By K. M. Rolls, F. W. Reuter, J. Wulff

The superconducting behavior and microstructural characteristics of a nominal Nb-40 wt pct Ti-0.239 wt pct O alloy were studied as a function of ther mo -mechanical processing treatment. Critical current density us applied transverse magnetic field was obtained for 0.010-in.-diam wires at 4.2°Kin steady fields 14 to 110 kG. Both optical metallogvaphy and transmission electron microscopy were used to delineate the micros tructures of the same wires. It wan found that a 1-hr 500°C precipitation heat treatment after cold drawing to final size led to the highest critical current density. Heat treatment at 600°C also led to a high critical current density, but the precipitate differs in kind and form from that at 500°C. The resistire critical field was also found to be sensitive to precipitation heat treatment since the effective composition of the superconducting phase changes. This is discussed in terms of the oxygen in interstitial solid solution. Two types of high-field superconducting wire are at present used in the construction of high-field superconducting solenoids. These types are solid-solution alloy wire such as Nb-Zr and Nb-Ti and composites of the brittle inter metallic compound Nb3Sn. The latter generally have a high super cur rent-carry ing capacity which is difficult to vary if properly made. The supercur rent- carry ing capacity of the former can be varied drastically and often predictably by suitable thermomechanical processing treatments. In general, the critical current density Jc of the solid-solution type of alloy is increased by cold work and by additions of interstitial elements along with aging heat treatments. The imperfections which result are be-iieved to be responsible for the observed increase in Jc. In 1962 Kneip and coworkers1 found that the critical faurrent density of Nb-Zr alloys could be increased by proper heat treatment preceded and followed by cold work. Betterton and coworkers2 using a Nb-25 at. pct Zr alloy found that small additions of oxygen or carbon enhanced the effect of this heat treatment. They suggested that the interstitials present aided precipitation in the alloy, leading to a filamentary structure with superior properties. If the precipitation heat treatment was omitted, interstitial additions had a negligible effect on Jc. wong3 showed that higher heat-treatment temperatures lowered Jc. Walker and co-workers,4 who studied microstructure (by transmission electron microscopy) as well as superconductivity, found that the Jc anisotropy introduced by cold rolling was itself affected by heat treatment. They were unable to clarify the relation between microstructure and critical current density, although evidence of precipitation was indicated. More recent investigation of Nb-Zr alloys,5,6 besides showing that structural defects and fiber ing due to cold work and precipitation serve to raise Jc, also elucidate important optically observable microstructural changes which occur upon precipitation. In these reports, coarsening of the microstructural features was found to decrease Jc. Vetrano and Boom,7 who studied Ti-20.7 at. pct Nb, found that Jc was increased to a maximum by a 415°C, 3-hr heat treatment following quenching from 800°C and cold working. Heat treatments can also affect the resistive critical field Hr. Final-size heat treatments of Nb-Zr wire can lower Hr drastically if gross phase decomposition occurs5'* or moderately if the effects of cold work are eliminated without changing significantly the composition of the phase of interest.3,5,6,8 The percentage of oxygen which can be added to Nb-Zr alloys to enhance Jc is limited by the difficulty of subsequent cold drawing. Since Nb-Ti and Ta-Ti alloys in contrast can tolerate appreciably higher percentages of oxygen, it was decided to investigate the superconducting behavior of various alloys in these systems. The present paper describes the results of adding oxygen to a nominal 40 wt pct Nb alloy as a function of thermomechanical treatment. I) EXPERIMENTAL PROCEDURE A small alloy ingot was prepared from high-purity niobium, iodide, crystal-bar titanium, and Nb2O5 powder by arc melting on a water-cooled copper hearth in a gettered argon atmosphere. The ingot was turned and remelted fourteen times to insure homogeneity. After final melting and rapid cooling, it was machined round to 0.415 in. diam, jacketed in stainless steel, and cold-swaged to 0.117 in. diam. The jacket was removed and swaging continued to 0.051 in. diam followed by wire drawing in carbide dies to 0.010 in. diam. Although it was intended that about 1500 ppm O (by weight) be added, inert gas fusion analysis indicated a 2390 ppm 0 content, apparently due to additional oxygen pickup in the arc furnace. Even so, the alloy was sufficiently ductile to be cold-worked to greater than 99.9 pct reduction

Jan 1, 1967

By J. W. Graham

For many years the author has been cognizant of the difficulty encountered by some in treating with the water influx formulas for unsteady-state fluid flow as pertain to the material balance equation. This has particularly applied in establishing reservoir performance and identifying reservoir pressure, which to the practicing engineer has entailed a trial-and-error procedure, and for others has necessitated resorting to computing devices and reiteration processes. In retrospect this difficulty stems from the fact that reservoir pressure in the material balance formulas, as well as associated with the water influx equations, is an inexplicit term, and the work reported in the past is irrefutable. However, what will be presented in this paper is another approach to the problem, whereby the entire material balance equation will be treated by the Laplace transformation, and reservoir pressure which hereto has been inexplicit, can now be isolated by mathematical procedure to relate that parameter with all the factors contributing to its change. This is the simplification entailed, that treats first with an undersaturated oil reservoir as an integrated effect from the inception of production. The second phase pertains to saturated oil reservoirs that encompass a survey traverse. Although both methods of approach are necessarily different in aspect, the most interesting fact is that the mathematics so deduced are identical. Both the linear and radial water-drive systems are incorporated. for which an illustrated factual example is offered for the latter, treating with a saturated oil reservoir. INTRODUCTIO N What is performed in this work is the simplification of an involved computation by advanced analysis. Although such may be construed as a contradiction when one treats with higher mathematics; nevertheless, when direction is given to such an undertaking the results car. be most revealing. Likewise, it is to be mentioned that the bases for these mathematics have been developed on the expediency of the occasion. This is not to be inferred as a qualification of this work, but rather the demands frequently placed upon the author in his private prac- tice in meeting a time limit. A situation, instead of being fraught with hazards, often has given emphasis to creative thought. What will be entailed in this work is the simplification of the material balance formulas by the Laplace Transformation., Although this reveals entirely new horizons that will be given expression in a forthcoming tract, it suffices in the present instance to limit our attention to this phase of the development that treats both with an undersaturated and saturated oil reservoir. To orient the reader's thoughts as to what is involved in this simplification is the recognition that reservoir pressure, as such, is an inexplicit term in the material balance equation. This is the independent parameter that defines the total history of performance in the author's' unsteady-state water influx formulas, as well as the basis for the physical dependency of fluid behavior within the formation as prescribed in the Schil-thuis' material balance equation. Therefore, to isolate reservoir pressure, which is the most essential factor in any reservoir study, is rather a cumbersome procedure entailing either a trial-and-error calculation for the engineer; or as some prefer, a reiteration process performed on a computing device. However, once such an equation can be transcribed as a Laplace transformation, this inexplicitness so expressed can be alleviated to identify reservoir pressure as an explicit function of all the factors contributing to its change. This is the simplification encompassed, that will treat first with an undersaturated oil reservoir as an integrated effect from the inception of production, and secondly, with a saturated oil reservoir as a survey traverse. Although the two approaches are necessarily different because of the uhvsics involved. it is an interesting commentary that the mathematics are identical, showing the interdependency of the two methods. In order to acquaint the reader with this development, the simplest case will be treated first; namely, an under-saturated oil reservoir subject to a linear water drive. However, what may be construed for this example as an idealistic case is actually a most practical application in certain parts of the world, where the size of the fields are so large that radial water-drive approaches the configuration of a linear drive. Further, to avoid the repetition of much symbolism, frequent references will be made to the work of the author and an associate on Laplace Transformations3,

