Search Documents

By Ross C. Anderson, William I. Weisman

THE manufacture of anhydrous sodium sulphate or salt cake from natural deposits in the United States has been in general somewhat of a marginal undertaking. Competition from foreign sources and from large quantities of byproduct sodium sulphate produced domestically in the manufacture of hydrochloric acid and other chemicals has existed and continues. For example, most of the sodium sulphate produced is a byproduct or co-product in the manufacture of hydrochloric acid through the reaction of sodium chloride with sulphuric acid. In recent years, many manufacturers of rayon have installed equipment to recover sodium sulphate from waste spin bath liquors; today this is an important source. Before World War II large quantities of sodium sulphate were imported from Germany. In 1949 imported material from Europe again appeared on the domestic market. Natural sodium sulphate from Canada in substantial quantities also enters the United States markets. Despite this kind of competition, numerous attempts have been made to exploit various natural deposits of sodium sulphate in this country, but only a very few of these have survived economically over a period of years. One of these few operations is the plant of the Ozark-Mahoning Co. located 13 miles south of Monahans in West Texas. Several factors contributing to the successful life of this plant may be summarized as follows: 1—Geographical location. Monahans is reasonably close, freightwise, to the Kraft paper mills in Texas, Arkansas, and Louisiana; the Kraft paper industry is the greatest consumer of sodium sulphate in the United States. 2—Availability of natural gas as low cost fuel. Proximity of the natural gas fields of West Texas has been a tremendous asset, as the availability of low-cost natural gas is to all industry throughout the Southwest. 3—The nature of the deposit. The occurrence of sodium sulphate brines in southeastern New Mexico and West Texas has been very well described by Lang,' who writes that the brines are found in the Castile formation of the Delaware basin. Here weathering has altered the anhydrite so that a relatively porous gypsiferous zone overlies a dense impervious mass of anhydrite. This porous zone provides traps where percolating ground waters that have picked up soluble salts may lodge. These traps or pockets are the natural brine reservoirs exploited at Monahans. Although several hundred wells have been drilled, currently some 25 wells serve to supply brine to the plant. All are within 1 1/2 miles of the plant and are conveniently tied together by an electric power system serving electric motors driving the pumps. Having the raw material in the form of a brine which can be pumped from shallow wells makes possible much simpler and more efficient handling than if it were in form of solids. By contrast, other deposits of sodium sulphate, such as those in Arizona, Nevada, and North Dakota, are in the form of the solid minerals, thenardite and mirabilite, which present somewhat more of a mining and mineral dressing problem.' The largest producer of sodium sulphate from natural sources in the United States is at Searles Lake, Cal., and there a brine also is utilized. 4—Water. Substantial quantities are needed for cooling towers and for operation of gas engines. An area underlain with brine is not a promising source of fresh water, but fortunately, after a long search, an adequate supply was found nearly two miles from the plant. It may be appropriate to discuss briefly the grades of sodium sulphate offered on the market. Salt cake is the name usually applied to the grade of sodium sulphate used by the Kraft paper industry. It may be a low analysis byproduct, 95 to 97 pct sodium sulphate, with as much as l 1/2 to 2 pct residual acid, or it may be a natural product. Usually salt cake is considered a low grade product, but a great deal of a higher grade of material is marketed under this name. The specifications for glassmakers' salt cake are somewhat higher than those of the paper industry, usually requiring 98 pct sodium sulphate. Technical anhydrous sodium sulphate is a high grade material and usually exceeds 99 pct sodium sulphate. It finds the biggest market in the textile industry and is used as a builder in some synthetic detergents. Glauber's salt, Na2SO4. 10H20, is usually of high purity. Preferred for some uses, it normally has been recrystallized from an anhydrous salt. A unique manufacturing process has been developed at Monahans. This process results in the production of an exceptionally high grade of salt cake, and qualifies for nearly all uses, including many which specify the technical anhydrous grade. All of the finished product, which is very white, passes a 10-mesh U. S. Standard screen, and is retained on a 200-mesh U. S. Standard screen. It is over 99 pct Na2SO4 with main impurities being sodium chloride and magnesium sulphate. Iron content is less than 0.01 pct. As mentioned, the raw material at Monahans is a brine drawn from wells. Attention was first attracted to this location because a so-called alkali

Jan 1, 1954

By Jei Y. Choi, Paul G. Shewmon

The surface self-diffusion coefficient of copper (D,) has been measured between 847° and 1069 "C for six different orientations. These were the(111), (110, (100, and three higher index surfaces. The activation energy for Ds (designated Q s) was found to be about 49 kcal per mol for all six surfaces, and Do about 2 x 104 sq cm per sec. At any temperature Ds varied by no more than a factor of three over these orientations. It is shown that, if the free energy of a surface atom is uniquely determined by its number of nearest neighbors, it follows from the Principle of microscopic reversibility that Qs should have the same value for all surface orientations, and Ds should vary little with orientation. This model also suggests that for clean fee metals Qs ~ 2/3 AH, (heat of vaporization). This is true for copper. ALTHOUGH it has been appreciated for several decades that atoms can diffuse more rapidly on a surface than through the bulk of a crystal, it has only been in the last few years that reliable values of the surface self-diffusion coefficient (Ds) have become available. Tracer studies of Ds had been attempted prior to this period, but when a tracer is placed on a surface, an ever increasing fraction of it is drained off into the lattice. The correction for this loss involves a very difficult, and as yet unperformed calculation. Those who have worked with tracers have not corrected for this loss.1, 2 Thus their results indicate that Ds is greater than the self-diffusion coefficient in the lattice (Dl), but it has not been established that they give quantitative data on Ds. A procedure which avoids the problem of tracer loss is to study the rate of mass-transfer under the effect of surface tension. If the surface asperity being studied is very small, the mass transfer occurs entirely by surface diffusion. The kinetics at which a grain boundary groove forms on an initially plane surface is a well-studied case of this type. The smoothing of a slight scratch in an otherwise flat surface is another procedure that has been studied. If these grooves are up to 20 to 30 µ in width, the dominant mechanism for mass transfer is surface diffusion (at least in the case of metals with low vapor pressures), and the widths can easily be measured with an interference microscope. Of these two, mass-transfer techniques only in the case of grain boundary grooving has a rigorous mathematical treatment been given. This was done by Mullins.3,4 His analysis predicted that in the case of copper in an atmosphere of an inert gas, surface diffusion should be the dominant transport mechanism. This analysis gave an equation for the groove profile and predicted that the width of the groove would increase as (time)1/4. Mullins and Shewmon showed that both of these predictions agreed with experiments.5 Thus the validity of the values of Ds given by this procedure seems to be well established. Gjostein has used copper bicrystals and the grain boundary grooving technique to determine Ds and the activation energy for surface selfdiffusion (9,) in the [001] direction on surfaces ranging between the (100) and (110) planes.= He reported that Qs = 41 kcal per mole and Do = 6.5 x 102 sq cm per sec for all orientations studied. Since the results did not change with the dew-point of the dry hydrogen atmosphere or the type of refractory tube used, he concluded that the surfaces were clean, or at least that the results were not influenced by any impurities chemisorbed from the atmosphere. The work reported here reproduces and extends Gjostein's study in that D s and Q s were determined for copper over a wider range of orientations. To study the effects of impurities, two purities of copper were used as well as cathodic etching to remove any possible electropolishing film. Gjostein postulated that the diffusing atoms on a surface near a low index plane are the few atoms which are adsorbed on the smooth region between ledges or steps in the surface. A more rigorous derivation of the equation relating Ds to the concentration and jump frequency of these adsorbed atoms is given here. Using this treatment, our empirical observation that Q s and D s are essentially the same for all surface orientations can be shown to follow from the assumption that the free energy of a surface atom is uniquely determined by its number of nearest neighbors. The studies of D s using the scratch technique have been carried out by Blakely and Mukura on nickel,' and by Geguzin and Oveharenko on copper. The latter study using copper gives values of D s roughly

