By J. M. Uys, T. B. King

The solubility of water in silicate melts of various compositions was measured. The basicity of the silicate did not appreciably affect the water solu-bulity at low-base content (acid compositions). Near the orthosilicate composition the solubility increased with basicity for silicates in which the cation displayed a weak ion-oxygen attraction and apparently decreased for those in which the cation showed a strong ion-oxygen attraction; metasilicates of the former class dissolved more water than those of the latter. Temperature had little effect on water solubility. The experimental results are interpreted on the basis of two modes of solution, the contribution of one decreasing, and that of the other increas -ing, with increased melt basicity. In the former, solution occurs through interaction with doubly-bonded oxygen atoms and in the latter, through interaction with singly-bonded oxygen atoms, or, in very basic melts, through reaction with free oxygen ions. THE hydrogen content of a steel melt is in a large measure determined by water dissolved in the slag. In some glasses water may be a major cause of "seeds". Water vapor in the furnace atmosphere is the primary source in both instances. A knowledge of the mechanism of water solution in silicate melts should help in assessment of practical methods for its control in steelmaking and glass refining. Walsh et a1.l measured the water content, expressed as hydrogen, of 40 pct lime-20 pct alumina-40 pct silica and 62 pct manganese oxide-38 pct silica melts as a function of the steam partial pressure, in equilibrium with the melt. Tomlinson 2 and, also, Russell3 investigated this relationship for a molten 30 pct soda-70 pct silica glass. In all three investigations, the solubility of water was found to be proportional to the square root of the partial pressure of steam. Moulson and Roberts 4 confirmed this relationship for a silica glass. On the basis of the square root relationship, Tomlinson2 and Russell3 interpreted the solution reaction as "network-breaking", similar to that expected on the addition of metal oxides to silica. Walsh et al.' postulated two possible modes of solution, one the mechanism suggested by Tomlinson and Russell and the other the reaction of the water molecule with an oxygen ion to form hydroxyl ions. These two modes of solution suggest opposite effects of melt basicity on water solubility. However, little appears to be known about the effect of melt basicity on water solubility. Walsh et a1.l found, in the lime-silica system, that the water content increased slightly with increased basicity. As these authors pointed out, this does not appear to be in accord with their further observation that slags containing little or no silica dissolve very little water. Kurkjian and Russell5 measured the effect of basicity on water solubility in alkali silicates in the composition range 15 to 45 mole pct alkali oxide. They found a minimum in the water content at about 25 mole pct alkali. This was interpreted on the basis of two concurrent solution reacZions; one in which solubility was proportional to the activity of doubly-bonded oxygen and, in the other, proportional to the activity of singly-bonded oxygen. The present work was aimed at establishing the effect of basicity on water solubility in silicate melts over as wide a range of compositions as practical. APPARATUS AND EXPERIMENTAL PROCEDURE The silicate melt was equilibrated with a "carrier-gas" of accurately known water content, quenched, and analyzed for water by a vacuum fusion technique. Some pertinent details of the equilibration procedure, analysis technique, preparation, and handling of the silicates are given below. Gas-Silicate Equilibration. The apparatus used to equilibrate the melt with the gas mixture was similar to that used by Walsh et al.' but with some important modifications.6 Purification trains were provided for nitrogen and hydrogen; whenever air or oxygen was used as carrier gas the nitrogen purifiCation train was used with the copper furnace at room temperature. Gas flow rates were measured with capillary flow meters; bleeders filled with a mixture of dibromo and tribromo ethyl benzene (density about 2 g per cc) were used for convenience in controlling flow rates.

Jan 1, 1963

By John Henderson

FOR some time now the most commonly accepted description of liquid silicate structure has been the "discrete ion" theory, proposed originally by Bockris and owe.' This theory is that when certain metal oxides and silica are melted together, the continuous three dimensional silica lattice is broken down into large anionic groups, such as sheets, chains, and rings, to form a liquid containing these complex anions and simple cations. Each composition is characterized by "an equilibrium mixture of two or more of the discrete ions",' and increasing metal oxide content causes a decrease in ion size. The implication is, and this implication has received tacit approval from subsequent workers, that these anions are rigid structures and that once formed they are quite stable. The discrete ion theory has been found to fit the results of the great majority of structural studies, but in a few areas it is not entirely satisfactory. For example it does not explain clearly the effect of temperature on melt structure,3 nor does it allow for free oxygen ions over wide composition ranges, the occurrence of which has been postulated to explain sulfur4 and water5 solubility in liquid silicates. In lime-silica-alumina melts the discrete ion theory is even less satisfactory, and in particular the apparent difference in the mechanism of transport of calcium in electrical conduction8 and self-diffusion,' and the mechanism of the self-diffusion of oxygen8 are very difficult to explain on this basis. By looking at melt structure in a slightly different way, however, a model emerges that does not pose these problems. It has been suggested5" that at each composition in a liquid silicate, there is a distribution of anion sizes; thus the dominant anionic species might be Si3,O9 but as well as these anions the melt may contain say sis0:i anions. Decreasing silica content and increasing temperature are said9 to reduce the size of the dominant species. Taking this concept further, it is now suggested that these complexes are not the rigid, stable entities originally envisaged, but rather that they exist on a time-average basis. In this way large groups are continually decaying to smaller groups and small groups reforming to larger groups. The most complete transport data 8-10 available are for a melt containing 40 wt pct CaO, 40 wt pct SiO2, and 20 wt pct Al2O3. Recalculating this composition in terms of ion fractions and bearing in mind the relative sizes of the constituent ions, Table I, it seems reasonable to regard this liquid as almost close packed oxygens, containing the other ions interstitially, in which regions of local order exist. On this basis, all oxygen positions are equivalent and, since an oxygen is always adjacent to other oxygens, its diffusion occurs by successive small movements, in a cooperative manner, in accord with modern liquid theories." Silicon diffusion is much less favorable, firstly because there are fewer positions into which it can move and secondly, because it has the rather rigid restriction that it always tends to be co-ordinated with four oxygens. Silicon self-diffusion is therefore probably best regarded as being effected by the decay and reformation of anionic groups or, in other words, by the redistribution of regions of local order. Calcium self-diffusion should occur more readily than silicon, because its co-ordination requirements are not as stringent, but not as readily as oxygen, because there are fewer positions into which it can move. There is the further restriction that electrical neutrality must be maintained, hence calcium diffusion should be regarded as the process providing for electrical neutrality in the redistribution of regions of local order. That is, silicon and calcium self-diffusion occur, basically, by the same process. Aluminum self-diffusivity should be somewhere between calcium and silicon because, for reasons discussed elsewhere,' part of the aluminum is equivalent to calcium and part equivalent to silicon. Consider now self-diffusion as a rate process. The simplest equation is: D = Do exp (-E/RT) [I] This equation can be restated in much more explicit forms but neither the accuracy of the available data, nor the present state of knowledge of rate theory as applied to liquids justifies any degree of sophistication. Nevertheless the terms of Eq. [I] do have significance;12 Do is related, however loose this relationship may be, to the frequency with which reacting species are in favorable positions to diffuse, and E is an indication of the energy barrier that must be overcome to allow diffusion to proceed. For the 40 wt pct CaO, 40 wt pct SiO2, 20 wt pct Al2O3, melt, the apparent activation energies for self-diffusion of calcium, silicon, and aluminum are not significantly different from 70 kcal per mole of diffusate,' in agreement with the postulate that these elements diffuse by the same process. For oxygen self-diffusion E is about 85 kcal per mole,' again in agreement with the idea that oxygen is transported,