By Frederic L. Kadey

Diatomite is a siliceous, sedimentary rock consisting principally of the fossilized skeletal remains of the diatom, a unicellular aquatic plant related to the algae. Thus, it has been formed by the induration of diatomaceous ooze, and consists mainly of diatomaceous silica, a form or variety of opal which is first formed in the cell walls of the living diatom. Diatomaceous silica is not generally regarded as a synonym or the equivalent for diatomite, although it has been so used at various times. Accurately, diatomaceous silica is the preferred name for the principal mineral component of which the rock, diatomite, is composed. The terms diatomaceous earth and kieselguhr are used as synonymous with diatomite. The designations tripoli, tripolite, infusorial earth, etc., were used at one time but are now obsolete. With the changing nomenclature, these terms that were at one time correct when proposed and used for generations would be considered incorrect if used today in the light of current knowledge. The designation diatomite is reserved for those accumulations of diatomaceous silica that are of sufficient quality, size, and minability to be considered of potential commercial value. Processed diatomite possesses an unusual particulate structure and chemical stability that lends itself to applications not filled by any other form of silica. Foremost among these applications is its use as a filter aid, which accounts for over half of its current consumption. Its unique diatom structure, low bulk density, high absorptive capacity, high surface area, and relatively low abrasion are attributes responsible for its utility as a functional filler and as an extender in paint, paper, rubber, and in plastics; and as an anti-caking agent; thermal insulating material; catalyst carrier; and chromatographic support; polish, abrasive, and pesticide extender to name a few representative applications. The United States is the principal producing country, although diatomite is found in numerous other locations. Geology Composition and Morphology Diatomaceous silica qualifies as a. mineral of organic origin in much the same way that aragonite and collophane do. The silica of the fossilized diatom skeleton closely resembles opal or hydrous silica in composition (SiO2 • nH2O) .4, 12, 203 The silica is of acute biological significance, not only for the cell wall component, but also for the basic life process.45, 51 Without silica, cell development ceases .31 In addition to bound water, varying between 3.5 and 8%, the siliceous skeleton may also contain, in solid solution, or as part of the Si02 complex, small amounts of associated inorganic components-alumina, principally-and lesser amounts of iron, 46, 49, 55 alkaline earths, alkali metals, and other minor constituents.59, 63, 67 Boron is reported to be an essential element for diatom growth .52, 58 Since diatomaceous silica is not pure hydrous silica but contains other intimately associated elements, there is good reason to consider it a distinct type or variety.4 Associated with the diatomaceous silica, and integrated as part of the diatomite, may be variable amounts of organic matter, soluble salts, and particles of rock-forming minerals that were syngenetically deposited or precipitated with the diatom frustules. Sand, clay, carbonate, and volcanic ash are typical common contaminants. Other contaminating minerals may be present, such as feldspar, mica, amphiboles, pyroxenes, rutile, zircon-the result of weathering, then transporting, and subsequent redeposition of surrounding land masses. Commercial diatomite may also contain fragments and particles of

Jan 1, 1983

By T. A. Read, M. S. Wechsler, D. S. Lieberman

A theoretical analysis of the austenite-martensite transformation is presented which predicts the habit plane, orientation relationships, and macroscopic distortions from a knowledge only of the crystal structures of the initial and final phases. THIS paper presents a new theory of the formation of martensite. This theory makes possible the calculation of the austenite planes on which the martensite plates form, the orientation relationship between the austenite and martensite crystal axes, and the macroscopic distortions which are observed. The only input data needed are the crystal structures and lattice parameters of the austenite and martensite. Considerable effort has been devoted over the past thirty years to the development of an understanding of the crystallographic features of martensite reactions. Much of this work has been done on steels and iron-nickel alloys, for which a great deal of data has been accumulated concerning the shape and orientation of the martensite plates, the relative orientations of the austenite and martensite crystal axes, and the observable distortions which result from transformation. These observations are reviewed in refs. 1, 2, and 3. The first major step toward an understanding of these phenomena was made in 1924 by Bain,' who showed that the a body-centered cubic structure can be produced from the 7 face-centered cubic structure by a contraction of about 17 pct in the direction of one of the austenite cube axes and an expansion of 12 pct in all directions perpendicular to it. Since that time, most of the efforts at further interpretation have been made by investigators who have worked from the phenomenological data, incorporating some of the information from the lattice properties, and have sought an analysis into likely deformations which would produce the observed results."- "11 but the three most recent papers on the subject have already been reviewed in some detail." Machlin and Cohenl0 measured the components of the distortion matrix and verified that the habit plane is a plane of zero distortion and rotation for the (259) case. They showed that the measured distortion matrix, when applied to the parent lattice, does not yield the product lattice and hence some inhomogeneous distortion must occur. Frank,u working from the lattice properties and taking some clues from the observations, considered the correspondence of close-packed rows and planes in the austenite and martensite. He predicted substantially the observed lattice relationship and habit plane for certain steels which have a (225) habit. Geisler12 suggested that there is a natural tendency for the habit plane to be a (111) and postulated certain slip processes to account for the fact that the experimentally observed habit plane is irrational and deviates from the assumed one. The present work differs from previous treatments of martensite formation in that it permits calculation of all the major manifestations of the process. Habit plane indices, orientation relationships, and observable distortions are all calculated from a knowledge of the crystal structures of the initial and final phases alone. The calculations contain no adjustable parameters. The agreement found between calculated results and the observations reported in the literature constitutes powerful evidence in favor of the mechanism of martensite formation proposed. The theory is applicable to systems other than steel (as is discussed later in this paper) which exhibit a diffusionless phase change but because of the wide-spread interest in the austenite-martensite transformation, particular attention will be given to the iron-base alloys. For other systems which undergo a similar face-centered cubic to face-centered tetragonal transformation, the mathematical treatment is identical with that presented here. Hence the theory successfully describes the transformation in the indium-thallium alloy.'" Homogeneous Transformation to Martensite The distortion which any homogeneously transforming volume of austenite undergoes in order to become martensite is shown in Fig. 1, as was first suggested by Bain.' (This distortion will hereafter be referred to as the "Bain distortion.") This specification of a contraction along one cube axis ;ombined with an expansion in all directions perpendicular to this axis describes what is properly called the "pure" distortion associated with this transformation. The distinction between a "pure" and an "impure" distortion plays an important part in the discussion which follows. A "pure" distortion is characterized by the existence of at least one set of orthogonal axes fixed in the body which are not rotated by the distortion. (These are called the "principal axes" of the distortion.) No such set of axes exists in the case of an "impure" distortion. On the other hand, an impure distortion can always be represented as the result of a pure distortion combined with the rotation of the specimen as a rigid body. For a given impure distortion the corresponding pure distortion