Jan 1, 1962

By K. E. Gray, G. M. Myers

In previous publications,5 results of single-blow bit tooth impacts on saturated rocks at various stress states were reported. This paper extends these earlier works to include study of bit impact tests on salt water-saturated Berea and Bandera sandstone samples under conditions of elevated confining and pore pressure. During the tests dynamic filtration and deposition of a mud cake were occurring due to the presence of drilling mud in the borehole and a borebole-to-formation pressure differential. Results indicate that saturation of these sandstones with salt water tends to make them weaker than when saturated with nonreactive fluids. Plastic failure often occurs even when extremely high fluid-loss muds are present in the borehole. The failure mode tends toward plasticity with decreasing fluid loss. Brittle failure of sandstones in mud-filled holes is apparently relatively rare. Depending on the stress level, and the associated failure mode, withdrawal of the bit tooth induces a tensile force that seems rather important relative to the quantity of rock removed by vertical tooth impact. INTRODUCTION A vast majority of the oil wells drilled today involve the use of colloidal muds having a measurable mud filtrate loss. It is known from field experience that reduction of the water loss of a mud generally results in a reduction of the penetration rate. This paper describes an investigation of crater formation at simulated bottom-hole pressure conditions for drilling fluids having different water losses. The literature on single bit tooth impact (cratering) at atmospheric conditions is extensive, but only a limited amount of work has been performed at the stress conditions similar to that found in oil wells. Spherical penetrator cratering tests on rocks at hydrostatic pressure were performed by Payne and Chippenda1e.1 Chisel impact studies on limestone with independently varying overburden and borehole pressure and atmospheric pore pressure were reported by Garner, et al.2 Gnirk and Cheatham3 performed "static" penetrator tests on dry rocks at equal overburden and borehole pressures. Podio and Gray4 studied the effect of pore fluid viscosity at atmospheric pore and borehole pressures and varying overburden pressures. Their results illustrated the importance of fluid saturation of the rock. Yang and Gray5 reported single tooth impact tests on saturated rocks at elevated borehole, pore and confining pressures, but with equal pore and borehole pressures. For the work reported in Refs. 4 and 5, filtration across the hole bottom purposely was avoided. Maurer6 has investigated the effect of independently varying pore and borehole pressures at elevated overburden pressures by using a zero water-loss mud in the borehole. His tests were carried out under conditions that allowed independent control of overburden, pore and borehole pressures, but without control of filtration at the hole bottom. EXPERIMENTAL APPARATUS AND PROCEDURE APPARATUS The single blow chisel impact apparatus used by Garner,2 as modified for this study, is shown in Fig. 1. A cross section of the pressure vessel is shown in Fig. 2. Several pieces of auxiliary equipment were added to the original apparatus in order that the borehole and pore pressure could be applied in a manner analogous to the actual bottom-hole situation. The pore-pressure system included a filtrate volume-measuring transducer and had sufficient surge capacity to allow filtrate to be injected into the sample without significant changes in pore pressure at points remote to the borehole. The borehole-pressure system contained a cross connection to the pore-pressure system so that both systems could be pressured simultaneously. The borehole-pore pressure differential was applied rapidly by the use of a quick and full-opening valve. The operation of this valve triggered two industrial

Jan 1, 1969

By F. W. Schremp, J. W. Chittum, T. S. Arczynski

This paper describes a laboratory study of causes of external casing corrosion and the test work that led to the use of oxygen scavengers to prevent this attack. External casing failures are classified as water-line, casing-casing, collar and body failures. A corrosion mechanism based on principles of differential oxygen availability is developed that is consistent with facts known about each kind of failure. The field use of oxygen scavengers is depicted as a direct result of the laboratory study. A part of the paper is devoted to reporting on the field use of hydra-zine to control external casing corrosion. Results of field measurements made over a period of several years are presented as evidence of the efectiveness of the hydrazine treatment. The first conclusion reached is that the use of hydrazine materially reduces the cathodic protection requirements for treated wells. This result is interpreted to mean that a reduction is taking place in the amount of corrosion on the casing. Results indicate also that hydrazine shows its greatest usefulness within the first 12 to 18 months after a well is completed when pitting corrosion is likely to be most active. INTRODUCTION According to surveys sponsored by the National Association of Corrosion Engineers,' the cost of repairing casing leaks caused by external corrosion may exceed $4 million per year. In addition, well damage and lost production resulting from casing leaks probably costs the petroleum industry an additional $5 to $6 million per year. Concern about the cost of external casing corrosion led to an extensive laboratory study of factors causing this external corrosion and to the development of a new approach to its prevention. This paper presents a discussion of various causes of external casing corrosion, details of laboratory studies and the results of the field use of an oxygen scavenger in well cementing fluids to prevent the external corrosion of oil-string casing. Measurements on test wells over a period of several years show that cathodic-protection current requirements are greatly reduced when hydrazine is used in cementing mud. Reduction of current requirements can be interpreted to mean that removal of oxygen by hydrazine has greatly suppressed corrosion cells on the external surface of the casing and thereby, has reduced corrosion. To date, hydrazine has been used by the Standard Oil Co. of California in more than 200 well completions. KINDS OF CASING FAILURES A survey of a large number of casing leaks disclosed four types of external casing failures — water-line, casing-casing, collar and body failures. These types are identified largely by their location on the casing. Water-line failures are found just below the surface of water or mud in the casing annulus. Casing-casing failures occur on the oil string just below the shoe of the surface string. Collar failures are found in the threaded ends of casing joints where they are screwed into casing collars. Body failures may occur at any point on the body of a casing joint. Ex- amples of each kind of failure have some of the general characteristics that are shown in Fig. 1. Water-line failures usually result in the circumferential severance of an oil-string casing. The corrosive action causing a water-line failure usually is sharply defined and is limited to a short length of the casing. Casing-casing failures usually are accompanied by pitting corrosion distributed around the oil-string casing for distances up to 100-ft below the shoe of the surface string. Casing-casing failures may also sever the casing. Collar failures seem to start on the first thread at the bottom of recesses between collar and casing joint. Corrosion proceeds across the threads by what appears to be a normal pitting mechanism. Both casing and collar are severely attacked. Body failures are the result of highly localized pitting at any point on a casing wall. Besides the pit that perforates a casing, a large number of other pits usually are found along one side of the casing joint. The pits occasionally are filled with corrosion products consisting largely of oxides and sulfides.' Frequently, the mill scale is largely intact on the rest of the casing. Examination of a casing failure does not always reveal the cause of the failure. Frequently, the necessary details are destroyed when the failure occurs. For example, formation water flowing through a perforation at high velocity may enlarge the hole and destroy any remaining evidence of the cause of the failure. One way to obtain undistorted information about a failure is to study the nature of other pits on the casing in the vicinity of the failure. A study of such pits frequently suggests that they are characteristic of an attack resulting from the differential availability of molecular oxygen.