Jan 1, 1963

By R. W. Kraft

The normal Mg-Mg,Sn eutectic is a classic example of a Chinese script eutectic. When the alloy is unidirectionally solidified, a much simpler topo-logical arrangement of the phase particles can be produced although individual grains still usually consist of two or more interpenetrating lamellar systerns. Specimens from unidirectionally solidified ingots were analyzed metallographicall~ and crys-tallographically, and it was found that the interfaces between the lamellae had a common crystallograPhic character describable by: Lamellar interfaces II {220}Mg2Sn 1) {1011}Mg Arguments are presented to explain why this particular orientation relationship tends to occur and it is shown that this criterion can be nearly satisfied simultaneously on up to four different lamellar systerns between two interpenetrating single crystals. Finally, on the basis of this work ad other similar work which has previously been done on Al-CuAl2 eutectics, a general principle pertaining to low-energy interfaces between two crystalline Phases is proposed. WITHIN the past few years several investigators1-4 have demonstrated that the microstructures of many eutectic alloys can be significantly altered by uni- directional solidification. If appropriate control is exercised over the purity of the alloy, the growth rate, and the thermal gradient during unidirectional solidification, ingots can be made in which the phase particles are aligned predominantly parallel to one another throughout substantial portions of the ingot. The present author has also shown for at least one of the alloys that the parallel lamellae tend to assume a unique crystallographic relationship during

Jan 1, 1963

By W. Klement

By quenching liquid alloys, single-phase solid solutions are obtained in the ranges 0 to 42.0 at. pct Co-Au and 0 to 15 and 75 to about 100 at. pet Co-Cu. Metastable solid solutions are also found in multiphase 42.0 to 49.0 and 69. 0 to about 100 at. pet Co-Au alloys. fie inability to achieve complete solid solubiliiies in Au-co and cu-co alloys is rationalized by a conszderation of the rate processes during cooling and solidification. Trends in lattice distortion and shifts in the compositions of the melting-point minima and critical points are discussed for the binary alloys of copper, silver, and gold with some of the transition metals of the first long period. By rapidly cooling alloys from the melt, a continuous series of metastable solid solutions can often be obtained for components of similar crystal structure which normally form eutectic systems.' The eutectic system Au-Co, Fig. 1, and the peritectic system Cu-Co, Fig. 2, were investigated in order to determine the extent of the metastable solid solutions attainable with the present technique.* EXPERIMENTAL PROCEDURES Most of the alloys were prepared by melting weighed quantities of the elements (purity greater than 99.9 pct) under hydrogen in alumina crucibles by means of induction heating. After reweighing, the alloys were cast under argon into 1 mm diam wires. However, it was not possible to prepare some of the Cu-Co alloys with the requisite homogeneity (over about 1 mm3) in this way. For these alloys, reduced powders (purity greater than 99.9 pct) were mixed for 12 to 48 hr, pressed into compacts that were sintered at 1000º to 1050°C for 6 to 48 hr under hydrogen, and then furnace-cooled. Alloy charges of a few mm3, cut from the cast wires or chipped from the sintered compacts, were heated to 1550º to 1600°C in 30 sec in an alumina insert held within a graphite support and then ejected by a pulse of helium onto a lightly polished copper strip on the inner periphery of a rotating wheel. The