Jan 1, 1954

By C. R. Fulton

The idea of making permanent magnets by sintering is not a new one, but until the introduction of the iron-nickel-aluminum permanent-magnet alloys there was little need for such a process. Permanent-magnet alloys in use up to the time of this development could be forged and machined to the exact size or shape required without too much difficulty. These new Fe-Ni-A1 alloys, which have become known as Alnico in this country, soon became very popular because of their superior magnetic properties, but when they were made by casting they did have some disadvantages when compared with the older type of permanent-magnet steels. Among these disadvantages were the following: 1. It was almost essential that they be cast to size, since they could not be readily forged or machined. The material could be ground but this was quite expensive, particularly for small magnets in large quantities. 2. The material had a large grain size and was mechanically weak. 3. Close tolerances could not be held and on small magnets this meant grinding almost the entire magnet. Because of the brittle nature of the material, there was considerable loss due to chipping and cracking during these grinding operations. 4. Because of its high aluminum content, the molten alloy had a high surface tension. It was difficult to prevent loss of aluminum by oxidation during the melting operation. In view of these difficulties it is not hard to understand why a process for sintering alnico was developed, or why sintered alnico has come into such widespread use in recent years. It might be well to qualify this by saying that it has come into widespread use for small magnets weighing 2 oz. and less, of the type shown on Fig. I. In this size range, sintered alnico has been able to compete in price with cast alnico. Magnets larger in size, of the type shown on Fig. 2, can be made but they do not compare favorably in price with the cast material. An idea of the range of sizes that have been produced is given by Fig. 3, which shows a small magnet weighing 0.006 oz. and a large magnet with a steel insert weighing 4 lb., both made from sintered alnico. Magnets weighing more than 2 oz., however, should not be made from sintered

Jan 1, 1945

By E. C. Wright

The bessemer process is nearly one hundred years old. William Kelly, the American inventor, was able to demonstrate that he had accomplished the pneumatic purification of molten pig iron as early as 1847; Henry Bessemer's English patent was granted in 1855. The application of this steelmaking process since then and the present position of bessemer steel are concisely discussed on pages 355 and 356 of the fifth edition of "The Making, Shaping and Treating of Steel." The great expansion of the automotive, machine-tool, chemical and oil industries after I9I0 opened up a large market for special steels, whereas the output of steel before that time was mainly for structural purposes. The need for building more blastfurnace capacity complementary to bessemer operations, combined with the availability of the' necessary amounts of steel scrap, both contributed to the extension of open-hearth plants at the -exense of besskmer capacity. The ability of the open-hearth furnaces to consume virtually all types of raw materials as far as phosphorus content is concerned, and the need for selecting low-phosphorus ores of rapidly decreasing sources for the bessemer, also played a part in the reduction of bessemer steelmaking operations and the increase in basic open-hearth plants. As a consequence, the proportion of bessemer steel made, in this country decreased from 65.7 per cent of the total in 1900 to 37.1 per cent in 1910, and only 6.8 per cent of the total in 1937. The metallurgical concepts existent between 1910 and 1920 caused the writing of many specifications of very low phosphorus and sulphur content, which definitely barred bessemer steel from many commodities. Now sulphur is being added to many open-hearth and bessemer steels in amounts far exceeding the maximum sulphur content of good bessemer steel. Re-phosphorizing is also widely practiced for several specific applications. Even today, the chemical-analysis limits of many important steel specifications have an arbitrary and archaic tinge. The old standard "0.30 to 0.60 per cent manganese" might be mentioned in this connection as similar to the rigid requirements for maximum sulphur and phosphorus that were established at least 25 years ago. The literature is full of vague and complee discussions of the effects of nitrogen and oxygen where these elements existed in steel in amounts less than 0.02 per cent. Many failures have been attributed to these elements without reasonable proof on which to base the conclusion. Methods of determining oxygen in steel require such complicated equipment that only a few research laboratories have the required apparatus. Even so, the accuracy of oxygen determinations in steel has been only recently reproducible. Up to the present time, no one has succeeded in obtaining a sample of molten steel that accurately indicates the full oxygen content of the metal in the furnace or ladle because the molten sample

Jan 1, 1944

By E. C. Wright

The bessemer process is nearly one hundred years old. William Kelly, the American inventor, was able to demonstrate that he had accomplished the pneumatic purification of molten pig iron as early as 1847; Henry Bessemer's English patent was granted in 1855. The application of this steelmaking process since then and the present position of bessemer steel are concisely discussed on pages 355 and 356 of the fifth edition of "The Making, Shaping and Treating of Steel." The great expansion of the automotive, machine-tool, chemical and oil industries after I9I0 opened up a large market for special steels, whereas the output of steel before that time was mainly for structural purposes. The need for building more blastfurnace capacity complementary to bessemer operations, combined with the availability of the' necessary amounts of steel scrap, both contributed to the extension of open-hearth plants at the -exense of besskmer capacity. The ability of the open-hearth furnaces to consume virtually all types of raw materials as far as phosphorus content is concerned, and the need for selecting low-phosphorus ores of rapidly decreasing sources for the bessemer, also played a part in the reduction of bessemer steelmaking operations and the increase in basic open-hearth plants. As a consequence, the proportion of bessemer steel made, in this country decreased from 65.7 per cent of the total in 1900 to 37.1 per cent in 1910, and only 6.8 per cent of the total in 1937. The metallurgical concepts existent between 1910 and 1920 caused the writing of many specifications of very low phosphorus and sulphur content, which definitely barred bessemer steel from many commodities. Now sulphur is being added to many open-hearth and bessemer steels in amounts far exceeding the maximum sulphur content of good bessemer steel. Re-phosphorizing is also widely practiced for several specific applications. Even today, the chemical-analysis limits of many important steel specifications have an arbitrary and archaic tinge. The old standard "0.30 to 0.60 per cent manganese" might be mentioned in this connection as similar to the rigid requirements for maximum sulphur and phosphorus that were established at least 25 years ago. The literature is full of vague and complee discussions of the effects of nitrogen and oxygen where these elements existed in steel in amounts less than 0.02 per cent. Many failures have been attributed to these elements without reasonable proof on which to base the conclusion. Methods of determining oxygen in steel require such complicated equipment that only a few research laboratories have the required apparatus. Even so, the accuracy of oxygen determinations in steel has been only recently reproducible. Up to the present time, no one has succeeded in obtaining a sample of molten steel that accurately indicates the full oxygen content of the metal in the furnace or ladle because the molten sample