By A. Hultgren, B. Herrlander

The original aim of the present investigation was to study the mechanism of cracking on hot-deforming red-short steels. During the microscopical examination of hot-deformed soft steels attention was directed to various patterns of so-called veining in the ferrite, as related to variations in the deformation procedure and the heat-treatment of the steels. Later, a hot-short steel of higher carbon content was also studied. Historical Storey1 suggested in 1914 that veining developed during the gamma-alpha transformation from the growing together of several alpha nuclei within the same gamma grain. Rawdon and Berglund2 found that in soft steel, forged somewhat below A3, the ferrite showed profuse veining, while usually there was very little veining after forging at very high temperatures. They emphasized the similarity between the pattern of veining formed by deformation about 600°C and that of slip lines formed by deformation at room temperature. They also suggested a relation between the gamma-alpha transformation and veining. They became convinced from etching and from the slip-line pattern in cold-deformed material, that the orientation within any ferrite grain showing veining was uniform. In recrystallized alpha grains veining was absent. Veining did not appear materially to affect the properties of ferrite. Independent of veining, continuous networks, attributed to preexisting delta and gamma grain boundaries were sometimes found, the former only in cast steel. Those networks were usually connected with small inclusions. Ammermann and Kornfeld3 confirmed that recrystallized ferrite grains showed no veining. In soft steel annealed between A1 and A3 there was veining only in the ferrite grains formed during cooling. Electrolytic iron deformed at 880' was free from veining. Bannister and Jones' considered veining in ferrite to be a manifestation of microscopical and sub-microscopica~ inclusions. NorthCOtt,5,6 in studies on veining in steel and other metals and alloys, attributed veining to oxide inclusions. It could generally be removed by annealing in hydrogen, a suggestion earlier made by Rawdon and Berg1und. TrittOn (discussion in ref. 5) emphasized the importance of perfect polishing for bringing out veining by etching, and thought the veins or subboundaries were produced during the gamma-alpha transformation, when it was rapid, as a result of the volume change and contraction during cooling. Slight distortion would not allow projecting parts of a growing crystal to join up with atomic symmetry. Hanemann and co-workers showed that veining in ferrite consisted of ridges

Jan 1, 1948

By J. H. Henderson, T. E. Morrisson

An irvestigation has been made of the production of oil through horizontal fractures of high capacity and large radius placed at the base of producing formations. The specific aitns of the study were to (I) determine by model studies the reservoir performance when gravity drainage is the only producing mechanism, and (2) develop a method of predicting such perfortnance from commonly measured reservoir proper-ties. Although the theoretical approach tailed to develop a rigorous analytic sorution to the transient problem, it (lid lead to a practical method of predicting performance. Predictions (Ire in good agreement with rates and recoveries observed in scaled-model experinzents. Capillary effects and the influence of relative permzenbil-ity are taken into account. The experimental program was mainly concerned with the influenre of fracture radius, fracture capacily and capillary hold-up on the total recovery and the rate of recovery. Much of the experimental work was done on a triangular model which represented one-eighth of a square well pattern, so constritcted that horizontal fractures of varying radii and flow capacity could be studied. An electrolytic model was used to relate the initial production rates to fracture radius, formation thickness and the drainage radius of the well pattern. The conclusions reached as a resrtlt of the work are as follows. I. The production of oil under gravity force alone into a well-propped horizontal fracture, whose radius is of the order of hundreds of feet, is a recovery method which combines high recoveries with very acceptable production rates. 2. The mechanism is effective in "dead oil" reservoirs as well as in reservoirs which possess the energy of solution gas. 3. A method of predicting performance has been developed which gives good agreement with experimental behavior in cases of practicnl interest. Even for very thick beds and large fracture radii, where actual conditions do not conform to the assumptions made, the method gives order of magnitude predictions which would not otherwise be possible. INTRODUCTION Gravity drainage of oil from a formation which has continuous ver- tical permeability over a reasonable depth interval is a surprisingly effective method of recovery. However, for a conventional well the production rates which result from gravity drainage are so low that the economics are seldom attractive. The same formation may produce rapidly and profitably by gravity alone through a high capacity, extensive (i.e., > 100-ft radius) horizontal fracture placed near the bottom of the pay section. Fig. 1 shows a schematic diagram of the plan. Energy in the reservoir gas is not a necessary condition for this recovery process. With a sufficiently large fracture, attractive production rates will result from gravity flow alone, and the producing GOR need only be the solution GOR. It is, of course, necessary to keep the fluid level in

By Y. A. Rocher, J. E. Dorn, L. A. Shepard

Creep activation energies for single aluminum crystals favorably oriented for shear by (010) [101] glide were detemined over the temperature range from 78" to 900°K. Observations of slip bands on the specimen surface were made in conjunction with the investigation. From 78" to 780°K, the activation energies obtained in this imestigation agreed closely with those previously found for creep by (111) [101] slip. Between 78" and 140°K, the activation energy was identified with the Peierls process, while between 260°and 780°K the activation energy was close to that for cross-slip. The coarse wavy slip bands nominally parallel to the (010) plane observed above 260°K were attributed to fine cross-slip. From 800" to 900°K, unusually high apparent activation energies ranging from 28,000 to 54,000 cal per mole were obtained. These apparent activation energies were attributed to re crystallization. AS illustrated in Fig. 1, a recent investigation1 has shown that creep of aluminum single crystals by the (111) [i01] mechanism is controlled by three unique processes, each of which is characterized by a single activation energy which is independent of the applied stress and the creep strain. A comparison of the observed activation energies with theoretically calculated values permits a fairly clear identification of the three operative creep processes. Below 450°K, where the activation energy for creep is 3,400 cal per mole, the deformation is controlled by the Peierls process, the activation energy for creep agreeing well with that calculated by seeger2 for the energy required to nucleate the motion of a dislocation loop against the atomic forces of the lattice. Between 590° and 750°K, the observed activation energy for creep of about 28,000 cal per mole agrees well with the energy necessary to induce cross-slip. Seeger and schoeck3 estimate that the activation energy is about 24,000 cal per mole whereas Friedel4 recently calculated this activation energy to be 28,000 cal per mole. Above 800°K the activation energy of 35,500 cal per mole that was observed for creep agrees well with that estimated for self-diffusion in aluminum.= In this range the operative rate-controlling slip process has been clearly identified as that arising from the climb of edge dislocations. The objective of this investigation is to ascertain whether a single crystal of aluminum favorably oriented for simple shear in the [loll direction on the (010) plane might exhibit uniquely different activation energies for creep from those obtained previously for (111) [101] slip. Whereas the exis- tence of such unique activation energies would constitute incontrover table evidence for new mechanisms of slip, the absence of any new activation energies might suggest that slip of aluminum is confined to the (111) [loll mechanism. Several factors prompted the selection of the (010) [101] orientation for study. First, there are more reported observations of (010) [loll slip than of any other nonoctahe-dral mechanism.8-10Secondly, Chalmers and Martius1l have concluded from considerations of the energies of dislocations that (010) slip is the second most favored mechanism in face-centered-cubic metals. Finally, favorable orientations for simple shear by the (010) [loll mechanism provide the least favored orientation for slip by the (111) [101] mechanism. EXPE-RIMENTAL PRO-CEDURE The high-purity aluminum stock, specimen preparation, shear fixture, extensometry, and experimental technique used in this investigation were the same as those previously reported.' Single-crystal spheres grown from the melt of 99.995 pct pure Al* were _ *The high-purity aluminum used in this investigation was graciously given by the Aluminum Company of America. oriented, carefully machined into dumbbell-shaped shear specimens, annealed, and chemically polished. The finished specimen had a central reduced section 0.190 in. wide and 0.590 in. in diam and 1/4-in. grip sections at both sides, 0.690 in. in diameter. The specimen was oriented in the stainless steel grips of the shear fixture with the (010) plane perpendicular to the dumbbell axis and the [loll direction parallel to the stress axis within 2 deg. Creep activation energies were calculated in the previously described manner1 from determinations of the instantaneous change in shear strain rate produced by an abrupt 15 to 20 deg increase or decrease in test temperature. If is the instantaneous strain rate at strain y and temperature T1, and ?2 the instantaneous rate at y and T2,