Jan 1, 1963

By F. Bonaccorso, G. Venturello, C. Antonione

A study of the effect of small amounts of interstitial impurities on recovery and re crystallization in high-purity iron (99.995 pct) has been undertaken. This paper gives results on the effect of carbon, introduced in small-dosed amounts @om 0.0005 to 0.0086 wt pct) by heating iron specimens of high purity m a static atmosphere of CO + ,. The materials prepared in this way, cold-worked 80 pct and subjected to a series of isochronal and isothermal annealings, were submitted to examinations by X-rays, micrographs, and hardness tests. It was observed that effect of carbon is remarkable in the sense of blocking recovery of mechanical properties up to the temperature at which re crystallization begins. On the contrary, carbon has a negligible effect on primary re crystallization temperature, when compared with the known effect of substitutional impurities. This is in agreement with the high mobility of interstitials. In effect, only a slight decrease, -20 pct, of the grain-boundary motion rate was noted, due to the interaction between the grain boundary and the carbon atoms. On the other hand, in the samples in which the carbon content is above the solubility limit at the temperature at which re crystallization occurs, a slight increase of nucleation frequency is noted due to the presence of precipitated carbides. ThE effect of purity on recovery and recrystalli-zation phenomena has been known for a long time; however, recently, new attention has been given to the problem since new methods for obtaining metals with extremely low impurity contents have become available. Most of this research work essentially concerns the effects of impurities which cause precipitates or give rise to substitutional solid solutions. The works of Bolling and winegard1 and Aust and utter' on lead, and Vandermeer and orddon' on aluminum, 01sen4 on nickel, and Abrahamson and Blakeney on iron should in particular be referred to. On the effect of this type of impurities a quantitative theory has been formulated by Detert and Lucke6 and has lately been discussed critically by Cahn7 and Gordon and vandermeer.' Interstitial solid solutions in iron have not as yet been studied. As the study of the effect of interstitials is of great interest both from a theoretical and practical standpoint, it was deemed useful to examine the effects of carbon, nitrogen, and boron on recovery and primary recrystallization of iron. There already is some work by Chaudron et al.,1-" on the effect of interstitials on iron; their work, however, mainly concerns secondary recrystallization. The present paper refers in particular to the effect of carbon. EXPERIMENTAL PART Preparation of Materials. The pure iron used for this research was obtained from FeCIS recrystal-lized and purified by extraction with isopropylic ether. From the ferric chloride purified in this manner, hydroxide was precipitated with a solution of very pure ammonia, and, by calcination in pure sintered alumina crucibles, oxide was obtained. Reduction of the oxide to iron sponge was performed in sintered alumina tubes with very pure hydrogen at 650°C; at the end of the operation temperature was increased to 900°C. Specimens for the experiments were obtained by sintering the sponge at 1480°C in pure Hz after a pre sinter ing treatment at 900° C. It is important to note that the treatment at 1480°C in Ha produces a further purification from more volatile elements such as zinc, cadmium, arsenic, lead, and tin. Details on the preparation and characteristics of this type of very pure iron are given in a previous work.'' Only the complete analysis performed by neutron-activation methodsz3 is given here, Table I. Some of the specimens prepared in this way were carburized in the 0 region with very low amounts of carbon by treating them at 700°C in a static atmosphere of Ha containing a definite amount of CO. The set-up used is described in Fig. 1. A gas-tight quartz tube containing the specimen to be carburized and an internal friction control specimen, after being evacuated, was filled with Hz

Jan 1, 1963

By Roland de Wit

Conclusions reached in a paper by weertmanl are amplified in a mathematical and graphical way. It is shown that in a stressed crystal a straight dis-location may be in a position of unstable equilibrium with respect to helix development, and how a small perturbation may start the dislocation off on its helical path. Helix development occurs by diffision; bulk diffusion is necessary for development from a screw, but core diffision is sufficient for development from an edge dislocation. For a mixed dislocation helix development can take place by core diffusion if the helix also climbs; a diffusion reversal takes place when the slope of the helix equals the slope of the Burgers vector. The work done on a crystal by the external forces is graphically shown to be consistent with the direction of motion of the dislocation in helix development. Finally a detailed mechanism for tangle formation from helices is presented. In the course of helix development a glide situation may be reached where a segment of each helix loop lies in a slip plane in which it can expand by glide. Thus is it visualized how a helix can deteriorate into a tangle. A paper by weertmanl proposes dislocation-tangle formation by a helical dislocation mechanism. The present paper amplifies Weertman's arguments in a mathematical and graphical way and presents some further ramifications of the proposed model. The importance of dislocation tangles is discussed in Weertman's paper and the references cited therein. The mechanism of their formation is not yet understood. Weertman proposes that in cold-worked crystals conditions exist suitable for the conversion of straight dislocations into helices and subsequently into tangles. Helix formation occurs by a diffusion process and Weertman proposes that at low temperatures only core diffusion is important. The present paper necessarily repeats some of Weertman's work. Since the mathematical development and notation used are slightly different from his, this was thought necessary for clarity. GEOMETRY OF THE HELIX weertman2 has shown that the equilibrium form of any dislocation line is a helix if it is assumed that the energy per unit length (line tension) of the dis- location is constant. For the special case that no external forces act on the dislocation, the helix reduces to a straight line. We shall assume in this paper that the dislocation has a helical form even when it is not in equilibrium. The parametric equation of a helix is, see Fig. l: where a is the radius of the cylinder tangent to the helix, and 270 the pitch of the helix. The pitch is related to v, the number of turns per unit length (along the axis) by the relation: When a = 0 Eq. [I] gives a straight line in the z direction. The growth of a straight dislocation into a helix is now described mathematically by letting a vary from zero to its final value. The tangent to the helix is given by where is the path length along the helix. This gives the direction of t and since its magnitude is unity we must have So that dcp/ds = (a2 +p2)-"'. The curvature of the helix is given by where n = -(cos + sin) is a unit vector normal to the helix. Note that the vectors k and n always point toward the axis of the helix, Fig. 1. FORCE ON THE HELIX The external force which makes the straight dis-