Jan 1, 1944

By J. A. Roberson, A. M. Adair

A plate of an 18 pct Ni (250 grade) maraging steel was homogenized, cold rolled, and re crystallized to produce a fine grained, homogeneous structure. The strength properties were then measured as a function of cold rollinq prior to aging. Material in the solution heat treated condition exhibited substantial strengthening from cold rolling. The strength increase and the rate of strengthening were proportional to the amount of cold work. This benefit, of up to 50 ksi, was retained during aging for 3 hr at 900°F. The structures produced by cold rolling and aging have been systematically investigated by transmission electron microscopy. The dislocation debris produced by cold work influences the morphology and distribution of precipitate particles as well as the rate of precipitation. An essential feature of the high nickel maraging steels is a martensitic transformation from y to a with the resultant production of a supersaturated bcc solid solution. This solution decomposes to form precipitates during a subsequent aging treatment.' The martensitic transformation in low carbon Fe-Ni alloys and the mechanical properties of these alloys have been studied extensively.2"4 The carbon content of maraging steel is kept very low to avoid the embrittling Fe3C phase and to minimize the acicular, or twinned martensite common to high carbon steels. Maraging steels are usually strengthened only by heat treatment, but cold working is also quite effective in this respect as was shown by Decker, Eash, and Goldman,' Kula and Hickey,5 and the present work. There is, however, some disagreement between the present results and those of Kula and Hickey. Because of their unusual combination of strength and toughness, the maraging steels are suitable for applications where reliability at high stress levels is required. The strength level is achieved through a combination of solid solution hardening,' substructure hardening,3 and precipitation hardening,6 of which the last is the most important. The toughness of these steels has been reported to be a result of the absence of brittle grain boundary precipitates,7 and the fact that the matrix is a massive martensite rather than a twinned martensite.' One of the problems in the manufacture and use of maraging steel has been its tendency to develop laminations in sheets parallel to the rolling plane.9,10 The present investigation was intended to determine whether or not an improvement in the microstructure of this steel by thermomechani-cal processing would improve mechanical properties. I) EXPERIMENTAL PROCEDURES A plate ($ in. thick) of an 18 pct Ni-250 grade maraging steel* was obtained and examined metallo- "Analysis, wt pct: 18.1 Ni, 8.6 Co, 5.3 Mo, 0.4 Ti, 0.07 Mn, 0.05 Cr, 0.05 Si, 0.002B. 0.1 Cu. 0.05 Al. 0.002 Zr, 0.016 C, balance Fe. graphically. It was found to contain laminations as described by previous investigators. This plate was then annealed at 2100°F for 24 hr to promote homogeneity. Pilot studies on small coupons had shown that this was the minimum temperature required to accomplish homogenization in 24 hr. Since this treatment caused excessive grain growth, the steel was subsequently cold rolled and recrystallized. Cold rolling was accomplished at about 5 pct per pass to a total reduction of 66 pct. The standard solution annealing treatment (1 hr at 1500°F) was adequate to cause recrystallization of the cold worked steel. The recrystallized steel was then cold rolled and ground by various amounts to produce specimens with uniform thickness and selected amounts of cold rolling. All tensile specimens with less than 90 pct cold reduction were ground to a thickness of 0.050 in. Specimens with 90 pct cold reduction were 0.025 in. thick. All

Jan 1, 1970

By G. Borelius

ABOUT the turn of the century, Gibbs' thermo-dynamic theory of heterogeneous equilibrium, on the one hand, and the experimental methods of thermal and microscopic analysis, on the other, gave to the physical metallurgist his first scientific tool, the equilibrium diagram. The classical equilibrium diagram of a binary alloy system shows the boundaries between ranges of homogeneous and heterogeneous equilibrium in their dependence of concentration and temperature. A homogeneous solid sohtion which on cooling passes such a boundary is assumed to precipitate, forming a mixture of two phases with different concentrations. The equilibriunl diagram and the equilibrium theory, however, give no information about the time scheme of the process or the intermediate states passed during precipitation. For this reason it satisfies neither the practical need of the metallurgist nor the curiosity of the physicist. As a matter of fact, in the heat treatment of alloys for technical use the objective very seldom is the equilibrium state. Thus good mechanical properties of construction material are connected, for the most part, with some intermediate state. As these intermediate states are thermodynamically unstable, there is, from a theoretical point of view, always to be expected a decay of the good properties with time; and it is a matter also of practical interest to know whether this natural life time of a material is of the order of, say, ten or thousands of years. Thus, for many reasons, there is a current demand to complete our knowledge of equilibrium through knowledge of the kinetics of the precipitation phenomena. From the point of view of the physicist, the most interesting question in this case is whether there are any general laws governing the kinetics. According to a generally accepted view, precipitation is ruled by two more or less independent phenomena, the formation of nuclei of a new phase and the growth of these nuclei. It is also commonly accepted that there is a tendency for the velocity of growth to increase with increasing temperature because of the increasing mobility of the atoms. There is also a tendency for the velocity of growth to decrease in the neighborhood of the two-phase boundaries. So far, however, very little is known quantitatively about this fundamental phenomenon in the case of solid metallic systems. In our laboratory attention has been directed especially toward the nucleation phenomena, and a series of measurements have been carried out with the guidance of a work- ing hypothesis (based on experiences from previous work on order-disorder transformations in alloys) about the influence on the nucleation of thermo-dynamic potential barriers. However, before discussing the experiments, the theoretical ideas will be considered. In a binary solid solution the arrangement of atoms on the lattice points approaches with increasing temperature a state of full randomness, as illustrated by the ball model of Fig. 1, that might represent a [111] plane of a face-centered alloy with 30 pct "black" and 70 pct "white" atoms. In reality the atoms are changing places continually with their neighbors so that the picture should rightly have been a moving one. On account of this thermal motion the concentration of black atoms within a certain group of, say, a hundred or a thousand lattice points fluctuates with time around the bulk concentration of 30 pct in a manner governed by statistical laws. With decreasing temperature two independent changes in this state grow more and more important. First, the mobility of the atoms decreases, and second, the forces between the atoms will have an increased influence on the fluctuations. In alloys with a tendency for precipitation, which are the concern of this lecture, the distribution function of concentration fluctuations will broaden, so that the relative probability of great local variations from the bulk concentration increases. Fig. 2 gives an example of such a fluctuation. When the alloy is supercooled below the solubility limit into the range of two-phase equilibrium, the fluctuations will now and then at some point give rise to a state that resembles the equilibrium state and thus will form a stable nucleus that is capable of growing by diffusion processes. In discussions with colleagues and in the literature, I have often encountered the idea that three or four atoms of the dissolved metal could form a nucleus of the new phase. A look at the ball model might be enough to indicate that this cannot be true. If it were true, there should be nothing but nuclei, whereas we know from experiment that nucleation must be a rather rare occurrence. In fact we have, as will be mentioned later, certain reasons to believe that the nuclei are formed by fluctuations containing some hundreds of atoms, which should be the order of the number of black balls in the fluctuating group of the figure, if it were extended into three dimensions. As a working hypothesis we have assumed that the fluctuations producing nuclei, though large and rare, still are ruled by the distribution laws of fluctuations of the supercooled solid solution in its initial state. Thus the probability of nucleation will be connected to the thermodynamic properties of the solid