Jan 1, 1960

By G. Derge, Ling Yang, John Henderson

Self-diffusion coefficients of aluminum have been measured by the capillary reservoir technique in liquids of the CaO-SiO2-Al2O3 system containirg equimolar portions of CaO and SiO2, in the temperature range 1400o to 1520oC. For the melt containing 6.0 mole pct Al2O3 the results can be expressed by the equation D = [(4.3 * 0.3) x 104] exp [(-85,000 * 17,500)/RT]cm~sec-'; for the melt containing 12.5 mole pct Al2O3, by the equation D = (5.4 i 0.2) exp [(-60,000 * 10,00O)/RT] cm2sec-: A concept of the constitution of these melts has been developed which proposes that the ratios O/(Si +Al) and Al2 O3/CaO determine the dominant species present. In recent years considerable work has been done on the system CaO-SiO2-A12O3 with a view to elucidating the structure of liquids of this system. Conductivity,' electromotive force, 3 density,4 and activity5 measurements have all contributed to an understanding of the problem, but as yet there is no entirely satisfactory theory that can account for all the observed experimental results. In principle, measurements of self-diffusion coefficients should give further information which is not obtainable in other ways. Self-diffusion coefficients for calcium, silicon,6 and oxygen7 have been measured. The present investigation extends the series of self-diffusion coefficient measurements to include aluminum and develops a concept of constitution for liquids of this system which is compatible with all the observed experimental results. EXPERIMENTAL The technique used in the measurement of the self-diffusion coefficient of aluminum was the capillary-reservoir method,8 A126 being incorporated in the melt contained in the capillary and inactive aluminum in the reservoir melt. This method was chosen because it minimizes convection currents' in the diffusion zone. It has the further advantage that the boundary conditions are such that a slight modifica- tion of Anderson and saddington's8 solution of Fick's Law yields an equation which requires measurements only of the length and the initial and final average specific activities of the solidified melt within the capillary. where t is the diffusion time, Co is the average specific activity of the melt contained in the capillary at t = O, C is the average specific activity of the melt contained in the capillary at t = t, 1is the length of the capillary, and D is the self-diffusion coefficient. The equation is of somewhat different form than those previously applied to high temperature diffusion studies because the specific activity of the melt in the reservoir was negligible both before and after diffusion. The diffusion apparatus is shown schematically in Fig. 1. It consisted of a silicon carbide resistance furnace containing the inactive melt in a graphite crucible, internal dimensions 7/8 by 4 in., enclosed in a 1 1/4- by 1 1/2- by 30-in. McDanel tube. A 3/8-in. McDanel thermocouple sheath to which graphite radiation shields and a graphite protection tube were affixed, was used to hold the capillaries. By moving this sheath through a rubber seal at the top of the McDanel tube the capillaries could be lowered into or raised out of the melt. Temperature was measured with a Pt-Pt 13 pct Rh thermocouple which was calibrated periodically against a standard couple. The furnace temperature was controlled to ± 5°C through the thermocouple immersed in the melt. Temperature variation over the depth of the melt was less than ± 3°C. The inactive melts were prepared from pure native quartz, assaying better than 99.9 pct SiO2, A.R. grade A12O3 and A.R. grade CaCO,. The same quartz and CaCO3 were used in preparing the active melts, the

Jan 1, 1962

By C. H. Mathewson

CHARACTER OF THE WORK IN HAND IN planning the present experiments, we have made a particular effort to secure that adjustment of working conditions which would render the forthcoming tests most serviceable by way of indicating the comparative properties of the three different commercial grades of copper used. More specifically, we have endeavored to obtain certain definite information with respect to the relative behavior under test of ordinary electrolytic copper and furnace-refined lake copper containing (a) a moderate percentage of arsenic and (b) a rather large percentage of arsenic, in addition to the usual content of silver and other impurities. These comparisons were made systematic and comprehensive by testing throughout a series of (eight) reductions running from 0 to 70 per cent. in the case of cold-rolled metal, and throughout a series of (15) temperatures running from 100° C. to 1,000° C. in the case of annealed metal. In other words, a survey of properties similar to that made by Grard,1 in the case of electrolytic copper, was here repeated (with modifications) and extended to two other commercial varieties of copper.

Jan 7, 1916

By C. B. E. Douglas

The following analysis was stimulated by a previous article on evaluation of the water problem at Eureka, Nev., which describes a method using formulas especially devised to calculate flow potential of extensive aquifers characterized by relatively even porosity and permeability throughout. The present discussion submits that the method was unsuitable for solving the kind of problem occurring at Eureka, where the amount of water available, rather than the flow potential, may have been the vital factor. IN an interesting article on evaluation of the water problem at Eureka, Nev.,1 W. T. Stuart describes how a difficult water problem, or one phase of it, may be evaluated by means of a small scale test. Test data are plotted by a method rendering, under certain conditions, a straight-line graph that can be projected to show how much the water table will be lowered by pumping at any specified rate for a given time. A formula is then used to determine the size of opening, or extent of workings, necessary to provide sufficient inflow to enable pumping to be maintained at that rate. At first glance this might seem the answer to a miner's prayer, but a word of caution is in order. It may not be the whole answer. Moreover, results obtained by the method described are reliable only for conditions approximating those assumed. Even where conditions do not meet this requirement, however, it may be possible to draw helpful inferences from the results, perhaps enough to facilitate another approach to evaluation of a problem. The two formulas Mr. Stuart used, the Theis formula and the one developed from it by Cooper and Jacob, were given field checks a number of years ago in valley alluvials by the Water Supply Div. of the U. S. Geological Survey and found to be reliable when the aquifer is very large in horizontal extent and sufficiently isotropic for the test well and observation wells to be in material of the same average permeability as the saturated part of the aquifer as a whole." Extensive valley alluvials, sands, and gravels can be evaluated in this way, and there are even cases in which the method could apply to porous limestones, such as flat beds of very large areal extent that have been submerged below the water table after extensive weathering. These are sometimes prolific sources of water for towns and industries. It is necessary for them to have been above the water table for some geologically long period of time in a fairly humid climate before submergence because the necessary high porosity and permeability, and large reservoir capacity, are the result of weathering, that is, of solution by the carbonic acid (H,CO3) in rainwater formed by the absorption of CO, from the air by raindrops, and this dissolving action must cease when all the H2CO3 has been consumed by re- action with the carbonate to form the more soluble bicarbonate. Consequently this weathering process is largely restricted to a zone that does not extend much below the water level, and submergence is necessary after the weathering to provide large reservoir capacity and good hydraulic continuity. On the other hand, water courses tend to form along faults and fractures in limestone, and to become enlarged by solution, well below water level when, as often happens, fresh meteoric water is circulated rapidly through them to considerable depth by hydrostatic pressure, as through an inverted syphon. Although the reservoir capacity of such water courses is relatively small they may extend far enough to tap more prolific sources. Cavities, and sometimes caves of considerable size, are found in limestones where the acid formed by the oxidation of sulphides has attacked them. This action can take place as deep below water level as surface water is carried by syphonic or artesian circulation, because the oxygen it carries in solution will not be consumed until it reacts with some reducing agent, such as a sulphide. Moreover, the formation of acid and solution of limestone in this way is not confined to the immediate vicinity of the sulphide. Oxidation of pyrite, for example, results in formation of acid in several successive stages, each taking place as more oxygen becomes available, as by the accession of fresh water into the circulation at some place beyond the sulphides. When the acid thus formed attacks the limestone, CO, is liberated and the ultimate effect of the complete oxidation of one unit of pyrite will be the removal of six times its volume of limestone as the sulphate and bicarbonate, both of which are relatively soluble. The reaction may be continued or renewed along a water course far from the site of the sulphides, where the small electric potential produced by contact with the limestone helped to start the reaction. Mr. Stuart refers2 0 caves in the old mining area in the block of Eldorado limestone southwest of the Ruby Hill fault at Eureka, Nev., and to the cavities encountered in drillholes in the downthrown block on the other side of the fault. Although he interprets these cavities as evidence that this formation was sufficiently isotropic (evenly porous and permeable) to give reliable results by the method he describes, they may, in fact, be entirely local conditions. There is reason to think they were probably formed