Jan 1, 1963

By K. R. Grube, D. N. Williams

It is often desirable to perform fatigue studies at relatively high strains and at low strain rates. A low-cost fatigue machine has been constructed for this purpose which has proven quite versatile. This machine is based on the principle of repeated bending of a strip sample over a shaped mandrel. A photograph of a group of fatigue tests in progress is shown in Fig. 1. The test sample is held in place between two shaped mandrels having a flat at their base to grip the sample firmly. A cam-driven loading frame is used to bend the sample alternately over each mandrel. The sample slides freely in this frame and is held in place by a light spring to accommodate increases in sample length. The pivot point for the loading frame is selected so as to minimize movement at the loading point during operation. The number of cycles to failure is recorded by a rachet counter which is kept in operation by a series electrical connection through the sample and is operated by the drive cam. The maximum strain imposed at the sample surface on bending from one mandrel to the other is readily calculated from the relationship, where t is the sample thickness and r is the radius of curvature of the mandrels. The rate of straining can be controlled by control of the cam speed. The device as shown in Fig. 1 is set up to run six samples at ambient temperature. A much larger number of samples can be run at one time without difficulty. ALSO-, by slight realignment of the components the mandrel unit can be enclosed in a separate chamber permitting control of test temperature and environment. This permits a variety of fatigue and corrosion fatigue problems to be studied.

Jan 1, 1963

By F. X. Tartaron

This article is a continuation of a previous paper by the writer in which Kick's Law was stated to be a part of comminution theory. ln the present paper, a broadening of ideas is attempted in order to state a general theory. The word "general" is employed because the new theory includes all previous laws and generalizations which are considered to be essentially correct. These ideas are combined into a coherent whole and the general theory can be expressed by the equation In the author's previous paper on comminution, ' the equations developed were based on Charles' equation of exponents a-n +1 = 0. 2 This paper is divided into two parts, designated as First Approach and Second Approach. In the First Approach, the equations of the previous paper are utilized, with Charles' equation of exponents being necessary. In the Second Approach, a separate and independent method is used to derive the same conclusions as in the First Approach, but without the use of Charles' equation of exponents. Holmes accepts the theoretical foundation of Kick's Law as sound but denies that the law as such operates in comminution. His idea is that Kick's Law requires homogenous matter whereas the presence of cracks, flaws and cleavage planes, which predominate in the coarser particles, makes matter unhomogene-ous. This explains why there is no experimental evidence to support Kick's Law. However, since the basis of the law is theoretically sound, all experimental evidence must be viewed as emanating from it. This requires modification of current comminution equations to fit this concept. Holmes makes the modification by changing the constant exponent n in the general energy equation used by Charles (E = - JCdx/xn) to a variable exponent r. The writer asserts that Kick's Law operates in comminution without modification but it does not

Jan 1, 1963

By W. L. Phillips

Stress-strain curves were obtained for single crystals of 70 pct Ag-30 pct Zn tested in tension and shear. Samples tested in tension and shear had comparable resolved shear stresses and stress-strain curves. The {111} <110> slip system was observed. It zoas found that the9.e is a barrier to slip in both latent close -packed directions and that the magnitude of these barriers is proportional to prior strain during easy glide. It was observed that cross-slip in tension and shear was most frequent in crystals with an initial orientation near <100> "Oershoot" zoas observed in tension. The amount of this "overshoot" was independent of initial orientation. AN idealized concept of plastic deformation indicates that a single crystal should yield at some stress that is dependent on crystal perfection and it should then continue to deform plastically by the process of easy glide which is characterized by a linear stress-strain curve and a low coefficient, d/dy, of work hardening. Hexagonal metal crystals generally conform to this ideal concept of laminar flow. In fcc metals the range of easy glide is always restricted in magnitude and it is strongly dependent on orientation, composition, crystal size, shape, surface preparation, and temperature. Since one of the principal differences between the two crystal systems, both of which deform by slip on close packed planes, is the existence of latent slip planes in the fcc crystals, it has been proposed that the transition from easy glide to turbulent flow, characterized by rapid linear hardening, is due to slip on secondary planes intersecting the primary plane.ls Several theories have been proposed to explain the linear hardening and parabolic stages of the stress -strain curve.6"10 The easy-glide region is the least understood of the three stages. The stress-strain characteristics of Cu-Zn, which shows a long easy-glide region, have been extensively investigated."-" In light of recent ideas on dislocations, cross-slip, effect of solute atoms, and stacking fault energy, it was felt that the certain features of this earlier work might be compared with another alloy, Ag-30 pct Zn, which also exhibits a long easy-glide region. Tension and shear stress at room temperatures were employed. The results obtained, together with some interpretation of the observations, are described below. EXPERIMENTAL PROCEDURE The silver and zinc used for mixing the alloys were 99.99 pct pure. The two components were weighed to within 0.1 pct of the weights required fo the alloy composition. They were then placed in a closed graphite mold and the mold and contents were heated in 100°C stages from 500&apos; to 900°C with sufficient time and vigorous agitation at each stage provided to dissolve the silver. The crucible was then heated to 1150°C and agitated violently before being quenched in oil. The resulting alloy rod was machined free of sur face defects and then placed in a graphite mold designed for growing single crystals. The graphite mold was closed with a graphite plug and was encased in a pyrex glass tube which was connected to a vacuum system. The tube and mold assembly were placed in a furnace; the tube was evacuated and the furnace was rapidly heated to a temperature sufficient for fusing and sealing the glass. The glass-encased evacuated mold and contents were then lowered through a vertical furnace. The top section of the furnace was held at 100 °C above the melting point of the alloy. The lowering rate was 1.5 in. per hr. The tension specimens were 1/4 in. diam; the shear specimens were 1/2 in. diam. These specimens were then removed from the mold, etched, and chemically polished with hot (60°C) Chase etch reagent (Crz03-4.0 g, NH4C1-7.5 g, NHOs-150 cc, HzS04-52 cc, and Hz0 to make 1 liter). In preparation for tensile testing, the specimens were carefully machined to a diameter of about 0.200 in. to permit a gage length of 6 in., annealed for 16 hr at 800&apos; to reduce coring, and then cleaned and polished. A modified Bausch-type shear apparatus which has been described previously18 were employed. The gage length was 1/8 in. This shear apparatus was placed in an Instron tensile testing machine. EXPERIMENTAL RESULTS A) Tension. Several specimens were extended at room temperature to determine the effect of initial orientation on the stress-strain curves of Ag-30 pct Zn. The initial orientation and the resolved shear stress supported by the active slip system at various total strains are plotted in Fig. 1. The critical resolved shear stress, t,, initial rate of work hardening, d/dy, and length of the easy-glide region are independent of orientation. The arrival at the symmetry line is shown by an arrow in Fig. 1. During the easy-glide region of the stress-strain