Jan 1, 1952

By R. W. Gurry

When a steel in the austenitic state, with all its carbon in solution, is maintained, at constant temperature, in contact with a gas that removes the carbon from the surface, yet without otherwise altering the composition of the steel, the change in weight of the specimen, after any period of exposure, is a direct measure of the amount of carbon it has then lost. The purpose of the present paper is to show how, by application of established mathematical reasoning based on the fundamental diffusion law and on certain postulates, this loss of weight yields a complete picture of the distribution of carbon throughout a specimen of regular shape after any period of exposure, with all the accuracy required in any practical occurrence of decarburization. Precisely the same is true for the gain in weight during the reverse process of carburization, or for the gradual gain or loss of any element, so long as the steel comprises only a single phase at temperature, provided always that the experimental conditions conform to the postulates. The change in carbon content from surface to center of the specimen is always continuous, when everything is in solution, even though under the microscope the decarburized zone (or carburized rim) may appear to be sharply defined. The experimental procedure is described and some typical results are presented, which are then interpreted by application of the diffusion law. Experimental Procedure Initially an endeavor was made to follow the gain of weight during the process of carburization in a hydrogen-toluene atmosphere, but it was soon found that the specimen became coated with graphite, which could not be removed without some loss of metal; therefore it was decided to continue carburization until the steel was saturated throughout, to remove all graphite from the surface of the specimen, and then to follow the loss of weight during decarburization in a moist hydrogen atmosphere at the same temperature as that used for carburizing. The carburizing procedure has been described in an earlier paper;' it suffices to state here that the carburization lasted about I40 hr. at 760°C. (1760°F.) and 44 hr. at iiio°C. (2030°F.), these periods being long enough-—on the basis of the calculations presented later—to ensure that the specimen was about 99.9 per cent saturated at each temperature. The specimen was a cylinder about 3.8 cm. long and 0.475 cm. in diameter; the materials were carbonyl iron, a commercial low-metalloid iron, and a steel with 3.6 per cent nickel and the usual proportion of other elements. The fully carburized specimen, after cooling at the top of the furnace tube, was placed in a lathe and sandpapered to remove all graphite; then the diameter was measured with a micrometer caliper, and the initial weighing (corresponding to complete saturation) was made. By means of a

Jan 1, 1942

By R. W. Gurry

When a steel in the austenitic state, with all its carbon in solution, is maintained, at constant temperature, in contact with a gas that removes the carbon from the surface, yet without otherwise altering the composition of the steel, the change in weight of the specimen, after any period of exposure, is a direct measure of the amount of carbon it has then lost. The purpose of the present paper is to show how, by application of established mathematical reasoning based on the fundamental diffusion law and on certain postulates, this loss of weight yields a complete picture of the distribution of carbon throughout a specimen of regular shape after any period of exposure, with all the accuracy required in any practical occurrence of decarburization. Precisely the same is true for the gain in weight during the reverse process of carburization, or for the gradual gain or loss of any element, so long as the steel comprises only a single phase at temperature, provided always that the experimental conditions conform to the postulates. The change in carbon content from surface to center of the specimen is always continuous, when everything is in solution, even though under the microscope the decarburized zone (or carburized rim) may appear to be sharply defined. The experimental procedure is described and some typical results are presented, which are then interpreted by application of the diffusion law. Experimental Procedure Initially an endeavor was made to follow the gain of weight during the process of carburization in a hydrogen-toluene atmosphere, but it was soon found that the specimen became coated with graphite, which could not be removed without some loss of metal; therefore it was decided to continue carburization until the steel was saturated throughout, to remove all graphite from the surface of the specimen, and then to follow the loss of weight during decarburization in a moist hydrogen atmosphere at the same temperature as that used for carburizing. The carburizing procedure has been described in an earlier paper;' it suffices to state here that the carburization lasted about I40 hr. at 760°C. (1760°F.) and 44 hr. at iiio°C. (2030°F.), these periods being long enough-—on the basis of the calculations presented later—to ensure that the specimen was about 99.9 per cent saturated at each temperature. The specimen was a cylinder about 3.8 cm. long and 0.475 cm. in diameter; the materials were carbonyl iron, a commercial low-metalloid iron, and a steel with 3.6 per cent nickel and the usual proportion of other elements. The fully carburized specimen, after cooling at the top of the furnace tube, was placed in a lathe and sandpapered to remove all graphite; then the diameter was measured with a micrometer caliper, and the initial weighing (corresponding to complete saturation) was made. By means of a

Jan 1, 1942

This issue presents the first of several articles making up the Bump Symposium, which was held at the 1958 Annual Meeting of AIME. Other Symposium papers will appear in the September issue of Mining Engineering. THE term mountain bump describes the sudden rupture of one or more coal pillars under excessive stress. These bursts occur with varying degrees of violence and sometimes include adjacent strata, especially the bottom rock. Many failures do not develop enough violence to be dangerous and are regarded as an aid to coal production, but severe occurrences are accompanied by tons of flying coal, dense clouds of dust, and excessive gas emission. Such bursts sometimes throw heavy machinery several feet. Major factors to be considered in the problem are the nature of the strata above and below the seam and the depth of cover. Bumps are classified as to their nature, extent of damage, and point of occurrence, e. g., face bump, coal bump, high side bump, low side pavement bump, and district bump. The problem is extremely complex, and it cannot be over-emphasized that preventive measures, if they are to be successful, must be based on a thorough study of conditions in the individual mine. In western Canada, for example, the McGillivray mine, operating in a 9-ft seam at 2000 ft, has experienced severe bumps, but there have been no occurrences in the International mine, which operates in the same coal seam at 2400 ft, where the coal averages 17 ft thick. Differences in conditions governing the operation of these two mines are described in one of the following articles (see page 883). Again, most bumps in coal mines take place along pillar extraction lines, but at the Sunnyside mine in Utah they also occur a long way from active workings and sometimes in virgin territory. It is usual, too, for such failures to occur under fairly deep cover. But at Sunnyside, to cite only one instance, there have been disturbances along the main fault zone under less than 500 ft of cover. All too often conditions favorable to bumps are revealed only by actual mining—at Springhill No. 2 mine, drilling in roof and pavement strata disclosed a 60-ft sandstone bed after operations had started— and where extraction has advanced too far for preventive measures to be incorporated in the mining plan, districts have had to be abandoned. But in an era when premium ores are being rapidly depleted in the face of rising demands, abandonment is not easily justified. There must be systematic planning to eliminate coal mine bumps, insofar as this is possible. As in the Gary district of West Virginia (see page 888) much has been accomplished by planned operations based on known factors in bump control. But even this is not enough. Precise instrumentation is needed to indicate where bumps are likely to occur, and in both the U. S. and Canada stress analysis studies are being carried out with this object in view. These pages reveal the progress being made.

