the present investigations.

Jan 1, 1962

By John Rogers

The goal of a detailed quantitative understanding of the variables insulfide flotation in terms of established, or new, scientific principles is still distant, although there has been a good beginning in the past 50 years with more rapid progress since 1930. Advances have paralleled closely those in other branches of surface chemistry and the development of a series of experimental techniques such as contact angle, surface area measurement, radioactive tracers, infrared spectra, electron diffraction, monolayer, and electro- chemical methods of investigation. The second editions of books by Sutherland and Warkl ( 1955) and Gaudin2 ( 19571, are detailed accounts of this progress. The complexity of sulfide mineral flotation systems is indicated by Sutherland and Warkl who list 32 variables of flotation, of which only 22 can usually be controlled by the metallurgist. A consequence of this multiplicity of variables, many of which may be specific to each particular ore, is that ways of floating sulfide minerals from new ores are still developed empirically. How- ever, this review will try to show how the chemistry of the function of frothers, collectors, depressants, and activators in sulfide flotation is being steadily unravelled. Chiefly, it will be concerned with the interaction of pure soluble compounds with individual sulfide minerals, the surfaces of which are often not stoichiometric for several reasons discussed by Plaksin.3 As a result, for example, a freshly cleaved galena surface has cathodic and anodic areas which have different degrees of oxidation and different reactivity to- wards collectors like xanthate. Such complicating considerations should be remembered in the subsequent discussion of pure minerals. THE NEED FOR FLOTATION REAGENTS After considerable controversy it has been established with a few exceptions that unoxidized, uncontaminated sulfides will not float. Moreover all flotation plants recovering sulfide minerals use collectors which are removed from the circuit with the sulfides. Gaudin, Miaw, and Spedden4 have discussed the relation between the crystal structure of solids and the native floatability of the exceptions mentioned above. A second question which has been much explored is the nature of the surface on which a collector like xanthate is adsorbed or reacts. Is this the un- changed surface of the sulfide mineral, or does the adsorption depend on the initial oxidation of the sulfide surface ? Sutherland and Warkl and Gaudin2 discuss the work of Taggart5 and others on this question without reaching any other conclusion than that oxygen was important.

Jan 1, 1962