Jan 1, 1956

By Ming-Kao Yen

A considerable amount of work has been reported in the literature in regard to the texture and earing behavior of copper strip. The rolling texture of copper has been confirmed as (110) [112] and (112) [111], which yields ears of a drawn cup at the position 45" from the rolling direction.1-3 The recrystallization texture has been established as the cubic or (100) [001] texture, where the earing positions are at 0" and 90" to the rolling direction.4-8 It has also been reported that in the development of cubically aligned grains of copper strips, the percentage of this cubic texture increased with an increase of final reduction and final annealing temperature.8,9 A comprehensive study on H.C. copper (British commercial copper of high-conductivity quality = Cu 99.95 pct, O2 0.03 pct, Ag 0.003 pct, Fe 0.005 pct and Pb < 0.001 pct) was made by Cook and Richards.6 They concluded that the recrystallization textures could be described as one or more of the following textures: (1) a single texture (100) 10011, (2) a twin texture (110) [112] and (3) a random orientation, depending upon the previous history of the specimen concerned. The effect of various alloying additions in copper was reported by Dahl and Pawlek.10 They found that certain alloying additions, such as 5 pct Zn, 1 pct Sn, 4 pct Al, 0.5 pct Be, 0.5 pct Cd, or 0.05 pct P suppressed the formation of cubic texture. Brick, Martin and Angierll reported that the cold rolled textures due to various additions fitted a rather simple pattern. However, the recrystallization textures were subject to very considerable variations. In the discussion of this paper, Baldwin stated that deoxidized copper containing 0.02 pct P gave a complicated recrystallization texture at lower temperature. When this copper was annealed at high temperature, a single texture appeared which was described as (110) [ill] but. according to a pri- vate communication from Baldwin, this orientation reported was in error and should have been reported as (110)[112]. He also reported that the earing positions of drawn cups were at 60" to the rolling direction.12 Recently, Howald, in his discussion on the paper by Hibbard and Yen,13 reported that the rolling texture of phosphorus deoxidized copper, containing from 0.006 to 0.020 pct phosphorus, was of the pure copper type. When these coppers were annealed at lower temperatures, they exhibited a random orientation, and when they were annealed at higher temperatures they had a mixed (111)[110] and (100)[001] texture, depending on the severity of the final reduction and annealing temperature. However, the specific influence of phosphorus and other impurities on the recrystallization textures and the deep drawing properties of copper strip has not been thoroughly reported. Therefore, an attempt has been made in the present work to determine the rolling and recrystallization textures and also the earing behavior of five types of commercial copper and thereby to evaluate the effect of phosphorus and some other significant impurities on the development of texture for cold reductions of about 87 to 89 pct. Materials Used The five types of copper employed in the present investigation were two phosphorus deoxidized coppers of different phosphorus content (0.007 and 0.013 pct P), an oxygen-free copper (OFHC), an electrolytic tough-pitch copper, and a fire-refined tough-pitch copper. These materials were subjected to a thorough spectroscopic and chemical analysis. The designations and the chemical compositions were as shown in Table 1. The coppers, FA1, FA2 and FA3. were hot-forged from 3-in. billets into a ½ X 6-in. plate and cold rolled to the ready-to-finish gauge indicated below. FA4 and FA5 were hot rolled and scalped to ready-to-finish gauge. The grain size of all the materials in the ready-to-finish condition was about 0.030 to 0.045 mm. Table 2 shows the last stage of the production schedule for each copper strip used. Experimental Procedure ANNEALING, GRAIN SIZE AND HARDNESS DETERMINATIONS Specimens of each type of copper were finally annealed in air for periods of one hour at temperatures ranging from 300 to 1600°F and were subsequently cooled in air. The average grain diameter of the annealed specimen was estimated by comparing with a standard grain size chart. Hardness was determined on the Rockwell 15 T scale. CUPPING TESTS Cups were made in a blanking and drawing set, in which blanks of 2-in. diam were drawn to a cup of 1.25-in. diam with an average depth of about 0.75 in. The clearance between the punch and die was about 0.032 in. The ears of the cup were measured with a special fixture which read the height of ears to one-thousandth of an inch on every ten-degree interval along the circumference of the cup. POLE FIGURES The usual transmission diffraction method with unfiltered copper radiation was employed to determine the pole-figures of the specimens cold-rolled or annealed at 900°F. All the pole-figures were derived from the positions of intensity maxima on 111 diffraction rings of the X ray photo-grams taken at 10 rotation of a

Jan 1, 1950

By H. Biloni, R. Morando

The surface structure and substructure of Al-Cu alloys solidified as conventional ingots and under particular conditions such as those used by Bower and Flemings are studied. The influence of lampblack coating on the mold walls is especially considered and the results compared with those obtained in copper and graphite molds where no coatings exist. When high heat extraction conditions exist the observations show that mechanism of copious nucleation is responsible for most of the chill zone. When the heat extraction through the mold walls is low, a coarse grain structure with dendritic morphology arises, with a size that depends on the degree of convection present, analogous to that analyzed by Bower and Flemings. In both cases the effect of the convection on the macroscopic and microscopic appearance is discussed. The ingot macrostructure consists of one or more of three zones: "chill zone", "columnar zone", and central "equiaxed zone". The mechanism of the columnar-equiaxed transition has been subject of considerable interest and at present at least three theories exist about the formation of the equiaxed region: 1) the constitutional supercooling theory1 maintains that the equiaxed crystals nucleate after the columnar zone has formed, as a result of the constitutional supercooling of the remaining liquid; 2) chalmers2 pointed out, however, that there were several objections to this proposal, and that consideration should be given to the possibility that all the crystals, equiaxed as well as columnar, originated during the initial chilling of the liquid layer in contact with the mold; 3) Jackson et aL3 and O&apos;Hara and ~iller~ suggested that a remelting mechanism of the dendrite arms is responsible for the formation of the equiaxed region. After the work of Cole and Bolling and other authors6 it became evident that convection (natural, reduced, or forced) plays a very important role in the transition from columnar to equiaxed and on the size of the resultant equiaxed structure. Until recently the accepted explanation of the chill zone was that it occurs as a result of copious nucleation in the liquid layer in contact with the mold walls.798 The columnar region is a subsequent result of the growth of favorably oriented grains and, as a result of a selection mechanism studied by Walton and Chalmers,9 elongated grains with marked texture are formed. Recently, however, Bower and Flemings" using an ingenious laboratory experiment introduced the idea that the "copious nucleation" mechanism is not responsible for the formation of the chill zone and that the presence of convection, introducing some form of "crystal multiplication", plays a decisive role in the formation of the chill zone. Unfortunately, it is important to consider that for their conclusions Bower and Flemings extrapolated the results obtained in their special experiments to the case of conventional ingots, and that these authors only analyzed the macrostructures of the specimens. Let us consider the work by Biloni and chalmers" concerning predendritic solidification. These authors were able to show that a study of the segregation substructure of A1-Cu gives information about the nucleation and growth of crystals formed in contact with a cold surface. A spherical predendritic region characterizes the first part of every grain nucleated in contact with the surface as a result of the chill effect. The aim of this paper is to elucidate through the observation of the segregation substructure the conditions under which (in the Bower and Flemings type of experiments and in conventional ingots) either the nucleation or the multiplication mechanism gives rise to the structure in contact with the mold walls. I) EXPERIMENTAL TECHNIQUES The experiments were performed on two alloys: Al-1 wt pct Cu and A1-5 wt pct Cu. The purity of the aluminum was 99.99 pct and the copper 99.999 pct. The results obtained with both alloys were similar. In the Bower and Flemings type of experiments the apparatus employed to obtain rapid solidification against a surface was similar to that used by those authors. The liquid was drawn by partial vacuum into the thin section mold cavity. Plate casts were 5 cm wide and usually 7.5 cm high. The thicknesses of the cast were 0.1 and 0.3 cm. Two different materials were used for the mold, copper and nuclear-grade graphite. The internal mold surfaces were polished and left uncoated for some experiments. In other experiments, the copper or graphite surface was coated with a thin film of lampblack material. In some of these particular experiments one of the mold walls was left with an uncoated region (usually in the form of a cross). The conventional ingots were cast in graphite or copper molds. In different experiments the mold walls were sometimes uncoated or coated with lampblack material. The results obtained in conventional and Bower and Flemings copper molds were compared with those obtained with copper molds coated with a very thin film of graphite; the results obtained were essentially similar. The size of the conventional ingots was 5 cm diam and 7 cm high in all cases. The cast surfaces produced by the Bower and Flemings type of experiments and conventional methods were observed macroscopically and microscopically without any metallographic preparation. As Biloni and Chalmers showed," the observation of the chill surface can give considerable information about the structure and segregation substructure.