Jan 1, 1959

By W. S. Gatley, F. C. Appl

This paper presents a combined analytical and experimental study of chisel penetration vs time during chisel impact on rock, a problem of fundamental importance in improving the performance of roller-cone bits or percussion drilling toots. For a given force-time relationship between chisel and rock, the problem of determining the penetration (displacement) vs time of the chisel is formidable. This is so because the rock is a nonlinear system with distributed mass and distributed damping (friction, dissipation of energy due to rupture, etc.). Since the literature does not contain adaptable solutions, the rock behavior to impact was simulated approximately by an "equivalent" lumped system, that is, an "equivalent" mass, spring, dashpot system. With this assumption, an analytical solution was found for chisel penetration vs time due to a sinusoidal load between chisel and rock. From this solution were found curves, in terms of dimension-less variables, for the maximum depth of penetration vs the frequency of the sinusoidal loading and for the energy transfer vs frequency. The results of this analysis were used to predict the penetration rate of rotary rock bits us rotary speed. The curve indicated that an optimum speed exists. To verify this analysis, an experimental apparatus was constructed and used to apply a sinusoidal pulse to a chisel penetrating a rock specimen under atmospheric conditions. Strain gauges were mounted on the chisel shank and a velocity transducer was mounted between the chisel and the rock surface. The velocity was integrated electrically and picked up simultaneously with the strain gauge signal on an oscilloscope. Permanent records were made photographically to provide simultaneous records of force us time and penetration us time. In comparing the experimental results for limestone and dolomite with the theoretical results, good agreement was found in the frequency range of the experiments. Unfortunately, the inertia effect (peak penetration) indicated by the theory occurs at a frequency much higher than could be obtained experimentally with the apparatus constructed. A "rate-of-loading" effect is indicated theoretically, but has not yet been verified experimentally. INTRODUCTION The process of drilling with percussion tools or rotary rock bits is basically related to the transient response of rock to surface impact. Each time a bit tooth contacts the rock, high stresses are developed which result in penetration and rock removal. As the tooth moves on, stresses are relieved and a new cycle begins as the next tooth contacts the rock. Thus the drilling process, which consists of an endless succession of these cycles, can be studied in terms of a single cycle. It is apparent, therefore, that the study of single-chisel impact on rock is fundamentally important in improving the performance of roller-cone and percussive-type drills. Previous studies in this area have been conducted by Simon1 and Hartman2 by means of drop tests. In these tests a chisel was attached to a weight and allowed to fall, due to the force of gravity, so that the chisel was driven into a rock specimen upon impact. Strain gauges were attached to the chisel shank and the resulting force-vs-time curves were recorded photographically from an oscilloscope screen. The depth of penetration and crater dimensions were also measured. These tests have provided much valuable information but, as mentioned by the investigators, have not provided complete information on the effect of "rate of loading'! This is partly due to the fact that the chisel motion during drop tests is not a controlled motion which can be varied in form and frequency. Therefore, it seemed that additional information could be obtained by studying chisel impact under conditions where both the motion and the frequency of loading could be controlled. This paper presents a combined analytical and exper-

By Nicholas J. Grant, A. W. Mullendore

Measurements of grain boundary sliding were made on polycrystal and bicrystal tensile creep specimens of Al-2 pct Mg at 500oand 700oF. Grain and pain boundary orientation factors were studied with respect to their effect on the magnitude and direction of grain boundary sliding. It was concluded that a large part of the observed sliding may be caused by the operation of slip crossing the grain boundaries. Supporting evidence for this model from other investigations is also given. GRAIN boundary sliding in metals during elevated temperature deformation has frequently been thought of as an independent mechanism with its own characteristic stress, temperature, and structure dependence. Further, it is common to regard the grain boundary as the weak link during creep deformation since: 1) the strength of apolycrystallinemetal, as meas-sured by creep rate or rupture life, decreases at\a more rapid rate when sliding comes into action, and 2) grain boundary sliding, as revealed by "boundary darkening" and fold formation is often the first visible deformation. On the other hand, more quantitative observations, in both polycrystals and bicrystals, have shown boundary deformation to be closely related to the over-all deformation of the specimen. The curve of grain boundary contribution to elongation vs time takes a shape similar to that of the total creep curve,',' and the apparent activation energy for sliding appears in most cases to have the same value as that for total creep.3 In order to reconcile these observations, one is left with these possibilities: 1) The grain boundary and grain deformation rates are both controlled by the same rate limiting processes. 2) The rate of sliding is limited by accommodation deformation in the grains. 3) Sliding is the consequence of grain deformation. 4) Grain deformation is dependent on prior grain boundary deformation. Alternatives 2) and 3) would view grain boundary sliding as occurring in series with another deformation process which could be rate controlling. McLean prefers item 3) as the sliding basis,4 where subgrain rotation results from dislocation accumulation in the substructure at the grain boundary. Crussard and Friedel's5 treatment of grain boundary migration considers that dislocations are forced into the grain boundary and are dissociated into dislocations with Burgers' vectors nearly parallel to the grain boundary. The movement of these partial grain boundary dislocations then produces the sliding. The results of this investigation have indicated alternative 3) to be the most appropriate and it is this aspect of grain boundary sliding which will be analyzed. EXPERIMENTAL PROCEDURE Three types of tensile creep tests were employed in this study: (I) A constant load test of one very coarsegrained polycrystalline specimen at 500° F, 3600 psi, 1 pct per/hr strain rate to examine the grain and grain boundary orientation factors in grain boundary sliding. (II) Constant strain rate tests of polycrystalline specimens at 510o and 715o F, 2 pct per/hr strain rate to determine the grain boundary contribution to elongation at very low total strains. (m) Constant strain rate tests of bicrystals of various grain and grain boundary orientations at 500°F, 2 pct per/hr strain rate to obtain further information on the orientation effects in grain boundary sliding. The material used in the tests was a high-purity Al-1'.92 mg alloy, kindly furnished by Alcoa. Its composition is given in Table I. The alloy is a solid solution at the test temperatures. The coarse grained polycrystalline specimen for test (I) was prepared by recrystallizingthe machined specimen, straining it about 1pct intension at room temperature and annealing at 900°F for 8hr. The constant strain rate specimens (11), with an 178 in. sq. by 1/2 in. long gage section, were cut from 1/8 in. thick sheet of cold rolled and annealed (8 hr at 1000oF) material. The latter specimens were supported in a special jig during the milling operations to avoid any bending, and the gage section was subsequently heavily electropolished to remove the cold-worked surface layer. The bicrystals (ID) were machined in the same

Jan 1, 1963

By JOHN A. MALONEY

AS noted in the February issue of MINING AND METALLURGY, an advisory committee to the Museum of Science and Industry of Chicago was authorized by the Institute's Board of Directors, with W. R. Wright of Chicago, former Director of the Institute, as chairman. Since that time the committee has been undergoing organization, and held its initial meeting at the Museum offices in Chicago on April 11 and 12. Functioning as consultants to the Geology and Mineral Industries branch of this new institution, the advisory committee is aiding in building an exhibit which will tell the story of geology, mining, and metallurgy to millions of visitors a year. Although patterned to some extent