Jan 1, 1963

By Wei-Kao Lu

A general rate equation is derived for gas -solid reactions in metallurgical processes by considering the contributions of chemical reaction at inter-phase boundaries and diffusion through the solid product layer simultaneously. This equation takes care of the whole range continuously from purely diffusion control to purely chemical reaction control. The parabolic law,&apos; McKewan&apos;s equationa derived with the assumption of interface area control and the equation derived by Kawasaki et al. with the assumption of purely diffusion control are found as the limiting cases of the corresponding forms of the general rate equation. Many metallurgical processes involving gas-solid reactions have been extensively studied. The common examples of these processes include the reduction of oxides to metallic products, the roasting of sulfides to oxides or chlorides and the oxidation of metals. Gas-solid reactions consist of at least two kinds of steps; one involves the transport of reactant and product to and from the reaction zone and the other is the chemical reaction taking place at the interphase boundaries. In the limiting cases one or the other of the above mentioned steps will be much slower than the other and is then rate controlling. For example, the oxidation of metals is diffusion controlled and obeys the parabolic law.&apos; On the other hand, if the diffusion rate is much larger than the chemical reaction rate then it will be controlled by the chemical reaction rate. This latter case occurs for the reduction of iron oxides studied by McKewan. If the rate of diffusion and of the chemical reaction have the same order of magnitude, a more detailed analysis is necessary. Thus at the beginning of the reaction when the solid and gaseous reactants are in direct contact, the reaction should be chemical reaction rate controlled as no diffusion process is involved. At the other extreme as the reaction zone moves further into the solid, the diffusion distance becomes greater and the diffusion rate continuously decreases. Eventually, therefore, for a sufficiently large sample the rate must become diffusion controlled. As the transition from one controlling step to the other must be continuous, we cannot describe this transition period by either of the two limiting cases. In this paper the author attempts to derive a general rate equation for gas-solid reaction systems. This is effected by considering the rates of diffusion and chemical reaction simultaneously from the state of pure diffusion control to pure chemical reaction control. I) DERIVATION The system under consideration is made of at least three phases, namely the gaseous one, the solid reactant, and the solid product as shown in Fig. 1. The notations are listed at the end of the paper. The mass transfer process involves the diffusion of reactants and products across the solid product layer. It is reasonable to consider that no chemical reaction will take place in the solid product layer with respect to both gaseous reactant and product. For the characteristics of local equilibrium of the system, the diffusion process is really in a quasi-steady-state. It will be proved in the following paragraphs. Then we can invoke the law of conservation of mass valid for all chemical species passing through the layer. The solid reactant sphere has an initial radius, ro, after a fraction of completeness of the reaction, the unreacted core has a radius ri, where r, is in the solid product region. Let Cg be the activity of gaseous reactant in the

Jan 1, 1963

By R. A. Wood, R. I. Jaffee, H. R. Ogden, D. N. Williams

The tensile properties, creep resistance. and thermal stability of highly alloyed Ti-Al-Zr alloys were examined. On the basis of these studies, the Ti-7Al-1ZZr composition was selected for more complete evaluation. The alloy was found to be weldable and free from excessive directionality. In addition, it developed maximum properties without requiring heat treatment other than an annealing operation in the alpha field. The alloy was recommended for scale up and is presently being investigated on a production-level basis. One of the more attractive properties of titanium alloys is their ability to withstand stress at moderately high temperatures, and a considerable amount of effort has been devoted to increasing the maximum service temperature of titanium alloys. This work has suggested that the optimum alloys for high-temperature service will be single-phase a (close-packed hexagonal) alloys containing significant amounts of aluminum. However, the maximum amount of aluminum which can be alloyed with titanium is between 6 and 8 pct,l since at high-aluminum contents an embrittlement reaction occurs in the anticipated service temperature range, 800" to 1100°F. It has been shown that the embrittlement reaction involves decomposition of the high-aluminum a phase to one or more new phases.&apos; Since this reaction does not occur at intermediate or low-aluminum contents, it was felt that intermediate Ti-A1 alloys might be strengthened by a-soluble ternary additions without inducing the embrittlement reaction. The first alloying addition considered was tin, which shows extensive solubility in a titanium and has moderate strengthening tendencies. Unfortunately, it was soon apparent that tin also promoted the embrittlement reaction, and that to obtain a stable alloy, the aluminum content had to be reduced as the tin content was increased. The second alloying addition considered was zirconium, which is similar to tin in its effects on titanium. This element did not contribute to the embrittlement reaction and, in fact, appeared to increase the maximum amount of aluminum which could be alloyed with titanium without inducing instability. This paper describes an investigation of the Ti-A1-Zr a alloy region. Alloys containing from 4 to 12 pct A1 and from 6 to 15 pct Zr were examined. The properties of these alloys are described and the bases for selecting an optimum composition is outlined. This composition, Ti-7A1-12Zr, is presently being scaled up in tonnage quantities, and is being evaluated extensively throughout the industry. In addition to presenting the basis for its selection, this paper presents a description of the properties developed in laboratory material as determined during the alloy investigation. These properties suggest that this alloy can fill an important position in applications requiring light weight, fabrica-bility, weldability, and strength to 1000oF or higher. EXPERIMENTAL PROCEDURES Titanium alloy ingots were prepared by inert electrode arc melting under an argon atmosphere. Alloying elements used were 110 Bhn titanium sponge, high-purity aluminum, and reactor-grade zirconium. Pancake-shaped ingots were prepared weighing approximately 300 g. The composition of the ingots was checked by weight measurements before and after melting. The pancake ingots were forged at 2000°F to approximately half their original thickness to give a flat plate roughly 1/2 in. thick. This plate was then rolled at 1800&apos; to 1600°F to 0.250 in. thick. All of the alloys examined fabricated well. However, alloys containing 15 pct Zr tended to overheat due to exothermic oxidation, and scaling was excessive. As might be anticipated from its effect in decreasing the ß transus, increased zirconium appeared to improve fabricability somewhat, especially during rolling at lower temperatures. Except for a limited study of heat-treatment response, all alloys were examined in the a-annealed condition. Prior to heat treatment the a and ß tran-sus temperatures were determined by metallo-graphic examination of samples quenched after annealing at 50-deg intervals in the transformation region. These data are shown in Fig. 1. Recrystal-lization appeared to occur in about 1 hr in the range 1300º to 1500ºF. Therefore, alloys were annealed for 1 hr at 1550ºF (4 and 5 pct Al), 1600ºF (6 through 7-1/2 pct Al), or 1650°F (8 or more pct Al). This produced an equiaxed a grain structure. In most alloys, a "ghost" structure was visible after the a-annealing treatment, as shown in Fig. 2. This structure apparently resulted from the acicular