Jan 1, 1969

By G. R. Leverant, C. P. Sullivan

To evaluate the effect of a dispersion of nondeform-able, incoherent, second-phase particles on high-strain cyclic deformation and fracture, recrystallized TD-nickel (Ni-2ThO2) and a commercially pure nickel, Ni-200, were fatigued under strain control at total strain ranges varying from 0.009 to 0.036. Relative to the Ni-200, the slip at the surface of the TD-nickel was more wavy and discontinuous due to the presence of the thoria particles. This made crevice formation (incipient cracking) within slip bands more difficult in TD-nickel than in Ni-200. Both materials cyclically hardened to a constant (saturation) flow stress which increased with increasing plastic strain amplitude. Cellular substructures were developed in both materials during cycling. The cell size in TD-nickel was controlled by the thoria particle distribution and was independent of plastic strain amplitude over the range investigated. The cell size in Ni-ZOO was larger than that in TD-nickel at similar plastic strain amplitudes and was a function of plastic strain amplitude. These results, together with the cyclic stress-strain curves for both materials, are discussed in terms of a model for fatigue strain accommodation at saturation recently proposed by Feltner and Laird. NUMEROUS fatigue investigations have considered the interrelation of slip character, dislocation substructure, and cracking in pure metals and solid-solution alloys. However, except for the studies of the low-strain fatigue of internally oxidized copper alloys1 and cast, dispersion-strengthened lead,&apos; little is known about the effects which small, incoherent, nondeform-able, second-phase particles have on cyclic deformation and cracking processes. Effects due to the particles alone are often obscured by a dislocation substructure introduced during thermomechanical processing of dispersion-strengthened metals. In the present study, recrystallized TD-nickel and a commercially pure nickel, Ni-200, were employed to evaluate the effect of a thoria dispersion on high-strai fatigue deformation and cracking at room temperature. I) MATERIAL AND EXPERIMENTAL PROCEDURE The TD-nickel was supplied by DuPont as a 5/8-in.-thick stress-relieved plate which had been subjected to a proprietary schedule of thermomechanical treatments, and the Ni-200 as 3/4-in. bar which was subsequently annealed for 2 hr at 850°C in argon resulting in an average grain diameter of 0.05 mm. The compositions of these materials are given in Table I. The microstructure of the TD-nickel consisted of elongated grains parallel to the primary working direction with an average width of 0.16 mm, Fig. l(a). Many fine annealing twins were present indicating that the starting material was in a recrystallized condition; this supposition was confirmed by the absence of of any extensive dislocation substructure, Fig. l(b). Sheetlike stringers parallel to the rolling direction were occasionally seen both within grains and at grain boundaries. Some approximately spherical particles about 2 in diam, which may correspond to exceptionally large thoria particle aggregates, were also present. The average Young&apos;s modulus of the plate material in the rolling direction was 21.8 X 106 psi which is consistent with a {100}<001>recrystalliza-tion texture3&apos;* being prominent. In transmission microscopy, the 2.3 vol pct of thoria particles generally appeared to be uniformly distributed although some clusters, 0.1 to 0.3 in diam, of larger particles were observed as previously reported for TD-nickel sheet,5 and stringering of particles was present in some areas as welt. The average diameter of the thoria particles was 450A with a calculated mean planar center-to-center spacing of 2100A, as determined by quantitative metallographic analysis.= The 0.2 pct offset yield stress was 36,000 psi which agrees with the value predicted by the modified Orowan relation7 for edge dislocations bowing between thoria particles of the size and spacing observed in the present investigation. Fig. 2 illustrates the specimen design employed for the axial high-strain fatigue testing. Adapters were screwed onto the threaded portions of each specimen so that testing could be performed in the same manner as that reported for buttonhead specimens.8 Stressing was coincident with the working direction for both materials. The gage section of each specimen was electropolished and lightly etched prior to testing. The total strain was controlled, being varied between zero and a maximum tensile strain ranging from 0.009 to 0.036. In addition to these tests, a circum-ferentially notched TD-nickel specimen was cycled over a total strain range of 0.0075. The same strain

Jan 1, 1969

By John F. Elliott, John P. Hager

The standard free energies of formation of the lowest stable sulfides of chromium, molybdenum, and tungsten in equilibrium with the corresponding metal hazle been determined by reacting the sulfide and metal with H2(g)/H2S(g) mixtures. The reaction is A method for estimating the standard ~nolav entropies and standard entropies of formation at 298°K of the sul-fides of refractory metals is presented. The standard free energies of formation of the lowest sulfides of the metals in group VIa of the periodic table are probably best determined with the reaction* is known with greater accuracy than is that property for any other sulfur-bearing compound or solution which might serve as a reference phase to establish the chemical potential of sulfur for the essential re- However, there still remain significant problems to the use of Reaction [I] in studying these sulfides. First, the equilibrium gas ratios (Ph2S/PH2) are very small, and with the most stable sulfides in the series the ratios tend to be at the limit of the range for precise chemical analysis (10-4); and second, the reaction rate for the formation or reduction of these sulfides appears to be relatively slow. A primary reason for the latter problem is that the gas phase near the equilibrium concentration has very little capacity for transport of sulfur. It is to be noted that the thermo-dynamic properties obtained from the experimental results by Eq. [I] apply for 1 g-atom of sulfur in the metal-saturated compound even though the exact composition of the compound has not been determined. The work reported here is a study of the standard free energies of formation of the lowest sulfides of chromium, molybdenum, and tungsten, and of copper, by Reaction [I]. In planning the experimental program, it was decided that the technique that has been used previously3"&apos; could be used with modification and that an improved analytical method was needed for determining H2S in the gas phase. THE EXPERIMENT The once-through flow of gas was selected in preference to recirculating the gas, a) because of the low sulfur capacity of the gas, b) because of the relatively slow rate of reaction and the danger of the