Jan 1, 1932

By Augustus Locke

San Francisco Meeting, October, 1911.) Two Opposed Interpretations of the Tonopah Structure.-The important geological publications concerning the Tonopah mining-district are those of Spurr 1 and of Burgess.2 In these publications are presented fundamental differences of interpretation, which are the more interesting because both authorities have had ample opportunity for observation, and because both are geologists of proved ability. I was vastly puzzled to know which had the better of it, and in order that I might reach a conclusion in my own mind, I recently spent some time in the district going over the physical evidence. Surprising as it may seem, this evidence looks agreeably conclusive. A review of it will, I believe, be of interest to those who are familiar with the previous publications. The general geological features of Tonopah are shown in Fig. 1, and the differences of interpretation referred to are outlined in the accompanying notes. Briefly, Burgess regards the various rocks as flows, lying in the order of their deposition. Spurr regards them in part as flows, and in part as flat-lying intrusives. The disagreement, then, concerns the rocks regarded on the one hand as intrusives, and, on the other hand, as flows. These rocks are chiefly the so-called calcitic andesite, the upper rhyolite, and the lower rhyolite. Economic Importance of the Question of Interpretation.-The economic importance of the question of interpretation is, of course, limited to its bearing on the probable distribution of 1 Geology of the Tonopah Mining District, Nevada, Professional Paper No. 42, U. S. Geological Survey (1905). Report on the Geology of the Property of the Montana-Tonopah Mining Co. (1910). An abstract of this report is given in the Mining and Scientific Press, vol. cii., No. 16,p. 560 (Apr. 22, 1911). 2 The Geology of the Producing Part of the Tonopah Mining District, Economic Geology, vol. iv., No. 8, pp. 681 to 712 (Dec., 1909).

Feb 1, 1912

By K. R. Carson, J. Weertman

An attempt is made to ascertain the mechanism of tangle and cell formation and its dependence upon dislocation-interstitial carbon interactions. The strain-hardening behavior of single crystals of 3.25 pct Si-Fe was determined at 300° and 425°K and under conditions of both continuous and interrupted tensile strain. Significantly enhanced hardening was observed in crystals deformed at the elevated temperature, and it was further accentuated by interrupted straining. Transmission electron microscopy was used to study the resultant dislocation structures. Strain aging was found to aid tangle and cell formation at 425°K, but at both temperatures embryo tangles formed solely from primary glide dislocations, presumably by a process involving cross slip and "mushrooming". IN the course of plastic deformation all bcc metals and alloys develop a dislocation structure characterized by loose-knit groups of tangled dislocations. With increasing strain the tangles become more tightly knit and grow larger; finally a three-dimensional cellular substructure is formed:1 This process has been observed with the transmission electron microscope.'-l7 However, most investigations were confined to the study of nearly pure polycrystalline metals at relatively low temperatures. At intermediate temperatures, 0.17 to 0.14 Tm where T, is the melting temperature in degrees absolute, the mobility of interstitial impurities such as carbon is high enough to permit migration to nearby glide dislocations but is still low enough so that a significant drag force is exerted.18,19 it is also in this temperature range that a hump occurs in the curve of work-hardening rate vs temperature for iron. Analogous plots for tantalum" and columbiumzo show a definite upward trend in the work-hardening rate. Keh and Weissman1 have pointed out that this behavior may be explained solely on the basis of changes in the dislocation configuration: at low temperatures the dislocations tend to be relatively straight and uniformly distributed, but at intermediate temperatures tightly knit tangles and cellular substructure appear. The interference of these tangles with glide dislocations causes the observed increase in the work-hardening rate. This explanation appears reasonable, yet one might ask what factors cause tangle formation to be so favorable at intermediate temperatures. It seens likely that the strong dislocation-interstitial interactions which are known to occur in this temperature range are at least partly responsible," with the magnitude of the effect being proportional to the interstitial concentration. The purpose of the present work is to study the relationship between tangle formation and strain hardening in a bcc metal in the temperature range 0.17 to 0.4 Tm. Particular emphasis was placed upon a study of the effects of interstitial-dislocation interactions. Single crystals of 3.25 pct Si-Fe containing about 200 ppm of C in solid solution were used in the investigation for the following reasons: 1) The mobility of interstitial carbon in 3.25 pct Si-Fe is negligible at 300°K but increases rapidly at slightly elevated temperature22. Hence, differences between the flow curves and dislocation structures of crystals deformed at 300°K, 0.17 T,, and crystals deformed, say, at 425°K, 0.24 Tm, should be appreciable because of the enhanced dislocation-carbon interactions at the elevated temperature. This effect was accentuated in some samples by interrupted straining, thereby introducing a certain amount of aging. 2) Near room temperature, slip in suitably oriented 3.25 pct Si-Fe single crystals is largely confined to the (110) planes.23'24 Dislocation structures formed under conditions of single glide are the least complicated and their method of formation is the most easily discernable. 3) Dislocations in Si-Fe can be tightly locked with carbon atmospheres by a low-temperature aging treatment. The subsequent thinning of samples to foil thicbess causes little or no rearrangement in the dislocation structure.25 EXPERIMENTAL PROCEDURE Large single-crystal sheets of 3.25 pct Si-Fe were donated by Dr. C. G. Dunn of the General Electric Research Laboratory, Schenectady, N. Y. The orientations of the sheets were determined and slabs 1.0 by 0.25 by 0.05 in. were cut such that the desired tensile axis corresponded to the long dimension. The slabs were mechanically polished and subsequently decar-burized by heating at 1000°C for 3 days in a flowing wet-hydrogen atmosphere. A carbon content of about 200 ppm was introduced by heating at 805°C for 25 min in a flowing atmosphere of dry hydrogen containing heptane vapor. Shaped copper tools were then used to spark-machine at 0.125 by 0.50 in. gage length onto each slab. Vacuum annealing at 1225°C for 2 days followed by a quench into the cold end of the furnace to retain carbon in solid solution concluded the soecimen preparation. Continuous tensile flow curves for crystals of severa1 orientations Were obtained both at 300' and 425°K. A strain rate of 6.67 x 10-4 Per set was used in these and all other tests. Crystals oriented for single glide, B and D in Fig. 1, were subjected to a 3.5 pct plastic elongation to insure uniform slip along the gage length; they were then immediately subjected to interrupted strain cycling as indicated in Fig. 2(a). Each cycle consisted of unloading to 1.5 kg per sq mm, holding

Jan 1, 1969

By Geo. W. Bain

PRODUCERS of building stone have had to seek new and attractive uses for their output to supplement the diminished orders for standard products. Lunar is the direct result of the need of new outlets for marble and is. probably the most ingenious and attractive type to reach the market in a quarter of a century. It is a highly translucent stone which retains the same glistening sparkle in transmitted light that marble exhibits by incident rays. This sparkle sets it apart entirely from translucencies made of glass or even onyx, alabaster, and the distinctive exceedingly fine textured calcite marbles produced in Alabama and quarried formerly in northern Vermont and Quebec.