Jan 1, 1963

By Sylvia Whitehead, G. M. Schwartz, J. N. Gundersen

Sylvia Whitehead (Petrologist, The Broken Hill Propriety Co. Ltd., Melbourne, Australia) — Examination of thin sections of jaspilites from numerous banded iron formations in Australia has revealed no evidence to suggest that silicate minerals have formed by reaction between magnetite and silica. Textural relations indicate that part of the magnetite crystallized very early in the history of the rocks, probably during diagenesis, and remained stable under conditions of metamorphism altering only to hematite or limonite under conditions of oxidation and weathering. Many jaspilites also contain later magnetite which is almost certainly of metamorphic origin. Wherever magnetite is present in quartz rich bands containing little or no silicate or carbonate, it is very fine grained and occurs generally as isolated, well formed octahedral crystals or as small crystalline aggregates. These show no evidence of corrosion or reaction with the quartz even in rocks where adjacent bands contain silicate minerals of moderate to high metamorphic grade. Concerning the silicate minerals, it is reasonably certain that bands of very fine grained stilpnomelane

Jan 1, 1963

By R. S. Craig, W. E. Wallace, G. S. Kamath

The destruction of long-range order in Mg-Cd, has previously been thought to occur as a second order process. In the present work a variety of X-ray diffraction techniques are employed to show that in this case and in Mg-Cd alloys containing frorn 20 to 33 1/3 at. pct Mg the process more nearly resembles an ordinary first order phase transformation. It is found that the ordered alloy, which occurs as a single phase at lgw temperatures, transforms with increasing temperature into a Cd-enriched disordered (P) phase and an Mg-enriched ordered (a) phase. The interval over which these two phases coexist under apparently equilibrium conditiovs extends from 25" to 87°C content. At 33 1/3 at. pct Mg the two-phase region has disappeared. Measurement of the long range order parameter, s, for the ordered phase in MgCd, (from superlattice line intensities) shows that it disorders only very slightly before it is transformed into the p form. Kinetic experiments reveal that when the a phase is formed frorn the p phase by suitably quenching so as to suppress phase segregation, the transformation is essentially complete and the a phase has acquired its equilibrium value of S in less than 1 min. In an earlier investigation carried out in this Laboratory1 the rate of disordering of the MgCd3 superlattice was determined over an extensive range of temperature. The process was found to be first order and the rate constant, k, was established. At the lowest temperatures studied k was found to increase exponentially with temperature. At higher temperatures, however, it passed through a maximum and for the 100 deg interval below the point at which the superlattice was destroyed k was observed to decrease with increasing temperature. The various theoretical treatments1-3 of order-disorder phenomena lead to a negative temperature coefficient for k near the superlattice critical temperature but this region for MgCdB seemed unusually wide. Detailed analysis of the point indicated&apos; that either the long-range order parameter, S, for MgCda varied with temperature in an anomalous way or the disordering in this instance is more complex than in the cases which have been treated theoretically. The original objective in the present work was simply to determine S vs temperature for MgCda to ascertain whether the disordering was in conformity with theoretical expectations.2° In an early stage of the work it was noted, however, that under equilibrium conditions ordered (a) and disordered (0) phases coexist in MgCd, over a considerable range of temperature. Since on thermo- dynamic grounds the coexisting phases must differ in composition, the investigation was enlarged to permit the compositions of the two phases in MgCd3 to be determined and to establish the extent of the two phase regions for alloys containing from 20 to 33 1/3 at. pct Cd.