Jan 1, 1968

By H. Conrad, V. V. Damiano, G. J. London

A method is described for producing single crystals of high-purity beryllium, Be-4.37pct Cu, and Be-5.24 pct Ni. These crystals were prepared for testing in compression parallel to the [0001] by orienting and lapping to within ±3&apos; of arc of the (0001). Microstrain testing apparatus is described along with c axis compression results for ingot purity beryllium, twelve-zone-pass material, and the above-mentioned alloys. Results show no measurable plasticity for the ingot purity material from -196" to 400°C, although some surface traces of (1122) slip was observed at 200°C and above. The twelve-zone-pass material shows substantial microstrain plasticity at 220°C with slip on (1122). Both alloys show significant plasticity at room temperature and above with slip also on (1122) planes. THE two slip systems which normally operate during the plastic deformation of beryllium in the vicinity of room temperature are:&apos; basal slip (0001)(1120) and prism slip . Pyramidal slip with a vector inclined to the basal plane has been reported for elevated temperatures,&apos;-a but occurs near room temperature only at very high stresses.~ A summary of the available data on the effect of temperature on the critical resolved shear stress for slip on these systems has been compiled by Conrad and Perlmutter.~ It has been postulated6&apos;7 that one of the principal factors contributing to the brittleness of poly crystalline beryllium at temperatures below about 200°C is the difficulty of operating pyramidal slip with a vector inclined to the basal plane. Hence, detailed information on the operation of such a slip system is important to understanding the brittleness of beryllium. The operation of pyramidal slip with a vector inclined to the basal plane is best accomplished in beryllium by compressing single crystals in a direction parallel to the c axis. In such a test the resolved macroscopic shear strzss on the basal and prism planes is zero and (1012) twinning which is favored by tension along the c axis does not occur. Hence, in c axis compression of beryllium the normal deformation modes are inhibited and the operation of pyramidal slip with a vector inclined to the basal plane is favored. In the present investigation, c axis compression tests were performed on beryllium single crystal as a function of temperature (77" to 700°K), purity (commercial and twelve zone pass), and alloy content (4.37 wt pct Cu and 5.24 wt pct Ni). Presented here is a description of the test techniques employed and the gross mechanical behavior observed. A detailed analysis of the slip traces developed on the surfaces of the deformed specimens during these tests and the results of electron transmission studies of the deformed crystals are given in a separate paper.B PROCEDURE 1) Materials and Preparation. Single crystals about 1 in. diam were prepared of the following materials: commercial-purity beryllium, high-purity beryllium, and two beryllium alloys, one with 4.37 wt pct Cu and the other with 5.24 wt pct Ni. The commercial-purity single crystals were obtained by cutting specimens from large-grained ingot of Pechiney SR material, which is approximately 99.98 pct pure. The high-purity crystals were prepared by floating-zone refining (twelve passes) a rod (7 in. by 1 in, diam) of Pechiney SR grade cast and extruded beryllium. Although an absolute chemical analysis of the zone-refined material was not established, mass spectro-graphic analysis, emission spectrographic analysis, and y activation analysis indicated that it contained in atomic fractions about 5 to 10 ppm each of carbon and oxygen, 1 to 5 ppm each of nickel and iron, and about 1 to 2 ppm of copper, with the remaining residual impurities being less than 1 ppm. Further indication of the purity of this material is provided by the critical resolved shear stress for basal slip, which was approximately 300 psi. The starting material for the alloy single crystals was 1-in.-diam floating-zone-refined (six passes) rod of Pechiney SR grade beryllium. Two such rods were wrapped respectively with sufficient weight of wire of high-purity copper (99.999 pct) or nickel (99.999 pct) to yield a 5 wt pct alloy. A seventh floating-zone pass was then applied to each of the rods to accomplish the initial alloying and an eighth pass for homogenization. Analytical samples were taken from regions of the rod immediately adjacent to where the mechanical test specimens were cut; these indicated 4.37 wt pct Cu and 5.24 wt pct Ni. 2) Crystal Orientation. To avoid the occurrence of basal slip during c axis compression testing, it is necessary to load the crystals as nearly parallel to the c axis as possible. Preliminary c axis compression tests indicated that plastic flow and/or fracture occurred at stresses of the order of 300,000 psi; hence on the basis of a critical resolved shear stress for basal slip of 300 to 400 psi, the maximum crystal misorientation permitted is about 4 to 5&apos; of arc. Since this accuracy cannot be obtained using the usual back-

Jan 1, 1969

By B. Herrlander, A. Hultgren

The original aim of the present investigation was to study the mechanism of cracking on hot-deforming red-short steels. During the microscopical examination of hot-deformed soft steels attention was directed to various patterns of so-called veining in the ferrite, as related to variations in the deformation procedure and the heat-treatment of the steels. Later, a hot-short steel of higher carbon content was also studied. Historical Storey1 suggested in 1914 that veining developed during the gamma-alpha transformation from the growing together of several alpha nuclei within the same gamma grain. Rawdon and Berglund2 found that in soft steel, forged somewhat below A3, the ferrite showed profuse veining, while usually there was very little veining after forging at very high temperatures. They emphasized the similarity between the pattern of veining formed by deformation about 600°C and that of slip lines formed by deformation at room temperature. They also suggested a relation between the gamma-alpha transformation and veining. They became convinced from etching and from the slip-line pattern in cold-deformed material, that the orientation within any ferrite grain showing veining was uniform. In recrystallized alpha grains veining was absent. Veining did not appear materially to affect the properties of ferrite. Independent of veining, continuous networks, attributed to preexisting delta and gamma grain boundaries were sometimes found, the former only in cast steel. Those networks were usually connected with small inclusions. Ammermann and Kornfeld3 confirmed that recrystallized ferrite grains showed no veining. In soft steel annealed between A1 and A3 there was veining only in the ferrite grains formed during cooling. Electrolytic iron deformed at 880&apos; was free from veining. Bannister and Jones&apos; considered veining in ferrite to be a manifestation of microscopical and sub-microscopica~ inclusions. NorthCOtt,5,6 in studies on veining in steel and other metals and alloys, attributed veining to oxide inclusions. It could generally be removed by annealing in hydrogen, a suggestion earlier made by Rawdon and Berg1und. TrittOn (discussion in ref. 5) emphasized the importance of perfect polishing for bringing out veining by etching, and thought the veins or subboundaries were produced during the gamma-alpha transformation, when it was rapid, as a result of the volume change and contraction during cooling. Slight distortion would not allow projecting parts of a growing crystal to join up with atomic symmetry. Hanemann and co-workers showed that veining in ferrite consisted of ridges

Jan 1, 1948

By S. J. Burns, W. W. Webb

The dislocation arrangements formed during unsteady propagation of cleavage fractures on (010) planes in LiF have been investigated by high-resolution etch-pit techniques and by X-ray diffraction topogvaphy. In impurity-hardened crystals, cracks propagating in any direction on (010) planes at velocities of about 103 cm per sec are usually accompanied by light plastic deformation which is enhanced wherever the crack is allowed to hesitate. Dislocations with [011] type Burger&apos;s vectors are often formed looped around the crack tip. They are dragged along with the crack tips leaving edge dislocations lying nearly parallel with the clearage surface about 5µ from it. These dislocations are easily overlooked since they may initially intersect with the cleavage surface infrequently and later may disappear from the crystals due to image forces during aging at room temperature. Although the plastic work associated with these dislocations is only comparable with the reversible (010) surface energy, an instability in crack propagation appears due to a limit of the velocity with which dislocations can be dragged along with the crack. Transition to a fully brittle nonplastic fracture mode occurs when the crack velocity exceeds the velocity with which dislocations can be moved by the stress field of the crack. TRANSITIONS between brittle and ductile modes of fracture appear to be common processes in the behavior of materials in which the flow stress is close to the stress at which brittle cracks can propagate. High-strength engineering alloys fit into this category and the transition from ductile to brittle modes of crack propagation may be associated with catastrophic failures in these important materials. The methods of theoretical mechanics indicate the geometrical conditions in which these processes may occur but the detailed mechanisms controlling the generation of dislocations in the initiation of the plastic mode and the process by which the loss of plasticity occurs on transition to the brittle mode are not yet clear. Since these mechanisms are not amenable to direct observation in engineering alloys we have chosen a semi-ductile alkali halide LiF as a model system in which to observe transition mechanisms between plastic and brittle modes of crack propagation. Cleavage cracks in this system are known to undergo a plastic-elastic transition at velocities between 103 to 104 cm per secl and dislocation configurations in LiF are amenable to study by optical-microscopic observation of dislocation etch pits2 and by X-ray diffraction topography.3 We have been able to identify a dislocation mechanism responsible for the transition from brittle to slightly plastic modes of crack propagation in LiF. A model based on this mechanism permits calculation of the critical crack-propagation velocity for this transition and indicates the importance of the stress dependence of dislocation velocity in determining the critical crack velocity. Of course, this model cannot be carried directly over to more complex materials but it is quite possible that its qualitative features are generally applicable. Dislocations intersecting fresh cleavage surfaces in LiF were reported by Gilman,4 by Forty,5 and by Wash-burn et a1.6 Such dislocations were construed to have been nucleated where the cleavage crack hesitated or stopped, near stress concentrators, such as cleavage steps, on the crystal face. The loci of such dislocations deposited On the cleavage plane in bands were called "stop lines" or "deformation zones". Gilman, Knudsen, and walshl measured the velocity of cleavage cracks in lithium fluoride by evaporating thin resistive strips on the crystal side and recording