Jan 1, 1936

By C. S. Matthews, H. C. Lefkovits

Drilling progress is often delayed by sticking of the drill string. The development of preventive and remedial methods has been hampered by incomplete understanding of the sticking mechanism. A recent lahorntory investigation hns indicated that one type of sticking may be attributed to the difference in pressure between the borehole and formation. This paper shows, by means of soil mechanics, that the primary cause for differential pressure sticking is cessation of pipe movement, whereas diflerential pressre and stanrtding time determine the severity of the sticking. The analysis stresses the importance of using low-weight muds with low solids content and low water loss to alleviate diflerential pressure sticking and describes why packed hole drilling, long strings of drill collars, and a large deviation from the vertical are conducive to sticking. Finally, preventrve and remedial methods ore evaluated, and a theory is presented on the release of stuck pipe by spotting oil. INTRODUCTION Since drilling with long strings of oversize drill collars has become standard practice in many areas, the incidence and severity of the stuck pipe problem has increased. It has been noticed that in the majority of these cases the sticking could not possibly be attributed to key seating or caving of shales. It appeared that, due to the differential pressure between the mud column and the formation fluid, the collars were pressed into the wall and so became "wall stuck". Points to note about differential pressure sticking are: (1) sticking is restricted to the drill collars, (2) the collars become stuck opposite a permeable formation, (3) the sticking occurs after an interruption of pipe movement, (4) circulation, if interrupted, can be restarted after the sticking is noticed, and (5) no large amounts of cuttings are circulated out after restarting circulation. Helmick and Longleyl investigated pipe sticking by differential pressure in the laboratory and found an empirical relationship between the differential pressure, the sticking time and the required pull-out force. In this paper an explanation of the mechanism is given based on Terzaghi's theory of clay consolidation. A qualitative description is given in the following paragraphs while the derivation of fonnulas is given in Appendices. This paper is a first attempt to explain pressure differential sticking and many points will require additional theoretical and practical investigation before the problem can be fully understood. PRESSURE DIFFERENTIAL STICKING AS A CONSOLIDATION PROBLEM In any borehole, where the mud pressure is higher than that exerted by the formation fluids, a mud cake is formed opposite the permeable sections of the hole and a continuous flow of filtrate takes place from the mud, through the cake and into the formation. This radial flow pattern requires a certain distribution of the hydraulic and the effective (grain-to-grain) stresses inside the mud cake. Any quantitative or qualitative change in the external pressure conditions will produce a change in the flow pattern and, consequently, also in the internal stress distribution inside the cake. In view of the low permeability and the high compressibility of a clay mud cake, the adjustment of the internal stress distribution is slow and is accompanied by a change in volume. Time dependent stresses are thus created which gradually diminish as the new state of equilibrium between internal and external pressures is approached. Some 30 years ago, Terzaghi developed his "Theory of Consolidation" to account for the time-dependent stresses and settling of clay formations under the influence of external loads. He derived a differential equation by which the time-dependent hydraulic stress and the consolidation can be computed for any point inside the layer during the consolidation process. His theory is based on the assumption that the change in stress is solely due to a change in water content and it may only be applied to one-dimensional consolidation phenomena. Other investiga-tors5,10 have expanded his theory to include processes of more than one dimension. The difference between the external pressures on the mud cake before and after sticking is a qualitative one (isolation of part of the cake by the static contact with the drill collars after pipe movement has been stopped)', and the time-dependent stresses thus created may be investigated by means of Terzaghi's theory. By this analysis the changes in the nature of the contact surface between the drill collars and the mud cake during the sticking can be explained; and the friction force between the two may be computed as a function of the sticking time, the borehole dimensions and the mud cake characteristics.

By R. L. Fleischer, W. F. Hosford

Tensile data for coarse grained aluminum Polycrystals suggest that the "grain size" effect is not due to dislocations piled up at grain boundaries but rather is primarily a relative size effect due to surface crystals being weaker and less confined. STUDIES directed at interpreting hardening of poly-crystalline metals normally identify their strain hardening properties with those in some particular type of single crystal.1"4 The recent recognition in face centered-cubic metals of a nearly linear stage with rapid hardening occuring at comparable rates for both polycrystals and single crystals, suggested that the same process or processes determine both cases and hence that there exists some justification for the use of single crystals to understand polycrystals. Further evidence for the above view may be found by an approach initiated by Chalmers:5 By using bicrystals of controlled orientation it is possible to begin to assemble a polycrystal and also to study grain boundary effects in detail. In this way it has been found that a single grain boundary affects easy glide but not the subsequent stage II hardening.6 This result suggests that a sensitive way to observe grain boundary effects in polycrystals would be to vary grain size and measure easy glide. As will be seen, easy glide is only possible for coarse-grained samples, and hence the results will serve to fill in the gap in measurements between single crystals and bicrystals on one hand and fine-grained polycrystals on the other. One problem inherent in comparing single crystals with polycrystals is the uncertainty as to what slip systems are acting in a polycrystal. To compare the two types of samples, rates of shear hardeninn---L. on the acting -planes are needed. and these may be computed only if it is known what particular systems are active. The acting systems were examined for a coarse-grained polycrystal and it will be shown that the systems supplying the preponderance of slip can be determined with little ambiguity. EXPERIMENTAL PROCEDURE Twelve samples of aluminum were prepared by chill casting into a heated graphite mold, followed by annealing at 635° ± 5°C for 24 hr with an 8-hr fur- nace cool, and finally either etching7 or electropol-ishing.' The samples, with a 7 to 10 cm length between grips and 4.4 by 6.6 mm in cross section, were deformed at a strain rate of about 3 10 -3 . per min in a tensile device which has been described elsewhere.5 The composition was reported by Alcoa as 99.992 pct Al, 0.004 pct Zn, 0.002 pct Cu, 0.001 pct Fe, and 0.001 pct Si; nine samples were deformed while immersed in liquid helium and three in air at room temperature. The stress-strain curve for one of the samples (P-1) deformed at 4.2 "K has been reported previ~usl~.~ This sample was selected for determination of active slip systems. Eighteen of the crystals were examined by optical microscopy to determine the angles of slip line traces and by X-ray back reflection to determine orientation. By this means the slip planes were determined and the resolved shear stress factors for possible slip systems could be computed. Finally each sample was sectioned so that after etching, the number of crystals could be counted for each of ten newly exposed surfaces. The average of these ten values will be termed n, the number of crystals per cross section. Values of 11, varied from 1.9 (nearly bamboo structure) to 12.7. Sketches of typical cross sections appear in Fig. 1. RESULTS AND DISCUSSION: SLIP SYSTEMS 1) Determination of Acting Slip Planes—The stress axis orientation and operative slip planes in eighteen crystals of sample P-1, as determined by slip line traces and crystal orientation, are summarized in Fig. 2. For one of the crystals two planes had a common trace. so that the traces alone did not distinguish which plane or planes were slipping. However it was found that the stress resolving factor for the primary system was 0.386, .while that for the most stressed system in the other plane (indicated bv the dotted arrow) is 0.138. It will be assumed tgerefore that only the primary plane acted. Since the orientations were determined after extending the samples 4 pct, the stress axes may be rotated from their original value by as much as 2 deg in some cases. It is interesting to note that in five crystals only one slip plane acted, in eight two acted, and in five three planes were observed—an average of two slip

Jan 1, 1962