Jan 1, 1963

By W. C. Leslie

W. C. Leslie (Edgar C. Bain Laboratory for Funda mental Research)—This investigation, with its com bination of high-purity metal, calorimetry, and metallography, will serve as a model for annealing studies for a long time to come. The evidence for a competition between recovery and recrystalliza-tion is particularly convincing. The demonstration of edge-nucleated recrystallization was so clear that it may obscure the necessity for other types of "nucleation" sites; otherwise, single crystals of aluminum could not be recrystallized after cold work. At least three types of sites have been found to operate in iron: 1) high-angle boundaries, probably in the same manner as in aluminum, 2) matrix sites, 3) inclusions or second-phase particles. In each instance, the cells developed during cold work and perfected during recovery are the "nucle for recrystallization. Observations by ourselves and others of the dislocation structure of cold-worked metals and of the structural changes that occur during annealing have led us to doubt the validity of the basic assumption of the Lucke-Detert theory, and of the modification developed by Gordon and Vandermeer, that during recrystallization of a metal containing foreign elements in solid solution a high-angle boundary is ad vancing into a cold-worked matrix having a random distribution of solute atoms. We contend that an es sential part of the cold-working and annealing of solid solution alloys is the trapping of solute atoms by the low-energy "wells" afforded by individual dislocations and by dislocation arrays. If cells are formed during cold work, the cell walls are stabilized by this concentration of solute atoms. Thus, solutes inhibit recrystallization not only by decreas-ing the rate of high-angle boundary migration, but also by preventing the formation of high-angle boundaries by subgrain growth or coalescence, i.e., solutes can inhibit both "nucleation" and growth. In addition to stabilizing the dislocation Structure, the solute-dislocation interactions may produce clusters of solute atoms which are not as readily assimilated into the recrystallized grains as are individual solute atoms. There is an additional complication. The dislocation structure formed upon cold working a dilute solid solution may not be the same as that formed during cold working of the pure solvent metal. The solute can either enhance or minimize the formation of cells during cold working. Both effects have been observed in binary alloys of iron. The annealing process is inextricably connected with the mechanisms of strain hardening and solid solution hardening. Although the correlation between experimental boundary migration rates and the predictions made from the theoretical equations are impressive, it should be mentioned that in at least four other instances (Pb-Ag and pb-Au,15, Fe-Mn,16, Fe-Mo)17 the agreement was rather poor. In brief, while it is probable that the migration of high-angle boundaries is held back by solutes in the manner described, this is only a partial explanation of the total effect of solutes upon recrystallization of cold-worked alloys. Paul Gordon and R. A. Vandermeer (author&apos;s reply)— The authors first wish to thank Dr. Leslie for his compliments of this work. It is perhaps worth pointing out that some of Dr. Leslie&apos;s remarks are directed toward subject matter covered in two earlier papers in our work.18,19 We agree with Dr. Leslie&apos;s main contention that the exact nature of the metal structure in the vicinity of a boundary should have an effect on the boundary migration. The theory of Lucke and Detert does not take such detail into account, nor does it account for orientation effects on the migration rates. We assume that since our data checks the theory so well, the effects of detailed structure are statistically averaged out by the polycrystalline techniques used just as are the effects of orientation factors.

Jan 1, 1963

By Leonard Bernstein, Harry Bartholomew

MANY of the properties of metals and alloys are structure dependent. Not the least of these is the grain structure. For example, in producing alloy bonds between silicon or germanium and gold-alloy foil at temperatures above their eutectics (which are, respectively, at 370" and 356°C) but below the melting points of the individual constituents, it was found that wetting was more complete with a fine-grain structure than with a coarse-grain structure. In cases where the assemblies were held together for long periods of time at elevated temperatures, wetting was not as critically dependent on the grain structure as was the case for shorter periods of time. When liquid phase forms, it first forms in the grain boundaries due to the fact that most of the impurities are concentrated at the grain boundaries and that most impurities tend to lower the melting point of the gold alloy somewhat. In addition, grain boundaries are at high-surface free-energy levels and are thus in a more favorable condition to initiate good wetting. A fine-grain structure will have more grain boundaries per unit area than coarse-grain structure thereby making wetting somewhat easier. To make the grain structure of an alloy sys- tem visible, a satisfactory method for differentiating between the different grains of which the system is composed must be employed. For the alloy bonding system previously described, the grain structure on the foil surface is of primary interest. Conventionally used etchants for the gold-alloy system will not adequately delineate grain boundaries in their structures. For this reason an alternate method is proposed for those cases where such a determination is necessary. Foil between 0.0005 and 0.005 in. thick has been used in this determination. The equipment used in this investigation was described in a previous publication.&apos; Essentially, it employs a resistance-type filament which can be heated up very rapidly and cooled very rapidly. A thin refractory material is placed on top of the heating element. This refractory material may be molybdenum, tantalum, tungsten, or even ceramic but its thickness should be less than 0.010 in. to minimize the temperature gradient across it. The gold-alloy foil is placed on top of this refractory material. The temperature of the heating filament is raised to 900°C and cooled down to below 100°C in 5 to 10 sec. During this cycle, the foil can be observed to plastically deform due to its own weight. With no further chemical etching, this assembly is then viewed under a standard metallurgical microscope and the grain size measured. Fig. 1 is a Au-1 pct Sb alloy at 400X magnification and Fig. 2 is a Au-1 pct Ga alloy at 130X. This technique has proved to be an adequate means for controlling processing conditions in producing large quantities of gold alloy foil.

Jan 1, 1963

Jan 1, 1963

By A. S. Yue

The interface morphology of the Mg-32 wt pct A1 eutectic has been studied in terms of the freezing rate, the temperature gradient, and the impurity content. For the impure eutectic it has been found that for a given temperature gradient a fast freezing rate favors the formation of a cellular intwface with sub-grain strucfure. This cellular interface can be changed to a planar interface of the same substructure either by decreasing the freezing rate or by increasing the temperature gradient. For the eutectic of highest purity, as purified by zme-refining, no cellular interface was found for any growth condition and only a planar interface with subgrain structure was observed. Furthermore, a layer of liquid adhering to the interface during de-cantation freezes with shapes and sizes of the phase particles different from those in the main eutectic solid. WHEN a molten metal or a binary eutectic liquid with zero freezing range is solidified unidirec-tionally, a cellular interface is usually formed-3 This interface is schematically represented by Fig. 1. The profile of the solid-liquid interface has a corrugated shape, as shown in Fig. l(a), while the decanted interface consists of cells, as shown in Fig. l(b). The cell boundary in a frozen eutectic is distinguishable from the cell interior by changes in particle shapes, as shown in Fig. 4. The formation of a cellular interface, according to Weart and ack,&apos; is attributed to a layer of constitutionally supercooled" liquid generated at the advancing interface by the simultaneous rejection of an impurity by the two phases of the eutectic mixture, which then permits freezing over an appreciable temperature range. This concept has been further elaborated by Tiller, who predicts that even in the absence of an impurity the rejection of solute ahead of each lamella of the eutectic may promote the formation of a cellular interface. More recently, Chilton and Winegard, and