Jan 1, 1967

By G. Meyrick, H. W. Paxton

Observations on the tensile deformation of single crystals of austenitic stainless steels as a function of composition, orientation, and temperature are described and compared with relevant data for other alloys. Crystals free from second phases show sharp yield points followed by Lüders&apos; extensions of up to 20 pct. The critical resolved shear stress is strongly temperature-dependent increasing fourfold between 423O and 77°K. A temperature-independent low rate of hardening follows the Luders&apos; extension and is frequently associated with overshoot. Unlike pure metals where Proficse cross slip usually occurs at the end of linear hardening, this stage is terminated either by cross slip or by slip on the conjugate system, the particular node apparently depending upon initial orientation and composition. The presence of 6 ferrite or martensite has a profound effect upon the magnitude of the yield stress and the shape of the stress-strain curve. In experiments on transgranular-stress corrosion cracking of austenitic stainless steels in boiling magnesium chloride, several workers1&apos;2 have shown that increasing amounts of nickel tend to reduce the probability of specimen failure. Reed and paxton3 have observed in single crystals that the macroscopic crack plane changes as the nickel content is increased. For 18 pct Cr-8 pct Ni, the crack plane is sensibly perpendicular to the applied tensile stress; for 20 pct Cr-20 pct Ni the crack plane is (100). The average crack-propagation speed is much lower in the 20 pct Ni crystals. Furthermore, the possible importance of stack-ing-fault energy in nucleation and growth of cracks has been suggested by a number of workers. While the general effect of variations in stack ing-fault energy appears to be quite well-correlated with observed variations in cracking characteristics, each of the theories assigns rather different detailed reasons for these effects. Because the stack ing-fault energy of austenitic steels is believed to be increased with increasing nickel content, and because some theories of trans-granular cracking postulate a mechanical stage in the crack propagation (rather than relying entirely on electrochemical solution), it appeared to be of some interest to investigate the mechanical properties of a series of different compositions of aus-tenite single crystals. These experiments were considered of intrinsic value in view of the relative scarcity of such data on fcc alloys. This paper gives the results of some experiments carried out with this aim in mind, and suggests various &apos;other experiments which may be helpful in future studies. The experiments are also of interest in view of the recent interest in obtaining higher-strength steels by control of the imperfection content of austenite; although the compositions are not directly comparable, the results are still probably valuable. Comparisons with experiments on other fcc alloy crystals are made where possible to see how well the general pattern of behavior is understood. EXPERIMENTAL PROCEDURE The alloys used in this investigation were vacuum-melted heats of nominally 20 pet Cr-20 pet Ni-60 pet Fe, 20pctCr-16 pct Ni-64 pct Fe, and 20 pctCr-12 pet Ni-68 pet Fe.* Analyses of the material are

Jan 1, 1964

By L. A. Schrider, J. A. Wasson

A method of predicting waterflood performance has been developed that combines certain facets of several previously published prediction techniques. The manner of combination has required the development and use of some new and some little-known relationships and has eliminated several of the weaker assumptions inherent in the original individual prediction methods. This approach, which was designed for computer solution, has removed the necessity of referring to plotted curves and permits the analytical prediction of water flood performance for a five-spot well pattern in either homogeneous or stratified reservoirs. The Predicted values are expressed in common oilfield units rather than in abstract or dimensionless terms. The calculation procedure has been programmed in FORTRAN IV and the entire program listing is available to potential users.* Introduction Prior to initiation of secondary recovery of oil by waterflooding, the possibilities of economic success or failure must be evaluated with the greatest practical accuracy. Although many prediction techniques are available, most, if not all, have serious limitations. In recent years, the Bureau of Mines has attempted to stimulate interest in the secondary recovery of oil from Appalachian pressure-depleted reservoirs. Waterflooding, because of its widespread acceptance and success, is the principal secondary-recovery method considered. During the life of the project, several performance prediction methods have been studied and applied. Because these methods, individually, have inherent assumptions and limi-tations, portions of some of them have been selected and combined in an effort to eliminate such shortcomings wherever possible. We believe that the resulting technique is as accurate as the necessary available data will permit and that it has several distinct advantages over previously published methods. Development of the Method The fractional flow equation developed by Buckley and Leverett&apos; from Darcy&apos;s law is the fundamental mathematical statement describing immiscible fluid-fluid displacement in porous media. A generalized form of this relationship, whose derivation is readily available in the literature, is The formation dip, a, is usually very small in those petroleum reservoirs being considered for pattern waterflooding in the Appalachian area. Therefore. in many cases. a has an almist negligible value. In addition, Ap, the difference between the density of water and the density of oil, is relatively small. For these reasons the gravitational term may often be neglected. Capillary pressure is a function of saturation, which is in turn a function of distance from the upstream boundary of the system or the injection well. In this study it is assumed that the frontal zone of the waterflooding (or zone of capillarity) has negligible length and that only those saturations in the water-swept zone at breakthrough and later are of interest. As the distance in a waterflood pattern is comparatively large and the change in water saturation with distance is usually small, the change in capillary pressure with distance is negligible. The simplified form of the fractional flow equation is appropriate, therefore, in this application. Three variables must be considered in determining that fraction of the total fluid flow that consists of water: the viscosity ratio, saturation, and relative permeability ratio.

Jan 1, 1969

By K. C. Hong, R. B. Jensen

The problem of determining the optimum set of steam volumes and cycle lengths for a single well undergoing multicycle steam stimulation in order to maximize the cumulative discounted net income has been formulated mathematically and programmed for a digital computer. The mathematical fonnulation of the problem and the method for its solution are discussed in this paper. The oil production performance during each stimulation cycle was simulated by either a constant percentage or a harmonic decline. Using simple analytical expressions for production performance, the cumulative discounted net income and cumulative time of operation were related to the pertinent process and cost parameters and two principal process control variables (cycle length and steam injection volume). The discrete maximum principles was used to transform the equations for cumulative time of operation and cumulative discounted net income into a set of simultaneous equations. The simultaneous equations then were solved by trial and error on a digital computer to determine the set of cycle lengths and stem injection volumes that gives maximum cumulative discounted net income over the project life. INTRODUCTION Steam stimulation is a process for improving the oil recovery rate from wells producing high-viscosity crudes. The process is applied on an individual well basis and is executed in a series of cycles, each consisting of three phases: steam injection, soaking (steam condensation), and production. Significant increases in production rate following the stimulation operation result from heating the reservoir around the wellbore. As heat is removed with produced fluids and dissipated into nonproductive formations, the production rate declines, usually to near the prestimulation value. Typical production responses are given in case histories reported by Owens and Suter,l and are depicted in Fig. 1. Duration of the production phase is equal to the time for the oil production rate to decline to some specified value and is called the cycle length. (Cycle length is defined as the producing portion of the cycle and does not include the downtime required for steam injection and soaking operations.) Termination of the production phase coincides with the start of steaming for the next cycle. The process is continued, cycle by cycle, until it becomes unprofitable. Models 2-4 have been developed to simulate behavior of a single well during one cycle of steam stimulation and have been used to investigate the effects of system and operating conditions on the production responses. However, these investigations have not shown how the models can be used to determine a most profitable set of operating conditions for a multicycle stimulation project. Perhaps these models are too complicated mathematically to be adapted readily to an optimization study. This paper presents a method for optimizing a multicycle steam stimulation project based on simple production performance models. First, the performance of a steam-stimulated well during each cycle was simulated by either a constant percentage or a harmonic decline model. Using these simple analytical expressions for production performance, the cumulative discounted net income (before tax) and cumulative time of operation for each cycle were related to the pertinent process and cost parameters and two process control variables—the cycle length and the steam injection volume. Finally, the profit function to be maximized was formed. The analogy between the above problem and problems of optimizing multistage decision processes that have been reported extensively in the chemical engineering literatures5-10 in recent years has led this investigation to the use of the discrete maximum principle.5-7 This principle was used to transform the equations for cumulative discounted net income and cumulative time of operation into a set of simultaneous equations characterizing the optimum operating conditions in terms of the two control variables. These equations

Jan 1, 1970