Jan 1, 1963

By A. Arrott, G. S. Ansell

A model is proposed to account for the observed strengthening behazlior of ferrous martensites. me model is based upon the inheritance of carbon-rich regions by the martensite which were present in the FERROUS martensite is formed by a nucleation and shear mechanism when austenite is cooled, at a rate which is fast enough to suppress the formation of pearlite, below a critical temperature (Ms ). Although the mechanism of the transformation process appears to be well understood,1,2 the mechanism re- austenite prior to transformation. These carbon-rich regions strengthen the martensite in a manner analogous to the strengthening effect due to a finely dispersed second phase. sponsible for the observed high strengths exhibited by ferrous martensites is uncertain. In this paper, a model is proposed to account for the strengthening of ferrous martensite. MODEL The maximum solubility of carbon in austenite is 1.98 wt pct as compared with a maximum solubility of 0.025 wt pct in ferrite. Prior to transformation, the carbon in the austenite is nonuniformly dis-

Jan 1, 1963

By I. R. Kramer

Studies of the effect of size of the specimen on the change of slopes of Stages I and 11 by surface removal showed that the change of Stage I was independent of size with respect to the polishing rate; however, the change in the slope of Stage 11 with polishing rate increased directly in proportion to the surface area. The removal of the surface during the test affected the plastic deformation characteristics of gold, aluminum, and zinc single crystals and polycrystalline aluminum. The apparent activation energy of aluminum was found to be decreased markedly by removing the surface during the deformation process. In previous papers1-3 it was shown that the surface played an important role in the plastic deformation of metals. By removing the surface layers of a crystal of aluminum by electrolytic polishing during tensile deformation, it was found that the slopes of Stages I, II, and III were decreased and the extents of Stages I and II were increased when the rate of metal removal was increased. By removing a sufficient amount of the surface layer after a specimen had been deformed into the Stage I region, upon reloading, the flow stress was the same as the original critical resolved shear stress and the extent of Stage I was the same as if the specimen had not been deformed previously. The slope of Stage I was decreased 50 pct and that of Stage 11 decreased 25 pct when the rate of metal removal was 50 X 10"5 ipm. These data show that in Stage I the work hardening is controlled almost entirely by the surface conditions, while in Stages 11 and III both surface conditions and internal obstacles to dislocation motion are important. It appears that during the egress of dislocations from the crystal, a fraction of them becomes stuck or trapped in the surface regions and a layer of a high dislocation concentration is formed. This layer would not only impede the motion of dislocations, but would provide a barrier against which dislocations may pile up. In this case, there will be a stress, opposite to that of the applied stress, imposed on the dislocation source and dislocations moving in the region beyond this layer. It has been found convenient to refer to this layer as a "debris" layer. The "debris" layer may be similar to the dislocation tangle observed by thin-film electron microscope techniques.4 Reported in this paper are the results of studies on the effects of removing the surface during plastic deformation on aluminum crystals of various sizes. The effects of the surface on the yield point behavior of gold and high-purity aluminum crystals as well as the creep behavior were also determined. The effects of surface removal on polycrystalline aluminum (1100-0 and 7075-T6) are also reported. EXPERIMENTAL PROCEDURE For those portions of the investigation involving creep and tensile specimens, single crystals, having a 3-in. gage length and a nominal 1/8-in. sq cross section, were prepared by a modified Bridgman technique using a multiple-cavity graphite mold. The single crystals were prepared from materials which had initial purities of 99.997, 99.999, 99.999, and 99.999 pct for Al, Cu, Zn, and Au, respectively. The aluminum specimens for the size effect studies were prepared through the use of a three-tier mold in which crystals having a cross section of 1/8, 1/4, and 1/2 in. were grown from a common seed. The mold design was arranged so that one 1/2-in. crystal, two 1/4-in. crystals, and four 1/8-in, crystals of the same orientation could be cast. With this technique, it was possible to obtain only one set of crystals with the same orientation. Because of this limitation, it was not possible to determine both the changes of extent and slope of the various stages since a large number of crystals of the same orientation would have been required. Instead, only the change of slope as a function of the rate of metal removal was studied by abruptly altering the current density of the electrolytic polishing bath at various strains within the regions of Stages I and 11. The experimental techniques used for the tensile studies were essentially the same as those used previously.1,3 The specimens were deformed in a 200-lb Instron tensile machine, usually at a rate of 10-5 sec-5. A methyl alcohol-nitric acid solution was used as the polishing bath for aluminum. The temperature was maintained constant within ±0.l°C by means of a water bath. The tensile machine was

Jan 1, 1963

By Douglas Ragland

Two subjects certain to incite interest among a few practicing engineers and almost all engineering educators are professional recognition and decline in engineering enrollments. It is not surprising that this interest on the part of the educators is universal; it is only regrettable that such an interest on the part of the practitioners is not more widespread. In fact, it is probably the hope of the profession that some of the more penetrating searches now being made into the nature of engineering will generate sufficient cause for perplexity that members of the profession will assume a significant degree of personal concern toward purely professional matters.

Jan 1, 1963